以一种新的Fe-Si合金制备工艺为出发点,研究了不同放电等离子体快速烧结工艺(SPS)和Si含量变化对Fe-Si合金材料显微组织与磁性能的影响。结果表明,在烧结温度为1 000℃时制备的Fe-6.5%Si合金(质量分数,下同)的综合磁性能较好,其在50Hz下的铁损为0.549W/kg,最大磁感应强度为0.124 3T,矫顽力245.6 A/m,磁导率0.338mH/m。另外,材料的最大磁感应强度随Si含量的增加显著增长,1 000Hz下,Fe-10.0%Si的最大磁感应强度可达到Fe-6.5%Si合金的5倍左右。 The effects of Si content and SPS technology on microstructure and magnetic properties of Fe-Si alloy material were studied in the paper.It shows that the magnetic properties are the best when the content of Si is 6.5wt% and the sintering temperature is 1 000℃,the iron loss is 0.549W / kg in 50Hz,maximum magnetic induction is 0.124 3T,coercive force is 245.6A / m and permeability is 0.338mH / m。And,the maximum magnetic induction increases significantly with the increase of Si.The maximum magneti... 

根据相关的取向电工钢典型专利技术,概述了日本高磁感低铁损取向电工钢低温板坯加热、抑制剂合理调节、关键成分Mn、C、Sn和Sb调节与利用、新型退火剂和绝缘溶液的制备及细化磁畴等生产工艺最新动态和进展情况,并提出了国内企业申请取向电工钢专利时应当借鉴之处。 According to related typical patent technology for grain-oriented electrical steel sheets,the recent trends and progress situation for production process of grain-oriented electrical steel sheets with high magnetic flux density and low core loss in Japan are summarized including low temperature slab heating,suitably regulating inhibitors,adjusting and utilizing key element Mn,C,Sn and Sb,manufacturing for new annealing agent and insulating solutions,and fining magnetic domain,and some suggestion... 

本发明是高磁感取向硅钢的脱碳退火工艺，首先对硅钢卷进行放卷、活套、清洗；再对硅钢进行脱碳、渗氮处理，氨气流量6‑20m3/h、加湿槽温度30‑70℃，脱碳温度780‑880℃、机组速度45‑75m/min、气氛中氢气比例20‑60％、氮气比例40％‑80％，然后冷却到常温；对硅钢进行活套；再对硅钢进行涂覆氧化镁，涂覆量4‑10g/㎡；最后对硅钢进行干燥和收卷成硅钢卷；通过本发明对高磁感取向硅钢的脱碳退火工艺流程进行了优化设计，调整了脱碳退火工艺中氨气流量、气氛、加湿槽水温等参数，优化了高磁感取向硅钢中碳元素、氮元素和氧元素的含量，最终使高磁感取向硅钢实现稳定的性能，磁感达1.92T。

本实用新型涉及分条机技术领域，且公开了一种硅钢加工用分条机，包括支撑台，支撑台的底部四角均安装有支撑腿,支撑台的两侧均垂直安装有U型架，U型架的顶部通过横梁连接固定，横梁的两端均安装有垂直向下设置的下压调节油缸，下压调节油缸的底部均固定连接固定座，固定座相互远离的一侧均安装有第二条形座；第二条形座的两端垂直贯穿设有导向轴，导向轴两端位于第二条形座外，在导向轴的两端均套设有支撑弹簧；导向轴的底部连接在第一条形座上，并且导向轴的顶部贯穿设有第三条形座，导向轴设有将第三条形座固定的螺母。本实用新型在使用时，上下两组剪切轮交错接触后，经过剪切轮下方的硅钢板能够得到有效地剪切，剪切效率高。

【作者】 朱传芳； 潘恒韬； ...

本实用新型公开了一种硅钢前处理铁泥泵反冲洗装置，包括污泥处理组件，所述污泥处理组件包括置放于污泥池的泵体、与泵体相连的传动轴管、设于传动轴管远离泵体一端的驱动电机以及与泵体相连的污泥管道，所述污泥管道的另一端穿过污泥池与排污管路连通；反冲洗组件，所述反冲洗组件包括与污泥管道相连的冲洗管道以及与冲洗管道相连的冲洗水泵，所述冲洗水泵的另一端与自来水供水管路相连；开关组件，所述开关组件包括设于污泥管道与排污管路连接处的第一阀门以及设于冲洗管道与冲洗水泵连接处的第二阀门。本实用新型减少了因铁泥堵死管道，所造成的电机过载烧坏，提高了生产效率，降低了维修维护成本。

本发明提出了一种可修饰取向硅钢表面的无铬无机绝缘涂料及其制备方法，该涂料按照重量份计包括以下组份：磷‑硅溶胶40‑70份、钛改性增稠剂预溶胶25份、抑泡剂0.2‑1份、流平剂0.05‑0.2份和去离子水3.8‑34.75份。该涂料的制备方法为：先制备磷‑硅溶胶和钛改性增稠剂预溶胶；然后向磷‑硅溶胶中加入抑泡剂并搅拌均匀；再加入去离子水并搅拌均匀；再分次缓慢加入钛改性增稠剂预溶胶并搅拌均匀；最后加入流平剂并搅拌均匀。本发明所制备的无铬无机绝缘涂料可修饰取向硅钢表面瑕疵露晶等形貌缺陷；在取向硅钢表面形成的绝缘涂层具有良好的附着力和耐热性；涂料采用的原料均为无污染的环保材料，解决了含铬绝缘涂料带来的环境危害。

为探究铬、锰元素及退火温度对高强无取向硅钢性能的影响规律,借助OM、SEM、EBSD与万能拉伸试验机等分析不同制造工艺下3组不同含量铬、锰元素的无取向硅钢热轧、常化及退火处理后组织与性能。结果表明,试验钢热轧后组织不均匀,心部为沿轧向分布纤维状组织,边部为少量再结晶晶粒,常化处理能显著改善热轧板组织均匀性,消除热轧板中心部位的纤维状组织。经冷轧及退火后得到多边形铁素体晶粒,其中960℃退火,晶粒尺寸偏大,有利织构{100}组分体积分数减少,不利织构{111}组分体积分数增加,成分为0.2Mn-1Cr的1号试验钢960℃退火后铁损最大,磁感强度偏小;成分为0.5Mn-1Cr的2号试验钢930℃退火后,磁性能与强度等综合性能最佳,工频铁损P_1.5/50为2.41W/kg,高频铁损P_1.0/400为17.36W/kg,磁感应强度B_{5 000}为1.638T,抗拉强度为685MPa。 In order to study the effect of Cr,Mn and annealing temperature on the properties of high-strength non-oriented silicon steel,the microstructure and properties of three groups of non-oriented silicon steel with different Cr,Mn content under different manufacturing processes were analyzed by means of OM,SEM,EBSD and universal tensile tester.The results show that the structure of experimental steel is not uniform after hot rolling,and the core is distributed in fibrous structure along the rolling ... 

在现普通冷轧无取向硅钢的基础上,降低Si含量,复合添加少量辅助元素,组合热轧板处理和成品退火加热技术,研制出了免常化处理的高磁感、低铁损并具有良好耐酸腐蚀性能的新系列无取向电工钢。 Based on existing common cold rolled non-oriented silicon steel,a new series of non-orientedelectrical steel with high induction,low core loss and excellent anti-corrosion property has been developed by reducing Si element,adding complexly a small amount of supplementary elements,and employing combined treatment of hot rolled sheet and finished product annealed heated technology. 

本实用新型提供了一种防止冷轧硅钢卷错位的剪切用输送装置，所述支架安装在放置架一侧，所述支架上设有安装块，所述安装块上设有支撑杆，所述支撑杆上设有气缸一，所述气缸一上设有固定片，所述放置架下设有安装块一，所述安装块一下设有万向轮，所述放置架一侧设有通口一，在使用的时候，可以对于冷轧硅钢卷进行剪切，可以防止在剪切的过程中错位，安装的支撑杆，可以用来放置硅钢卷，里面安装的气缸一可以固定硅钢卷的位置，方便进行旋转，外壳内两侧安装的压板可以通过气缸二压住硅钢片，可以防止其在剪切的过程中错位，安装的刀片可以通过滑轨进行前后移动切割，支架与底座之间没有连接，可以在一卷硅钢卷使用完之后进行更换。

对熔融态钢液进行处理,研究了电脉冲对于取向硅钢凝固组织的影响作用,利用正交试验法研究了脉冲电容、频率、处理时间和电压等脉冲参数的作用效果。结果表明:电脉冲对钢锭晶粒组织具有明显的细化作用,凝固组织的等轴晶比例大幅上升,影响等轴晶比例的最显著性因素为脉冲频率,最优正交试验参数为电容1 200μF,脉冲频率1 Hz,处理时间5 s,脉冲电压800 V。随着输入能量的增大等轴晶率先增大后减小,脉冲输入能量为某值时,等轴晶率最大,利用经典形核理论和热力学对这一现象进行了解释。 The influence of electric pulse on the solidification structure of oriented silicon steel was investigated by applying electric pulse in molten steel.The affection due to different electric pulse parameters such as electric capacity,frequency,applied time and voltage was studied by orthogonal design test.The result showed that solidification structure of oriented silicon steel could be improved by the electric pulse,and the equiaxed crystal ratio increased obviously.The most influential paramete... 

本发明的一种超低碳含钇取向硅钢及其制备方法，化学组成及质量百分比为Si：2.0～4.5％，C：≤0.003％，Y：0.001～0.1％，Mn：0.1～0.25％，Al：0.01～0.02％，Cu:0～0.3％，S：0.02～0.035％，N：0.009～0.011％，其余为Fe和不可避免的杂质元素。生产工艺为：连铸、铸坯加热、热轧、常化、冷轧、初次再结晶退火、二次再结晶退火。本发明采用超低碳的成分，取消了常规取向硅钢脱碳退火工艺，简化了生产流程。通过稀土微合金化解决了因超低碳成分导致的单向铁素体组织抑制剂析出困难的技术难题。本发明制备的含钇取向硅钢厚度为0.2～0.35mm，磁感应强度B8为1.85～1.94T，铁损P17/50为0.9～1.2W/kg，可以用于变压器的铁芯材料，制备流程更为简洁。