本发明涉及一种冷连轧法生产无取向高硅钢的方法,RH真空脱碳处理后,铝脱氧及部分铝合金化,合金化后大罐钢水净循环大于3次或大于5分钟;熔炼合格钢水至连铸开浇前静置时间大于二十分钟;控制过热度5~15℃;采用电磁搅拌,控制等轴晶比例45%以上;3)热轧工序板坯装炉温度大于750℃;常化使晶粒尺寸在90~110μm范围内;连续退火炉加热段温度设定950~1150℃,均热段温度设定900~1050℃,全氮气干气氛保护,控制晶粒尺寸120~170μm。生产全过程中的热履历参数控制,充分发挥设计的微合金元素功能,改变析出物的组成、大小、形态及分布。
2021-08-19 81 6.8

结合工业化生产的无取向硅钢,进行了RH精炼喂CaSi线去除钢中的非金属夹杂物试验研究。针对不同的钙处理条件,分析了CaS夹杂生成热力学,观察了夹杂物的形貌和尺寸分布,确定了夹杂物的类型、数量,探讨了钙处理后钢中夹杂物的变化规律。结果表明,本试验条件下,钙处理可以有效抑制MnS、AlN夹杂物的生成,有效促进钢中微细夹杂物的聚合、上浮、去除,钢质纯净度明显提高。经过合适的钙处理后,钢中的夹杂物以独立存在的CaO为主,同时有少量含CaO、SiO2、MgO的复合夹杂,没有发现CaS夹杂存在。这部分夹杂物的尺寸集中分布在2~20μm,数量约为1.8×105个/mm3。 Experimental study on removal of non-metallic inclusions in non-oriented silicon steel obtained from industrial production by CaSi wire feeding during RH refining process was carried out.The thermodynamics of CaS inclusion formation was analyzed,the morphology and the size distribution of inclusions were observed,and the numbers and types of inclusions were also determined for the steel specimens treated under different calcium treatment conditions.Furthermore,the variation of inclusion characte... 
2013-01-28 77 5.8

本实用新型公开了一种带缓冲保护装置的硅钢片纵剪线,包括工作台,工作台的顶部外壁设置有放料辊,工作台靠近放料辊的一侧设置有牵引辊,工作台靠近牵引辊的一侧设置有整平机构,工作台的内部设置有第一缓冲坑,第一缓冲坑的顶部设置有导料辊,第一缓冲坑的内部设置有第三转轴,第三转轴的外壁传动连接有皮带,皮带的内壁传动连接有第二转轴,皮带的外壁传动连接有第一转轴,第三转轴的外壁固定安装有转筒,转筒的外壁设置有伸缩杆,伸缩杆的外壁套接有弹簧,伸缩杆的底部设置有滚珠,通过设置的第一缓冲坑与第二缓冲坑结构,可防止硅钢片在进入第一缓冲坑与第二缓冲坑时弯曲程度过大导致的断裂,且双重的缓冲装置更有利于对硅钢片的保护。
2020-12-24 75 6.8

采用取向分布函数和取向线分析方法对低温板坯加热取向硅钢从热轧到初次再结晶工艺阶段的织构进行了研究。研究表明:一次冷轧后各层的织构组分与热轧板各层面的织构组分存在着继承关系,次表层存在很强的{001}<110>织构,中心层的织构和热轧板的中心层相似,存在强的{001}<110>和{112}<110>织构;中间退火后发生再结晶,各织构组分的强度有所减弱,Goss织构组分再次出现;二次冷轧后沿厚度方向上的织构不均匀性不明显,{111}<112>织构强度最高,几乎是其他织构组分的1倍,{001}<110>织构大幅降低;初次再结晶后织构沿厚度方向没有明显的不均匀性,{111}<110>为最强的织构组分,并且具有一定强度的Goss位向。 The texture from the first cold rolling to the primary recrystallization of low temperature slab reheating grain-oriented electrical steel were researched by orientation distribution function and orientation distribution intensity technique.The results show that after the first stage of cold rolling,there is a strong {001}<110> texture in the subsurface and the texture in center layer is very similar to the center layer of hot band which has strong {001}<110> and {112}<110> tex... 
2011-08-28 116 5.8

介绍了电工钢生产线连退机组的表面处理工艺,特别是电解清洗系统的工作机理、设备构造、生产工艺及各种影响因素。 This paper introduces the technology of surface treatment of continuous annealing unit in electrical steel production line,in particular the working mechanism,structure of equipment,production techniques and various influence factors of the electrolytic cleaning system. 
2023-05-11 1.21k 5.8

以试验室模拟CSP工艺生产的Fe-3Si热轧钢带为研究对象,采用正交试验及方差分析的方法,研究了取向硅钢初次再结晶退火工艺对高温退火后获得锋锐的高斯织构的影响。结果表明:取向硅钢两段式初次再结晶脱碳退火工艺参数加热段保温时间及加热温度是高温退火后获得锋锐高斯织构的主要影响因素,其可信度分别在90%和85%以上;在本试验条件下,通过正交试验获得的最佳退火工艺为:冷硬板经600℃保温3 min和850℃保温6 min。 Fe-3Si hot rolled strip was produced by simulating CSP technology in the laboratory.Orthogonal experiment and analysis of variance were carried out to investigate the influence of primary recrystallization on the sharp Goss texture of the oriented silicon steel.The results show that holding time of the heating section and the heating temperature for a sharp Goss texture of the samples annealed has important implications in this experiment conditions,the two-step decarburization annealing process... 
2013-02-28 79 5.8

本发明提供一种硅锰镇静无取向硅钢冶炼方法。该无取向硅钢化学成分质量百分比为C≤0.005%,Si:0.25%‑1.20%,Mn:0.2%‑0.8%,P:0.015%‑0.065%,S≤0.005%,Als≤0.005%,余量为Fe及不可避免的杂质。其生产方法包括转炉出钢结束加石灰、渣面脱氧剂调渣;RH真空精炼脱碳结束后进行脱氧合金化,合金化后3‑5min由真空室料仓加入合成渣,处理一段时间后净循环8‑12min,破空出钢运至连铸浇注。得到钢水中主要为SiO2‑CaO‑Al2O3系夹杂,一方面避免了钢水中生成低熔点SiO2‑MnO系夹杂,轧制过程沿轧制向伸长,阻碍晶粒长大;另一方面也避免了生成纯SiO2或高SiO2组分类酸性夹杂,导致冶炼过程耐火材料的严重侵蚀。本发明可控制钢中非金属夹杂物类型,提高钢水洁净度,改善冶炼过程中对耐火材料的侵蚀。
2021-01-21 67 6.8

本实用新型涉及硅钢技术领域,尤其为一种用于硅钢绝缘涂料生产用储存装置,包括储存装置、顶盖和定位板,所述储存装置与顶盖铰链连接,所述顶盖内侧后端固定连接有定位块,所述定位块前端转动连接有连接块,所述连接块的另一端内侧转动连接有转动杆,通过设置的定位块、连接块、转动块、转动杆、推杆、档杆、挡块、弹簧、固定板和垫片,在使用时,盖上顶盖后,通过推动推杆,使推杆通过转动块带动转动杆在连接块内转动,推杆推动挡块,使挡块通过档杆挤压弹簧,从而对推杆进行限位,然后带动连接块在定位块上转动,从而使连接块挤压固定板,使固定板带动垫片,使垫片与储存装置贴合更紧,防止漏气,防止空气进去,防止涂料干燥。
2021-05-12 45 6.8

本实用新型公开了一种铁芯硅钢片移动夹具,包括底板,所述底板上表面固定连接有固定板,所述底板的后表面固定连接有支撑腿,右侧所述支撑腿的前表面固定连接有转轴,所述转轴的外表面转动连接有转动板,所述底板的上表面且位于固定板的右侧固定连接有支杆,所述底板的上表面且位于支杆的右侧固定连接有第一电机。本实用新型,通过设计转动板、第一绳索与第二伸缩杆,实现在转移硅钢片时,将其竖直排列,增加其抗弯能力,通过设计第一伸缩杆与限位块,实现其在移动的过程中避免相互摩擦,达到保护硅钢片的目的,通过设计滑动板、第二伸缩杆、支撑板,实现在上下转运的过程中,仅有上侧进行接触,且呈三角形更加稳定。
2021-04-14 54 6.8

本发明是高磁感取向硅钢的脱碳退火工艺,首先对硅钢卷进行放卷、活套、清洗;再对硅钢进行脱碳、渗氮处理,氨气流量6‑20m3/h、加湿槽温度30‑70℃,脱碳温度780‑880℃、机组速度45‑75m/min、气氛中氢气比例20‑60%、氮气比例40%‑80%,然后冷却到常温;对硅钢进行活套;再对硅钢进行涂覆氧化镁,涂覆量4‑10g/㎡;最后对硅钢进行干燥和收卷成硅钢卷;通过本发明对高磁感取向硅钢的脱碳退火工艺流程进行了优化设计,调整了脱碳退火工艺中氨气流量、气氛、加湿槽水温等参数,优化了高磁感取向硅钢中碳元素、氮元素和氧元素的含量,最终使高磁感取向硅钢实现稳定的性能,磁感达1.92T。
2021-04-23 86 6.8

本发明公开了一种改善高牌号无取向硅钢表面色差缺陷的方法,属于冷轧卷板表面质量改进技术领域。所述方法为:将连铸坯依次进行热轧、常化、酸洗、单机架轧制和连续退火工序,其中按重量百分数计,所述的连铸坯含有如下成分:C<0.003%、Si1.6~2.0%、Mn0.35~0.65%、Al0.35~0.65%、P<0.02%、S<0.0025%、余量为Fe和其他不可避免的杂质元素,所有成分合计100%;其中热轧工序的卷取温度为620~640℃。本发明所述方法能够降低带钢表面氧化铁厚度并改变带钢表面氧化铁结构,改善高牌号无取向硅钢表面色差缺陷。
2021-03-25 99 6.8

根据本发明的一个实施例的无取向电工钢板,以重量%计,所述钢板包含Si:1.5%以下、C:0.01%以下且0%除外、Mn:0.03至3%、P:0.01至0.2%、S:0.001至0.02%、Al:0.01%以下且0%除外、N:0.005%以下且0%除外、和Cu:0.02至0.3%,Ca和Mg各自单独或以合计含量包含0.0001至0.005重量%,Sb和Sn各自单独或以合计含量包含0.001至0.2重量%,余量包含Fe和不可避免的杂质。
2020-12-17 90 6.8