以构建高磁感、低铁损、免轧制高硅电工钢铁芯为出发点,提出采用单辊甩带制备非晶铁硅合金薄带、微氧化法在铁硅合金粉末表面包覆高电阻率铁硅氧化物薄膜制备核壳异质结构高硅电工钢纳米粉末、放电等离子烧结快速成形制备颗粒间绝缘的高硅电工钢铁芯。研究了不同氧化包覆时间对SPS烧结试样密度、物相组成、微观结构和静磁性能的影响。研究表明,在氧化包覆5h烧结温度800℃工艺条件下,制备的6.5%Si高硅电工钢铁芯的静磁性能最佳,饱和磁化强度为128.84A.m2/kg、矫顽力为2.25kA/m、剩磁为3.47A.m2/kg。其饱和磁化强度与粉末压延法制备的高硅钢相当,但矫顽力降低了1/3。 The paper takes preparation 6.5%Si steel with high induction,low core loss and removing rolling as the starting point,amorphous Fe-Si ribbons was synthesized by melt spinning method,6.5%Si steel nanopowders with high resietivity core shell structure was prepared by the slight oxidation process and 6.5% Si steel iron core with evaluating internal was sintered by spark plasma sintering process(SPS).The essay focuses studies the effects of different oxidation cladding time on sample density,phase c... 

针对攀钢高硫铁水冶炼现状,结合不同生产工艺路线,论述了攀钢近年来为实现低硫电工钢的生产,在铁水预处理、转炉冶炼、钢水精炼过程中硫控制技术的开发与应用,形成了低硫洁净钢生产工艺技术,实现了低硫电工钢的生产。低硫电工钢RH脱硫率可达到20%左右,成品[S]控制在0.006%左右。 According to the smelting situations of hot metal with high sulphur content at Panzhihua Steel,combined with different produce processes,technologies for controlling the sulfur content during hot metal pretreatment,converter smelting,and second refining are developed. Technologies in low-sulfur clean steelmaking are formed. Low-sulfur electric steel are produced. As for the desulfurization rate of lowsulfur electric steel can reach about 20%,and the content of [S] in products is controlled to ab... 

本实用新型公开了一种将硅钢片堆栈模块化的电机转子，包括：堆栈模块、转子端板和电机轴；堆栈模块卡接在电机轴的外侧，且堆栈模块的两端通过转子端板连接固定；堆栈模块包括多个相互连接的硅钢片，每个硅钢片上均设有连接件，硅钢片通过连接件相互连接。本实用新型通过在硅钢片上增设连接件将多个硅钢片叠加成堆栈模块，降低了固定难度和管理难度，而且可以使用机器人自动化产线的大规模生产，生产效率高。

含铜抑制剂作为取向硅钢的主抑制剂或辅助抑制剂不仅可以抑制初次晶粒的长大,促进二次再结晶,还可以降低铸坯的加热温度。取向硅钢中主要抑制剂为10～50 nm Cu₂S,在钢的铸坯、热轧、冷轧、脱碳等工艺过程均可析出;（Cu,Mn）_1.8S、Cu_1.8S、ε-Cu等主要作为辅助抑制剂,尺寸一般为30～50 nm（或大于50 nm）,主要在热轧阶段析出。总结了国内外有关取向硅钢中含铜抑制剂析出行为的研究进展,当前主要研究不同生产流程和工序中含铜抑制剂的析出行为和作用机理。 As main inhibitor or auxiliary inhibitor for grain-oriented silicon steel,the particles of inhibitor bearing copper not only inhibit the primary crystal growing and promote the secondary recrystallization,but also decrease the heat temperature of casting slab.The main inhibitor for grain-oriented silicon steel is 10～50 nm Cu₂S,which precipitate in process and procedure including steel casting slab,hot rolling,cold rolling and decarburizing process,while the 30～50 nm or more than 50 nm... 

本发明公开了一种物理喷砂方式制备取向硅钢薄带无底层原料的方法，步骤包括：S1、坯料预处理；S2、涂覆隔离剂，后进行高温退火；S3、拉伸热平整；S4、表面喷砂处理，去除底层；S5、去应力退火；本发明优点在于，采用喷砂的物理办法制备取向硅钢薄带无底层原料，代替了传统的用酸去除取向硅钢涂层或硅酸镁底层，结合退火去应力，显著改善了加工质量，使整个加工过程更加环保，也有利于控制成本。

以CaO-CaF2复合渣系为脱硫剂,在RH精炼过程采用真空投入法进行高牌号无取向电工钢深脱硫工业试验,采用KTH模型计算分析了RH炉渣成分对硫容量CS的影响。研究结果表明,炉渣成分控制在w((CaO))/w((SiO2))为5~7,w((CaO))/w((Al2O3))为1.5~1.8,w((Al2O3))为25%~30%,w((FeO+MnO))<5%,脱硫剂加入量为6~8kg/t时,钢中硫质量分数从平均0.003 1%降低到0.001 8%,最高脱硫率达到47.1%,平均脱硫率为41.7%。 The industrial trials on deep desulphurization of high grade non-oriented electrical steel were finished through using CaO-CaF2complex based fluxes in RH process.Using the KTH model,the effect of refining slag composition on the sulfide capacities was analyzed.The results show that the chemical composition of refining slag(mass fraction,%)is w((CaO/SiO2))between 5to 7,w((CaO))/w((Al2O3))beween 1.5to 1.8,w((Al2O3)) between 25%to 30%,w((FeO+MnO))less than 5%,and the desulphurizer addition level of... 

试验的铸态取向硅钢（/%:0.044⁰.056C,3.12³.32Si,0.08⁰.11Mn,0.002⁰.008S,0.002 9⁰.029 1Als,0.006 2⁰.010 9N）由30 kg高频真空感应炉熔炼。通过场发射扫描电子显微镜/能谱仪（FE-SEM/EDS）研究结果表明,0.002 9%Als钢中氧化物主要为SiO₂,存在片状、棒状及近似球状的独立MnS,未发现含铝的氧化物或氮化物;0.0090%Als钢中出现以Al₂O₃为主的复合氧化夹杂物,存在MnS与AlN的复合析出物。钢中Als增加,复合析出物多呈簇状发展。氧化物容易成为MnS-AlN复合析出的核心,钢中Als含量越低,夹杂物中的MnS含量越高;作为核心的氧化物夹杂的尺寸越小,形成的复合夹杂物的形状越规则,尺寸也越小。热力学计算结果表明,钢中Als含量主要影响了钢中氧化物夹杂的组成和AlN的析出温度及析出量。 Test as-cast grain-oriented silicon steel（/%:0.044 ⁰.056C,3.12 3.32Si,0.08 0.11Mn,0.002⁰.008S,0.002 9⁰.029 1 Als,0.006 2⁰.010 9N） is melted by a 30 kg high frequency vacuum induction furnace.The research results by using field emission-scanning electron microscope/energy dispersive spectrometer（FE-SEM/EDS） show that in 0.002 9%Als steel the main oxide is SiO₂,and there is independent laminable,rod-like and approximate ... 

本实用新型提供了一种变压器硅钢片吊装工具，属于变压器技术领域。其技术方案为：一种变压器硅钢片吊装工具，包括勾体，所述勾体上端设置有吊环，所述勾体下端设置有吊台，所述吊台上设置有阻挡机构，所述阻挡机构设置在所述吊台的底面。本实用新型的有益效果为：本实用新型通过勾体对硅钢片进行起吊，可以有效的防止硅钢片两端卷边，从而减少了变压器空载损耗，阻挡机构可以有效的防止硅钢片在运输过程中从吊台上摔落，从而保护了硅钢片的完整性，提高了使用效率。

研究了常化对CSP流程生产的wSi=1.6%的无取向电工钢组织、织构和成品磁性能的影响。结果表明,经CSP流程生产,且在相同的冷轧及退火制度下,经1 000℃×2min常化处理的wSi=1.6%的无取向电工钢热轧板,其最终退火成品的铁损P15/50比不常化试样下降了10.5%,磁感B50比不常化试样提高了2.5%;常化使wSi=1.6%的无取向电工钢成品的平均晶粒尺寸增大,成品铁损P15/50相应减小;同时,常化使wSi=1.6%的无取向电工钢成品中高斯织构的强度增加,γ纤维织构的强度减弱,这有利于成品磁感B50的提高。 The effect of normalizing on microstructure,texture and magnetic properties of non-oriented electrical steel with wSi=1.6% produced by CSP process was investigated.The results show that,under the same cold rolling and annealing system,the iron loss(P15/50) of annealed samples whose hot bands has been normalized by 1 000 ℃×2 min process decreases by 10.5% and magnetic induction(B50) increases by 2.5% compared with the samples whose hot bands was not normalized.The average grain size of non-orient... 

本发明涉及一种提高取向硅钢冷轧加工性的生产方法，工艺流程为：冶炼、连铸、热轧、常化、酸洗、冷轧、脱碳渗氮、涂MgO、高温退火、涂绝缘层及热拉伸平整；粗轧中坯厚度35‑45mm，两段常化后进行带钢横向分段式冷却水分布。本发明通过对热轧中坯厚度、终轧温度及卷取温度，常化冷却水量及控制方式的调控，使轧前表层晶粒尺寸降低5‑10μm、珠光体体积分数降低6％，轧材冷轧加工性明显改善、成材率可提高8％以上。通过后续冷轧、脱碳退火和高温退火等工序处理，可保证完善的二次再结晶组织及良好磁性能。

本发明提供了一种取向硅钢的磁畴细化方法，属于高磁感取向硅钢生产技术领域技术领域，包括：采用激光在带钢表面烧蚀出若干沟槽；采用腐蚀液对所述沟槽进行腐蚀，获得刻槽；其中，所述沟槽与带钢宽度方向的夹角为0‑20°；所述沟槽的深度为0.5～20μm，宽度为30～200μm；所述刻槽深度为0.5～30μm、宽度为30～300μm。该方法能够显著的细化磁畴，降低取向硅钢片单位损耗，同时细化磁畴的效果能够承受800℃‑900℃的消除应力退火。本发明还提供了一种取向硅钢的磁畴细化方法在取向硅钢生产中的应用。

本发明涉及一种超纯净无取向冷轧硅钢中非金属夹杂物形貌的原位观察方法，包括如下步骤：制备无取向冷轧硅钢样品，将待测试面用打磨至1000#，使样品表面平整光滑，并进行机械抛光和表面清洗。对处理好的样品在电化学工作站上进行电化学腐蚀，电解液为：1~8wt%氯化物MCl溶液，余量为去离子水，通入CO2气体至饱和，加入适量NaHCO3和三乙醇胺作为稳定剂调节pH值将其稳定在6.0~6.5之间。电化学设定参数：开路：0.5~2h，动电位极化测试：扫描速率:0.1mV/S~1.0mV/S，测试区间：VS.SCE‑0.8V~0.2V，测试温度为：10~25℃。取不同区间内做完电化学腐蚀的样品用去离子水冲洗，吹干。通过扫描电子显微镜+能谱仪对非金属夹杂物的形貌进行原位观察和成分分析。