对低温加热工艺生产的以AlN为主抑制剂的高磁感取向硅钢高温退火过程进行中断实验,借助电子背散射衍射技术对高温退火过程中高斯晶粒的演变进行了研究.在升温过程中高斯晶粒平均尺寸先减小再增大.800℃时取向分布函数图出现高斯织构组分,但强度很弱,高斯晶粒偏离角在10°以上;900℃时高斯晶粒平均生长速率超过其他晶粒;950~1000℃时高斯晶粒异常长大,偏离角3°~6°;在1000℃之前高斯取向晶粒相比于其他晶粒没有尺寸优势. The high-temperature annealing process of high permeability grain-oriented silicon steel with AlN as an inhibitor was studied by interrupting test.The evolution of Goss texture in this process was analyzed by electron back-scattered diffraction.It is found that the Goss grain size first decreases and then increases with the rise of temperature.Goss texture appears in the orientation distribution function at 800 ℃,but the intensity is very weak and the deviation angle is more than 10°.The average... 

本发明属于变压器铁芯生产加工技术领域，具体涉及一种硅钢常化用缝合设备，包括动力机构、钢带送料机构、固定座和移动座，移动座上开有多个凹槽和设有冲压刀；固定座上开有凹腔，凹腔内滑动连接有凸模板，凸模板上设有与凹槽配合的凸块；钢带送料机构包括放料辊、设在放料辊上的钢带卷和送料部，送料部用于输送钢带并使钢带依次穿过硅钢片上的各个开口。动力机构包括动力部、传动筒、均与传动筒连通的固定筒和中间筒。本方案中，在硅钢片的叠合处开设了桥型孔，利用钢带穿过硅钢片叠合处的桥型孔，相当于利用钢带将硅钢片缝合在一起，这样设置能够较好将不同的硅钢片连接成一体。

本发明提供了一种无取向硅钢RH顶枪喷粉脱硫工艺，RH脱碳结束测温定氧，立即加入铝粒脱氧合金化、之后立即依次连续加入合金进行成分调整，合金加完后立即开始顶枪喷粉；加入铝粒的量＝铝粒理论加入量+0.2‑0.4kg/t钢；喷粉时，控制喷粉速度与钢液循环流量相匹配；本发明从真空条件下脱硫热力学和动力学角度出发对具有顶枪喷粉功能的RH脱硫工艺进行改进，提高脱硫率。

针对节能电机对无取向电工钢在磁性能方面的特殊要求,采用普通W600牌号的热轧板为原料,通过大量的现场工艺试验,研究总结出了\"超低张力\"的运行工艺、\"先快后慢\"的加热工艺、\"先湿后干\"的退火脱碳工艺、\"先缓后急\"的冷却工艺,生产出P1.5/50≤4.0 W/kg、B50≥1.70 T的冷轧电工钢产品,满足了节能电机的要求。 Based on the special requirements of no-oriented electrical steel for saving energy motor in magnetic aspects,using common W600 brand of hot rolled plate as raw material,through a large number of real tests,an ultra-low tension process,heating process which was quick at first and then slow,annealing decarburization process which was dry after the first wet,and a cooling technology of \"slow after the first urgent\" were concluded.Electrical steel product with P1.5/50≤4.0W/kg,B50≥1.70T was produced... 

本实用新型公开了一种硅钢片快速叠片装置，包括模具箱，所述模具箱的上表面开设有放置槽，放置槽的内底壁开设有滑动调节槽，滑动调节槽的内侧壁转动连接有调节丝杆，调节丝杆的外表面螺纹连接有滑动块，滑动块的上表面分别固定连接有第一电动伸缩杆和支撑板，第一电动伸缩杆的顶端固定连接有固定板，固定板的上表面开设有滑槽。该硅钢片快速叠片装置，通过设置支撑板、放置板、第二电动伸缩杆与缓冲橡胶块，能方便将硅钢片进行叠放，通过设置第一电动伸缩杆、固定板、支架板、滚动轮与复位弹簧，便于对已经放置好的硅钢片进行固定，从而使整个装置具有方便快速自动叠片的效果，降低工作人员的劳动强度，提高硅钢片叠片的效率。

本发明提供了一种无取向电工钢，以质量百分比计，其成分包括C：0.0010～0.0050％，Si≤2.5％，Al≤0.01％，Mn≤0.80％，P≤0.10％，S≤0.0070％，N≤0.0030％，其余为Fe及不可避免的杂质。本发明还提供了一种无取向电工钢的制备方法。本发明提供的一种无取向电工钢，不添加偏析或稀土等贵重元素且磁性能好、成材率高，本发明提供的无取向电工钢制备方法，工艺流程简单、生产周期短、制取成本低，且无需热轧板常化。

电工钢反复弯曲次数是电工钢性能检验的重要指标之一,直接影响到用户在使用电工钢过程的机加工性能。主要分析了试样宽度、试样张力、晶粒取向、反复弯曲设备等因素对电工钢反复弯曲试验的影响,并对各个因素的影响程度进行量化以及原因探讨,从而归纳形成各影响因素的基本规律,以便为电工钢实际生产、用户使用提供科学指导。结果表明:试样宽度增加,反复弯曲次数也会不断增加,晶粒位向对取向电工钢的反复弯曲次数影响较大,当支座顶部到拨杆底部的距离减小或拉紧力增加时,反复弯曲次数会不断减小,但当拉紧力达到60N以上时,对反复弯曲次数影响不大,试样经退火后,反复弯曲次数略有上升。 The reverse bend number is an important performance of electrical steels′capabilities,affecting the machining performance directly when the customers used.It investigated some factors,such as sample′s width,sample′s tension load,grain orientation and equipment,how to effect the reverse bend test for electrical steel,measured the influence degree,and discussed the reason,in order to form basic rules which could be guided the manufacturing and using for electrical steel.Results showed that the rev... 

组织和织构是影响无取向硅钢性能的重要因素。为改善产品性能，研究了冷轧压下率（71.7%～87.0%）对高牌号无取向硅钢组织、织构、磁性能和力学性能的影响。结果表明，随冷轧压下率的增加，退火晶粒平均尺寸先减小后增大；高斯和立方织构强度减弱，γ纤维织构增强，α纤维织构转变为较强的α^*（{h, 1, 1}〈1/h, 1, 2〉）织构，并随冷轧压下率的增加而增强，同时其峰值逐渐向{111}面移动；工频铁损P_1.5/50、高频铁损P_1.0/400和磁极化强度J₅₀₀₀同时降低，屈服强度变化不大，表面硬度逐渐增加。当冷轧压下率由84.7%增至87.0%、厚度减至0.30 mm时，高频铁损降幅是工频铁损的11倍，表面硬度增幅变大。以上研究成果对硅钢减薄后织构及组织的优化提供了很好的指导。 Microstructure and texture are critical factors on non-oriented silicon steel properties. In order to improve product properties, this paper studied the effect of cold rolling reduction rate（71.7%-87.0%） on microstructure, texture, magnetic properties and mechanical properties of high-grade non-oriented silicon steel. The results show that with the increase of cold rolling reduction rate, the average size of annealing grain decreases first and then increases. The intensity of Goss and λ fiber te... 

本发明属于钢铁冶炼技术领域，涉及一种超低铝极低硫无取向硅钢的冶炼方法，包括如下步骤：KR铁水预处理→BOF复吹转炉冶炼→RH真空炉精炼→LF精炼→连铸；采用本发明中的冶炼方法，铁水脱后硫可以适当放宽，转炉出钢温度可以适当降低，RH工序无需采用OB法升温，也无需RH顶枪喷粉或者加入合成渣脱硫，LF只需实现微调成分、调节温度、平衡炉机节奏以及适当脱硫。此种冶炼方法充分利用并发挥了各工序优势，避免了在某一工序完成所有冶炼任务，一旦发生事故，容易造成生产中断，产品质量难以保证。

本实用新型涉及一种硅钢冲压片质量筛查分拣装置，包括：第一组传送带机构，第一摄像头，设置于第一组传送带机构的上方，用于对硅钢冲压片的第一表面的残损进行检测；第一机械手机构，设置于第一组传送带机构的上方且位于所述第一摄像头的后方；翻转装置，设置第一组传送带机构的后方，用于对第一组传送带机构传输的初检良品进行翻面并将翻面后的初检良品传输给第二组传送带机构；第二组传送带机构，设置于翻转装置的后方；第二摄像头，设置于第二组传送带机构的上方，用于对硅钢冲压片的第二表面的残损进行检测；第二机械手机构，设置于第二组传送带机构的上方且位于第二摄像头的后方。本实用新型可高效的检测每一个产品的外观质量。

采用光学显微镜、X射线衍射仪等分析了宁波钢铁有限公司生产的取向硅钢不同工序下的组织及织构演变规律。结果表明:铸坯经过热轧后,沿着厚度方向组织不均匀;一次冷轧并经脱碳退火后,组织由条状纤维状变成等轴状的初次再结晶晶粒,初次再结晶平均晶粒尺寸为18.17μm,织构主要以α织构和γ织构为主;在二次冷轧后,晶粒再次被压缩,转变为纤维状,织构主要为γ织构;经过高温退火后,发生二次再结晶,晶粒异常长大,晶粒尺寸达到厘米级,织构成分为单一且锋锐的Goss织构。 The microstructure and texture evolution of oriented silicon steel produced by Ningbo Iron and Steel Co.,Ltd.were analyzed by optical microscope and X-ray diffraction.The results showed that the microstructure of the slab was inhomogenous along the thickness direction after hot rolling.After first cold rolling and decarburizing annealing,the microstructure changed from strip fibrous to equiaxed primary recrystallized grains,and the average grain size of the primary recrystallization microstructu... 

阐述了国内外高磁感取向硅钢的生产研究水平与发展趋势,包括通过提高高斯晶粒取向度、细化磁畴、涂覆张力涂层、减薄钢片厚度进一步降低铁损以及低温加热技术和短流程技术新工艺。分析高磁感取向硅钢在我国大型电力变压器上的应用情况,结果表明,发展更薄规格高磁感、低铁损、低磁致伸缩取向硅钢可为大型变压器的安全性、节能性及环保性提供有效保障。 The research progress and development trend of high magnetic induction grain-oriented silicon steel at home and abroad are summarized,including the technology of improving the Goss alignment,refining domain wall,adding stress coating,decreasing thickness of sheet,and the new technique of reducing heating temperature of casting slab and shortening operational.Moreover,the application of high magnetic induction grain-oriented silicon in power transformer is presented.Developing grain-oriented sili...