硅钢资料

研究二次冷轧压下率对于硅的质量分数为3.0%的无取向硅钢组织结构和磁性能的影响。结果表明:当第二次冷轧压下率从0变化至16.7%时,铁损逐渐增加,磁感逐渐降低。当第二次冷轧压下率大于16.7%时,随压下率的增加,铁损逐渐减小,磁感逐渐增加。当第二次冷轧压下率大于38%时,二次冷轧法所能获得的磁性能明显优于一次冷轧法。 Effect of double cold reduction on magnetic,microstructure and texture of 3.0% Si non-oriented silicon steel sheets was investigated.The results show that the iron loss increases and magnetic induction reduces as the percentage redcution in secondary cold rolling changes from 0 to 16.7%.The core loss can be reduced remarkably,and magnetic induction can get a little benefit if the percentage redcution in double cold reduction is higher 16.7%.In case of higher than 38% of the percentage redcution ... 

硅钢是钢铁产品中的\"工艺品\",是高附加值产品,通过对我国主要硅钢生产厂家的工艺设备,市场情况分析,简要介绍了我国硅钢生产消费现状,未来生产能力预测及硅钢未来发展趋势。 Silicon steel is the \"crafts\" of steel products,also is high value-added product.By analyzing process equipment and market condition of major silicon steel-making plant of China,it briefly introduces our current production consumption status,future production capacity prediction and future development trend of silicon steel. 

通过对湿H2气氛下,相同退火温度、不同退火时间的CGO硅钢初次再结晶样品进行金相组织观察,并进行了EBSD微观织构分析,研究了CGO硅钢初次再结晶过程中的组织及再结晶织构演变行为。结果表明,在湿H2气氛下,820℃保温,CGO硅钢初次再结晶过程约在120 s时完成。随着退火时间的延长,γ面上{111}<112>织构含量逐渐减少,{111}<110>织构先减少后增多,随着再结晶的完成,部分{111}<112>取向晶粒向高斯{110}<001>取向转化的同时,也向{111}<110>取向转化,高斯{110}<001>织构含量逐渐增多。高斯取向晶粒较多是由{111}<112>取向晶粒转化而来,同时也证明了CGO硅钢高斯取向晶粒的二次再结晶异常长大生长机制为择优形核。 Microstructure development and texture evolution of conventional grain oriented silicon steel,which were annealed at same annealing temperature and different annealing time under wet H2 atmosphere,were investigated through metallographic observation and electron backscattered diffraction analyzing.The results show that the primary recrystallization finishes in 120 s at 820 ℃ under wet H2 atmosphere.With the extending of annealing time,{111}<112> texture decreases,{111}<110> texture d... 

一种增大压下率的电工钢冷轧装置及冷轧方法，属于电工钢冷轧技术领域，该电工钢冷轧装置，包括单机架可逆轧机，单机架可逆轧机的两侧均设置有电磁感应加热装置和氮气风冷装置，氮气风冷装置靠近单机架可逆轧机的轧制进口或入口设置，本发明的有益效果是，本发明通过在单机架可逆轧机两侧增设电磁感应加热装置和氮气风冷装置，对每道次轧制过程中可在线调节电磁感应加热温度，实现了边去应力退火边轧制，保证了正常的轧制工作，达到了高效轧制更薄规格电工钢产品的目的和消化生产CSP热轧超厚过渡坯的目的。

本实用新型涉及硅钢片铁芯装配组件技术领域，公开了一种硅钢片铁芯的装配工装，包括装配组件，所述装配组件的内部上方安装有液压伸缩杆，所述液压伸缩杆的底端固定连接有压板，所述压板的表面开设有孔槽，所述装配组件的底端安装有铁芯，且铁芯的顶端贯穿孔槽的内部，所述铁芯的外部套设有硅钢片，所述硅钢片的外壁对称设有限位辊，所述装配组件的内壁对称安装有电动滑台，且电动滑台的内部设有滑块，本实用新型通过在液压伸缩杆的顶端安装有压板，并且压板的表面开设有与铁芯相匹配的孔槽，液压伸缩杆带动压板升降，对硅钢片进行压实，减少硅钢片之间的缝隙，使得硅钢片之间连接的更加紧凑，减少了工作人员的劳动量。

对CSP流程生产的无取向电工钢M50W800不同尺寸样品的磁性能进行了测试和分析,结果表明:采用不同单片检测的磁性能结果与标准的Epstein方圈样品检测对比,存在明显的偏差;且同一尺寸的单片纵横向样品之间相比较,对应的磁性能差异性也较大。几种不同尺寸的单片样品,以320mm×30mm尺寸的纵横向平均值最接近标准Epstein方圈样的性能值,其铁损偏差最小。 The magnetic properties of M50W800 non-oriented electrical steel produced by CSP process were tested and analyzed with samples of different sizes,showing that significant deviation existed compared to that of Epstein square circle sample.In particular,obvious difference in magnetic properties also existed between longitudinal and transverse samples of the same size.For test samples of different sizes,the average magnetic properties of 320mm×30mm samples are the closest to that of Epstein square ... 

本发明属于冶金技术领域，具体涉及一种基于纳米析出强化制备高强度无取向硅钢的方法。该无取向硅钢包括如下重量百分比的化学成分：Si2.5～4.5wt.％，Ni2.5～6.5wt.％，Al1.0～3.0wt.％，Mn0.1～1.0wt.％，Cu0～1.0wt.％，(C+N+O+S)≤100ppm，其余为Fe；该无取向硅钢的制造方法包括：真空冶炼、浇铸锻造及热轧加工(或者薄带连铸)、常化热处理、酸洗与冷轧加工、再结晶退火、时效热处理。本发明制备的新能源汽车驱动电机转子用高强无取向硅钢厚度为0.20～0.50mm，磁感应强度B50为1.60～1.70T，P10/400为10～31W/kg，屈服强度Rp0.2为700～1000MPa，抗拉强度Rm为740～1150MPa，延伸率A为8～20％，可以满足用户对新能源汽车驱动电机用无取向硅钢性能要求。

取向硅钢热轧板中组织、织构梯度对发展完善的二次再结晶十分关键,通过对2种不同热轧工艺生产取向硅钢的组织、织构进行研究,结果表明:采用后道次大压下热轧工艺时热轧板表层再结区晶粒平均尺寸增加,再结晶区厚度增加,高温退火后二次晶粒尺寸减小;采用后道次大压下热轧工艺热轧时,热轧板中平均等效应变高,热轧板厚度心部{100}〈011〉和{100}〈001〉位向取向强度降低,({111}～{113})〈110〉位向取向强度提高,高温退火后{110}〈001〉位向偏离角降低,磁性能提高。 The texture and microstructure gradient in hot rolled grain oriented silicon steel strip was one of the essential factors to achieve a perfect secondary recrystallization.The texture and microstructure of grain oriented silicon steel strip as-rolled with two different hot rolling parameters was investigated.The results show that with big reduction at the end rolling process,the intensity of {100}〈011〉 and {100}〈001〉 orientation reduces with({111}-{113})〈110〉 orientation intensity enhanced in hot... 

本实用新型公开了一种硅钢板带加工用表面成型设备，包括底座，所述底座的上端固定连接有底部支撑架，所述底部支撑架的上端固定连接有机体，所述机体的上端固定连接有密封盖。本实用新型在打磨过程中，水泵可以将过滤箱内的冷却液通过进液机构上的进液管泵入到进液机构内，再经过进液孔进入到第二转轴内，再进入到打磨辊筒内，最后经过喷头喷到钢带表面，对钢带表面进行冷却，且可以将打磨下来的粉末带走，防止粉末飘散；冷却在喷出后，经过集液斗的收集，进入到过滤箱内，在过滤箱内设置过滤网可以对冷却液进行过滤，从而可以对冷却液进行重复使用。

在实验室模拟CSP工艺条件下制备了取向硅钢,研究了二次冷轧中间退火工艺对组织和织构的影响。结果表明,中间退火温度对取向硅钢脱碳,高温退火组织及织构均产生明显影响。经940℃中间退火后,取向硅钢脱碳再结晶晶粒较850℃中间退火的多,且再经高温退火处理后,晶粒粗化,最大晶粒尺寸达4.8 mm;高斯织构组分密度达27.00,较850℃中间退火试样高。 Grain-oriented silicon steel was prepared by simulated CSP technology in laboratory. Effects of secondary cold-rolled intermediate annealing on microstructure and texture were studied. The results show that intermediate annealing has obvious effects on the microstructure and texture of the steels after decarburization annealing and high temperature annealing. After intermediate annealing at 940 ℃,recrystallized grain of decarburization annealed steel is more than that of intermediate annealed at... 

本实用新型公开了一种硅钢片二次搭接夹具，包括底座、位于底座顶部的调节板以及位于调节板顶部一端的固定杆，所述底座包括设置在底座内部顶端中间位置处的活动槽。本实用新型通过连接块将第一夹钳与第二液压缸的输出端相连接，通过第一夹钳和第二夹钳对硅钢片进行固定，将焊条焊接在一组硅钢片上，伺服电机带动调节杆发生转动，调节杆外侧的外螺纹和活动块内部的螺纹孔相互配合，可使活动块在活动槽内部发生活动，通过活动块带动调节板发生前后移动，从而使对硅钢片进行前后一端，通过滑轨使调节板的移动更加稳定，使两组硅钢片相对齐，通过固定块使第一液压缸带动调节架左右移动，使焊条与两组硅钢片紧密接触，实现二次搭接。

本实用新型公开了一种冷轧取向硅钢带整平装置，包括两个上下对称分布的保护罩，所述保护罩的内部均转动连接有展平辊，且展平辊的一端均延伸至保护罩的外部，所述保护罩的外壁设置有传动罩，且传动罩的外壁设置有动力箱，所述动力箱与展平辊传动连接，上下两个所述展平辊之间设置有其,特征在于，所述保护罩的两侧外壁均固定连接有支撑架，且支撑架的一侧外壁均设置有延展机构，两个所述延展机构之间设置有连接架，且连接架的一侧外壁设置有吸水布，所述吸水布的内部设置有胶板。本实用新型吸水布与硅钢带本体的外壁滑动接触，以此将展平时涂抹在硅钢带本体表面的水溶性润滑剂刮抹掉，减少硅钢带本体表面上的水分。