【摘要】 应用CAFE法对6.5%Si高硅钢铸锭凝固组织进行了模拟研究,确定出了适合高硅钢组织模拟的模型。进一步用该模型研究了过热度及冷却条件对凝固组织的影响,结果表明,随着过热度的降低,凝固组织中柱状晶比例和晶粒平均面积均减小。水冷条件下,高硅钢铸锭凝固组织几乎全是柱状晶,而且晶粒粗大。空冷条件下,等轴晶区扩大,但柱状晶仍占主要部分。缓冷条件下,等轴晶区占主要部分,晶粒平均面积和空冷条件下相当。
【Abstract】 The solidification structure of 6. 5% Si steel ingot was simulated based on CAFE method and the model suitable for simulating the structure of high silicon steel wad ascertained. The influence of superheat and cooling condition on the solidification structure were studied. It was shown that with the superheat decreasing,the proportion of columnar crystals decrease,and the average grain size become smaller. Under water cooling condition,the solidification structure of casting was composed of almo…
【关键词】 6.5%Si高硅钢；
凝固组织；
数值模拟；
CAFE法；
凝固热参数；
【Key words】 6.5%Si steel；
solidification structure；
numerical simulation；
CAFE method；
solidification thermal parameters；
凝固组织；
数值模拟；
CAFE法；
凝固热参数；
【Key words】 6.5%Si steel；
solidification structure；
numerical simulation；
CAFE method；
solidification thermal parameters；
【基金】 国家高技术研究发展计划(863计划)资助项目(2012AA03A505);国家自然科学基金资助项目(U1360201)
原文发表于《功能材料》2014年第19期
论文PDF全文下载
原文链接：http://1guigang.com/down/thesis/43147.html，转载请注明出处~~~