硅钢资料

综述了退火温度、时间对无取向电工钢磁性的影响。退火温度主要影响无取向电工钢不同织构的占有率,退火时间主要影响晶粒尺寸的大小,晶粒尺寸的变化对织构的形成也有一定的影响。磁感最高点出现在纤维组织完全消失,(111)面织构组分较弱的组织状态。铁损的降低主要依赖于磁滞损耗的降低,织构的影响不大。 The effects of annealing temperature and time on the non-oriented electrical steel magnetic properties were reviewed.Annealing temperature and time mainly affects the different textures share and the grain sizes of non-oriented electrical steel respectively.Changes of the grain sizes also have a certain effect on textures formation.The highest point of the magnetic induction value in the fibrous tissue completely disappears and{111} plane texture has a lower state of the component content.Iron l... 

结合工业化生产的无取向硅钢,进行了RH精炼喂CaSi线去除钢中的非金属夹杂物试验研究。针对不同的钙处理条件,分析了CaS夹杂生成热力学,观察了夹杂物的形貌和尺寸分布,确定了夹杂物的类型、数量,探讨了钙处理后钢中夹杂物的变化规律。结果表明,本试验条件下,钙处理可以有效抑制MnS、AlN夹杂物的生成,有效促进钢中微细夹杂物的聚合、上浮、去除,钢质纯净度明显提高。经过合适的钙处理后,钢中的夹杂物以独立存在的CaO为主,同时有少量含CaO、SiO2、MgO的复合夹杂,没有发现CaS夹杂存在。这部分夹杂物的尺寸集中分布在2～20μm,数量约为1.8×105个/mm3。 Experimental study on removal of non-metallic inclusions in non-oriented silicon steel obtained from industrial production by CaSi wire feeding during RH refining process was carried out.The thermodynamics of CaS inclusion formation was analyzed,the morphology and the size distribution of inclusions were observed,and the numbers and types of inclusions were also determined for the steel specimens treated under different calcium treatment conditions.Furthermore,the variation of inclusion characte... 

本实用新型公开了硅钢专用消泡剂生产温度控制装置，包括底板及设置在底板上端的温控桶，所述温控桶的内部设置有温控腔，所述温控桶的上下两端分别安装有进料口及出料口，所述温控桶的内部设置有便于温度控制的温度控制机构，所述底板上设置有用于搅拌的搅拌机构；所述温度控制机构包括安装在温控桶上的进气管及出气管，所述进气管及出气管与温控腔的内部相通设置。本实用新型的硅钢专用消泡剂生产温度控制装置，整个温控处理操作简单、实施便捷，便于对消泡剂进行温度控制，且冷却介质或者加热介质可以直接对消泡剂进行加热或是降温，降低了输送过程中的能量消耗，提高了消泡剂温度控制的效率。

本发明的一种超低碳含钇取向硅钢及其制备方法，化学组成及质量百分比为Si：2.0～4.5％，C：≤0.003％，Y：0.001～0.1％，Mn：0.1～0.25％，Al：0.01～0.02％，Cu:0～0.3％，S：0.02～0.035％，N：0.009～0.011％，其余为Fe和不可避免的杂质元素。生产工艺为：连铸、铸坯加热、热轧、常化、冷轧、初次再结晶退火、二次再结晶退火。本发明采用超低碳的成分，取消了常规取向硅钢脱碳退火工艺，简化了生产流程。通过稀土微合金化解决了因超低碳成分导致的单向铁素体组织抑制剂析出困难的技术难题。本发明制备的含钇取向硅钢厚度为0.2～0.35mm，磁感应强度B8为1.85～1.94T，铁损P17/50为0.9～1.2W/kg，可以用于变压器的铁芯材料，制备流程更为简洁。

本实用新型公开了一种具有废料回收机构的硅钢板带加工用切割装置，包括箱体，所述箱体的前侧靠近顶部处设有电机，所述箱体的顶部靠近前侧处固定连接有竖板，本实用新型一种具有废料回收机构的硅钢板带加工用切割装置，电机在工作时既能带动切割刀进行切割作业，同时还能带动第一筛板和第二筛板以相邻转轴为中心上下摆动，切割的废屑从切割槽穿过达到箱体内腔，第一筛板和第二筛板对废料进行筛分处理，通过隔板设置，隔板将集料盒分为两个存储空间，隔板右侧存储穿过第一筛板和第二筛板的细料，隔板的左侧存储被第一筛板和第二筛板过滤下来的粗料，既方便操作人员对废料进行集中处理，还对废料进行了筛分处理，以此方便对废料进行分类重复利用。

对高牌号无取向电工钢35W300的成品进行了第二次退火,对第二次退火后的成品性能、纵横向磁性能差异和组织变化进行了分析。结果表明,随着第二次退火温度的升高,晶粒长大,磁性能优化。铁损平均值下降0.087 5W/kg,磁感平均值升高0.008T。第二次退火温度为820℃的产品的磁性能能够满足用户使用要求。 The product of high grade non-oriented electrical steel 35W300 was annealed at the second time.Microstructure,the difference of magnetic properties in the vertical and horizontal and were studied.The results show that the grain grew up and magnetic properties optimized with the increase of annealing temperature for the second time.Iron loss average declines in 0.0875 W/kg,magnetic induction average increases 0.008 T.The magnetic properties can meet the requirements of users at the second anneali... 

针对采用含钒铁水生产无取向电工钢存在的铁水脱硫率低、转炉冶炼过程回硫量大、成品硫含量偏高的问题,通过对含钒钛铁水脱硫,减少转炉冶炼过程回硫以及RH脱硫技术等方面的研究,大幅度降低了电工钢成品硫含量。生产表明钢中w(S)=0.001 9%～0.006 9%,平均为0.004 2%;w(S)≤0.008%的比例达到了100%,且w(S)≤0.005%的比例也达到了91.43%。 In cognizance of the problems of low desulphurization rate for hot metal,large sulfur-recovery in converter as well as high sulfur content in products in producing non-orientation electrical steel with vanadium-content hot metal countermeasures have been carried out.Sulfur content in non-orientation electrical steel is decreased obviously by way of study on technologies of desulphurization for hot metal with vanadium & titanium,sulfur-recovery control in converter and desulphurization in RH ... 

本发明涉及薄规格高牌号无取向硅钢冷轧领域。一种提高超薄规格高牌号无取向硅钢厚度精度的冷轧方法，硅钢成品厚度规格在0.15mm～0.25mm，坯料采用常化酸洗切边后的硅钢卷，初始厚度为2.0～2.3mm，采用二十辊单机架轧机轧制，在轧制过程中，对整个轧制过程进行控制。本发明的有益效果是：解决二十辊轧机超薄规格无取向冷轧硅钢纵向厚度波动同时减小横向同板差的方法。

轧制力是影响冷轧带钢厚度精度的关键因素。为实现高精度的冷轧带钢厚度控制,通过优化变形抗力模型参数和摩擦系数模型参数提高冷轧轧制力模型计算精度,并使用指数平滑法的自学习算法保证轧制力精度的稳定性。在首钢股份公司迁安钢铁公司20辊森基米尔轧机生产线进行S12硅钢钢种轧制力优化试验,将优化的模型参数应用于L2并投入现场生产,结果表明该优化方法不仅提高了轧制力设定精度,而且减小了冷轧硅钢的厚度超差长度,提高了成材率。 The rolling force is the key factor which influences the accuracy of cold-rolling strip thickness. To implement high precision control of cold-rolling strip thickness,we optimize the deformation resistance model parameters and friction coefficient model parameters to improve the calculation precision of cold-rolling force model,and use exponential smoothing self-learn algorithm to ensure the stability of rolling force accuracy. In Shougang Qiangang 20-high Sendzimir mill single stand production ... 

本实用新型公开了一种硅钢片加工用进料结构，涉及到硅钢片加工技术领域，包括壳体，壳体的两侧均贯穿开设有通槽，通槽的内部活动贯穿设置有活动板，活动板位于壳体内部的一端贯穿开设有方槽，其中一个方槽的顶端内壁和另一个方槽的底端内壁均固定设置有多个呈等间距分布的锯齿。本实用新型通过将多个硅钢片均挂在两个架板上的挂槽内，因硅钢片重量，带动两个延伸杆向下移动，延伸杆带动活动块向下移动，活动块带动齿条向下移动，从而带动齿轮转动，齿轮转动的同时，能够通过多个锯齿带动两个活动板相互靠近，从而使两个夹板相互靠近并夹紧多个硅钢片，从而能够固定住硅钢片，防止硅钢片传输时滑动，造成磨损。

本发明公开了一种弧形硅钢片、弧形硅钢片治具及弧形硅钢片制造方法；弧形硅钢片治具包括压制底板和侧挤压板，压制底板和侧挤压板之间具有挤压间隙，挤压间隙的两侧分别设置有位于压制底板内侧的外挤压面和位于压制底板外侧的内挤压面，外挤压面和内挤压面的对应位置上开设有若干齿槽加工台阶，压制底板的下方开设有若干与挤压间隙连通的焊接孔，压制底板和侧挤压板的侧面对应位置设置有贯穿压制底板和侧挤压板的冲压模孔；通过弧形硅钢片制造方法，采用弧形硅钢片治具制成弧形硅钢片。本发明采用弧形硅钢片治具及弧形硅钢片制造方法实现动子中弧形硅钢片的压制成型，通过弧形硅钢片实现直线电机的圆周运动或圆弧运动。

本发明涉及硅钢带的制备技术领域，具体公开一种软磁性高硅钢极薄带及其制备方法。所述软磁性高硅钢极薄带的制备方法包括熔炼、包覆CaF2和TiB2偶合涂层、微波热压成型、酸洗、渗氮、一次退火、三道热轧、二次退火、三次温轧和三次退火。本发明提供的软磁性高硅钢极薄带的制备方法制得的软磁性高硅钢极薄带的晶粒细化程度高、组织均匀，改变了传统的相析出路径，有效消除了有序相的形成，使其具有优异的延展性，并具备更高的磁感和更低的铁损。