硅钢资料

试验研究了球刻痕法对高磁感取向硅钢的铁损、矫顽力、相对磁导率、巴克豪森噪声等磁学性能的影响.研究结果表明:经过球刻痕处理后,高磁感取向硅钢的铁损明显降低,矫顽力下降,8 mm球刻痕过后铁损值与矫顽力分别下降16.2%和14.7%,且铁损和矫顽力均随刻痕间距降低而减少.刻痕后的高磁感取向硅钢磁导率在高磁感应强度下明显上升,刻痕后巴克豪森噪声值明显降低,经过对比分析确定8 mm为球刻痕的最佳刻痕间距.从磁畴观察、细化磁畴的原理等方面解释了细化磁畴对高磁感取向硅钢性能的影响原因. The effects of the ball scribing on magnetic properties of high permeability grain-oriented silicon steels,including the iron loss,coercive force,relative permeability,and Barkhausen noise were investigated. The results showed that the iron loss and coercive force of the high permeability grain-oriented silicon steels apparently decreased 16. 2% and 14. 7% respectively after 8 mm ball scribing and they both decreased with the decrease of the scribing spacing at the same magnetic flux density. At... 

介绍了国内、外电工钢极薄带的生产现状及市场应用的情况,以及典型生产企业的生产规模、产品性能和应用领域,指出扩大高牌号无取向电工钢生产、提高产品质量是目前电工钢发展的迫切要求。 The production situation and market application of ultra thin electrical steel strip at home and abroad were described.The production capability,product property and application area of typical corporation were introduced.The results indicate that the urgency needed of electrical steel development is expanding high-grade non-oriented electrical steel production and improving products quality at present. 

硅钢是钢铁产品中的\"工艺品\",是高附加值产品,通过对我国主要硅钢生产厂家的工艺设备,市场情况分析,简要介绍了我国硅钢生产消费现状,未来生产能力预测及硅钢未来发展趋势。 Silicon steel is the \"crafts\" of steel products,also is high value-added product.By analyzing process equipment and market condition of major silicon steel-making plant of China,it briefly introduces our current production consumption status,future production capacity prediction and future development trend of silicon steel. 

本发明涉及变压器的技术领域，特别是涉及一种应用电工钢的变压器，其通过设置扇叶与冷凝盘管，通过冷却液与风冷共同对电工钢铁芯进行降温，避免电工钢铁芯工作过热导致电工钢铁芯损坏，提高使用稳定性；包括变压器箱体、两组固定支撑腿、电工钢铁芯、固定卡块、风机支架、风机、扇叶转轴、扇叶、冷却箱体、循环泵、冷却管、冷凝盘管、冷风机支架和冷风机，所述变压器箱体内部设置有空腔，所述变压器箱体右端连通设置有散热口，两组所述固定支撑腿对称固定安装在变压器箱体内部，所述固定支撑腿内端设置有紧固卡槽，所述电工钢铁芯左右两端对称固定安装有两组固定卡块，所述固定卡块固定卡装在固定支撑腿紧固卡槽中。

通过对湿H2气氛下,相同退火温度、不同退火时间的CGO硅钢初次再结晶样品进行金相组织观察,并进行了EBSD微观织构分析,研究了CGO硅钢初次再结晶过程中的组织及再结晶织构演变行为。结果表明,在湿H2气氛下,820℃保温,CGO硅钢初次再结晶过程约在120 s时完成。随着退火时间的延长,γ面上{111}<112>织构含量逐渐减少,{111}<110>织构先减少后增多,随着再结晶的完成,部分{111}<112>取向晶粒向高斯{110}<001>取向转化的同时,也向{111}<110>取向转化,高斯{110}<001>织构含量逐渐增多。高斯取向晶粒较多是由{111}<112>取向晶粒转化而来,同时也证明了CGO硅钢高斯取向晶粒的二次再结晶异常长大生长机制为择优形核。 Microstructure development and texture evolution of conventional grain oriented silicon steel,which were annealed at same annealing temperature and different annealing time under wet H2 atmosphere,were investigated through metallographic observation and electron backscattered diffraction analyzing.The results show that the primary recrystallization finishes in 120 s at 820 ℃ under wet H2 atmosphere.With the extending of annealing time,{111}<112> texture decreases,{111}<110> texture d... 

结合工业化生产的无取向硅钢,进行了RH精炼添加稀土合金实验。结果表明,1.15%(质量分数)Si钢的脱硫反应,主要发生在添加稀土合金之后的前5min。最佳的稀土合金添加量为0.6～0.9kg/t钢。钢液经过稀土处理后,加入的稀土总量越多,稀土氧硫化物夹杂物的尺寸就越大,但热轧带钢再结晶效果会逐渐变差,成品带钢晶粒尺寸先是快速长大,而后逐渐减小。最佳的钢中存留稀土含量与钢的化学成分有关,应严格控制在2.0×10-3%～6.0×10-3%(质量分数)。在此范围内,钢的铁损先是快速降低,而后缓慢升高,钢的磁感应强度则单调降低。 Based on the industrial production of non-oriented electrical steel,rare earth(RE) alloy treatment during the RH refining process was studied.The results showed that the effects of desulfurization and total concentration of RE remained in steel mainly depended on the chemical compositions of different steel grades.For 1.15wt% Si steel grade,the desulfurization reaction mainly focused on the initial 5min after RE alloy added during the RH refining process.The suitable RE alloy addition was 0.6-0.... 

本实用新型公开了一种电机硅钢片用激光切割机的高压空气冷却干燥装置，包括一端侧带密封端盖且另一端侧设出气接头的换热筒、设在密封端盖的制冷剂进液管和回气管，密封端盖设有进气接头，换热筒内设热交换器，热交换器由换热盘管、换热翅片和下截圆挡板、上截圆挡板组成，下截圆挡板的平底切边、上截圆挡板的平顶切边分别与换热筒内壁具有间隔；制冷剂进液管的一端与制冷系统的一端连接而其另一端顺次连接分液头、毛细管、换热盘管的上端入口，回气管的一端与制冷系统的另一端连接而其另一端依次连接回气汇总管、换热盘管的下端出口；换热筒的底部安装有带放水阀的自动排水部件。通过本装置换热后可获得冷却干燥的高压空气以供激光切割机使用。

本发明属于金属材料加工技术领域，具体涉及取向硅钢罩式炉高温退火低保温阶段节能工艺，包括：1)将涂镁取向硅钢卷装入密闭的罩式炉中，并向罩式炉内通入氮气将炉内氧气充分排出，使炉内氧含量浓度≤300PPm；2)通电升温并将氮气转换为10m3/h氮气与氨分解气的混合气体，升温2h将温度升温至500‑600℃后，恒温13h；3)将温度氮气与氨分解气的混合气体转换为12m3/h氨分解气，并升温2h将温度升至650℃恒温15h，使内部气体露点小于‑10℃；本发明提供退火工艺，钢卷在高温下不被水蒸汽氧化，消除钢带表面露金、发红、发黑、水印、色泽不均、导通缺陷，降低钢带铁损、提高磁感、降低生产成本。此外，本发明进一步减少退火过程中氨分解气的用量，具有极高的工业应用价值。

对高牌号无取向电工钢35W300的成品进行了第二次退火,对第二次退火后的成品性能、纵横向磁性能差异和组织变化进行了分析。结果表明,随着第二次退火温度的升高,晶粒长大,磁性能优化。铁损平均值下降0.087 5W/kg,磁感平均值升高0.008T。第二次退火温度为820℃的产品的磁性能能够满足用户使用要求。 The product of high grade non-oriented electrical steel 35W300 was annealed at the second time.Microstructure,the difference of magnetic properties in the vertical and horizontal and were studied.The results show that the grain grew up and magnetic properties optimized with the increase of annealing temperature for the second time.Iron loss average declines in 0.0875 W/kg,magnetic induction average increases 0.008 T.The magnetic properties can meet the requirements of users at the second anneali... 

本发明涉及电工钢生产技术领域，具体涉及一种冷轧取向电工钢钢带的渗氮处理工艺，旨在解决现有技术渗氮速度慢，渗氮效果不佳，能耗大，生产周期长的问题，包括以下步骤：S1、经过冶炼、连铸后，对铸坯进行热连轧、常化酸洗、冷轧及脱碳退火的工序；S2、在渗氮炉内进行两段渗氮处理：S21、第一段渗氮处理的渗氮温度为750‑950℃，渗氮时间为25‑35s,另外，渗氮介质的喷射压力为0.15‑0.25MPa,渗氮介质的流量为5‑20NL/min；S22、经稀土溶液浸泡1‑2小时后，继续第二段渗氮处理，其渗氮温度为460‑560℃，渗氮时间为10‑25s，另外，渗氮介质的喷射压力为0.15‑0.25MPa,渗氮介质的流量为1‑10NL/min；S3、涂隔离剂、高温净化退火后得到成品。

本发明涉及一种硅钢片叠压设备，包括加压机构，加压机构包括压台和压板，压台四角均设置导向柱，导向柱下端与压台固定连接，上端垂直向上延伸且穿透压板四角，压板上方设置有加力机构，加力机构包括固定板、活动板和挤压弹簧，固定板、活动板和压板平行设置，固定板设置与最上方且与导向柱上端固定连接，活动板设置于固定板和压板之间，固定板上穿透有多个螺杆，螺杆下端抵靠活动板顶面；活动板与压板之间均匀分布有多个挤压弹簧。本技术方案压台和压板构成了用于挤压叠放的硅钢片，通过转动螺杆可以将活动板向下推动，进而使活动板通过挤压弹簧将压板向下推动对叠放的硅钢片进行施压，装置结构简单、操作简单方便。

本发明涉及冶金技术领域，具体涉及一种高牌号硅钢用连铸结晶器保护渣及其制备方法和应用。本发明提供的连铸结晶器保护渣，所述保护渣包括如下质量百分比的化学成分：SiO2：40‑45％、CaO：20‑27％、MgO：1.0‑2.5％、Al2O3：1‑3％、Na2O：12‑16％、F：10‑13％、C：1‑3％，其余为不可避免的杂质；其中所述保护渣的二元碱度CaO/SiO2为0.5‑0.6，熔点为950‑1000℃，1300℃下的粘度为0.25‑0.35Pa·s。本发明提供的连铸结晶器保护渣，通过低碱度、低熔点、低粘度的保护渣可有效抑制高牌号硅钢材料在连铸时铸坯表面易出现凹陷和裂纹的现象。