本发明公开了一种高强度碳化硅钢球，所述高强度碳化硅钢球包括以下重量份的原料：碳化硅20‑30份、铬1‑2份、氮化硼3‑5份、铁10‑20份、钼2‑3份、锰钢30‑40份、镍5‑8份、钛6‑8份、磷2‑3份、硫2‑3份；一种高强度碳化硅钢球制备方法，包括如下步骤S1、熔融；S2、模锻成球；S3、打磨；S4、二次加热；S5、高温淬火；S6、机油回火；S7、检测成品。本发明制备的高强度碳化硅钢球具有抗折强度高、洛氏硬度高及抗压强度高等优异的机械性能，并且使用寿命长，运转精确度高，并且其工艺简单，生产耗能低，无“三废”产生，环保性高。

研究了激光加热辅助圆盘剪高速切割技术,以解决现有冷轧生产线硅钢切边技术存在的微裂纹、应力、毛刺和边浪等问题。建立了激光加热温度场有限元分析模型,根据生产线上圆盘剪加工的实际过程,探讨了数值模拟中热源的加载形式,研究了激光对板材进行辅助加热时各个工艺参数如激光功率、光斑尺寸以及激光入射角度对切割工艺的影响,并通过实验对工艺参数进行了优化。最后,进了验证实验。实验结果显示:当激光加热点运动至圆盘剪刃口位置时,温度为100℃左右,此时材料硬度降低到原有硬度的70%~80%,降低了切削力,减少了圆盘剪的磨损,可有效提高圆盘剪的寿命。 Laser assisted trimmer side cutting technology was studied to overcome the problems such as micro cracks,stress,burrs and edge waves existing in a cold rolling production line of silicon steel side cutting.A finite element analysis model for the laser hearting temperature field was established, the loading form of a heating source was determined and influences of various processing parameters like laser powers,spot sizes,and laser incident angles on laser assisted heating sheet materials were di... 

本申请涉及一种中温普通取向硅钢及其制备方法，依次包括加热、除鳞、控制轧制、控制冷却、卷取；加热、控制轧制、控制冷却、卷取过程中分别控制硅钢边部组织类型、边部脱碳宽度、边部晶粒大小，从而降低了后续冷轧工序的裂口率和提高了成材率。本申请提供的一种中温普通取向硅钢的制备方法，通过改善加热炉气氛、优化控制轧制工艺、优化控制冷却工艺以及调整板坯的装钢间距。制备后的硅钢边部硬度明显降低，在后续冷轧工序中，严重裂口率显著降低。

本实用新型提供了一种带有可回收再利用功能的冷轧硅钢卷捆扎装置，底座上设有安装块一，加紧装置一安装在安装块一上，加紧装置一包括外壳，外壳内设有凹槽一，凹槽一内设有通口，凹槽一内设有气缸，气缸一端设有夹块，气缸一侧设有挡板，挡板安装在凹槽一上，外壳上设有凸块，硅钢卷进行捆扎，可以重复利用，加紧装置一与加紧装置二可以把硅钢卷两端进行固定吗，里面安装的气缸可以加紧硅钢卷，安装的吸盘可把加紧装置二的位置提高，方便进行固定上端，安装的承重块可以起到防止倾斜的作用，在不使用的时候加紧装置一与加紧装置二之间可以通过卡扣之间的连接进行固定。

本实用新型涉及一种方便叉车转运的硅钢卷，属于硅钢卷技术领域。包括卷盘、转轴、支撑板、底座和叉车叉座，所述卷盘与转轴固定，所述支撑板为两件，对称布置在底座上，支撑板上设有卡槽，转轴安装在卡槽内，所述底座的下方设有两个对称布置的叉车叉座，所述叉车叉座上设有供叉车叉板插入的叉板槽；本实用新型硅钢卷通过可拆卸安装在带叉车叉座的支撑架上，在实际生产中，通过叉车就可以很方便地实现在车间复杂环境下转运，快速灵活，提高了工作效率。

本发明揭示了一种无取向硅钢的生产方法。所述生产方法中：按照Si:0.3～1.2％炼钢、制坯；将铸坯加热到1050～1150℃并保温150min以上，而后轧成厚度40～45mm的中间坯，再经精轧、卷取得到厚度为3.00±0.25mm的热轧卷板，精轧开轧温度≤Ar1＝872℃+1000*(11*[Si]‑14*[Mn]+21*[Al])；当Ar1≥1000℃，终轧温度T≤840℃，否则T≤Ar1‑160℃；卷取温度≤550℃；经常化、酸连轧得到0.500±0.005mm的冷硬卷，常化温度为850～950℃；退火温度820～950℃，经成品退火、冷却、涂层和精整，得到无取向硅钢成品。

​6月28日国联证券发布：《电力设备出海2024年中期投资策略：需求方兴未艾，供给释...

电动汽车电机在高速旋转时承受离心力和电磁力的作用,在进行电机转子设计时,既要考虑电磁性能,还要考虑机械性能。对电机转子受力情况进行了综述,分析了转子用电工钢疲劳性能参数的重要性,详细阐述了试样抛光、表面处理、试样的对中和安装对测试结果的影响。 The motor of electric vehicle bears big force for high speed rotors,mainly including centrifugal and electromagnetic forces.The magnetic and mechanical aspects of the electrical steel are crucial to machine design.In this paper,the forces applied on the motor were summarized and importance of fatigue properties was analyzed.The influence of specimen polish,surface treatment,alignment and installation on fatigue testing result were represented in detail. 

【摘要】 <正>3月底,宝钢\"低温高磁感取向硅钢制造...

系统研究了无取向硅钢用磷酸盐系涂层性能的影响因素。以氢氧化铝和磷酸为原料制备磷酸二氢铝,再添加适量的添加剂酒石酸铵、二氧化硅、环氧树脂,得到的涂液涂布于硅钢表面,并控制合适的烘干温度,通过耐盐雾实验考察各因素对涂液耐腐蚀性能的影响。实验结果表明,在磷酸与氢氧化铝物质的量比为3.4∶1、酒石酸铵用量为2%、二氧化硅用量为1%、环氧树脂用量为5%、烘干温度为300℃条件下,所得涂层材料的防(耐)腐蚀效果最佳。 The factors influencing the performance of phosphate anticorrosive coating for non-oriented silicon were systematically studied.Aluminum dihydrogen phosphate was prepared with aluminum hydroxide and phosphoric acid as raw materials.Then added the right amount of additives,such as ammonium tartrate,silicon dioxide,and epoxy resin to prepare the liquid coating,which was coated on the surface of the silicon steel,and finally controlled a suitable drying temperature.The influences of various factors... 

本发明公开了一种耐热刻痕型取向硅钢涂层用涂液，其溶剂为水，其含有：磷酸盐、胶态二氧化硅、铬酐和乙醇。本发明还公开了一种耐热刻痕型取向硅钢板，其包括基板，所述基板表面具有采用上述的耐热刻痕型取向硅钢涂层用涂液涂覆在基板上而形成的涂层。相应地，本发明还公开了上述取向硅钢板的制造方法，其包括步骤：在基板表面涂覆所述涂液，基板的刻痕沟槽涂液填充率＞95％；进行烧结处理，其中烧结处理中的板温为780‑900℃。本发明的耐热刻痕型取向硅钢涂层用涂液具有良好的流动性，其可以涂覆于耐热刻痕取向硅钢基板的表面中，涂覆后，能有效填充基板的刻痕沟槽，且可以在其表面形成涂层，保证耐热刻痕取向硅钢在具有低铁损的同时具备更高的安全性。

研究了CSP工艺流程生产的硅含量为1.5%的无取向电工钢在不同常化温度下对磁性能的变化。研究结果表明:随着常化温度的提高,热轧板的晶粒尺寸增大,且组织均匀性提高;此外成品的有利织构组分{100}<0vw>、α、η增强,不利织构组分减弱;铁损P1.5/50呈下降趋势,磁感B50上升平缓。在常化工艺为970℃×2.5min下,对应的铁损P1.5/50<3.4W/kg,磁感B50>1.74T。 The effect of normalizing temperature on the magnetic properties of non-oriented electrical steel containing 1.5%silicon produced by CSP process was studied.The results show that with increasing normalizing temperature,the average grain size of hot-rolled plate increases and the microstructure uniformity is improved.Furthermore,the texture components of finished products are improved through enhancing of{100}<0vw>,αandηtextures and weakening of{111}<112>texture;the core loss P1.5/50 ...