硅钢资料

针对传统工艺生产硅钢周期长、能耗大等缺点,采用双辊连铸工艺制备3%Si无取向硅钢连铸薄带,利用MEM,SEM和TEM观察了铸带的组织、织构及析出物,同时对比了Al的质量分数为0.6%和0.9%的连铸薄带在组织、织构及析出物特征方面的异同.结果表明:双辊连铸工艺生产的3%Si无取向硅钢铸带的组织为均匀等轴晶粒,平均晶粒尺寸约为300μm;织构组成随Al质量分数的不同具有明显差别,Al质量分数为0.9%的铸带中{100}织构强度是随机织构的7倍;铸带中的析出物为AlN和MnS,最大尺寸分别为500和50 nm左右. Given the lengthy production cycle,high energy consumption,and other shortcomings of the traditional process for producing silicon steel,a twin-roll casting process was used to produce 3%Si non-oriented silicon steel casting strips. MEM,SEM,and TEM were used to compare micro-structure,texture,and precipitate characteristics of a casting strip containing 0.6%Al with another containing 0.9%Al.The structure of 3%Si non-oriented silicon steel produced by the twin-roll casting process was a uniform i... 

利用背散射衍射技术(EBSD)和XRD,研究了两段式脱碳退火工艺对取向硅钢纵截面初次再结晶的微区取向、取向差分布、特殊晶界(CSL)及高温退火试样高斯织构。分析了初次再结晶晶界特征对取向硅钢高温退火后宏观织构的影响。结果表明:初次再结晶的纵截面基体中Σ3和Σ5晶界使得高斯晶粒有着较高的迁移率,在高温退火时借助20o～45°的大角度晶界的界面能吞并周围{111}<112>晶粒迅速长大,形成密度水平较高的高斯织构。 Micro area orientation of primary recrystallization,the misorientation distribution,special boundaries under different two-stage decarburization annealing and the Goss texture under high temperature annealing the longitudinal section of grain-oriented silicon steel were detected by electron back scattering diffraction(EBSD) and X-ray diffraction(XRD).The effect of primary recrystallization grain boundary on macrotexture after high temperature annealing was analyzed.The results show that the Σ3 a... 

本发明公开了一种批量稳定生产高牌号无取向电工钢的方法，包括以下步骤：开卷→加热→水套冷却→水雾冷却→水喷淋冷却→抛丸→酸洗→切边→卷取→使用单机架六辊轧机进行轧制成卷；该方法可实现高牌号无取向电工钢在六辊UCM轧机冷轧后无边裂产生，可将带钢板形值控制在‑5I～+5I，厚度精度控制在±3μm，该方法生产的高牌号无取向电工钢无板形及表面质量缺陷，产品质量良好，可实现高牌号无取向电工钢的批量稳定轧制。

本发明公开了一种硅钢片压装工装，其涉及电机生产技术领域。其技术方案要点包括下压板，所述下压板上设置有限位结构，所述限位结构用于在硅钢片压装过程中对硅钢片进行限位；所述限位结构包括能够转动调节的限位挡块，所述限位挡块包括多个分别用于对不同尺寸规格的硅钢片进行限位的限位面，且该多个所述限位面与限位挡块的转动轴线之间的最小距离均不相同。本发明能够适用于多种规格的硅钢片，而且操作方便，稳定性好。

本实用新型涉及一种便捷型铁芯硅钢片组装系统。该便捷型铁芯硅钢片组装系统包括硅钢片叠放装置，硅钢片叠放装置包括固定座，固定座上通过轴承转动装配有齿圈，固定座上固定连接有与齿圈同轴的固定盘，固定盘的中心设有中心孔，固定盘上设有六个沿固定盘径向延伸的滑槽，六个滑槽沿固定盘周向均匀分布，每个滑槽内分别滑动装配有滑块，齿圈的上侧面设有上螺纹，滑槽的下侧面设有与上螺纹相匹配的下螺纹，滑块的内端设有定位板，定位板的外侧面上设有用于与硅钢片中心孔孔壁上的割槽相匹配的定位条。相比于现有技术，本实用新型能够对硅钢片进行定位，从而确保各片硅钢片的中心孔以及割槽相对应，提高了硅钢片叠放效率，从而提高了生产效率。

本实用新型涉及硅钢生产设备技术领域，具体公开了硅钢冷轧用厚壁套筒，包括外筒和内筒，所述外筒与内筒之间固定有若干连接板，所述外筒上开设有插缝槽，所述外筒的内壁上设有靠近插缝槽设置的限位件，所述限位件包括锁止板和弹性件，弹性件一端固定在外筒的内壁上，另一端固定在锁止板的顶部，所述锁止板上设有朝向插缝槽的斜面。本专利中通过外筒与内筒设置，既提高了整个套筒的厚度，使其能够承受硅钢带卷绕时的压力，同时也减少因提高套筒厚度使得套筒的重量增加的问题，这样设置整个套筒的质量较轻。

本实用新型公开了一种硅钢片落料收集箱，涉及到硅钢片加工领域，包括支撑架，所述支撑架的顶端通过回转轴承活动连接有收集箱，所述支撑架的一端固定连接有落料筒，所述收集箱的顶端固定连接有进料口，所述收集箱的下端一侧固定连接有出料口。本实用新型通过在支撑架上设置有可活动的落料筒，落料筒能够根据不同型号的硅钢片将出料口转动至不同的收集箱处，使得本装置能够将不同型号的硅钢片进行分类收集，提高了本装置的工作效率，并通过限位组件能够将落料筒限位，防止落料筒随意转动，保证了本装置收集的稳定性，同时在落料筒的内部设置有缓冲块，缓冲块在阻尼板和缓冲弹簧的作用下起到了阻尼缓冲的作用，避免硅钢片在落料的过程中受损。

采用中、厚板坯生产技术对取向硅钢进行了研制和开发,对热轧及后工序样品进行了金相组织观察和EBSD分析,探讨了两种组织及织构的差异性,研究结果表明:除高温退火样品外,中板坯生产的取向硅钢各工序样品平均晶粒尺寸大;厚板坯生产的取向硅钢热轧和常化样品亚表层Goss织构强;中板坯和厚板坯的脱碳退火板织构没有明显区别。中板坯生产的取向硅钢成本低,产品磁性能和质量与厚板坯相当。 Grain oriented silicon steel was researched and developed by medium thickness slab and thick slab.Microstructures observation and EBSD analysis to the samples of hot rolling and following processes were carried out,respectively.The differences between the two kinds of microstructures and textures were discussed.The results show that the average grain sizes of every process samples are larger except that of high temperature annealing samples of grain oriented silicon steel produced by medium thic... 

采用扫描电镜、场发射扫描电镜、能谱仪等对50SW1300冷轧无取向硅钢中的夹杂物分不同尺寸区间进行数量统计,利用主成分回归分析法,即数据的标准化处理—主成分分析—回归分析—标准化的变量还原成原始变量—确定显著影响因素,综合分析夹杂物总量及各尺寸区间的夹杂物数量对无取向硅钢磁性能的影响。结果表明:主成分回归分析能够从夹杂物尺寸区间及数量的多个影响因素中提取主要的因素,定量研究其对磁性能的影响。分析表明,显著影响无取向硅钢铁损的夹杂物为100~500nm的AlN、AlN+MnS、MnS、Al2O3、AlN+Al2O3,而劣化磁感最明显的夹杂物尺寸区间为100~200nm。 Different size intervals of inclusions in cold rolled non-oriented silicon steel 50SW1300 were counted by scanning electron microscope(SEM),field emission scanning electron microscope(FESEM)and energy disperse spectroscopy(EDS).With principal component regression method:standardization for experimental data,principal component analysis,regression analysis,transform standardized variables into original variables,determination of significant factor,effects of the total number of inclusions and the... 

本实用新型公开了一种镀铝锌硅钢板平整装置，包括辊轮整形装置与曲面压平装置，所述辊轮整形装置包括第二底板，所述第二底板的上表面固定连接有两个驱动电机，所述驱动电机的输出端固定连接有第二推杆，所述第二推杆的输出端固定连接有滑动块，所述滑动块的左侧壁转动连接有转杆，所述转杆的中部固定连接有辊轮；所述曲面压平装置包括第一底板、顶板，所述第一底板与顶板之间固定连接有四根导柱，所述导柱的中部滑动连接有上模座，所述上模座的下表面可拆卸连接有上模具，所述第一底板的上表面固定连接有下模座，所述下模座的上表面可拆卸连接有下模具。本实用新型中，辊轮整形机与曲面压平机结合能够有效地提高钢板的压平后的平整度。

本实用新型公开了一种硅钢卷切边防护装置，包括从左到右依次设置的开卷机、分切机、张力调节机以及收卷机，所述张力调节机前后两侧均设置有通过电机驱动用于收拢切边废料的收料装置。本实用新型，通过两组滚轮的夹持能够对废料进行导向，使得废料准确的经过检测组件之间，通过上下触头相对设置，将切边废料夹在中间，当出现断料后，中间没有支撑，下触头通过第一弹簧带动与上触头接触，形成闭合电路，通过报警组件进行报警，断料时，报警组件工作的同时，收料装置上的电机断电，且第一电磁铁和第二电磁铁通电产生磁性，相互吸附，将上夹板向下带动，上下夹板通过两组防滑垫将料头夹住，避免被甩出，大大增加安全系数。

本发明涉及一种冷连轧法生产无取向高硅钢的方法，RH真空脱碳处理后，铝脱氧及部分铝合金化，合金化后大罐钢水净循环大于3次或大于5分钟；熔炼合格钢水至连铸开浇前静置时间大于二十分钟；控制过热度5～15℃；采用电磁搅拌，控制等轴晶比例45％以上；3)热轧工序板坯装炉温度大于750℃；常化使晶粒尺寸在90～110μm范围内；连续退火炉加热段温度设定950～1150℃，均热段温度设定900～1050℃，全氮气干气氛保护，控制晶粒尺寸120～170μm。生产全过程中的热履历参数控制，充分发挥设计的微合金元素功能，改变析出物的组成、大小、形态及分布。