借助光学显微镜、扫描电镜、交流磁性能测量仪和万能拉伸试验机研究了0.3 mm厚高强无取向电工钢冷轧板在780、820、860和900℃退火保温2 min后的组织、织构和性能。结果表明:在退火温度范围内,试验钢均发生了完全再结晶,得到等轴状的铁素体晶粒;随着退火温度的升高,平均晶粒尺寸从9.2μm增长到41.3μm,工频铁损和400 Hz高频铁损均先大幅减小后趋于平缓,磁感应强度先升高后降低。在820℃退火时,铁损P_1.5/50=5.51 W/kg,P_1.0/400=33.22 W/kg均处于较低值,磁感应强度B₅₀₀₀最大,为1.649 T。试验钢的屈服强度和抗拉强度均随退火温度的升高而降低,780℃退火时屈服强度为496 MPa, 900℃退火时降低至407 MPa。综合磁性能和力学性能考虑,试验钢的最佳退火温度是820℃。 Microstructure, texture and properties of 0.3 mm thick high strength non-oriented electrical steel cold rolled sheet annealed at 780 ℃, 820 ℃, 860 ℃ and 900 ℃ for 2 min were studied by means of optical microscope, scanning electron microscopy, AC magnetic property tester and universal tensile testing machine. The results show that in the annealing temperature range, complete recrystallization of the experimental steel occurs and equiaxed ferrite grains are obtained. With the increase of annealin... 

本实用新型涉及一种取向硅钢高温退火设备，尤其涉及一种取向硅钢全氢式高温罩式炉外罩，从外至内包括圆柱形外壳和耐火保温层，所述耐火保温层内壁铺设有电阻带；所述圆柱形外壳上部设有外罩顶盖；所述耐火保温层由陶瓷纤维模块堆砌而成，所述电阻带通过钉子铺设在陶瓷纤维模块上；电阻带头一端通过接线棒引出炉壳外，另一端中性点在炉内短接。本实用新型保温层内层采用模块化的高纯度陶瓷纤维代替耐火砖，该材料具有重量轻、蓄热少，低导热性能带来高的节能效果，具有抵抗热冲击的能力，加上模块化的结构，安装快捷，衬体无需烘干和养护，所以安装好以后便可立即投入使用。

采用X-射线衍射分析技术测定了取向硅钢热轧板在不同压下率下不同厚度处的织构。结果表明,在压下率低于80%的情况下,几乎所有试样的不同厚度处的织构均为旋转立方织构类型{100}<011>,但不同压下率、不同厚度处的织构强度存在很大差异;在压下率大于80%的情况下,不同试样的不同厚度处的织构类型发生了变化,其织构类型为旋转立方织构或高斯织构{011}<100>,且当织构类型为旋转立方织构时,织构强度存在很大差异,而当织构类型为高斯织构时,织构强度差异相对较小。 The texture of the grain oriented silicon steel hot rolled plate at different compressibility has been measured.The experimental results have shown that the texture of all samples at different thickness is {100}<011> when the compressibility is below 80%,and its intensity at different compressibility and thickness is difference.The texture of all samples at different thickness is variable when the compressibility is above 80%,it is {100}<011> or {011}<100>,and the intensity of ... 

针对宝钢集团、日本新日铁住金和JFE公司公开的相关专利等资料,总结了国内外高强度无取向电工钢的研究进展,分析了不同电工钢的化学成分、生产工艺及产品性能,指出固溶强化、细晶强化、析出强化、位错强化都有可能被用来提高无取向电工钢的强度,并阐述了四种强化方式的优缺点;指出在高强度无取向电工钢的研发过程中,需根据其具体用途确定目标性能,再采用合适的强化手段,最终实现力学性能、磁性能和生产性能之间的平衡。 The research progress of high strength non-oriented electrical steels at home and abroad is summarized according to related patents brought into the public by Baosteel,Nippon Steel & Sumitomo Metal corporation and JFE corporation.The characteristics of chemical composition,production technology and properties of products in the patents are analyzed.Each of solution strengthening method,fine-grain strengthening method, precipitation strengthening method or dislocations strengthening method ma... 

简述了无取向硅钢环保涂层发展背景,分析了硅钢环保涂层的特点及国内、外研究进展,提出了硅钢保涂层下一步的发展方向。 The back ground of environmental protection coating of non-oriented silicon steel was described in this paper.The characteristics and study progress in domestic and foreign of environmental protection coating of non-oriented silicon steel were analysised.The next development direction of environmental protection coating of non-oriented silicon steel was put forward. 

采用XRD、SEM和激光粒度仪等手段,观察并研究了不同特性氧化镁在硅钢表面形成硅酸镁底层形貌特点,并结合热力学和差热-失重分析了MgO-SiO2的反应机理。研究结果表明:粒度小,活性值高的特种氧化镁在高温退火过程中与基体表面氧化物生成的硅酸镁底层,界面中硅酸镁底层嵌入基体较多,表面致密,颗粒细小,有利于形成附着性能优良的硅酸镁底层。 Surface microstructure of Mg2SiO4 coatings formed on the surface of oriented silicon steel coated with different kinds of MgO was investigated by XRD and SEM.The reaction mechanism between MgO and SiO2 was analyzed by TG-DSC and thermodynamic calculation.Results revealed that when the MgO with finer microstructure size and higher activity is employed,a dense Mg2SiO4 layer with finer microstructure and good binding to the steel substrate can be obtained.The results are very helpful for the prepar... 

本发明属于金属材料加工技术领域，具体涉及取向硅钢罩式炉高温退火低保温阶段二段式退火工艺，包括：将涂镁取向硅钢卷装入密闭的罩式炉中，并向罩式炉内通入氮气将炉内氧气充分排出；通电升温并将氮气转换为10m3/h氨分解气，接着点燃放散阀，将温度升至500‑600℃，恒温13h；500‑600℃低保温结束后检测内部气体露点是否小于0℃；本发明提供的取向硅钢罩式炉高温退火低保温阶段二段式退火工艺能够解决普通冷轧取向硅钢罩式炉高温退火热处理低保温阶段，钢卷在高温下不被水蒸汽氧化，消除钢带表面露金、发红、发黑、水印、色泽不均、导通缺陷，降低钢带铁损、提高磁感、降低生产成本。

本实用新型公开了一种硅钢板带生产加工用除油烘干装置，包括壳体，所述壳体的外表面上对称设置有电机，所述电机的输出端固定连接有输送带，所述壳体的顶部设置有机体，所述机体的内部设置有除油机构，所述除油机构的一侧设置油烘干机构，所述壳体的底部设置油收集箱，所述收集箱的内部设置有收集槽。本实用新型，利用除油机构可对成硅钢板带生产后进行一定的除油处理，除油的效果更好更彻底，同时相比以往的方式提高了一定的工作效率，具有一定的实用性，利用烘干机构可进行除油后的成硅钢板带进行烘干处理，防止水渍残留在表面上，影响一定的美观效果，具有一定的实用性。

综述了国内外大钢铁企业与研究机构采用获得抑制剂法生产低温高磁感取向硅钢的开发及应用情况,分析了以该法生产高磁感取向硅钢过程中抑制剂的控制技术,包括固有抑制剂组成方案、气态渗氮方式与工艺及高温退火工艺的制定.研究表明,固有抑制剂组成方案的设计思路大体一致,化合物抑制剂以AlN为主、硫化物为辅,同时添加少量Sn,Sb等单元素抑制剂,但组成元素含量存在一定差别;在脱碳退火后用NH3进行非平衡渗氮处理已成为气态渗氮的主要方式,但最佳方式仍未明确,具体选择需依据实际生产条件,相应脱碳及渗氮工艺的控制条件差别较大;高温退火工艺中升温制度差别不大,升温阶段退火气氛中N2含量的选择存在差别.此外,分析了抑制剂控制技术目前存在的关键问题,并指出了进一步的研究方向. The current application and exploitation on production of low-temperature high magnetic induction grain-oriented silicon steel with acquired inhibitor method at both iron and steel enterprises and research institutions in the world are reviewed. The control techniques of inhibitors, which include the composition design for inherent inhibitors, nitriding method and process, and secondary recrystallization annealing, are thoroughly analyzed and proposed. It is indicated that the design ideas for i... 

本发明公开了一种提高超高磁感取向硅钢底层质量的退火隔离剂及其制备方法和应用。本发明所述退火隔离剂包括如下组分：MgO、TiO2、硼酸、Na2O、Sb2(SO4)3；以MgO质量为标准，其余各组分相对MgO的质量百分数为：TiO21.9～40％，硼酸0.05～0.1％，Na2O1～5％，Sb2(SO4)31～5％。本发明制备的退火隔离剂提高了超高磁感取向硅钢的成材率；提高了取向硅钢的底层附着性，降低了产品让步率；制备的超高磁感的取向硅钢可满足高容量变压器的使用要求。

一种在取向硅钢中获得沿晶断口的方法：将取向硅钢样品加工成俄歇电子能谱仪标准试样；对标准试样进行表面清理；充氢：将标准试样所设定的预设断口处放入充氢装置的含硫脲溶液中，并使取向硅钢样品为阴极；将铂片置入并作为阳极；阴极充氢电流为1.25～1.35A，充氢电流密度在0.1～0.8A/m2，充氢时间在12～50h，充氢电压为36～39V；进行表面分析。本发明不仅工艺简单，便于操作，用时短，所用毒化剂是硫脲，从而避免了采用剧毒的三氧化二砷作为毒化剂，对人体健康有极大威胁的问题，且所获得的取向硅钢断口均为典型沿晶断口，适用于取向硅钢晶界偏聚行为以及晶界微区成分分析。

为研究常化温度对热轧无取向硅钢组织与织构的影响,采用光学显微镜、背电子散射衍射技术研究了不同常化温度对其影响。结果表明,实验硅钢板在700～850℃温度下常化时,随常化温度的升高,晶粒尺寸增大,有利组分α织构增强,不利组分γ织构降低。对比研究了800℃和850℃常化热轧板CSL晶界分布图与取向差分布图,在本文研究条件下,Goss织构易在Σ=3,9的CSL晶界及晶粒取向差为30°～55°处形成。 The hot strips normalized at different temperatures were investigated by optical microscope and EBSD to study the effect of normalizing temperature on microstructure and texture of hot-rolled non-oriented silicon steel sheets.The results show that the grain size increases,the intensity of α-fibre texture increases,and the γ-fibre texture decreases when the hot strips are normalized at the 700-850 ℃.And CSL boundaries of Σ=3 and 15,and misorientation angles between 30° and 55° are more likely rel...