本发明提供了一种电工钢表面涂层剂及使用方法，所述电工钢表面涂层剂包括如下的压力重量份组分：碲化合物10～50份，树脂10～30份、硅烷偶联剂0.5～5份、柠檬酸13～18份，将得到的电工钢表面涂层剂涂布在钢基表面，加热干燥，烧结，形成涂层。形成的涂层附着力强，生产涂覆质量较好，过钢量达到预期2000吨以上，具有良好的防锈性能，磨损程度较低，同时绿色环保。

试验研究了球刻痕法对高磁感取向硅钢的铁损、矫顽力、相对磁导率、巴克豪森噪声等磁学性能的影响.研究结果表明:经过球刻痕处理后,高磁感取向硅钢的铁损明显降低,矫顽力下降,8 mm球刻痕过后铁损值与矫顽力分别下降16.2%和14.7%,且铁损和矫顽力均随刻痕间距降低而减少.刻痕后的高磁感取向硅钢磁导率在高磁感应强度下明显上升,刻痕后巴克豪森噪声值明显降低,经过对比分析确定8 mm为球刻痕的最佳刻痕间距.从磁畴观察、细化磁畴的原理等方面解释了细化磁畴对高磁感取向硅钢性能的影响原因. The effects of the ball scribing on magnetic properties of high permeability grain-oriented silicon steels,including the iron loss,coercive force,relative permeability,and Barkhausen noise were investigated. The results showed that the iron loss and coercive force of the high permeability grain-oriented silicon steels apparently decreased 16. 2% and 14. 7% respectively after 8 mm ball scribing and they both decreased with the decrease of the scribing spacing at the same magnetic flux density. At... 

两炉次无取向硅钢XG800WR（/%:0.003～0.004C、0.71～0.75Si、0.32～0.33Mn、0.004～0.007S、0.016P）的炼钢流程为铁水预处理（KR）-210 t顶底复吹转炉-钢包吹氩-RH脱碳精炼-230mm×1220 mm板坯连铸。53 t中间包钢水过热度为25～30℃,钢包到中间包采用长水口全程吹氩保护浇铸,中间包至结晶器采用浸入式水口浇铸。结果表明,在RH、中间包、结晶器过程中钢中总氧以及夹杂物数量和尺寸均明显降低;但在钢包到中间包过程T[O]、[N]和钢中夹杂物数量增加,说明长水口浇铸过程存在二次氧化。连铸坯中T[O]、[N]平均他分别为11×10^-6和30×10^-6,显微夹杂物数量平均为4个/mm²。铸坯中的显微夹杂物主要为3～5μm的AlN,同时存在少量的MnS、Al₂O₃·AlN和Al₂O₃·MgO·MnS。 The steelmaking flow sheet for two heats non-oriented silicon steel XG800WR（/%:0.003～0.004C. 0.71～0.75Si,0.32～0.33Mn,0.004～0.007S,0.016P） is hot metal pretreatment（KR）-210 t top and bottom combined blown converter-ladle argon blowing-RH decarburization refining-230 mm×1 220 mm slab casting.The superheating extent of liquid in 53 t tundish is 25～30℃,whole casting is shielded by blowing argon with long nozzle from ladle to tundish and the submerged nozzle is adopted in casting from tundish to mold... 

本实用新型涉及硅钢片切割设备领域，具体涉及一种变压器铁芯硅钢板的剪切装置，包括操作台，操作台的顶部安装有传送辊，传送辊的侧部安装有限位装置，限位装置的侧部依次安装有送料装置和切割装置，切割装置包括固定座，固定座的顶部固定连接有底板，底板的两侧固定连接有导向柱，导向柱的顶部安装有顶板，导向柱上且位于顶板的下方滑动设置有刀架，刀架上安装有切割刀，顶板上安装有液压缸，液压缸的自由端的端部与刀架的顶部固定连接；解决现有的硅钢片切割效率低的问题。

为研究退火工艺对普通取向硅钢初次再结晶组织的影响,对经不同温度、保温时间和升温速率退火后的材料组织进行了分析。结果表明:在等温退火条件下,加热至600℃时开始发生初次再结晶,800℃以上初次再结晶组织发展完善;而在最终冷轧板直接进行最终高温退火的情况下,加热温度在500～700℃时,将升温速率提高到80℃/h,初次再结晶组织更易于发展完善。 To investigate the influence of annealing process on the recrystallization of common grain oriented silicon steel,microstructures of sheets annealed at different temperature,soaking time and heating rate are observed.Results show that under the condition of isothermal annealing,recrystallization begins at 600℃ and fully develops above 800℃,while in the case that the final cold rolled sheets are directly thrown to final high temperature annealing,recrystallization is likely to develop with the he... 

针对某厂DMS森吉米尔轧机生产无取向硅钢表面麻面缺陷的问题，根据生产实际，对其形成原因从乳化液及工作辊两方面因素进行了分析。结果表明：乳化液对麻面缺陷的产生有一定影响，但不是主要因素，主要原因是由于二十辊森吉米尔轧机工作辊辊径较小，轧制相同长度带钢轧辊运转周期较大，容易产生疲劳失效而导致。为此，提出通过调整冷轧工序成品轧制道次的压下率以减小轧制力，从而减小工作辊的磨损疲劳；通过对轧制乳化液浓度、温度的合理控制，以改善润滑效果、提高轧制速度，而进一步缓解轧辊疲劳的改进措施，使该钢厂无取向硅钢麻面缺陷发生率由原来的18%降至0.8%,带钢表面质量明显改善。 For the problem of surface pockmarks of non-oriented silicon steel strip produced by a DMS Sendzimir mill, based on the production practice, the formation causes were analyzed from two aspects of emulsion and working roll. The results show that the emulsion has a certain effect on the formation of surface pockmarks defects, but it is not the main factor. The main reason is that the working roll diameter of the 20-high Sendzimir mill is small, and the running period of the roll rolling the same l... 

本发明涉及一种变压器硅钢片智能叠片机械及叠片方法，包括工作台、叠片机构、交替机构、放置机构和交换机构，所述的工作台上方设置有叠片机构，叠片机构上右方设置有交替机构，叠片机构左右对称设置有放置机构，放置机构前方设置有交换机构，本发明采用放置机构放置待叠片的硅钢片，一号电动气缸与二号电动气缸分别交替带动连接板上的一号电磁铁与连板上的二号电磁铁吸附二号水平板上弧形杆内的硅钢片到一号数片板上的圆弧挡板内，当二号水平板上弧形杆内的硅钢片吸附完时，推动放置硅钢片的三号水平板在前后两个导向板之间，然后再将待叠片的硅钢片放在二号水平板上的弧形杆内，这种交换方式节约了叠放时间，提高了工作效率。

本发明公开了一种无取向电工钢清洗工艺，包括以下步骤：1)在脱脂剂箱体中添加脱脂剂溶剂，通过喷射泵将脱脂剂分别从上下两路管道喷出，经过流量控制电磁阀进入喷射梁，通过喷嘴喷洒在带钢表面；2)带钢轧制后温度为100～150℃，速度为600～1000m/min，带钢表面高温确保脱脂剂与带钢表面残留油脂反应充分，且在高速下喷射的脱脂剂与带钢相向而行，使带钢表面反应后残留硅泥、铁粉被迅速带走；3)喷射后的脱脂剂流入收集槽中，通过泵重新打入脱脂剂箱体中，实现脱脂剂的循环利用。其利用轧制时产生的高温及高速对带钢表面残留乳化液斑迹、铁粉、硅泥进行清洗，清洗彻底高效。

本实用新型公开了水性硅钢绝缘涂料制备用袋式过滤机，包括下壳体，所述下壳体顶部铰接有一对上壳体，一对所述上壳体均具有连接板，一对所述连接板通过若干个吊环连接，所述上壳体外侧壁面设有上固定座，所述下壳体后壁面设有出液管，所述下壳体内部设有弹出支撑板机构，所述上壳体内部设有上壳体清洁机构，所述下壳体内部设有下壳体清洁机构。本实用新型涉及袋式过滤器技术领域，本装置结构紧凑，通过一对第一气缸铰接于一对上壳体两侧，使上壳体实现向自动两侧打开的功能，取出支撑板时较为方便，上壳体内壁面的挤压销能够对支撑板进行挤压，当上壳体被打开时，支撑板失去挤压销的限位作用时就会从限位槽中弹出，给人们带来了方便。

本发明提供了一种轴向开关磁阻电机转子硅钢块的半成品成型结构，包括一硅钢片盘，所述硅钢片盘具有内端部和外端部，及贯穿所述内端部和所述外端部的多个固定孔，多个所述固定孔沿着所述硅钢片盘的周向等距间隔排列，并且相邻的两个所述固定孔之间形成硅钢块；多个齿棒，每一所述固定孔内分别插接一所述齿棒；一固型组件，所述固型组件固定于所述内端部和所述外端部上。所述硅钢片盘通过所述固定孔分隔成多个形状一致的所述硅钢块，多个所述硅钢块通过切割分离，并可对应组装成一转子，成型方便快捷，还保障产品形状的一致性，实现工业化批量生产。

本发明公开了一种降低无取向硅钢W800头部窄尺的控制方法，步骤1、筛选板坯长度，并使板坯进入加热炉后头部均朝向轧机方向；步骤2、控制板坯头部温差小于10℃；步骤3、固定粗轧到精轧区间内的轧机机架轧制速度；步骤4、固定相变机架，使板坯的奥氏体‑铁素体相变发生在F2和F3机架中；步骤5、调整精轧机架间的负荷分配，降低F2和F3机架的压下量；步骤6、调整活套张力，降低F2和F3机架的活套单位张力补偿；步骤7、降低模型AGC增益，降低F2和F3机架的AGC补偿的辊缝波动量。本发明通过控制固定相变机架、优化相变机架的负荷分配、AGC补偿系数、活套张力等，使秒流量保持平衡，减少无取向硅钢W800头部窄尺。

适用范围 本标准规定了700 MW及以上级大电机用冷轧无取向电工钢带的术语和...