硅钢资料

采用XRD、SEM和激光粒度仪等手段,观察并研究了不同特性氧化镁在硅钢表面形成硅酸镁底层形貌特点,并结合热力学和差热-失重分析了MgO-SiO2的反应机理。研究结果表明:粒度小,活性值高的特种氧化镁在高温退火过程中与基体表面氧化物生成的硅酸镁底层,界面中硅酸镁底层嵌入基体较多,表面致密,颗粒细小,有利于形成附着性能优良的硅酸镁底层。 Surface microstructure of Mg2SiO4 coatings formed on the surface of oriented silicon steel coated with different kinds of MgO was investigated by XRD and SEM.The reaction mechanism between MgO and SiO2 was analyzed by TG-DSC and thermodynamic calculation.Results revealed that when the MgO with finer microstructure size and higher activity is employed,a dense Mg2SiO4 layer with finer microstructure and good binding to the steel substrate can be obtained.The results are very helpful for the prepar... 

针对新日铁公开的相关专利,总结日本高强度无取向电工钢的研究进展,分析了各专利化学成分、生产工艺及产品性能的特点,指出固溶强化、细晶强化、析出强化、位错强化都有可能被用来提高无取向电工钢的强度。在高强度无取向电工钢的研发过程中,需要根据其具体用途确定目标性能,再采用合适的强化手段,从而实现力学性能、磁性能和生产性能之间的平衡。 Authors summarize the research progress of high strength non-oriented electrical steel in Japan by learning related patents brought into the public by Nippon Steel. Authors also analyze the characteristics of the chemical composition, production technology and properties of products in the patents and point out that any ones of solution strengthening method, fine-grain strengthening method, precipitation strengthening method or dislocations strengthening method may be used to improve the strengt... 

本发明公开一种硅钢片叠片装置，涉及硅钢片叠加领域，包括：上料机构，其包括第一定位装置，第一定位装置包括多个第一轴向定位柱，第一轴向定位柱与周向开孔一一对应，多个第一轴向定位柱分别穿过不同位置的周向开孔；精定位机构，其周向定位硅钢片；下料机构，其包括第二定位装置，第二定位装置包括用于与硅钢片的中心孔相配合的中心定位柱；用于将设置于第一轴向定位柱上的硅钢片移动至精定位机构的移载机构；摄像装置；机器臂，摄像装置与机器臂通信连接，机器臂根据摄像装置拍的键槽方口特征调整硅钢片的角度、并将硅钢片移动至中心定位柱。该硅钢片叠片装置能够有效降低人工劳动强度，并提高叠放效率。

本实用新型涉及变压器技术领域，具体为一种变压器铁芯的硅钢片加工装置，包括工作台，工作台的顶端靠两侧的位置均开设有滑槽，工作台的底端内壁靠两侧的位置均固定安装有两组伸缩杆，两组伸缩杆的顶端均与滑板的底端外表面相固定，滑板的顶端靠两侧的位置均贴合有滑块，两组滑块的顶端均固定安装有螺纹套，两组螺纹套的内部均与双向螺纹杆的外表面相活动螺接，双向螺纹杆的一端固定安装有摇把，双向螺纹杆的外表面靠中间的位置设置有限位块，摇把的顶端固定安装有固定块。两组弧形板和若干组凸块的设置可对硅钢片进行实时校准的作用，并使得叠加的硅钢片始终保持在同一垂直水平线上从而方便后续操作。

本发明公开了一种弧形硅钢片、弧形硅钢片治具及弧形硅钢片制造方法；弧形硅钢片治具包括压制底板和侧挤压板，压制底板和侧挤压板之间具有挤压间隙，挤压间隙的两侧分别设置有位于压制底板内侧的外挤压面和位于压制底板外侧的内挤压面，外挤压面和内挤压面的对应位置上开设有若干齿槽加工台阶，压制底板的下方开设有若干与挤压间隙连通的焊接孔，压制底板和侧挤压板的侧面对应位置设置有贯穿压制底板和侧挤压板的冲压模孔；通过弧形硅钢片制造方法，采用弧形硅钢片治具制成弧形硅钢片。本发明采用弧形硅钢片治具及弧形硅钢片制造方法实现动子中弧形硅钢片的压制成型，通过弧形硅钢片实现直线电机的圆周运动或圆弧运动。

本实用新型公开了一种变压器硅钢片卷吊装件，包括横梁和两个吊钩组件，在横梁两端之间的中部设置有吊挂连接构件；两个吊钩组件呈左右对称设置于横梁，吊钩组件与横梁滑动连接，在吊钩组件与横梁之间设置有第一锁紧机构，横梁通过吊挂连接构件与吊机上的吊索连接，在对不同宽度的硅钢片卷进行吊装时，松开两个第一锁紧机构，调节好其中一个吊钩组件的位置，并锁紧固定好，使得固定好的吊钩组件插入硅钢片卷其中一端内，最后将另外一个吊钩组件插入硅钢片卷另一端内，并锁紧固定，本实用新型通过两个吊钩组件来勾住硅钢片卷的两端，可避免硅钢片卷在起吊过程中损坏卷边，也可满足不同宽度的硅钢片卷的吊装。

试验了通过NaCl-KCl-NaF-SiO₂熔盐在电流密度50 mA/cm²、电沉积脉冲电流正反向比9:1和750⁸50℃60min电沉积下阴极（/mm）20×20×0.5的1.6Si无取向冷轧硅钢片断面层硅的分布,并通过计算得出Si的扩散系数。结果表明,电沉积温度由750℃提高至850℃时,试样中Si含量增加,扩散的深度由18μm提高到40μm;电沉积温度与Si在钢中的扩散系数近似符合Arrhenius指数关系。 The distribution of silicon at cross section of cathode（/mm） 20 × 20 × 0.5 sheet of 1.6Si non-oriented cold rolled silicon steel after electro-deposit treatment by NaCl-KCl-NaF-SiO₂ molten salt with current intensity 50 mA/cm²,electro-deposit pulse current positive-negative ratio 9:1 at 750 850 ℃ for 60 min has been tested and the diffusion coefficient of Si is obtained by calculation.Results show that with increasing electro-deposit temperature from 750 ℃ to 85... 

本实用新型涉及变压器铁芯生产技术领域，尤其涉及一种硅钢片卷自动上料装置。包括所述底座上方设置有支撑座，所述支撑座上方转轴连接有翻转座，所述翻转座前后两侧设置有支撑柱，所述托架底部前后两侧设置有支撑套，所述支撑套对应滑动连接在支撑柱上，所述支撑套左侧上方设置有凸台，所述凸台右侧在支撑套上方设置有卡槽，所述卡槽右侧开口，所述硅钢带卷设置在卡槽内部，将钢卷平躺放置在托架的卡槽内部，通过翻转液压缸可将托架和钢卷进行树立，钢卷一侧靠在托架上，钢卷树立过程比较平稳，通过三组液压缸可实现钢卷自动上料的过程，在钢卷树立过程中，可通过绳索将钢卷固定在托架上。

目的提高硅钢的磁性能。方法采用多弧离子镀技术,在普通取向硅钢薄板两面沉积高硅FeSi合金层制得高硅梯度硅钢,并进行热处理,观察其显微组织,测量磁性能。结果退火态高硅梯度硅钢表面的高硅FeSi合金层与基底结合紧密,均匀致密。高硅梯度硅钢中硅含量呈梯度分布,最表层硅质量分数为11.0%,随着深度增加,硅含量逐渐降低,在距表面20μm处硅质量分数仍能达到6.5%。沉积态高硅梯度硅钢的电阻率ρ、低频铁损P10/50、高频铁损P10/1k及磁感应强度B8分别为68.6μΩ·cm,0.82W/kg,83.3 W/kg和1.73 T,退火后分别为63.1μΩ·cm,0.44 W/kg,54.38 W/kg和1.89 T。结论由于表层高硅FeSi合金层的存在,梯度高硅钢的低频磁学性能良好,但高频损耗需进一步改善。 Objective To improve the magnetic properties of silicon steel. Methods FeSi alloy coatings with high-silicon content were deposited on the surface of common grain-oriented silicon steel by cathodic arc plasma evaporation,and then a kind of high silicon gradient steel was prepared. The morphologies,content and magnetic properties of the samples were tested. Results FeSi alloy coatings were featured with compact microstructures and excellent adhesive quality with the substrates. The silicon conten... 

本实用新型公开了一种用于焊接硅钢板带的焊接机构，包括握把，该握把的一侧设置有下钳嘴及上钳嘴，该握把的另一侧设置有机械臂，下钳嘴的顶端设置有第一铜片，第一铜片的一侧顶端活动设置有下夹片，且上钳嘴的顶端设置有与下夹片相配合的上夹片，握把一侧内部设置有第二铜片，且第一铜片与第二铜片相互靠近的一侧均设置有金属弹片，两组金属弹片之间卡接设置有卡块一。有益效果：通过设置下夹片与上夹片实现对焊条进行夹紧，且下夹片与上夹片中的转动块均为活动连接，在实际焊接过程中可以利用焊条带动下夹片与转动块转动，从而实现焊条与握把之间角度的调节，进而满足不同的焊接条件，提高焊接效率。

本发明涉及一种冷连轧法生产无取向高硅钢的方法，RH真空脱碳处理后，铝脱氧及部分铝合金化，合金化后大罐钢水净循环大于3次或大于5分钟；熔炼合格钢水至连铸开浇前静置时间大于二十分钟；控制过热度5～15℃；采用电磁搅拌，控制等轴晶比例45％以上；3)热轧工序板坯装炉温度大于750℃；常化使晶粒尺寸在90～110μm范围内；连续退火炉加热段温度设定950～1150℃，均热段温度设定900～1050℃，全氮气干气氛保护，控制晶粒尺寸120～170μm。生产全过程中的热履历参数控制，充分发挥设计的微合金元素功能，改变析出物的组成、大小、形态及分布。

本发明提供了一种取向硅钢的磁畴细化方法，属于高磁感取向硅钢生产技术领域技术领域，包括：采用激光在带钢表面烧蚀出若干沟槽；采用腐蚀液对所述沟槽进行腐蚀，获得刻槽；其中，所述沟槽与带钢宽度方向的夹角为0‑20°；所述沟槽的深度为0.5～20μm，宽度为30～200μm；所述刻槽深度为0.5～30μm、宽度为30～300μm。该方法能够显著的细化磁畴，降低取向硅钢片单位损耗，同时细化磁畴的效果能够承受800℃‑900℃的消除应力退火。本发明还提供了一种取向硅钢的磁畴细化方法在取向硅钢生产中的应用。