硅钢资料

本实用新型涉及电机技术领域，具体涉及一种具有低应力结构的硅钢片、转子和电机。包括硅钢片、开设在硅钢片上的磁钢槽和嵌设在所述磁钢槽内的磁钢组件，所述磁钢组件包括多个磁钢组，所述磁钢组包括靠近转子边缘的一对小永磁体和靠近转子内侧的一对大永磁体，所述硅钢片在转子轭部沿周向分布有径向开槽，且所述径向开槽从硅钢片的中心向边缘延伸。其通过在转子轭部沿周向分设置从硅钢片的中心向边缘延伸的径向开槽，能降低大永磁体左右两侧铁芯刚度差距，从而有效降低隔磁桥处的应力，防止磁钢和铁芯产生形变而断裂。其无需改变电机转子外圆结构，在保证转矩输出的前提下，防止高速旋转时带来空气啸叫声。

为了确保硅钢铬酸盐涂料的环保性,需要严格控制涂料的固化工艺,保证涂料固化过程中涂料中的六价铬充分转化为三价铬。对涂料及原料进行热重分析(TG)及差示扫描量热法分析(DSC)。结果表明,MgO与铬酐混合转化为MgCrO4,使六价铬稳定性增强,其中大部分Cr6+转变为Cr3+发生在620~700℃,在450~500℃高于铬酐发生大量失重,因此必须加入还原剂保证涂料中六价铬被充分还原;超过360℃后树脂会发生分解,因此实际板温不能超过360℃;加入了还原剂的整体涂料的失重温度区间主要在260~320℃,因此涂料固化时钢板的实际温度最佳区间为320~360℃。 Because of the silicon steel chromate coating’s environmental requirements,the paint curing process must be controlled strictly to ensure all Cr( Ⅵ) transforms to Cr( Ⅲ). The TG and DSC analyses of the paint are studied. The reaction of MgO and CrO3 would generate MgCrO4,enhancing the stability of Cr( Ⅵ). The most r( Ⅵ) in MgCrO4 changes to Cr( Ⅲ) at 620-700 ℃,while the CrO3 has a large weight loss at 450-500 ℃. The reductant must be added in the paint to make sure the Cr( Ⅵ) could transform suf... 

本发明公开了一种无取向电工钢清洗工艺，包括以下步骤：1)在脱脂剂箱体中添加脱脂剂溶剂，通过喷射泵将脱脂剂分别从上下两路管道喷出，经过流量控制电磁阀进入喷射梁，通过喷嘴喷洒在带钢表面；2)带钢轧制后温度为100～150℃，速度为600～1000m/min，带钢表面高温确保脱脂剂与带钢表面残留油脂反应充分，且在高速下喷射的脱脂剂与带钢相向而行，使带钢表面反应后残留硅泥、铁粉被迅速带走；3)喷射后的脱脂剂流入收集槽中，通过泵重新打入脱脂剂箱体中，实现脱脂剂的循环利用。其利用轧制时产生的高温及高速对带钢表面残留乳化液斑迹、铁粉、硅泥进行清洗，清洗彻底高效。

本发明涉及电工钢生产技术领域，具体涉及一种冷轧取向电工钢钢带的渗氮处理工艺，旨在解决现有技术渗氮速度慢，渗氮效果不佳，能耗大，生产周期长的问题，包括以下步骤：S1、经过冶炼、连铸后，对铸坯进行热连轧、常化酸洗、冷轧及脱碳退火的工序；S2、在渗氮炉内进行两段渗氮处理：S21、第一段渗氮处理的渗氮温度为750‑950℃，渗氮时间为25‑35s,另外，渗氮介质的喷射压力为0.15‑0.25MPa,渗氮介质的流量为5‑20NL/min；S22、经稀土溶液浸泡1‑2小时后，继续第二段渗氮处理，其渗氮温度为460‑560℃，渗氮时间为10‑25s，另外，渗氮介质的喷射压力为0.15‑0.25MPa,渗氮介质的流量为1‑10NL/min；S3、涂隔离剂、高温净化退火后得到成品。

本发明公开了一种适应高频率工况下低铁损无取向电工钢及其生产方法，所述生产方法包括以下步骤：钢水连续浇铸成板坯—热轧—正火—酸洗—冷轧—连续退火—涂绝缘涂层并固化；所述冷轧步骤中，采用六辊单机架往复式轧机经5道次一次冷轧至目标厚度，冷轧过程中前三道次采用变速异步轧制方法，使钢板表层在剪应力作用下位错密度增加，这样在退火后表层晶粒尺寸细化而心部晶粒粗大，通过本发明的方法可生产得到心部为粗大等轴晶粒，表层为纳米级细等轴晶粒的电工钢产品，该产品的铁损P1.5/50≤2.35W/kg，P1.0/400≤14.0W/kg。

本实用新型公开一种硅钢片卷料悬吊上料装置，包括装配架，装配架之间装配有若干个左右间隔设置的硅钢片卷料限位装置，所述硅钢片卷料限位装置用于装载硅钢片卷料、装配架包括前后对称设置的架板，所述架板上具有矩形凸出端、前、后部位之间所述矩形凸出端之间装配有若干个左右间隔设置的长螺杆、长螺杆贯穿所述硅钢片卷料限位装置，所述长螺杆的端部螺纹连接有螺母、架板的底部固定连接有两个左右间隔设置的轮架杆，所述轮架杆的左右两端均转动连接有滚轮、轮架杆之间固定连接有C形架杆，所述C形架杆上固定连接有悬吊环体，实现将大量生产加工使用的硅钢片卷料进行上料。采用上述方式不仅实现将大量生产加工需要的硅钢片卷料进行输送。

该电磁钢板用涂敷组合物含有环氧树脂、潜伏性环氧树脂固化剂和热塑性弹性体，上述热塑性弹性体的熔点为100℃～200℃，并且弯曲弹性模量为超过5MPa且为100MPa以下，相对于上述环氧树脂与上述潜伏性环氧树脂固化剂的合计100质量份，上述热塑性弹性体的含量为10质量份以上且低于40质量份。

冷轧中中低牌号的无取向硅钢多采用万能凸度轧机(Universal crown mill,UCM)生产,其板形好坏受制于UCM轧机板形调节手段的协调使用。为掌握UCM轧机的板形控制特点,建立基于二维变厚度有限元的辊系弹性变形和基于三维差分的轧件塑性变形的六辊轧机耦合模型,对UCM轧机的板形调控性能进行详尽的分析,包括工作辊和中间辊弯辊、中间辊窜辊的调控功效、辊间接触压力分布等。在此基础上,提出可用指导生产的板形控制策略,指出UCM轧机在横向厚差控制方面的不足。针对工业生产中UCM轧机轧制无取向硅钢横向厚差大的问题,在大量仿真计算的基础上,开发具有高次曲线函数的边部变凸度(Edge variable crown,EVC)的工作辊。采用该工作辊后,各种品种的无取向硅钢的横向厚差不大于10μm的百分比由24%提高到99%,横向厚差的均值小于6μm,远小于之前的13μm。 Medium-low grade non-oriented silicon steel is rolled often by universal crown mill(UCM) during cold rolling.Its shape quality is dependent on the coordinated control of several shape adjustment devices of UCM.In order to understand the shape control characteristics of UCM,coupling model of six-high rolling mill,based on two-dimensional varying thickness finite element rolls elastic deformation model and three-dimensional finite difference strip plastic deformation model,is setup for the detaile... 

以试验室模拟CSP工艺生产的Fe-3Si热轧钢带为研究对象,采用正交试验及方差分析的方法,研究了取向硅钢初次再结晶退火工艺对高温退火后获得锋锐的高斯织构的影响。结果表明:取向硅钢两段式初次再结晶脱碳退火工艺参数加热段保温时间及加热温度是高温退火后获得锋锐高斯织构的主要影响因素,其可信度分别在90%和85%以上;在本试验条件下,通过正交试验获得的最佳退火工艺为:冷硬板经600℃保温3 min和850℃保温6 min。 Fe-3Si hot rolled strip was produced by simulating CSP technology in the laboratory.Orthogonal experiment and analysis of variance were carried out to investigate the influence of primary recrystallization on the sharp Goss texture of the oriented silicon steel.The results show that holding time of the heating section and the heating temperature for a sharp Goss texture of the samples annealed has important implications in this experiment conditions,the two-step decarburization annealing process... 

本实用新型公开了一种防护性能好的硅钢板带加工用卷曲设备，包括底座，所述底座的上表面固定连接有L型安装架，所述L型安装架的一侧固定设有第一电机，所述第一电机的输出端固定连接有第一转轴，所述第一转轴的外表面沿周向等间距设有多组可调卷绕机构，所述第一转轴的一侧设有驱动调节机构。本实用新型通过设置可调卷绕机构及驱动调节机构，硅钢板带卷绕完成后，第二电机带动主动齿轮转动，主动齿轮带动从动齿轮及第二转轴转动，从而两个移动块相互远离带动连杆转动，两个连杆转动带动弧形板向靠近第二转轴的方向移动，从而使弧形板脱离钢带卷的内圈，便于将钢带卷取下，防止工人用力操作过程中划伤。

研究了含铜低碳低硅无取向电工钢中的析出相及其析出机理.由能谱(EDS)及选区电子衍射(SAED)分析可知,铁素体基体上存在的大量弥散分布的等轴状析出相为类B2结构的铜.这些铜析出相的析出机理可以是一般析出、位错析出、台阶机理相间析出和弓出机理相间析出:一般析出在550、650和750℃三个等温温度均可发生;位错析出只发生在较低的等温温度(550℃),此时析出相呈特殊的平行短列状;台阶机理相间析出也可在上述三个等温温度下发生,但650℃等温时最有利于台阶机理相间析出,此时析出相平直列状分布;弓出机理相间析出只发生在较高的等温温度(750℃),析出相弯曲列状分布. Precipitates in low-carbon low-silicon non-oriented electrical steel containing Cu were studied and the precipitation mechanism was analyzed by means of energy dispersive spectrometry(EDS) and selected area electron diffraction(SAED).It is found that the equiaxed precipitates of Cu with B2-like structure distribute dispersively in the non-oriented electrical steel.The precipitation mechanism involves general precipitation,dislocation precipitation,interphase precipitations formed by the ledge me... 

本实用新型涉及一种三角硅钢片检测吸附装置，包括：成品硅钢片传送机构，成品硅钢片传送机构的上方依次设置有初检相机、吸附捕捉装置和废料盒。初检相机用于检测成品硅钢片上是否粘附有三角硅钢片，吸附捕捉装置用于将成品硅钢片上粘附的三角硅钢片吸附捕捉，废料盒用于集中存放吸附的三角硅钢片。初检相机和吸附捕捉装置分别与控制系统连接，控制系统用于通过初检相机拍摄的图像识别成品硅钢片上是否粘附有三角硅钢片。本实用新型通过初检相机实现三角硅钢片的精准识别，通过吸附装置将粘附在成品硅钢片上的三角硅钢片吸附捕捉，通过废料盒使得三角硅钢片的集中存储和清理更加便捷，通过本装置节省了人力、并且比人工操作更加精准。