硅钢资料

本发明公开了一种取向硅钢实验室轧机二次冷轧方法，包括取样→制样→冷轧轧制规程制定→实验轧机二次冷轧。本发明所要解决的技术问题是提供一种取向硅钢实验室轧机二次冷轧方法，本发明提供的方法轧制出来的取向硅钢二次冷轧试样，对于开展后续研究提供了更加可靠的试样和条件。

【作者】 韩超； 代智肄； ...

取向硅钢利用析出物作为抑制剂,抑制初次再结晶晶粒的长大,抑制剂是取向硅钢发生二次再结晶的基本条件之一。文中通过低温板坯加热技术制备取向硅钢,采用透射电镜(TEM)观察并研究了高温退火阶段抑制剂的演化过程。结果表明,渗氮后形成的非晶态Si3N4析出物不稳定,在700～750℃退火升温阶段转化为(Al,Si)N;(Al,Si)N颗粒在800℃发生团聚,随后长大并粗化;(Al,Si)N是低温取向硅钢主要抑制剂,随退火温度的升高,(Al,Si)N抑制力大幅下降。 Precipitates as inhibitor are used to inhibit the grain growth of primary recrystallization in grain-oriented silicon steel,and inhibitor is one of the basic conditions for occurring of secondary recrystallization.The grain-oriented silicon steel was produced by low temperature slab heating and nitriding technique.The evolution of inhibitor was observed by transmission electron microscopy.The results show that Si3N4 particles are precipitated after nitriding,and Si3N4 particles are amorphous and... 

本发明涉及硅钢技术领域，尤其涉及一种硅钢连退炉辊除瘤方法及装置。包括连杆、手柄、磨削片、密封盖、端盖与套筒；磨削片垂直固接在连杆一端的外壁上，手柄固接在连杆的另一端，手柄与磨削片处于同一平面上；连杆套接在套筒内，连杆能沿套筒轴向移动，套筒固接在端盖上；硅钢连退炉辊下方的炉墙设有与连杆及磨削片相应的磨辊孔，端盖或密封盖固接在磨辊孔处。1)确定结瘤炉辊；2)确定结瘤在碳套辊上的位置；3)插入除瘤装置；4)磨削；5)抽出。本发明降低废品量，提高成材率；减少停炉处理结瘤时间，降低能耗，提高生产率；提高难磨瘤辊的修复率，降低炉辊成本。

本发明公开了一种含铝无取向硅钢中残余元素的控制方法。工艺流程包括KR脱硫‑转炉冶炼‑RH处理‑连铸。转炉控制合理的炉料结构，采用多渣吹炼，挡渣出钢。所用废钢中Ti、V、Nb等残余元素的质量分数之和≤0.005％，废钢和铁水的比例为0.2‑0.3。转炉吹炼终点炉渣成分中Ti、V、Nb等残余元素的氧化物含量之和为0.1‑0.5％，出钢后钢包顶渣厚度为50‑60mm；RH脱碳、脱氧、合金化后，净循环时间≤5min。通过本发明的实施，含铝无取向硅钢成品中Ti、V的含量≤0.002％，Nb含量≤0.001％，硅钢的磁性能显著提高。

本实用新型公开了一种基于取向电工钢用收卷组件及其固定结构，包括主体，所述主体的后侧中部固定安装有固定杆，所述固定杆的侧面活动安装有活动机构，所述活动机构包括活动块，活动区，弹簧，主动块，连接孔，连接杆，齿轮，卷筒，挡板。该种基于取向电工钢用收卷组件及其固定结构，活动块会带动活动区内部的主动块在其内部移动，可以通过连接杆带动齿轮进行转动，因齿轮侧面啮合连接有齿口，从而会顺着主体的侧面进行移动，当齿轮移动到主体的一角时，会带动活动区内部的弹簧收缩，弹簧可根据齿轮到主体中心的距离长短进行伸缩，物料会通过卷筒落到卷块的表面，从而可以对物料进行收卷，最后达到了便于收卷，降低物体损害的目的。

本实用新型公开了一种用于硅钢片自动叠片的机械手，包括底板与第一竖杆，所述底板上端一侧设置有第一竖杆，所述底板与第一竖杆固定连接，所述底板上端轴心处设置有垂直传动机构，本实用新型中在放置架的内部设置有重力传感器，并且该重力传感器通过程序设定，当上端物品的重力达到设定值时，这时重力传感器就会将警报灯的电源接通，这时警报灯就会进行工作，从而可以提醒工作人员堆码完成，本实用新型中在放置架的底端设置有垫脚，这样可以方便叉车将该放置架进行移动，本实用新型中通过在夹持机构内部靠近机械手的一侧设置有工业相机，这样可以使得机械手通过工业相机观察到传输带上方的工件，这样可以使得夹持的更加便捷。

采用双辊薄带连铸技术试制了3.98%Si-0.71%Al无取向硅钢铸带,研究了二次冷轧法对硅钢组织和磁性能的影响。结果表明:硅钢铸带显微组织为等轴晶组织,铸带再结晶较完全,常化对铸带显微组织影响较小。二次冷轧工艺和一次冷轧工艺下,最终退火后成品显微组织为等轴晶组织,二次冷轧法最终退火后的晶粒尺寸小于一次冷轧法。二次冷轧法能够提高成品磁性能. Effect of double cold rolling on magnetic properties and microstructure of 3.98%Si-0.71%Al non-oriented silicon Steel Sheets cast by twin-roll thin strip casting process were investigated.The results show that the structure of the thin strip is equiaxed crystal,the recrystallization is complete and normalizing has lesser effect on microstructure.Using both cold rolled and double cold rolled process,the microstructure is equiaxed grain after final annealing.The average grain size of annealed shee... 

本发明公开了一种取向硅钢实验室常化工艺方法，采用两段式常化工艺，可以模拟现场常化生产，为现场批量生产提供有效的工艺参考，缩短现场调试工艺次数和废品率、次品率，降低制造成本。

对应用动态加热进行短时温度退火的取向电工钢进行了二次再结晶研究。所进行研究的实验用取向电工钢是经过终冷轧和后续罩式退火后的一条工业化生产线生产的。研究结果表明,运用短时热处理条件可引起研究钢完全的异常晶粒长大。在实验室处理的材料的织构和金相组织与工业化生产的经过终退火而获得的相同的取向电工钢类似。但是,在实验室处理的取向电工钢的二次再结晶的矩阵中可观测到\"寄生\"晶粒。从磁性观点看,这些\"寄生\"晶粒含有不理想的{111}取向织构。 The present study was made to investigate secondary recrystallization in grain-oriented steels annealed at short time temperature exposures with application of dynamical heating.The investigated GO(Grain Oriented) steels for experiments were taken from one industrial line after final cold rolling reduction and subsequent box annealing.It was shown that application of short time heat treatment conditions could lead to complete abnormal grain growth in the investigated GO steel.The texture and mic... 

本发明涉及一种高性能取向硅钢冷轧工艺，具体涉及取向硅钢制造技术领域。本发明的冷轧工艺包括一次冷轧和二次冷轧，其中，取向硅钢热轧板厚度在2.0～3.0mm，一次冷轧轧制采用4或5道次轧制，轧至厚度0.60～0.62mm，轧制温度为100℃～105℃；二次冷轧轧制采用2道次，轧至厚度0.24～0.26mm，轧制温度为95℃～100℃。本发明通过对一次冷轧和二次冷轧中各道次的压下率、轧制张力、轧制速度、轧制温度进行优化设计，从而能够进一步优化织构，确保二次冷轧板高斯织构含量在0.8～1.5％，且轧制稳定性高，进而有效保证了所得取向硅钢的磁性能。

研究了硅钢铸坯再加热过程中夹杂物的析出行为。采用非水溶液电解提取+扫描电镜观察方法,观察了试样的显微组织,统计了夹杂物的尺寸、种类、数量、分布。结果表明,均热温度为1 523 K时,水淬试样的夹杂物尺寸绝大部分小于0.5μm,0.5～5.0μm的夹杂物数量很少,没有发现5.0μm以上的夹杂物。此外,均热时间为10、30、60、90、120、240 min时,对应试样中0.05～0.2μm的夹杂物数量分别为4.04×104、4.73×104、3.70×104、3.33×104、3.10×104、1.56×104个/mm3。绝大部分夹杂物以MnS、AlN、CuxS类为主,并以三类夹杂物中的两类复合或三类复合居多。三类复合夹杂物总量占每组试样夹杂物总量的90%或以上。随均热时间延长,典型的夹杂物组成会发生如下变化:MnS+AlN+CuxS MnS+AlN AlN。与此同时,MnS、AlN、CuxS三者复合比例从45.2%(均热10 min)降为9.7%(均热240 min)。 The methods of electrolysis extraction from nonaqueous solution and scanning electron microscope were adopted to study the precipitation behavior of non-metallic inclusions in Si steel slabs during reheating processes.The morphologies,chemical compositions,quantity and size distribution of non-metallic inclusions in these steel samples were analyzed.Results show that,when the soaking temperature is 1 523 K,almost all of the non-metallic inclusions are smaller than 0.5 μm,few are in the range of ...