叠片系数是冷轧无取向电工钢的重要质量指标。为了提高叠片系数,必须保证无取向电工钢板形良好以及横向厚差小。针对攀钢冷轧厂4机架HC轧机轧制无取向电工钢的边部减薄问题,以无取向电工钢横向厚差最小作为目标函数,建立了一套针对无取向电工钢边部减薄控制的辊型曲线优化数学模型,开发了无取向电工钢专用辊型曲线,使无取向电工钢横向厚差从25μm降低到10μm以下,取得了良好的控制效果。 The lamination factor is an important quality index of non-oriented silicon steel strip.Considering the lamination factor,the non-oriented silicon steel must have a good shape and a smaller transverse thickness difference.In order to solve the edge thinning of non-oriented silicon steel strip in Panzhihua Steel,a mathematic model for designing the roll shape is built.In the model,the transverse thickness difference of non-oriented silicon steel strip is taken as the objective function.Based on t... 

本实用新型公开了硅钢片卷材加工用张力机构以及硅钢片剪切机，包括安装架、转动装置和按压装置，安装架的上安装块、连接块和下安装块组成凹槽，转动装置包括下转轴和转动驱动单元，下转轴水平设置，可转动地安装于下安装块上，设置于凹槽中，按压装置包括有上转轴和按压驱动单元，上转轴水平设置于下转轴的上方，可转动地安装于上安装块上，设置于凹槽中，并且可沿上安装块上下运动，其中，上转轴可与下转轴抵接。根据本实用新型的硅钢片卷材加工用张力机构以及硅钢片剪切机，可加强硅钢片卷材输送过程中的张力，降低硅钢片卷材输送的位置偏差率，提高产品合格率，提高原材料利用率，从而提高生产效率。

采用热模拟方法及EBSD技术,研究Fe-3 wt%Si电工钢在不同温度下组织的动、静态再结晶及晶粒取向特征,特别是少量奥氏体对铁素体动、静态再结晶组织及取向的影响。结果表明,不同温度形变的组织主要分三类:形变长条铁素体、珠光体和等轴细小铁素体。长条形变铁素体内发生动态回复或连续式的动态再结晶,奥氏体周围的铁素体动态再结晶加速,部分以传统的不连续方式动态再结晶。铁素体、奥氏体都可发生静态再结晶。奥氏体的静态再结晶在1050℃以上明显,铁素体的静态再结晶随温度的升高逐渐进行,最显著的再结晶发生在1050℃。不同温度形变的样品,其形变晶粒取向主要以<111>和<100>为主,小等轴铁素体晶粒除与大形变铁素体取向相近外,出现了<110>取向及其它取向。 Static and dynamic recrystallization and grain orientations in a hot-compressed Fe-3 wt% Si electrical steels were studied at different temperatures using Gleeble simulator and EBSD technique,particularly focusing on the effect of small amount of austenite on ferritic microstructure and orientations.The results show that microstructure of the compressed steel,depending on deformation temperature,consisted of elongated and deformed ferrite,pearlite and fine equal-axed ferrite.The elongated ferrit... 

对1990~2010年在我国申请的冷轧无取向硅钢涂层的专利数量、专利技术领域分布进行了统计,对典型涂层专利技术进行了分析,探讨了无取向硅钢涂层的发展趋势。统计分析结果表明,目前无取向硅钢涂层典型的专利技术主要有自粘结涂层、无铬含稀土元素涂层、含钼酸盐环保涂层及采用有机-无机纳米杂化材料为主成膜物形成的涂层等。无取向硅钢涂层发展的趋势主要是无铬环保的半无机、半有机型涂层。 The patent quantity of cold-rolled non-oriented silicon steel coating and distribution of technology fields applied in China in 1990-2010 were summarized.The analysis results indicate that typical patent technologies include self-adhesion coating,chromium-free and with rare earth element coating,environment-friendly and with molybdate coating,coatings with organic-inorganic hybrid materials as main forming agent and so on.The main development trends of coatings on silicon steel are among semi-in... 

【作者】 张煜； 朱国辉； ...

针对陶瓷辊表面结瘤清除时间长、清除效果差等缺陷,研究正反转陶瓷辊除瘤法,以缩短除瘤时间,增强除瘤效果。 The general removal of ceramic roller surface tumor costs a long time and the effect is poor.This paper probed into the ceramic roller tumor removal in order to shorten time and enhance the effect of eliminating. 

一种厚度≤0.15mm无取向硅钢带，其组分及wt%为：Si：2.0～6.5%，Mn：0.13～0.40%，S≤0.020%，P≤0.020%，Als：0.15～0.9%，C≤0.010%；工艺：经冶炼、浇注成坯后热轧至中间坯厚度；冷轧；常温脱脂；光亮罩式退火；经碱洗后涂覆；分条。本发明在保证铁损P1.0/400£13W/kg,磁感B2000³1.5T下，还使钢带厚度公差不超过±0.005mm,最小叠装系数³0.92完全满足连续冲制要求。

研究了硼酸对以Al(H2PO4)3为基料的无铬无取向硅钢绝缘涂层各项性能的影响。用盐雾实验、动电位极化及交流阻抗等试验手段研究了不同硼酸含量对硅钢绝缘涂层的耐蚀性和电化学行为的影响,同时采用SEM对涂层的表面形貌进行了研究。结果表明,硼酸含量为9.7%时,涂层的耐盐雾性及电化学性能最好;硼酸含量过少或过多时,涂层的耐蚀性和电化学性能都较差。 Influence of boric acid on the performance of chromium-free non-oriented silicon steel insulating coating based on aluminum dihydrogen phosphate was investigated.Salt spray experiment,potentiodynamic polarization and electrochemical impedance spectroscopy were used to study the influence of boric acid content on the corrosion resistance and electrochemical behavior of the insulation coating of silicon steel.Surface morphologies of the coatings were tested by SEM.Result shows that when the boric ... 

随着中国电工钢产量的增加,硅钢级氧化镁需求量不断增加,传统的以白云石为原料制备氧化镁的工艺已经无法满足市场需求。中国是一个卤水资源丰富的国家,因此,研究如何资源化综合利用盐湖资源变得越来越重要。硅钢级氧化镁是一种制备取向硅钢的涂层材料,主要用于取向硅钢高温退火处理阶段,起到隔离剂、绝缘膜层、脱硫、脱磷等作用。综述了制备硅钢级氧化镁的方法、工艺流程、研究进展及存在的问题,指出了硅钢级氧化镁制备技术的发展方向,并对中国卤水资源的利用提出了建议。 With the increasing output of electric steel,the demand for silicon steel grade magnesium oxide(MgO) is larger and larger in China,and the traditional MgO production process with dolomite as raw material has been unable to meet market demand.China is a brine resource-rich country,the study of how to comprehensively utilize salt lake resources has become increasingly important.As a coating material used for preparing oriented silicon steel,silicon steel grade MgO is mainly used in the process of ... 

1.本外观设计产品的名称：硅钢片。;2.本外观设计产品的用途：多片硅钢片用来共同组成马达的转子的其中一个部件。;3.本外观设计产品的设计要点：在于本外观设计产品的形状。;4.最能表明设计要点的图片或照片：立体图。;

本发明是改善硅钢边缘裂边的工艺，包括：S1：对普通取向硅钢卷进行放卷、活套、清洗、加热、冷却；S2：对硅钢进行收卷，收卷张力系数为3‑9kg/mm2；S3：对硅钢卷用收紧带收紧打包，打包带张力为3‑8kg；S4：罩式炉进行炉底板检测，炉底板不平度＜2mm；S5：将收紧打包后的硅钢卷送入罩式炉内进行高温退火处理；本发明的优点：通过调整取向硅钢材料生产过程中对CA线收卷张力的控制、CA收紧带的使用与控制、罩式炉炉底板的平整度，实现1200mm以上宽度材料平均不良切边宽度≤45mm，边部裂边尺寸减少40％。有效提高了加工材料成材率，提高了纵剪材料使用率，降低了吨钢成本，减少了纵剪生产停顿，提高了效率。

本发明公开了一种硅钢氧化镁废水回用处理与污泥资源化工艺，包括：预过滤：氧化镁废水进入过滤容器，过滤得到的水，返回调节池中，直至预过滤澄清；过滤过程：氧化镁废水在预过滤阶段逐渐澄清后进入过滤程序，产生的过滤水满足要求后，自流入产水箱；滤饼干燥：停止过滤后，将过滤容器中的水排空至调节池，之后按照与过滤相同的方向通压缩空气，通过压缩使滤饼干燥；反吹排泥：滤饼干燥完成后，通反向的压缩空气，之后进入下一个过滤周期；经过处理后，过滤阶段产生的合格水循环利用；滤饼干燥后进一步进行资源化处理。本发明实现了废水回用；产生的沉淀污泥经处理后可分别作为钛白粉的生产原料和土壤改良剂，具有良好的社会效益和环境效益。