采用X射线衍射仪分析无取向硅钢冷轧织构和再结晶退火织构的演化,研究了热轧组织对无取向硅钢织构以及磁性能的影响。结果表明,具有均匀、粗大晶粒组织的热轧板,冷轧形成更多的剪切带,导致成品板形成高的高斯织构组分,并提高了{100}织构强度,降低了γ纤维织构,最终导致成品磁感应强度升高,铁损下降。 The texture evolution of non-oriented silicon steel during cold-rolling and recrystallization annealing was investigated by X-ray diffractometer.The effects of hot band microstructure on the texture and magnetic properties of non-oriented silicon steel were analyzed.The results show that more shear bands appear during cold rolling due to homogeneous coarse grain in hot band.So strong{110}<001> texture after recrystallization annealing forms.At the same time,the {100} texture components inc... 

【作者】 朱一知； 陈山； ...

本发明相对于板厚较薄的电磁钢板提供不会导致磁特性劣化的基于激光的加工方法。在对电磁钢板进行使用激光的熔断并将该电磁钢板加工成规定的形状的电磁钢板的加工方法中，使上述激光的扫描速度成为10000mm/min以上来进行上述熔断。

根据本发明的一个实施例的无取向电工钢板，以重量％计，所述钢板包含Si：2.2至4.5％、Mn：0.5％以下且0％除外、Al：0.001至0.5％、Sn：0.07至0.25％和N：0.0010至0.0090％，余量包含Fe和不可避免的杂质。所述钢板包含从钢板表面向内存在的表层部和存在于表层部里面的中心部，中心部包含0.005重量％以下的N，所述表层部比中心部更包含0.001重量％以上的N，表层部的平均晶粒粒径为60μm以下，中心部的平均晶粒为70至300μm。

本发明涉及硅钢卷取领域，具体涉及提高硅钢收卷速度的卷取系统，包括机架、第一卷取辊、第二卷取辊、第三卷取辊和切捆机构，第一卷取辊、第二卷取辊和第三卷取辊依次转动设置于机架上；切捆机构包括切割刀、挤压板和成卷的胶带，切割刀竖直滑动设置于第一卷取辊和第二卷取辊的上方，切割刀上固定有两个支撑条，两个支撑条之间设置有支撑辊，成卷的胶带套设于支撑辊上，切割刀上还设有供胶带穿过的通槽；挤压板内设有装有墨水的盛墨腔，挤压板一侧的两端固定有排墨管，排墨管与盛墨腔连通，且排墨管与切割刀的侧壁转动连接。采用本技术方案时，有利于提高硅钢卷取效率。

以试验室模拟CSP工艺生产的Fe-3Si热轧钢带为研究对象,采用正交试验及方差分析的方法,研究了取向硅钢初次再结晶退火工艺对高温退火后获得锋锐的高斯织构的影响。结果表明:取向硅钢两段式初次再结晶脱碳退火工艺参数加热段保温时间及加热温度是高温退火后获得锋锐高斯织构的主要影响因素,其可信度分别在90%和85%以上;在本试验条件下,通过正交试验获得的最佳退火工艺为:冷硬板经600℃保温3 min和850℃保温6 min。 Fe-3Si hot rolled strip was produced by simulating CSP technology in the laboratory.Orthogonal experiment and analysis of variance were carried out to investigate the influence of primary recrystallization on the sharp Goss texture of the oriented silicon steel.The results show that holding time of the heating section and the heating temperature for a sharp Goss texture of the samples annealed has important implications in this experiment conditions,the two-step decarburization annealing process... 

本发明提供一种改善表面麻点缺陷的薄规格中低牌号无取向硅钢及其生产方法，成分C≤0.0025％，1.2≤Si≤1.65％，0.25％≤Mn≤0.35％，0.06％≤P≤0.11％，0.1％≤Als≤0.2％，S≤0.0025％、N≤0.0025％，Ti≤0.0025％，其余为Fe及不可避免的杂质。与现有技术相比，本发明采用较低氢气浓度，防止炉内氧化铁皮还原，减轻碳套辊的腐蚀程度，减少碳套辊结瘤率，改善带钢表面质量；采用合理合金成分设计，提高带钢的力学强度，降低碳套辊结瘤对带钢表面的影响程度，改善带钢表面质量。产品厚度为0.35mm，板面麻点发生率降低，无手感，且辊身周长周期范围内麻点个数≤5个。

研究了含铜低碳低硅无取向电工钢中的析出相及其析出机理.由能谱(EDS)及选区电子衍射(SAED)分析可知,铁素体基体上存在的大量弥散分布的等轴状析出相为类B2结构的铜.这些铜析出相的析出机理可以是一般析出、位错析出、台阶机理相间析出和弓出机理相间析出:一般析出在550、650和750℃三个等温温度均可发生;位错析出只发生在较低的等温温度(550℃),此时析出相呈特殊的平行短列状;台阶机理相间析出也可在上述三个等温温度下发生,但650℃等温时最有利于台阶机理相间析出,此时析出相平直列状分布;弓出机理相间析出只发生在较高的等温温度(750℃),析出相弯曲列状分布. Precipitates in low-carbon low-silicon non-oriented electrical steel containing Cu were studied and the precipitation mechanism was analyzed by means of energy dispersive spectrometry(EDS) and selected area electron diffraction(SAED).It is found that the equiaxed precipitates of Cu with B2-like structure distribute dispersively in the non-oriented electrical steel.The precipitation mechanism involves general precipitation,dislocation precipitation,interphase precipitations formed by the ledge me... 

利用背散射衍射技术(EBSD)和XRD,研究了两段式脱碳退火工艺对取向硅钢纵截面初次再结晶的微区取向、取向差分布、特殊晶界(CSL)及高温退火试样高斯织构。分析了初次再结晶晶界特征对取向硅钢高温退火后宏观织构的影响。结果表明:初次再结晶的纵截面基体中Σ3和Σ5晶界使得高斯晶粒有着较高的迁移率,在高温退火时借助20o～45°的大角度晶界的界面能吞并周围{111}<112>晶粒迅速长大,形成密度水平较高的高斯织构。 Micro area orientation of primary recrystallization,the misorientation distribution,special boundaries under different two-stage decarburization annealing and the Goss texture under high temperature annealing the longitudinal section of grain-oriented silicon steel were detected by electron back scattering diffraction(EBSD) and X-ray diffraction(XRD).The effect of primary recrystallization grain boundary on macrotexture after high temperature annealing was analyzed.The results show that the Σ3 a... 

薄带连铸流程下取向硅钢粗大λ晶粒(〈100〉//ND,normal direction)的“遗传”会导致磁性能恶化.为解决这一问题，针对取向硅钢的热轧孪生行为开展研究，结果表明：凝固组织粗大的取向硅钢在650℃热轧时可产生大量{112}〈111〉形变孪晶，这与具有高层错能的硅钢在较高温度下难以孪生变形的传统认知不同.热轧过程中复杂的应力状态降低了变形孪晶的取向依赖性，由于具有更高的储存能，孪晶界/孪晶界及孪晶界/晶界交叉点成为再结晶形核的优先位置，大大提高了常化过程中的再结晶率，受沿孪晶界应变分布及孪晶间距离的限制，沿孪晶界形核的再结晶晶粒通常呈“饼状”,最终形成以细小且取向漫散的再结晶晶粒为主的常化组织，消除了初始凝固组织中有害的粗大λ晶粒. In strip casting grain-oriented silicon steels, the inheritance of coarse λ grains(〈100〉//ND, normal direction) can deteriorate their magnetic properties. To solve the problem, twinning behaviors in strip casting grain-oriented silicon steels during hot rolling were investigated in this work. It is found that after rolling at 650 ℃, a number of {112}〈111〉deformation twins are formed in the coarse solidification microstructure of the steels, in contrast to the well-accepted view that it is diffic... 

【作者】 严伟明； ...

本实用新型涉及一种点火器线圈硅钢片结构，包括E型件和I型件，其特征在于：所述E型件和I型件可组合成日字形；所述E型件和I型件的棱面外周顶面和底面均设置切棱；所述E型件包括竖边和设置在竖边三个横边，其中所述竖边的转角位置圆角处理，竖边外侧为弧形边；所述竖边与三个横边接触的位置设置孔眼；位于中间位置横边外侧设置凹部，位于下端横边外侧设置凸部；所述I型件靠近E型件一侧中间和下端位置设置凸部和凹部，其上端与E型件上端横边外侧重合接触。本实用新型设计新颖，改进巧妙，由于E型件具有弧形边可以有利于拾取，方便工作操作，同时采用采用接触的方式接触，增加了组合体的稳定性。