利用场发射电镜及能谱仪研究了取向电工钢薄、厚板坯铸锭中不同区域的析出相差异,确定了MnS、AlN及Fe3C的析出顺序和形貌特征。结果表明AlN以先析出的MnS为形核核心,形成粗大微米级的复合析出相。针状Fe3C既可以在复合析出相表面形成也可以在基体中单独出现,主要受冷却速度的影响。在1250℃保温1～2 h,AlN、Fe3C均可完全回溶,但部分MnS仍不回溶。MnS尺寸随着保温时间延长而增大。导致热轧板中沿轧向分布的粗大MnS,减弱了粒子钉扎力。 Precipitates in thin and thick slabs of electrical silicon steel were investigated by means of field emission SEM and EDS analysis.The precipitation sequence and the morphology of MnS,AlN and Fe3C particles were identified.AlN particles are observed to be nucleated on surface of MnS forming micron-meter-sized complex particles.Acicular Fe3C can precipitate on surface of the complex MnS/AlN particles or directly from matrix depending on cooling rate of the slabs.After holding at 1250 ℃ for 1-2 h,... 

本实用新型公开了一种带缓冲保护装置的硅钢片纵剪线，包括工作台，工作台的顶部外壁设置有放料辊，工作台靠近放料辊的一侧设置有牵引辊，工作台靠近牵引辊的一侧设置有整平机构，工作台的内部设置有第一缓冲坑，第一缓冲坑的顶部设置有导料辊，第一缓冲坑的内部设置有第三转轴，第三转轴的外壁传动连接有皮带，皮带的内壁传动连接有第二转轴，皮带的外壁传动连接有第一转轴，第三转轴的外壁固定安装有转筒，转筒的外壁设置有伸缩杆，伸缩杆的外壁套接有弹簧，伸缩杆的底部设置有滚珠，通过设置的第一缓冲坑与第二缓冲坑结构，可防止硅钢片在进入第一缓冲坑与第二缓冲坑时弯曲程度过大导致的断裂，且双重的缓冲装置更有利于对硅钢片的保护。

考虑剪应变对微孔洞损伤演化的影响,对GTN损伤模型的损伤演化机制进行修正,建立了适用于不同应力三轴度水平的损伤模型。结合隐式应力更新算法和显式有限元计算,采用VUMAT子程序实现了修正GTN模型在有限元软件ABAQUS中的数值计算。通过模拟纯剪切和剪切-拉伸两组试样的损伤演化和断裂行为,验证了修正GTN模型在不同应力三轴度承载条件下的有效性。运用修正GTN损伤模型模拟含边部缺口的带钢在轧制过程中裂纹的萌生和扩展行为,模拟结果与实验相一致,表明该模型可有效地用于带钢缺陷在轧制过程中扩展行为的分析和预测。模拟和实验结果表明,带钢边部缺口在轧制过程中,缺口前沿和后沿均会萌生裂纹,且后沿裂纹扩展更为明显。 Considering the effect of shear strain of micro-void on damage evolution, a modified GTN model applicable to various stress triaxiality conditions is proposed by modifying the damage evolution mechanism of the GTN damage model. The modified model is implemented in commercial finite element software ABAQUS by combining the implicit stress update method with an explicit finite element solving algorithm and through the user-defined material subroutine VUMAT. The damage evolution and the failure pro... 

本发明公开了一种低铁损高磁导率无取向电工钢及其生产方法，所述生产方法包括以下步骤：钢水连续浇铸成板坯，板坯经加热炉加热，再经热轧得到热轧板，然后经空冷和水冷后在500～650℃进行卷取；热轧板经常化处理、盐酸酸洗；酸洗后在可逆轧机上进行冷轧；最后经成品退火，退火温度为840～900℃，加热时间为240～500s；然后以不超过3℃/s的冷却速度冷却至500℃以下；涂覆绝缘涂层、固化，后经二次退火，即可得到低铁损高磁导率无取向电工钢，其磁性能满足P1.5/50≤3.50W/kg，μ1.5≥3800Gs/Oe，B5000≥1.76T的要求。

【作者】 姚昌国； ...

【作者】 陶永根； ...

本实用新型公开了一种用于硅钢板带加工的整平装置，包括底座，所述底座的上表面固定设有下安装座，所述下安装座上设有下整平机构，所述底座的上表面固定连接有门型安装架，所述门型安装架的顶部贯穿设有螺杆，所述螺杆的底面设有上安装座，所述上安装座的正面通过轴承座转动连接有第三转轴，所述第三转轴的外表面固定连接有调向齿轮，所述上安装座上设有上整平机构。本实用新型通过设置通过设置多组上整平辊和下整平辊，改善该装置的整平效果，且通过转动齿轮与调向齿轮的设置，使该装置的多个上整平辊同步转动，且相邻两个整平辊之间的间隙可以设置的较小，使该装置结构紧凑，提高空间利用率。

【摘要】 <正>编号:2012016获奖等级:特等完成单位:...

研究二次冷轧压下率对于硅的质量分数为3.0%的无取向硅钢组织结构和磁性能的影响。结果表明:当第二次冷轧压下率从0变化至16.7%时,铁损逐渐增加,磁感逐渐降低。当第二次冷轧压下率大于16.7%时,随压下率的增加,铁损逐渐减小,磁感逐渐增加。当第二次冷轧压下率大于38%时,二次冷轧法所能获得的磁性能明显优于一次冷轧法。 Effect of double cold reduction on magnetic,microstructure and texture of 3.0% Si non-oriented silicon steel sheets was investigated.The results show that the iron loss increases and magnetic induction reduces as the percentage redcution in secondary cold rolling changes from 0 to 16.7%.The core loss can be reduced remarkably,and magnetic induction can get a little benefit if the percentage redcution in double cold reduction is higher 16.7%.In case of higher than 38% of the percentage redcution ... 

以试验室模拟CSP工艺生产的Fe-3Si热轧钢带为研究对象,采用正交试验及方差分析的方法,研究了取向硅钢初次再结晶退火工艺对高温退火后获得锋锐的高斯织构的影响。结果表明:取向硅钢两段式初次再结晶脱碳退火工艺参数加热段保温时间及加热温度是高温退火后获得锋锐高斯织构的主要影响因素,其可信度分别在90%和85%以上;在本试验条件下,通过正交试验获得的最佳退火工艺为:冷硬板经600℃保温3 min和850℃保温6 min。 Fe-3Si hot rolled strip was produced by simulating CSP technology in the laboratory.Orthogonal experiment and analysis of variance were carried out to investigate the influence of primary recrystallization on the sharp Goss texture of the oriented silicon steel.The results show that holding time of the heating section and the heating temperature for a sharp Goss texture of the samples annealed has important implications in this experiment conditions,the two-step decarburization annealing process... 

通过对湿H2气氛下,相同退火温度、不同退火时间的CGO硅钢初次再结晶样品进行金相组织观察,并进行了EBSD微观织构分析,研究了CGO硅钢初次再结晶过程中的组织及再结晶织构演变行为。结果表明,在湿H2气氛下,820℃保温,CGO硅钢初次再结晶过程约在120 s时完成。随着退火时间的延长,γ面上{111}<112>织构含量逐渐减少,{111}<110>织构先减少后增多,随着再结晶的完成,部分{111}<112>取向晶粒向高斯{110}<001>取向转化的同时,也向{111}<110>取向转化,高斯{110}<001>织构含量逐渐增多。高斯取向晶粒较多是由{111}<112>取向晶粒转化而来,同时也证明了CGO硅钢高斯取向晶粒的二次再结晶异常长大生长机制为择优形核。 Microstructure development and texture evolution of conventional grain oriented silicon steel,which were annealed at same annealing temperature and different annealing time under wet H2 atmosphere,were investigated through metallographic observation and electron backscattered diffraction analyzing.The results show that the primary recrystallization finishes in 120 s at 820 ℃ under wet H2 atmosphere.With the extending of annealing time,{111}<112> texture decreases,{111}<110> texture d... 

本发明涉及变压器硅钢片冲裁加工技术领域，具体涉及一种变压器硅钢片制造成型加工机械及加工方法，包括垫板、冲裁装置和进料装置，所述的垫板上安装有冲裁装置，冲裁装置上安装有进料装置；本发明可以解决变压器硅钢片在冲裁成型时存在的以下难题：一、在通过冲裁设备对变压器硅钢片进行冲裁作业时，由于变压器硅钢片大多没有进行稳定的定位作业，使得变压器硅钢片冲裁时产生偏差，降低了变压器硅钢片的冲裁质量，若使用定位机构进行定位处理，还会额外增加操作时间，降低了加工效率；二、需要人工进行送料作业，由于人工送料的间距难以控制，导致变压器硅钢片的冲裁位置发生偏差，造成变压器硅钢片的浪费。