本发明提供了一种高强度硅钢热处理系统及热处理方法，包括固定架、放卷筒、收卷筒、热处理炉和清理装置，所述的固定架的下端与已有地面相连，固定架左右对称排布，且固定架前后对称，位于地面左端的前后正相对的固定架之间转动连接有放卷筒，位于地面右端的前后正相对的固定架之间转动连接有收卷筒，放卷筒与收卷筒之间设置有热处理炉，收卷筒与热处理炉之间设置有清理装置,本发明通过直线运动状态的凸型滑块与清洁刷可将硅钢胚体表面的灰尘等杂质清扫至硅钢的两侧，以实现对硅钢胚体的表面进行清洁的功能，以免硅钢表面的灰尘等杂质在加热的过程中形成粘结块粘附在硅钢的表面，进而增强热处理的效果。

测试了高强无取向电工钢的S-N曲线,并借助光学显微镜、扫描电子显微镜、透射电子显微镜分析了实验钢组织,疲劳断口形貌和位错结构。结果表明:室温条件下,频率为20Hz,应力比R为0.1,循环10~7周次时,实验钢的疲劳强度为360MPa,疲劳裂纹萌生于实验钢的次表面,裂纹萌生点附近有沿晶开裂现象,疲劳裂纹扩展区域有解理台阶与疲劳条纹,瞬间断裂区是韧性断裂,有大量韧窝。实验钢在循环应力作用下基体中产生了大量位错,并有驻留滑移带终止在晶界位置。 The S-N curve of a high strength non-oriented electrical steel was tested.The microstructure and fatigue fracture morphology and dislocation were analyzed by optical microscope,scanning electron microscope,transmission electron microscope.The results showed that:at room temperature and the frequency of 20 Hz and the stress ratio Rof 0.1,the fatigue strength of the experimental steel was 360 MPa when the cycle was 10~7 cycles.The fatigue crack initiation at the surface of the steel and the interg... 

以不断增长的薄板坯流程为背景,与传统流程对比分析了薄板坯流程无取向电工钢热轧晶粒组织特征;以50W800和50W1300钢为典型实例,探讨了两种流程下成品板晶粒组织、织构、磁性能及其磁时效行为的基体差异和相关原理。研究表明,薄板坯流程热轧板组织较粗大,有利于在成品板中获得粗大的晶粒和有利的织构,从而得到较低的铁损和较高的磁感。然而,薄板坯流程会造成第二相粒子的细小弥散分布与不充分析出,容易因磁时效而使磁性能恶化。 Based on the rapid development of compact strip production(CSP) processing,the characteristics of hot band grain structure produced by CSP processing were analyzed in comparison with those of conventional technology.The basic differences in grain size,texture,magnetic properties and the magnetic aging behaviors of the final sheet products produced by the two processing technologies and the corresponding principles were discussed,while steel 50W800 and 50W1300 were taken as examples.It is indicat... 

本发明提供虽然为薄壁但磁特性优异的方向性电磁钢板的制造方法。本发明的一个方案提供一种方向性电磁钢板的制造方法，其包括热轧工序、任选的热轧板退火工序、酸洗工序、冷轧工序、一次再结晶退火工序、成品退火工序和平坦化退火工序，在酸洗工序中，使用包含0.0001g/L～5.00g/L的Cu的酸洗溶液，冷轧钢板的板厚为0.15mm～0.23mm，一次再结晶退火工序的升温工序中的30℃～400℃的温度区域的平均升温速度超过50℃/秒且为1000℃/秒以下。

本实用新型涉及取向硅钢高温连续退火炉领域，尤其涉及一种取向硅钢高温连续退火炉隔离装置，包括安装在炉壳上的隔离炉门及设置在隔离炉门四周的密封井；隔离炉门顶部两侧安装有水冷却装置；水冷却装置上部设有隔离炉门动力牵引装置；密封井包括固定密封井和伸缩密封井，伸缩密封井位于固定密封井内部并与固定密封井滑动连接，伸缩密封井与固定密封井端部连接处设有密封装置。本实用新型可以确保隔离炉门升降过程中实现无缝全密封状态，提高密封效果，且采用伸缩密封井实际降低了密封井的高度，间接降低了水冷却装置连接管道上升至最高点的净空标高，与传统固定式密封井高度相比可以降低高度50％～80％，从而降低厂房净空标高，节省厂房基建投资。

介绍了双蓄热燃烧技术的特点和高温硅钢加热炉的特点,探讨了双蓄热燃烧技术在高温硅钢加热炉中使用的技术难点,分析了双蓄热燃烧技术在高温硅钢加热炉上使用的可能性。 Introduced characteristics of double regenerative combustion technology and high temperature silicon steel reheating furnace,discussed technical difficulties for using double regenerative combustion technology,analyzed the possibility of double regenerative combustion technology applied to high temperature silicon steel reheating furnace. 

对碳-锰-硅钢进行不同配分温度的Q&P(Quenching and Partitioning)处理,测试了热处理后不同钢的力学性能和残余奥氏体含量,并用扫描电子显微镜和透射电镜观察其显微组织,分析了配分温度对显微组织和力学性能的影响。结果表明:试验钢显微组织基本由低碳板条状马氏体、块状铁素体和条状残余奥氏体组成;随配分温度的升高,试验钢的抗拉强度呈下降趋势,伸长率与奥氏体含量的变化趋势相同,但变化规律不确定;提高锰含量能稳定残余奥氏体,从而提高试验钢的伸长率,并使伸长率对配分温度不敏感。 The C-Mn-Si steel was quenched and partitioned at different partitioning temperatures,the mechanical properties and residual austenite contents were investigated,the microstructure was observed by SEM and TEM,and the effect of partitioning temperature on microstructure and mechanical properties was analyzed.The results show that the microstructure of the tested steel consisted of lath martensite with low carbon,nubby ferrite and banded residual austenite.The tensile strength of the tested steel ... 

本发明涉及一种硅钢片视觉识别与无损检测方法，测量硅钢片的厚度并且计算已经叠积完成的硅钢片的总高度，记录最后叠积的一片硅钢片的形状和两定位孔坐标，计算和输出当前硅钢片的形状、两定位孔坐标的位置偏差值和两定位孔坐标的定位孔间距，记录硅钢片两端的接缝宽度和坐标并且输出搭接形状，判断定位孔间距、两定位孔位置、接缝宽度是否符合标准，以及两片硅钢片是否已经搭接上，通过打齐硅钢片使之符合要求、或者停机人工调整。本发明还涉及一种硅钢片视觉识别与无损检测装置。本发明利用激光测距仪、相机实现了无损检测，实现了每片硅钢片高度值、定位孔、接缝宽度的即时自动测量，通过PLC控制系统将控制信息传输至机械臂进行放置精度微调。

本发明提供了一种电工钢表面涂层剂及使用方法，所述电工钢表面涂层剂包括如下的压力重量份组分：碲化合物10～50份，树脂10～30份、硅烷偶联剂0.5～5份、柠檬酸13～18份，将得到的电工钢表面涂层剂涂布在钢基表面，加热干燥，烧结，形成涂层。形成的涂层附着力强，生产涂覆质量较好，过钢量达到预期2000吨以上，具有良好的防锈性能，磨损程度较低，同时绿色环保。

本发明公开了硅钢片铁芯生产线，包括放卷机构、剪切机构、送料机构、叠片机构和下料机构，送料机构包括磁性传送带、送料件和第一定位杆，磁性传送带包括上传送带和下传送带，送料件可沿磁性传送带的正交方向平行伸出，其中，第一送料分台和第二送料分台安装于上传送带的下方并且相背运动，第三送料分台和第四送料分台安装于下传送带的下方并且相背运动，第一定位杆用于定位硅钢片，叠片机构包括叠放台、悬梁和两个六自由度机械手，六自由度机械手吊装于悬梁上，包括有电永磁铁，用于吸取硅钢片，下料机构包括滑板，叠放台放置于滑板上。根据本发明的硅钢片铁芯生产线，可提高设备自动化程度，提高叠片速度，从而提高生产线的生产效率。

本实用新型公开了一种变压器铁芯硅钢片的收片装置，包括固定平台、硅钢片出料机构、压片机构、支撑平台和升降调节机构，所述固定平台设置在硅钢片出料机构的出料端下方，所述压片机构对应于硅钢片出料机构的出料口设置在硅钢片出料机构的上方，从所述硅钢片出料机构传送出的硅钢片通过压片机构压覆在固定平台上；所述固定平台上设置有升降调节机构，所述升降调节机构的升降端设置有支撑平台，所述支撑平台相对于固定平台在竖向方向上位移调节设置，能够对硅钢片叠放平面进行高度调节，保证出料高度的一致性，使得出料规整性较好。

一种含Bi高磁感取向硅钢热轧带钢边部质量控制方法：炼钢；连铸；铸坯加热；粗轧，粗轧道次不低于4道次，各道次压下率控制在20~33%；规精轧及进行后工序。本发明通过对热轧工序的控制，能使热轧带钢边部开裂的尺寸降低至不超过5mm，且边部开裂≤2mm比率能达到95%以上，后工序切边量很少甚至无需切边即可进行冷轧，使产品成材率能比现有技术提高2~4%；且由于铸坯加热温度的降低使能耗也随之降低。