研究了退火温度和退火时间对电沉积硅钢试样中的断面层组织、硅在试样中的分布情况、织构分布和磁性能的影响。结果表明:退火温度为1000℃、退火时间为210 min时得到的试样晶粒分布均匀、硅在试样中分布均匀、硅平均浓度为6.3715%(接近6.5%)。试样的织构分析及磁性能检测的结果表明,在较高温度下延长退火时间可增加{100}和{110}面织构,降低铁损,所得试样的磁性能较为良好。 The effect of annealing temperature and time on the microstructure, distribution of silicon,texture and magnetism of the high silicon steel prepared by electrodeposition was investigated. The results showed that after annealing at 1000℃ for 210 min, the mean grain size of steel was about 190 μm with a uniform grain size distribution, and the silicon is also uniformly distributed on the entire cross section with an average Si concentration 6.3715%(close to 6.5%); With the increasing annealing tim... 

无取向硅钢特别是中牌号以上的无取向硅钢,随着含硅量的提高,常温下塑性较差,冷轧过程中轧制力明显提高,如果存在原料质量问题,极易发生断带事故,影响硅钢冷轧过程的成材率和生产效率。通过优化冷轧工艺参数,可提高冷轧稳定性。生产中通过合理分配冷轧各道次压下量和轧制速度,保证了轧制过程的稳定,很大程度减少了冷轧断带事故的发生。 Non-oriented silicon steel, especially in the low and middle grade, with the increase of silicon content, plasticity is poor at room temperature, rolling force in cold rolling process significantly improved .If there is the quality defect of raw materials , easily sheet is rolling off. Affect finished product rate and production efficiency in process of cold-rolled silicon steel. Through optimization of cold rolled process parameter , improve the stability of cold-rolling process. Through reason... 

本实用新型公开了一种汽轮发电机定子硅钢片压紧装置，包括基座，所述基座上设置有左支撑架与右支撑架，所述左支撑架通过螺丝安装固定于基座顶部左侧，所述右支撑架通过螺丝安装固定于基座顶部右侧。本实用新型可轻松对发电机定子硅钢片进行压紧操作，便于后期螺母装配。

本实用新型公开了超薄硅钢铁芯卷绕张力控制装置和纠偏装置，包括工作台、固定架和底座，工作台的顶部安装有固定架，所述工作台的底部设置有按压杆组件，所述按压杆组件的底部连接有底座，所述工作台顶部的前端和尾端均安装有固定板，所述固定板的内壁设置有收捆轴，所述工作台的顶部安装有滑轨板，且滑轨板位于固定板的内侧。本实用新型通过导向辊和衔接板的设置，工作人员在使用时，根据收捆轴上铁芯的缠绕位置，对两侧导向辊进行调节，从而通过导向辊的转动性对铁芯的活动起到定位作用，两侧导向辊的主要作用是起到带料输送出来时的导向作用，能够保证带料快速平稳的送料时不发生跑偏现象。

本发明公开了一种取向硅钢产品的在线性能判级与精确分切装置和方法，使得同一个分卷上的性能分布均匀，避免分卷出现性能废品或多个性能等级的情况，提高分卷性能稳定性。提供的一种取向硅钢产品的在线性能判级与精准分切方法包括生产数据采集、铁损曲线自学习、数据存储、性能在线判级、缺陷数据采集、缺陷判级、智能分切等模块，依据修正后的磁性能全长数据，得到产品的性能判级结果，结合表面缺陷判级结果，综合确定分切位置，制定最佳分切方案。本发明可以实现取向硅钢生产过程中的性能在线判级和精准分切，得到性能均匀、表面质量好的分卷，减少分卷性能不稳定带来的损失。

本实用新型公开了一种用于硅钢片叠装的工装，包括安装底座，所述安装底座上设置有限位装置，所述限位装置包括多个水平限位柱和多个竖直限位柱；各个水平限位柱之间的缝隙的尺寸等于其对应放置的硅钢片的宽度，各个竖直限位柱与安装底座的底边之间的距离等于其对应放置的硅钢片的总长度；所述各个竖直限位柱设置在各个水平限位柱之间的缝隙所正对的位置；采用多个水平限位柱和多个竖直限位柱进行水平和竖直方向上均对硅钢片进行定位；使用此工装叠装出来的成品，长短一致，侧面相当整齐；本实用新型，结构简单，操作方便。

【作者】 汤婧； ...

本实用新型涉及一种硅钢片叠压精准定位设备，包括压台、压板和仿形燕尾键，所述压台上开有与仿形燕尾键下端相对的限位槽，所述压板设置与压台上方，所述压板上开有与仿形燕尾键上端相对的限位孔。本技术方案当硅钢片叠放压合之后，仿形燕尾键可以去除，并能够在硅钢片组成的铁芯上形成燕尾槽，用于后期燕尾键的组装，且能够保证燕尾槽内的结构规则，便于后期燕尾键组装。

对新能源汽车以及驱动电机的现有市场和未来市场规模进行梳理分析，通过自建计算公式推导出我国2021年1-11月份驱动电机用电工钢的总量，进而预测未来10年中国新能源汽车驱动电机用电工钢情况，为无取向电工钢的生产和在电机中的应用提供有价值的参考。 The current market and future market size of new energy vehicles and traction motors were analyzed,and the total amount of electrical steels used in traction motors in China from January to November 2021 was derived by using self-built calculation formulas,and then the situation in the next ten years of electrical steel used in traction motors of new energy vehicles in China was predicted.It will provide a valuable reference for the production of non-grain oriented electrical steel and its appli... 

简要介绍了宝钢无取向电工钢的发展历程、产品大纲、电磁性能控制情况,以及高附加值新产品的开发、应用情况。概述了近年来宝钢无取向电工钢生产技术进步,主要包括夹杂物控制技术、连轧机高牌号硅钢制造技术、同板差控制技术、环保涂层开发技术等。 This paper briefly summarizes the development history, product catalogue, and magnetic properties of non-oriented electrical steel sheets at Baosteel, as well as the development and application of high-value-added steel grades. Recent advances in manufacturing electrical steel sheets are also introduced, including technologies for controlling inclusion, producing high-grade steel strips by a tandem rolling mill, and controlling the transverse thickness difference of steel sheets, as well as the ... 

本发明一种基于冷轧全流程数据的硅钢铁损预测方法，其对冷轧硅钢进行全流程物料跟踪，以基于聚类算法分类，并选取代表性工艺作为神经网络的训练集来对冷轧硅钢铁损进行预测，以探明冷轧各机组工艺对冷轧硅钢铁损的影响。

观察了取向硅钢极薄带经冷轧至不同厚度,并经过不同工艺热处理后的显微组织及亚结构。结果表明:冷轧压下量越大,显微组织中位错密度越高,冷变形组织越多,等轴晶粒越少;增加冷轧压下量可以使试样的再结晶温度降低,当钢带厚度为0.08 mm时,在650℃退火时就能发生明显的再结晶。 Microstructure and substructure of the grain oriented ultra-thin silicon steel sheets is analyzed,which are rolled down to different thickness and treated with different heat treatment process.The result shows that there are higher dislocation density,more cold deformation structure and less equiaxed crystal grain in microstructure of the steel sheets with more cold rolled reduction.Increase of cold rolled reduction will decrease recrystallization temperature,and when thickness of the steel shee...