硅钢资料

运用电子背散射衍射(EBSD)和X射线衍射(XRD)技术对硅钢热轧板的织构在板厚方向的分布进行了研究,并分析了两种织构测量方法的特点。EBSD技术能直观给出板厚方向的微观织构,XRD能得到钢板的宏观统计织构信息,结合两种技术的分析,能更直观更精确的研究不同织构在板厚方向的分布。 The texture distribution along the thickness of the silicon steel has been investigated by electron backscatter diffraction(EBSD) and X-ray diffraction(XRD) technique.The characteristics of two technique of texture analysis have been investigated.Combined the two techniques,the texture distribution along the thickness of the silicon steel could be realized distinctly and accurately. 

研究了应用电感耦合等离子体质谱法(ICP-MS)测定硅钢中痕量铜和镍的分析方法。采用硝酸分解样品,通过内标校正和基体匹配消除了基体干扰的影响,同时根据测量时存在的质谱干扰情况,选择同位素65Cu和60Ni作为测定元素和通过调节仪器参数使双电荷离子的产率最低,以减少带来的干扰。该方法用于硅钢中痕量铜和镍的测定,所得的结果与ICP-AES法测定结果完全吻合,各元素测定结果的RSD值小于5%,加标回收率为97.3%～100.3%。 A method for the determination trace copper and nickel in silicon steel by inductively coupled plasma mass spectrometry(ICP-MS) was studied.The samples were dissolved in HNO3.The effect of matrix interference was eliminated by internal standard correction and matrix matching.Meanwhile,according to the mass spectral interferences in determination,the isotopes including 65Cu and 60Ni were used as measuring elements.The yield of double-charge ions were minimized by adjusting instrumental parameters... 

本发明公开了一种提高薄板坯连铸生产高铝无取向硅钢可浇性的方法，在保证生产顺行、质量稳定的基础上，能使高铝无取向硅钢连浇炉数由10炉提高至16炉，在提高小时产量、降低生产成本方面效果显著。

本文中简要介绍了武汉钢铁有限公司采用薄板坯连铸连轧CSP(compact strip production, CSP)工艺生产中低牌号无取向硅钢的实践情况.CSP工艺生产的硅钢具有成品磁性均匀、板形好的优势，但是在利用该技术生产中低牌号无取向硅钢时，常存在成品板表面瓦楞状缺陷严重、连铸生产效率低等问题.通过优化炼钢成分、热轧等相关工艺，可消除热轧板厚度方向中心的粗大形变组织，从源头上避免了粗大{100}<011>纤维组织的出现，消除了瓦楞状缺陷；通过提升冶炼效率和控制钢中夹杂物总量，可优化隧道炉的加热温度与在炉时间，大幅度提升了连铸生产效率，实现了中低牌号无取向硅钢的批量稳定制造，使CSP产线成为中低牌号无取向硅钢热轧板原料的主要供给生产线.如何进一步提升钢水纯洁度、提高连铸生产效率、降低生产成本，以及挖掘该产线生产薄带钢的技术优点，是未来工作的重点. This paper briefly introduces the practice of producing medium and low grade non oriented silicon steel(NGO) with CSP(compact strip production, CSP)technology in Wuhan Iron and Steel Co., Ltd.. This technology has the inherent advantages of uniform magnetic properties and good shape for silicon steel finished strip. However, in the actual production process, there are serious corrugated defects on the surface of silicon steel finished strip, and production efficiency of continuous casting is low... 

目的提高硅钢的磁性能。方法采用多弧离子镀技术,在普通取向硅钢薄板两面沉积高硅FeSi合金层制得高硅梯度硅钢,并进行热处理,观察其显微组织,测量磁性能。结果退火态高硅梯度硅钢表面的高硅FeSi合金层与基底结合紧密,均匀致密。高硅梯度硅钢中硅含量呈梯度分布,最表层硅质量分数为11.0%,随着深度增加,硅含量逐渐降低,在距表面20μm处硅质量分数仍能达到6.5%。沉积态高硅梯度硅钢的电阻率ρ、低频铁损P10/50、高频铁损P10/1k及磁感应强度B8分别为68.6μΩ·cm,0.82W/kg,83.3 W/kg和1.73 T,退火后分别为63.1μΩ·cm,0.44 W/kg,54.38 W/kg和1.89 T。结论由于表层高硅FeSi合金层的存在,梯度高硅钢的低频磁学性能良好,但高频损耗需进一步改善。 Objective To improve the magnetic properties of silicon steel. Methods FeSi alloy coatings with high-silicon content were deposited on the surface of common grain-oriented silicon steel by cathodic arc plasma evaporation,and then a kind of high silicon gradient steel was prepared. The morphologies,content and magnetic properties of the samples were tested. Results FeSi alloy coatings were featured with compact microstructures and excellent adhesive quality with the substrates. The silicon conten... 

本发明公开了一种精确控制高磁感取向硅钢板坯Als含量的方法，转炉出钢20～40秒时，定量加入金属铝，加入量按0.15～0.35kg/吨钢；转炉出钢及合金加入后，底吹搅拌均匀3～5min后，加入一定量金属铝后再底吹搅拌均匀3～5min后将钢水吊运至RH开始精炼处理，铝加入量按[WAls目标+(0.009～0.0120％)]范围控制；钢水在RH精炼过程经过2～3次酸溶铝的成分微调后结束精炼，精炼结束Als按[WAls目标+(0.0030～0.0045％)]目标范围控制；RH精炼结束样酸溶铝检测结果出来后，在连铸开浇前，在钢包内补加铝线使钢液中Als在[WAls目标+Δ浇注Als损]目标范围内；连铸进行氩气环流保护浇注，其中氩气环流流量控制在6～12m3/h；浇注成合格板坯后按正常工艺进行热轧及后工序生产。

本发明涉及一种提高低温高磁感取向硅钢附着性的方法，该方法在现有低温高磁感取向硅钢连续式脱碳退火炉中，通过在脱碳退火前区通入氮气、氢气干式混合气，在脱碳退火后区通入氮气、氢气湿式混合气进行脱碳，在渗氮区通入氮气、氢气湿式混合气及氨气进行渗氮，解决了低温高磁感取向硅钢附着性不好的难题。本发明方法提高了钢中总氧量、增加了氧化层厚度、改善了氧化层结构，经高温退火后生成了致密的硅酸镁底层，附着性大幅提高，测试结果均在C级以上，大部分样品在B级以上。

本发明涉及含Cu无取向硅钢的生产方法，转炉炼钢，真空处理过后连铸成坯；铸坯化学成分：1.0≤Si/Cu≤3.0,3.0≤Si+Cu≤5.5％，S≤0.0015％，(Mn+Cu)/S≥3000，其他为Fe,Als,P以及不可避免的杂质元素；对铸坯进行粗轧；粗轧后的中间坯采用热卷机进行强制卷取，开卷后中间坯进入保温箱，控制保温箱内冷却速度≤5℃/s；进入保温箱的中间坯温度T1满足：1000‑(Si+Cu)×103≤T1≤1100‑(Si+Cu)×103；高压除鳞，精轧，层流冷却，卷取；连续酸洗；冷轧到目标厚度，成品退火，涂层；成品卷进行时效处理。成品卷具有较低的中高频铁损，高磁感和高屈服强度。

本发明公开了一种消除取向硅钢单边浪缺陷的方法，其包括如下步骤：1)、制作专用盖板；所述专用盖板包括环形板，所述环形板外边缘设有多个剪开处；2)、将待装炉的取向硅钢钢卷吊运至高温退火炉炉台；3)、将专用盖板铺于取向硅钢钢卷上端面外圈；4)、将专用盖板上的各剪开处向下弯折，勾住取向硅钢钢卷外沿；5)、扣上内罩，内罩底边砂封；6)、钢卷进炉，完成高温退火过程。本发明能有效保护钢卷边部，防止钢卷上端面翻边；该方法还能将钢卷内部水分排出，避免钢带表面氧化。

一种含Bi高磁感取向硅钢热轧带钢边部质量控制方法：炼钢；连铸；铸坯加热；粗轧，粗轧道次不低于4道次，各道次压下率控制在20~33%；规精轧及进行后工序。本发明通过对热轧工序的控制，能使热轧带钢边部开裂的尺寸降低至不超过5mm，且边部开裂≤2mm比率能达到95%以上，后工序切边量很少甚至无需切边即可进行冷轧，使产品成材率能比现有技术提高2~4%；且由于铸坯加热温度的降低使能耗也随之降低。

【机构】 武汉钢铁学院轧钢七二级电工钢结业小组； ...

在50Kg氧化镁坩埚真空感应炉上进行高硅电工钢的脱氧试验。结果表明,通过控制原料的成分、高真空下的碳氧反应和炉衬分解向钢液中的供氧,可使钢液的总氧含量≤15×10-6;在维持高温高真空条件下,当钢液中的反应达到一定程度后,延长精炼时间并不能降低钢液的总氧含量;完成精炼后加入硅钙合金沉淀脱氧可进一步降低钢液的总含氧量,但脱氧效果有限。 The test of high-silicon electric steel deoxidation has been carried out in 50Kg vacuum induction furnace with magnesium oxide crucible.Results show that the total oxygen could be ≤15×10-6in molten steel by controlling material components,carbon-oxygen reaction in high vacuum and oxygen contamination from crucible materials on molten steel;And when the reaction was carried through to a certain extent,total oxygen in molten steel could not be reduced by the extension of refining period in high va...