硅钢资料

【作者】 马芳； 张春红； ...

研究了卷取工艺对一种新型含铜无取向电工钢晶粒尺寸、织构演变、铁损和磁感应强度的影响。结果表明,试样织构组分主要为{111}、{112}、{100}和高斯织构,在550℃卷取、保温2～3h,{100}织构有增强趋势,磁感应强度较高,铁损较低。 The effects of coiling process on grain size,texture,core loss and magnetic induction of a new cold rolled non-oriented electrical steel with copper were investigated.The results show that there are mainly {111},{112},{100} and {110}<001> texture.Coiling at 550℃and keeping for 2～3 hours,the {100} texture is enhanced,magnetic induction is higher and core loss is lower. 

介绍了电工钢生产线连退机组的表面处理工艺,特别是电解清洗系统的工作机理、设备构造、生产工艺及各种影响因素。 This paper introduces the technology of surface treatment of continuous annealing unit in electrical steel production line,in particular the working mechanism,structure of equipment,production techniques and various influence factors of the electrolytic cleaning system. 

【作者】 O.M.Гбанов； A.E.Чеглов； ...

本发明提供虽然为薄壁但磁特性优异的方向性电磁钢板的制造方法。本发明的一个方案提供一种方向性电磁钢板的制造方法，其包括热轧工序、任选的热轧板退火工序、酸洗工序、冷轧工序、一次再结晶退火工序、成品退火工序和平坦化退火工序，在酸洗工序中，使用包含0.0001g/L～5.00g/L的Cu的酸洗溶液，冷轧钢板的板厚为0.15mm～0.23mm，一次再结晶退火工序的升温工序中的30℃～400℃的温度区域的平均升温速度超过50℃/秒且为1000℃/秒以下。

本发明公开了一种极薄取向硅钢铁芯及其制造方法，所述制造方法，包括：S1、剪切分条：将取向硅钢根据制作铁芯的宽度要求进行分条剪切；S2、卷绕：根据铁芯的规格型号要求，选取铁芯模具进行卷绕；S3、压块固定：将卷绕好的铁芯用压块固定；S4、退火加工：将固定好的铁芯，阶梯式升温至780℃保温3h退火处理，保护气氛为氮气，之后冷却降温；S5、浸胶：将降温后的铁芯，进行真空浸胶处理；S6、烘干：将浸胶处理后的铁芯烘干处理；S7、装配。该发明制造的极薄取向硅钢铁芯，能彻底消除内应力，磁路各处均无高磁阻存在，空载电流与励磁电流均大幅度下降，从而最大限度的恢复了极薄取向硅钢加工后原有择优取向织构及电磁性能。

本发明提出一种预判取向硅钢冷轧脆断发生的方法，将酸洗带头20‑30cm进行剪切取样，在取到的样板上面注明工作侧和传动侧；将取好的样板送至焊缝检测冲压机处，通过冲压机对样板进行冲压，根据不同钢带厚度，设定不同冲孔机压力，对样板进行冲压后，通过观察裂纹形貌，预判常化卷在冷轧轧制过程中是否会发生脆断，本发明使带钢在冷轧前能够制定相应的对策措施，从而降低冷轧断带所产生的损失。

本发明的一种方式的无取向性电磁钢板用热轧钢板，以质量％计含有：C：0.0050％以下、Si：0.5％以上3.5％以下、Mn：0.1％以上1.5％以下、Al：0.1％以上1.5％以下、Cu：0.01％以上0.10％以下、Sn：0.01％以上0.20％以下；剩余部分由Fe和杂质构成；在从表面到深度10μm的范围内，具有0.12％以上的Cu的浓度峰值。

本实用新型公开了一种硅钢片分流导料机构，属于硅钢片导料领域，包括传送带，所述传送带包括主带和副带，所述副带设置在主带的前面，所述主带横向设置，所述主带的后面设置有导流机构，所述导流机构包括电机、导流板和助力组件，所述主带的后面设置有安装架，所述安装架的顶部竖向固定连接有连接板，所述电机安装在连接板上，所述电机的输出轴与导流板的顶部固定套接，通过启动电机，电机带动导流板旋转，导流板在连接组件下带动助力组件旋转，使得主带上的物品被导流板进行阻挡，通过助力组件传送到副带上，避免了传送带方向单一，容易导致硅钢片对堆积的问题，从而减少硅钢片的损坏量，进而节约成本。

对高牌号无取向电工钢35W300的成品进行了第二次退火,对第二次退火后的成品性能、纵横向磁性能差异和组织变化进行了分析。结果表明,随着第二次退火温度的升高,晶粒长大,磁性能优化。铁损平均值下降0.087 5W/kg,磁感平均值升高0.008T。第二次退火温度为820℃的产品的磁性能能够满足用户使用要求。 The product of high grade non-oriented electrical steel 35W300 was annealed at the second time.Microstructure,the difference of magnetic properties in the vertical and horizontal and were studied.The results show that the grain grew up and magnetic properties optimized with the increase of annealing temperature for the second time.Iron loss average declines in 0.0875 W/kg,magnetic induction average increases 0.008 T.The magnetic properties can meet the requirements of users at the second anneali... 

采用\"热轧复合+冷轧减薄+退火\"方法成功制备了0.20mm厚的硅浓度梯度高硅钢薄带,并采用SEM和X射线衍射技术对制备过程中组织和织构演变进行了研究。热轧复合板微观组织呈明显层状分布,复合界面为紧密冶金结合且经过83%的大冷轧变形未开裂。热轧和冷轧复合板带中均形成强α和γ织构,再结晶退火后形成强γ织构。冷轧和退火织构沿板厚呈显著的梯度分布特征,其主要来自于复合界面两侧硅浓度和初始热轧织构的差异性以及冷变形的不均匀性。 Gradient high silicon steel thin sheets with thickness of 0.20 mm were successfully produced by the rolling and annealing method,including hot rolling bonding,cold rolling,and annealing.Microstructure and texture evolution was investigated by means of SEM and X-ray diffraction.Microstructure of hot-rolling-bonding shows obviously layered distribution,the composite interface was closely metallurgical bonding and no cracking appears even after 83%cold rolling.Strongαandγfibers develop in the hot a... 

在实验室模拟CSP流程制备了不同含量稀土铈(质量分数0~0.018%)的1.2%Si无取向电工钢,并对其进行1 000℃×5min的再结晶退火处理,研究了铈质量分数对无取向电工钢夹杂物、显微组织、再结晶织构和磁性能的影响。结果表明:随着铈质量分数的增加,微细夹杂物数量、再结晶晶粒尺寸、{100}和{110}织构组分、磁感应强度先增后减,{111}织构组分、铁损先减后增;铈的质量分数为0.005 1%时,钢中的夹杂物数量最少,再结晶晶粒尺寸最大,有利织构最多,磁性能最优,铁损P15/50为3.253W·kg-1,磁感应强度B50为1.751T。 Non-oriented electrical steels containing different contents rare earth Ce element(0-0.018wt%) were prepared in the laboratory by simulated CSP(compact strip production)process,and then recrystallization annealing at 1 000 ℃ for 5 min were performed,the effects of Ce content on inclusion,microstructure, recrystallization texture and magnetic properties of non-oriented electrical steels were studied.The results show that with the increase of Ce content,the amounts of fine inclusion,the size of re...