本发明涉及电工钢的生产方法，更具体地说，涉及一种预应力生产中低牌号无取向电工钢的方法，包括铁水预处理；预处理后的铁水进行转炉冶炼并吹氩脱氧；吹氩后的钢水送入精炼炉中进行冶炼并加入低碳合金进行合金化；合金化处理的钢水通过薄板坯连铸机铸成板坯并采用薄板胚连铸连轧生产工艺进行轧制获得热轧板；所述热轧板经过酸洗冷轧，随后进行预应力拉伸并退火，采用涂层进行涂镀、烧结后卷取。本发明采用预应力拉伸，改善无取向电工钢退火前钢板内部应力的分布，制备的冷轧无取向电工钢产品的电磁性能P15/50≤5.4W/kg，磁感应强度≥1.72T，板形同板差≤8um。

通过金相分析和电子背散射衍射技术研究了一种新型含铜无取向电工钢在950℃退火不同时间(3～180s)空冷后的组织和织构取向的演变。结果表明:该钢在退火3s时的主要织构为α和γ线织构,{100}<110>织构最强;退火20s时织构以<111><112>、{111}<110>、{112}<110>、高斯织构和立方织构为主,随着退火时间的延长,高斯织构和立方织构强度呈减弱趋势;合理控制保温时间有利于提高{100}、{110}面织构的占有率。 Evolution of microstructure and texture oriented of a new non-oriented electrical steel during annealing at 950℃for different times(3-180) s and air cooling was studied by metallography and electron back-scattering diffraction analysis.The results show that after annealing for 3 s most of the texture oriented alongα-fibre andγ-fibre,the intensity of {100}〈110〉was the strongest.{111}〈112〉,{111}〈110〉,{112}〈110〉,Gauss texture and cube texture were the main texture after annealing for 20 s,with the ... 

借助OM、激光共聚焦显微镜、质谱仪和电解萃取等设备和方法，研究了添加微量稀土La（质量分数0.001 1%）的取向硅钢在轧制前采用不同加热保温时间对抑制剂固溶行为的影响。结果表明：当稀土取向硅钢在1 250℃分别保温10、20、30 min后，试验钢晶粒尺寸随保温时间延长有先快后慢的长大趋势；三种抑制剂元素Mn、Cu和Al均发生固溶，保温时间对Mn和Cu两种元素的固溶影响明显，固溶量分别由69.8%和43.7%增加至84.2%和85.2%；随着保温时间的延长，稀土取向硅钢中抑制剂的小尺寸未溶物逐渐减少直至消失，较大尺寸未溶物（300～600 nm）逐渐转变为小尺寸未溶物逐步溶入基体中，数量减少且未溶物的类型由复杂逐渐转变为单一。 In this paper the solid solution behavior of the inhibitor under various holding time in 0.001 1 %La oriented silicon steel during reheating had been investigated by using OM, LM, methods of electrolytic extraction and mass spectrometer. The results showed that grain size of the test steel increased significantly with the holding time prolonging when the rare earth oriented silicon steel was heated to1 250 ℃ and held for 10, 20 min and 30 min respectively, and the growth trend slowed down after ... 

本实用新型公开了一种镀铝锌硅钢钣冲压装置,包括安装板，所述安装板的上表面延伸至下表面开设有上下管贯通的板件交换槽，所述安装板的上表面且位于板件交换槽的正上方通过固定螺栓固定连接有模座板。本实用新型，通过设置二次镀膜箱，对冲压后的硅钢钣进行二次铝锌镀膜，避免了冲裁面的暴露导致硅钢钣慢性腐蚀，提升了镀铝锌硅钢板的质量和使用寿命，通过设置夹取机构，对硅钢钣自动取放操作，减少了人力操作，提高了效率的同时，提高了设备安全性，通过设置废料回收槽，对冲压产生的边角料进行集中回收在利用，提升了生产过程中的环保性，通过优化结构设计，提高了镀锌硅钢钣的生产效率，降低生产成本。

1.本外观设计产品的名称：硅钢片横剪线。;2.本外观设计产品的用途：对硅钢片料带的冲切、裁断。;3.本外观设计产品的设计要点：在于形状与图案的结合。;4.最能表明设计要点的图片或照片：立体图。;

采用双辊连铸工艺制备了硅的质量分数分别为0.5%,1.0%,3.0%,4.5%的硅钢薄带,用光学显微镜观察其组织,并研究了后处理工艺对薄带组织和性能的影响。结果表明:硅含量为0.5%和1.0%的薄带适合采用一次冷轧+850～950℃退火的后处理工艺,而硅含量在3.0%以上的薄带适合采用二次冷轧+950℃退火的后处理工艺;硅含量为3.0%和4.5%的薄带在冷轧并950℃退火后,其磁性能最佳,铁芯损耗约为4.30 W·kg^-1,磁感应强度约为1.68T。 Silicon steel thin strips with silicon content of 0.5wt%,1.0wt%,3.0wt%and 4.5wt%were prepared by twin-roll continuous casting process,and the microstructure of the strips were observed by means of optical microscopy,and on the basis,the effect of post-treatment process on microstructure and properties of the strips was studied.The results show that the post-treatment process of one-time cold rolling and annealing between 850—950℃was suitable for the strips with silicon content of 0.5wt%and 1.0wt... 

本发明公开了一种普通级稀土取向硅钢制备方法，通过添加稀土元素，利用第二相作用，对铸坯组织、热轧组织、初次再结晶晶粒和二次再结晶晶粒的影响，改善成品磁性能，即降低铁损，提高磁感。

【作者】 罗海文； 向睿； ...

在现普通冷轧无取向硅钢的基础上,降低Si含量,复合添加少量辅助元素,组合热轧板处理和成品退火加热技术,研制出了免常化处理的高磁感、低铁损并具有良好耐酸腐蚀性能的新系列无取向电工钢。 Based on existing common cold rolled non-oriented silicon steel,a new series of non-orientedelectrical steel with high induction,low core loss and excellent anti-corrosion property has been developed by reducing Si element,adding complexly a small amount of supplementary elements,and employing combined treatment of hot rolled sheet and finished product annealed heated technology. 

针对马钢无取向电工钢孔洞缺陷的分布规律及形貌特征,对缺陷样进行了显微分析,并利用生产实绩数据分析了该缺陷产生的原因。结合热轧生产过程,主要通过避免带钢撞击导卫以及降低导卫结瘤的产生等措施,可有效抑制热卷异物压入产生,从而降低冷轧工序孔洞的产生。 In viewing of the distribution and morphology characteristics of the hole defect of non-oriented electrical steel in Maanshan Iron and Steel Co.,Ltd.,the causes of the defect were analyzed by micro analysis of the defect sample and the production data.Combined with the production process of hot rolling,by avoiding the impact of strip steel on the guide and reducing the nodule formation on the guide,the pressing of foreign bodies in hot coiling could be effectively suppressed,thus reducing the fo... 

本实用新型提供一种对硅钢片横剪线片料进行穿针叠柱与输送的装置，包括输送装置、穿针定位装置、纵向移动平台和转运装置，所述的输送装置设在纵向移动平台上方，所述的穿针定位装置位于输送装置底部，穿针定位装置固定在纵向移动平台上，所述的转运装置布置在输送装置的输出侧；所述的转运装置通过对接机构与输送装置对接。本实用新型能够完成硅钢片的穿针叠柱，并将此硅钢片柱整体输送到指定工位。本实用新型采用输送装置和穿针定位装置的上下分层布置结构，首先完成了硅钢片的穿针定位，然后完成硅钢片柱的整体输送，整个工艺方法中不使用吊运设备，提高了生产效率。

一种甩带法制备高磁性能含磷硅钢薄带的方法，属于合金材料领域。本发明以硅钢(Fe‑(3‑6.5)wt.％Si)块体为母合金，并添加一定量的硅铁合金及磷铁合金，放置于中频感应炉中，熔融后经快速凝固‑甩带、冷轧、热处理工艺，得到具有优异性能的含磷硅钢薄带。对于硅钢而言，P元素的少量加入能够有效的提升电阻率从而显著降低铁损，且具备优化软磁性能的作用。而采用甩带法能够充分利用其快速凝固的特征，从根本上避免了P元素在传统熔炼冷却过程中严重偏析的缺陷，极佳地保证了产品的组织优势与软磁性能。本发明具有操作简单、生产效率高、产品精度高、工艺流程短、无污染与夹杂、性能优异等优点。