本实用新型公开了一种变压器硅钢片整平工装，涉及变压器装配技术领域，包括底板，所述底板顶部一角处安装有第一气缸，所述第一气缸的输出端固定有支撑块，所述支撑块一端设置有第一L型垫块，所述第一L型垫块两端皆开设有配合槽。本实用新型通过设置有第一L型垫块、第二L型垫块、传动带、第一气缸和第二气缸之间的配合，通过第二L型垫块内侧对运动中的变压器硅钢片进行拦截，第一气缸的输出端伸出带动第一L型垫块进行移动，使第一L型垫块将变压器硅钢片推至第二L型垫块拐角处，工作人员通过控制第一气缸输出端来回伸缩对硅钢片进行反复挤压整平，有效提高了变压器硅钢片整平机的工作效率，节约成本。

通过热力学计算,分析了实验钢中主要析出物析出的可能性。结果表明:在液相和固液两相区中,AlN和MnS均不能析出;在奥氏体区,AlN和MnS具备热力学析出条件,平衡析出温度分别为1547、1582 K。成品退火板中的析出物主要为AlN和MnS。扫描电镜下观察到的AlN形貌多为长条状,MnS形貌多为棒状或近似球形。这两种析出物占了析出物总量的85%以上,尺寸集中分布在400~800nm;复合析出物主要是(Al2O3+MnS)和(AlN+MnS),形貌不规则,尺寸集中在0.7~1.5μm;透射电镜下观察到了少量100nm以下独立的AlN析出。 According to thermodynamic calculation, the precipitation probability of precipitates was analyzed, AlN and MnS can not precipitate in liquid phase area and solid-liquid two-phase area. In austenite area, both the AlN and MnS have precipitation condition in thermodynamics and precipitates at 1547 K and 1582 K, respectively. The precipitates in annealing plate are mainly AlN and MnS. The shape of AlN is mostly strip, and MnS is stick or near sphericity. They accounted for over 85% of the total qu... 

一种厚度≤0.15mm无取向硅钢带，其组分及wt%为：Si：2.0～6.5%，Mn：0.13～0.40%，S≤0.020%，P≤0.020%，Als：0.15～0.9%，C≤0.010%；工艺：经冶炼、浇注成坯后热轧至中间坯厚度；冷轧；常温脱脂；光亮罩式退火；经碱洗后涂覆；分条。本发明在保证铁损P1.0/400£13W/kg,磁感B2000³1.5T下，还使钢带厚度公差不超过±0.005mm,最小叠装系数³0.92完全满足连续冲制要求。

本实用新型公开了超薄硅钢铁芯卷绕张力控制装置和纠偏装置，包括工作台、固定架和底座，工作台的顶部安装有固定架，所述工作台的底部设置有按压杆组件，所述按压杆组件的底部连接有底座，所述工作台顶部的前端和尾端均安装有固定板，所述固定板的内壁设置有收捆轴，所述工作台的顶部安装有滑轨板，且滑轨板位于固定板的内侧。本实用新型通过导向辊和衔接板的设置，工作人员在使用时，根据收捆轴上铁芯的缠绕位置，对两侧导向辊进行调节，从而通过导向辊的转动性对铁芯的活动起到定位作用，两侧导向辊的主要作用是起到带料输送出来时的导向作用，能够保证带料快速平稳的送料时不发生跑偏现象。

本实用新型实施例涉及一种硅钢卷、定子、转子铁芯、转子和盘式电机，所述硅钢卷由多条硅钢条卷绕形成具有多层硅钢层结构，每条硅钢条均构成多层硅钢层，每条硅钢条所构成的多层硅钢层中，距离最近的两层硅钢层之间具有一层或多层其他硅钢条构成的硅钢层。该硅钢卷用作转子铁芯或定子时降低了层间涡流损耗。

本文对某厂硅钢DR510温度、成分及过程控制水平和成品的组织、力学性能进行了研究,并在此基础上提出了工艺优化方案,有一定的借鉴和推广价值。 In this paper,the critical process and the products quality,including temperature,composition and process controlling level,the organization and mechanical properties of the finished product,were studied.On the basis of that the optimized technical plan provided,and this control technology is worth using and spreading. 

利用场发射扫描电镜观察了以MnS为主要抑制剂的普通取向电工钢加工过程中第二相粒子的分布状态,统计了粒子面密度、平均尺寸以及相应的尺寸分布.结果显示,热轧加工造成了大量第二相粒子弥散、细小地析出,同时基体仍保持过饱和状态.冷轧变形会造成第二相粒子的回溶行为,而基体的过饱和状态会减弱回溶现象.中间退火与脱碳退火过程中会同时存在新粒子的形核及已析出粒子的粗化两个过程,而在最终二次再结晶升温阶段则以第二相粒子明显粗化为主. The distribution of second phase particles in conventional grain-oriented electrical steels during manufacturing processes with MnS as inhibitors was observed by field emission scanning electron microscopy,while the areal particle density,the average particle size and the corresponding size distribution were statistically determined.It is indicated that hot rolling leads to dispersive precipitation of a large amount of fine second phase particles and the matrix keeps a supersaturated state furth... 

采用取向分布函数和取向线分析方法对低温板坯加热取向硅钢从热轧到初次再结晶工艺阶段的织构进行了研究。研究表明:一次冷轧后各层的织构组分与热轧板各层面的织构组分存在着继承关系,次表层存在很强的{001}<110>织构,中心层的织构和热轧板的中心层相似,存在强的{001}<110>和{112}<110>织构;中间退火后发生再结晶,各织构组分的强度有所减弱,Goss织构组分再次出现;二次冷轧后沿厚度方向上的织构不均匀性不明显,{111}<112>织构强度最高,几乎是其他织构组分的1倍,{001}<110>织构大幅降低;初次再结晶后织构沿厚度方向没有明显的不均匀性,{111}<110>为最强的织构组分,并且具有一定强度的Goss位向。 The texture from the first cold rolling to the primary recrystallization of low temperature slab reheating grain-oriented electrical steel were researched by orientation distribution function and orientation distribution intensity technique.The results show that after the first stage of cold rolling,there is a strong {001}<110> texture in the subsurface and the texture in center layer is very similar to the center layer of hot band which has strong {001}<110> and {112}<110> tex... 

本发明公开了硅钢片铁芯生产线，包括放卷机构、剪切机构、送料机构、叠片机构和下料机构，送料机构包括磁性传送带、送料件和第一定位杆，磁性传送带包括上传送带和下传送带，送料件可沿磁性传送带的正交方向平行伸出，其中，第一送料分台和第二送料分台安装于上传送带的下方并且相背运动，第三送料分台和第四送料分台安装于下传送带的下方并且相背运动，第一定位杆用于定位硅钢片，叠片机构包括叠放台、悬梁和两个六自由度机械手，六自由度机械手吊装于悬梁上，包括有电永磁铁，用于吸取硅钢片，下料机构包括滑板，叠放台放置于滑板上。根据本发明的硅钢片铁芯生产线，可提高设备自动化程度，提高叠片速度，从而提高生产线的生产效率。

本发明公开了一种硅钢与碳钢混合生产条件下提高钢带表面清洁度的方法，硅钢与碳钢混合冷轧轧制条件下，通过控制冷轧乳化液指标，轧机工作辊表面粗糙度，退火工序氢气吹扫流量，平整及重分卷工序钢带涂油量等措施，能够提高钢带表面清洁度。

一种基于临界变形制备高强度无取向电工钢的方法，按以下步骤进行：(1)按电工钢成分真空精炼钢水，连铸制成连铸坯；(2)在900～1100℃热处理30～120min，然后热轧制成热轧板；(3)冷轧冷轧板；冷轧板厚度为目标厚度+(0.01～0.1)mm；(4)在400～700℃进行一次退火处理，在850～1200℃进行二次退火处理；(5)酸洗去除氧化层，然后进行温轧或二次冷轧进行临界变形。本发明的方法利用位错强化机制采用临界变形提高无取向电工钢的强度的原理，利用一次退火二次退火进行一次调控织构并临界变形对织构二次调控的方法增加对磁性能有利的再结晶织构来优化磁性能，该生产方式工艺简单，成本较低，生产效率高，适用于大批量生产。

本实用新型公开了一种镀铝锌硅钢钣冲压装置,包括安装板，所述安装板的上表面延伸至下表面开设有上下管贯通的板件交换槽，所述安装板的上表面且位于板件交换槽的正上方通过固定螺栓固定连接有模座板。本实用新型，通过设置二次镀膜箱，对冲压后的硅钢钣进行二次铝锌镀膜，避免了冲裁面的暴露导致硅钢钣慢性腐蚀，提升了镀铝锌硅钢板的质量和使用寿命，通过设置夹取机构，对硅钢钣自动取放操作，减少了人力操作，提高了效率的同时，提高了设备安全性，通过设置废料回收槽，对冲压产生的边角料进行集中回收在利用，提升了生产过程中的环保性，通过优化结构设计，提高了镀锌硅钢钣的生产效率，降低生产成本。