硅钢资料

本发明公开了一种取向硅钢微观织构EBSD试样制样方法，包括：1)取样，采用线切割机制取向硅钢试样；2)制样，采用热镶嵌机镶制取向硅钢试样，按照常规方法进行粗磨、细磨、抛光、清洗、吹干；采用240目、400目、600目氧、800目、1000、2000目氧化铝砂纸对试样依次进行一次打磨处理；采用5.0um高效金刚石抛光剂对试样进行抛光处理；3)电解抛光，取向硅钢试样机械抛光后再进行电解抛光。

本发明涉及一种硅钢片纵剪边料收卷装置，包括：用于将收卷装置固定于地面的机架底座，机架底座一端设置固定支架，固定支架上安装电动定尺收料盘；在机架底座上设置电动可移动支架，电动可移动支架在机架底座的长方向上相对固定支架移动，电动可移动支架上安装电动可调收料盘；电动可移动支架、电动定尺收料盘、电动可调收料盘与PLC控制系统连接，PLC控制系统用于控制电动可移动支架的移动距离、以及控制电动定尺收料盘和电动可调收料盘的收料速度。本发明还涉及一种硅钢片纵剪边料收卷方法。将本发明的收卷装置安装在硅钢片滚剪线切刀后面的输送平台下部，卧式布局，不占用外部空间，和滚剪线无缝集成在一起，自动完成硅钢片纵剪边料收卷工作。

对碳-锰-硅钢进行不同配分温度的Q&P(Quenching and Partitioning)处理,测试了热处理后不同钢的力学性能和残余奥氏体含量,并用扫描电子显微镜和透射电镜观察其显微组织,分析了配分温度对显微组织和力学性能的影响。结果表明:试验钢显微组织基本由低碳板条状马氏体、块状铁素体和条状残余奥氏体组成;随配分温度的升高,试验钢的抗拉强度呈下降趋势,伸长率与奥氏体含量的变化趋势相同,但变化规律不确定;提高锰含量能稳定残余奥氏体,从而提高试验钢的伸长率,并使伸长率对配分温度不敏感。 The C-Mn-Si steel was quenched and partitioned at different partitioning temperatures,the mechanical properties and residual austenite contents were investigated,the microstructure was observed by SEM and TEM,and the effect of partitioning temperature on microstructure and mechanical properties was analyzed.The results show that the microstructure of the tested steel consisted of lath martensite with low carbon,nubby ferrite and banded residual austenite.The tensile strength of the tested steel ... 

本发明公开了一种轻便电动自行车轮毂电机用无取向电工钢及制造方法，属于无取向钢领域。针对现有小型电机无取向钢加工难度大，效率低的问题，本发明提供一种轻便电动自行车轮毂电机用无取向电工钢，包括如下重量百分比的各组分：Si：1.50％～3.00％；Als：0.50％～2.00％；Mn：0.20％～1.00％；P：0.01％～0.20％；C：≤0.005％S：≤0.03％；N：≤0.03％；Ti：≤0.005％,其余为铁和不可避免的杂质；其中C、S、N和Ti的重量百分比满足下式：C％+S％+N％+Ti％≤0.01％。本发明通过合理控制元素含量提高硅钢的延塑性，便于加工。本发明提供的制造方法降低卷绕铁芯中的涡流和磁滞损耗，同时能够避免钢卷表面氧化和表面氮化物析出，降低铁芯损耗，与现有同铁损级别无取向硅钢相比延伸率较高，后续冷加工性能更加优异。在保证优良性能的同时便于加工。

本申请提供了涂布的晶粒取向电工钢板及其生产方法。在一个示例性实施方案中，所述方法包括生产具有约2.5至约4重量％的硅、约0.005至约0.1重量％的碳和约90至约97.5重量％的铁的熔融钢。将熔融钢浇铸成板坯并且然后冷轧成具有表面的板。使用脱碳退火对板进行脱碳，然后使用重结晶退火进行重结晶以生产晶粒取向电工钢。施加涂层覆盖所述表面，其中所述涂层包括有机可辐射固化交联剂和光引发剂。通过将涂层暴露于辐射源来固化涂层。

本发明公开了一种超薄取向硅钢用的半有机绝缘涂料。该半有机绝缘涂料，按质量百分比计，包括以下组分：10～25％磷酸盐，1～10％含有环氧基的硅烷耦合剂，0.2～2.0％有机硅烷，1～10％铬酐，1.5～6％二氧化硅粒子，0.3～5％碱，余量为水；其中二氧化硅粒子的粒径为100～300nm。该半有机绝缘涂料应用于超薄取向硅钢表面时，既提高了涂层与基体的附着性，又保证了涂层的绝缘性和耐热性，涂层附着性为A级，叠片系数大于0.96，可耐900℃高温，并且涂层较薄(小于1μm)时，钢板的绝缘电阻大于30Ω·cm2/片，绝缘性能优异，可满足超薄取向硅钢的应用需求。

对1990~2010年在我国申请的冷轧无取向硅钢涂层的专利数量、专利技术领域分布进行了统计,对典型涂层专利技术进行了分析,探讨了无取向硅钢涂层的发展趋势。统计分析结果表明,目前无取向硅钢涂层典型的专利技术主要有自粘结涂层、无铬含稀土元素涂层、含钼酸盐环保涂层及采用有机-无机纳米杂化材料为主成膜物形成的涂层等。无取向硅钢涂层发展的趋势主要是无铬环保的半无机、半有机型涂层。 The patent quantity of cold-rolled non-oriented silicon steel coating and distribution of technology fields applied in China in 1990-2010 were summarized.The analysis results indicate that typical patent technologies include self-adhesion coating,chromium-free and with rare earth element coating,environment-friendly and with molybdate coating,coatings with organic-inorganic hybrid materials as main forming agent and so on.The main development trends of coatings on silicon steel are among semi-in... 

在Gleeble-3500热/力模拟试验机上对HW600钢进行高温压缩试验,研究在不同试验条件下的变形抗力。试验结果表明:变形温度对变形抗力的影响最为显著,在相同的变形速率下,随着变形温度的升高,变形抗力降低;在同一变形温度下,变形速率增大,变形抗力增加;在同一变形温度、变形速率下,随着变形程度的增加,变形抗力急剧增大,真应变达到0.1后,变形抗力增加趋势变缓。 The high-temperature compression test is done for HW600 steel with Gleeble-3500 thermal simulation testing machine to research its resistance to deformation under different test conditions.It is showed from result that deformation temperature has greatest effect on the resistance,and along with the temperature getting higher the resistance lowered under same deformation rate;the resistance increases along with deformation rate getting greater under same temperature;and under same deformation tem... 

本发明提供一种提高硅锰镇静硅钢浇注性的生产方法，属于钢铁冶炼技术领域。其生产流程包括：转炉冶炼→RH真空精炼→连铸。转炉出钢严格控制下渣量，加石灰、渣面脱氧剂调渣；RH真空精炼脱碳结束后，先加入低碳低硫硅铁脱氧，再加入金属锰、磷铁等进行合金化，同时向钢包渣面加入低碳钢渣面脱氧剂对炉渣进行改质，待钢水成分全部命中后加入钙镁铁合金，循环3‑5min后净循环处理6‑10min，破空出钢；连铸采取保护浇注，浇注过程选用塞棒头中Al2O3≥80％、C≤10％、SiC含量8‑15％、气孔率≤12％，质量密度≥2.9g/cm3的塞棒进行控流，连浇炉数≥15炉/中包。本发明可以显著改善浇注过程塞棒头侵蚀问题，提高连浇炉数，降低生产成本。

【作者】 吴玉美； 陆晔； ...

本实用新型公开了一种用于硅钢绝缘涂料生产的吸尘装置，包括底板、支撑平台和集尘箱，所述底板底端四角处通过螺栓连接固定有可制动万向轮，所述底板上端四角处焊接有导向套。有益效果在于：本实用新型通过设置真空泵、集尘箱、万向吸气臂、吸尘罩以及活性炭滤网，可在硅钢绝缘涂料生产过程中将逸出的物料粉尘进行有效的收集，确保硅钢绝缘涂料生产环境的洁净，有利于人体健康，通过设置电机、螺套、螺杆、导向柱以及导向套，可实现根据实际吸尘的需要实现装置高度的便捷调节，提高了装置的实用性。

就冷轧硅钢废水处理生产中面临的主要问题进行分析,从技术角度及运行管理角度提出工艺优化升级改进措施及应对策略;同时从后续深度处理,逐步实现零排放目标的角度进行探讨,为冷轧硅钢废水减量化、出路乃至废水零排放提供一些思路。 The main problems in the wastewater treatment process of cold-rolled silicon steel lines are analyzed and process upgrading measures and optimization strategy are put forward from both technical and management views.At the same time,downstream deep treatment to gradually achieve the target of zero discharge is discussed,to provide some ideas for reduction or even zero discharge of wastewater from cold-rolled silicon steel lines.