本发明公开了一种物理喷砂方式制备取向硅钢薄带无底层原料的方法，步骤包括：S1、坯料预处理；S2、涂覆隔离剂，后进行高温退火；S3、拉伸热平整；S4、表面喷砂处理，去除底层；S5、去应力退火；本发明优点在于，采用喷砂的物理办法制备取向硅钢薄带无底层原料，代替了传统的用酸去除取向硅钢涂层或硅酸镁底层，结合退火去应力，显著改善了加工质量，使整个加工过程更加环保，也有利于控制成本。

为了确定普通冷轧取向硅钢最优的中间完全脱碳退火工艺,在其一次冷轧后进行5种不同工艺的脱碳退火处理,借助扫描电镜及电子背散射衍射技术研究了不同工艺脱碳退火后的组织、织构和脱碳效果。结果表明:经5种工艺脱碳退火处理后,初次再结晶的平均晶粒尺寸均约为19μm,且不随退火温度和时间的变化而变化;经840℃×10min工艺退火后的晶粒最均匀,高斯织构位向更准确,高斯织构面积分数最多,为3.1%,可将碳脱至0.003 5%。 In order to determine the optimal intermediate complete decarburizing annealing processes for common grain-oriented(CGO)silicon steel,five kinds of intermediate decarburizing annealing processes were conducted,the microstructure,texture and decarbonization after different decarburizing annealing processes were studied by scanning electron microscopy and electro back-scattered diffraction(EBSD)technology.The results show that the average grains sizes of primary recrystallization were about 19μm a... 

【作者】 卢鹏； ...

试验研究了0.3 mm取向硅钢冷轧板(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005A1)的退火温度(760~880℃7 min)和退火时间(820℃3~9 min)对该钢的晶粒尺寸,再结晶和织构的影响。结果表明,最佳初次再结晶退火工艺为820℃5 min,该钢的平均晶粒尺寸为14.20μm,完全再结晶率为92%,不利{111}<110>结构含量为3.16%,有利织构{111}<112>,{012}<001>和高斯织构含量分别0.40%,4.73%和2.46%。 The effect of annealing temperature(at 760 ~ 880 X.for 7 min) and time(at 820℃ for 3~9 min) on grain size,recrystallization rate and texture of 0.3 mm cold-rolled sheet of oriented silicon steel(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005Al) has been tested and studied.Results show that with optimum recrystallized annealing at 820℃ for 5 min,the silicon steel average grain size is 14.20 fun,the complete recrystaUization rate is 92%,the unfavourable-texture {111}< 110 > content in steel is ... 

分别采用传统冷轧轧制液和纳米TiO₂的冷轧轧制液,对无取向硅钢板进行了四辊冷轧实验.重点研究两种冷轧轧制液的轧制润滑性能和对轧后硅钢薄带表面质量和耐蚀性能的影响.通过场发射电子显微镜和能谱仪对使用两种轧制液轧后得到的硅钢薄带表面形貌和成分进行了分析.给出了轧制液中TiO₂纳米粒子在轧制过程中的抗磨减摩机理.在轧制载荷较高时,纳米TiO₂轧制液具有优良的轧制润滑性能并能显著改善轧后硅钢薄带的表面质量.同时在高载荷作用下,TiO₂纳米粒子被压入硅钢薄带基体,形成一个滑动系来支撑载荷,从而使润滑膜的耐磨性提高. Non-oriented silicon steel strips were rolled on a four-high cold rolling mill lubricated by a traditional cold rolling liquid and a nano-TiO₂ cold rolling liquid,with emphasis on studying the rolling lubrication performance of both the liquids and their effect on the surface quality and corrosion resisting property of the silicon steel strips.The surface micrograph and composition of the silicon steel strips after being rolled with both the liquids were characterized by field emissio... 

分析了影响脱碳效果和结晶行为的各种要素及其相互制约关系,提出了Hi-B连续退火工艺曲线,总结得出快速加热及合理稳态气氛是实现工艺制度的关键。结合实际工程,介绍了在连续退火炉设计中快速加热和气氛设计的考虑方法,并指出随着Hi-B产品的发展,如何改进这些方法将是连退工程研发的方向之一。 The factors which affect decarbonization and crystallization and the mutual restriction between them were analyzed.A complete continuous annealing process for Hi-B was put forward.As a result,the rapid heating and the proper steady atmosphere were two important factors.According to an actual project,the consider methods for designing rapid heating and proper steady atmosphere were introduced,and it is pointed that with the development of Hi-B technique,how to improve these techniques would be on... 

本发明特别涉及一种控制边部质量的低牌号无取向硅钢的热轧生产方法，属于无取向硅钢热轧生产技术领域，方法包括：将低牌号无取向硅钢的板坯进行第一次粗轧，将第一次粗轧后的板坯进行第二次粗轧，其中，在第二次粗轧机前的立辊上设置立辊润滑装置，所述立辊润滑装置向所述立辊供给的润滑油的油量为100mL/min‑400mL/min；将第二次粗轧后的板坯进行精除鳞、精轧和卷取，获得边部质量合格的热轧卷；保证良好的立辊辊面状态，可有效解决边部粗糙，有效解决了低牌号无取向硅钢边部粗糙状态，极大的提高了冷轧后工序毛边轧制率，提高了硅钢全工序成材率。

通过对3%Si CGO硅钢进行恒变形速率、不同变形温度下的单道次压缩实验,结合Thermal-Calc软件,金相分析,SEM及EBSD技术,研究了取向硅钢热变形过程中组织和微观织构的变化规律。结果表明:实验钢是在双相区变形,变形后组织主要是铁素体和少量的珠光体。随变形温度的升高,晶粒由长条状变为等轴状,尺寸逐渐变大;CGO硅钢在热变形过程中立方{100}<001>取向是较为稳定存在的。随着变形温度的提高,{111}<110>等取向逐渐转向{110}<1 10>取向,且{110}<1 10>取向逐渐变得锋锐。 3% Si CGO silicon steel was studied at constant strain rate and different deformation temperatures by single-pass compression deformation experiments to reveal the evolution of microstructure and texture during thermal deformation in oriented silicon steel,and the Thermal-Calc software,metallurgical,SEM and EBSD technique was used in the experiment. The results show that experimental steel is deformed at the temperatures of two-phase zone. The microstructure of the deformed steel consists of fer... 

本发明公开了硅钢片均衡堆垛分料系统，包括分料机构和接料机构，分料机构包括料架，料架上具有托板，托板两侧设有第一滚筒架，第一滚筒架顶部设有分料结构；分料结构可实现上下、水平移动；分料结构包括支撑架，支撑架上设有倒吸件；倒吸件包括磁块槽和挡料板，磁块槽设于挡料板上方，磁块槽底部设有磁块，磁块槽上方设有压料胶条，磁块槽和压料胶条可上下移动，接料机构的接料底座可平移，剪力臂架可升降，以改变第二滚筒架高度和水平位置。本发明的优点在于：通过分料结构的倒吸件吸附硅钢片，再将数个硅钢片同时放置于托板侧边数排滚筒上的放置板上，可实现多柱硅钢片的均衡堆垛，通过接料机构可进行多柱硅钢片的同时稳定出料，转运效率高。

本发明公开一种冷轧硅钢的横向同板差控制方法，具体如下：S1、确定冷轧钢板横向同板差的影响因子，包括：热轧钢卷的热卷凸度、工作辊辊型插入量、中间辊窜动值及冷轧钢卷的总切边量；S2、以影响因子为变量构建冷轧钢板横向同板差的计算模型；S3、将热轧钢卷的热卷凸度及冷轧钢板的目标横向同板差输入计算模型，确定最小冷轧钢卷总切边量下的工作辊辊型插入量及中间辊窜动值。明确客户所需的横向同板差，通过改变工作辊辊型插入量X2及工作辊窜动值X3，以此得到冷轧成品钢卷的总切边量最小值，在满足客户对横向同板差的使用要求前提下，降低生产成本，提高产品竞争力。

本实用新型属于检测设备技术领域，尤其为永磁同步电动机硅钢片的检测设备，包括检测台板，所述检测台板的两侧固定连接有立固框，所述立固框的上端固定连接有交叉式顶板，所述交叉式顶板的上端固定安装有液压缸，所述液压缸的输出端固定连接有挤压板，所述检测台板的上端表面固定连接有立固块，所述立固块上插设有拔拉杆，所述拔拉杆的一端固定连接有夹固板，所述检测台板的上端表面开设有条形槽，所述条形槽的内部固定连接有横固杆，所述横固杆的外围套设有弹簧。本实用新型通过设置夹固机构，使得硅钢片冲片在进行抗压检测之前能够得到更好的固定，从而避免检测的过程中产生飞弹现象，确保了设备的使用安全性。

本实用新型公开了一种具有导气槽的低空载损耗电工钢用罩式炉，包括：炉台，顶部设置有加热元件以及连通炉台外缘至中心凹陷的导气通道；炉板，压设于炉台上，设置有与中心凹陷上下对应的中心通孔；砂封槽，设置于炉台的外周，槽底低于导气通道；炉罩，罩设于炉台的顶部及外周形成炉腔，与砂封槽相压接；进气通道，穿设于炉台的中心凹陷中，具有开口向上的排气口；炉罩的炉台套接段内壁设置有导气槽，导气槽的延伸方向与炉罩的高度方向一致，导气槽将气流导向炉台外缘的导气通道进气口。该具有导气槽的低空载损耗电工钢用罩式炉的炉罩设置有导气槽，利用导气槽将硅钢卷外周下行的气流导入炉台的导气通道中，改善钢卷热处理过程中的流场和温度场。