轧制力是影响冷轧带钢厚度精度的关键因素。为实现高精度的冷轧带钢厚度控制,通过优化变形抗力模型参数和摩擦系数模型参数提高冷轧轧制力模型计算精度,并使用指数平滑法的自学习算法保证轧制力精度的稳定性。在首钢股份公司迁安钢铁公司20辊森基米尔轧机生产线进行S12硅钢钢种轧制力优化试验,将优化的模型参数应用于L2并投入现场生产,结果表明该优化方法不仅提高了轧制力设定精度,而且减小了冷轧硅钢的厚度超差长度,提高了成材率。 The rolling force is the key factor which influences the accuracy of cold-rolling strip thickness. To implement high precision control of cold-rolling strip thickness,we optimize the deformation resistance model parameters and friction coefficient model parameters to improve the calculation precision of cold-rolling force model,and use exponential smoothing self-learn algorithm to ensure the stability of rolling force accuracy. In Shougang Qiangang 20-high Sendzimir mill single stand production ... 
2014-05-28 50 5.8

【作者】 宋波; ...
2013-05-28 26 5.8

两炉次无取向硅钢XG800WR(/%:0.003~0.004C、0.71~0.75Si、0.32~0.33Mn、0.004~0.007S、0.016P)的炼钢流程为铁水预处理(KR)-210 t顶底复吹转炉-钢包吹氩-RH脱碳精炼-230mm×1220 mm板坯连铸。53 t中间包钢水过热度为25~30℃,钢包到中间包采用长水口全程吹氩保护浇铸,中间包至结晶器采用浸入式水口浇铸。结果表明,在RH、中间包、结晶器过程中钢中总氧以及夹杂物数量和尺寸均明显降低;但在钢包到中间包过程T[O]、[N]和钢中夹杂物数量增加,说明长水口浇铸过程存在二次氧化。连铸坯中T[O]、[N]平均他分别为11×10-6和30×10-6,显微夹杂物数量平均为4个/mm2。铸坯中的显微夹杂物主要为3~5μm的AlN,同时存在少量的MnS、Al2O3·AlN和Al2O3·MgO·MnS。 The steelmaking flow sheet for two heats non-oriented silicon steel XG800WR(/%:0.003~0.004C. 0.71~0.75Si,0.32~0.33Mn,0.004~0.007S,0.016P) is hot metal pretreatment(KR)-210 t top and bottom combined blown converter-ladle argon blowing-RH decarburization refining-230 mm×1 220 mm slab casting.The superheating extent of liquid in 53 t tundish is 25~30℃,whole casting is shielded by blowing argon with long nozzle from ladle to tundish and the submerged nozzle is adopted in casting from tundish to mold... 
2011-05-28 53 5.8

根据本发明的一个实施例的取向电工钢板,其中存在于电工钢板表面的沟槽以及与沟槽底部相连的再结晶和其他再结晶的平均取向度差为0.5°至10°。
2020-12-18 57 6.8

本实用新型公开了一种取向硅钢二轧料氧化镁冷涂装置,包括主体,所述主体的中部安装有架体,且架体的右侧安装有冷涂机构,所述冷涂机构的右端一侧安装有液压气缸,且液压气缸的内壁连接有连接杆,所述架体的前后两端安装有调节架机构,所述调节架机构的表面安装有防护块,且防护块的内壁安装有橡皮套。该取向硅钢二轧料氧化镁冷涂装置设置有冷涂机构,且箱体通过安装有单独喷管和连接喷头,便于使用者两者兼合使用,可使用单独喷管也可连接喷头,使用者可根据自己使用的需求,对单独喷管和连接喷头进行针对性使用,单独喷管通过安装扣将连接喷头进行拼接使用,箱体通过旋转轴与支撑架的旋转,便于将箱体进行角度旋转。
2020-12-14 48 6.8

本实用新型涉及一种硅钢冲压片质量筛查分拣装置,包括:第一组传送带机构,第一摄像头,设置于第一组传送带机构的上方,用于对硅钢冲压片的第一表面的残损进行检测;第一机械手机构,设置于第一组传送带机构的上方且位于所述第一摄像头的后方;翻转装置,设置第一组传送带机构的后方,用于对第一组传送带机构传输的初检良品进行翻面并将翻面后的初检良品传输给第二组传送带机构;第二组传送带机构,设置于翻转装置的后方;第二摄像头,设置于第二组传送带机构的上方,用于对硅钢冲压片的第二表面的残损进行检测;第二机械手机构,设置于第二组传送带机构的上方且位于第二摄像头的后方。本实用新型可高效的检测每一个产品的外观质量。
2021-08-16 33 6.8

本发明公开了一种高磁感取向硅钢,其含有Fe及不可避免的杂质元素,其还含有质量百分含量如下的下述各化学元素:C:0.02~0.08%,Si:2.0~4.5%,Mn:0.02~0.30%,S≤0.0050%,Als:0.01~0.04%,N:0.002~0.01%,Nb:0.0050~0.0600%;以及P:0.01~0.1%,Sn:0.01~0.30%,Cu:0.01~0.50%的至少其中一种。此外,本发明还公开了上述高磁感取向硅钢的制造方法,其包括步骤:(1)制得板坯;(2)板坯加热;(3)热轧,其包括:粗轧、在热卷箱内卷取保温,以及精轧;其中粗轧结束温度高于970℃;卷取温度为800~1050℃,卷取时间为30~200s;精轧开始温度低于1050℃;(4)冷轧;(5)脱碳退火;(6)渗氮;(7)涂覆退火隔离剂;(8)高温退火;(9)涂覆绝缘涂层和激光刻痕。
2021-10-19 61 6.8

热轧轧制工艺对产品性能和轧制稳定性影响很大,对中低牌号无取向电工钢,当在两相区轧制时,热轧塑性明显降低,板形变坏,易出现边裂等情况。以50W1000为例,通过对其变形抗力进行研究,得出把两相区控制在F4与F5之间为最佳轧制工艺的结论。在此基础上制定了一套较为合理的热轧工艺制度。采用新的轧制工艺后,50W1000热轧精轧的稳定性明显改善,热轧产品合格率由开发初期的40%左右提高到95%以上。 The hot rolling process has great influence on product′s performance and rolling stability.For the low medium grade non-oriented electrical steel,when non-oriented electrical steel is rolled in tow phase region,the hot rolling plasticity reduces obviously,the shape of strip goes bad and easily to crack at the edge.The deformation resistance of 50W1000 steel was investigated.The results show that the optimal rolling process is to control the two phase region between F4 and F5.Based on the results... 
2011-03-28 64 5.8

针对薄板坯连铸连轧流程结合\"获得抑制剂法\"所制备的低温高磁感取向硅钢,通过热力学计算研究了AlN与MnS在连铸与均热过程中的析出规律与行为。计算结果表明,连铸过程中AlN在凝固后的高温α相中便可能析出,而MnS仅可能在凝固后的α+γ两相区内析出。钢中AlN与MnS在均热过程中均处于部分固溶与部分析出的状态。后续高温渗氮处理后初次晶粒的异常长大并不明显,表明渗氮处理前钢中固有抑制剂的数量相对充足。 The precipitation behavior of MnS and AlN in low-temperature high magnetic induction grain-oriented silicon steel produced by thin slab casting and rolling process with\"acquired inhibitor method\"during continuous casting and soaking was studied by thermodynamic calculation.The calculated results show that AlN is likely to precipitate in ferrite after solidification.However,MnS can precipitate only in the two phase region of ferrite and austenite.Meanwhile,MnS and AlN in the steel can not be comp... 
2014-10-28 59 5.8

介绍了重庆钢铁股份有限公司炼钢厂生产低碳低硅钢的脱氧工艺,对连铸过程中水口结瘤的原因进行分析,并提出了优化措施。生产实践表明:钢水中的活性氧质量分数控制在10×10-6~30×10-6时,单中包浇铸炉数由6~7炉提高到11~12炉,同时能保证连铸顺行和减少铸坯气孔。 The deoxidation process of low-carbon and low-silicon steel in steel plant of Chongqing Steel was introduced.The nuzzle clogging was analyzed and some measures were put forward.Production experiments showed that when the active oxygen was controlled between 10×10-6~30×10-6,the amount of furnaces would rise from 6~7 to 11~12,which will make the casting process work well and reduce casting holes. 
2011-05-28 41 5.8

以一种新的Fe-Si合金制备工艺为出发点,研究了不同放电等离子体快速烧结工艺(SPS)和Si含量变化对Fe-Si合金材料显微组织与磁性能的影响。结果表明,在烧结温度为1 000℃时制备的Fe-6.5%Si合金(质量分数,下同)的综合磁性能较好,其在50Hz下的铁损为0.549W/kg,最大磁感应强度为0.124 3T,矫顽力245.6 A/m,磁导率0.338mH/m。另外,材料的最大磁感应强度随Si含量的增加显著增长,1 000Hz下,Fe-10.0%Si的最大磁感应强度可达到Fe-6.5%Si合金的5倍左右。 The effects of Si content and SPS technology on microstructure and magnetic properties of Fe-Si alloy material were studied in the paper.It shows that the magnetic properties are the best when the content of Si is 6.5wt% and the sintering temperature is 1 000℃,the iron loss is 0.549W / kg in 50Hz,maximum magnetic induction is 0.124 3T,coercive force is 245.6A / m and permeability is 0.338mH / m。And,the maximum magnetic induction increases significantly with the increase of Si.The maximum magneti... 
2013-04-28 43 5.8

一种高强型高频电磁性能优异的硅钢薄带板,钢中化学成分按重量百分比计为:C≤0.0027%、Si3.10%~3.35%、Als0.80%~1.2%、Mn0.20%~0.85%、P≤0.050%、S≤0.0020%、N≤0.0020%、Ti≤0.0020%、V≤0.0020%、Nb0.0050%~0.080%,其余为Fe和不可避免的杂质。本发明的无取向硅钢薄带产品用于新能源汽车驱动电机的制造,其强度高,中高频电磁特性优异。
2021-09-15 35 6.8