本实用新型公开了一种薄带取向电工钢的热处理炉板，炉板的中心设置有气流循环通孔，炉板的硅钢卷预定压接面设置有通气槽，炉板内设置有进气孔，进气孔的第一孔口设置于通气槽中，进气孔的第二孔口设置于炉板的侧壁上。该薄带取向电工钢的热处理炉板在设置通气槽的基础上，进一步设置进气孔，通过向进气孔中导入气流，增加通气槽的进气量，有助于硅钢卷与炉板压接侧边处水蒸气的及时排出，进一步提高卷内硅钢的热处理品质。本实用新型还公开了一种包含热处理炉板的薄带取向电工钢罩式炉。

以构建高磁感、低铁损、免轧制高硅电工钢铁芯为出发点,提出采用单辊甩带制备非晶铁硅合金薄带、微氧化法在铁硅合金粉末表面包覆高电阻率铁硅氧化物薄膜制备核壳异质结构高硅电工钢纳米粉末、放电等离子烧结快速成形制备颗粒间绝缘的高硅电工钢铁芯。研究了不同氧化包覆时间对SPS烧结试样密度、物相组成、微观结构和静磁性能的影响。研究表明,在氧化包覆5h烧结温度800℃工艺条件下,制备的6.5%Si高硅电工钢铁芯的静磁性能最佳,饱和磁化强度为128.84A.m2/kg、矫顽力为2.25kA/m、剩磁为3.47A.m2/kg。其饱和磁化强度与粉末压延法制备的高硅钢相当,但矫顽力降低了1/3。 The paper takes preparation 6.5%Si steel with high induction,low core loss and removing rolling as the starting point,amorphous Fe-Si ribbons was synthesized by melt spinning method,6.5%Si steel nanopowders with high resietivity core shell structure was prepared by the slight oxidation process and 6.5% Si steel iron core with evaluating internal was sintered by spark plasma sintering process(SPS).The essay focuses studies the effects of different oxidation cladding time on sample density,phase c... 

本实用新型公开了一种硅钢片分流导料机构，属于硅钢片导料领域，包括传送带，所述传送带包括主带和副带，所述副带设置在主带的前面，所述主带横向设置，所述主带的后面设置有导流机构，所述导流机构包括电机、导流板和助力组件，所述主带的后面设置有安装架，所述安装架的顶部竖向固定连接有连接板，所述电机安装在连接板上，所述电机的输出轴与导流板的顶部固定套接，通过启动电机，电机带动导流板旋转，导流板在连接组件下带动助力组件旋转，使得主带上的物品被导流板进行阻挡，通过助力组件传送到副带上，避免了传送带方向单一，容易导致硅钢片对堆积的问题，从而减少硅钢片的损坏量，进而节约成本。

本发明提供了一种无取向电工钢，包括：C0.001～0.010％，Si0.5～4.0％，Mn0.05～0.8％，Al0.2～1.5％，P≤0.002％，S≤0.0015％，O≤0.002％，N≤0.0015％，各成分均为质量百分比；还提供一种无取向电工钢制造方法，包括：冶炼钢水、薄带连铸、常化酸洗、冷轧以及退火涂层。本发明中，在冶炼钢水时，控制钢水中C、Si、Mn、Al、P、S、O以及N几种成分的含量，且通过常化工艺，可以有效控制无取向电工钢成品的产品质量，具有较低的铁损以及较高的电磁性能，另外整体制造流程比较短，能够达到节能环保的目的，而通过冷连扎，有利于提高产品的质量、成材率和生产效率。

考虑剪应变对微孔洞损伤演化的影响,对GTN损伤模型的损伤演化机制进行修正,建立了适用于不同应力三轴度水平的损伤模型。结合隐式应力更新算法和显式有限元计算,采用VUMAT子程序实现了修正GTN模型在有限元软件ABAQUS中的数值计算。通过模拟纯剪切和剪切-拉伸两组试样的损伤演化和断裂行为,验证了修正GTN模型在不同应力三轴度承载条件下的有效性。运用修正GTN损伤模型模拟含边部缺口的带钢在轧制过程中裂纹的萌生和扩展行为,模拟结果与实验相一致,表明该模型可有效地用于带钢缺陷在轧制过程中扩展行为的分析和预测。模拟和实验结果表明,带钢边部缺口在轧制过程中,缺口前沿和后沿均会萌生裂纹,且后沿裂纹扩展更为明显。 Considering the effect of shear strain of micro-void on damage evolution, a modified GTN model applicable to various stress triaxiality conditions is proposed by modifying the damage evolution mechanism of the GTN damage model. The modified model is implemented in commercial finite element software ABAQUS by combining the implicit stress update method with an explicit finite element solving algorithm and through the user-defined material subroutine VUMAT. The damage evolution and the failure pro... 

一种硅钢生产线退火炉前的换热装置，包含有抽风机（1）、立柱（2）、热交换器（3）、软管（4）和热风机（5）；其特征在于：所述的热交换器（3）由若干组U形不锈钢管连接而成，一端固定在轴套（8）上，另一端通过链条（10）连接在立柱（2）顶端的链条盘（9）上，当链条盘（9）转动时，链条（10）拉动热交换器（3）绕着横轴（7）抬起或放下。本实用新型通过抽风机（1）将清洁空气抽到热交换器（3）内进行加热，然后再通过软管（4）将热空气输送到热风机（5）内来加热硅钢板（14），有效的利用了热能，避免了凝露导致的板面发蓝现象。

通过对3%Si CGO硅钢进行恒变形速率、不同变形温度下的单道次压缩实验,结合Thermal-Calc软件,金相分析,SEM及EBSD技术,研究了取向硅钢热变形过程中组织和微观织构的变化规律。结果表明:实验钢是在双相区变形,变形后组织主要是铁素体和少量的珠光体。随变形温度的升高,晶粒由长条状变为等轴状,尺寸逐渐变大;CGO硅钢在热变形过程中立方{100}<001>取向是较为稳定存在的。随着变形温度的提高,{111}<110>等取向逐渐转向{110}<1 10>取向,且{110}<1 10>取向逐渐变得锋锐。 3% Si CGO silicon steel was studied at constant strain rate and different deformation temperatures by single-pass compression deformation experiments to reveal the evolution of microstructure and texture during thermal deformation in oriented silicon steel,and the Thermal-Calc software,metallurgical,SEM and EBSD technique was used in the experiment. The results show that experimental steel is deformed at the temperatures of two-phase zone. The microstructure of the deformed steel consists of fer... 

通过后天抑制剂获得法制备了取向硅钢,对渗氮前后和高温退火升温阶段析出物的析出和转化规律进行了研究。研究结果表明,渗氮前脱碳退火态基体中存在少量的粗大AlN颗粒和细小AlN颗粒,渗氮处理后新析出大量的Si3N4析出物,高温退火升温阶段Si3N4将转化为(Al,Si)N,随着温度的继续升高(Al,Si)N颗粒将发生粗化,(Al,Si)N是后天抑制剂获得法制备取向硅钢的主要抑制剂。 Grain-oriented silicon steels were produced by acquired inhibitor method.The rule of precipitate transformation was studied after nitriding treatment and high-temperature finishing annealing.The results show that a small amount of large AlN and fine AlN are found in matrix before nitriding treatment,and a large amount of Si3N4 is precipitated in matrix after nitriding treatment.During the temperature rising period of high-temperature finishing annealing,Si3N4 would transform into(Al,Si)N,and(Al,... 

利用EBSD技术对CGO硅钢热轧、中间退火、脱碳退火及二次再结晶退火组织及织构进行分析,研究了CGO硅钢各阶段加工制备过程中高斯{110}<001>晶粒的形状、尺寸及分布特点,分析了高斯取向晶粒在各工序过程中的遗传继承性特点。结果表明,CGO硅钢热轧板的次表层存在Goss取向晶粒,历经一次冷轧及中间退火后Goss取向晶粒基本消失,一次再结晶之后Goss织构仍不是主要织构,主要织构为{111}<110>和{111}<112>,说明Goss取向晶粒在二次再结晶退火前数量及尺寸上并不占优势,二次再结晶过程中Goss取向晶粒异常长大形成锋锐Goss织构。{111}<110>和{111}<112>织构组分的强度在一次冷轧中不断增加,{111}<112>织构组分的强度在二次冷轧后达到最大而{111}<110>织构组分是在初次再结晶后变强。 Grain shape,size and distribution of { 110} < 001 > Goss grains in CGO steel and the hereditary characteristics of Goss orientated grains during each processing period were investigated,based on the analysis of the microstructure and texture of the CGO silicon steel during hot rolling,intermediate annealing,decarburizing annealing and secondary recrystallization annealing by means of EBSD. The results show that Goss orientated grains exist in the subsurface of the hot rolled plate,and Goss... 

本实用新型公开了一种变压器铁芯硅钢片叠装对齐工装，包括叠装平台、定位板、推齐板和下压板；定位板和推齐板分别位于叠装平台的两侧，下压板位于叠装平台的上方；定位板用于对铁芯长度或宽度侧进行定位；推齐板平推铁芯使各硅钢片抵靠定位板而对齐；下压板下压铁芯使各硅钢片叠装紧密。本实用新型提供的一种变压器铁芯硅钢片叠装对齐工装，能够提高铁芯生产精度，并提高硅钢片叠装效率。

本实用新型属于清洁度检测装置领域，具体的说是硅钢前处理带钢表面清洁度在线检测系统，包括操作台和清洁单元；所述清洁单元设置在操作台的端部；所述操作台的端部固接有支撑腿；所述支撑腿的端部固接有顶板；通过设置的清洁单元，对工业相机的镜头表面进行清洁，转动轮盘调节角度，推动推板将水箱内部的水分喷洒在镜头的表面，按压连接杆的端部，橡胶柱和弹簧受力，使用刮板对镜头的表面进行刮擦清理，将镜头的表面灰尘清理干净，避免了灰尘堵塞镜头，影响拍摄效果。

本发明提出一种预判取向硅钢冷轧脆断发生的方法，将酸洗带头20‑30cm进行剪切取样，在取到的样板上面注明工作侧和传动侧；将取好的样板送至焊缝检测冲压机处，通过冲压机对样板进行冲压，根据不同钢带厚度，设定不同冲孔机压力，对样板进行冲压后，通过观察裂纹形貌，预判常化卷在冷轧轧制过程中是否会发生脆断，本发明使带钢在冷轧前能够制定相应的对策措施，从而降低冷轧断带所产生的损失。