对碳-锰-硅钢进行不同配分温度的Q&P(Quenching and Partitioning)处理,测试了热处理后不同钢的力学性能和残余奥氏体含量,并用扫描电子显微镜和透射电镜观察其显微组织,分析了配分温度对显微组织和力学性能的影响。结果表明:试验钢显微组织基本由低碳板条状马氏体、块状铁素体和条状残余奥氏体组成;随配分温度的升高,试验钢的抗拉强度呈下降趋势,伸长率与奥氏体含量的变化趋势相同,但变化规律不确定;提高锰含量能稳定残余奥氏体,从而提高试验钢的伸长率,并使伸长率对配分温度不敏感。 The C-Mn-Si steel was quenched and partitioned at different partitioning temperatures,the mechanical properties and residual austenite contents were investigated,the microstructure was observed by SEM and TEM,and the effect of partitioning temperature on microstructure and mechanical properties was analyzed.The results show that the microstructure of the tested steel consisted of lath martensite with low carbon,nubby ferrite and banded residual austenite.The tensile strength of the tested steel ... 

本发明提供一种电磁屏蔽用1050铝/50W800无取向电工钢钢板生产方法，包括S1)、将轧制好的铝卷和钢卷分别放置在两个开卷机上开卷；S2)、开卷后分别采用HCl、NaOH溶液清洗；S3)、用旋转钢丝刷法对铝板、钢板待结合面进行机械处理10‑15s；S4)、将铝板、钢板置于丙酮溶液中超声波清洗2‑3min；S5)、将表面处理后的铝板、钢板进行预拉伸或者预压缩，S6)、将预应力处理的铝板、钢板边部进行焊接；S7)、将焊接好的钢铝板进行轧前的预热处理；S8)、然后进行连续退火炉中进行退火处理，本发明将金属铝板、钢板通过热轧轧制复合化结合在一起，界面剪切强度≥100MPa，反复弯曲次数≥10次。

本实用新型公开了一种无取向硅钢绝缘涂层粘结性检测装置，涉及涂层粘结性检测技术领域，为解决现有的无取向硅钢绝缘涂层，在对绝缘涂层粘结性检测过程中，其检测结构单一，容易导致检测不准的问题。所述基座的上方设置有存料罐，所述存料罐的内壁设置有防腐涂层，所述存料罐的底部设置有声波感应器，所述声波感应器的一侧设置有液位感应器，所述液位感应器的一侧设置有自控温度调整器，所述存料罐的上方设置有控制盘，所述控制盘的表面设置有PLC操控器，所述控制盘的上方设置有电机，所述电机的一侧设置有带轮结构，所述带轮结构的一侧设置有伸缩气缸，所述伸缩气缸的一侧设置有联动结构，所述伸缩气缸的一端设置有收缩棒。

本发明公开了一种硅钢冷轧吹扫辊，涉及硅钢加工设备领域，包括安装架、上轧辊和下轧辊、下调节机构、上调节机构以及吹扫机构；所述下调节机构包括调节支撑底板、楔形插块以及调节油缸；所述上调节机构包括顶升油缸、顶升杠杆和顶升连杆；所述吹扫机构包括吹扫连接座、吹扫管道和吹扫排管。本发明通过在上轧辊和下轧辊的出料端安装吹扫机构能够便于对出料的钢带表面进行吹扫清洁，能够有效提升钢带成品的表面质量；由于下轧辊在轧制过程中承受的重量较大，通过调节油缸带动下轧辊两侧的楔形插块来回移动的方式对下轧辊的高度进行微调，能够保证下轧辊在轧制过程中整体的稳定可靠性。

本实用新型公开了一种连续热浸镀铝锌硅钢板,包括硅钢裸板，所述硅钢裸板的左侧边固定连接有第一铝锌输送条，所述硅钢裸板的右侧边固定连接有第二铝锌输送条。本实用新型，通过给待镀铝锌层的硅钢裸板左右侧边设置铝锌输送条，避免了镀层完成后需要对未镀膜的部位进程切除，降低了生产繁杂度，节约了生产成本，避免了材料的浪费，通过给铝锌输送条的前后侧面设置直齿面，提高连续热浸镀膜过程中的输送精度，从而提高了镀膜的均匀性，通过给铝锌输送条设置导向槽，提高硅钢板输送过程中的运动稳定性，通过优化硅钢钣的自身结构，提高了热浸镀铝锌层的效率，并节约了生产成本。

本实用新型公开了一种具有废料回收机构的硅钢板带加工用切割装置，包括箱体，所述箱体的前侧靠近顶部处设有电机，所述箱体的顶部靠近前侧处固定连接有竖板，本实用新型一种具有废料回收机构的硅钢板带加工用切割装置，电机在工作时既能带动切割刀进行切割作业，同时还能带动第一筛板和第二筛板以相邻转轴为中心上下摆动，切割的废屑从切割槽穿过达到箱体内腔，第一筛板和第二筛板对废料进行筛分处理，通过隔板设置，隔板将集料盒分为两个存储空间，隔板右侧存储穿过第一筛板和第二筛板的细料，隔板的左侧存储被第一筛板和第二筛板过滤下来的粗料，既方便操作人员对废料进行集中处理，还对废料进行了筛分处理，以此方便对废料进行分类重复利用。

介绍了一种适用于超大晶粒取向硅钢的高斯晶粒取向偏离角的X射线衍射测量方法，提出了将试探法和探测器扫描法相结合的方式进行测量。结果表明：该方法可以同时获得准确的实际衍射角度和取向偏离角度，试样制备方式简单，对设备的要求低且测量结果准确。 This paper introduces a X-ray diffraction measurement method of Gaussian grain orientation deviation angle for ultra-large grain oriented silicon steel, and puts forward a method of combining the test method with the detector scanning. The results show that this method can obtain accurate actual diffraction angle and orientation deviation angle at the same time. The sample preparation method is simple, the requirements for equipment are low, and the measurement results are accurate. 

本发明涉及一种无取向电工钢片绝缘涂液，它的主要有效成分包括有机树脂、水溶性磷酸二氢盐、硅溶胶、涂料助剂、和特定水溶性金属盐。上述各组分的质量组成比例为：有机树脂100份，水溶性磷酸二氢盐100‑250份，硅溶胶0‑100份、涂料助剂0‑20份，特定水溶性金属盐10‑50份，其余为水，涂液的固含量为15～40％。其中特定水溶性金属盐是指水溶性磷酸二氢盐以外的二价或多价金属盐，这种盐可以在磷酸二氢盐溶液中稳定存在，但是在电工钢涂层烧结温区会氧化或分解。本发明的绝缘涂液固化速度快且固化彻底，涂层具有优异的耐盐雾性能。

研究了应用电感耦合等离子体质谱法(ICP-MS)测定硅钢中痕量铜和镍的分析方法。采用硝酸分解样品,通过内标校正和基体匹配消除了基体干扰的影响,同时根据测量时存在的质谱干扰情况,选择同位素65Cu和60Ni作为测定元素和通过调节仪器参数使双电荷离子的产率最低,以减少带来的干扰。该方法用于硅钢中痕量铜和镍的测定,所得的结果与ICP-AES法测定结果完全吻合,各元素测定结果的RSD值小于5%,加标回收率为97.3%～100.3%。 A method for the determination trace copper and nickel in silicon steel by inductively coupled plasma mass spectrometry(ICP-MS) was studied.The samples were dissolved in HNO3.The effect of matrix interference was eliminated by internal standard correction and matrix matching.Meanwhile,according to the mass spectral interferences in determination,the isotopes including 65Cu and 60Ni were used as measuring elements.The yield of double-charge ions were minimized by adjusting instrumental parameters... 

阐述了影响硅钢卷材下料利用率的因素,并结合具体事例利用计算机排样系统进行了详细分析,对提高硅钢卷材的利用率具有一定的指导作用。 It describes the factors influenceing the the utilization ratio of the roll of Silicon steel,and analyzes it in detail combined with concrete examples by a computer arrangement system,which can give a guide for increasing the utilization ratio of the roll of Silicon steel. 

2.9 mm热轧3%Si高牌号无取向硅钢板（/%:0.004 6C、3.04Si、0.32Mn、0.49Als、0.004S、0.013P、0.0042N）由CSP（Compact Strip Production紧凑式带材生产线）流程:120 t BOF-70 mm CC-热轧工艺生产。热轧终轧温度872℃,卷取温度683℃。铸坯及热轧板的组织和夹杂物的分析结果表明,铸坯组织为典型的贯穿柱状晶组织;热轧板边部为再结晶组织,中部为纤维组织带有少量再结晶晶粒;高牌号无取向硅钢的主要夹杂物为铸坯-Al₂O₃,AlN和Cu₂S+MnS;热轧板-Al₂O₃,AlN,AIN+MnS和Cu₂S+MnS。 The 2.9 mm hot rolled 3%Si high grade non-oriented silicon steel plate（/%:0.004 6C,3.04Si, 0.32Mn,0.49Als,0.004S,0.013P,0.004 2N） is produced by CSP（Compact Strip Production） flow sheet i.e.120 t BOF-70 mm CC-hot rolling process with end rolling at 872℃and coiling at 683℃.The analysis results on structure and inclusions in casting slab and hot rolled plate show that the structure of slab is typical trans-columnar crystal,the structure of hot rolled plate at edge is recrystallized grain and in ce... 

本发明公开了一种超高效变频空调压缩机用无取向硅钢薄带及其制造方法，属于无取向硅钢技术领域。本发明包括以下重量百分比的组分：C≤0.003％，Si：2.0％～2.5％，Mn：0.15％～0.5％，Als：0.3％～0.7％，Sn：0.05％～0.11％，S≤0.003％，P≤0.03％，B：0.002％～0.004％，Ca：0.003％～0.005％，N≤0.003％，Ti≤0.003％，其余为Fe及不可避免的杂质，且Mn/S比控制在20～60范围内，B/N比控制在0.7～1.5，Ca/S的比例≥1。为解决现有技术中存在的问题，本发明通过添加合金元素以及偏析元素，配合连铸、热轧、常化和连续退火等热处理工艺，以及优良的冷轧板形控制技术，实现0.30～0.35mm厚度薄规格的高效无取向硅钢产品，具备优异的磁性能和高屈强比的力学性能，满足高效变频空调压缩机电机磁性能和关节式定子高速冲裁对力学性能和板形的高标准要求。