为了确保硅钢铬酸盐涂料的环保性,需要严格控制涂料的固化工艺,保证涂料固化过程中涂料中的六价铬充分转化为三价铬。对涂料及原料进行热重分析(TG)及差示扫描量热法分析(DSC)。结果表明,MgO与铬酐混合转化为MgCrO4,使六价铬稳定性增强,其中大部分Cr6+转变为Cr3+发生在620~700℃,在450~500℃高于铬酐发生大量失重,因此必须加入还原剂保证涂料中六价铬被充分还原;超过360℃后树脂会发生分解,因此实际板温不能超过360℃;加入了还原剂的整体涂料的失重温度区间主要在260~320℃,因此涂料固化时钢板的实际温度最佳区间为320~360℃。 Because of the silicon steel chromate coating’s environmental requirements,the paint curing process must be controlled strictly to ensure all Cr( Ⅵ) transforms to Cr( Ⅲ). The TG and DSC analyses of the paint are studied. The reaction of MgO and CrO3 would generate MgCrO4,enhancing the stability of Cr( Ⅵ). The most r( Ⅵ) in MgCrO4 changes to Cr( Ⅲ) at 620-700 ℃,while the CrO3 has a large weight loss at 450-500 ℃. The reductant must be added in the paint to make sure the Cr( Ⅵ) could transform suf... 

森吉米尔二十辊轧机是冷轧电工钢的主要机型,具有整体刚度大,辊径小,轧制道次压下量大,产品精度高等特点,简要介绍了近年来冷轧电工钢森吉米尔二十辊轧机领域进展,在轧机结构、厚度自动控制、板形自动控制等方面的技术及研究。 20-h Sendzmir reversible mill is the main type of cold rolled electrical steel which has the characteristic of high integral stiffness,small roller diameter,high pass reduction and high product quality.In this paper,the recent progress of frame structure,automatic gauge control,automatic flatness control of Sendzmir mill is introduced. 

稀土元素在许多钢中发挥着独特而且不可替代的重要作用。半个世纪以来,它的作用已经在各种低合金和特殊合金钢中的研究及应用中得到充分的证明;然而,作为具有稀土资源优势的中国,在属于重要功能材料的无取向电工钢中稀土的应用却落后于国外,本文就中国稀土在无取向电工钢中的应用研究作简要的评述,希望能够进一步推进此领域的研究,并且促进中国稀土在无取向电工钢中应用技术的发展,缩短与国外差距,并提出了在此应用领域今后需深入开展的研究方向。 Rare earth elements play a unique and irreplaceable role in a lot of steels,it has given the full proof by the practice of various low alloy steels and special alloy steels since half century.However,as our country has the advantage of rare earth resources,RE application technology in non-oriented electrical steels has lagged behind abroad.The application researches of rare earth in non-oriented electrical steel in our country are briefly reviewed in this paper,which hope to promote the research... 

本发明涉及冶金技术领域，具体涉及一种硅锰镇静无取向硅钢的生产方法及浸入式水口。本发明提供的硅锰镇静无取向硅钢的生产方法，包括如下步骤：1)转炉出钢：转炉出钢后对钢水进行真空抽渣，抽渣结束后向钢水中加入石灰、萤石造渣，待渣料熔化后将钢水运至RH工位处理；2)RH真空精炼：将运至RH工位的钢水通过RH真空精炼处理后进行破空、出钢，出钢后在钢包渣面加入渣面脱氧剂以对炉渣进行扩散脱氧；3)连铸浇注：对加入渣面脱氧剂的钢水采用浸入式水口进行浇注。本发明提供的生产方法可有效改善浸入式水口的侵蚀状况，提高浸入式水口的使用寿命，增加连浇炉数，进而提高连铸坯质量稳定性，降低生产成本。

本发明公开了一种基于机器视觉的高牌号冷轧硅钢孔洞检测系统。该系统包括：线扫光源、线阵相机、速度检测模块和工控机；线扫光源安装在钢板生产线中钢板的下方，且线扫光源的光线能够对准钢板和线阵相机；线阵相机安装在钢板的上方，且与工控机连接，用于连续扫描钢板以获取连续的钢板图像；速度检测模块与线阵相机连接，用于检测钢板的移动速度，线阵相机能够根据钢板的移动速度调整行频；工控机用于根据钢板图像检测钢板是否存在孔洞。本发明的基于机器视觉的高牌号冷轧硅钢孔洞检测系统通过利用线阵相机和工控机能够实现冷轧钢板的孔洞的自动检测，检测效率高，识别精度高，能够降低漏检率和误检率，操作方便，安全可靠。

为了弄清楚高硫硅钢中的硫化物析出行为及其对钢的微观组织和电磁性能的影响，以便为工业化生产制定更为合理的硫含量控制标准和采取更为有效措施减轻炼钢生产的硫含量控制压力，结合0.25% Si 无取向硅钢 ，采用非水溶液电解提取 + 扫描电镜/透射电镜观察相结合的方法 ，研究了0.006 8%、0.010 2%、0.025 5% 和 0.035 3% 硫含量条件下，钢中的硫化物夹杂物组成和存在形式及其形貌、种类、尺寸、数量变化，以及相应的热轧、成品试样的微观组织和电磁性能变化。结果表明，随着钢中硫含量的增加，钢中的硫化物逐渐由 MnS→MnS+Cu₂S→Cu₂S转变，数量逐渐增多，尺寸向高低两个方向发展。相应地，导致热轧再结晶组织劣化和抑制了成品晶粒尺寸长大。随着钢中硫含量的增加，钢的磁感、铁损劣化程度逐渐增大。钢中的硫含量平均每增加 0.01%，涡流损耗、磁滞损耗分别劣化0.24 W/kg 和 0.41 W/kg，而磁感会劣化 0.009 T。但是 ，在硫含量为 0.010 2% 时 ，铁损可以低于 6.0W/kg，而在硫含量为 0.025 5% ... In order to find out the precipitation behavior of sulfide inclusions and the corresponding changes of microstructure and electromagnetic properties of high sulfur silicon steel sheets, so that to design more suitable sulfur concentration controlling limit for industrial manufacture and to release the steel-making difficulty effectively, Based on the change of given sulfur concentration 0.006 8%, 0.010 2%0.025 3% and 0.035 3%, the type and composition, the size and number, and the size distribut... 

无氧化炉具有加热效率高、投资与运营成本低、作业率高、表面质量及板型良好、NOx排放相对低等优势,在硅钢热处理领域应用前景广泛。本文阐述了确定无氧化炉(NOF)加热能力详细过程,涵盖炉温、炉断面尺寸、炉长、热平衡结算、加热能力计算等,为今后无氧化炉(NOF)在硅钢热处理应用时的设计提供了借鉴,同时也为今后明火直接加热的工业炉设计提供了参考。 Non-oxidation furnace has the advantage s of high heating efficiency, low investment and operation cost, high operation rate, good surface quality and plate shape, and relatively low NOxemission,and it still has wide application prospect in the field of silicon steel heat treatment. The detailed process of determining the heating capacity of a non-oxidizing furnace(NOF) is described, covering furnace temperature, furnace section size, furnace length, heat balance settlement, heating capacity cal... 

采用自主研发的脉冲磁场退火装置，在取向硅钢脱碳退火过程中分别施加不同强度的磁场，并采用光学显微镜和X射线衍射仪研究了脉冲磁场脱碳退火后试样的显微组织和宏观织构。结果表明，脱碳退火过程中施加脉冲磁场后取向硅钢的平均晶粒尺寸均增加，当磁场强度为40 mT时，平均晶粒尺寸最大，为13.06μm。此外，取向硅钢试样的立方织构{001}<100>强度减弱，高斯织构{110}<001>和{111}<112>织构增强，有利于获得更好的成品织构和磁性能。 Self-developed pulsed magnetic field annealing device was used to apply magnetic field of different intensities during decarburization annealing of an oriented silicon steel, and microstructure and macro-texture of the specimens after decarburization annealing in a pulsed magnetic field were studied by using optical microscope and X-ray diffractometer. The results show that the average grain size of the oriented silicon steel increases with the application of pulsed magnetic field during decarbu... 

本发明相对于板厚较薄的电磁钢板提供不会导致磁特性劣化的基于激光的加工方法。在对电磁钢板进行使用激光的熔断并将该电磁钢板加工成规定的形状的电磁钢板的加工方法中，使上述激光的扫描速度成为10000mm/min以上来进行上述熔断。

本实用新型公开了一种具有防护功能的变压器硅钢剪床，所述辅助机构包括沿着剪切机构前后对称设置的固定架，所述固定架的底部与床台的顶部固定连接，所述固定架上螺纹连接有调节螺杆，所述调节螺杆的底端转动连接有横架，所述横架的底部开设有凹槽，所述凹槽的内部固定连接有固定杆，所述固定杆的外表面固定连接有固定柱，本实用新型涉及剪床技术领域。该具有防护功能的变压器硅钢剪床，通过在固定架、调节螺杆、横架、凹槽、固定杆、固定柱和横杆的配合使用下，对板材进行扶持，降低安全隐患，解决了现有的剪床没有对板材进行扶持的措施，板材掉落不仅会对板材发生损坏，也有可能对工作人员带来伤害的问题。

【作者】 马芳； 张春红； ...

本发明涉及一种用于控制硅钢毛刺状厚度波动的工艺，包括如下步骤；将连铸坯送入加热炉中进行加热，连铸坯入炉温度为400‑680℃，连铸坯在炉时间为185‑220min；将加热后的连铸坯进行热轧，轧辊偏心量为0‑0.025mm，将热轧后的带钢进行卷取；将卷取后的带钢酸洗后进行冷轧，冷轧操作模式由多次阶段升降速模式调整为一次性升降速模式，且在一次性升降速阶段将MN‑AGC增益系数增大；将冷轧后的带钢进行卷取，退火后得到硅钢片成品。本发明所公开的用于控制硅钢毛刺状厚度波动的工艺，该工艺对加热、热轧、卷取及冷轧各工序进行优化协调，能够有效解决硅钢毛刺状厚度波动的问题，实现无取向硅钢全长厚度控制精度的提升，而且无需进行设备和系统改造，容易实现，易于推广。