硅钢资料

电工钢反复弯曲次数是电工钢性能检验的重要指标之一,直接影响到用户在使用电工钢过程的机加工性能。主要分析了试样宽度、试样张力、晶粒取向、反复弯曲设备等因素对电工钢反复弯曲试验的影响,并对各个因素的影响程度进行量化以及原因探讨,从而归纳形成各影响因素的基本规律,以便为电工钢实际生产、用户使用提供科学指导。结果表明:试样宽度增加,反复弯曲次数也会不断增加,晶粒位向对取向电工钢的反复弯曲次数影响较大,当支座顶部到拨杆底部的距离减小或拉紧力增加时,反复弯曲次数会不断减小,但当拉紧力达到60N以上时,对反复弯曲次数影响不大,试样经退火后,反复弯曲次数略有上升。 The reverse bend number is an important performance of electrical steels′capabilities,affecting the machining performance directly when the customers used.It investigated some factors,such as sample′s width,sample′s tension load,grain orientation and equipment,how to effect the reverse bend test for electrical steel,measured the influence degree,and discussed the reason,in order to form basic rules which could be guided the manufacturing and using for electrical steel.Results showed that the rev... 

本文中简要介绍了武汉钢铁有限公司采用薄板坯连铸连轧CSP(compact strip production, CSP)工艺生产中低牌号无取向硅钢的实践情况.CSP工艺生产的硅钢具有成品磁性均匀、板形好的优势，但是在利用该技术生产中低牌号无取向硅钢时，常存在成品板表面瓦楞状缺陷严重、连铸生产效率低等问题.通过优化炼钢成分、热轧等相关工艺，可消除热轧板厚度方向中心的粗大形变组织，从源头上避免了粗大{100}<011>纤维组织的出现，消除了瓦楞状缺陷；通过提升冶炼效率和控制钢中夹杂物总量，可优化隧道炉的加热温度与在炉时间，大幅度提升了连铸生产效率，实现了中低牌号无取向硅钢的批量稳定制造，使CSP产线成为中低牌号无取向硅钢热轧板原料的主要供给生产线.如何进一步提升钢水纯洁度、提高连铸生产效率、降低生产成本，以及挖掘该产线生产薄带钢的技术优点，是未来工作的重点. This paper briefly introduces the practice of producing medium and low grade non oriented silicon steel(NGO) with CSP(compact strip production, CSP)technology in Wuhan Iron and Steel Co., Ltd.. This technology has the inherent advantages of uniform magnetic properties and good shape for silicon steel finished strip. However, in the actual production process, there are serious corrugated defects on the surface of silicon steel finished strip, and production efficiency of continuous casting is low... 

一种使铋收得率不低于70%的含铋取向硅钢冶炼方法，其步骤：常规转炉冶炼并出钢至钢包中；RH精炼处理，其间：控制渣层厚度不低于45mm，且渣成分在：Al2O3：25～35wt%，CaO：40～50wt%，MgO:10～15wt%，且结束时钢水温度控制在1530～1590℃；真空精炼结束后进行镇静；后将铋颗粒与石灰石颗粒混装容器加入钢水中；保护浇注和后工序生产。本发明将铋颗粒与石灰石颗粒混合加入，石灰石在钢液中分解产生的气体不仅可以减缓铋颗粒下沉速度，使铋能够快速扩散均匀，更主要的是还可以强化铋颗粒在钢液中的扩散，最终可获得铋收得率高于70%即在71～75%的理想效果。

本发明提出一种预判取向硅钢冷轧脆断发生的方法，将酸洗带头20‑30cm进行剪切取样，在取到的样板上面注明工作侧和传动侧；将取好的样板送至焊缝检测冲压机处，通过冲压机对样板进行冲压，根据不同钢带厚度，设定不同冲孔机压力，对样板进行冲压后，通过观察裂纹形貌，预判常化卷在冷轧轧制过程中是否会发生脆断，本发明使带钢在冷轧前能够制定相应的对策措施，从而降低冷轧断带所产生的损失。

一种取向硅钢环形炉钢卷冷却装置，涉及冶金领域。该取向硅钢环形炉钢卷冷却装置用于控制环形炉的冷却一段内钢卷的冷却速度，其包括设于冷却一段的炉体内耐火层和绝热层之间的至少一块冷却板及多条设于绝热层内的冷却管，冷却管与一块冷却板贴合接触，冷却管设有用于控制流量的流量控制阀，绝热层还连接有贯穿其以对冷却板的温度进行检测的第一热电偶。本申请提供的取向硅钢环形炉钢卷冷却装置可满足不同品种和规格取向硅钢对冷却速度的要求，能够在满足出炉钢卷板形质量要求基础上减少钢卷在冷却一段的处理时间，提高环形炉的生产效益，同时能够减轻因钢卷重量波动、台车空装等因素对钢卷磁性能和板形质量的影响。

【作者】 康凌晨； 王丽娜； ...

【作者】 谌剑； ...

对w(Si)=3%无取向硅钢进行表面机械研磨处理(SMAT)和异步轧制(CSR),获得表面纳米结构,再进行550～650℃、4 h固体粉末渗硅处理,用透射电镜(TEM)、扫描电镜(SEM)和X射线衍射仪(XRD)研究表层组织演变。结果表明:经过SMAT后,w(Si)=3%无取向硅钢表面形成了等轴状、取向呈随机分布的、晶粒尺寸为10 nm的纳米晶组织;异步轧制后,表面纳米晶组织保持不变;550～650℃、4 h渗硅处理后,SMAT+CSR样品表面形成化合物层,其厚度随着温度的升高由17μm增加到52μm;化合物层由Fe3Si和FeSi相组成. Nanostructured surface layer was fabricated on a 3%(mass fraction) non-grain oriented silicon steel by means of surface mechanical attrition treatment(SMAT) and cross-shear rolling(CSR),and then a solid powder siliconizing treatment was carried out for the SMAT+CSR sample at 550~650 ℃ for 4 h.The microstructural evolution was examined by using transmission electron microscopy(TEM),scanning electron microscopy(SEM) and X-ray diffraction(XRD).Experimental results show that: equiaxed nanocrystallin... 

采用X-射线衍射分析技术测定了取向硅钢热轧板在不同压下率下不同厚度处的织构。结果表明,在压下率低于80%的情况下,几乎所有试样的不同厚度处的织构均为旋转立方织构类型{100}<011>,但不同压下率、不同厚度处的织构强度存在很大差异;在压下率大于80%的情况下,不同试样的不同厚度处的织构类型发生了变化,其织构类型为旋转立方织构或高斯织构{011}<100>,且当织构类型为旋转立方织构时,织构强度存在很大差异,而当织构类型为高斯织构时,织构强度差异相对较小。 The texture of the grain oriented silicon steel hot rolled plate at different compressibility has been measured.The experimental results have shown that the texture of all samples at different thickness is {100}<011> when the compressibility is below 80%,and its intensity at different compressibility and thickness is difference.The texture of all samples at different thickness is variable when the compressibility is above 80%,it is {100}<011> or {011}<100>,and the intensity of ... 

目的提高硅钢的磁性能。方法采用多弧离子镀技术,在普通取向硅钢薄板两面沉积高硅FeSi合金层制得高硅梯度硅钢,并进行热处理,观察其显微组织,测量磁性能。结果退火态高硅梯度硅钢表面的高硅FeSi合金层与基底结合紧密,均匀致密。高硅梯度硅钢中硅含量呈梯度分布,最表层硅质量分数为11.0%,随着深度增加,硅含量逐渐降低,在距表面20μm处硅质量分数仍能达到6.5%。沉积态高硅梯度硅钢的电阻率ρ、低频铁损P10/50、高频铁损P10/1k及磁感应强度B8分别为68.6μΩ·cm,0.82W/kg,83.3 W/kg和1.73 T,退火后分别为63.1μΩ·cm,0.44 W/kg,54.38 W/kg和1.89 T。结论由于表层高硅FeSi合金层的存在,梯度高硅钢的低频磁学性能良好,但高频损耗需进一步改善。 Objective To improve the magnetic properties of silicon steel. Methods FeSi alloy coatings with high-silicon content were deposited on the surface of common grain-oriented silicon steel by cathodic arc plasma evaporation,and then a kind of high silicon gradient steel was prepared. The morphologies,content and magnetic properties of the samples were tested. Results FeSi alloy coatings were featured with compact microstructures and excellent adhesive quality with the substrates. The silicon conten... 

【作者】 王爱华； ...

本发明涉及无取向硅钢生产技术领域，公开了一种改善含Cu高强度无取向硅钢冷轧质量的方法，包括如下步骤：A)含Cu高强度无取向硅钢热轧卷化学成分(wt,％)：Si：2.0～3.5％，Als≤1.5％，Cu：1～3％，其他为Fe,Als,Mn以及不可避免的杂质元素，对热轧卷进行常化酸洗处理，常化温度T常满足：T常≤1620‑(0.5Als+1.5Si+Cu)％×104，单位℃；B)将常化后的热轧卷在电磁感应加热炉内进行加热；C)在冷轧机组开卷机进行开卷，冷轧第一道次开卷温度T冷轧满足：1.5×(Si+Cu)％×103‑T室温≤T冷轧≤40+2×(Si+Cu)％×103，单位℃，式中，T室温为室温；D)按照4‑6道次冷轧到目标厚度。本发明改善含Cu高强度无取向硅钢冷轧质量的方法，在采用传统常化工艺路线，保证较高的强度和磁性水平前提下，改善冷轧质量，提高成品成材率。