本发明涉及低温取向硅钢片制造领域，具体为一种重质硅钢级氧化镁的生产工艺。为提升现有取向硅钢片的表面质量，将工业氧化镁、聚乙烯醇粘结剂和水在不锈钢反应罐中水热合成氢氧化镁，经压滤、煅烧、冷却、气流粉碎、包装产物为重质硅钢级氧化镁。产品具有生产工艺独特、成本较低，能明显提高取向硅钢片的表面质量和增加磁感应强度，降低铁损，提高取向硅钢片的正品率。可针对性在取向硅钢片生产厂家推广使用。

借助OM、激光共聚焦显微镜、质谱仪和电解萃取等设备和方法，研究了添加微量稀土La（质量分数0.001 1%）的取向硅钢在轧制前采用不同加热保温时间对抑制剂固溶行为的影响。结果表明：当稀土取向硅钢在1 250℃分别保温10、20、30 min后，试验钢晶粒尺寸随保温时间延长有先快后慢的长大趋势；三种抑制剂元素Mn、Cu和Al均发生固溶，保温时间对Mn和Cu两种元素的固溶影响明显，固溶量分别由69.8%和43.7%增加至84.2%和85.2%；随着保温时间的延长，稀土取向硅钢中抑制剂的小尺寸未溶物逐渐减少直至消失，较大尺寸未溶物（300～600 nm）逐渐转变为小尺寸未溶物逐步溶入基体中，数量减少且未溶物的类型由复杂逐渐转变为单一。 In this paper the solid solution behavior of the inhibitor under various holding time in 0.001 1 %La oriented silicon steel during reheating had been investigated by using OM, LM, methods of electrolytic extraction and mass spectrometer. The results showed that grain size of the test steel increased significantly with the holding time prolonging when the rare earth oriented silicon steel was heated to1 250 ℃ and held for 10, 20 min and 30 min respectively, and the growth trend slowed down after ... 

利用OM、TEM与EDS技术,对Fe-3.2%Si低温取向硅钢热轧板进行不同常化冷却工艺处理后的显微组织、析出相及最终产品的磁性能进行分析,并与热轧板的组织和析出相进行对比。结果表明,常化板较热轧板的表层组织均匀,基体中再结晶比例增加,带状组织变窄;常化板中析出物的数量明显比热轧板的多,析出物主要有AlN、MnS及复合析出的(Cu,Mn)S等。在常化温度1120℃、保温3 min的条件下,采用二段式冷却较空冷、淬沸水、淬常温水的冷却工艺,常化板表层显微组织更均匀,沿板厚方向的显微组织的不均匀性显著,取向硅钢的磁性能最高;常化后采用二段式冷却工艺析出的细小析出物数量最多,且弥散分布在基体中,抑制剂的抑制效果最好,对成品获得高磁性最有利。 Microstructure, precipitate and magnetic characteristic of final products with different normalizing cooling processes for Fe-3.2%Si low-temperature hot-rolled grain-oriented silicon steel were analyzed and compared with the hot-rolled plate by optical microscopy(OM), transmission electron microscopy(TEM), and energy dispersive spectrometry(EDS). The results show that, the surface microstructure is uniform, the proportion of recrystallization in matrix increases, and the banding textures are nar... 

对低温加热工艺生产的以AlN为主抑制剂的高磁感取向硅钢高温退火过程进行中断实验,借助电子背散射衍射技术对高温退火过程中高斯晶粒的演变进行了研究.在升温过程中高斯晶粒平均尺寸先减小再增大.800℃时取向分布函数图出现高斯织构组分,但强度很弱,高斯晶粒偏离角在10°以上;900℃时高斯晶粒平均生长速率超过其他晶粒;950~1000℃时高斯晶粒异常长大,偏离角3°~6°;在1000℃之前高斯取向晶粒相比于其他晶粒没有尺寸优势. The high-temperature annealing process of high permeability grain-oriented silicon steel with AlN as an inhibitor was studied by interrupting test.The evolution of Goss texture in this process was analyzed by electron back-scattered diffraction.It is found that the Goss grain size first decreases and then increases with the rise of temperature.Goss texture appears in the orientation distribution function at 800 ℃,but the intensity is very weak and the deviation angle is more than 10°.The average... 

本发明揭示了一种无取向硅钢及其生产方法。该无取向硅钢的化学成分：Si:2.95%~3.15%，Al:0.75%~0.95%，Si+2Al:4.6%~4.9%，Mn:0.5%~0.7%，Sn:0.03%~0.04%，Cu≤0.03%，Cr≤0.03%，Ni≤0.03%，Nb≤0.004%，V≤0.004%，Ti≤0.004%，C≤0.0025%，P≤0.015%，S≤0.0015%，N≤0.004%，余量铁；Mn/S≥380，Al/N≥200；无取向硅钢的再结晶晶粒尺寸50~80μm。本发明在保证磁性能的同时，提高了强度，解决了现有技术所存在的磁性能和强度的兼顾问题。

【摘要】 <正>2012年3月29日中国钢铁工业协会在上...

试验研究了退火温度(850~950℃)和时间(5~18 min)对2.3 mm热轧硅钢板(/%:0.036C,3.15Si,0.21Mn,0.005P,0.007S,0.032A1)6道次轧制的0.35 mm冷轧板组织和织构的影响。结果表明,退火温度越高,晶粒平均尺寸越大,900℃5 min退火时平均晶粒尺寸41.39μm,试样织构主要集中在γ取向线上的{111}<112>织构组分和{111}<110>织构组分;900℃18 min退火时平均晶粒尺寸为48.08μm,试样的{111}面织构和{112}面织构密度都明显减弱,{001}面织构增强,磁性能较优。 The effect of annealing temperature(850 ~950 ℃) and holding time(5 ~ 18 min) on structure and texture of 0.35 mm sheet by 6 passes cold-rolling from 2.3 mm hot-rolled plate of silicon steel(/%:0.036 C,3.15 Si,0.21 Mn,0.005 P,0.007 S,0.032A1) has been tested and studied.Results show that the higher the annealing temperature the coarser the average grain size;As annealing at 900 ℃ for 5 min the average grain size of steel sheet is 41.39 μm,and the texture in sample is mainly concentrated in y orie... 

利用加热炉模拟、动态再结晶以及热模拟等试验方法以及扫描电镜、金相显微镜等分析观察手段对无取向硅钢边裂的成因进行了探讨。结果表明,长时间加热使得板坯边部晶粒异常长大,晶界氧化并脱碳,轧制过程中边部温度过低,动态再结晶过程变弱,使得板坯边部延伸性能变差,是导致硅钢边裂的主要原因。建议通过适当降低铸坯加热温度、缩短保温时间、提高终轧温度来改善硅钢边裂缺陷。 The behaviors of high temperature oxidation,dynamic recrystallization,and hot ductility,microstructure evolution were investigated on the non-oriented electrical steel sheets to discuss the formation of edge crack.The key causes of cracking was found to be the coarse as-cast microstructure,grain boundary oxidation and decarburization in reheating furnace,as well as reduced temperature at strip edge region during hot rolling process resulting in reduced hot ductility and lack of enough dynamic re... 

通过对辉光放电发射光谱参数的优化,以铁元素为内标来消除基体效应,建立了测定硅钢薄板中微量硼元素的方法。优化的实验参数为:放电电压1200 V,放电电流50 mA,预溅射时间40 s,积分时间10 s。校准曲线硼元素含量范围0.0001%~0.022%,相关系数大于0.999,测量结果与认定值一致,相对标准偏差小于10%。完全能够满足日常分析测试的要求。 A glow discharge optical emission spectrometry(GD-OES) method for determining trace boron element in silicon steel sheets were established through optimization of instrumental parameters and using Fe element as an internal standard to eliminate the matrix effect.The optimized instrumental parameters included discharge voltage,discharge current,pre-sputtering time and integration time,which are 1200 V,50 mA,40 s,and 10 s,respectively.The content of boron element that can be determined from the ca... 

本实用新型公开了硅钢片卷材加工用张力机构以及硅钢片剪切机，包括安装架、转动装置和按压装置，安装架的上安装块、连接块和下安装块组成凹槽，转动装置包括下转轴和转动驱动单元，下转轴水平设置，可转动地安装于下安装块上，设置于凹槽中，按压装置包括有上转轴和按压驱动单元，上转轴水平设置于下转轴的上方，可转动地安装于上安装块上，设置于凹槽中，并且可沿上安装块上下运动，其中，上转轴可与下转轴抵接。根据本实用新型的硅钢片卷材加工用张力机构以及硅钢片剪切机，可加强硅钢片卷材输送过程中的张力，降低硅钢片卷材输送的位置偏差率，提高产品合格率，提高原材料利用率，从而提高生产效率。

本发明属于钢材领域，具体的说是硅钢连退硅钢钢卷表面质量等级智能判定系统，包括支撑固定罩、竖直支撑柱、万向轮和智能判断单元；所述支撑固定罩的下端固接有多个竖直支撑柱；所述竖直支撑柱的下端固接有万向轮；所述支撑固定罩内设有智能判断单元；通过表面自动检测仪和针孔检测仪检查钢卷的表面质量，对于检测到质量缺陷的位置，输出信号给工控机，工控机控制喷标机工作，对质量缺陷的位置进行标记，通过控制摄像单元工作拍照记录，并记录钢卷的长度位置，通过在工控机内运行标记控制系统和自动判定模型，即可对钢卷的缺陷位置进行判断，实现精确的检测到钢卷的缺陷位置，并记录每卷钢卷的质量，并输出质量报告，记录留存。

本发明公开了一种生产高表面质量镀铝硅钢带的方法，属于连续热浸镀铝硅技术领域。本发明的生产高表面质量镀铝硅钢带的方法，包括酸洗、冷轧、清洗、连续退火、热浸镀铝硅和冷却处理，所述冷却包括预冷段和强冷段，其中预冷段是通过预冷风机将带钢温度冷却至620～630℃，强冷段包括三段强冷，三段强冷采用水雾冷却，且控制强冷段冷却速率≥30℃/s。本发明通过控制钢带表面粗糙度、清洗质量、退火炉气氛、气刀参数以及镀层结晶控制器参数，可以有效控制铝硅产品表面结晶尺寸、减少漏镀等典型缺陷，生产出高表面镀铝硅钢带。