本实用新型涉及风电磁钢盒技术领域，且公开了一种风电磁钢盒高精度加工模具，包括上模和下模，上模位于下模的上方，下模的前侧通过多个螺栓螺纹连接有安装板，安装板的前侧固定设有两个对称设置的固定板，两个固定板之间固定设有固定杆，固定杆的杆壁两端均通过第一转动轴承转动连接有套筒，套筒的两侧均开设有环形槽，两个环形槽的槽壁内部均设有限位机构，两个固定板相靠近一侧均开设有四个呈四角对称设置的插孔，套筒的两端均通过套环固定设有环形板，环形板的两侧均开设有滑槽，两个滑槽之间设有推动机构。本实用新型能够消除风电磁钢盒加工过程中人工将板件送至模具之间所带来的的危险。

对取向硅钢熔融态钢液进行处理,对比研究了不同脉冲参数的作用效果。结果表明,电脉冲对钢锭晶粒组织具有明显的细化作用,凝固组织等轴晶比例大幅上升。在脉冲电容、频率、处理时间和电压中,影响等轴晶比例的最显著性因素为脉冲频率;最优正交实验参数为:电容1 200μF,脉冲频率1 Hz,处理时间5 s,脉冲电压800 V;随着输入能量的增大,等轴晶率先增大后减小,脉冲输入能量为某值时,等轴晶率最大,通过经典形核理论和热力学对这一现象进行了解释。 Research on the influence of the electric pulse on the solidification structure of oriented silicon steel was preformed.Electric pulses in different parameters were applied to molten steel and results were compared.The result shows that solidification structure of oriented silicon steel can be improved by the electric pulse,and the equiaxed crystal ratio increases obviously.Among the four parameter factors of electric capacity,frequency,applied time and voltage,the most effective factor is frequ... 

本发明公开了一种基于硅钢服役特性的立体卷铁心单框损耗测量方法及系统，根据硅钢片在立体卷铁心中的服役特性，获得测量铁心单框所需的非正弦励磁电压波形，通过所述立体卷铁心的心柱绕组电压和单框绕组电压之间的关系，确定所述被测立体卷铁心单框所需的电压有效值，再通过计算机、数据采集卡D/A转换器、功率放大器、隔离变压器和示波器，直接在所述立体卷铁心单框上加载励磁电压，利用功率表测量立体卷铁心单框损耗。本发明利用硅钢的服役特性，获得测量立体卷铁心单框所需的非正弦励磁电压波形和电压有效值，再将励磁电压直接加载到被测立体卷铁心单框，测量立体卷单框铁心损耗。

根据本发明的一个实施例的无取向电工钢板，以重量％计，所述钢板包含Si：2.2至4.5％、Mn：0.5％以下且0％除外、Al：0.001至0.5％、Sn：0.07至0.25％和N：0.0010至0.0090％，余量包含Fe和不可避免的杂质。所述钢板包含从钢板表面向内存在的表层部和存在于表层部里面的中心部，中心部包含0.005重量％以下的N，所述表层部比中心部更包含0.001重量％以上的N，表层部的平均晶粒粒径为60μm以下，中心部的平均晶粒为70至300μm。

本发明涉及一种硅钢热处理方法，尤其涉及一种取向硅钢极薄带绝缘层涂覆方法，包括以下步骤：(1)接入普碳钢引带的准备工作；(2)各炉段张力的设定工作；(3)炉内气氛及温度的调节工作；(4)绝缘层厚度及厚度的检测工作；(5)极薄带涂层涂覆及烘干工作；(6)极薄带表面绝缘涂层及磁性能检测工作。本发明采用与极薄带厚度相当的普碳钢作为引带，通过引带测试产线张力和绝缘层涂覆的厚度，一方面可通过普碳钢薄带的运行加速炉内温度和气氛的稳定性，节约炉内稳定时间；另一方面可通过成本较低的普碳钢检测炉内张力和温度的设定，及绝缘涂层的涂覆效果，避免开始采用硅钢带出现断带，及涂覆不合格后造成产品报废带来的成本升高。

本发明提供能够制造磁特性与被膜密合性优异的电磁钢板的新颖并且得以改良的电磁钢板的制造方法。一种电磁钢板的制造方法，其特征在于，其包括以下工序：使电磁钢板与溶液相接触，所述电磁钢板以质量％计含有C：超过0％且0.10％以下、Si：2.5％以上且4.5％以下、Mn：0.01％以上且5.0％以下、S、Se及Te中的1种或2种以上的合计：超过0％且0.050％以下、酸可溶性Al：超过0％且5.0％以下、N：超过0％且0.015％以下、P：超过0％且1.0％以下、剩余部分由Fe及杂质构成，其中，上述溶液含有Cu、Hg、Ag、Pb、Cd、Co、Zn及Ni中的1种或2种以上，各元素的浓度合计为0.00001％以上且1.0000％以下。

以轻烧氧化镁粉为原料,经消化、碳化制得重镁水,在热解反应前采用络合剂对重镁水中的杂质钙、铁进行络合掩蔽,再经热解得到碱式碳酸镁,碱式碳酸镁经煅烧可制得钙、铁杂质含量较低的氧化镁。在重镁水络合除杂过程中,考察了络合剂三乙醇胺、柠檬酸、草酸单独和复合使用的除铁、除钙效果。以三乙醇胺为络合剂时,在200 mL重镁水中加10 mL三乙醇胺(1∶1),氧化镁产品中w(氧化镁)=99.3%、w(氧化钙)=0.31%、w(氧化铁)=0.042%;使用草酸和柠檬酸作为复合络合剂时,在200 mL重镁水中加入1.0 g柠檬酸和2.0 g草酸,氧化镁产品中w(氧化镁)=98.2%、w(氧化钙)=0.24%、w(氧化铁)=0.030%。 Light-burned magnesia as a raw material was hydrated and carbonated to obtain magnesium bicarbonate liquor.Before the pyrolyzing of magnesium bicarbonate liquor,complexants were used to cover Fe and Ca impurities.Then the treated liquid was pyrolyzed to obtain basic magnesium carbonate which was calcined to magnesium oxide with low calcium and iron content.During the complexing purification of magnesium bicarbonate liquor,the Fe and Ca removing effects of single or compound complexing agents,suc... 

对低温加热工艺生产的以AlN为主抑制剂的高磁感取向硅钢高温退火过程进行中断实验,借助电子背散射衍射技术对高温退火过程中高斯晶粒的演变进行了研究.在升温过程中高斯晶粒平均尺寸先减小再增大.800℃时取向分布函数图出现高斯织构组分,但强度很弱,高斯晶粒偏离角在10°以上;900℃时高斯晶粒平均生长速率超过其他晶粒;950~1000℃时高斯晶粒异常长大,偏离角3°~6°;在1000℃之前高斯取向晶粒相比于其他晶粒没有尺寸优势. The high-temperature annealing process of high permeability grain-oriented silicon steel with AlN as an inhibitor was studied by interrupting test.The evolution of Goss texture in this process was analyzed by electron back-scattered diffraction.It is found that the Goss grain size first decreases and then increases with the rise of temperature.Goss texture appears in the orientation distribution function at 800 ℃,but the intensity is very weak and the deviation angle is more than 10°.The average... 

本发明公开了一种改善高牌号无取向硅钢表面色差缺陷的方法，属于冷轧卷板表面质量改进技术领域。所述方法为：将连铸坯依次进行热轧、常化、酸洗、单机架轧制和连续退火工序，其中按重量百分数计，所述的连铸坯含有如下成分：C＜0.003%、Si1.6~2.0%、Mn0.35~0.65%、Al0.35~0.65%、P＜0.02%、S＜0.0025%、余量为Fe和其他不可避免的杂质元素，所有成分合计100%；其中热轧工序的卷取温度为620~640℃。本发明所述方法能够降低带钢表面氧化铁厚度并改变带钢表面氧化铁结构，改善高牌号无取向硅钢表面色差缺陷。

组织和织构是影响无取向硅钢性能的重要因素。为改善产品性能，研究了冷轧压下率（71.7%～87.0%）对高牌号无取向硅钢组织、织构、磁性能和力学性能的影响。结果表明，随冷轧压下率的增加，退火晶粒平均尺寸先减小后增大；高斯和立方织构强度减弱，γ纤维织构增强，α纤维织构转变为较强的α^*（{h, 1, 1}〈1/h, 1, 2〉）织构，并随冷轧压下率的增加而增强，同时其峰值逐渐向{111}面移动；工频铁损P_1.5/50、高频铁损P_1.0/400和磁极化强度J₅₀₀₀同时降低，屈服强度变化不大，表面硬度逐渐增加。当冷轧压下率由84.7%增至87.0%、厚度减至0.30 mm时，高频铁损降幅是工频铁损的11倍，表面硬度增幅变大。以上研究成果对硅钢减薄后织构及组织的优化提供了很好的指导。 Microstructure and texture are critical factors on non-oriented silicon steel properties. In order to improve product properties, this paper studied the effect of cold rolling reduction rate（71.7%-87.0%） on microstructure, texture, magnetic properties and mechanical properties of high-grade non-oriented silicon steel. The results show that with the increase of cold rolling reduction rate, the average size of annealing grain decreases first and then increases. The intensity of Goss and λ fiber te... 

针对宝钢集团、日本新日铁住金和JFE公司公开的相关专利等资料,总结了国内外高强度无取向电工钢的研究进展,分析了不同电工钢的化学成分、生产工艺及产品性能,指出固溶强化、细晶强化、析出强化、位错强化都有可能被用来提高无取向电工钢的强度,并阐述了四种强化方式的优缺点;指出在高强度无取向电工钢的研发过程中,需根据其具体用途确定目标性能,再采用合适的强化手段,最终实现力学性能、磁性能和生产性能之间的平衡。 The research progress of high strength non-oriented electrical steels at home and abroad is summarized according to related patents brought into the public by Baosteel,Nippon Steel & Sumitomo Metal corporation and JFE corporation.The characteristics of chemical composition,production technology and properties of products in the patents are analyzed.Each of solution strengthening method,fine-grain strengthening method, precipitation strengthening method or dislocations strengthening method ma...