硅钢资料

目前随着电工钢用户冲压设备的升级,冲压速度逐步提高,对电工钢产品的硬度和强度指标提出了更高的要求。与普通硬度级别的无取向硅钢相比,高硬度50BW600的Hv硬度提高15~20,达到125以上,同时对电磁性能指标也有较高要求。本钢通过化学成份和热轧及冷轧连退生产工艺的设计,经过小批量生产试验,满足用户要求。通过对工艺的严格控制,在大批量生产过程中,保证了产品的力学性能和电磁性的检验合格率。 Currently with upgrading of stamping equipment of silicon steel user, gradually increasing of stamping speed, propose higher demand for hardness and strength of silicon steel. Compared with conventional 50BW600, high hardness 50BW600 have higher hardness, reach greater than 125Hv. Through design of chemical composition with hot mill and annealing, production test of small quantities, stamping performance meet user request. 

对低温法生产的以AlN为主抑制剂的Hi-B取向硅钢高温退火过程进行了中断实验,借助EBSD及TEM技术对高温退火连续升温过程中织构与析出物的演变进行了研究。实验结果表明,800℃时ODF图出现高斯织构组分,但强度很弱,高斯晶粒偏离角在10°以上;950~1 000℃时高斯晶粒异常长大,偏离角3~6°;高温退火过程析出物主要有球形、规则立方形及不规则多面体形3种形貌,由于渗N的影响,Zener因子先增大再减小,并且析出物在高斯晶界前沿优先粗化。 The annealing process at high temperature of Hi-B silicon steel using low slab reheat temperature and with AlN as the inhibitor has been studied by interrupting test,and the evolution of texture and precipitates during continuous heating-up in the annealing process at high temperature was analyzed by EBSD and TEM. The results showed that Goss texture appears in ODF at 800 ℃,but the intensity of Goss texture was very weak and the deviation angle was more than10°. Goss grains grow abnormally durin... 

本发明一种焊接压力容器用碳锰硅钢钢板及其生产方法，钢板化学成分及其重量百分含量为：C：0.18‑0.26%，Si：0.18‑0.65%，Mn：0.92‑1.72%，P≤0.008%，S≤0.002%，Cu：0.30‑0.40%，Ni：0.25‑0.35%，Cr：0.25‑0.35%，Mo≤0.10%，V≤0.10%，B：0.003‑0.005%，余量为Fe及不可避免的杂质元素。本发明钢板中加入的贵合金元素含量相对较少，冶炼成本及后续的生产成本控制较低，市场潜力和竞争力很大。

本实用新型涉及硅钢二次轧制的技术领域，且公开了一种用于硅钢成品二次轧制的轧辊间距调整机构，包括安装架，所述安装架的内部设置有上、下相对的两组工作辊，两组工作辊的内部均固定连接有转轴，外侧均滑动连接有保护组件，其中下工作辊通过保护组件与安装架固定连接，上工作辊的上方固定连接有升降组件，上、下两组工作辊之间固定连接有限位组件，通过升降组件带动上工作辊的上下移动，来调整上工作辊和下工作辊之间的距离，保持二次轧制时较大的压下率，同时限位机构能有效防止因工作辊距离太近而导致的硅钢断带的情况。

一种变压器硅钢片转运吊车，属变压器生产技术领域，包括车架、驱动部和承载部，驱动部连接车架和承载部，承载部上承载硅钢片。车架包括底板、支撑单耳、后耳片，底板前端两侧向前上方各延伸一个支撑单耳，支撑单耳连接驱动部，底板的中后部两侧各具有一个后耳片，后耳片也连接驱动部。驱动部包括连杆、底双耳、支撑双耳、轴座、转轴和液压缸，连杆具有一对，连杆下端具有底双耳，连杆的中下部具有支撑双耳，连杆的顶部具有轴座，底双耳铰接在支撑单耳上，转轴安装在两个连杆顶部的轴座上，液压缸的两端分别连接在后耳片和支撑双耳上。承载部包括托盘、侧部耳片、拉杆、下双耳和上挂耳，托盘两侧各具有一对侧部耳片，拉杆呈倒Y字形结构。

磁性能指标是硅钢产品最关键的质量指标之一，但是目前磁性能判定100%依赖于样品的离线实验室检测结果，生产线配置的在线检测仪的测量结果由于精度问题，不宜直接用于成品牌号判级。本文在现有硅钢产品质量管控体系基础上，利用大数据技术对生产数据进行分析与建模，构建不同磁性能指标在线检测模型，并在现有信息系统上完成模型库的集成部署，实现硅钢产品全长、多指标磁性能结果的拟合数据输出，支撑取样优化、精准分切、辅助综合判定等功能应用，进一步优化硅钢产品质量管控体系。 The magnetic performance index of silicon steel products is one of the most critical quality indexes.However,at present,100%determination of magnetic performance depends on the offline laboratory test results of samples,and the measurement results of the online detector configured in the production line cannot be applied in practice due to the accuracy problem.Based on the existing quality control system of silicon steel products,big data technology was used to analyze and model the production d... 

【作者】 李波； 杨晓江； ...

【作者】 党其； ...

采用固溶强化、细晶强化和位错强化方法,模拟TSCR流程试开发高强度无取向电工钢,试开发钢的主要合金成分为3%Si、0.83%Al和2.99%Mn。分析热轧、常化、退火后的钢板组织,并针对不同的成品板组织,详尽地分析了相应的力学性能和磁性能。试验电工钢平均晶粒直径为12.37μm时,R p0.2为530 MPa,R m为618 MPa;当退火制度为700℃×4 min,成品组织完全为未再结晶的回复组织时,R p0.2为853.5 MPa,R m为895.5 MPa。该成分的电工钢P15/50或P10/400最小时,对应的平均晶粒直径都大于59.67μm;P10/800或P10/1000最小时,对应的平均晶粒直径都处于12.37~59.67μm尺寸区间。 TSCR was simulated to develop high-strength non-oriented electrical steel with 3% of Si,0.83% of Al and 2.99% of Mn by solution strengthening,grain refinement strengthening and dislocation strengthening.The microstructures of hot rolled plates,normalized plates and annealed plates were analyzed.Furthermore,the mechanical properties and magnetic properties of products with different microstructures were detailedly studied.As the average grain diameter of the steel was 12.37 μm,the yield strength ... 

本发明公开了一种降低无取向硅钢W800头部窄尺的控制方法，步骤1、筛选板坯长度，并使板坯进入加热炉后头部均朝向轧机方向；步骤2、控制板坯头部温差小于10℃；步骤3、固定粗轧到精轧区间内的轧机机架轧制速度；步骤4、固定相变机架，使板坯的奥氏体‑铁素体相变发生在F2和F3机架中；步骤5、调整精轧机架间的负荷分配，降低F2和F3机架的压下量；步骤6、调整活套张力，降低F2和F3机架的活套单位张力补偿；步骤7、降低模型AGC增益，降低F2和F3机架的AGC补偿的辊缝波动量。本发明通过控制固定相变机架、优化相变机架的负荷分配、AGC补偿系数、活套张力等，使秒流量保持平衡，减少无取向硅钢W800头部窄尺。

本发明涉及一种硅钢片纵剪边料收卷装置，包括：用于将收卷装置固定于地面的机架底座，机架底座一端设置固定支架，固定支架上安装电动定尺收料盘；在机架底座上设置电动可移动支架，电动可移动支架在机架底座的长方向上相对固定支架移动，电动可移动支架上安装电动可调收料盘；电动可移动支架、电动定尺收料盘、电动可调收料盘与PLC控制系统连接，PLC控制系统用于控制电动可移动支架的移动距离、以及控制电动定尺收料盘和电动可调收料盘的收料速度。本发明还涉及一种硅钢片纵剪边料收卷方法。将本发明的收卷装置安装在硅钢片滚剪线切刀后面的输送平台下部，卧式布局，不占用外部空间，和滚剪线无缝集成在一起，自动完成硅钢片纵剪边料收卷工作。

本实用新型公开了一种硅钢片二次搭接夹具，包括底座、位于底座顶部的调节板以及位于调节板顶部一端的固定杆，所述底座包括设置在底座内部顶端中间位置处的活动槽。本实用新型通过连接块将第一夹钳与第二液压缸的输出端相连接，通过第一夹钳和第二夹钳对硅钢片进行固定，将焊条焊接在一组硅钢片上，伺服电机带动调节杆发生转动，调节杆外侧的外螺纹和活动块内部的螺纹孔相互配合，可使活动块在活动槽内部发生活动，通过活动块带动调节板发生前后移动，从而使对硅钢片进行前后一端，通过滑轨使调节板的移动更加稳定，使两组硅钢片相对齐，通过固定块使第一液压缸带动调节架左右移动，使焊条与两组硅钢片紧密接触，实现二次搭接。