针对节能电机对无取向电工钢在磁性能方面的特殊要求,采用普通W600牌号的热轧板为原料,通过大量的现场工艺试验,研究总结出了\"超低张力\"的运行工艺、\"先快后慢\"的加热工艺、\"先湿后干\"的退火脱碳工艺、\"先缓后急\"的冷却工艺,生产出P1.5/50≤4.0 W/kg、B50≥1.70 T的冷轧电工钢产品,满足了节能电机的要求。 Based on the special requirements of no-oriented electrical steel for saving energy motor in magnetic aspects,using common W600 brand of hot rolled plate as raw material,through a large number of real tests,an ultra-low tension process,heating process which was quick at first and then slow,annealing decarburization process which was dry after the first wet,and a cooling technology of \"slow after the first urgent\" were concluded.Electrical steel product with P1.5/50≤4.0W/kg,B50≥1.70T was produced... 

【作者】 谌剑； ...

本发明公开了一种利用取向硅钢氧化镁废弃物生产镁质球团的方法，采用取向硅钢生产过程中的废氧化镁污泥、废氧化镁粉等氧化镁废弃物，以及粗粒铁矿粉、镜像赤铁矿、磁铁精矿、膨润土和石灰石粉为原料，依次经预处理、配料、造球后，再在链箅机‑回转窑‑环冷机上进行干燥预热、焙烧和冷却，得到镁质球团。本发明利用氧化镁废弃物制备镁质球团，既有利于减少氧化镁废弃物带来的环保压力及其外运时产生的处置费用，也能显著降低镁质球团的制造成本，综合利用了钢铁厂的现有资源，生产出环境友好、低成本的镁质球团，为高炉提供优质原料，最终降低炼铁过程的污染物排放，减少环境污染。

本实用新型提供了一种新型的去角硅钢片，包括硅钢片本体，所述硅钢片本体包括叠放区和防护区，所述硅钢片本体设有防护结构，所述防护结构包括叠放区上设有的多个均匀分布的降噪凹槽，所述防护区上下两端分别设有多个防护条，且两两防护条之间设为连接槽，每个所述防护条皆包括与硅钢片本体连接的防护层和减震层，所述防护区底部两侧分别设有减震柱，所述防护区中间设有贯穿孔，所述贯穿孔内设有绝缘螺栓。本实用新型能降低噪音和减少震动影响，从而避免使得变压器寿命及功能性降低。

本申请公开了一种低铝无取向硅钢结晶器液面波动的控制方法，包括：步骤1：KR脱硫，脱硫后铁水硫含量≤0.0015%；步骤2：转炉吹炼，转炉出钢后钢包顶渣厚度≤30mm；步骤3：RH真空处理，RH脱碳结束后，加入铝粒脱氧后钢液循环3‑5min，提升气体流量至0.8‑1.0m3/（h·t）；随后加入合金进行脱氧合金化，提升气体流量至0.5‑0.7m3/（h·t）；步骤4：连续浇注，长水口氩气流量150‑200L/min，连铸塞棒氩气流量5‑10L/min，背压≥0.05bar。本申请的控制方法控制结晶器液面波动≤±1.5mm的比例稳定在90%以上。

本发明提出了一种可修饰取向硅钢表面的无铬无机绝缘涂料及其制备方法，该涂料按照重量份计包括以下组份：磷‑硅溶胶40‑70份、钛改性增稠剂预溶胶25份、抑泡剂0.2‑1份、流平剂0.05‑0.2份和去离子水3.8‑34.75份。该涂料的制备方法为：先制备磷‑硅溶胶和钛改性增稠剂预溶胶；然后向磷‑硅溶胶中加入抑泡剂并搅拌均匀；再加入去离子水并搅拌均匀；再分次缓慢加入钛改性增稠剂预溶胶并搅拌均匀；最后加入流平剂并搅拌均匀。本发明所制备的无铬无机绝缘涂料可修饰取向硅钢表面瑕疵露晶等形貌缺陷；在取向硅钢表面形成的绝缘涂层具有良好的附着力和耐热性；涂料采用的原料均为无污染的环保材料，解决了含铬绝缘涂料带来的环境危害。

本发明公开了一种冷轧硅钢重卷的钢卷跟踪方法，将冷轧硅钢重卷工序中的工艺参数与带钢的长度进行映射，可以查看单位长度处的带钢的工艺参数，为后续进行数据分析、优化参数提供了数据支撑。还将带钢的卷取长度和入口长度进行映射，可以得到带钢在单位长度处的长度值对应的是上一道工序中的长度位置，为后续进行跨工序的长度追溯提供了前提条件。本发明通过收集该工序影响产品质量的关键工艺参数，并形成数字钢卷，可准确预测产品的质量情况，同时根据生产实际大数据，可以对该工序的工艺参数进行优化，实现提升质量、提高生产效率、节能降耗、减少产品封闭率等。

采用双辊薄带连铸技术试制了3.98%Si-0.71%Al无取向硅钢铸带,研究了二次冷轧法对硅钢组织和磁性能的影响。结果表明:硅钢铸带显微组织为等轴晶组织,铸带再结晶较完全,常化对铸带显微组织影响较小。二次冷轧工艺和一次冷轧工艺下,最终退火后成品显微组织为等轴晶组织,二次冷轧法最终退火后的晶粒尺寸小于一次冷轧法。二次冷轧法能够提高成品磁性能. Effect of double cold rolling on magnetic properties and microstructure of 3.98%Si-0.71%Al non-oriented silicon Steel Sheets cast by twin-roll thin strip casting process were investigated.The results show that the structure of the thin strip is equiaxed crystal,the recrystallization is complete and normalizing has lesser effect on microstructure.Using both cold rolled and double cold rolled process,the microstructure is equiaxed grain after final annealing.The average grain size of annealed shee... 

组织和织构是影响无取向硅钢性能的重要因素。为改善产品性能，研究了冷轧压下率（71.7%～87.0%）对高牌号无取向硅钢组织、织构、磁性能和力学性能的影响。结果表明，随冷轧压下率的增加，退火晶粒平均尺寸先减小后增大；高斯和立方织构强度减弱，γ纤维织构增强，α纤维织构转变为较强的α^*（{h, 1, 1}〈1/h, 1, 2〉）织构，并随冷轧压下率的增加而增强，同时其峰值逐渐向{111}面移动；工频铁损P_1.5/50、高频铁损P_1.0/400和磁极化强度J₅₀₀₀同时降低，屈服强度变化不大，表面硬度逐渐增加。当冷轧压下率由84.7%增至87.0%、厚度减至0.30 mm时，高频铁损降幅是工频铁损的11倍，表面硬度增幅变大。以上研究成果对硅钢减薄后织构及组织的优化提供了很好的指导。 Microstructure and texture are critical factors on non-oriented silicon steel properties. In order to improve product properties, this paper studied the effect of cold rolling reduction rate（71.7%-87.0%） on microstructure, texture, magnetic properties and mechanical properties of high-grade non-oriented silicon steel. The results show that with the increase of cold rolling reduction rate, the average size of annealing grain decreases first and then increases. The intensity of Goss and λ fiber te... 

本发明公开了一种电工钢片磁致伸缩模型的建模方法，包括：测量不同旋转磁场下电工钢片磁致伸缩对称蝴蝶曲线εk；对所测量的对称蝴蝶曲线进行辨识，构建磁致伸缩蝴蝶曲线εk的Everett函数数据库；将输入的矢量磁场B波形用旋转磁场形状参数Bmax,最大值方向的方向角θ和椭圆长短轴的长度比λ拟合，得到拟合后结果；通过线性插值法在磁致伸缩Everett函数数据库中进行插值，获得拟合后结果所对应的磁致伸缩Everett函数值Ek；根据Everett函数值Ek计算得出对应的磁致伸缩蝴蝶曲线εk。应用本发明实施例，不仅可以描述矢量磁致伸缩特性，还可以通过计算估算出旋转磁场下的瞬态磁致伸缩。此外，还能够考虑磁致伸缩的各向异性特性。

以试验室模拟CSP工艺生产的Fe-3Si热轧钢带为研究对象,采用正交试验及方差分析的方法,研究了取向硅钢初次再结晶退火工艺对高温退火后获得锋锐的高斯织构的影响。结果表明:取向硅钢两段式初次再结晶脱碳退火工艺参数加热段保温时间及加热温度是高温退火后获得锋锐高斯织构的主要影响因素,其可信度分别在90%和85%以上;在本试验条件下,通过正交试验获得的最佳退火工艺为:冷硬板经600℃保温3 min和850℃保温6 min。 Fe-3Si hot rolled strip was produced by simulating CSP technology in the laboratory.Orthogonal experiment and analysis of variance were carried out to investigate the influence of primary recrystallization on the sharp Goss texture of the oriented silicon steel.The results show that holding time of the heating section and the heating temperature for a sharp Goss texture of the samples annealed has important implications in this experiment conditions,the two-step decarburization annealing process... 

本发明公开了硅钢片卷材加工用张力机构以及硅钢片剪切机，包括安装架、转动装置和按压装置，安装架的上安装块、连接块和下安装块组成凹槽，转动装置包括下转轴和转动驱动单元，下转轴水平设置，可转动地安装于下安装块上，设置于凹槽中，按压装置包括有上转轴和按压驱动单元，上转轴水平设置于下转轴的上方，可转动地安装于上安装块上，设置于凹槽中，并且可沿上安装块上下运动，其中，上转轴可与下转轴抵接。根据本发明的硅钢片卷材加工用张力机构以及硅钢片剪切机，可加强硅钢片卷材输送过程中的张力，降低硅钢片卷材输送的位置偏差率，提高产品合格率，提高原材料利用率，从而提高生产效率。