采用双辊薄带连铸工艺制备了厚度为2.4mm的3.98%Si-0.71%Al无取向硅钢带,经常化、冷轧、不同温度退火后,对其显微组织、析出物、织构和磁性能进行了检测分析。结果表明:随着退火温度的提高,退火板晶粒尺寸增大,组织均匀性提高;退火板析出物主要是AlN和MnS与AlN复合析出物,尺寸较粗大,达0.5~2.5μm;退火板织构沿厚度方向变化明显,表层和1/2层存在较强的{100}织构,1/2层还存在较强的{111}织构,1/4层主要是{112}织构;随退火温度的升高相应的铁损和磁感应强度均降低。 Using twin roll thin strip continuous casting technique,the 3.98%Si-0.71%Al no-oriented silicon steel strip in thickness of 2.4mm was produced.The microstructure,precipitates,texture,and magnetic properties of the sheet after normalizing,cold rolling and annealing at different temperatures were studied.The results show that with annealing temperature increase,the grain size and uniformity of annealed sheet increased.The main precipitates in coarse size of 0.5-2.5μm in annealed sheet were AlN and... 

本实用新型公开了一种用于硅钢片生产的螺杆式压缩机立式油气筒，包括：筒体，所述筒体上侧设置有处理模块，且上端为出气口，所述筒体一侧固定安装有用于导入油气的导料管；抽油组件，所述抽油组件包括导管、吸油口管和接口管，所述导管固定安装在筒体远离导料管的一侧，所述接口管固定连接在导管位于筒体外侧的一端，所述吸油口管固定连接在导管位于筒体内侧的一端；过滤组件，所述过滤组件包括过滤板和卡板，所述筒体两侧对称开设有两个安装口，所述过滤板卡设在安装口内部，两个所述过滤板为半圆形，所述卡板固定连接在开口的侧边。本实用新型可以及时的对筒体内部的油渣进行清理，保证了对油液的吸收，延长了油气筒的使用寿命。

本实用新型公开了转盘式硅钢片转运装置，属于硅钢片转运领域，包括本体，所述本体的顶部设置有收纳箱，所述本体的内部水平设置有横板，所述横板的两侧分别与本体内腔的两侧固定连接，所述横板的底部设置有平移机构，所述横板横向活动套接在连接杆，所述连接杆顶端与收纳箱的底部固定连接，所述连接杆的底端固定连接有转动盘，所述转动盘的底部固定连接有固定杆，所述固定杆上活动套接有套筒，通过设置平移机构，平移机构带动铰接杆，铰接杆拉动固定杆，固定杆带动转动盘，转动盘通过连接杆带动收纳箱，使得收纳箱可以进行旋转，将远离工作人员的一侧，调整至靠近工作人员的一侧，从而方便进行安放硅钢片。

本发明涉及低温取向硅钢片制造领域，具体为一种重质硅钢级氧化镁的生产工艺。为提升现有取向硅钢片的表面质量，将工业氧化镁、聚乙烯醇粘结剂和水在不锈钢反应罐中水热合成氢氧化镁，经压滤、煅烧、冷却、气流粉碎、包装产物为重质硅钢级氧化镁。产品具有生产工艺独特、成本较低，能明显提高取向硅钢片的表面质量和增加磁感应强度，降低铁损，提高取向硅钢片的正品率。可针对性在取向硅钢片生产厂家推广使用。

本发明提供一种高磁感低铁损硅钢极薄带的生产方法，包括：对硅钢极薄带进行清洗，并对清洗后的所述硅钢极薄带进行烘干；对烘干后的硅钢极薄带进行涂覆隔离层；将涂覆有所述隔离层的硅钢极薄带进行高温退火处理，其中，高温退火过程包括：快速升温至300～600℃，慢速升温至800～1300℃，并在预设温度时进行保温，保温至预设时间后进行冷却，冷却至50～300℃；对退火处理后的硅钢极薄带进行表面清洗、干燥以及涂覆绝缘层；将涂敷绝缘涂层的硅钢极薄带进行烘干烧结处理，并卷取成品。利用本发明，解决目前硅钢极薄带在连续退火涂层工艺存中存在张力不易控制，而导致硅钢带材的板形变差且极易发生断带等问题。

本实用新型公开了硅钢片铁芯生产线，包括放卷机构、剪切机构、送料机构、叠片机构和下料机构，送料机构包括磁性传送带、送料件和第一定位杆，磁性传送带包括上传送带和下传送带，送料件可沿磁性传送带的正交方向平行伸出，其中，第一送料分台和第二送料分台安装于上传送带的下方并且相背运动，第三送料分台和第四送料分台安装于下传送带的下方并且相背运动，第一定位杆用于定位硅钢片，叠片机构包括叠放台、悬梁和两个六自由度机械手，六自由度机械手吊装于悬梁上，包括有电永磁铁，用于吸取硅钢片，下料机构包括滑板，叠放台放置于滑板上。根据本实用新型的硅钢片铁芯生产线，可提高设备自动化程度，提高叠片速度，从而提高生产线的生产效率。

试验研究了0.3 mm取向硅钢冷轧板(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005A1)的退火温度(760~880℃7 min)和退火时间(820℃3~9 min)对该钢的晶粒尺寸,再结晶和织构的影响。结果表明,最佳初次再结晶退火工艺为820℃5 min,该钢的平均晶粒尺寸为14.20μm,完全再结晶率为92%,不利{111}<110>结构含量为3.16%,有利织构{111}<112>,{012}<001>和高斯织构含量分别0.40%,4.73%和2.46%。 The effect of annealing temperature(at 760 ~ 880 X.for 7 min) and time(at 820℃ for 3~9 min) on grain size,recrystallization rate and texture of 0.3 mm cold-rolled sheet of oriented silicon steel(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005Al) has been tested and studied.Results show that with optimum recrystallized annealing at 820℃ for 5 min,the silicon steel average grain size is 14.20 fun,the complete recrystaUization rate is 92%,the unfavourable-texture {111}< 110 > content in steel is ... 

【摘要】 <正>为了确保电工钢的产品质量,在生产线...

研究了卷取工艺对一种新型含铜无取向电工钢晶粒尺寸、织构演变、铁损和磁感应强度的影响。结果表明,试样织构组分主要为{111}、{112}、{100}和高斯织构,在550℃卷取、保温2～3h,{100}织构有增强趋势,磁感应强度较高,铁损较低。 The effects of coiling process on grain size,texture,core loss and magnetic induction of a new cold rolled non-oriented electrical steel with copper were investigated.The results show that there are mainly {111},{112},{100} and {110}<001> texture.Coiling at 550℃and keeping for 2～3 hours,the {100} texture is enhanced,magnetic induction is higher and core loss is lower. 

电动汽车电机在高速旋转时承受离心力和电磁力的作用,在进行电机转子设计时,既要考虑电磁性能,还要考虑机械性能。对电机转子受力情况进行了综述,分析了转子用电工钢疲劳性能参数的重要性,详细阐述了试样抛光、表面处理、试样的对中和安装对测试结果的影响。 The motor of electric vehicle bears big force for high speed rotors,mainly including centrifugal and electromagnetic forces.The magnetic and mechanical aspects of the electrical steel are crucial to machine design.In this paper,the forces applied on the motor were summarized and importance of fatigue properties was analyzed.The influence of specimen polish,surface treatment,alignment and installation on fatigue testing result were represented in detail. 

利用光学显微镜、TEM和EBSD研究了退火温度对双辊连铸无取向硅钢再结晶组织的影响。结果表明,900℃退火后组织分布不均匀,有大量带状组织,平均晶粒尺寸29.5μm。提高退火温度,晶粒尺寸增大,组织均匀化程度增加,1050℃退火时,带状组织基本消失,平均晶粒尺寸42.2μm。 Effect of annealing temperature on recrystallization microstructure of non-oriented electrical steel produced by twin-roll casting process was investigated using OM,TEM and EBSD.The results show that the recrystallization microstructure is uneven because of many banded grains existing,average grain size is 29.5 μm.With annealing temperature increasing,the recrystallization grain size increases,microstructure becomes more homogeneous.When 1050 ℃ annealing,the banded structure almost disappear and...