硅钢资料

冷轧无取向硅钢是高技术含量、高附加值产品,工艺复杂,生产周期长,过程控制难度大,被誉为钢铁产品中的\"工艺品\"。热轧生产工艺又是无取向硅钢生产的重中之重,直接决定了硅钢的铁损和电磁性等多项指标。 Cold rolled non-oriented silicon steel is high technology content、high addedvalue product. Its process is complex, Its production cycle is of Length, and Its Process control is difficult. Which is known as the iron and steel products \" Arts and crafts\". Hot rolling production process is the top priority of non-oriented silicon steel, Which Directly determines iron loss of the silicon steel and electromagnetic property, etc many index. 

借助高温激光共聚焦显微镜,在线观察了不同Mn含量的无取向硅钢中夹杂物的尺寸、类型、数量变化。结果表明,Mn含量(质量分数)为0.77%、0.32%时,试样中的夹杂物数量分别约为1000万个/mm3、1600万个/mm3。Mn含量较高的钢种,会优先析出球形、椭球形MnS夹杂物,其析出数量较少,尺寸相对较大,可以有效抑制AlN、CuxS夹杂物析出;Mn含量较低的钢种,会在试样再加热后冷却过程中,先析出相当数量MnS夹杂物,并作为AlN夹杂物析出核心,形成MnS+AlN复合夹杂物。这种复合夹杂物数量较多,尺寸也较大。 Based on the high temperature confocal microscope, the chage of size, type, and quantity of inclusions in non-oriented silicon steels with different Mn content were observed by in-situ SEM. Results show that the inclusion quantities are 10 million per mm3 and 16 million per mm3,while the mass fractions of Mn are 0.77% and 0.32%, respectively. In the silicon steel with higher Mn content, the spherical and ellipsoidal MnS inclusion will precipitate first, which can retard the precipitation of AlN ... 

针对采用含钒铁水生产无取向电工钢存在的铁水脱硫率低、转炉冶炼过程回硫量大、成品硫含量偏高的问题,通过对含钒钛铁水脱硫,减少转炉冶炼过程回硫以及RH脱硫技术等方面的研究,大幅度降低了电工钢成品硫含量。生产表明钢中w(S)=0.001 9%～0.006 9%,平均为0.004 2%;w(S)≤0.008%的比例达到了100%,且w(S)≤0.005%的比例也达到了91.43%。 In cognizance of the problems of low desulphurization rate for hot metal,large sulfur-recovery in converter as well as high sulfur content in products in producing non-orientation electrical steel with vanadium-content hot metal countermeasures have been carried out.Sulfur content in non-orientation electrical steel is decreased obviously by way of study on technologies of desulphurization for hot metal with vanadium & titanium,sulfur-recovery control in converter and desulphurization in RH ... 

本申请提供一种电工钢及其制备方法，制备方法包括：将电工钢的板坯进行热轧获得钢卷；将热轧后的钢卷进行酸洗冷轧；将酸洗冷轧后的钢卷进行第一次罩式退火；将第一次罩式退火后的钢卷进行平整；将平整后的钢卷进行第二次罩式退火；将第二次罩式退火后的钢卷进行重卷，以获得电工钢。本申请提供的电工钢的制备方法采用两次罩式退火，退火的主要目的是消除酸洗冷轧工序产生的加工硬化，使钢板充分再结晶，获得理想的铁损及磁感应强度。而采用两次罩式退火，相对于一次罩式退火工序来说，能够进一步降低铁损，提高电工钢的磁性能。

【摘要】 <正>近日,从重钢集团获悉,日前重钢炼钢厂...

本发明揭示了一种高牌号无取向硅钢及其生产方法。所述无取向硅钢的化学成分以质量百分比计包含：C:0.002～0.004％，S≤0.003％，Si:1.4～1.7％，Mn:0.7～0.95％，P≤0.03％，Sn:0.015～0.035％，11×([Si]‑1.4％)＝14×([Mn]‑0.7％)。所述无取向硅钢的生产方法中，连铸坯加热温度1120～1150℃，精轧终轧温度为890±15℃，最后一道次精轧的压下量≥30％且最后两道次精轧的总压下量≥50％，卷取温度650±20℃；在酸连轧之前不需要进行常化处理，且所得无取向硅钢的磁性能佳，表面无瓦楞缺陷，满足低成本高牌号无取向硅钢的需求。

对西昌钢钒炼钢厂200 t BOF(顶底复吹)-RH-CC工艺生产50PRW800无取向硅钢RH精炼过程中主要成份进行了分析。找出了目前工艺中影响钢液质量的主要因素是钢水脱氧处理不彻底,造成加入的部分硅元素烧损。操作工艺改为铝的脱氧即合金化操作一步完成,保证了钢水中氧处于一个较低的范围,从而减少对硅元素的烧损,提高合金收得率。 The factors of BOF-RH-CC process affecting the compositions of liquid steel were systematically investigated and studied of Xichang Steel and Vanadium Company. The main factors affecting the steel cleanliness were picked out. All results showed that the loss of silicon elements resulting from the deoxidization of liquid steel was not completely. It was suggested that the addition of aluminum for deoxidizing and alloying of molten steel was executed as one step in order to lower the oxygen potent... 

【作者】 陶永根； ...

本发明提供了一种CSP流程生产高效冷轧无取向电工钢及生产方法，成分：C≤0.0030％、Si 1.00‑1.70％、Als≤0.0050％、Mn 0.10‑0.30％、Sn0.01‑0.3％、P≤0.050％、S≤0.0080％、N≤0.0030％、Nb≤0.0030％、V≤0.0030％、Ti≤0.0030％，其余为Fe以及不可避免的杂质。与现有技术相比，本发明CSP流程生产高效冷轧无取向电工钢的方法，通过控制钢中的化学成分，并采用合适的生产工艺，实现了表面质量优良，低铁损、高磁感、低制造成本且生产高效。

本发明涉及硅钢片切片领域，具体涉及一种硅钢片自动切片设备，包括下拉机构、推料机构、硅钢片输送机构、硅钢片推动机构、压片机构、导料壳、两个斜切机构、连接机构和三角切边机构，该硅钢片自动切片设备，通过移动连接机构，使得该设备能够进行两种硅钢片的切割加工，使得该设备能够满足多种硅钢片的加工，通过在移动三角切边机构和斜切机构的位置，使得该设备能够加工出各种硅钢片，且能够单一旋转加工那种硅钢片，并且一次加工出两张硅钢片，通过硅钢片输送机构带动推料机构进行同时运动，避免两个硅钢片之间叠起，当原料与推料机构的端部接触时，由于推料机构的拉动速度比硅钢片推动机构的速度快，避免原料上发生褶皱而影响切割的位置。

本实用新型公开了一种风电机组取向电工钢用罩式炉的砂封振动装置，包括：基座，设置有行走机构，行走机构带动基座沿环形砂封槽槽壁行走；振动齿座，与基座连接，定位座和基座之间夹设有弹性缓振件；振动件，与定位座固定连接；振动齿，与振动齿座固定连接，设置于基座的行走轨迹内侧。该风电机组取向电工钢用罩式炉的砂封振动装置利用砂封槽的槽壁作为行走机构的轨道，振动齿不仅可以平整砂封槽中的密封砂，振动状态下还能使密封砂填充得更趋密实，避免局部密封不良的问题，优化密封效果。

本实用新型公开了一种变压器硅钢片剪切收料装置，其包括底板和存放架推出机构，底板的前侧中部设置有用于放置外设剪切设备的放置区；存放架推出机构包括滑动板座、锁紧组件，滑动板座可左右滑动地安装于底板的上表面，在滑动板的上表面设置有两个用于放置外设的硅钢片存放架的存放架放置槽，两个存放架放置槽呈左右间隔设置，锁紧组件用于锁紧滑动板座与底板之间的相对位置。当该硅钢片存放架存放完后，将滑动板座推动至使得另外一个存放架放置槽设置于放置区的正后方，另外的硅钢片存放架继续接受剪切设备掉落的硅钢片体，可连续地实现硅钢片体的落料存放，令转运和落料的操作不相互干涉，提高生产的效率。