运用EBSD和光学显微镜,研究了0.25%~0.45%Cu对无取向电工钢热轧板显微组织,成品板显微组织、织构和磁性能的影响。实验结果表明:卷取过程中Cu元素在热轧板表层的偏聚作用显著阻碍了热轧板表层再结晶晶粒长大,导致热轧板表层晶粒尺寸随着Cu含量增加而逐渐较小,但热轧板中间晶粒尺寸变化不大。同时发现Cu元素能够明显改善织构类型,使有利织构组分增加,不利织构组分减少,同时减弱织构强度。从实验结果可知0.35%Cu能够显著改善电工钢的磁性能,铁损P15/50最低达到4.1 W/kg,磁感B50最高值达到1.8 T。 Effects of high content Cu on microstructure of hot rolled plates and microstructure,texture and magnetic properties of annealed finish product plates of non-oriented electrical steel were examined by means of EBSD technique and optical microscope. The results show that surface segregation of Cu significantly hindered recrystallized grain growth of surface layer in hot rolled plate during the coiling,as a result,the surface grain sizes of the hot-rohed plates decrease with the increase of Cu con... 

一种生产取向硅钢的氧化镁涂层烘烤质量控制方法，通过对带钢的实时温度测量建立对烘烤输出功率的实时反馈调节，据此形成基于烘烤输出功率的烘烤质量的实时控制。本发明的一种生产取向硅钢的氧化镁涂层烘烤质量控制方法，通过在烘烤炉出口的带钢上方增加一套可在带钢横向方向移动的在线板温计，基于在线板温检测值对烘烤炉状态进行监控，并建立烘烤输出功率控制系统实时调整，使得氧化镁涂层烘烤质量均匀，提高取向硅钢产品质量稳定性，节省能源消耗。

本发明涉及无取向硅钢技术领域，尤其涉及一种改善高牌号无取向硅钢冷轧断带的控制方法。按重量百分比计：[Si+Al]≥4.0％；Mn、S含量满足：S≤0.0015，[Mn]/[S]:200～400；1)热轧过程中使用保温罩，热轧轧制时投入边部加热，头尾100米内卷曲温度提高15～30℃；2)常化机组圆盘剪进行边部剪边前增加加热装置，剪切后增加毛刺打磨装置，采用煤气明火加热，保证钢板温度在韧脆转变温度以上；3)圆盘剪间隙满足关系式：ds＝(0.15～0.45)d0ds:圆盘剪间隙，μm；d0:常化板板厚，mm；4)常化采用快速加热，控制钢带的预热段升温速度320～380℃/min，机组速度20～30m/min；5)常化工艺后，控制边部小于20μm的晶粒占比在5％以内。有效的减少了冷轧断带的发生，提高成材率1.30％以上，降低了生产成本。

本实用新型公开了一种大型硅钢片生产用输送装置，包括支撑座，所述支撑座的顶部安装有第一支架和第二支架，且第一支架位于第二支架的上方，所述第二支架的一端伸出支撑座的底部，其中，所述第一支架的外部套设有多组第一皮带，所述第一支架的内部安装有多组气缸，且气缸的一侧安装有感应器；所述第二支架的外部套设有两组第二皮带以及两组第三皮带，且两组第二皮带分别位于第二支架的两侧，两组所述第三皮带位于两组第二皮带之间，且第三皮带的长度小于第二皮带的长度。本实用新型所述的一种大型硅钢片生产用输送装置，通过对第一皮带增加磁性，并对调整第三皮带之间间距，能够轻松将转子和定子进行分类堆叠，节省机械手运行的时间。

轧制力是影响冷轧带钢厚度精度的关键因素。为实现高精度的冷轧带钢厚度控制,通过优化变形抗力模型参数和摩擦系数模型参数提高冷轧轧制力模型计算精度,并使用指数平滑法的自学习算法保证轧制力精度的稳定性。在首钢股份公司迁安钢铁公司20辊森基米尔轧机生产线进行S12硅钢钢种轧制力优化试验,将优化的模型参数应用于L2并投入现场生产,结果表明该优化方法不仅提高了轧制力设定精度,而且减小了冷轧硅钢的厚度超差长度,提高了成材率。 The rolling force is the key factor which influences the accuracy of cold-rolling strip thickness. To implement high precision control of cold-rolling strip thickness,we optimize the deformation resistance model parameters and friction coefficient model parameters to improve the calculation precision of cold-rolling force model,and use exponential smoothing self-learn algorithm to ensure the stability of rolling force accuracy. In Shougang Qiangang 20-high Sendzimir mill single stand production ... 

【摘要】 <正>3月底,宝钢\"低温高磁感取向硅钢制造...

对欧盟市场汽车压缩机专用产品进行技术解析,对比分析了其电磁性能、退火和发蓝处理、物理性能、化学成分、应用特点等参数。探讨国内外电工钢产品应用方式的不同特点,并结合鞍钢自身工艺装备和炼钢、热轧、冷轧工艺参数介绍了其生产可行性。提供了冶金工艺流程下,后工序电工钢专业生产线及传统冷轧系统生产线两种生产方式,均能满足用户最终使用要求。 The technology of automotive compressor accommodation manufacture of European Economic and Monetary Union market was described.The magnetic properties,annealing bluing,physical properties,chemical composition,application parameters were analysed.The different characteristics of the application of electrical steel products,the feasibility of manufacture on the existing technology and equipment,steelmaking,hot rolled,cold rolled technical parameters were discussed.The professional product line of ... 

取向硅钢常化工序主要采用现场实测带钢温度的方式测定冷却速率，并通过稳定冷却水温、调整冷却水量及喷梁运行数量等方式保证合理的冷却速率，给常化工艺设计和生产带来诸多不便。通过对常化工艺水冷过程带钢的传热分析求解，在建立带钢水冷温度模型的基础上，研究了不同冷却工艺参数对带钢温度及冷却速率的影响规律以及冷却工艺的交互作用结果。结果表明：模型计算结果能够较好地反映取向硅钢在常化水冷过程中的温度及冷却速率的变化，其计算误差为0.80%～4.11%;在特定取向硅钢厚度规格和常化工艺下，随着常化冷却水量及有效冷却长度的增加，带钢水冷温度及冷却速率与呈非线性变化；常化水冷工艺主要通过调控带钢与冷却水之间热交换量和交换时间实现对带钢温度的控制，实际生产中需综合考虑机组速度、冷却水量及有效冷却长度之间的交互作用，选定喷梁投入数量和冷却水量以获得稳定的冷却速率。 The cooling rate of normalization process mainly determined by measuring the grain oriented silicon steel strip temperature on site, and ensures the cooling rate by stabilizing the cooling water temperature, adjusting the cooling water volume and the operation quantity of spray beam, which brings inconvenience to the normalization process design and production. Based on the heat transfer of strip in the water cooling section of normalization process, the water cooling temperature model for the n... 

一种厚度≤0.15mm无取向硅钢带，其组分及wt%为：Si：2.0～6.5%，Mn：0.13～0.40%，S≤0.020%，P≤0.020%，Als：0.15～0.9%，C≤0.010%；工艺：经冶炼、浇注成坯后热轧至中间坯厚度；冷轧；常温脱脂；光亮罩式退火；经碱洗后涂覆；分条。本发明在保证铁损P1.0/400£13W/kg,磁感B2000³1.5T下，还使钢带厚度公差不超过±0.005mm,最小叠装系数³0.92完全满足连续冲制要求。

本实用新型涉及一种硅钢片叠压精准定位设备，包括压台、压板和仿形燕尾键，所述压台上开有与仿形燕尾键下端相对的限位槽，所述压板设置与压台上方，所述压板上开有与仿形燕尾键上端相对的限位孔。本技术方案当硅钢片叠放压合之后，仿形燕尾键可以去除，并能够在硅钢片组成的铁芯上形成燕尾槽，用于后期燕尾键的组装，且能够保证燕尾槽内的结构规则，便于后期燕尾键组装。

本发明公开了一种高硅钢的冷轧生产工艺。该生产工艺属于机械制造技术领域，其中的处理工序的加热工序通过电磁感应加热装置加热，待处理钢经过加热工序的速度为30‑200mpm，加热工序的加热温度为70‑120℃。本发明具有生产效率高和生产质量高的特点，特别是在加热工序中对待处理钢采用电磁感应加热装置进行加热，使其可以快速有效地提升温度，以满足高硅钢的冷轧生产工艺要求，减少断带事故，具有很好的实用性和创新性。

某冷连轧机生产无取向硅钢板材时,其边缘降的长度合格率频繁超标。为满足用户的叠片厚度精度要求,这类产品必须以增大切边量的方式来保证交货质量,而这种方式又直接降低了金属收得率,提高了生产成本。基于此,以该产线现有设备特性为基础,详细分析其软、硬件功能模式,分别对辊形与反馈控制进行全面分析与优化改进。通过现场试验论证,充分明确依托辊形优化与反馈控制程序的改进能显著提高边缘降的控制水平,该技术的使用为生产现场的边缘降控制提供了合理的技术支撑。 A cold rolling mill production of non-oriented silicon steel sheet,the thickness difference of the edge( edge-drop) is usually exceed the preset standard value,In order to meet the accuracy requirements of the user flatness,these production must be trimed wider length to meet the delivery quality of the user need, which directly reduce the metal yield and increase the manufacturing cost. Therefor,the software and hardware of the production line has been analyzed, and the work roll shape and feed...