电动汽车电机在高速旋转时承受离心力和电磁力的作用,在进行电机转子设计时,既要考虑电磁性能,还要考虑机械性能。对电机转子受力情况进行了综述,分析了转子用电工钢疲劳性能参数的重要性,详细阐述了试样抛光、表面处理、试样的对中和安装对测试结果的影响。 The motor of electric vehicle bears big force for high speed rotors,mainly including centrifugal and electromagnetic forces.The magnetic and mechanical aspects of the electrical steel are crucial to machine design.In this paper,the forces applied on the motor were summarized and importance of fatigue properties was analyzed.The influence of specimen polish,surface treatment,alignment and installation on fatigue testing result were represented in detail. 

涂层技术在高磁感取向硅钢生产中起着重要的作用.根据生产实践,介绍了高磁感取向硅钢生产中涂层的种类和作用、涂料的成分和对产品性能的影响、涂层工艺质量控制要点和检验方法等,并提出了通过优化涂层工艺改善高磁感取向硅钢性能和外观质量的方法. Surface coating technique plays an important role in producing high magnetic inductivity grain-oriented silicon steel.Based on production practice,this paper describes the types and function of the coating,the composition of the coating and its effect on the product performance,the quality control and inspection method for the coatings,as well as proposes ways to improve the magnetic property and surface quality of the steel by optimizing the coating process. 

对西昌钢钒炼钢厂200 t BOF(顶底复吹)-RH-CC工艺生产50PRW800无取向硅钢RH精炼过程中主要成份进行了分析。找出了目前工艺中影响钢液质量的主要因素是钢水脱氧处理不彻底,造成加入的部分硅元素烧损。操作工艺改为铝的脱氧即合金化操作一步完成,保证了钢水中氧处于一个较低的范围,从而减少对硅元素的烧损,提高合金收得率。 The factors of BOF-RH-CC process affecting the compositions of liquid steel were systematically investigated and studied of Xichang Steel and Vanadium Company. The main factors affecting the steel cleanliness were picked out. All results showed that the loss of silicon elements resulting from the deoxidization of liquid steel was not completely. It was suggested that the addition of aluminum for deoxidizing and alloying of molten steel was executed as one step in order to lower the oxygen potent... 

本发明提供了一种无取向硅钢RH顶枪喷粉脱硫工艺，RH脱碳结束测温定氧，立即加入铝粒脱氧合金化、之后立即依次连续加入合金进行成分调整，合金加完后立即开始顶枪喷粉；加入铝粒的量＝铝粒理论加入量+0.2‑0.4kg/t钢；喷粉时，控制喷粉速度与钢液循环流量相匹配；本发明从真空条件下脱硫热力学和动力学角度出发对具有顶枪喷粉功能的RH脱硫工艺进行改进，提高脱硫率。

本发明公开了一种高磁感取向硅钢，其含有Fe及不可避免的杂质元素，其还含有质量百分含量如下的下述各化学元素：C：0.02～0.08％，Si：2.0～4.5％，Mn：0.02～0.30％，S≤0.0050％，Als：0.01～0.04％，N：0.002～0.01％，Nb：0.0050～0.0600％；以及P：0.01～0.1％，Sn：0.01～0.30％，Cu：0.01～0.50％的至少其中一种。此外，本发明还公开了上述高磁感取向硅钢的制造方法，其包括步骤：(1)制得板坯；(2)板坯加热；(3)热轧，其包括：粗轧、在热卷箱内卷取保温，以及精轧；其中粗轧结束温度高于970℃；卷取温度为800～1050℃，卷取时间为30～200s；精轧开始温度低于1050℃；(4)冷轧；(5)脱碳退火；(6)渗氮；(7)涂覆退火隔离剂；(8)高温退火；(9)涂覆绝缘涂层和激光刻痕。

本发明涉及硅钢卷取领域，具体涉及提高硅钢收卷速度的卷取系统，包括机架、第一卷取辊、第二卷取辊、第三卷取辊和切捆机构，第一卷取辊、第二卷取辊和第三卷取辊依次转动设置于机架上；切捆机构包括切割刀、挤压板和成卷的胶带，切割刀竖直滑动设置于第一卷取辊和第二卷取辊的上方，切割刀上固定有两个支撑条，两个支撑条之间设置有支撑辊，成卷的胶带套设于支撑辊上，切割刀上还设有供胶带穿过的通槽；挤压板内设有装有墨水的盛墨腔，挤压板一侧的两端固定有排墨管，排墨管与盛墨腔连通，且排墨管与切割刀的侧壁转动连接。采用本技术方案时，有利于提高硅钢卷取效率。

介绍在取向硅钢生产中抑制剂的作用以及多元抑制剂的机理和应用情况,分析多元抑制剂方案中各种元素对高磁感取向硅钢性能的影响,并根据生产实践提出了进一步研究的方向. The role of an inhibitor in the production of grain oriented silicon steel,and the mechanism of multiplex inhibitor in the production are described in the present article.In addition,the influence of various elements in the multiplex inhibitor on the performance of grain oriented silicon steel with high magnetic induction is elucidated.Further work needed in this research is also indicated. 

本实用新型提供了一种新型的去角硅钢片，包括硅钢片本体，所述硅钢片本体包括叠放区和防护区，所述硅钢片本体设有防护结构，所述防护结构包括叠放区上设有的多个均匀分布的降噪凹槽，所述防护区上下两端分别设有多个防护条，且两两防护条之间设为连接槽，每个所述防护条皆包括与硅钢片本体连接的防护层和减震层，所述防护区底部两侧分别设有减震柱，所述防护区中间设有贯穿孔，所述贯穿孔内设有绝缘螺栓。本实用新型能降低噪音和减少震动影响，从而避免使得变压器寿命及功能性降低。

本实用新型公开了硅钢专用消泡剂生产温度控制装置，包括底板及设置在底板上端的温控桶，所述温控桶的内部设置有温控腔，所述温控桶的上下两端分别安装有进料口及出料口，所述温控桶的内部设置有便于温度控制的温度控制机构，所述底板上设置有用于搅拌的搅拌机构；所述温度控制机构包括安装在温控桶上的进气管及出气管，所述进气管及出气管与温控腔的内部相通设置。本实用新型的硅钢专用消泡剂生产温度控制装置，整个温控处理操作简单、实施便捷，便于对消泡剂进行温度控制，且冷却介质或者加热介质可以直接对消泡剂进行加热或是降温，降低了输送过程中的能量消耗，提高了消泡剂温度控制的效率。

本发明一种铝镇静含硅钢的脱氧方法，包括转炉冶炼、LF炉精炼工序，转炉工序：转炉出钢过程采用含硅脱氧剂进行脱氧，出钢完毕后，向钢液表面加入顶渣改质剂，数量为400±25kg/炉，所述顶渣改质剂的成分及其质量百分含量为：Al2O3：9％±1％，CaO：27.5％±1.5％，SiO2：3％±1％，Al：50％±2％，CaF2：7％±1％。精炼工序：采用铝脱氧剂进行脱氧、造渣。本发明通过两步脱氧工艺，大幅降低脱氧成本同时提高钢水质量，由于硅脱氧相对于铝脱氧在钢水中形成的夹杂物更容易上浮，所以也提高了钢水纯净度，提高钢水质量。

通过测试取向硅钢不同工艺条件下的碳含量,探讨了CGO取向硅钢碳含量控制的最优处理条件,研究了脱碳温度和脱碳时间对相同初始碳含量取向硅钢的脱碳效果的影响。结果表明,在气氛为(15%~20%)H2+(75%~80%)N2,炉压差为10~20 Pa的条件下,CGO取向硅钢合适的脱碳温度为1 073 K~1 123 K,脱碳时间为10~20 min。在该处理条件下,能取得较好的脱碳效果。 By means of testing carbon content of oriented silicon steel below the distinct technical conditions,inquires the excellent handle terms of carbon content controlling for CGO oriented silicon steel,studies effects of decarburization annealing temperature and decarburization annealing time to the oriented silicon steel decarburization efficiency in same initial carbon content.The results show that,under the condition of atmosphere(15% ~ 20%) H2+(75% ~ 80%)N2 and furnace pressure difference 10 ~ 2... 

本发明提供在金属带钢表面以所希望的槽宽度形成线状槽进而磁特性极其优异的方向性电磁钢板。在金属带钢的至少单面形成抗蚀剂被膜，接着，对上述抗蚀剂被膜一边在横穿上述金属带钢的轧制方向的方向进行扫描一边照射激光，除去经上述激光照射的部分的上述抗蚀剂被膜，接着，对上述金属带钢的除去了上述抗蚀剂被膜的部分实施蚀刻处理而形成线状槽，上述抗蚀剂被膜以固体成分换算计含有20质量％以上的无机化合物，在上述金属带钢表面，上述激光具有长轴直径与短轴直径之比为5.0以上的椭圆状的射束形状，并且扫描正交方向的射束直径为10μm～100μm。