硅钢资料

采用EBSD技术研究了有、无拉应力作用下无取向硅钢在晶粒长大过程中织构转变及晶界变化的规律。结果表明:在晶粒生长期间,无应力作用下的硅钢中,{111}〈112〉,{111}〈110〉织构组分强化,而{100}〈001〉织构组分弱化;与无拉应力作用下的情况相比,施加5MPa的拉应力时,{111}〈112〉,{111}〈110〉织构组分强化的速率下降,{100}〈001〉织构组分变化不明显。对于在晶粒生长期间持续变化的{111}〈112〉,{111}〈110〉和{100}〈001〉织构组分而言,虽然有、无拉应力作用下硅钢的{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率均下降,而{100}〈001〉织构组分的高取向差角度晶界频率则上升,但当有拉应力作用后,{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率下降的速率变小,{100}〈001〉织构组分的高取向差角度晶界频率上升的速率稍有变小。通过对无取向硅钢在晶粒长大过程中织构转变及晶界变化规律的研究,分析了合金原子在晶界的偏聚行为。 The rules of texture and grain boundary transformation in the nonoriented silicon steel under applied stress or without applied stress during grain growth were investigated by EBSD.The results show that the {111}〈112〉 and {111}〈110〉 components in the nonoriented silicon steel without stress are strengthened during grain growth whereas {100}〈001〉 component is weakened,but the growth rate of {111}〈112〉 and {111}〈110〉 component decreases,while the area fraction of {100}〈001〉 component doesn’t chang... 

本发明涉及含Cu无取向硅钢的生产方法，转炉炼钢，真空处理过后连铸成坯；铸坯化学成分：1.0≤Si/Cu≤3.0,3.0≤Si+Cu≤5.5％，S≤0.0015％，(Mn+Cu)/S≥3000，其他为Fe,Als,P以及不可避免的杂质元素；对铸坯进行粗轧；粗轧后的中间坯采用热卷机进行强制卷取，开卷后中间坯进入保温箱，控制保温箱内冷却速度≤5℃/s；进入保温箱的中间坯温度T1满足：1000‑(Si+Cu)×103≤T1≤1100‑(Si+Cu)×103；高压除鳞，精轧，层流冷却，卷取；连续酸洗；冷轧到目标厚度，成品退火，涂层；成品卷进行时效处理。成品卷具有较低的中高频铁损，高磁感和高屈服强度。

某厂对电工钢的轧制策略进行了优化，粗轧道次由“1+5”改为“1+3”。在优化后的生产过程中，每次变换钢种，烫辊材就会出现窄尺现象，而紧随其后的电工钢板则出现超宽现象。文中针对该问题，介绍了宽度设定模型和宽度自适应模型的原理，阐述了该问题出现的原因及解决方案，并通过对宽度自适应模型的应用研究及优化攻关，有效地解决了问题，大幅提升了实物质量，降低了宽度封锁率。 The rolling strategy of electrical steel was optimized in a factory,and the rough rolling pass was changed from “1+5”to“1+3”.Subsequently,the following problems were occurred in the production process:when the steel grade changed,the roasting roller steel before the electrical steel appeared the narrow width phenomenon,and then the electrical steel appeared the ultra-wide phenomenon.This paper introduced the principle of width setting model and width adaptive model,and expounded the causes and s... 

在50Kg氧化镁坩埚真空感应炉上进行高硅电工钢的脱氧试验。结果表明,通过控制原料的成分、高真空下的碳氧反应和炉衬分解向钢液中的供氧,可使钢液的总氧含量≤15×10-6;在维持高温高真空条件下,当钢液中的反应达到一定程度后,延长精炼时间并不能降低钢液的总氧含量;完成精炼后加入硅钙合金沉淀脱氧可进一步降低钢液的总含氧量,但脱氧效果有限。 The test of high-silicon electric steel deoxidation has been carried out in 50Kg vacuum induction furnace with magnesium oxide crucible.Results show that the total oxygen could be ≤15×10-6in molten steel by controlling material components,carbon-oxygen reaction in high vacuum and oxygen contamination from crucible materials on molten steel;And when the reaction was carried through to a certain extent,total oxygen in molten steel could not be reduced by the extension of refining period in high va... 

利用X-射线衍射织构分析和线形分析技术测定了交叉轧制双取向硅钢在制备工艺各阶段的织构及微结构,进而探讨了立方织构({100}<001>)的形成过程。通过对实验结果的分析可知,二次冷轧和交叉轧制工艺为立方织构提供了内能优势和有利的形变织构,而低温预退火工艺既强化了立方织构的内能优势,又为立方织构的异常长大提供了有利的组织保证,最终在抑制剂(AlN和MnS)的协同作用下,硅钢在二次再结晶退火后形成了强烈的立方织构。 The texture and substructure of the double oriented electrical steels produced by the cross rolling technology during the difference process has been measured by means of the X-ray texture and diffraction peak profile analysis technology,and research the formation mechanism of cube texture,{100}<001>.The results show that the dominances of inner energy and deformation texture were supplied by secondary cold rolling and the cross rolling technology and strengthened by pre-annealing at a low... 

【机构】 武钢研究院； ...

本文中简要介绍了武汉钢铁有限公司采用薄板坯连铸连轧CSP(compact strip production, CSP)工艺生产中低牌号无取向硅钢的实践情况.CSP工艺生产的硅钢具有成品磁性均匀、板形好的优势，但是在利用该技术生产中低牌号无取向硅钢时，常存在成品板表面瓦楞状缺陷严重、连铸生产效率低等问题.通过优化炼钢成分、热轧等相关工艺，可消除热轧板厚度方向中心的粗大形变组织，从源头上避免了粗大{100}<011>纤维组织的出现，消除了瓦楞状缺陷；通过提升冶炼效率和控制钢中夹杂物总量，可优化隧道炉的加热温度与在炉时间，大幅度提升了连铸生产效率，实现了中低牌号无取向硅钢的批量稳定制造，使CSP产线成为中低牌号无取向硅钢热轧板原料的主要供给生产线.如何进一步提升钢水纯洁度、提高连铸生产效率、降低生产成本，以及挖掘该产线生产薄带钢的技术优点，是未来工作的重点. This paper briefly introduces the practice of producing medium and low grade non oriented silicon steel(NGO) with CSP(compact strip production, CSP)technology in Wuhan Iron and Steel Co., Ltd.. This technology has the inherent advantages of uniform magnetic properties and good shape for silicon steel finished strip. However, in the actual production process, there are serious corrugated defects on the surface of silicon steel finished strip, and production efficiency of continuous casting is low... 

一种适合冷连轧的高效变频压缩机用无取向硅钢，其化学成分及wt%为：C：≤0.0025%、Si：2.4~2.8%、Mn：0.35~0.65%、Al：0.5~0.8%、S：≤0.0020%、N：≤0.0025%、P：≤0.03%、Sb或Sn：0.03~0.08%；生产方法：冶炼浇注；对铸坯加热；粗轧；精轧；卷取；常化；经酸洗后冷连轧；退火；涂敷及精整。本发明产品性能既保证产品磁性能又提高生产效率、提高成材率和降低生产成本的效果，五机架连轧机只需要一次轧过即可，且连轧机相比单机架轧机减少了来回轧制的带头带尾切废量，因而可提高成材率，生产效率和成材率提高，自然降低生产成本。

本发明提出一种预判取向硅钢冷轧脆断发生的方法，将酸洗带头20‑30cm进行剪切取样，在取到的样板上面注明工作侧和传动侧；将取好的样板送至焊缝检测冲压机处，通过冲压机对样板进行冲压，根据不同钢带厚度，设定不同冲孔机压力，对样板进行冲压后，通过观察裂纹形貌，预判常化卷在冷轧轧制过程中是否会发生脆断，本发明使带钢在冷轧前能够制定相应的对策措施，从而降低冷轧断带所产生的损失。

一种含Bi高磁感取向硅钢热轧带钢边部质量控制方法：炼钢；连铸；铸坯加热；粗轧，粗轧道次不低于4道次，各道次压下率控制在20~33%；规精轧及进行后工序。本发明通过对热轧工序的控制，能使热轧带钢边部开裂的尺寸降低至不超过5mm，且边部开裂≤2mm比率能达到95%以上，后工序切边量很少甚至无需切边即可进行冷轧，使产品成材率能比现有技术提高2~4%；且由于铸坯加热温度的降低使能耗也随之降低。

一种低温高磁感取向硅钢的热轧方法：经转炉冶炼并浇注成坯；对铸坯加热后进行粗轧：首先确定粗轧减宽量；根据所确定的粗轧减宽量进行粗轧；进行精轧；常规进行下工序。本发明采用低温板坯加热技术，降低了板坯烧损和修炉负担，且边裂发生率比现有技术的不低于18%的基础上能降低5%以上，由此节约资源及降低能耗。

硅钢工业退火炉温度控制具有强耦合、纯滞后、多扰动等特点,它的控制方法代表着一类非线性系统控制的解决方法。以硅钢工业退火炉温度为控制对象,在双交叉限幅控制的基础上引入了智能学习系统,形成了基于智能学习系统的双交叉限幅控制方法来解决此类非线性系统的控制问题,并通过模块化的编程来实现其功能。结果表明:与传统的PID控制相比,该控制方法的控制精度、抗扰性等控制指标有明显提高,是解决此类非线性控制的一种有效方法。 The temperature control of silicon steel industrial annealing furnace has the features of strong coupling,pure lag,multidisturbance. The control method represents the solution of a class of nonlinear control systems. The control object is the temperature control of silicon steel industrial an-nealing furnace, the intelligent learning system based on Double Across Limit Control is introducedand used to solve control problem of this kind of nonlinear system, and the module programming isused to re...