分析了电感耦合等离子体发射光谱法(ICP-AES)测定硅钢中铌的检测过程,讨论了该检测过程中不确定度的主要来源,建立了该方法的定量的数学模型,并根据这一模型计算出了检测结果的合成标准不确定度和扩展不确定度。 The measurement of niobium content in silicon steel by inductively coupled plasma atomic emission spectrometry(ICP-AES) was analyzed,by which the main factors affecting the uncertainty of the measurement were ascertained and the calculation formula was given.Finally,according to the formula the combined uncertainty and expanded uncertainty were obtained. 

采用化学气相沉积(CVD)渗硅处理工艺连续制备6.5%Si高硅钢,具有优质的软磁性能,通过理论研究化学反应并且用简单的试验设备做进一步的探讨。根据试验的结果对连续制备6.5%Si高硅钢的CVD工艺构造提出全面、有效的建议,实现制备6.5%Si高硅钢系统。 CVD method for continuously manufacturing 6.5%Si Steel Sheet has excellent soft magnetic.Carried out a theoretical study of related chemical reaction and performing basic research with a simple test apparatus.Based on the results,finally proposed an overall process configuration to realize such a production-CVD method for continuously manufacturing 6.5%Si Steel Sheet. 

本发明公开了一种高磁感取向硅钢高效脱碳退火工艺，主要工艺流程为：炼钢连铸→热轧→酸洗常化→冷轧→脱碳和初次再结晶退火→渗氮处理(低温Hi‑B)→涂覆氧化镁隔离剂→高温退火→拉伸平整退火→涂覆绝缘涂层→精整，低温HiB不同于高温Hi‑B的工艺流程主要是在脱碳退火后增加了渗氮段。本发明在保证产品实物质量不低于现有水平(国内领先水平)的前提下，使Hi‑B钢退火效率达到世界领先，制造成本大幅降低。

【机构】 武汉钢铁学院轧钢七二级电工钢结业小组； ...

阐述了电工钢在\"双碳\"中的作用,强调了电工钢的生产工艺技术及在减少碳排放、降低能耗中的作用,对下游能效升级带来明显的节能及降碳成果。同时,分析了2021年电工钢的生产运行情况,介绍了电工钢的未来发展,并针对如何减少碳排放以及生产更多的更低铁损、更高磁感的电工钢谈了几点启示。 The effects of electrical steels on carbon peak and carbon neutralization were expounded,especially on the achievements of obvious energy saving and carbon reduction to the downstream energy efficiency upgrading bringing from the production technology of electrical steels and their effects to reducing carbon emission and energy consumption.Meanwhile the production situation of electrical steels in 2021 was analyzed,and the future development of electrical steels was introduced,and some advices w... 

本发明涉及无取向硅钢生产技术领域，公开了一种改善含Cu高强度无取向硅钢冷轧质量的方法，包括如下步骤：A)含Cu高强度无取向硅钢热轧卷化学成分(wt,％)：Si：2.0～3.5％，Als≤1.5％，Cu：1～3％，其他为Fe,Als,Mn以及不可避免的杂质元素，对热轧卷进行常化酸洗处理，常化温度T常满足：T常≤1620‑(0.5Als+1.5Si+Cu)％×104，单位℃；B)将常化后的热轧卷在电磁感应加热炉内进行加热；C)在冷轧机组开卷机进行开卷，冷轧第一道次开卷温度T冷轧满足：1.5×(Si+Cu)％×103‑T室温≤T冷轧≤40+2×(Si+Cu)％×103，单位℃，式中，T室温为室温；D)按照4‑6道次冷轧到目标厚度。本发明改善含Cu高强度无取向硅钢冷轧质量的方法，在采用传统常化工艺路线，保证较高的强度和磁性水平前提下，改善冷轧质量，提高成品成材率。

一种提高有效氮和底层质量的高磁感取向硅钢制造方法：冶炼后连铸成坯；对铸坯加热；热轧、常化及酸洗后时效冷轧；在湿式气氛下脱碳退火；在湿式混合气氛下均热；在湿式混合气氛下渗氮退火；进行后工序。本发明与现有技术相比，通过合理控制渗氮过程，提高渗氮后钢板基体内氮含量与总氮量之间的比例达到80%以上，使无点状露晶产生，最终获得产品的底层质量优异。

目的提高硅钢的磁性能。方法采用多弧离子镀技术,在普通取向硅钢薄板两面沉积高硅FeSi合金层制得高硅梯度硅钢,并进行热处理,观察其显微组织,测量磁性能。结果退火态高硅梯度硅钢表面的高硅FeSi合金层与基底结合紧密,均匀致密。高硅梯度硅钢中硅含量呈梯度分布,最表层硅质量分数为11.0%,随着深度增加,硅含量逐渐降低,在距表面20μm处硅质量分数仍能达到6.5%。沉积态高硅梯度硅钢的电阻率ρ、低频铁损P10/50、高频铁损P10/1k及磁感应强度B8分别为68.6μΩ·cm,0.82W/kg,83.3 W/kg和1.73 T,退火后分别为63.1μΩ·cm,0.44 W/kg,54.38 W/kg和1.89 T。结论由于表层高硅FeSi合金层的存在,梯度高硅钢的低频磁学性能良好,但高频损耗需进一步改善。 Objective To improve the magnetic properties of silicon steel. Methods FeSi alloy coatings with high-silicon content were deposited on the surface of common grain-oriented silicon steel by cathodic arc plasma evaporation,and then a kind of high silicon gradient steel was prepared. The morphologies,content and magnetic properties of the samples were tested. Results FeSi alloy coatings were featured with compact microstructures and excellent adhesive quality with the substrates. The silicon conten... 

某厂对电工钢的轧制策略进行了优化，粗轧道次由“1+5”改为“1+3”。在优化后的生产过程中，每次变换钢种，烫辊材就会出现窄尺现象，而紧随其后的电工钢板则出现超宽现象。文中针对该问题，介绍了宽度设定模型和宽度自适应模型的原理，阐述了该问题出现的原因及解决方案，并通过对宽度自适应模型的应用研究及优化攻关，有效地解决了问题，大幅提升了实物质量，降低了宽度封锁率。 The rolling strategy of electrical steel was optimized in a factory,and the rough rolling pass was changed from “1+5”to“1+3”.Subsequently,the following problems were occurred in the production process:when the steel grade changed,the roasting roller steel before the electrical steel appeared the narrow width phenomenon,and then the electrical steel appeared the ultra-wide phenomenon.This paper introduced the principle of width setting model and width adaptive model,and expounded the causes and s... 

一种使铋收得率不低于70%的含铋取向硅钢冶炼方法，其步骤：常规转炉冶炼并出钢至钢包中；RH精炼处理，其间：控制渣层厚度不低于45mm，且渣成分在：Al2O3：25～35wt%，CaO：40～50wt%，MgO:10～15wt%，且结束时钢水温度控制在1530～1590℃；真空精炼结束后进行镇静；后将铋颗粒与石灰石颗粒混装容器加入钢水中；保护浇注和后工序生产。本发明将铋颗粒与石灰石颗粒混合加入，石灰石在钢液中分解产生的气体不仅可以减缓铋颗粒下沉速度，使铋能够快速扩散均匀，更主要的是还可以强化铋颗粒在钢液中的扩散，最终可获得铋收得率高于70%即在71～75%的理想效果。

本发明公开了一种可替代高磁感取向硅钢常化退火的热处理方法。该方法包括对所述取向硅钢的铸坯依次进行热轧、酸洗和冷轧，省去了常化酸洗工序中的常化退火工艺。所述热轧工序包括加热、粗轧和精轧过程，所述精轧过程中，热轧板离开精轧机最后一个机架时的温度达到1000～1050℃；或者，所述酸洗工序后，对热轧板进行通电加热至1000～1050℃；然后，对热轧板采用短时通电加热控制冷却速度，通电加热2‑5s使热轧板的温度降至940～960℃。采用该热处理方法得到高磁感取向硅钢常化板等效织构，满足生产高磁感取向硅钢的织构组分条件，其简化了高磁感取向硅钢的制造工艺，降低了生产成本和能耗，提高了生产效率。

本发明涉及一种提高低温高磁感取向硅钢附着性的方法，该方法在现有低温高磁感取向硅钢连续式脱碳退火炉中，通过在脱碳退火前区通入氮气、氢气干式混合气，在脱碳退火后区通入氮气、氢气湿式混合气进行脱碳，在渗氮区通入氮气、氢气湿式混合气及氨气进行渗氮，解决了低温高磁感取向硅钢附着性不好的难题。本发明方法提高了钢中总氧量、增加了氧化层厚度、改善了氧化层结构，经高温退火后生成了致密的硅酸镁底层，附着性大幅提高，测试结果均在C级以上，大部分样品在B级以上。