硅钢资料

以质量分数为25%的丙烯酸乳液MC-102、15%Al(H2PO4)3溶液、0.01%H3BO3、0.01%Zn(Ac)2·2H2O和2%二乙二醇丁醚组分,在不同固化工艺下制备涂层。极化曲线和电导率测试发现300℃处理60 s得到的涂层具有良好的耐腐蚀性和绝缘性;水煮实验证明该涂层具有良好的耐水性;断口线扫描发现涂层具有良好的附着性。 A formula comprising MC-102 acrylic emulsion 25%,aluminium dihydrogen phosphate15%,boric acid 0. 01%,zinc acetate dihydrate 0. 01% and diethylene glycol monobutyl ether 2% was used to prepare coatings via different treatment process. The conductivity test and polarization curves revealed that a coating cured at 300 ℃ for 60 s showed good insulative and anticorrosive properties. The water boiling test indicated that the said coating had good water resistance. A cross section of the coating was in... 

本发明提出了一种可修饰取向硅钢表面的无铬无机绝缘涂料及其制备方法，该涂料按照重量份计包括以下组份：磷‑硅溶胶40‑70份、钛改性增稠剂预溶胶25份、抑泡剂0.2‑1份、流平剂0.05‑0.2份和去离子水3.8‑34.75份。该涂料的制备方法为：先制备磷‑硅溶胶和钛改性增稠剂预溶胶；然后向磷‑硅溶胶中加入抑泡剂并搅拌均匀；再加入去离子水并搅拌均匀；再分次缓慢加入钛改性增稠剂预溶胶并搅拌均匀；最后加入流平剂并搅拌均匀。本发明所制备的无铬无机绝缘涂料可修饰取向硅钢表面瑕疵露晶等形貌缺陷；在取向硅钢表面形成的绝缘涂层具有良好的附着力和耐热性；涂料采用的原料均为无污染的环保材料，解决了含铬绝缘涂料带来的环境危害。

本实用新型公开了一种基于取向电工钢用收卷组件及其固定结构，包括主体，所述主体的后侧中部固定安装有固定杆，所述固定杆的侧面活动安装有活动机构，所述活动机构包括活动块，活动区，弹簧，主动块，连接孔，连接杆，齿轮，卷筒，挡板。该种基于取向电工钢用收卷组件及其固定结构，活动块会带动活动区内部的主动块在其内部移动，可以通过连接杆带动齿轮进行转动，因齿轮侧面啮合连接有齿口，从而会顺着主体的侧面进行移动，当齿轮移动到主体的一角时，会带动活动区内部的弹簧收缩，弹簧可根据齿轮到主体中心的距离长短进行伸缩，物料会通过卷筒落到卷块的表面，从而可以对物料进行收卷，最后达到了便于收卷，降低物体损害的目的。

【作者】 罗海文； 向睿； ...

本发明涉及金属冶炼工艺，尤其是一种降低无取向硅钢W800冶炼成本的方法，开吹阶段，着火后，加入头批渣料，石灰加入量占石灰总加入量的70%，石灰石加入量占石灰石总加入总量的100%，轻烧白云石加入量占轻烧白云石总加入总量的100%，待化渣后，枪位降低；化渣后将剩余30%石灰加入，加入剩余石灰过程中利用矿石调整温度；吹炼后期，并逐步压枪，终点拉碳枪位至1.4m，并使枪位在此高度不少于30s；到达冶炼终点。本工艺通过降低转炉渣量、提碳降氧和提高终点温度来减少铁水锰氧化量和促进氧化锰还原量，进而降低RH金属锰加入量，降低生产成本。

本发明公开了一种硅钢冷连轧轧制过程温度获取方法、装置及电子设备，通过获取硅钢冷连轧生产过程的工业参数数据以及各机架间硅钢的实际温度测试数据，然后基于工业参数数据以及预设初始模型，确定硅钢冷连轧生产过程的温度预测模型，接着基于硅钢轧制前的预热温度以及温度预测模型，得到硅钢冷连轧轧制过程各机架变形区出口与下一机架变形区入口之间的预测温度数据，再将预测温度数据与实际温度测试数据进行对比，并根据对比结果中的温度差异值对相应机架间的乳化液参数进行修正，直至温度差异值小于预设阈值，得到修正后的温度预测模型，能够用于实现硅钢冷连轧轧制过程中，任意采样点硅钢温度的获取。

本发明公开了一种电力变压器硅钢片自动叠片生产设备，包括支撑板和叠片立板，其中一组所述支撑板的表面安装有叠片立板，另一组所述支撑板的顶部安装有检测立板；所述叠片立板的背面安装有连杆，所述连杆的尾端连接有限位环，所述限位环的内部等距贯穿安装有第一电动伸缩杆，所述第一电动伸缩杆的尾端表面套接有橡胶套，所述叠片立板的背面设有滑槽，所述滑槽的底壁安装有缓冲弹簧，所述滑槽的顶壁安装有第二电动伸缩杆，所述第二电动伸缩杆的尾端连接有拦截条，两组所述支撑板的顶部均安装有立块。本发明通过设置有叠片立板、限位环、拦截条以及缓冲弹簧的配合，可简化本叠片设备的整体占地面积，简化叠片加工程序。

对冷轧无取向硅钢在冶炼过程中各个工序的顶渣进行了检测,分析了顶渣变化原因,并得出结论:硅钢生产宜采用复吹转炉,以降低吹炼终点渣中TFe含量,进而减轻对精炼的压力;使用低S、低Al2O3含量中间包覆盖剂;RH脱氧及合金化顺序采用先加硅铁后加铝;首罐宜经LF提温并降低渣中TFe。 The top-surface slag used for the various production processes in smelting coldrolled non-oriented electrical steel is tested and based on tested results the cause of the top surface slag change is analyzed.So it is concluded that the combined blown converter is more suitable to be used for smelting electrical steel in order to reduce the content of TFe in slag at blow end point and then much better results can be achieved during the period of refining.Secondly the tundish flux contenting low co... 

本发明公开了一种适应高频率工况下低铁损无取向电工钢及其生产方法，所述生产方法包括以下步骤：钢水连续浇铸成板坯—热轧—正火—酸洗—冷轧—连续退火—涂绝缘涂层并固化；所述冷轧步骤中，采用六辊单机架往复式轧机经5道次一次冷轧至目标厚度，冷轧过程中前三道次采用变速异步轧制方法，使钢板表层在剪应力作用下位错密度增加，这样在退火后表层晶粒尺寸细化而心部晶粒粗大，通过本发明的方法可生产得到心部为粗大等轴晶粒，表层为纳米级细等轴晶粒的电工钢产品，该产品的铁损P1.5/50≤2.35W/kg，P1.0/400≤14.0W/kg。

通过金相分析和电子背散射衍射技术研究了一种新型含铜无取向电工钢在950℃退火不同时间(3～180s)空冷后的组织和织构取向的演变。结果表明:该钢在退火3s时的主要织构为α和γ线织构,{100}<110>织构最强;退火20s时织构以<111><112>、{111}<110>、{112}<110>、高斯织构和立方织构为主,随着退火时间的延长,高斯织构和立方织构强度呈减弱趋势;合理控制保温时间有利于提高{100}、{110}面织构的占有率。 Evolution of microstructure and texture oriented of a new non-oriented electrical steel during annealing at 950℃for different times(3-180) s and air cooling was studied by metallography and electron back-scattering diffraction analysis.The results show that after annealing for 3 s most of the texture oriented alongα-fibre andγ-fibre,the intensity of {100}〈110〉was the strongest.{111}〈112〉,{111}〈110〉,{112}〈110〉,Gauss texture and cube texture were the main texture after annealing for 20 s,with the ... 

对应用动态加热进行短时温度退火的取向电工钢进行了二次再结晶研究。所进行研究的实验用取向电工钢是经过终冷轧和后续罩式退火后的一条工业化生产线生产的。研究结果表明,运用短时热处理条件可引起研究钢完全的异常晶粒长大。在实验室处理的材料的织构和金相组织与工业化生产的经过终退火而获得的相同的取向电工钢类似。但是,在实验室处理的取向电工钢的二次再结晶的矩阵中可观测到\"寄生\"晶粒。从磁性观点看,这些\"寄生\"晶粒含有不理想的{111}取向织构。 The present study was made to investigate secondary recrystallization in grain-oriented steels annealed at short time temperature exposures with application of dynamical heating.The investigated GO(Grain Oriented) steels for experiments were taken from one industrial line after final cold rolling reduction and subsequent box annealing.It was shown that application of short time heat treatment conditions could lead to complete abnormal grain growth in the investigated GO steel.The texture and mic... 

本实用新型涉及硅钢片钢卷制造技术领域，且公开了一种用于硅钢片钢卷制造的收卷装置，解决了现有硅钢片钢卷制造过程中不便于更好的进行收卷的问题，其包括收卷辊，所述收卷辊的两侧边均对称安装有固定连接杆，固定连接杆远离收卷辊的一端安装有连接板，连接板远离固定连接杆的一侧边中部安装有连接轴，收卷辊的顶部与底部均对称连接有活动挡板，收卷辊的内部开设有安装槽，安装槽的内部安装有调节机构，且调节机构与活动挡板连接；本实用新型，便于能够确保在收卷过程中硅钢片钢卷不会发生偏移，以便于能够达到更好的收卷效果。