硅钢资料

采用X-射线衍射分析技术测定了取向硅钢热轧板在不同压下率下不同厚度处的织构。结果表明,在压下率低于80%的情况下,几乎所有试样的不同厚度处的织构均为旋转立方织构类型{100}<011>,但不同压下率、不同厚度处的织构强度存在很大差异;在压下率大于80%的情况下,不同试样的不同厚度处的织构类型发生了变化,其织构类型为旋转立方织构或高斯织构{011}<100>,且当织构类型为旋转立方织构时,织构强度存在很大差异,而当织构类型为高斯织构时,织构强度差异相对较小。 The texture of the grain oriented silicon steel hot rolled plate at different compressibility has been measured.The experimental results have shown that the texture of all samples at different thickness is {100}<011> when the compressibility is below 80%,and its intensity at different compressibility and thickness is difference.The texture of all samples at different thickness is variable when the compressibility is above 80%,it is {100}<011> or {011}<100>,and the intensity of ... 

本发明涉及含Cu无取向硅钢的生产方法，转炉炼钢，真空处理过后连铸成坯；铸坯化学成分：1.0≤Si/Cu≤3.0,3.0≤Si+Cu≤5.5％，S≤0.0015％，(Mn+Cu)/S≥3000，其他为Fe,Als,P以及不可避免的杂质元素；对铸坯进行粗轧；粗轧后的中间坯采用热卷机进行强制卷取，开卷后中间坯进入保温箱，控制保温箱内冷却速度≤5℃/s；进入保温箱的中间坯温度T1满足：1000‑(Si+Cu)×103≤T1≤1100‑(Si+Cu)×103；高压除鳞，精轧，层流冷却，卷取；连续酸洗；冷轧到目标厚度，成品退火，涂层；成品卷进行时效处理。成品卷具有较低的中高频铁损，高磁感和高屈服强度。

本文中简要介绍了武汉钢铁有限公司采用薄板坯连铸连轧CSP(compact strip production, CSP)工艺生产中低牌号无取向硅钢的实践情况.CSP工艺生产的硅钢具有成品磁性均匀、板形好的优势，但是在利用该技术生产中低牌号无取向硅钢时，常存在成品板表面瓦楞状缺陷严重、连铸生产效率低等问题.通过优化炼钢成分、热轧等相关工艺，可消除热轧板厚度方向中心的粗大形变组织，从源头上避免了粗大{100}<011>纤维组织的出现，消除了瓦楞状缺陷；通过提升冶炼效率和控制钢中夹杂物总量，可优化隧道炉的加热温度与在炉时间，大幅度提升了连铸生产效率，实现了中低牌号无取向硅钢的批量稳定制造，使CSP产线成为中低牌号无取向硅钢热轧板原料的主要供给生产线.如何进一步提升钢水纯洁度、提高连铸生产效率、降低生产成本，以及挖掘该产线生产薄带钢的技术优点，是未来工作的重点. This paper briefly introduces the practice of producing medium and low grade non oriented silicon steel(NGO) with CSP(compact strip production, CSP)technology in Wuhan Iron and Steel Co., Ltd.. This technology has the inherent advantages of uniform magnetic properties and good shape for silicon steel finished strip. However, in the actual production process, there are serious corrugated defects on the surface of silicon steel finished strip, and production efficiency of continuous casting is low... 

电动汽车电机在高速旋转时承受离心力和电磁力的作用,在进行电机转子设计时,既要考虑电磁性能,还要考虑机械性能。对电机转子受力情况进行了综述,分析了转子用电工钢疲劳性能参数的重要性,详细阐述了试样抛光、表面处理、试样的对中和安装对测试结果的影响。 The motor of electric vehicle bears big force for high speed rotors,mainly including centrifugal and electromagnetic forces.The magnetic and mechanical aspects of the electrical steel are crucial to machine design.In this paper,the forces applied on the motor were summarized and importance of fatigue properties was analyzed.The influence of specimen polish,surface treatment,alignment and installation on fatigue testing result were represented in detail. 

本发明公开了一种高磁感取向硅钢高效脱碳退火工艺，主要工艺流程为：炼钢连铸→热轧→酸洗常化→冷轧→脱碳和初次再结晶退火→渗氮处理(低温Hi‑B)→涂覆氧化镁隔离剂→高温退火→拉伸平整退火→涂覆绝缘涂层→精整，低温HiB不同于高温Hi‑B的工艺流程主要是在脱碳退火后增加了渗氮段。本发明在保证产品实物质量不低于现有水平(国内领先水平)的前提下，使Hi‑B钢退火效率达到世界领先，制造成本大幅降低。

一种低温高磁感取向硅钢的热轧方法：经转炉冶炼并浇注成坯；对铸坯加热后进行粗轧：首先确定粗轧减宽量；根据所确定的粗轧减宽量进行粗轧；进行精轧；常规进行下工序。本发明采用低温板坯加热技术，降低了板坯烧损和修炉负担，且边裂发生率比现有技术的不低于18%的基础上能降低5%以上，由此节约资源及降低能耗。

研究了铝和铬元素在无取向电工钢晶粒长大过程中对织构及晶界变化的影响规律。试验结果表明:电工钢在晶粒长大过程中的主要织构组分均为{111}<112>。在晶粒生长期间,不加铝的1号试样中,{111}<112>、{111}<110>织构组分强化,而{100}<001>织构组分弱化;与1号试样相比,在加入0.2%的铝(质量分数,下同)的2号试样中,{111}<112>、{111}<110>织构组分强化(增加)的速率下降,{100}<001>织构组分变化不明显,甚至稍有增加。在含铝的试样中再加入0.3 5%的铬之后(3号试样),{111}<112>{、111}<110>和{100}<001>织构组分的变化规律与1号试样相似,但当电工钢中加入0.72%的铬之后(4号试样),上述3种织构组分的变化规律与2号试样相似。对于在晶粒生长期间持续变化的3种织构组分而言,1号试样的{1 1 1}<112>和{111}<110>织构组分的高(低)取向差角度晶界频率下降(... The effect rule of Aluminm and Chromium on texture and grain boundary transformation in the nonoriented electrical steel during grain growth was investigated.The experimental result shows that the main texture component is {111}<112> in the electrical steel.The {111}<112> and {111}<110> components in specimen 1 without Alumium were strengthened during grain growth whereas {100}<001> component was weakened.But the growth rate of {111}<112> and {111}<110> compon... 

介绍了国内、外电工钢极薄带的生产现状及市场应用的情况,以及典型生产企业的生产规模、产品性能和应用领域,指出扩大高牌号无取向电工钢生产、提高产品质量是目前电工钢发展的迫切要求。 The production situation and market application of ultra thin electrical steel strip at home and abroad were described.The production capability,product property and application area of typical corporation were introduced.The results indicate that the urgency needed of electrical steel development is expanding high-grade non-oriented electrical steel production and improving products quality at present. 

本发明涉及取向硅钢制造技术领域，公开了一种快速判断取向硅钢初次再结晶晶粒直径的方法，包括如下步骤：选取取向硅钢热轧来料，进行生产，对产出的钢板在同部位各取若干个拉伸试样，加工拉伸和分析，取得屈服强度，在拉伸试样部位两侧连续制取金相试样，计算对应拉伸试样的平均晶粒直径D，将性能数据和平均晶粒直径进行统计分析，建立屈服强度与晶粒直径的对应关系，实际生产时，在产出的钢板上取判断试样，取得判断试样的屈服强度，进而取得判断试样的晶粒直径。本发明快速判断取向硅钢初次再结晶晶粒直径的方法，通过机械性能检验，来间接指示初次晶粒的大小，检测速度快，评价更准确。

本发明公开了一种适用于无取向硅钢极薄带表面涂覆的涂液，它由水溶性丙烯树脂、成膜助剂、耐盐雾助剂、流平剂、纳米氢氧化锆、消泡剂、水按质量比100:(2～8):(1～3):(1～5):(0～1):(0.1～0.5):(70～130)组成。将该涂液在无取向硅钢极薄带表面可表现出良好的涂覆性，经烘烤固化后形成的绝缘涂层表面透明光滑，附着性和绝缘性能优良，可有效提升无取向硅钢极薄带的综合性能，适合推广应用。

【作者】 康凌晨； 王丽娜； ...

阐述了电工钢在\"双碳\"中的作用,强调了电工钢的生产工艺技术及在减少碳排放、降低能耗中的作用,对下游能效升级带来明显的节能及降碳成果。同时,分析了2021年电工钢的生产运行情况,介绍了电工钢的未来发展,并针对如何减少碳排放以及生产更多的更低铁损、更高磁感的电工钢谈了几点启示。 The effects of electrical steels on carbon peak and carbon neutralization were expounded,especially on the achievements of obvious energy saving and carbon reduction to the downstream energy efficiency upgrading bringing from the production technology of electrical steels and their effects to reducing carbon emission and energy consumption.Meanwhile the production situation of electrical steels in 2021 was analyzed,and the future development of electrical steels was introduced,and some advices w...