硅钢资料

采用自主研发的脉冲磁场退火装置，在取向硅钢脱碳退火过程中分别施加不同强度的磁场，并采用光学显微镜和X射线衍射仪研究了脉冲磁场脱碳退火后试样的显微组织和宏观织构。结果表明，脱碳退火过程中施加脉冲磁场后取向硅钢的平均晶粒尺寸均增加，当磁场强度为40 mT时，平均晶粒尺寸最大，为13.06μm。此外，取向硅钢试样的立方织构{001}<100>强度减弱，高斯织构{110}<001>和{111}<112>织构增强，有利于获得更好的成品织构和磁性能。 Self-developed pulsed magnetic field annealing device was used to apply magnetic field of different intensities during decarburization annealing of an oriented silicon steel, and microstructure and macro-texture of the specimens after decarburization annealing in a pulsed magnetic field were studied by using optical microscope and X-ray diffractometer. The results show that the average grain size of the oriented silicon steel increases with the application of pulsed magnetic field during decarbu... 

阐述了电工钢在\"双碳\"中的作用,强调了电工钢的生产工艺技术及在减少碳排放、降低能耗中的作用,对下游能效升级带来明显的节能及降碳成果。同时,分析了2021年电工钢的生产运行情况,介绍了电工钢的未来发展,并针对如何减少碳排放以及生产更多的更低铁损、更高磁感的电工钢谈了几点启示。 The effects of electrical steels on carbon peak and carbon neutralization were expounded,especially on the achievements of obvious energy saving and carbon reduction to the downstream energy efficiency upgrading bringing from the production technology of electrical steels and their effects to reducing carbon emission and energy consumption.Meanwhile the production situation of electrical steels in 2021 was analyzed,and the future development of electrical steels was introduced,and some advices w... 

本发明提供一种以热轧卷为单元观察时具有在长边方向整个长度上均匀的织构，磁特性的变动小的取向性电磁钢板的制造方法。上述取向性电磁钢板的制造方法，包括如下步骤：将具有规定的成分组成的钢坯热轧而制成热轧板，将上述热轧板退火而制成热轧板退火板，对上述热轧板退火板实施1次或者隔着中间退火的2次以上的冷轧而制成最终板厚的冷轧板，对上述冷轧板实施一次再结晶退火和二次再结晶退火；至少1次冷轧的总压下率为80％以上，并且利用连轧机进行，利用上述连轧机的至少一个机架进行的轧制在压下率为30％以上且上述机架的工作辊的咬入温度T0℃的条件下进行，其中，将上述热轧板退火板的前端和尾端中的一方或两方的上述工作辊的咬入温度设为70℃以上且比上述钢板的温度T0℃高10℃以上的温度。

本发明公开了一种硅钢片压装工装，其涉及电机生产技术领域。其技术方案要点包括下压板，所述下压板上设置有限位结构，所述限位结构用于在硅钢片压装过程中对硅钢片进行限位；所述限位结构包括能够转动调节的限位挡块，所述限位挡块包括多个分别用于对不同尺寸规格的硅钢片进行限位的限位面，且该多个所述限位面与限位挡块的转动轴线之间的最小距离均不相同。本发明能够适用于多种规格的硅钢片，而且操作方便，稳定性好。

对取向硅钢熔融态钢液进行处理,对比研究了不同脉冲参数的作用效果。结果表明,电脉冲对钢锭晶粒组织具有明显的细化作用,凝固组织等轴晶比例大幅上升。在脉冲电容、频率、处理时间和电压中,影响等轴晶比例的最显著性因素为脉冲频率;最优正交实验参数为:电容1 200μF,脉冲频率1 Hz,处理时间5 s,脉冲电压800 V;随着输入能量的增大,等轴晶率先增大后减小,脉冲输入能量为某值时,等轴晶率最大,通过经典形核理论和热力学对这一现象进行了解释。 Research on the influence of the electric pulse on the solidification structure of oriented silicon steel was preformed.Electric pulses in different parameters were applied to molten steel and results were compared.The result shows that solidification structure of oriented silicon steel can be improved by the electric pulse,and the equiaxed crystal ratio increases obviously.Among the four parameter factors of electric capacity,frequency,applied time and voltage,the most effective factor is frequ... 

为了解决目前冷轧产线硅钢现有切边技术存在的微裂纹、应力、毛刺和边浪等问题,采用光纤激光器进行了高速切割实验,对激光功率、切割速度、激光模式等影响因素进行了分析,同时对高速切割时的切割前沿形状进行了研究。结果表明,切割最高速度随着功率的增加而增加;随着离焦量的增加,切割质量下降,挂渣增多,切缝宽度增加,切割深度变浅;基模激光器能量密度更高,所以薄板切割时的切割速度高于多模激光器;切割前沿随着切割速度的增加会变得平缓,速度足够大时,切割前沿甚至接近与切割方向平行,此时切缝下部存在挂渣现象。 In order to solve the problems such as micro crack,stress,burr,edge waves and so on,existing in cold rolling production line of silicon steel side cutting,experimentsof high speed laser cutting using fiber laser were carried out.Laser power,cutting speed,laser mode and other factors were analyzed,at the same time,cutting front geometries were studied.The results show that the maximum speed increases with power.And the increases of defocus result in poor quality,wider kerf and shallowerkerf.Energ... 

本实用新型公开了一种变压器铁芯硅钢片的堆叠装置，包括底座、摆动机构、摆动板和垫高倾板，所述底座上设置有摆动机构，所述摆动板的一端铰接设置在底座上，且所述摆动板间距于摆动轴线的板体与摆动机构对应设置，所述摆动机构驱动摆动板在竖向面内进行往复摆动，所述垫高倾板间距于摆动板设置在底座上，且所述垫高倾板与摆动板之间构成用于叠放硅钢片的叠放区，所述叠放区的底部呈高低倾斜设置，且所述叠放区的低端侧朝向于摆动板，能够使得硅钢片的收集简单，且十分整齐。

本实用新型涉及一种便捷型铁芯硅钢片组装系统。该便捷型铁芯硅钢片组装系统包括硅钢片叠放装置，硅钢片叠放装置包括固定座，固定座上通过轴承转动装配有齿圈，固定座上固定连接有与齿圈同轴的固定盘，固定盘的中心设有中心孔，固定盘上设有六个沿固定盘径向延伸的滑槽，六个滑槽沿固定盘周向均匀分布，每个滑槽内分别滑动装配有滑块，齿圈的上侧面设有上螺纹，滑槽的下侧面设有与上螺纹相匹配的下螺纹，滑块的内端设有定位板，定位板的外侧面上设有用于与硅钢片中心孔孔壁上的割槽相匹配的定位条。相比于现有技术，本实用新型能够对硅钢片进行定位，从而确保各片硅钢片的中心孔以及割槽相对应，提高了硅钢片叠放效率，从而提高了生产效率。

本实用新型属于硅钢片加工技术领域，具体涉及一种利于常化的硅钢缝合结构，包括上层硅钢片、下层硅钢片和连接带，下层硅钢片的一端位于上层硅钢片的下方并与上层硅钢片叠合，上层硅钢片和下层硅钢片的叠合处开有多个排成直线的桥型孔，连接带依次穿过各个桥型孔并同时卡合在上层硅钢片和下层硅钢片上。本方案中，在上层硅钢片和下层硅钢片的叠合处开设桥型孔，利用连接带穿过上层硅钢片和下层硅钢片叠合处的桥型孔，相当于利用连接带将上层硅钢片和下层硅钢片缝合在一起，这样设置能够较好将上层硅钢片和下层硅钢片连接成一体。

本发明特别涉及一种中频用取向硅钢极薄带及其钢基板的制备方法，属于硅钢极薄带制备技术领域，方法包括：将硅钢原料进行冷轧，获得硅钢薄带；将硅钢薄带进行退火，退火采用至少3段式连续退火工艺，获得钢基板；采用本法制得的钢基板制备的中频用取向硅钢极薄带具备优良的磁性能和板形，采用多段式退火，获得稳定的成品性能，制造工艺简单，可实施性高，采用无底层取向硅钢作为母材，节能环保，产品表面质量好，产品可满足中频条件下(≧400Hz)的使用要求。

通过对取向硅钢进行脉冲磁场退火实验,发现在相同的退火时间(6.0 min)内,低于1 T的脉冲磁场可以在一定程度上提高取向硅钢的磁感(B8),而高于1 T的脉冲磁场则会使取向硅钢的磁性能急剧恶化.同时发现,脉冲直流电加热方式会使取向硅钢的磁性能恶化.研究表明,脉冲磁场退火有望成为一种调控材料微观结构的有效手段. We have carried out experiments of annealing by pulse magnetic field.The results show that a pulse magnetic field with intensity lower than 1 T can promote magnetic induction density(B8) of grain-oriented silicon steel,while the magnetic properties deteriorate sharply when intensity is higher than 1 T.It has also been found that heating by using pulse direct current can cause the magnetic properties to deteriorate,in contrast to the traditional heating using resistance furnace.Our research shows... 