硅钢资料

对高磁感取向硅钢冷轧板分别进行800、950、1050和1120℃不脱碳的预退火处理,在800℃预退火,成品的磁性能较好。织构分析的结果表明,随着预退火温度升高,初次再结晶后有利织构组分{111}<112>与不利织构组分(118)[110]的比值f(111)/f(118)逐渐降低,初次再结晶织构的变化是成品磁性的影响因素之一。 Preliminary annealing process at different temperatures for cold-rolled strips of a high permeability grain-oriented silicon steel was investigated to study the effect of the annealing temperature on microstructure and magnetic performance of the steel.Results show that the magnetic performances of the products annealed at 800 ℃ are best.Analysis of primary recrystallization texture indicates that with rising temperature,f(111)/f(118) which is the ratio of the favorable component {111}<112>... 

本发明公开了一种新能源汽车驱动电机用35WD1600电工钢及其生产方法。属于新能源汽车驱动电机电工钢生产技术领域，主要解决的是现有技术新能源驱动电机电工钢性能较差的技术问题，包括以下化学元素成分及重量百分比：C≤0.005％，Si为2.5～2.8％，Mn为0.2～0.4％，P为0.08～0.12％，S≤0.008％，Cu为0.20～0.30％，Ni为0.16～0.25％，Al为0.3～0.5％，其余为Fe及不可避免的杂质。生产方法包括以下步骤：(1)铁水预处理；(2)转炉冶炼；(3)RH精炼；(4)连铸连轧；(5)酸洗；(6)第一次冷轧脱碳退火；(7)第二次冷轧脱碳退火；(8)涂层；(9)烧结卷取。本发明的新能源汽车驱动电机用35WD1600电工钢，性能达到新能源汽车驱动电机用冷轧无取向电工钢带国家标准及客户性的要求，焊接性能、板形、冲片性能良好。

采用XRD、SEM和激光粒度仪等手段,观察并研究了不同特性氧化镁在硅钢表面形成硅酸镁底层形貌特点,并结合热力学和差热-失重分析了MgO-SiO2的反应机理。研究结果表明:粒度小,活性值高的特种氧化镁在高温退火过程中与基体表面氧化物生成的硅酸镁底层,界面中硅酸镁底层嵌入基体较多,表面致密,颗粒细小,有利于形成附着性能优良的硅酸镁底层。 Surface microstructure of Mg2SiO4 coatings formed on the surface of oriented silicon steel coated with different kinds of MgO was investigated by XRD and SEM.The reaction mechanism between MgO and SiO2 was analyzed by TG-DSC and thermodynamic calculation.Results revealed that when the MgO with finer microstructure size and higher activity is employed,a dense Mg2SiO4 layer with finer microstructure and good binding to the steel substrate can be obtained.The results are very helpful for the prepar... 

本实用新型涉及电机技术领域，具体涉及一种具有低应力结构的硅钢片、转子和电机。包括硅钢片、开设在硅钢片上的磁钢槽和嵌设在所述磁钢槽内的磁钢组件，所述磁钢组件包括多个磁钢组，所述磁钢组包括靠近转子边缘的一对小永磁体和靠近转子内侧的一对大永磁体，所述硅钢片在转子轭部沿周向分布有径向开槽，且所述径向开槽从硅钢片的中心向边缘延伸。其通过在转子轭部沿周向分设置从硅钢片的中心向边缘延伸的径向开槽，能降低大永磁体左右两侧铁芯刚度差距，从而有效降低隔磁桥处的应力，防止磁钢和铁芯产生形变而断裂。其无需改变电机转子外圆结构，在保证转矩输出的前提下，防止高速旋转时带来空气啸叫声。

本发明公开了一种极薄取向硅钢铁芯及其制造方法，所述制造方法，包括：S1、剪切分条：将取向硅钢根据制作铁芯的宽度要求进行分条剪切；S2、卷绕：根据铁芯的规格型号要求，选取铁芯模具进行卷绕；S3、压块固定：将卷绕好的铁芯用压块固定；S4、退火加工：将固定好的铁芯，阶梯式升温至780℃保温3h退火处理，保护气氛为氮气，之后冷却降温；S5、浸胶：将降温后的铁芯，进行真空浸胶处理；S6、烘干：将浸胶处理后的铁芯烘干处理；S7、装配。该发明制造的极薄取向硅钢铁芯，能彻底消除内应力，磁路各处均无高磁阻存在，空载电流与励磁电流均大幅度下降，从而最大限度的恢复了极薄取向硅钢加工后原有择优取向织构及电磁性能。

本发明公开了一种消除取向硅钢单边浪缺陷的方法，其包括如下步骤：1)、制作专用盖板；所述专用盖板包括环形板，所述环形板外边缘设有多个剪开处；2)、将待装炉的取向硅钢钢卷吊运至高温退火炉炉台；3)、将专用盖板铺于取向硅钢钢卷上端面外圈；4)、将专用盖板上的各剪开处向下弯折，勾住取向硅钢钢卷外沿；5)、扣上内罩，内罩底边砂封；6)、钢卷进炉，完成高温退火过程。本发明能有效保护钢卷边部，防止钢卷上端面翻边；该方法还能将钢卷内部水分排出，避免钢带表面氧化。

研究了硼酸对以Al(H2PO4)3为基料的无铬无取向硅钢绝缘涂层各项性能的影响。用盐雾实验、动电位极化及交流阻抗等试验手段研究了不同硼酸含量对硅钢绝缘涂层的耐蚀性和电化学行为的影响,同时采用SEM对涂层的表面形貌进行了研究。结果表明,硼酸含量为9.7%时,涂层的耐盐雾性及电化学性能最好;硼酸含量过少或过多时,涂层的耐蚀性和电化学性能都较差。 Influence of boric acid on the performance of chromium-free non-oriented silicon steel insulating coating based on aluminum dihydrogen phosphate was investigated.Salt spray experiment,potentiodynamic polarization and electrochemical impedance spectroscopy were used to study the influence of boric acid content on the corrosion resistance and electrochemical behavior of the insulation coating of silicon steel.Surface morphologies of the coatings were tested by SEM.Result shows that when the boric ... 

选用国内外无取向硅钢标杆企业A、B、C的产品,采用非水溶液电解提取+SEM(EDS)方法,分析了其典型牌号对应成品试样中的夹杂物。结果表明,从磁性能控制角度而言,受钢的化学成分及生产工艺影响,A、B、C企业成品试样的夹杂物尺寸、种类、数量存在差异,这些差异对其磁性能产生显著影响;从夹杂物控制角度而言,A、B、C企业对应成品试样的夹杂物,以MnS、CuxS复合或者AlN、MnS、CuxS复合为主,其中1.0μm以下的夹杂物数量分别为2.34×107个/mm3、2.98×107个/mm3和11.98×107个/mm3,1.0μm以上夹杂物数量均很少,夹杂物的平均尺寸从大到小依次为A企业、B企业、C企业。 According to the production of three benchmarking manufacture enterprises A,B and C of non-oriented silicon steel at home and abroad,the inclusions in finished steel samples with typical grades were investigated by electrolytic extraction from non-aqueous solution and SEM(EDS).Results show that,from the viewpoint of improving the magnetic properties,affected by chemical composition and production technique,the size,type and amount of inclusions in finished steel samples are various,which will af... 

本实用新型涉及到一种应用于硅钢片冲压过程的冲压联动接料装置，包括固定连接在冲头侧面上的连杆，连杆一端远离冲头且连接有一根销，销上转动连接有摆杆，摆杆的一端开设有长孔，销插接在长孔内，摆杆另一端通过铰轴转动连接在机架上，摆杆设置有铰轴的一端连接有一根联臂，联臂下端通过转轴连接有接料盘，转轴与冲台之间设置有平行于转轴的托辊，托辊高于转轴，接料盘接近冲台的一端搁置在托辊上，冲头处于上止点时，接料盘接近冲台的一端伸入冲头和冲台之间且位于冲头正下方，冲头处于下止点时，接料盘接近冲台的一端退出冲头和冲台之间，位于冲台一侧，所述冲头下端面设置有凸模，冲台上端面设置有与凸模配合的凹模。

本发明公开了一种硅钢冷连轧轧制过程温度获取方法、装置及电子设备，通过获取硅钢冷连轧生产过程的工业参数数据以及各机架间硅钢的实际温度测试数据，然后基于工业参数数据以及预设初始模型，确定硅钢冷连轧生产过程的温度预测模型，接着基于硅钢轧制前的预热温度以及温度预测模型，得到硅钢冷连轧轧制过程各机架变形区出口与下一机架变形区入口之间的预测温度数据，再将预测温度数据与实际温度测试数据进行对比，并根据对比结果中的温度差异值对相应机架间的乳化液参数进行修正，直至温度差异值小于预设阈值，得到修正后的温度预测模型，能够用于实现硅钢冷连轧轧制过程中，任意采样点硅钢温度的获取。

介绍了重庆钢铁股份有限公司炼钢厂生产低碳低硅钢的脱氧工艺,对连铸过程中水口结瘤的原因进行分析,并提出了优化措施。生产实践表明:钢水中的活性氧质量分数控制在10×10-6～30×10-6时,单中包浇铸炉数由6～7炉提高到11～12炉,同时能保证连铸顺行和减少铸坯气孔。 The deoxidation process of low-carbon and low-silicon steel in steel plant of Chongqing Steel was introduced.The nuzzle clogging was analyzed and some measures were put forward.Production experiments showed that when the active oxygen was controlled between 10×10-6～30×10-6,the amount of furnaces would rise from 6～7 to 11～12,which will make the casting process work well and reduce casting holes. 

本实用新型涉及电工钢加工技术领域，尤其涉及一种电工钢切片用清洁设备，其包括箱体、第一盒体、烘干装置、清洁组件、进水管和出水管；箱体后侧内壁上转动设置导向辊；第一盒体前侧面上设置第二盒体；烘干装置设置在箱体内壁上；第一转动轴转动设置在第一盒体前后内壁上；刷辊设置在第一转动轴上，刷辊上的刷毛与电工钢钢带表面接触；清洁组件设置两组；第二盒体内设置有带动第一转动轴转动且沿第一转动轴轴线方向来回运动的动力组件；两组进水管出水口位于第一盒体上方且朝向电工钢钢带表面；出水管竖直设置在箱体底部。本实用新型中，刷辊转动的同时沿第一转动轴轴线方向来回做往复运动，不存在清洁间隙，提高了清洁效果。