硅钢资料

电动汽车电机在高速旋转时承受离心力和电磁力的作用,在进行电机转子设计时,既要考虑电磁性能,还要考虑机械性能。对电机转子受力情况进行了综述,分析了转子用电工钢疲劳性能参数的重要性,详细阐述了试样抛光、表面处理、试样的对中和安装对测试结果的影响。 The motor of electric vehicle bears big force for high speed rotors,mainly including centrifugal and electromagnetic forces.The magnetic and mechanical aspects of the electrical steel are crucial to machine design.In this paper,the forces applied on the motor were summarized and importance of fatigue properties was analyzed.The influence of specimen polish,surface treatment,alignment and installation on fatigue testing result were represented in detail. 

涂层技术在高磁感取向硅钢生产中起着重要的作用.根据生产实践,介绍了高磁感取向硅钢生产中涂层的种类和作用、涂料的成分和对产品性能的影响、涂层工艺质量控制要点和检验方法等,并提出了通过优化涂层工艺改善高磁感取向硅钢性能和外观质量的方法. Surface coating technique plays an important role in producing high magnetic inductivity grain-oriented silicon steel.Based on production practice,this paper describes the types and function of the coating,the composition of the coating and its effect on the product performance,the quality control and inspection method for the coatings,as well as proposes ways to improve the magnetic property and surface quality of the steel by optimizing the coating process. 

本实用新型公开了一种冲制电机硅钢片用高速冲床的润滑油温控调节装置，包括换热机体、呈上下布置在换热机体内的冷冻水出水汇总管与冷冻水进水分配管以及冷冻水热交换换热管，冷冻水进水分配管、冷冻水热交换换热管和冷冻水出水汇总管依次连接，冷冻水进口外接冷冻水流量调节阀，冷冻水出口流出的冷冻水回流至冷却水池；换热机体顶部的一侧、另一侧分别开有进油口、出油口，进油口设油温检测盲管，油温检测盲管内设感温探头，感温探头与冷冻水流量调节阀信号连接。采用冷冻水换热冷却高温润滑油，带走油液热量，通过对冷冻水的流量控制调节，冷却后的油液温度恒定，以满足冲床润滑、冷却需要，以及减少冲床的换油周期。

本发明涉及一种电力变压器取向硅钢片自动化加工系统，包括支撑台、支撑板、传动机构、堆叠机构和调整机构，所述的支撑台上端左右两侧对称设置有支撑板，支撑板相对面设置有传动机构，支撑台上端中部设置有堆叠机构，支撑台上端面上且位于堆叠机构左右两侧对称设置有调整机构；本发明能解决以下问题：本发明通过传动机构对硅钢片前后移动，通过推动支链对硅钢片移位、放置、拿取，增加对硅钢片进行自动化堆叠效果；通过调整机构对硅钢片X方向面和Y方向面进行感应式自动调整；通过堆叠机构对硅钢片二次调整，避免硅钢片发生移动，从而使硅钢片堆叠的更加整齐，并且节约制造成本。

本发明涉及一种提高低温高磁感取向硅钢附着性的方法，该方法在现有低温高磁感取向硅钢连续式脱碳退火炉中，通过在脱碳退火前区通入氮气、氢气干式混合气，在脱碳退火后区通入氮气、氢气湿式混合气进行脱碳，在渗氮区通入氮气、氢气湿式混合气及氨气进行渗氮，解决了低温高磁感取向硅钢附着性不好的难题。本发明方法提高了钢中总氧量、增加了氧化层厚度、改善了氧化层结构，经高温退火后生成了致密的硅酸镁底层，附着性大幅提高，测试结果均在C级以上，大部分样品在B级以上。

本发明公开了一种基于机器视觉的高牌号冷轧硅钢孔洞检测系统。该系统包括：线扫光源、线阵相机、速度检测模块和工控机；线扫光源安装在钢板生产线中钢板的下方，且线扫光源的光线能够对准钢板和线阵相机；线阵相机安装在钢板的上方，且与工控机连接，用于连续扫描钢板以获取连续的钢板图像；速度检测模块与线阵相机连接，用于检测钢板的移动速度，线阵相机能够根据钢板的移动速度调整行频；工控机用于根据钢板图像检测钢板是否存在孔洞。本发明的基于机器视觉的高牌号冷轧硅钢孔洞检测系统通过利用线阵相机和工控机能够实现冷轧钢板的孔洞的自动检测，检测效率高，识别精度高，能够降低漏检率和误检率，操作方便，安全可靠。

该电磁钢板用涂布组合物是含有环氧树脂、高温固化型交联剂以及无机微粒的电磁钢板用涂布组合物，相对于所述环氧树脂的100质量份，所述高温固化型交联剂为5～30质量份，所述无机微粒是从金属氢氧化物、在25℃下与水反应而成为金属氢氧化物的金属氧化物、以及具有羟基的硅酸盐矿物中选择的一种以上，所述无机微粒的体积平均粒径为0.05～2.0μm，所述环氧树脂的含量相对于所述电磁钢板用涂布组合物的总质量为45质量％以上，所述无机微粒的含量相对于所述环氧树脂100质量份为1～100质量份。

以CaO-CaF2复合渣系为脱硫剂,在RH精炼过程采用真空投入法进行高牌号无取向电工钢深脱硫工业试验,采用KTH模型计算分析了RH炉渣成分对硫容量CS的影响。研究结果表明,炉渣成分控制在w((CaO))/w((SiO2))为5~7,w((CaO))/w((Al2O3))为1.5~1.8,w((Al2O3))为25%~30%,w((FeO+MnO))<5%,脱硫剂加入量为6~8kg/t时,钢中硫质量分数从平均0.003 1%降低到0.001 8%,最高脱硫率达到47.1%,平均脱硫率为41.7%。 The industrial trials on deep desulphurization of high grade non-oriented electrical steel were finished through using CaO-CaF2complex based fluxes in RH process.Using the KTH model,the effect of refining slag composition on the sulfide capacities was analyzed.The results show that the chemical composition of refining slag(mass fraction,%)is w((CaO/SiO2))between 5to 7,w((CaO))/w((Al2O3))beween 1.5to 1.8,w((Al2O3)) between 25%to 30%,w((FeO+MnO))less than 5%,and the desulphurizer addition level of... 

本发明涉及无取向硅钢技术领域，尤其涉及一种改善高牌号无取向硅钢冷轧断带的控制方法。按重量百分比计：[Si+Al]≥4.0％；Mn、S含量满足：S≤0.0015，[Mn]/[S]:200～400；1)热轧过程中使用保温罩，热轧轧制时投入边部加热，头尾100米内卷曲温度提高15～30℃；2)常化机组圆盘剪进行边部剪边前增加加热装置，剪切后增加毛刺打磨装置，采用煤气明火加热，保证钢板温度在韧脆转变温度以上；3)圆盘剪间隙满足关系式：ds＝(0.15～0.45)d0ds:圆盘剪间隙，μm；d0:常化板板厚，mm；4)常化采用快速加热，控制钢带的预热段升温速度320～380℃/min，机组速度20～30m/min；5)常化工艺后，控制边部小于20μm的晶粒占比在5％以内。有效的减少了冷轧断带的发生，提高成材率1.30％以上，降低了生产成本。

本发明公开了一种宽频率低铁损无取向电工钢及其制备方法，属于无取向电工钢生产制造技术领域。它从电工钢表面向内依次包括0.005mm～0.1mm的渗透层和钢材内芯；所述渗透层是由硅原子向电工钢内渗透形成，渗透层中的硅元素含量为3wt％～8wt％；所述钢材内芯包括2.0wt％～5.5wt％的硅元素和不少于93.2wt％的铁元素。本发明能保证无取向电工钢具有低频低铁损性能同时有效降低高频条件下的铁损，具体铁损性能为：铁损P1.5/50≤2.35W/kg，铁损P1.0/400≤13.8W/kg。

本发明涉及一种冷连轧法生产无取向高硅钢的方法，RH真空脱碳处理后，铝脱氧及部分铝合金化，合金化后大罐钢水净循环大于3次或大于5分钟；熔炼合格钢水至连铸开浇前静置时间大于二十分钟；控制过热度5～15℃；采用电磁搅拌，控制等轴晶比例45％以上；3)热轧工序板坯装炉温度大于750℃；常化使晶粒尺寸在90～110μm范围内；连续退火炉加热段温度设定950～1150℃，均热段温度设定900～1050℃，全氮气干气氛保护，控制晶粒尺寸120～170μm。生产全过程中的热履历参数控制，充分发挥设计的微合金元素功能，改变析出物的组成、大小、形态及分布。

研究了硅钢铸坯再加热过程中夹杂物的析出行为。采用非水溶液电解提取+扫描电镜观察方法,观察了试样的显微组织,统计了夹杂物的尺寸、种类、数量、分布。结果表明,均热温度为1 523 K时,水淬试样的夹杂物尺寸绝大部分小于0.5μm,0.5～5.0μm的夹杂物数量很少,没有发现5.0μm以上的夹杂物。此外,均热时间为10、30、60、90、120、240 min时,对应试样中0.05～0.2μm的夹杂物数量分别为4.04×104、4.73×104、3.70×104、3.33×104、3.10×104、1.56×104个/mm3。绝大部分夹杂物以MnS、AlN、CuxS类为主,并以三类夹杂物中的两类复合或三类复合居多。三类复合夹杂物总量占每组试样夹杂物总量的90%或以上。随均热时间延长,典型的夹杂物组成会发生如下变化:MnS+AlN+CuxS MnS+AlN AlN。与此同时,MnS、AlN、CuxS三者复合比例从45.2%(均热10 min)降为9.7%(均热240 min)。 The methods of electrolysis extraction from nonaqueous solution and scanning electron microscope were adopted to study the precipitation behavior of non-metallic inclusions in Si steel slabs during reheating processes.The morphologies,chemical compositions,quantity and size distribution of non-metallic inclusions in these steel samples were analyzed.Results show that,when the soaking temperature is 1 523 K,almost all of the non-metallic inclusions are smaller than 0.5 μm,few are in the range of ...