硅钢资料

系统研究了无取向硅钢用磷酸盐系涂层性能的影响因素。以氢氧化铝和磷酸为原料制备磷酸二氢铝,再添加适量的添加剂酒石酸铵、二氧化硅、环氧树脂,得到的涂液涂布于硅钢表面,并控制合适的烘干温度,通过耐盐雾实验考察各因素对涂液耐腐蚀性能的影响。实验结果表明,在磷酸与氢氧化铝物质的量比为3.4∶1、酒石酸铵用量为2%、二氧化硅用量为1%、环氧树脂用量为5%、烘干温度为300℃条件下,所得涂层材料的防(耐)腐蚀效果最佳。 The factors influencing the performance of phosphate anticorrosive coating for non-oriented silicon were systematically studied.Aluminum dihydrogen phosphate was prepared with aluminum hydroxide and phosphoric acid as raw materials.Then added the right amount of additives,such as ammonium tartrate,silicon dioxide,and epoxy resin to prepare the liquid coating,which was coated on the surface of the silicon steel,and finally controlled a suitable drying temperature.The influences of various factors... 

试验研究了球刻痕法对高磁感取向硅钢的铁损、矫顽力、相对磁导率、巴克豪森噪声等磁学性能的影响.研究结果表明:经过球刻痕处理后,高磁感取向硅钢的铁损明显降低,矫顽力下降,8 mm球刻痕过后铁损值与矫顽力分别下降16.2%和14.7%,且铁损和矫顽力均随刻痕间距降低而减少.刻痕后的高磁感取向硅钢磁导率在高磁感应强度下明显上升,刻痕后巴克豪森噪声值明显降低,经过对比分析确定8 mm为球刻痕的最佳刻痕间距.从磁畴观察、细化磁畴的原理等方面解释了细化磁畴对高磁感取向硅钢性能的影响原因. The effects of the ball scribing on magnetic properties of high permeability grain-oriented silicon steels,including the iron loss,coercive force,relative permeability,and Barkhausen noise were investigated. The results showed that the iron loss and coercive force of the high permeability grain-oriented silicon steels apparently decreased 16. 2% and 14. 7% respectively after 8 mm ball scribing and they both decreased with the decrease of the scribing spacing at the same magnetic flux density. At... 

介绍了国内、外电工钢极薄带的生产现状及市场应用的情况,以及典型生产企业的生产规模、产品性能和应用领域,指出扩大高牌号无取向电工钢生产、提高产品质量是目前电工钢发展的迫切要求。 The production situation and market application of ultra thin electrical steel strip at home and abroad were described.The production capability,product property and application area of typical corporation were introduced.The results indicate that the urgency needed of electrical steel development is expanding high-grade non-oriented electrical steel production and improving products quality at present. 

本发明公开了一种适用于无取向硅钢极薄带表面涂覆的涂液，它由水溶性丙烯树脂、成膜助剂、耐盐雾助剂、流平剂、纳米氢氧化锆、消泡剂、水按质量比100:(2～8):(1～3):(1～5):(0～1):(0.1～0.5):(70～130)组成。将该涂液在无取向硅钢极薄带表面可表现出良好的涂覆性，经烘烤固化后形成的绝缘涂层表面透明光滑，附着性和绝缘性能优良，可有效提升无取向硅钢极薄带的综合性能，适合推广应用。

本发明涉及变压器的技术领域，特别是涉及一种应用电工钢的变压器，其通过设置扇叶与冷凝盘管，通过冷却液与风冷共同对电工钢铁芯进行降温，避免电工钢铁芯工作过热导致电工钢铁芯损坏，提高使用稳定性；包括变压器箱体、两组固定支撑腿、电工钢铁芯、固定卡块、风机支架、风机、扇叶转轴、扇叶、冷却箱体、循环泵、冷却管、冷凝盘管、冷风机支架和冷风机，所述变压器箱体内部设置有空腔，所述变压器箱体右端连通设置有散热口，两组所述固定支撑腿对称固定安装在变压器箱体内部，所述固定支撑腿内端设置有紧固卡槽，所述电工钢铁芯左右两端对称固定安装有两组固定卡块，所述固定卡块固定卡装在固定支撑腿紧固卡槽中。

结合工业化生产的无取向硅钢,进行了RH精炼添加稀土合金实验。结果表明,1.15%(质量分数)Si钢的脱硫反应,主要发生在添加稀土合金之后的前5min。最佳的稀土合金添加量为0.6～0.9kg/t钢。钢液经过稀土处理后,加入的稀土总量越多,稀土氧硫化物夹杂物的尺寸就越大,但热轧带钢再结晶效果会逐渐变差,成品带钢晶粒尺寸先是快速长大,而后逐渐减小。最佳的钢中存留稀土含量与钢的化学成分有关,应严格控制在2.0×10-3%～6.0×10-3%(质量分数)。在此范围内,钢的铁损先是快速降低,而后缓慢升高,钢的磁感应强度则单调降低。 Based on the industrial production of non-oriented electrical steel,rare earth(RE) alloy treatment during the RH refining process was studied.The results showed that the effects of desulfurization and total concentration of RE remained in steel mainly depended on the chemical compositions of different steel grades.For 1.15wt% Si steel grade,the desulfurization reaction mainly focused on the initial 5min after RE alloy added during the RH refining process.The suitable RE alloy addition was 0.6-0.... 

本实用新型涉及硅钢片铁芯装配组件技术领域，公开了一种硅钢片铁芯的装配工装，包括装配组件，所述装配组件的内部上方安装有液压伸缩杆，所述液压伸缩杆的底端固定连接有压板，所述压板的表面开设有孔槽，所述装配组件的底端安装有铁芯，且铁芯的顶端贯穿孔槽的内部，所述铁芯的外部套设有硅钢片，所述硅钢片的外壁对称设有限位辊，所述装配组件的内壁对称安装有电动滑台，且电动滑台的内部设有滑块，本实用新型通过在液压伸缩杆的顶端安装有压板，并且压板的表面开设有与铁芯相匹配的孔槽，液压伸缩杆带动压板升降，对硅钢片进行压实，减少硅钢片之间的缝隙，使得硅钢片之间连接的更加紧凑，减少了工作人员的劳动量。

概述了高磁感取向硅钢生产工艺的研究现状及发展趋势。介绍了国内外薄板坯连铸连轧流程生产高磁感取向硅钢的研究现状。从流程工序特点、热履历、组织与抑制剂控制方面进行对比,分析了薄板坯连铸连轧流程相对传统板坯流程生产高磁感取向硅钢的技术优势,在此基础上提出了利用该流程生产高磁感取向硅钢需要解决的主要技术难点。 The current status and development trend of production process for high magnetic induction grain-oriented silicon steel are summarized.The research status of producing high magnetic induction grain-oriented silicon steel by thin slab casting and rolling process at home and abroad is introduced.The potential technical advantages of producing high magnetic induction grain-oriented silicon steel by thin slab casting and rolling process are obtained by analyzing in terms of process characteristics,t... 

本发明涉及电工钢生产技术领域，具体涉及一种冷轧取向电工钢钢带的渗氮处理工艺，旨在解决现有技术渗氮速度慢，渗氮效果不佳，能耗大，生产周期长的问题，包括以下步骤：S1、经过冶炼、连铸后，对铸坯进行热连轧、常化酸洗、冷轧及脱碳退火的工序；S2、在渗氮炉内进行两段渗氮处理：S21、第一段渗氮处理的渗氮温度为750‑950℃，渗氮时间为25‑35s,另外，渗氮介质的喷射压力为0.15‑0.25MPa,渗氮介质的流量为5‑20NL/min；S22、经稀土溶液浸泡1‑2小时后，继续第二段渗氮处理，其渗氮温度为460‑560℃，渗氮时间为10‑25s，另外，渗氮介质的喷射压力为0.15‑0.25MPa,渗氮介质的流量为1‑10NL/min；S3、涂隔离剂、高温净化退火后得到成品。

本发明提供一种超低铝无取向硅钢夹杂物控制方法。该钢种化学成分质量百分比为C≤0.005％，Si：0.25％‑1.50％，Mn：0.15％‑0.55％，P：0.02％‑0.06％，S≤0.005％，Als≤0.005％，余量为Fe及不可避免的杂质。工艺流程为：KR→BOF→RH→连铸。转炉出钢严格控制下渣量，出钢结束加石灰、渣面脱氧剂调渣；RH脱碳结束后，先加低碳低硫硅铁、金属铝或铝钙铁合金复合脱氧，最后加入金属锰、磷铁进行合金化，然后净循环6‑10min，破空出钢运至连铸浇注。得到钢水中主要为SiO2‑Al2O3系夹杂，避免了生成低熔点SiO2‑MnO系夹杂，轧制延展变长，影响晶粒长大；同时也避免了生成高SiO2组分类酸性夹杂，导致耐材的侵蚀。可显著改善钢中非金属夹杂物类型，提高无取向硅钢的性能，并提高了钢水浇注性能。

本发明涉及一种防止低温加热取向硅钢热轧边裂的方法，包括：1)控制取向硅钢铸坯进入加热炉前的表面温度；2)控制加热段各段炉气温度；3)二加热段采用加速加热；4)控制总加热时间；5)控制出炉温度；6)控制精轧道次及侧压量；7)控制精轧道次及终轧温度；8)精轧前对钢带边部进行加热补偿。本发明通过合理制定取向硅钢的加热温度、加热时间和轧制工艺制度，避免或消除了低温加热取向硅钢热轧边裂问题。

介绍了微合金元素锡、铌、稀土对无取向硅钢性能的影响,并扼要分析了这些元素对硅钢性能的影响机理:晶界偏聚元素Sn可细化晶粒提高硅钢磁性能;微合金元素Nb细化铁素体晶粒,提高硅钢的强度、韧性和塑性及磁性能;稀土元素(RE)在硅钢中的主要作用包括净化钢液、变质夹杂物、改善铸态组织和性能及微合金化,减少晶界上出现偏析的几率。 The influence of micro-alloy elements on properties of non-oriented silicon steel and the mechanism for effect of the micro-alloy elements including Sn、Nb and RE on the properties of steel are presented and analyzed in this paper.Grain boundary segregation elements Sn in steel can grain refinement and improve the magnetic properties;Micro-alloy elements Nb can refine the ferrite grain,increase the silicon steel strength,toughness and plastic;The main role of the RE in the silicon steel including...