采用中、厚板坯生产技术对取向硅钢进行了研制和开发,对热轧及后工序样品进行了金相组织观察和EBSD分析,探讨了两种组织及织构的差异性,研究结果表明:除高温退火样品外,中板坯生产的取向硅钢各工序样品平均晶粒尺寸大;厚板坯生产的取向硅钢热轧和常化样品亚表层Goss织构强;中板坯和厚板坯的脱碳退火板织构没有明显区别。中板坯生产的取向硅钢成本低,产品磁性能和质量与厚板坯相当。 Grain oriented silicon steel was researched and developed by medium thickness slab and thick slab.Microstructures observation and EBSD analysis to the samples of hot rolling and following processes were carried out,respectively.The differences between the two kinds of microstructures and textures were discussed.The results show that the average grain sizes of every process samples are larger except that of high temperature annealing samples of grain oriented silicon steel produced by medium thic... 

随着中国电工钢产量的增加,硅钢级氧化镁需求量不断增加,传统的以白云石为原料制备氧化镁的工艺已经无法满足市场需求。中国是一个卤水资源丰富的国家,因此,研究如何资源化综合利用盐湖资源变得越来越重要。硅钢级氧化镁是一种制备取向硅钢的涂层材料,主要用于取向硅钢高温退火处理阶段,起到隔离剂、绝缘膜层、脱硫、脱磷等作用。综述了制备硅钢级氧化镁的方法、工艺流程、研究进展及存在的问题,指出了硅钢级氧化镁制备技术的发展方向,并对中国卤水资源的利用提出了建议。 With the increasing output of electric steel,the demand for silicon steel grade magnesium oxide(MgO) is larger and larger in China,and the traditional MgO production process with dolomite as raw material has been unable to meet market demand.China is a brine resource-rich country,the study of how to comprehensively utilize salt lake resources has become increasingly important.As a coating material used for preparing oriented silicon steel,silicon steel grade MgO is mainly used in the process of ... 

对硅钢板材分别进行异步和同步轧制,研究了轧制参数包括速比、压下量和道次对板材表面显微组织的演变的作用.结果表明,异步轧制硅钢板材表面形成了晶粒尺寸为10~50 nm,取向接近随机分布的纳米晶,而同步轧制板材的表面只形成了位错胞,证明异步轧制可以诱发表面纳米化.异步轧制板材表面纳米晶的形成过程为:在剪切力的反复作用下,高密度位错形成、滑移、湮灭和重组形成亚微米尺度的亚微晶/位错胞.随着压下量和轧制道次增加,高密度位错重复以上过程使晶粒尺寸减小、取向差增大,最终形成取向接近随机分布的纳米晶组织.大压下量和多道次是异步轧制诱发板材表面纳米化的关键,而速比的增加可以加快纳米化进程. Surface nanocrystallization(SNC) can effectively enhance the surface and global properties of the metallic materials,such as microhardness,intensity,fatigue,wear and corrosion resistances,therefore provides more promising practical industrial applicability.Up to now,several SNC treatment methods were developed based either on the principles of ball impactions or friction sliding,however,difficulty still exists for the surface treatment of large-dimensional samples with high efficiency.Recently,m... 

电动汽车电机在高速旋转时承受离心力和电磁力的作用,在进行电机转子设计时,既要考虑电磁性能,还要考虑机械性能。对电机转子受力情况进行了综述,分析了转子用电工钢疲劳性能参数的重要性,详细阐述了试样抛光、表面处理、试样的对中和安装对测试结果的影响。 The motor of electric vehicle bears big force for high speed rotors,mainly including centrifugal and electromagnetic forces.The magnetic and mechanical aspects of the electrical steel are crucial to machine design.In this paper,the forces applied on the motor were summarized and importance of fatigue properties was analyzed.The influence of specimen polish,surface treatment,alignment and installation on fatigue testing result were represented in detail. 

本发明提出了一种可修饰取向硅钢表面的无铬无机绝缘涂料及其制备方法，该涂料按照重量份计包括以下组份：磷‑硅溶胶40‑70份、钛改性增稠剂预溶胶25份、抑泡剂0.2‑1份、流平剂0.05‑0.2份和去离子水3.8‑34.75份。该涂料的制备方法为：先制备磷‑硅溶胶和钛改性增稠剂预溶胶；然后向磷‑硅溶胶中加入抑泡剂并搅拌均匀；再加入去离子水并搅拌均匀；再分次缓慢加入钛改性增稠剂预溶胶并搅拌均匀；最后加入流平剂并搅拌均匀。本发明所制备的无铬无机绝缘涂料可修饰取向硅钢表面瑕疵露晶等形貌缺陷；在取向硅钢表面形成的绝缘涂层具有良好的附着力和耐热性；涂料采用的原料均为无污染的环保材料，解决了含铬绝缘涂料带来的环境危害。

为了确定普通冷轧取向硅钢最优的中间完全脱碳退火工艺,在其一次冷轧后进行5种不同工艺的脱碳退火处理,借助扫描电镜及电子背散射衍射技术研究了不同工艺脱碳退火后的组织、织构和脱碳效果。结果表明:经5种工艺脱碳退火处理后,初次再结晶的平均晶粒尺寸均约为19μm,且不随退火温度和时间的变化而变化;经840℃×10min工艺退火后的晶粒最均匀,高斯织构位向更准确,高斯织构面积分数最多,为3.1%,可将碳脱至0.003 5%。 In order to determine the optimal intermediate complete decarburizing annealing processes for common grain-oriented(CGO)silicon steel,five kinds of intermediate decarburizing annealing processes were conducted,the microstructure,texture and decarbonization after different decarburizing annealing processes were studied by scanning electron microscopy and electro back-scattered diffraction(EBSD)technology.The results show that the average grains sizes of primary recrystallization were about 19μm a... 

本发明揭示了一种无取向硅钢及其生产方法。所述生产方法包括：按照Si0.8～1.1％、Mn0.2～0.4％、不添加Sn和Sb进行炼钢，并制坯；将铸坯加热到1060～1120℃并保温150min以上，而后轧成厚度40～45mm的中间坯，再经精轧、卷取得到厚度为3.00±0.25mm的热轧卷板，精轧开轧温度≤872℃+1000*(11*[Si]‑14*[Mn]+21*[Al])；精轧终轧温度≤820℃，卷取温度≤560℃；常化、酸连轧，得到厚度为0.500±0.005mm的冷硬卷，常化温度850～900℃；成品退火温度820～880℃，退火后经冷却、涂层和精整，得到无取向硅钢。

本发明涉及电机技术领域，具体涉及一种具有低应力结构的硅钢片、转子和电机。包括硅钢片、开设在硅钢片上的磁钢槽和嵌设在所述磁钢槽内的磁钢组件，所述磁钢组件包括多个磁钢组，所述磁钢组包括靠近转子边缘的一对小永磁体和靠近转子内侧的一对大永磁体，所述硅钢片在转子轭部沿周向分布有径向开槽，且所述径向开槽从硅钢片的中心向边缘延伸。其通过在转子轭部沿周向分设置从硅钢片的中心向边缘延伸的径向开槽，能降低大永磁体左右两侧铁芯刚度差距，从而有效降低隔磁桥处的应力，防止磁钢和铁芯产生形变而断裂。其无需改变电机转子外圆结构，在保证转矩输出的前提下，防止高速旋转时带来空气啸叫声。

本发明公开了一种低碳低硅钢铝质复合脱氧剂及其制备和使用方法，属于钢铁冶金技术领域。本发明为改善低碳低硅钢种可浇性差、夹杂降级率高的问题，提供了一种低碳低硅钢铝质复合脱氧剂，其包括：金属铝：50～60％；7Al2O3·12CaO预熔渣：10～20％，钝化CaO：10％～20％，Fe：10～20％，其余为微量杂质元素。本发明通过深入研究铝脱氧后钢中夹杂物的行为，提供了一种低碳低硅钢铝质复合脱氧剂，通过在转炉出钢过程加入该脱氧剂，能够有效降低钢中大型夹杂比例、对夹杂物改性，在不延长精炼时间的情况下降低夹杂物总量，改善目前此类钢种生产过程中存在的可浇性差，夹杂降级率高的问题。

本发明属于金属材料加工技术领域，具体涉及取向硅钢罩式炉高温退火低保温阶段二段式退火工艺，包括：将涂镁取向硅钢卷装入密闭的罩式炉中，并向罩式炉内通入氮气将炉内氧气充分排出；通电升温并将氮气转换为10m3/h氨分解气，接着点燃放散阀，将温度升至500‑600℃，恒温13h；500‑600℃低保温结束后检测内部气体露点是否小于0℃；本发明提供的取向硅钢罩式炉高温退火低保温阶段二段式退火工艺能够解决普通冷轧取向硅钢罩式炉高温退火热处理低保温阶段，钢卷在高温下不被水蒸汽氧化，消除钢带表面露金、发红、发黑、水印、色泽不均、导通缺陷，降低钢带铁损、提高磁感、降低生产成本。

采用取向分布函数分析了无取向电工钢不同再结晶退火温度下的织构变化及织构对磁感应强度和铁损的影响,并计算了无取向电工钢的磁晶各向异性能。结果表明,随着实验钢的再结晶退火温度升高,Goss织构和立方织构组分显著增强,而{111}面织构强度却减弱。较高的退火温度有利于减小织构因子,提高磁感应强度。磁晶各向异性能计算结果显示,随着再结晶退火温度升高,无取向电工钢板的磁晶各向异性能降低。 The recrystallization texture and the relationship of texture to magnetic induction intensity and core loss of a non-oriented electrical steel were investigated by orientation distribution function analysis. The magnetic anisotropy energy of the steel was calculated also. The results show that,the intensity of Goss texture and cubic texture increases,but the intensity of { 111} texture decreases with increasing recrystallization annealing temperatures of the steel. The higher annealing temperatu... 

一种硅钢厂调功器故障报警自动复位的方法，包括：通过人机界面对炼钢炉温度进行设定，并在炼钢过程中实时获取炼钢炉温度；将炼钢炉实时温度与设定温度进行对比，当炼钢炉实时温度低于设定温度时，启动调节器；调节器输出功率使电阻带加热，使炼钢炉实时温度达到设定温度；当调节器发生故障时，调节器将故障信号发送给后台服务器，后台服务器根据故障指令，按预设规则控制与调节器连接的继电器，控制继电器按压复位按钮，使调节器自动复位。本发明解决了现有技术中通过电气人员来通过复位消除故障状态，耽误时间长，容易产生废品的问题。