从影响高牌号无取向硅钢退火工艺的主要参数入手,介绍高牌号无取向硅钢退火炉在加热、气氛控制、冷却、涂层烘烤方面的新技术,并展望无取向硅钢退火炉的发展方向。 Based on the technology parameters of high-grade non-oriented silicon steel annealing,the new technology of the annealing line,which includes heating,atmosphere control,cooling,coating baking,is introduced,and the development direction of non-oriented silicon steel annealing furnace is pointed out. 

概述了高磁感取向硅钢生产工艺的研究现状及发展趋势。介绍了国内外薄板坯连铸连轧流程生产高磁感取向硅钢的研究现状。从流程工序特点、热履历、组织与抑制剂控制方面进行对比,分析了薄板坯连铸连轧流程相对传统板坯流程生产高磁感取向硅钢的技术优势,在此基础上提出了利用该流程生产高磁感取向硅钢需要解决的主要技术难点。 The current status and development trend of production process for high magnetic induction grain-oriented silicon steel are summarized.The research status of producing high magnetic induction grain-oriented silicon steel by thin slab casting and rolling process at home and abroad is introduced.The potential technical advantages of producing high magnetic induction grain-oriented silicon steel by thin slab casting and rolling process are obtained by analyzing in terms of process characteristics,t... 

为了弄清楚高硫硅钢中的硫化物析出行为及其对钢的微观组织和电磁性能的影响，以便为工业化生产制定更为合理的硫含量控制标准和采取更为有效措施减轻炼钢生产的硫含量控制压力，结合0.25% Si 无取向硅钢 ，采用非水溶液电解提取 + 扫描电镜/透射电镜观察相结合的方法 ，研究了0.006 8%、0.010 2%、0.025 5% 和 0.035 3% 硫含量条件下，钢中的硫化物夹杂物组成和存在形式及其形貌、种类、尺寸、数量变化，以及相应的热轧、成品试样的微观组织和电磁性能变化。结果表明，随着钢中硫含量的增加，钢中的硫化物逐渐由 MnS→MnS+Cu₂S→Cu₂S转变，数量逐渐增多，尺寸向高低两个方向发展。相应地，导致热轧再结晶组织劣化和抑制了成品晶粒尺寸长大。随着钢中硫含量的增加，钢的磁感、铁损劣化程度逐渐增大。钢中的硫含量平均每增加 0.01%，涡流损耗、磁滞损耗分别劣化0.24 W/kg 和 0.41 W/kg，而磁感会劣化 0.009 T。但是 ，在硫含量为 0.010 2% 时 ，铁损可以低于 6.0W/kg，而在硫含量为 0.025 5% ... In order to find out the precipitation behavior of sulfide inclusions and the corresponding changes of microstructure and electromagnetic properties of high sulfur silicon steel sheets, so that to design more suitable sulfur concentration controlling limit for industrial manufacture and to release the steel-making difficulty effectively, Based on the change of given sulfur concentration 0.006 8%, 0.010 2%0.025 3% and 0.035 3%, the type and composition, the size and number, and the size distribut... 

本实用新型公开了一种硅钢卷上料装置，包括两支撑台和设置在两支撑台之间的输送组件，所述输送组件包括轨道和设置在轨道上的输送件，所述输送件包括滑板、支撑板、承重板和气缸，所述轨道平行于两支撑台设置在两支撑台之间，所述滑板可滑动设置在轨道上，所述支撑板通过气缸可升降设置在滑板上，所述承重板设置在支撑板上，所述承重板的截面呈U型，其上设置有第二缓冲条。其可实现硅钢卷的轻松上料，省时省力的同时，安全性大大提高。

本实用新型公开了一种实验室模拟硅钢带连续常化退火炉，属于热处理技术领域。该退火炉包括：炉膛，沿退火炉本体的长度方向贯通，所述炉膛的两端的开口处设有炉门，炉门上设有透气孔，炉膛内自左向右依次分为多个加热区；滑轨，沿炉膛的长度方向设于所述炉膛的底部；移动机构，设在滑轨上且能沿滑轨移动；牵引绳，由耐高温材料制成，其一端与移动机构连接，另一端延伸至退火炉本体的外部；牵引绳收放机构，设于退火炉本体的外部，并与牵引绳的外端连接，用于收放牵引绳。本实用新型的退火炉采用三段加热区域，独立控温，能够模拟硅钢带预热、加热、均热、冷却等连续常化工艺，实验条件更接近工业生产。

两炉次无取向硅钢XG800WR（/%:0.003～0.004C、0.71～0.75Si、0.32～0.33Mn、0.004～0.007S、0.016P）的炼钢流程为铁水预处理（KR）-210 t顶底复吹转炉-钢包吹氩-RH脱碳精炼-230mm×1220 mm板坯连铸。53 t中间包钢水过热度为25～30℃,钢包到中间包采用长水口全程吹氩保护浇铸,中间包至结晶器采用浸入式水口浇铸。结果表明,在RH、中间包、结晶器过程中钢中总氧以及夹杂物数量和尺寸均明显降低;但在钢包到中间包过程T[O]、[N]和钢中夹杂物数量增加,说明长水口浇铸过程存在二次氧化。连铸坯中T[O]、[N]平均他分别为11×10^-6和30×10^-6,显微夹杂物数量平均为4个/mm²。铸坯中的显微夹杂物主要为3～5μm的AlN,同时存在少量的MnS、Al₂O₃·AlN和Al₂O₃·MgO·MnS。 The steelmaking flow sheet for two heats non-oriented silicon steel XG800WR（/%:0.003～0.004C. 0.71～0.75Si,0.32～0.33Mn,0.004～0.007S,0.016P） is hot metal pretreatment（KR）-210 t top and bottom combined blown converter-ladle argon blowing-RH decarburization refining-230 mm×1 220 mm slab casting.The superheating extent of liquid in 53 t tundish is 25～30℃,whole casting is shielded by blowing argon with long nozzle from ladle to tundish and the submerged nozzle is adopted in casting from tundish to mold... 

本实用新型提供了一种变压器硅钢片吊装工具，属于变压器技术领域。其技术方案为：一种变压器硅钢片吊装工具，包括勾体，所述勾体上端设置有吊环，所述勾体下端设置有吊台，所述吊台上设置有阻挡机构，所述阻挡机构设置在所述吊台的底面。本实用新型的有益效果为：本实用新型通过勾体对硅钢片进行起吊，可以有效的防止硅钢片两端卷边，从而减少了变压器空载损耗，阻挡机构可以有效的防止硅钢片在运输过程中从吊台上摔落，从而保护了硅钢片的完整性，提高了使用效率。

该电磁钢板包括母材钢板、第1绝缘被膜及第2绝缘被膜，该第1绝缘被膜被形成于所述母材钢板的第1面，并具有粘结能量，该第2绝缘被膜被形成于作为所述母材钢板的所述第1面的背面的第2面，并具有粘结能量，所述第1绝缘被膜的平均铅笔硬度为HB以上3H以下，所述第2绝缘被膜的平均铅笔硬度比所述第1绝缘被膜的平均铅笔硬度更高。

本发明公开一种硅钢片叠片装置，涉及硅钢片叠加领域，包括：上料机构，其包括第一定位装置，第一定位装置包括多个第一轴向定位柱，第一轴向定位柱与周向开孔一一对应，多个第一轴向定位柱分别穿过不同位置的周向开孔；精定位机构，其周向定位硅钢片；下料机构，其包括第二定位装置，第二定位装置包括用于与硅钢片的中心孔相配合的中心定位柱；用于将设置于第一轴向定位柱上的硅钢片移动至精定位机构的移载机构；摄像装置；机器臂，摄像装置与机器臂通信连接，机器臂根据摄像装置拍的键槽方口特征调整硅钢片的角度、并将硅钢片移动至中心定位柱。该硅钢片叠片装置能够有效降低人工劳动强度，并提高叠放效率。

本发明公开了一种硅钢片横剪线裁切设备，包括：本体，所述本体包括工作台、挡屑罩和裁切装置，所述挡屑罩内水平固定安装有横杆，所述裁切装置与横杆下表面滑动连接；两个定位机构，所述定位机构包括第一螺纹杆、第一滑块和压板，所述挡屑罩内壁开设有两个安装槽，两根所述第一螺纹杆分别转动安装在两个安装槽内，两个所述第一滑块分别螺纹套设在两根第一螺纹杆上，两个所述压板分别与两个第一滑块远离安装槽槽底的一端水平固定链接；两个驱动机构，所述驱动机构用于控制第一螺纹杆发生转动。通过驱动装置控制定位机构中压板在垂直方向上的位置便可快速实现对硅钢片的定位工作和解除工作，方便快捷，提高了裁切工作的效率。

本发明提供退火隔离剂的制备方法以及退火隔离剂和方向性电磁钢板。由该方法得到的退火隔离剂纯度高、分散性以及密接强度优异，可以在方向性电磁钢板表面形成均匀致密的镁橄榄石层。退火隔离剂的制备方法，其包括：工序(1)：将氧化镁和铵盐溶液混合并反应，制备镁盐溶液和氨，然后使精制的镁盐溶液与氨反应而得到氢氧化镁；工序(2)：将得到的氢氧化镁的一部分在155～230℃下高温熟化，并且将得到的氢氧化镁的另一部分在10～100℃下低温熟化；工序(3)：将在上述各条件下熟化的氢氧化镁混合、烧成，得到氧化镁用于退火隔离剂。

无取向硅钢的磁性能主要取决于铁素体的晶粒尺寸、晶体织构和钢中的夹杂物。通过合适的化学成分设计以及采用适宜的夹杂物控制技术,可以获得最佳的夹杂物控制效果,使其纯净度大幅度提高或者无害,最终获得磁性能优良的高级别无取向硅钢。同时,为满足节能、环保、高效需求,无取向硅钢正朝着节能降耗、环境友好以及多功能、高效率、易加工等方向发展。 The magnetic properties of non-oriented silicon steel mainly depend on the grain size of ferrite,the crystallographic texture,and the inclusions in the steel.The optimum inclusion control effects can be obtained through a suitable chemical composition design and an appropriate inclusion control technique,and then the liquid steel will get be clean or the inclusion will get be harmless,finally the excellent magnetic property of the non-oriented silicon steel can be obtained.Meanwhile,in order to ...