取向硅钢热轧板中织构梯度对发展完善的二次再结晶十分关键,通过添加铜可以显著降低取向硅钢板坯加热温度,从而影响热轧板织构分布。利用X射线衍射仪,分析了实验室模拟薄板坯连铸连轧(TSCR)工艺的3种不同铜含量的取向硅钢热轧板织构。结果表明:不同铜含量热轧板表面到厚度1/4处均为弱的热轧织构,热轧板心部主要为{100}面织构;铜含量约在0.4%时,热轧板次表层的{110}<001>织构比例最高,而热轧板心部的{100}<110>织构比例最低;铜含量对热轧织构中{114}<110>和{001}<100>织构发展有显著影响。 The texture gradient in hot rolled grain oriented silicon steel strip is one of the essential factors to achieve a perfect secondary recrystallization.The addition of copper can significantly reduce the slab reheating temperature of grain oriented silicon steel,so as to impact the texture distribution in the hot rolled strip.The texture of hot rolled grain oriented silicon steel strip as-rolled by thin slab casting and rolling process(TSCR) in laboratory with three different copper contents was ... 

本实用新型公开了一种取向硅钢毛刷辊损耗检测装置及钢带刷洗机构。该取向硅钢毛刷辊损耗检测装置包括：固定基座，设置于刷辊的辊面侧方；压力测试元件，用于与刷辊的刷毛相顶压并测试刷毛对测力件的压力；接近机构，连接压力测试元件与固定基座，驱动测力件朝向或者背向刷辊运动。该取向硅钢毛刷辊损耗检测装置中的接近机构带动压力测试元件向刷辊一侧运动，直至刷毛与压力测试元件相顶压，当压力值至预定范围后，获得接近机构带动压力测试元件朝向刷辊的运动量，进而获得刷毛的损耗量；保证钢带刷洗清洁效果的同时，降低刷辊维护成本。

针对节能电机对无取向电工钢在磁性能方面的特殊要求,采用普通W600牌号的热轧板为原料,通过大量的现场工艺试验,研究总结出了\"超低张力\"的运行工艺、\"先快后慢\"的加热工艺、\"先湿后干\"的退火脱碳工艺、\"先缓后急\"的冷却工艺,生产出P1.5/50≤4.0 W/kg、B50≥1.70 T的冷轧电工钢产品,满足了节能电机的要求。 Based on the special requirements of no-oriented electrical steel for saving energy motor in magnetic aspects,using common W600 brand of hot rolled plate as raw material,through a large number of real tests,an ultra-low tension process,heating process which was quick at first and then slow,annealing decarburization process which was dry after the first wet,and a cooling technology of \"slow after the first urgent\" were concluded.Electrical steel product with P1.5/50≤4.0W/kg,B50≥1.70T was produced... 

一种硅钢片测量装置，属变压器绝缘件生产技术领域，包括工作台、止动滑块、纵梁和测量部，止动滑块安装在工作台上，纵梁架设在止动滑块和工作台上，测量部安装在纵梁上。工作台包括台面、立柱和横向燕尾槽，四个立柱将台面支撑于地面，台面的下侧安装一个横向燕尾槽。止动滑块安装在横向燕尾槽内，止动滑块包括块体、推杆、楔块、挡片、弹簧和蘑菇头，块体横向具有通孔，通孔内安装推杆和弹簧，块体纵向具有一对侧槽，侧槽内安装楔块，通孔内具有一个凸台，凸台位于靠近蘑菇头的一侧，蘑菇头用于弹簧的限位。止动滑块上安装纵梁，纵梁包括滑板、纵向燕尾槽，滑板的一端安装在止动滑块上，滑板上具有纵向燕尾槽，纵向燕尾槽上安装测量部。

一种不含铬取向电磁钢板用涂料、其制备方法及带涂层的不含铬取向电磁钢板的制备方法，属于取向电磁钢板技术领域。所述涂料按质量份配比组成如下：100份磷酸盐、60～120份二氧化硅溶胶、5～50份氧化锡溶胶、2～40份硼酸和0.5～10份二氧化硅粉体。本发明所述制备方法环境友好、能够满足规模化生产要求，制备的涂料不含铬、具有良好的稳定性和涂敷性，并且本发明所述涂料能够使取向电磁钢板表面涂层具有良好的耐吸湿性、耐腐蚀性、耐热性、张力效果和抗粘片性。

研究表明,硅钢中的夹杂物对成品带钢的磁性能有显著影响。为研究冶炼过程硅钢中的夹杂物遗传变化,进而提出更有效的控制措施加以去除,本文结合典型的无取向硅钢生产炉次,采用非水溶液电解提取+扫描电镜观察方法分析冶炼过程中上述炉次典型试样的夹杂物。结果表明:转炉冶炼结束、RH精炼开始时,钢的氧化物夹杂总量最大,约为0.23%;RH精炼过程中,氧化物夹杂总量不断降低,并在脱碳结束时达到最低,约为0.02%;连铸过程中,氧化物夹杂总量仍有不断降低趋势,但夹杂物的平均尺寸变化不大。本试验条件下,中间包试样的夹杂物数量约为1.59×104个/mm3。 As we all know, the non-metallic inclusion effects magnetic properties of silicon steel sheets obviously. The article aims to study the heredity of non-metallic inclusion in non-oriented silicon steels during the steel making process, and then provides a more effective controlling measure to remove the inclusions. Based on the typical non-oriented silicon steel charges, the non-aqueous solution extraction and SEM observation were adopted to analyze the non-metallic inclusions. Results show that,... 

本发明公开了一种提高薄板坯连铸生产高铝无取向硅钢可浇性的方法，在保证生产顺行、质量稳定的基础上，能使高铝无取向硅钢连浇炉数由10炉提高至16炉，在提高小时产量、降低生产成本方面效果显著。

结合工业化生产过程中出现的同卷带钢头、尾磁性能差异现象,对50SW1300牌号无取向硅钢同卷带钢头、尾试样的夹杂物、晶体织构和显微组织进行了分析研究。结果表明,夹杂物、晶体织构是影响成品钢卷磁性能的重要因素。夹杂物是造成同卷带钢头、尾铁损差异的主要原因。夹杂物数量越多,尤其是小尺寸的夹杂物数量越多,对成品带钢的磁性能影响越大,对于本试验而言,AlN和MnS是影响成品带钢磁性能的主要夹杂物。晶体织构是造成同卷带钢头、尾磁感应强度差异的主要原因。有益的{100}和Goss织构含量越大,有害的{111}<110>和{111}<112>织构含量越小,即有益织构与有害织构含量比越大,成品带钢的磁感应强度越大。 Based on the industrial manufacture of non-oriented silicon steel sheets 50SW1300, the magnetic property variation of head and tail of the same finished steel sheets was discussed by analyzing non-metallic inclusion, crystal texture, and microstructure. Results show that, both of the non-metallic inclusion and the crystal texture will affect the magnetic properties significantly. The non-metallic inclusion is the key factor of the core loss variation of head and tail of the same finished steel s... 

本发明公开了一种带有紧固硅钢带的非晶合金铁心制造方法，包括以下步骤：步骤(1)：切割非晶带材片和紧固硅钢带；步骤(2)：对所述非晶带材片和紧固硅钢带进行套装与成型，每组非晶带材片两端搭接，紧固硅钢带设置于非晶带材片之间，得到成型铁心；步骤(3)：对所述成型铁心进行磁场热处理；步骤(4)：对所述成型铁心进行表面涂封。通过本发明提供的方法生产非晶合金铁心，操作方便、提升非晶合金铁心的结构稳定性，并且进一步降低铁心因磁致伸缩产生的噪声。

采用铸坯低倍组织检验和化学分析的方法,研究板坯连铸机二冷区电磁搅拌器电流和频率参数对无取向电工钢XG800WR板坯中心偏析和等轴晶率的影响,结果表明:铸坯等轴晶率随着搅拌器电流强度和电流频率的增大而增加。采用二冷区电磁搅拌可减小中心易偏析元素S的偏析,试验得出:减小铸坯S偏析效果最好的电磁搅拌参数为电流380～400A,频率6Hz。 The effect of electromagnetic stirring current and frequency parameter at secondary cooling area on the central segregation and equiaxed crystal ratio of XG800WR non - oriented electrical steels slab was investigated through the methods of chemical and macrostructure analysis.The results shows that the rate of equiaxed crystal zone is going up with increasing of current intensity and current frequency.Electromagnetic stirring in the secondary cooling area can be easily reduced segregation caused... 

本发明揭示了一种高牌号无取向硅钢及其生产方法。所述无取向硅钢的化学成分以质量百分比计包含：C:0.002～0.004％，S≤0.003％，Si:1.4～1.7％，Mn:0.7～0.95％，P≤0.03％，Sn:0.015～0.035％，11×([Si]‑1.4％)＝14×([Mn]‑0.7％)。所述无取向硅钢的生产方法中，连铸坯加热温度1120～1150℃，精轧终轧温度为890±15℃，最后一道次精轧的压下量≥30％且最后两道次精轧的总压下量≥50％，卷取温度650±20℃；在酸连轧之前不需要进行常化处理，且所得无取向硅钢的磁性能佳，表面无瓦楞缺陷，满足低成本高牌号无取向硅钢的需求。