试验研究了0.3 mm取向硅钢冷轧板(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005A1)的退火温度(760~880℃7 min)和退火时间(820℃3~9 min)对该钢的晶粒尺寸,再结晶和织构的影响。结果表明,最佳初次再结晶退火工艺为820℃5 min,该钢的平均晶粒尺寸为14.20μm,完全再结晶率为92%,不利{111}<110>结构含量为3.16%,有利织构{111}<112>,{012}<001>和高斯织构含量分别0.40%,4.73%和2.46%。 The effect of annealing temperature(at 760 ~ 880 X.for 7 min) and time(at 820℃ for 3~9 min) on grain size,recrystallization rate and texture of 0.3 mm cold-rolled sheet of oriented silicon steel(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005Al) has been tested and studied.Results show that with optimum recrystallized annealing at 820℃ for 5 min,the silicon steel average grain size is 14.20 fun,the complete recrystaUization rate is 92%,the unfavourable-texture {111}< 110 > content in steel is ... 

本发明的一个实施方案提供一种取向电工钢板及其制造方法，以重量％计，所述取向电工钢板包含：Si：3.0‑4.5％、Mn：0.05‑0.2％、Al：0.015‑0.035％、C：0.0015％以下(0％除外)、N：0.0015％以下(0％除外)、S：0.0015％以下(0％除外)、余量的Fe及其它不可避免的杂质，并且满足以下关系式1和关系式2。[关系式1](W13/50/W17/50)≤0.57[关系式2](W15/50/W17/50)≤0.76(其中，所述关系式1中，Wx/y表示施加磁场的大小为x/10T且频率为yHz的条件下的铁损值)。

本实用新型公开了一种直流力矩电机的定子硅钢片固定结构，包括设置于外壳内的硅钢片组，所述硅钢片组的后端被所述外壳的后端的内壁抵顶住，所述硅钢片组的前端被设置于所述外壳前端的可动压圈压紧固定。本实用新型所述的直流力矩电机的定子硅钢片固定结构中，通过在外壳内壁的前端和后端分别设置阶梯台，以对硅钢片组前后两端进行限制抵顶，可令散片形式的多个硅钢片组牢固的设置于外壳之内。

本实用新型公开了一种环保型无取向硅钢绝缘涂层液生产用篮式研磨机，包括底座，底座顶端的一侧固定安装有支撑柱，支撑柱的顶端固定安装有顶板，顶板的底端设有研磨组件，研磨组件包括两个固定板，两个固定板分别固定安装的顶板底端的中部和底端的另一侧，底座上设有固定组件，固定组件包括四个支撑板，四个支撑板均固定设置底座顶端的另一侧，四个支撑板的顶端固定安装有固定环，固定环的内部放置有料缸，本实用新型的有益效果是：通过研磨组件在粗磨后快速切换至细磨，不需要切换研磨机，提高研磨的效率，通过固定组件将放置在固定环内部的料缸进行固定，防止研磨过程中料缸发生移动。

通过热力学计算及实验室研究,对钙处理前后50W600无取向硅钢退火冷轧板中夹杂物的类型、数量及尺寸进行了系统分析。结果表明,50W600无取向硅钢经钙处理后(w(Ca)=0.002 6%),钙在1 600℃的钢液中主要以固态的CaO·2Al2O3、CaO·6Al2O3及溶解钙的形式存在。在钢液的凝固过程中,钢中的溶解钙和硫反应生成了CaS和CaS-MnS复合夹杂,有效抑制了MnS的弥散析出,减少了钢中微细夹杂物的数量。同时钙处理促进了钢中微细夹杂物的聚合长大,导致显微夹杂物的数量增加。 Based on thermodynamic calculation and laboratory experiment,the type,quantity and size of inclusions in annealed cold-rolled steel sheets of 50W600 non-oriented silicon steel before and after calcium treatment were systematically studied.Results showed that after calcium treatment(w(Ca) = 0.002 6%),calcium was mainly in the form of CaO·2Al2O3,CaO·6Al2O3 and dissolved calcium in steel at 1 600 ℃.Dissolved calcium could combine with sulfur to form CaS inclusions and compound CaS-MnS inclusions du... 

利用本钢技术中心试验厂技术手段,并与北京钢铁研究院合作,试制了用作家电用电机、微电机、小电机或部分中型电机铁芯的冷轧无取向电工钢。试制钢硅含量小于0.5%,钢板表面平滑,公称厚度0.5mm,且厚度均匀偏差小,性能测定结果表明,产品的磁性能、力学性能满足其使用要求。 BX STEELTechnology Center pilot plant using technical means,and with Beijing Iron and Steel Research Institute,trial cold rolled non-oriented electrical steel that has been used as appliance motor core,micro motor core,small motor core,or part of the medium-sized motor core。Trial steel of silicon content is less than 0.5%,steel plate surface is smooth,the nominal thickness of 0.5mm,and the thickness deviation is small,performance measurement results show that the magnetic properties,mechanical p... 

目前高磁感冷轧硅钢生产过程中，采用经验方法确定的乳化液流量设定值往往会造成硅钢产品的磁感性能达不到预期目标，针对此情况，基于轧机轧制机理研究了的乳化液流量数学模型，确定了乳化液流量设定值。实践表明，使用该数学模型输出的乳化液流量设定值，可提高轧制过程中乳化液流量控制精度，从而提高高磁感冷轧硅钢的轧制性能。 In view of the current production process of high magnetically inductive cold-rolled silicon steel, the mathematical model of emulsified fluid flow based on mill rolling mechanism is studied in view of the situation in which the magnetic sensing performance of silicon steel products is often not up to the expected target by using empirical method to determine the emulsified liquid flow setting. Practice shows that the emulsified fluid flow setting value output from this mathematical model improv... 

冷轧中中低牌号的无取向硅钢多采用万能凸度轧机(Universal crown mill,UCM)生产,其板形好坏受制于UCM轧机板形调节手段的协调使用。为掌握UCM轧机的板形控制特点,建立基于二维变厚度有限元的辊系弹性变形和基于三维差分的轧件塑性变形的六辊轧机耦合模型,对UCM轧机的板形调控性能进行详尽的分析,包括工作辊和中间辊弯辊、中间辊窜辊的调控功效、辊间接触压力分布等。在此基础上,提出可用指导生产的板形控制策略,指出UCM轧机在横向厚差控制方面的不足。针对工业生产中UCM轧机轧制无取向硅钢横向厚差大的问题,在大量仿真计算的基础上,开发具有高次曲线函数的边部变凸度(Edge variable crown,EVC)的工作辊。采用该工作辊后,各种品种的无取向硅钢的横向厚差不大于10μm的百分比由24%提高到99%,横向厚差的均值小于6μm,远小于之前的13μm。 Medium-low grade non-oriented silicon steel is rolled often by universal crown mill(UCM) during cold rolling.Its shape quality is dependent on the coordinated control of several shape adjustment devices of UCM.In order to understand the shape control characteristics of UCM,coupling model of six-high rolling mill,based on two-dimensional varying thickness finite element rolls elastic deformation model and three-dimensional finite difference strip plastic deformation model,is setup for the detaile... 

依据GB/T 15616—2008《金属及合金的电子探针定量分析方法》,采用电子探针波谱仪对某W600硅钢中的硅含量进行了定量测定,对影响其定量测定结果的不确定度分量进行了分析,并对不确定度的各个分量进行了计算和合成,最后给出了硅钢中硅含量测定结果的不确定度报告:该硅钢中的硅含量(质量分数)为1.50%,扩展不确定度U=0.20%,取包含因子k=2。 According to GB/T 15616-2008\"Quantitative Method for Electron Prohe Microanalysis of Metals and Alloys\",the quantitative results of Si content in some W600 silicon steel was measured hy EPMA-WDS.The uncertainty components which might affect the measurement results were considered,calculated and synthesized. Finally the uncertainty result for the quantitative value of Si content in the silicon steel was got.The mass content of Si was 1.50%,and expanded uncertainty U=0.20%under the condition of co... 

根据现场实际的生产控制情况,指出了热轧原料断面轮廓缺陷以一定的比列遗传给了冷轧带钢,分析了不同热轧原料断面轮廓对冷轧电工钢尺寸精度的具体影响,提出了相应的规律。并阐明了严格控制热轧原料断面轮廓形貌,对保证冷轧电工钢尺寸精度具有重大意义,对于中国现行的冷轧电工钢生产具有指导意义。 Based on the actual situation of production control,it was pointed out that the section profile defects of hot-rolled raw materials were geneticed to the cold-rolled strip.The specific impact analysis for the profile of different hot-rolled raw materials to the dimensional accuracy of cold-rolled silicon steel was analyzed.As a result, the corresponding orderliness are given;And the strict control to section profile of the hot-rolled material is of great significance to ensure the dimensional ac... 

本发明公开了一种提高超高磁感取向硅钢底层质量的退火隔离剂及其制备方法和应用。本发明所述退火隔离剂包括如下组分：MgO、TiO2、硼酸、Na2O、Sb2(SO4)3；以MgO质量为标准，其余各组分相对MgO的质量百分数为：TiO21.9～40％，硼酸0.05～0.1％，Na2O1～5％，Sb2(SO4)31～5％。本发明制备的退火隔离剂提高了超高磁感取向硅钢的成材率；提高了取向硅钢的底层附着性，降低了产品让步率；制备的超高磁感的取向硅钢可满足高容量变压器的使用要求。

本实用新型公开了一种取向电工钢生产用控温装置，涉及取向电工钢生产用控温技术领域，为解决现有控温装置中的温度检测装置需要蓄电池对其进行供电，不仅增大了能量消耗，也对环境造成影响的问题，所述输送机构上方并列等距固定安装有三个温度检测机构，且两个温度检测机构之间均设置有一个喷水降温机构，所述输送机构上方两侧固定安装有限位块，且限位块内部并列等距设置有四个电动伸缩器，一侧所述电动伸缩器前端固定安装有温差发电挡板，所述温度检测机构上方设置有接收器，且温度检测机构下方内部并列等距设置有红外线温度检测器。