研究了铝和铬元素在无取向电工钢晶粒长大过程中对织构及晶界变化的影响规律。试验结果表明:电工钢在晶粒长大过程中的主要织构组分均为{111}<112>。在晶粒生长期间,不加铝的1号试样中,{111}<112>、{111}<110>织构组分强化,而{100}<001>织构组分弱化;与1号试样相比,在加入0.2%的铝(质量分数,下同)的2号试样中,{111}<112>、{111}<110>织构组分强化(增加)的速率下降,{100}<001>织构组分变化不明显,甚至稍有增加。在含铝的试样中再加入0.3 5%的铬之后(3号试样),{111}<112>{、111}<110>和{100}<001>织构组分的变化规律与1号试样相似,但当电工钢中加入0.72%的铬之后(4号试样),上述3种织构组分的变化规律与2号试样相似。对于在晶粒生长期间持续变化的3种织构组分而言,1号试样的{1 1 1}<112>和{111}<110>织构组分的高(低)取向差角度晶界频率下降(... The effect rule of Aluminm and Chromium on texture and grain boundary transformation in the nonoriented electrical steel during grain growth was investigated.The experimental result shows that the main texture component is {111}<112> in the electrical steel.The {111}<112> and {111}<110> components in specimen 1 without Alumium were strengthened during grain growth whereas {100}<001> component was weakened.But the growth rate of {111}<112> and {111}<110> compon... 

分析了电感耦合等离子体发射光谱法(ICP-AES)测定硅钢中铌的检测过程,讨论了该检测过程中不确定度的主要来源,建立了该方法的定量的数学模型,并根据这一模型计算出了检测结果的合成标准不确定度和扩展不确定度。 The measurement of niobium content in silicon steel by inductively coupled plasma atomic emission spectrometry(ICP-AES) was analyzed,by which the main factors affecting the uncertainty of the measurement were ascertained and the calculation formula was given.Finally,according to the formula the combined uncertainty and expanded uncertainty were obtained. 

本发明公开了一种高磁感取向硅钢高效脱碳退火工艺，主要工艺流程为：炼钢连铸→热轧→酸洗常化→冷轧→脱碳和初次再结晶退火→渗氮处理(低温Hi‑B)→涂覆氧化镁隔离剂→高温退火→拉伸平整退火→涂覆绝缘涂层→精整，低温HiB不同于高温Hi‑B的工艺流程主要是在脱碳退火后增加了渗氮段。本发明在保证产品实物质量不低于现有水平(国内领先水平)的前提下，使Hi‑B钢退火效率达到世界领先，制造成本大幅降低。

本发明公开了一种高硅钢的冷轧生产工艺。该生产工艺属于机械制造技术领域，其中的处理工序的加热工序通过电磁感应加热装置加热，待处理钢经过加热工序的速度为30‑200mpm，加热工序的加热温度为70‑120℃。本发明具有生产效率高和生产质量高的特点，特别是在加热工序中对待处理钢采用电磁感应加热装置进行加热，使其可以快速有效地提升温度，以满足高硅钢的冷轧生产工艺要求，减少断带事故，具有很好的实用性和创新性。

通过观察冲剪边缘组织,测量冲剪边缘的显微硬度、残余应力的分布情况和磁性能的变化研究了冲剪加工对无取向硅钢50WW800边缘组织和磁性能的影响。对冲剪后硅钢片进行750℃退火,分析退火对组织和磁性能的影响。结果表明,硅钢片剪切边缘会存在0.4 mm的形变硬化层,边缘应力大,铁损增加。退火后变形减小,形变硬化层变小,残余应力大幅度减少,铁损减少。 The influence of punching process on cutting edge microstructure and magnetic properties of non-oriented silicon steel 50WW800was studied by observing microstructure and measuring microhardness near cutting edge.The residual stress distribution in the silicon steel tooth and magnetic properties were measured.Effect of annealing at 750 ℃ on microstructure and magnetic properties of the silicon steel was analyzed.The results show that a cut-edge hardening layer up to 0.4 mm is observed,residual st... 

介绍了国内无底层取向电工钢生产技术水平、产量和用途，简述了无底层取向电工钢作为取向电工钢超/极薄带母料及应用于制作大型发电机组铁心、风电等电机铁心和变压器铁心等的情况。 The production technology level,output and application of domestic glassless grainoriented electrical steel were introduced,and the application of glassless grain-oriented electrical steel as parent material of ultra-thin strip of grain-oriented electrical steel and in making large-scale electric generator cores,wind power motor cores and transformer cores were briefly described. 

运用电子背散射衍射(EBSD)和X射线衍射(XRD)技术对硅钢热轧板的织构在板厚方向的分布进行了研究,并分析了两种织构测量方法的特点。EBSD技术能直观给出板厚方向的微观织构,XRD能得到钢板的宏观统计织构信息,结合两种技术的分析,能更直观更精确的研究不同织构在板厚方向的分布。 The texture distribution along the thickness of the silicon steel has been investigated by electron backscatter diffraction(EBSD) and X-ray diffraction(XRD) technique.The characteristics of two technique of texture analysis have been investigated.Combined the two techniques,the texture distribution along the thickness of the silicon steel could be realized distinctly and accurately. 

本发明提出一种预判取向硅钢冷轧脆断发生的方法，将酸洗带头20‑30cm进行剪切取样，在取到的样板上面注明工作侧和传动侧；将取好的样板送至焊缝检测冲压机处，通过冲压机对样板进行冲压，根据不同钢带厚度，设定不同冲孔机压力，对样板进行冲压后，通过观察裂纹形貌，预判常化卷在冷轧轧制过程中是否会发生脆断，本发明使带钢在冷轧前能够制定相应的对策措施，从而降低冷轧断带所产生的损失。

介绍了国内、外电工钢极薄带的生产现状及市场应用的情况,以及典型生产企业的生产规模、产品性能和应用领域,指出扩大高牌号无取向电工钢生产、提高产品质量是目前电工钢发展的迫切要求。 The production situation and market application of ultra thin electrical steel strip at home and abroad were described.The production capability,product property and application area of typical corporation were introduced.The results indicate that the urgency needed of electrical steel development is expanding high-grade non-oriented electrical steel production and improving products quality at present. 

本发明公开了一种高牌号硅钢的穿带激光焊接方法，包括：将焊缝中硅含量降低到Si焊＜1.9%。采用激光+填丝焊接，填丝ER50‑6碳钢焊丝；根据焊缝截面积和激光焊接速度；激光填丝焊接时，激光线能量应足够大，达到填丝在熔池中充分混合，均匀分布，不至于填丝的成分浮在熔池的上半部分。采用此方法使焊缝组织从粗大铁素体变成细小、致密的无碳贝氏体，晶内沉淀相和晶间脆性相相对大幅减少，提高了焊缝韧性和成形性能，保证了高硅硅钢带的穿带焊接和连续生产。

本发明涉及含Cu无取向硅钢的生产方法，转炉炼钢，真空处理过后连铸成坯；铸坯化学成分：1.0≤Si/Cu≤3.0,3.0≤Si+Cu≤5.5％，S≤0.0015％，(Mn+Cu)/S≥3000，其他为Fe,Als,P以及不可避免的杂质元素；对铸坯进行粗轧；粗轧后的中间坯采用热卷机进行强制卷取，开卷后中间坯进入保温箱，控制保温箱内冷却速度≤5℃/s；进入保温箱的中间坯温度T1满足：1000‑(Si+Cu)×103≤T1≤1100‑(Si+Cu)×103；高压除鳞，精轧，层流冷却，卷取；连续酸洗；冷轧到目标厚度，成品退火，涂层；成品卷进行时效处理。成品卷具有较低的中高频铁损，高磁感和高屈服强度。

某厂对电工钢的轧制策略进行了优化，粗轧道次由“1+5”改为“1+3”。在优化后的生产过程中，每次变换钢种，烫辊材就会出现窄尺现象，而紧随其后的电工钢板则出现超宽现象。文中针对该问题，介绍了宽度设定模型和宽度自适应模型的原理，阐述了该问题出现的原因及解决方案，并通过对宽度自适应模型的应用研究及优化攻关，有效地解决了问题，大幅提升了实物质量，降低了宽度封锁率。 The rolling strategy of electrical steel was optimized in a factory,and the rough rolling pass was changed from “1+5”to“1+3”.Subsequently,the following problems were occurred in the production process:when the steel grade changed,the roasting roller steel before the electrical steel appeared the narrow width phenomenon,and then the electrical steel appeared the ultra-wide phenomenon.This paper introduced the principle of width setting model and width adaptive model,and expounded the causes and s...