硅钢资料

采用X-射线衍射分析技术测定了取向硅钢热轧板在不同压下率下不同厚度处的织构。结果表明,在压下率低于80%的情况下,几乎所有试样的不同厚度处的织构均为旋转立方织构类型{100}<011>,但不同压下率、不同厚度处的织构强度存在很大差异;在压下率大于80%的情况下,不同试样的不同厚度处的织构类型发生了变化,其织构类型为旋转立方织构或高斯织构{011}<100>,且当织构类型为旋转立方织构时,织构强度存在很大差异,而当织构类型为高斯织构时,织构强度差异相对较小。 The texture of the grain oriented silicon steel hot rolled plate at different compressibility has been measured.The experimental results have shown that the texture of all samples at different thickness is {100}<011> when the compressibility is below 80%,and its intensity at different compressibility and thickness is difference.The texture of all samples at different thickness is variable when the compressibility is above 80%,it is {100}<011> or {011}<100>,and the intensity of ... 

本发明公开了一种消除取向硅钢单边浪缺陷的方法，其包括如下步骤：1)、制作专用盖板；所述专用盖板包括环形板，所述环形板外边缘设有多个剪开处；2)、将待装炉的取向硅钢钢卷吊运至高温退火炉炉台；3)、将专用盖板铺于取向硅钢钢卷上端面外圈；4)、将专用盖板上的各剪开处向下弯折，勾住取向硅钢钢卷外沿；5)、扣上内罩，内罩底边砂封；6)、钢卷进炉，完成高温退火过程。本发明能有效保护钢卷边部，防止钢卷上端面翻边；该方法还能将钢卷内部水分排出，避免钢带表面氧化。

采用EBSD技术研究了有、无拉应力作用下无取向硅钢在晶粒长大过程中织构转变及晶界变化的规律。结果表明:在晶粒生长期间,无应力作用下的硅钢中,{111}〈112〉,{111}〈110〉织构组分强化,而{100}〈001〉织构组分弱化;与无拉应力作用下的情况相比,施加5MPa的拉应力时,{111}〈112〉,{111}〈110〉织构组分强化的速率下降,{100}〈001〉织构组分变化不明显。对于在晶粒生长期间持续变化的{111}〈112〉,{111}〈110〉和{100}〈001〉织构组分而言,虽然有、无拉应力作用下硅钢的{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率均下降,而{100}〈001〉织构组分的高取向差角度晶界频率则上升,但当有拉应力作用后,{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率下降的速率变小,{100}〈001〉织构组分的高取向差角度晶界频率上升的速率稍有变小。通过对无取向硅钢在晶粒长大过程中织构转变及晶界变化规律的研究,分析了合金原子在晶界的偏聚行为。 The rules of texture and grain boundary transformation in the nonoriented silicon steel under applied stress or without applied stress during grain growth were investigated by EBSD.The results show that the {111}〈112〉 and {111}〈110〉 components in the nonoriented silicon steel without stress are strengthened during grain growth whereas {100}〈001〉 component is weakened,but the growth rate of {111}〈112〉 and {111}〈110〉 component decreases,while the area fraction of {100}〈001〉 component doesn’t chang... 

介绍了国内、外电工钢极薄带的生产现状及市场应用的情况,以及典型生产企业的生产规模、产品性能和应用领域,指出扩大高牌号无取向电工钢生产、提高产品质量是目前电工钢发展的迫切要求。 The production situation and market application of ultra thin electrical steel strip at home and abroad were described.The production capability,product property and application area of typical corporation were introduced.The results indicate that the urgency needed of electrical steel development is expanding high-grade non-oriented electrical steel production and improving products quality at present. 

【机构】 武汉钢铁学院轧钢七二级电工钢结业小组； ...

利用X-射线衍射织构分析和线形分析技术测定了交叉轧制双取向硅钢在制备工艺各阶段的织构及微结构,进而探讨了立方织构({100}<001>)的形成过程。通过对实验结果的分析可知,二次冷轧和交叉轧制工艺为立方织构提供了内能优势和有利的形变织构,而低温预退火工艺既强化了立方织构的内能优势,又为立方织构的异常长大提供了有利的组织保证,最终在抑制剂(AlN和MnS)的协同作用下,硅钢在二次再结晶退火后形成了强烈的立方织构。 The texture and substructure of the double oriented electrical steels produced by the cross rolling technology during the difference process has been measured by means of the X-ray texture and diffraction peak profile analysis technology,and research the formation mechanism of cube texture,{100}<001>.The results show that the dominances of inner energy and deformation texture were supplied by secondary cold rolling and the cross rolling technology and strengthened by pre-annealing at a low... 

研究了应用电感耦合等离子体质谱(ICP-MS)同时测定硅钢中痕量铝、钼、钒、钛、铌元素的分析方法。通过条件试验对测量参数进行了优化,确定RF功率1 400 W,泵速30rpm,采样深度140,雾化压力0.90。样品采用硝酸分解,以Be、Y混合内标校正了测量过程中高基体引起的信号漂移。根据测量时存在的质谱干扰情况,选择同位素27 Al、98 Mo、51 V、47 Ti和93 Nb作为测定同位素,同时通过调节仪器参数使得双电荷离子和氧化物离子的产率最低,以减少其带来的干扰。采用基体匹配法配制校准溶液,以标准加入法建立工作曲线,并扣除试剂空白。该方法各元素的测定下限均可达到1μg/g。用于硅钢标准样品的测定,所得结果与参考值完全吻合,各元素的RSD小于5.2%。 A method for the determination of trace aluminum,molybdenum,vanadium,titanium and niobium in silicon steel by inductively coupled plasma mass spectrometry(ICP-MS) was described.A series of single parameter condition experiment was conducted.The optimized operation parameters with RF power 1 400 W,turbo pump rate 30 rpm,sampling depth 140 and nebulizer pressure 0.90 were obtained.The samples were dissolved by HNO3,and the Be and Y mixing internal standard were used to eliminate the signal drift c... 

一种使铋收得率不低于70%的含铋取向硅钢冶炼方法，其步骤：常规转炉冶炼并出钢至钢包中；RH精炼处理，其间：控制渣层厚度不低于45mm，且渣成分在：Al2O3：25～35wt%，CaO：40～50wt%，MgO:10～15wt%，且结束时钢水温度控制在1530～1590℃；真空精炼结束后进行镇静；后将铋颗粒与石灰石颗粒混装容器加入钢水中；保护浇注和后工序生产。本发明将铋颗粒与石灰石颗粒混合加入，石灰石在钢液中分解产生的气体不仅可以减缓铋颗粒下沉速度，使铋能够快速扩散均匀，更主要的是还可以强化铋颗粒在钢液中的扩散，最终可获得铋收得率高于70%即在71～75%的理想效果。

一种取向硅钢环形炉钢卷冷却装置，涉及冶金领域。该取向硅钢环形炉钢卷冷却装置用于控制环形炉的冷却一段内钢卷的冷却速度，其包括设于冷却一段的炉体内耐火层和绝热层之间的至少一块冷却板及多条设于绝热层内的冷却管，冷却管与一块冷却板贴合接触，冷却管设有用于控制流量的流量控制阀，绝热层还连接有贯穿其以对冷却板的温度进行检测的第一热电偶。本申请提供的取向硅钢环形炉钢卷冷却装置可满足不同品种和规格取向硅钢对冷却速度的要求，能够在满足出炉钢卷板形质量要求基础上减少钢卷在冷却一段的处理时间，提高环形炉的生产效益，同时能够减轻因钢卷重量波动、台车空装等因素对钢卷磁性能和板形质量的影响。

【机构】 武钢研究院； ...

本发明涉及取向硅钢制造技术领域，公开了一种快速判断取向硅钢初次再结晶晶粒直径的方法，包括如下步骤：选取取向硅钢热轧来料，进行生产，对产出的钢板在同部位各取若干个拉伸试样，加工拉伸和分析，取得屈服强度，在拉伸试样部位两侧连续制取金相试样，计算对应拉伸试样的平均晶粒直径D，将性能数据和平均晶粒直径进行统计分析，建立屈服强度与晶粒直径的对应关系，实际生产时，在产出的钢板上取判断试样，取得判断试样的屈服强度，进而取得判断试样的晶粒直径。本发明快速判断取向硅钢初次再结晶晶粒直径的方法，通过机械性能检验，来间接指示初次晶粒的大小，检测速度快，评价更准确。

运用电子背散射衍射(EBSD)和X射线衍射(XRD)技术对硅钢热轧板的织构在板厚方向的分布进行了研究,并分析了两种织构测量方法的特点。EBSD技术能直观给出板厚方向的微观织构,XRD能得到钢板的宏观统计织构信息,结合两种技术的分析,能更直观更精确的研究不同织构在板厚方向的分布。 The texture distribution along the thickness of the silicon steel has been investigated by electron backscatter diffraction(EBSD) and X-ray diffraction(XRD) technique.The characteristics of two technique of texture analysis have been investigated.Combined the two techniques,the texture distribution along the thickness of the silicon steel could be realized distinctly and accurately.