高强无取向硅钢主要应用于高速电机，要求其具备高强度和优异磁性能，但目前无取向硅钢的磁性能和强度难以兼顾。因此，设计并制备了添加微量Cr的含Nb高强无取向硅钢，通过光学显微镜、EBSD、万能拉伸试验机、四探针测试仪和磁性能测量仪等研究了Cr对含Nb高强无取向硅钢微观组织、织构、力学性能及磁性能的影响。结果表明，添加质量分数为0.5%的Cr抑制了热轧组织的回复，使常化和退火组织再结晶减弱，常化和退火后有利织构面积分数增加，不利织构面积分数减小。添加质量分数为0.5%的Cr使含Nb无取向硅钢的屈服强度显著增大，磁感略升高，但对铁损几乎没有影响。Cr对屈服强度的影响一方面是由于Cr的固溶强化作用，另一方面Cr促进了Nb的析出而使Nb的析出强化效果增强；而Cr提高含Nb高强无取向硅钢的磁感主要是由于促进有利织构形成的同时抑制了不利织构的形成，使得织构因子增大；添加Cr使无取向硅钢的电阻率增加从而使铁损降低，同时Cr促进了Nb的析出，而这种富Nb析出相不仅抑制晶粒长大且会阻碍磁畴移动而使铁损增高，在两方面因素的综合作用下，添加质量分数为0.5%的Cr对含Nb高强无取向硅钢的铁损几乎没有影响。因此，... High strength non-oriented silicon steel is mainly used in high-speed motors, which requires good mechanical and magnetic properties. However, it is difficult for non-oriented silicon steel to obtain high strength and good magnetic properties at the same time. In this paper, the Cr-microalloyed Nb-containing high strength non-oriented silicon steel was designed and prepared. The effect of Cr on the microstructure, texture, mechanical properties and magnetic properties of Nb-containing high stren... 

本发明提出了一种无机绝缘漆，由下列物质组成，其重量百分比为：质量百分含量为50～55％的磷酸二氢铝溶液：30～70％；质量百分含量为60～70％的磷酸二氢锰溶液：10～15％；质量百分含量为80～85％的硼酸溶液：5～6％；质量百分含量为99％的硅烷偶联剂溶液：1～5％；质量百分含量为30～35％的硝酸盐溶液：0.1～0.5％；硅溶胶：10～15％；纳米硅酸铝：10～15％；纳米二氧化硅：20～30％；消泡剂：1～5％；水溶剂：适量。本发明采用磷酸二氢铝、纳米二氧化硅为主料制备了一种极薄硅钢带薄绝缘无机绝缘漆的涂层，涂层厚度均匀性好，涂层表面光亮、附着性强、绝缘电阻系数高。

本实用新型提供了一种便于清洗的冷轧硅钢生产用轧机，两个所述支架安装在底座上，所述支架上设有安装盖，支架之间设有上支撑辊，上支撑辊下设有上工作辊，上工作辊安装在支架之间，上工作辊下设有下工作辊，这种便于清洗的冷轧硅钢生产用轧机，在使用的时候，可以对于冷轧硅钢进行生产处理，生产之后可以进行清洗设备，安装的上工作辊与下工作辊可以对于硅钢进行冷轧处理，在工作时，两侧安装的承重块可以对于机械进行一个固定，起到稳固作用，两侧安装的转动辊可以放置硅钢，安装的清洗头可以对于机械进行清洗，吹风器可以对于机械进行干燥处理，防止机械生锈，底座上安装的沥水板可以隔断灰尘和铁屑，防止堵塞。

本发明提供了一种超高磁感无取向硅钢及其制造方法和在汽车发电机生产中的应用，成分：C：≤0.005％、Si：0.5‑1.2％、Mn：0.1‑0.5％、P：0.01‑0.1％、S：≤0.004％、Al：≤0.005％、N：≤0.005％、Ti：≤0.003％，余量为铁和不可避免的杂质。通过成分设计，配合CSP薄板坯连铸连轧工艺、常化工艺，不用添加贵金属元素，不添加贵金属元素，流程短、成本低、磁感高、性能稳定；节省成本的同时，具有优良的磁性能，采用本发明生产的汽车发电机铁芯，与常规产品生产的铁芯相比，重量可减轻15％以上，缩小了发电机尺寸，满足汽车发电机小型化、高效化的要求。

主要研究了0.7%Si无取向电工钢退火试样的组织、晶粒尺寸和织构对其磁性能的影响。结果表明,随着退火温度的升高,晶粒尺寸逐渐增大,组织的均匀性得到改善;ɑ取向线上的纤维织构多集中于{114}<110>和{223}<110>附近,再结晶结束后,织构含量变化不大。{111}<110>织构取向密度值随温度升高而下降,{112}<111>织构与{111}<110>织构变化相反。晶粒尺寸增大对磁感强度的影响较小,而对铁损的影响较大。 Influences of microstructure,grain size and texture on the magnetic properties of 0.7% Si non-oriented electrical steels annealed samples were studied.The results show that with annealing temperature increasing the average grain size is increased gradually.Uniformity of the microstructure is improved;the textures of ɑ-fiber gathered in the vicinity of the { 114} < 110 > and { 223 } < 110 > texture.After recrystallization,the volume fraction of texture changes small.{ 111} < 110 &g... 

针对攀钢高硫铁水冶炼现状,结合不同生产工艺路线,论述了攀钢近年来为实现低硫电工钢的生产,在铁水预处理、转炉冶炼、钢水精炼过程中硫控制技术的开发与应用,形成了低硫洁净钢生产工艺技术,实现了低硫电工钢的生产。低硫电工钢RH脱硫率可达到20%左右,成品[S]控制在0.006%左右。 According to the smelting situations of hot metal with high sulphur content at Panzhihua Steel,combined with different produce processes,technologies for controlling the sulfur content during hot metal pretreatment,converter smelting,and second refining are developed. Technologies in low-sulfur clean steelmaking are formed. Low-sulfur electric steel are produced. As for the desulfurization rate of lowsulfur electric steel can reach about 20%,and the content of [S] in products is controlled to ab... 

根据新日铁、JFE及浦项等国外钢铁公司2008年以来在日本专利局、欧洲专利局(EP)及世界知识产权组织(WIPO)申请公开的有关生产Hi-B取向电工钢典型专利技术,概述了近年来国外大型钢铁企业采用低温板坯加热(坯加热温度<1 280℃)技术生产Hi-B取向电工钢主要技术重点,即将调节关键化学成分Al、N、Sn及Sb等与工艺改进相结合。最后介绍了国外大型钢铁企业采用低温板坯加热技术生产Hi-B取向电工钢实例。 The latest developments on technology for manufacturing Hi-B grain oriented electrical steel sheets developed by Nippon Steel Corp.,JFE Steel and POSCO were described according to the patents published by World Intellectual Property Organization,Japan Patent Office and European Patent Office over the recent years.The low temperature slab heating process(particularly slab-heating temperature<1 280 ℃) together with suitably adjusting key chemical elements such as Al,N,Sn and Sb elements was the... 

电工钢试样加工产生的剪切应力会恶化钢板的磁性,对不同牌号硅钢片的横向、纵向试样退火前后磁性能的变化进行研究,结果表明:无取向硅钢片在剪切过程中横向、纵向的磁性受到剪切应力影响是不一样的。 The electrical steel sample processing magnetic of electrical steel will worsen due to the shear stress of sample. In this paper,the magnetic change of transverse,longitudinal specimens of different type of silicon steel sheet before and after annealing are studied. The results show that the magnetic of non- oriented silicon steel sheet affected in the process of shear is not the same in horizontal and vertical direction. 

本发明公开了一种用于取向硅钢卷的焊缝切除方法，包括在焊接机组完成钢卷焊接后，在距离焊缝预设距离位置处冲孔；而后，钢卷到达成品退火工序时，利用孔洞检测装置检测焊缝冲孔，并根据焊缝冲孔得到焊缝位置，并记录该焊缝位置；并在分卷工序中，根据记录得到的焊缝位置对焊缝进行切除。这样，该方法利用焊缝冲孔，结合孔洞检测装置，将焊缝位置信息传递到分切工序，使得焊缝识别切除率较高，有效解决了取向硅钢焊缝无法精准定位切除的问题，实现了卷中焊缝多工序结合精准切除。

本实用新型涉及一种硅钢片叠压精准定位设备，包括压台、压板和仿形燕尾键，所述压台上开有与仿形燕尾键下端相对的限位槽，所述压板设置与压台上方，所述压板上开有与仿形燕尾键上端相对的限位孔。本技术方案当硅钢片叠放压合之后，仿形燕尾键可以去除，并能够在硅钢片组成的铁芯上形成燕尾槽，用于后期燕尾键的组装，且能够保证燕尾槽内的结构规则，便于后期燕尾键组装。

本实用新型涉及电机技术领域，具体涉及一种具有低应力隔磁桥的硅钢片和电机转子。包括硅钢片、开设在硅钢片上的若干个磁钢槽组和永磁体，若干个磁钢槽组沿所述硅钢片周向分布，每个磁钢槽组均至少包括一对沿径向对称分布的磁钢槽，永磁体嵌设于磁钢槽内，磁钢槽朝向硅钢片内侧的一端设有空腔，一对磁钢槽的空腔之间通过隔磁桥隔离，隔磁桥的空腔上壁面与空腔侧壁面之间通过第一椭圆弧过渡连接，隔磁桥的空腔下壁面与空腔侧壁面之间通过第二椭圆弧过渡连接。有效降低该处隔磁桥在拐角处所受应力，进而提高该隔磁桥的强度，避免磁钢和铁芯产生形变而断裂。

一种高硅钢材料的制备方法，步骤包括靶材、金属基材表面清理；排除密闭容器内空气、通保护气；双辉光等离子预轰击靶材和基材，净化表面；等离子溅射、加热、保温；缓慢冷却取出。预轰击靶材、基材，去除表面吸附层、活化基材，交替升高基材电压、靶材电压，使靶材中的合金元素被离子轰击而溅射出来、扩散进入基材内部形成表面高硅钢层。“双辉光等离子表面冶金技术”制备高硅钢的工艺简单易行、可控性高、成本低、无污染且基体和表面的结合力高，适合大规模产业化生产；更重要的是该方法采用交替离子轰击、扩渗速度快，结合强度高，得到硅含量均匀分布或呈梯度分布的高硅钢材料，为制备更高品质的无噪音、低铁损的高硅钢产业化奠定基础。