硅钢高温退火环形炉炉壳制作与安装精度要求较高,施工时通过对壳体原材料矫正、炉壳板拼焊、下料切割、型钢骨架组装及焊接、骨架及炉壳板矫正、骨架与炉壳板组装及焊接、炉壳矫正、零配件装置、定位钻孔、报验检查、出厂、内侧板安装、外侧板安装、顶板安装等环节的工艺技术控制,能保质高效地完成硅钢高温退火环形炉炉壳制作与安装,为以后同类工程的施工提供可借鉴经验。 The required precision of manufacture and installation technique of the silicon steel high temperature annealing annular-furnace shell is high.During construction , manufacture and installation of the silicon steel high temperature annealing annular-furnace shell could be finished high efficiently through correcting the raw materials of shell , furnace shell plate welding , material cutting , steel frame assembly and welding , skeleton and shell plate correction , skeleton and furnace shell asse... 

介绍了国内、外电工钢极薄带的生产现状及市场应用的情况,以及典型生产企业的生产规模、产品性能和应用领域,指出扩大高牌号无取向电工钢生产、提高产品质量是目前电工钢发展的迫切要求。 The production situation and market application of ultra thin electrical steel strip at home and abroad were described.The production capability,product property and application area of typical corporation were introduced.The results indicate that the urgency needed of electrical steel development is expanding high-grade non-oriented electrical steel production and improving products quality at present. 

一种电工钢切片用导向装置，涉及电工钢生产装置技术领域，包括导向台、支撑腿、安装块、转轴、辊体、电动机、安装板、滑杆、移动板和导向板；支撑腿设置在导向台底部；安装块设置有两个，两个安装块均设置在导向台横向一侧，两个安装块沿纵向分布；转轴转动设置在两个安装块之间；辊体设置在转轴上，辊体位于两个安装块之间，辊体位于导向台上方；电动机设置在安装块上，电动机与转轴驱动连接；安装板设置有两个，两个安装板分别设置在导向台纵向两侧上部；滑杆设置有两个，两个滑杆均设置在两个安装板之间，两个滑杆沿横向分布。本实用新型能够在电工钢的钢带切片之前进行导向限位工步，使得电工钢切割时不会被切割歪，切片的精度高。

本实用新型公开了一种变压器硅钢片剪切收料装置，其包括底板和存放架推出机构，底板的前侧中部设置有用于放置外设剪切设备的放置区；存放架推出机构包括滑动板座、锁紧组件，滑动板座可左右滑动地安装于底板的上表面，在滑动板的上表面设置有两个用于放置外设的硅钢片存放架的存放架放置槽，两个存放架放置槽呈左右间隔设置，锁紧组件用于锁紧滑动板座与底板之间的相对位置。当该硅钢片存放架存放完后，将滑动板座推动至使得另外一个存放架放置槽设置于放置区的正后方，另外的硅钢片存放架继续接受剪切设备掉落的硅钢片体，可连续地实现硅钢片体的落料存放，令转运和落料的操作不相互干涉，提高生产的效率。

借助光学显微镜、扫描电镜、交流磁性能测量仪和万能拉伸试验机研究了0.3 mm厚高强无取向电工钢冷轧板在780、820、860和900℃退火保温2 min后的组织、织构和性能。结果表明:在退火温度范围内,试验钢均发生了完全再结晶,得到等轴状的铁素体晶粒;随着退火温度的升高,平均晶粒尺寸从9.2μm增长到41.3μm,工频铁损和400 Hz高频铁损均先大幅减小后趋于平缓,磁感应强度先升高后降低。在820℃退火时,铁损P_1.5/50=5.51 W/kg,P_1.0/400=33.22 W/kg均处于较低值,磁感应强度B₅₀₀₀最大,为1.649 T。试验钢的屈服强度和抗拉强度均随退火温度的升高而降低,780℃退火时屈服强度为496 MPa, 900℃退火时降低至407 MPa。综合磁性能和力学性能考虑,试验钢的最佳退火温度是820℃。 Microstructure, texture and properties of 0.3 mm thick high strength non-oriented electrical steel cold rolled sheet annealed at 780 ℃, 820 ℃, 860 ℃ and 900 ℃ for 2 min were studied by means of optical microscope, scanning electron microscopy, AC magnetic property tester and universal tensile testing machine. The results show that in the annealing temperature range, complete recrystallization of the experimental steel occurs and equiaxed ferrite grains are obtained. With the increase of annealin... 

本发明提供了一种可修饰取向硅钢表面的无机绝缘涂料及其制备和使用方法，该涂料按照重量份计，包括：大颗粒硅溶胶5‑35份、磷酸二氢铝10‑30份、小颗粒硅溶胶5‑35份、铬酐0.5‑5份、增稠剂1‑10份、钛白粉0.01‑0.5份及去离子水0‑78.49份；该涂料的固含量为20‑40％。该涂料制备方法为：将增稠剂、去离子水、磷酸二氢铝、大颗粒硅溶胶、小颗粒硅溶胶，铬酐和钛白粉依次加入反应器中搅拌均匀，室温静置0.5‑1h。该涂料在使用时，需先将取向硅钢片进行清洁干燥预处理后，再将涂料辊涂在取向硅钢片上固化烧结并控制膜厚。本发明所提供的涂料制成的涂层表面平整均匀、颜色光亮，具有优良的附着性、耐蚀性、热稳定性和绝缘性，并且能修饰因硅酸镁底层质量不良引起的露晶亮点缺陷。

研究了采用高温卷取热轧态原料和常化态原料生产高牌号冷轧无取向电工钢组织、织构和磁性能。研究发现钢卷采用750℃高温卷取,下线后立即采用\"保温罩\"对钢卷进行保温,时间96h,然后空冷至100℃时上线生产的工艺可取代常化工艺生产高牌号冷轧无取向电工钢。冷轧上线前,热轧态原料的表层为大量的再结晶组织,这部分组织包括了热轧轧制时保留下来的动态再结晶组织,钢卷本身高温回复后产生再结晶晶粒,以及在保温罩内保温时形成的再结晶组织。高温卷取的热轧态和常化态的热轧卷作为原料时,试样织构类型相似,取向分布密度接近,再结晶后织构类型仍然相似,取向分布密度仍然接近。Goss织构对磁性能增加有促进作用。实验钢中较好的磁性能对应的织构[{100}+Goss]/{111}的比值较高,体现了织构的遗传性。 Microstructure,texture and magnetic properties of high grade cold rolled nonoriented electrical steel which made of hot rolled material with high temperature coiling and with normalization were studied.Steels coiled in high temperature(at 750 ℃),stacked with insulation cover for 96hand air cooled to 100 ℃ were using to manufacture high grade nonoriented electrical steel.The process can replace the normalization process.There are a lot of recrystallized grains in the surface layer of the coil wit... 

【摘要】 <正>日前,宝钢自主研发的新型高磁感取向...

主要研究了0.7%Si无取向电工钢退火试样的组织、晶粒尺寸和织构对其磁性能的影响。结果表明,随着退火温度的升高,晶粒尺寸逐渐增大,组织的均匀性得到改善;ɑ取向线上的纤维织构多集中于{114}<110>和{223}<110>附近,再结晶结束后,织构含量变化不大。{111}<110>织构取向密度值随温度升高而下降,{112}<111>织构与{111}<110>织构变化相反。晶粒尺寸增大对磁感强度的影响较小,而对铁损的影响较大。 Influences of microstructure,grain size and texture on the magnetic properties of 0.7% Si non-oriented electrical steels annealed samples were studied.The results show that with annealing temperature increasing the average grain size is increased gradually.Uniformity of the microstructure is improved;the textures of ɑ-fiber gathered in the vicinity of the { 114} < 110 > and { 223 } < 110 > texture.After recrystallization,the volume fraction of texture changes small.{ 111} < 110 &g... 

针对目前大部分无取向电工钢处理液为含铬处理液、且需在较高温度下固化的情况,在分析成膜物质性质的基础上,试验研究了一种可低温快速固化的电工钢环保绝缘处理液,研究了其涂装工艺,并测定了涂层的附着性、绝缘性、耐热性、耐蚀性等性能。试验结果表明:该处理液可在150~250℃下快速烘干固化,涂层表面光滑且致密均匀,性能优良,可满足中小电机的使用要求。 At present,most of the insulating fluid for non-oriented electrical steel contains chromium,and should be cured at high temperature.On the basis of analyzing the characteristics of the film-forming substance,a kind of eco-friendly insulating fluid with lower curing temperature for non-oriented electrical steel sheet was developed in the experiments.Then its coating process was studied,and the adhesiveness,insulativity,heat resistance,corrosion resistance and other properties of the coating was m... 

【作者】 朱传芳； 潘恒韬； ...

一种低温高磁感取向硅钢的热轧方法：经转炉冶炼并浇注成坯；对铸坯加热后进行粗轧：首先确定粗轧减宽量；根据所确定的粗轧减宽量进行粗轧；进行精轧；常规进行下工序。本发明采用低温板坯加热技术，降低了板坯烧损和修炉负担，且边裂发生率比现有技术的不低于18%的基础上能降低5%以上，由此节约资源及降低能耗。