目前随着电工钢用户冲压设备的升级,冲压速度逐步提高,对电工钢产品的硬度和强度指标提出了更高的要求。与普通硬度级别的无取向硅钢相比,高硬度50BW600的Hv硬度提高15~20,达到125以上,同时对电磁性能指标也有较高要求。本钢通过化学成份和热轧及冷轧连退生产工艺的设计,经过小批量生产试验,满足用户要求。通过对工艺的严格控制,在大批量生产过程中,保证了产品的力学性能和电磁性的检验合格率。 Currently with upgrading of stamping equipment of silicon steel user, gradually increasing of stamping speed, propose higher demand for hardness and strength of silicon steel. Compared with conventional 50BW600, high hardness 50BW600 have higher hardness, reach greater than 125Hv. Through design of chemical composition with hot mill and annealing, production test of small quantities, stamping performance meet user request. 

本实用新型公开了一种取向硅钢绝缘层烘干装置，涉及取向硅钢技术领域，为解决现有取向硅钢在表面层进行烘干的时候，能源大多没有循环利用，不够节能的问题。所述烘干装置主体的上端面设置有加热泵回送机构，所述加热泵回送机构通过输送管道与烘干装置主体连接，且输送管道设置有两个，两个所述输送管道的两端分别贯穿并延伸至烘干装置主体和加热泵回送机构的内部，所述烘干装置主体的内部设置有烘干输送腔体，所述烘干输送腔体的上方和下方均设置有过滤网，且过滤网设置有两个，两个所述过滤网的一侧均设置有加热机构。

硅钢工业退火炉温度控制具有强耦合、纯滞后、多扰动等特点,它的控制方法代表着一类非线性系统控制的解决方法。以硅钢工业退火炉温度为控制对象,在双交叉限幅控制的基础上引入了智能学习系统,形成了基于智能学习系统的双交叉限幅控制方法来解决此类非线性系统的控制问题,并通过模块化的编程来实现其功能。结果表明:与传统的PID控制相比,该控制方法的控制精度、抗扰性等控制指标有明显提高,是解决此类非线性控制的一种有效方法。 The temperature control of silicon steel industrial annealing furnace has the features of strong coupling,pure lag,multidisturbance. The control method represents the solution of a class of nonlinear control systems. The control object is the temperature control of silicon steel industrial an-nealing furnace, the intelligent learning system based on Double Across Limit Control is introducedand used to solve control problem of this kind of nonlinear system, and the module programming isused to re... 

介绍了国内无底层取向电工钢生产技术水平、产量和用途，简述了无底层取向电工钢作为取向电工钢超/极薄带母料及应用于制作大型发电机组铁心、风电等电机铁心和变压器铁心等的情况。 The production technology level,output and application of domestic glassless grainoriented electrical steel were introduced,and the application of glassless grain-oriented electrical steel as parent material of ultra-thin strip of grain-oriented electrical steel and in making large-scale electric generator cores,wind power motor cores and transformer cores were briefly described. 

本发明公开了一种高强度碳化硅钢球，所述高强度碳化硅钢球包括以下重量份的原料：碳化硅20‑30份、铬1‑2份、氮化硼3‑5份、铁10‑20份、钼2‑3份、锰钢30‑40份、镍5‑8份、钛6‑8份、磷2‑3份、硫2‑3份；一种高强度碳化硅钢球制备方法，包括如下步骤S1、熔融；S2、模锻成球；S3、打磨；S4、二次加热；S5、高温淬火；S6、机油回火；S7、检测成品。本发明制备的高强度碳化硅钢球具有抗折强度高、洛氏硬度高及抗压强度高等优异的机械性能，并且使用寿命长，运转精确度高，并且其工艺简单，生产耗能低，无“三废”产生，环保性高。

对熔融态钢液进行处理,研究了电脉冲对于取向硅钢凝固组织的影响作用,利用正交试验法研究了脉冲电容、频率、处理时间和电压等脉冲参数的作用效果。结果表明:电脉冲对钢锭晶粒组织具有明显的细化作用,凝固组织的等轴晶比例大幅上升,影响等轴晶比例的最显著性因素为脉冲频率,最优正交试验参数为电容1 200μF,脉冲频率1 Hz,处理时间5 s,脉冲电压800 V。随着输入能量的增大等轴晶率先增大后减小,脉冲输入能量为某值时,等轴晶率最大,利用经典形核理论和热力学对这一现象进行了解释。 The influence of electric pulse on the solidification structure of oriented silicon steel was investigated by applying electric pulse in molten steel.The affection due to different electric pulse parameters such as electric capacity,frequency,applied time and voltage was studied by orthogonal design test.The result showed that solidification structure of oriented silicon steel could be improved by the electric pulse,and the equiaxed crystal ratio increased obviously.The most influential paramete... 

采用传统的轧制和退火工艺制备了0.30mm厚的6.5%(质量分数)Si高硅电工钢薄板,采用X射线衍射技术对退火过程中的再结晶织构进行了研究。冷轧高硅钢薄板700℃退火形成以{111}〈112〉为峰值的γ织构(〈111〉∥ND)和以{001}〈210〉为峰值的{001}织构;而900℃以上温度退火则形成强{001}〈210〉织构。进一步的研究表明是在晶粒长大过程中{001}〈210〉发展成为主要再结晶织构组分。 High silicon steel thin sheets with thickness of 0.3mm were successfully produced by conventional rolling and annealing methods.Recrystallization texture was investigated by means of X-ray diffraction.It is found that recrystallization texture is mainly composed of γ fiber(〈111〉∥ND)with peak at {111}〈112〉 and {001} fiber with peak at {001}〈210〉 after annealing at 700℃,while strong {001}〈210〉 component dominates recrystallization texture after annealing above 900℃.It is during grain growth that {... 

针对不同牌号的无取向硅钢产生结疤缺陷的难易程度和表面结疤缺陷的外形特征及分布规律,分析了该缺陷产生的原因。通过调整剪前导板的对中度,设置精轧侧导板开度余量及短行程数值,及时修补与更换侧导板,减少带坯与侧导板挤撞程度,有效地降低了结疤缺陷发生率。 This article analyses the cause of the scab defects according to the defects appearance characters and distribution law,degree of difficulty to form scar of non-oriented silicon steel. It can effectively decrease the scabs by different methods,such as adjusting the center line of guide plate,setting the opening margin and short stroke value of the side guide on finishing mill,timely repairing and replacing of side guide,decreasing the collision between the strip and side guide. 

对RH法(真空循环脱气法)生产的冷轧硅钢的脱硫原理及影响因素进行了分析研究。研究表明:降低顶渣中FeO、MnO的含量,提高钢液温度,增加脱硫剂的加入量并延长其循环时间有利于提高脱硫效率。 The principles of desulfurization and its influence factors of cold rolling silicon steel during RH process have been studied in this paper.The result indicated that reducing contents of FeO and MnO,rising temperature of the liquid steel,increasing quantity of desulfurizer,lengthening cycle time of desulfurzer are benefit for desulfurization. 

本发明提供了一种CSP流程生产高效冷轧无取向电工钢及生产方法，成分：C≤0.0030％、Si 1.00‑1.70％、Als≤0.0050％、Mn 0.10‑0.30％、Sn0.01‑0.3％、P≤0.050％、S≤0.0080％、N≤0.0030％、Nb≤0.0030％、V≤0.0030％、Ti≤0.0030％，其余为Fe以及不可避免的杂质。与现有技术相比，本发明CSP流程生产高效冷轧无取向电工钢的方法，通过控制钢中的化学成分，并采用合适的生产工艺，实现了表面质量优良，低铁损、高磁感、低制造成本且生产高效。

本发明提供一种退火隔离剂及退火隔离剂悬浮液的制备方法与无底层低温高磁感取向硅钢的制备方法。所述退火隔离剂按照重量份包括如下组分：CaO：1‑5份，Al2O3：50‑58份，Ca(AlO2)2：1‑5份，MgO：30～38份，添加剂：1‑2份。本发明的退火隔离剂不仅能够起到高温退火时钢板之间的隔离作用，而且能够在升温过程中保护抑制剂对二次再结晶晶粒的抑制能力，确保二次再结晶晶粒稳定长大，成品磁性能优异，进而稳定制备出表面光洁，边部完全无底层的低温取向硅钢成品。

本实用新型公开了一种硅钢炉用保护气的循环系统，包括与硅钢炉群排气管相连通的氢气提纯净化单元、与氢气提纯净化单元相连的氮氢配比单元以及与氮氢配比单元相连的用于对氮氢混合气中加入水蒸气的加湿单元；所述加湿单元与硅钢炉群的进气管相连通。本实用新型便于对尾气中的氢气回收再利用，可节省资源。本实用新型适用于硅钢退火炉等设备中，用于实现氢气的循环再利用。