硅钢资料

通过固溶度积公式计算及热模拟实验,对不同热装和加热温度条件下的无取向硅钢铸坯中析出相进行了研究.在低于950℃热装时,铸坯中AlN的析出量和尺寸不再变化,但MnS和AlN-MnS的数量及平均尺寸随着热装温度降低而进一步增加,并在温度低于600℃时达到最大值后保持不变.与1200℃相比,1100℃加热的铸坯中AlN、MnS的总固溶量相对更少.相比850℃热装,600℃热装再加热到1100℃的铸坯中AlN和MnS的总固溶量更少,且AlN和MnS尺寸更大.合适的热装温度和加热温度分别为600℃和1100℃. Based on solubility product calculation and thermal simulation experiments,precipitated phases in continuous casting slabs of non-oriented silicon steel were systematically studied at different hot charging and heating temperatures.When the hot charging temperature is below 950 ℃,the content and size of AlN remain unchanged,but the quantity and size of MnS and AlN-MnS increase when the hot charging temperature decreases,reach maximum and remain unchanged when the hot charging temperature is belo... 

研究了激光加热辅助圆盘剪高速切割技术,以解决现有冷轧生产线硅钢切边技术存在的微裂纹、应力、毛刺和边浪等问题。建立了激光加热温度场有限元分析模型,根据生产线上圆盘剪加工的实际过程,探讨了数值模拟中热源的加载形式,研究了激光对板材进行辅助加热时各个工艺参数如激光功率、光斑尺寸以及激光入射角度对切割工艺的影响,并通过实验对工艺参数进行了优化。最后,进了验证实验。实验结果显示:当激光加热点运动至圆盘剪刃口位置时,温度为100℃左右,此时材料硬度降低到原有硬度的70%~80%,降低了切削力,减少了圆盘剪的磨损,可有效提高圆盘剪的寿命。 Laser assisted trimmer side cutting technology was studied to overcome the problems such as micro cracks,stress,burrs and edge waves existing in a cold rolling production line of silicon steel side cutting.A finite element analysis model for the laser hearting temperature field was established, the loading form of a heating source was determined and influences of various processing parameters like laser powers,spot sizes,and laser incident angles on laser assisted heating sheet materials were di... 

对新能源汽车以及驱动电机的现有市场和未来市场规模进行梳理分析，通过自建计算公式推导出我国2021年1-11月份驱动电机用电工钢的总量，进而预测未来10年中国新能源汽车驱动电机用电工钢情况，为无取向电工钢的生产和在电机中的应用提供有价值的参考。 The current market and future market size of new energy vehicles and traction motors were analyzed,and the total amount of electrical steels used in traction motors in China from January to November 2021 was derived by using self-built calculation formulas,and then the situation in the next ten years of electrical steel used in traction motors of new energy vehicles in China was predicted.It will provide a valuable reference for the production of non-grain oriented electrical steel and its appli... 

研究了传统工艺流程生产的2%Si无取向电工钢在不同退火温度下的磁性能。研究结果表明,随着退火温度的升高,显微组织均匀性提高且晶粒尺寸增大;有利织构组分{100}<0vw>、α、η增强,不利织构组分减弱;成品的铁损P1.5/50先下降后略有上升,磁感B50上升平缓;在890℃×2 min的退火工艺条件下,成品电工钢的磁性能最佳,对应的铁损P1.5/50小于3.2 W/kg,磁感B50高于1.74 T。 In this paper,the effect of annealing temperature on magnetic properties of non-oriented electrical steel with 2% silicon was studied.Results show that the uniformity of microstructure and the average grain size increase with the rise of annealing temperature.The texture components of annealing can be improved by enhancing {100} <0vw>,α,η fiber textures and weakening {111} <112> fiber texture.The tendency of core loss P1.5/50 shows that it decreases first and then increases,while the... 

本发明涉及电工钢的生产方法，更具体地说，涉及一种预应力生产中低牌号无取向电工钢的方法，包括铁水预处理；预处理后的铁水进行转炉冶炼并吹氩脱氧；吹氩后的钢水送入精炼炉中进行冶炼并加入低碳合金进行合金化；合金化处理的钢水通过薄板坯连铸机铸成板坯并采用薄板胚连铸连轧生产工艺进行轧制获得热轧板；所述热轧板经过酸洗冷轧，随后进行预应力拉伸并退火，采用涂层进行涂镀、烧结后卷取。本发明采用预应力拉伸，改善无取向电工钢退火前钢板内部应力的分布，制备的冷轧无取向电工钢产品的电磁性能P15/50≤5.4W/kg，磁感应强度≥1.72T，板形同板差≤8um。

采用火花源原子发射光谱分析测定电工钢中超低C,研究试样制备方法、Ar纯度和压力等条件对分析结果的影响,并对工作曲线进行了优化,实现了一次分析同时测定电工钢的多种元素,满足炉前和精炼在线分析的要求。 Ultra-low carbon in electrical steel is determined with spark-source atom emission spectrum.It is researched the influence of sample making method,purity of Ar,and pressure on analysis result.The work curve is optimized.The determination of many elements in electrical steel only in one analysis is realized.It meets demands of on-line analysis for blast furnace and refining. 

【摘要】 <正>3月底,宝钢\"低温高磁感取向硅钢制造...

本发明属于硅钢制造技术领域，具体涉及一种改善硅钢热轧板边部质量的加工方法，包括：连铸、铸坯预变形处理、铸坯加热处理和热轧处理；其中，所述铸坯预变形处理包括：在所述铸坯的温度为500～900℃下，对所述铸坯的沿长度方向的两侧壁通过立辊施加压力，直至形变量h为10～50mm；所述铸坯加热处理的加热温度为1100～1200℃，保温时间为4～6h。本发明提供的改善硅钢热轧板边部质量的加工方法，采用铸坯两侧壁的侧压工艺，有效解决了热轧板边部裂纹的缺陷，提高了边部塑性，提高了成材率并降低了生产成本。

根据本发明的一个实施例的无取向电工钢板，以重量％计，所述钢板包含Si：2.2至4.5％、Mn：0.5％以下且0％除外、Al：0.001至0.5％、Sn：0.07至0.25％和N：0.0010至0.0090％，余量包含Fe和不可避免的杂质。所述钢板包含从钢板表面向内存在的表层部和存在于表层部里面的中心部，中心部包含0.005重量％以下的N，所述表层部比中心部更包含0.001重量％以上的N，表层部的平均晶粒粒径为60μm以下，中心部的平均晶粒为70至300μm。

本实用新型提供了一种轴向磁通电机转子的硅钢盘，所述硅钢盘具有沿周向间隔排列的多组转子槽，相邻的两组转子槽之间界定了一硅钢块，每组转子槽的数量为两个，且相对设置于所述硅钢盘轴向的两侧，每组的两所述转子槽之间界定了一连接相邻两所述硅钢块的连接筋，多个所述硅钢块通过连接筋连接，并形成一整体的硅钢盘，相对现有技术独立成型多个硅钢块来说，不仅避免硅钢块丢失，还有效提升硅钢盘装配为转子盘的成型效率，以及保证各硅钢块在转子盘上的位置一致性，从而大幅增强转子盘的机械可靠性。

本实用新型公开了一种用于激光切割的铁芯硅钢片夹持装置，包括固定座，所述固定座的上方设置有底板，所述底板的上方设置有压板，所述压板与底板的内部且靠近前后侧边缘处均活动连接有转动辊，所述转动辊的表面活动连接有输送带，所述固定座的表面开设有排料口，所述底板的上表面开设有泄料口，所述压板的上表面开设有加工预留口，所述压板的内部且位于转动辊之间固定连接有转轴，所述转轴的表面固定连接有从动锥齿轮，所述压板的内部且靠近左侧边缘处固定连接有电机，所述电机的输出端固定连接有转动杆。本实用新型，该装置结构简单合理，能很好地解决现有技术的不足，能实现在夹持的时候进行送料工作，有利于提高硅钢片的加工效率。

【摘要】 <正>为了确保电工钢的产品质量,在生产线...