在实验室模拟CSP流程制备了不同含量稀土铈(质量分数0~0.018%)的1.2%Si无取向电工钢,并对其进行1 000℃×5min的再结晶退火处理,研究了铈质量分数对无取向电工钢夹杂物、显微组织、再结晶织构和磁性能的影响。结果表明:随着铈质量分数的增加,微细夹杂物数量、再结晶晶粒尺寸、{100}和{110}织构组分、磁感应强度先增后减,{111}织构组分、铁损先减后增;铈的质量分数为0.005 1%时,钢中的夹杂物数量最少,再结晶晶粒尺寸最大,有利织构最多,磁性能最优,铁损P15/50为3.253W·kg-1,磁感应强度B50为1.751T。 Non-oriented electrical steels containing different contents rare earth Ce element(0-0.018wt%) were prepared in the laboratory by simulated CSP(compact strip production)process,and then recrystallization annealing at 1 000 ℃ for 5 min were performed,the effects of Ce content on inclusion,microstructure, recrystallization texture and magnetic properties of non-oriented electrical steels were studied.The results show that with the increase of Ce content,the amounts of fine inclusion,the size of re... 

研究表明,硅钢中的夹杂物对成品带钢的磁性能有显著影响。为研究冶炼过程硅钢中的夹杂物遗传变化,进而提出更有效的控制措施加以去除,本文结合典型的无取向硅钢生产炉次,采用非水溶液电解提取+扫描电镜观察方法分析冶炼过程中上述炉次典型试样的夹杂物。结果表明:转炉冶炼结束、RH精炼开始时,钢的氧化物夹杂总量最大,约为0.23%;RH精炼过程中,氧化物夹杂总量不断降低,并在脱碳结束时达到最低,约为0.02%;连铸过程中,氧化物夹杂总量仍有不断降低趋势,但夹杂物的平均尺寸变化不大。本试验条件下,中间包试样的夹杂物数量约为1.59×104个/mm3。 As we all know, the non-metallic inclusion effects magnetic properties of silicon steel sheets obviously. The article aims to study the heredity of non-metallic inclusion in non-oriented silicon steels during the steel making process, and then provides a more effective controlling measure to remove the inclusions. Based on the typical non-oriented silicon steel charges, the non-aqueous solution extraction and SEM observation were adopted to analyze the non-metallic inclusions. Results show that,... 

本发明公开了一种宽频率低铁损无取向电工钢及其制备方法，属于无取向电工钢生产制造技术领域。它从电工钢表面向内依次包括0.005mm～0.1mm的渗透层和钢材内芯；所述渗透层是由硅原子向电工钢内渗透形成，渗透层中的硅元素含量为3wt％～8wt％；所述钢材内芯包括2.0wt％～5.5wt％的硅元素和不少于93.2wt％的铁元素。本发明能保证无取向电工钢具有低频低铁损性能同时有效降低高频条件下的铁损，具体铁损性能为：铁损P1.5/50≤2.35W/kg，铁损P1.0/400≤13.8W/kg。

本发明涉及一种冷连轧法生产无取向高硅钢的方法，RH真空脱碳处理后，铝脱氧及部分铝合金化，合金化后大罐钢水净循环大于3次或大于5分钟；熔炼合格钢水至连铸开浇前静置时间大于二十分钟；控制过热度5～15℃；采用电磁搅拌，控制等轴晶比例45％以上；3)热轧工序板坯装炉温度大于750℃；常化使晶粒尺寸在90～110μm范围内；连续退火炉加热段温度设定950～1150℃，均热段温度设定900～1050℃，全氮气干气氛保护，控制晶粒尺寸120～170μm。生产全过程中的热履历参数控制，充分发挥设计的微合金元素功能，改变析出物的组成、大小、形态及分布。

本实用新型提供了一种无取向硅钢涂层喷涂装置，属于冶金行业涂层技术领域，包括上涂辊和下涂辊，所述上涂辊一侧设有上喷淋管，下涂辊一侧设有下喷淋管，在上涂辊和下涂辊间的水平面上方设置一个倾斜挡板，所述上喷淋管对准倾斜挡板，下喷淋管对准下涂辊，所述下涂辊下方设置一个涂液收集槽，下涂辊部分置于涂液收集槽中，涂液收集槽底板设有涂液回流口，所述涂液收集槽通过一个升降装置调节自身高度。该装置稳定性好，可靠性高，能够有效保证无取向硅钢下表面涂层质量，避免出现漏涂或者涂层条纹缺陷，提高无取向硅钢涂层质量。

本发明公开了一种适用于无取向硅钢极薄带表面涂覆的涂液，它由水溶性丙烯树脂、成膜助剂、耐盐雾助剂、流平剂、纳米氢氧化锆、消泡剂、水按质量比100:(2～8):(1～3):(1～5):(0～1):(0.1～0.5):(70～130)组成。将该涂液在无取向硅钢极薄带表面可表现出良好的涂覆性，经烘烤固化后形成的绝缘涂层表面透明光滑，附着性和绝缘性能优良，可有效提升无取向硅钢极薄带的综合性能，适合推广应用。

试验的铸态取向硅钢（/%:0.044⁰.056C,3.12³.32Si,0.08⁰.11Mn,0.002⁰.008S,0.002 9⁰.029 1Als,0.006 2⁰.010 9N）由30 kg高频真空感应炉熔炼。通过场发射扫描电子显微镜/能谱仪（FE-SEM/EDS）研究结果表明,0.002 9%Als钢中氧化物主要为SiO₂,存在片状、棒状及近似球状的独立MnS,未发现含铝的氧化物或氮化物;0.0090%Als钢中出现以Al₂O₃为主的复合氧化夹杂物,存在MnS与AlN的复合析出物。钢中Als增加,复合析出物多呈簇状发展。氧化物容易成为MnS-AlN复合析出的核心,钢中Als含量越低,夹杂物中的MnS含量越高;作为核心的氧化物夹杂的尺寸越小,形成的复合夹杂物的形状越规则,尺寸也越小。热力学计算结果表明,钢中Als含量主要影响了钢中氧化物夹杂的组成和AlN的析出温度及析出量。 Test as-cast grain-oriented silicon steel（/%:0.044 ⁰.056C,3.12 3.32Si,0.08 0.11Mn,0.002⁰.008S,0.002 9⁰.029 1 Als,0.006 2⁰.010 9N） is melted by a 30 kg high frequency vacuum induction furnace.The research results by using field emission-scanning electron microscope/energy dispersive spectrometer（FE-SEM/EDS） show that in 0.002 9%Als steel the main oxide is SiO₂,and there is independent laminable,rod-like and approximate ... 

研究了锰含量对w(Si)=1.8%Si无取向电工钢组织和性能的影响。结果表明,钢中锰含量从0.3%增加到1.2%时,由于α_γ相变的产生,铸坯低倍组织、热轧板金相组织及成品织构等均发生了不同程度的变化,对成品表面质量及磁性能产生了明显的影响。 The effects of manganese content on structure and properties of w(Si)=1.8% non-oriented electrical steels have been studied.Results show that with increasing manganese content to 1.2% from 0.3%,macrostructure of continuous casting slab,hot rolled band metallurgical structure and finished product texture vary in some extent because of the occurrence of α-γ phase transformation,the surface quality and magnetic properties of finished product are affected greatly. 

本发明公开了用于激光切割硅钢片及超薄件的高效快速定位夹紧装置，属于激光切割机技术领域。用于激光切割硅钢片及超薄件的高效快速定位夹紧装置，包括基体，所述基体内设有储渣腔，还包括：长条板，通过支块对称固定连接在所述基体的两侧；两组传送辊，转动连接在所述长条板上，本发明可以对硅钢片快速的进行锁紧固定，防止激光切割机在对硅钢片进行切割时，硅钢片发生移动，有效的提高了对硅钢片的切割精度和切割效率，同时切割产生的废料则会在自身重力的作用下掉落进储渣腔内进行收集，从而便于工作人员后续对废料进行集中处理，在对硅钢片进行传送时，可以增大硅钢片与传送辊之间的摩擦力，有效的提高了在传送硅钢片时的稳定性。

主要研究了氧化锌对以Al(H2PO4)3为基料的无铬无取向硅钢绝缘涂层各项性能的影响.用盐雾实验和动电位极化研究了不同氧化锌含量对硅钢绝缘涂层的耐蚀性和电化学行为的影响.采用SEM和体视显微镜对涂层的表面形貌和附着性能进行研究.结果表明,氧化锌含量为4.0%时,氧化锌能完全中和涂层表面的游离磷酸,涂层的耐蚀性和附着性最好;氧化锌含量过少或过多时,涂层的耐蚀性和附着性都较差. This paper studies the influence of zinc oxide on the performance of chromium-free non-oriented silicon steel insulating coating which based on aluminum dihydrogen phosphate.Salt spray experiment and potentiodynamic polarization were used to study the influence of zinc oxide content on the corrosion resistance and electrochemical behavior of the insulation coating of silicon steel.The surface morphology and adhesion of coating were tested by SEM and stereo microscope.The results show that when t... 

本发明公开了一种改善取向硅钢边部变形的热处理辅助方法，在高温退火工序前，在钢卷的下端预设位置处放置阻热环并固定；在高温退火完成后，拆除固定件并移除所述阻热环。本发明通过施加阻热环，降低了取向硅钢卷在高温退火过程中的升温速率，降低了钢卷在升温及冷却过程中的胀缩量，有效改善了边部变形情况。同时，本发明由于采用一体式隔热材料，其装配及移除难度大幅度降低，有利于推广应用。

本发明属于冶金技术领域，具体涉及一种基于纳米析出强化制备高强度无取向硅钢的方法。该无取向硅钢包括如下重量百分比的化学成分：Si2.5～4.5wt.％，Ni2.5～6.5wt.％，Al1.0～3.0wt.％，Mn0.1～1.0wt.％，Cu0～1.0wt.％，(C+N+O+S)≤100ppm，其余为Fe；该无取向硅钢的制造方法包括：真空冶炼、浇铸锻造及热轧加工(或者薄带连铸)、常化热处理、酸洗与冷轧加工、再结晶退火、时效热处理。本发明制备的新能源汽车驱动电机转子用高强无取向硅钢厚度为0.20～0.50mm，磁感应强度B50为1.60～1.70T，P10/400为10～31W/kg，屈服强度Rp0.2为700～1000MPa，抗拉强度Rm为740～1150MPa，延伸率A为8～20％，可以满足用户对新能源汽车驱动电机用无取向硅钢性能要求。