硅钢资料

以市场上购买的取向硅钢成品板为原料，经不同压下率冷轧至0.23～0.08 mm不等。借助X射线衍射仪(XRD)检测了冷轧后样品中的织构组分及其含量，利用电子背散射技术(EBSD)测量了试样的取向因子分布情况。观察了孪晶的形貌与晶体学特征，分析了硅钢超薄带的塑性变形行为。结果发现，在平面压缩应力下，{112}<111>滑移系的取向因子较大。随冷轧压下率的增加，Goss织构的含量逐渐减少，{212}<141>织构组分的含量先增加后减少，{111}<112>织构组分的含量逐渐增加，织构组分以{110}<001>→{212}<141>→{111}<112>顺序演变。冷轧后样品中出现了孪晶，其晶体取向为{001}<110>,冷轧过程中孪晶取向没有发生变化。 The commercial finished oriented silicon steel plate as the raw material were rolled to 0.23-0.08 mm. With the X-ray diffractometer(XRD), the texture components and their volume fractions in the cold-rolled samples were detected. And the orientation factor distribution of the cross-section of the samples was measured by the electron backscattering technique(EBSD). The morphology and crystallographic characteristics of twins were observed, and the plastic deformation behaviors of the ultra-thin o... 

本实用新型公开了高牌号取向硅钢生产用辊轧机，包括辊轧机本体和夹送辊，所述辊轧机本体的底端安置于承托组件的顶端，且承托组件的两侧对称设置有机架，所述辊轧机本体一侧的机架顶端对称安装有两个换向机构，且两个换向机构顶部的一侧共同设置有上下两个夹送辊。该种高牌号取向硅钢生产用辊轧机中不仅能够通过两个液压缸同步伸缩，带动横担的两端反向旋转，从而灵活调节夹送辊的相对水平高度，进而提高了钢带输送角度的调节效率；而且在夹送辊旋转输送钢带时，换热介质经由两组导液管、旋转接头在夹送辊中输入、输出，通过直接接触进行全面换热，如此循环往复，进一步提高了对钢带的冷却效率。

采用光学显微镜和X射线衍射仪研究了常化退火处理对无取向硅钢热轧板和成品退火板显微组织和织构的影响。结果表明:常化退火处理消除了热轧板中的变形组织,促使变形晶粒完成再结晶;常化退火处理使高斯织构和立方织构易通过再结晶在变形带内形核和长大,可显著降低成品退火板的{111}和{112}不利织构组分的占有率,提高{100}和{110}有利织构组分的占有率,从而有利于提高无取向硅钢成品板的磁性能。 The effect of normalizing annealing treatment on microstructure and texture of non-oriented silicon steel hot rolled plates and final products were investigated by means of optical microscope and X-ray diffractometer analysis.The results show that the deformed microstructure of the hot rolled plates transformed into recrystallized grain after normalizing annealing treatment.The grains of Goss texture and cubic texture crystallographic orientation were formed and grown by recrystallization in the... 

根据相关的取向电工钢典型专利技术,概述了日本高磁感低铁损取向电工钢低温板坯加热、抑制剂合理调节、关键成分Mn、C、Sn和Sb调节与利用、新型退火剂和绝缘溶液的制备及细化磁畴等生产工艺最新动态和进展情况,并提出了国内企业申请取向电工钢专利时应当借鉴之处。 According to related typical patent technology for grain-oriented electrical steel sheets,the recent trends and progress situation for production process of grain-oriented electrical steel sheets with high magnetic flux density and low core loss in Japan are summarized including low temperature slab heating,suitably regulating inhibitors,adjusting and utilizing key element Mn,C,Sn and Sb,manufacturing for new annealing agent and insulating solutions,and fining magnetic domain,and some suggestion... 

本发明公开一种冷轧硅钢的横向同板差控制方法，具体如下：S1、确定冷轧钢板横向同板差的影响因子，包括：热轧钢卷的热卷凸度、工作辊辊型插入量、中间辊窜动值及冷轧钢卷的总切边量；S2、以影响因子为变量构建冷轧钢板横向同板差的计算模型；S3、将热轧钢卷的热卷凸度及冷轧钢板的目标横向同板差输入计算模型，确定最小冷轧钢卷总切边量下的工作辊辊型插入量及中间辊窜动值。明确客户所需的横向同板差，通过改变工作辊辊型插入量X2及工作辊窜动值X3，以此得到冷轧成品钢卷的总切边量最小值，在满足客户对横向同板差的使用要求前提下，降低生产成本，提高产品竞争力。

采用CVD法制备6.5%Si高硅钢,介绍了具体的制备工艺过程,研究了温度对渗硅速率和试样质量减轻的影响,同时分析了扩散时间对高硅钢中硅分布的影响。结果表明:在CVD反应过程中,反应温度高于1050℃将大大提高渗硅速率,但当温度大于1200℃后,渗硅速率趋于稳定;渗硅后,试样会减轻、减薄,随着温度升高,试样质量减轻的速率逐渐增大,在1200℃左右趋于稳定;扩散时间越长,硅分布越均匀,结合制备效率进行考虑,满足Δw表-中/b≤5的时间为适宜的扩散时间。 6.5%Si high silicon steel was manufactured by using CVD method and the process was introduced,the influence of temperature on the siliconizing rate and quality reducing rate,diffusion time on silicon distribution were investigated.Results as follows: the siliconizing rate will increase quickly when the temperature is higher than 1050 ℃,but the siliconizing rate will become steadily as the temperature up to 1200 ℃;The quality reducing rate will increase with the elevating of temperature and the r... 

利用光学显微镜、TEM和EBSD研究了退火温度对双辊连铸无取向硅钢再结晶组织的影响。结果表明,900℃退火后组织分布不均匀,有大量带状组织,平均晶粒尺寸29.5μm。提高退火温度,晶粒尺寸增大,组织均匀化程度增加,1050℃退火时,带状组织基本消失,平均晶粒尺寸42.2μm。 Effect of annealing temperature on recrystallization microstructure of non-oriented electrical steel produced by twin-roll casting process was investigated using OM,TEM and EBSD.The results show that the recrystallization microstructure is uneven because of many banded grains existing,average grain size is 29.5 μm.With annealing temperature increasing,the recrystallization grain size increases,microstructure becomes more homogeneous.When 1050 ℃ annealing,the banded structure almost disappear and... 

本实用新型公开了一种成品取向硅钢片加工用的卷绕装置，包括机箱和卷绕机，所述机箱的下表面固定安装有底座，所述机箱的一侧表面靠近上方固定安装有控制箱，所述机箱的两侧表面靠近前方固定安装有伸缩机，所述机箱的前端面固定安装有挡板，所述挡板的前端设有卷绕机，所述底座的上表面且位于卷绕机的下方固定安装有定位筒，所述定位筒的内部活动安装有托杆。本实用新型所述的一种成品取向硅钢片加工用的卷绕装置，可以有效的控制卷绕机卷绕取向硅钢片的厚度，从而保证每次卷绕取向硅钢片的厚度都相同，利用伸缩机可以对不同宽度的取向硅钢片进行边缘位置的夹紧，并且可以控制卷绕板与卷绕机之间的间距，从而控制卷绕后取向硅钢片的内径大小。

本发明涉及取向硅钢技术领域，且公开了一种气耗优化成本较低的取向硅钢高温退火工艺，包括如下步骤：S1、将铸坯装炉装炉前先对炉台利用高压空气进行清扫，将通气管内的粉尘或其它杂质吹扫干净，然后根据钢卷的卷径大小选用与之匹配的料盘和料筐，将铸坯放入炉内；S2、炉台密封将装有铸坯的炉台完全密封。该种气耗优化成本较低的取向硅钢高温退火工艺，在高保温阶段使用氨分解气，而氨分解气相对氢气而言比较稳定，在生产成本上也较氢气低，大大的降低了成本节约了能耗，在低保温阶段是为了消除应力，形成一次再结晶晶粒，进行脱碳，高保温阶段二次再结晶，净化钢质和形成烧结硅酸镁底层，最后退火完成后，完成烧结绝缘涂层、热拉伸平整。

本发明涉及一种高性能取向硅钢冷轧工艺，具体涉及取向硅钢制造技术领域。本发明的冷轧工艺包括一次冷轧和二次冷轧，其中，取向硅钢热轧板厚度在2.0～3.0mm，一次冷轧轧制采用4或5道次轧制，轧至厚度0.60～0.62mm，轧制温度为100℃～105℃；二次冷轧轧制采用2道次，轧至厚度0.24～0.26mm，轧制温度为95℃～100℃。本发明通过对一次冷轧和二次冷轧中各道次的压下率、轧制张力、轧制速度、轧制温度进行优化设计，从而能够进一步优化织构，确保二次冷轧板高斯织构含量在0.8～1.5％，且轧制稳定性高，进而有效保证了所得取向硅钢的磁性能。

本实用新型公开了一种优化取向硅钢底层质量的打孔隔板，包括取向硅钢底层和分隔板，所述取向硅钢底层的上方安装有分隔板，且分隔板的内部设置有通孔，所述通孔的下方安装有卡合板，且卡合板的下方安装有硅胶密封垫，所述分隔板的右侧安装有三脚架，且三脚架的右侧安装有螺钉，所述三脚架的左侧安装有螺母，且三脚架的下方安装有固定横杆，所述分隔板的上方安装有定位套筒，且定位套筒的内部设置有内螺纹，所述内螺纹的内部安装有定位横杆，且定位横杆的两侧设置有外螺纹。该种优化取向硅钢底层质量的打孔隔板中，通过设置的通孔，分隔板将取向硅钢底层分隔时，通过通孔可以将分隔连通，减少在使用时分隔板阻拦取向硅钢底层的磁感性能。

在Gleeble-3500热/力模拟试验机上对HW600钢进行高温压缩试验,研究在不同试验条件下的变形抗力。试验结果表明:变形温度对变形抗力的影响最为显著,在相同的变形速率下,随着变形温度的升高,变形抗力降低;在同一变形温度下,变形速率增大,变形抗力增加;在同一变形温度、变形速率下,随着变形程度的增加,变形抗力急剧增大,真应变达到0.1后,变形抗力增加趋势变缓。 The high-temperature compression test is done for HW600 steel with Gleeble-3500 thermal simulation testing machine to research its resistance to deformation under different test conditions.It is showed from result that deformation temperature has greatest effect on the resistance,and along with the temperature getting higher the resistance lowered under same deformation rate;the resistance increases along with deformation rate getting greater under same temperature;and under same deformation tem...