对CSP流程生产的无取向电工钢M50W800不同尺寸样品的磁性能进行了测试和分析,结果表明:采用不同单片检测的磁性能结果与标准的Epstein方圈样品检测对比,存在明显的偏差;且同一尺寸的单片纵横向样品之间相比较,对应的磁性能差异性也较大。几种不同尺寸的单片样品,以320mm×30mm尺寸的纵横向平均值最接近标准Epstein方圈样的性能值,其铁损偏差最小。 The magnetic properties of M50W800 non-oriented electrical steel produced by CSP process were tested and analyzed with samples of different sizes,showing that significant deviation existed compared to that of Epstein square circle sample.In particular,obvious difference in magnetic properties also existed between longitudinal and transverse samples of the same size.For test samples of different sizes,the average magnetic properties of 320mm×30mm samples are the closest to that of Epstein square ... 

对高牌号无取向电工钢35W300的成品进行了第二次退火,对第二次退火后的成品性能、纵横向磁性能差异和组织变化进行了分析。结果表明,随着第二次退火温度的升高,晶粒长大,磁性能优化。铁损平均值下降0.087 5W/kg,磁感平均值升高0.008T。第二次退火温度为820℃的产品的磁性能能够满足用户使用要求。 The product of high grade non-oriented electrical steel 35W300 was annealed at the second time.Microstructure,the difference of magnetic properties in the vertical and horizontal and were studied.The results show that the grain grew up and magnetic properties optimized with the increase of annealing temperature for the second time.Iron loss average declines in 0.0875 W/kg,magnetic induction average increases 0.008 T.The magnetic properties can meet the requirements of users at the second anneali... 

本发明公开了一种硅钢氧化镁废水资源化处理方法及处理系统，硅钢氧化镁废水进入过滤浓缩干化一体化装置经预过滤、过滤、干燥、排泥后得到清液和泥饼；泥饼经烘干后得到烘干泥饼；烘干泥饼溶解于硫酸溶液中，反应后的混合液固液分离得到上层清液和沉淀物，上层清液经中和、蒸发结晶后得到结晶物，沉淀物进行清洗、烘干处理。本发明还设计了实现上述处理方法的处理系统，该系统包括过滤浓缩干化一体化装置、烘干装置、溶解装置以及产水箱；本发明的硅钢氧化镁废水经处理后的清液满足回用要求，可返回机组循环利用，实现废水回用，泥饼经烘干、溶解后可分别作为钛白粉生产原料和土壤改良剂，具有经济环保双重效果，以及良好的社会效益和环境效益。

一种在取向硅钢中获得沿晶断口的方法：将取向硅钢样品加工成俄歇电子能谱仪标准试样；对标准试样进行表面清理；充氢：将标准试样所设定的预设断口处放入充氢装置的含硫脲溶液中，并使取向硅钢样品为阴极；将铂片置入并作为阳极；阴极充氢电流为1.25～1.35A，充氢电流密度在0.1～0.8A/m2，充氢时间在12～50h，充氢电压为36～39V；进行表面分析。本发明不仅工艺简单，便于操作，用时短，所用毒化剂是硫脲，从而避免了采用剧毒的三氧化二砷作为毒化剂，对人体健康有极大威胁的问题，且所获得的取向硅钢断口均为典型沿晶断口，适用于取向硅钢晶界偏聚行为以及晶界微区成分分析。

传统轧制法制备6.5wt.%高硅钢过程中温轧工艺具有显著不同于3 wt.%Si的电工钢的特点及组织织构特征,是开发新型基于织构优化的高硅钢的关键环节。采用EBSD技术对通过热轧、温轧、冷轧及退火工艺制备0.3mm厚的6.5wt.%Si电工钢板的组织和织构进行分析,重点研究温轧过程中的中间退火和大、小压下率组合以控制织构。结果表明,在热轧退火板是部分再结晶组织的情况下,一次性温轧或先小形变量、中间退火后再大形变量的工艺可得到更多的Goss晶粒;经过最终退火后Goss取向会发生偏转,形成部分黄铜取向,而{111}〈112〉取向的晶粒内形核生成近Goss取向的再结晶晶粒;大压下量轧制是最终组织中{111}取向晶粒较多的主要原因。 Warm rolling,a key process of developing new type high-Si electrical steel based on texture optimization,has significant different characteristics from 3wt% Si steel in conventional preparing process. 0. 3mm thickness 6. 5wt. % Si steel,obtained by a series of processes including hot and warm rolling,intermediate annealing and then cold rolling,was analyzed from microstructure and texture by EBSD,which are utilized mainly for investigating the intermediate annealing process and the combination o... 

本实用新型属于硅钢片加工技术领域，具体涉及一种利于常化的硅钢缝合结构，包括上层硅钢片、下层硅钢片和连接带，下层硅钢片的一端位于上层硅钢片的下方并与上层硅钢片叠合，上层硅钢片和下层硅钢片的叠合处开有多个排成直线的桥型孔，连接带依次穿过各个桥型孔并同时卡合在上层硅钢片和下层硅钢片上。本方案中，在上层硅钢片和下层硅钢片的叠合处开设桥型孔，利用连接带穿过上层硅钢片和下层硅钢片叠合处的桥型孔，相当于利用连接带将上层硅钢片和下层硅钢片缝合在一起，这样设置能够较好将上层硅钢片和下层硅钢片连接成一体。

无取向硅钢的磁性能主要取决于铁素体的晶粒尺寸、晶体织构和钢中的夹杂物。通过合适的化学成分设计以及采用适宜的夹杂物控制技术,可以获得最佳的夹杂物控制效果,使其纯净度大幅度提高或者无害,最终获得磁性能优良的高级别无取向硅钢。同时,为满足节能、环保、高效需求,无取向硅钢正朝着节能降耗、环境友好以及多功能、高效率、易加工等方向发展。 The magnetic properties of non-oriented silicon steel mainly depend on the grain size of ferrite,the crystallographic texture,and the inclusions in the steel.The optimum inclusion control effects can be obtained through a suitable chemical composition design and an appropriate inclusion control technique,and then the liquid steel will get be clean or the inclusion will get be harmless,finally the excellent magnetic property of the non-oriented silicon steel can be obtained.Meanwhile,in order to ... 

本实用新型公开了一种铁芯硅钢片卷材的自动放卷上料装置，包括放卷机、导向平台和防折组件，所述导向平台间距设置在放卷机的下方，所述导向平台与放卷机之间构成供料带缓冲的缓冲空间，所述料带在缓冲空间内呈U型状走向，所述导向平台的上方间距设置有防折组件，所述防折组件与导向平台之间构成供所述料带通过的导向通道，所述防折组件设置在料带的内弯侧。通过防折组件对料带的内弯侧进行支撑，能够有效的防止料带被过度弯折，能够对料带进行缓冲和缓冲保护，保证料带放卷上料的稳定性。

本发明涉及一种变压器铁芯制造硅钢片绝缘涂装方法，其使用了一种涂装设备，该涂装设备包括基座、支撑架、转动装置、下降装置、滚涂装置与涂装仓，通过顺时针转动转动环，转动环转动带动齿轮转动，从而实现两个支撑弧形板展开的每个硅钢片进行内部支撑，通过向右推动推杆，从而对每个硅钢片进行阻隔，开启驱动电机，驱动电机输出端带动中心转轴转动，使滑动杆向下移送时带动匚型架向下移动，实现对匚型架内的硅钢片进行浸涂，匚型架向上移动时由于弹簧的作用力进行上下摆动，从而对硅钢片上多余的绝缘漆进行摆掉，开启电动推杆向前移动，从而对支撑弧形板外侧的多个硅钢片进行表面滚涂，避免硅钢片表面在浸涂绝缘漆时产生凸块。

本发明公开了一种取向硅钢微观织构EBSD试样制样方法，包括：1)取样，采用线切割机制取向硅钢试样；2)制样，采用热镶嵌机镶制取向硅钢试样，按照常规方法进行粗磨、细磨、抛光、清洗、吹干；采用240目、400目、600目氧、800目、1000、2000目氧化铝砂纸对试样依次进行一次打磨处理；采用5.0um高效金刚石抛光剂对试样进行抛光处理；3)电解抛光，取向硅钢试样机械抛光后再进行电解抛光。

【作者】 朱一知； 陈山； ...

本发明涉及一种提高取向硅钢冷轧加工性的生产方法，工艺流程为：冶炼、连铸、热轧、常化、酸洗、冷轧、脱碳渗氮、涂MgO、高温退火、涂绝缘层及热拉伸平整；粗轧中坯厚度35‑45mm，两段常化后进行带钢横向分段式冷却水分布。本发明通过对热轧中坯厚度、终轧温度及卷取温度，常化冷却水量及控制方式的调控，使轧前表层晶粒尺寸降低5‑10μm、珠光体体积分数降低6％，轧材冷轧加工性明显改善、成材率可提高8％以上。通过后续冷轧、脱碳退火和高温退火等工序处理，可保证完善的二次再结晶组织及良好磁性能。