硅钢资料

无氧化炉具有加热效率高、投资与运营成本低、作业率高、表面质量及板型良好、NOx排放相对低等优势,在硅钢热处理领域应用前景广泛。本文阐述了确定无氧化炉(NOF)加热能力详细过程,涵盖炉温、炉断面尺寸、炉长、热平衡结算、加热能力计算等,为今后无氧化炉(NOF)在硅钢热处理应用时的设计提供了借鉴,同时也为今后明火直接加热的工业炉设计提供了参考。 Non-oxidation furnace has the advantage s of high heating efficiency, low investment and operation cost, high operation rate, good surface quality and plate shape, and relatively low NOxemission,and it still has wide application prospect in the field of silicon steel heat treatment. The detailed process of determining the heating capacity of a non-oxidizing furnace(NOF) is described, covering furnace temperature, furnace section size, furnace length, heat balance settlement, heating capacity cal... 

本文介绍了无取向硅钢C6涂液的性能,研究了配水量、固化程度和涂层厚度等因素对无取向硅钢C6涂层性能的影响。结果表明,随着配水量的增加,完全固化所需的时间增加,涂液固体含量降低,涂层厚度减小;随着固化程度的提高,涂层硬度先增大然后趋于恒定,而柔韧性逐渐变差,在过固化后急剧恶化;涂层厚度对涂层的表面外观、附着性和绝缘层间电阻均有显著影响。 Based on the introduction about the performance of C6 varnish for non-oriented silicon steel sheets,effects of water amount,curing degree and coating thickness are discussed. Results show that with the increase of water amount,the time required to cure completely extends,and both the solid content of C6 varnish and the coating thickness decrease. As the curing degree increases,the hardness of the coating increases first and then tends to be constant,however the flexibility degenerates,especially... 

采用热模拟方法及EBSD技术,研究Fe-3 wt%Si电工钢在不同温度下组织的动、静态再结晶及晶粒取向特征,特别是少量奥氏体对铁素体动、静态再结晶组织及取向的影响。结果表明,不同温度形变的组织主要分三类:形变长条铁素体、珠光体和等轴细小铁素体。长条形变铁素体内发生动态回复或连续式的动态再结晶,奥氏体周围的铁素体动态再结晶加速,部分以传统的不连续方式动态再结晶。铁素体、奥氏体都可发生静态再结晶。奥氏体的静态再结晶在1050℃以上明显,铁素体的静态再结晶随温度的升高逐渐进行,最显著的再结晶发生在1050℃。不同温度形变的样品,其形变晶粒取向主要以<111>和<100>为主,小等轴铁素体晶粒除与大形变铁素体取向相近外,出现了<110>取向及其它取向。 Static and dynamic recrystallization and grain orientations in a hot-compressed Fe-3 wt% Si electrical steels were studied at different temperatures using Gleeble simulator and EBSD technique,particularly focusing on the effect of small amount of austenite on ferritic microstructure and orientations.The results show that microstructure of the compressed steel,depending on deformation temperature,consisted of elongated and deformed ferrite,pearlite and fine equal-axed ferrite.The elongated ferrit... 

本发明涉及硅钢技术领域，尤其涉及一种硅钢连退炉辊除瘤方法及装置。包括连杆、手柄、磨削片、密封盖、端盖与套筒；磨削片垂直固接在连杆一端的外壁上，手柄固接在连杆的另一端，手柄与磨削片处于同一平面上；连杆套接在套筒内，连杆能沿套筒轴向移动，套筒固接在端盖上；硅钢连退炉辊下方的炉墙设有与连杆及磨削片相应的磨辊孔，端盖或密封盖固接在磨辊孔处。1)确定结瘤炉辊；2)确定结瘤在碳套辊上的位置；3)插入除瘤装置；4)磨削；5)抽出。本发明降低废品量，提高成材率；减少停炉处理结瘤时间，降低能耗，提高生产率；提高难磨瘤辊的修复率，降低炉辊成本。

通过固溶度积公式计算及热模拟实验,对不同热装和加热温度条件下的无取向硅钢铸坯中析出相进行了研究.在低于950℃热装时,铸坯中AlN的析出量和尺寸不再变化,但MnS和AlN-MnS的数量及平均尺寸随着热装温度降低而进一步增加,并在温度低于600℃时达到最大值后保持不变.与1200℃相比,1100℃加热的铸坯中AlN、MnS的总固溶量相对更少.相比850℃热装,600℃热装再加热到1100℃的铸坯中AlN和MnS的总固溶量更少,且AlN和MnS尺寸更大.合适的热装温度和加热温度分别为600℃和1100℃. Based on solubility product calculation and thermal simulation experiments,precipitated phases in continuous casting slabs of non-oriented silicon steel were systematically studied at different hot charging and heating temperatures.When the hot charging temperature is below 950 ℃,the content and size of AlN remain unchanged,but the quantity and size of MnS and AlN-MnS increase when the hot charging temperature decreases,reach maximum and remain unchanged when the hot charging temperature is belo... 

利用OM、SEM、TEM等实验方法研究了卷取工艺对一种新型含铜无取向电工钢晶粒度和析出相的影响。结果表明,该电工钢热轧带卷取后的晶粒尺寸为18～24μm,在卷取过程中,热轧带中有一定数量的第二相析出,经EDS能谱及选区电子衍射分析,这些析出相主要为AlN。随着卷取工艺的变化,该电工钢的晶粒度大小变化不明显,析出相的类型、尺寸大小不发生改变,体积分数发生一定的改变。 The effects of coiling process on grain size and precipitates of a new copper-bearing non-oriented electrical steel were investigated by OM,TEM and other experimental method.The results show that the grain size of hot-rolled bands after coiling is 18～24 μm.The second phases precipitate during coiling process.They are mainly AlN by EDS spectra and selected area electron diffraction.With the change of coiling process,the grain size of the electrical steel does not change significantly;the type and... 

本发明涉及电工钢的生产方法，更具体地说，涉及一种预应力生产中低牌号无取向电工钢的方法，包括铁水预处理；预处理后的铁水进行转炉冶炼并吹氩脱氧；吹氩后的钢水送入精炼炉中进行冶炼并加入低碳合金进行合金化；合金化处理的钢水通过薄板坯连铸机铸成板坯并采用薄板胚连铸连轧生产工艺进行轧制获得热轧板；所述热轧板经过酸洗冷轧，随后进行预应力拉伸并退火，采用涂层进行涂镀、烧结后卷取。本发明采用预应力拉伸，改善无取向电工钢退火前钢板内部应力的分布，制备的冷轧无取向电工钢产品的电磁性能P15/50≤5.4W/kg，磁感应强度≥1.72T，板形同板差≤8um。

本发明属于酸洗设备技术领域，具体涉及一种硅钢生产用酸洗设备，包括酸洗池、放卷机构和收卷机构，酸洗池被依次分隔为第一酸洗腔、第二酸洗腔、浸泡腔和喷洗腔；第一酸洗腔和第二酸洗腔内滑动连接有刷洗架，浸泡腔内滑动连接有定位架，喷洗腔内滑动连接有喷洗架；刷洗架、定位架和喷洗架上均转动连接有多根转辊，转辊上设有刷毛；刷洗架和喷洗架上设有用于驱动转辊转动的驱动件；喷洗架上的转辊开有空腔和多个与空腔连通的喷孔，喷洗架上开有与空腔连通的通道和与通道连通的进水口；喷洗腔的底部和侧壁设有多个喷头；酸洗池内转动连接有多根位于第一隔墙上方的刷辊。在本方案，通过酸洗以及充分的刷洗，能够充分有效的除去硅钢表面的氧化皮。

本发明提供在金属带钢表面以所希望的槽宽度形成线状槽进而磁特性极其优异的方向性电磁钢板。在金属带钢的至少单面形成抗蚀剂被膜，接着，对上述抗蚀剂被膜一边在横穿上述金属带钢的轧制方向的方向进行扫描一边照射激光，除去经上述激光照射的部分的上述抗蚀剂被膜，接着，对上述金属带钢的除去了上述抗蚀剂被膜的部分实施蚀刻处理而形成线状槽，上述抗蚀剂被膜以固体成分换算计含有20质量％以上的无机化合物，在上述金属带钢表面，上述激光具有长轴直径与短轴直径之比为5.0以上的椭圆状的射束形状，并且扫描正交方向的射束直径为10μm～100μm。

一种电工钢切片用辅助定位装置，涉及电工钢加工技术领域，包括加工台、支撑腿、定位块、侧板、滑杆、移动板、顶板、滑动架、伸缩杆、切片装置、定位杆和挡板；支撑腿设置在加工台底部；定位块设置有两组，两组定位块均设置在加工台上，两组定位块沿横向分布，每组定位块设置有两个，每组的两个定位块沿纵向分布；侧板设置有两个，两个侧板均设置在加工台纵向一侧，两个侧板沿横向分布；滑杆设置在两个侧板之间；移动板沿横向滑动设置在滑杆上；顶板设置在移动板靠近加工台的纵向一侧，顶板位于移动板上端。本实用新型能够方便工作人员切割出一定尺寸的电工钢切片，且切割精度很高。

提供能够稳定地制造磁特性优异且钢卷长度方向的铁损的偏差少的取向性电磁钢板的取向性电磁钢板的制造方法。本发明是一种取向性电磁钢板的制造方法，包括如下工序：对钢坯进行热轧，根据情况实施退火，然后通过1次冷轧或夹有中间退火的2次以上的冷轧来制成具有最终板厚的冷轧板，接着对上述具有最终板厚的冷轧板进行脱碳退火，然后实施二次再结晶退火；在最终的冷轧之前，将钢板以100℃/s以上的升温速度加热到100℃～350℃的加热温度，上述钢板从达到加热温度到进入最终的冷轧的第1道次的时间为5秒以内。

介绍了CSP工艺生产无取向电工钢各工序的设备特点、采用的工艺控制手段和电工钢产品质量情况,结合生产实践证明了马钢CSP工艺开发的无取向电工钢产品丰富了薄板坯连铸连轧的品种结构,发挥了薄板坯连铸连轧生产无取向电工钢性能均一、稳定的特点。 The equipment characteristic,the process control method and the quality of non-orientated silicon steel by CSP process were introduced.Combined with the production situation,it is proved that production of non-orientated silicon steel developed on Masteel CSP line would enrich product structure of thin slab continuous casting and rolling,and it exerts stable performance of non-orientated silicon steel.