硅钢资料

本实用新型提供了一种硅钢叠铁芯线圈吊装夹具，属于变压器的技术领域，缓解了现有技术中存在的线圈吊装夹具单次只能进行单个垫块装配，效率较低的技术问题。所述夹具包括：中心盘、吊环、连接杆、吊臂、勾具；连接杆一端连接中心盘，所述连接杆的数量为3个，且两两之间的夹角为120°；所述吊环设置于中心盘上方；每个所述连接杆另一端连接一个吊臂；每个吊臂上设置有勾具。

分析了影响脱碳效果和结晶行为的各种要素及其相互制约关系,提出了Hi-B连续退火工艺曲线,总结得出快速加热及合理稳态气氛是实现工艺制度的关键。结合实际工程,介绍了在连续退火炉设计中快速加热和气氛设计的考虑方法,并指出随着Hi-B产品的发展,如何改进这些方法将是连退工程研发的方向之一。 The factors which affect decarbonization and crystallization and the mutual restriction between them were analyzed.A complete continuous annealing process for Hi-B was put forward.As a result,the rapid heating and the proper steady atmosphere were two important factors.According to an actual project,the consider methods for designing rapid heating and proper steady atmosphere were introduced,and it is pointed that with the development of Hi-B technique,how to improve these techniques would be on... 

利用光学显微镜（OM）和扫描电镜（SEM）研究了不同稀土Ce含量的50W470无取向硅钢的铸坯、热轧板和冷轧退火板的宏观和微观组织，并采用磁性能测试仪测定其磁性能。结果表明：当稀土Ce的加入量从0增加到66×10^-6（质量分数）时，铸坯的柱状晶平均宽度从3.82 mm减小到3.24 mm,等轴晶率从43.1%增加到51.3%;热轧板的平均晶粒尺寸逐渐增加，从26.2μm增加到33.3μm,再结晶百分数从24%增加到37%;退火板的平均晶粒尺寸从36.2μm增加到39.3μm;磁性能测试表明，微观组织的变化有利于50W470无取向硅钢铁损降低和磁感提高。 Macro-structure and microstructure of as-cast plate, hot rolled plate and cold rolled annealed plate of 50 W470 non-oriented silicon steel with different rare earth Ce content was studied by optical microscope（OM） and scanning electron microscopy（SEM）, and their magnetic properties were measured by magnetic property tester. The results show that when the addition amount of rare earth Ce increases from 0 to 66×10^-6（mass fraction）, the average width of columnar crystal of the as-cast pl... 

本实用新型涉及熔融石英陶瓷生产技术领域，且公开了一种高密度熔融石英陶瓷高磁感硅钢炉，包括底板，所述底板的顶部固定连接有高磁感硅钢炉本体，所述高磁感硅钢炉本体的顶部固定连接有密封轨，所述底板顶部的左右两端均固定连接有立柱，所述立柱的顶部固定连接有箱体，所述箱体的右侧固定连接有调节电机，所述调节电机的输出轴固定连接有螺杆，所述螺杆外表面的左右两端均螺纹连接有滑块，所述滑块的底部铰接有连杆，所述连杆的底部铰接有封板。该高密度熔融石英陶瓷高磁感硅钢炉，通过将调节电机的旋转力，转换为封板的上下移动力，无需人工手动开启或关闭，消除了安全隐患的同时，省时省力，操作简便。

本实用新型公开了一种取向电工钢生产用控温装置，涉及取向电工钢生产用控温技术领域，为解决现有控温装置中的温度检测装置需要蓄电池对其进行供电，不仅增大了能量消耗，也对环境造成影响的问题，所述输送机构上方并列等距固定安装有三个温度检测机构，且两个温度检测机构之间均设置有一个喷水降温机构，所述输送机构上方两侧固定安装有限位块，且限位块内部并列等距设置有四个电动伸缩器，一侧所述电动伸缩器前端固定安装有温差发电挡板，所述温度检测机构上方设置有接收器，且温度检测机构下方内部并列等距设置有红外线温度检测器。

本发明公开了一种适宜缠绕式加工的低铁损无取向硅钢及其生产方法，属于硅钢生产技术领域。本发明的无取向硅钢包括以下质量百分比的元素：Si：1.5～2.5％，Mn：0.15～1.0％、Als：0.5～1.5％，其余为Fe及不可避免的杂质。其生产工艺步骤为：铁水预处理、转炉冶炼、真空处理、连铸；加热热轧；常化处理；冷轧、退火；保温、冷却；涂覆绝缘层。本发明通过对无取向硅钢的组分及其配比，结合工艺操作进行优化，能够生产得到电磁性能及延伸率均优异的无取向硅钢，从而能够有效满足电工钢缠绕式加工及使用需求，且其制造工序流程短、成本相对较低。

以青海盐湖氯化镁为初级原料,采用喷雾热解法制备原料氧化镁。原料氧化镁通过水化制备氢氧化镁。将氢氧化镁过滤、洗涤、烘干、粉碎、煅烧,制备硅钢级氧化镁。本文重点考察煅烧温度、煅烧时间、料层厚度等因素对氧化镁水化率的影响,采用均匀实验设计和DPS数据处理,确定最优煅烧实验条件为:煅烧温度1250℃,煅烧保温时间4小时,料层厚度0.5cm。在此条件下得到的硅钢级氧化镁完全满足硅钢及氧化镁的行业标准。 The magnesium oxide is prepared by Spray pyrolysis process,which magnesium chloride from Qinghai Salt Lake is used as primary raw material,and hydrated to magnesium hydroxide,then obtained silicon steel magnesia through filtering,washing,drying,crushing and calcinations.In this paper,influences of some factors on magnesia hydration rate are studied,such as calcination temperature,calcination time and material thickness.After average experimental design and DPS data processing,optimal calcination... 

连续酸洗退火机组(CPAL)对于当前生产高磁感取向硅钢和高牌号无取向硅钢是必不可少的一个环节。常化炉是常化酸洗机组关键的组成部分。本文对国内自主建造的两条退火酸洗机组的工艺流程,特别是常化炉段进行了对比分析。总结出了常化炉的工艺及组成特点,对生产过程中暴露的问题进行了仔细的分析并提出了改进的意见,对于以后新建常化炉具有一定的提示作用。 The continous pickling annealing line(CPAL) is an essential step in producing high magnetic induction grain-oriented silicon steel and high grade non-oriented silicon steel.The normalizing furnace is a very important part of the CAPL.In this paper,the process flows of two CAPL with independent manufacture in our country have been compared,especially the part of normalizing furnaces.The characteristics of process and component are summarized and problems of the normalizing furnace during the prod... 

本发明提供在金属带钢表面以所希望的槽宽度形成线状槽进而磁特性极其优异的方向性电磁钢板。在金属带钢的至少单面形成抗蚀剂被膜，接着，对上述抗蚀剂被膜一边在横穿上述金属带钢的轧制方向的方向进行扫描一边照射激光，除去经上述激光照射的部分的上述抗蚀剂被膜，接着，对上述金属带钢的除去了上述抗蚀剂被膜的部分实施蚀刻处理而形成线状槽，上述抗蚀剂被膜以固体成分换算计含有20质量％以上的无机化合物，在上述金属带钢表面，上述激光具有长轴直径与短轴直径之比为5.0以上的椭圆状的射束形状，并且扫描正交方向的射束直径为10μm～100μm。

本发明的一个实施方案提供一种取向电工钢板及其制造方法，以重量％计，所述取向电工钢板包含：Si：3.0‑4.5％、Mn：0.05‑0.2％、Al：0.015‑0.035％、C：0.0015％以下(0％除外)、N：0.0015％以下(0％除外)、S：0.0015％以下(0％除外)、余量的Fe及其它不可避免的杂质，并且满足以下关系式1和关系式2。[关系式1](W13/50/W17/50)≤0.57[关系式2](W15/50/W17/50)≤0.76(其中，所述关系式1中，Wx/y表示施加磁场的大小为x/10T且频率为yHz的条件下的铁损值)。

【作者】 杨佳直； ...

结合工业化生产的无取向硅钢,进行了RH精炼添加稀土合金实验。结果表明,1.15%(质量分数)Si钢的脱硫反应,主要发生在添加稀土合金之后的前5min。最佳的稀土合金添加量为0.6～0.9kg/t钢。钢液经过稀土处理后,加入的稀土总量越多,稀土氧硫化物夹杂物的尺寸就越大,但热轧带钢再结晶效果会逐渐变差,成品带钢晶粒尺寸先是快速长大,而后逐渐减小。最佳的钢中存留稀土含量与钢的化学成分有关,应严格控制在2.0×10-3%～6.0×10-3%(质量分数)。在此范围内,钢的铁损先是快速降低,而后缓慢升高,钢的磁感应强度则单调降低。 Based on the industrial production of non-oriented electrical steel,rare earth(RE) alloy treatment during the RH refining process was studied.The results showed that the effects of desulfurization and total concentration of RE remained in steel mainly depended on the chemical compositions of different steel grades.For 1.15wt% Si steel grade,the desulfurization reaction mainly focused on the initial 5min after RE alloy added during the RH refining process.The suitable RE alloy addition was 0.6-0....