硅钢资料

利用背散射衍射技术(EBSD)和XRD,研究了两段式脱碳退火工艺对取向硅钢纵截面初次再结晶的微区取向、取向差分布、特殊晶界(CSL)及高温退火试样高斯织构。分析了初次再结晶晶界特征对取向硅钢高温退火后宏观织构的影响。结果表明:初次再结晶的纵截面基体中Σ3和Σ5晶界使得高斯晶粒有着较高的迁移率,在高温退火时借助20o～45°的大角度晶界的界面能吞并周围{111}<112>晶粒迅速长大,形成密度水平较高的高斯织构。 Micro area orientation of primary recrystallization,the misorientation distribution,special boundaries under different two-stage decarburization annealing and the Goss texture under high temperature annealing the longitudinal section of grain-oriented silicon steel were detected by electron back scattering diffraction(EBSD) and X-ray diffraction(XRD).The effect of primary recrystallization grain boundary on macrotexture after high temperature annealing was analyzed.The results show that the Σ3 a... 

为研究常化温度对热轧无取向硅钢组织与织构的影响,采用光学显微镜、背电子散射衍射技术研究了不同常化温度对其影响。结果表明,实验硅钢板在700～850℃温度下常化时,随常化温度的升高,晶粒尺寸增大,有利组分α织构增强,不利组分γ织构降低。对比研究了800℃和850℃常化热轧板CSL晶界分布图与取向差分布图,在本文研究条件下,Goss织构易在Σ=3,9的CSL晶界及晶粒取向差为30°～55°处形成。 The hot strips normalized at different temperatures were investigated by optical microscope and EBSD to study the effect of normalizing temperature on microstructure and texture of hot-rolled non-oriented silicon steel sheets.The results show that the grain size increases,the intensity of α-fibre texture increases,and the γ-fibre texture decreases when the hot strips are normalized at the 700-850 ℃.And CSL boundaries of Σ=3 and 15,and misorientation angles between 30° and 55° are more likely rel... 

针对传统工艺生产硅钢周期长、能耗大等缺点,采用双辊连铸工艺制备3%Si无取向硅钢连铸薄带,利用MEM,SEM和TEM观察了铸带的组织、织构及析出物,同时对比了Al的质量分数为0.6%和0.9%的连铸薄带在组织、织构及析出物特征方面的异同.结果表明:双辊连铸工艺生产的3%Si无取向硅钢铸带的组织为均匀等轴晶粒,平均晶粒尺寸约为300μm;织构组成随Al质量分数的不同具有明显差别,Al质量分数为0.9%的铸带中{100}织构强度是随机织构的7倍;铸带中的析出物为AlN和MnS,最大尺寸分别为500和50 nm左右. Given the lengthy production cycle,high energy consumption,and other shortcomings of the traditional process for producing silicon steel,a twin-roll casting process was used to produce 3%Si non-oriented silicon steel casting strips. MEM,SEM,and TEM were used to compare micro-structure,texture,and precipitate characteristics of a casting strip containing 0.6%Al with another containing 0.9%Al.The structure of 3%Si non-oriented silicon steel produced by the twin-roll casting process was a uniform i... 

通过对连退线SF炉内的电加热体的焊接技术进行总结分析,得出焊接时应采用的主要方法,采用本焊接方法可提高电加热体的焊接速度和焊接质量,保证了焊接质量和施工工期。 SF furnace for continuous annealing line heating body welding technology summary,the main method used in welding,welding method by using the electric heater to improve the welding speed and welding quality through the implementation of this method to ensure the welding quality and Construction period. 

冷轧无取向硅钢是高技术含量、高附加值产品,工艺复杂,生产周期长,过程控制难度大,被誉为钢铁产品中的\"工艺品\"。热轧生产工艺又是无取向硅钢生产的重中之重,直接决定了硅钢的铁损和电磁性等多项指标。 Cold rolled non-oriented silicon steel is high technology content 、high added value product. Its process is complex, its production cycle is of length, and its process control is difficult, which is known as the iron and steel products \" Arts and crafts\". Hot rolling production process is the top priority of non-oriented silicon steel, which directly determines iron loss of the silicon steel and electromagnetic property,as well as other many index. 

本实用新型公开了一种电工钢自粘涂层液生产用搅拌釜，包括釜体，釜体的内部通过两个第一隔板分隔成第一安装腔、第二安装腔和搅拌腔，釜体的内部设有传动组件，传动组件包括伺服电机、主动轴和两个从动轴，伺服电机固定安装在釜体顶端的中部，伺服电机的输出轴与主动轴的顶端固定连接，本实用新型的有益效果是：通过设有八个与十二个搅拌叶片相交错的挡板，避免搅拌轴在搅拌过程中产生离心力造成漩涡，使自粘内外侧的涂层液得到充分搅拌，通过设有循环泵机、第二隔板和流通槽使搅拌釜内的自粘涂层液处于流通的状态，使底部不易被搅拌的涂层液能够得到充分搅拌，在提高搅拌釜的灵活性的同时，保留其原有的稳定性。

【摘要】 <正>日前,宝钢自主研发的新型高磁感取向...

一种电工钢切片用辅助定位装置，涉及电工钢加工技术领域，包括加工台、支撑腿、定位块、侧板、滑杆、移动板、顶板、滑动架、伸缩杆、切片装置、定位杆和挡板；支撑腿设置在加工台底部；定位块设置有两组，两组定位块均设置在加工台上，两组定位块沿横向分布，每组定位块设置有两个，每组的两个定位块沿纵向分布；侧板设置有两个，两个侧板均设置在加工台纵向一侧，两个侧板沿横向分布；滑杆设置在两个侧板之间；移动板沿横向滑动设置在滑杆上；顶板设置在移动板靠近加工台的纵向一侧，顶板位于移动板上端。本实用新型能够方便工作人员切割出一定尺寸的电工钢切片，且切割精度很高。

本发明涉及薄规格高牌号无取向硅钢冷轧领域。一种提高超薄规格高牌号无取向硅钢厚度精度的冷轧方法，硅钢成品厚度规格在0.15mm～0.25mm，坯料采用常化酸洗切边后的硅钢卷，初始厚度为2.0～2.3mm，采用二十辊单机架轧机轧制，在轧制过程中，对整个轧制过程进行控制。本发明的有益效果是：解决二十辊轧机超薄规格无取向冷轧硅钢纵向厚度波动同时减小横向同板差的方法。

文章以国内某公司硅钢厂连续退火机组1号辐射管加热段为研究对象,分析炉内传热机理,建立并开发了辐射管加热段的传热模型。采用生产实际数据对模型进行了验证,以总燃料消耗量最小为目标,得出该炉段长度方向上燃料的最佳分配机制。所得结论为该公司连续退火机组节能控制提供理论依据。 Taking the radiant tube heating section of No.1 continuous annealing unit in a silicon steel plant of a domestic company as the research object, the heat transfer mechanism in the furnace is analyzed, and the heat transfer model of the radiant tube heating section is established and developed. The model is verified by the actual production data. Aiming at the minimum total fuel consumption, the optimal fuel distribution mechanism in the length direction of the furnace section is obtained. The co... 

本发明涉及硅钢板技术领域，尤其涉及一种硅钢板毛刺修整机，包括工作台，所述工作台顶端面的一侧通过升降座安装有打磨机构，工作台顶端的另一侧设置有连接柱，连接柱上部的一侧水平安装固定有横梁，横梁底端面的中部竖直安装有液压杆，液压杆的底端安装有打磨机构，且上、下两个打磨机构交错分布，本发明中通过上、下两个打磨机构的主打磨带对硅钢板的顶端面和底端面进行打磨，副打磨带对硅钢板的侧端面进行打磨，从而能够对硅钢板的水平端面以及侧端面同时进行打磨去毛刺，提高了硅钢板整体毛刺修整的效率。

本发明涉及一种变压器硅钢片智能叠片机械及叠片方法，包括工作台、叠片机构、交替机构、放置机构和交换机构，所述的工作台上方设置有叠片机构，叠片机构上右方设置有交替机构，叠片机构左右对称设置有放置机构，放置机构前方设置有交换机构，本发明采用放置机构放置待叠片的硅钢片，一号电动气缸与二号电动气缸分别交替带动连接板上的一号电磁铁与连板上的二号电磁铁吸附二号水平板上弧形杆内的硅钢片到一号数片板上的圆弧挡板内，当二号水平板上弧形杆内的硅钢片吸附完时，推动放置硅钢片的三号水平板在前后两个导向板之间，然后再将待叠片的硅钢片放在二号水平板上的弧形杆内，这种交换方式节约了叠放时间，提高了工作效率。