硅钢资料

在实验室试制了TSCR流程的低碳低硅无取向硅钢,研究了在850～1050℃不同温度常化对冷轧量0.5mm厚钢板再经950℃×7min退火后的组织、织构和磁性能的影响。结果表明:随常化温度的升高,使热轧板晶粒尺寸增大,晶界更清晰,组织均匀性更好;由于第二相AlN和MnS析出物尺寸比较大,使冷轧退火后钢板晶粒也随常化温度升高呈单调增大趋势;γ有利织构和{111}、{112}不利织构与常化温度升高同时增强,但前者增强更多;冷轧板退火后铁损随常化温度升高呈单调下降,磁感呈单调上升趋势。 The low-carbon and low-silicon non-oriented silicon steel was prepared by thin slab casting and rolling(TSCR) in lab.The effect of normalizing at different temperatures in 850-1 050℃on microstructure, texture and magnetic properties of 0.5 mm cold-rolled sheets after annealing at 950℃for 7 min was researched. The results show that with increasing the normalizing temperature,the grain size of hot-rolled sheets increased,the grain boundaries were more clear and the rnicrostructure uniformity was b... 

本实用新型公开了一种取向硅钢二轧料氧化镁冷涂装置，包括主体，所述主体的中部安装有架体，且架体的右侧安装有冷涂机构，所述冷涂机构的右端一侧安装有液压气缸，且液压气缸的内壁连接有连接杆，所述架体的前后两端安装有调节架机构，所述调节架机构的表面安装有防护块，且防护块的内壁安装有橡皮套。该取向硅钢二轧料氧化镁冷涂装置设置有冷涂机构，且箱体通过安装有单独喷管和连接喷头，便于使用者两者兼合使用，可使用单独喷管也可连接喷头，使用者可根据自己使用的需求，对单独喷管和连接喷头进行针对性使用，单独喷管通过安装扣将连接喷头进行拼接使用，箱体通过旋转轴与支撑架的旋转，便于将箱体进行角度旋转。

文章以国内某公司硅钢厂连续退火机组1号辐射管加热段为研究对象,分析炉内传热机理,建立并开发了辐射管加热段的传热模型。采用生产实际数据对模型进行了验证,以总燃料消耗量最小为目标,得出该炉段长度方向上燃料的最佳分配机制。所得结论为该公司连续退火机组节能控制提供理论依据。 Taking the radiant tube heating section of No.1 continuous annealing unit in a silicon steel plant of a domestic company as the research object, the heat transfer mechanism in the furnace is analyzed, and the heat transfer model of the radiant tube heating section is established and developed. The model is verified by the actual production data. Aiming at the minimum total fuel consumption, the optimal fuel distribution mechanism in the length direction of the furnace section is obtained. The co... 

本发明属于硅钢制备技术领域，具体涉及一种无底层取向硅钢的制备方法。其中，所述脱碳退火的过程中，带钢表层的氧化膜厚度为1.5～2.5μm；所述氧化膜中Si元素和Fe元素的原子重量比满足：Si/(Si+Fe)≥0.76；所述高温退火的过程中，冷却段依次包括：在温度为1200～500℃时，罩内冷却；其中，保护气体为包括有氮气和氢气的混合气体，所述混合气体中氢气的体积百分比＞3％；在温度为500～200℃时，罩内冷却；其中，保护气体为氮气；在温度＜200℃时，揭开内罩进行空气冷却。本发明提供的无底层取向硅钢的制备方法中，通过控制带钢在脱碳退火阶段的氧化膜厚度以及高温退火的冷却段等一些工艺，从而得到了表面光洁化好、表面均质化好、成材率高、磁性能优良的无底层取向硅钢。

本发明涉及一种用于控制硅钢毛刺状厚度波动的工艺，包括如下步骤；将连铸坯送入加热炉中进行加热，连铸坯入炉温度为400‑680℃，连铸坯在炉时间为185‑220min；将加热后的连铸坯进行热轧，轧辊偏心量为0‑0.025mm，将热轧后的带钢进行卷取；将卷取后的带钢酸洗后进行冷轧，冷轧操作模式由多次阶段升降速模式调整为一次性升降速模式，且在一次性升降速阶段将MN‑AGC增益系数增大；将冷轧后的带钢进行卷取，退火后得到硅钢片成品。本发明所公开的用于控制硅钢毛刺状厚度波动的工艺，该工艺对加热、热轧、卷取及冷轧各工序进行优化协调，能够有效解决硅钢毛刺状厚度波动的问题，实现无取向硅钢全长厚度控制精度的提升，而且无需进行设备和系统改造，容易实现，易于推广。

本实用新型公开了一种硅钢片横剪线裁切设备，包括：本体，所述本体包括工作台、挡屑罩和裁切装置，所述挡屑罩内水平固定安装有横杆，所述裁切装置与横杆下表面滑动连接；两个定位机构，所述定位机构包括第一螺纹杆、第一滑块和压板，所述挡屑罩内壁开设有两个安装槽，两根所述第一螺纹杆分别转动安装在两个安装槽内，两个所述第一滑块分别螺纹套设在两根第一螺纹杆上，两个所述压板分别与两个第一滑块远离安装槽槽底的一端水平固定链接；两个驱动机构，所述驱动机构用于控制第一螺纹杆发生转动。通过驱动装置控制定位机构中压板在垂直方向上的位置便可快速实现对硅钢片的定位工作和解除工作，方便快捷，提高了裁切工作的效率。

采用扫描电镜、原子力显微镜研究了铬酸镁半无机绝缘涂层的微观结构。结果表明,涂层厚度为数微米,涂层中的有机树脂乳液颗粒均匀分布在无机涂层的表面,从而保证了涂层具有良好的冲片性能。采用极化曲线研究了涂层的耐蚀性能,发现铬酸镁与铬酸锌绝缘涂层的耐蚀性能相当。 In this paper,the microstructure and anti-corrosion property of magnesium chromate coating on non-oriented silicon steel were studied.The microstructure was observed by SEM and AFM.The anti-corrosion properties were evaluated by polarization curves.The results show that the thickness of coating is several microns and the polymer particles were scattered on the surface of inorganic coating,which is the guarantee for lamination property.The corrosion resistance of the magnesium chromate film was e... 

本发明公开了一种提高薄板坯连铸生产高铝无取向硅钢可浇性的方法，在保证生产顺行、质量稳定的基础上，能使高铝无取向硅钢连浇炉数由10炉提高至16炉，在提高小时产量、降低生产成本方面效果显著。

采用双辊薄带连铸工艺制备了厚度为2.4mm的3.98%Si-0.71%Al无取向硅钢带,经常化、冷轧、不同温度退火后,对其显微组织、析出物、织构和磁性能进行了检测分析。结果表明:随着退火温度的提高,退火板晶粒尺寸增大,组织均匀性提高;退火板析出物主要是AlN和MnS与AlN复合析出物,尺寸较粗大,达0.5~2.5μm;退火板织构沿厚度方向变化明显,表层和1/2层存在较强的{100}织构,1/2层还存在较强的{111}织构,1/4层主要是{112}织构;随退火温度的升高相应的铁损和磁感应强度均降低。 Using twin roll thin strip continuous casting technique,the 3.98%Si-0.71%Al no-oriented silicon steel strip in thickness of 2.4mm was produced.The microstructure,precipitates,texture,and magnetic properties of the sheet after normalizing,cold rolling and annealing at different temperatures were studied.The results show that with annealing temperature increase,the grain size and uniformity of annealed sheet increased.The main precipitates in coarse size of 0.5-2.5μm in annealed sheet were AlN and... 

结合工业化生产的50A1300牌号无取向硅钢,分析了化学成分、RH精炼脱氧方式、板坯装炉温度以及热轧平整工艺等对磁性能的影响,探讨成品钢磁性能的改善。结果表明,采取改善后,50A1300牌号无取向硅钢的磁性能得到明显改善。2012年,该钢种平均铁损、磁感应强度分别达到5.26 W/kg、1.762 T,能够较好地满足用户市场需求及同行对标需要。 Based on the industrial manufacture of 50A1300 grade non-oriented silicon steel sheets,effects of chemical composition,deoxidization method in RH vacuum refining,charging temperature of steel slabs,hot rolling and flattening progress on magnetic properties are analyzed.The optimization methods of magnetic properties of steels are discussed. Results show that the magnetic properties are obviously improved by the adopted measures above. In 2012,the average core loss and the magnetic induction of 5... 

6.5%Si电工钢是一种优异的软磁材料,织构对其磁性能影响很大。利用温轧工艺对6.5%Si电工钢热轧板进行不同压下率轧制,研究了温轧板织构随压下率的变化规律。实验结果显示,随着压下率的增大,{100}〈110〉、{110}〈100〉和γ纤维织构在薄板表层中的强度先增强后减弱,当压下率达到75%时,沿板厚方向形成3个组织区域:表层细晶粒区({110}〈100〉取向为主)、过渡层({111}〈110〉和{111}〈112〉变形晶粒区)和中心层(以拉长的γ纤维织构和{100}〈110〉取向晶粒为主),这种组织和织构不均性对后期织构的发展有重大影响。 6.5wt% Si electric steel has excellent soft magnetic properties,on which texture play important role.In this experiment,warm rolling technique was employed to investigate the effect of rolling reduction on texture.It was found that the density of {100}〈110〉,{110}〈100〉 and γ-fiber textures first increased and then decreased with increasing of the rolling reduction.At 75% reduction,the microstructure along the thickness of the sheet formed three zones,containing surface layer with {110}〈100〉 orien... 

本发明涉及一种超纯净无取向冷轧硅钢中非金属夹杂物形貌的原位观察方法，包括如下步骤：制备无取向冷轧硅钢样品，将待测试面用打磨至1000#，使样品表面平整光滑，并进行机械抛光和表面清洗。对处理好的样品在电化学工作站上进行电化学腐蚀，电解液为：1~8wt%氯化物MCl溶液，余量为去离子水，通入CO2气体至饱和，加入适量NaHCO3和三乙醇胺作为稳定剂调节pH值将其稳定在6.0~6.5之间。电化学设定参数：开路：0.5~2h，动电位极化测试：扫描速率:0.1mV/S~1.0mV/S，测试区间：VS.SCE‑0.8V~0.2V，测试温度为：10~25℃。取不同区间内做完电化学腐蚀的样品用去离子水冲洗，吹干。通过扫描电子显微镜+能谱仪对非金属夹杂物的形貌进行原位观察和成分分析。