本发明公开了一种可替代高磁感取向硅钢常化退火的热处理方法。该方法包括对所述取向硅钢的铸坯依次进行热轧、酸洗和冷轧，省去了常化酸洗工序中的常化退火工艺。所述热轧工序包括加热、粗轧和精轧过程，所述精轧过程中，热轧板离开精轧机最后一个机架时的温度达到1000～1050℃；或者，所述酸洗工序后，对热轧板进行通电加热至1000～1050℃；然后，对热轧板采用短时通电加热控制冷却速度，通电加热2‑5s使热轧板的温度降至940～960℃。采用该热处理方法得到高磁感取向硅钢常化板等效织构，满足生产高磁感取向硅钢的织构组分条件，其简化了高磁感取向硅钢的制造工艺，降低了生产成本和能耗，提高了生产效率。

利用X-射线衍射织构分析和线形分析技术测定了交叉轧制双取向硅钢在制备工艺各阶段的织构及微结构,进而探讨了立方织构({100}<001>)的形成过程。通过对实验结果的分析可知,二次冷轧和交叉轧制工艺为立方织构提供了内能优势和有利的形变织构,而低温预退火工艺既强化了立方织构的内能优势,又为立方织构的异常长大提供了有利的组织保证,最终在抑制剂(AlN和MnS)的协同作用下,硅钢在二次再结晶退火后形成了强烈的立方织构。 The texture and substructure of the double oriented electrical steels produced by the cross rolling technology during the difference process has been measured by means of the X-ray texture and diffraction peak profile analysis technology,and research the formation mechanism of cube texture,{100}<001>.The results show that the dominances of inner energy and deformation texture were supplied by secondary cold rolling and the cross rolling technology and strengthened by pre-annealing at a low... 

采用X-射线衍射分析技术测定了取向硅钢热轧板在不同压下率下不同厚度处的织构。结果表明,在压下率低于80%的情况下,几乎所有试样的不同厚度处的织构均为旋转立方织构类型{100}<011>,但不同压下率、不同厚度处的织构强度存在很大差异;在压下率大于80%的情况下,不同试样的不同厚度处的织构类型发生了变化,其织构类型为旋转立方织构或高斯织构{011}<100>,且当织构类型为旋转立方织构时,织构强度存在很大差异,而当织构类型为高斯织构时,织构强度差异相对较小。 The texture of the grain oriented silicon steel hot rolled plate at different compressibility has been measured.The experimental results have shown that the texture of all samples at different thickness is {100}<011> when the compressibility is below 80%,and its intensity at different compressibility and thickness is difference.The texture of all samples at different thickness is variable when the compressibility is above 80%,it is {100}<011> or {011}<100>,and the intensity of ... 

一种含Bi高磁感取向硅钢热轧带钢边部质量控制方法：炼钢；连铸；铸坯加热；粗轧，粗轧道次不低于4道次，各道次压下率控制在20~33%；规精轧及进行后工序。本发明通过对热轧工序的控制，能使热轧带钢边部开裂的尺寸降低至不超过5mm，且边部开裂≤2mm比率能达到95%以上，后工序切边量很少甚至无需切边即可进行冷轧，使产品成材率能比现有技术提高2~4%；且由于铸坯加热温度的降低使能耗也随之降低。

介绍了国内无底层取向电工钢生产技术水平、产量和用途，简述了无底层取向电工钢作为取向电工钢超/极薄带母料及应用于制作大型发电机组铁心、风电等电机铁心和变压器铁心等的情况。 The production technology level,output and application of domestic glassless grainoriented electrical steel were introduced,and the application of glassless grain-oriented electrical steel as parent material of ultra-thin strip of grain-oriented electrical steel and in making large-scale electric generator cores,wind power motor cores and transformer cores were briefly described. 

某厂对电工钢的轧制策略进行了优化，粗轧道次由“1+5”改为“1+3”。在优化后的生产过程中，每次变换钢种，烫辊材就会出现窄尺现象，而紧随其后的电工钢板则出现超宽现象。文中针对该问题，介绍了宽度设定模型和宽度自适应模型的原理，阐述了该问题出现的原因及解决方案，并通过对宽度自适应模型的应用研究及优化攻关，有效地解决了问题，大幅提升了实物质量，降低了宽度封锁率。 The rolling strategy of electrical steel was optimized in a factory,and the rough rolling pass was changed from “1+5”to“1+3”.Subsequently,the following problems were occurred in the production process:when the steel grade changed,the roasting roller steel before the electrical steel appeared the narrow width phenomenon,and then the electrical steel appeared the ultra-wide phenomenon.This paper introduced the principle of width setting model and width adaptive model,and expounded the causes and s... 

本发明公开了一种适用于无取向硅钢极薄带表面涂覆的涂液，它由水溶性丙烯树脂、成膜助剂、耐盐雾助剂、流平剂、纳米氢氧化锆、消泡剂、水按质量比100:(2～8):(1～3):(1～5):(0～1):(0.1～0.5):(70～130)组成。将该涂液在无取向硅钢极薄带表面可表现出良好的涂覆性，经烘烤固化后形成的绝缘涂层表面透明光滑，附着性和绝缘性能优良，可有效提升无取向硅钢极薄带的综合性能，适合推广应用。

电动汽车电机在高速旋转时承受离心力和电磁力的作用,在进行电机转子设计时,既要考虑电磁性能,还要考虑机械性能。对电机转子受力情况进行了综述,分析了转子用电工钢疲劳性能参数的重要性,详细阐述了试样抛光、表面处理、试样的对中和安装对测试结果的影响。 The motor of electric vehicle bears big force for high speed rotors,mainly including centrifugal and electromagnetic forces.The magnetic and mechanical aspects of the electrical steel are crucial to machine design.In this paper,the forces applied on the motor were summarized and importance of fatigue properties was analyzed.The influence of specimen polish,surface treatment,alignment and installation on fatigue testing result were represented in detail. 

本发明实施例公开了一种硅钢稀酸废水零排放处理方法和系统，所述方法包括：获得稀酸废水；对所述稀酸废水中的含硅固体杂质进行分离与回收，以获得稀酸废水净化液和含硅脱水泥饼；将所述稀酸废水净化液进行两级电吸附分盐处理，利用直流电场将稀酸废水中氯化亚铁组份浓缩分离，以获得分盐浓水和分盐淡水；将所述分盐浓水与酸再生工艺耦合，以获得再生盐酸；将所述分盐淡水调质再生处理，以获得铁系絮凝剂和再生工业净化水。所述硅钢稀酸废水零排放处理方法和系统，可以较低成本和能耗实现硅钢稀酸性废水全回用，真正实现废水零排放；可回收稀酸废水中的铁素和稀盐酸，不产生固体废物，可彻底实现废弃物资源化利用。

对w(Si)=3%无取向硅钢进行表面机械研磨处理(SMAT)和异步轧制(CSR),获得表面纳米结构,再进行550～650℃、4 h固体粉末渗硅处理,用透射电镜(TEM)、扫描电镜(SEM)和X射线衍射仪(XRD)研究表层组织演变。结果表明:经过SMAT后,w(Si)=3%无取向硅钢表面形成了等轴状、取向呈随机分布的、晶粒尺寸为10 nm的纳米晶组织;异步轧制后,表面纳米晶组织保持不变;550～650℃、4 h渗硅处理后,SMAT+CSR样品表面形成化合物层,其厚度随着温度的升高由17μm增加到52μm;化合物层由Fe3Si和FeSi相组成. Nanostructured surface layer was fabricated on a 3%(mass fraction) non-grain oriented silicon steel by means of surface mechanical attrition treatment(SMAT) and cross-shear rolling(CSR),and then a solid powder siliconizing treatment was carried out for the SMAT+CSR sample at 550~650 ℃ for 4 h.The microstructural evolution was examined by using transmission electron microscopy(TEM),scanning electron microscopy(SEM) and X-ray diffraction(XRD).Experimental results show that: equiaxed nanocrystallin... 

本发明涉及一种提高低温高磁感取向硅钢附着性的方法，该方法在现有低温高磁感取向硅钢连续式脱碳退火炉中，通过在脱碳退火前区通入氮气、氢气干式混合气，在脱碳退火后区通入氮气、氢气湿式混合气进行脱碳，在渗氮区通入氮气、氢气湿式混合气及氨气进行渗氮，解决了低温高磁感取向硅钢附着性不好的难题。本发明方法提高了钢中总氧量、增加了氧化层厚度、改善了氧化层结构，经高温退火后生成了致密的硅酸镁底层，附着性大幅提高，测试结果均在C级以上，大部分样品在B级以上。

电工钢反复弯曲次数是电工钢性能检验的重要指标之一,直接影响到用户在使用电工钢过程的机加工性能。主要分析了试样宽度、试样张力、晶粒取向、反复弯曲设备等因素对电工钢反复弯曲试验的影响,并对各个因素的影响程度进行量化以及原因探讨,从而归纳形成各影响因素的基本规律,以便为电工钢实际生产、用户使用提供科学指导。结果表明:试样宽度增加,反复弯曲次数也会不断增加,晶粒位向对取向电工钢的反复弯曲次数影响较大,当支座顶部到拨杆底部的距离减小或拉紧力增加时,反复弯曲次数会不断减小,但当拉紧力达到60N以上时,对反复弯曲次数影响不大,试样经退火后,反复弯曲次数略有上升。 The reverse bend number is an important performance of electrical steels′capabilities,affecting the machining performance directly when the customers used.It investigated some factors,such as sample′s width,sample′s tension load,grain orientation and equipment,how to effect the reverse bend test for electrical steel,measured the influence degree,and discussed the reason,in order to form basic rules which could be guided the manufacturing and using for electrical steel.Results showed that the rev...