硅钢资料

近年来，在节能减排背景之下，国内外众多研究者对无取向电工钢磁性能的提升做了大量研究。为了探索无取向电工钢磁性能提升的方法，对锡或锑对无取向电工钢磁性能的作用机制(晶粒尺寸和晶体织构的控制)进行分析。基于该作用机制，介绍锡或锑的添加对无取向电工钢磁性能的影响。经研究发现，适量的锡或锑在晶界偏聚，不会阻碍晶界的移动并且致使晶粒尺寸降低；与此同时，锡或锑在晶界偏聚不仅抑制{111}织构在原始晶界处形核及生长，还降低(100)晶粒表面能，促进(100)晶粒生长。因此，适量添加锡或锑，可使无取向电工钢铁损下降、磁感提升。最后结合生产工艺，建议无取向电工钢的研究方向应为稀土含量对高牌号无取向硅钢夹杂物尺寸和数量分布的影响，锡或锑的添加量和常化工艺参数(常化时间、常化温度)对常化晶粒尺寸的影响。 In recent years, due to the background of energy saving and emission reduction, numerous researchers all around the world have done a lot of investigations on the improvement of magnetic properties for non-oriented electrical steel. In order to explore the method of improving the magnetic properties of non-oriented electrical steel, the mechanism of tin or antimony on the magnetic properties(the control of grain size and crystallographic texture) of non-oriented electrical steel is illuminated. ... 

本实用新型公开了一种硅钢板带生产加工用除油烘干装置，包括壳体，所述壳体的外表面上对称设置有电机，所述电机的输出端固定连接有输送带，所述壳体的顶部设置有机体，所述机体的内部设置有除油机构，所述除油机构的一侧设置油烘干机构，所述壳体的底部设置油收集箱，所述收集箱的内部设置有收集槽。本实用新型，利用除油机构可对成硅钢板带生产后进行一定的除油处理，除油的效果更好更彻底，同时相比以往的方式提高了一定的工作效率，具有一定的实用性，利用烘干机构可进行除油后的成硅钢板带进行烘干处理，防止水渍残留在表面上，影响一定的美观效果，具有一定的实用性。

针对不同牌号的无取向硅钢产生结疤缺陷的难易程度和表面结疤缺陷的外形特征及分布规律,分析了该缺陷产生的原因。通过调整剪前导板的对中度,设置精轧侧导板开度余量及短行程数值,及时修补与更换侧导板,减少带坯与侧导板挤撞程度,有效地降低了结疤缺陷发生率。 This article analyses the cause of the scab defects according to the defects appearance characters and distribution law,degree of difficulty to form scar of non-oriented silicon steel. It can effectively decrease the scabs by different methods,such as adjusting the center line of guide plate,setting the opening margin and short stroke value of the side guide on finishing mill,timely repairing and replacing of side guide,decreasing the collision between the strip and side guide. 

本发明公开了一种消除取向硅钢热轧边裂的制造方法，通过成分设计、热轧加热和轧制参数优化等方面控制方面，有效解决取向硅钢热轧板边裂缺陷，提高材料的成材率，可以有效消除取向硅钢热轧板的边裂并能保证良好的成品磁性能。

通过对35W300高牌号0.35 mm冷轧无取向电工钢卷(/%:0.002C、2.71Si、0.22Mn、0.015P、0.003S、0.0020N、0.55Als)头、中、尾组织、织构及对应的磁性能的试验研究,发现因热轧时12 MPa高压水连续冷却造成接触轧辊的钢卷头、中、尾在不同温度下轧制,卷取后钢卷头部处于卷心、温度略高而冷却速度略低于钢卷尾部,致使钢卷纵向组织、织构不同,成品卷头、尾各250 m内磁感逐渐增加,铁损逐渐降低,250 m外至钢卷中部磁性能稳定。通过将热轧辊的冷却方式改为周期冷却和卷取后的层流冷却改为钢卷70 m后开始冷却,至钢卷尾部70 m前停止冷却的方式使得钢卷纵向铁损差异明显减小,磁感差异略有改善。 According to the test research on structure and texture of head,meddle and end of 35W300 high grade 0.35 mm cold rolled non-oriented electrical steel strip coil(/%:0.002C,2.71Si,0.22Mn,0.015P,0.003S,0.002 0 N,0.55Als) and corresponding magnetic properties,It is found that due to 12 MPa high pressure water continuous cooling the roller in hot rolling process led to head,middle and tail of strip rolling at different temperature and after coiling the head of strip coil being in center of coil led t... 

本实用新型公开了一种薄带取向电工钢的热处理炉板，炉板的中心设置有气流循环通孔，炉板的硅钢卷预定压接面设置有通气槽，炉板内设置有进气孔，进气孔的第一孔口设置于通气槽中，进气孔的第二孔口设置于炉板的侧壁上。该薄带取向电工钢的热处理炉板在设置通气槽的基础上，进一步设置进气孔，通过向进气孔中导入气流，增加通气槽的进气量，有助于硅钢卷与炉板压接侧边处水蒸气的及时排出，进一步提高卷内硅钢的热处理品质。本实用新型还公开了一种包含热处理炉板的薄带取向电工钢罩式炉。

针对传统工艺生产硅钢周期长、能耗大等缺点,采用双辊连铸工艺制备3%Si无取向硅钢连铸薄带,利用MEM,SEM和TEM观察了铸带的组织、织构及析出物,同时对比了Al的质量分数为0.6%和0.9%的连铸薄带在组织、织构及析出物特征方面的异同.结果表明:双辊连铸工艺生产的3%Si无取向硅钢铸带的组织为均匀等轴晶粒,平均晶粒尺寸约为300μm;织构组成随Al质量分数的不同具有明显差别,Al质量分数为0.9%的铸带中{100}织构强度是随机织构的7倍;铸带中的析出物为AlN和MnS,最大尺寸分别为500和50 nm左右. Given the lengthy production cycle,high energy consumption,and other shortcomings of the traditional process for producing silicon steel,a twin-roll casting process was used to produce 3%Si non-oriented silicon steel casting strips. MEM,SEM,and TEM were used to compare micro-structure,texture,and precipitate characteristics of a casting strip containing 0.6%Al with another containing 0.9%Al.The structure of 3%Si non-oriented silicon steel produced by the twin-roll casting process was a uniform i... 

研究了薄板坯连铸连轧流程(TSCR)条件下热轧工艺对3.2%Si-0.7%Al无取向硅钢组织、织构演变及磁性能的影响规律。结果表明,提高均热温度和热轧温度有助于获得粗大的变形组织和强烈的{001}〈110〉织构,进而对后续的组织、织构演变进程及磁性能产生有利的遗传影响。与低温均热和低温热轧相比,高温均热和高温热轧得到的最终成品板的再结晶晶粒较粗大,λ纤维再结晶织构较强而γ纤维再结晶织构较弱,磁感应强度较高。 It was investigated that the effects of thin slab cast rolling(TSCR) hot rolling processes on microstructural,textural evolution and magnetic properties of 3.2%Si-0.7%Al non-oriented silicon steel.The results show that much larger hot rolling deformed microstructure and much stronger {001}〈110〉 texture could be obtained by increasing the soaking and hot rolling temperatures,which had good heritable effects on subsequent microstructural,textural evolution and magnetic properties.The final sheets ... 

本实用新型公开了一种硅钢片表面涂漆装置，包括平台，所述平台的上表面固定安装有固定框，固定框的内顶壁开设有矩形槽，矩形槽的两侧内壁转动连接有丝杠，且固定框的侧面设置有用于驱动丝杠转动的驱动电机，丝杠的表面螺纹连接有移动块，移动块的下表面固定安装有连接杆。该硅钢片表面涂漆装置，在对硅钢片进行喷涂时，能够将硅钢片挂在挂钩上，并启动驱动电机带动丝杠转动，从而使硅钢片移动至雾化喷头的位置后，在喷涂泵和旋转电机的作用下对其进行旋转喷涂，从而有效的提高了喷涂的均匀度，同时喷涂完成后，驱动电机反转，并启动暖风机，在硅钢片向外移动的过程中通过蛇形管道对其进行热风干处理，简单便捷，有效的提高了工作效率。

主要对硅钢退火炉耐材施工进行阐述,对一期工程与二期工程施工经验进行总结,包括设计、施工、耐材生产、人员素质等方面,指出了工程项目所所存在的不足,为同类型炉窑的施工提供借鉴。 This paper describes the construction of silicon steel annealing furnace refractories;and it was summarized the construction experience of phase-Ⅰ and phase-Ⅱ projects,including design,construction,refractory production,the quality of personnel etc,and pointed out the shortcomings of the project,which provided a reference for the construction of the same type of furnaces. 

提供一种如下的无取向性电磁钢板用钢板：含有：C：0.0040％以下、Si：1.9％以上3.5％以下、Al：0.10％以上3.0％以下、Mn：0.10％以上2.0％以下、P：0.09％以下、S：0.005％以下、N：0.0040％以下、B：0.0060％以下；剩余部分由Fe和杂质构成；分别从板宽方向的两端部向板宽中央10mm的各位置的板厚方向截面组织的重结晶率不足50％；将板宽记为W时，分别距板宽方向的两端部1/4W的位置的板厚方向截面组织的重结晶率在50％以上。

以水氯镁石为原料,采用氨法沉镁-煅烧-添加剂的方法制备硅钢级氧化镁。考察了反应温度、反应pH值、陈化时间对中间体氢氧化镁纯度及转化率的影响;研究了煅烧温度和煅烧时间对氧化镁水化率的影响及添加剂的量对氧化镁悬浮性能的影响。控制实验条件为:反应温度55℃,pH值为9.5,陈化时间2h,煅烧温度1050℃,煅烧时间2h,添加剂量为0.8%,制得氧化镁的纯度为98.99%、水化率为2.92%、悬浮性能为3mm/h,达到硅钢级氧化镁的要求。 Using bischofite as raw material,the preparation of magnesium oxide with silico-steel grade was studied.The effects of reaction temperature,reaction pH value and aging time on the intermediate magnesium hydroxide purity and conversion rate were studied.Calcinations temperature,calcinations time relationship to the hydration rate of MgO and amount of additive to the suspension performance of MgO were investigated.The results indicated that the optimum technological conditions were as follows:reac...