硅钢资料

采用XRD、SEM和激光粒度仪等手段,观察并研究了不同特性氧化镁在硅钢表面形成硅酸镁底层形貌特点,并结合热力学和差热-失重分析了MgO-SiO2的反应机理。研究结果表明:粒度小,活性值高的特种氧化镁在高温退火过程中与基体表面氧化物生成的硅酸镁底层,界面中硅酸镁底层嵌入基体较多,表面致密,颗粒细小,有利于形成附着性能优良的硅酸镁底层。 Surface microstructure of Mg2SiO4 coatings formed on the surface of oriented silicon steel coated with different kinds of MgO was investigated by XRD and SEM.The reaction mechanism between MgO and SiO2 was analyzed by TG-DSC and thermodynamic calculation.Results revealed that when the MgO with finer microstructure size and higher activity is employed,a dense Mg2SiO4 layer with finer microstructure and good binding to the steel substrate can be obtained.The results are very helpful for the prepar... 

采用双辊薄带连铸工艺试制了2.6 mm厚5.28%Si-1.11%Al高硅钢薄带,对比了1050℃×5 min正火及不正火铸带280℃冷轧至0.5 mm后,再经900～1100℃退火的磁性能。结果表明,高硅钢铸带显微组织为等轴晶组织,正火后铸带边部晶粒长大,中心层晶粒变化较小。成品中析出物主要为较粗大的AlN和AlN+MnS复合析出物,尺寸为0.5～2.5μm。与不正火试样相比,正火试样成品铁损大幅降低,磁感小幅下降;随退火温度的升高,两种工艺下铁损和磁感都是先降低后升高,在1050℃出现最低值。 2.6 mm thickness 5.28% Si-1.11% Al non-oriented high silicon steel was produced by twin roll thin strip casting.Magnetic property of the strip un-normalized and normalized at 1050 ℃×5 min was contrasted after cold rolled to 0.5 mm at 280 ℃ and 900-1100 ℃ final annealing.The results show that microstructure of the strip is equiaxed crystal.The surface grain is coarsened and the center layer grain has little change of the normalized strip.The main precipitates are AlN and MnS+AlN with 0.5-2.5 μm s... 

本发明提供一种无取向硅钢用涂层溶液及其制备方法和应用，以所述无取向硅钢用涂层溶液的总质量为基础计，所述无取向硅钢用涂层溶液包括如下质量百分含量的原料组分：磷酸盐溶液55％～60％；树脂溶液20％～25％；二乙二醇丁醚2％～4％；改性剂3％～5％；余量为水。由本发明所述无取向硅钢用涂层溶液形成的绝缘涂层厚度均匀，表面光滑，具有优良的绝缘性、耐腐蚀性、附着性，而且硅钢片的冲片性能好、叠片系数高。

对取向硅钢在不同气氛下的高温退火工艺进行实验室模拟，利用X射线衍射仪（XRD）分析了硅钢退火至900℃和1170℃时的样品表面氧化层和底层的物相组成，采用场发射扫描电镜（SEM）观察了样品表面氧化层和底层在截面方向上的微观形貌特征，并计算了高温退火一次升温阶段氧化反应的吉布斯自由能以及900℃时退火气氛的氧分压。结果表明：当退火气氛的露点温度保持一定时，较高的氢气含量有利于生成完整连续的底层；当退火气氛的水氢分压比保持一定时，在露点温度与氢气含量两者较低的条件下，底层附着性不佳易脱落，较高条件下，底层中夹杂着较多的铁单质；当氧化层中无FeO时，底层完整连续但易脱落，当FeO层较薄时，底层下方存在部分未反应的SiO₂,当FeO层较厚时，底层不完整连续且有分层。 The high temperature annealing process of grain-oriented silicon steel in different atmospheres was simulated in the laboratory. X-ray diffractometer（XRD） was used to analyze the phase compositions of the surface oxide layer and forsterite film of the silicon steel annealed to 900 ℃ and 1170 ℃. Field-emission scanning electron microscopy（SEM） was used to observe the micro morphology characteristics of the surface oxide layer and forsterite film of the samples in the cross section direction. The ... 

本发明提供一种无取向电工钢的制造方法，包括连铸和RH精炼工序，连铸坯化学元素质量含量为C≤0.0050%、Si：0.50~2.20%、Mn：0.20~1.20%、P：0.020~0.040%、S≤0.0020%、Als≤0.0050%、Ti≤0.0005%、N≤0.0025%，余量为Fe及不可避免的杂质；且0.4≤Mn/Si≤0.6；RH精炼工序，脱碳结束后向钢中同时加入铝粒、微碳硅铁复合脱氧，使用铝粒脱除氧量与使用微碳硅铁脱除氧量之比为1/15~1/5，钢中主要生成低熔点MnO‑SiO2‑Al2O3夹杂，能被快速去除，钢水洁净度高。本发明电工钢与现有的电工钢相比，在相同磁感应强度下铁损更低。

实验室模拟薄板坯连铸连轧(TSCR)流程制造高磁感取向硅钢,借助电子背散射衍射(EBSD)技术对不同Sn含量的热轧板织构进行了研究。研究结果表明:不同Sn含量热轧板表层及次表层均为高斯织构、铜型织构及黄铜织构的混合织构,中心层为{100}面织构;Sn含量为0.1%时,热轧板表层及次表层高斯织构组分最多,取向密度最大,成品磁感最高,达到1.875 T。 Texture of grain oriented silicon steel hot rolled by thin slab casting and rolling process(TSCR) in laboratory with different Sn contents was analyzed by electron back-scattered diffraction(EBSD).The results show that the hot rolled slabs with different Sn contents have the same texture,i.e.,Goss,Copper and Brass.Specifically,the texture of core layer is {100};While the hot rolled slab with 0.10% Sn,the surface layer and subsurface layer have a sharpness Goss texture and the finished products h... 

采用EBSD检测技术,分析了50W800无取向电工钢在重要生产工序间织构的演变以及织构沿带钢宽度方向上的差异性。结果表明:热轧板织构沿带钢宽度方向上的差异性主要体现在表层织构。带钢边部表层织构主要由旋转立方织构、α纤维织构以及少量的γ纤维织构组成,带钢宽度1/4处的表层织构主要存在高斯织构,带钢宽度1/2处的表层织构主要为(110)面织构以及少量的铜型织构。各处的带钢宽度1/4处和1/2处的织构类型基本一致,都以α纤维织构和旋转立方织构为主。冷轧后,各处的表层织构类型差异较小,均为γ纤维织构和α纤维织构。由板宽边部至中心处织构强度值逐渐降低。退火后,各处织构的组分基本一致,为较强的γ纤维织构和较弱的(100)面织构。各处织构强度值差异较小,变化趋势与冷轧板一致。 The texture of non-oriented electrical steel 50W800 was detected by EBSD technique.The evolution of the texture between important processes and the difference of texture along the width direction of strip were analyzed.The result shows that the difference along the width direction of strip of texture at the surface of hot rolled plate is most obvious.The texture at the surface of strip edge is primarily made of rotating cube texture,αfiber texture and weakγfiber texture.Goss texture is mainly co... 

本实用新型涉及硅钢片钢卷技术领域，且公开了一种用于硅钢片钢卷制造的焊接装置，解决了目前对钢片钢卷的夹持效果不好，导致硅钢片钢卷在焊接时会出现两侧位置偏移，焊接效果不好的问题，包括底板，所述底板上端中部连接有安装板，安装板上端两侧通过第一螺栓与底板上端固定连接；本实用新型，通过对硅钢卷本体的位置进行固定，且不会导致硅钢卷本体位置发生偏移，导致硅钢卷焊接效果不好；通过第一电机带动第一滑块滑动，使得第一转杆与第二转杆位于第一滑块上端与下端转动，带动第一支撑板与第二支撑板移动，能够对硅钢卷本体进行支撑，能够对硅钢卷本体进行支撑，便于进行焊接。

本发明涉及一种硅钢片铁芯用自动叠装系统，托板、上料单元、精定位单元、叠装单元、抓取单元，所述上料单元有一个，位于中部位置，所述精定位单元一共有两个，分别位于上料单元的两侧，所述叠装单元一共有两个，分别位于两个精定位单元的两侧，从而使得整个自动叠装系统由中间向两侧方向均依次为上料单元、精定位单元、叠装单元。本发明的优点在于：通过对上料单元、精定位单元、叠装单元的数量及排布位置进行重新设计，采用由中间向两侧供料的方式，使得两侧的上料顺序均独立运行，不存在相互干涉的风险，确保单侧的上料顺序的顺利进行，相对应的也就降低了程序设计的复杂程度，减轻了设计人员的工作强度。

试验研究了退火温度(850~950℃)和时间(5~18 min)对2.3 mm热轧硅钢板(/%:0.036C,3.15Si,0.21Mn,0.005P,0.007S,0.032A1)6道次轧制的0.35 mm冷轧板组织和织构的影响。结果表明,退火温度越高,晶粒平均尺寸越大,900℃5 min退火时平均晶粒尺寸41.39μm,试样织构主要集中在γ取向线上的{111}<112>织构组分和{111}<110>织构组分;900℃18 min退火时平均晶粒尺寸为48.08μm,试样的{111}面织构和{112}面织构密度都明显减弱,{001}面织构增强,磁性能较优。 The effect of annealing temperature(850 ~950 ℃) and holding time(5 ~ 18 min) on structure and texture of 0.35 mm sheet by 6 passes cold-rolling from 2.3 mm hot-rolled plate of silicon steel(/%:0.036 C,3.15 Si,0.21 Mn,0.005 P,0.007 S,0.032A1) has been tested and studied.Results show that the higher the annealing temperature the coarser the average grain size;As annealing at 900 ℃ for 5 min the average grain size of steel sheet is 41.39 μm,and the texture in sample is mainly concentrated in y orie... 

本申请提供一种电工钢及其制备方法，制备方法包括：将电工钢的板坯进行热轧获得钢卷；将热轧后的钢卷进行酸洗冷轧；将酸洗冷轧后的钢卷进行第一次罩式退火；将第一次罩式退火后的钢卷进行平整；将平整后的钢卷进行第二次罩式退火；将第二次罩式退火后的钢卷进行重卷，以获得电工钢。本申请提供的电工钢的制备方法采用两次罩式退火，退火的主要目的是消除酸洗冷轧工序产生的加工硬化，使钢板充分再结晶，获得理想的铁损及磁感应强度。而采用两次罩式退火，相对于一次罩式退火工序来说，能够进一步降低铁损，提高电工钢的磁性能。

本实用新型公开了一种硅钢片加工装置，涉及到硅钢片加工装置技术领域，包括安装板，所述安装板的上表面两端均固定连接有固定板，所述安装板的上表面一侧固定连接有涂覆装置，所述安装板的上表面中部固定连接有压平装置，所述安装板的上表面另一侧固定连接有烘干装置，所述固定板的一侧底端通过轴承活动连接有传动辊。本实用新型通过在安装板的上表面一侧设置涂覆装置，涂覆装置对硅钢片的两面进行绝缘层涂覆，在安装板的上表面中部设置压平装置，压平装置包括两个压辊，压辊的一侧设置的限位块中部开设有螺纹孔，转动双向螺杆使得限位块运动，从而使得两个压辊之间的间距被调节，可以根据生产需求调节绝缘涂料的压平厚度。