【作者】 姚昌国； ...

【作者】 O.M.Гбанов； A.E.Чеглов； ...

【作者】 朱传芳； 潘恒韬； ...

试验研究了0.3 mm取向硅钢冷轧板(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005A1)的退火温度(760~880℃7 min)和退火时间(820℃3~9 min)对该钢的晶粒尺寸,再结晶和织构的影响。结果表明,最佳初次再结晶退火工艺为820℃5 min,该钢的平均晶粒尺寸为14.20μm,完全再结晶率为92%,不利{111}<110>结构含量为3.16%,有利织构{111}<112>,{012}<001>和高斯织构含量分别0.40%,4.73%和2.46%。 The effect of annealing temperature(at 760 ~ 880 X.for 7 min) and time(at 820℃ for 3~9 min) on grain size,recrystallization rate and texture of 0.3 mm cold-rolled sheet of oriented silicon steel(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005Al) has been tested and studied.Results show that with optimum recrystallized annealing at 820℃ for 5 min,the silicon steel average grain size is 14.20 fun,the complete recrystaUization rate is 92%,the unfavourable-texture {111}< 110 > content in steel is ... 

本发明属于双取向硅钢技术领域，公开了一种双取向硅钢薄带及其制备方法，包括：选取具有Si、Al、Mn、C和Fe，且具有一定取向的硅钢薄带；将其进行冷轧；将冷轧板在N2、H2保护气氛中进行退火处理。本发明通过合理的轧制和退火工艺搭配，使具有Goss取向的硅钢薄带转变为具有旋转立方取向的硅钢薄带，将单取向硅钢转变为双取向硅钢。本发明具有工艺简单和便于利用钢铁企业现有设备的特点，所制备的双取向硅钢薄带具有双向铁损低和磁感高的性能。本发明制备的双取向硅钢薄带在与轧向成45°的两个方向上具有优异的双向磁性能，解决了现有双取向硅钢薄带的制备工艺复杂、设备要求高、不利于工业生产的问题。

本实用新型提供了一种无取向硅钢涂层喷涂装置，属于冶金行业涂层技术领域，包括上涂辊和下涂辊，所述上涂辊一侧设有上喷淋管，下涂辊一侧设有下喷淋管，在上涂辊和下涂辊间的水平面上方设置一个倾斜挡板，所述上喷淋管对准倾斜挡板，下喷淋管对准下涂辊，所述下涂辊下方设置一个涂液收集槽，下涂辊部分置于涂液收集槽中，涂液收集槽底板设有涂液回流口，所述涂液收集槽通过一个升降装置调节自身高度。该装置稳定性好，可靠性高，能够有效保证无取向硅钢下表面涂层质量，避免出现漏涂或者涂层条纹缺陷，提高无取向硅钢涂层质量。

利用背散射衍射技术(EBSD)和XRD,研究了两段式脱碳退火工艺对取向硅钢纵截面初次再结晶的微区取向、取向差分布、特殊晶界(CSL)及高温退火试样高斯织构。分析了初次再结晶晶界特征对取向硅钢高温退火后宏观织构的影响。结果表明:初次再结晶的纵截面基体中Σ3和Σ5晶界使得高斯晶粒有着较高的迁移率,在高温退火时借助20o～45°的大角度晶界的界面能吞并周围{111}<112>晶粒迅速长大,形成密度水平较高的高斯织构。 Micro area orientation of primary recrystallization,the misorientation distribution,special boundaries under different two-stage decarburization annealing and the Goss texture under high temperature annealing the longitudinal section of grain-oriented silicon steel were detected by electron back scattering diffraction(EBSD) and X-ray diffraction(XRD).The effect of primary recrystallization grain boundary on macrotexture after high temperature annealing was analyzed.The results show that the Σ3 a... 

本实用新型涉及熔融石英陶瓷生产技术领域，且公开了一种高密度熔融石英陶瓷高磁感硅钢炉，包括底板，所述底板的顶部固定连接有高磁感硅钢炉本体，所述高磁感硅钢炉本体的顶部固定连接有密封轨，所述底板顶部的左右两端均固定连接有立柱，所述立柱的顶部固定连接有箱体，所述箱体的右侧固定连接有调节电机，所述调节电机的输出轴固定连接有螺杆，所述螺杆外表面的左右两端均螺纹连接有滑块，所述滑块的底部铰接有连杆，所述连杆的底部铰接有封板。该高密度熔融石英陶瓷高磁感硅钢炉，通过将调节电机的旋转力，转换为封板的上下移动力，无需人工手动开启或关闭，消除了安全隐患的同时，省时省力，操作简便。

通过观察冲剪边缘组织,测量冲剪边缘的显微硬度、残余应力的分布情况和磁性能的变化研究了冲剪加工对无取向硅钢50WW800边缘组织和磁性能的影响。对冲剪后硅钢片进行750℃退火,分析退火对组织和磁性能的影响。结果表明,硅钢片剪切边缘会存在0.4 mm的形变硬化层,边缘应力大,铁损增加。退火后变形减小,形变硬化层变小,残余应力大幅度减少,铁损减少。 The influence of punching process on cutting edge microstructure and magnetic properties of non-oriented silicon steel 50WW800was studied by observing microstructure and measuring microhardness near cutting edge.The residual stress distribution in the silicon steel tooth and magnetic properties were measured.Effect of annealing at 750 ℃ on microstructure and magnetic properties of the silicon steel was analyzed.The results show that a cut-edge hardening layer up to 0.4 mm is observed,residual st... 

本发明公开了一种取向硅钢产品的在线性能判级与精确分切装置和方法，使得同一个分卷上的性能分布均匀，避免分卷出现性能废品或多个性能等级的情况，提高分卷性能稳定性。提供的一种取向硅钢产品的在线性能判级与精准分切方法包括生产数据采集、铁损曲线自学习、数据存储、性能在线判级、缺陷数据采集、缺陷判级、智能分切等模块，依据修正后的磁性能全长数据，得到产品的性能判级结果，结合表面缺陷判级结果，综合确定分切位置，制定最佳分切方案。本发明可以实现取向硅钢生产过程中的性能在线判级和精准分切，得到性能均匀、表面质量好的分卷，减少分卷性能不稳定带来的损失。

本发明公开了一种去除无取向硅钢夹杂物的方法，在中间包预设脉冲电流装置，将所述脉冲电流装置的正极连接在上挡渣堰处，负极连接在下导流坝处，在钢水浇注过程中，施加电脉冲处理即可。本发明基于中间包钢水流场的研究，在中间包上挡渣堰和下导流坝之间施加脉冲电场，扩大了脉冲电场作用的钢水区域，且随着钢水流场运动，流场与脉冲电场相互作用，使得细小的SiO2和MnS夹杂物在钢水运动过程中更有效的碰撞、聚集、长大，并有充足的时间充分上浮，从而达到有效去除铸坯夹杂物，降低铸坯中S和O含量，大幅提高钢水纯净度，进而提高硅钢成品磁性能。

本实用新型涉及一种硅钢片点数机，包括底座、分拣器、收拢器和输送器。其中，分拣器通过机架倾斜连接于底座上，用于分拣硅钢片，分拣器上设置有计数器，计数器依次计数分拣器分拣的硅钢片的数量。收拢器包括托盘和振动器，托盘设于分拣器的下方，用于承装分拣器分拣的硅钢片，振动器设于底座上，与托盘上硅钢片抵接，振动器振动能够将托盘上的硅钢片收拢整齐。输送器与底座和托盘相连，输送器工作能够带动托盘移动，以将托盘上的硅钢片输送至下一工位。本实用新型采用的是分拣清点的方式，事先无需摆放整齐，将每片硅钢片进行分拣计数，有效避免了摆放不整齐造成的计数不精确的问题。