硅钢资料

本实用新型公开了一种新型嵌线结构的硅钢片组件，包括硅钢片组和骨架，硅钢片组由若干相同形状的硅钢片堆叠而成，硅钢片为倒U型的薄片体，骨架由一限位框架和两固定杆组成，限位框架由一矩形框架和位于矩形框架四角的限位凸块组成，硅钢片组卡设在矩形框架上，限位凸块对硅钢片组进行限位，两固定杆平行设置在硅钢片组的上方，且固定杆的两末端分别与限位凸块相固定。本实用新型具有装配简单、不易变形的优点。

本实用新型公开了一种硅钢片冲压模具，包括上模和下模，上模和下模之间通过导向杆连接，下模上设有出料槽，出料槽的底部设有一磨盘，磨盘通过齿轮连接电机。本实用新型结构设计合理巧妙，当硅钢片冲压下落时，磨盘通过电机带动转动，对硅钢片的周围进行打磨，使硅钢片边缘平整，叠铆时上下不易错位。

用还原分离-原子荧光光谱法分析了硅钢中的痕量汞.分析方法的不确定度主要来自测量重复性,样品溶液浓度,工作曲线变动性,标准溶液,移取、配制标准溶液,仪器变动性等.文章分别对上述构成合成不确定度大小的分量进行了计算讨论. Trace mercury in silicon steel and galvanized sheet was analyzed by adopting reduced separation-atomic fluorescence spectrometry.The uncertainty of the analysis method mainly comes from measurement repeatability,sample concentration,working curve volatility,standard solution,pipetting and preparation of standard solution,and instrument variability,etc.The essay conducted all calculations and discussions on the above components that determine uncertainty. 

本申请公开了一种低铝无取向硅钢结晶器液面波动的控制方法，包括：步骤1：KR脱硫，脱硫后铁水硫含量≤0.0015%；步骤2：转炉吹炼，转炉出钢后钢包顶渣厚度≤30mm；步骤3：RH真空处理，RH脱碳结束后，加入铝粒脱氧后钢液循环3‑5min，提升气体流量至0.8‑1.0m3/（h·t）；随后加入合金进行脱氧合金化，提升气体流量至0.5‑0.7m3/（h·t）；步骤4：连续浇注，长水口氩气流量150‑200L/min，连铸塞棒氩气流量5‑10L/min，背压≥0.05bar。本申请的控制方法控制结晶器液面波动≤±1.5mm的比例稳定在90%以上。

【作者】 常波； ...

本实用新型属于输送设备技术领域，具体涉及一种硅钢拉伸平整用转向辊，包括辊本体，辊本体的中部可拆卸的安装有环形凸块，环形凸块的宽度在350‑450mm，环形凸块的厚度在3‑5mm。在本方案中，在辊本体的中部设置环形凸块，环形凸块能较好的与硅钢的中部位置接触贴合，辊本体通过环形凸块除了能较好的将硅钢输送向前，还能有效防止硅钢跑偏。环形凸块可拆卸的安装辊本体上，当环形凸块使用了一段时间发生了严重的磨损时，更换新的环形凸块即可，无须更换辊本体，有效节省成本。

运用电子背散射衍射(EBSD)技术,研究了50W600无取向硅钢在热轧→冷轧→退火工序间织构的演变。结果表明:由于热轧板沿板厚方向的应力场和温度场存在差异,导致热轧板不同层织构类型和强度存在差异;热轧板表层主要存在铜型、黄铜和高斯织构,1/4层织构主要为α纤维织构和较弱的高斯织构,中心层织构较单一,主要为α纤维织构;和热轧板相比,冷轧板各层织构差异较小,为典型的轧制织构(α纤维织构和γ纤维织构);退火板各层都表现为γ纤维织构增强、α纤维织构减弱,旋转立方织构基本消失。 The texture evolution of 50W600non-oriented silicon steel in hot rolling,cold rolling and annealing process was investigated by electron back-scatter diffraction(EBSD)technology.Results show that the hot rolled plate texture types and intensities along thickness direction were different because of the different stress fields and temperature fields.The major texture types in the surface of hot rolled plate were copper,brass and Gauss texture.The texture was composed ofαfibre texture and weaker Ga... 

为了解决目前冷轧产线硅钢现有切边技术存在的微裂纹、应力、毛刺和边浪等问题,采用光纤激光器进行了高速切割实验,对激光功率、切割速度、激光模式等影响因素进行了分析,同时对高速切割时的切割前沿形状进行了研究。结果表明,切割最高速度随着功率的增加而增加;随着离焦量的增加,切割质量下降,挂渣增多,切缝宽度增加,切割深度变浅;基模激光器能量密度更高,所以薄板切割时的切割速度高于多模激光器;切割前沿随着切割速度的增加会变得平缓,速度足够大时,切割前沿甚至接近与切割方向平行,此时切缝下部存在挂渣现象。 In order to solve the problems such as micro crack,stress,burr,edge waves and so on,existing in cold rolling production line of silicon steel side cutting,experimentsof high speed laser cutting using fiber laser were carried out.Laser power,cutting speed,laser mode and other factors were analyzed,at the same time,cutting front geometries were studied.The results show that the maximum speed increases with power.And the increases of defocus result in poor quality,wider kerf and shallowerkerf.Energ... 

本发明提供能够制造实现高磁通密度且磁特性优异的方向性电磁钢板的新颖并且得以改良的方向性电磁钢板的制造方法。本发明的一方案提供一种方向性电磁钢板的制造方法，其特征在于，其包含热轧工序、冷轧工序、一次再结晶退火工序、最终退火工序及平坦化退火工序，并进行喷丸处理和/或矫平加工处理及与溶液相接触的处理，上述溶液含有规定量的Cu等，pH为‑1.5以上且低于7，液温为15℃以上且100℃以下，钢板在上述溶液中浸渍的时间为5秒以上且200秒以下。

一种高硅钢的电渣重熔生产方法，电渣重熔过程渣系组成为，按重量计，CaF255%～59%、Al2O326%～30%、CaO7%～10%、SiO21%～9%，所述高Si钢，按重量计，钢中含有Si0.5%～2.0%，Al0.01％～0.05％。采用本专利设计的渣系成分配比，保护气氛电渣的情况下，可有效控制Si含量0.5‑2.0%的高Si钢电渣过程不增铝。

本申请实施例公开了一种硅钢铁芯生产用多功能卷绕机，包括平台板，所述平台板底部的左侧固定连接有旋转电机，所述旋转电机的输出端固定连接有旋转杆，所述旋转杆的顶部固定连接有转盘，所述转盘的顶部固定连接有铁芯型模，所述铁芯型模的外表面活动连接有限定座，所述平台板顶部中心的左侧固定连接有第一U型板。第一弹簧和升降板的配合使用，可以让使用者下压升降板，使得升降板带动安装杆进行向下移动，继而使得安装杆脱离第二U型板所开设的轴槽，继而使得安装杆的顶部存在一定的间隙，进而可以通过间隙将带盘插入在安装杆上，该方式装卸起来简单快捷，可以有效的减少装卸带盘所消耗的时间，从而提高了设备的工作效率。

本发明涉及变压器硅钢片技术领域，尤其是涉及一种变压器硅钢片组件成型冲裁机械及成型冲裁方法，包括基座、收卷装置、挤压装置、滚动装置和冲压装置，所述基座的上端位于四角处均固定连接有竖杆，竖杆的上端共同连接有横板，横板的下端设置有冲压装置，基座的上端设置有收卷装置，基座的上端位于收卷装置的后方设置有挤压装置，基座的上端位于挤压装置的后方设置有滚动装置；通过拉动拉环，带动圆板和推杆挤压第一弹簧，第一弹簧的挤压，使得推杆远离推槽，进而可取出模具，对模具进行更换；通过往凹槽内加入放置板，防止压板在撞击模具时，对模具进行支撑，防止模具发生变形。