硅钢资料

采用化学气相沉积(CVD)渗硅处理工艺连续制备6.5%Si高硅钢,具有优质的软磁性能,通过理论研究化学反应并且用简单的试验设备做进一步的探讨。根据试验的结果对连续制备6.5%Si高硅钢的CVD工艺构造提出全面、有效的建议,实现制备6.5%Si高硅钢系统。 CVD method for continuously manufacturing 6.5%Si Steel Sheet has excellent soft magnetic.Carried out a theoretical study of related chemical reaction and performing basic research with a simple test apparatus.Based on the results,finally proposed an overall process configuration to realize such a production-CVD method for continuously manufacturing 6.5%Si Steel Sheet. 

【作者】 吴玉美； 陆晔； ...

利用热模拟试验机、光学显微镜和X射线衍射仪对Fe-3.2%Si低温取向硅钢热轧工艺参数对组织及织构的影响进行了研究。结果表明,Fe-3.2%Si硅钢在1110℃粗轧、880℃终轧,轧后以10℃/s的速度冷却到550℃卷取,然后空冷到室温,热轧硅钢板沿板厚方向的显微组织不均匀性显著,对后续发展完善的二次再结晶有重要作用。无论是热轧板,常化板还是冷轧板,它们的织构集中分布在γ取向线上,γ取向线的织构除取向密度不同外,织构种类是一致的,这说明γ取向线上织构是有继承性的。从热轧到常化,织构取向密度显著减小,经二次冷轧后,织构密度又显著升高,可见,轧制变形有助于织构的形成并使织构强度升高。 The influence of hot-rolled process parameters on the microstructure and texture of Fe-3.2%Si low temperature hot rolled grain-oriented silicon steel were researched by hot simulation experiment machine,light microscope and X-ray diffractometer.The results show that,Fe-3.2%Si silicon steel is rolled by the technology with a temperature of rough rolling of1110℃,finish rolling of 880℃,coiling with the speed of 10℃ /s,and then cooled to room temperature with air.The microstructure of hot-rolled sil... 

本发明适用于电机硅钢片卷绕成型，用于各种条形冲带的电机定子铁芯卷绕机构，它包括PLC控制系统、人机操作面板、精密双轨道移动架、锁紧机构、同步电机、条形硅钢片导向槽、左右立板、一对可调整平导轮、一对齿轮、传动主轴、气（液）可调节机构、上锥形压辊、下锥形压辊、凸轮盘、驱动定位销、从动轴、左右移动护板、调整锁紧螺母、硅钢片收紧定型器、收集旋转盘、成型螺栓、特制吊装螺栓、旋转电机及机架等。采用本机构，可将各种规格条形冲带辊压成螺旋状，经收紧定型器处理后，定型的叠片不会出现褶皱,可满足不同电机定子铁芯的要求，加工质量较佳。

本发明属于酸洗设备技术领域，具体涉及一种硅钢生产用酸洗设备，包括酸洗池、放卷机构和收卷机构，酸洗池被依次分隔为第一酸洗腔、第二酸洗腔、浸泡腔和喷洗腔；第一酸洗腔和第二酸洗腔内滑动连接有刷洗架，浸泡腔内滑动连接有定位架，喷洗腔内滑动连接有喷洗架；刷洗架、定位架和喷洗架上均转动连接有多根转辊，转辊上设有刷毛；刷洗架和喷洗架上设有用于驱动转辊转动的驱动件；喷洗架上的转辊开有空腔和多个与空腔连通的喷孔，喷洗架上开有与空腔连通的通道和与通道连通的进水口；喷洗腔的底部和侧壁设有多个喷头；酸洗池内转动连接有多根位于第一隔墙上方的刷辊。在本方案，通过酸洗以及充分的刷洗，能够充分有效的除去硅钢表面的氧化皮。

取向硅钢常化工序主要采用现场实测带钢温度的方式测定冷却速率，并通过稳定冷却水温、调整冷却水量及喷梁运行数量等方式保证合理的冷却速率，给常化工艺设计和生产带来诸多不便。通过对常化工艺水冷过程带钢的传热分析求解，在建立带钢水冷温度模型的基础上，研究了不同冷却工艺参数对带钢温度及冷却速率的影响规律以及冷却工艺的交互作用结果。结果表明：模型计算结果能够较好地反映取向硅钢在常化水冷过程中的温度及冷却速率的变化，其计算误差为0.80%～4.11%;在特定取向硅钢厚度规格和常化工艺下，随着常化冷却水量及有效冷却长度的增加，带钢水冷温度及冷却速率与呈非线性变化；常化水冷工艺主要通过调控带钢与冷却水之间热交换量和交换时间实现对带钢温度的控制，实际生产中需综合考虑机组速度、冷却水量及有效冷却长度之间的交互作用，选定喷梁投入数量和冷却水量以获得稳定的冷却速率。 The cooling rate of normalization process mainly determined by measuring the grain oriented silicon steel strip temperature on site, and ensures the cooling rate by stabilizing the cooling water temperature, adjusting the cooling water volume and the operation quantity of spray beam, which brings inconvenience to the normalization process design and production. Based on the heat transfer of strip in the water cooling section of normalization process, the water cooling temperature model for the n... 

综述了国内外大钢铁企业与研究机构采用获得抑制剂法生产低温高磁感取向硅钢的开发及应用情况,分析了以该法生产高磁感取向硅钢过程中抑制剂的控制技术,包括固有抑制剂组成方案、气态渗氮方式与工艺及高温退火工艺的制定.研究表明,固有抑制剂组成方案的设计思路大体一致,化合物抑制剂以AlN为主、硫化物为辅,同时添加少量Sn,Sb等单元素抑制剂,但组成元素含量存在一定差别;在脱碳退火后用NH3进行非平衡渗氮处理已成为气态渗氮的主要方式,但最佳方式仍未明确,具体选择需依据实际生产条件,相应脱碳及渗氮工艺的控制条件差别较大;高温退火工艺中升温制度差别不大,升温阶段退火气氛中N2含量的选择存在差别.此外,分析了抑制剂控制技术目前存在的关键问题,并指出了进一步的研究方向. The current application and exploitation on production of low-temperature high magnetic induction grain-oriented silicon steel with acquired inhibitor method at both iron and steel enterprises and research institutions in the world are reviewed. The control techniques of inhibitors, which include the composition design for inherent inhibitors, nitriding method and process, and secondary recrystallization annealing, are thoroughly analyzed and proposed. It is indicated that the design ideas for i... 

本实用新型公开了一种薄带取向电工钢的热处理炉板，炉板的中心设置有气流循环通孔，炉板的硅钢卷预定压接面设置有通气槽，炉板内设置有进气孔，进气孔的第一孔口设置于通气槽中，进气孔的第二孔口设置于炉板的侧壁上。该薄带取向电工钢的热处理炉板在设置通气槽的基础上，进一步设置进气孔，通过向进气孔中导入气流，增加通气槽的进气量，有助于硅钢卷与炉板压接侧边处水蒸气的及时排出，进一步提高卷内硅钢的热处理品质。本实用新型还公开了一种包含热处理炉板的薄带取向电工钢罩式炉。

试验研究了球刻痕法对高磁感取向硅钢的铁损、矫顽力、相对磁导率、巴克豪森噪声等磁学性能的影响.研究结果表明:经过球刻痕处理后,高磁感取向硅钢的铁损明显降低,矫顽力下降,8 mm球刻痕过后铁损值与矫顽力分别下降16.2%和14.7%,且铁损和矫顽力均随刻痕间距降低而减少.刻痕后的高磁感取向硅钢磁导率在高磁感应强度下明显上升,刻痕后巴克豪森噪声值明显降低,经过对比分析确定8 mm为球刻痕的最佳刻痕间距.从磁畴观察、细化磁畴的原理等方面解释了细化磁畴对高磁感取向硅钢性能的影响原因. The effects of the ball scribing on magnetic properties of high permeability grain-oriented silicon steels,including the iron loss,coercive force,relative permeability,and Barkhausen noise were investigated. The results showed that the iron loss and coercive force of the high permeability grain-oriented silicon steels apparently decreased 16. 2% and 14. 7% respectively after 8 mm ball scribing and they both decreased with the decrease of the scribing spacing at the same magnetic flux density. At... 

本实用新型涉及一种取向硅钢氧化镁线涂层装置，尤其涉及一种取向硅钢氧化镁涂层线用冷涂辊，具有涂层辊本体及包覆在涂层辊本体外层的橡胶涂层；涂层辊本体内部为空腔结构，空腔结构内通有循环冷冻液。本实用新型涂层辊内部设计成空腔结构，并通过循环冷冻液对涂层辊进行冷却降温，既可以达到通过涂层辊对氧化镁进行降温的目的，从而满足工艺要求，防止质量缺陷的产生，还可延缓涂层辊因反复摩擦生热造成橡胶层老化，从而延缓涂层辊使用寿命。

本发明涉及冶金技术领域，具体涉及一种硅锰镇静无取向硅钢的生产方法及浸入式水口。本发明提供的硅锰镇静无取向硅钢的生产方法，包括如下步骤：1)转炉出钢：转炉出钢后对钢水进行真空抽渣，抽渣结束后向钢水中加入石灰、萤石造渣，待渣料熔化后将钢水运至RH工位处理；2)RH真空精炼：将运至RH工位的钢水通过RH真空精炼处理后进行破空、出钢，出钢后在钢包渣面加入渣面脱氧剂以对炉渣进行扩散脱氧；3)连铸浇注：对加入渣面脱氧剂的钢水采用浸入式水口进行浇注。本发明提供的生产方法可有效改善浸入式水口的侵蚀状况，提高浸入式水口的使用寿命，增加连浇炉数，进而提高连铸坯质量稳定性，降低生产成本。

本发明公开了一种取向硅钢实验室轧机二次冷轧方法，包括取样→制样→冷轧轧制规程制定→实验轧机二次冷轧。本发明所要解决的技术问题是提供一种取向硅钢实验室轧机二次冷轧方法，本发明提供的方法轧制出来的取向硅钢二次冷轧试样，对于开展后续研究提供了更加可靠的试样和条件。