取向硅钢热轧板中织构梯度对发展完善的二次再结晶十分关键,通过添加铜可以显著降低取向硅钢板坯加热温度,从而影响热轧板织构分布。利用X射线衍射仪,分析了实验室模拟薄板坯连铸连轧(TSCR)工艺的3种不同铜含量的取向硅钢热轧板织构。结果表明:不同铜含量热轧板表面到厚度1/4处均为弱的热轧织构,热轧板心部主要为{100}面织构;铜含量约在0.4%时,热轧板次表层的{110}<001>织构比例最高,而热轧板心部的{100}<110>织构比例最低;铜含量对热轧织构中{114}<110>和{001}<100>织构发展有显著影响。 The texture gradient in hot rolled grain oriented silicon steel strip is one of the essential factors to achieve a perfect secondary recrystallization.The addition of copper can significantly reduce the slab reheating temperature of grain oriented silicon steel,so as to impact the texture distribution in the hot rolled strip.The texture of hot rolled grain oriented silicon steel strip as-rolled by thin slab casting and rolling process(TSCR) in laboratory with three different copper contents was ... 

6.5%Si电工钢是一种优异的软磁材料,织构对其磁性能影响很大。利用温轧工艺对6.5%Si电工钢热轧板进行不同压下率轧制,研究了温轧板织构随压下率的变化规律。实验结果显示,随着压下率的增大,{100}〈110〉、{110}〈100〉和γ纤维织构在薄板表层中的强度先增强后减弱,当压下率达到75%时,沿板厚方向形成3个组织区域:表层细晶粒区({110}〈100〉取向为主)、过渡层({111}〈110〉和{111}〈112〉变形晶粒区)和中心层(以拉长的γ纤维织构和{100}〈110〉取向晶粒为主),这种组织和织构不均性对后期织构的发展有重大影响。 6.5wt% Si electric steel has excellent soft magnetic properties,on which texture play important role.In this experiment,warm rolling technique was employed to investigate the effect of rolling reduction on texture.It was found that the density of {100}〈110〉,{110}〈100〉 and γ-fiber textures first increased and then decreased with increasing of the rolling reduction.At 75% reduction,the microstructure along the thickness of the sheet formed three zones,containing surface layer with {110}〈100〉 orien... 

结合工业化生产的无取向硅钢,进行了RH精炼添加稀土合金实验。结果表明,1.15%(质量分数)Si钢的脱硫反应,主要发生在添加稀土合金之后的前5min。最佳的稀土合金添加量为0.6～0.9kg/t钢。钢液经过稀土处理后,加入的稀土总量越多,稀土氧硫化物夹杂物的尺寸就越大,但热轧带钢再结晶效果会逐渐变差,成品带钢晶粒尺寸先是快速长大,而后逐渐减小。最佳的钢中存留稀土含量与钢的化学成分有关,应严格控制在2.0×10-3%～6.0×10-3%(质量分数)。在此范围内,钢的铁损先是快速降低,而后缓慢升高,钢的磁感应强度则单调降低。 Based on the industrial production of non-oriented electrical steel,rare earth(RE) alloy treatment during the RH refining process was studied.The results showed that the effects of desulfurization and total concentration of RE remained in steel mainly depended on the chemical compositions of different steel grades.For 1.15wt% Si steel grade,the desulfurization reaction mainly focused on the initial 5min after RE alloy added during the RH refining process.The suitable RE alloy addition was 0.6-0.... 

双辊连铸技术是冶金及材料领域内的一项前沿技术,对于生产高品质硅钢具有独特优势.本实验研究了一种双辊铸轧w[Si]=4.5%的无取向硅钢,考察其铸态和常化处理后样品的组织、织构及析出相尺寸特征.结果表明:铸带组织以与铸带法向成5~20(°)倾角的柱状晶为主,晶内存在少量0.3~0.4μm的AlN析出相,铸带织构以λ(<001>//ND)织构为主,表层织构漫散.950℃/10 min常化处理后,析出相尺寸增大,表层λ织构增强. As an advanced technique of metallurgy and material science,twin- roll strip casting has unique advantages for producing high quality silicon steel. The present study was aimed at a 4. 5% Si non- oriented electrical steel for analyzing the structure,texture and the size of precipitates at the initial and normalized state. The results revealed that the initial structure mainly consisted of columnar grains with 5 ~ 20( °) angle to the normal of cast strip,and some AlN precipitates of 0. 3 ~ 0. 4 μ... 

本发明公开了一种普通级稀土取向硅钢制备方法，通过添加稀土元素，利用第二相作用，对铸坯组织、热轧组织、初次再结晶晶粒和二次再结晶晶粒的影响，改善成品磁性能，即降低铁损，提高磁感。

本发明一种解决取向硅钢热轧板晶粒粗大的方法，在取向硅钢的成分设计中减少固溶温度较高的MnS的含量，降低铸坯加热温度，同时计算实际取向硅钢成分中γ‑相含量与温度之间的关系，依据计算结果设计取向硅钢的热轧工艺，可以保证20％～30％的γ‑相数量，成功解决取向硅钢热轧板晶粒粗大的问题。

通过观察冲剪边缘组织,测量冲剪边缘的显微硬度、残余应力的分布情况和磁性能的变化研究了冲剪加工对无取向硅钢50WW800边缘组织和磁性能的影响。对冲剪后硅钢片进行750℃退火,分析退火对组织和磁性能的影响。结果表明,硅钢片剪切边缘会存在0.4 mm的形变硬化层,边缘应力大,铁损增加。退火后变形减小,形变硬化层变小,残余应力大幅度减少,铁损减少。 The influence of punching process on cutting edge microstructure and magnetic properties of non-oriented silicon steel 50WW800was studied by observing microstructure and measuring microhardness near cutting edge.The residual stress distribution in the silicon steel tooth and magnetic properties were measured.Effect of annealing at 750 ℃ on microstructure and magnetic properties of the silicon steel was analyzed.The results show that a cut-edge hardening layer up to 0.4 mm is observed,residual st... 

本发明公开了一种高效无取向电工钢的制备方法,属于电工钢技术领域，具体步骤包括:开卷→焊接→清洗→连续退火脱碳→冷却→涂层→绝缘涂层干燥→绝缘涂层烧结→空冷→表面质量检查→分卷包装。本发明使产品的铁损为3.08w/kg，磁感为1.711T，达到了高效无取向电工钢的产品要求，并通过稳定生产，其铁损稳定在3.1w/kg，磁感稳定在1.71T，完全能达到产品需求。

本发明涉及金属冶炼工艺，尤其是一种降低无取向硅钢W800冶炼成本的方法，开吹阶段，着火后，加入头批渣料，石灰加入量占石灰总加入量的70%，石灰石加入量占石灰石总加入总量的100%，轻烧白云石加入量占轻烧白云石总加入总量的100%，待化渣后，枪位降低；化渣后将剩余30%石灰加入，加入剩余石灰过程中利用矿石调整温度；吹炼后期，并逐步压枪，终点拉碳枪位至1.4m，并使枪位在此高度不少于30s；到达冶炼终点。本工艺通过降低转炉渣量、提碳降氧和提高终点温度来减少铁水锰氧化量和促进氧化锰还原量，进而降低RH金属锰加入量，降低生产成本。

本发明的一个实施方案提供一种取向电工钢板及其制造方法，以重量％计，所述取向电工钢板包含：Si：3.0‑4.5％、Mn：0.05‑0.2％、Al：0.015‑0.035％、C：0.0015％以下(0％除外)、N：0.0015％以下(0％除外)、S：0.0015％以下(0％除外)、余量的Fe及其它不可避免的杂质，并且满足以下关系式1和关系式2。[关系式1](W13/50/W17/50)≤0.57[关系式2](W15/50/W17/50)≤0.76(其中，所述关系式1中，Wx/y表示施加磁场的大小为x/10T且频率为yHz的条件下的铁损值)。

本实用新型属于硅钢片加工技术领域，尤其是一种永磁同步电机生产用硅钢片加工装置，针对了对硅钢片在进行加工过程中的稳定性与对尘屑的防护效果较差的问题，现提出如下方案，其包括工作台，工作台的顶端侧壁固定有支撑架，支撑架的一侧侧壁固定有转动电机，转动电机的输出端连接有打磨头，工作台的一侧内壁转动连接有转动杆；本实用新型中通过转动杆的转动，使其能够带动转动齿轮与传动齿轮进行转动，实现防护组件对硅钢片在进行加工中的防护效果，实现对硅钢片在进行加工中的固定限位效果，提高其在加工过程中的稳定性与防护功能，通过移动杆的上下移动，使其能够对加工完成的硅钢片进行推动，便于工作人员对其进行拿取。

本发明公开了一种硅钢片压装工装，其涉及电机生产技术领域。其技术方案要点包括下压板，所述下压板上设置有限位结构，所述限位结构用于在硅钢片压装过程中对硅钢片进行限位；所述限位结构包括能够转动调节的限位挡块，所述限位挡块包括多个分别用于对不同尺寸规格的硅钢片进行限位的限位面，且该多个所述限位面与限位挡块的转动轴线之间的最小距离均不相同。本发明能够适用于多种规格的硅钢片，而且操作方便，稳定性好。