针对传统工艺生产硅钢周期长、能耗大等缺点,采用双辊连铸工艺制备3%Si无取向硅钢连铸薄带,利用MEM,SEM和TEM观察了铸带的组织、织构及析出物,同时对比了Al的质量分数为0.6%和0.9%的连铸薄带在组织、织构及析出物特征方面的异同.结果表明:双辊连铸工艺生产的3%Si无取向硅钢铸带的组织为均匀等轴晶粒,平均晶粒尺寸约为300μm;织构组成随Al质量分数的不同具有明显差别,Al质量分数为0.9%的铸带中{100}织构强度是随机织构的7倍;铸带中的析出物为AlN和MnS,最大尺寸分别为500和50 nm左右. Given the lengthy production cycle,high energy consumption,and other shortcomings of the traditional process for producing silicon steel,a twin-roll casting process was used to produce 3%Si non-oriented silicon steel casting strips. MEM,SEM,and TEM were used to compare micro-structure,texture,and precipitate characteristics of a casting strip containing 0.6%Al with another containing 0.9%Al.The structure of 3%Si non-oriented silicon steel produced by the twin-roll casting process was a uniform i... 

本发明涉及变压器的技术领域，特别是涉及一种应用电工钢的变压器，其通过设置扇叶与冷凝盘管，通过冷却液与风冷共同对电工钢铁芯进行降温，避免电工钢铁芯工作过热导致电工钢铁芯损坏，提高使用稳定性；包括变压器箱体、两组固定支撑腿、电工钢铁芯、固定卡块、风机支架、风机、扇叶转轴、扇叶、冷却箱体、循环泵、冷却管、冷凝盘管、冷风机支架和冷风机，所述变压器箱体内部设置有空腔，所述变压器箱体右端连通设置有散热口，两组所述固定支撑腿对称固定安装在变压器箱体内部，所述固定支撑腿内端设置有紧固卡槽，所述电工钢铁芯左右两端对称固定安装有两组固定卡块，所述固定卡块固定卡装在固定支撑腿紧固卡槽中。

热卷箱位于热连轧带钢生产线粗轧与精轧机之间,是热连轧生产中比较理想的中间保温设备。由于取向硅钢变形温度区间较窄,在生产中易出现边裂现象,同时中间坯的边部温度难于得到保证,因此一般不采用热卷箱设备生产,限制了传统热连轧生产线产品开发的品种。通过合理优化热卷箱控制工艺参数,解决了某厂传统热连轧生产线用热卷箱生产取向硅钢的边部质量问题,成功地生产出取向硅钢带。 The hot coil-box is an ideal heat retaining apparatus for hot rolling,lined between roughing mill and finishing mill. But oriented silicon steel has a narrow deformation temperature range,so that the edge crack easily occurs and it is difficult to insure the temperature of the intermediate blank. Therefore,the hot coil-box is rarely used in producing oriented silicon steel,which restricts the product development of the traditional hot rolling line. The article reasonable optimized process parame... 

针对本钢薄板坯铸机在生产无取向电工硅钢的过程中存在的铸坯拉断、中包增碳、增氮等问题,进行了连铸工艺优化。通过采用新型无碳中间包覆盖剂、环保中间包干式料及专用结晶器保护渣后,降低了铸坯增碳量;通过控制钢包到中间包的增氮环节,降低钢水增氮;适当增大二冷水量,控制钢水过热度,防止铸坯拉断等生产事故的发生。改进工艺后,精炼后到成品铸坯的平均增碳量能控制在10×10-6以内,平均增氮量能控制在4×10-6以内。 The technology optimization has been adopted for preventing nitrogen increasing and carbon increasing in Benxi thin slab producing non-oriented silicon steel.Measures accordingly were adopted and satisfactory results were achieved. 

一种增大压下率的电工钢冷轧装置及冷轧方法，属于电工钢冷轧技术领域，该电工钢冷轧装置，包括单机架可逆轧机，单机架可逆轧机的两侧均设置有电磁感应加热装置和氮气风冷装置，氮气风冷装置靠近单机架可逆轧机的轧制进口或入口设置，本发明的有益效果是，本发明通过在单机架可逆轧机两侧增设电磁感应加热装置和氮气风冷装置，对每道次轧制过程中可在线调节电磁感应加热温度，实现了边去应力退火边轧制，保证了正常的轧制工作，达到了高效轧制更薄规格电工钢产品的目的和消化生产CSP热轧超厚过渡坯的目的。

采用EBSD技术研究了有、无拉应力作用下无取向硅钢在晶粒长大过程中织构转变及晶界变化的规律。结果表明:在晶粒生长期间,无应力作用下的硅钢中,{111}〈112〉,{111}〈110〉织构组分强化,而{100}〈001〉织构组分弱化;与无拉应力作用下的情况相比,施加5MPa的拉应力时,{111}〈112〉,{111}〈110〉织构组分强化的速率下降,{100}〈001〉织构组分变化不明显。对于在晶粒生长期间持续变化的{111}〈112〉,{111}〈110〉和{100}〈001〉织构组分而言,虽然有、无拉应力作用下硅钢的{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率均下降,而{100}〈001〉织构组分的高取向差角度晶界频率则上升,但当有拉应力作用后,{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率下降的速率变小,{100}〈001〉织构组分的高取向差角度晶界频率上升的速率稍有变小。通过对无取向硅钢在晶粒长大过程中织构转变及晶界变化规律的研究,分析了合金原子在晶界的偏聚行为。 The rules of texture and grain boundary transformation in the nonoriented silicon steel under applied stress or without applied stress during grain growth were investigated by EBSD.The results show that the {111}〈112〉 and {111}〈110〉 components in the nonoriented silicon steel without stress are strengthened during grain growth whereas {100}〈001〉 component is weakened,but the growth rate of {111}〈112〉 and {111}〈110〉 component decreases,while the area fraction of {100}〈001〉 component doesn’t chang... 

本实用新型涉及变压器技术领域，具体为一种变压器铁芯的硅钢片加工装置，包括工作台，工作台的顶端靠两侧的位置均开设有滑槽，工作台的底端内壁靠两侧的位置均固定安装有两组伸缩杆，两组伸缩杆的顶端均与滑板的底端外表面相固定，滑板的顶端靠两侧的位置均贴合有滑块，两组滑块的顶端均固定安装有螺纹套，两组螺纹套的内部均与双向螺纹杆的外表面相活动螺接，双向螺纹杆的一端固定安装有摇把，双向螺纹杆的外表面靠中间的位置设置有限位块，摇把的顶端固定安装有固定块。两组弧形板和若干组凸块的设置可对硅钢片进行实时校准的作用，并使得叠加的硅钢片始终保持在同一垂直水平线上从而方便后续操作。

一种电工钢切片用辅助定位装置，涉及电工钢加工技术领域，包括加工台、支撑腿、定位块、侧板、滑杆、移动板、顶板、滑动架、伸缩杆、切片装置、定位杆和挡板；支撑腿设置在加工台底部；定位块设置有两组，两组定位块均设置在加工台上，两组定位块沿横向分布，每组定位块设置有两个，每组的两个定位块沿纵向分布；侧板设置有两个，两个侧板均设置在加工台纵向一侧，两个侧板沿横向分布；滑杆设置在两个侧板之间；移动板沿横向滑动设置在滑杆上；顶板设置在移动板靠近加工台的纵向一侧，顶板位于移动板上端。本实用新型能够方便工作人员切割出一定尺寸的电工钢切片，且切割精度很高。

一种高硅钢的电渣重熔生产方法，电渣重熔过程渣系组成为，按重量计，CaF255%～59%、Al2O326%～30%、CaO7%～10%、SiO21%～9%，所述高Si钢，按重量计，钢中含有Si0.5%～2.0%，Al0.01％～0.05％。采用本专利设计的渣系成分配比，保护气氛电渣的情况下，可有效控制Si含量0.5‑2.0%的高Si钢电渣过程不增铝。

本实用新型涉及一种取向硅钢高温退火设备，尤其涉及一种取向硅钢全氢式高温罩式炉外罩，从外至内包括圆柱形外壳和耐火保温层，所述耐火保温层内壁铺设有电阻带；所述圆柱形外壳上部设有外罩顶盖；所述耐火保温层由陶瓷纤维模块堆砌而成，所述电阻带通过钉子铺设在陶瓷纤维模块上；电阻带头一端通过接线棒引出炉壳外，另一端中性点在炉内短接。本实用新型保温层内层采用模块化的高纯度陶瓷纤维代替耐火砖，该材料具有重量轻、蓄热少，低导热性能带来高的节能效果，具有抵抗热冲击的能力，加上模块化的结构，安装快捷，衬体无需烘干和养护，所以安装好以后便可立即投入使用。

本实用新型公开了一种硅钢板带运输使用的固定设备，所述壳体的侧壁固定连接有多个第一放置轴，所述壳体的侧壁固定连接有多个第一限位套，且第一限位套与第一放置轴同轴心，所述第一限位套的内部设置有第一压板，所述壳体的内部设置有第一滑槽及第二滑槽，所述壳体的一侧设置有滑板。本实用新型通过将硅钢板带卷起后用绑线绑紧后，放入第一放置轴外表面后推入第一限位套内部，放好一行成硅钢板带后将将第一个滑板底部的滑杆放入第一滑槽内，推动滑板进入壳体内，使插杆插入凹槽内，再对下一列的硅钢板带进行放置，安装完成后，将挡板放入第二滑槽内，推动滑板向壳体内移动，将挡板向壳体内移动。

本发明提供一种超低铝无取向硅钢夹杂物控制方法。该钢种化学成分质量百分比为C≤0.005％，Si：0.25％‑1.50％，Mn：0.15％‑0.55％，P：0.02％‑0.06％，S≤0.005％，Als≤0.005％，余量为Fe及不可避免的杂质。工艺流程为：KR→BOF→RH→连铸。转炉出钢严格控制下渣量，出钢结束加石灰、渣面脱氧剂调渣；RH脱碳结束后，先加低碳低硫硅铁、金属铝或铝钙铁合金复合脱氧，最后加入金属锰、磷铁进行合金化，然后净循环6‑10min，破空出钢运至连铸浇注。得到钢水中主要为SiO2‑Al2O3系夹杂，避免了生成低熔点SiO2‑MnO系夹杂，轧制延展变长，影响晶粒长大；同时也避免了生成高SiO2组分类酸性夹杂，导致耐材的侵蚀。可显著改善钢中非金属夹杂物类型，提高无取向硅钢的性能，并提高了钢水浇注性能。