硅钢资料

研究了常化温度、常化时间及常化后冷却速度对Si的质量分数为1.6%的无取向电工钢成品磁性能的影响。结果表明:在850~1 050℃范围内,随着常化温度的升高,成品铁损先减小后增大,成品磁感应强度先增大后减小;当常化温度为1 000℃时,成品平均铁损最低,平均磁感应强度最高;常化时间从3min延长到7min时,成品铁损先减小后增大,成品磁感应强度则呈单调下降趋势;随着常化冷却速度的降低,成品铁损先减小后增大,成品磁感应强度则呈单调增大趋势;对于Si的质量分数为1.6%的无取向电工钢,最佳的常化制度为:在1 000℃进行常化,时间5min,常化后空冷。对热轧板进行常化后,热轧板发生了不同程度的再结晶和晶粒长大。提高常化温度、延长常化时间、降低冷却速度,都能使常化板晶粒粗化,进而粗化成品板晶粒,改善磁性能。通过扫描电镜观察发现,成品板中析出物主要为AlN和MnS的复合析出物,以及少量的单独析出的AlN和MnS,而常化工艺主要是通过粗化析出相,减少细小析出相数量,从而减少对晶界钉扎作用来改善成品磁性能。 The effects of normalizing temperature,normalizing time and cooling rate after normalizing on magnetic properties of non-oriented electrical steel with mass fraction of Si of 1.6% were investigated.The results show that core loss of product decreases first and then increases,while magnetic induction increases first and then decreases with the increase of normalizing temperature from 850 to 1 050℃.Average core loss of product is the lowest and average magnetic induction is the highest when normal... 

研究了硼酸对以Al(H2PO4)3为基料的无铬无取向硅钢绝缘涂层各项性能的影响。用盐雾实验、动电位极化及交流阻抗等试验手段研究了不同硼酸含量对硅钢绝缘涂层的耐蚀性和电化学行为的影响,同时采用SEM对涂层的表面形貌进行了研究。结果表明,硼酸含量为9.7%时,涂层的耐盐雾性及电化学性能最好;硼酸含量过少或过多时,涂层的耐蚀性和电化学性能都较差。 Influence of boric acid on the performance of chromium-free non-oriented silicon steel insulating coating based on aluminum dihydrogen phosphate was investigated.Salt spray experiment,potentiodynamic polarization and electrochemical impedance spectroscopy were used to study the influence of boric acid content on the corrosion resistance and electrochemical behavior of the insulation coating of silicon steel.Surface morphologies of the coatings were tested by SEM.Result shows that when the boric ... 

本发明公开了一种降低无取向硅钢W800头部窄尺的控制方法，步骤1、筛选板坯长度，并使板坯进入加热炉后头部均朝向轧机方向；步骤2、控制板坯头部温差小于10℃；步骤3、固定粗轧到精轧区间内的轧机机架轧制速度；步骤4、固定相变机架，使板坯的奥氏体‑铁素体相变发生在F2和F3机架中；步骤5、调整精轧机架间的负荷分配，降低F2和F3机架的压下量；步骤6、调整活套张力，降低F2和F3机架的活套单位张力补偿；步骤7、降低模型AGC增益，降低F2和F3机架的AGC补偿的辊缝波动量。本发明通过控制固定相变机架、优化相变机架的负荷分配、AGC补偿系数、活套张力等，使秒流量保持平衡，减少无取向硅钢W800头部窄尺。

本发明公开了一种适用于无取向硅钢极薄带表面涂覆的涂液，它由水溶性丙烯树脂、成膜助剂、耐盐雾助剂、流平剂、纳米氢氧化锆、消泡剂、水按质量比100:(2～8):(1～3):(1～5):(0～1):(0.1～0.5):(70～130)组成。将该涂液在无取向硅钢极薄带表面可表现出良好的涂覆性，经烘烤固化后形成的绝缘涂层表面透明光滑，附着性和绝缘性能优良，可有效提升无取向硅钢极薄带的综合性能，适合推广应用。

本实用新型公开了一种取向硅钢绝缘涂液用废液回收利用装置，涉及取向硅钢绝缘涂液技术领域，为解决现有取向硅钢绝缘涂液的废液在回收时没有进行多层热分解，导致回收利用率低的问题。所述下料筒的下端设置有调节筒，所述调节筒的下端设置有分流筒，所述分流筒的下端设置有出料筒，所述调节筒的内部设置有下料板，所述下料板的一端设置有转轴，所述转轴的一端设置有交流电机，所述下料板的侧表面设置有外接孔，所述下料筒的筒壁内设置有加热板，所述下料筒的内部设置有一级过滤网，所述分流筒的内部设置有隔挡板，所述隔挡板的一侧设置有二级过滤网。

本文以热轧常化板为初始材料,采用二次冷轧法与三次冷轧法制备了0.1 mm厚的取向硅钢薄带,测定相应的磁性能,并通过EBSD取向成像技术检测了二次冷轧法与三次冷轧法各工艺过程中织构与组织演变规律。结果表明,采用最终冷轧压下率适中的三次冷轧法,能在冷轧至0.1 mm时保存较多的高斯晶核,使得高温退火后的磁性能明显优于二次冷轧法。最终冷轧压下率通过影响脱碳退火后样品中的{111}<112>织构组分及Goss晶粒数量对最终二次再结晶产生重要影响。 Grain-oriented silicon steel sheets with a thickness of 0. 1 mm were produced from hot-rolled and normalized sheets by two-step-rolling and three-step-rolling methods. Their magnetic properties were measured,and the textures were detected by EBSD technique. The results show that the three-step-rolling method,which has a moderate reduction rate of final cold rolling,can maintain more { 110} < 001 >nucleus,and thus obtaining better magnetic properties compared with the two-step-method. The f... 

为了更好的解决电力系统防污闪涂料RTV-Ⅰ长期应用暴露出来的问题以及目前RTV-Ⅱ防污闪涂料存在的一些不足,结合具体实际需求,在电力系统外绝缘领域,应用新型防污闪硬质涂层——防污闪纳米硅钢涂层,并对分别喷涂了防污闪纳米硅钢涂层以及RTV涂料的绝缘子进行对比运行情况研究分析。研究结果表明,防污闪纳米硅钢涂层是一种同时具有优异憎水性迁移性能和自洁性能的新型涂层,具有良好的应用前景。 In order to solve the problem exposed of anti-pollution flashover coating RTV-Ⅰwhich has been used long-term in power system,as well as to better solve some shortcomings of the current anti-pollution flashover coating RTV-Ⅱ,in this paper,a new anti-pollution flashover hard coating — anti-pollution flashover nanometer silicon hard coating(NSHC) is applied in the field of power system insulation for the specific practical needs.At the same time insulators which are separately sprayed by the NSHC a... 

本发明提供了一种无取向电工钢，以质量百分比计，其成分包括C：0.0010～0.0050％，Si≤2.5％，Al≤0.01％，Mn≤0.80％，P≤0.10％，S≤0.0070％，N≤0.0030％，其余为Fe及不可避免的杂质。本发明还提供了一种无取向电工钢的制备方法。本发明提供的一种无取向电工钢，不添加偏析或稀土等贵重元素且磁性能好、成材率高，本发明提供的无取向电工钢制备方法，工艺流程简单、生产周期短、制取成本低，且无需热轧板常化。

本实用新型公开一种电机加工硅钢片上料装置，包括上料底座，上料底座的顶部固定连接有若干个硅钢片卷料限位柱，上述装置还包括设置在上料底座上方的上料顶座，上料顶座的底部固定连接有若干个与硅钢片卷料限位柱配合的定位柱，上料底座与上料顶座之间滑动连接有两个对称设置的滑动螺杆，滑动螺杆滑动连接所述上料顶座，滑动螺杆的上端螺纹连接有装配螺母，上料底座的左右侧壁部位均装配有第一折形板，上料顶座左右侧壁部位均装配有与第一折形板对称设置的第二折形板，第一折形板与第二折形板之间装配有悬吊组件。采用上述方式不仅实现将若干个硅钢片卷料采用一个夹持定位设备进行夹持定位，且上述装置部件设计安全上料。

为研究常化温度对热轧无取向硅钢组织与织构的影响,采用光学显微镜、背电子散射衍射技术研究了不同常化温度对其影响。结果表明,实验硅钢板在700～850℃温度下常化时,随常化温度的升高,晶粒尺寸增大,有利组分α织构增强,不利组分γ织构降低。对比研究了800℃和850℃常化热轧板CSL晶界分布图与取向差分布图,在本文研究条件下,Goss织构易在Σ=3,9的CSL晶界及晶粒取向差为30°～55°处形成。 The hot strips normalized at different temperatures were investigated by optical microscope and EBSD to study the effect of normalizing temperature on microstructure and texture of hot-rolled non-oriented silicon steel sheets.The results show that the grain size increases,the intensity of α-fibre texture increases,and the γ-fibre texture decreases when the hot strips are normalized at the 700-850 ℃.And CSL boundaries of Σ=3 and 15,and misorientation angles between 30° and 55° are more likely rel... 

本发明公开了叠片装置，以及采用该叠片装置的硅钢片收料设备，包括分料装置和本发明第一方面实施例的叠片装置，分料装置包括有分料件、上分料传送带和下分料传送带，上分料传送带的一端和下分料传送带的一端与分料件连接，分料件用于将硅钢片分别输送至上分料传送带和下分料传送带，本发明第一方面实施例的叠片装置，叠片装置的数量为两个，两个叠片装置上下平行设置，并且分别与上分料传送带和下分料传送带的远离分料件的一端连接。根据本发明的叠片装置，以及采用该叠片装置的硅钢片收料设备，可实现硅钢片的自动叠片，提高生产效率。

本实用新型涉及电工钢加工技术领域，尤其涉及一种电工钢切片用清洁设备，其包括箱体、第一盒体、烘干装置、清洁组件、进水管和出水管；箱体后侧内壁上转动设置导向辊；第一盒体前侧面上设置第二盒体；烘干装置设置在箱体内壁上；第一转动轴转动设置在第一盒体前后内壁上；刷辊设置在第一转动轴上，刷辊上的刷毛与电工钢钢带表面接触；清洁组件设置两组；第二盒体内设置有带动第一转动轴转动且沿第一转动轴轴线方向来回运动的动力组件；两组进水管出水口位于第一盒体上方且朝向电工钢钢带表面；出水管竖直设置在箱体底部。本实用新型中，刷辊转动的同时沿第一转动轴轴线方向来回做往复运动，不存在清洁间隙，提高了清洁效果。