本实用新型属于冷轧硅钢技术领域的一种冷轧硅钢无压回水自动控制设备，包括底座，底座外表面的上端固定连接有工作台，工作台外表面上端的两侧分别固定连接有固定柱和压辊主体，工作台外表面上端的中部滑动连接有移动架，压辊主体的下端设置有集水槽，集水槽的内表面设置有浮球液位传感器。液压杆工作推动移动架位移到合适的位置，再通过气缸使伸缩管发生位移，使出水口接近钢板，设置的水箱高于出水口所以水可以在重力的作用下流淌，流出的水流到集水槽内，水流在集水槽内聚集，水流使浮球液位传感器的浮球上升，上升到合适的位置时，浮球液位传感器通过电缆发生电信号至控制器，此设置可以实现设备的自动控制，省去人工进行操作。

针对攀钢高硫铁水冶炼现状,结合不同生产工艺路线,论述了攀钢近年来为实现低硫电工钢的生产,在铁水预处理、转炉冶炼、钢水精炼过程中硫控制技术的开发与应用,形成了低硫洁净钢生产工艺技术,实现了低硫电工钢的生产。低硫电工钢RH脱硫率可达到20%左右,成品[S]控制在0.006%左右。 According to the smelting situations of hot metal with high sulphur content at Panzhihua Steel,combined with different produce processes,technologies for controlling the sulfur content during hot metal pretreatment,converter smelting,and second refining are developed. Technologies in low-sulfur clean steelmaking are formed. Low-sulfur electric steel are produced. As for the desulfurization rate of lowsulfur electric steel can reach about 20%,and the content of [S] in products is controlled to ab... 

本实用新型涉及硅钢片钢卷制造技术领域，且公开了一种用于硅钢片钢卷制造的收卷装置，解决了现有硅钢片钢卷制造过程中不便于更好的进行收卷的问题，其包括收卷辊，所述收卷辊的两侧边均对称安装有固定连接杆，固定连接杆远离收卷辊的一端安装有连接板，连接板远离固定连接杆的一侧边中部安装有连接轴，收卷辊的顶部与底部均对称连接有活动挡板，收卷辊的内部开设有安装槽，安装槽的内部安装有调节机构，且调节机构与活动挡板连接；本实用新型，便于能够确保在收卷过程中硅钢片钢卷不会发生偏移，以便于能够达到更好的收卷效果。

本实用新型公开了一种无取向硅钢喷涂用即时干燥装置，包括干燥箱，所述干燥箱内滑动连接有加热台，所述干燥箱顶部设置有加热箱，所述加热箱左右两侧分别设置有进风管和出风管，所述进风管和出风管均与干燥箱连通，所述加热箱内部从左到有依次固定连接有风机和加热网，所述干燥箱内设有带式传送机，通过带式传送机使喷涂过后的硅钢在干燥箱中移动，首先经过加热台加热，使涂层表面干燥硬化，不会变形，然后再经过加热箱吹出的风对硅钢表面的涂层进行进一步的烘干，从而保证干燥过程中涂层不会起褶皱。

本发明涉及无取向硅钢技术领域，具体提供了一种无取向硅钢的制备方法，对再结晶率为70‑90％、平均晶粒尺寸为10‑15μm、硬度HV为140‑170的硅钢半成品在温度为T＝(772～777)+2900×W(Si)的条件下进行去应力退火，制得无取向硅钢，晶粒在去应力退火过程中均匀长大，平均晶粒尺寸80μm以上，有效降低铁损，使磁性能大幅度提高，铁损P1.5/50≤3.5W/kg，磁感B5000≥1.72T，电磁性能优异，满足客户使用要求，此外，本发明采用的硬度HV为140‑170的硅钢半成品在冲压过程中不易变形，机械加工性能优良。

【摘要】 <正>3月15日,随着第5754卷HiB钢下线,武钢...

借助高温激光共聚焦显微镜,在线观察了不同Mn含量的无取向硅钢中夹杂物的尺寸、类型、数量变化。结果表明,Mn含量(质量分数)为0.77%、0.32%时,试样中的夹杂物数量分别约为1000万个/mm3、1600万个/mm3。Mn含量较高的钢种,会优先析出球形、椭球形MnS夹杂物,其析出数量较少,尺寸相对较大,可以有效抑制AlN、CuxS夹杂物析出;Mn含量较低的钢种,会在试样再加热后冷却过程中,先析出相当数量MnS夹杂物,并作为AlN夹杂物析出核心,形成MnS+AlN复合夹杂物。这种复合夹杂物数量较多,尺寸也较大。 Based on the high temperature confocal microscope, the chage of size, type, and quantity of inclusions in non-oriented silicon steels with different Mn content were observed by in-situ SEM. Results show that the inclusion quantities are 10 million per mm3 and 16 million per mm3,while the mass fractions of Mn are 0.77% and 0.32%, respectively. In the silicon steel with higher Mn content, the spherical and ellipsoidal MnS inclusion will precipitate first, which can retard the precipitation of AlN ... 

两炉次无取向硅钢XG800WR（/%:0.003～0.004C、0.71～0.75Si、0.32～0.33Mn、0.004～0.007S、0.016P）的炼钢流程为铁水预处理（KR）-210 t顶底复吹转炉-钢包吹氩-RH脱碳精炼-230mm×1220 mm板坯连铸。53 t中间包钢水过热度为25～30℃,钢包到中间包采用长水口全程吹氩保护浇铸,中间包至结晶器采用浸入式水口浇铸。结果表明,在RH、中间包、结晶器过程中钢中总氧以及夹杂物数量和尺寸均明显降低;但在钢包到中间包过程T[O]、[N]和钢中夹杂物数量增加,说明长水口浇铸过程存在二次氧化。连铸坯中T[O]、[N]平均他分别为11×10^-6和30×10^-6,显微夹杂物数量平均为4个/mm²。铸坯中的显微夹杂物主要为3～5μm的AlN,同时存在少量的MnS、Al₂O₃·AlN和Al₂O₃·MgO·MnS。 The steelmaking flow sheet for two heats non-oriented silicon steel XG800WR（/%:0.003～0.004C. 0.71～0.75Si,0.32～0.33Mn,0.004～0.007S,0.016P） is hot metal pretreatment（KR）-210 t top and bottom combined blown converter-ladle argon blowing-RH decarburization refining-230 mm×1 220 mm slab casting.The superheating extent of liquid in 53 t tundish is 25～30℃,whole casting is shielded by blowing argon with long nozzle from ladle to tundish and the submerged nozzle is adopted in casting from tundish to mold... 

本发明公开了一种控制无取向硅钢厚度稳定性的轧制工艺，涉及硅钢厚度控制方法领域。本发明通过降低硅钢精轧入口温度，并调节粗轧区域、精轧区域和卷取区域的生产参数，保证后续卷取工序的轧制稳定性及卷形质量，严格控制无取向硅钢的厚度稳定性。本发明提供的轧制工艺使硅钢的厚度命中率得到了明显提升，提升了后续冷轧工艺的轧制速度，轧制力波动减小，提高了产品质量。

本实用新型涉及钢卷加热装置技术领域，且公开了一种用于硅钢片钢卷制造的加热装置，目前硅钢片钢卷加热不均匀的问题，其包括加热箱，所述加热箱的内腔一侧活动安装有主动轴，主动轴的外侧固定安装有主动齿轮，主动轴的左侧固定安装有位于加热箱外侧的电机，主动轴的两侧均活动安装有从动轴，两个从动轴的外侧均固定安装有从动齿轮，本实用新型，通过电机和主动轴以及主动齿轮的配合，可使得主动轴转动，并通过主动齿轮与两个从动齿轮的啮合，进而使得从动齿轮和主动齿轮同时转动，并通过两个加热盘对加热箱内部进行加热，从而使得固定盘和连接盘之间的钢卷边转动边加热，从而解决了硅钢片钢卷加热不均匀的问题。

本发明提供一种改善表面麻点缺陷的薄规格中低牌号无取向硅钢及其生产方法，成分C≤0.0025％，1.2≤Si≤1.65％，0.25％≤Mn≤0.35％，0.06％≤P≤0.11％，0.1％≤Als≤0.2％，S≤0.0025％、N≤0.0025％，Ti≤0.0025％，其余为Fe及不可避免的杂质。与现有技术相比，本发明采用较低氢气浓度，防止炉内氧化铁皮还原，减轻碳套辊的腐蚀程度，减少碳套辊结瘤率，改善带钢表面质量；采用合理合金成分设计，提高带钢的力学强度，降低碳套辊结瘤对带钢表面的影响程度，改善带钢表面质量。产品厚度为0.35mm，板面麻点发生率降低，无手感，且辊身周长周期范围内麻点个数≤5个。