借助实验室设备研究了B元素对高牌号无取向硅钢热轧板组织和磁性能的影响。结果表明,与无硼钢相比,含硼钢的热轧板晶粒尺寸略小,析出物的类型和尺寸没有区别,主要是AlN和(AlN+MnS)复合析出物,少量的MnS析出物,尺寸集中在1.0～2.5μm范围内。未发现BN析出物。在力学性能方面,B对钢的软化作用不明显。在磁性能方面,含硼钢的铁损为3.215W/kg,磁感为1.710T,综合磁性能比无硼钢差。 Influences of boron on microstructure and properties of hot rolled band in high-grade non-oriented silicon steel are researched in this paper by experimental equipments.Compared with boron-free steel,the result shows that boron-bearing steel has smaller grain size,but the type and size of precipitations have no differences.The main precipitates are AlN,(MnS + AlN) composite precipitate and few MnS,the range of which are between 1.0 μm and 2.5 μm.BN precipitation is not found.With reward to mecha... 

本发明公开了大型风电电机硅钢片自动装配系统，涉及机械生产技术领域。该发明包括硅钢片、自动导引运输车、硅钢片标准运输箱、机械手、吸盘夹具和大型风电电机转子；自动导引运输车与硅钢片标准运输箱插接配合；吸盘夹具设置在机械手末端；大型风电电机转子周圈地面粘贴电磁轨道；自动导引运输车与电磁轨道滚动配合。本发明通过设置好的程序，自动导引运输车沿着电磁轨道移动，到达程序设定工位，自动导引运输车自动停止，机械手开始动作，通过吸盘夹具上的真空吸盘吸取硅钢片，然后机械手将吸取的硅钢片移动装配位置，此时红外位置传感器再次精确定位，机械手对硅钢片的位置进行微调，位置调整好后，机械手完成最后的自动叠片步骤。

试验的铸态取向硅钢（/%:0.044⁰.056C,3.12³.32Si,0.08⁰.11Mn,0.002⁰.008S,0.002 9⁰.029 1Als,0.006 2⁰.010 9N）由30 kg高频真空感应炉熔炼。通过场发射扫描电子显微镜/能谱仪（FE-SEM/EDS）研究结果表明,0.002 9%Als钢中氧化物主要为SiO₂,存在片状、棒状及近似球状的独立MnS,未发现含铝的氧化物或氮化物;0.0090%Als钢中出现以Al₂O₃为主的复合氧化夹杂物,存在MnS与AlN的复合析出物。钢中Als增加,复合析出物多呈簇状发展。氧化物容易成为MnS-AlN复合析出的核心,钢中Als含量越低,夹杂物中的MnS含量越高;作为核心的氧化物夹杂的尺寸越小,形成的复合夹杂物的形状越规则,尺寸也越小。热力学计算结果表明,钢中Als含量主要影响了钢中氧化物夹杂的组成和AlN的析出温度及析出量。 Test as-cast grain-oriented silicon steel（/%:0.044 ⁰.056C,3.12 3.32Si,0.08 0.11Mn,0.002⁰.008S,0.002 9⁰.029 1 Als,0.006 2⁰.010 9N） is melted by a 30 kg high frequency vacuum induction furnace.The research results by using field emission-scanning electron microscope/energy dispersive spectrometer（FE-SEM/EDS） show that in 0.002 9%Als steel the main oxide is SiO₂,and there is independent laminable,rod-like and approximate ... 

【作者】 韩超； 代智肄； ...

基于BOF→RH→CSP生产工艺,研究了RH精炼过程钢中夹杂物类型演变及MgO·Al2O3夹杂物形成规律,同时对MgO·Al2O3夹杂物的形成条件进行了热力学计算,借助CFD数值模拟软件研究了RH精炼过程卷渣行为。研究发现,RH精炼过程20和30 min时,w([MgO])/w([Al2O3])为0.005~0.020,未发现MgO·Al2O3夹杂物;RH出站后夹杂物w([MgO])/w([Al2O3])为0.3~0.5,且RH精炼结束后MgO·Al2O3夹杂物占夹杂物总量的58.4%;另外,RH精炼过程钢液表面速度CFD模拟结果为0.57 m/s,大于临界卷渣速度0.45 m/s,且顶渣成分与夹杂物成分相近,存在卷渣现象。热力学计算表明,钢液与炉渣平衡时钢中w([Al])为0.31%~0.37%,w([Mg])为0.00024%~0.00028%,在MgO·Al2O3生成区域之内。减少RH处理过程卷渣,浇铸过程下渣及控制顶渣和包衬相中MgO质量分数可抑制MgO·Al2O3夹杂物形成。 Based on the practical production of non-oriented silicon steel, the evolution of inclusion type and the formation of MgO·Al2O3inclusion were analyzed in the process of BOF→RH→CSP. The thermodynamic conditions for forming MgO·Al2O3inclusion were discussed and the behavior of slag entrapment of molten steel was also simulated by CFD software during RH refining. The results showed that the value of w([MgO])/w([Al2O3]) was in the range of 0.005-0.020 and no MgO · Al2O3 inclusion was observed at 20 ... 

一种分步调控制备高磁感高强度无取向电工钢的方法，按以下步骤进行：(1)按设定成分采用转炉冶炼钢水，制成连铸坯，含C0.001～0.008％，Si1.5～4.8％，Cu0.5～2％，Ni0.5～1.5％，Al0.2～1％，Mn0.2～1.5％，P＆lt;0.005％，S＆lt;0.005％，其余为Fe；(2)将连铸坯置于均热炉保温，多道次热轧相邻两道次间隔时间为30～180s；空冷；(3)常化处理；(4)多道次冷轧；(5)退火处理；(6)时效处理。本发明的方法成本较低、工艺简单，生产的无取向电工钢兼具优异的力、磁性能，能够很好的满足驱动/牵引电机的使用需求。

采用经验设计法初步确定了取向硅钢铸坯感应加热线圈设计参数,应用Ansoft仿真软件分别对36组不同线圈高度、线圈内径的感应加热炉在不同频率下的三维整体磁场和铸坯的温度场进行了数值仿真。通过对比仿真结果,确定电磁场分布最佳的一组感应加热炉设计参数为线圈高度h=1.50 m、线圈内径D1=0.575 m、电流频率f=110 Hz。在该参数下应用Ansoft仿真软件对取向硅钢铸坯感应加热炉的温度场进行了仿真,结果发现温度场分布均匀,可满足取向硅钢铸坯加热要求。 The induction heating coil design parameters for the oriented silicon steel casting blank were determined preliminary by experience design method,and 36 groups three-dimensional electromagnetic field with different height and inside diameter of coil under different frequencies of the induction heating furnace and the temperature field of the casting blank were investigated by numerical simulation using Ansoft simulation software. By comparing the simulation results of electromagnetic field distr... 

本实用新型公开了一种能限位的硅钢片，包括主体，主体的上表面设置有限位柱，限位柱的轴心处开设有散热孔，主体的上表面开设有限位槽，主体的外壁设置有凹槽，主体的下表面设置有限位凸起，主体的下表面开设有限位孔；该一种能限位的硅钢片通过在主体的外壁设置凹槽可以方便拿取，在其上下表面分别设置限位柱与限位孔，可以使主体间的位置相对固定不会轻易挪动。

本实用新型提供一种对硅钢片横剪线片料进行穿针叠柱与输送的装置，包括输送装置、穿针定位装置、纵向移动平台和转运装置，所述的输送装置设在纵向移动平台上方，所述的穿针定位装置位于输送装置底部，穿针定位装置固定在纵向移动平台上，所述的转运装置布置在输送装置的输出侧；所述的转运装置通过对接机构与输送装置对接。本实用新型能够完成硅钢片的穿针叠柱，并将此硅钢片柱整体输送到指定工位。本实用新型采用输送装置和穿针定位装置的上下分层布置结构，首先完成了硅钢片的穿针定位，然后完成硅钢片柱的整体输送，整个工艺方法中不使用吊运设备，提高了生产效率。

本实用新型涉及电工钢加工技术领域，尤其涉及一种电工钢切片用清洁设备，其包括箱体、第一盒体、烘干装置、清洁组件、进水管和出水管；箱体后侧内壁上转动设置导向辊；第一盒体前侧面上设置第二盒体；烘干装置设置在箱体内壁上；第一转动轴转动设置在第一盒体前后内壁上；刷辊设置在第一转动轴上，刷辊上的刷毛与电工钢钢带表面接触；清洁组件设置两组；第二盒体内设置有带动第一转动轴转动且沿第一转动轴轴线方向来回运动的动力组件；两组进水管出水口位于第一盒体上方且朝向电工钢钢带表面；出水管竖直设置在箱体底部。本实用新型中，刷辊转动的同时沿第一转动轴轴线方向来回做往复运动，不存在清洁间隙，提高了清洁效果。

本发明公开了一种硅钢环形炉内罩的内圆直径自动检测装置及方法，该内圆直径自动检测装置包括设置在检测点地面上的水平工作台，设置在所述水平工作台上的水平调节机构，设置在所述水平工作台上的扫描机构，以及与所述扫描机构通信互联的检测处理机构。该内圆直径自动检测装置是非接触式设备，不受内罩温度的限制，使用方便灵活，设备可靠性好，安全性高，对环境无污染，不仅能够有效节约校圆机的使用频次，而且大大增强了炉子的安全可靠性。

本实用新型涉及硅钢生产设备技术领域，具体公开了一种硅钢清洗用张力刷辊结构，包括中空的辊筒，辊筒两端固定有连接盘，连接盘上固定有转轴，辊筒的表面开设有若干排水槽，若干排水槽沿辊筒的周向等间距分布，辊筒的中部设有积水环槽，积水环槽内开设有连通辊筒内壁的进水孔，排水槽为倾斜设置，且排水槽的低端与积水环槽连通，连接盘上开设有排水孔。本专利中对硅钢带进行张紧时，完成清洗的硅钢带表面的水会沿着排水槽进入积水环槽，并从积水环槽进入到辊筒的内部，后排走，这样防止钢带上的水滞留在辊筒的表面，使得辊筒与钢带之间出现打滑的情况；另外多个排水槽的设置，还能够提高钢带与辊筒之间的贴附性，防止出现打滑的问题产生。