本发明揭示了一种新能源驱动电机用无取向硅钢及其生产方法。所述硅钢通过依序进行的炼钢、连铸、热轧、常化、酸洗、无预热单机架冷轧、退火、冷却、涂层和精整制备而成，炼钢时不添加Cu、Cr、Ni、Nb、V、Ti，硅钢的化学成分：Si:2.95％～3.15％，Al:0.75％～0.95％，Si+2Al:4.6％～4.9％，Mn:0.5％～0.7％，Sn:0.03％～0.04％，C≤0.0025％，余量铁；Mn/S≥380，Al/N≥200。本发明在保证磁性能的同时，提高了强度，解决了现有技术所存在的磁性能和强度的兼顾问题，能够满足新能源汽车的驱动电机上的应用要求。

针对某硅钢车间ST机组的除尘系统除尘效率较低、排放浓度不达标、二次污染较严重的问题,通过现场调研,对除尘系统、含尘气体组分与物性参数等进行测试和分析,运用管道伴热技术改善粉尘黏性后,再选取合适的除尘器对粉尘进行除尘处理,大大地提高了系统的除尘效率。 To solve the problems of low dust removal efficiency, substandard emission concentration and severe secondary pollution, some investigations are conducted to test and analyze the dust removal system,dust-gas composition and relevant physical parameters.Moreover, dust removal efficiency is greatly improved by the use of pipe heat tracing technology and by choosing appropriate dust remover. 

本实用新型公开了一种基于取向电工钢用收卷组件及其固定结构，包括主体，所述主体的后侧中部固定安装有固定杆，所述固定杆的侧面活动安装有活动机构，所述活动机构包括活动块，活动区，弹簧，主动块，连接孔，连接杆，齿轮，卷筒，挡板。该种基于取向电工钢用收卷组件及其固定结构，活动块会带动活动区内部的主动块在其内部移动，可以通过连接杆带动齿轮进行转动，因齿轮侧面啮合连接有齿口，从而会顺着主体的侧面进行移动，当齿轮移动到主体的一角时，会带动活动区内部的弹簧收缩，弹簧可根据齿轮到主体中心的距离长短进行伸缩，物料会通过卷筒落到卷块的表面，从而可以对物料进行收卷，最后达到了便于收卷，降低物体损害的目的。

采用EBSD技术研究了有、无拉应力作用下无取向硅钢在晶粒长大过程中织构转变及晶界变化的规律。结果表明:在晶粒生长期间,无应力作用下的硅钢中,{111}〈112〉,{111}〈110〉织构组分强化,而{100}〈001〉织构组分弱化;与无拉应力作用下的情况相比,施加5MPa的拉应力时,{111}〈112〉,{111}〈110〉织构组分强化的速率下降,{100}〈001〉织构组分变化不明显。对于在晶粒生长期间持续变化的{111}〈112〉,{111}〈110〉和{100}〈001〉织构组分而言,虽然有、无拉应力作用下硅钢的{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率均下降,而{100}〈001〉织构组分的高取向差角度晶界频率则上升,但当有拉应力作用后,{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率下降的速率变小,{100}〈001〉织构组分的高取向差角度晶界频率上升的速率稍有变小。通过对无取向硅钢在晶粒长大过程中织构转变及晶界变化规律的研究,分析了合金原子在晶界的偏聚行为。 The rules of texture and grain boundary transformation in the nonoriented silicon steel under applied stress or without applied stress during grain growth were investigated by EBSD.The results show that the {111}〈112〉 and {111}〈110〉 components in the nonoriented silicon steel without stress are strengthened during grain growth whereas {100}〈001〉 component is weakened,but the growth rate of {111}〈112〉 and {111}〈110〉 component decreases,while the area fraction of {100}〈001〉 component doesn’t chang... 

本实用新型涉及一种用于叠装变压器铁芯硅钢片的装置，包括托板，托板的上表面固定设置有固定板，固定板的内部开设有沉槽；双向螺纹杆，双向螺纹杆设置在固定板的内部，双向螺纹杆的一端贯穿固定板的侧壁并连接有把手；支撑柱，支撑柱的表面开设有连接槽，连接槽的内部铰接有连接杆；有益效果为：本实用新型提出的一种用于叠装变压器铁芯硅钢片的装置在托板的左右两侧设置有两组对称分布的固定板，通过对双向螺纹杆的旋转，螺接在双向螺纹杆表面的两组滑块将会相对移动，铰接在滑块上表面的两组支撑柱将会形成三角形对铁芯进行防护。

本发明属于智慧物流技术领域，具体的说是一种用于硅钢卷运输的智慧物流系统及防塌卷装置，包括运输模块、支撑模块、感应模块与分析模块；所述支撑模块以设置在硅钢卷内圈的支撑组件为载体；所述感应模块以设置在支撑组件上的感应组件为载体，且所述感应组件内设置有若干个均匀分布的压力感应器；所述分析模块以中央处理器为载体；本发明通过在支撑硅钢卷的支撑组件上设置感应组件，使得工作人员对硅钢卷内部的清洁度与杂质位置进行有效的判断，并通过定点清理其内部的杂质，减少硅钢卷内部的硅钢片在支撑时被压伤的情况，提高了硅钢卷在物流运输时的安全性。

承钢采用铁水预处理(脱硫)→转炉提钒→转炉冶炼→RH精炼→连铸→轧制工艺,成功研发了无取向电工钢CGW800。试制的CGW800钢碳含量≤0.006 0%、氮含量<0.004 0%,热轧后的金相组织为铁素体和少量渗碳体,晶粒度5.5级,获得了较粗大、均匀的晶粒,钢板的成分和力学性能达到了标准要求。 In Cheng Steel,the CGW800 non- oriented electrical steel is successfully developed with process of hot metal pre- treating,vanadium extracting with converter,smelting with converter,RH refining,continuous casting and rolling. In the steel,the carbon content is not higher than 0. 006 0%,nitrogen less than0. 004 0%,the metallographic structure after hot rolling is ferrite and a little amount of cementite,grain size is 5. 5 degree,relative large and even grain got. The composition and mechanical pr... 

针对川威950的工艺现状,结合无取向低硅钢SGG生产的工艺特点,主要从控制其钢坯加热和轧制以及终轧温度和卷曲温度几方面入手,进行无取向低硅钢生产的工艺控制研究。同时根据近6000吨的生产实践表明,该工艺措施能很好的满足该钢种的需要。 950 process Chuanwei status quo,with non-oriented silicon steel production process features low,mainly from the control of billet heating and rolling and finish rolling temperature and coiling temperature of several aspects,for non-oriented silicon steel production process of low control at the same time According to nearly 6,000 tons of production practice shows that the process measures could well meet the needs of the steel. 

本发明公开了一种硅钢轧制系统，包括：轧机组，所述轧机组包括M架轧机，用于轧制硅钢，所述M架轧机的前N架轧机的轧辊为高速钢轧辊，其中，M、N为正整数；硅钢检测装置，位于所述轧机组最后一架轧机的出口处，用于对出口硅钢的参数信息进行检测；控制器，与所述硅钢检测装置通信连接，用于在所述参数信息不满足预设参数条件时，控制所述轧机组停止工作；磨床，用于在所述轧机组停止工作后，对所述N架轧机中的每架轧机进行辊形精度检测，对不满足预设辊形精度范围的轧辊进行磨削。

【机构】 武钢研究院； ...

针对传统工艺生产硅钢周期长、能耗大等缺点,采用双辊连铸工艺制备3%Si无取向硅钢连铸薄带,利用MEM,SEM和TEM观察了铸带的组织、织构及析出物,同时对比了Al的质量分数为0.6%和0.9%的连铸薄带在组织、织构及析出物特征方面的异同.结果表明:双辊连铸工艺生产的3%Si无取向硅钢铸带的组织为均匀等轴晶粒,平均晶粒尺寸约为300μm;织构组成随Al质量分数的不同具有明显差别,Al质量分数为0.9%的铸带中{100}织构强度是随机织构的7倍;铸带中的析出物为AlN和MnS,最大尺寸分别为500和50 nm左右. Given the lengthy production cycle,high energy consumption,and other shortcomings of the traditional process for producing silicon steel,a twin-roll casting process was used to produce 3%Si non-oriented silicon steel casting strips. MEM,SEM,and TEM were used to compare micro-structure,texture,and precipitate characteristics of a casting strip containing 0.6%Al with another containing 0.9%Al.The structure of 3%Si non-oriented silicon steel produced by the twin-roll casting process was a uniform i... 

为研究退火工艺对普通取向硅钢初次再结晶组织的影响,对经不同温度、保温时间和升温速率退火后的材料组织进行了分析。结果表明:在等温退火条件下,加热至600℃时开始发生初次再结晶,800℃以上初次再结晶组织发展完善;而在最终冷轧板直接进行最终高温退火的情况下,加热温度在500～700℃时,将升温速率提高到80℃/h,初次再结晶组织更易于发展完善。 To investigate the influence of annealing process on the recrystallization of common grain oriented silicon steel,microstructures of sheets annealed at different temperature,soaking time and heating rate are observed.Results show that under the condition of isothermal annealing,recrystallization begins at 600℃ and fully develops above 800℃,while in the case that the final cold rolled sheets are directly thrown to final high temperature annealing,recrystallization is likely to develop with the he...