分别采用传统冷轧轧制液和纳米TiO₂的冷轧轧制液,对无取向硅钢板进行了四辊冷轧实验.重点研究两种冷轧轧制液的轧制润滑性能和对轧后硅钢薄带表面质量和耐蚀性能的影响.通过场发射电子显微镜和能谱仪对使用两种轧制液轧后得到的硅钢薄带表面形貌和成分进行了分析.给出了轧制液中TiO₂纳米粒子在轧制过程中的抗磨减摩机理.在轧制载荷较高时,纳米TiO₂轧制液具有优良的轧制润滑性能并能显著改善轧后硅钢薄带的表面质量.同时在高载荷作用下,TiO₂纳米粒子被压入硅钢薄带基体,形成一个滑动系来支撑载荷,从而使润滑膜的耐磨性提高. Non-oriented silicon steel strips were rolled on a four-high cold rolling mill lubricated by a traditional cold rolling liquid and a nano-TiO₂ cold rolling liquid,with emphasis on studying the rolling lubrication performance of both the liquids and their effect on the surface quality and corrosion resisting property of the silicon steel strips.The surface micrograph and composition of the silicon steel strips after being rolled with both the liquids were characterized by field emissio... 

借助OM、激光共聚焦显微镜、质谱仪和电解萃取等设备和方法，研究了添加微量稀土La（质量分数0.001 1%）的取向硅钢在轧制前采用不同加热保温时间对抑制剂固溶行为的影响。结果表明：当稀土取向硅钢在1 250℃分别保温10、20、30 min后，试验钢晶粒尺寸随保温时间延长有先快后慢的长大趋势；三种抑制剂元素Mn、Cu和Al均发生固溶，保温时间对Mn和Cu两种元素的固溶影响明显，固溶量分别由69.8%和43.7%增加至84.2%和85.2%；随着保温时间的延长，稀土取向硅钢中抑制剂的小尺寸未溶物逐渐减少直至消失，较大尺寸未溶物（300～600 nm）逐渐转变为小尺寸未溶物逐步溶入基体中，数量减少且未溶物的类型由复杂逐渐转变为单一。 In this paper the solid solution behavior of the inhibitor under various holding time in 0.001 1 %La oriented silicon steel during reheating had been investigated by using OM, LM, methods of electrolytic extraction and mass spectrometer. The results showed that grain size of the test steel increased significantly with the holding time prolonging when the rare earth oriented silicon steel was heated to1 250 ℃ and held for 10, 20 min and 30 min respectively, and the growth trend slowed down after ... 

一种高硅钢材料的制备方法，步骤包括靶材、金属基材表面清理；排除密闭容器内空气、通保护气；双辉光等离子预轰击靶材和基材，净化表面；等离子溅射、加热、保温；缓慢冷却取出。预轰击靶材、基材，去除表面吸附层、活化基材，交替升高基材电压、靶材电压，使靶材中的合金元素被离子轰击而溅射出来、扩散进入基材内部形成表面高硅钢层。“双辉光等离子表面冶金技术”制备高硅钢的工艺简单易行、可控性高、成本低、无污染且基体和表面的结合力高，适合大规模产业化生产；更重要的是该方法采用交替离子轰击、扩渗速度快，结合强度高，得到硅含量均匀分布或呈梯度分布的高硅钢材料，为制备更高品质的无噪音、低铁损的高硅钢产业化奠定基础。

通过对辉光放电发射光谱参数的优化,以铁元素为内标来消除基体效应,建立了测定硅钢薄板中微量硼元素的方法。优化的实验参数为:放电电压1200 V,放电电流50 mA,预溅射时间40 s,积分时间10 s。校准曲线硼元素含量范围0.0001%~0.022%,相关系数大于0.999,测量结果与认定值一致,相对标准偏差小于10%。完全能够满足日常分析测试的要求。 A glow discharge optical emission spectrometry(GD-OES) method for determining trace boron element in silicon steel sheets were established through optimization of instrumental parameters and using Fe element as an internal standard to eliminate the matrix effect.The optimized instrumental parameters included discharge voltage,discharge current,pre-sputtering time and integration time,which are 1200 V,50 mA,40 s,and 10 s,respectively.The content of boron element that can be determined from the ca... 

某厂对电工钢的轧制策略进行了优化，粗轧道次由“1+5”改为“1+3”。在优化后的生产过程中，每次变换钢种，烫辊材就会出现窄尺现象，而紧随其后的电工钢板则出现超宽现象。文中针对该问题，介绍了宽度设定模型和宽度自适应模型的原理，阐述了该问题出现的原因及解决方案，并通过对宽度自适应模型的应用研究及优化攻关，有效地解决了问题，大幅提升了实物质量，降低了宽度封锁率。 The rolling strategy of electrical steel was optimized in a factory,and the rough rolling pass was changed from “1+5”to“1+3”.Subsequently,the following problems were occurred in the production process:when the steel grade changed,the roasting roller steel before the electrical steel appeared the narrow width phenomenon,and then the electrical steel appeared the ultra-wide phenomenon.This paper introduced the principle of width setting model and width adaptive model,and expounded the causes and s... 

本发明是高磁感取向硅钢的脱碳退火工艺，首先对硅钢卷进行放卷、活套、清洗；再对硅钢进行脱碳、渗氮处理，氨气流量6‑20m3/h、加湿槽温度30‑70℃，脱碳温度780‑880℃、机组速度45‑75m/min、气氛中氢气比例20‑60％、氮气比例40％‑80％，然后冷却到常温；对硅钢进行活套；再对硅钢进行涂覆氧化镁，涂覆量4‑10g/㎡；最后对硅钢进行干燥和收卷成硅钢卷；通过本发明对高磁感取向硅钢的脱碳退火工艺流程进行了优化设计，调整了脱碳退火工艺中氨气流量、气氛、加湿槽水温等参数，优化了高磁感取向硅钢中碳元素、氮元素和氧元素的含量，最终使高磁感取向硅钢实现稳定的性能，磁感达1.92T。

本实用新型公开了一种硅钢片绝缘测试装置，包括检测箱体、固定调节装置、探测装置和绝缘探测仪，所述固定调节装置、探测装置和绝缘探测仪设于检测箱体内，固定调节装置包括底座、支撑杆、放置板、夹板和夹持螺杆，所述支撑杆设于底座上，支撑杆上设有旋转腔，旋转腔内设有旋转电机，放置板旋转设于旋转腔上，旋转电机输出端设于放置板上，所述夹板滑动设于放置板两侧，夹持螺杆旋转设于放置板上；本实用新型属于绝缘测试领域，具体是一种通过固定调节装置可将硅钢片夹持固定，便于不同位置的调节，通过探测装置进行探测，并通过绝缘探测仪的检测于控制计算机将数据呈现和计算，减少手动操作，提高安全性的硅钢片绝缘测试装置。

本实用新型公开了一种取向硅钢二轧料氧化镁冷涂装置，包括主体，所述主体的中部安装有架体，且架体的右侧安装有冷涂机构，所述冷涂机构的右端一侧安装有液压气缸，且液压气缸的内壁连接有连接杆，所述架体的前后两端安装有调节架机构，所述调节架机构的表面安装有防护块，且防护块的内壁安装有橡皮套。该取向硅钢二轧料氧化镁冷涂装置设置有冷涂机构，且箱体通过安装有单独喷管和连接喷头，便于使用者两者兼合使用，可使用单独喷管也可连接喷头，使用者可根据自己使用的需求，对单独喷管和连接喷头进行针对性使用，单独喷管通过安装扣将连接喷头进行拼接使用，箱体通过旋转轴与支撑架的旋转，便于将箱体进行角度旋转。

【作者】 陈迪安； 李春生； ...

一种硅钢厂调功器故障报警自动复位的方法，包括：通过人机界面对炼钢炉温度进行设定，并在炼钢过程中实时获取炼钢炉温度；将炼钢炉实时温度与设定温度进行对比，当炼钢炉实时温度低于设定温度时，启动调节器；调节器输出功率使电阻带加热，使炼钢炉实时温度达到设定温度；当调节器发生故障时，调节器将故障信号发送给后台服务器，后台服务器根据故障指令，按预设规则控制与调节器连接的继电器，控制继电器按压复位按钮，使调节器自动复位。本发明解决了现有技术中通过电气人员来通过复位消除故障状态，耽误时间长，容易产生废品的问题。

近年来，在节能减排背景之下，国内外众多研究者对无取向电工钢磁性能的提升做了大量研究。为了探索无取向电工钢磁性能提升的方法，对锡或锑对无取向电工钢磁性能的作用机制(晶粒尺寸和晶体织构的控制)进行分析。基于该作用机制，介绍锡或锑的添加对无取向电工钢磁性能的影响。经研究发现，适量的锡或锑在晶界偏聚，不会阻碍晶界的移动并且致使晶粒尺寸降低；与此同时，锡或锑在晶界偏聚不仅抑制{111}织构在原始晶界处形核及生长，还降低(100)晶粒表面能，促进(100)晶粒生长。因此，适量添加锡或锑，可使无取向电工钢铁损下降、磁感提升。最后结合生产工艺，建议无取向电工钢的研究方向应为稀土含量对高牌号无取向硅钢夹杂物尺寸和数量分布的影响，锡或锑的添加量和常化工艺参数(常化时间、常化温度)对常化晶粒尺寸的影响。 In recent years, due to the background of energy saving and emission reduction, numerous researchers all around the world have done a lot of investigations on the improvement of magnetic properties for non-oriented electrical steel. In order to explore the method of improving the magnetic properties of non-oriented electrical steel, the mechanism of tin or antimony on the magnetic properties(the control of grain size and crystallographic texture) of non-oriented electrical steel is illuminated. ... 

本发明涉及一种低耗高效硅钢常化酸洗工艺及酸洗设备，其有效利用常化炉出口余温作为加热带钢的介质，使带钢与低温的酸液接触表面发生强烈的物理化学反应，快速酸洗剥离表层粗大的氧化铁皮，降低酸洗系统的酸液温度，通过调控溶液氧化还原特性提高酸洗效率去除残留的铁橄榄石，节约了能耗，同时取消了高投资高运行成本的抛丸工艺，实现了低耗高效硅钢常化酸洗的目的。