硅钢资料

本发明公开了一种高热导率耐腐蚀电工钢自粘结涂料及制备方法，本发明的自粘结涂料包括以下质量百分比的组分：双酚A型环氧树脂25％～35％、酚醛环氧树脂4％～8％、异辛基磷酸酯0.2％～0.5％、丙二醇甲醚5％～10％、乳化剂5％～8％、二甲氨基乙氧基三恶硼杂八环1％～3％、铵封闭路易斯酸盐0.5％～2％、氮化硼纤维3％～12％、氧化铝纤维0.4％～1.0％、研磨助剂0.2％～0.3％、余量为纯水。该自粘结涂料一次固化后形成的活化态自粘结涂层显著提高对电工钢基材的耐腐蚀性，该自粘结涂层具有良好的热导率，一次固化与二次热压固化工艺条件操作难度显著降低。本发明的自粘结涂料制备方法操作简单，实施可行性高。

【作者】 宋波； 朱一知； ...

采用拉伸试验和显微组织观测的方法确定了GTN损伤模型中的9个损伤参数,运用GTN损伤模型对冷轧硅钢薄板边部缺陷的扩展及边裂的产生进行了有限元模拟,并与预置缺口的钢板轧制试验进行对比。结果表明:轧制过程中边部缺陷是造成钢板边部裂纹萌生和扩展的一个重要原因,GTN损伤模型可用来预测含边部缺陷硅钢薄板在冷轧过程中边裂的产生;预测结果与试验结果基本一致。 The crack initiation and propagation of silicon steel strip with edge defect during cold rolling process was studied by using GTN damage model in this paper.Nine damage parameters in GTN model were identified by tensile testing and microstructure observing,and then the FE simulation of edge defect evolution of silicon steel strip during rolling process was conducted on the base of GTN damage model,and then the results were compared with rolling experimental results.The results show that the edge... 

本发明提供了一种可修饰取向硅钢表面的无机绝缘涂料及其制备和使用方法，该涂料按照重量份计，包括：大颗粒硅溶胶5‑35份、磷酸二氢铝10‑30份、小颗粒硅溶胶5‑35份、铬酐0.5‑5份、增稠剂1‑10份、钛白粉0.01‑0.5份及去离子水0‑78.49份；该涂料的固含量为20‑40％。该涂料制备方法为：将增稠剂、去离子水、磷酸二氢铝、大颗粒硅溶胶、小颗粒硅溶胶，铬酐和钛白粉依次加入反应器中搅拌均匀，室温静置0.5‑1h。该涂料在使用时，需先将取向硅钢片进行清洁干燥预处理后，再将涂料辊涂在取向硅钢片上固化烧结并控制膜厚。本发明所提供的涂料制成的涂层表面平整均匀、颜色光亮，具有优良的附着性、耐蚀性、热稳定性和绝缘性，并且能修饰因硅酸镁底层质量不良引起的露晶亮点缺陷。

本实用新型涉及硅钢片加工领域，且公开了一种用于硅钢片钢卷制造的风冷装置，解决了目前市场上的用于硅钢片钢卷制造的风冷装置工作效率低下，风冷效果不佳的问题，其包括风冷箱，所述风冷箱两侧的下部分别开设有输入口和输出口，风冷箱的内部通过输入口和输出口活动连接有硅钢片本体，风冷箱内腔的顶部固定连接有制冷框，制冷框内腔的两侧之间安装有制冷环形管，制冷框内腔的顶部通过支架固定连接有吹风罩，风冷箱底部的两侧均安装有稳定架，该用于硅钢片钢卷制造的风冷装置，结构设计巧妙、降温迅速、操作便捷，通过制冷框与集风架进行对硅钢片本体进行双重风冷处理，大大提高了整个装置的风冷效果和工作效率，并且人工维护少、生产成本低。

本文中简要介绍了武汉钢铁有限公司采用薄板坯连铸连轧CSP(compact strip production, CSP)工艺生产中低牌号无取向硅钢的实践情况.CSP工艺生产的硅钢具有成品磁性均匀、板形好的优势，但是在利用该技术生产中低牌号无取向硅钢时，常存在成品板表面瓦楞状缺陷严重、连铸生产效率低等问题.通过优化炼钢成分、热轧等相关工艺，可消除热轧板厚度方向中心的粗大形变组织，从源头上避免了粗大{100}<011>纤维组织的出现，消除了瓦楞状缺陷；通过提升冶炼效率和控制钢中夹杂物总量，可优化隧道炉的加热温度与在炉时间，大幅度提升了连铸生产效率，实现了中低牌号无取向硅钢的批量稳定制造，使CSP产线成为中低牌号无取向硅钢热轧板原料的主要供给生产线.如何进一步提升钢水纯洁度、提高连铸生产效率、降低生产成本，以及挖掘该产线生产薄带钢的技术优点，是未来工作的重点. This paper briefly introduces the practice of producing medium and low grade non oriented silicon steel(NGO) with CSP(compact strip production, CSP)technology in Wuhan Iron and Steel Co., Ltd.. This technology has the inherent advantages of uniform magnetic properties and good shape for silicon steel finished strip. However, in the actual production process, there are serious corrugated defects on the surface of silicon steel finished strip, and production efficiency of continuous casting is low... 

本发明提供虽然为薄壁但磁特性优异的方向性电磁钢板的制造方法。本发明的一个方案提供一种方向性电磁钢板的制造方法，其包括热轧工序、任选的热轧板退火工序、酸洗工序、冷轧工序、一次再结晶退火工序、成品退火工序和平坦化退火工序，在酸洗工序中，使用包含0.0001g/L～5.00g/L的Cu的酸洗溶液，冷轧钢板的板厚为0.15mm～0.23mm，一次再结晶退火工序的升温工序中的30℃～400℃的温度区域的平均升温速度超过50℃/秒且为1000℃/秒以下。

采用硅钢自动测量装置及X射线衍射仪检测出样品在实验前后的磁性能参数和织构强度.结果表明:较低的电压、9 Hz、较长的处理时间以及退火温度为650℃有利于增高铁损降低比例;较低的电压、较高的频率以及退火温度为650℃有利于增加磁感应强度增高比例.最佳的提高磁性能的实验参数是:频率为9 Hz,电压为500 V,处理时间为6 min,退火温度为650℃.通过织构分析可以验证:取向硅钢磁感应强度的变化取决于{110}<001>晶粒取向度值,而{110}<001>取向度值可看成是一个反映总体平均偏离角大小情况的综合值. An automatic measurement system for silicon steel and an X-ray diffraction meter were used for measuring the magnetic property parameters and texture of ex-processed samples and processed samples.It is shown that under the condition of a lower voltage,9Hz,a longer processed time and an annealing temperature of 650℃,the decrease rate of iron loss can be increased;a lower voltage,a higher frequency and an annealing temperature of 650℃ are in favor of improving the increase rate of magnetic inducti... 

本发明公开了硅钢片均衡堆垛分料系统，包括分料机构和接料机构，分料机构包括料架，料架上具有托板，托板两侧设有第一滚筒架，第一滚筒架顶部设有分料结构；分料结构可实现上下、水平移动；分料结构包括支撑架，支撑架上设有倒吸件；倒吸件包括磁块槽和挡料板，磁块槽设于挡料板上方，磁块槽底部设有磁块，磁块槽上方设有压料胶条，磁块槽和压料胶条可上下移动，接料机构的接料底座可平移，剪力臂架可升降，以改变第二滚筒架高度和水平位置。本发明的优点在于：通过分料结构的倒吸件吸附硅钢片，再将数个硅钢片同时放置于托板侧边数排滚筒上的放置板上，可实现多柱硅钢片的均衡堆垛，通过接料机构可进行多柱硅钢片的同时稳定出料，转运效率高。

本实用新型公开了一种用于变压器硅钢片加工的剪切装置，属于变压器生产设备技术领域，包括工作台，所述工作台的侧壁处固接有侧板，侧板的侧壁上固接有固定板一和固定板二，固定板一上安装有电机，电机的输出轴与旋转轴一的一端固接，旋转轴一靠近电机一端的外侧壁上固接有不完全齿轮一，不完全齿轮一与柱齿轮一相啮合，柱齿轮一固接在旋转轴二的一端处；可进行持续剪切工作，切刀旋转进行剪切工作，需要的剪切力更小，同时不易容易损伤切刀和硅钢片，自动化程度高，能满足硅钢片的大批量生产需求，在对硅钢片进行传送时，受到挡板的两侧限位作用，从而确保硅钢片不易发生倾斜，确保硅钢片的成品质量。

本发明公开了一种硅钢轧制系统，包括：轧机组，所述轧机组包括M架轧机，用于轧制硅钢，所述M架轧机的前N架轧机的轧辊为高速钢轧辊，其中，M、N为正整数；硅钢检测装置，位于所述轧机组最后一架轧机的出口处，用于对出口硅钢的参数信息进行检测；控制器，与所述硅钢检测装置通信连接，用于在所述参数信息不满足预设参数条件时，控制所述轧机组停止工作；磨床，用于在所述轧机组停止工作后，对所述N架轧机中的每架轧机进行辊形精度检测，对不满足预设辊形精度范围的轧辊进行磨削。

本实用新型公开了一种高精度硅钢片加工用多向定位组件，包括底板、安装板、橡胶轮组一和橡胶轮组二，所述底板上端两侧对称设置有U型的所述安装板，所述安装板内底端中部安装有安装架二，所述安装架二上安装有所述橡胶轮组二。有益效果在于：本实用新型通过螺杆、调节套、安装架一、安装架二、橡胶轮组一、橡胶轮组二、弹簧以及连接柱的设计，能够实现高精度硅钢片在加工时的有效夹紧定位，避免了高精度硅钢片在加工时的晃动滑移，提高了高精度硅钢片的加工质量，通过电推杆、滑块以及滑槽的设计，能够根据高精度硅钢片的尺寸来调节安装板之间的间距，以满足也不同尺寸高精度硅钢片的加工需求，提高了定位组件使用的灵活性。