硅钢资料

针对采用含钒铁水生产无取向电工钢存在的铁水脱硫率低、转炉冶炼过程回硫量大、成品硫含量偏高的问题,通过对含钒钛铁水脱硫,减少转炉冶炼过程回硫以及RH脱硫技术等方面的研究,大幅度降低了电工钢成品硫含量。生产表明钢中w(S)=0.001 9%～0.006 9%,平均为0.004 2%;w(S)≤0.008%的比例达到了100%,且w(S)≤0.005%的比例也达到了91.43%。 In cognizance of the problems of low desulphurization rate for hot metal,large sulfur-recovery in converter as well as high sulfur content in products in producing non-orientation electrical steel with vanadium-content hot metal countermeasures have been carried out.Sulfur content in non-orientation electrical steel is decreased obviously by way of study on technologies of desulphurization for hot metal with vanadium & titanium,sulfur-recovery control in converter and desulphurization in RH ... 

冷轧无取向硅钢（/%:0.003C,2.35Si,0.22Mn,0.011P,0.002S,0.36A1,0.003 0N）经890℃或940℃3 min常化的2.3 mm热轧板冷轧成0.35 mm薄板。研究了常化温度和800⁹20℃3 min退火对该钢高频（400Hz）磁性能和抗拉强度的影响。结果表明,830⁹20℃退火时高频铁损P_10/400值最低,随退火温度增加,晶粒尺寸增大,钢的抗拉强度降低;该钢的最佳热处理工艺为常化温度940℃,退火温度830℃,其抗拉强度R_m、高频铁损P_10/400和磁感应强度J₅₀分别为565 MPa,21.5 W/kg和1.69 T。 The cold-rolled non-oriented silicon steel（/%:0.003C,2.35Si,0.22Mn,0.011P,0.002S,0.36A1,0.003 0N） is cold-rolled to 0.35 mm sheet from 2.3 mm hot-rolled plate normalized at 890 ℃ or 940℃ for 3 min.The effect of normalizing temperature and annealing process at 800 ⁹20 °C for 3 min on high frequency（400 Hz） magnetic properties and tensile strength of the steel has been tested and studied.Results show that with annealing at 830 920 ℃the high frequency iron loss value P_10... 

本实用新型公开了一种无取向硅钢绝缘涂层粘结性检测装置，涉及涂层粘结性检测技术领域，为解决现有的无取向硅钢绝缘涂层，在对绝缘涂层粘结性检测过程中，其检测结构单一，容易导致检测不准的问题。所述基座的上方设置有存料罐，所述存料罐的内壁设置有防腐涂层，所述存料罐的底部设置有声波感应器，所述声波感应器的一侧设置有液位感应器，所述液位感应器的一侧设置有自控温度调整器，所述存料罐的上方设置有控制盘，所述控制盘的表面设置有PLC操控器，所述控制盘的上方设置有电机，所述电机的一侧设置有带轮结构，所述带轮结构的一侧设置有伸缩气缸，所述伸缩气缸的一侧设置有联动结构，所述伸缩气缸的一端设置有收缩棒。

本发明涉及无取向硅钢技术领域，具体提供了一种无取向硅钢的制备方法，对再结晶率为70‑90％、平均晶粒尺寸为10‑15μm、硬度HV为140‑170的硅钢半成品在温度为T＝(772～777)+2900×W(Si)的条件下进行去应力退火，制得无取向硅钢，晶粒在去应力退火过程中均匀长大，平均晶粒尺寸80μm以上，有效降低铁损，使磁性能大幅度提高，铁损P1.5/50≤3.5W/kg，磁感B5000≥1.72T，电磁性能优异，满足客户使用要求，此外，本发明采用的硬度HV为140‑170的硅钢半成品在冲压过程中不易变形，机械加工性能优良。

采用非水溶液电解方法来提取无取向硅钢中夹杂物。通过扫描电镜(SEM)观察结果表明:无取向硅钢中主要夹杂物为六棱柱的AlN、不规则硅酸盐及球状的铁的硫化物和氧化物,其中AlN夹杂尺寸在1~5μm,数量较多,还有部分AlN的复合夹杂。进一步研究了AlN复合夹杂形成机理,采用了Thermo-Calc热力学计算软件计算出该钢样中AlN、MnS析出温度分别为1 240℃、1 200℃,而Al2O3析出温度大于1 800℃,从而为AlN复合夹杂形成机理提供了一个理论依据。 Extracting inclusions from non-oriented silicon steel in non-aqueous electrolysis is a nondestructive method to gain inclusions.Scanning electron microscopy shows that the main inclusions in non-oriented silicon steel were hexagonal AlN,which was of large quantity,irregular silicate,spherical iron sulfide and oxide.The size of AlN inclusions ranged from 1to 5μm,and there were some duplex inclusions of AlN.To further study the formation mechanism of AlN duplex inclusions,Thermo-Calc thermodynamic... 

实验室模拟薄板坯连铸连轧(TSCR)流程制造高磁感取向硅钢,借助电子背散射衍射(EBSD)技术对不同Sn含量的热轧板织构进行了研究。研究结果表明:不同Sn含量热轧板表层及次表层均为高斯织构、铜型织构及黄铜织构的混合织构,中心层为{100}面织构;Sn含量为0.1%时,热轧板表层及次表层高斯织构组分最多,取向密度最大,成品磁感最高,达到1.875 T。 Texture of grain oriented silicon steel hot rolled by thin slab casting and rolling process(TSCR) in laboratory with different Sn contents was analyzed by electron back-scattered diffraction(EBSD).The results show that the hot rolled slabs with different Sn contents have the same texture,i.e.,Goss,Copper and Brass.Specifically,the texture of core layer is {100};While the hot rolled slab with 0.10% Sn,the surface layer and subsurface layer have a sharpness Goss texture and the finished products h... 

本实用新型公开了一种硅钢炉底辊套管生产用原料破碎装置，包括外壳和固定圆板，所述外壳的端面设置有密封盖和两组电机，两组所述电机的输出端均贯穿外壳的端面，两组所述电机的输出端均卡接安装有破碎辊，所述外壳的内部转动安装有循环滤网管，两组所述破碎辊的下方安装有提示收集箱，所述外壳的下部固定贯穿安装有出料管，且出料管的侧壁安装有电磁阀，所述密封盖的端面固定贯穿安装有四组进料管，且四组所述进料管的外置端端部均固定安装有安装法兰。有益效果：本实用新型采用了循环滤网管，通过设置的循环滤网管，能够对不合格的原料颗粒进行多次破碎，为硅钢炉底辊套管生产用原料破碎装置的破碎工作带来一种保障。

本发明涉及一种取向硅钢连续高温罩式退火炉及其退火工艺，其包括梯度窑炉，所述梯度窑炉包括A1段退火炉、B段退火炉、C段退火炉、D1段退火炉、A2段退火炉和D2段退火炉；所述A1段退火炉、B段退火炉、C段退火炉、D1段退火炉、A2段退火炉和D2段退火炉依次连接；其中，A1段退火炉、B段退火炉、C段退火炉和D1段退火炉炉顶高度不同，A1段退火炉与A2段退火炉炉顶高度相同，D1段退火炉与D2段退火炉炉顶高度相同。上述在炉顶结构上根据生产工艺，采用的梯度分层次布局，使其在炉顶形成障碍，减缓气流的流通速度达到节能的目的，同时对各个工艺段炉窑内温度的均匀性有提升，并且能够提高产品的质量。

本实用新型公开了一种具有废料回收机构的硅钢板带加工用切割装置，包括箱体，所述箱体的前侧靠近顶部处设有电机，所述箱体的顶部靠近前侧处固定连接有竖板，本实用新型一种具有废料回收机构的硅钢板带加工用切割装置，电机在工作时既能带动切割刀进行切割作业，同时还能带动第一筛板和第二筛板以相邻转轴为中心上下摆动，切割的废屑从切割槽穿过达到箱体内腔，第一筛板和第二筛板对废料进行筛分处理，通过隔板设置，隔板将集料盒分为两个存储空间，隔板右侧存储穿过第一筛板和第二筛板的细料，隔板的左侧存储被第一筛板和第二筛板过滤下来的粗料，既方便操作人员对废料进行集中处理，还对废料进行了筛分处理，以此方便对废料进行分类重复利用。

本发明公开了一种控制无取向电工钢横向同板差的装置，包括热轧机、圆盘剪、冷轧机和输送辊道，圆盘剪安装在输送辊道两侧且位于热轧机和冷轧机之间，无取向电工钢在输送辊道的运输下依次经过热轧机、圆盘剪和冷轧机，设定热轧机对无取向电工钢的楔形和凸度进行控制，控制无取向电工钢的楔形在20微米内、凸度为20～45微米，冷轧机的工作辊设有倒角。冷轧机为UCM五连轧轧机，UCM五连轧轧机中1#和2#轧机工作辊的单边设有倒角，1#和2#轧机中上工作辊的操作端设有倒角，下工作辊的传动端设有倒角。倒角的深度为0.2～0.3mm，倒角在工作辊上的起始位置到工作辊端面的距离为265‑285mm。本发明还公开了一种控制无取向电工钢横向同板差的方法。

【作者】 常波； ...

根据相关的取向电工钢典型专利技术,概述了日本高磁感低铁损取向电工钢低温板坯加热、抑制剂合理调节、关键成分Mn、C、Sn和Sb调节与利用、新型退火剂和绝缘溶液的制备及细化磁畴等生产工艺最新动态和进展情况,并提出了国内企业申请取向电工钢专利时应当借鉴之处。 According to related typical patent technology for grain-oriented electrical steel sheets,the recent trends and progress situation for production process of grain-oriented electrical steel sheets with high magnetic flux density and low core loss in Japan are summarized including low temperature slab heating,suitably regulating inhibitors,adjusting and utilizing key element Mn,C,Sn and Sb,manufacturing for new annealing agent and insulating solutions,and fining magnetic domain,and some suggestion...