试验研究了退火温度(850~950℃)和时间(5~18 min)对2.3 mm热轧硅钢板(/%:0.036C,3.15Si,0.21Mn,0.005P,0.007S,0.032A1)6道次轧制的0.35 mm冷轧板组织和织构的影响。结果表明,退火温度越高,晶粒平均尺寸越大,900℃5 min退火时平均晶粒尺寸41.39μm,试样织构主要集中在γ取向线上的{111}<112>织构组分和{111}<110>织构组分;900℃18 min退火时平均晶粒尺寸为48.08μm,试样的{111}面织构和{112}面织构密度都明显减弱,{001}面织构增强,磁性能较优。 The effect of annealing temperature(850 ~950 ℃) and holding time(5 ~ 18 min) on structure and texture of 0.35 mm sheet by 6 passes cold-rolling from 2.3 mm hot-rolled plate of silicon steel(/%:0.036 C,3.15 Si,0.21 Mn,0.005 P,0.007 S,0.032A1) has been tested and studied.Results show that the higher the annealing temperature the coarser the average grain size;As annealing at 900 ℃ for 5 min the average grain size of steel sheet is 41.39 μm,and the texture in sample is mainly concentrated in y orie... 

本实用新型涉及硅钢生产设备技术领域，具体公开了一种硅钢清洗用张力刷辊结构，包括中空的辊筒，辊筒两端固定有连接盘，连接盘上固定有转轴，辊筒的表面开设有若干排水槽，若干排水槽沿辊筒的周向等间距分布，辊筒的中部设有积水环槽，积水环槽内开设有连通辊筒内壁的进水孔，排水槽为倾斜设置，且排水槽的低端与积水环槽连通，连接盘上开设有排水孔。本专利中对硅钢带进行张紧时，完成清洗的硅钢带表面的水会沿着排水槽进入积水环槽，并从积水环槽进入到辊筒的内部，后排走，这样防止钢带上的水滞留在辊筒的表面，使得辊筒与钢带之间出现打滑的情况；另外多个排水槽的设置，还能够提高钢带与辊筒之间的贴附性，防止出现打滑的问题产生。

电工钢试样加工产生的剪切应力会恶化钢板的磁性,对不同牌号硅钢片的横向、纵向试样退火前后磁性能的变化进行研究,结果表明:无取向硅钢片在剪切过程中横向、纵向的磁性受到剪切应力影响是不一样的。 The electrical steel sample processing magnetic of electrical steel will worsen due to the shear stress of sample. In this paper,the magnetic change of transverse,longitudinal specimens of different type of silicon steel sheet before and after annealing are studied. The results show that the magnetic of non- oriented silicon steel sheet affected in the process of shear is not the same in horizontal and vertical direction. 

本实用新型公开了硅钢片铁芯生产线，包括放卷机构、剪切机构、送料机构、叠片机构和下料机构，送料机构包括磁性传送带、送料件和第一定位杆，磁性传送带包括上传送带和下传送带，送料件可沿磁性传送带的正交方向平行伸出，其中，第一送料分台和第二送料分台安装于上传送带的下方并且相背运动，第三送料分台和第四送料分台安装于下传送带的下方并且相背运动，第一定位杆用于定位硅钢片，叠片机构包括叠放台、悬梁和两个六自由度机械手，六自由度机械手吊装于悬梁上，包括有电永磁铁，用于吸取硅钢片，下料机构包括滑板，叠放台放置于滑板上。根据本实用新型的硅钢片铁芯生产线，可提高设备自动化程度，提高叠片速度，从而提高生产线的生产效率。

以青海盐湖氯化镁为初级原料,采用喷雾热解法制备原料氧化镁。原料氧化镁通过水化制备氢氧化镁。将氢氧化镁过滤、洗涤、烘干、粉碎、煅烧,制备硅钢级氧化镁。本文重点考察煅烧温度、煅烧时间、料层厚度等因素对氧化镁水化率的影响,采用均匀实验设计和DPS数据处理,确定最优煅烧实验条件为:煅烧温度1250℃,煅烧保温时间4小时,料层厚度0.5cm。在此条件下得到的硅钢级氧化镁完全满足硅钢及氧化镁的行业标准。 The magnesium oxide is prepared by Spray pyrolysis process,which magnesium chloride from Qinghai Salt Lake is used as primary raw material,and hydrated to magnesium hydroxide,then obtained silicon steel magnesia through filtering,washing,drying,crushing and calcinations.In this paper,influences of some factors on magnesia hydration rate are studied,such as calcination temperature,calcination time and material thickness.After average experimental design and DPS data processing,optimal calcination... 

本发明公开了一种硅钢高温加热炉用铬基高氮合金垫块及其制备方法，所述合金垫块含有Cr、Mo、N、La、Ce和Fe，不含有钨；所述合金垫块在高温抗氧化性能和高温抗蠕变性能上，优于现有技术的铬铁合金；本发明可以优化替代现有的硅钢高温加热炉用铬铁合金垫块，满足硅钢在加热炉中的加热需求，大规模工厂化生产，拥有极高的使用价值和广阔的应用市场。

对CSP流程生产的无取向电工钢M50W800不同尺寸样品的磁性能进行了测试和分析,结果表明:采用不同单片检测的磁性能结果与标准的Epstein方圈样品检测对比,存在明显的偏差;且同一尺寸的单片纵横向样品之间相比较,对应的磁性能差异性也较大。几种不同尺寸的单片样品,以320mm×30mm尺寸的纵横向平均值最接近标准Epstein方圈样的性能值,其铁损偏差最小。 The magnetic properties of M50W800 non-oriented electrical steel produced by CSP process were tested and analyzed with samples of different sizes,showing that significant deviation existed compared to that of Epstein square circle sample.In particular,obvious difference in magnetic properties also existed between longitudinal and transverse samples of the same size.For test samples of different sizes,the average magnetic properties of 320mm×30mm samples are the closest to that of Epstein square ... 

本实用新型公开了一种电机硅钢片用激光切割机的高压空气冷却干燥装置，包括一端侧带密封端盖且另一端侧设出气接头的换热筒、设在密封端盖的制冷剂进液管和回气管，密封端盖设有进气接头，换热筒内设热交换器，热交换器由换热盘管、换热翅片和下截圆挡板、上截圆挡板组成，下截圆挡板的平底切边、上截圆挡板的平顶切边分别与换热筒内壁具有间隔；制冷剂进液管的一端与制冷系统的一端连接而其另一端顺次连接分液头、毛细管、换热盘管的上端入口，回气管的一端与制冷系统的另一端连接而其另一端依次连接回气汇总管、换热盘管的下端出口；换热筒的底部安装有带放水阀的自动排水部件。通过本装置换热后可获得冷却干燥的高压空气以供激光切割机使用。

本发明公开了一种弧形硅钢片、弧形硅钢片治具及弧形硅钢片制造方法；弧形硅钢片治具包括压制底板和侧挤压板，压制底板和侧挤压板之间具有挤压间隙，挤压间隙的两侧分别设置有位于压制底板内侧的外挤压面和位于压制底板外侧的内挤压面，外挤压面和内挤压面的对应位置上开设有若干齿槽加工台阶，压制底板的下方开设有若干与挤压间隙连通的焊接孔，压制底板和侧挤压板的侧面对应位置设置有贯穿压制底板和侧挤压板的冲压模孔；通过弧形硅钢片制造方法，采用弧形硅钢片治具制成弧形硅钢片。本发明采用弧形硅钢片治具及弧形硅钢片制造方法实现动子中弧形硅钢片的压制成型，通过弧形硅钢片实现直线电机的圆周运动或圆弧运动。

本实用新型涉及硅钢片铁芯装配组件技术领域，公开了一种硅钢片铁芯的装配工装，包括装配组件，所述装配组件的内部上方安装有液压伸缩杆，所述液压伸缩杆的底端固定连接有压板，所述压板的表面开设有孔槽，所述装配组件的底端安装有铁芯，且铁芯的顶端贯穿孔槽的内部，所述铁芯的外部套设有硅钢片，所述硅钢片的外壁对称设有限位辊，所述装配组件的内壁对称安装有电动滑台，且电动滑台的内部设有滑块，本实用新型通过在液压伸缩杆的顶端安装有压板，并且压板的表面开设有与铁芯相匹配的孔槽，液压伸缩杆带动压板升降，对硅钢片进行压实，减少硅钢片之间的缝隙，使得硅钢片之间连接的更加紧凑，减少了工作人员的劳动量。

本发明提供一种无取向硅钢低温无铬环保绝缘涂层立式干燥固化工艺，冷轧无取向硅钢在镀锌机组经过退火后，通过涂层机涂覆低温无铬环保绝缘涂层，再经过立式干燥炉完成干燥固化，生产冷轧无取向硅钢产品。低温无铬环保绝缘涂层厚度0.8~1.0μm；立式干燥炉各段炉温：加热一段炉温420~450℃，加热二段炉温460~490℃，加热三段炉温500~530℃，加热三段出口板温200~240℃，冷却段出口板温60~65℃；立式干燥炉各段加热时间：加热一段、加热二段、加热三段的加热时间均为3.5~4s。采用本发明工艺不仅能保证钢带涂层均匀，使最终产品的涂层具有优异的绝缘性、耐蚀性、附着性、冲片性、焊接性和耐热性，满足下游工序要求，还可提高产品合格率，减少废品，保证生产顺行。

介绍了硅钢CSP工程辊底式均热炉的技术特性,详细阐述了辊底式均热炉工艺特点。根据硅钢均热要求,通过采取不同烧嘴布置方法和燃烧控制技术,选用耐火纤维模块和绝热材料等相关技术措施,满足了出钢温度要求。 The technical specialty for roller hearth furnace of silicon steel CSP Plant was introduced,and the technology characteristics of the roller hearth furnace were illuminated in detail.According to the reheating require of the silicon steel,different burner arrangement and combustion control methods were applied,and technology measures such as selecting refractory fiber module and insulation material and so on were taken,the temperature requirement of silicon steel was met.