通过在实验室条件下模拟薄板坯连铸连轧流程,并在以Cu2S为主抑制剂制造普通取向硅钢(CGO)的基础上,加入适量钒钛,研究了钒钛对取向硅钢组织与磁性能的影响。结果表明,适量钒钛使热轧板和脱碳退火板组织更好,尤其使脱碳退火板的晶粒更加细小和均匀;加入适量钒钛不但使热轧板表面高斯织构强度更高,更使脱碳退火板中有利于高斯织构发展的γ织构强度更高;适量钒钛能形成Cu2S+(V,Ti)N等复合析出物,起到辅助抑制剂作用,加强抑制能力。细小均匀的晶粒、强度更高的有利织构和更强的抑制能力使CGO钢磁性能更佳。 Effect of V and Ti on microstructure and magnetic properties of conventional grain-oriented silicon steel(CGO) were investigated under simulated thin slab continuous casting and rolling process in laboratory with Cu2 S as the dominant inhibitor. The results show that appropriate amount V and Ti make the microstructures of the hot rolled sheet and the decarburizing annealed sheet better,especially make the grains of the decarburizing annealed sheet more tiny and uniform. Adding appropriate V and ... 

针对节能电机对无取向电工钢在磁性能方面的特殊要求,采用普通W600牌号的热轧板为原料,通过大量的现场工艺试验,研究总结出了\"超低张力\"的运行工艺、\"先快后慢\"的加热工艺、\"先湿后干\"的退火脱碳工艺、\"先缓后急\"的冷却工艺,生产出P1.5/50≤4.0 W/kg、B50≥1.70 T的冷轧电工钢产品,满足了节能电机的要求。 Based on the special requirements of no-oriented electrical steel for saving energy motor in magnetic aspects,using common W600 brand of hot rolled plate as raw material,through a large number of real tests,an ultra-low tension process,heating process which was quick at first and then slow,annealing decarburization process which was dry after the first wet,and a cooling technology of \"slow after the first urgent\" were concluded.Electrical steel product with P1.5/50≤4.0W/kg,B50≥1.70T was produced... 

本实用新型属于硅钢片加工技术领域，尤其是一种永磁同步电机生产用硅钢片加工装置，针对了对硅钢片在进行加工过程中的稳定性与对尘屑的防护效果较差的问题，现提出如下方案，其包括工作台，工作台的顶端侧壁固定有支撑架，支撑架的一侧侧壁固定有转动电机，转动电机的输出端连接有打磨头，工作台的一侧内壁转动连接有转动杆；本实用新型中通过转动杆的转动，使其能够带动转动齿轮与传动齿轮进行转动，实现防护组件对硅钢片在进行加工中的防护效果，实现对硅钢片在进行加工中的固定限位效果，提高其在加工过程中的稳定性与防护功能，通过移动杆的上下移动，使其能够对加工完成的硅钢片进行推动，便于工作人员对其进行拿取。

【机构】 武钢研究院； ...

本发明公开了一种硅钢含铬涂层废液处理过程中六价铬浓度在线监控方法，提出一种准确检测废液中六价铬含量的方法和检测时间的确定，实现了含铬废水原液中六价铬含量预测和焦亚硫酸溶液添加量的确定及六价铬在线检测预处理系统的启动时间的确定，确保处理装置安全高效运行。在酸化还原罐上安装氧化还原电位检测仪，实时检测含铬废液在整个处理过程中ORP的变化，推测含铬涂层废液中六价铬还原情况，初步判断还原过程的终点，为在线六价铬自动检测仪的启动提供依据，最终实现解毒后废液六价铬的含量低于0.05mg/L，达到六价铬含量超低处理的要求。

近年来，在节能减排背景之下，国内外众多研究者对无取向电工钢磁性能的提升做了大量研究。为了探索无取向电工钢磁性能提升的方法，对锡或锑对无取向电工钢磁性能的作用机制(晶粒尺寸和晶体织构的控制)进行分析。基于该作用机制，介绍锡或锑的添加对无取向电工钢磁性能的影响。经研究发现，适量的锡或锑在晶界偏聚，不会阻碍晶界的移动并且致使晶粒尺寸降低；与此同时，锡或锑在晶界偏聚不仅抑制{111}织构在原始晶界处形核及生长，还降低(100)晶粒表面能，促进(100)晶粒生长。因此，适量添加锡或锑，可使无取向电工钢铁损下降、磁感提升。最后结合生产工艺，建议无取向电工钢的研究方向应为稀土含量对高牌号无取向硅钢夹杂物尺寸和数量分布的影响，锡或锑的添加量和常化工艺参数(常化时间、常化温度)对常化晶粒尺寸的影响。 In recent years, due to the background of energy saving and emission reduction, numerous researchers all around the world have done a lot of investigations on the improvement of magnetic properties for non-oriented electrical steel. In order to explore the method of improving the magnetic properties of non-oriented electrical steel, the mechanism of tin or antimony on the magnetic properties(the control of grain size and crystallographic texture) of non-oriented electrical steel is illuminated. ... 

为探究铬、锰元素及退火温度对高强无取向硅钢性能的影响规律,借助OM、SEM、EBSD与万能拉伸试验机等分析不同制造工艺下3组不同含量铬、锰元素的无取向硅钢热轧、常化及退火处理后组织与性能。结果表明,试验钢热轧后组织不均匀,心部为沿轧向分布纤维状组织,边部为少量再结晶晶粒,常化处理能显著改善热轧板组织均匀性,消除热轧板中心部位的纤维状组织。经冷轧及退火后得到多边形铁素体晶粒,其中960℃退火,晶粒尺寸偏大,有利织构{100}组分体积分数减少,不利织构{111}组分体积分数增加,成分为0.2Mn-1Cr的1号试验钢960℃退火后铁损最大,磁感强度偏小;成分为0.5Mn-1Cr的2号试验钢930℃退火后,磁性能与强度等综合性能最佳,工频铁损P_1.5/50为2.41W/kg,高频铁损P_1.0/400为17.36W/kg,磁感应强度B_{5 000}为1.638T,抗拉强度为685MPa。 In order to study the effect of Cr,Mn and annealing temperature on the properties of high-strength non-oriented silicon steel,the microstructure and properties of three groups of non-oriented silicon steel with different Cr,Mn content under different manufacturing processes were analyzed by means of OM,SEM,EBSD and universal tensile tester.The results show that the structure of experimental steel is not uniform after hot rolling,and the core is distributed in fibrous structure along the rolling ... 

本发明属于金属材料加工技术领域，具体涉及取向硅钢罩式炉高温退火低保温阶段二段式退火工艺，包括：将涂镁取向硅钢卷装入密闭的罩式炉中，并向罩式炉内通入氮气将炉内氧气充分排出；通电升温并将氮气转换为10m3/h氨分解气，接着点燃放散阀，将温度升至500‑600℃，恒温13h；500‑600℃低保温结束后检测内部气体露点是否小于0℃；本发明提供的取向硅钢罩式炉高温退火低保温阶段二段式退火工艺能够解决普通冷轧取向硅钢罩式炉高温退火热处理低保温阶段，钢卷在高温下不被水蒸汽氧化，消除钢带表面露金、发红、发黑、水印、色泽不均、导通缺陷，降低钢带铁损、提高磁感、降低生产成本。

薄带连铸流程下取向硅钢粗大λ晶粒(〈100〉//ND,normal direction)的“遗传”会导致磁性能恶化.为解决这一问题，针对取向硅钢的热轧孪生行为开展研究，结果表明：凝固组织粗大的取向硅钢在650℃热轧时可产生大量{112}〈111〉形变孪晶，这与具有高层错能的硅钢在较高温度下难以孪生变形的传统认知不同.热轧过程中复杂的应力状态降低了变形孪晶的取向依赖性，由于具有更高的储存能，孪晶界/孪晶界及孪晶界/晶界交叉点成为再结晶形核的优先位置，大大提高了常化过程中的再结晶率，受沿孪晶界应变分布及孪晶间距离的限制，沿孪晶界形核的再结晶晶粒通常呈“饼状”,最终形成以细小且取向漫散的再结晶晶粒为主的常化组织，消除了初始凝固组织中有害的粗大λ晶粒. In strip casting grain-oriented silicon steels, the inheritance of coarse λ grains(〈100〉//ND, normal direction) can deteriorate their magnetic properties. To solve the problem, twinning behaviors in strip casting grain-oriented silicon steels during hot rolling were investigated in this work. It is found that after rolling at 650 ℃, a number of {112}〈111〉deformation twins are formed in the coarse solidification microstructure of the steels, in contrast to the well-accepted view that it is diffic... 

本实用新型涉及热轧设备技术领域，公开了一种高磁感取向硅钢加工用具有定位结构的热轧装置，包括：机体，所述机体的下端固定有底座，所述机体的上端固定有顶板，所述机体的中部开设有安置腔，所述安置腔的两侧内壁开设有滑槽，所述顶板的上端嵌装有液压杆，且液压杆的伸缩端贯穿在安置腔的内部，所述液压杆的伸缩端固定有第一辊座，所述第一辊座的下方安置有第二辊座。该高磁感取向硅钢加工用具有定位结构的热轧装置设置有辊盘，辊盘用于通过螺栓固定内侧的轧辊，使得轧辊能够跟随辊盘的转动而转动，动力传输较为稳定，且轧辊可以从辊盘上进行拆卸，在轧辊损坏进行应急处理时操作更加便利，轧辊便于更换和维护。

本发明涉及一种超纯净无取向冷轧硅钢中非金属夹杂物形貌的原位观察方法，包括如下步骤：制备无取向冷轧硅钢样品，将待测试面用打磨至1000#，使样品表面平整光滑，并进行机械抛光和表面清洗。对处理好的样品在电化学工作站上进行电化学腐蚀，电解液为：1~8wt%氯化物MCl溶液，余量为去离子水，通入CO2气体至饱和，加入适量NaHCO3和三乙醇胺作为稳定剂调节pH值将其稳定在6.0~6.5之间。电化学设定参数：开路：0.5~2h，动电位极化测试：扫描速率:0.1mV/S~1.0mV/S，测试区间：VS.SCE‑0.8V~0.2V，测试温度为：10~25℃。取不同区间内做完电化学腐蚀的样品用去离子水冲洗，吹干。通过扫描电子显微镜+能谱仪对非金属夹杂物的形貌进行原位观察和成分分析。

本发明提供一种电磁屏蔽用1050铝/50W800无取向电工钢钢板生产方法，包括S1)、将轧制好的铝卷和钢卷分别放置在两个开卷机上开卷；S2)、开卷后分别采用HCl、NaOH溶液清洗；S3)、用旋转钢丝刷法对铝板、钢板待结合面进行机械处理10‑15s；S4)、将铝板、钢板置于丙酮溶液中超声波清洗2‑3min；S5)、将表面处理后的铝板、钢板进行预拉伸或者预压缩，S6)、将预应力处理的铝板、钢板边部进行焊接；S7)、将焊接好的钢铝板进行轧前的预热处理；S8)、然后进行连续退火炉中进行退火处理，本发明将金属铝板、钢板通过热轧轧制复合化结合在一起，界面剪切强度≥100MPa，反复弯曲次数≥10次。