本发明提供一种提高硅锰镇静硅钢浇注性的生产方法，属于钢铁冶炼技术领域。其生产流程包括：转炉冶炼→RH真空精炼→连铸。转炉出钢严格控制下渣量，加石灰、渣面脱氧剂调渣；RH真空精炼脱碳结束后，先加入低碳低硫硅铁脱氧，再加入金属锰、磷铁等进行合金化，同时向钢包渣面加入低碳钢渣面脱氧剂对炉渣进行改质，待钢水成分全部命中后加入钙镁铁合金，循环3‑5min后净循环处理6‑10min，破空出钢；连铸采取保护浇注，浇注过程选用塞棒头中Al2O3≥80％、C≤10％、SiC含量8‑15％、气孔率≤12％，质量密度≥2.9g/cm3的塞棒进行控流，连浇炉数≥15炉/中包。本发明可以显著改善浇注过程塞棒头侵蚀问题，提高连浇炉数，降低生产成本。

研究了热处理工艺(退火温度、保温时间、冷却方式)对含Mn的Fe-6.5wt%Si高硅钢热轧带的显微组织及硬度的影响。结果表明,退火温度对Fe-6.5wt%Si合金的组织和显微硬度均有较大影响,随退火温度升高,平均晶粒尺寸和显微硬度均明显增大。小于1 h退火时,晶粒长大缓慢,而长时间(>1 h)退火时,一些次表层晶粒将发生异常长大。水冷组织比空冷组织略细小,但水冷显著降低了显微硬度。Mn含量提高能抑制850℃退火时晶粒的长大,并且促进退火后高硅钢的软化。 The influences of heat treatment process(annealing temperature,heating time,cooling methods) on the microstructure and microhardness of Fe-6.5wt%Si high silicon steel containing manganese for hot rolled strip were studied.The results show that the annealing temperature has a great effect on the microstructure and microhardness of Fe-6.5wt%Si alloy,and as the annealing temperature increases,the average grain sizes and microhardness will significantly increase.When annealing time for less than 1 h... 

【作者】 陶永根； ...

本实用新型公开了一种硅钢片制作用防止硅胶泄露结构，包括运行组件与固定密封组件，所述运行组件的内侧壁设有固定密封组件，所述运行组件包括板体、第一凹槽、壳体、硅钢片、支撑板、连接块、密封圈、防护板和通孔，所述板体的内侧壁开设有第一凹槽，所述第一凹槽的内部设有壳体，所述壳体的内侧壁设有硅钢片，所述硅钢片的两侧相互对称焊接有四个连接块，四个所述连接块相斥一侧均贴合于第一凹槽的内侧壁，本实用新型首先通过硅钢片两侧密封圈保障密封效果，设置的橡胶管起到二次密封防护作用，并借助其内部的弹簧及U型板实现防偏移的效果，最后一方面可以在壳体相邻组件内侧加胶并且提高其内部硅钢片的厚度，以此实现多重密封防漏。

利用EBSD技术研究了电工钢中不同的柱状晶尺寸及退火工艺下{100}织构的演变规律。结果表明,初始晶粒尺寸的影响最显著。细小柱状晶热轧后经过常化处理,组织已均匀,但中心层有强{100}织构。粗大柱状晶中{100}织构的遗传性强,常化及中间退火后,中心层仍有粗大的以{100}取向为主的晶粒;脱碳退火后才能完成组织均匀化和织构梯度的弱化。常化时的升温速度也对织构演变存在影响,低的升温速度有利于{100}织构的保留,但升温速度的影响没有初始晶粒尺寸及退火次数的影响显著。细小柱状晶样品经过热轧及三次退火工艺适合制备取向电工钢。 Evolution of {100} texture of different columnar grains and annealing process was investigated in electrical steels with the help of EBSD technique.The results show that the effect of initial grain size is the strongest.The initial fine-grained specimen shows uniform microstructure after the normalizing process,while {100} grains appear preferentially in the central layer of sheets.The heredity of {100} texture in the initial coarse-grained specimen is more significant.{100} mainly-oriented coar... 

本发明涉及一种永磁电机铁芯电工钢材料优化匹配方法及系统，涉及电机技术领域，包括根据永磁电机的应用场合，确定设计指标和永磁电机模型，并根据永磁电机模型确定电机性能；判断永磁电机的电机性能是否符合设计指标，若是确定第一集合、第二集合以及第三集合的交集；该交集的元素为永磁电机的电机性能满足第一指标、第二指标以及第三指标时对应的硅钢材料。本发明综合考虑了电机的电磁场、温度场、应力场性能，可以在多种电工钢材料中选出与该种转子结构匹配度最高的电工钢材料。

考虑剪应变对微孔洞损伤演化的影响,对GTN损伤模型的损伤演化机制进行修正,建立了适用于不同应力三轴度水平的损伤模型。结合隐式应力更新算法和显式有限元计算,采用VUMAT子程序实现了修正GTN模型在有限元软件ABAQUS中的数值计算。通过模拟纯剪切和剪切-拉伸两组试样的损伤演化和断裂行为,验证了修正GTN模型在不同应力三轴度承载条件下的有效性。运用修正GTN损伤模型模拟含边部缺口的带钢在轧制过程中裂纹的萌生和扩展行为,模拟结果与实验相一致,表明该模型可有效地用于带钢缺陷在轧制过程中扩展行为的分析和预测。模拟和实验结果表明,带钢边部缺口在轧制过程中,缺口前沿和后沿均会萌生裂纹,且后沿裂纹扩展更为明显。 Considering the effect of shear strain of micro-void on damage evolution, a modified GTN model applicable to various stress triaxiality conditions is proposed by modifying the damage evolution mechanism of the GTN damage model. The modified model is implemented in commercial finite element software ABAQUS by combining the implicit stress update method with an explicit finite element solving algorithm and through the user-defined material subroutine VUMAT. The damage evolution and the failure pro... 

针对马钢无取向电工钢孔洞缺陷的分布规律及形貌特征,对缺陷样进行了显微分析,并利用生产实绩数据分析了该缺陷产生的原因。结合热轧生产过程,主要通过避免带钢撞击导卫以及降低导卫结瘤的产生等措施,可有效抑制热卷异物压入产生,从而降低冷轧工序孔洞的产生。 In viewing of the distribution and morphology characteristics of the hole defect of non-oriented electrical steel in Maanshan Iron and Steel Co.,Ltd.,the causes of the defect were analyzed by micro analysis of the defect sample and the production data.Combined with the production process of hot rolling,by avoiding the impact of strip steel on the guide and reducing the nodule formation on the guide,the pressing of foreign bodies in hot coiling could be effectively suppressed,thus reducing the fo... 

【作者】 朱一知； 陈山； ...

本实用新型属于硅钢片加工技术领域，具体涉及一种利于常化的硅钢缝合结构，包括上层硅钢片、下层硅钢片和连接带，下层硅钢片的一端位于上层硅钢片的下方并与上层硅钢片叠合，上层硅钢片和下层硅钢片的叠合处开有多个排成直线的桥型孔，连接带依次穿过各个桥型孔并同时卡合在上层硅钢片和下层硅钢片上。本方案中，在上层硅钢片和下层硅钢片的叠合处开设桥型孔，利用连接带穿过上层硅钢片和下层硅钢片叠合处的桥型孔，相当于利用连接带将上层硅钢片和下层硅钢片缝合在一起，这样设置能够较好将上层硅钢片和下层硅钢片连接成一体。

本实用新型涉及一种硅钢片抓取平台，其包括抓取框架，包括抓取框架，所述抓取框架上设有多个支架，对应于非切割区域的支架上设有大真空吸盘，对应于切割区域的支架上设有小真空吸盘。本实用新型结构简单，通过多个真空吸盘来进行硅钢片的抓取也不会损坏加工后的硅钢片，还提高了硅钢片的搬运效率。此外，通过气动系统实现对吸盘的自动吸气，提高了对吸盘操作的便利性。

观察了取向硅钢极薄带经冷轧至不同厚度,并经过不同工艺热处理后的显微组织及亚结构。结果表明:冷轧压下量越大,显微组织中位错密度越高,冷变形组织越多,等轴晶粒越少;增加冷轧压下量可以使试样的再结晶温度降低,当钢带厚度为0.08 mm时,在650℃退火时就能发生明显的再结晶。 Microstructure and substructure of the grain oriented ultra-thin silicon steel sheets is analyzed,which are rolled down to different thickness and treated with different heat treatment process.The result shows that there are higher dislocation density,more cold deformation structure and less equiaxed crystal grain in microstructure of the steel sheets with more cold rolled reduction.Increase of cold rolled reduction will decrease recrystallization temperature,and when thickness of the steel shee...