硅钢资料

本发明提供一种超低铝无取向硅钢夹杂物控制方法。该钢种化学成分质量百分比为C≤0.005％，Si：0.25％‑1.50％，Mn：0.15％‑0.55％，P：0.02％‑0.06％，S≤0.005％，Als≤0.005％，余量为Fe及不可避免的杂质。工艺流程为：KR→BOF→RH→连铸。转炉出钢严格控制下渣量，出钢结束加石灰、渣面脱氧剂调渣；RH脱碳结束后，先加低碳低硫硅铁、金属铝或铝钙铁合金复合脱氧，最后加入金属锰、磷铁进行合金化，然后净循环6‑10min，破空出钢运至连铸浇注。得到钢水中主要为SiO2‑Al2O3系夹杂，避免了生成低熔点SiO2‑MnO系夹杂，轧制延展变长，影响晶粒长大；同时也避免了生成高SiO2组分类酸性夹杂，导致耐材的侵蚀。可显著改善钢中非金属夹杂物类型，提高无取向硅钢的性能，并提高了钢水浇注性能。

利用光学显微镜、TEM和EBSD研究了退火温度对双辊连铸无取向硅钢再结晶组织的影响。结果表明,900℃退火后组织分布不均匀,有大量带状组织,平均晶粒尺寸29.5μm。提高退火温度,晶粒尺寸增大,组织均匀化程度增加,1050℃退火时,带状组织基本消失,平均晶粒尺寸42.2μm。 Effect of annealing temperature on recrystallization microstructure of non-oriented electrical steel produced by twin-roll casting process was investigated using OM,TEM and EBSD.The results show that the recrystallization microstructure is uneven because of many banded grains existing,average grain size is 29.5 μm.With annealing temperature increasing,the recrystallization grain size increases,microstructure becomes more homogeneous.When 1050 ℃ annealing,the banded structure almost disappear and... 

本实用新型公开了一种用于硅钢板带加工的整平装置，包括底座，所述底座的上表面固定设有下安装座，所述下安装座上设有下整平机构，所述底座的上表面固定连接有门型安装架，所述门型安装架的顶部贯穿设有螺杆，所述螺杆的底面设有上安装座，所述上安装座的正面通过轴承座转动连接有第三转轴，所述第三转轴的外表面固定连接有调向齿轮，所述上安装座上设有上整平机构。本实用新型通过设置通过设置多组上整平辊和下整平辊，改善该装置的整平效果，且通过转动齿轮与调向齿轮的设置，使该装置的多个上整平辊同步转动，且相邻两个整平辊之间的间隙可以设置的较小，使该装置结构紧凑，提高空间利用率。

本发明公开了一种超薄取向硅钢用的半有机绝缘涂料。该半有机绝缘涂料，按质量百分比计，包括以下组分：10～25％磷酸盐，1～10％含有环氧基的硅烷耦合剂，0.2～2.0％有机硅烷，1～10％铬酐，1.5～6％二氧化硅粒子，0.3～5％碱，余量为水；其中二氧化硅粒子的粒径为100～300nm。该半有机绝缘涂料应用于超薄取向硅钢表面时，既提高了涂层与基体的附着性，又保证了涂层的绝缘性和耐热性，涂层附着性为A级，叠片系数大于0.96，可耐900℃高温，并且涂层较薄(小于1μm)时，钢板的绝缘电阻大于30Ω·cm2/片，绝缘性能优异，可满足超薄取向硅钢的应用需求。

借助电子背散射衍射(EBSD)及ZEISS-200MAT金相显微镜对某钢厂普通取向硅钢(CGO)进行研究,研究结果表明:热轧板组织、织构沿板厚方向存在明显的不均匀性,在热轧板表层及次表层发生再结晶,同时存在强度较高的Goss织构,中心层存在较强的{001}<110>变形织构。冷轧组织均呈纤维状条带组织,一次冷轧后,热轧板中的Goss织构消失,织构主要为α、γ织构,经中间脱碳退火后,α、γ织构强度减弱,并出现一定强度的Goss织构和利于Goss织构发展的{554}<225>、{332}<113>等织构,经二次冷轧后,二次冷轧织构类型与一次冷轧织构一致,但织构强度不同。 The grain-oriented silicon steel produced by a steel factory was investigated by EBSD and ZEISS-200 MAT metallographic microscope.The results show that the textures and microstructures along thickness of hot rolled slab are inhomogeneous.The surface layer and the layer near that are recrystallized structure which has a high Goss texture,but there is deformation texture{001}<110>in the central layer.The structure after cold rolling is a structure like fiber strip.After the first cold rollin... 

本发明涉及无取向硅钢技术领域，具体提供了一种无取向硅钢的制备方法，对再结晶率为70‑90％、平均晶粒尺寸为10‑15μm、硬度HV为140‑170的硅钢半成品在温度为T＝(772～777)+2900×W(Si)的条件下进行去应力退火，制得无取向硅钢，晶粒在去应力退火过程中均匀长大，平均晶粒尺寸80μm以上，有效降低铁损，使磁性能大幅度提高，铁损P1.5/50≤3.5W/kg，磁感B5000≥1.72T，电磁性能优异，满足客户使用要求，此外，本发明采用的硬度HV为140‑170的硅钢半成品在冲压过程中不易变形，机械加工性能优良。

分析了高转矩和高转速条件下高效驱动马达铁芯材料对无取向硅钢磁性能要求,讨论了无取向硅钢的高磁通密度和低铁损对电机转矩和效率的影响,介绍了国内外高磁感无取向硅钢发展情况。在生产工艺上,提高钢质纯净度,弱化夹杂物和第二相粒子对畴壁移动和再结晶晶粒长大的钉扎作用,添加微量晶界和带钢表面的偏析元素促使有利织构发展等技术可提高无取向硅钢的磁通密度。 The requirements of high efficient drive motor core materials under the conditions of high torque and high speed were analyzed.The effects of high magnetic flux density of non-oriented silicon steel on the torque and efficiency of the motor were discussed.The development of non-oriented silicon steel with high magnetic was introduced.The magnetic flux density of non-oriented silicon steel sheet can be obviously improved by some production technologies,such as purification steel,weakening the pin... 

此无取向性电磁钢板具有预定的化学组成，所述化学组成满足(2×[Mn]+2.5×[Ni]+[Cu])－([Si]+2×[sol.Al]+4×[P])≧1.50％，以SEM－EBSD测定距表面1/2板厚深度的与轧制面平行的面时，将{hkl}＜uvw＞取向的晶粒相对于全部视野的面积率记为Ahkl－uvw时，A411－011在15.0％以上，且平均晶体粒径为50μm～150μm。

本实用新型公开了一种硅钢片分流导料机构，属于硅钢片导料领域，包括传送带，所述传送带包括主带和副带，所述副带设置在主带的前面，所述主带横向设置，所述主带的后面设置有导流机构，所述导流机构包括电机、导流板和助力组件，所述主带的后面设置有安装架，所述安装架的顶部竖向固定连接有连接板，所述电机安装在连接板上，所述电机的输出轴与导流板的顶部固定套接，通过启动电机，电机带动导流板旋转，导流板在连接组件下带动助力组件旋转，使得主带上的物品被导流板进行阻挡，通过助力组件传送到副带上，避免了传送带方向单一，容易导致硅钢片对堆积的问题，从而减少硅钢片的损坏量，进而节约成本。

本发明公开了一种控制无取向硅钢边部黑线的生产方法，涉及硅钢轧制工艺领域。本发明提供的方法缩小加热区的装钢间距，降低粗轧冷却水量，并减小R1第一道次侧压量，增大R2末道次立辊侧压量，调整精轧区侧导板和卷取区侧导板的开口度，减少或消无取向硅钢边部黑线。本发明提供的生产方法控制了热轧卷边部翘皮黑线问题，将热轧卷出现边部黑线的概率由之前的60%以上降低至现在的3%以下，热轧及冷轧卷的表面质量得到了明显提升，酸洗裁剪量减小，成材率明显提升，冷轧过程的轧制稳定性也明显提升。

本实用新型公开了一种薄带取向电工钢的热处理炉板，炉板的中心设置有气流循环通孔，炉板的硅钢卷预定压接面设置有通气槽，炉板内设置有进气孔，进气孔的第一孔口设置于通气槽中，进气孔的第二孔口设置于炉板的侧壁上。该薄带取向电工钢的热处理炉板在设置通气槽的基础上，进一步设置进气孔，通过向进气孔中导入气流，增加通气槽的进气量，有助于硅钢卷与炉板压接侧边处水蒸气的及时排出，进一步提高卷内硅钢的热处理品质。本实用新型还公开了一种包含热处理炉板的薄带取向电工钢罩式炉。

结合扫描电镜和大样电解研究了CSP流程W800牌号无取向电工钢表面线状缺陷中夹杂物成分及来源，采用SPSS软件回归分析了生产过程各因素对表面线状缺陷的影响。研究表明：稳态浇铸过程铸坯中大型夹杂物含量为5.39 mg/10 kg。引起无取向电工钢表面线状缺陷的大型夹杂物主要为脱氧产物、镁铝尖晶石和钢包顶渣，主要类型为Al₂O₃、MgO-Al₂O₃、CaO-Al₂O₃-MgO和CaO-Al₂O₃-SiO₂。非稳态浇铸过程钢水洁净度明显降低，热轧板表面线状缺陷比例上升。影响表面线状缺陷的主要因素为RH出站时顶渣的w（CaO）/w（Al₂O₃）、RH脱氧结束氧位及中间包最低吨位。 Combining scanning electron microscopy and large sample electrolysis, the composition and source of inclusions in the surface linear defects of W800 grade non-oriented electrical steel in the CSP process were studied. SPSS software was used to regress and analyze the main factors which affected the surface linear defects in the steelmaking process. Research shows that the content of large inclusions in the steady state casting process is 5.39 mg/10 kg. The large inclusions which cause linear def...