硅钢资料

为了提升新能源车用驱动电机的功率密度,各大电机厂商都在不断地提升电机转速,随之而来的问题就是电机的铁耗也在不断增高,如何降低电机铁耗成为了电机厂商必须要解决的难题。本文讨论了电机铁耗的组成部分及影响因素,并对1台8极48槽的永磁同步电机分别使用3种不同厚度的材料进行仿真,对比其效率及铁耗分布,推导出驱动电机中硅钢厚度、铁耗及成本的关系,最后对驱动电机选材提出建议。 In order to increase the power density of traction motor for new energy vehicles,major motor manufacturers have been constantly increasing the motor speed.The following problem that manufacturers have to solve is how to reduce the increasing iron loss when the motor speed is increased.The components and influencing factors of motors’ iron loss were discussed in this paper,and an 8-pole 48-slot permanent magnet synchronous motor using three different thickness materials was simulated.To compare i... 

借助实验室设备研究了B元素对高牌号无取向硅钢热轧板组织和磁性能的影响。结果表明,与无硼钢相比,含硼钢的热轧板晶粒尺寸略小,析出物的类型和尺寸没有区别,主要是AlN和(AlN+MnS)复合析出物,少量的MnS析出物,尺寸集中在1.0～2.5μm范围内。未发现BN析出物。在力学性能方面,B对钢的软化作用不明显。在磁性能方面,含硼钢的铁损为3.215W/kg,磁感为1.710T,综合磁性能比无硼钢差。 Influences of boron on microstructure and properties of hot rolled band in high-grade non-oriented silicon steel are researched in this paper by experimental equipments.Compared with boron-free steel,the result shows that boron-bearing steel has smaller grain size,but the type and size of precipitations have no differences.The main precipitates are AlN,(MnS + AlN) composite precipitate and few MnS,the range of which are between 1.0 μm and 2.5 μm.BN precipitation is not found.With reward to mecha... 

本实用新型涉及硅钢二次轧制的技术领域，且公开了一种用于硅钢成品二次轧制的轧辊间距调整机构，包括安装架，所述安装架的内部设置有上、下相对的两组工作辊，两组工作辊的内部均固定连接有转轴，外侧均滑动连接有保护组件，其中下工作辊通过保护组件与安装架固定连接，上工作辊的上方固定连接有升降组件，上、下两组工作辊之间固定连接有限位组件，通过升降组件带动上工作辊的上下移动，来调整上工作辊和下工作辊之间的距离，保持二次轧制时较大的压下率，同时限位机构能有效防止因工作辊距离太近而导致的硅钢断带的情况。

本实用新型公开了一种硅钢环形炉台车用垫片，垫片为多个陶瓷纤维高密度板拼接而成的环状，垫片的内边缘和外边缘均呈正八边形；陶瓷纤维高密度板的导热系数不大于0.15W/(m·k)。上述垫片在实际使用时，铺设于台车的底座，并在垫片上砌筑耐火砖，最后在耐火砖上浇筑耐火浇注料。因垫片的导热系数很低，因此能够减少台车底座背面热量的散失，并且能够避免高温对台车内钢卷造成影响，保证了钢卷的质量。因此，本实用新型提出的硅钢环形炉台车用垫片，对台车进行了改进，保证了钢卷的品质，解决了现阶段该领域的难题。

本发明涉及取向硅钢技术领域，尤其涉及一种取向硅钢边浪的控制方法、装置、设备和存储介质，该方法包括：在将通过脱碳退火阶段的取向硅钢的带钢进行卷取过程中，在带钢的下端侧上刻上刻痕线，其中，下端侧为带钢与高温退火炉的承托底板接触的一侧，刻痕线平行于带钢轧制的方向；控制卷取后的带钢通过高温退火阶段和热拉伸平整阶段后至精整阶段时，沿着刻痕线，切除带刚的边浪；其中，边浪为在带钢的刻痕线至下端侧的边的部分。该控制方法可显著改善高温退火后取向硅钢边部浪形，有效降低精整切边量，提高取向硅钢的板形质量及成材率，降低生产成本。

本实用新型涉及一种堆叠定子硅钢片复位装置，主要包括气动按压装置与弹簧悬架，弹簧悬架中设有的硅钢片放置板，硅钢片放置板中心部位嵌入式连接有滑动杆，滑动杆的一侧设有固定顶针，且滑动杆的顶部还设有弧形倒角，滑动杆一端套接有硅钢片，另一端与固定板连接；固定板两侧上套接有轴套，轴套内滑动设置有定位滑轴，定位滑轴的外部套接有螺旋弹簧组成弹簧减震器，且螺旋弹簧设置在轴套上底面与硅钢片放置板下底面之间；这种结构的设置通过硅钢片放置板上设置的固定顶针，使得硅钢片与硅钢片放置板之间的连接更加稳定，同时通过弹簧减震器的设置可以降低机器手下压的压力，从而增强硅钢片的承受力。

本发明属于退火工艺技术领域，公开了一种高牌号无取向硅钢剪切方法，包括：待剪切带钢由夹送辊输送到达剪切位后，夹送辊释放对所述待剪切带钢的夹持；位于所述待剪切带钢下方的下剪刃上移，推顶所述待剪切带钢在低张力状态下持续向上运动；在所述待剪切带钢与上剪刃接触后，将所述待剪切带钢剪断。本发明提供的高牌号无取向硅钢剪切方法能够极大的减少高牌号无取向硅钢的剪切缺陷，降低废品量，提升剪切效率。

从取向硅钢生产路线的选择、工艺技术的改进和生产设备的改造三方面进行了生产取向硅钢的节能降耗技术改造.通过完善多元抑制剂配方生产低温取向硅钢,通过加抛丸的酸洗、带面超声波清洗、改进连续退火炉以及余热循环利用等技术改造,使2012年取向硅钢的产量与未进行技术改造前的2009年相比提高了2.5倍,产品磁性上升了一个半牌号,能耗下降了8.9%,成材率提高了6.4%,生产成本下降了22%,综合效益显著. Energy saving technological transformation was carried out in the production of grain oriented silicon steel from three aspects of the oriented silicon steel production process route selection,technology improvement and equipment renovation.Through the improvement of multiple inhibitor formulations for producing low-temperature grain-oriented silicon steel,and by adding the blasting pickling,the belt surface ultrasonic cleaning,improvement of continuous annealing furnace,waste heat recycling tec... 

以构建高磁感、低铁损、免轧制高硅电工钢铁芯为出发点,提出采用单辊甩带制备非晶铁硅合金薄带、微氧化法在铁硅合金粉末表面包覆高电阻率铁硅氧化物薄膜制备核壳异质结构高硅电工钢纳米粉末、放电等离子烧结快速成形制备颗粒间绝缘的高硅电工钢铁芯。研究了不同氧化包覆时间对SPS烧结试样密度、物相组成、微观结构和静磁性能的影响。研究表明,在氧化包覆5h烧结温度800℃工艺条件下,制备的6.5%Si高硅电工钢铁芯的静磁性能最佳,饱和磁化强度为128.84A.m2/kg、矫顽力为2.25kA/m、剩磁为3.47A.m2/kg。其饱和磁化强度与粉末压延法制备的高硅钢相当,但矫顽力降低了1/3。 The paper takes preparation 6.5%Si steel with high induction,low core loss and removing rolling as the starting point,amorphous Fe-Si ribbons was synthesized by melt spinning method,6.5%Si steel nanopowders with high resietivity core shell structure was prepared by the slight oxidation process and 6.5% Si steel iron core with evaluating internal was sintered by spark plasma sintering process(SPS).The essay focuses studies the effects of different oxidation cladding time on sample density,phase c... 

采用低温板坯加热制备取向硅钢,通过透射电镜(TEM)观察并研究热轧板中的析出物,用ODF织构法研究热轧板距表面1/8、1/4和1/2处的织构分布。结果表明,热轧板中的析出物主要是密排六方AlN,AlN形貌呈规则长方形,AlN颗粒大小不等,分布密度低;热轧板中的织构沿板厚方向,由亚表层的{110}<001>织构向1/2中心层的α线织构变化,其中{110}<001>织构在热轧板距表面1/4层处最强。 The low temperature grain-oriented silicon steels were produced by acquired inhibitor method.The precipitates in hot rolling strip were observed and studied by transmission electron microscope,and the texture distribution in 1/8,1/4 and 1/2 layers of hot rolling strip were analyzed by ODF method.The results showed that the square shaped h-AlN is the main precipitates in hot rolling strip.The precipitates are varying in size and distribution.The texture of hot rolling strip in thick direction are... 

应用CAFE法对6.5%Si高硅钢铸锭凝固组织进行了模拟研究,确定出了适合高硅钢组织模拟的模型。进一步用该模型研究了过热度及冷却条件对凝固组织的影响,结果表明,随着过热度的降低,凝固组织中柱状晶比例和晶粒平均面积均减小。水冷条件下,高硅钢铸锭凝固组织几乎全是柱状晶,而且晶粒粗大。空冷条件下,等轴晶区扩大,但柱状晶仍占主要部分。缓冷条件下,等轴晶区占主要部分,晶粒平均面积和空冷条件下相当。 The solidification structure of 6. 5% Si steel ingot was simulated based on CAFE method and the model suitable for simulating the structure of high silicon steel wad ascertained. The influence of superheat and cooling condition on the solidification structure were studied. It was shown that with the superheat decreasing,the proportion of columnar crystals decrease,and the average grain size become smaller. Under water cooling condition,the solidification structure of casting was composed of almo... 

无取向硅钢特别是中牌号以上的无取向硅钢,随着含硅量的提高,常温下塑性较差,冷轧过程中轧制力明显提高,如果存在原料质量问题,极易发生断带事故,影响硅钢冷轧过程的成材率和生产效率。通过优化冷轧工艺参数,可提高冷轧稳定性。生产中通过合理分配冷轧各道次压下量和轧制速度,保证了轧制过程的稳定,很大程度减少了冷轧断带事故的发生。 Non-oriented silicon steel, especially in the low and middle grade, with the increase of silicon content, plasticity is poor at room temperature, rolling force in cold rolling process significantly improved .If there is the quality defect of raw materials , easily sheet is rolling off. Affect finished product rate and production efficiency in process of cold-rolled silicon steel. Through optimization of cold rolled process parameter , improve the stability of cold-rolling process. Through reason...