本实用新型公开了一种取向硅钢绝缘涂层液生产用分散机，包括固定底座，固定底座顶端的一侧固定安装有套筒，套筒的内部滑动设有活塞杆，套筒的内部设有电动液压升降柱，电动液压升降柱的底端固定安装在固定底座顶端的中部，电动液压升降柱的顶端与活塞杆的底端固定连接，活塞杆的顶端固定连接有箱体，箱体底端的一侧固定安装有伺服电机，本实用新型的有益效果是：通过滑块、橡胶块、空心转轴和伺服电机的配合使涂层液搅拌分散的更加均匀，通过固定装置可以将盛有涂层液的桶固定住，防止涂层液桶转动，这样可以使涂层液进行充分搅拌，不需要时刻对其调整固定，这样也可以提升工作效率，提高生产速率，而且操作方便。

根据相关的取向电工钢典型专利技术,概述了日本高磁感低铁损取向电工钢低温板坯加热、抑制剂合理调节、关键成分Mn、C、Sn和Sb调节与利用、新型退火剂和绝缘溶液的制备及细化磁畴等生产工艺最新动态和进展情况,并提出了国内企业申请取向电工钢专利时应当借鉴之处。 According to related typical patent technology for grain-oriented electrical steel sheets,the recent trends and progress situation for production process of grain-oriented electrical steel sheets with high magnetic flux density and low core loss in Japan are summarized including low temperature slab heating,suitably regulating inhibitors,adjusting and utilizing key element Mn,C,Sn and Sb,manufacturing for new annealing agent and insulating solutions,and fining magnetic domain,and some suggestion... 

本发明公开了一种显示取向硅钢高温退火试样显微组织的方法，其主要流程为：取样→制样→腐蚀→金相观察；本发明提供的方法显示的试样晶界清晰完整，达到人工和金相分析软件的评级要求，对于精确测量取向硅钢显微组织和磁性能分析提供了更加可靠的条件。

本发明公开了一种硅钢高温加热炉用铬基高氮合金垫块及其制备方法，所述合金垫块含有Cr、Mo、N、La、Ce和Fe，不含有钨；所述合金垫块在高温抗氧化性能和高温抗蠕变性能上，优于现有技术的铬铁合金；本发明可以优化替代现有的硅钢高温加热炉用铬铁合金垫块，满足硅钢在加热炉中的加热需求，大规模工厂化生产，拥有极高的使用价值和广阔的应用市场。

本发明揭示了一种高牌号无取向硅钢及其生产方法，生产方法包括冶炼、连铸、热轧、酸洗、切边、常化、冷轧，冶炼最终所得钢水化学成分以质量百分比计为：C≤0.005％、Si≥2.8％、Als0.5～1.2％、Mn0.25～0.8％、P≤0.02％、S≤0.0040％、N≤0.0020％、Nb≤0.0020％、V≤0.0020％、Ti≤0.0020％，其余为Fe以及不可避免的杂质；切边工序对热轧卷板的两侧进行切边，单侧的剪切宽度为10～20mm；常化在罩式退火炉中进行，均热温度为T＝{(990～1010)‑100×[30×(Si)+20×(Al)]}℃，(Si)为Si的质量百分比，(Al)为Al的质量百分比，均热时间为6h，之后冷却；钢卷在罩式退火炉中冷却至预设温度T0时取出送至冷轧线冷轧，T0为120～180℃，第一道次轧制时的轧制力恒定且轧制力为11000～12000kN。本发明可避免高牌号无取向硅钢在冷轧过程中由于脆性高而导致的频繁断带。

本实用新型公开了一种硅钢片用叠压装置，包括机架，机架上设有工作平台，工作平台的顶面上沿轴向并排设有定位块和可远离或者靠近定位块的抵紧块，定位块的水平截面呈L状，且其与定位块之间形成叠压区，叠压区的上方水平设有可竖直移动的传动板，传动板上竖向滑动穿设有若干均匀分布的导杆，导杆的两端均伸出传动板，且顶端设有限位块，底端共同安装有水平设置的压板，导杆上套设有位于压板和传动板之间的弹簧，机架上还设有与传动板和抵紧块均相连的可编程控制器。本实用新型解决了如何能高效且保质地对硅钢片进行叠压的技术问题，具有工人劳动强度低、叠压效率高且叠压质量好等优点。

本实用新型公开了一种硅钢片横剪线裁切设备，包括：本体，所述本体包括工作台、挡屑罩和裁切装置，所述挡屑罩内水平固定安装有横杆，所述裁切装置与横杆下表面滑动连接；两个定位机构，所述定位机构包括第一螺纹杆、第一滑块和压板，所述挡屑罩内壁开设有两个安装槽，两根所述第一螺纹杆分别转动安装在两个安装槽内，两个所述第一滑块分别螺纹套设在两根第一螺纹杆上，两个所述压板分别与两个第一滑块远离安装槽槽底的一端水平固定链接；两个驱动机构，所述驱动机构用于控制第一螺纹杆发生转动。通过驱动装置控制定位机构中压板在垂直方向上的位置便可快速实现对硅钢片的定位工作和解除工作，方便快捷，提高了裁切工作的效率。

作为一种具有优异高频铁磁性能的合金,Fe-6.5%Si(质量分数)高硅钢在高频工况条件下降损效果明显,对电气行业应用器件高频化、小型化、节能等具有十分重要的意义。通过与取向硅钢测量B-P数据对比,验证了高硅钢高频超低损特性,且轧制高硅钢与日本CVD法生产高硅钢存在基本相同的铁损值。采用国标Epstein Square法对0.30mm高硅钢薄板进行单片测试,并对由0.30mm高硅钢薄板首次装配成的电感器进行铁损测试,对比测试结果表明,元件测试与单片测试数据基本吻合,高磁感应强度条件下,元件测试结果略低于单片测试,分析原因为:线圈引起励磁压降;元件叠片间出现短路,电流增大,损耗增加;气隙板厚度过大。 As one core material with excellent high-frequency ferromagnetism,Fe-6.5%Si performs obviously reduction on core loss in high field frequency which means much to high frequency,minimization,energy conservation in electric industry.Super low loss was verified by drawing B-P curves based on detected experimental data,and which went equal to Fe-6.5%Si thin strip fabricated by CVD in Japan.Fe-6.5%Si was firstly fabricated as inductor in this research,and its core loss was determined for comparison w... 

为了消除硅钢在连续退火机组产生的浪形缺陷,对浪形缺陷产生的主要原因进行了分析。制定了相应控制措施,对炉内带钢张力、冷却段输出、碳套辊与带钢的同步性、无氧化炉燃烧状态等参数进行了调整;在生产组织上安排高低牌号宽窄规格穿插生产、定期更换碳套辊等,实施后效果明显。 The main cause leading to waviness defects of silicon steel is analyzed in order to eliminate the waviness defects of silicon steel in continuous annealing line.And thus corresponding measures for controlling these defects are made by means of adjusting these parameters such as the tension of silicon steel coils in continuous annealing furnace,the output in cooling section and the combusting condition of the non-oxidation furnace as well as keeping the synchronization between carbon sleeved roll... 

通过观察冲剪边缘组织,测量冲剪边缘的显微硬度、残余应力的分布情况和磁性能的变化研究了冲剪加工对无取向硅钢50WW800边缘组织和磁性能的影响。对冲剪后硅钢片进行750℃退火,分析退火对组织和磁性能的影响。结果表明,硅钢片剪切边缘会存在0.4 mm的形变硬化层,边缘应力大,铁损增加。退火后变形减小,形变硬化层变小,残余应力大幅度减少,铁损减少。 The influence of punching process on cutting edge microstructure and magnetic properties of non-oriented silicon steel 50WW800was studied by observing microstructure and measuring microhardness near cutting edge.The residual stress distribution in the silicon steel tooth and magnetic properties were measured.Effect of annealing at 750 ℃ on microstructure and magnetic properties of the silicon steel was analyzed.The results show that a cut-edge hardening layer up to 0.4 mm is observed,residual st... 

本申请涉及激光焊接技术领域，特别涉及一种电机定子硅钢片自动焊接工装。该工装包括定位组件，压板组件和旋转组件。其中，定位组件用于承载定子硅钢片，所述定位组件具有用于在径向上对定子硅钢片进行限位的限位结构；所述压板组件位于定位组件的顶端，用于压住定子硅钢片；旋转组件承托于定位组件的底端，并带动定位组件转动。本申请实施例提供的一种电机定子硅钢片自动焊接工装，能够解决在旋转焊接时，无法保证定子硅钢片与工装夹具的同心度相同，致使焊缝质量不过关的问题，以及激光焊接中，硅钢片与工装夹具易粘连的问题。

本实用新型属于输送设备技术领域，具体涉及一种硅钢拉伸平整用转向辊，包括辊本体，辊本体的中部可拆卸的安装有环形凸块，环形凸块的宽度在350‑450mm，环形凸块的厚度在3‑5mm。在本方案中，在辊本体的中部设置环形凸块，环形凸块能较好的与硅钢的中部位置接触贴合，辊本体通过环形凸块除了能较好的将硅钢输送向前，还能有效防止硅钢跑偏。环形凸块可拆卸的安装辊本体上，当环形凸块使用了一段时间发生了严重的磨损时，更换新的环形凸块即可，无须更换辊本体，有效节省成本。