通过在实验室条件下模拟薄板坯连铸连轧流程,并在以Cu2S为主抑制剂制造普通取向硅钢(CGO)的基础上,加入适量钒钛,研究了钒钛对取向硅钢组织与磁性能的影响。结果表明,适量钒钛使热轧板和脱碳退火板组织更好,尤其使脱碳退火板的晶粒更加细小和均匀;加入适量钒钛不但使热轧板表面高斯织构强度更高,更使脱碳退火板中有利于高斯织构发展的γ织构强度更高;适量钒钛能形成Cu2S+(V,Ti)N等复合析出物,起到辅助抑制剂作用,加强抑制能力。细小均匀的晶粒、强度更高的有利织构和更强的抑制能力使CGO钢磁性能更佳。 Effect of V and Ti on microstructure and magnetic properties of conventional grain-oriented silicon steel(CGO) were investigated under simulated thin slab continuous casting and rolling process in laboratory with Cu2 S as the dominant inhibitor. The results show that appropriate amount V and Ti make the microstructures of the hot rolled sheet and the decarburizing annealed sheet better,especially make the grains of the decarburizing annealed sheet more tiny and uniform. Adding appropriate V and ... 

本申请涉及硅钢制造技术领域，尤其涉及一种去除耐热刻痕取向硅钢中熔覆物的化学试剂及其方法。所述化学试剂的组分以质量分数计包括：强酸溶液：8％～20％；酸性氧化剂：5％～15％或助剂：5％～20％；其余为溶剂；其中，所述强酸溶液包括硫酸、盐酸和硝酸中任意一种。本申请实施例提供的该方法，通过10％～20％强酸溶液，可快速有效地去除取向硅钢刻痕处的熔融物，而酸性氧化剂：5％～15％，或助剂：5％～20％结合合适浓度的强酸溶液，可以将取向硅钢的基体破坏降到最小，两种综合作用，得到表面平整的耐热刻痕取向硅钢。

一种高硅钢材料的制备方法，步骤包括靶材、金属基材表面清理；排除密闭容器内空气、通保护气；双辉光等离子预轰击靶材和基材，净化表面；等离子溅射、加热、保温；缓慢冷却取出。预轰击靶材、基材，去除表面吸附层、活化基材，交替升高基材电压、靶材电压，使靶材中的合金元素被离子轰击而溅射出来、扩散进入基材内部形成表面高硅钢层。“双辉光等离子表面冶金技术”制备高硅钢的工艺简单易行、可控性高、成本低、无污染且基体和表面的结合力高，适合大规模产业化生产；更重要的是该方法采用交替离子轰击、扩渗速度快，结合强度高，得到硅含量均匀分布或呈梯度分布的高硅钢材料，为制备更高品质的无噪音、低铁损的高硅钢产业化奠定基础。

【作者】 杨洪林； ...

结合硅钢退火炉项目中应用PDSOFT软件进行三维配管设计的案例,描述PDSOFT软件的应用过程,总结其使用要点,分析其优缺点,并提出了推广三维设计软件的思路,对今后PDSOFT在相似项目中的推广应用有参考和借鉴价值。 Combining the case of using PDSOFT software to design the three-dimensional piping,the application process of the PDSOFT software is described,the using points are summarized,the advantages and disadvantages are analyzed,and the ideas of promoting the three-dimensional design software are put forward,which have a strong reference value for the promotion and application of PDSOFT in similar projects in the future. 

本实用新型公开了一种具有导气槽的低空载损耗电工钢用罩式炉，包括：炉台，顶部设置有加热元件以及连通炉台外缘至中心凹陷的导气通道；炉板，压设于炉台上，设置有与中心凹陷上下对应的中心通孔；砂封槽，设置于炉台的外周，槽底低于导气通道；炉罩，罩设于炉台的顶部及外周形成炉腔，与砂封槽相压接；进气通道，穿设于炉台的中心凹陷中，具有开口向上的排气口；炉罩的炉台套接段内壁设置有导气槽，导气槽的延伸方向与炉罩的高度方向一致，导气槽将气流导向炉台外缘的导气通道进气口。该具有导气槽的低空载损耗电工钢用罩式炉的炉罩设置有导气槽，利用导气槽将硅钢卷外周下行的气流导入炉台的导气通道中，改善钢卷热处理过程中的流场和温度场。

近年来，在节能减排背景之下，国内外众多研究者对无取向电工钢磁性能的提升做了大量研究。为了探索无取向电工钢磁性能提升的方法，对锡或锑对无取向电工钢磁性能的作用机制(晶粒尺寸和晶体织构的控制)进行分析。基于该作用机制，介绍锡或锑的添加对无取向电工钢磁性能的影响。经研究发现，适量的锡或锑在晶界偏聚，不会阻碍晶界的移动并且致使晶粒尺寸降低；与此同时，锡或锑在晶界偏聚不仅抑制{111}织构在原始晶界处形核及生长，还降低(100)晶粒表面能，促进(100)晶粒生长。因此，适量添加锡或锑，可使无取向电工钢铁损下降、磁感提升。最后结合生产工艺，建议无取向电工钢的研究方向应为稀土含量对高牌号无取向硅钢夹杂物尺寸和数量分布的影响，锡或锑的添加量和常化工艺参数(常化时间、常化温度)对常化晶粒尺寸的影响。 In recent years, due to the background of energy saving and emission reduction, numerous researchers all around the world have done a lot of investigations on the improvement of magnetic properties for non-oriented electrical steel. In order to explore the method of improving the magnetic properties of non-oriented electrical steel, the mechanism of tin or antimony on the magnetic properties(the control of grain size and crystallographic texture) of non-oriented electrical steel is illuminated. ... 

根据新日铁、JFE及浦项等国外钢铁公司2008年以来在日本专利局、欧洲专利局(EP)及世界知识产权组织(WIPO)申请公开的有关生产Hi-B取向电工钢典型专利技术,概述了近年来国外大型钢铁企业采用低温板坯加热(坯加热温度<1 280℃)技术生产Hi-B取向电工钢主要技术重点,即将调节关键化学成分Al、N、Sn及Sb等与工艺改进相结合。最后介绍了国外大型钢铁企业采用低温板坯加热技术生产Hi-B取向电工钢实例。 The latest developments on technology for manufacturing Hi-B grain oriented electrical steel sheets developed by Nippon Steel Corp.,JFE Steel and POSCO were described according to the patents published by World Intellectual Property Organization,Japan Patent Office and European Patent Office over the recent years.The low temperature slab heating process(particularly slab-heating temperature<1 280 ℃) together with suitably adjusting key chemical elements such as Al,N,Sn and Sb elements was the... 

【作者】 凌健； ...

本发明提供了一种轴向开关磁阻电机转子硅钢块的成型方法，包括(a)提供一硅钢片盘，其中所述硅钢片盘具有内端部和外端部，及贯穿所述内端部和所述外端部的多个固定孔，相邻的两个所述固定孔之间形成硅钢块；(b)提供多个齿棒，逐一将多个所述齿棒依次插入于所述固定孔；(c)提供一固型组件，将所述固型组件固定于所述内端部和所述外端部上；(d)沿着所述硅钢块和所述固定孔之间界定的切割位置进行切割，以获得组装转子的多个硅钢块。所述硅钢片盘通过所述固定孔分隔成多个形状一致的所述硅钢块，多个所述硅钢块通过切割分离，并可对应组装成一转子，成型方便快捷，还保障产品形状的一致性，实现工业化批量生产。

通过试验确定氩气分析流量为3.5L/min,静态流量为0.75L/min,冲洗时间为3s,预燃时间为12s,积分时间为5s的激发条件,采用火花源原子发射光谱法测定取向硅钢中碳、硅、锰、磷、硫。分别采用铣床铣样、砂轮磨样两种制样方式进行了精密度考察,发现制样方式对结果影响不大;讨论了取向硅钢样品中碳、硅、锰、磷、硫测定时可能存在的共存元素干扰,发现硅对锰元素的干扰不可忽略,采用干扰系数法进行了校正,据此拟合得到各元素校准曲线的相关系数均在0.999 0以上。精密度考察结果表明,碳、硅、锰、磷、硫的相对标准偏差(n=10)在0.71%~9.4%之间。对两块取向硅钢生产样品进行分析,并与钢铁研究总院进行比对分析,结果一致,且偏差均在允许范围内。 Carbon,silicon,manganese,phosphorus and sulfur in oriented silicon steel were determined by spark source atomic emission spectrometry.The selected excitation conditions were as follows:the analytical flow rate of argon was 3.5L/min,the static flow rate was 0.75L/min,the flush time was3s,the precombustion time was 12sand the integration time was 5s.Two sample preparation methods,including milling machine and grinding wheel,were investigated.The precision test results showed that,the determination... 

本发明揭示了一种新能源驱动电机用无取向硅钢及其生产方法。所述硅钢通过依序进行的炼钢、连铸、热轧、常化、酸洗、无预热单机架冷轧、退火、冷却、涂层和精整制备而成，炼钢时不添加Cu、Cr、Ni、Nb、V、Ti，硅钢的化学成分：Si:2.95％～3.15％，Al:0.75％～0.95％，Si+2Al:4.6％～4.9％，Mn:0.5％～0.7％，Sn:0.03％～0.04％，C≤0.0025％，余量铁；Mn/S≥380，Al/N≥200。本发明在保证磁性能的同时，提高了强度，解决了现有技术所存在的磁性能和强度的兼顾问题，能够满足新能源汽车的驱动电机上的应用要求。