硅钢资料

利用EBSD技术对CGO硅钢热轧、中间退火、脱碳退火及二次再结晶退火组织及织构进行分析,研究了CGO硅钢各阶段加工制备过程中高斯{110}<001>晶粒的形状、尺寸及分布特点,分析了高斯取向晶粒在各工序过程中的遗传继承性特点。结果表明,CGO硅钢热轧板的次表层存在Goss取向晶粒,历经一次冷轧及中间退火后Goss取向晶粒基本消失,一次再结晶之后Goss织构仍不是主要织构,主要织构为{111}<110>和{111}<112>,说明Goss取向晶粒在二次再结晶退火前数量及尺寸上并不占优势,二次再结晶过程中Goss取向晶粒异常长大形成锋锐Goss织构。{111}<110>和{111}<112>织构组分的强度在一次冷轧中不断增加,{111}<112>织构组分的强度在二次冷轧后达到最大而{111}<110>织构组分是在初次再结晶后变强。 Grain shape,size and distribution of { 110} < 001 > Goss grains in CGO steel and the hereditary characteristics of Goss orientated grains during each processing period were investigated,based on the analysis of the microstructure and texture of the CGO silicon steel during hot rolling,intermediate annealing,decarburizing annealing and secondary recrystallization annealing by means of EBSD. The results show that Goss orientated grains exist in the subsurface of the hot rolled plate,and Goss... 

对无取向电工钢中的夹杂进行了系统的分析。利用小样电解,采取不同电解液,不同的分离方法对无取向电工钢中稳定和不稳定夹杂物进行了提取、分离和收集。利用扫描电镜(SEM)、X-射线衍射、ICP等对电解分离收集的夹杂物进行了定性和定量分析。 The inclusion analysis of the non-oriented electrical steel has been investigated.By using small sample electrolytic analysis,with different electrolytes and different separation ways,the stable inclusions and unstable inclusions was drew,separated,and collected.With utilizing the methods of SEM,X-ray and ICP,the qualitative and quantitative analysis of inclusions in the non-oriented electrical steel was obtained. 

分析了高转矩和高转速条件下高效驱动马达铁芯材料对无取向硅钢磁性能要求,讨论了无取向硅钢的高磁通密度和低铁损对电机转矩和效率的影响,介绍了国内外高磁感无取向硅钢发展情况。在生产工艺上,提高钢质纯净度,弱化夹杂物和第二相粒子对畴壁移动和再结晶晶粒长大的钉扎作用,添加微量晶界和带钢表面的偏析元素促使有利织构发展等技术可提高无取向硅钢的磁通密度。 The requirements of high efficient drive motor core materials under the conditions of high torque and high speed were analyzed.The effects of high magnetic flux density of non-oriented silicon steel on the torque and efficiency of the motor were discussed.The development of non-oriented silicon steel with high magnetic was introduced.The magnetic flux density of non-oriented silicon steel sheet can be obviously improved by some production technologies,such as purification steel,weakening the pin... 

本发明提供一种能够有效地抑制去应力退火中的渗碳、氮化的，实施了耐热型的磁畴细化处理的取向性电磁钢板。该取向性电磁钢板在一侧面具有多个槽，在所述钢板的表面至少具备镁橄榄石被膜，该多个槽是朝向横切轧制方向的方向线状地延伸且在该轧制方向隔着间隔地并列，并且，形成于所述槽的底部的所述镁橄榄石被膜厚度的平均值为0.45μm以上，并且该厚度的标准偏差σ为0.34μm以下。

【作者】 彭志华； ...

本发明公开了一种电工钢片磁致伸缩模型的建模方法，包括：测量不同旋转磁场下电工钢片磁致伸缩对称蝴蝶曲线εk；对所测量的对称蝴蝶曲线进行辨识，构建磁致伸缩蝴蝶曲线εk的Everett函数数据库；将输入的矢量磁场B波形用旋转磁场形状参数Bmax,最大值方向的方向角θ和椭圆长短轴的长度比λ拟合，得到拟合后结果；通过线性插值法在磁致伸缩Everett函数数据库中进行插值，获得拟合后结果所对应的磁致伸缩Everett函数值Ek；根据Everett函数值Ek计算得出对应的磁致伸缩蝴蝶曲线εk。应用本发明实施例，不仅可以描述矢量磁致伸缩特性，还可以通过计算估算出旋转磁场下的瞬态磁致伸缩。此外，还能够考虑磁致伸缩的各向异性特性。

测试了高强无取向电工钢的S-N曲线,并借助光学显微镜、扫描电子显微镜、透射电子显微镜分析了实验钢组织,疲劳断口形貌和位错结构。结果表明:室温条件下,频率为20Hz,应力比R为0.1,循环10~7周次时,实验钢的疲劳强度为360MPa,疲劳裂纹萌生于实验钢的次表面,裂纹萌生点附近有沿晶开裂现象,疲劳裂纹扩展区域有解理台阶与疲劳条纹,瞬间断裂区是韧性断裂,有大量韧窝。实验钢在循环应力作用下基体中产生了大量位错,并有驻留滑移带终止在晶界位置。 The S-N curve of a high strength non-oriented electrical steel was tested.The microstructure and fatigue fracture morphology and dislocation were analyzed by optical microscope,scanning electron microscope,transmission electron microscope.The results showed that:at room temperature and the frequency of 20 Hz and the stress ratio Rof 0.1,the fatigue strength of the experimental steel was 360 MPa when the cycle was 10~7 cycles.The fatigue crack initiation at the surface of the steel and the interg... 

结合工业化生产的无取向硅钢,探讨了氧硫交互作用对钢中夹杂物生成的影响。借助非水溶液电解+扫描电镜法,研究了不同O、S含量下钢中夹杂物的变化规律。结果表明,本实验条件下,提高O含量、降低S含量,会劣化热轧组织再结晶效果。在劣化效果上,O的作用大于S;低Si、无Al硅钢中,应尽可能降低O含量、适当提高S含量,以粗化钢中微细夹杂物,减少尺寸小于1.0μm的夹杂物的数量;O、S含量与钢中夹杂物数量不具有关联性。生产过程中,不仅要严格控制O、S含量,还要严格控制生产工艺,以免生成较多的有害夹杂物。 Based on the industrial production of non-oriented silicon steel,the effects of interaction between oxygen and sulfur on the formation of inclusions were discussed.The change of non-metallic inclusions in steel sheets was investigated by means of electrolysis with non-aqueous solution under different oxygen and sulfur content.Results show that the recrystallization microstructure of hot rolled sheets will be deteriorated with the increase of oxygen content and the decrease of sulfur content.The ... 

本实用新型涉及拆包装置技术领域，且公开了一种硅钢片钢卷原料拆包装置，解决了现有的硅钢片钢卷原料拆包装置不具备便捷移动功能的问题，其包括装置本体，所述装置本体的底部设有安装块，安装块顶部的两端均安装有螺纹销，安装块的两端均安装有稳定机构，安装块底部的两端均固定连接有支撑板，安装块底部的两侧均安装有连接板，两个连接板底部的两端均安装有移动轮，安装块底部的中部安装有一对气缸；使本装置能够在需要时便捷的进行移动，并且能够有效的保持连接板的稳定，同时能够有效的对插板进行固定，使置物板能够有效的保持稳定，从而能够在需要时便捷的搬运本装置，进而提高了本装置的实用性。

通过Axio Imager金相显微镜考察4.5%~7.0%硅(质量分数)对高硅钢材料组织形貌的影响,并利用Fe-6.5%Si高硅钢薄板制备方法对其进行轧制,通过DDL50电子万能试验机对阶段产品进行力学性能测试。结果证明,硅含量为5.58%的高硅钢在实验硅含量区间内存在最大延伸率及最小铸态组织晶粒尺寸。 An investigation about the influence of 4.5%-7.0% Si on microstructure and mechanical properties of high-silicon steel was presented.SEM was adopted to take an observation towards microstructure during fabrication,and DDL50electronic universal testing machine was applied into the detection of tensile curves.The results show that silicon steel with 5.58% Si provides the maximum elongation and minimum grain size as cast. 

综述了国内外大钢铁企业与研究机构采用获得抑制剂法生产低温高磁感取向硅钢的开发及应用情况,分析了以该法生产高磁感取向硅钢过程中抑制剂的控制技术,包括固有抑制剂组成方案、气态渗氮方式与工艺及高温退火工艺的制定.研究表明,固有抑制剂组成方案的设计思路大体一致,化合物抑制剂以AlN为主、硫化物为辅,同时添加少量Sn,Sb等单元素抑制剂,但组成元素含量存在一定差别;在脱碳退火后用NH3进行非平衡渗氮处理已成为气态渗氮的主要方式,但最佳方式仍未明确,具体选择需依据实际生产条件,相应脱碳及渗氮工艺的控制条件差别较大;高温退火工艺中升温制度差别不大,升温阶段退火气氛中N2含量的选择存在差别.此外,分析了抑制剂控制技术目前存在的关键问题,并指出了进一步的研究方向. The current application and exploitation on production of low-temperature high magnetic induction grain-oriented silicon steel with acquired inhibitor method at both iron and steel enterprises and research institutions in the world are reviewed. The control techniques of inhibitors, which include the composition design for inherent inhibitors, nitriding method and process, and secondary recrystallization annealing, are thoroughly analyzed and proposed. It is indicated that the design ideas for i... 

本发明是改善硅钢边缘裂边的工艺，包括：S1：对普通取向硅钢卷进行放卷、活套、清洗、加热、冷却；S2：对硅钢进行收卷，收卷张力系数为3‑9kg/mm2；S3：对硅钢卷用收紧带收紧打包，打包带张力为3‑8kg；S4：罩式炉进行炉底板检测，炉底板不平度＜2mm；S5：将收紧打包后的硅钢卷送入罩式炉内进行高温退火处理；本发明的优点：通过调整取向硅钢材料生产过程中对CA线收卷张力的控制、CA收紧带的使用与控制、罩式炉炉底板的平整度，实现1200mm以上宽度材料平均不良切边宽度≤45mm，边部裂边尺寸减少40％。有效提高了加工材料成材率，提高了纵剪材料使用率，降低了吨钢成本，减少了纵剪生产停顿，提高了效率。