本实用新型公开了一种硅钢片切割装置，包括底座和硅钢片本体，所述底座的上表面分别设置有驱动机构和切割框，驱动机构的表面设置有激光切割机构，切割框的内底壁开设有条形槽，条形槽的内壁转动连接有丝杠，丝杠的表面螺纹连接有滑动块，滑动块的上表面固定安装有定位框，定位框的内壁设置有电动推杆，电动推杆的推送端设置有定位板。该硅钢片切割装置，在对硅钢片进行切割时，能够通过小型电机的转动使定位框从切割框内移出，从而便于操作人员对硅钢片本体的放置，放置完成后，小型电机反转，使定位框带动硅钢片本体进入切割框内并与在转动辊的作用下滑动进入定位槽内，从而实现对硅钢片本体的有效定位，提高了切割的精确性。

借助光学显微镜、扫描电镜、交流磁性能测量仪和万能拉伸试验机研究了0.3 mm厚高强无取向电工钢冷轧板在780、820、860和900℃退火保温2 min后的组织、织构和性能。结果表明:在退火温度范围内,试验钢均发生了完全再结晶,得到等轴状的铁素体晶粒;随着退火温度的升高,平均晶粒尺寸从9.2μm增长到41.3μm,工频铁损和400 Hz高频铁损均先大幅减小后趋于平缓,磁感应强度先升高后降低。在820℃退火时,铁损P_1.5/50=5.51 W/kg,P_1.0/400=33.22 W/kg均处于较低值,磁感应强度B₅₀₀₀最大,为1.649 T。试验钢的屈服强度和抗拉强度均随退火温度的升高而降低,780℃退火时屈服强度为496 MPa, 900℃退火时降低至407 MPa。综合磁性能和力学性能考虑,试验钢的最佳退火温度是820℃。 Microstructure, texture and properties of 0.3 mm thick high strength non-oriented electrical steel cold rolled sheet annealed at 780 ℃, 820 ℃, 860 ℃ and 900 ℃ for 2 min were studied by means of optical microscope, scanning electron microscopy, AC magnetic property tester and universal tensile testing machine. The results show that in the annealing temperature range, complete recrystallization of the experimental steel occurs and equiaxed ferrite grains are obtained. With the increase of annealin... 

本发明公开了一种硅钢片横剪线裁切设备，包括：本体，所述本体包括工作台、挡屑罩和裁切装置，所述挡屑罩内水平固定安装有横杆，所述裁切装置与横杆下表面滑动连接；两个定位机构，所述定位机构包括第一螺纹杆、第一滑块和压板，所述挡屑罩内壁开设有两个安装槽，两根所述第一螺纹杆分别转动安装在两个安装槽内，两个所述第一滑块分别螺纹套设在两根第一螺纹杆上，两个所述压板分别与两个第一滑块远离安装槽槽底的一端水平固定链接；两个驱动机构，所述驱动机构用于控制第一螺纹杆发生转动。通过驱动装置控制定位机构中压板在垂直方向上的位置便可快速实现对硅钢片的定位工作和解除工作，方便快捷，提高了裁切工作的效率。

一种硅钢生产线退火炉前的换热装置，包含有抽风机（1）、立柱（2）、热交换器（3）、软管（4）和热风机（5）；其特征在于：所述的热交换器（3）由若干组U形不锈钢管连接而成，一端固定在轴套（8）上，另一端通过链条（10）连接在立柱（2）顶端的链条盘（9）上，当链条盘（9）转动时，链条（10）拉动热交换器（3）绕着横轴（7）抬起或放下。本发明通过抽风机（1）将清洁空气抽到热交换器（3）内进行加热，然后再通过软管（4）将热空气输送到热风机（5）内来加热硅钢板（14），有效的利用了热能，避免了凝露导致的板面发蓝现象。

本发明属于冶金技术领域，具体涉及一种基于纳米析出强化制备高强度无取向硅钢的方法。该无取向硅钢包括如下重量百分比的化学成分：Si2.5～4.5wt.％，Ni2.5～6.5wt.％，Al1.0～3.0wt.％，Mn0.1～1.0wt.％，Cu0～1.0wt.％，(C+N+O+S)≤100ppm，其余为Fe；该无取向硅钢的制造方法包括：真空冶炼、浇铸锻造及热轧加工(或者薄带连铸)、常化热处理、酸洗与冷轧加工、再结晶退火、时效热处理。本发明制备的新能源汽车驱动电机转子用高强无取向硅钢厚度为0.20～0.50mm，磁感应强度B50为1.60～1.70T，P10/400为10～31W/kg，屈服强度Rp0.2为700～1000MPa，抗拉强度Rm为740～1150MPa，延伸率A为8～20％，可以满足用户对新能源汽车驱动电机用无取向硅钢性能要求。

本申请提供一种电工钢及其制备方法，制备方法包括：将电工钢的板坯进行热轧获得钢卷；将热轧后的钢卷进行酸洗冷轧；将酸洗冷轧后的钢卷进行第一次罩式退火；将第一次罩式退火后的钢卷进行平整；将平整后的钢卷进行第二次罩式退火；将第二次罩式退火后的钢卷进行重卷，以获得电工钢。本申请提供的电工钢的制备方法采用两次罩式退火，退火的主要目的是消除酸洗冷轧工序产生的加工硬化，使钢板充分再结晶，获得理想的铁损及磁感应强度。而采用两次罩式退火，相对于一次罩式退火工序来说，能够进一步降低铁损，提高电工钢的磁性能。

抑制回硅是低硅品种钢冶炼的重点和难点,南钢中厚板卷厂通过转炉出钢弱脱氧操作,精炼炉弱脱氧升温,脱氧、脱硫造渣,连铸严格的保护浇注及吹氩塞棒、吹氩浸入式上水口的应用等一系列工艺优化和操作的改进,使整个冶炼过程钢水回硅量稳定控制在200×10-6以内,钢水终点成分完全满足低硅钢要求。 Control of increasing silicon is the emphasis and difficulty in low silicon varieties steel smelting.The Nisco Wide Plate/Coil Plant can control the silicon content in molten steel keeping within 200×10-6 through whole steelmaking process by using oxygen residual operation in converter tapping,oxygen residual and increasing temperature,deoxidation,desulfurization,slag refining,protection cast,blowing argon by plugged nozzle,blowing argon by submerged entry nozzle in continuous casting,and other ... 

对应用动态加热进行短时温度退火的取向电工钢进行了二次再结晶研究。所进行研究的实验用取向电工钢是经过终冷轧和后续罩式退火后的一条工业化生产线生产的。研究结果表明,运用短时热处理条件可引起研究钢完全的异常晶粒长大。在实验室处理的材料的织构和金相组织与工业化生产的经过终退火而获得的相同的取向电工钢类似。但是,在实验室处理的取向电工钢的二次再结晶的矩阵中可观测到\"寄生\"晶粒。从磁性观点看,这些\"寄生\"晶粒含有不理想的{111}取向织构。 The present study was made to investigate secondary recrystallization in grain-oriented steels annealed at short time temperature exposures with application of dynamical heating.The investigated GO(Grain Oriented) steels for experiments were taken from one industrial line after final cold rolling reduction and subsequent box annealing.It was shown that application of short time heat treatment conditions could lead to complete abnormal grain growth in the investigated GO steel.The texture and mic... 

通过Axio Imager金相显微镜考察4.5%~7.0%硅(质量分数)对高硅钢材料组织形貌的影响,并利用Fe-6.5%Si高硅钢薄板制备方法对其进行轧制,通过DDL50电子万能试验机对阶段产品进行力学性能测试。结果证明,硅含量为5.58%的高硅钢在实验硅含量区间内存在最大延伸率及最小铸态组织晶粒尺寸。 An investigation about the influence of 4.5%-7.0% Si on microstructure and mechanical properties of high-silicon steel was presented.SEM was adopted to take an observation towards microstructure during fabrication,and DDL50electronic universal testing machine was applied into the detection of tensile curves.The results show that silicon steel with 5.58% Si provides the maximum elongation and minimum grain size as cast. 

本发明公开了一种低牌号无取向电工钢的制造方法，包括：在炼钢时，增加所述低牌号无取向电工钢的板坯的铝元素含量，增加量按重量百分比计为0.08％～0.12％；在热轧板坯加热时，控制所述板坯的出炉温度为1150℃～1200℃；在热轧粗轧时，控制所述板坯的粗轧RT2温度为1000～1050℃；上述方法通过提高铝含量，以升高低牌号无取向电工钢的相转变温度，再结合板坯的出炉温度控制和粗轧RT2温度控制，保证低牌号无取向电工钢在精轧过程中不会因为相变区轧制而产生轧制力波动，从而稳定精轧轧制过程，提高精轧后低牌号无取向电工钢板卷的尺寸和板型精度。

本发明公开了一种高牌号硅钢的穿带激光焊接方法，包括：将焊缝中硅含量降低到Si焊＜1.9%。采用激光+填丝焊接，填丝ER50‑6碳钢焊丝；根据焊缝截面积和激光焊接速度；激光填丝焊接时，激光线能量应足够大，达到填丝在熔池中充分混合，均匀分布，不至于填丝的成分浮在熔池的上半部分。采用此方法使焊缝组织从粗大铁素体变成细小、致密的无碳贝氏体，晶内沉淀相和晶间脆性相相对大幅减少，提高了焊缝韧性和成形性能，保证了高硅硅钢带的穿带焊接和连续生产。

本实用新型涉及变压器铁芯装配技术领域，具体公开了一种硅钢片铁芯的装配工装，包括底座、对称设于底座上的两个承压条以及快速装夹机构；所述快速装夹机构包括设于两个承压条一侧的安装框架、安装于安装框架两侧的侧挡板、紧固组件以及将安装框架和承压条之间定位的卡接组件；所述卡接组件包括安装于安装框架一侧的定位块、以及开设于承压条一侧的定位槽，所述定位块的内部开设有安装槽，本实用新型通过快速装夹机构能够实现安装框架的快速定位，从而便于安装框架的安装，有效的提高了安装框架的拆装效率，有助于硅钢片铁芯的快速装配，可提高硅钢片铁芯的装配效率，增加硅钢片铁芯的生产效益。