硅钢资料

本发明公开了一种低磁场条件下高磁感应强度无取向电工钢及生产方法，步骤包括：冶炼：炼钢、连铸生产铸坯，所述铸坯中：以质量百分比计，Si2.0％、Mn0.2‑0.5％、ALs0.3‑0.6％、N≤0.002％、S≤0.002％、Ca≤0.001％，余量为Fe及不可避免的杂质；板坯热轧、卷取；常化处理；退火处理。本发明通过合理的电工钢成分设定、生产工艺、稳定的控制精度，从一贯制角度对产品进行设计及控制，最终能够保证产品质量稳定、具有低磁场条件下高磁感应强度的Si含量2％的0.35mm厚度无取向电工钢产品。

通过试验确定氩气分析流量为3.5L/min,静态流量为0.75L/min,冲洗时间为3s,预燃时间为12s,积分时间为5s的激发条件,采用火花源原子发射光谱法测定取向硅钢中碳、硅、锰、磷、硫。分别采用铣床铣样、砂轮磨样两种制样方式进行了精密度考察,发现制样方式对结果影响不大;讨论了取向硅钢样品中碳、硅、锰、磷、硫测定时可能存在的共存元素干扰,发现硅对锰元素的干扰不可忽略,采用干扰系数法进行了校正,据此拟合得到各元素校准曲线的相关系数均在0.999 0以上。精密度考察结果表明,碳、硅、锰、磷、硫的相对标准偏差(n=10)在0.71%~9.4%之间。对两块取向硅钢生产样品进行分析,并与钢铁研究总院进行比对分析,结果一致,且偏差均在允许范围内。 Carbon,silicon,manganese,phosphorus and sulfur in oriented silicon steel were determined by spark source atomic emission spectrometry.The selected excitation conditions were as follows:the analytical flow rate of argon was 3.5L/min,the static flow rate was 0.75L/min,the flush time was3s,the precombustion time was 12sand the integration time was 5s.Two sample preparation methods,including milling machine and grinding wheel,were investigated.The precision test results showed that,the determination... 

本发明特别涉及一种控制边部翘皮的热轧电工钢的生产方法和生产系统，属于钢表面质量检测技术领域，方法包括：建立热轧电工钢边部翘皮的数据库，数据库包括翘皮类型及各翘皮类型的翘皮发生原因和翘皮发生的区域；对待质检的热轧电工钢表面进行识别，并对比数据库，获得待质检的热轧电工钢表面翘皮的翘皮类型；根据待质检的热轧电工钢表面翘皮的俏皮类型获得该类型翘皮的翘皮发生原因和翘皮发生的区域；根据翘皮发生原因和翘皮发生的区域，调整生产操作，用以减少热轧电工钢的边部翘皮；通过对边部翘皮进行准确分类及识别，能够准确的分辨出边部翘皮的产生原因，采取有针对性的措施防止缺陷扩大，最大程度的降低缺陷发生量，提高质量控制水平。

本发明属于硅钢制造技术领域，具体涉及一种改善硅钢热轧板边部质量的加工方法，包括：连铸、铸坯预变形处理、铸坯加热处理和热轧处理；其中，所述铸坯预变形处理包括：在所述铸坯的温度为500～900℃下，对所述铸坯的沿长度方向的两侧壁通过立辊施加压力，直至形变量h为10～50mm；所述铸坯加热处理的加热温度为1100～1200℃，保温时间为4～6h。本发明提供的改善硅钢热轧板边部质量的加工方法，采用铸坯两侧壁的侧压工艺，有效解决了热轧板边部裂纹的缺陷，提高了边部塑性，提高了成材率并降低了生产成本。

本发明涉及一种永磁电机铁芯电工钢材料优化匹配方法及系统，涉及电机技术领域，包括根据永磁电机的应用场合，确定设计指标和永磁电机模型，并根据永磁电机模型确定电机性能；判断永磁电机的电机性能是否符合设计指标，若是确定第一集合、第二集合以及第三集合的交集；该交集的元素为永磁电机的电机性能满足第一指标、第二指标以及第三指标时对应的硅钢材料。本发明综合考虑了电机的电磁场、温度场、应力场性能，可以在多种电工钢材料中选出与该种转子结构匹配度最高的电工钢材料。

本发明属于硅钢制备技术领域，具体涉及一种无底层取向硅钢的制备方法。其中，所述脱碳退火的过程中，带钢表层的氧化膜厚度为1.5～2.5μm；所述氧化膜中Si元素和Fe元素的原子重量比满足：Si/(Si+Fe)≥0.76；所述高温退火的过程中，冷却段依次包括：在温度为1200～500℃时，罩内冷却；其中，保护气体为包括有氮气和氢气的混合气体，所述混合气体中氢气的体积百分比＞3％；在温度为500～200℃时，罩内冷却；其中，保护气体为氮气；在温度＜200℃时，揭开内罩进行空气冷却。本发明提供的无底层取向硅钢的制备方法中，通过控制带钢在脱碳退火阶段的氧化膜厚度以及高温退火的冷却段等一些工艺，从而得到了表面光洁化好、表面均质化好、成材率高、磁性能优良的无底层取向硅钢。

轧制力是影响冷轧带钢厚度精度的关键因素。为实现高精度的冷轧带钢厚度控制,通过优化变形抗力模型参数和摩擦系数模型参数提高冷轧轧制力模型计算精度,并使用指数平滑法的自学习算法保证轧制力精度的稳定性。在首钢股份公司迁安钢铁公司20辊森基米尔轧机生产线进行S12硅钢钢种轧制力优化试验,将优化的模型参数应用于L2并投入现场生产,结果表明该优化方法不仅提高了轧制力设定精度,而且减小了冷轧硅钢的厚度超差长度,提高了成材率。 The rolling force is the key factor which influences the accuracy of cold-rolling strip thickness. To implement high precision control of cold-rolling strip thickness,we optimize the deformation resistance model parameters and friction coefficient model parameters to improve the calculation precision of cold-rolling force model,and use exponential smoothing self-learn algorithm to ensure the stability of rolling force accuracy. In Shougang Qiangang 20-high Sendzimir mill single stand production ... 

根据现场实际的生产控制情况,指出了热轧原料断面轮廓缺陷以一定的比列遗传给了冷轧带钢,分析了不同热轧原料断面轮廓对冷轧电工钢尺寸精度的具体影响,提出了相应的规律。并阐明了严格控制热轧原料断面轮廓形貌,对保证冷轧电工钢尺寸精度具有重大意义,对于中国现行的冷轧电工钢生产具有指导意义。 Based on the actual situation of production control,it was pointed out that the section profile defects of hot-rolled raw materials were geneticed to the cold-rolled strip.The specific impact analysis for the profile of different hot-rolled raw materials to the dimensional accuracy of cold-rolled silicon steel was analyzed.As a result, the corresponding orderliness are given;And the strict control to section profile of the hot-rolled material is of great significance to ensure the dimensional ac... 

本发明特别涉及一种中频用取向硅钢极薄带及其钢基板的制备方法，属于硅钢极薄带制备技术领域，方法包括：将硅钢原料进行冷轧，获得硅钢薄带；将硅钢薄带进行退火，退火采用至少3段式连续退火工艺，获得钢基板；采用本法制得的钢基板制备的中频用取向硅钢极薄带具备优良的磁性能和板形，采用多段式退火，获得稳定的成品性能，制造工艺简单，可实施性高，采用无底层取向硅钢作为母材，节能环保，产品表面质量好，产品可满足中频条件下(≧400Hz)的使用要求。

本发明涉及取向硅钢技术领域，尤其涉及一种取向硅钢边浪的控制方法、装置、设备和存储介质，该方法包括：在将通过脱碳退火阶段的取向硅钢的带钢进行卷取过程中，在带钢的下端侧上刻上刻痕线，其中，下端侧为带钢与高温退火炉的承托底板接触的一侧，刻痕线平行于带钢轧制的方向；控制卷取后的带钢通过高温退火阶段和热拉伸平整阶段后至精整阶段时，沿着刻痕线，切除带刚的边浪；其中，边浪为在带钢的刻痕线至下端侧的边的部分。该控制方法可显著改善高温退火后取向硅钢边部浪形，有效降低精整切边量，提高取向硅钢的板形质量及成材率，降低生产成本。

本发明公开了一种取向硅钢高温退火底板，涉及钢卷生产技术领域，解决了钢卷的尺寸变形导致钢卷切边量过大的技术问题。包括应变诱导板，应变诱导板的板面开设有若干凹槽，相邻凹槽之间于应变诱导板的板面形成凸楞，钢卷放置于应变诱导板的板面上，其中部分的钢卷端面支撑于凸楞上，其余的钢卷端面悬置于凹槽上。本发明通过在应变诱导板上设置凹槽与凸楞，钢卷在高温退火过程中同样受重力产生蠕变变形，但蠕变变形按照凸楞所设定的方向进行，从而将产生的不均匀的“大浪”分割成碎化均匀的“细浪”，使得钢卷边部的变形细小、均匀、可控，从而降低了大象脚变形的缺陷影响程度，减小了钢卷的切边量，提高了成材率，同时能够获得良好的边部板形。

无取向硅钢的磁性能主要取决于铁素体的晶粒尺寸、晶体织构和钢中的夹杂物。通过合适的化学成分设计以及采用适宜的夹杂物控制技术,可以获得最佳的夹杂物控制效果,使其纯净度大幅度提高或者无害,最终获得磁性能优良的高级别无取向硅钢。同时,为满足节能、环保、高效需求,无取向硅钢正朝着节能降耗、环境友好以及多功能、高效率、易加工等方向发展。 The magnetic properties of non-oriented silicon steel mainly depend on the grain size of ferrite,the crystallographic texture,and the inclusions in the steel.The optimum inclusion control effects can be obtained through a suitable chemical composition design and an appropriate inclusion control technique,and then the liquid steel will get be clean or the inclusion will get be harmless,finally the excellent magnetic property of the non-oriented silicon steel can be obtained.Meanwhile,in order to ...