组织和织构是影响无取向硅钢性能的重要因素。为改善产品性能，研究了冷轧压下率（71.7%～87.0%）对高牌号无取向硅钢组织、织构、磁性能和力学性能的影响。结果表明，随冷轧压下率的增加，退火晶粒平均尺寸先减小后增大；高斯和立方织构强度减弱，γ纤维织构增强，α纤维织构转变为较强的α^*（{h, 1, 1}〈1/h, 1, 2〉）织构，并随冷轧压下率的增加而增强，同时其峰值逐渐向{111}面移动；工频铁损P_1.5/50、高频铁损P_1.0/400和磁极化强度J₅₀₀₀同时降低，屈服强度变化不大，表面硬度逐渐增加。当冷轧压下率由84.7%增至87.0%、厚度减至0.30 mm时，高频铁损降幅是工频铁损的11倍，表面硬度增幅变大。以上研究成果对硅钢减薄后织构及组织的优化提供了很好的指导。 Microstructure and texture are critical factors on non-oriented silicon steel properties. In order to improve product properties, this paper studied the effect of cold rolling reduction rate（71.7%-87.0%） on microstructure, texture, magnetic properties and mechanical properties of high-grade non-oriented silicon steel. The results show that with the increase of cold rolling reduction rate, the average size of annealing grain decreases first and then increases. The intensity of Goss and λ fiber te... 

研究了硅钢铸坯再加热过程中夹杂物的析出行为。采用非水溶液电解提取+扫描电镜观察方法,观察了试样的显微组织,统计了夹杂物的尺寸、种类、数量、分布。结果表明,均热温度为1 523 K时,水淬试样的夹杂物尺寸绝大部分小于0.5μm,0.5～5.0μm的夹杂物数量很少,没有发现5.0μm以上的夹杂物。此外,均热时间为10、30、60、90、120、240 min时,对应试样中0.05～0.2μm的夹杂物数量分别为4.04×104、4.73×104、3.70×104、3.33×104、3.10×104、1.56×104个/mm3。绝大部分夹杂物以MnS、AlN、CuxS类为主,并以三类夹杂物中的两类复合或三类复合居多。三类复合夹杂物总量占每组试样夹杂物总量的90%或以上。随均热时间延长,典型的夹杂物组成会发生如下变化:MnS+AlN+CuxS MnS+AlN AlN。与此同时,MnS、AlN、CuxS三者复合比例从45.2%(均热10 min)降为9.7%(均热240 min)。 The methods of electrolysis extraction from nonaqueous solution and scanning electron microscope were adopted to study the precipitation behavior of non-metallic inclusions in Si steel slabs during reheating processes.The morphologies,chemical compositions,quantity and size distribution of non-metallic inclusions in these steel samples were analyzed.Results show that,when the soaking temperature is 1 523 K,almost all of the non-metallic inclusions are smaller than 0.5 μm,few are in the range of ... 

本申请实施例公开了一种硅钢铁芯生产用多功能卷绕机，包括平台板，所述平台板底部的左侧固定连接有旋转电机，所述旋转电机的输出端固定连接有旋转杆，所述旋转杆的顶部固定连接有转盘，所述转盘的顶部固定连接有铁芯型模，所述铁芯型模的外表面活动连接有限定座，所述平台板顶部中心的左侧固定连接有第一U型板。第一弹簧和升降板的配合使用，可以让使用者下压升降板，使得升降板带动安装杆进行向下移动，继而使得安装杆脱离第二U型板所开设的轴槽，继而使得安装杆的顶部存在一定的间隙，进而可以通过间隙将带盘插入在安装杆上，该方式装卸起来简单快捷，可以有效的减少装卸带盘所消耗的时间，从而提高了设备的工作效率。

本实用新型涉及硅钢生产设备技术领域，具体公开了硅钢冷轧用厚壁套筒，包括外筒和内筒，所述外筒与内筒之间固定有若干连接板，所述外筒上开设有插缝槽，所述外筒的内壁上设有靠近插缝槽设置的限位件，所述限位件包括锁止板和弹性件，弹性件一端固定在外筒的内壁上，另一端固定在锁止板的顶部，所述锁止板上设有朝向插缝槽的斜面。本专利中通过外筒与内筒设置，既提高了整个套筒的厚度，使其能够承受硅钢带卷绕时的压力，同时也减少因提高套筒厚度使得套筒的重量增加的问题，这样设置整个套筒的质量较轻。

一种通过粉末烧结制备高磁性能含磷硅钢薄片的方法，属于粉末冶金技术领域。本发明通过真空熔炼气雾化制备成分范围为Fe‑(3‑6.5)wt.％Si‑(0.05‑1)wt.％P的合金粉，将其放置在陶瓷坩埚中均匀振实并放置重物压住，随后进行高温烧结使其冶金结合，再经热轧、冷轧、退火等处理后，得到具有优异性能的含磷硅钢薄片。本发明在硅钢材料体系中加入P元素，能够有效降低铁损、优化磁性能并促进活化烧结；采用气雾化粉末能够很好地保证产品的少夹杂和纯净度；在低熔点P元素及粉末压烧的协同作用下解决了球形气雾化粉末难以成形的缺陷，并避免了需添加成形剂导致的工艺复杂性及后续的脱胶残碳问题，有效缩短制备工艺流程，具有操作简单、生产效率高、工艺流程短、性能优异等优点。

本实用新型属于硅钢片加工技术领域，尤其是一种永磁同步电机生产用硅钢片加工装置，针对了对硅钢片在进行加工过程中的稳定性与对尘屑的防护效果较差的问题，现提出如下方案，其包括工作台，工作台的顶端侧壁固定有支撑架，支撑架的一侧侧壁固定有转动电机，转动电机的输出端连接有打磨头，工作台的一侧内壁转动连接有转动杆；本实用新型中通过转动杆的转动，使其能够带动转动齿轮与传动齿轮进行转动，实现防护组件对硅钢片在进行加工中的防护效果，实现对硅钢片在进行加工中的固定限位效果，提高其在加工过程中的稳定性与防护功能，通过移动杆的上下移动，使其能够对加工完成的硅钢片进行推动，便于工作人员对其进行拿取。

试验的铸态取向硅钢（/%:0.044⁰.056C,3.12³.32Si,0.08⁰.11Mn,0.002⁰.008S,0.002 9⁰.029 1Als,0.006 2⁰.010 9N）由30 kg高频真空感应炉熔炼。通过场发射扫描电子显微镜/能谱仪（FE-SEM/EDS）研究结果表明,0.002 9%Als钢中氧化物主要为SiO₂,存在片状、棒状及近似球状的独立MnS,未发现含铝的氧化物或氮化物;0.0090%Als钢中出现以Al₂O₃为主的复合氧化夹杂物,存在MnS与AlN的复合析出物。钢中Als增加,复合析出物多呈簇状发展。氧化物容易成为MnS-AlN复合析出的核心,钢中Als含量越低,夹杂物中的MnS含量越高;作为核心的氧化物夹杂的尺寸越小,形成的复合夹杂物的形状越规则,尺寸也越小。热力学计算结果表明,钢中Als含量主要影响了钢中氧化物夹杂的组成和AlN的析出温度及析出量。 Test as-cast grain-oriented silicon steel（/%:0.044 ⁰.056C,3.12 3.32Si,0.08 0.11Mn,0.002⁰.008S,0.002 9⁰.029 1 Als,0.006 2⁰.010 9N） is melted by a 30 kg high frequency vacuum induction furnace.The research results by using field emission-scanning electron microscope/energy dispersive spectrometer（FE-SEM/EDS） show that in 0.002 9%Als steel the main oxide is SiO₂,and there is independent laminable,rod-like and approximate ... 

利用OM、TEM与EDS技术,对Fe-3.2%Si低温取向硅钢热轧板进行不同常化冷却工艺处理后的显微组织、析出相及最终产品的磁性能进行分析,并与热轧板的组织和析出相进行对比。结果表明,常化板较热轧板的表层组织均匀,基体中再结晶比例增加,带状组织变窄;常化板中析出物的数量明显比热轧板的多,析出物主要有AlN、MnS及复合析出的(Cu,Mn)S等。在常化温度1120℃、保温3 min的条件下,采用二段式冷却较空冷、淬沸水、淬常温水的冷却工艺,常化板表层显微组织更均匀,沿板厚方向的显微组织的不均匀性显著,取向硅钢的磁性能最高;常化后采用二段式冷却工艺析出的细小析出物数量最多,且弥散分布在基体中,抑制剂的抑制效果最好,对成品获得高磁性最有利。 Microstructure, precipitate and magnetic characteristic of final products with different normalizing cooling processes for Fe-3.2%Si low-temperature hot-rolled grain-oriented silicon steel were analyzed and compared with the hot-rolled plate by optical microscopy(OM), transmission electron microscopy(TEM), and energy dispersive spectrometry(EDS). The results show that, the surface microstructure is uniform, the proportion of recrystallization in matrix increases, and the banding textures are nar... 

将Fe-1.5Si硅钢试样分别在1 000~1 200℃空气条件下氧化30 min,观察发现在1 000℃和1 100℃时,氧化层与基体界面处存在硅酸亚铁,而当温度为1 200℃时,硅酸亚铁不但存在于界面处,同时也存在于氧化层中.将各温度下得到的带有氧化层的试样进行单道次热轧试验,压下率分别为10%和30%,发现1 000℃和1 100℃时,较高的压下率使氧化层破碎更加严重,但是单道次热轧未能改变氧化层的结构;当温度为1 200℃时,由于液态的硅酸亚铁的出现,单道次热轧能够将界面处的液化的硅酸亚铁层挤压到氧化层中,消除了硅酸亚铁层的钉扎基体的效应,改善了氧化层与基体界面的平直度. Specimens of Fe-1.5Si silicon steel were oxidized at 1 000 ~ 1 200 ℃ in air for 30 min.At 1 000 ℃ and 1 100 ℃ fayalite was observed at the scale/substrate interface.While at 1 200 ℃fayalite was found both at the scale/substrate interface and at the outer oxide layer.Then after the single-pass hot rolling process,with the compression ratio of 10% and 30%,it was found that at 1000 ℃ and 1 100 ℃,higher compression rate accelerated the broken of the scale layers,but the scale structure was not affec... 

借助电子背散射衍射(EBSD)及ZEISS-200MAT金相显微镜对某钢厂普通取向硅钢(CGO)进行研究,研究结果表明:热轧板组织、织构沿板厚方向存在明显的不均匀性,在热轧板表层及次表层发生再结晶,同时存在强度较高的Goss织构,中心层存在较强的{001}<110>变形织构。冷轧组织均呈纤维状条带组织,一次冷轧后,热轧板中的Goss织构消失,织构主要为α、γ织构,经中间脱碳退火后,α、γ织构强度减弱,并出现一定强度的Goss织构和利于Goss织构发展的{554}<225>、{332}<113>等织构,经二次冷轧后,二次冷轧织构类型与一次冷轧织构一致,但织构强度不同。 The grain-oriented silicon steel produced by a steel factory was investigated by EBSD and ZEISS-200 MAT metallographic microscope.The results show that the textures and microstructures along thickness of hot rolled slab are inhomogeneous.The surface layer and the layer near that are recrystallized structure which has a high Goss texture,but there is deformation texture{001}<110>in the central layer.The structure after cold rolling is a structure like fiber strip.After the first cold rollin... 

本实用新型公开了高牌号取向硅钢生产用辊轧机，包括辊轧机本体和夹送辊，所述辊轧机本体的底端安置于承托组件的顶端，且承托组件的两侧对称设置有机架，所述辊轧机本体一侧的机架顶端对称安装有两个换向机构，且两个换向机构顶部的一侧共同设置有上下两个夹送辊。该种高牌号取向硅钢生产用辊轧机中不仅能够通过两个液压缸同步伸缩，带动横担的两端反向旋转，从而灵活调节夹送辊的相对水平高度，进而提高了钢带输送角度的调节效率；而且在夹送辊旋转输送钢带时，换热介质经由两组导液管、旋转接头在夹送辊中输入、输出，通过直接接触进行全面换热，如此循环往复，进一步提高了对钢带的冷却效率。

根据本发明的一个实施例的双取向电工钢板，以重量％计，所述钢板包含Si：2.0至4.0％、Al：0.01至0.04％、S：0.0004至0.02％、Mn：0.05至0.3％、N：0.01％以下且0％除外、C：0.005％以下且0％除外、P：0.005至0.15％、Ti：0.001至0.005％、Ca：0.0001至0.005％和Mg：0.0001至0.005％，余量包含Fe和其他不可避免的杂质，具有从{100}＆lt;001＆gt;起15°以内的取向的晶粒的面积分数为60至99％，具有从{100}＆lt;025＆gt;起15°以内的取向的晶粒的面积分数为1至30％。