测试了高强无取向电工钢的S-N曲线,并借助光学显微镜、扫描电子显微镜、透射电子显微镜分析了实验钢组织,疲劳断口形貌和位错结构。结果表明:室温条件下,频率为20Hz,应力比R为0.1,循环10~7周次时,实验钢的疲劳强度为360MPa,疲劳裂纹萌生于实验钢的次表面,裂纹萌生点附近有沿晶开裂现象,疲劳裂纹扩展区域有解理台阶与疲劳条纹,瞬间断裂区是韧性断裂,有大量韧窝。实验钢在循环应力作用下基体中产生了大量位错,并有驻留滑移带终止在晶界位置。 The S-N curve of a high strength non-oriented electrical steel was tested.The microstructure and fatigue fracture morphology and dislocation were analyzed by optical microscope,scanning electron microscope,transmission electron microscope.The results showed that:at room temperature and the frequency of 20 Hz and the stress ratio Rof 0.1,the fatigue strength of the experimental steel was 360 MPa when the cycle was 10~7 cycles.The fatigue crack initiation at the surface of the steel and the interg... 

无取向硅钢特别是中牌号以上的无取向硅钢,随着含硅量的提高,常温下塑性较差,冷轧过程中轧制力明显提高,如果存在原料质量问题,极易发生断带事故,影响硅钢冷轧过程的成材率和生产效率。通过优化冷轧工艺参数,可提高冷轧稳定性。生产中通过合理分配冷轧各道次压下量和轧制速度,保证了轧制过程的稳定,很大程度减少了冷轧断带事故的发生。 Non-oriented silicon steel, especially in the low and middle grade, with the increase of silicon content, plasticity is poor at room temperature, rolling force in cold rolling process significantly improved .If there is the quality defect of raw materials , easily sheet is rolling off. Affect finished product rate and production efficiency in process of cold-rolled silicon steel. Through optimization of cold rolled process parameter , improve the stability of cold-rolling process. Through reason... 

本实用新型涉及卷绕机技术领域，且公开了一种硅钢片卷绕机连接调节机构，包括两个支撑板，两个支撑板的顶部之间水平固定连接有横板，两个支撑板的下端均开设有安装口，两个安装口之间水平设有安装板，安装板的底部两端均垂直连接有驱动液压缸，驱动液压缸的底部分别连接在对应位置处的安装口内；安装板的一侧开设有条形口，条形口内水平连接有若干支撑杆，条形口的两端底部均垂直连接有固定板，两个固定板之间水平连接有若干横杆，横杆上沿长度方向等距设有若干移动座，移动座的顶部垂直连接有分隔板。本实用新型设置的分隔板可对硅钢带进行分隔，且设置的剪切刀向下对硅钢带进行切割，提高了装置的实用性。

为了解决在纹理背景下冷轧硅钢表面缺陷的分割问题,提出了基于局部信息结构张量和活动轮廓模型的硅钢表面缺陷分割方法。将图像的局部信息引入到结构张量中;在结构张量提取的特征空间中,以KL距离作为区域的概率密度相似性度量建立分割图像的活动轮廓模型;采用Split-Bregman数值解法对模型进行求解。运用提出的分割方法对硅钢表面的一些常见缺陷如纵向划伤、横向划伤、异物和孔洞等进行分割实验。实验结果表明,该方法可以准确地分割出硅钢表面缺陷区域,验证了该方法的有效性。 In order to address the segmentation problem for cold rolled silicon steel surface defect based on the texture background,a novel method based on structure tensor and active contour model is proposed.Image local information is introduced to the structure tensor.In the extracted feature space of structure tensor,KL distance is treated as a regional similarity measure of the probability density to establish active contour model for image segmentation.The numerical solution of Split-Bregman is used... 

本文介绍了无取向硅钢C6涂液的性能,研究了配水量、固化程度和涂层厚度等因素对无取向硅钢C6涂层性能的影响。结果表明,随着配水量的增加,完全固化所需的时间增加,涂液固体含量降低,涂层厚度减小;随着固化程度的提高,涂层硬度先增大然后趋于恒定,而柔韧性逐渐变差,在过固化后急剧恶化;涂层厚度对涂层的表面外观、附着性和绝缘层间电阻均有显著影响。 Based on the introduction about the performance of C6 varnish for non-oriented silicon steel sheets,effects of water amount,curing degree and coating thickness are discussed. Results show that with the increase of water amount,the time required to cure completely extends,and both the solid content of C6 varnish and the coating thickness decrease. As the curing degree increases,the hardness of the coating increases first and then tends to be constant,however the flexibility degenerates,especially... 

简述了无取向硅钢环保涂层发展背景,分析了硅钢环保涂层的特点及国内、外研究进展,提出了硅钢保涂层下一步的发展方向。 The back ground of environmental protection coating of non-oriented silicon steel was described in this paper.The characteristics and study progress in domestic and foreign of environmental protection coating of non-oriented silicon steel were analysised.The next development direction of environmental protection coating of non-oriented silicon steel was put forward. 

【作者】 谌剑； ...

本实用新型涉及硅钢片铁芯性能测试技术领域，公开了CD型硅钢片铁芯性能测试工装，包括：机台，上部后侧固定有竖直向上的后侧板；托板，水平设置在所述机台上方；夹持机构，设置在所述机台上，所述夹持机构包括：第二气缸，其驱动杆端部固定套接有夹持块，夹持块外端部固定有橡胶缓冲块；橡胶垫，固定在所述托板右侧上部。本实用新型通过设置第一气缸驱动连接于托板，可以先根据硅钢片的厚度，通过操作气缸控制器控制第一气缸工作带动托板在机台上进行升降高度，从而调整托板与夹持块的高度差，提高装置的实用性和广泛性，较为实用，适合广泛推广和使用。

本实用新型涉及变压器材料检测技术领域，具体为一种硅钢片检测装置，包括材料检测装置主体，材料检测装置主体包括相互连接的铁损测试仪主机及磁导计，磁导计的顶端设置有清洁机构，清洁机构包括固定盒、拉块及刷块，固定盒固接于磁导计上，拉块插设于固定盒中、能够在固定盒中上下移动，固定盒的内部底面上及拉块的底端上分别安装有刷块，铁损测试仪主机上还设有束线机构。本实用新型使得用户可在检测硅钢片前，对硅钢片两面沾染的灰尘污渍进行擦拭，避免灰尘污渍影响对硅钢片的测定结果，可方便地对刷块进行清洁更换，使得用户可方便地对电源线和导线进行收纳。

本实用新型涉及变压器铁芯制备的技术领域，特别是涉及一种变压器铁芯制备用硅钢片涂漆设备，其满足不同身高的操作人员对装置的操作要求，提高装置的实用性；包括工作台、喷涂机构和输送机构，喷涂机构和输送机构均安装在工作台顶端，输送机构上设置有烘干机构；还包括固定板、支腿、连接板和升降机构，四组支腿呈四角分布安装在固定板底端，连接板横向安装在四组支腿之间，升降机构安装在固定板上；升降机构包括电机、电机座、支杆、第一连接杆、滑套、限位板、丝杆螺母、丝杠和花键轴，电机安装在电机座上，电机座安装在连接板顶端，四组支杆呈四角分布安装在工作台底端，四组第一连接杆呈四角分布安装在固定板顶端。

本发明涉及一种冷连轧法生产无取向高硅钢的方法，RH真空脱碳处理后，铝脱氧及部分铝合金化，合金化后大罐钢水净循环大于3次或大于5分钟；熔炼合格钢水至连铸开浇前静置时间大于二十分钟；控制过热度5～15℃；采用电磁搅拌，控制等轴晶比例45％以上；3)热轧工序板坯装炉温度大于750℃；常化使晶粒尺寸在90～110μm范围内；连续退火炉加热段温度设定950～1150℃，均热段温度设定900～1050℃，全氮气干气氛保护，控制晶粒尺寸120～170μm。生产全过程中的热履历参数控制，充分发挥设计的微合金元素功能，改变析出物的组成、大小、形态及分布。

日本住友金属成功地开发了一种资源节约型高强度无取向电工钢SXRC,这种电工钢是通过固溶铌适度抑制位错的合并对消而得到一种特殊的微观组织,因此兼具很高的力学性能和磁性,特别适用于HEV、EV驱动电机转子。而且,不使用昂贵的镍就可以达到期望的强度,合金成本可控,是一种优越的资源节约型产品。 Sumitomo metal industries ltd of Japan successfully developed a type of high strength non-orientation electrical steel SXRC of resources-saving.The steel has both high mechanical performance and good magnetic property thanks to the special microstructure produced by the formation of Nb solid solution serving to appropriately inhibit the combination and cancellation of dislocations.The material is,in particular,suitable for manufacturing rotors of HEV and EV driving motors.Besides,expected streng...