研究了热轧卷取时间对无取向电工钢晶粒组织、织构演变、铁损和磁感的影响。结果表明,成品晶粒尺寸在120～140μm之间,随卷取时间的增加,成品晶粒尺寸增大。成品织构主要由γ纤维、а纤维和高斯织构等构成。随着保温时间的增加,{111}<110>和{112}<110>织构强度降低。随卷取时间的增加,成品P1.5降低。热轧板最佳的卷取工艺为550℃保温2～3 h,电工钢的综合磁性能优良。 The effects of hot-rolling coiling time on microstructure,texture,core loss and magnetic induction of a new cold-rolled non-oriented electrical steel containing copper were investigated.The test results showed that for final product the grain sizes are 120-140um,with the increase of coiling time,the grain size increase.For final product there are mainly γ-fibre,а-fibre,and {110}<001> texture,Coiling at 550℃ for hot rolled plate,the {111}<110>,{112}<110> texture was weaked with ... 

本实用新型公开了一种新型嵌线结构的硅钢片组件，包括硅钢片组和骨架，硅钢片组由若干相同形状的硅钢片堆叠而成，硅钢片为倒U型的薄片体，骨架由一限位框架和两固定杆组成，限位框架由一矩形框架和位于矩形框架四角的限位凸块组成，硅钢片组卡设在矩形框架上，限位凸块对硅钢片组进行限位，两固定杆平行设置在硅钢片组的上方，且固定杆的两末端分别与限位凸块相固定。本实用新型具有装配简单、不易变形的优点。

本发明提供了一种CSP流程生产高效冷轧无取向电工钢及生产方法，成分：C≤0.0030％、Si 1.00‑1.70％、Als≤0.0050％、Mn 0.10‑0.30％、Sn0.01‑0.3％、P≤0.050％、S≤0.0080％、N≤0.0030％、Nb≤0.0030％、V≤0.0030％、Ti≤0.0030％，其余为Fe以及不可避免的杂质。与现有技术相比，本发明CSP流程生产高效冷轧无取向电工钢的方法，通过控制钢中的化学成分，并采用合适的生产工艺，实现了表面质量优良，低铁损、高磁感、低制造成本且生产高效。

​6月28日国联证券发布：《电力设备出海2024年中期投资策略：需求方兴未艾，供给释...

本实用新型涉及一种用于电机电磁钢板叠装的液压治具，属于电机生产治具技术领域。该用于电机电磁钢板叠装的液压治具，包括上压板和下压板，上压板和下压板呈之母“U”型。本实用新型设计了一种用于电机电磁钢板叠装的液压治具在使用过程中，将液压治具的底部放置在初步叠装放置的电磁钢板上，在通过液压装置来压紧液压治具，液压治具将压力传导和均匀分散，使得整个电磁钢板受理均匀。总之，该用于电机电磁钢板叠装的液压治具结构设计合理，可以加大液压机上电磁钢板的受力面积，使得受力均匀，从而快速完成压装缩短作业时间，提高了电磁钢板叠装效率和质量。

本发明提供退火隔离剂的制备方法以及退火隔离剂和方向性电磁钢板。由该方法得到的退火隔离剂纯度高、分散性以及密接强度优异，可以在方向性电磁钢板表面形成均匀致密的镁橄榄石层。退火隔离剂的制备方法，其包括：工序(1)：将氧化镁和铵盐溶液混合并反应，制备镁盐溶液和氨，然后使精制的镁盐溶液与氨反应而得到氢氧化镁；工序(2)：将得到的氢氧化镁的一部分在155～230℃下高温熟化，并且将得到的氢氧化镁的另一部分在10～100℃下低温熟化；工序(3)：将在上述各条件下熟化的氢氧化镁混合、烧成，得到氧化镁用于退火隔离剂。

采用X-射线衍射分析技术测定了取向硅钢热轧板在不同压下率下不同厚度处的织构。结果表明,在压下率低于80%的情况下,几乎所有试样的不同厚度处的织构均为旋转立方织构类型{100}<011>,但不同压下率、不同厚度处的织构强度存在很大差异;在压下率大于80%的情况下,不同试样的不同厚度处的织构类型发生了变化,其织构类型为旋转立方织构或高斯织构{011}<100>,且当织构类型为旋转立方织构时,织构强度存在很大差异,而当织构类型为高斯织构时,织构强度差异相对较小。 The texture of the grain oriented silicon steel hot rolled plate at different compressibility has been measured.The experimental results have shown that the texture of all samples at different thickness is {100}<011> when the compressibility is below 80%,and its intensity at different compressibility and thickness is difference.The texture of all samples at different thickness is variable when the compressibility is above 80%,it is {100}<011> or {011}<100>,and the intensity of ... 

作为一种具有优异高频铁磁性能的合金,Fe-6.5%Si(质量分数)高硅钢在高频工况条件下降损效果明显,对电气行业应用器件高频化、小型化、节能等具有十分重要的意义。通过与取向硅钢测量B-P数据对比,验证了高硅钢高频超低损特性,且轧制高硅钢与日本CVD法生产高硅钢存在基本相同的铁损值。采用国标Epstein Square法对0.30mm高硅钢薄板进行单片测试,并对由0.30mm高硅钢薄板首次装配成的电感器进行铁损测试,对比测试结果表明,元件测试与单片测试数据基本吻合,高磁感应强度条件下,元件测试结果略低于单片测试,分析原因为:线圈引起励磁压降;元件叠片间出现短路,电流增大,损耗增加;气隙板厚度过大。 As one core material with excellent high-frequency ferromagnetism,Fe-6.5%Si performs obviously reduction on core loss in high field frequency which means much to high frequency,minimization,energy conservation in electric industry.Super low loss was verified by drawing B-P curves based on detected experimental data,and which went equal to Fe-6.5%Si thin strip fabricated by CVD in Japan.Fe-6.5%Si was firstly fabricated as inductor in this research,and its core loss was determined for comparison w... 

本发明提出了一种控制磁畴结构来降低铁损的取向性电磁钢板的制造方法中，即使在实施了去应力退火的情况下，也能够保持铁损降低效果，并且在磁畴控制处理后磁通密度不会降低的方法。本发明的制造方法中，在取向性电磁钢板的表面，沿与钢板的轧制方向交叉的方向线状地照射周边比中心低的环状的强度分布的激光。

本实用新型属于抛丸设备技术领域，具体涉及一种硅钢抛丸用耐磨抛丸头，包括壳体、进丸管、定向套、分丸轮、多块截面呈工字形的叶片和两块对称设置的护板，多块叶片沿护板的周向均匀分布，叶片安装在两块护板之间；叶片的左右两侧分别设有一组卡槽，一组卡槽包括两个卡槽，一组卡槽上滑动连接有能与叶片表面接触的耐磨板；叶片上设有用于固定耐磨板位置的固定件；壳体内可拆卸的安装有耐磨衬板。在本方案中，将耐磨板可拆除的安装在叶片中，耐磨板对叶片有保护的作用，能避免叶片被磨损；当耐磨板损坏后只需更换新的耐磨板，而不需更换叶片，能够有效节省成本。同样的耐磨衬板对壳体也有保护作用，能够在很大程度上减少壳体被磨损。

研究了卷取工艺对一种新型含铜无取向电工钢晶粒尺寸、织构演变、铁损和磁感应强度的影响。结果表明,试样织构组分主要为{111}、{112}、{100}和高斯织构,在550℃卷取、保温2～3h,{100}织构有增强趋势,磁感应强度较高,铁损较低。 The effects of coiling process on grain size,texture,core loss and magnetic induction of a new cold rolled non-oriented electrical steel with copper were investigated.The results show that there are mainly {111},{112},{100} and {110}<001> texture.Coiling at 550℃and keeping for 2～3 hours,the {100} texture is enhanced,magnetic induction is higher and core loss is lower. 

本实用新型公开了一种硅钢板带运输使用的固定设备，所述壳体的侧壁固定连接有多个第一放置轴，所述壳体的侧壁固定连接有多个第一限位套，且第一限位套与第一放置轴同轴心，所述第一限位套的内部设置有第一压板，所述壳体的内部设置有第一滑槽及第二滑槽，所述壳体的一侧设置有滑板。本实用新型通过将硅钢板带卷起后用绑线绑紧后，放入第一放置轴外表面后推入第一限位套内部，放好一行成硅钢板带后将将第一个滑板底部的滑杆放入第一滑槽内，推动滑板进入壳体内，使插杆插入凹槽内，再对下一列的硅钢板带进行放置，安装完成后，将挡板放入第二滑槽内，推动滑板向壳体内移动，将挡板向壳体内移动。