硅钢资料

研究了铝和铬元素在无取向电工钢晶粒长大过程中对织构及晶界变化的影响规律。试验结果表明:电工钢在晶粒长大过程中的主要织构组分均为{111}<112>。在晶粒生长期间,不加铝的1号试样中,{111}<112>、{111}<110>织构组分强化,而{100}<001>织构组分弱化;与1号试样相比,在加入0.2%的铝(质量分数,下同)的2号试样中,{111}<112>、{111}<110>织构组分强化(增加)的速率下降,{100}<001>织构组分变化不明显,甚至稍有增加。在含铝的试样中再加入0.3 5%的铬之后(3号试样),{111}<112>{、111}<110>和{100}<001>织构组分的变化规律与1号试样相似,但当电工钢中加入0.72%的铬之后(4号试样),上述3种织构组分的变化规律与2号试样相似。对于在晶粒生长期间持续变化的3种织构组分而言,1号试样的{1 1 1}<112>和{111}<110>织构组分的高(低)取向差角度晶界频率下降(... The effect rule of Aluminm and Chromium on texture and grain boundary transformation in the nonoriented electrical steel during grain growth was investigated.The experimental result shows that the main texture component is {111}<112> in the electrical steel.The {111}<112> and {111}<110> components in specimen 1 without Alumium were strengthened during grain growth whereas {100}<001> component was weakened.But the growth rate of {111}<112> and {111}<110> compon... 

本发明提出一种预判取向硅钢冷轧脆断发生的方法，将酸洗带头20‑30cm进行剪切取样，在取到的样板上面注明工作侧和传动侧；将取好的样板送至焊缝检测冲压机处，通过冲压机对样板进行冲压，根据不同钢带厚度，设定不同冲孔机压力，对样板进行冲压后，通过观察裂纹形貌，预判常化卷在冷轧轧制过程中是否会发生脆断，本发明使带钢在冷轧前能够制定相应的对策措施，从而降低冷轧断带所产生的损失。

【机构】 武钢研究院； ...

本发明公开了一种高硅钢的冷轧生产工艺。该生产工艺属于机械制造技术领域，其中的处理工序的加热工序通过电磁感应加热装置加热，待处理钢经过加热工序的速度为30‑200mpm，加热工序的加热温度为70‑120℃。本发明具有生产效率高和生产质量高的特点，特别是在加热工序中对待处理钢采用电磁感应加热装置进行加热，使其可以快速有效地提升温度，以满足高硅钢的冷轧生产工艺要求，减少断带事故，具有很好的实用性和创新性。

阐述了电工钢在\"双碳\"中的作用,强调了电工钢的生产工艺技术及在减少碳排放、降低能耗中的作用,对下游能效升级带来明显的节能及降碳成果。同时,分析了2021年电工钢的生产运行情况,介绍了电工钢的未来发展,并针对如何减少碳排放以及生产更多的更低铁损、更高磁感的电工钢谈了几点启示。 The effects of electrical steels on carbon peak and carbon neutralization were expounded,especially on the achievements of obvious energy saving and carbon reduction to the downstream energy efficiency upgrading bringing from the production technology of electrical steels and their effects to reducing carbon emission and energy consumption.Meanwhile the production situation of electrical steels in 2021 was analyzed,and the future development of electrical steels was introduced,and some advices w... 

一种低温高磁感取向硅钢的热轧方法：经转炉冶炼并浇注成坯；对铸坯加热后进行粗轧：首先确定粗轧减宽量；根据所确定的粗轧减宽量进行粗轧；进行精轧；常规进行下工序。本发明采用低温板坯加热技术，降低了板坯烧损和修炉负担，且边裂发生率比现有技术的不低于18%的基础上能降低5%以上，由此节约资源及降低能耗。

电工钢反复弯曲次数是电工钢性能检验的重要指标之一,直接影响到用户在使用电工钢过程的机加工性能。主要分析了试样宽度、试样张力、晶粒取向、反复弯曲设备等因素对电工钢反复弯曲试验的影响,并对各个因素的影响程度进行量化以及原因探讨,从而归纳形成各影响因素的基本规律,以便为电工钢实际生产、用户使用提供科学指导。结果表明:试样宽度增加,反复弯曲次数也会不断增加,晶粒位向对取向电工钢的反复弯曲次数影响较大,当支座顶部到拨杆底部的距离减小或拉紧力增加时,反复弯曲次数会不断减小,但当拉紧力达到60N以上时,对反复弯曲次数影响不大,试样经退火后,反复弯曲次数略有上升。 The reverse bend number is an important performance of electrical steels′capabilities,affecting the machining performance directly when the customers used.It investigated some factors,such as sample′s width,sample′s tension load,grain orientation and equipment,how to effect the reverse bend test for electrical steel,measured the influence degree,and discussed the reason,in order to form basic rules which could be guided the manufacturing and using for electrical steel.Results showed that the rev... 

【机构】 武汉钢铁学院轧钢七二级电工钢结业小组； ...

采用X-射线衍射分析技术测定了取向硅钢热轧板在不同压下率下不同厚度处的织构。结果表明,在压下率低于80%的情况下,几乎所有试样的不同厚度处的织构均为旋转立方织构类型{100}<011>,但不同压下率、不同厚度处的织构强度存在很大差异;在压下率大于80%的情况下,不同试样的不同厚度处的织构类型发生了变化,其织构类型为旋转立方织构或高斯织构{011}<100>,且当织构类型为旋转立方织构时,织构强度存在很大差异,而当织构类型为高斯织构时,织构强度差异相对较小。 The texture of the grain oriented silicon steel hot rolled plate at different compressibility has been measured.The experimental results have shown that the texture of all samples at different thickness is {100}<011> when the compressibility is below 80%,and its intensity at different compressibility and thickness is difference.The texture of all samples at different thickness is variable when the compressibility is above 80%,it is {100}<011> or {011}<100>,and the intensity of ... 

本发明实施例公开了一种硅钢稀酸废水零排放处理方法和系统，所述方法包括：获得稀酸废水；对所述稀酸废水中的含硅固体杂质进行分离与回收，以获得稀酸废水净化液和含硅脱水泥饼；将所述稀酸废水净化液进行两级电吸附分盐处理，利用直流电场将稀酸废水中氯化亚铁组份浓缩分离，以获得分盐浓水和分盐淡水；将所述分盐浓水与酸再生工艺耦合，以获得再生盐酸；将所述分盐淡水调质再生处理，以获得铁系絮凝剂和再生工业净化水。所述硅钢稀酸废水零排放处理方法和系统，可以较低成本和能耗实现硅钢稀酸性废水全回用，真正实现废水零排放；可回收稀酸废水中的铁素和稀盐酸，不产生固体废物，可彻底实现废弃物资源化利用。

本发明公开了一种高牌号硅钢的穿带激光焊接方法，包括：将焊缝中硅含量降低到Si焊＜1.9%。采用激光+填丝焊接，填丝ER50‑6碳钢焊丝；根据焊缝截面积和激光焊接速度；激光填丝焊接时，激光线能量应足够大，达到填丝在熔池中充分混合，均匀分布，不至于填丝的成分浮在熔池的上半部分。采用此方法使焊缝组织从粗大铁素体变成细小、致密的无碳贝氏体，晶内沉淀相和晶间脆性相相对大幅减少，提高了焊缝韧性和成形性能，保证了高硅硅钢带的穿带焊接和连续生产。

某厂对电工钢的轧制策略进行了优化，粗轧道次由“1+5”改为“1+3”。在优化后的生产过程中，每次变换钢种，烫辊材就会出现窄尺现象，而紧随其后的电工钢板则出现超宽现象。文中针对该问题，介绍了宽度设定模型和宽度自适应模型的原理，阐述了该问题出现的原因及解决方案，并通过对宽度自适应模型的应用研究及优化攻关，有效地解决了问题，大幅提升了实物质量，降低了宽度封锁率。 The rolling strategy of electrical steel was optimized in a factory,and the rough rolling pass was changed from “1+5”to“1+3”.Subsequently,the following problems were occurred in the production process:when the steel grade changed,the roasting roller steel before the electrical steel appeared the narrow width phenomenon,and then the electrical steel appeared the ultra-wide phenomenon.This paper introduced the principle of width setting model and width adaptive model,and expounded the causes and s...