低温取向硅钢热轧析出物与织构的研究
采用低温板坯加热制备取向硅钢,通过透射电镜(TEM)观察并研究热轧板中的析出物,用ODF织构法研究热轧板距表面1/8、1/4和1/2处的织构分布。结果表明,热轧板中的析出物主要是密排六方AlN,AlN形貌呈规则长方形,AlN颗粒大小不等,分布密度低;热轧板中的织构沿板厚方向,由亚表层的{110}<001>织构向1/2中心层的α线织构变化,其中{110}<001>织构在热轧板距表面1/4层处最强。 The low temperature grain-oriented silicon steels were produced by acquired inhibitor method.The precipitates in hot rolling strip were observed and studied by transmission electron microscope,and the texture distribution in 1/8,1/4 and 1/2 layers of hot rolling strip were analyzed by ODF method.The results showed that the square shaped h-AlN is the main precipitates in hot rolling strip.The precipitates are varying in size and distribution.The texture of hot rolling strip in thick direction are...
CN202110784113.5一种硅钢连退炉辊除瘤方法及装置
本发明涉及硅钢技术领域,尤其涉及一种硅钢连退炉辊除瘤方法及装置。包括连杆、手柄、磨削片、密封盖、端盖与套筒;磨削片垂直固接在连杆一端的外壁上,手柄固接在连杆的另一端,手柄与磨削片处于同一平面上;连杆套接在套筒内,连杆能沿套筒轴向移动,套筒固接在端盖上;硅钢连退炉辊下方的炉墙设有与连杆及磨削片相应的磨辊孔,端盖或密封盖固接在磨辊孔处。1)确定结瘤炉辊;2)确定结瘤在碳套辊上的位置;3)插入除瘤装置;4)磨削;5)抽出。本发明降低废品量,提高成材率;减少停炉处理结瘤时间,降低能耗,提高生产率;提高难磨瘤辊的修复率,降低炉辊成本。
CN202110777033.7一种控制高牌号硅钢退火产生月牙印缺陷的方法
本发明涉及一种控制高牌号硅钢退火产生月牙印缺陷的方法,多次调整硅钢退火线入炉及出炉张力参数,使带钢处于预设悬垂量内;本发明避免高速运行下带钢撞在炉辊上,从而产生月牙印缺陷,提高了产品的质量。
CN202121007093.2一种电工钢加工用绝缘喷涂装置
本实用新型公开了一种电工钢加工用绝缘喷涂装置,包括底板,所述底板顶部外壁的中央位置设有安装通孔,所述安装通孔的两侧内壁上均通过轴承连接有转杆,所述底板的一侧外壁上固定连接有第一电机,第一电机输出轴的一端连接有连接杆,连接杆的一端固定连接在一个转杆的一端,两个所述转杆的一端固定连接有同一个放置架,所述放置架的两侧内壁上均固定连接有两个伸缩杆,四个所述伸缩杆活塞杆的外壁上均设有复位弹簧。本实用新型第二电机可以驱动每一个空心管转动的过程中,空心管内的绝缘漆从管壁的喷孔喷洒而出,而空心管外的扇板则配合交错分布的喷孔将雾化喷洒的绝缘漆打乱喷洒在电工钢上,全面且充分的完成喷涂。
热处理工艺对含Mn高硅钢热轧带的组织及硬度的影响
研究了热处理工艺(退火温度、保温时间、冷却方式)对含Mn的Fe-6.5wt%Si高硅钢热轧带的显微组织及硬度的影响。结果表明,退火温度对Fe-6.5wt%Si合金的组织和显微硬度均有较大影响,随退火温度升高,平均晶粒尺寸和显微硬度均明显增大。小于1 h退火时,晶粒长大缓慢,而长时间(>1 h)退火时,一些次表层晶粒将发生异常长大。水冷组织比空冷组织略细小,但水冷显著降低了显微硬度。Mn含量提高能抑制850℃退火时晶粒的长大,并且促进退火后高硅钢的软化。 The influences of heat treatment process(annealing temperature,heating time,cooling methods) on the microstructure and microhardness of Fe-6.5wt%Si high silicon steel containing manganese for hot rolled strip were studied.The results show that the annealing temperature has a great effect on the microstructure and microhardness of Fe-6.5wt%Si alloy,and as the annealing temperature increases,the average grain sizes and microhardness will significantly increase.When annealing time for less than 1 h...
CN202122099636.4一种防溢出的无取向硅钢绝缘涂液存储装置
本实用新型公开了一种防溢出的无取向硅钢绝缘涂液存储装置,涉及无取向硅钢绝缘涂液技术领域,为解决现有无取向硅钢绝缘涂液存储设备在存储过程中存在涂液过满,导致液体溢出产生浪费现象的问题。所述绝缘涂液存储机构本体上方的一侧设置有液位监测器,所述液位监测器的下端设置有监测杆,所述液位监测器的输出端设置有单片机,且液位监测器的输出端与单片机电性连接,所述绝缘涂液存储机构本体的内壁设置有压力传感器,且压力传感器设置有若干个,所述压力传感器的输出端与单片机的输入端电性连接,所述绝缘涂液存储机构本体的内部设置有泵体,且泵体设置有两个,所述泵体的一端设置有溢流输送管。
CN202111332457.9一种无取向硅钢用涂层溶液及其制备方法和应用
本发明提供一种无取向硅钢用涂层溶液及其制备方法和应用,以所述无取向硅钢用涂层溶液的总质量为基础计,所述无取向硅钢用涂层溶液包括如下质量百分含量的原料组分:磷酸盐溶液55%~60%;树脂溶液20%~25%;二乙二醇丁醚2%~4%;改性剂3%~5%;余量为水。由本发明所述无取向硅钢用涂层溶液形成的绝缘涂层厚度均匀,表面光滑,具有优良的绝缘性、耐腐蚀性、附着性,而且硅钢片的冲片性能好、叠片系数高。