硅钢资料

本实用新型涉及变压器铁芯加工的技术领域，特别是涉及一种变压器铁芯加工用硅钢片裁剪装置，其可提高下料的便利性，同时提升工作效率；包括操作台、集料板、气缸、底架、两组立板、电机、从动轴、传送带、缓冲座、两组高弹簧和两组低弹簧，操作台底端设有四组支腿，操作台顶端设有送料组件和裁剪机，操作台上设有下料口，集料板转动安装在下料口内，气缸顶端和操作台底端固定连接，集料板底端滑动设有铰接座，气缸的输出端和铰接座铰接，立板通过两组立板固定安装在操作台底端，电机固定安装在底架前端，电机的输出端设有主动轴，主动轴转动安装在底架内，从动轴转动安装在底架内，主动轴和从动轴之间通过传送带传动连接。

选用国内外无取向硅钢标杆企业A、B、C的产品,采用非水溶液电解提取+SEM(EDS)方法,分析了其典型牌号对应成品试样中的夹杂物。结果表明,从磁性能控制角度而言,受钢的化学成分及生产工艺影响,A、B、C企业成品试样的夹杂物尺寸、种类、数量存在差异,这些差异对其磁性能产生显著影响;从夹杂物控制角度而言,A、B、C企业对应成品试样的夹杂物,以MnS、CuxS复合或者AlN、MnS、CuxS复合为主,其中1.0μm以下的夹杂物数量分别为2.34×107个/mm3、2.98×107个/mm3和11.98×107个/mm3,1.0μm以上夹杂物数量均很少,夹杂物的平均尺寸从大到小依次为A企业、B企业、C企业。 According to the production of three benchmarking manufacture enterprises A,B and C of non-oriented silicon steel at home and abroad,the inclusions in finished steel samples with typical grades were investigated by electrolytic extraction from non-aqueous solution and SEM(EDS).Results show that,from the viewpoint of improving the magnetic properties,affected by chemical composition and production technique,the size,type and amount of inclusions in finished steel samples are various,which will af... 

本发明揭示了一种高牌号无取向硅钢及其生产方法，生产方法包括冶炼、连铸、热轧、酸洗、切边、常化、冷轧，冶炼最终所得钢水化学成分以质量百分比计为：C≤0.005％、Si≥2.8％、Als0.5～1.2％、Mn0.25～0.8％、P≤0.02％、S≤0.0040％、N≤0.0020％、Nb≤0.0020％、V≤0.0020％、Ti≤0.0020％，其余为Fe以及不可避免的杂质；切边工序对热轧卷板的两侧进行切边，单侧的剪切宽度为10～20mm；常化在罩式退火炉中进行，均热温度为T＝{(990～1010)‑100×[30×(Si)+20×(Al)]}℃，(Si)为Si的质量百分比，(Al)为Al的质量百分比，均热时间为6h，之后冷却；钢卷在罩式退火炉中冷却至预设温度T0时取出送至冷轧线冷轧，T0为120～180℃，第一道次轧制时的轧制力恒定且轧制力为11000～12000kN。本发明可避免高牌号无取向硅钢在冷轧过程中由于脆性高而导致的频繁断带。

本实用新型公开了一种硅钢片激光曲线开料机，本实用新型涉及电力设备技术领域，目前现有的硅钢立体三角形卷铁芯的机械式斜度开料机在开料过程中精度差、效率低，且在硅钢片送料的过程中，长时间后硅钢片容易发生松散情况，同时只能对单一厚度的硅钢片进行输送工作，包括放料组件和开料组件以及收料组件，所述放料组件用于对硅钢片的放料工作，所述开料组件用于对硅钢片的开料工作，所述收料组件用于对硅钢片的收料工作。该硅钢片激光曲线开料机，通过利用高速激光曲线开料，效率高精度好，且硅钢片在输送的过程中，能够自动调整导向辊的位置，进而能够对硅钢片起到很好的导向作用，使其表面时刻为张紧状态，进而保证硅钢片的开料效果。

结合硅钢退火炉项目中应用PDSOFT软件进行三维配管设计的案例,描述PDSOFT软件的应用过程,总结其使用要点,分析其优缺点,并提出了推广三维设计软件的思路,对今后PDSOFT在相似项目中的推广应用有参考和借鉴价值。 Combining the case of using PDSOFT software to design the three-dimensional piping,the application process of the PDSOFT software is described,the using points are summarized,the advantages and disadvantages are analyzed,and the ideas of promoting the three-dimensional design software are put forward,which have a strong reference value for the promotion and application of PDSOFT in similar projects in the future. 

本申请提供了涂布的晶粒取向电工钢板及其生产方法。在一个示例性实施方案中，所述方法包括生产具有约2.5至约4重量％的硅、约0.005至约0.1重量％的碳和约90至约97.5重量％的铁的熔融钢。将熔融钢浇铸成板坯并且然后冷轧成具有表面的板。使用脱碳退火对板进行脱碳，然后使用重结晶退火进行重结晶以生产晶粒取向电工钢。施加涂层覆盖所述表面，其中所述涂层包括有机可辐射固化交联剂和光引发剂。通过将涂层暴露于辐射源来固化涂层。

本实用新型公开了一种变压器硅钢片剪切收料装置，其包括底板和存放架推出机构，底板的前侧中部设置有用于放置外设剪切设备的放置区；存放架推出机构包括滑动板座、锁紧组件，滑动板座可左右滑动地安装于底板的上表面，在滑动板的上表面设置有两个用于放置外设的硅钢片存放架的存放架放置槽，两个存放架放置槽呈左右间隔设置，锁紧组件用于锁紧滑动板座与底板之间的相对位置。当该硅钢片存放架存放完后，将滑动板座推动至使得另外一个存放架放置槽设置于放置区的正后方，另外的硅钢片存放架继续接受剪切设备掉落的硅钢片体，可连续地实现硅钢片体的落料存放，令转运和落料的操作不相互干涉，提高生产的效率。

介绍了烟气余热利用系统的工艺流程及控制思想,结合该系统在钢厂硅钢连续退火机组中的应用实践,估算出烟气余热利用系统每年可节约蒸汽5 040 t,经济效益良好,同时分析了该系统存在的问题及对策。 Introduced a method about the process and control of the application of waste heat system, which had been used into a silicon steel continuous annealing line and profiting a good economic benefit by saving a large number of steam every year, which has been estimated about 5 040 tons, and analyzed the problems and solutions existed in this system. 

利用OM、EBSD等手段研究了热轧板两段式正火时在700℃保温不同时间(0、10、30、60 min)对含Sb冷轧无取向电工钢磁性能的影响。结果表明,700℃保温10 min处理的样品铁损最小,磁感最高。对成品板的组织分析结果表明,试样的晶粒尺寸随700℃保温时间的延长先增大后减小,保温10 min时晶粒尺寸达到最大;分析成品试样织构发现,有利织构组分随700℃保温时间的延长先增加后减少,保温10 min时有利织构组分所占百分比最高。因此,含Sb冷轧无取向电工钢两段式正火时在700℃保温10 min时磁性能最好。 Effect of two-stage normalization on magnetic property of non-oriented electrical steel containing antimony was investigated by using optical microscope(OM) and electron back-scattered diffraction technology(EBSD).The experimental results show that the iron loss and magnetic permeability of the specimen insulated at 700 ℃ for 10 min are lowest and highest respectively.The grain size of the finish specimens increases first and then decreases with the increase of holding time.Similarly,the advanta... 

研究了冷轧95%变形量无取向硅钢不同退火温度(710～1 050℃)下再结晶织构特征.再结晶刚完成时(710℃退火),呈现强γ({111<112>～<134>)与弱{114}<481>织构特征;随退火温度升高至900℃,γ明显减弱,{114}<481>组分持续增强,形成典型的{h,1,1}<1/h,1,2>织构;进一步升温至1 050℃,再结晶织构不再发生明显变化.基于EBSD分析,{114}<481>组分的持续强化可归因于其明显的尺寸优势以及较高频率的高能晶界(取向差角为20°～45°). A non-oriented silicon steel was heavily rolled to 95% reduction and subsequently annealed at 710~1 050 ℃ to investigate recrystallization texture evolution.When annealed at 710 ℃ with complete recrystallization,the texture is characterized by a strong partial γ fiber spreading from {111}<112> to {111}<134> and a weak {114}<481> component.As annealing at 900 ℃,γ fiber is decreased significantly while {114}<481> is increased consistently,producing a typical {h,1,1}<1/h,... 

结合工业化生产的高效硅钢,进行了RH精炼稀土处理试验研究。针对不同的稀土处理条件,观察了夹杂物的形貌和尺寸分布,探讨了稀土处理后钢中的夹杂物形成、变化规律。结果表明:试验条件下,最佳的稀土合金添加数量为0.6～0.9 kg/t。经过合适的稀土处理后,可以有效抑制尺寸相对较小的、不规则的AlN、MnS复合夹杂生成,促进钢中微细夹杂物的聚合、上浮,钢质纯净度得到明显提高。此时,钢中全氧含量最低,脱硫效果最佳,钢中的夹杂物主要是尺寸相对较大的、近似球形或者椭球形的稀土类夹杂。 Based on the industrial production of non-oriented silicon steel,the experiment on RE treatment during the RH refining process was studied.The morphology and the size distribution were observed for the steel specimens treated with different RE treatment conditions.Further more,the formation and change of inclusions of final steel sheets after RE treatment were discussed.The results show that the suitable RE added amount was 0.6～0.9 kg/t.After the suitable RE treatment,the formation of AlN and Mn... 

一种含Bi高磁感取向硅钢热轧带钢边部质量控制方法：炼钢；连铸；铸坯加热；粗轧，粗轧道次不低于4道次，各道次压下率控制在20~33%；规精轧及进行后工序。本发明通过对热轧工序的控制，能使热轧带钢边部开裂的尺寸降低至不超过5mm，且边部开裂≤2mm比率能达到95%以上，后工序切边量很少甚至无需切边即可进行冷轧，使产品成材率能比现有技术提高2~4%；且由于铸坯加热温度的降低使能耗也随之降低。