电动汽车电机在高速旋转时承受离心力和电磁力的作用,在进行电机转子设计时,既要考虑电磁性能,还要考虑机械性能。对电机转子受力情况进行了综述,分析了转子用电工钢疲劳性能参数的重要性,详细阐述了试样抛光、表面处理、试样的对中和安装对测试结果的影响。 The motor of electric vehicle bears big force for high speed rotors,mainly including centrifugal and electromagnetic forces.The magnetic and mechanical aspects of the electrical steel are crucial to machine design.In this paper,the forces applied on the motor were summarized and importance of fatigue properties was analyzed.The influence of specimen polish,surface treatment,alignment and installation on fatigue testing result were represented in detail. 

通过后天抑制剂获得法制备了取向硅钢,对渗氮前后和高温退火升温阶段析出物的析出和转化规律进行了研究。研究结果表明,渗氮前脱碳退火态基体中存在少量的粗大AlN颗粒和细小AlN颗粒,渗氮处理后新析出大量的Si3N4析出物,高温退火升温阶段Si3N4将转化为(Al,Si)N,随着温度的继续升高(Al,Si)N颗粒将发生粗化,(Al,Si)N是后天抑制剂获得法制备取向硅钢的主要抑制剂。 Grain-oriented silicon steels were produced by acquired inhibitor method.The rule of precipitate transformation was studied after nitriding treatment and high-temperature finishing annealing.The results show that a small amount of large AlN and fine AlN are found in matrix before nitriding treatment,and a large amount of Si3N4 is precipitated in matrix after nitriding treatment.During the temperature rising period of high-temperature finishing annealing,Si3N4 would transform into(Al,Si)N,and(Al,... 

本发明公开了一种宽频率低铁损变频电机用无取向电工钢及制造方法，属于无取向电工钢领域。针对现有无取向钢在较宽频率范围内电磁性较差的问题，本发明提供一种宽频率低铁损变频电机用无取向电工钢，包括如下重量百分比的各组分：Si：2.80％～3.50％；Als：0.20％～0.60％；Mn：0.20％～0.60％；P：0.01％～0.20％；C：≤0.005％；S：≤0.02％；N：≤0.02％；Ti：≤0.005％；其余为铁和不可避免的杂质；其中C、S、N和Ti的重量百分比满足下式：C％+S％+N％+Ti％≤0.009％。通过控制合金元素的含量达到电工钢电阻率增加、磁滞伸缩减小，涡流和磁滞损耗均降低的目的。通过本发明提供的制造方法在正火过程中选用低温工艺，改善随着合金元素量的增加金属强度增加、塑性降低、冷加工性能降低的问题，使其最终在较宽频率范围内电磁性能优异。

该电磁钢板为母材钢板的其中一个或两个表面中的至少一部分被具有接合能力的绝缘被膜覆盖的电磁钢板，所述绝缘被膜的25～100℃的温度范围的对数衰减率为0.3以下。

本发明提供了一种无取向硅钢RH顶枪喷粉脱硫工艺，RH脱碳结束测温定氧，立即加入铝粒脱氧合金化、之后立即依次连续加入合金进行成分调整，合金加完后立即开始顶枪喷粉；加入铝粒的量＝铝粒理论加入量+0.2‑0.4kg/t钢；喷粉时，控制喷粉速度与钢液循环流量相匹配；本发明从真空条件下脱硫热力学和动力学角度出发对具有顶枪喷粉功能的RH脱硫工艺进行改进，提高脱硫率。

本文研究了丙烯酸树脂含量对以Al(H2PO4)3为基料的无铬无取向硅钢绝缘涂层各项性能的影响.用盐雾实验、动电位极化及交流阻抗等试验手段研究了不同树脂含量对硅钢绝缘涂层的耐盐雾性能和电化学行为的影响,同时采用SEM对涂层的表面形貌和附着性进行研究.结果表明,树脂含量为19.9~29.4%时,涂层的耐蚀性和附着性最好;树脂含量过多时,涂层的耐蚀性和附着性均较差. This paper studies the influence of acrylic resin on the performance of insulating coating of aluminum dihydrogen phosphate on chromium-free non-oriented silicon steel.Salt spray experiment,potentiodynamic polarization and electrochemical impedance spectroscopy were used to study the influence of acrylic resin content on the salt spray resistance and electrochemical behavior of the insulation coating of nonoriented silicon steel.The surface morphologys and adhesion of coating were tested by SEM.... 

采用双辊薄带连铸技术试制了3.98%Si-0.71%Al无取向硅钢铸带,研究了二次冷轧法对硅钢组织和磁性能的影响。结果表明:硅钢铸带显微组织为等轴晶组织,铸带再结晶较完全,常化对铸带显微组织影响较小。二次冷轧工艺和一次冷轧工艺下,最终退火后成品显微组织为等轴晶组织,二次冷轧法最终退火后的晶粒尺寸小于一次冷轧法。二次冷轧法能够提高成品磁性能. Effect of double cold rolling on magnetic properties and microstructure of 3.98%Si-0.71%Al non-oriented silicon Steel Sheets cast by twin-roll thin strip casting process were investigated.The results show that the structure of the thin strip is equiaxed crystal,the recrystallization is complete and normalizing has lesser effect on microstructure.Using both cold rolled and double cold rolled process,the microstructure is equiaxed grain after final annealing.The average grain size of annealed shee... 

本发明公开了一种超薄取向硅钢用的半有机绝缘涂料。该半有机绝缘涂料，按质量百分比计，包括以下组分：10～25％磷酸盐，1～10％含有环氧基的硅烷耦合剂，0.2～2.0％有机硅烷，1～10％铬酐，1.5～6％二氧化硅粒子，0.3～5％碱，余量为水；其中二氧化硅粒子的粒径为100～300nm。该半有机绝缘涂料应用于超薄取向硅钢表面时，既提高了涂层与基体的附着性，又保证了涂层的绝缘性和耐热性，涂层附着性为A级，叠片系数大于0.96，可耐900℃高温，并且涂层较薄(小于1μm)时，钢板的绝缘电阻大于30Ω·cm2/片，绝缘性能优异，可满足超薄取向硅钢的应用需求。

本发明涉及一种百吨级超低氮硅钢大钢锭的制造方法，涉及硅钢的制造技术领域，包括以下步骤：取优质废钢、生铁配料作为炉料，电炉冶炼，电炉冶炼，LF精炼、两次VD脱气，精炼包真空吹氩直注的工艺方法。其优点在于，本发明提供的百吨级超低氮硅钢大钢锭的制造方法，采用本方法制造的百吨级大型超低氮硅钢钢锭，成分全部满足规范要求，其中氮含量控制在25ppm以下，氧含量控制在10ppm以下，氢含量控制在0.7ppm以下，硫含量控制0.002％以下，磷含量控制0.006％以下，铝含量控制0.020％以下。

本发明提供一种在同一卷材内得到稳定的磁特性的方向性电磁钢板的制造方法。上述方向性电磁钢板的制造方法，包括如下步骤：将具有规定的成分组成的钢坯热轧而制成热轧板，将上述热轧板退火而制成热轧板退火板，对上述热轧板退火板实施1次或隔着中间退火的2次以上的冷轧而制成最终板厚的冷轧板，对上述冷轧板实施一次再结晶退火和二次再结晶退火；上述冷轧包括至少1次的压下率为80％以上且轧制速度为设定值R0(mpm)期间的钢板温度T0(℃)与轧制速度为0.5×R0(mpm)以下期间的钢板温度T1(℃)满足式(1)的冷轧。

本发明是关于一种薄规格无取向硅钢35BW440，该无取向硅钢35BW440包括以下质量百分比的元素：C：≤0.003％，Si：0.8％‑2.0％，Mn：0.4％‑1.2％，P：≤0.015％，S：≤0.003％，Als：0.25％‑0.6％，N：≤0.003％，Sb：0.04％‑0.1％，O：≤0.0025％，其余为Fe及不可避免的杂质。在没有电磁搅拌设备增加无取向硅钢磁感应强度的前提下，通过加入Sb元素，增加对电磁性能有利的{110}和{100}织构组分，提高电磁性能，采用二次冷轧及中间连续退火的工艺，提高无取向硅钢的表面质量。

本发明公开了一种切口耐蚀性良好的无取向硅钢及其生产方法，属于电工钢生产技术领域。本发明的无取向硅钢包括以下质量百分比的元素：Si：0.2～2.7％，Mn：0.15～1.0％、Als：0.5～1.0％，Cr：0.1～0.3％；Ni:0.2～0.5％，P：≤0.01％，其余为Fe及不可避免的杂质。其生产工艺为：铁水预处理、转炉炼钢、真空处理、连铸、加热、热轧、酸洗、冷轧、退火处理和涂覆绝缘层。本发明通过合理的成分配比以及相匹配的生产工艺进行生产，最终得到了切口耐蚀性优良的低铁损、高磁感的无取向硅钢，从而能够有效满足电工钢的使用需求。