在实验室模拟CSP工艺条件下制备了取向硅钢,研究了二次冷轧中间退火工艺对组织和织构的影响。结果表明,中间退火温度对取向硅钢脱碳,高温退火组织及织构均产生明显影响。经940℃中间退火后,取向硅钢脱碳再结晶晶粒较850℃中间退火的多,且再经高温退火处理后,晶粒粗化,最大晶粒尺寸达4.8 mm;高斯织构组分密度达27.00,较850℃中间退火试样高。 Grain-oriented silicon steel was prepared by simulated CSP technology in laboratory. Effects of secondary cold-rolled intermediate annealing on microstructure and texture were studied. The results show that intermediate annealing has obvious effects on the microstructure and texture of the steels after decarburization annealing and high temperature annealing. After intermediate annealing at 940 ℃,recrystallized grain of decarburization annealed steel is more than that of intermediate annealed at... 

本实用新型公开了一种电工钢加工用绝缘喷涂装置，包括底板，所述底板顶部外壁的中央位置设有安装通孔，所述安装通孔的两侧内壁上均通过轴承连接有转杆，所述底板的一侧外壁上固定连接有第一电机，第一电机输出轴的一端连接有连接杆，连接杆的一端固定连接在一个转杆的一端，两个所述转杆的一端固定连接有同一个放置架，所述放置架的两侧内壁上均固定连接有两个伸缩杆，四个所述伸缩杆活塞杆的外壁上均设有复位弹簧。本实用新型第二电机可以驱动每一个空心管转动的过程中，空心管内的绝缘漆从管壁的喷孔喷洒而出，而空心管外的扇板则配合交错分布的喷孔将雾化喷洒的绝缘漆打乱喷洒在电工钢上，全面且充分的完成喷涂。

本发明公开一种硅钢级氧化镁制备方法、硅钢级氧化镁保护膜，涉及氧化镁制备技术领域。将得到的粗氧化镁产品进行净化处理；将净化处理后的粗氧化镁产品与金属镁碳还原剂，在真空状态下，利用真空碳热还原技术进行金属镁的置换，制得金属镁；金属镁碳还原剂与粗氧化镁产品的质量比为（1~1.5）：1；制得的金属镁在纯氧下制得氧化镁；将制得氧化镁根据实际需求获得不同粒径硅钢级氧化镁颗粒。本发明产品各项指标优于企业标准的硅钢级氧化镁。而且不会受原料中含有的钙等杂质的影响，产品纯度很容易达标，同时，还存在能耗较低、生产成本低等优点，解决了业在降低能耗方面的突破可应用于工业化生产。

本发明涉及一种高性能取向硅钢冷轧工艺，具体涉及取向硅钢制造技术领域。本发明的冷轧工艺包括一次冷轧和二次冷轧，其中，取向硅钢热轧板厚度在2.0～3.0mm，一次冷轧轧制采用4或5道次轧制，轧至厚度0.60～0.62mm，轧制温度为100℃～105℃；二次冷轧轧制采用2道次，轧至厚度0.24～0.26mm，轧制温度为95℃～100℃。本发明通过对一次冷轧和二次冷轧中各道次的压下率、轧制张力、轧制速度、轧制温度进行优化设计，从而能够进一步优化织构，确保二次冷轧板高斯织构含量在0.8～1.5％，且轧制稳定性高，进而有效保证了所得取向硅钢的磁性能。

采用扫描电镜、场发射扫描电镜、能谱仪等对50SW1300冷轧无取向硅钢中的夹杂物分不同尺寸区间进行数量统计,利用主成分回归分析法,即数据的标准化处理—主成分分析—回归分析—标准化的变量还原成原始变量—确定显著影响因素,综合分析夹杂物总量及各尺寸区间的夹杂物数量对无取向硅钢磁性能的影响。结果表明:主成分回归分析能够从夹杂物尺寸区间及数量的多个影响因素中提取主要的因素,定量研究其对磁性能的影响。分析表明,显著影响无取向硅钢铁损的夹杂物为100~500nm的AlN、AlN+MnS、MnS、Al2O3、AlN+Al2O3,而劣化磁感最明显的夹杂物尺寸区间为100~200nm。 Different size intervals of inclusions in cold rolled non-oriented silicon steel 50SW1300 were counted by scanning electron microscope(SEM),field emission scanning electron microscope(FESEM)and energy disperse spectroscopy(EDS).With principal component regression method:standardization for experimental data,principal component analysis,regression analysis,transform standardized variables into original variables,determination of significant factor,effects of the total number of inclusions and the... 

一种基于大数据分析技术的电工钢用户选材询单推荐方法，于终端计算机内、以可与终端计算机各数据库进行信息交互的形式、设置一计算模块；经此计算模块完成依次的基于各数据库的有效信息的采集、用户询单选材推荐方案模型的设置、基于有效信息及推荐方案模型完成推荐牌号的生成，根据设定的评估模型对生成的推荐牌号及信息评估运算的运行，据此建立对用户的选材询单推荐。本发明的一种基于大数据分析技术的电工钢用户选材询单推荐方法，基于L4计算机系统开发出的计算模块及相应的可与计算模块进行信息交互的用户界面完成，形成可根据不同用户需求对应的不同评价体系，完成与不同用户需求适配的方案推荐。

研究稀土Ce的添加对含Sn高磁感无取向电工钢磁性能及夹杂物的影响。对比分析了两种成分钢的磁性能以及各过程工艺条件下夹杂物种类和分布情况。结果表明,在含Sn高磁感无取向电工钢中加入稀土元素Ce可以粗化夹杂物,提高成品晶粒的均匀性,有效降低铁损;同时Ce的添加不影响Sn元素提高磁感的效果,磁感保持不变。 Effect of Ce on magnetic properties and inclusion of Sn-bearing high permeability non-oriented electrical steel was investigated. A comparative analysis of the magnetic properties and the types and distributions of inclusion in the two sheets with different composition shows that the addition of Ce to the Sn-bearing high permeability non-oriented electrical steel can coarse the inclusion,improve the homogeneity of the finished grain and effectively decrease the core loss. Also,the addition of Ce... 

对RH法(真空循环脱气法)生产的冷轧硅钢的脱硫原理及影响因素进行了分析研究。研究表明:降低顶渣中FeO、MnO的含量,提高钢液温度,增加脱硫剂的加入量并延长其循环时间有利于提高脱硫效率。 The principles of desulfurization and its influence factors of cold rolling silicon steel during RH process have been studied in this paper.The result indicated that reducing contents of FeO and MnO,rising temperature of the liquid steel,increasing quantity of desulfurizer,lengthening cycle time of desulfurzer are benefit for desulfurization. 

本实用新型公开了一种硅钢片加工装置，涉及硅钢片加工领域，包括底板，所述底板的上方左右两端固定连接有液压伸缩杆，所述液压伸缩杆的顶部固定连接有连接板。该硅钢片加工装置，可灵活调节两组打孔机之间的距离，可使用该加工装置加工出不同孔距的硅钢片，也即可加工出所需不同种类的硅钢片，加工灵活性强，使用范围广泛，通过开启电机，最终可使得两组打孔机同时进行向内侧或外侧进行移动，实现调节硅钢片两组打孔的位置。

一种甩带法制备高磁性能含磷硅钢薄带的方法，属于合金材料领域。本发明以硅钢(Fe‑(3‑6.5)wt.％Si)块体为母合金，并添加一定量的硅铁合金及磷铁合金，放置于中频感应炉中，熔融后经快速凝固‑甩带、冷轧、热处理工艺，得到具有优异性能的含磷硅钢薄带。对于硅钢而言，P元素的少量加入能够有效的提升电阻率从而显著降低铁损，且具备优化软磁性能的作用。而采用甩带法能够充分利用其快速凝固的特征，从根本上避免了P元素在传统熔炼冷却过程中严重偏析的缺陷，极佳地保证了产品的组织优势与软磁性能。本发明具有操作简单、生产效率高、产品精度高、工艺流程短、无污染与夹杂、性能优异等优点。

本实用新型公开了一种硅钢片分流导料机构，属于硅钢片导料领域，包括传送带，所述传送带包括主带和副带，所述副带设置在主带的前面，所述主带横向设置，所述主带的后面设置有导流机构，所述导流机构包括电机、导流板和助力组件，所述主带的后面设置有安装架，所述安装架的顶部竖向固定连接有连接板，所述电机安装在连接板上，所述电机的输出轴与导流板的顶部固定套接，通过启动电机，电机带动导流板旋转，导流板在连接组件下带动助力组件旋转，使得主带上的物品被导流板进行阻挡，通过助力组件传送到副带上，避免了传送带方向单一，容易导致硅钢片对堆积的问题，从而减少硅钢片的损坏量，进而节约成本。

采用光学显微镜、X射线衍射仪等分析了宁波钢铁有限公司生产的取向硅钢不同工序下的组织及织构演变规律。结果表明:铸坯经过热轧后,沿着厚度方向组织不均匀;一次冷轧并经脱碳退火后,组织由条状纤维状变成等轴状的初次再结晶晶粒,初次再结晶平均晶粒尺寸为18.17μm,织构主要以α织构和γ织构为主;在二次冷轧后,晶粒再次被压缩,转变为纤维状,织构主要为γ织构;经过高温退火后,发生二次再结晶,晶粒异常长大,晶粒尺寸达到厘米级,织构成分为单一且锋锐的Goss织构。 The microstructure and texture evolution of oriented silicon steel produced by Ningbo Iron and Steel Co.,Ltd.were analyzed by optical microscope and X-ray diffraction.The results showed that the microstructure of the slab was inhomogenous along the thickness direction after hot rolling.After first cold rolling and decarburizing annealing,the microstructure changed from strip fibrous to equiaxed primary recrystallized grains,and the average grain size of the primary recrystallization microstructu...