硅钢资料

【作者】 刘玲月； 李军辉； ...

本文中简要介绍了武汉钢铁有限公司采用薄板坯连铸连轧CSP(compact strip production, CSP)工艺生产中低牌号无取向硅钢的实践情况.CSP工艺生产的硅钢具有成品磁性均匀、板形好的优势，但是在利用该技术生产中低牌号无取向硅钢时，常存在成品板表面瓦楞状缺陷严重、连铸生产效率低等问题.通过优化炼钢成分、热轧等相关工艺，可消除热轧板厚度方向中心的粗大形变组织，从源头上避免了粗大{100}<011>纤维组织的出现，消除了瓦楞状缺陷；通过提升冶炼效率和控制钢中夹杂物总量，可优化隧道炉的加热温度与在炉时间，大幅度提升了连铸生产效率，实现了中低牌号无取向硅钢的批量稳定制造，使CSP产线成为中低牌号无取向硅钢热轧板原料的主要供给生产线.如何进一步提升钢水纯洁度、提高连铸生产效率、降低生产成本，以及挖掘该产线生产薄带钢的技术优点，是未来工作的重点. This paper briefly introduces the practice of producing medium and low grade non oriented silicon steel(NGO) with CSP(compact strip production, CSP)technology in Wuhan Iron and Steel Co., Ltd.. This technology has the inherent advantages of uniform magnetic properties and good shape for silicon steel finished strip. However, in the actual production process, there are serious corrugated defects on the surface of silicon steel finished strip, and production efficiency of continuous casting is low... 

本发明公开了一种低牌号无取向电工钢的制造方法，包括：在炼钢时，增加所述低牌号无取向电工钢的板坯的铝元素含量，增加量按重量百分比计为0.08％～0.12％；在热轧板坯加热时，控制所述板坯的出炉温度为1150℃～1200℃；在热轧粗轧时，控制所述板坯的粗轧RT2温度为1000～1050℃；上述方法通过提高铝含量，以升高低牌号无取向电工钢的相转变温度，再结合板坯的出炉温度控制和粗轧RT2温度控制，保证低牌号无取向电工钢在精轧过程中不会因为相变区轧制而产生轧制力波动，从而稳定精轧轧制过程，提高精轧后低牌号无取向电工钢板卷的尺寸和板型精度。

对无取向硅钢炼钢全流程钢液增钛的原因进行了分析,认为铁水钛含量、转炉出钢温度、转炉下渣量、精炼渣TiO₂含量、钢水罐及RH浸入管混钢种生产是影响钢液增钛的主要原因。通过采取低钛铁水冶炼,减少转炉下渣量,提高出钢温度,添加白灰改质精炼渣等措施,均能够降低钢液中的钛含量。 After analyzing the causes leading to increased content of titanium in molten nonoriented silicon steel during whole steelmaking process, it was concluded that such factors as content of titanium in hot metal, tapping temperature from converter, quantity of roughing slag entered into the ladle from converter, content of TiO₂ in refining slag, molten steel ladle car,carrying out the steelmaking of different steel grades by the same ladle and same RH immersion tube were the main causes ... 

本发明涉及取向硅钢技术领域，且公开了一种气耗优化成本较低的取向硅钢高温退火工艺，包括如下步骤：S1、将铸坯装炉装炉前先对炉台利用高压空气进行清扫，将通气管内的粉尘或其它杂质吹扫干净，然后根据钢卷的卷径大小选用与之匹配的料盘和料筐，将铸坯放入炉内；S2、炉台密封将装有铸坯的炉台完全密封。该种气耗优化成本较低的取向硅钢高温退火工艺，在高保温阶段使用氨分解气，而氨分解气相对氢气而言比较稳定，在生产成本上也较氢气低，大大的降低了成本节约了能耗，在低保温阶段是为了消除应力，形成一次再结晶晶粒，进行脱碳，高保温阶段二次再结晶，净化钢质和形成烧结硅酸镁底层，最后退火完成后，完成烧结绝缘涂层、热拉伸平整。

本发明提供一种无取向硅钢低温无铬环保绝缘涂层立式干燥固化工艺，冷轧无取向硅钢在镀锌机组经过退火后，通过涂层机涂覆低温无铬环保绝缘涂层，再经过立式干燥炉完成干燥固化，生产冷轧无取向硅钢产品。低温无铬环保绝缘涂层厚度0.8~1.0μm；立式干燥炉各段炉温：加热一段炉温420~450℃，加热二段炉温460~490℃，加热三段炉温500~530℃，加热三段出口板温200~240℃，冷却段出口板温60~65℃；立式干燥炉各段加热时间：加热一段、加热二段、加热三段的加热时间均为3.5~4s。采用本发明工艺不仅能保证钢带涂层均匀，使最终产品的涂层具有优异的绝缘性、耐蚀性、附着性、冲片性、焊接性和耐热性，满足下游工序要求，还可提高产品合格率，减少废品，保证生产顺行。

硅钢连续退火线是无取向硅钢生产的成品线。由于受机组布置的影响,带钢经转向辊进出口活套后,当套量达到60%后就出现偏离生产线的情况,从而影响最终产品的质量及成材率,甚至损坏设备。针对某冷轧厂硅钢连续退火机组出口活套入口处带钢跑偏开展纠偏研究,利用Matlab对该纠偏系统进行动态仿真研究,分析系统的稳定性。 Silicon steel continuous annealing line is non oriented silicon steel production of finished product line.Due to the influence of unit layout,strip by roll Import & Export loop,when the set volume reached 60% after the emergence of deviation from the production line,thus affecting the quality of the final product and the rate of finished products,and even damage the equipment.For the export of continuous annealing line in cold rolling silicon steel strip deviation rectification loop at the e... 

无取向硅钢的磁性能主要取决于铁素体的晶粒尺寸、晶体织构和钢中的夹杂物。通过合适的化学成分设计以及采用适宜的夹杂物控制技术,可以获得最佳的夹杂物控制效果,使其纯净度大幅度提高或者无害,最终获得磁性能优良的高级别无取向硅钢。同时,为满足节能、环保、高效需求,无取向硅钢正朝着节能降耗、环境友好以及多功能、高效率、易加工等方向发展。 The magnetic properties of non-oriented silicon steel mainly depend on the grain size of ferrite,the crystallographic texture,and the inclusions in the steel.The optimum inclusion control effects can be obtained through a suitable chemical composition design and an appropriate inclusion control technique,and then the liquid steel will get be clean or the inclusion will get be harmless,finally the excellent magnetic property of the non-oriented silicon steel can be obtained.Meanwhile,in order to ... 

本发明涉及磁悬浮电机轴硅钢片叠压领域，尤其涉及一种永磁电机内嵌式硅钢片的叠压装置、叠压工装及方法和磁悬浮鼓风机。该装置包括带槽钢板和多个长钢板；带槽钢板设置有转轴孔，转轴孔面积大于电机转轴套合硅钢片部分的截面积并且被电机转轴穿过；多个长钢板底端分别与带槽钢板相连接，并且带槽钢板上表面与硅钢片相贴合；多个长钢板竖直分布并且其分布位置与硅钢片中的多个磁钢槽相对应，长钢板外表面与硅钢片中的磁钢槽相配合。该装置通过对硅钢片的磁钢槽进行定位，保证叠压后的硅钢片的磁钢槽对齐，提高硅钢片内嵌磁钢质量。

本实用新型公开了一种生产硅钢片的轧制装置，包括工作台，所述工作台的正面开设有收集腔，收集腔的内底壁滑动连接有收纳盒，工作台的上表面分别固定连接有两个支撑板和倒L型滑动台，两个支撑板的相对面分别转动连接有上压辊和下压辊，上压辊的外表面套设有两个调节环，两个调节环的相对面均固定连接有切刀，工作台的上表面开设有与收集腔相连通的下料孔，下料孔的内侧壁开设有滑动槽。该生产硅钢片的轧制装置，通过设置上压辊、下压辊与驱动电机，便于对硅钢片进行传动，通过设置调节环、切刀与固定螺栓，便于根据生产需求调节硅钢片切边的距离，从而使整个装置具有方便对轧制后硅钢片进行切边处理的效果，方便后续轧制工作的进行。

本发明提供了基于硅钢片性能的分类方法、系统、计算机和存储介质，通过抽样选取待分析硅钢片，获取待分析硅钢片的基准B‑H曲线和基准B‑P曲线，以及通过预设检测方法测得待分析硅钢片的样本B‑H曲线和样本B‑P曲线后，根据预设磁通密度监测范围分别选取基准B‑H曲线、基准B‑P曲线、样本B‑H曲线和样本B‑P曲线对应的B‑H基准样本点、B‑P基准样本点、B‑H待分析样本点和B‑P待分析样本点，并基于依此分别得到B‑H样本点距离与B‑P样本点距离分析待分析硅钢片的性能，以及根据分析结果对待分析硅钢片进行分类的方法，基于性能曲线的数据分析对硅钢片性能进行合理的评估分类，不仅实现了对硅钢片质量的有效监控，而且为其使用策略的制定提供可靠依据，保证产品质量的同时，为产品用料选择提供便利。

研究了常化对CSP流程生产的wSi=1.6%的无取向电工钢组织、织构和成品磁性能的影响。结果表明,经CSP流程生产,且在相同的冷轧及退火制度下,经1 000℃×2min常化处理的wSi=1.6%的无取向电工钢热轧板,其最终退火成品的铁损P15/50比不常化试样下降了10.5%,磁感B50比不常化试样提高了2.5%;常化使wSi=1.6%的无取向电工钢成品的平均晶粒尺寸增大,成品铁损P15/50相应减小;同时,常化使wSi=1.6%的无取向电工钢成品中高斯织构的强度增加,γ纤维织构的强度减弱,这有利于成品磁感B50的提高。 The effect of normalizing on microstructure,texture and magnetic properties of non-oriented electrical steel with wSi=1.6% produced by CSP process was investigated.The results show that,under the same cold rolling and annealing system,the iron loss(P15/50) of annealed samples whose hot bands has been normalized by 1 000 ℃×2 min process decreases by 10.5% and magnetic induction(B50) increases by 2.5% compared with the samples whose hot bands was not normalized.The average grain size of non-orient...