采用ZMLMC超高梯度定向凝固装置,研究了5种凝固速率(10、35、80、150和450μm/s)对定向凝固50W600无取向硅钢的固液界面稳定性转变规律和一次、二次枝晶间距的影响。研究结果表明,在特定的温度梯度下,随着凝固速率的增加,定向凝固的固液界面由胞状晶转变为胞状枝晶,再转变为细小的树枝晶。随着凝固速率的增加,定向凝固组织的枝晶形貌逐渐细化,一次和二次枝晶间距逐渐减小,且与冷却速率之间都符合指数关系:λ1=151.73×(G L·R)-0.31,λ2=22.07×(G L·R)-0.44。当冷却速率达到4.275℃/s时,一次、二次枝晶间距分别为112μm、14.1μm。 Under the conditions of certain temperature gradient and different solidification rate,the directional solidification experiment of non-oriented electrical steel 50W600 was carried out.The microstructure of 50W600 steel was also analyzed in different solidification rate.The result shows that the solid/liquid interface of the steel undergoes an evolution from cellular,cellular dendrite and finally to fine dendrite morphologies.The dendrite refines gradually and the distance between dendrites decr... 

对3层高硅电工钢复合板铸坯进行热轧及温轧变形加工后，采用正火、退火两种热处理方式处理，并观察轧制过程中产生的裂纹，研究不同状态下复合板的磁性能。对不同状态下的试样进行扩散退火处理，研究复合板中裂纹变化及其对磁性能的影响。结果表明：不同热处理工艺下合金内部的裂纹尺寸差异明显，裂纹尺寸对复合板的磁性能影响显著，相对于深裂纹，其他因素的影响较小；温轧变形加工后，复合板内层出现有序组织，但该有序组织在合金存在深裂纹的前提下并不能从本质上提高合金的磁性能；扩散退火工艺可以消除复合板内部的浅裂纹及微裂纹，但不能消除尺寸较大的裂纹，故而不能显著提高存在深裂纹的复合板的磁性能。 After hot rolling and warm rolling deformation processing of casting billet for three-layer high silicon electrical steel composite plate, it was normalized and annealed for heat treatment. Then, the cracks produced during the rolling process were observed, and the magnetic properties of composite plate in different states were also investigated. Furthermore, the samples in different states were subjected to diffusion annealing treatment, and the changes of crack in composite plate and their eff... 

本发明涉及一种在连续的退火和覆层线(1)中对非晶粒取向的电工钢带(2)进行再结晶退火的方法，其中电工钢带(2)在感应炉(5)中以至少80K/s的加热速率加热到至少680℃的温度，并且然后在可能的第二连续炉(8)中以最大20K/s的加热速率加热到至少820℃的温度，其中在感应炉(5)上游将电工钢带(2)首先经由第一连续炉(3)以至多60K/s的加热速率加热到至少300℃的温度。

本发明公开了一种精确控制高磁感取向硅钢连铸坯Als成分的方法，本发明涉及的主要是高磁感取向硅钢生产过程的连铸工艺环节，负责将高温液态钢水浇注凝固成固态连铸坯。通过采取控制大包下渣、加入足量中间包覆盖剂、采用长水口+石墨垫圈+氩封保护浇注等方法，将精炼结束到连铸过程Als降低量稳定控制在0.0030～0.0045%范围内，稳定了二次氧化程度。通过采用本方法生产的连铸坯Als含量稳定在0.0245～0.0275%范围内，为提高取向硅钢产品的磁感和铁损性能奠定坚实的基础保障。

电工钢反复弯曲次数是电工钢性能检验的重要指标之一,直接影响到用户在使用电工钢过程的机加工性能。主要分析了试样宽度、试样张力、晶粒取向、反复弯曲设备等因素对电工钢反复弯曲试验的影响,并对各个因素的影响程度进行量化以及原因探讨,从而归纳形成各影响因素的基本规律,以便为电工钢实际生产、用户使用提供科学指导。结果表明:试样宽度增加,反复弯曲次数也会不断增加,晶粒位向对取向电工钢的反复弯曲次数影响较大,当支座顶部到拨杆底部的距离减小或拉紧力增加时,反复弯曲次数会不断减小,但当拉紧力达到60N以上时,对反复弯曲次数影响不大,试样经退火后,反复弯曲次数略有上升。 The reverse bend number is an important performance of electrical steels′capabilities,affecting the machining performance directly when the customers used.It investigated some factors,such as sample′s width,sample′s tension load,grain orientation and equipment,how to effect the reverse bend test for electrical steel,measured the influence degree,and discussed the reason,in order to form basic rules which could be guided the manufacturing and using for electrical steel.Results showed that the rev... 

根据相关的取向电工钢典型专利技术,概述了日本高磁感低铁损取向电工钢低温板坯加热、抑制剂合理调节、关键成分Mn、C、Sn和Sb调节与利用、新型退火剂和绝缘溶液的制备及细化磁畴等生产工艺最新动态和进展情况,并提出了国内企业申请取向电工钢专利时应当借鉴之处。 According to related typical patent technology for grain-oriented electrical steel sheets,the recent trends and progress situation for production process of grain-oriented electrical steel sheets with high magnetic flux density and low core loss in Japan are summarized including low temperature slab heating,suitably regulating inhibitors,adjusting and utilizing key element Mn,C,Sn and Sb,manufacturing for new annealing agent and insulating solutions,and fining magnetic domain,and some suggestion... 

本发明公开了非晶与硅钢卷绕机用恒张力一体式纠偏机构，包括放卷结构和收卷结构，所述放卷结构和收卷结构间依次连接张力装置和纠偏装置，所述纠偏装置下方设置有纠偏张力控制系统；所述纠偏张力控制系统包括放卷张力程序模块、速度张力闭环反馈程序模块和纠偏定位程序模块；所述放卷张力程序模块与张力装置电信号连接；所述速度张力闭环反馈程序模块与放卷结构和收卷结构电信号连接；所述纠偏定位程序模块与纠偏装置电信号连接。通过集纠偏控制与张力控制于一体，并设置了纠偏张力控制系统，提高了卷绕精度，降低了设备制造成本，并有效解决了设备占用空间较大的问题。

本发明公开了一种控制无取向硅钢边部黑线的生产方法，涉及硅钢轧制工艺领域。本发明提供的方法缩小加热区的装钢间距，降低粗轧冷却水量，并减小R1第一道次侧压量，增大R2末道次立辊侧压量，调整精轧区侧导板和卷取区侧导板的开口度，减少或消无取向硅钢边部黑线。本发明提供的生产方法控制了热轧卷边部翘皮黑线问题，将热轧卷出现边部黑线的概率由之前的60%以上降低至现在的3%以下，热轧及冷轧卷的表面质量得到了明显提升，酸洗裁剪量减小，成材率明显提升，冷轧过程的轧制稳定性也明显提升。

本实用新型公开了一种硅钢炉底辊套管生产用沥青浸煮装置，包括机身底座和支撑腿,所述机身底座顶部表面中间位置固定安装有浸煮机构，所述浸煮机构两侧内部中间位置固定安装有电热丝。本实用新型通过，采用了生产框、搅拌桨，在实际使用过程中，代加工工件可以放置到生产框内部，然后进行沥青浸煮作业，通过搅拌桨可以对沥青进行持续不断的搅拌，使得沥青与工件的接触面积增大，提高浸煮效果，当浸煮完成之后，通过液压缸将生产框向上移动，使得生产框两侧卡接在电动伸缩套内部，然后通过振动电机运转带动生产框进行左右震动，使得工件表面残留的沥青得以掉落，提高工件表面的整洁度，便于后续使用，具有浸煮效果好、沥青无残留的优点。

【作者】 刘彤； ...

本发明给出了一种用于将由电工钢带(3)或电工板材制成的板件(4)叠组成板叠(2)的方法，板叠分别具有在相对于预定的目标叠组高度(hs)的公差范围(Δh)内的叠组高度(hp)。

本申请实施例公开了一种硅钢铁芯生产用多功能卷绕机，包括平台板，所述平台板底部的左侧固定连接有旋转电机，所述旋转电机的输出端固定连接有旋转杆，所述旋转杆的顶部固定连接有转盘，所述转盘的顶部固定连接有铁芯型模，所述铁芯型模的外表面活动连接有限定座，所述平台板顶部中心的左侧固定连接有第一U型板。第一弹簧和升降板的配合使用，可以让使用者下压升降板，使得升降板带动安装杆进行向下移动，继而使得安装杆脱离第二U型板所开设的轴槽，继而使得安装杆的顶部存在一定的间隙，进而可以通过间隙将带盘插入在安装杆上，该方式装卸起来简单快捷，可以有效的减少装卸带盘所消耗的时间，从而提高了设备的工作效率。