采用X射线衍射仪分析无取向硅钢冷轧织构和再结晶退火织构的演化,研究了热轧组织对无取向硅钢织构以及磁性能的影响。结果表明,具有均匀、粗大晶粒组织的热轧板,冷轧形成更多的剪切带,导致成品板形成高的高斯织构组分,并提高了{100}织构强度,降低了γ纤维织构,最终导致成品磁感应强度升高,铁损下降。 The texture evolution of non-oriented silicon steel during cold-rolling and recrystallization annealing was investigated by X-ray diffractometer.The effects of hot band microstructure on the texture and magnetic properties of non-oriented silicon steel were analyzed.The results show that more shear bands appear during cold rolling due to homogeneous coarse grain in hot band.So strong{110}<001> texture after recrystallization annealing forms.At the same time,the {100} texture components inc... 
2023-05-09 135 5.8

以太钢热连轧厂的硅钢为研究对象,利用凸度仪测量热轧带钢出口凸度值,采用矩阵和失效模式的分析方法了解影响带钢凸度变化的主次因素。研究结果表明:通过有效控制轧制过程中的加热温度、时间及采用合理的辊型,硅钢凸度精度提高了4.34%左右。 In this paper,we take the hot-rolled silicon steelsheet of Taigang as the research symbol,exit profile was measured by convex instrument,the primary and secondary factors that affect the strip profile were measured by using matrix and failure mode analysis methed.The results indicate that convexity accuracy has significantly improved by nearly 4.34% through the effective control of the heating temperature,heating time and the use of correct roller type in the process of hot rolling. 
2012-05-28 71 5.8

冷轧无取向硅钢是高技术含量、高附加值产品,工艺复杂,生产周期长,过程控制难度大,被誉为钢铁产品中的\"工艺品\"。热轧生产工艺又是无取向硅钢生产的重中之重,直接决定了硅钢的铁损和电磁性等多项指标。 Cold rolled non-oriented silicon steel is high technology content、high addedvalue product. Its process is complex, Its production cycle is of Length, and Its Process control is difficult. Which is known as the iron and steel products \" Arts and crafts\". Hot rolling production process is the top priority of non-oriented silicon steel, Which Directly determines iron loss of the silicon steel and electromagnetic property, etc many index. 
2023-05-09 149 5.8

采用EBSD技术研究了有、无拉应力作用下无取向硅钢在晶粒长大过程中织构转变及晶界变化的规律。结果表明:在晶粒生长期间,无应力作用下的硅钢中,{111}〈112〉,{111}〈110〉织构组分强化,而{100}〈001〉织构组分弱化;与无拉应力作用下的情况相比,施加5MPa的拉应力时,{111}〈112〉,{111}〈110〉织构组分强化的速率下降,{100}〈001〉织构组分变化不明显。对于在晶粒生长期间持续变化的{111}〈112〉,{111}〈110〉和{100}〈001〉织构组分而言,虽然有、无拉应力作用下硅钢的{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率均下降,而{100}〈001〉织构组分的高取向差角度晶界频率则上升,但当有拉应力作用后,{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率下降的速率变小,{100}〈001〉织构组分的高取向差角度晶界频率上升的速率稍有变小。通过对无取向硅钢在晶粒长大过程中织构转变及晶界变化规律的研究,分析了合金原子在晶界的偏聚行为。 The rules of texture and grain boundary transformation in the nonoriented silicon steel under applied stress or without applied stress during grain growth were investigated by EBSD.The results show that the {111}〈112〉 and {111}〈110〉 components in the nonoriented silicon steel without stress are strengthened during grain growth whereas {100}〈001〉 component is weakened,but the growth rate of {111}〈112〉 and {111}〈110〉 component decreases,while the area fraction of {100}〈001〉 component doesn’t chang... 
2012-09-28 86 5.8

一种适用于取向电工钢产线的一体化生产计划排程方法,基于L4,建立基于如下步骤的整条取向电工钢产线的自动生产计划排程,S1:以排程所需的必要数据为基础,按核心工序为排程起点,分别依次递进式完成前工序、后工序的排程,形成初始计划排程;S2:对初始计划排程建立基于设定的评价因子构成的综合评估,形成由综合评估结果构成的综合评估结果数据集;S3:对综合评估结果数据集建立优化算法运算,根据运算结果确定生产计划排程。本发明的一种适用于取向电工钢产线的一体化生产计划排程方法,可实现较大程度的自动化,提高生产计划编制效率,增强操作人员对生产计划的整体情况掌握,并可根据设备状态及计划执行情况自动对计划作出快速响应。
2021-08-25 85 6.8

本发明公开了一种硅钢环形炉内罩的内圆直径自动检测装置及方法,该内圆直径自动检测装置包括设置在检测点地面上的水平工作台,设置在所述水平工作台上的水平调节机构,设置在所述水平工作台上的扫描机构,以及与所述扫描机构通信互联的检测处理机构。该内圆直径自动检测装置是非接触式设备,不受内罩温度的限制,使用方便灵活,设备可靠性好,安全性高,对环境无污染,不仅能够有效节约校圆机的使用频次,而且大大增强了炉子的安全可靠性。
2021-03-25 65 6.8

本发明公开了一种用于取向硅钢卷的焊缝切除方法,包括在焊接机组完成钢卷焊接后,在距离焊缝预设距离位置处冲孔;而后,钢卷到达成品退火工序时,利用孔洞检测装置检测焊缝冲孔,并根据焊缝冲孔得到焊缝位置,并记录该焊缝位置;并在分卷工序中,根据记录得到的焊缝位置对焊缝进行切除。这样,该方法利用焊缝冲孔,结合孔洞检测装置,将焊缝位置信息传递到分切工序,使得焊缝识别切除率较高,有效解决了取向硅钢焊缝无法精准定位切除的问题,实现了卷中焊缝多工序结合精准切除。
2020-12-16 94 6.8

变压器D21硅钢铁芯片采用冲压工艺生产。首先对其工艺进行了分析,确定了冲压方案。对产品进行了排样设计,计算了冲压力,确定了压力中心。然后,设计了单工序落料模具,完成了模具装配图。 D21 silicon steel chips for transformer are produced by stamping.First,its stamping process was analyzed and the scheme of the stamping process was determined.The product layout was designed,the punching pressure was calculated,the pressure center was determined.Then,the blanking die with single procedure was designed,the die assembly drawing was completed. 
2013-07-28 49 5.8

以CaO-CaF2复合渣系为脱硫剂,在RH精炼过程采用真空投入法进行高牌号无取向电工钢深脱硫工业试验,采用KTH模型计算分析了RH炉渣成分对硫容量CS的影响。研究结果表明,炉渣成分控制在w((CaO))/w((SiO2))为5~7,w((CaO))/w((Al2O3))为1.5~1.8,w((Al2O3))为25%~30%,w((FeO+MnO))<5%,脱硫剂加入量为6~8kg/t时,钢中硫质量分数从平均0.003 1%降低到0.001 8%,最高脱硫率达到47.1%,平均脱硫率为41.7%。 The industrial trials on deep desulphurization of high grade non-oriented electrical steel were finished through using CaO-CaF2complex based fluxes in RH process.Using the KTH model,the effect of refining slag composition on the sulfide capacities was analyzed.The results show that the chemical composition of refining slag(mass fraction,%)is w((CaO/SiO2))between 5to 7,w((CaO))/w((Al2O3))beween 1.5to 1.8,w((Al2O3)) between 25%to 30%,w((FeO+MnO))less than 5%,and the desulphurizer addition level of... 
2014-02-28 99 5.8

本发明涉及涂层液技术领域,且公开了取向硅钢绝缘涂层液,其配比为:二氧化硅10‑15%、硼酸5‑8%、磷酸二氢盐2‑5%、金属溶胶20‑25%、氢氧化铝占5‑6%、有机酸处理的复合盐溶液20‑30%、分散剂0.5‑1%,其余为水,采用硅溶胶作为辅助成膜物,粘结力较强,对附着性影响很大。硅溶胶能够很均匀地包裹在被胶结物质的表面,通过自干成膜,保持了很高的常温结合强度;而磷酸盐涂层的固化是通过受热分解,脱水聚合完成的,低温强度差,中温强度高,充分利用了硅溶胶低温的结合强度和磷酸盐中、高温时的结合性能,消除了常规涂层烘烤时容易出现的收缩、起泡现象,阻止了微气孔的形成,提高了涂层的表面光滑度,粘结强度和稳定性同时保持绝缘涂层的光泽、光滑和稳定性。
2020-12-31 77 6.8

本实用新型涉及一种硅钢片点数机,包括底座、分拣器、收拢器和输送器。其中,分拣器通过机架倾斜连接于底座上,用于分拣硅钢片,分拣器上设置有计数器,计数器依次计数分拣器分拣的硅钢片的数量。收拢器包括托盘和振动器,托盘设于分拣器的下方,用于承装分拣器分拣的硅钢片,振动器设于底座上,与托盘上硅钢片抵接,振动器振动能够将托盘上的硅钢片收拢整齐。输送器与底座和托盘相连,输送器工作能够带动托盘移动,以将托盘上的硅钢片输送至下一工位。本实用新型采用的是分拣清点的方式,事先无需摆放整齐,将每片硅钢片进行分拣计数,有效避免了摆放不整齐造成的计数不精确的问题。
2021-03-25 67 6.8

运用EBSD和光学显微镜,研究了0.25%~0.45%Cu对无取向电工钢热轧板显微组织,成品板显微组织、织构和磁性能的影响。实验结果表明:卷取过程中Cu元素在热轧板表层的偏聚作用显著阻碍了热轧板表层再结晶晶粒长大,导致热轧板表层晶粒尺寸随着Cu含量增加而逐渐较小,但热轧板中间晶粒尺寸变化不大。同时发现Cu元素能够明显改善织构类型,使有利织构组分增加,不利织构组分减少,同时减弱织构强度。从实验结果可知0.35%Cu能够显著改善电工钢的磁性能,铁损P15/50最低达到4.1 W/kg,磁感B50最高值达到1.8 T。 Effects of high content Cu on microstructure of hot rolled plates and microstructure,texture and magnetic properties of annealed finish product plates of non-oriented electrical steel were examined by means of EBSD technique and optical microscope. The results show that surface segregation of Cu significantly hindered recrystallized grain growth of surface layer in hot rolled plate during the coiling,as a result,the surface grain sizes of the hot-rohed plates decrease with the increase of Cu con... 
2013-11-28 86 5.8