【作者】 康凌晨； 王丽娜； ...

分析了电感耦合等离子体发射光谱法(ICP-AES)测定硅钢中铌的检测过程,讨论了该检测过程中不确定度的主要来源,建立了该方法的定量的数学模型,并根据这一模型计算出了检测结果的合成标准不确定度和扩展不确定度。 The measurement of niobium content in silicon steel by inductively coupled plasma atomic emission spectrometry(ICP-AES) was analyzed,by which the main factors affecting the uncertainty of the measurement were ascertained and the calculation formula was given.Finally,according to the formula the combined uncertainty and expanded uncertainty were obtained. 

通过对激光粒度分析仪测量硅钢级氧化镁(MgO)的分析条件进行优化,如分散介质、分散方式、样品预处理、仪器暗淡度等,探讨了硅钢级MgO粒度范围测量重现性较好的试验方法,满足硅钢生产过程控制对MgO粒度的要求。 The analysis condition of the laser particle size analyzer on grain oriented silicon-steel grade magnesium oxide is optimized,including the dispersion medium,dispersion methods,sample preparation,and instrument obscuration,etc.Therefore,particle size measurement with good reproducibility for silicon-steel magnesium oxide is discussed,which may meet the requirement of MgO particle size for silicon-steel process control. 

本发明公开了一种改善取向硅钢内外圈和边部表面质量的方法及环形炉，在一次冷轧工序中，采用错边卷曲，卷曲张力按渐变张力进行控制且头尾的卷曲张力大、中部的卷曲张力小，MgO的涂覆量与卷曲张力同步变化且头尾的涂覆量少、中部的涂覆量多；在高温退火工序中，环形炉的底板上增设一层由若干扇形块绕中心均布形成的垫层，相邻扇形块之间存在空隙，环形炉的内罩内钢卷的上端加盖通风式的盖板，盖板底面的内圈间隙伸入钢卷孔、外圈间隙套在钢卷上、中间通过绕中心均布的导流槽支撑在钢卷端面上，导流槽呈螺旋状且入口与盖板内圈上的开口一一对应连通、出口延伸至盖板底面外圈内侧。本发明可显著减少表面缺陷，明显改善表面质量和磁性，操作容易。

本发明涉及含Cu无取向硅钢的生产方法，转炉炼钢，真空处理过后连铸成坯；铸坯化学成分：1.0≤Si/Cu≤3.0,3.0≤Si+Cu≤5.5％，S≤0.0015％，(Mn+Cu)/S≥3000，其他为Fe,Als,P以及不可避免的杂质元素；对铸坯进行粗轧；粗轧后的中间坯采用热卷机进行强制卷取，开卷后中间坯进入保温箱，控制保温箱内冷却速度≤5℃/s；进入保温箱的中间坯温度T1满足：1000‑(Si+Cu)×103≤T1≤1100‑(Si+Cu)×103；高压除鳞，精轧，层流冷却，卷取；连续酸洗；冷轧到目标厚度，成品退火，涂层；成品卷进行时效处理。成品卷具有较低的中高频铁损，高磁感和高屈服强度。

本发明公开了一种可替代高磁感取向硅钢常化退火的热处理方法。该方法包括对所述取向硅钢的铸坯依次进行热轧、酸洗和冷轧，省去了常化酸洗工序中的常化退火工艺。所述热轧工序包括加热、粗轧和精轧过程，所述精轧过程中，热轧板离开精轧机最后一个机架时的温度达到1000～1050℃；或者，所述酸洗工序后，对热轧板进行通电加热至1000～1050℃；然后，对热轧板采用短时通电加热控制冷却速度，通电加热2‑5s使热轧板的温度降至940～960℃。采用该热处理方法得到高磁感取向硅钢常化板等效织构，满足生产高磁感取向硅钢的织构组分条件，其简化了高磁感取向硅钢的制造工艺，降低了生产成本和能耗，提高了生产效率。

一种含Bi高磁感取向硅钢热轧带钢边部质量控制方法：炼钢；连铸；铸坯加热；粗轧，粗轧道次不低于4道次，各道次压下率控制在20~33%；规精轧及进行后工序。本发明通过对热轧工序的控制，能使热轧带钢边部开裂的尺寸降低至不超过5mm，且边部开裂≤2mm比率能达到95%以上，后工序切边量很少甚至无需切边即可进行冷轧，使产品成材率能比现有技术提高2~4%；且由于铸坯加热温度的降低使能耗也随之降低。

采用EBSD技术研究了有、无拉应力作用下无取向硅钢在晶粒长大过程中织构转变及晶界变化的规律。结果表明:在晶粒生长期间,无应力作用下的硅钢中,{111}〈112〉,{111}〈110〉织构组分强化,而{100}〈001〉织构组分弱化;与无拉应力作用下的情况相比,施加5MPa的拉应力时,{111}〈112〉,{111}〈110〉织构组分强化的速率下降,{100}〈001〉织构组分变化不明显。对于在晶粒生长期间持续变化的{111}〈112〉,{111}〈110〉和{100}〈001〉织构组分而言,虽然有、无拉应力作用下硅钢的{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率均下降,而{100}〈001〉织构组分的高取向差角度晶界频率则上升,但当有拉应力作用后,{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率下降的速率变小,{100}〈001〉织构组分的高取向差角度晶界频率上升的速率稍有变小。通过对无取向硅钢在晶粒长大过程中织构转变及晶界变化规律的研究,分析了合金原子在晶界的偏聚行为。 The rules of texture and grain boundary transformation in the nonoriented silicon steel under applied stress or without applied stress during grain growth were investigated by EBSD.The results show that the {111}〈112〉 and {111}〈110〉 components in the nonoriented silicon steel without stress are strengthened during grain growth whereas {100}〈001〉 component is weakened,but the growth rate of {111}〈112〉 and {111}〈110〉 component decreases,while the area fraction of {100}〈001〉 component doesn’t chang... 

在50Kg氧化镁坩埚真空感应炉上进行高硅电工钢的脱氧试验。结果表明,通过控制原料的成分、高真空下的碳氧反应和炉衬分解向钢液中的供氧,可使钢液的总氧含量≤15×10-6;在维持高温高真空条件下,当钢液中的反应达到一定程度后,延长精炼时间并不能降低钢液的总氧含量;完成精炼后加入硅钙合金沉淀脱氧可进一步降低钢液的总含氧量,但脱氧效果有限。 The test of high-silicon electric steel deoxidation has been carried out in 50Kg vacuum induction furnace with magnesium oxide crucible.Results show that the total oxygen could be ≤15×10-6in molten steel by controlling material components,carbon-oxygen reaction in high vacuum and oxygen contamination from crucible materials on molten steel;And when the reaction was carried through to a certain extent,total oxygen in molten steel could not be reduced by the extension of refining period in high va... 

一种提高有效氮和底层质量的高磁感取向硅钢制造方法：冶炼后连铸成坯；对铸坯加热；热轧、常化及酸洗后时效冷轧；在湿式气氛下脱碳退火；在湿式混合气氛下均热；在湿式混合气氛下渗氮退火；进行后工序。本发明与现有技术相比，通过合理控制渗氮过程，提高渗氮后钢板基体内氮含量与总氮量之间的比例达到80%以上，使无点状露晶产生，最终获得产品的底层质量优异。

【作者】 姚昌国； ...

本发明公开了一种消除取向硅钢单边浪缺陷的方法，其包括如下步骤：1)、制作专用盖板；所述专用盖板包括环形板，所述环形板外边缘设有多个剪开处；2)、将待装炉的取向硅钢钢卷吊运至高温退火炉炉台；3)、将专用盖板铺于取向硅钢钢卷上端面外圈；4)、将专用盖板上的各剪开处向下弯折，勾住取向硅钢钢卷外沿；5)、扣上内罩，内罩底边砂封；6)、钢卷进炉，完成高温退火过程。本发明能有效保护钢卷边部，防止钢卷上端面翻边；该方法还能将钢卷内部水分排出，避免钢带表面氧化。