本申请涉及硅钢制造技术领域，尤其涉及一种去除耐热刻痕取向硅钢中熔覆物的化学试剂及其方法。所述化学试剂的组分以质量分数计包括：强酸溶液：8％～20％；酸性氧化剂：5％～15％或助剂：5％～20％；其余为溶剂；其中，所述强酸溶液包括硫酸、盐酸和硝酸中任意一种。本申请实施例提供的该方法，通过10％～20％强酸溶液，可快速有效地去除取向硅钢刻痕处的熔融物，而酸性氧化剂：5％～15％，或助剂：5％～20％结合合适浓度的强酸溶液，可以将取向硅钢的基体破坏降到最小，两种综合作用，得到表面平整的耐热刻痕取向硅钢。

1.本外观设计产品的名称：硅钢片横剪线。;2.本外观设计产品的用途：对硅钢片料带的冲切、裁断。;3.本外观设计产品的设计要点：在于形状与图案的结合。;4.最能表明设计要点的图片或照片：立体图。;

采用中、厚板坯生产技术对取向硅钢进行了研制和开发,对热轧及后工序样品进行了金相组织观察和EBSD分析,探讨了两种组织及织构的差异性,研究结果表明:除高温退火样品外,中板坯生产的取向硅钢各工序样品平均晶粒尺寸大;厚板坯生产的取向硅钢热轧和常化样品亚表层Goss织构强;中板坯和厚板坯的脱碳退火板织构没有明显区别。中板坯生产的取向硅钢成本低,产品磁性能和质量与厚板坯相当。 Grain oriented silicon steel was researched and developed by medium thickness slab and thick slab.Microstructures observation and EBSD analysis to the samples of hot rolling and following processes were carried out,respectively.The differences between the two kinds of microstructures and textures were discussed.The results show that the average grain sizes of every process samples are larger except that of high temperature annealing samples of grain oriented silicon steel produced by medium thic... 

主要研究了0.7%Si无取向电工钢退火试样的组织、晶粒尺寸和织构对其磁性能的影响。结果表明,随着退火温度的升高,晶粒尺寸逐渐增大,组织的均匀性得到改善;ɑ取向线上的纤维织构多集中于{114}<110>和{223}<110>附近,再结晶结束后,织构含量变化不大。{111}<110>织构取向密度值随温度升高而下降,{112}<111>织构与{111}<110>织构变化相反。晶粒尺寸增大对磁感强度的影响较小,而对铁损的影响较大。 Influences of microstructure,grain size and texture on the magnetic properties of 0.7% Si non-oriented electrical steels annealed samples were studied.The results show that with annealing temperature increasing the average grain size is increased gradually.Uniformity of the microstructure is improved;the textures of ɑ-fiber gathered in the vicinity of the { 114} < 110 > and { 223 } < 110 > texture.After recrystallization,the volume fraction of texture changes small.{ 111} < 110 &g... 

本发明公开了一种取向硅钢微观织构EBSD试样制样方法，包括：1)取样，采用线切割机制取向硅钢试样；2)制样，采用热镶嵌机镶制取向硅钢试样，按照常规方法进行粗磨、细磨、抛光、清洗、吹干；采用240目、400目、600目氧、800目、1000、2000目氧化铝砂纸对试样依次进行一次打磨处理；采用5.0um高效金刚石抛光剂对试样进行抛光处理；3)电解抛光，取向硅钢试样机械抛光后再进行电解抛光。

本发明涉及一种控制高牌号硅钢退火产生月牙印缺陷的方法，多次调整硅钢退火线入炉及出炉张力参数，使带钢处于预设悬垂量内；本发明避免高速运行下带钢撞在炉辊上，从而产生月牙印缺陷，提高了产品的质量。

以试验室模拟CSP工艺生产的Fe-3Si热轧钢带为研究对象,采用正交试验及方差分析的方法,研究了取向硅钢初次再结晶退火工艺对高温退火后获得锋锐的高斯织构的影响。结果表明:取向硅钢两段式初次再结晶脱碳退火工艺参数加热段保温时间及加热温度是高温退火后获得锋锐高斯织构的主要影响因素,其可信度分别在90%和85%以上;在本试验条件下,通过正交试验获得的最佳退火工艺为:冷硬板经600℃保温3 min和850℃保温6 min。 Fe-3Si hot rolled strip was produced by simulating CSP technology in the laboratory.Orthogonal experiment and analysis of variance were carried out to investigate the influence of primary recrystallization on the sharp Goss texture of the oriented silicon steel.The results show that holding time of the heating section and the heating temperature for a sharp Goss texture of the samples annealed has important implications in this experiment conditions,the two-step decarburization annealing process... 

2.9 mm热轧3%Si高牌号无取向硅钢板（/%:0.004 6C、3.04Si、0.32Mn、0.49Als、0.004S、0.013P、0.0042N）由CSP（Compact Strip Production紧凑式带材生产线）流程:120 t BOF-70 mm CC-热轧工艺生产。热轧终轧温度872℃,卷取温度683℃。铸坯及热轧板的组织和夹杂物的分析结果表明,铸坯组织为典型的贯穿柱状晶组织;热轧板边部为再结晶组织,中部为纤维组织带有少量再结晶晶粒;高牌号无取向硅钢的主要夹杂物为铸坯-Al₂O₃,AlN和Cu₂S+MnS;热轧板-Al₂O₃,AlN,AIN+MnS和Cu₂S+MnS。 The 2.9 mm hot rolled 3%Si high grade non-oriented silicon steel plate（/%:0.004 6C,3.04Si, 0.32Mn,0.49Als,0.004S,0.013P,0.004 2N） is produced by CSP（Compact Strip Production） flow sheet i.e.120 t BOF-70 mm CC-hot rolling process with end rolling at 872℃and coiling at 683℃.The analysis results on structure and inclusions in casting slab and hot rolled plate show that the structure of slab is typical trans-columnar crystal,the structure of hot rolled plate at edge is recrystallized grain and in ce... 

一种高强型高频电磁性能优异的硅钢薄带板，钢中化学成分按重量百分比计为：C≤0.0027％、Si3.10％～3.35％、Als0.80％～1.2％、Mn0.20％～0.85％、P≤0.050％、S≤0.0020％、N≤0.0020％、Ti≤0.0020％、V≤0.0020％、Nb0.0050％～0.080％，其余为Fe和不可避免的杂质。本发明的无取向硅钢薄带产品用于新能源汽车驱动电机的制造，其强度高，中高频电磁特性优异。

一种甩带法制备高磁性能含磷硅钢薄带的方法，属于合金材料领域。本发明以硅钢(Fe‑(3‑6.5)wt.％Si)块体为母合金，并添加一定量的硅铁合金及磷铁合金，放置于中频感应炉中，熔融后经快速凝固‑甩带、冷轧、热处理工艺，得到具有优异性能的含磷硅钢薄带。对于硅钢而言，P元素的少量加入能够有效的提升电阻率从而显著降低铁损，且具备优化软磁性能的作用。而采用甩带法能够充分利用其快速凝固的特征，从根本上避免了P元素在传统熔炼冷却过程中严重偏析的缺陷，极佳地保证了产品的组织优势与软磁性能。本发明具有操作简单、生产效率高、产品精度高、工艺流程短、无污染与夹杂、性能优异等优点。

本发明公开了一种电机制造硅钢片酸洗处理设备及其酸洗处理方法，该电机制造硅钢片酸洗处理设备包括开卷机、一号安装台、二号安装台、一号限位机构、二号限位机构、打磨装置、酸洗装置、干燥装置和切分装置。此外本发明还提一种电机制造硅钢片酸洗处理设备的使用方法,包括以下步骤：S1、硅钢卷安装开卷；S2、表面打磨；S3、硅钢酸洗；S4、表面干燥；S5、硅钢切分。本发明能够在硅钢片在酸洗前对其表面进行打磨处理，有效去除硅钢片表面较为明显的锈迹或者粘附有杂物，使得酸溶液能够与硅钢片表面充分接触反应，而且在硅钢片酸洗后能够及时干燥，有效防止酸溶液继续与硅钢片过度反应，达到提高产品质量的目的。

本发明涉及到一种应用于硅钢片冲压过程的冲压联动接料装置，包括固定连接在冲头侧面上的连杆，连杆一端远离冲头且连接有一根销，销上转动连接有摆杆，摆杆的一端开设有长孔，销插接在长孔内，摆杆另一端通过铰轴转动连接在机架上，摆杆设置有铰轴的一端连接有一根联臂，联臂下端通过转轴连接有接料盘，转轴与冲台之间设置有平行于转轴的托辊，托辊高于转轴，接料盘接近冲台的一端搁置在托辊上，冲头处于上止点时，接料盘接近冲台的一端伸入冲头和冲台之间且位于冲头正下方，冲头处于下止点时，接料盘接近冲台的一端退出冲头和冲台之间，位于冲台一侧，所述冲头下端面设置有凸模，冲台上端面设置有与凸模配合的凹模。