一种变压器硅钢片转运吊车，属变压器生产技术领域，包括车架、驱动部和承载部，驱动部连接车架和承载部，承载部上承载硅钢片。车架包括底板、支撑单耳、后耳片，底板前端两侧向前上方各延伸一个支撑单耳，支撑单耳连接驱动部，底板的中后部两侧各具有一个后耳片，后耳片也连接驱动部。驱动部包括连杆、底双耳、支撑双耳、轴座、转轴和液压缸，连杆具有一对，连杆下端具有底双耳，连杆的中下部具有支撑双耳，连杆的顶部具有轴座，底双耳铰接在支撑单耳上，转轴安装在两个连杆顶部的轴座上，液压缸的两端分别连接在后耳片和支撑双耳上。承载部包括托盘、侧部耳片、拉杆、下双耳和上挂耳，托盘两侧各具有一对侧部耳片，拉杆呈倒Y字形结构。

研究了罩式炉常化工艺对50W350硅钢热轧板组织、夹杂物和性能的影响。研究结果显示，罩式炉常化工艺在温度一定的情况下，随着保温时间延长，硅钢晶粒逐步再结晶并长大，同时析出物也在聚集长大。通过制定合理的罩式炉常化工艺，可以实现硅钢晶粒的再结晶和长大，从而达到连续退火炉常化工艺产品技术要求。 The influence of normalization process with a bell furnace on the structure,inclusions and properties of 50W350electrical steel hot-rolled sheet was studied.The research results showed that:when the steel was normalized at a certain temperature in the bell furnace,the silicon steel grains gradually recrystallized and grew up with the extension of the annealing holding time,and at the same time,the precipitates also gathered and grew up.The recrystallization and growth of the silicon steel grains... 

该电磁钢板包括母材钢板、第1绝缘被膜及第2绝缘被膜，该第1绝缘被膜被形成于所述母材钢板的第1面，并具有粘结能量，该第2绝缘被膜被形成于作为所述母材钢板的所述第1面的背面的第2面，并具有粘结能量，所述第1绝缘被膜的平均铅笔硬度为HB以上3H以下，所述第2绝缘被膜的平均铅笔硬度比所述第1绝缘被膜的平均铅笔硬度更高。

本发明涉及硅钢片横剪线技术领域，具体为一种用于硅钢片横剪线的冲孔和剪切的数控自动化车床，包括底座，底座的左侧上方与基座的底部上方设置有基座，基座的前侧中部设置有钢片辊，基座的右侧设置有凹槽，凹槽设置在底座内部，凹槽的左右两侧端部设置有齿轮，齿轮的外侧设置有皮带，凹槽的右侧上方设置有挡板，有益效果是：挡板的开口结构，使硅钢片自左向右经过挡板后，会处于底座上方正中间，方便调整硅钢片的水平位置，并使其可以准确进入夹板内部。通过弹簧的弹力作用，控制拉绳的位置，以此来实现拉绳带动夹块的关闭，使绕片筒在转动过程中，夹块可以将硅钢片的端部牢牢固定住。

本实用新型涉及硅钢轧制油反应设备技术领域，尤其是一种硅钢轧制油专用反应装置，它包括反应罐，所述反应罐的内底部焊接有导热板，所述导热板的底面安装有安装壳，所述安装壳的内部固定安装有电热盘，所述反应罐的右侧面底部固定安装有温度传感器，所述反应罐内设置有搅拌机构，本实用新型通过设有温度传感器、电热盘和控制器，能够有效控制反应罐内部的温度，使其内部的温度能够达到设定的温度值，防止因温度过高而爆炸，提高了安全性，而且，通过由搅拌电机、搅拌轴、主搅拌叶、分搅拌叶和螺旋搅拌杆组成的新型搅拌机构，该搅拌机构的搅拌覆盖率大，搅拌效果较好，能够进一步加快物料间化学反应的速率，提高生产效率。

本实用新型公开了一种变压器铁芯硅钢片的收片装置，包括固定平台、硅钢片出料机构、压片机构、支撑平台和升降调节机构，所述固定平台设置在硅钢片出料机构的出料端下方，所述压片机构对应于硅钢片出料机构的出料口设置在硅钢片出料机构的上方，从所述硅钢片出料机构传送出的硅钢片通过压片机构压覆在固定平台上；所述固定平台上设置有升降调节机构，所述升降调节机构的升降端设置有支撑平台，所述支撑平台相对于固定平台在竖向方向上位移调节设置，能够对硅钢片叠放平面进行高度调节，保证出料高度的一致性，使得出料规整性较好。

针对攀枝花钢钒有限公司难以稳定生产w(S)≤0.006%高级别电工钢的问题,通过开发RH脱硫剂、钢包渣改性及工艺参数控制,形成了RH脱硫系统工艺技术。经工业试验表明,采用该工艺技术后,钢水脱硫率最高达到42%,成品w(S)控制在0.005%以下,全氧、氮含量也得到了较好的控制,且脱硫剂没有引起钢水增碳,满足高级别电工钢的生产要求。 In light of the difficulty of production of high level electrical steel w(S)≤0.006 % steadily in Panzhihua steel & vanadium Co.,Ltd.the process technology of RH desulfurization system has been formed by developing the RH desulfurizer,modifying the ladle slag and controlling the process parameters.Industrial experiments show that the desulfurization rate of hot metal rises to 42 % and the w(S) of the finished products is controlled in below 0.005 % and total oxygen and nitrogen contents are a... 

采用RH精炼添加钙合金方式对硅钢进行钙处理。结果表明,钙合金添加量为0.67、1.00、1.67kg/t钢时,钢中钙含量分别为0、2×10-6、4×10-6;随着钙合金添加量增大,钢中夹杂物粒度逐渐由0～2μm向2～4、4～6μm偏移;不同钙处理条件下,钢中均存在粒径小于1μm和粒径为1～5μm的MnS、CuxS夹杂物,后者或单独存在,或同AlN、CaS夹杂复合;粒径为5～10μm区间,钢中的夹杂物基本以钙的氧、硫化物为主。与钙处理前相比,钙合金添加量为0.67、1.00、1.67kg/t钢时,粒径小于1.0μm的微细夹杂物减少幅度分别为68.06%、87.50%、94.94%。钙合金添加量为1.67kg/t钢时,可以去除钢中绝大部分的微细夹杂物。 Ca alloy was added into the liquid steel during RH refining,and the results show that Ca concentration in final Si steel sheets is insignificant,about 0,2×10-6 and 4×10-6 when the added amount of Ca is 0.67,1.00 and 1.67 kg/t steel,respectively.With the increase in the added Ca alloy amount,the inclusions in the steel gradually change from those of 0～2 μm to those of 2～4 and 4～6 μm.Under different Ca treatments,there exist MnS and CuxS inclusions whose size is below 1 μm as well as MnS and CuxS ... 

本发明提供的一种耐热型低损耗取向硅钢，取向硅钢的单面采用激光刻痕形成平行线状沟槽；所述激光刻痕为取向硅钢制备工艺中的渗氮步骤之后和在涂覆MgO涂层步骤之前实施；在渗氮步骤之后和在涂覆MgO涂层步骤之前进行激光刻痕加工不会破坏高温退火后形成的硅酸镁底层，底层完整性好，刻痕形成的沟槽位于取向硅钢带材金属基体表面，在高温退火过程中沟槽内直接反应生成硅酸镁底层，最终取向硅钢带材表面涂覆张应力涂层后光滑、平整、无凹凸，取向硅钢带材损耗低、叠片系数高、耐热，成品取向硅钢带材既可用于制备立体卷铁心变压器也可用于制备叠片铁心变压器。

本发明公开了一种高磁感取向硅钢，其含有Fe及不可避免的杂质元素，其还含有质量百分含量如下的下述各化学元素：C：0.02～0.08％，Si：2.0～4.5％，Mn：0.02～0.30％，S≤0.0050％，Als：0.01～0.04％，N：0.002～0.01％，Nb：0.0050～0.0600％；以及P：0.01～0.1％，Sn：0.01～0.30％，Cu：0.01～0.50％的至少其中一种。此外，本发明还公开了上述高磁感取向硅钢的制造方法，其包括步骤：(1)制得板坯；(2)板坯加热；(3)热轧，其包括：粗轧、在热卷箱内卷取保温，以及精轧；其中粗轧结束温度高于970℃；卷取温度为800～1050℃，卷取时间为30～200s；精轧开始温度低于1050℃；(4)冷轧；(5)脱碳退火；(6)渗氮；(7)涂覆退火隔离剂；(8)高温退火；(9)涂覆绝缘涂层和激光刻痕。

本文对某厂硅钢DR510温度、成分及过程控制水平和成品的组织、力学性能进行了研究,并在此基础上提出了工艺优化方案,有一定的借鉴和推广价值。 In this paper,the critical process and the products quality,including temperature,composition and process controlling level,the organization and mechanical properties of the finished product,were studied.On the basis of that the optimized technical plan provided,and this control technology is worth using and spreading. 

本实用新型涉及变压器铁芯生产技术领域，尤其涉及一种硅钢片卷自动上料装置。包括所述底座上方设置有支撑座，所述支撑座上方转轴连接有翻转座，所述翻转座前后两侧设置有支撑柱，所述托架底部前后两侧设置有支撑套，所述支撑套对应滑动连接在支撑柱上，所述支撑套左侧上方设置有凸台，所述凸台右侧在支撑套上方设置有卡槽，所述卡槽右侧开口，所述硅钢带卷设置在卡槽内部，将钢卷平躺放置在托架的卡槽内部，通过翻转液压缸可将托架和钢卷进行树立，钢卷一侧靠在托架上，钢卷树立过程比较平稳，通过三组液压缸可实现钢卷自动上料的过程，在钢卷树立过程中，可通过绳索将钢卷固定在托架上。