通过固溶度积公式计算及热模拟实验,对不同热装和加热温度条件下的无取向硅钢铸坯中析出相进行了研究.在低于950℃热装时,铸坯中AlN的析出量和尺寸不再变化,但MnS和AlN-MnS的数量及平均尺寸随着热装温度降低而进一步增加,并在温度低于600℃时达到最大值后保持不变.与1200℃相比,1100℃加热的铸坯中AlN、MnS的总固溶量相对更少.相比850℃热装,600℃热装再加热到1100℃的铸坯中AlN和MnS的总固溶量更少,且AlN和MnS尺寸更大.合适的热装温度和加热温度分别为600℃和1100℃. Based on solubility product calculation and thermal simulation experiments,precipitated phases in continuous casting slabs of non-oriented silicon steel were systematically studied at different hot charging and heating temperatures.When the hot charging temperature is below 950 ℃,the content and size of AlN remain unchanged,but the quantity and size of MnS and AlN-MnS increase when the hot charging temperature decreases,reach maximum and remain unchanged when the hot charging temperature is belo... 

综述了电工钢从生产到成品过程中涉及到的检测项目、检测方法及仪器,并通过对电工钢标准的发展改进,详细阐述了我国现有的电工钢技术标准体系,同时对代表企业的电工钢重点指标进行了摘录对比,为综合应用电工钢检测方法并促进电工钢的发展提供了一定的参考。 This article summarizes the testing items,methods,and instruments involved in the process from manufacturing to finished products of electric steel. The current electric steel technical standards system in our country is also elaborated in detail,along with the development and improvement of electric steel standards. Meanwhile,by comparison of electric steel KPI in representitive companies,this article provides references for comprehensive application of electric steels testing methods and promo... 

本发明公开了一种改善取向硅钢边部变形的热处理辅助方法，在高温退火工序前，在钢卷的下端预设位置处放置阻热环并固定；在高温退火完成后，拆除固定件并移除所述阻热环。本发明通过施加阻热环，降低了取向硅钢卷在高温退火过程中的升温速率，降低了钢卷在升温及冷却过程中的胀缩量，有效改善了边部变形情况。同时，本发明由于采用一体式隔热材料，其装配及移除难度大幅度降低，有利于推广应用。

本发明涉及电机技术领域，具体涉及一种具有低应力结构的硅钢片、转子和电机。包括硅钢片、开设在硅钢片上的磁钢槽和嵌设在所述磁钢槽内的磁钢组件，所述磁钢组件包括多个磁钢组，所述磁钢组包括靠近转子边缘的一对小永磁体和靠近转子内侧的一对大永磁体，所述硅钢片在转子轭部沿周向分布有径向开槽，且所述径向开槽从硅钢片的中心向边缘延伸。其通过在转子轭部沿周向分设置从硅钢片的中心向边缘延伸的径向开槽，能降低大永磁体左右两侧铁芯刚度差距，从而有效降低隔磁桥处的应力，防止磁钢和铁芯产生形变而断裂。其无需改变电机转子外圆结构，在保证转矩输出的前提下，防止高速旋转时带来空气啸叫声。

结合扫描电镜和大样电解研究了CSP流程W800牌号无取向电工钢表面线状缺陷中夹杂物成分及来源，采用SPSS软件回归分析了生产过程各因素对表面线状缺陷的影响。研究表明：稳态浇铸过程铸坯中大型夹杂物含量为5.39 mg/10 kg。引起无取向电工钢表面线状缺陷的大型夹杂物主要为脱氧产物、镁铝尖晶石和钢包顶渣，主要类型为Al₂O₃、MgO-Al₂O₃、CaO-Al₂O₃-MgO和CaO-Al₂O₃-SiO₂。非稳态浇铸过程钢水洁净度明显降低，热轧板表面线状缺陷比例上升。影响表面线状缺陷的主要因素为RH出站时顶渣的w（CaO）/w（Al₂O₃）、RH脱氧结束氧位及中间包最低吨位。 Combining scanning electron microscopy and large sample electrolysis, the composition and source of inclusions in the surface linear defects of W800 grade non-oriented electrical steel in the CSP process were studied. SPSS software was used to regress and analyze the main factors which affected the surface linear defects in the steelmaking process. Research shows that the content of large inclusions in the steady state casting process is 5.39 mg/10 kg. The large inclusions which cause linear def... 

硅钢连续退火线是无取向硅钢生产的成品线。由于受机组布置的影响,带钢经转向辊进出口活套后,当套量达到60%后就出现偏离生产线的情况,从而影响最终产品的质量及成材率,甚至损坏设备。针对某冷轧厂硅钢连续退火机组出口活套入口处带钢跑偏开展纠偏研究,利用Matlab对该纠偏系统进行动态仿真研究,分析系统的稳定性。 Silicon steel continuous annealing line is non oriented silicon steel production of finished product line.Due to the influence of unit layout,strip by roll Import & Export loop,when the set volume reached 60% after the emergence of deviation from the production line,thus affecting the quality of the final product and the rate of finished products,and even damage the equipment.For the export of continuous annealing line in cold rolling silicon steel strip deviation rectification loop at the e... 

本发明涉及一种低耗高效硅钢常化酸洗工艺及酸洗设备，其有效利用常化炉出口余温作为加热带钢的介质，使带钢与低温的酸液接触表面发生强烈的物理化学反应，快速酸洗剥离表层粗大的氧化铁皮，降低酸洗系统的酸液温度，通过调控溶液氧化还原特性提高酸洗效率去除残留的铁橄榄石，节约了能耗，同时取消了高投资高运行成本的抛丸工艺，实现了低耗高效硅钢常化酸洗的目的。

本实用新型提供了一种新型的去角硅钢片，包括硅钢片本体，所述硅钢片本体包括叠放区和防护区，所述硅钢片本体设有防护结构，所述防护结构包括叠放区上设有的多个均匀分布的降噪凹槽，所述防护区上下两端分别设有多个防护条，且两两防护条之间设为连接槽，每个所述防护条皆包括与硅钢片本体连接的防护层和减震层，所述防护区底部两侧分别设有减震柱，所述防护区中间设有贯穿孔，所述贯穿孔内设有绝缘螺栓。本实用新型能降低噪音和减少震动影响，从而避免使得变压器寿命及功能性降低。

【作者】 康凌晨； 王丽娜； ...

一种薄规格带钢或者硅钢尾部卷取控制工艺，属于热连轧带钢卷取设备技术领域，解决薄规格带钢和硅钢尾部起套导致卸卷异常、卷形合格率下降的技术问题。解决方案为：在卷取厚度小于等于2.3mm的带钢或所卷取带钢的材质代码等于硅钢的材质代码的情况下，带钢尾部到达精轧F2机架时，G辊道速度V1=K1×D×ω×π/60；带钢尾部继续前行并到达精轧F6机架时，G辊道速度V2=K2×D×ω×π/60；在卷取厚度大于2.3mm的带钢且所卷取带钢的材质代码不等于硅钢的材质代码的情况下，G辊道投滞后速度的滞后率取值范围为90%~70%。本发明具有设计合理、工作效率高、产品质量好、可有效避免产品缺陷等优点。

本发明提供退火隔离剂的制备方法以及退火隔离剂和方向性电磁钢板。由该方法得到的退火隔离剂纯度高、分散性以及密接强度优异，可以在方向性电磁钢板表面形成均匀致密的镁橄榄石层。退火隔离剂的制备方法，其包括：工序(1)：将氧化镁和铵盐溶液混合并反应，制备镁盐溶液和氨，然后使精制的镁盐溶液与氨反应而得到氢氧化镁；工序(2)：将得到的氢氧化镁的一部分在155～230℃下高温熟化，并且将得到的氢氧化镁的另一部分在10～100℃下低温熟化；工序(3)：将在上述各条件下熟化的氢氧化镁混合、烧成，得到氧化镁用于退火隔离剂。

本发明公开了一种硅钢片压装工装，其涉及电机生产技术领域。其技术方案要点包括下压板，所述下压板上设置有限位结构，所述限位结构用于在硅钢片压装过程中对硅钢片进行限位；所述限位结构包括能够转动调节的限位挡块，所述限位挡块包括多个分别用于对不同尺寸规格的硅钢片进行限位的限位面，且该多个所述限位面与限位挡块的转动轴线之间的最小距离均不相同。本发明能够适用于多种规格的硅钢片，而且操作方便，稳定性好。