硅钢资料

通过对湿H2气氛下,相同退火温度、不同退火时间的CGO硅钢初次再结晶样品进行金相组织观察,并进行了EBSD微观织构分析,研究了CGO硅钢初次再结晶过程中的组织及再结晶织构演变行为。结果表明,在湿H2气氛下,820℃保温,CGO硅钢初次再结晶过程约在120 s时完成。随着退火时间的延长,γ面上{111}<112>织构含量逐渐减少,{111}<110>织构先减少后增多,随着再结晶的完成,部分{111}<112>取向晶粒向高斯{110}<001>取向转化的同时,也向{111}<110>取向转化,高斯{110}<001>织构含量逐渐增多。高斯取向晶粒较多是由{111}<112>取向晶粒转化而来,同时也证明了CGO硅钢高斯取向晶粒的二次再结晶异常长大生长机制为择优形核。 Microstructure development and texture evolution of conventional grain oriented silicon steel,which were annealed at same annealing temperature and different annealing time under wet H2 atmosphere,were investigated through metallographic observation and electron backscattered diffraction analyzing.The results show that the primary recrystallization finishes in 120 s at 820 ℃ under wet H2 atmosphere.With the extending of annealing time,{111}<112> texture decreases,{111}<110> texture d... 

本实用新型提供了一种轴向磁通电机转子的硅钢盘，所述硅钢盘具有沿周向间隔排列的多组转子槽，相邻的两组转子槽之间界定了一硅钢块，每组转子槽的数量为两个，且相对设置于所述硅钢盘轴向的两侧，每组的两所述转子槽之间界定了一连接相邻两所述硅钢块的连接筋，多个所述硅钢块通过连接筋连接，并形成一整体的硅钢盘，相对现有技术独立成型多个硅钢块来说，不仅避免硅钢块丢失，还有效提升硅钢盘装配为转子盘的成型效率，以及保证各硅钢块在转子盘上的位置一致性，从而大幅增强转子盘的机械可靠性。

本发明公开了一种可替代高磁感取向硅钢常化退火的热处理方法。该方法包括对所述取向硅钢的铸坯依次进行热轧、酸洗和冷轧，省去了常化酸洗工序中的常化退火工艺。所述热轧工序包括加热、粗轧和精轧过程，所述精轧过程中，热轧板离开精轧机最后一个机架时的温度达到1000～1050℃；或者，所述酸洗工序后，对热轧板进行通电加热至1000～1050℃；然后，对热轧板采用短时通电加热控制冷却速度，通电加热2‑5s使热轧板的温度降至940～960℃。采用该热处理方法得到高磁感取向硅钢常化板等效织构，满足生产高磁感取向硅钢的织构组分条件，其简化了高磁感取向硅钢的制造工艺，降低了生产成本和能耗，提高了生产效率。

本发明提供了一种无取向电工钢，以质量百分比计，其成分包括C：0.0010～0.0050％，Si≤2.5％，Al≤0.01％，Mn≤0.80％，P≤0.10％，S≤0.0070％，N≤0.0030％，其余为Fe及不可避免的杂质。本发明还提供了一种无取向电工钢的制备方法。本发明提供的一种无取向电工钢，不添加偏析或稀土等贵重元素且磁性能好、成材率高，本发明提供的无取向电工钢制备方法，工艺流程简单、生产周期短、制取成本低，且无需热轧板常化。

本文中简要介绍了武汉钢铁有限公司采用薄板坯连铸连轧CSP(compact strip production, CSP)工艺生产中低牌号无取向硅钢的实践情况.CSP工艺生产的硅钢具有成品磁性均匀、板形好的优势，但是在利用该技术生产中低牌号无取向硅钢时，常存在成品板表面瓦楞状缺陷严重、连铸生产效率低等问题.通过优化炼钢成分、热轧等相关工艺，可消除热轧板厚度方向中心的粗大形变组织，从源头上避免了粗大{100}<011>纤维组织的出现，消除了瓦楞状缺陷；通过提升冶炼效率和控制钢中夹杂物总量，可优化隧道炉的加热温度与在炉时间，大幅度提升了连铸生产效率，实现了中低牌号无取向硅钢的批量稳定制造，使CSP产线成为中低牌号无取向硅钢热轧板原料的主要供给生产线.如何进一步提升钢水纯洁度、提高连铸生产效率、降低生产成本，以及挖掘该产线生产薄带钢的技术优点，是未来工作的重点. This paper briefly introduces the practice of producing medium and low grade non oriented silicon steel(NGO) with CSP(compact strip production, CSP)technology in Wuhan Iron and Steel Co., Ltd.. This technology has the inherent advantages of uniform magnetic properties and good shape for silicon steel finished strip. However, in the actual production process, there are serious corrugated defects on the surface of silicon steel finished strip, and production efficiency of continuous casting is low... 

运用EBSD和光学显微镜,研究了0.25%~0.45%Cu对无取向电工钢热轧板显微组织,成品板显微组织、织构和磁性能的影响。实验结果表明:卷取过程中Cu元素在热轧板表层的偏聚作用显著阻碍了热轧板表层再结晶晶粒长大,导致热轧板表层晶粒尺寸随着Cu含量增加而逐渐较小,但热轧板中间晶粒尺寸变化不大。同时发现Cu元素能够明显改善织构类型,使有利织构组分增加,不利织构组分减少,同时减弱织构强度。从实验结果可知0.35%Cu能够显著改善电工钢的磁性能,铁损P15/50最低达到4.1 W/kg,磁感B50最高值达到1.8 T。 Effects of high content Cu on microstructure of hot rolled plates and microstructure,texture and magnetic properties of annealed finish product plates of non-oriented electrical steel were examined by means of EBSD technique and optical microscope. The results show that surface segregation of Cu significantly hindered recrystallized grain growth of surface layer in hot rolled plate during the coiling,as a result,the surface grain sizes of the hot-rohed plates decrease with the increase of Cu con... 

利用本钢技术中心试验厂技术手段,并与北京钢铁研究院合作,试制了用作家电用电机、微电机、小电机或部分中型电机铁芯的冷轧无取向电工钢。试制钢硅含量小于0.5%,钢板表面平滑,公称厚度0.5mm,且厚度均匀偏差小,性能测定结果表明,产品的磁性能、力学性能满足其使用要求。 BX STEELTechnology Center pilot plant using technical means,and with Beijing Iron and Steel Research Institute,trial cold rolled non-oriented electrical steel that has been used as appliance motor core,micro motor core,small motor core,or part of the medium-sized motor core。Trial steel of silicon content is less than 0.5%,steel plate surface is smooth,the nominal thickness of 0.5mm,and the thickness deviation is small,performance measurement results show that the magnetic properties,mechanical p... 

本实用新型公开了一种变压器铁芯硅钢片板材滚切后打磨装置，包括机体、导向机构、隔板、前端打磨体和后端打磨体，所述导向机构设置在机体上，且所述导向机构导向若干料带的位移，所述导向机构之间设置有若干隔板，所述前端打磨体设置在料带传送方向上的前端，所述后端打磨体设置在料带传送方向上的后端，且所述前端打磨体、后端打磨体分别设置在两两相邻的料带之间；传送状态下的料带切割边缘相对于前端打磨体、后端打磨体打磨。在料带传动的同时，通过前端打磨体和后端打磨体的相对运动同时对两个料带的边缘进行打磨，结构简单，成本低，且能够提升料带外观质量。

实验室模拟薄板坯连铸连轧(TSCR)流程制造高磁感取向硅钢,借助电子背散射衍射(EBSD)技术对不同Sn含量的热轧板织构进行了研究。研究结果表明:不同Sn含量热轧板表层及次表层均为高斯织构、铜型织构及黄铜织构的混合织构,中心层为{100}面织构;Sn含量为0.1%时,热轧板表层及次表层高斯织构组分最多,取向密度最大,成品磁感最高,达到1.875 T。 Texture of grain oriented silicon steel hot rolled by thin slab casting and rolling process(TSCR) in laboratory with different Sn contents was analyzed by electron back-scattered diffraction(EBSD).The results show that the hot rolled slabs with different Sn contents have the same texture,i.e.,Goss,Copper and Brass.Specifically,the texture of core layer is {100};While the hot rolled slab with 0.10% Sn,the surface layer and subsurface layer have a sharpness Goss texture and the finished products h... 

研究了退火温度对3.1%Si无取向硅钢组织和磁性能的影响规律。结果表明:退火温度从940℃提高至1 000℃,平均晶粒尺寸由98μm增加到145μm,铁损P_1.5/50从2.576 W/kg降低至2.408W/kg。随着退火温度的升高,γ不利织构组分强度逐渐降低,{111}〈112〉织构组分强度降低约16%,磁感B₅₀逐渐升高,磁性能水平提高。 The effects of annealing temperature on microstructure and texture and magnetic properties of 3.1%Si non-oriented silicon steel were investigated in this paper.The results showed that,when the annealing temperature increased from 940℃ to 1 000℃,the average grain size of metallographic structure increased from 98μm to 145μm,the iron loss value P_1.5/50 decreased from2.576 W/kg to 2.408 W/kg.And as the annealing temperature increased,the strength of the unfavorable texture componentγgrad... 

一种基于大数据分析技术的电工钢用户选材询单推荐方法，于终端计算机内、以可与终端计算机各数据库进行信息交互的形式、设置一计算模块；经此计算模块完成依次的基于各数据库的有效信息的采集、用户询单选材推荐方案模型的设置、基于有效信息及推荐方案模型完成推荐牌号的生成，根据设定的评估模型对生成的推荐牌号及信息评估运算的运行，据此建立对用户的选材询单推荐。本发明的一种基于大数据分析技术的电工钢用户选材询单推荐方法，基于L4计算机系统开发出的计算模块及相应的可与计算模块进行信息交互的用户界面完成，形成可根据不同用户需求对应的不同评价体系，完成与不同用户需求适配的方案推荐。

本发明提供一种在同一卷材内得到稳定的磁特性的方向性电磁钢板的制造方法。上述方向性电磁钢板的制造方法，包括如下步骤：将具有规定的成分组成的钢坯热轧而制成热轧板，将上述热轧板退火而制成热轧板退火板，对上述热轧板退火板实施1次或隔着中间退火的2次以上的冷轧而制成最终板厚的冷轧板，对上述冷轧板实施一次再结晶退火和二次再结晶退火；上述冷轧包括至少1次的压下率为80％以上且轧制速度为设定值R0(mpm)期间的钢板温度T0(℃)与轧制速度为0.5×R0(mpm)以下期间的钢板温度T1(℃)满足式(1)的冷轧。