针对不同牌号的无取向硅钢产生结疤缺陷的难易程度和表面结疤缺陷的外形特征及分布规律,分析了该缺陷产生的原因。通过调整剪前导板的对中度,设置精轧侧导板开度余量及短行程数值,及时修补与更换侧导板,减少带坯与侧导板挤撞程度,有效地降低了结疤缺陷发生率。 This article analyses the cause of the scab defects according to the defects appearance characters and distribution law,degree of difficulty to form scar of non-oriented silicon steel. It can effectively decrease the scabs by different methods,such as adjusting the center line of guide plate,setting the opening margin and short stroke value of the side guide on finishing mill,timely repairing and replacing of side guide,decreasing the collision between the strip and side guide. 

针对某硅钢车间ST机组的除尘系统除尘效率较低、排放浓度不达标、二次污染较严重的问题,通过现场调研,对除尘系统、含尘气体组分与物性参数等进行测试和分析,运用管道伴热技术改善粉尘黏性后,再选取合适的除尘器对粉尘进行除尘处理,大大地提高了系统的除尘效率。 To solve the problems of low dust removal efficiency, substandard emission concentration and severe secondary pollution, some investigations are conducted to test and analyze the dust removal system,dust-gas composition and relevant physical parameters.Moreover, dust removal efficiency is greatly improved by the use of pipe heat tracing technology and by choosing appropriate dust remover. 

本发明公开了一种高效无取向硅钢极薄带的工业连续化生产方法，其包括异步轧制、脱脂、热处理、急速冷却、涂绝缘层、烘干烧结、卷取收集各工序；其中，异步轧制中的异步比为1:1.05～1:1.24；脱脂、热处理、急速冷却、涂绝缘层、烘干烧结、卷取收集工序为连续化生产工艺；热处理工序中，第一步为预热，预热温度为500℃～720℃，预热时间20秒～125秒；第二步为相变热处理，相变热处理温度为840℃～940℃，相变热处理时间100秒～600秒；急速冷却工序中，30秒内将钢带温度降温至350℃以下。优点在于:实现工业化连续生产无取向硅钢极薄带，有效提高产能，生产的无取向硅钢极薄带具备高磁感、低铁损等磁性能。

本发明涉及涂层液技术领域，且公开了取向硅钢绝缘涂层液，其配比为：二氧化硅10‑15%、硼酸5‑8%、磷酸二氢盐2‑5%、金属溶胶20‑25%、氢氧化铝占5‑6%、有机酸处理的复合盐溶液20‑30%、分散剂0.5‑1%，其余为水，采用硅溶胶作为辅助成膜物，粘结力较强，对附着性影响很大。硅溶胶能够很均匀地包裹在被胶结物质的表面，通过自干成膜，保持了很高的常温结合强度；而磷酸盐涂层的固化是通过受热分解，脱水聚合完成的，低温强度差，中温强度高，充分利用了硅溶胶低温的结合强度和磷酸盐中、高温时的结合性能，消除了常规涂层烘烤时容易出现的收缩、起泡现象，阻止了微气孔的形成，提高了涂层的表面光滑度，粘结强度和稳定性同时保持绝缘涂层的光泽、光滑和稳定性。

针对马钢无取向电工钢孔洞缺陷的分布规律及形貌特征,对缺陷样进行了显微分析,并利用生产实绩数据分析了该缺陷产生的原因。结合热轧生产过程,主要通过避免带钢撞击导卫以及降低导卫结瘤的产生等措施,可有效抑制热卷异物压入产生,从而降低冷轧工序孔洞的产生。 In viewing of the distribution and morphology characteristics of the hole defect of non-oriented electrical steel in Maanshan Iron and Steel Co.,Ltd.,the causes of the defect were analyzed by micro analysis of the defect sample and the production data.Combined with the production process of hot rolling,by avoiding the impact of strip steel on the guide and reducing the nodule formation on the guide,the pressing of foreign bodies in hot coiling could be effectively suppressed,thus reducing the fo... 

本实用新型公开了一种硅钢片制作用防止硅胶泄露结构，包括运行组件与固定密封组件，所述运行组件的内侧壁设有固定密封组件，所述运行组件包括板体、第一凹槽、壳体、硅钢片、支撑板、连接块、密封圈、防护板和通孔，所述板体的内侧壁开设有第一凹槽，所述第一凹槽的内部设有壳体，所述壳体的内侧壁设有硅钢片，所述硅钢片的两侧相互对称焊接有四个连接块，四个所述连接块相斥一侧均贴合于第一凹槽的内侧壁，本实用新型首先通过硅钢片两侧密封圈保障密封效果，设置的橡胶管起到二次密封防护作用，并借助其内部的弹簧及U型板实现防偏移的效果，最后一方面可以在壳体相邻组件内侧加胶并且提高其内部硅钢片的厚度，以此实现多重密封防漏。

本实用新型公开了一种电工钢出炉水雾冷却装置，包括冷却箱和电工钢本体，所述冷却箱的顶部内璧固定有等距分布的第一支管，且第一支管的一端固定连接有第一进水管，所述冷却箱的底部固定有对称分布的两个支撑板，且支撑板的相对侧外壁靠近顶端转动连接有等距分布的辊轮，所述冷却箱的底部内壁和支撑板的上表面均固定有第二支管，所述第一支管和第二支管的圆周外壁均固定有等距分布的喷头。本实用新型水雾分别进入第一支管和第二支管后，从喷头喷出，对电工钢本体的上下两面喷洒降温，水雾均匀的附着于电工钢片的表面，并实现冷却作业，提高冷却效率，也保证了硅钢片的质量，避免硅钢片表面冷却不均匀致使厚度不一。

以取向电工钢成分为基础,制备了含C或Mn和S的4种实验钢。观察了接近平衡析出状态实验钢经60%冷轧后在600～1000℃范围再结晶退火过程中微观组织演变,统计分析了再结晶体积分数随退火时间的变化规律,进而计算了各实验钢静态再结晶的激活能。观察了高含C实验钢退火初期再结晶晶粒优先出现的部位。结果表明900～1000℃范围内各实验钢铁素体的化学成分相似,因而其再结晶激活能基本一致。在600～800℃范围内铁素体内会有阻碍再结晶进程的三次渗碳体析出,从而使再结晶激活能明显提高。高C含量实验钢中还会有从奥氏体转变而来的粗大珠光体或渗碳体,轧制过程中其附近形成的变形区会促进600～800℃加热时该区域附近率先发生再结晶形核、降低再结晶激活能。固溶的Mn、S元素可微弱提高再结晶激活能,但高Mn、S含量会改变粗渗碳体从奥氏体析出时的形态。 Four experimental steels based on grain oriented electrical steel containing C,or Mn and S were prepared.Microstructure evolution of the steels close to a state of equilibrium precipitation were observed during annealing processes at 600-1000 ℃after 60% cold rolling,the changes of recrystallization volume fraction were analyzed statistically as the annealing was prolonged,and the activation energy for static recrystallization of the steels were calculated.The locations,where the recrystallizatio... 

考虑剪应变对微孔洞损伤演化的影响,对GTN损伤模型的损伤演化机制进行修正,建立了适用于不同应力三轴度水平的损伤模型。结合隐式应力更新算法和显式有限元计算,采用VUMAT子程序实现了修正GTN模型在有限元软件ABAQUS中的数值计算。通过模拟纯剪切和剪切-拉伸两组试样的损伤演化和断裂行为,验证了修正GTN模型在不同应力三轴度承载条件下的有效性。运用修正GTN损伤模型模拟含边部缺口的带钢在轧制过程中裂纹的萌生和扩展行为,模拟结果与实验相一致,表明该模型可有效地用于带钢缺陷在轧制过程中扩展行为的分析和预测。模拟和实验结果表明,带钢边部缺口在轧制过程中,缺口前沿和后沿均会萌生裂纹,且后沿裂纹扩展更为明显。 Considering the effect of shear strain of micro-void on damage evolution, a modified GTN model applicable to various stress triaxiality conditions is proposed by modifying the damage evolution mechanism of the GTN damage model. The modified model is implemented in commercial finite element software ABAQUS by combining the implicit stress update method with an explicit finite element solving algorithm and through the user-defined material subroutine VUMAT. The damage evolution and the failure pro... 

{100}织构因具有两个易磁化方向能够明显的提高磁性能,因此如何在表面获得具有{100}织构一直是无取向电工钢研究焦点。本文主要介绍了获得{100}织构的主要工艺方法及其基本原理,并结合实际生产过程对各工艺方法的优缺点进行了分析;一方面,优化无取向电工钢的成分,降低碳、锰元素含量以避免脱碳退火和真空退火,简化生产工艺;另一方面,调节升温速度、降温速度和退火气氛,使{100}晶面的表面能或弹性应变能最低,制备具有{100}织构柱状晶组织的无取向电工钢是今后的发展方向。 Because { 100} texture has two easy magnetization directions,which can significantly improve magnetization properfies,how to develop { 100} texture is a focus for researchers and manufactures. In the paper,main manufacturing processes and basic principle are introdued,and their advantages and disadvantages in practical production are analyzed. On the one hand,the production process can be simplified by optimizing chemical compositions,such as reducing the content of C and Mn,which can avoid deca... 

本实用新型公开了一种硅钢板带运输使用的固定设备，所述壳体的侧壁固定连接有多个第一放置轴，所述壳体的侧壁固定连接有多个第一限位套，且第一限位套与第一放置轴同轴心，所述第一限位套的内部设置有第一压板，所述壳体的内部设置有第一滑槽及第二滑槽，所述壳体的一侧设置有滑板。本实用新型通过将硅钢板带卷起后用绑线绑紧后，放入第一放置轴外表面后推入第一限位套内部，放好一行成硅钢板带后将将第一个滑板底部的滑杆放入第一滑槽内，推动滑板进入壳体内，使插杆插入凹槽内，再对下一列的硅钢板带进行放置，安装完成后，将挡板放入第二滑槽内，推动滑板向壳体内移动，将挡板向壳体内移动。

采用硅钢自动测量装置及X射线衍射仪检测出样品在实验前后的磁性能参数和织构强度.结果表明:较低的电压、9 Hz、较长的处理时间以及退火温度为650℃有利于增高铁损降低比例;较低的电压、较高的频率以及退火温度为650℃有利于增加磁感应强度增高比例.最佳的提高磁性能的实验参数是:频率为9 Hz,电压为500 V,处理时间为6 min,退火温度为650℃.通过织构分析可以验证:取向硅钢磁感应强度的变化取决于{110}<001>晶粒取向度值,而{110}<001>取向度值可看成是一个反映总体平均偏离角大小情况的综合值. An automatic measurement system for silicon steel and an X-ray diffraction meter were used for measuring the magnetic property parameters and texture of ex-processed samples and processed samples.It is shown that under the condition of a lower voltage,9Hz,a longer processed time and an annealing temperature of 650℃,the decrease rate of iron loss can be increased;a lower voltage,a higher frequency and an annealing temperature of 650℃ are in favor of improving the increase rate of magnetic inducti...