本实用新型公开了一种变压器铁芯硅钢片纵剪滚切装置，包括纵剪机本体、弹性压覆机构和涂油机构，所述纵剪机本体的进料端设置有弹性压覆机构，料带通过弹性压覆机构压覆在纵剪机本体的支撑平台上，所述支撑平台上凹设有安装凹槽，所述安装凹槽内设置有涂油机构，所述涂油机构朝向于料带的底面涂油，通过涂油机构对板材的切割面进行涂油，能够对料带起到润滑和冷却的作用，提升料带切割质量。

试验研究了球刻痕法对高磁感取向硅钢的铁损、矫顽力、相对磁导率、巴克豪森噪声等磁学性能的影响.研究结果表明:经过球刻痕处理后,高磁感取向硅钢的铁损明显降低,矫顽力下降,8 mm球刻痕过后铁损值与矫顽力分别下降16.2%和14.7%,且铁损和矫顽力均随刻痕间距降低而减少.刻痕后的高磁感取向硅钢磁导率在高磁感应强度下明显上升,刻痕后巴克豪森噪声值明显降低,经过对比分析确定8 mm为球刻痕的最佳刻痕间距.从磁畴观察、细化磁畴的原理等方面解释了细化磁畴对高磁感取向硅钢性能的影响原因. The effects of the ball scribing on magnetic properties of high permeability grain-oriented silicon steels,including the iron loss,coercive force,relative permeability,and Barkhausen noise were investigated. The results showed that the iron loss and coercive force of the high permeability grain-oriented silicon steels apparently decreased 16. 2% and 14. 7% respectively after 8 mm ball scribing and they both decreased with the decrease of the scribing spacing at the same magnetic flux density. At... 

本实用新型涉及一种无取向硅钢蠕变性能测试装置，包括基座，基座的顶部和侧面设有开口；试样夹持装置，试样夹持装置安装在基座的顶部，用于夹持硅钢蠕变试样；转换力杆，转换力杆安装在基座的侧面，与试样夹持装置连接；可调节式砝码盘，可调节式砝码盘安装在转换力杆上，可调节式砝码盘上能够放置不同重量的砝码，转换力杆将砝码的重力转换成水平力，以实现对硅钢蠕变试样不同应力水平的加载；可调节式灯座，设置在试验腔内并与基座的侧面插接；加热装置，放置到可调节式灯座上，用于给硅钢蠕变试样加热。本实用新型具有解决无法实现不同应力和温度下硅钢材料的蠕变研究的问题的效果。

一种生产取向硅钢的氧化镁涂层烘烤质量控制方法，通过对带钢的实时温度测量建立对烘烤输出功率的实时反馈调节，据此形成基于烘烤输出功率的烘烤质量的实时控制。本发明的一种生产取向硅钢的氧化镁涂层烘烤质量控制方法，通过在烘烤炉出口的带钢上方增加一套可在带钢横向方向移动的在线板温计，基于在线板温检测值对烘烤炉状态进行监控，并建立烘烤输出功率控制系统实时调整，使得氧化镁涂层烘烤质量均匀，提高取向硅钢产品质量稳定性，节省能源消耗。

针对新日铁公开的相关专利,总结日本高强度无取向电工钢的研究进展,分析了各专利化学成分、生产工艺及产品性能的特点,指出固溶强化、细晶强化、析出强化、位错强化都有可能被用来提高无取向电工钢的强度。在高强度无取向电工钢的研发过程中,需要根据其具体用途确定目标性能,再采用合适的强化手段,从而实现力学性能、磁性能和生产性能之间的平衡。 Authors summarize the research progress of high strength non-oriented electrical steel in Japan by learning related patents brought into the public by Nippon Steel. Authors also analyze the characteristics of the chemical composition, production technology and properties of products in the patents and point out that any ones of solution strengthening method, fine-grain strengthening method, precipitation strengthening method or dislocations strengthening method may be used to improve the strengt... 

本发明涉及硅钢收卷技术领域，具体公开了硅钢冷涂后锥度张力收卷工艺，将张力卷筒装配到卷取机上，张力卷筒包括转轴和若干支撑板，若干支撑板形成圆筒结构，若干支撑板上连接块底部的斜面形成锥形结构；还包括位于转轴两端的驱动杆，驱动杆转动连接有锥形杆，锥形杆与锥形结构为锥度配合，锥形杆的长度为L；将硅钢头部搭接在张力卷筒外部，当硅钢在张力卷筒外部卷绕4～7圈后，驱动杆移动的速度为V；当锥形杆进入的距离为1/3L时，将速度降低至2/3V；当锥形杆进入的距离为2/3L时，将速度降低至1/3V；当锥形杆全部进入时，驱动杆停止移动，硅钢继续卷绕。本专利公开的收卷工艺利用了锥度张力原理，得到的硅钢卷不会坍塌。

本发明公开了一种酸洗低牌号无取向硅钢的方法，从酸洗线前拉矫机的延伸率设定、酸液浓度、酸液温度、酸洗槽内液位的控制、酸液中铁离子的含量等方面入手，解决酸洗低牌号无取向硅钢的问题。

为探究铬、锰元素及退火温度对高强无取向硅钢性能的影响规律,借助OM、SEM、EBSD与万能拉伸试验机等分析不同制造工艺下3组不同含量铬、锰元素的无取向硅钢热轧、常化及退火处理后组织与性能。结果表明,试验钢热轧后组织不均匀,心部为沿轧向分布纤维状组织,边部为少量再结晶晶粒,常化处理能显著改善热轧板组织均匀性,消除热轧板中心部位的纤维状组织。经冷轧及退火后得到多边形铁素体晶粒,其中960℃退火,晶粒尺寸偏大,有利织构{100}组分体积分数减少,不利织构{111}组分体积分数增加,成分为0.2Mn-1Cr的1号试验钢960℃退火后铁损最大,磁感强度偏小;成分为0.5Mn-1Cr的2号试验钢930℃退火后,磁性能与强度等综合性能最佳,工频铁损P_1.5/50为2.41W/kg,高频铁损P_1.0/400为17.36W/kg,磁感应强度B_{5 000}为1.638T,抗拉强度为685MPa。 In order to study the effect of Cr,Mn and annealing temperature on the properties of high-strength non-oriented silicon steel,the microstructure and properties of three groups of non-oriented silicon steel with different Cr,Mn content under different manufacturing processes were analyzed by means of OM,SEM,EBSD and universal tensile tester.The results show that the structure of experimental steel is not uniform after hot rolling,and the core is distributed in fibrous structure along the rolling ... 

本发明属于变压器铁芯生产加工技术领域，具体涉及一种硅钢常化用缝合设备，包括动力机构、钢带送料机构、固定座和移动座，移动座上开有多个凹槽和设有冲压刀；固定座上开有凹腔，凹腔内滑动连接有凸模板，凸模板上设有与凹槽配合的凸块；钢带送料机构包括放料辊、设在放料辊上的钢带卷和送料部，送料部用于输送钢带并使钢带依次穿过硅钢片上的各个开口。动力机构包括动力部、传动筒、均与传动筒连通的固定筒和中间筒。本方案中，在硅钢片的叠合处开设了桥型孔，利用钢带穿过硅钢片叠合处的桥型孔，相当于利用钢带将硅钢片缝合在一起，这样设置能够较好将不同的硅钢片连接成一体。

本实用新型公开了一种硅钢片加工用进料结构，涉及到硅钢片加工技术领域，包括壳体，壳体的两侧均贯穿开设有通槽，通槽的内部活动贯穿设置有活动板，活动板位于壳体内部的一端贯穿开设有方槽，其中一个方槽的顶端内壁和另一个方槽的底端内壁均固定设置有多个呈等间距分布的锯齿。本实用新型通过将多个硅钢片均挂在两个架板上的挂槽内，因硅钢片重量，带动两个延伸杆向下移动，延伸杆带动活动块向下移动，活动块带动齿条向下移动，从而带动齿轮转动，齿轮转动的同时，能够通过多个锯齿带动两个活动板相互靠近，从而使两个夹板相互靠近并夹紧多个硅钢片，从而能够固定住硅钢片，防止硅钢片传输时滑动，造成磨损。

为了优化激光刻痕降低取向硅钢铁损的工艺,寻找刻痕速度、脉冲能量、扫描间距等重要刻痕参数的最佳匹配关系,提出了一种基于人工神经网络与遗传算法的优化模型,并利用这种模型对30Q130取向硅钢材料的刻痕工艺进行了优化实验,结果表明,这种模型稳定可靠,可以作为取向硅钢刻痕工艺优化的一种有效的措施。 A laser is often considered to scribe the grain-oriented silicon steel surfaces after cold-rolling and annealing to reduce the core loss.It is necessary to select the best scribing parameters to maximize the reduction in this process.This paper proposes an optimization method of genetic algorithm during laser scribing of 30Q130 steel,by developing an artificial neural network prediction model using a database form a designed orthogonal experiment.The objective is to determine the best combinatio... 

本发明特别涉及一种控制边部质量的低牌号无取向硅钢的热轧生产方法，属于无取向硅钢热轧生产技术领域，方法包括：将低牌号无取向硅钢的板坯进行第一次粗轧，将第一次粗轧后的板坯进行第二次粗轧，其中，在第二次粗轧机前的立辊上设置立辊润滑装置，所述立辊润滑装置向所述立辊供给的润滑油的油量为100mL/min‑400mL/min；将第二次粗轧后的板坯进行精除鳞、精轧和卷取，获得边部质量合格的热轧卷；保证良好的立辊辊面状态，可有效解决边部粗糙，有效解决了低牌号无取向硅钢边部粗糙状态，极大的提高了冷轧后工序毛边轧制率，提高了硅钢全工序成材率。