硅钢资料

介绍了电工钢生产线连退机组的表面处理工艺,特别是电解清洗系统的工作机理、设备构造、生产工艺及各种影响因素。 This paper introduces the technology of surface treatment of continuous annealing unit in electrical steel production line,in particular the working mechanism,structure of equipment,production techniques and various influence factors of the electrolytic cleaning system. 

本实用新型属于清洁度检测装置领域，具体的说是硅钢前处理带钢表面清洁度在线检测系统，包括操作台和清洁单元；所述清洁单元设置在操作台的端部；所述操作台的端部固接有支撑腿；所述支撑腿的端部固接有顶板；通过设置的清洁单元，对工业相机的镜头表面进行清洁，转动轮盘调节角度，推动推板将水箱内部的水分喷洒在镜头的表面，按压连接杆的端部，橡胶柱和弹簧受力，使用刮板对镜头的表面进行刮擦清理，将镜头的表面灰尘清理干净，避免了灰尘堵塞镜头，影响拍摄效果。

为了提升新能源车用驱动电机的功率密度,各大电机厂商都在不断地提升电机转速,随之而来的问题就是电机的铁耗也在不断增高,如何降低电机铁耗成为了电机厂商必须要解决的难题。本文讨论了电机铁耗的组成部分及影响因素,并对1台8极48槽的永磁同步电机分别使用3种不同厚度的材料进行仿真,对比其效率及铁耗分布,推导出驱动电机中硅钢厚度、铁耗及成本的关系,最后对驱动电机选材提出建议。 In order to increase the power density of traction motor for new energy vehicles,major motor manufacturers have been constantly increasing the motor speed.The following problem that manufacturers have to solve is how to reduce the increasing iron loss when the motor speed is increased.The components and influencing factors of motors’ iron loss were discussed in this paper,and an 8-pole 48-slot permanent magnet synchronous motor using three different thickness materials was simulated.To compare i... 

本发明公开了一种无底层取向硅钢的制备方法，包括以下步骤：S1、坯料预处理、S2、脱碳退火、S3、涂覆隔离剂、S4、高温退火、S5、拉伸热平整和S6、激光去除底层，所述激光去除底层的工艺参数为：激光400‑500W，重复频率100‑150kHz，振镜扫描速度6000‑7000mm/s。本发明利用激光刻痕的物理方法制备了无底层取向硅钢，代替了传统的用酸去除取向硅钢涂层或硅酸镁底层，制备的取向硅钢表面光亮，不含涂层或硅酸镁底层，同时通过退火补偿了激光制备过程中对钢带产生的塑性变形，制备的无底层取向硅钢，磁性能稳定。

本实用新型公开了一种取向硅钢绝缘层烘干装置，涉及取向硅钢技术领域，为解决现有取向硅钢在表面层进行烘干的时候，能源大多没有循环利用，不够节能的问题。所述烘干装置主体的上端面设置有加热泵回送机构，所述加热泵回送机构通过输送管道与烘干装置主体连接，且输送管道设置有两个，两个所述输送管道的两端分别贯穿并延伸至烘干装置主体和加热泵回送机构的内部，所述烘干装置主体的内部设置有烘干输送腔体，所述烘干输送腔体的上方和下方均设置有过滤网，且过滤网设置有两个，两个所述过滤网的一侧均设置有加热机构。

本实用新型公开了一种硅钢卷切边防护装置，包括从左到右依次设置的开卷机、分切机、张力调节机以及收卷机，所述张力调节机前后两侧均设置有通过电机驱动用于收拢切边废料的收料装置。本实用新型，通过两组滚轮的夹持能够对废料进行导向，使得废料准确的经过检测组件之间，通过上下触头相对设置，将切边废料夹在中间，当出现断料后，中间没有支撑，下触头通过第一弹簧带动与上触头接触，形成闭合电路，通过报警组件进行报警，断料时，报警组件工作的同时，收料装置上的电机断电，且第一电磁铁和第二电磁铁通电产生磁性，相互吸附，将上夹板向下带动，上下夹板通过两组防滑垫将料头夹住，避免被甩出，大大增加安全系数。

冷轧中中低牌号的无取向硅钢多采用万能凸度轧机(Universal crown mill,UCM)生产,其板形好坏受制于UCM轧机板形调节手段的协调使用。为掌握UCM轧机的板形控制特点,建立基于二维变厚度有限元的辊系弹性变形和基于三维差分的轧件塑性变形的六辊轧机耦合模型,对UCM轧机的板形调控性能进行详尽的分析,包括工作辊和中间辊弯辊、中间辊窜辊的调控功效、辊间接触压力分布等。在此基础上,提出可用指导生产的板形控制策略,指出UCM轧机在横向厚差控制方面的不足。针对工业生产中UCM轧机轧制无取向硅钢横向厚差大的问题,在大量仿真计算的基础上,开发具有高次曲线函数的边部变凸度(Edge variable crown,EVC)的工作辊。采用该工作辊后,各种品种的无取向硅钢的横向厚差不大于10μm的百分比由24%提高到99%,横向厚差的均值小于6μm,远小于之前的13μm。 Medium-low grade non-oriented silicon steel is rolled often by universal crown mill(UCM) during cold rolling.Its shape quality is dependent on the coordinated control of several shape adjustment devices of UCM.In order to understand the shape control characteristics of UCM,coupling model of six-high rolling mill,based on two-dimensional varying thickness finite element rolls elastic deformation model and three-dimensional finite difference strip plastic deformation model,is setup for the detaile... 

针对目前大部分无取向电工钢处理液为含铬处理液、且需在较高温度下固化的情况,在分析成膜物质性质的基础上,试验研究了一种可低温快速固化的电工钢环保绝缘处理液,研究了其涂装工艺,并测定了涂层的附着性、绝缘性、耐热性、耐蚀性等性能。试验结果表明:该处理液可在150~250℃下快速烘干固化,涂层表面光滑且致密均匀,性能优良,可满足中小电机的使用要求。 At present,most of the insulating fluid for non-oriented electrical steel contains chromium,and should be cured at high temperature.On the basis of analyzing the characteristics of the film-forming substance,a kind of eco-friendly insulating fluid with lower curing temperature for non-oriented electrical steel sheet was developed in the experiments.Then its coating process was studied,and the adhesiveness,insulativity,heat resistance,corrosion resistance and other properties of the coating was m... 

本申请涉及激光焊接技术领域，特别涉及一种电机定子硅钢片自动焊接工装。该工装包括定位组件，压板组件和旋转组件。其中，定位组件用于承载定子硅钢片，所述定位组件具有用于在径向上对定子硅钢片进行限位的限位结构；所述压板组件位于定位组件的顶端，用于压住定子硅钢片；旋转组件承托于定位组件的底端，并带动定位组件转动。本申请实施例提供的一种电机定子硅钢片自动焊接工装，能够解决在旋转焊接时，无法保证定子硅钢片与工装夹具的同心度相同，致使焊缝质量不过关的问题，以及激光焊接中，硅钢片与工装夹具易粘连的问题。

本发明涉及薄规格高牌号无取向硅钢冷轧领域。一种提高超薄规格高牌号无取向硅钢厚度精度的冷轧方法，硅钢成品厚度规格在0.15mm～0.25mm，坯料采用常化酸洗切边后的硅钢卷，初始厚度为2.0～2.3mm，采用二十辊单机架轧机轧制，在轧制过程中，对整个轧制过程进行控制。本发明的有益效果是：解决二十辊轧机超薄规格无取向冷轧硅钢纵向厚度波动同时减小横向同板差的方法。

本发明公开了一种无瓦楞状缺陷的高磁感低铁损无取向电工钢板，其各化学元素质量百分含量为：0＜C≤0.0035％、Si：1.2～2.8％、Mn：0.2～1.0％、P：0.04～0.15％、Sn+Sb：0.02～0.2％，余量为Fe和其他不可避免的杂质。此外，本发明还公开了上述高磁感低铁损无取向电工钢板的制造方法，其包括步骤：(1)冶炼和连铸，其中在该步骤不采用电磁搅拌；(2)热轧，其包括：粗轧、精轧、卷取和均热；其中在粗轧步骤采用2～6道次进行轧制，且粗轧单道次压下率控制在20％～40％之间；(3)上述热轧步骤后不进行常化步骤而直接进行冷轧；(4)连续退火。本发明所述的无瓦楞状缺陷的高磁感低铁损无取向电工钢板在保证较低生产成本的同时，还具有高磁感和低铁损的特性。

本发明公开了一种直流换流阀饱和电抗器用超薄硅钢铁心质量的评估方法，包括以下步骤：S1、外观评价；S2、叠装系数评价；S3、磁性能评价；S4、噪声评价；S5、耐受环境温度变化评价和S6、长期运行性能评价，本发明考虑了直流换流阀饱和电抗器对超薄硅钢铁心外观、叠装系数、磁性能、噪声及长期运行等特性要求，实现了超薄硅钢铁心外形外观的性能评估、铁心基本参数评估、电磁性能评估、耐受环境温度变化评估及长期电热运行特性评估，为直流换流阀饱和电抗器用超薄硅钢铁心可靠运行提供了保障。