退火温度对无取向电工钢组织和磁性能的影响
主要研究了0.7%Si无取向电工钢退火试样的组织、晶粒尺寸和织构对其磁性能的影响。结果表明,随着退火温度的升高,晶粒尺寸逐渐增大,组织的均匀性得到改善;ɑ取向线上的纤维织构多集中于{114}<110>和{223}<110>附近,再结晶结束后,织构含量变化不大。{111}<110>织构取向密度值随温度升高而下降,{112}<111>织构与{111}<110>织构变化相反。晶粒尺寸增大对磁感强度的影响较小,而对铁损的影响较大。 Influences of microstructure,grain size and texture on the magnetic properties of 0.7% Si non-oriented electrical steels annealed samples were studied.The results show that with annealing temperature increasing the average grain size is increased gradually.Uniformity of the microstructure is improved;the textures of ɑ-fiber gathered in the vicinity of the { 114} < 110 > and { 223 } < 110 > texture.After recrystallization,the volume fraction of texture changes small.{ 111} < 110 &g...
退火温度对2%Si无取向电工钢磁性能的影响
研究了传统工艺流程生产的2%Si无取向电工钢在不同退火温度下的磁性能。研究结果表明,随着退火温度的升高,显微组织均匀性提高且晶粒尺寸增大;有利织构组分{100}<0vw>、α、η增强,不利织构组分减弱;成品的铁损P1.5/50先下降后略有上升,磁感B50上升平缓;在890℃×2 min的退火工艺条件下,成品电工钢的磁性能最佳,对应的铁损P1.5/50小于3.2 W/kg,磁感B50高于1.74 T。 In this paper,the effect of annealing temperature on magnetic properties of non-oriented electrical steel with 2% silicon was studied.Results show that the uniformity of microstructure and the average grain size increase with the rise of annealing temperature.The texture components of annealing can be improved by enhancing {100} <0vw>,α,η fiber textures and weakening {111} <112> fiber texture.The tendency of core loss P1.5/50 shows that it decreases first and then increases,while the...
硅钢连续退火生产线设备改造
针对硅钢连续生产线设备存在的故障、隐患以及精度等影响产品质量的问题进行分析及改造,实现保证生产线设备稳定运行、提高设备精度及硅钢产品质量的目的。 This paper analyzes and transforms the electrical equipment failures, risks existed in slicon continuous production line, and the effect of accuracy to product quality, in order to ensure stable operation of equipment in production line and improve the accuracy of device, quality of silicon.
CN202110417952.3一种硅钢片自动化纵剪裁切加工设备及加工方法
本发明涉及一种硅钢片自动化纵剪裁切加工设备及加工方法,包括固定架、放卷筒、纵剪装置和裁切装置,所述的固定架的下端与已有地面相连,固定架前后对称分布,前后正相对的固定架之间转动连接有放卷筒,放卷筒的右侧从左至右依次设置有纵剪装置和裁切装置,本发明通过电机、转轴、转动杆做同步高速旋转运动转动杆带动切割刀做同步高速旋转运动,从而可实现切割刀对硅钢卷进行纵向裁剪的功能,使较宽的硅钢卷一分为二形成较窄的硅钢卷,以便提高后续对硅钢进行进一步的加工的速率。
取向硅钢常化水冷温度模型及控制方法研究
取向硅钢常化工序主要采用现场实测带钢温度的方式测定冷却速率,并通过稳定冷却水温、调整冷却水量及喷梁运行数量等方式保证合理的冷却速率,给常化工艺设计和生产带来诸多不便。通过对常化工艺水冷过程带钢的传热分析求解,在建立带钢水冷温度模型的基础上,研究了不同冷却工艺参数对带钢温度及冷却速率的影响规律以及冷却工艺的交互作用结果。结果表明:模型计算结果能够较好地反映取向硅钢在常化水冷过程中的温度及冷却速率的变化,其计算误差为0.80%~4.11%;在特定取向硅钢厚度规格和常化工艺下,随着常化冷却水量及有效冷却长度的增加,带钢水冷温度及冷却速率与呈非线性变化;常化水冷工艺主要通过调控带钢与冷却水之间热交换量和交换时间实现对带钢温度的控制,实际生产中需综合考虑机组速度、冷却水量及有效冷却长度之间的交互作用,选定喷梁投入数量和冷却水量以获得稳定的冷却速率。 The cooling rate of normalization process mainly determined by measuring the grain oriented silicon steel strip temperature on site, and ensures the cooling rate by stabilizing the cooling water temperature, adjusting the cooling water volume and the operation quantity of spray beam, which brings inconvenience to the normalization process design and production. Based on the heat transfer of strip in the water cooling section of normalization process, the water cooling temperature model for the n...
硅钢芯片冲裁工艺分析与对策
分析了冲裁硅钢芯片时出现的质量问题,针对影响硅钢芯片冲裁质量的4大因素——人、原材料状态、工艺和工装进行了工艺试验和分析,根据原材料状态的差异,采用不同工艺方案,特别是如何合理选择冲裁模具间隙,解决了硅钢芯片冲裁时产生的主要质量问题,使冲裁的硅钢芯片达到最佳质量状态,并满足硅钢芯片的使用性能。 The problems occurred during silicon steel chip punching and the factors that affect the quality of silicon steel chip punching were analyzed,the factors include 4aspects,that is,people,raw material status,process and frock,at the same time,process tests and analysis aimed at the factors that affect punching quality were did,according to the difference of raw material status,corresponding process schedules wee taken,especially in how to reasonably select punching dies clearance,which solved the ...
CN202111129070.3一种增大压下率的电工钢冷轧装置及冷轧方法
一种增大压下率的电工钢冷轧装置及冷轧方法,属于电工钢冷轧技术领域,该电工钢冷轧装置,包括单机架可逆轧机,单机架可逆轧机的两侧均设置有电磁感应加热装置和氮气风冷装置,氮气风冷装置靠近单机架可逆轧机的轧制进口或入口设置,本发明的有益效果是,本发明通过在单机架可逆轧机两侧增设电磁感应加热装置和氮气风冷装置,对每道次轧制过程中可在线调节电磁感应加热温度,实现了边去应力退火边轧制,保证了正常的轧制工作,达到了高效轧制更薄规格电工钢产品的目的和消化生产CSP热轧超厚过渡坯的目的。
热轧卷取时间对新型冷轧无取向电工钢组织和性能的影响
研究了热轧卷取时间对无取向电工钢晶粒组织、织构演变、铁损和磁感的影响。结果表明,成品晶粒尺寸在120~140μm之间,随卷取时间的增加,成品晶粒尺寸增大。成品织构主要由γ纤维、а纤维和高斯织构等构成。随着保温时间的增加,{111}<110>和{112}<110>织构强度降低。随卷取时间的增加,成品P1.5降低。热轧板最佳的卷取工艺为550℃保温2~3 h,电工钢的综合磁性能优良。 The effects of hot-rolling coiling time on microstructure,texture,core loss and magnetic induction of a new cold-rolled non-oriented electrical steel containing copper were investigated.The test results showed that for final product the grain sizes are 120-140um,with the increase of coiling time,the grain size increase.For final product there are mainly γ-fibre,а-fibre,and {110}<001> texture,Coiling at 550℃ for hot rolled plate,the {111}<110>,{112}<110> texture was weaked with ...
CN202111182553.X一种多组分{100}织构无取向电工钢的制备方法
本发明涉及冶金技术领域,具体涉及一种多组分{100}织构无取向电工钢的制备方法。本发明通过控制薄带连铸参数制备1.5~2.5mm厚的无取向电工钢铸带,直接冷轧至厚度为0.35~0.50mm后,先进行预回复退火,再进行成品退火,此过程中控制退火温度、时间以及升降温速率。本发明所制备的无取向电工钢具有多组分{100}织构,包括{100}&lt;001&gt;、{100}&lt;012&gt;和{100}&lt;011&gt;,{100}织构组分体积分数达到25~39%,其轧向磁感值1.71~1.78T,横向磁感值1.70~1.76T,板面45°方向磁感值达到1.65~1.67T。本发明通过优化退火工艺,利用{100}变形组织的强回复与再结晶协同作用,从而显著增强{100}退火织构,方法简单有效。
CN202111244942.0一种低损耗宽料取向硅钢的生产方法
本发明公开了一种低损耗宽料取向硅钢的生产方法。本发明所述生产方法是通过在罩式炉的内罩中增加带有通气孔的聚气罩及与聚气罩配合的炉底板,配合工艺优化,控制原料化学成分,使气体和钢卷之间的浓度更均匀,反应更充分,气流流动方向更易控制,所制备的取向硅钢性能稳定,磁性能优良,且铁损达到1.12W/KG以下的比例提高至98.77%,平均铁损达到1.06W/KG以内,使取向硅钢卷的铁损大幅度降低,电磁性能更好。
CN202110893627.4一种硅钢板毛刺修整机
本发明涉及硅钢板技术领域,尤其涉及一种硅钢板毛刺修整机,包括工作台,所述工作台顶端面的一侧通过升降座安装有打磨机构,工作台顶端的另一侧设置有连接柱,连接柱上部的一侧水平安装固定有横梁,横梁底端面的中部竖直安装有液压杆,液压杆的底端安装有打磨机构,且上、下两个打磨机构交错分布,本发明中通过上、下两个打磨机构的主打磨带对硅钢板的顶端面和底端面进行打磨,副打磨带对硅钢板的侧端面进行打磨,从而能够对硅钢板的水平端面以及侧端面同时进行打磨去毛刺,提高了硅钢板整体毛刺修整的效率。