硅钢资料

本发明公开了一种高硅钢的冷轧生产工艺。该生产工艺属于机械制造技术领域，其中的处理工序的加热工序通过电磁感应加热装置加热，待处理钢经过加热工序的速度为30‑200mpm，加热工序的加热温度为70‑120℃。本发明具有生产效率高和生产质量高的特点，特别是在加热工序中对待处理钢采用电磁感应加热装置进行加热，使其可以快速有效地提升温度，以满足高硅钢的冷轧生产工艺要求，减少断带事故，具有很好的实用性和创新性。

本发明公开了一种改善取向硅钢内外圈和边部表面质量的方法及环形炉，在一次冷轧工序中，采用错边卷曲，卷曲张力按渐变张力进行控制且头尾的卷曲张力大、中部的卷曲张力小，MgO的涂覆量与卷曲张力同步变化且头尾的涂覆量少、中部的涂覆量多；在高温退火工序中，环形炉的底板上增设一层由若干扇形块绕中心均布形成的垫层，相邻扇形块之间存在空隙，环形炉的内罩内钢卷的上端加盖通风式的盖板，盖板底面的内圈间隙伸入钢卷孔、外圈间隙套在钢卷上、中间通过绕中心均布的导流槽支撑在钢卷端面上，导流槽呈螺旋状且入口与盖板内圈上的开口一一对应连通、出口延伸至盖板底面外圈内侧。本发明可显著减少表面缺陷，明显改善表面质量和磁性，操作容易。

介绍了国内无底层取向电工钢生产技术水平、产量和用途，简述了无底层取向电工钢作为取向电工钢超/极薄带母料及应用于制作大型发电机组铁心、风电等电机铁心和变压器铁心等的情况。 The production technology level,output and application of domestic glassless grainoriented electrical steel were introduced,and the application of glassless grain-oriented electrical steel as parent material of ultra-thin strip of grain-oriented electrical steel and in making large-scale electric generator cores,wind power motor cores and transformer cores were briefly described. 

研究了铝和铬元素在无取向电工钢晶粒长大过程中对织构及晶界变化的影响规律。试验结果表明:电工钢在晶粒长大过程中的主要织构组分均为{111}<112>。在晶粒生长期间,不加铝的1号试样中,{111}<112>、{111}<110>织构组分强化,而{100}<001>织构组分弱化;与1号试样相比,在加入0.2%的铝(质量分数,下同)的2号试样中,{111}<112>、{111}<110>织构组分强化(增加)的速率下降,{100}<001>织构组分变化不明显,甚至稍有增加。在含铝的试样中再加入0.3 5%的铬之后(3号试样),{111}<112>{、111}<110>和{100}<001>织构组分的变化规律与1号试样相似,但当电工钢中加入0.72%的铬之后(4号试样),上述3种织构组分的变化规律与2号试样相似。对于在晶粒生长期间持续变化的3种织构组分而言,1号试样的{1 1 1}<112>和{111}<110>织构组分的高(低)取向差角度晶界频率下降(... The effect rule of Aluminm and Chromium on texture and grain boundary transformation in the nonoriented electrical steel during grain growth was investigated.The experimental result shows that the main texture component is {111}<112> in the electrical steel.The {111}<112> and {111}<110> components in specimen 1 without Alumium were strengthened during grain growth whereas {100}<001> component was weakened.But the growth rate of {111}<112> and {111}<110> compon... 

【机构】 武钢研究院； ...

本发明涉及一种提高低温高磁感取向硅钢附着性的方法，该方法在现有低温高磁感取向硅钢连续式脱碳退火炉中，通过在脱碳退火前区通入氮气、氢气干式混合气，在脱碳退火后区通入氮气、氢气湿式混合气进行脱碳，在渗氮区通入氮气、氢气湿式混合气及氨气进行渗氮，解决了低温高磁感取向硅钢附着性不好的难题。本发明方法提高了钢中总氧量、增加了氧化层厚度、改善了氧化层结构，经高温退火后生成了致密的硅酸镁底层，附着性大幅提高，测试结果均在C级以上，大部分样品在B级以上。

通过对激光粒度分析仪测量硅钢级氧化镁(MgO)的分析条件进行优化,如分散介质、分散方式、样品预处理、仪器暗淡度等,探讨了硅钢级MgO粒度范围测量重现性较好的试验方法,满足硅钢生产过程控制对MgO粒度的要求。 The analysis condition of the laser particle size analyzer on grain oriented silicon-steel grade magnesium oxide is optimized,including the dispersion medium,dispersion methods,sample preparation,and instrument obscuration,etc.Therefore,particle size measurement with good reproducibility for silicon-steel magnesium oxide is discussed,which may meet the requirement of MgO particle size for silicon-steel process control. 

采用X-射线衍射分析技术测定了取向硅钢热轧板在不同压下率下不同厚度处的织构。结果表明,在压下率低于80%的情况下,几乎所有试样的不同厚度处的织构均为旋转立方织构类型{100}<011>,但不同压下率、不同厚度处的织构强度存在很大差异;在压下率大于80%的情况下,不同试样的不同厚度处的织构类型发生了变化,其织构类型为旋转立方织构或高斯织构{011}<100>,且当织构类型为旋转立方织构时,织构强度存在很大差异,而当织构类型为高斯织构时,织构强度差异相对较小。 The texture of the grain oriented silicon steel hot rolled plate at different compressibility has been measured.The experimental results have shown that the texture of all samples at different thickness is {100}<011> when the compressibility is below 80%,and its intensity at different compressibility and thickness is difference.The texture of all samples at different thickness is variable when the compressibility is above 80%,it is {100}<011> or {011}<100>,and the intensity of ... 

一种适合冷连轧的高效变频压缩机用无取向硅钢，其化学成分及wt%为：C：≤0.0025%、Si：2.4~2.8%、Mn：0.35~0.65%、Al：0.5~0.8%、S：≤0.0020%、N：≤0.0025%、P：≤0.03%、Sb或Sn：0.03~0.08%；生产方法：冶炼浇注；对铸坯加热；粗轧；精轧；卷取；常化；经酸洗后冷连轧；退火；涂敷及精整。本发明产品性能既保证产品磁性能又提高生产效率、提高成材率和降低生产成本的效果，五机架连轧机只需要一次轧过即可，且连轧机相比单机架轧机减少了来回轧制的带头带尾切废量，因而可提高成材率，生产效率和成材率提高，自然降低生产成本。

研究了应用电感耦合等离子体质谱(ICP-MS)同时测定硅钢中痕量铝、钼、钒、钛、铌元素的分析方法。通过条件试验对测量参数进行了优化,确定RF功率1 400 W,泵速30rpm,采样深度140,雾化压力0.90。样品采用硝酸分解,以Be、Y混合内标校正了测量过程中高基体引起的信号漂移。根据测量时存在的质谱干扰情况,选择同位素27 Al、98 Mo、51 V、47 Ti和93 Nb作为测定同位素,同时通过调节仪器参数使得双电荷离子和氧化物离子的产率最低,以减少其带来的干扰。采用基体匹配法配制校准溶液,以标准加入法建立工作曲线,并扣除试剂空白。该方法各元素的测定下限均可达到1μg/g。用于硅钢标准样品的测定,所得结果与参考值完全吻合,各元素的RSD小于5.2%。 A method for the determination of trace aluminum,molybdenum,vanadium,titanium and niobium in silicon steel by inductively coupled plasma mass spectrometry(ICP-MS) was described.A series of single parameter condition experiment was conducted.The optimized operation parameters with RF power 1 400 W,turbo pump rate 30 rpm,sampling depth 140 and nebulizer pressure 0.90 were obtained.The samples were dissolved by HNO3,and the Be and Y mixing internal standard were used to eliminate the signal drift c... 

一种提高有效氮和底层质量的高磁感取向硅钢制造方法：冶炼后连铸成坯；对铸坯加热；热轧、常化及酸洗后时效冷轧；在湿式气氛下脱碳退火；在湿式混合气氛下均热；在湿式混合气氛下渗氮退火；进行后工序。本发明与现有技术相比，通过合理控制渗氮过程，提高渗氮后钢板基体内氮含量与总氮量之间的比例达到80%以上，使无点状露晶产生，最终获得产品的底层质量优异。