本发明特别涉及一种控制边部质量的低牌号无取向硅钢的热轧生产方法，属于无取向硅钢热轧生产技术领域，方法包括：将低牌号无取向硅钢的板坯进行第一次粗轧，将第一次粗轧后的板坯进行第二次粗轧，其中，在第二次粗轧机前的立辊上设置立辊润滑装置，所述立辊润滑装置向所述立辊供给的润滑油的油量为100mL/min‑400mL/min；将第二次粗轧后的板坯进行精除鳞、精轧和卷取，获得边部质量合格的热轧卷；保证良好的立辊辊面状态，可有效解决边部粗糙，有效解决了低牌号无取向硅钢边部粗糙状态，极大的提高了冷轧后工序毛边轧制率，提高了硅钢全工序成材率。

研究了冷轧95%变形量无取向硅钢不同退火温度(710～1 050℃)下再结晶织构特征.再结晶刚完成时(710℃退火),呈现强γ({111<112>～<134>)与弱{114}<481>织构特征;随退火温度升高至900℃,γ明显减弱,{114}<481>组分持续增强,形成典型的{h,1,1}<1/h,1,2>织构;进一步升温至1 050℃,再结晶织构不再发生明显变化.基于EBSD分析,{114}<481>组分的持续强化可归因于其明显的尺寸优势以及较高频率的高能晶界(取向差角为20°～45°). A non-oriented silicon steel was heavily rolled to 95% reduction and subsequently annealed at 710~1 050 ℃ to investigate recrystallization texture evolution.When annealed at 710 ℃ with complete recrystallization,the texture is characterized by a strong partial γ fiber spreading from {111}<112> to {111}<134> and a weak {114}<481> component.As annealing at 900 ℃,γ fiber is decreased significantly while {114}<481> is increased consistently,producing a typical {h,1,1}<1/h,... 

本实用新型公开了一种硅钢片加工装置，涉及到硅钢片加工装置技术领域，包括安装板，所述安装板的上表面两端均固定连接有固定板，所述安装板的上表面一侧固定连接有涂覆装置，所述安装板的上表面中部固定连接有压平装置，所述安装板的上表面另一侧固定连接有烘干装置，所述固定板的一侧底端通过轴承活动连接有传动辊。本实用新型通过在安装板的上表面一侧设置涂覆装置，涂覆装置对硅钢片的两面进行绝缘层涂覆，在安装板的上表面中部设置压平装置，压平装置包括两个压辊，压辊的一侧设置的限位块中部开设有螺纹孔，转动双向螺杆使得限位块运动，从而使得两个压辊之间的间距被调节，可以根据生产需求调节绝缘涂料的压平厚度。

本实用新型公开了一种镀铝锌硅钢钣冲压装置,包括安装板，所述安装板的上表面延伸至下表面开设有上下管贯通的板件交换槽，所述安装板的上表面且位于板件交换槽的正上方通过固定螺栓固定连接有模座板。本实用新型，通过设置二次镀膜箱，对冲压后的硅钢钣进行二次铝锌镀膜，避免了冲裁面的暴露导致硅钢钣慢性腐蚀，提升了镀铝锌硅钢板的质量和使用寿命，通过设置夹取机构，对硅钢钣自动取放操作，减少了人力操作，提高了效率的同时，提高了设备安全性，通过设置废料回收槽，对冲压产生的边角料进行集中回收在利用，提升了生产过程中的环保性，通过优化结构设计，提高了镀锌硅钢钣的生产效率，降低生产成本。

分别采用传统冷轧轧制液和纳米TiO₂的冷轧轧制液,对无取向硅钢板进行了四辊冷轧实验.重点研究两种冷轧轧制液的轧制润滑性能和对轧后硅钢薄带表面质量和耐蚀性能的影响.通过场发射电子显微镜和能谱仪对使用两种轧制液轧后得到的硅钢薄带表面形貌和成分进行了分析.给出了轧制液中TiO₂纳米粒子在轧制过程中的抗磨减摩机理.在轧制载荷较高时,纳米TiO₂轧制液具有优良的轧制润滑性能并能显著改善轧后硅钢薄带的表面质量.同时在高载荷作用下,TiO₂纳米粒子被压入硅钢薄带基体,形成一个滑动系来支撑载荷,从而使润滑膜的耐磨性提高. Non-oriented silicon steel strips were rolled on a four-high cold rolling mill lubricated by a traditional cold rolling liquid and a nano-TiO₂ cold rolling liquid,with emphasis on studying the rolling lubrication performance of both the liquids and their effect on the surface quality and corrosion resisting property of the silicon steel strips.The surface micrograph and composition of the silicon steel strips after being rolled with both the liquids were characterized by field emissio... 

【机构】 武钢研究院； ...

采用EBSD技术研究了有、无拉应力作用下无取向硅钢在晶粒长大过程中织构转变及晶界变化的规律。结果表明:在晶粒生长期间,无应力作用下的硅钢中,{111}〈112〉,{111}〈110〉织构组分强化,而{100}〈001〉织构组分弱化;与无拉应力作用下的情况相比,施加5MPa的拉应力时,{111}〈112〉,{111}〈110〉织构组分强化的速率下降,{100}〈001〉织构组分变化不明显。对于在晶粒生长期间持续变化的{111}〈112〉,{111}〈110〉和{100}〈001〉织构组分而言,虽然有、无拉应力作用下硅钢的{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率均下降,而{100}〈001〉织构组分的高取向差角度晶界频率则上升,但当有拉应力作用后,{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率下降的速率变小,{100}〈001〉织构组分的高取向差角度晶界频率上升的速率稍有变小。通过对无取向硅钢在晶粒长大过程中织构转变及晶界变化规律的研究,分析了合金原子在晶界的偏聚行为。 The rules of texture and grain boundary transformation in the nonoriented silicon steel under applied stress or without applied stress during grain growth were investigated by EBSD.The results show that the {111}〈112〉 and {111}〈110〉 components in the nonoriented silicon steel without stress are strengthened during grain growth whereas {100}〈001〉 component is weakened,but the growth rate of {111}〈112〉 and {111}〈110〉 component decreases,while the area fraction of {100}〈001〉 component doesn’t chang... 

采用光学显微镜和X射线衍射仪研究了常化退火处理对无取向硅钢热轧板和成品退火板显微组织和织构的影响。结果表明:常化退火处理消除了热轧板中的变形组织,促使变形晶粒完成再结晶;常化退火处理使高斯织构和立方织构易通过再结晶在变形带内形核和长大,可显著降低成品退火板的{111}和{112}不利织构组分的占有率,提高{100}和{110}有利织构组分的占有率,从而有利于提高无取向硅钢成品板的磁性能。 The effect of normalizing annealing treatment on microstructure and texture of non-oriented silicon steel hot rolled plates and final products were investigated by means of optical microscope and X-ray diffractometer analysis.The results show that the deformed microstructure of the hot rolled plates transformed into recrystallized grain after normalizing annealing treatment.The grains of Goss texture and cubic texture crystallographic orientation were formed and grown by recrystallization in the... 

采用Nb对Fe-6.5%Si(质量分数)高硅钢进行微合金化处理,结果表明:Nb在高硅钢薄板制备过程中细晶效果明显.铸态、锻态和热轧态组织的晶粒分别细化了17.50%,24.51%和30.13%.铸态样品压缩强度由1365 MPa提高至1520 MPa,延伸率提高77.78%;温轧板试样室温拉伸强度由573 MPa提高至621 MPa,延伸率提高44.44%.利用XRD对厚度为0.30—1.68 mm的温轧板的板面织构演变过程进行跟踪测量,结果发现:初始织构以(011)〈100〉Goss织构为主,单道次变形量为26.2%的情况下,Goss织构完全转化为(100)〈011〉旋转立方织构,随后,在单道次变形为22.6%的情况下,旋转立方织构完全转化为{111}面织构,即纤维织构,并稳定保持至0.30 mm. Fe-6.5%Si（mass fraction） alloy possess perfect magnetic properties,though intermetallics of Fe₁₄Si₂ phase brought 6.5%Si leads to room temperature brittleness and hinder this significant materials industrialization.Nb was adopted into micro-alloying of Fe-6.5%Si high silicon steel. OM,thermal simulated test machine and XRD were employed to study the influence of Nb on high silicon steel in processing stages.Textures of warm-rolled high silicon steel strips were determined b... 

介绍了攀钢冶炼电工钢过程硫含量变化以及过程回硫、增硫情况,采取针对性措施,如:提高铁水装入量、转炉采用石英砂代替复合造渣剂造渣、RH脱硫等,降低钢中硫含量。结果表明:采取相应措施后,电工钢炼成率大幅提高,成品w[S]≤0.008%的比例由改进前的62%提高到92.4%,取得了明显的冶金效果。 The resulfurization and the change of sulphur content in production of electrical steel is analyzed.The targeted measures have been taken,such as increase the loaded quantity of liquid iron,quartz sand replaces the composite slagging agent in the converter and RH desulfurization to decrease the sulphur content of the steel.The result shows,after the measures have been taken,the finished product ratio of electrical steel increase a lot.The ratio of sulfur content of finished product no more than ... 

本发明公开了一种电机制造硅钢片酸洗处理设备及其酸洗处理方法，该电机制造硅钢片酸洗处理设备包括开卷机、一号安装台、二号安装台、一号限位机构、二号限位机构、打磨装置、酸洗装置、干燥装置和切分装置。此外本发明还提一种电机制造硅钢片酸洗处理设备的使用方法,包括以下步骤：S1、硅钢卷安装开卷；S2、表面打磨；S3、硅钢酸洗；S4、表面干燥；S5、硅钢切分。本发明能够在硅钢片在酸洗前对其表面进行打磨处理，有效去除硅钢片表面较为明显的锈迹或者粘附有杂物，使得酸溶液能够与硅钢片表面充分接触反应，而且在硅钢片酸洗后能够及时干燥，有效防止酸溶液继续与硅钢片过度反应，达到提高产品质量的目的。

本实用新型涉及一种多物理因素耦合作用电工钢片矢量磁特性自动测量系统，多物理因素耦合作用电工钢片矢量磁特性自动测量系统包括上位机、数据采集卡、低通滤波器、功率放大器、隔离放大器、励磁装置、矢量B‑H传感器、x方向励磁线圈、y方向励磁线圈、单片机系统、电源、温度自动加载模块和应力自动加载模块。本实用新型实现了电工钢片复杂磁特性测量过程中温度和应力的自动加载，解决了人为操作繁琐，耗时的缺点，使得电工钢片复杂磁特性的测量过程更加方便，高效，可行性更高。