本实用新型属于抛丸设备技术领域，具体涉及一种防止钢丸随硅钢板移动的料仓结构，包括料仓，料仓的相对两侧上开有对称设置的开口；料仓的侧壁上滑动连接有位于开口上方的刮板，刮板与料仓之间连接有弹性件；料仓内靠近硅钢前进方向的一侧上设有用于清理硅钢表面物质的清理机构。在刮板与料仓之间连接弹性件，在弹性件的作用下，刮板的下端能够始终贴合在硅钢的上表面，刮板能较好的封堵硅钢与开口之间的缝隙，避免钢丸通过开口与硅钢之间的缝隙排出，提高抛丸机的密封性。

通过实验室25 kg真空感应炉冶炼和锻轧研究了0.26%～0.95%Al含量对0.5 mm 2.2%Si无取向硅钢冷轧板组织、织构和磁性能的影响。试验结果表明,0.26%～0.81%Al含量时,随钢中Al含量的增加,成品退火钢板的晶粒尺寸增加同时铁损减少;当Al含量大于0.81%时,随Al含量增加,钢板的晶粒尺寸减小,同时铁损增加。Al含量对硅钢板磁感的影响没有明显的规律。2.2%Si无取向硅钢的合适Al含量为0.48%～0.81%。 The effect of 0.26%～0.95%Al content on structure,texture and magnetic performance of 0.5 mm cold rolled sheet of 2.2%Si non-oriented silicon steel has been studied by a 25 kg vacuum induction furnace smelting,and forging -rolling in laboratory.Results show that as 0.26%～0.81%Al,with increasing Al content in steel the grain size of annealed finished sheet increases while iron loss of sheet decreases,and as Al content in steel is more than 0.81%,the grain size of sheet decreases while iron loss in... 

研究了CSP工艺流程生产的硅含量为1.5%的无取向电工钢在不同常化温度下对磁性能的变化。研究结果表明:随着常化温度的提高,热轧板的晶粒尺寸增大,且组织均匀性提高;此外成品的有利织构组分{100}<0vw>、α、η增强,不利织构组分减弱;铁损P1.5/50呈下降趋势,磁感B50上升平缓。在常化工艺为970℃×2.5min下,对应的铁损P1.5/50<3.4W/kg,磁感B50>1.74T。 The effect of normalizing temperature on the magnetic properties of non-oriented electrical steel containing 1.5%silicon produced by CSP process was studied.The results show that with increasing normalizing temperature,the average grain size of hot-rolled plate increases and the microstructure uniformity is improved.Furthermore,the texture components of finished products are improved through enhancing of{100}<0vw>,αandηtextures and weakening of{111}<112>texture;the core loss P1.5/50 ... 

本实用新型涉及变压器组装辅助设备领域，具体涉及一种变压器铁芯硅钢板的夹紧装置，包括操作台，操作台的侧部安装有安装板，安装板的顶部固定连接有陶瓷管，安装板的一侧安装有连接座，连接座的底部连接有上连接有接线螺栓，接线螺栓上连接有用于切割泡沫棒的钨丝，接线螺栓与电源相连接；解决现有的泡沫棒人工切割效率低的问题。

本发明涉及硅钢片切片领域，具体涉及一种硅钢片自动切片设备，包括下拉机构、推料机构、硅钢片输送机构、硅钢片推动机构、压片机构、导料壳、两个斜切机构、连接机构和三角切边机构，该硅钢片自动切片设备，通过移动连接机构，使得该设备能够进行两种硅钢片的切割加工，使得该设备能够满足多种硅钢片的加工，通过在移动三角切边机构和斜切机构的位置，使得该设备能够加工出各种硅钢片，且能够单一旋转加工那种硅钢片，并且一次加工出两张硅钢片，通过硅钢片输送机构带动推料机构进行同时运动，避免两个硅钢片之间叠起，当原料与推料机构的端部接触时，由于推料机构的拉动速度比硅钢片推动机构的速度快，避免原料上发生褶皱而影响切割的位置。

本实用新型涉及一种取向硅钢高温退火设备，尤其涉及一种取向硅钢全氢式高温罩式炉外罩，从外至内包括圆柱形外壳和耐火保温层，所述耐火保温层内壁铺设有电阻带；所述圆柱形外壳上部设有外罩顶盖；所述耐火保温层由陶瓷纤维模块堆砌而成，所述电阻带通过钉子铺设在陶瓷纤维模块上；电阻带头一端通过接线棒引出炉壳外，另一端中性点在炉内短接。本实用新型保温层内层采用模块化的高纯度陶瓷纤维代替耐火砖，该材料具有重量轻、蓄热少，低导热性能带来高的节能效果，具有抵抗热冲击的能力，加上模块化的结构，安装快捷，衬体无需烘干和养护，所以安装好以后便可立即投入使用。

【作者】 谌剑； ...

通过试验确定氩气分析流量为3.5L/min,静态流量为0.75L/min,冲洗时间为3s,预燃时间为12s,积分时间为5s的激发条件,采用火花源原子发射光谱法测定取向硅钢中碳、硅、锰、磷、硫。分别采用铣床铣样、砂轮磨样两种制样方式进行了精密度考察,发现制样方式对结果影响不大;讨论了取向硅钢样品中碳、硅、锰、磷、硫测定时可能存在的共存元素干扰,发现硅对锰元素的干扰不可忽略,采用干扰系数法进行了校正,据此拟合得到各元素校准曲线的相关系数均在0.999 0以上。精密度考察结果表明,碳、硅、锰、磷、硫的相对标准偏差(n=10)在0.71%~9.4%之间。对两块取向硅钢生产样品进行分析,并与钢铁研究总院进行比对分析,结果一致,且偏差均在允许范围内。 Carbon,silicon,manganese,phosphorus and sulfur in oriented silicon steel were determined by spark source atomic emission spectrometry.The selected excitation conditions were as follows:the analytical flow rate of argon was 3.5L/min,the static flow rate was 0.75L/min,the flush time was3s,the precombustion time was 12sand the integration time was 5s.Two sample preparation methods,including milling machine and grinding wheel,were investigated.The precision test results showed that,the determination... 

对无取向电工钢中的夹杂进行了系统的分析。利用小样电解,采取不同电解液,不同的分离方法对无取向电工钢中稳定和不稳定夹杂物进行了提取、分离和收集。利用扫描电镜(SEM)、X-射线衍射、ICP等对电解分离收集的夹杂物进行了定性和定量分析。 The inclusion analysis of the non-oriented electrical steel has been investigated.By using small sample electrolytic analysis,with different electrolytes and different separation ways,the stable inclusions and unstable inclusions was drew,separated,and collected.With utilizing the methods of SEM,X-ray and ICP,the qualitative and quantitative analysis of inclusions in the non-oriented electrical steel was obtained. 

本实用新型公开了一种硅钢板带运输使用的固定设备，所述壳体的侧壁固定连接有多个第一放置轴，所述壳体的侧壁固定连接有多个第一限位套，且第一限位套与第一放置轴同轴心，所述第一限位套的内部设置有第一压板，所述壳体的内部设置有第一滑槽及第二滑槽，所述壳体的一侧设置有滑板。本实用新型通过将硅钢板带卷起后用绑线绑紧后，放入第一放置轴外表面后推入第一限位套内部，放好一行成硅钢板带后将将第一个滑板底部的滑杆放入第一滑槽内，推动滑板进入壳体内，使插杆插入凹槽内，再对下一列的硅钢板带进行放置，安装完成后，将挡板放入第二滑槽内，推动滑板向壳体内移动，将挡板向壳体内移动。

利用光学显微镜、TEM和EBSD研究了退火温度对双辊连铸无取向硅钢再结晶组织的影响。结果表明,900℃退火后组织分布不均匀,有大量带状组织,平均晶粒尺寸29.5μm。提高退火温度,晶粒尺寸增大,组织均匀化程度增加,1050℃退火时,带状组织基本消失,平均晶粒尺寸42.2μm。 Effect of annealing temperature on recrystallization microstructure of non-oriented electrical steel produced by twin-roll casting process was investigated using OM,TEM and EBSD.The results show that the recrystallization microstructure is uneven because of many banded grains existing,average grain size is 29.5 μm.With annealing temperature increasing,the recrystallization grain size increases,microstructure becomes more homogeneous.When 1050 ℃ annealing,the banded structure almost disappear and... 

本发明属于冶金技术领域，涉及一种超短流程稀土取向硅钢及其制备方法，化学组成及其重量百分比为Si：2.0～4.5％，C：≤0.003％，Y：0.001～0.05％，Mn：0.15～0.35％，Al：0.03～0.04％，Cu：0～0.5％，S：0.025～0.04％，N：0.011～0.013％，其余为Fe和不可避免的杂质元素。制备工艺包括：钢水冶炼、薄带连铸、冷轧、再结晶退火。与常规生产方式相比，取消了连铸、粗轧、热连轧、常化和脱碳退火等工序，极大简化了生产流程。通过添加稀土元素钇，促进了抑制剂的析出，还显著细化了薄带连铸硅钢的凝固组织，提高组织均匀性，获得了均匀细小的等轴晶，优化了取向硅钢的性能。