本实用新型公开一种硅钢片卷料悬吊上料装置，包括装配架，装配架之间装配有若干个左右间隔设置的硅钢片卷料限位装置，所述硅钢片卷料限位装置用于装载硅钢片卷料、装配架包括前后对称设置的架板，所述架板上具有矩形凸出端、前、后部位之间所述矩形凸出端之间装配有若干个左右间隔设置的长螺杆、长螺杆贯穿所述硅钢片卷料限位装置，所述长螺杆的端部螺纹连接有螺母、架板的底部固定连接有两个左右间隔设置的轮架杆，所述轮架杆的左右两端均转动连接有滚轮、轮架杆之间固定连接有C形架杆，所述C形架杆上固定连接有悬吊环体，实现将大量生产加工使用的硅钢片卷料进行上料。采用上述方式不仅实现将大量生产加工需要的硅钢片卷料进行输送。

结合扫描电镜和大样电解研究了CSP流程W800牌号无取向电工钢表面线状缺陷中夹杂物成分及来源，采用SPSS软件回归分析了生产过程各因素对表面线状缺陷的影响。研究表明：稳态浇铸过程铸坯中大型夹杂物含量为5.39 mg/10 kg。引起无取向电工钢表面线状缺陷的大型夹杂物主要为脱氧产物、镁铝尖晶石和钢包顶渣，主要类型为Al₂O₃、MgO-Al₂O₃、CaO-Al₂O₃-MgO和CaO-Al₂O₃-SiO₂。非稳态浇铸过程钢水洁净度明显降低，热轧板表面线状缺陷比例上升。影响表面线状缺陷的主要因素为RH出站时顶渣的w（CaO）/w（Al₂O₃）、RH脱氧结束氧位及中间包最低吨位。 Combining scanning electron microscopy and large sample electrolysis, the composition and source of inclusions in the surface linear defects of W800 grade non-oriented electrical steel in the CSP process were studied. SPSS software was used to regress and analyze the main factors which affected the surface linear defects in the steelmaking process. Research shows that the content of large inclusions in the steady state casting process is 5.39 mg/10 kg. The large inclusions which cause linear def... 

本发明公开了一种低铁损高磁导率无取向电工钢及其生产方法，所述生产方法包括以下步骤：钢水连续浇铸成板坯，板坯经加热炉加热，再经热轧得到热轧板，然后经空冷和水冷后在500～650℃进行卷取；热轧板经常化处理、盐酸酸洗；酸洗后在可逆轧机上进行冷轧；最后经成品退火，退火温度为840～900℃，加热时间为240～500s；然后以不超过3℃/s的冷却速度冷却至500℃以下；涂覆绝缘涂层、固化，后经二次退火，即可得到低铁损高磁导率无取向电工钢，其磁性能满足P1.5/50≤3.50W/kg，μ1.5≥3800Gs/Oe，B5000≥1.76T的要求。

主要对硅钢退火炉耐材施工进行阐述,对一期工程与二期工程施工经验进行总结,包括设计、施工、耐材生产、人员素质等方面,指出了工程项目所所存在的不足,为同类型炉窑的施工提供借鉴。 This paper describes the construction of silicon steel annealing furnace refractories;and it was summarized the construction experience of phase-Ⅰ and phase-Ⅱ projects,including design,construction,refractory production,the quality of personnel etc,and pointed out the shortcomings of the project,which provided a reference for the construction of the same type of furnaces. 

本实用新型提供了一种变压器硅钢片吊装工具，属于变压器技术领域。其技术方案为：一种变压器硅钢片吊装工具，包括勾体，所述勾体上端设置有吊环，所述勾体下端设置有吊台，所述吊台上设置有阻挡机构，所述阻挡机构设置在所述吊台的底面。本实用新型的有益效果为：本实用新型通过勾体对硅钢片进行起吊，可以有效的防止硅钢片两端卷边，从而减少了变压器空载损耗，阻挡机构可以有效的防止硅钢片在运输过程中从吊台上摔落，从而保护了硅钢片的完整性，提高了使用效率。

本发明涉及一种电力变压器取向硅钢片自动化加工系统，包括支撑台、支撑板、传动机构、堆叠机构和调整机构，所述的支撑台上端左右两侧对称设置有支撑板，支撑板相对面设置有传动机构，支撑台上端中部设置有堆叠机构，支撑台上端面上且位于堆叠机构左右两侧对称设置有调整机构；本发明能解决以下问题：本发明通过传动机构对硅钢片前后移动，通过推动支链对硅钢片移位、放置、拿取，增加对硅钢片进行自动化堆叠效果；通过调整机构对硅钢片X方向面和Y方向面进行感应式自动调整；通过堆叠机构对硅钢片二次调整，避免硅钢片发生移动，从而使硅钢片堆叠的更加整齐，并且节约制造成本。

利用DSC、XRD,结合热焓分析对硅钢级氧化镁和二氧化硅的固相反应行为进行了研究。比较了不同二氧化硅原料及混合方法对硅钢级氧化镁反应性的影响,找到了一种更为有效的硅钢级氧化镁反应性的评估方法,克服了传统柠檬酸活性法在比较不同厂家生产的氧化镁的反应性上的局限性。进一步研究了Na₂B₄O₇添加剂、TiO₂添加剂对氧化镁和二氧化硅反应行为的影响,结果表明,Na₂B₄O₇添加剂含量的增加对反应有利,而TiO₂添加剂对反应有阻碍作用。 The solid-state reaction behavior between silicon-steel grade MgO and SiO₂ was investigated by DSC and XRD combined with enthalpimetric analysis.The influence of different kinds of SiO₂ and different preparation methods were studied and a specifical measurement that is more reliable was proposed to evaluate reactivity of silicon steel grade MgO.It overcomes the limitation of the traditional citric acid activity（CAA） method,which can not be used to evaluate the reactivity of... 

含铜抑制剂作为取向硅钢的主抑制剂或辅助抑制剂不仅可以抑制初次晶粒的长大,促进二次再结晶,还可以降低铸坯的加热温度。取向硅钢中主要抑制剂为10～50 nm Cu₂S,在钢的铸坯、热轧、冷轧、脱碳等工艺过程均可析出;（Cu,Mn）_1.8S、Cu_1.8S、ε-Cu等主要作为辅助抑制剂,尺寸一般为30～50 nm（或大于50 nm）,主要在热轧阶段析出。总结了国内外有关取向硅钢中含铜抑制剂析出行为的研究进展,当前主要研究不同生产流程和工序中含铜抑制剂的析出行为和作用机理。 As main inhibitor or auxiliary inhibitor for grain-oriented silicon steel,the particles of inhibitor bearing copper not only inhibit the primary crystal growing and promote the secondary recrystallization,but also decrease the heat temperature of casting slab.The main inhibitor for grain-oriented silicon steel is 10～50 nm Cu₂S,which precipitate in process and procedure including steel casting slab,hot rolling,cold rolling and decarburizing process,while the 30～50 nm or more than 50 nm... 

用于层叠铁芯的电磁钢板为一种在母材钢板(2)的表面具有绝缘被膜(3)的电磁钢板，该绝缘被膜(3)是涂布电磁钢板用涂布组合物而构成的，所述电磁钢板用涂布组合物以特定的比例配合有环氧树脂、第1固化剂及第2固化剂，该第1固化剂由包含具有烷基及烷氧基中的任意一者或两者的酚骨架的酚醛树脂构成，该第2固化剂为从酚醛甲阶树脂及苯酚酚醛清漆树脂中选择的1种以上。

本发明提供一种优化无取向硅钢连续退火工艺的铁损预测方法，步骤包括：S1.建立预测模型回归方程表达式；S2.将无取向硅钢中的硅、锰、铝质量含量及预设的退火速度、退火温度代入S1中的回归方程表达式中进行计算；S3.将步骤S2计算得到的预测值与目标值进行比较，如果预测值在目标值的允许误差范围内，则按照预设的退火速度、退火温度进行生产；否则对预设的退火速度、退火温度进行调整，直至预测值能够达到目标值的要求后再进行生产。本发明提供的模型能够提高产品质量，对优化无取向硅钢连续退火工艺具有指导意义。

本实用新型涉及电机技术领域，具体涉及一种具有低应力隔磁桥的硅钢片和电机转子。包括硅钢片、开设在硅钢片上的若干个磁钢槽组和永磁体，若干个磁钢槽组沿所述硅钢片周向分布，每个磁钢槽组均至少包括一对沿径向对称分布的磁钢槽，永磁体嵌设于磁钢槽内，磁钢槽朝向硅钢片内侧的一端设有空腔，一对磁钢槽的空腔之间通过隔磁桥隔离，隔磁桥的空腔上壁面与空腔侧壁面之间通过第一椭圆弧过渡连接，隔磁桥的空腔下壁面与空腔侧壁面之间通过第二椭圆弧过渡连接。有效降低该处隔磁桥在拐角处所受应力，进而提高该隔磁桥的强度，避免磁钢和铁芯产生形变而断裂。

通过在实验室条件下模拟薄板坯连铸连轧流程,并在以Cu2S为主抑制剂制造普通取向硅钢(CGO)的基础上,加入适量钒钛,研究了钒钛对取向硅钢组织与磁性能的影响。结果表明,适量钒钛使热轧板和脱碳退火板组织更好,尤其使脱碳退火板的晶粒更加细小和均匀;加入适量钒钛不但使热轧板表面高斯织构强度更高,更使脱碳退火板中有利于高斯织构发展的γ织构强度更高;适量钒钛能形成Cu2S+(V,Ti)N等复合析出物,起到辅助抑制剂作用,加强抑制能力。细小均匀的晶粒、强度更高的有利织构和更强的抑制能力使CGO钢磁性能更佳。 Effect of V and Ti on microstructure and magnetic properties of conventional grain-oriented silicon steel(CGO) were investigated under simulated thin slab continuous casting and rolling process in laboratory with Cu2 S as the dominant inhibitor. The results show that appropriate amount V and Ti make the microstructures of the hot rolled sheet and the decarburizing annealed sheet better,especially make the grains of the decarburizing annealed sheet more tiny and uniform. Adding appropriate V and ...