硅钢资料

本发明公开了一种耐热刻痕型取向硅钢涂层用涂液，其溶剂为水，其含有：磷酸盐、胶态二氧化硅、铬酐和乙醇。本发明还公开了一种耐热刻痕型取向硅钢板，其包括基板，所述基板表面具有采用上述的耐热刻痕型取向硅钢涂层用涂液涂覆在基板上而形成的涂层。相应地，本发明还公开了上述取向硅钢板的制造方法，其包括步骤：在基板表面涂覆所述涂液，基板的刻痕沟槽涂液填充率＞95％；进行烧结处理，其中烧结处理中的板温为780‑900℃。本发明的耐热刻痕型取向硅钢涂层用涂液具有良好的流动性，其可以涂覆于耐热刻痕取向硅钢基板的表面中，涂覆后，能有效填充基板的刻痕沟槽，且可以在其表面形成涂层，保证耐热刻痕取向硅钢在具有低铁损的同时具备更高的安全性。

研究了热轧卷取时间对无取向电工钢晶粒组织、织构演变、铁损和磁感的影响。结果表明,成品晶粒尺寸在120～140μm之间,随卷取时间的增加,成品晶粒尺寸增大。成品织构主要由γ纤维、а纤维和高斯织构等构成。随着保温时间的增加,{111}<110>和{112}<110>织构强度降低。随卷取时间的增加,成品P1.5降低。热轧板最佳的卷取工艺为550℃保温2～3 h,电工钢的综合磁性能优良。 The effects of hot-rolling coiling time on microstructure,texture,core loss and magnetic induction of a new cold-rolled non-oriented electrical steel containing copper were investigated.The test results showed that for final product the grain sizes are 120-140um,with the increase of coiling time,the grain size increase.For final product there are mainly γ-fibre,а-fibre,and {110}<001> texture,Coiling at 550℃ for hot rolled plate,the {111}<110>,{112}<110> texture was weaked with ... 

采用电子背散射衍射技术测定50SW1300冷轧无取向硅钢中不同尺寸范围晶粒的含量,利用主成分回归分析法,综合研究不同尺寸范围晶粒的含量对无取向硅钢磁性能的影响。结果表明:通过主成分回归分析法能够从不同尺寸范围晶粒的含量的多个影响因素中获取主要的因素,定量研究它们对无取向硅钢磁性能的影响规律。分析表明,无取向硅钢的铁损与不同尺寸范围晶粒的含量之间存在着可靠的多元线性关系,在一定范围内,较大尺寸晶粒的含量越多,其对铁损优化的作用越明显;而无取向硅钢的磁感与不同尺寸范围晶粒的含量之间并无线性关系。 Distribution of grain size in cold rolled non-oriented silicon steel 50SW1300 was measured by EBSD.The effects of the distribution of grain size on magnetic properties of the non-oriented silicon steel were comprehensively researched by means of principal component regression method.The results indicate that the main factors influencing the magnetic properties in the distribution of grain sizes,which can be used to guantitative study the magnetlic properies of the steel,are obtained by principal... 

本发明的一个实施方案提供一种取向电工钢板及其制造方法，以重量％计，所述取向电工钢板包含：Si：3.0‑4.5％、Mn：0.05‑0.2％、Al：0.015‑0.035％、C：0.0015％以下(0％除外)、N：0.0015％以下(0％除外)、S：0.0015％以下(0％除外)、余量的Fe及其它不可避免的杂质，并且满足以下关系式1和关系式2。[关系式1](W13/50/W17/50)≤0.57[关系式2](W15/50/W17/50)≤0.76(其中，所述关系式1中，Wx/y表示施加磁场的大小为x/10T且频率为yHz的条件下的铁损值)。

本实用新型涉及一种硅钢切边重卷机组，包括依次衔接布置的开卷机、入口穿带装置、入口转向夹送辊、入口剪、切边单元、出口转向夹送辊和卷取单元，所述切边单元包括沿带钢运行方向依次衔接布置的切边夹送辊、入口稳定辊、切边剪和出口稳定辊，所述切边剪的废料出口侧衔接布置有碎边剪，所述碎边剪的废料出口侧配置有切边废料输出装置。本实用新型提供的硅钢切边重卷机组，采用切边剪+碎边剪的组合对带钢进行切边操作，避免了传统的废边卷取方式，能较好地适用于硅钢切边操作。采用切边夹送辊与入口稳定辊和出口稳定辊配合，能显著地提高切边操作时带钢运行稳定性以及保证带钢切边质量，可相应地提高生产效率。

系统研究了无取向硅钢用磷酸盐系涂层性能的影响因素。以氢氧化铝和磷酸为原料制备磷酸二氢铝,再添加适量的添加剂酒石酸铵、二氧化硅、环氧树脂,得到的涂液涂布于硅钢表面,并控制合适的烘干温度,通过耐盐雾实验考察各因素对涂液耐腐蚀性能的影响。实验结果表明,在磷酸与氢氧化铝物质的量比为3.4∶1、酒石酸铵用量为2%、二氧化硅用量为1%、环氧树脂用量为5%、烘干温度为300℃条件下,所得涂层材料的防(耐)腐蚀效果最佳。 The factors influencing the performance of phosphate anticorrosive coating for non-oriented silicon were systematically studied.Aluminum dihydrogen phosphate was prepared with aluminum hydroxide and phosphoric acid as raw materials.Then added the right amount of additives,such as ammonium tartrate,silicon dioxide,and epoxy resin to prepare the liquid coating,which was coated on the surface of the silicon steel,and finally controlled a suitable drying temperature.The influences of various factors... 

【作者】 刘彤； ...

概述了高磁感取向硅钢生产工艺的研究现状及发展趋势。介绍了国内外薄板坯连铸连轧流程生产高磁感取向硅钢的研究现状。从流程工序特点、热履历、组织与抑制剂控制方面进行对比,分析了薄板坯连铸连轧流程相对传统板坯流程生产高磁感取向硅钢的技术优势,在此基础上提出了利用该流程生产高磁感取向硅钢需要解决的主要技术难点。 The current status and development trend of production process for high magnetic induction grain-oriented silicon steel are summarized.The research status of producing high magnetic induction grain-oriented silicon steel by thin slab casting and rolling process at home and abroad is introduced.The potential technical advantages of producing high magnetic induction grain-oriented silicon steel by thin slab casting and rolling process are obtained by analyzing in terms of process characteristics,t... 

本发明公开了一种适宜缠绕式加工的低铁损无取向硅钢及其生产方法，属于硅钢生产技术领域。本发明的无取向硅钢包括以下质量百分比的元素：Si：1.5～2.5％，Mn：0.15～1.0％、Als：0.5～1.5％，其余为Fe及不可避免的杂质。其生产工艺步骤为：铁水预处理、转炉冶炼、真空处理、连铸；加热热轧；常化处理；冷轧、退火；保温、冷却；涂覆绝缘层。本发明通过对无取向硅钢的组分及其配比，结合工艺操作进行优化，能够生产得到电磁性能及延伸率均优异的无取向硅钢，从而能够有效满足电工钢缠绕式加工及使用需求，且其制造工序流程短、成本相对较低。

本实用新型公开了一种铁芯硅钢片卷材的自动放卷上料装置，包括放卷机、导向平台和防折组件，所述导向平台间距设置在放卷机的下方，所述导向平台与放卷机之间构成供料带缓冲的缓冲空间，所述料带在缓冲空间内呈U型状走向，所述导向平台的上方间距设置有防折组件，所述防折组件与导向平台之间构成供所述料带通过的导向通道，所述防折组件设置在料带的内弯侧。通过防折组件对料带的内弯侧进行支撑，能够有效的防止料带被过度弯折，能够对料带进行缓冲和缓冲保护，保证料带放卷上料的稳定性。

本发明公开了一种用于取向硅钢卷的焊缝切除方法，包括在焊接机组完成钢卷焊接后，在距离焊缝预设距离位置处冲孔；而后，钢卷到达成品退火工序时，利用孔洞检测装置检测焊缝冲孔，并根据焊缝冲孔得到焊缝位置，并记录该焊缝位置；并在分卷工序中，根据记录得到的焊缝位置对焊缝进行切除。这样，该方法利用焊缝冲孔，结合孔洞检测装置，将焊缝位置信息传递到分切工序，使得焊缝识别切除率较高，有效解决了取向硅钢焊缝无法精准定位切除的问题，实现了卷中焊缝多工序结合精准切除。

本发明公开一种硅钢级氧化镁制备方法、硅钢级氧化镁保护膜，涉及氧化镁制备技术领域。将得到的粗氧化镁产品进行净化处理；将净化处理后的粗氧化镁产品与金属镁碳还原剂，在真空状态下，利用真空碳热还原技术进行金属镁的置换，制得金属镁；金属镁碳还原剂与粗氧化镁产品的质量比为（1~1.5）：1；制得的金属镁在纯氧下制得氧化镁；将制得氧化镁根据实际需求获得不同粒径硅钢级氧化镁颗粒。本发明产品各项指标优于企业标准的硅钢级氧化镁。而且不会受原料中含有的钙等杂质的影响，产品纯度很容易达标，同时，还存在能耗较低、生产成本低等优点，解决了业在降低能耗方面的突破可应用于工业化生产。