本发明提供一种超低铝无取向硅钢夹杂物控制方法。该钢种化学成分质量百分比为C≤0.005％，Si：0.25％‑1.50％，Mn：0.15％‑0.55％，P：0.02％‑0.06％，S≤0.005％，Als≤0.005％，余量为Fe及不可避免的杂质。工艺流程为：KR→BOF→RH→连铸。转炉出钢严格控制下渣量，出钢结束加石灰、渣面脱氧剂调渣；RH脱碳结束后，先加低碳低硫硅铁、金属铝或铝钙铁合金复合脱氧，最后加入金属锰、磷铁进行合金化，然后净循环6‑10min，破空出钢运至连铸浇注。得到钢水中主要为SiO2‑Al2O3系夹杂，避免了生成低熔点SiO2‑MnO系夹杂，轧制延展变长，影响晶粒长大；同时也避免了生成高SiO2组分类酸性夹杂，导致耐材的侵蚀。可显著改善钢中非金属夹杂物类型，提高无取向硅钢的性能，并提高了钢水浇注性能。

采用扫描电镜、原子力显微镜研究了铬酸镁半无机绝缘涂层的微观结构。结果表明,涂层厚度为数微米,涂层中的有机树脂乳液颗粒均匀分布在无机涂层的表面,从而保证了涂层具有良好的冲片性能。采用极化曲线研究了涂层的耐蚀性能,发现铬酸镁与铬酸锌绝缘涂层的耐蚀性能相当。 In this paper,the microstructure and anti-corrosion property of magnesium chromate coating on non-oriented silicon steel were studied.The microstructure was observed by SEM and AFM.The anti-corrosion properties were evaluated by polarization curves.The results show that the thickness of coating is several microns and the polymer particles were scattered on the surface of inorganic coating,which is the guarantee for lamination property.The corrosion resistance of the magnesium chromate film was e... 

分析了影响脱碳效果和结晶行为的各种要素及其相互制约关系,提出了Hi-B连续退火工艺曲线,总结得出快速加热及合理稳态气氛是实现工艺制度的关键。结合实际工程,介绍了在连续退火炉设计中快速加热和气氛设计的考虑方法,并指出随着Hi-B产品的发展,如何改进这些方法将是连退工程研发的方向之一。 The factors which affect decarbonization and crystallization and the mutual restriction between them were analyzed.A complete continuous annealing process for Hi-B was put forward.As a result,the rapid heating and the proper steady atmosphere were two important factors.According to an actual project,the consider methods for designing rapid heating and proper steady atmosphere were introduced,and it is pointed that with the development of Hi-B technique,how to improve these techniques would be on... 

本实用新型涉及一种多物理因素耦合作用电工钢片矢量磁特性自动测量系统，多物理因素耦合作用电工钢片矢量磁特性自动测量系统包括上位机、数据采集卡、低通滤波器、功率放大器、隔离放大器、励磁装置、矢量B‑H传感器、x方向励磁线圈、y方向励磁线圈、单片机系统、电源、温度自动加载模块和应力自动加载模块。本实用新型实现了电工钢片复杂磁特性测量过程中温度和应力的自动加载，解决了人为操作繁琐，耗时的缺点，使得电工钢片复杂磁特性的测量过程更加方便，高效，可行性更高。

本实用新型公开了一种变压器用硅钢片存放架，其包括多个存放板座和多个支撑柱，多个存放板座依次呈上下间隔设置，在相邻两个存放板座之间设置若干支撑柱，支撑柱的上下两端分别与相邻两个存放板座可拆卸地连接，在存放板座四周的边沿设置有多个吊挂结构，存放架从下往上进行搭设过程中，硅钢片可依次从下往下依次叠放于多个存放板座上，提高存放量，降低存放占用的车间面积；在吊运时，从上往下依次把存放有硅钢片的存放板座吊起移动即可，实现硅钢片的快捷吊运，在不使用时或者运输时，可把支撑柱拆下，存放板座叠在一起进行存放收纳。本实用新型可应用于变压器硅钢片的存放吊运。

利用OM、EBSD等手段研究了热轧板两段式正火时在700℃保温不同时间(0、10、30、60 min)对含Sb冷轧无取向电工钢磁性能的影响。结果表明,700℃保温10 min处理的样品铁损最小,磁感最高。对成品板的组织分析结果表明,试样的晶粒尺寸随700℃保温时间的延长先增大后减小,保温10 min时晶粒尺寸达到最大;分析成品试样织构发现,有利织构组分随700℃保温时间的延长先增加后减少,保温10 min时有利织构组分所占百分比最高。因此,含Sb冷轧无取向电工钢两段式正火时在700℃保温10 min时磁性能最好。 Effect of two-stage normalization on magnetic property of non-oriented electrical steel containing antimony was investigated by using optical microscope(OM) and electron back-scattered diffraction technology(EBSD).The experimental results show that the iron loss and magnetic permeability of the specimen insulated at 700 ℃ for 10 min are lowest and highest respectively.The grain size of the finish specimens increases first and then decreases with the increase of holding time.Similarly,the advanta... 

本发明公开了一种去除无取向硅钢夹杂物的方法，在中间包预设脉冲电流装置，将所述脉冲电流装置的正极连接在上挡渣堰处，负极连接在下导流坝处，在钢水浇注过程中，施加电脉冲处理即可。本发明基于中间包钢水流场的研究，在中间包上挡渣堰和下导流坝之间施加脉冲电场，扩大了脉冲电场作用的钢水区域，且随着钢水流场运动，流场与脉冲电场相互作用，使得细小的SiO2和MnS夹杂物在钢水运动过程中更有效的碰撞、聚集、长大，并有充足的时间充分上浮，从而达到有效去除铸坯夹杂物，降低铸坯中S和O含量，大幅提高钢水纯净度，进而提高硅钢成品磁性能。

一种电工钢切片用辅助定位装置，涉及电工钢加工技术领域，包括加工台、支撑腿、定位块、侧板、滑杆、移动板、顶板、滑动架、伸缩杆、切片装置、定位杆和挡板；支撑腿设置在加工台底部；定位块设置有两组，两组定位块均设置在加工台上，两组定位块沿横向分布，每组定位块设置有两个，每组的两个定位块沿纵向分布；侧板设置有两个，两个侧板均设置在加工台纵向一侧，两个侧板沿横向分布；滑杆设置在两个侧板之间；移动板沿横向滑动设置在滑杆上；顶板设置在移动板靠近加工台的纵向一侧，顶板位于移动板上端。本实用新型能够方便工作人员切割出一定尺寸的电工钢切片，且切割精度很高。

本申请实施例公开了一种硅钢片卷绕机调节装置，包括底部支撑座，所述底部支撑座一侧的内部活动套接有伸缩调节板，所述伸缩调节板的上部固定连接有上部定位套，所述上部定位套内部的上端活动套接有第一定位板，所述上部定位套的内部安装有第一螺纹定位杆。该硅钢片卷绕机调节装置，通过带动硅钢片夹持在上下两个夹持板之间，即可带动夹持板之间的挤压力，带动硅钢片两侧位置进行限定，避免硅钢片收卷时出现振动和偏移的问题，同时装置夹持板的内部活动套接有滚轮，即可在硅钢片移动过程中，可带动滚轮旋转，即可带动硅钢片与滚轮之间的摩擦阻力降低，至此可带动硅钢片移动时的灵活性，避免硅钢片移动时出现卡死的问题。

本实用新型公开了一种硅钢片组扣件自动压平装置，包括：定位单元，定位单元包括转盘、校位板和第一驱动组件，第一驱动组件连接并驱动校位板沿竖直方向运动，校位板滑动连接有第一校位柱，第一校位柱相对转盘偏心布置；第一推送单元，位于转盘的一侧，第一推送单元包括第一推送气缸和第一推块，第一推送气缸连接并驱动第一推块沿水平方向运动；冲压单元，位于转盘背离第一推送气缸的一侧，冲压单元包括第二驱动组件和冲压柱，第二驱动组件连接并驱动冲压柱沿竖直方向运动。转盘、校位柱和第一驱动组件配合，周向定位硅钢片组，再通过冲压柱将凸出于硅钢片组的扣件压平，完成硅钢片组的整形，整体更为美观，方便后续的装配使用。

本实用新型涉及一种无取向硅钢蠕变性能测试装置，包括基座，基座的顶部和侧面设有开口；试样夹持装置，试样夹持装置安装在基座的顶部，用于夹持硅钢蠕变试样；转换力杆，转换力杆安装在基座的侧面，与试样夹持装置连接；可调节式砝码盘，可调节式砝码盘安装在转换力杆上，可调节式砝码盘上能够放置不同重量的砝码，转换力杆将砝码的重力转换成水平力，以实现对硅钢蠕变试样不同应力水平的加载；可调节式灯座，设置在试验腔内并与基座的侧面插接；加热装置，放置到可调节式灯座上，用于给硅钢蠕变试样加热。本实用新型具有解决无法实现不同应力和温度下硅钢材料的蠕变研究的问题的效果。

一种通过粉末烧结制备高磁性能含磷硅钢薄片的方法，属于粉末冶金技术领域。本发明通过真空熔炼气雾化制备成分范围为Fe‑(3‑6.5)wt.％Si‑(0.05‑1)wt.％P的合金粉，将其放置在陶瓷坩埚中均匀振实并放置重物压住，随后进行高温烧结使其冶金结合，再经热轧、冷轧、退火等处理后，得到具有优异性能的含磷硅钢薄片。本发明在硅钢材料体系中加入P元素，能够有效降低铁损、优化磁性能并促进活化烧结；采用气雾化粉末能够很好地保证产品的少夹杂和纯净度；在低熔点P元素及粉末压烧的协同作用下解决了球形气雾化粉末难以成形的缺陷，并避免了需添加成形剂导致的工艺复杂性及后续的脱胶残碳问题，有效缩短制备工艺流程，具有操作简单、生产效率高、工艺流程短、性能优异等优点。