利用本钢技术中心试验厂技术手段,并与北京钢铁研究院合作,试制了用作家电用电机、微电机、小电机或部分中型电机铁芯的冷轧无取向电工钢。试制钢硅含量小于0.5%,钢板表面平滑,公称厚度0.5mm,且厚度均匀偏差小,性能测定结果表明,产品的磁性能、力学性能满足其使用要求。 BX STEELTechnology Center pilot plant using technical means,and with Beijing Iron and Steel Research Institute,trial cold rolled non-oriented electrical steel that has been used as appliance motor core,micro motor core,small motor core,or part of the medium-sized motor core。Trial steel of silicon content is less than 0.5%,steel plate surface is smooth,the nominal thickness of 0.5mm,and the thickness deviation is small,performance measurement results show that the magnetic properties,mechanical p... 

本发明属于冶金技术领域，涉及一种超短流程稀土取向硅钢及其制备方法，化学组成及其重量百分比为Si：2.0～4.5％，C：≤0.003％，Y：0.001～0.05％，Mn：0.15～0.35％，Al：0.03～0.04％，Cu：0～0.5％，S：0.025～0.04％，N：0.011～0.013％，其余为Fe和不可避免的杂质元素。制备工艺包括：钢水冶炼、薄带连铸、冷轧、再结晶退火。与常规生产方式相比，取消了连铸、粗轧、热连轧、常化和脱碳退火等工序，极大简化了生产流程。通过添加稀土元素钇，促进了抑制剂的析出，还显著细化了薄带连铸硅钢的凝固组织，提高组织均匀性，获得了均匀细小的等轴晶，优化了取向硅钢的性能。

【作者】 杨佳直； ...

取向硅钢利用析出物作为抑制剂,抑制初次再结晶晶粒的长大,抑制剂是取向硅钢发生二次再结晶的基本条件之一。文中通过低温板坯加热技术制备取向硅钢,采用透射电镜(TEM)观察并研究了高温退火阶段抑制剂的演化过程。结果表明,渗氮后形成的非晶态Si3N4析出物不稳定,在700～750℃退火升温阶段转化为(Al,Si)N;(Al,Si)N颗粒在800℃发生团聚,随后长大并粗化;(Al,Si)N是低温取向硅钢主要抑制剂,随退火温度的升高,(Al,Si)N抑制力大幅下降。 Precipitates as inhibitor are used to inhibit the grain growth of primary recrystallization in grain-oriented silicon steel,and inhibitor is one of the basic conditions for occurring of secondary recrystallization.The grain-oriented silicon steel was produced by low temperature slab heating and nitriding technique.The evolution of inhibitor was observed by transmission electron microscopy.The results show that Si3N4 particles are precipitated after nitriding,and Si3N4 particles are amorphous and... 

本实用新型公开了一种冷轧取向硅钢带整平装置，包括两个上下对称分布的保护罩，所述保护罩的内部均转动连接有展平辊，且展平辊的一端均延伸至保护罩的外部，所述保护罩的外壁设置有传动罩，且传动罩的外壁设置有动力箱，所述动力箱与展平辊传动连接，上下两个所述展平辊之间设置有其,特征在于，所述保护罩的两侧外壁均固定连接有支撑架，且支撑架的一侧外壁均设置有延展机构，两个所述延展机构之间设置有连接架，且连接架的一侧外壁设置有吸水布，所述吸水布的内部设置有胶板。本实用新型吸水布与硅钢带本体的外壁滑动接触，以此将展平时涂抹在硅钢带本体表面的水溶性润滑剂刮抹掉，减少硅钢带本体表面上的水分。

本发明涉及一种混合硅钢定子结构及与其配套的转子结构及永磁电机，属于电机技术领域，包括：定子，由多个第一硅钢片叠压构成；多个线圈绕组，均匀设置在定子的内壁上；第一硅钢片包括：多个连接块与多个连接臂，连接块与连接臂交替排列构成硅钢环片，连接块采用无取向硅钢且与两侧的连接臂通过拼合结构连接，连接臂采用取向硅钢；多个定子齿，呈放射状均匀设置在硅钢环片的内侧，定子齿与连接块也通过拼合结构连接，定子齿采用取向硅钢；本发明通过取向硅钢、无取向硅钢混合组成的定子，能够有效提导磁性能；本发明能够稳定提升定子上的磁性能，增加电机的输出能力，实用性强，值得推广。

用还原分离-原子荧光光谱法分析了硅钢中的痕量汞.分析方法的不确定度主要来自测量重复性,样品溶液浓度,工作曲线变动性,标准溶液,移取、配制标准溶液,仪器变动性等.文章分别对上述构成合成不确定度大小的分量进行了计算讨论. Trace mercury in silicon steel and galvanized sheet was analyzed by adopting reduced separation-atomic fluorescence spectrometry.The uncertainty of the analysis method mainly comes from measurement repeatability,sample concentration,working curve volatility,standard solution,pipetting and preparation of standard solution,and instrument variability,etc.The essay conducted all calculations and discussions on the above components that determine uncertainty. 

无取向硅钢的磁性能主要取决于铁素体的晶粒尺寸、晶体织构和钢中的夹杂物。通过合适的化学成分设计以及采用适宜的夹杂物控制技术,可以获得最佳的夹杂物控制效果,使其纯净度大幅度提高或者无害,最终获得磁性能优良的高级别无取向硅钢。同时,为满足节能、环保、高效需求,无取向硅钢正朝着节能降耗、环境友好以及多功能、高效率、易加工等方向发展。 The magnetic properties of non-oriented silicon steel mainly depend on the grain size of ferrite,the crystallographic texture,and the inclusions in the steel.The optimum inclusion control effects can be obtained through a suitable chemical composition design and an appropriate inclusion control technique,and then the liquid steel will get be clean or the inclusion will get be harmless,finally the excellent magnetic property of the non-oriented silicon steel can be obtained.Meanwhile,in order to ... 

1.本外观设计产品的名称：硅钢片。;2.本外观设计产品的用途：多片硅钢片用来共同组成马达的转子的其中一个部件。;3.本外观设计产品的设计要点：在于本外观设计产品的形状。;4.最能表明设计要点的图片或照片：立体图。;

本发明揭示了一种超低铁损无取向硅钢及其生产方法，生产方法包括：依次采用铁水脱硫、转炉冶炼、RH炉精炼进行冶钢，最终所得钢水化学成分以质量百分比计为：C≤0.003％、Si：2.8～3.4％、Mn：0.1～0.5％、Al：0.6～1.3％、S≤0.0015％、N≤0.0020％、P≤0.03％、Ti≤0.003％、V≤0.003％、Nb≤0.003％，且同时满足3.80％≤Si+Al≤4.15％，其余为Fe以及不可避免的杂质；将冶炼所得钢水连铸成连铸坯；对连铸坯加热后经过多道次轧制得到热轧卷板；对热轧卷板的两侧边部进行剪切；常化酸洗，常化温度为900～930℃，常化时间为30～60s；经多道次冷轧成厚度为0.35～0.5mm的无取向硅钢，其中，第一道次冷轧时的压下率≥37％，轧制速率为70～180m/min。本发明制备的无取向硅钢具有超低铁损，而且冷轧时不易断带。

本发明提供一种改善表面麻点缺陷的薄规格中低牌号无取向硅钢及其生产方法，成分C≤0.0025％，1.2≤Si≤1.65％，0.25％≤Mn≤0.35％，0.06％≤P≤0.11％，0.1％≤Als≤0.2％，S≤0.0025％、N≤0.0025％，Ti≤0.0025％，其余为Fe及不可避免的杂质。与现有技术相比，本发明采用较低氢气浓度，防止炉内氧化铁皮还原，减轻碳套辊的腐蚀程度，减少碳套辊结瘤率，改善带钢表面质量；采用合理合金成分设计，提高带钢的力学强度，降低碳套辊结瘤对带钢表面的影响程度，改善带钢表面质量。产品厚度为0.35mm，板面麻点发生率降低，无手感，且辊身周长周期范围内麻点个数≤5个。

本实用新型提供了一种用于冷轧无取向硅钢卷的具有防护功能的转运装置，其特征在于，包括：壳体，所述壳体的底部两侧拐角处均设有支撑块，所述支撑块的上方均设有减震器，采用吊装搬运冷轧无取向硅钢卷，可能会在移动的过程中因为滑动掉落，会发生不可预料的风险，地面搬运会降低风险，危险程度相对降低。转运装置的壳体内部的下方设有减震器，能够有效的减少冷轧无取向硅钢卷的晃动，从而减少对冷轧无取向硅钢卷的损坏，也降低因为搬运过程中的晃动带来的危险，通过气缸的伸缩可以固定不同直径的冷轧无取向硅钢卷，防滑板和防滑垫为橡胶材料，既可以防止冷轧无取向硅钢卷的滑动，也可以有效减小冷轧无取向硅钢卷的晃动。