硅钢资料

取向硅钢常化工序主要采用现场实测带钢温度的方式测定冷却速率，并通过稳定冷却水温、调整冷却水量及喷梁运行数量等方式保证合理的冷却速率，给常化工艺设计和生产带来诸多不便。通过对常化工艺水冷过程带钢的传热分析求解，在建立带钢水冷温度模型的基础上，研究了不同冷却工艺参数对带钢温度及冷却速率的影响规律以及冷却工艺的交互作用结果。结果表明：模型计算结果能够较好地反映取向硅钢在常化水冷过程中的温度及冷却速率的变化，其计算误差为0.80%～4.11%;在特定取向硅钢厚度规格和常化工艺下，随着常化冷却水量及有效冷却长度的增加，带钢水冷温度及冷却速率与呈非线性变化；常化水冷工艺主要通过调控带钢与冷却水之间热交换量和交换时间实现对带钢温度的控制，实际生产中需综合考虑机组速度、冷却水量及有效冷却长度之间的交互作用，选定喷梁投入数量和冷却水量以获得稳定的冷却速率。 The cooling rate of normalization process mainly determined by measuring the grain oriented silicon steel strip temperature on site, and ensures the cooling rate by stabilizing the cooling water temperature, adjusting the cooling water volume and the operation quantity of spray beam, which brings inconvenience to the normalization process design and production. Based on the heat transfer of strip in the water cooling section of normalization process, the water cooling temperature model for the n... 

层叠铁芯使用的电磁钢板是在母材钢板(2)的表面具有涂布电磁钢板用涂布组合物而形成的绝缘被膜(3)的电磁钢板，所述电磁钢板用涂布组合物以特定的比率配合有环氧树脂、由烷基酚构成的第一固化剂、由苯酚甲阶酚醛树脂和苯酚酚醛清漆树脂中的任意一方或双方构成的第二固化剂。

电工钢试样加工产生的剪切应力会恶化钢板的磁性,对不同牌号硅钢片的横向、纵向试样退火前后磁性能的变化进行研究,结果表明:无取向硅钢片在剪切过程中横向、纵向的磁性受到剪切应力影响是不一样的。 The electrical steel sample processing magnetic of electrical steel will worsen due to the shear stress of sample. In this paper,the magnetic change of transverse,longitudinal specimens of different type of silicon steel sheet before and after annealing are studied. The results show that the magnetic of non- oriented silicon steel sheet affected in the process of shear is not the same in horizontal and vertical direction. 

本发明提供了一种取向硅钢制作的电机凸极转子，包括由取向硅钢一体制作而成的凸极极身、轭部与极靴，整个转子的易磁方向为径向，通过对轭部厚度、相邻凸极根部中心点距离、凸极极身宽度和极靴尺寸等进行特殊结构设计，能够提高电机功率密度与效率，且无二次气隙与额外的工艺需求。

【作者】 陶永根； ...

研究了常化温度、常化时间及常化后冷却速度对Si的质量分数为1.6%的无取向电工钢成品磁性能的影响。结果表明:在850~1 050℃范围内,随着常化温度的升高,成品铁损先减小后增大,成品磁感应强度先增大后减小;当常化温度为1 000℃时,成品平均铁损最低,平均磁感应强度最高;常化时间从3min延长到7min时,成品铁损先减小后增大,成品磁感应强度则呈单调下降趋势;随着常化冷却速度的降低,成品铁损先减小后增大,成品磁感应强度则呈单调增大趋势;对于Si的质量分数为1.6%的无取向电工钢,最佳的常化制度为:在1 000℃进行常化,时间5min,常化后空冷。对热轧板进行常化后,热轧板发生了不同程度的再结晶和晶粒长大。提高常化温度、延长常化时间、降低冷却速度,都能使常化板晶粒粗化,进而粗化成品板晶粒,改善磁性能。通过扫描电镜观察发现,成品板中析出物主要为AlN和MnS的复合析出物,以及少量的单独析出的AlN和MnS,而常化工艺主要是通过粗化析出相,减少细小析出相数量,从而减少对晶界钉扎作用来改善成品磁性能。 The effects of normalizing temperature,normalizing time and cooling rate after normalizing on magnetic properties of non-oriented electrical steel with mass fraction of Si of 1.6% were investigated.The results show that core loss of product decreases first and then increases,while magnetic induction increases first and then decreases with the increase of normalizing temperature from 850 to 1 050℃.Average core loss of product is the lowest and average magnetic induction is the highest when normal... 

系统研究了无取向硅钢用磷酸盐系涂层性能的影响因素。以氢氧化铝和磷酸为原料制备磷酸二氢铝,再添加适量的添加剂酒石酸铵、二氧化硅、环氧树脂,得到的涂液涂布于硅钢表面,并控制合适的烘干温度,通过耐盐雾实验考察各因素对涂液耐腐蚀性能的影响。实验结果表明,在磷酸与氢氧化铝物质的量比为3.4∶1、酒石酸铵用量为2%、二氧化硅用量为1%、环氧树脂用量为5%、烘干温度为300℃条件下,所得涂层材料的防(耐)腐蚀效果最佳。 The factors influencing the performance of phosphate anticorrosive coating for non-oriented silicon were systematically studied.Aluminum dihydrogen phosphate was prepared with aluminum hydroxide and phosphoric acid as raw materials.Then added the right amount of additives,such as ammonium tartrate,silicon dioxide,and epoxy resin to prepare the liquid coating,which was coated on the surface of the silicon steel,and finally controlled a suitable drying temperature.The influences of various factors... 

结合工业化生产的高效硅钢,进行了RH精炼稀土处理试验研究。针对不同的稀土处理条件,观察了夹杂物的形貌和尺寸分布,探讨了稀土处理后钢中的夹杂物形成、变化规律。结果表明:试验条件下,最佳的稀土合金添加数量为0.6～0.9 kg/t。经过合适的稀土处理后,可以有效抑制尺寸相对较小的、不规则的AlN、MnS复合夹杂生成,促进钢中微细夹杂物的聚合、上浮,钢质纯净度得到明显提高。此时,钢中全氧含量最低,脱硫效果最佳,钢中的夹杂物主要是尺寸相对较大的、近似球形或者椭球形的稀土类夹杂。 Based on the industrial production of non-oriented silicon steel,the experiment on RE treatment during the RH refining process was studied.The morphology and the size distribution were observed for the steel specimens treated with different RE treatment conditions.Further more,the formation and change of inclusions of final steel sheets after RE treatment were discussed.The results show that the suitable RE added amount was 0.6～0.9 kg/t.After the suitable RE treatment,the formation of AlN and Mn... 

本发明提供一种优化无取向硅钢连续退火工艺的铁损预测方法，步骤包括：S1.建立预测模型回归方程表达式；S2.将无取向硅钢中的硅、锰、铝质量含量及预设的退火速度、退火温度代入S1中的回归方程表达式中进行计算；S3.将步骤S2计算得到的预测值与目标值进行比较，如果预测值在目标值的允许误差范围内，则按照预设的退火速度、退火温度进行生产；否则对预设的退火速度、退火温度进行调整，直至预测值能够达到目标值的要求后再进行生产。本发明提供的模型能够提高产品质量，对优化无取向硅钢连续退火工艺具有指导意义。

1.本外观设计产品的名称：硅钢片横剪线。;2.本外观设计产品的用途：对硅钢片料带的冲切、裁断。;3.本外观设计产品的设计要点：在于形状与图案的结合。;4.最能表明设计要点的图片或照片：立体图。;

本发明公开了一种高牌号硅钢的穿带激光焊接方法，包括：将焊缝中硅含量降低到Si焊＜1.9%。采用激光+填丝焊接，填丝ER50‑6碳钢焊丝；根据焊缝截面积和激光焊接速度；激光填丝焊接时，激光线能量应足够大，达到填丝在熔池中充分混合，均匀分布，不至于填丝的成分浮在熔池的上半部分。采用此方法使焊缝组织从粗大铁素体变成细小、致密的无碳贝氏体，晶内沉淀相和晶间脆性相相对大幅减少，提高了焊缝韧性和成形性能，保证了高硅硅钢带的穿带焊接和连续生产。

本发明涉及一种硅钢片自动化纵剪裁切加工设备及加工方法，包括固定架、放卷筒、纵剪装置和裁切装置，所述的固定架的下端与已有地面相连，固定架前后对称分布，前后正相对的固定架之间转动连接有放卷筒，放卷筒的右侧从左至右依次设置有纵剪装置和裁切装置，本发明通过电机、转轴、转动杆做同步高速旋转运动转动杆带动切割刀做同步高速旋转运动，从而可实现切割刀对硅钢卷进行纵向裁剪的功能，使较宽的硅钢卷一分为二形成较窄的硅钢卷，以便提高后续对硅钢进行进一步的加工的速率。