研究了CSP流程试制50W270高牌号无取向硅钢热轧→常化→冷轧→退火过程中织构的演变.利用电子背散射衍射技术对全流程织构进行测量和分析.发现热轧板织构在厚度方向上存在较大差异,表层主要为铜型、黄铜和高斯织构,1/4层存在微弱的高斯织构和旋转立方织构,中心层以γ纤维织构和旋转立方织构为主,还含有较弱的α纤维织构.与热轧板相比,常化板表层和1/4层织构变化不大,中心层旋转立方织构和α纤维织构增强.冷轧板各层均具有α纤维织构和γ纤维织构.与冷轧板相比,成品板各层中α纤维织构基本消失,还出现了立方织构和高斯织构. This article focuses on texture evolution in 50W270 high-brand non-oriented silicon steel produced by CSP in hot rolling,normalizing,cold rolling,and annealing processes.The texture in the whole process was measured and analyzed by electron back-scatter diffraction.It is found that the texture along the thickness direction in hot-rolled strips changes obviously;there are mainly copper,brass,and Goss textures in the surface layer;the 1/4 layer has weak Goss texture and rotating cube texture;γ-fib... 

本实用新型公开了一种可拼接的饰面硅钢石膏板，包括硅钢石膏板，所述硅钢石膏板的一侧外壁贯穿开设有一个固定槽，所述硅钢石膏板位于固定槽的两端外壁均贯穿开设有一个第一螺纹槽，且两个所述第一螺纹槽均贯穿延伸至固定槽内，两个所述第一螺纹槽的内壁均螺纹连接有一根固定螺栓，先将一块硅钢石膏板的一侧固定块插入另一块需要连接的硅钢石膏板开设的固定槽内，再转动固定螺栓，将固定螺栓转入第二螺纹槽内，将固定块与收纳槽进行固定连接，直至将转动帽转动进收纳槽内，当需要上下连接时，将硅钢石膏板上端定位槽插入定位杆内，将两个硅钢石膏板连接，避免在拼接时硅钢石膏板松动，影响使用人员的安装。

本实用新型涉及一种多物理因素耦合作用电工钢片矢量磁特性自动测量系统，多物理因素耦合作用电工钢片矢量磁特性自动测量系统包括上位机、数据采集卡、低通滤波器、功率放大器、隔离放大器、励磁装置、矢量B‑H传感器、x方向励磁线圈、y方向励磁线圈、单片机系统、电源、温度自动加载模块和应力自动加载模块。本实用新型实现了电工钢片复杂磁特性测量过程中温度和应力的自动加载，解决了人为操作繁琐，耗时的缺点，使得电工钢片复杂磁特性的测量过程更加方便，高效，可行性更高。

本申请提供了一种提高高磁感取向硅钢渗氮效率的方法，属于高磁感取向硅钢渗氮处理技术领域，包括所述高磁感取向硅钢按重量百分比包括：Si：2.8～3.4％、C：0.040～0.070％、Als：0.015～0.045％、Mn：0.06～0.14％、S：0.003～0.020％、N：0.003～0.010％、Cu：0.01～0.025％、Sn：0.03％～0.07％、Cr及Ni，Cr和Ni的总含量小于0.5％，其余为Fe和不可避免杂质物，其特征在于，控制脱碳退火后钢带表层氧化物中铁系氧化物的比例，该装置能够增加脱碳退火后钢带表面氧化层中铁系氧化物占整个氧化层重量的比例，从而在获得同等渗氮量的情况下实现了快速渗氮，缩短渗氮时间，提高渗氮效率。

本发明提供一种无铝低合金无取向硅钢氧含量控制方法，属于钢铁冶炼技术领域。该无取向硅钢化学成分按质量百分比为C≤0.005％，Si：0.2％‑0.6％，Mn：0.20％‑0.50％，P：0.03％‑0.08％，S≤0.005％，Als≤0.005％，余量为Fe及不可避免的杂质。其工艺流程为：KR铁水预处理→转炉冶炼→RH真空精炼→连铸。转炉出钢严格控制下渣量，加石灰、萤石、高铝渣面脱氧剂控氧调渣；RH真空精炼脱碳结束后，加低碳低硫硅铁、金属锰、磷铁等脱氧合金化，循环5min后，再加入金属铝终脱氧，同时向钢包渣面加入高铝渣面脱氧剂对炉渣进行脱氧，成分全部达标后净循环时间≥8min，破空、出钢；连铸进行全程保护浇注。使用本发明提供的操作方法，可以得到自由氧含量≤15ppm，总氧含量≤35ppm的钢水，提高钢水洁净度。

本发明公开了一种低磁场条件下高磁感应强度无取向电工钢及生产方法，步骤包括：冶炼：炼钢、连铸生产铸坯，所述铸坯中：以质量百分比计，Si2.0％、Mn0.2‑0.5％、ALs0.3‑0.6％、N≤0.002％、S≤0.002％、Ca≤0.001％，余量为Fe及不可避免的杂质；板坯热轧、卷取；常化处理；退火处理。本发明通过合理的电工钢成分设定、生产工艺、稳定的控制精度，从一贯制角度对产品进行设计及控制，最终能够保证产品质量稳定、具有低磁场条件下高磁感应强度的Si含量2％的0.35mm厚度无取向电工钢产品。

两炉次无取向硅钢XG800WR（/%:0.003～0.004C、0.71～0.75Si、0.32～0.33Mn、0.004～0.007S、0.016P）的炼钢流程为铁水预处理（KR）-210 t顶底复吹转炉-钢包吹氩-RH脱碳精炼-230mm×1220 mm板坯连铸。53 t中间包钢水过热度为25～30℃,钢包到中间包采用长水口全程吹氩保护浇铸,中间包至结晶器采用浸入式水口浇铸。结果表明,在RH、中间包、结晶器过程中钢中总氧以及夹杂物数量和尺寸均明显降低;但在钢包到中间包过程T[O]、[N]和钢中夹杂物数量增加,说明长水口浇铸过程存在二次氧化。连铸坯中T[O]、[N]平均他分别为11×10^-6和30×10^-6,显微夹杂物数量平均为4个/mm²。铸坯中的显微夹杂物主要为3～5μm的AlN,同时存在少量的MnS、Al₂O₃·AlN和Al₂O₃·MgO·MnS。 The steelmaking flow sheet for two heats non-oriented silicon steel XG800WR（/%:0.003～0.004C. 0.71～0.75Si,0.32～0.33Mn,0.004～0.007S,0.016P） is hot metal pretreatment（KR）-210 t top and bottom combined blown converter-ladle argon blowing-RH decarburization refining-230 mm×1 220 mm slab casting.The superheating extent of liquid in 53 t tundish is 25～30℃,whole casting is shielded by blowing argon with long nozzle from ladle to tundish and the submerged nozzle is adopted in casting from tundish to mold... 

介绍了硅钢氧化镁制备方法及高质量硅钢氧化镁制备技术的研究进展,并对利用我国丰富的卤水资源制备硅钢氧化镁进行了展望。 The preparation methods of silicon steel magnesium oxide and research progress of high quality silicon steel magnesium oxide preparation technology were introduced.The use of abundant brine resources in the preparation of silicon steel magnesium oxide was prospected. 

用于层叠铁芯的电磁钢板为一种在母材钢板(2)的表面具有绝缘被膜(3)的电磁钢板，该绝缘被膜(3)是涂布电磁钢板用涂布组合物而构成的，所述电磁钢板用涂布组合物以特定的比例配合有环氧树脂、第1固化剂及第2固化剂，该第1固化剂由包含具有烷基及烷氧基中的任意一者或两者的酚骨架的酚醛树脂构成，该第2固化剂为从酚醛甲阶树脂及苯酚酚醛清漆树脂中选择的1种以上。

本实用新型公开了一种用于硅钢片自动排列叠片装置，包括：第一壳体，所述第一壳体的一侧开设有第一条形孔，所述第一壳体的内侧顶部安装有两个气缸，所述第一壳体内部位于气缸下方设有第一固定板，两个所述气缸的活塞杆均与第一固定板固定连接，所述第一壳体的内侧底部焊接有两个弹簧，所述弹簧的顶部焊接有第二固定板，所述第一壳体的内侧底部安装有第一触碰开关，所述第二固定板底部靠近第一触碰开关的一侧焊接有第一固定块；本实用新型在使用时，通过设置气缸推动第一固定板带动硅钢片运动，使硅钢片移动至第二固定板上，完成对硅钢片的自动叠片工作，无需人工手动对硅钢片进行叠片，提高硅钢片的叠片效率并减少人工劳动负担。

承钢采用铁水预处理(脱硫)→转炉提钒→转炉冶炼→RH精炼→连铸→轧制工艺,成功研发了无取向电工钢CGW800。试制的CGW800钢碳含量≤0.006 0%、氮含量<0.004 0%,热轧后的金相组织为铁素体和少量渗碳体,晶粒度5.5级,获得了较粗大、均匀的晶粒,钢板的成分和力学性能达到了标准要求。 In Cheng Steel,the CGW800 non- oriented electrical steel is successfully developed with process of hot metal pre- treating,vanadium extracting with converter,smelting with converter,RH refining,continuous casting and rolling. In the steel,the carbon content is not higher than 0. 006 0%,nitrogen less than0. 004 0%,the metallographic structure after hot rolling is ferrite and a little amount of cementite,grain size is 5. 5 degree,relative large and even grain got. The composition and mechanical pr... 

【作者】 徐刚； ...