本发明涉及金属冶炼工艺，尤其是一种降低无取向硅钢W800冶炼成本的方法，开吹阶段，着火后，加入头批渣料，石灰加入量占石灰总加入量的70%，石灰石加入量占石灰石总加入总量的100%，轻烧白云石加入量占轻烧白云石总加入总量的100%，待化渣后，枪位降低；化渣后将剩余30%石灰加入，加入剩余石灰过程中利用矿石调整温度；吹炼后期，并逐步压枪，终点拉碳枪位至1.4m，并使枪位在此高度不少于30s；到达冶炼终点。本工艺通过降低转炉渣量、提碳降氧和提高终点温度来减少铁水锰氧化量和促进氧化锰还原量，进而降低RH金属锰加入量，降低生产成本。

通过对3%Si CGO硅钢进行恒变形速率、不同变形温度下的单道次压缩实验,结合Thermal-Calc软件,金相分析,SEM及EBSD技术,研究了取向硅钢热变形过程中组织和微观织构的变化规律。结果表明:实验钢是在双相区变形,变形后组织主要是铁素体和少量的珠光体。随变形温度的升高,晶粒由长条状变为等轴状,尺寸逐渐变大;CGO硅钢在热变形过程中立方{100}<001>取向是较为稳定存在的。随着变形温度的提高,{111}<110>等取向逐渐转向{110}<1 10>取向,且{110}<1 10>取向逐渐变得锋锐。 3% Si CGO silicon steel was studied at constant strain rate and different deformation temperatures by single-pass compression deformation experiments to reveal the evolution of microstructure and texture during thermal deformation in oriented silicon steel,and the Thermal-Calc software,metallurgical,SEM and EBSD technique was used in the experiment. The results show that experimental steel is deformed at the temperatures of two-phase zone. The microstructure of the deformed steel consists of fer... 

本实用新型公开了一种硅钢片激光曲线开料机，本实用新型涉及电力设备技术领域，目前现有的硅钢立体三角形卷铁芯的机械式斜度开料机在开料过程中精度差、效率低，且在硅钢片送料的过程中，长时间后硅钢片容易发生松散情况，同时只能对单一厚度的硅钢片进行输送工作，包括放料组件和开料组件以及收料组件，所述放料组件用于对硅钢片的放料工作，所述开料组件用于对硅钢片的开料工作，所述收料组件用于对硅钢片的收料工作。该硅钢片激光曲线开料机，通过利用高速激光曲线开料，效率高精度好，且硅钢片在输送的过程中，能够自动调整导向辊的位置，进而能够对硅钢片起到很好的导向作用，使其表面时刻为张紧状态，进而保证硅钢片的开料效果。

对1990~2010年在我国申请的冷轧无取向硅钢涂层的专利数量、专利技术领域分布进行了统计,对典型涂层专利技术进行了分析,探讨了无取向硅钢涂层的发展趋势。统计分析结果表明,目前无取向硅钢涂层典型的专利技术主要有自粘结涂层、无铬含稀土元素涂层、含钼酸盐环保涂层及采用有机-无机纳米杂化材料为主成膜物形成的涂层等。无取向硅钢涂层发展的趋势主要是无铬环保的半无机、半有机型涂层。 The patent quantity of cold-rolled non-oriented silicon steel coating and distribution of technology fields applied in China in 1990-2010 were summarized.The analysis results indicate that typical patent technologies include self-adhesion coating,chromium-free and with rare earth element coating,environment-friendly and with molybdate coating,coatings with organic-inorganic hybrid materials as main forming agent and so on.The main development trends of coatings on silicon steel are among semi-in... 

本发明涉及一种硅钢热处理方法，尤其涉及一种取向硅钢极薄带绝缘层涂覆方法，包括以下步骤：(1)接入普碳钢引带的准备工作；(2)各炉段张力的设定工作；(3)炉内气氛及温度的调节工作；(4)绝缘层厚度及厚度的检测工作；(5)极薄带涂层涂覆及烘干工作；(6)极薄带表面绝缘涂层及磁性能检测工作。本发明采用与极薄带厚度相当的普碳钢作为引带，通过引带测试产线张力和绝缘层涂覆的厚度，一方面可通过普碳钢薄带的运行加速炉内温度和气氛的稳定性，节约炉内稳定时间；另一方面可通过成本较低的普碳钢检测炉内张力和温度的设定，及绝缘涂层的涂覆效果，避免开始采用硅钢带出现断带，及涂覆不合格后造成产品报废带来的成本升高。

本发明涉及一种含磷无铝高效无取向硅钢生产方法，生产方法取消常化工艺，具体步骤如下：1)将钢水冶炼至目标成分后，浇铸成坯；2)板坯热装，热装温度≥500℃，热轧板坯加热炉均热段板坯温度1150～1200℃；终轧温度控制在860～930℃，卷取温度700～800℃3)酸洗后冷轧，控制冷轧整体压下率80％以内，至成品厚度；4)连续退火炉快速加热段温度设定1050～1180℃，增加有利织构组织形核，均热段温度设定830～950℃，全氮气干气氛保护，退火工艺速度120～150m/min，满足晶粒度8～4级。本发明不需进行热轧卷常化处理，降低了制造成本。

在实验室模拟CSP流程制备了不同含量稀土铈(质量分数0~0.018%)的1.2%Si无取向电工钢,并对其进行1 000℃×5min的再结晶退火处理,研究了铈质量分数对无取向电工钢夹杂物、显微组织、再结晶织构和磁性能的影响。结果表明:随着铈质量分数的增加,微细夹杂物数量、再结晶晶粒尺寸、{100}和{110}织构组分、磁感应强度先增后减,{111}织构组分、铁损先减后增;铈的质量分数为0.005 1%时,钢中的夹杂物数量最少,再结晶晶粒尺寸最大,有利织构最多,磁性能最优,铁损P15/50为3.253W·kg-1,磁感应强度B50为1.751T。 Non-oriented electrical steels containing different contents rare earth Ce element(0-0.018wt%) were prepared in the laboratory by simulated CSP(compact strip production)process,and then recrystallization annealing at 1 000 ℃ for 5 min were performed,the effects of Ce content on inclusion,microstructure, recrystallization texture and magnetic properties of non-oriented electrical steels were studied.The results show that with the increase of Ce content,the amounts of fine inclusion,the size of re... 

一种高磁感低铁损取向硅钢生产用表面涂层涂覆装置，包括：加工台，加工台上端固定连接支撑架，支撑架下端一侧固定连接伺服电机，伺服电机输出端固定连接第一齿轮，第一齿轮下端啮合连接第二齿轮，第二齿轮中部固定连接螺纹杆，螺纹杆上螺纹连接移动环，螺纹杆远离第二齿轮一侧转动连接支撑板，支撑板上端固定连接支撑架，移动环下端固定连接伸缩杆，支撑架下端前后部均固定连接连接框，本实用新型的有益效果是：通过设置的伺服电机、第一齿轮、第二齿轮、螺纹杆和移动环等结构，能够实现伸缩板带动硅钢板移动，从而能够完成自动化推料，减少工人劳力支出的同时，也能够避免工作人员手臂靠近涂层辊，从而避免安全事故的发生。

本发明涉及电工钢的生产方法，更具体地说，涉及一种预应力生产中低牌号无取向电工钢的方法，包括铁水预处理；预处理后的铁水进行转炉冶炼并吹氩脱氧；吹氩后的钢水送入精炼炉中进行冶炼并加入低碳合金进行合金化；合金化处理的钢水通过薄板坯连铸机铸成板坯并采用薄板胚连铸连轧生产工艺进行轧制获得热轧板；所述热轧板经过酸洗冷轧，随后进行预应力拉伸并退火，采用涂层进行涂镀、烧结后卷取。本发明采用预应力拉伸，改善无取向电工钢退火前钢板内部应力的分布，制备的冷轧无取向电工钢产品的电磁性能P15/50≤5.4W/kg，磁感应强度≥1.72T，板形同板差≤8um。

本发明涉及一种电机定子硅钢片激光焊接装置，其包括底座；工作台，其安装于所述底座；下压旋转组件，其包括：焊接支座，其安装于所述底座上；用于压紧定子硅钢片的下压组件，所述下压组件位于所述工作台的上方，且可沿垂直于所述工作台的板面的方向移动；用于驱动所述定子硅钢片旋转的旋转组件，其安装于所述下压组件靠近所述工作台的一端，所述旋转组件可绕所述下压组件的轴线旋转；以及激光焊接头组件，其固定于所述底座。通过在焊接工作台上设置下压旋转组件，下压组件可以驱动下压使定子硅钢片压紧，旋转组件可以驱动定子硅钢片旋转，进行下一道焊缝焊接，直到该定子硅钢片所有焊缝焊接完成，使用方便，省时省力。

本实用新型涉及一种取向硅钢高温退火设备，尤其涉及一种取向硅钢全氢式高温罩式炉外罩，从外至内包括圆柱形外壳和耐火保温层，所述耐火保温层内壁铺设有电阻带；所述圆柱形外壳上部设有外罩顶盖；所述耐火保温层由陶瓷纤维模块堆砌而成，所述电阻带通过钉子铺设在陶瓷纤维模块上；电阻带头一端通过接线棒引出炉壳外，另一端中性点在炉内短接。本实用新型保温层内层采用模块化的高纯度陶瓷纤维代替耐火砖，该材料具有重量轻、蓄热少，低导热性能带来高的节能效果，具有抵抗热冲击的能力，加上模块化的结构，安装快捷，衬体无需烘干和养护，所以安装好以后便可立即投入使用。

本发明公开了一种硅钢片横剪线裁切设备，包括：本体，所述本体包括工作台、挡屑罩和裁切装置，所述挡屑罩内水平固定安装有横杆，所述裁切装置与横杆下表面滑动连接；两个定位机构，所述定位机构包括第一螺纹杆、第一滑块和压板，所述挡屑罩内壁开设有两个安装槽，两根所述第一螺纹杆分别转动安装在两个安装槽内，两个所述第一滑块分别螺纹套设在两根第一螺纹杆上，两个所述压板分别与两个第一滑块远离安装槽槽底的一端水平固定链接；两个驱动机构，所述驱动机构用于控制第一螺纹杆发生转动。通过驱动装置控制定位机构中压板在垂直方向上的位置便可快速实现对硅钢片的定位工作和解除工作，方便快捷，提高了裁切工作的效率。