硅钢资料

对两种硅钢水溶性极厚绝缘涂层进行了不同温度的热老化实验。通过TG-DTA,GDS,FT-IR,SEM和光泽度仪等测试方法对老化的涂层进行分析表征,提出了评估硅钢水溶性极厚绝缘涂层热老化性能的合理温度区间,探讨了涂层热老化行为,并分析了两种涂层热老化性能的差异。结果表明,涂层附着性随着老化时间的延长逐渐下降。FT-IR表征结果显示,热老化过程中,涂料交联形成的化学键未发生断裂,交联剂氨基树脂的三嗪环被破坏是聚合物三维网络结构坍塌的主要原因。 Thermal aging expriments at different temperature were carried out on two types of water-soluble and extra-thick insulation coatings for non-oriented silicon steel,and a series of test methods such as glossmeters,TG-DTA,FT-IR,GDS,SEM were applied in analysis.For evaluating the thermal aging effect of this kind of insulation coating,the proper temperature range was proposed.The difference of aging performance between two coatings was been investigated and the related behaviors were been discussed... 

本发明公开一种冷轧硅钢的横向同板差控制方法，具体如下：S1、确定冷轧钢板横向同板差的影响因子，包括：热轧钢卷的热卷凸度、工作辊辊型插入量、中间辊窜动值及冷轧钢卷的总切边量；S2、以影响因子为变量构建冷轧钢板横向同板差的计算模型；S3、将热轧钢卷的热卷凸度及冷轧钢板的目标横向同板差输入计算模型，确定最小冷轧钢卷总切边量下的工作辊辊型插入量及中间辊窜动值。明确客户所需的横向同板差，通过改变工作辊辊型插入量X2及工作辊窜动值X3，以此得到冷轧成品钢卷的总切边量最小值，在满足客户对横向同板差的使用要求前提下，降低生产成本，提高产品竞争力。

试验2.3Si无取向硅钢(/%:0.003C,2.30Si,0.16Mn,≤0.020P,≤0.005S,0.54Al)冷轧板由常化和未常化的2.5 mm热轧板冷轧至0.6 mm(压下率76%),经750~950℃2.5 min中间退火后再冷轧至0.5 mm(压下率16.7%),成品板经890℃+960℃2.5 min退火。研究了中间退火温度对该钢晶粒尺寸、织构和磁性能的影响。结果表明,随中间退火温度的升高,二次冷轧前晶粒和成品晶粒增大,成品中不利织构组分{111}和{112}减弱,磁性能得到改善。热轧板经过常化时的磁性能明显好于未经常化时的磁性能,但中间退火温度较高时常化对磁性能的有利作用减弱。 The test cold sheet of 2.3Si non-oriented silicon steel(/%:0.003C,2.30Si,0.16Mn,≤0.020P,≤0.005S,0.54Al) is first cold-rolled from normalized and un-normalizing 2.5 mm hot-rolled plate to 0.6 mm sheet(reduction 76%),then intermediate annealed at 750~950℃ for 2.5 min and double cold-rolled to 0.5 mm sheet(reduction16.7%),the finished sheet annealed at 890℃+960℃ for 2.5 min.Effect of the intermediate annealing temperature on grain size,texture and magnetic performance of the steel has been studied.... 

本实用新型公开了一种无取向硅钢喷涂用即时干燥装置，包括干燥箱，所述干燥箱内滑动连接有加热台，所述干燥箱顶部设置有加热箱，所述加热箱左右两侧分别设置有进风管和出风管，所述进风管和出风管均与干燥箱连通，所述加热箱内部从左到有依次固定连接有风机和加热网，所述干燥箱内设有带式传送机，通过带式传送机使喷涂过后的硅钢在干燥箱中移动，首先经过加热台加热，使涂层表面干燥硬化，不会变形，然后再经过加热箱吹出的风对硅钢表面的涂层进行进一步的烘干，从而保证干燥过程中涂层不会起褶皱。

本发明提供了一种取向硅钢的磁畴细化方法，属于高磁感取向硅钢生产技术领域技术领域，包括：采用激光在带钢表面烧蚀出若干沟槽；采用腐蚀液对所述沟槽进行腐蚀，获得刻槽；其中，所述沟槽与带钢宽度方向的夹角为0‑20°；所述沟槽的深度为0.5～20μm，宽度为30～200μm；所述刻槽深度为0.5～30μm、宽度为30～300μm。该方法能够显著的细化磁畴，降低取向硅钢片单位损耗，同时细化磁畴的效果能够承受800℃‑900℃的消除应力退火。本发明还提供了一种取向硅钢的磁畴细化方法在取向硅钢生产中的应用。

通过热力学计算,分析了实验钢中主要析出物析出的可能性。结果表明:在液相和固液两相区中,AlN和MnS均不能析出;在奥氏体区,AlN和MnS具备热力学析出条件,平衡析出温度分别为1547、1582 K。成品退火板中的析出物主要为AlN和MnS。扫描电镜下观察到的AlN形貌多为长条状,MnS形貌多为棒状或近似球形。这两种析出物占了析出物总量的85%以上,尺寸集中分布在400~800nm;复合析出物主要是(Al2O3+MnS)和(AlN+MnS),形貌不规则,尺寸集中在0.7~1.5μm;透射电镜下观察到了少量100nm以下独立的AlN析出。 According to thermodynamic calculation, the precipitation probability of precipitates was analyzed, AlN and MnS can not precipitate in liquid phase area and solid-liquid two-phase area. In austenite area, both the AlN and MnS have precipitation condition in thermodynamics and precipitates at 1547 K and 1582 K, respectively. The precipitates in annealing plate are mainly AlN and MnS. The shape of AlN is mostly strip, and MnS is stick or near sphericity. They accounted for over 85% of the total qu... 

采用非水溶液电解方法来提取无取向硅钢中夹杂物。通过扫描电镜(SEM)观察结果表明:无取向硅钢中主要夹杂物为六棱柱的AlN、不规则硅酸盐及球状的铁的硫化物和氧化物,其中AlN夹杂尺寸在1~5μm,数量较多,还有部分AlN的复合夹杂。进一步研究了AlN复合夹杂形成机理,采用了Thermo-Calc热力学计算软件计算出该钢样中AlN、MnS析出温度分别为1 240℃、1 200℃,而Al2O3析出温度大于1 800℃,从而为AlN复合夹杂形成机理提供了一个理论依据。 Extracting inclusions from non-oriented silicon steel in non-aqueous electrolysis is a nondestructive method to gain inclusions.Scanning electron microscopy shows that the main inclusions in non-oriented silicon steel were hexagonal AlN,which was of large quantity,irregular silicate,spherical iron sulfide and oxide.The size of AlN inclusions ranged from 1to 5μm,and there were some duplex inclusions of AlN.To further study the formation mechanism of AlN duplex inclusions,Thermo-Calc thermodynamic... 

本发明属于硅钢制造技术领域，具体涉及一种改善硅钢热轧板边部质量的加工方法，包括：连铸、铸坯预变形处理、铸坯加热处理和热轧处理；其中，所述铸坯预变形处理包括：在所述铸坯的温度为500～900℃下，对所述铸坯的沿长度方向的两侧壁通过立辊施加压力，直至形变量h为10～50mm；所述铸坯加热处理的加热温度为1100～1200℃，保温时间为4～6h。本发明提供的改善硅钢热轧板边部质量的加工方法，采用铸坯两侧壁的侧压工艺，有效解决了热轧板边部裂纹的缺陷，提高了边部塑性，提高了成材率并降低了生产成本。

本发明涉及一种含磷高磁感无取向硅钢的生产方法，工艺路线：铁水脱硫－转炉冶炼－RH精炼－连铸－热轧－酸洗－冷轧－连续炉退火－涂层－性能检验－包装，具体步骤包括：1)将钢水冶炼至目标成分后采用连铸方式将钢水铸成坯；2)热轧板坯加热炉均热段板坯温度950～1050℃，终轧温度控制在780～830℃，卷取温度600～680℃；3)酸洗后冷轧，控制冷轧整体压下率80％以上，至成品厚度，增加剪切带组织；4)连续退火炉快速加热段温度设定1000～1150℃，增加有利织构组织形核；均热段温度设定750～830℃，全氮气干气氛保护，退火工艺速度110～150m/min，满足晶粒度8～4级。本发明在减少硅、铝、锰合金添加量的情况下，改善铁损提高磁感性能，提高机械性能。

选取了三种50W 800无取向电工钢,分析了化学成分、晶粒尺寸、织构、以及200℃时效处理48 h前后的磁性能和第二相粒子析出状态的变化。结果表明,钢板中第二相粒子的分布密度对钢板铁损有最重要的影响。降低钢中C、N元素含量,或改进钢板热加工参数以降低成品钢板中第二相粒子形成元素的过饱和度均有利于明显降低钢板磁时效过程中的铁损增幅。钢板中对磁性能有利的织构也有利于降低钢板铁损的时效幅度。 The evolution of chemical composition,grain size,texture,as well as magnetic property after aging treatment at 200 ℃ for 48 h and distribution of second phase particles precipitation in three selected 50W800 non-oriented electrical steels were analyzed.The results show that the distribution density of second phase particles has great influence on core loss.Reducing C and N content,or improving hot-working parameters to reduce the supersaturation of elements forming second phase particles in prod... 

一种低温高磁感取向硅钢的热轧方法：经转炉冶炼并浇注成坯；对铸坯加热后进行粗轧：首先确定粗轧减宽量；根据所确定的粗轧减宽量进行粗轧；进行精轧；常规进行下工序。本发明采用低温板坯加热技术，降低了板坯烧损和修炉负担，且边裂发生率比现有技术的不低于18%的基础上能降低5%以上，由此节约资源及降低能耗。

本实用新型公开了一种基于单片机的硅钢片卷料收卷装置，涉及硅钢片生产技术领域。本实用新型包括底板，底板的上表面固定连接有固定板，固定板的右侧面开设有第一滑动槽，第一滑动槽连接有移动模块，移动模块固定连接有限位杆，底板滑动连接有移动板，移动板开设有第二滑动槽，第二滑动槽滑动连接有第二移动块，限位杆与第二移动块滑动连接，固定板的右侧面转动连接有转动杆，底板的上表面固定安装有转动电机，转动杆穿过移动板与转动电机通过传动模块连接。本实用新型通过转动电机带动转动杆旋转对硅钢片进行收卷工作，通过调整固定板和移动板的间距防止硅钢片收卷不齐平，通过调整限位杆的间距对收卷后的硅钢片进行限制，防止硅钢片松散导致收卷不规则。