本发明属于金属材料加工技术领域，具体涉及取向硅钢罩式炉高温退火低保温阶段节能工艺，包括：1)将涂镁取向硅钢卷装入密闭的罩式炉中，并向罩式炉内通入氮气将炉内氧气充分排出，使炉内氧含量浓度≤300PPm；2)通电升温并将氮气转换为10m3/h氮气与氨分解气的混合气体，升温2h将温度升温至500‑600℃后，恒温13h；3)将温度氮气与氨分解气的混合气体转换为12m3/h氨分解气，并升温2h将温度升至650℃恒温15h，使内部气体露点小于‑10℃；本发明提供退火工艺，钢卷在高温下不被水蒸汽氧化，消除钢带表面露金、发红、发黑、水印、色泽不均、导通缺陷，降低钢带铁损、提高磁感、降低生产成本。此外，本发明进一步减少退火过程中氨分解气的用量，具有极高的工业应用价值。

通过固溶度积公式计算及热模拟实验,对不同热装和加热温度条件下的无取向硅钢铸坯中析出相进行了研究.在低于950℃热装时,铸坯中AlN的析出量和尺寸不再变化,但MnS和AlN-MnS的数量及平均尺寸随着热装温度降低而进一步增加,并在温度低于600℃时达到最大值后保持不变.与1200℃相比,1100℃加热的铸坯中AlN、MnS的总固溶量相对更少.相比850℃热装,600℃热装再加热到1100℃的铸坯中AlN和MnS的总固溶量更少,且AlN和MnS尺寸更大.合适的热装温度和加热温度分别为600℃和1100℃. Based on solubility product calculation and thermal simulation experiments,precipitated phases in continuous casting slabs of non-oriented silicon steel were systematically studied at different hot charging and heating temperatures.When the hot charging temperature is below 950 ℃,the content and size of AlN remain unchanged,but the quantity and size of MnS and AlN-MnS increase when the hot charging temperature decreases,reach maximum and remain unchanged when the hot charging temperature is belo... 

硅钢高温退火环形炉炉壳制作与安装精度要求较高,施工时通过对壳体原材料矫正、炉壳板拼焊、下料切割、型钢骨架组装及焊接、骨架及炉壳板矫正、骨架与炉壳板组装及焊接、炉壳矫正、零配件装置、定位钻孔、报验检查、出厂、内侧板安装、外侧板安装、顶板安装等环节的工艺技术控制,能保质高效地完成硅钢高温退火环形炉炉壳制作与安装,为以后同类工程的施工提供可借鉴经验。 The required precision of manufacture and installation technique of the silicon steel high temperature annealing annular-furnace shell is high.During construction , manufacture and installation of the silicon steel high temperature annealing annular-furnace shell could be finished high efficiently through correcting the raw materials of shell , furnace shell plate welding , material cutting , steel frame assembly and welding , skeleton and shell plate correction , skeleton and furnace shell asse... 

本发明公开了一种硅钢冷连轧轧制过程温度获取方法、装置及电子设备，通过获取硅钢冷连轧生产过程的工业参数数据以及各机架间硅钢的实际温度测试数据，然后基于工业参数数据以及预设初始模型，确定硅钢冷连轧生产过程的温度预测模型，接着基于硅钢轧制前的预热温度以及温度预测模型，得到硅钢冷连轧轧制过程各机架变形区出口与下一机架变形区入口之间的预测温度数据，再将预测温度数据与实际温度测试数据进行对比，并根据对比结果中的温度差异值对相应机架间的乳化液参数进行修正，直至温度差异值小于预设阈值，得到修正后的温度预测模型，能够用于实现硅钢冷连轧轧制过程中，任意采样点硅钢温度的获取。

通过对激光粒度分析仪测量硅钢级氧化镁(MgO)的分析条件进行优化,如分散介质、分散方式、样品预处理、仪器暗淡度等,探讨了硅钢级MgO粒度范围测量重现性较好的试验方法,满足硅钢生产过程控制对MgO粒度的要求。 The analysis condition of the laser particle size analyzer on grain oriented silicon-steel grade magnesium oxide is optimized,including the dispersion medium,dispersion methods,sample preparation,and instrument obscuration,etc.Therefore,particle size measurement with good reproducibility for silicon-steel magnesium oxide is discussed,which may meet the requirement of MgO particle size for silicon-steel process control. 

冷轧取向硅钢工程中有很多的超长、大体积以及薄壁的混凝土结构,裂缝控制是土建施工的关键。在工程中,按照\"抗放兼施、先放后抗、以抗为主\"的原则,采用\"无缝分块跳仓法\",防止超长混凝土结构收缩产生裂缝;在隧道和池体的底板与墙板施工中,采用\"整体浇筑\"法,避免了墙板因约束应力而产生的裂缝。 In the Cold-rolled grain-oriented silicon steel project,there are many overlength,bulk mass,thin-walled concretes structures,how to control the crack is the key of civil engineering construction.In these projects,according to the principle of\"release with resist,resist before release,resist is dominant \",the crack of the over-long structure and shrinkage can be prevented by the method of\"seamless block skip bin \".In the construction of the bottom plate and wall of the tunnel and the pool,the cra... 

本发明涉及一种含磷高磁感无取向硅钢的生产方法，工艺路线：铁水脱硫－转炉冶炼－RH精炼－连铸－热轧－酸洗－冷轧－连续炉退火－涂层－性能检验－包装，具体步骤包括：1)将钢水冶炼至目标成分后采用连铸方式将钢水铸成坯；2)热轧板坯加热炉均热段板坯温度950～1050℃，终轧温度控制在780～830℃，卷取温度600～680℃；3)酸洗后冷轧，控制冷轧整体压下率80％以上，至成品厚度，增加剪切带组织；4)连续退火炉快速加热段温度设定1000～1150℃，增加有利织构组织形核；均热段温度设定750～830℃，全氮气干气氛保护，退火工艺速度110～150m/min，满足晶粒度8～4级。本发明在减少硅、铝、锰合金添加量的情况下，改善铁损提高磁感性能，提高机械性能。

本发明揭示了一种高硅无取向电工钢及其生产方法。该方法包括：1）钢水冶炼并连铸成坯；2）加热并保温，之后热轧得到热轧卷板，其中粗轧出口温度940±20℃，精轧终轧温度840±20℃，卷取温度650±20℃；3）常化，常化温度((732~742)+3000[Si])℃，常化时长4min~5min；4）常化后直接进行冷轧，而后连续退火和涂层，退火温度940℃~990℃且退火时长1.5min~3min；5）涂层处理后的钢板加工成型，而后进行去应力退火，退火温度为((761~766)+3000[Si])℃。如此，在保证磁性能的同时，解决了冷轧难度大的问题。

【机构】 武钢研究院； ...

​6月28日国联证券发布：《电力设备出海2024年中期投资策略：需求方兴未艾，供给释...

本发明涉及取向硅钢技术领域，尤其涉及一种取向硅钢边浪的控制方法、装置、设备和存储介质，该方法包括：在将通过脱碳退火阶段的取向硅钢的带钢进行卷取过程中，在带钢的下端侧上刻上刻痕线，其中，下端侧为带钢与高温退火炉的承托底板接触的一侧，刻痕线平行于带钢轧制的方向；控制卷取后的带钢通过高温退火阶段和热拉伸平整阶段后至精整阶段时，沿着刻痕线，切除带刚的边浪；其中，边浪为在带钢的刻痕线至下端侧的边的部分。该控制方法可显著改善高温退火后取向硅钢边部浪形，有效降低精整切边量，提高取向硅钢的板形质量及成材率，降低生产成本。

一种硅钢变压器绕线模具，包括模具本体、顶梁、举升梁、螺杆、绕盘，其特征在于顶梁设置在模具本体的顶部，举升梁设置在模具本体的下端，模具本体的顶端设有螺丝杆，顶梁穿过螺丝杆通过活动螺母固定，模具本体的中部设有镂空，螺杆转动设置在镂空中，螺杆穿过模具本体下端与绕盘连接，模具本体的中部设有至少两个连接梁，举升梁在连接梁中穿过移动，并且中部穿过螺杆，模具本体的底部设有槽体，模具本体的中部连接梁与槽体底部链接，举升梁移动到最低点时设置在槽体内，本方案通过螺杆和绕盘以及举升梁的相互作用将线圈通过机械能作用顶出模具，省去了人为的力量。