硅钢资料

一种使铋收得率不低于70%的含铋取向硅钢冶炼方法，其步骤：常规转炉冶炼并出钢至钢包中；RH精炼处理，其间：控制渣层厚度不低于45mm，且渣成分在：Al2O3：25～35wt%，CaO：40～50wt%，MgO:10～15wt%，且结束时钢水温度控制在1530～1590℃；真空精炼结束后进行镇静；后将铋颗粒与石灰石颗粒混装容器加入钢水中；保护浇注和后工序生产。本发明将铋颗粒与石灰石颗粒混合加入，石灰石在钢液中分解产生的气体不仅可以减缓铋颗粒下沉速度，使铋能够快速扩散均匀，更主要的是还可以强化铋颗粒在钢液中的扩散，最终可获得铋收得率高于70%即在71～75%的理想效果。

对w(Si)=3%无取向硅钢进行表面机械研磨处理(SMAT)和异步轧制(CSR),获得表面纳米结构,再进行550～650℃、4 h固体粉末渗硅处理,用透射电镜(TEM)、扫描电镜(SEM)和X射线衍射仪(XRD)研究表层组织演变。结果表明:经过SMAT后,w(Si)=3%无取向硅钢表面形成了等轴状、取向呈随机分布的、晶粒尺寸为10 nm的纳米晶组织;异步轧制后,表面纳米晶组织保持不变;550～650℃、4 h渗硅处理后,SMAT+CSR样品表面形成化合物层,其厚度随着温度的升高由17μm增加到52μm;化合物层由Fe3Si和FeSi相组成. Nanostructured surface layer was fabricated on a 3%(mass fraction) non-grain oriented silicon steel by means of surface mechanical attrition treatment(SMAT) and cross-shear rolling(CSR),and then a solid powder siliconizing treatment was carried out for the SMAT+CSR sample at 550~650 ℃ for 4 h.The microstructural evolution was examined by using transmission electron microscopy(TEM),scanning electron microscopy(SEM) and X-ray diffraction(XRD).Experimental results show that: equiaxed nanocrystallin... 

【作者】 王爱华； ...

本发明提出一种预判取向硅钢冷轧脆断发生的方法，将酸洗带头20‑30cm进行剪切取样，在取到的样板上面注明工作侧和传动侧；将取好的样板送至焊缝检测冲压机处，通过冲压机对样板进行冲压，根据不同钢带厚度，设定不同冲孔机压力，对样板进行冲压后，通过观察裂纹形貌，预判常化卷在冷轧轧制过程中是否会发生脆断，本发明使带钢在冷轧前能够制定相应的对策措施，从而降低冷轧断带所产生的损失。

运用电子背散射衍射(EBSD)和X射线衍射(XRD)技术对硅钢热轧板的织构在板厚方向的分布进行了研究,并分析了两种织构测量方法的特点。EBSD技术能直观给出板厚方向的微观织构,XRD能得到钢板的宏观统计织构信息,结合两种技术的分析,能更直观更精确的研究不同织构在板厚方向的分布。 The texture distribution along the thickness of the silicon steel has been investigated by electron backscatter diffraction(EBSD) and X-ray diffraction(XRD) technique.The characteristics of two technique of texture analysis have been investigated.Combined the two techniques,the texture distribution along the thickness of the silicon steel could be realized distinctly and accurately. 

研究了应用电感耦合等离子体质谱(ICP-MS)同时测定硅钢中痕量铝、钼、钒、钛、铌元素的分析方法。通过条件试验对测量参数进行了优化,确定RF功率1 400 W,泵速30rpm,采样深度140,雾化压力0.90。样品采用硝酸分解,以Be、Y混合内标校正了测量过程中高基体引起的信号漂移。根据测量时存在的质谱干扰情况,选择同位素27 Al、98 Mo、51 V、47 Ti和93 Nb作为测定同位素,同时通过调节仪器参数使得双电荷离子和氧化物离子的产率最低,以减少其带来的干扰。采用基体匹配法配制校准溶液,以标准加入法建立工作曲线,并扣除试剂空白。该方法各元素的测定下限均可达到1μg/g。用于硅钢标准样品的测定,所得结果与参考值完全吻合,各元素的RSD小于5.2%。 A method for the determination of trace aluminum,molybdenum,vanadium,titanium and niobium in silicon steel by inductively coupled plasma mass spectrometry(ICP-MS) was described.A series of single parameter condition experiment was conducted.The optimized operation parameters with RF power 1 400 W,turbo pump rate 30 rpm,sampling depth 140 and nebulizer pressure 0.90 were obtained.The samples were dissolved by HNO3,and the Be and Y mixing internal standard were used to eliminate the signal drift c... 

本文中简要介绍了武汉钢铁有限公司采用薄板坯连铸连轧CSP(compact strip production, CSP)工艺生产中低牌号无取向硅钢的实践情况.CSP工艺生产的硅钢具有成品磁性均匀、板形好的优势，但是在利用该技术生产中低牌号无取向硅钢时，常存在成品板表面瓦楞状缺陷严重、连铸生产效率低等问题.通过优化炼钢成分、热轧等相关工艺，可消除热轧板厚度方向中心的粗大形变组织，从源头上避免了粗大{100}<011>纤维组织的出现，消除了瓦楞状缺陷；通过提升冶炼效率和控制钢中夹杂物总量，可优化隧道炉的加热温度与在炉时间，大幅度提升了连铸生产效率，实现了中低牌号无取向硅钢的批量稳定制造，使CSP产线成为中低牌号无取向硅钢热轧板原料的主要供给生产线.如何进一步提升钢水纯洁度、提高连铸生产效率、降低生产成本，以及挖掘该产线生产薄带钢的技术优点，是未来工作的重点. This paper briefly introduces the practice of producing medium and low grade non oriented silicon steel(NGO) with CSP(compact strip production, CSP)technology in Wuhan Iron and Steel Co., Ltd.. This technology has the inherent advantages of uniform magnetic properties and good shape for silicon steel finished strip. However, in the actual production process, there are serious corrugated defects on the surface of silicon steel finished strip, and production efficiency of continuous casting is low... 

分析了电感耦合等离子体发射光谱法(ICP-AES)测定硅钢中铌的检测过程,讨论了该检测过程中不确定度的主要来源,建立了该方法的定量的数学模型,并根据这一模型计算出了检测结果的合成标准不确定度和扩展不确定度。 The measurement of niobium content in silicon steel by inductively coupled plasma atomic emission spectrometry(ICP-AES) was analyzed,by which the main factors affecting the uncertainty of the measurement were ascertained and the calculation formula was given.Finally,according to the formula the combined uncertainty and expanded uncertainty were obtained. 

本发明涉及无取向硅钢生产技术领域，公开了一种改善含Cu高强度无取向硅钢冷轧质量的方法，包括如下步骤：A)含Cu高强度无取向硅钢热轧卷化学成分(wt,％)：Si：2.0～3.5％，Als≤1.5％，Cu：1～3％，其他为Fe,Als,Mn以及不可避免的杂质元素，对热轧卷进行常化酸洗处理，常化温度T常满足：T常≤1620‑(0.5Als+1.5Si+Cu)％×104，单位℃；B)将常化后的热轧卷在电磁感应加热炉内进行加热；C)在冷轧机组开卷机进行开卷，冷轧第一道次开卷温度T冷轧满足：1.5×(Si+Cu)％×103‑T室温≤T冷轧≤40+2×(Si+Cu)％×103，单位℃，式中，T室温为室温；D)按照4‑6道次冷轧到目标厚度。本发明改善含Cu高强度无取向硅钢冷轧质量的方法，在采用传统常化工艺路线，保证较高的强度和磁性水平前提下，改善冷轧质量，提高成品成材率。

【作者】 姚昌国； ...

采用EBSD技术研究了有、无拉应力作用下无取向硅钢在晶粒长大过程中织构转变及晶界变化的规律。结果表明:在晶粒生长期间,无应力作用下的硅钢中,{111}〈112〉,{111}〈110〉织构组分强化,而{100}〈001〉织构组分弱化;与无拉应力作用下的情况相比,施加5MPa的拉应力时,{111}〈112〉,{111}〈110〉织构组分强化的速率下降,{100}〈001〉织构组分变化不明显。对于在晶粒生长期间持续变化的{111}〈112〉,{111}〈110〉和{100}〈001〉织构组分而言,虽然有、无拉应力作用下硅钢的{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率均下降,而{100}〈001〉织构组分的高取向差角度晶界频率则上升,但当有拉应力作用后,{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率下降的速率变小,{100}〈001〉织构组分的高取向差角度晶界频率上升的速率稍有变小。通过对无取向硅钢在晶粒长大过程中织构转变及晶界变化规律的研究,分析了合金原子在晶界的偏聚行为。 The rules of texture and grain boundary transformation in the nonoriented silicon steel under applied stress or without applied stress during grain growth were investigated by EBSD.The results show that the {111}〈112〉 and {111}〈110〉 components in the nonoriented silicon steel without stress are strengthened during grain growth whereas {100}〈001〉 component is weakened,but the growth rate of {111}〈112〉 and {111}〈110〉 component decreases,while the area fraction of {100}〈001〉 component doesn’t chang... 

一种适合冷连轧的高效变频压缩机用无取向硅钢，其化学成分及wt%为：C：≤0.0025%、Si：2.4~2.8%、Mn：0.35~0.65%、Al：0.5~0.8%、S：≤0.0020%、N：≤0.0025%、P：≤0.03%、Sb或Sn：0.03~0.08%；生产方法：冶炼浇注；对铸坯加热；粗轧；精轧；卷取；常化；经酸洗后冷连轧；退火；涂敷及精整。本发明产品性能既保证产品磁性能又提高生产效率、提高成材率和降低生产成本的效果，五机架连轧机只需要一次轧过即可，且连轧机相比单机架轧机减少了来回轧制的带头带尾切废量，因而可提高成材率，生产效率和成材率提高，自然降低生产成本。