B元素对高牌号无取向硅钢热轧板组织和性能的影响

【作者】
李永超;
樊立峰;
项利;
岳尔斌;
张延玲;
仇圣桃;

【Author】
LI Yong-chao1,2,FAN Li-Feng2,XIANG Li2, YUE Er-bin2,ZHANG Yan-ling1,QIU Sheng-tao2(1.School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing,Beijing 100083,China; 2.National Engineering & Research Center of Continuous Casting Technology CISRI,Beijing 100081,China)

【机构】
北京科技大学冶金与生态工程学院;
钢铁研究总院连铸技术国家工程研究中心;

【摘要】 借助实验室设备研究了B元素对高牌号无取向硅钢热轧板组织和磁性能的影响。结果表明,与无硼钢相比,含硼钢的热轧板晶粒尺寸略小,析出物的类型和尺寸没有区别,主要是AlN和(AlN+MnS)复合析出物,少量的MnS析出物,尺寸集中在1.0~2.5μm范围内。未发现BN析出物。在力学性能方面,B对钢的软化作用不明显。在磁性能方面,含硼钢的铁损为3.215W/kg,磁感为1.710T,综合磁性能比无硼钢差。 

【Abstract】 Influences of boron on microstructure and properties of hot rolled band in high-grade non-oriented silicon steel are researched in this paper by experimental equipments.Compared with boron-free steel,the result shows that boron-bearing steel has smaller grain size,but the type and size of precipitations have no differences.The main precipitates are AlN,(MnS + AlN) composite precipitate and few MnS,the range of which are between 1.0 μm and 2.5 μm.BN precipitation is not found.With reward to mecha… 

【关键词】 无取向硅钢;
硼元素;
析出物;
铁损;
磁感;

【Key words】 non-oriented silicon steel;
boron element;
precipitations;
core loss;
magnetic induction;
【基金】 国家自然基金项目(50734001)

原文发表于《金属功能材料》2011年第05期

论文PDF全文下载

此内容查看价格为5.8立即购买(VIP免费)
不用注册会员、不用登陆账号,直接支付购买查看,客服QQ:1093451816,此外成为本站VIP可免费查看本内容。
原文链接:http://1guigang.com/down/thesis/45253.html,转载请注明出处~~~
0
广告位招租

站点公告

网站试运行,请大家关注本站公众号,多提宝贵意见!

显示验证码
没有账号?注册  忘记密码?