本发明提供一种无取向硅钢低温无铬环保绝缘涂层立式干燥固化工艺，冷轧无取向硅钢在镀锌机组经过退火后，通过涂层机涂覆低温无铬环保绝缘涂层，再经过立式干燥炉完成干燥固化，生产冷轧无取向硅钢产品。低温无铬环保绝缘涂层厚度0.8~1.0μm；立式干燥炉各段炉温：加热一段炉温420~450℃，加热二段炉温460~490℃，加热三段炉温500~530℃，加热三段出口板温200~240℃，冷却段出口板温60~65℃；立式干燥炉各段加热时间：加热一段、加热二段、加热三段的加热时间均为3.5~4s。采用本发明工艺不仅能保证钢带涂层均匀，使最终产品的涂层具有优异的绝缘性、耐蚀性、附着性、冲片性、焊接性和耐热性，满足下游工序要求，还可提高产品合格率，减少废品，保证生产顺行。

本发明公开了一种消除取向硅钢热轧边裂的制造方法，通过成分设计、热轧加热和轧制参数优化等方面控制方面，有效解决取向硅钢热轧板边裂缺陷，提高材料的成材率，可以有效消除取向硅钢热轧板的边裂并能保证良好的成品磁性能。

试验研究了0.3 mm取向硅钢冷轧板(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005A1)的退火温度(760~880℃7 min)和退火时间(820℃3~9 min)对该钢的晶粒尺寸,再结晶和织构的影响。结果表明,最佳初次再结晶退火工艺为820℃5 min,该钢的平均晶粒尺寸为14.20μm,完全再结晶率为92%,不利{111}<110>结构含量为3.16%,有利织构{111}<112>,{012}<001>和高斯织构含量分别0.40%,4.73%和2.46%。 The effect of annealing temperature(at 760 ~ 880 X.for 7 min) and time(at 820℃ for 3~9 min) on grain size,recrystallization rate and texture of 0.3 mm cold-rolled sheet of oriented silicon steel(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005Al) has been tested and studied.Results show that with optimum recrystallized annealing at 820℃ for 5 min,the silicon steel average grain size is 14.20 fun,the complete recrystaUization rate is 92%,the unfavourable-texture {111}< 110 > content in steel is ... 

本申请提供了一种取向硅钢铸坯的制备方法及铸坯系统，该制备方法用于对精炼后的钢水进行连铸处理，所述连铸处理包括以下步骤：进行凝固处理，以使所述精炼后的部分钢水凝固形成坯壳；凝固处理时，进行电磁搅拌，以使所述精炼后的剩余钢水最终形成铸坯，其中，所述电磁搅拌的位置和结晶器出口的间距为0.3～1.5m，所述电磁搅拌的电流范围为0A～900A。上述制备方法通过调节电磁搅拌的位置和电流大小来调节电磁搅拌的强度，进而通过电磁搅拌的强度来调节等轴晶的生成量，扩大等轴晶率的范围。

本发明公布了以铜析出粒子为抑制剂的一类取向电工钢及其生产方法，所述取向电工钢化学成分的质量百分比为：C：0.001％～0.07％；Si：2.5％～3.5％；Si+Mn+Al：≤3.5％；Cu：1.0％～2.0％；S：≤0.003％；N：≤0.0045％；其余为Fe和不可避免杂质元素。该取向电工钢的生产工艺步骤可以包括：连铸坯板坯加热、热轧、常化、冷轧、脱碳处理、时效处理、二次再结晶退火处理等。本方法免除了高温热轧加热和二次再结晶后高温长时间加热以净化钢板基体的退火环节，进而可实现连续式二次再结晶退火，大幅度降低了生产能耗，并显著提高生产效率。

分析了高转矩和高转速条件下高效驱动马达铁芯材料对无取向硅钢磁性能要求,讨论了无取向硅钢的高磁通密度和低铁损对电机转矩和效率的影响,介绍了国内外高磁感无取向硅钢发展情况。在生产工艺上,提高钢质纯净度,弱化夹杂物和第二相粒子对畴壁移动和再结晶晶粒长大的钉扎作用,添加微量晶界和带钢表面的偏析元素促使有利织构发展等技术可提高无取向硅钢的磁通密度。 The requirements of high efficient drive motor core materials under the conditions of high torque and high speed were analyzed.The effects of high magnetic flux density of non-oriented silicon steel on the torque and efficiency of the motor were discussed.The development of non-oriented silicon steel with high magnetic was introduced.The magnetic flux density of non-oriented silicon steel sheet can be obviously improved by some production technologies,such as purification steel,weakening the pin... 

薄带连铸流程下取向硅钢粗大λ晶粒(〈100〉//ND,normal direction)的“遗传”会导致磁性能恶化.为解决这一问题，针对取向硅钢的热轧孪生行为开展研究，结果表明：凝固组织粗大的取向硅钢在650℃热轧时可产生大量{112}〈111〉形变孪晶，这与具有高层错能的硅钢在较高温度下难以孪生变形的传统认知不同.热轧过程中复杂的应力状态降低了变形孪晶的取向依赖性，由于具有更高的储存能，孪晶界/孪晶界及孪晶界/晶界交叉点成为再结晶形核的优先位置，大大提高了常化过程中的再结晶率，受沿孪晶界应变分布及孪晶间距离的限制，沿孪晶界形核的再结晶晶粒通常呈“饼状”,最终形成以细小且取向漫散的再结晶晶粒为主的常化组织，消除了初始凝固组织中有害的粗大λ晶粒. In strip casting grain-oriented silicon steels, the inheritance of coarse λ grains(〈100〉//ND, normal direction) can deteriorate their magnetic properties. To solve the problem, twinning behaviors in strip casting grain-oriented silicon steels during hot rolling were investigated in this work. It is found that after rolling at 650 ℃, a number of {112}〈111〉deformation twins are formed in the coarse solidification microstructure of the steels, in contrast to the well-accepted view that it is diffic... 

本实用新型公开了一种形成优质玻璃膜的取向硅钢脱碳退火板，包括主体，所述主体的中部安装有组合架机构，所述组合架机构的前后两端安装有开边架，且组合架机构的底端安装有固定机构，所述主体的中部开设有槽口架，所述组合架机构的中部安装有拼接机构。该形成优质玻璃膜的取向硅钢脱碳退火板设置有拼接机构，便于使用者将内退板与拼接板进行组合使用，通过内退板的四角安装的扣体卡合安装在内槽进行固定锁紧，便于将内退板与拼接板进行组合，加强主体的防护性，便于使用者多次使用和来回使用，由于退火板可反复利用，方便后期形成优质玻璃膜，通过拼接板通过中心凸板与凸槽板进行组合，方便将拼接板的大小进行调节与更换。

本实用新型提出了一种非取向极薄硅钢带刮油装置，包括机壳、固定架、第一安装板及第二安装板；机壳内侧设有固定架，固定架上端设有第一承托板，第一承托板上方设有第一安装板，第一安装板上至少设有一个上刮油刀片，第一安装板与第一弹簧下端连接，第一弹簧上端与机壳顶端相连接，固定架下端与第二弹簧上端连接，第二弹簧下端连接第二安装板，第二安装板上至少设有一个下刮油刀片，机壳底部设有第二承托板，第二承托板与下刮油刀片对应设置；上刮油刀片和下刮油刀片一端设有固定安装孔，另一端均设有斜面。本实用新型的刮油刀片通过弹簧自适应抵接于厚度不同的硅钢带表面，清洁效果好，设计结构简单，维护方便，可循环利用，降低了生产成本。

本实用新型公开了一种硅钢片加工装置，涉及到硅钢片加工装置技术领域，包括安装板，所述安装板的上表面两端均固定连接有固定板，所述安装板的上表面一侧固定连接有涂覆装置，所述安装板的上表面中部固定连接有压平装置，所述安装板的上表面另一侧固定连接有烘干装置，所述固定板的一侧底端通过轴承活动连接有传动辊。本实用新型通过在安装板的上表面一侧设置涂覆装置，涂覆装置对硅钢片的两面进行绝缘层涂覆，在安装板的上表面中部设置压平装置，压平装置包括两个压辊，压辊的一侧设置的限位块中部开设有螺纹孔，转动双向螺杆使得限位块运动，从而使得两个压辊之间的间距被调节，可以根据生产需求调节绝缘涂料的压平厚度。

1.本外观设计产品的名称：硬质合金刀（硅钢片刃切剪用）。;2.本外观设计产品的用途：用于硅钢片刃的剪切。;3.本外观设计产品的设计要点：在于其整体形状。;4.最能表明设计要点的图片或照片：立体图。;5.使用时为安装面，故不常见，省略后视图。;

本发明提供退火隔离剂的制备方法以及退火隔离剂和方向性电磁钢板。由该方法得到的退火隔离剂纯度高、分散性以及密接强度优异，可以在方向性电磁钢板表面形成均匀致密的镁橄榄石层。退火隔离剂的制备方法，其包括：工序(1)：将氧化镁和铵盐溶液混合并反应，制备镁盐溶液和氨，然后使精制的镁盐溶液与氨反应而得到氢氧化镁；工序(2)：将得到的氢氧化镁的一部分在155～230℃下高温熟化，并且将得到的氢氧化镁的另一部分在10～100℃下低温熟化；工序(3)：将在上述各条件下熟化的氢氧化镁混合、烧成，得到氧化镁用于退火隔离剂。