提出一种基于粒子群优化算法实现的硅钢涂层厚度近红外光谱检测新方法。首先,采用近红外光谱仪采集获得了硅钢表面绝缘涂层的近红外光谱,然后,采用离散粒子群算法筛选出近红外光谱数据的最佳波长变量并组成新的光谱数据,最后,建立涂层厚度的核偏最小二乘定量分析模型。实验显示,所建定量分析模型对检验样本分析的绝对误差范围为-0.12～0.19μm,最大相对误差为14.31%,完全符合现场检验需要。研究表明,离散粒子群算法可以有效地筛选出携带更多有用信息的波长变量,提高定量分析模型的分析准确度和速度,是一种有效的近红外光谱波长筛选方法,同时,近红外光谱法也是一种有效的硅钢绝缘涂层厚度检测方法。 A novel thickness measurement NIR spectrometry for surface insulation coating of silicon steel based on discrete binary particle swarm optimization(DBPSO) algorithm is presented.First,we used NIR spectrometer to collect the NIR spectra of insulation coating of silicon steel,and then,DBPSO algorithm was used to select the optimal wavelength variates and composed a new spectra set.Last,the authors created the thickness quantitative analysis model using kernel partial least square algorithm.The exp... 

本实用新型公开了一种用于硅钢板带的表面清理装置，包括机体，所述机体的内部设置有转动机构，所述转动机构的内部安装有固定机构，所述机体的外表面一侧固定连接有驱动电机，所述驱动电机的输出端固定连接有螺杆，所述螺杆的外部设置有螺纹套，且螺纹套在螺杆上螺纹转动连接，所述螺纹套的底部固定连接有电动推杆，所述电动推杆的输出端固定连接有连接板。本实用新型，利用转动机构可很好的进行翻转，便于对两面进行清理，从而提高了一定的工作效率，相比人工翻转清理时效果更好，具有一定的实用性，利用固定机构可很好对于成硅钢板带进行固定，可方便进行清理，提高清理时的工作效率，实用性较强。

在现普通冷轧无取向硅钢的基础上,降低Si含量,复合添加少量辅助元素,组合热轧板处理和成品退火加热技术,研制出了免常化处理的高磁感、低铁损并具有良好耐酸腐蚀性能的新系列无取向电工钢。 Based on existing common cold rolled non-oriented silicon steel,a new series of non-orientedelectrical steel with high induction,low core loss and excellent anti-corrosion property has been developed by reducing Si element,adding complexly a small amount of supplementary elements,and employing combined treatment of hot rolled sheet and finished product annealed heated technology. 

本发明一种解决取向硅钢热轧板晶粒粗大的方法，在取向硅钢的成分设计中减少固溶温度较高的MnS的含量，降低铸坯加热温度，同时计算实际取向硅钢成分中γ‑相含量与温度之间的关系，依据计算结果设计取向硅钢的热轧工艺，可以保证20％～30％的γ‑相数量，成功解决取向硅钢热轧板晶粒粗大的问题。

本实用新型涉及物料混合技术领域，尤其为一种用于硅钢绝缘涂料温控反应釜，包括反应釜，所述反应釜右侧上方固定连接有输料管，所述输料管右端面固定连接有电机外壳，所述输料管右侧上方内部固定连接有入料管，所述电机外壳内部右侧固定连接有第二电机，所述第二电机左侧顶端转动连接有输料轴，所述反应釜上端面固定连接有第一电机；本实用新型中,通过设置的输料轴，能将物料慢慢输送至反应釜内，防止一次性将物料倒入反应釜中发生强烈反应，并且将小块物料放置进入料管时，可以在入料管内进行堆积，而第二电机旋转带动输料轴运动时，可以将入料管底部的物料卷进输料轴的空隙中，移动至顶端，物料会自动落下，非常方便。

本发明的一种超低碳含钇取向硅钢及其制备方法，化学组成及质量百分比为Si：2.0～4.5％，C：≤0.003％，Y：0.001～0.1％，Mn：0.1～0.25％，Al：0.01～0.02％，Cu:0～0.3％，S：0.02～0.035％，N：0.009～0.011％，其余为Fe和不可避免的杂质元素。生产工艺为：连铸、铸坯加热、热轧、常化、冷轧、初次再结晶退火、二次再结晶退火。本发明采用超低碳的成分，取消了常规取向硅钢脱碳退火工艺，简化了生产流程。通过稀土微合金化解决了因超低碳成分导致的单向铁素体组织抑制剂析出困难的技术难题。本发明制备的含钇取向硅钢厚度为0.2～0.35mm，磁感应强度B8为1.85～1.94T，铁损P17/50为0.9～1.2W/kg，可以用于变压器的铁芯材料，制备流程更为简洁。

概述了无抑制剂法生产取向电工钢的特性及其用途;总结无抑制剂生产取向电工钢的原理及工艺方案.重点讨论了成分方案,即元素对磁性能的影响和最终高温退火方案对二次再结晶的影响.研究结果表明,无抑制剂取向硅钢化学成分范围没有普通取向硅钢和高磁感取向硅钢严格,提高了成材率;最终高温退火决定了二次再结晶的好坏,从而最终决定成品磁性能,最佳的高温退火温度在850～950℃之间. This article provides an overview on the characteristics and uses of inhibitorless process producing grain-oriented electrical steels.The mechanism of inhibitorless process and technology programs were discussed.The results show that the chemical composition and final annealing were determined according to magnetic properties.The inhibitor-free grain oriented silicon steel has loose range of chemical composition;Secondary recrystallization occurs mainly in the final annealing and the best anneal... 

作为一种具有优异高频铁磁性能的合金,Fe-6.5%Si(质量分数)高硅钢在高频工况条件下降损效果明显,对电气行业应用器件高频化、小型化、节能等具有十分重要的意义。通过与取向硅钢测量B-P数据对比,验证了高硅钢高频超低损特性,且轧制高硅钢与日本CVD法生产高硅钢存在基本相同的铁损值。采用国标Epstein Square法对0.30mm高硅钢薄板进行单片测试,并对由0.30mm高硅钢薄板首次装配成的电感器进行铁损测试,对比测试结果表明,元件测试与单片测试数据基本吻合,高磁感应强度条件下,元件测试结果略低于单片测试,分析原因为:线圈引起励磁压降;元件叠片间出现短路,电流增大,损耗增加;气隙板厚度过大。 As one core material with excellent high-frequency ferromagnetism,Fe-6.5%Si performs obviously reduction on core loss in high field frequency which means much to high frequency,minimization,energy conservation in electric industry.Super low loss was verified by drawing B-P curves based on detected experimental data,and which went equal to Fe-6.5%Si thin strip fabricated by CVD in Japan.Fe-6.5%Si was firstly fabricated as inductor in this research,and its core loss was determined for comparison w... 

本发明涉及冶金技术领域，具体涉及一种多组分{100}织构无取向电工钢的制备方法。本发明通过控制薄带连铸参数制备1.5～2.5mm厚的无取向电工钢铸带，直接冷轧至厚度为0.35～0.50mm后，先进行预回复退火，再进行成品退火，此过程中控制退火温度、时间以及升降温速率。本发明所制备的无取向电工钢具有多组分{100}织构，包括{100}＆lt;001＆gt;、{100}＆lt;012＆gt;和{100}＆lt;011＆gt;，{100}织构组分体积分数达到25～39％，其轧向磁感值1.71～1.78T，横向磁感值1.70～1.76T，板面45°方向磁感值达到1.65～1.67T。本发明通过优化退火工艺，利用{100}变形组织的强回复与再结晶协同作用，从而显著增强{100}退火织构，方法简单有效。

通过热力学计算及实验室研究,对钙处理前后50W600无取向硅钢退火冷轧板中夹杂物的类型、数量及尺寸进行了系统分析。结果表明,50W600无取向硅钢经钙处理后(w(Ca)=0.002 6%),钙在1 600℃的钢液中主要以固态的CaO·2Al2O3、CaO·6Al2O3及溶解钙的形式存在。在钢液的凝固过程中,钢中的溶解钙和硫反应生成了CaS和CaS-MnS复合夹杂,有效抑制了MnS的弥散析出,减少了钢中微细夹杂物的数量。同时钙处理促进了钢中微细夹杂物的聚合长大,导致显微夹杂物的数量增加。 Based on thermodynamic calculation and laboratory experiment,the type,quantity and size of inclusions in annealed cold-rolled steel sheets of 50W600 non-oriented silicon steel before and after calcium treatment were systematically studied.Results showed that after calcium treatment(w(Ca) = 0.002 6%),calcium was mainly in the form of CaO·2Al2O3,CaO·6Al2O3 and dissolved calcium in steel at 1 600 ℃.Dissolved calcium could combine with sulfur to form CaS inclusions and compound CaS-MnS inclusions du... 

【摘要】 <正>近日,世界上最先进的硅钢冷连轧酸轧...

一种分步调控制备高磁感高强度无取向电工钢的方法，按以下步骤进行：(1)按设定成分采用转炉冶炼钢水，制成连铸坯，含C0.001～0.008％，Si1.5～4.8％，Cu0.5～2％，Ni0.5～1.5％，Al0.2～1％，Mn0.2～1.5％，P＆lt;0.005％，S＆lt;0.005％，其余为Fe；(2)将连铸坯置于均热炉保温，多道次热轧相邻两道次间隔时间为30～180s；空冷；(3)常化处理；(4)多道次冷轧；(5)退火处理；(6)时效处理。本发明的方法成本较低、工艺简单，生产的无取向电工钢兼具优异的力、磁性能，能够很好的满足驱动/牵引电机的使用需求。