本实用新型公开了一种电工钢出炉水雾冷却装置，包括冷却箱和电工钢本体，所述冷却箱的顶部内璧固定有等距分布的第一支管，且第一支管的一端固定连接有第一进水管，所述冷却箱的底部固定有对称分布的两个支撑板，且支撑板的相对侧外壁靠近顶端转动连接有等距分布的辊轮，所述冷却箱的底部内壁和支撑板的上表面均固定有第二支管，所述第一支管和第二支管的圆周外壁均固定有等距分布的喷头。本实用新型水雾分别进入第一支管和第二支管后，从喷头喷出，对电工钢本体的上下两面喷洒降温，水雾均匀的附着于电工钢片的表面，并实现冷却作业，提高冷却效率，也保证了硅钢片的质量，避免硅钢片表面冷却不均匀致使厚度不一。

对低温加热工艺生产的以AlN为主抑制剂的高磁感取向硅钢高温退火过程进行中断实验,借助电子背散射衍射技术对高温退火过程中高斯晶粒的演变进行了研究.在升温过程中高斯晶粒平均尺寸先减小再增大.800℃时取向分布函数图出现高斯织构组分,但强度很弱,高斯晶粒偏离角在10°以上;900℃时高斯晶粒平均生长速率超过其他晶粒;950~1000℃时高斯晶粒异常长大,偏离角3°~6°;在1000℃之前高斯取向晶粒相比于其他晶粒没有尺寸优势. The high-temperature annealing process of high permeability grain-oriented silicon steel with AlN as an inhibitor was studied by interrupting test.The evolution of Goss texture in this process was analyzed by electron back-scattered diffraction.It is found that the Goss grain size first decreases and then increases with the rise of temperature.Goss texture appears in the orientation distribution function at 800 ℃,but the intensity is very weak and the deviation angle is more than 10°.The average... 

本发明涉及一种电机定子硅钢片激光焊接装置，其包括底座；工作台，其安装于所述底座；下压旋转组件，其包括：焊接支座，其安装于所述底座上；用于压紧定子硅钢片的下压组件，所述下压组件位于所述工作台的上方，且可沿垂直于所述工作台的板面的方向移动；用于驱动所述定子硅钢片旋转的旋转组件，其安装于所述下压组件靠近所述工作台的一端，所述旋转组件可绕所述下压组件的轴线旋转；以及激光焊接头组件，其固定于所述底座。通过在焊接工作台上设置下压旋转组件，下压组件可以驱动下压使定子硅钢片压紧，旋转组件可以驱动定子硅钢片旋转，进行下一道焊缝焊接，直到该定子硅钢片所有焊缝焊接完成，使用方便，省时省力。

本发明公开了一种新能源汽车驱动电机用35WD1600电工钢及其生产方法。属于新能源汽车驱动电机电工钢生产技术领域，主要解决的是现有技术新能源驱动电机电工钢性能较差的技术问题，包括以下化学元素成分及重量百分比：C≤0.005％，Si为2.5～2.8％，Mn为0.2～0.4％，P为0.08～0.12％，S≤0.008％，Cu为0.20～0.30％，Ni为0.16～0.25％，Al为0.3～0.5％，其余为Fe及不可避免的杂质。生产方法包括以下步骤：(1)铁水预处理；(2)转炉冶炼；(3)RH精炼；(4)连铸连轧；(5)酸洗；(6)第一次冷轧脱碳退火；(7)第二次冷轧脱碳退火；(8)涂层；(9)烧结卷取。本发明的新能源汽车驱动电机用35WD1600电工钢，性能达到新能源汽车驱动电机用冷轧无取向电工钢带国家标准及客户性的要求，焊接性能、板形、冲片性能良好。

本发明公开了一种极薄取向硅钢铁芯及其制造方法，所述制造方法，包括：S1、剪切分条：将取向硅钢根据制作铁芯的宽度要求进行分条剪切；S2、卷绕：根据铁芯的规格型号要求，选取铁芯模具进行卷绕；S3、压块固定：将卷绕好的铁芯用压块固定；S4、退火加工：将固定好的铁芯，阶梯式升温至780℃保温3h退火处理，保护气氛为氮气，之后冷却降温；S5、浸胶：将降温后的铁芯，进行真空浸胶处理；S6、烘干：将浸胶处理后的铁芯烘干处理；S7、装配。该发明制造的极薄取向硅钢铁芯，能彻底消除内应力，磁路各处均无高磁阻存在，空载电流与励磁电流均大幅度下降，从而最大限度的恢复了极薄取向硅钢加工后原有择优取向织构及电磁性能。

本发明涉及硅钢卷取领域，具体涉及提高硅钢收卷速度的卷取系统，包括机架、第一卷取辊、第二卷取辊、第三卷取辊和切捆机构，第一卷取辊、第二卷取辊和第三卷取辊依次转动设置于机架上；切捆机构包括切割刀、挤压板和成卷的胶带，切割刀竖直滑动设置于第一卷取辊和第二卷取辊的上方，切割刀上固定有两个支撑条，两个支撑条之间设置有支撑辊，成卷的胶带套设于支撑辊上，切割刀上还设有供胶带穿过的通槽；挤压板内设有装有墨水的盛墨腔，挤压板一侧的两端固定有排墨管，排墨管与盛墨腔连通，且排墨管与切割刀的侧壁转动连接。采用本技术方案时，有利于提高硅钢卷取效率。

电动汽车电机在高速旋转时承受离心力和电磁力的作用,在进行电机转子设计时,既要考虑电磁性能,还要考虑机械性能。对电机转子受力情况进行了综述,分析了转子用电工钢疲劳性能参数的重要性,详细阐述了试样抛光、表面处理、试样的对中和安装对测试结果的影响。 The motor of electric vehicle bears big force for high speed rotors,mainly including centrifugal and electromagnetic forces.The magnetic and mechanical aspects of the electrical steel are crucial to machine design.In this paper,the forces applied on the motor were summarized and importance of fatigue properties was analyzed.The influence of specimen polish,surface treatment,alignment and installation on fatigue testing result were represented in detail. 

【作者】 卢鹏； ...

结合实际生产0.4%Si无取向硅钢，统计了不含Sn和0.025%Sn无取向硅钢的磁性能变化，利用金相显微镜、X射线衍射仪观察分析不同成分下试样的显微组织和微观织构。试验结果表明：Sn元素可以显著降低无取向硅钢的晶粒尺寸，0.025%Sn试样的平均晶粒尺寸比不含Sn减小28.4%;加入Sn元素后抑制了无取向硅钢中不利于磁性能的{111}面织构组分强度，提高了对磁性能有利的{100}面织构组分强度，0.025%Sn与不含Sn相比磁感均值从1.756 T提升至1.768 T,铁损均值从5.476 W/kg降低至5.204 W/kg,明显改善了无取向硅钢磁性能。 In this paper combined with the actual production of 0.4% Si non oriented silicon steel, the magnetic properties of non oriented silicon steel without Sn and 0.025% Sn were counted. The microstructure and microtexture of samples with different compositions were observed and analyzed by metallographic microscope and X-ray diffraction. The results show that: Sn can significantly reduce the grain size of non oriented silicon steel, and the average grain size of 0.025% Sn sample is 28.4% smaller tha... 

研究了冷轧95%变形量无取向硅钢不同退火温度(710～1 050℃)下再结晶织构特征.再结晶刚完成时(710℃退火),呈现强γ({111<112>～<134>)与弱{114}<481>织构特征;随退火温度升高至900℃,γ明显减弱,{114}<481>组分持续增强,形成典型的{h,1,1}<1/h,1,2>织构;进一步升温至1 050℃,再结晶织构不再发生明显变化.基于EBSD分析,{114}<481>组分的持续强化可归因于其明显的尺寸优势以及较高频率的高能晶界(取向差角为20°～45°). A non-oriented silicon steel was heavily rolled to 95% reduction and subsequently annealed at 710~1 050 ℃ to investigate recrystallization texture evolution.When annealed at 710 ℃ with complete recrystallization,the texture is characterized by a strong partial γ fiber spreading from {111}<112> to {111}<134> and a weak {114}<481> component.As annealing at 900 ℃,γ fiber is decreased significantly while {114}<481> is increased consistently,producing a typical {h,1,1}<1/h,... 

本实用新型提供了一种去角硅钢片铁芯加工用的吊装装置，包括安装板，所述安装板下设有防护筒，所述防护筒包括左半筒和右半筒，所述安装板上设有移动组件，所述移动组件包括气缸，所述气缸连接有伸缩杆，所述伸缩杆另一端连接有安放框架；所述左半筒和右半筒底壁皆设为开口状且侧壁上设有连通槽，所述左半筒和右半筒上分别设有防护组件，所述防护组件包括异型板和连接盒，所述异型板底部连接有固定板，所述固定板和连接盒之间连接有挤压弹簧，所述挤压弹簧内部设有传动杆，所述左半筒和右半筒内部两侧分别设有防护板。本实用新型可以有效挂住硅钢片，不会挤压坏封胶，且具有防护措施。

本发明公开了一种含铝电工钢连铸高效生产的方法，其中CSP连铸连轧包括以下步骤：利用普通硅铁合金中的残余钙元素进行钙处理，钢水中Al2O3夹杂物得到球化；转炉终点氧含量加入改质剂；根据连铸拉速设定结晶器电磁制动电流参数，并制定不同拉速条件下的二冷修正系数；采用低粘度低转折温度消耗量为0.30kg/t高拉速结晶器保护渣，本发明连铸拉速从最高的4.2m/min提高至5.8m/min，提升幅度达到了38％，实现了薄板坯连铸连轧工艺技术条件下含铝电工钢50W1300的高效低耗生产。