硅钢资料

【作者】 杨佳直； ...

本发明是关于一种薄规格无取向硅钢35BW440，该无取向硅钢35BW440包括以下质量百分比的元素：C：≤0.003％，Si：0.8％‑2.0％，Mn：0.4％‑1.2％，P：≤0.015％，S：≤0.003％，Als：0.25％‑0.6％，N：≤0.003％，Sb：0.04％‑0.1％，O：≤0.0025％，其余为Fe及不可避免的杂质。在没有电磁搅拌设备增加无取向硅钢磁感应强度的前提下，通过加入Sb元素，增加对电磁性能有利的{110}和{100}织构组分，提高电磁性能，采用二次冷轧及中间连续退火的工艺，提高无取向硅钢的表面质量。

利用光学显微镜、TEM和EBSD研究了退火温度对双辊连铸无取向硅钢再结晶组织的影响。结果表明,900℃退火后组织分布不均匀,有大量带状组织,平均晶粒尺寸29.5μm。提高退火温度,晶粒尺寸增大,组织均匀化程度增加,1050℃退火时,带状组织基本消失,平均晶粒尺寸42.2μm。 Effect of annealing temperature on recrystallization microstructure of non-oriented electrical steel produced by twin-roll casting process was investigated using OM,TEM and EBSD.The results show that the recrystallization microstructure is uneven because of many banded grains existing,average grain size is 29.5 μm.With annealing temperature increasing,the recrystallization grain size increases,microstructure becomes more homogeneous.When 1050 ℃ annealing,the banded structure almost disappear and... 

研究了电工钢SXRC的显微结构和疲劳性能,并与DP钢进行了比较。结果表明,退火温度低温化能够有效的抑制电工钢的再结晶。该钢在固溶铌的作用下,能够在保证电机磁性的同时具有一定的强度。与DP钢相比,SXRC钢的抗疲劳性能更好。 The microstructures and fatigue properties of the electrical steel SXRC we re investigated, and the properties were also compared with the steel DP. The results show that the recrystallization of the electrical steel can be suppressed at lower annealing temperature. The steel presents favorable motor magnetic and also a compatible strength with the help of solid-solution Nb. Compared with the steel DP, the fatigue resistance of the steel SXRC is preferable. 

提供一种可以制造具有优异特性的变压器的、兼顾低铁损和良好的磁致伸缩特性的方向性电磁钢板。本发明的方向性电磁钢板具有在与轧制方向交叉的方向上线状延伸的线状应变区域，线状应变区域具有在轧制方向上具有压缩应力的区域，在与该具有压缩应力的区域的轧制方向邻接的区域具有在轧制方向上具有拉伸应力的区域。

利用XRD和EBSD研究了长轴分别平行于轧向(RD)、横向(TD)和轧面法向(ND)的柱状晶样品在热轧、冷轧及退火过程中的组织、织构演变规律,并分别从几何诱导和取向诱导两个方面分析了晶界的交互作用.结果表明,热轧时由表面摩擦剪切作用引起的组织和织构梯度直接影响并遗传给后续冷轧及退火样品.热轧后,不同样品的初始晶粒形状各向异性差异消失,形成相同的各向异性晶界组织,但晶体学各向异性发生改变,导致随后冷轧、退火组织及织构的变化均不同于直接冷轧的柱状晶样品.研究中特别关注了对磁性能有利的{100}取向区域与晶界的关系. Columnar grains show their special characteristics of morphological and crystallographic anisotropies, and thus markedly influence the microstructure and texture evolution during rolling and annealing process in electrical steel. The rolling and annealing microstructure and texture of three columnar grained samples with the long axes arranged along different directions were investigated by means of XRD and EBSD techniques, and the effects of columnar grain boundaries were analyzed from the view ... 

本实用新型提供了一种硅钢叠铁芯线圈吊装夹具，属于变压器的技术领域，缓解了现有技术中存在的线圈吊装夹具单次只能进行单个垫块装配，效率较低的技术问题。所述夹具包括：中心盘、吊环、连接杆、吊臂、勾具；连接杆一端连接中心盘，所述连接杆的数量为3个，且两两之间的夹角为120°；所述吊环设置于中心盘上方；每个所述连接杆另一端连接一个吊臂；每个吊臂上设置有勾具。

运用电子背散射衍射(EBSD)和X射线衍射(XRD)技术对硅钢热轧板的织构在板厚方向的分布进行了研究,并分析了两种织构测量方法的特点。EBSD技术能直观给出板厚方向的微观织构,XRD能得到钢板的宏观统计织构信息,结合两种技术的分析,能更直观更精确的研究不同织构在板厚方向的分布。 The texture distribution along the thickness of the silicon steel has been investigated by electron backscatter diffraction(EBSD) and X-ray diffraction(XRD) technique.The characteristics of two technique of texture analysis have been investigated.Combined the two techniques,the texture distribution along the thickness of the silicon steel could be realized distinctly and accurately. 

本实用新型属于抛丸设备技术领域，具体涉及一种防止钢丸随硅钢板移动的料仓结构，包括料仓，料仓的相对两侧上开有对称设置的开口；料仓的侧壁上滑动连接有位于开口上方的刮板，刮板与料仓之间连接有弹性件；料仓内靠近硅钢前进方向的一侧上设有用于清理硅钢表面物质的清理机构。在刮板与料仓之间连接弹性件，在弹性件的作用下，刮板的下端能够始终贴合在硅钢的上表面，刮板能较好的封堵硅钢与开口之间的缝隙，避免钢丸通过开口与硅钢之间的缝隙排出，提高抛丸机的密封性。

【作者】 罗海文； 向睿； ...

研究了CSP工艺生产≤0.005%C-1.1%Si的2.2mm无取向电工钢热轧板在800～1000℃常化对0.5mm冷轧板840℃退火后组织和磁性能的影响。结果表明,热轧板常化温度升高,冷轧板退火后的再结晶晶粒增大,铁损降低,磁感增加;热轧板常化温度超过900℃,因第二相固溶而后弥散析出,退火后冷轧晶粒细化,铁损增加,因此该无取向电工钢热轧板最佳常化温度为900℃。 The effect of normalizing at 800-1000℃ of CSP produced plate(≤0.005%C-1.1%Si) on the microstructure and magnetic properties of downstream cold-rolled non-oriented electrical steel annealed at 840℃ was studied.Results show that with increasing normalizing temperature of hot-rolled material the recrystallized grain size of annealed sheet increases,iron loss reduced and magnetic induction increases.As normalizing temperature excesses 900℃,grain is refined and iron loss increases after annealing due... 

本实用新型公开了一种形成优质玻璃膜的取向硅钢脱碳退火板，包括主体，所述主体的中部安装有组合架机构，所述组合架机构的前后两端安装有开边架，且组合架机构的底端安装有固定机构，所述主体的中部开设有槽口架，所述组合架机构的中部安装有拼接机构。该形成优质玻璃膜的取向硅钢脱碳退火板设置有拼接机构，便于使用者将内退板与拼接板进行组合使用，通过内退板的四角安装的扣体卡合安装在内槽进行固定锁紧，便于将内退板与拼接板进行组合，加强主体的防护性，便于使用者多次使用和来回使用，由于退火板可反复利用，方便后期形成优质玻璃膜，通过拼接板通过中心凸板与凸槽板进行组合，方便将拼接板的大小进行调节与更换。