【作者】 周威； 刘侃； ...

针对目前大部分无取向电工钢处理液为含铬处理液、且需在较高温度下固化的情况,在分析成膜物质性质的基础上,试验研究了一种可低温快速固化的电工钢环保绝缘处理液,研究了其涂装工艺,并测定了涂层的附着性、绝缘性、耐热性、耐蚀性等性能。试验结果表明:该处理液可在150~250℃下快速烘干固化,涂层表面光滑且致密均匀,性能优良,可满足中小电机的使用要求。 At present,most of the insulating fluid for non-oriented electrical steel contains chromium,and should be cured at high temperature.On the basis of analyzing the characteristics of the film-forming substance,a kind of eco-friendly insulating fluid with lower curing temperature for non-oriented electrical steel sheet was developed in the experiments.Then its coating process was studied,and the adhesiveness,insulativity,heat resistance,corrosion resistance and other properties of the coating was m... 

本发明公开了一种无取向电工钢清洗工艺，包括以下步骤：1)在脱脂剂箱体中添加脱脂剂溶剂，通过喷射泵将脱脂剂分别从上下两路管道喷出，经过流量控制电磁阀进入喷射梁，通过喷嘴喷洒在带钢表面；2)带钢轧制后温度为100～150℃，速度为600～1000m/min，带钢表面高温确保脱脂剂与带钢表面残留油脂反应充分，且在高速下喷射的脱脂剂与带钢相向而行，使带钢表面反应后残留硅泥、铁粉被迅速带走；3)喷射后的脱脂剂流入收集槽中，通过泵重新打入脱脂剂箱体中，实现脱脂剂的循环利用。其利用轧制时产生的高温及高速对带钢表面残留乳化液斑迹、铁粉、硅泥进行清洗，清洗彻底高效。

借助电子背散射衍射(EBSD)及ZEISS-200MAT金相显微镜对某钢厂普通取向硅钢(CGO)进行研究,研究结果表明:热轧板组织、织构沿板厚方向存在明显的不均匀性,在热轧板表层及次表层发生再结晶,同时存在强度较高的Goss织构,中心层存在较强的{001}<110>变形织构。冷轧组织均呈纤维状条带组织,一次冷轧后,热轧板中的Goss织构消失,织构主要为α、γ织构,经中间脱碳退火后,α、γ织构强度减弱,并出现一定强度的Goss织构和利于Goss织构发展的{554}<225>、{332}<113>等织构,经二次冷轧后,二次冷轧织构类型与一次冷轧织构一致,但织构强度不同。 The grain-oriented silicon steel produced by a steel factory was investigated by EBSD and ZEISS-200 MAT metallographic microscope.The results show that the textures and microstructures along thickness of hot rolled slab are inhomogeneous.The surface layer and the layer near that are recrystallized structure which has a high Goss texture,but there is deformation texture{001}<110>in the central layer.The structure after cold rolling is a structure like fiber strip.After the first cold rollin... 

研究了退火温度对3.1%Si无取向硅钢组织和磁性能的影响规律。结果表明:退火温度从940℃提高至1 000℃,平均晶粒尺寸由98μm增加到145μm,铁损P_1.5/50从2.576 W/kg降低至2.408W/kg。随着退火温度的升高,γ不利织构组分强度逐渐降低,{111}〈112〉织构组分强度降低约16%,磁感B₅₀逐渐升高,磁性能水平提高。 The effects of annealing temperature on microstructure and texture and magnetic properties of 3.1%Si non-oriented silicon steel were investigated in this paper.The results showed that,when the annealing temperature increased from 940℃ to 1 000℃,the average grain size of metallographic structure increased from 98μm to 145μm,the iron loss value P_1.5/50 decreased from2.576 W/kg to 2.408 W/kg.And as the annealing temperature increased,the strength of the unfavorable texture componentγgrad... 

【机构】 武汉钢铁学院轧钢七二级电工钢结业小组； ...

利用背散射衍射技术(EBSD)和XRD,研究了两段式脱碳退火工艺对取向硅钢纵截面初次再结晶的微区取向、取向差分布、特殊晶界(CSL)及高温退火试样高斯织构。分析了初次再结晶晶界特征对取向硅钢高温退火后宏观织构的影响。结果表明:初次再结晶的纵截面基体中Σ3和Σ5晶界使得高斯晶粒有着较高的迁移率,在高温退火时借助20o～45°的大角度晶界的界面能吞并周围{111}<112>晶粒迅速长大,形成密度水平较高的高斯织构。 Micro area orientation of primary recrystallization,the misorientation distribution,special boundaries under different two-stage decarburization annealing and the Goss texture under high temperature annealing the longitudinal section of grain-oriented silicon steel were detected by electron back scattering diffraction(EBSD) and X-ray diffraction(XRD).The effect of primary recrystallization grain boundary on macrotexture after high temperature annealing was analyzed.The results show that the Σ3 a... 

本发明涉及一种含磷无铝高效无取向硅钢生产方法，生产方法取消常化工艺，具体步骤如下：1)将钢水冶炼至目标成分后，浇铸成坯；2)板坯热装，热装温度≥500℃，热轧板坯加热炉均热段板坯温度1150～1200℃；终轧温度控制在860～930℃，卷取温度700～800℃3)酸洗后冷轧，控制冷轧整体压下率80％以内，至成品厚度；4)连续退火炉快速加热段温度设定1050～1180℃，增加有利织构组织形核，均热段温度设定830～950℃，全氮气干气氛保护，退火工艺速度120～150m/min，满足晶粒度8～4级。本发明不需进行热轧卷常化处理，降低了制造成本。

本申请提供了一种快速判断取向硅钢常化板冷轧脆性的方法，属于取向硅钢材料技术领域，包括常化机组尾部卷取时随机取样，每卷分别在板中间和两侧碎边边丝进行取样，均沿轧向取样，在试样温度为常温条件下，对碎边边丝进行弯曲测试，并记录每条碎边边丝式样的弯曲次数，统计对应取样的钢卷在冷轧工序的脆断情况，将弯曲实验结果与冷轧脆断情况进行对应统计分析，根据常化板边部的试样弯曲次数是否大于或者等于1次，若否，则判定冷轧脆断。通过检测不同常化工艺条件下常化板的反弯次数，再验证不同弯曲次数前提下的冷轧可轧性，找出弯曲次数与可轧性的对应关系，从而确定常化板的最小反弯次数，以此对冷轧脆性进行判定。

本实用新型涉及硅钢片钢卷技术领域，且公开了一种用于硅钢片钢卷制造的焊接装置，解决了目前对钢片钢卷的夹持效果不好，导致硅钢片钢卷在焊接时会出现两侧位置偏移，焊接效果不好的问题，包括底板，所述底板上端中部连接有安装板，安装板上端两侧通过第一螺栓与底板上端固定连接；本实用新型，通过对硅钢卷本体的位置进行固定，且不会导致硅钢卷本体位置发生偏移，导致硅钢卷焊接效果不好；通过第一电机带动第一滑块滑动，使得第一转杆与第二转杆位于第一滑块上端与下端转动，带动第一支撑板与第二支撑板移动，能够对硅钢卷本体进行支撑，能够对硅钢卷本体进行支撑，便于进行焊接。

1.本外观设计产品的名称：硬质合金刀（硅钢片刃切剪用）。;2.本外观设计产品的用途：用于硅钢片刃的剪切。;3.本外观设计产品的设计要点：在于其整体形状。;4.最能表明设计要点的图片或照片：立体图。;5.使用时为安装面，故不常见，省略后视图。;

该电磁钢板包括母材钢板、第1绝缘被膜及第2绝缘被膜，该第1绝缘被膜被形成于所述母材钢板的第1面，并具有粘结能量，该第2绝缘被膜被形成于作为所述母材钢板的所述第1面的背面的第2面，并具有粘结能量，所述第1绝缘被膜的平均铅笔硬度为HB以上3H以下，所述第2绝缘被膜的平均铅笔硬度比所述第1绝缘被膜的平均铅笔硬度更高。