硅钢资料

传统轧制法制备6.5wt.%高硅钢过程中温轧工艺具有显著不同于3 wt.%Si的电工钢的特点及组织织构特征,是开发新型基于织构优化的高硅钢的关键环节。采用EBSD技术对通过热轧、温轧、冷轧及退火工艺制备0.3mm厚的6.5wt.%Si电工钢板的组织和织构进行分析,重点研究温轧过程中的中间退火和大、小压下率组合以控制织构。结果表明,在热轧退火板是部分再结晶组织的情况下,一次性温轧或先小形变量、中间退火后再大形变量的工艺可得到更多的Goss晶粒;经过最终退火后Goss取向会发生偏转,形成部分黄铜取向,而{111}〈112〉取向的晶粒内形核生成近Goss取向的再结晶晶粒;大压下量轧制是最终组织中{111}取向晶粒较多的主要原因。 Warm rolling,a key process of developing new type high-Si electrical steel based on texture optimization,has significant different characteristics from 3wt% Si steel in conventional preparing process. 0. 3mm thickness 6. 5wt. % Si steel,obtained by a series of processes including hot and warm rolling,intermediate annealing and then cold rolling,was analyzed from microstructure and texture by EBSD,which are utilized mainly for investigating the intermediate annealing process and the combination o... 

在实验室模拟CSP流程制备了不同含量稀土铈(质量分数0~0.018%)的1.2%Si无取向电工钢,并对其进行1 000℃×5min的再结晶退火处理,研究了铈质量分数对无取向电工钢夹杂物、显微组织、再结晶织构和磁性能的影响。结果表明:随着铈质量分数的增加,微细夹杂物数量、再结晶晶粒尺寸、{100}和{110}织构组分、磁感应强度先增后减,{111}织构组分、铁损先减后增;铈的质量分数为0.005 1%时,钢中的夹杂物数量最少,再结晶晶粒尺寸最大,有利织构最多,磁性能最优,铁损P15/50为3.253W·kg-1,磁感应强度B50为1.751T。 Non-oriented electrical steels containing different contents rare earth Ce element(0-0.018wt%) were prepared in the laboratory by simulated CSP(compact strip production)process,and then recrystallization annealing at 1 000 ℃ for 5 min were performed,the effects of Ce content on inclusion,microstructure, recrystallization texture and magnetic properties of non-oriented electrical steels were studied.The results show that with the increase of Ce content,the amounts of fine inclusion,the size of re... 

本实用新型属于输送设备技术领域，具体涉及一种硅钢拉伸平整用转向辊，包括辊本体，辊本体的中部可拆卸的安装有环形凸块，环形凸块的宽度在350‑450mm，环形凸块的厚度在3‑5mm。在本方案中，在辊本体的中部设置环形凸块，环形凸块能较好的与硅钢的中部位置接触贴合，辊本体通过环形凸块除了能较好的将硅钢输送向前，还能有效防止硅钢跑偏。环形凸块可拆卸的安装辊本体上，当环形凸块使用了一段时间发生了严重的磨损时，更换新的环形凸块即可，无须更换辊本体，有效节省成本。

根据本发明的一个实施例的双取向电工钢板，具有从{100}＆lt;001＆gt;起15°以内的取向的晶粒的分数为50至75％，并且具有从{100}＆lt;380＆gt;起15°以内的取向的晶粒的分数为50至75％。

通过后天抑制剂获得法制备了取向硅钢,对渗氮前后和高温退火升温阶段析出物的析出和转化规律进行了研究。研究结果表明,渗氮前脱碳退火态基体中存在少量的粗大AlN颗粒和细小AlN颗粒,渗氮处理后新析出大量的Si3N4析出物,高温退火升温阶段Si3N4将转化为(Al,Si)N,随着温度的继续升高(Al,Si)N颗粒将发生粗化,(Al,Si)N是后天抑制剂获得法制备取向硅钢的主要抑制剂。 Grain-oriented silicon steels were produced by acquired inhibitor method.The rule of precipitate transformation was studied after nitriding treatment and high-temperature finishing annealing.The results show that a small amount of large AlN and fine AlN are found in matrix before nitriding treatment,and a large amount of Si3N4 is precipitated in matrix after nitriding treatment.During the temperature rising period of high-temperature finishing annealing,Si3N4 would transform into(Al,Si)N,and(Al,... 

通过测试取向硅钢不同工艺条件下的碳含量,探讨了CGO取向硅钢碳含量控制的最优处理条件,研究了脱碳温度和脱碳时间对相同初始碳含量取向硅钢的脱碳效果的影响。结果表明,在气氛为(15%~20%)H2+(75%~80%)N2,炉压差为10~20 Pa的条件下,CGO取向硅钢合适的脱碳温度为1 073 K~1 123 K,脱碳时间为10~20 min。在该处理条件下,能取得较好的脱碳效果。 By means of testing carbon content of oriented silicon steel below the distinct technical conditions,inquires the excellent handle terms of carbon content controlling for CGO oriented silicon steel,studies effects of decarburization annealing temperature and decarburization annealing time to the oriented silicon steel decarburization efficiency in same initial carbon content.The results show that,under the condition of atmosphere(15% ~ 20%) H2+(75% ~ 80%)N2 and furnace pressure difference 10 ~ 2... 

研究了热轧卷取时间对无取向电工钢晶粒组织、织构演变、铁损和磁感的影响。结果表明,成品晶粒尺寸在120～140μm之间,随卷取时间的增加,成品晶粒尺寸增大。成品织构主要由γ纤维、а纤维和高斯织构等构成。随着保温时间的增加,{111}<110>和{112}<110>织构强度降低。随卷取时间的增加,成品P1.5降低。热轧板最佳的卷取工艺为550℃保温2～3 h,电工钢的综合磁性能优良。 The effects of hot-rolling coiling time on microstructure,texture,core loss and magnetic induction of a new cold-rolled non-oriented electrical steel containing copper were investigated.The test results showed that for final product the grain sizes are 120-140um,with the increase of coiling time,the grain size increase.For final product there are mainly γ-fibre,а-fibre,and {110}<001> texture,Coiling at 550℃ for hot rolled plate,the {111}<110>,{112}<110> texture was weaked with ... 

本发明提出了一种无机绝缘漆，由下列物质组成，其重量百分比为：质量百分含量为50～55％的磷酸二氢铝溶液：30～70％；质量百分含量为60～70％的磷酸二氢锰溶液：10～15％；质量百分含量为80～85％的硼酸溶液：5～6％；质量百分含量为99％的硅烷偶联剂溶液：1～5％；质量百分含量为30～35％的硝酸盐溶液：0.1～0.5％；硅溶胶：10～15％；纳米硅酸铝：10～15％；纳米二氧化硅：20～30％；消泡剂：1～5％；水溶剂：适量。本发明采用磷酸二氢铝、纳米二氧化硅为主料制备了一种极薄硅钢带薄绝缘无机绝缘漆的涂层，涂层厚度均匀性好，涂层表面光亮、附着性强、绝缘电阻系数高。

通过固溶度积公式计算及热模拟实验,对不同热装和加热温度条件下的无取向硅钢铸坯中析出相进行了研究.在低于950℃热装时,铸坯中AlN的析出量和尺寸不再变化,但MnS和AlN-MnS的数量及平均尺寸随着热装温度降低而进一步增加,并在温度低于600℃时达到最大值后保持不变.与1200℃相比,1100℃加热的铸坯中AlN、MnS的总固溶量相对更少.相比850℃热装,600℃热装再加热到1100℃的铸坯中AlN和MnS的总固溶量更少,且AlN和MnS尺寸更大.合适的热装温度和加热温度分别为600℃和1100℃. Based on solubility product calculation and thermal simulation experiments,precipitated phases in continuous casting slabs of non-oriented silicon steel were systematically studied at different hot charging and heating temperatures.When the hot charging temperature is below 950 ℃,the content and size of AlN remain unchanged,but the quantity and size of MnS and AlN-MnS increase when the hot charging temperature decreases,reach maximum and remain unchanged when the hot charging temperature is belo... 

本实用新型涉及硅钢片生产技术领域，特别涉及一种电机硅钢片冲槽生产线，包括支架，支架下方依次设有:毛坯料垛，毛坯料垛由待冲毛坯片堆成，待冲毛坯片中心具有通孔；理片机；定子冲槽机，定子冲槽机用于在毛坯片上冲裁形成已冲毛坯片，已冲毛坯片包括定子片和转子坯片；第一液压升降机，第一液压升降机用于承载定子片；转子冲槽机，转子冲槽机用于冲裁转子坯片从而形成转子片；第二液压升降机，第二液压升降机用于承载冲裁得到的转子片；输送装置，输送装置用于输送待冲毛坯片、已冲毛坯片、转子坯片或转子片，本实用新型提出一种适用范围广、运行效率高、结构简单、价格适宜的电机硅钢片冲槽自动线。

研究了电工钢SXRC的显微结构和疲劳性能,并与DP钢进行了比较。结果表明,退火温度低温化能够有效的抑制电工钢的再结晶。该钢在固溶铌的作用下,能够在保证电机磁性的同时具有一定的强度。与DP钢相比,SXRC钢的抗疲劳性能更好。 The microstructures and fatigue properties of the electrical steel SXRC we re investigated, and the properties were also compared with the steel DP. The results show that the recrystallization of the electrical steel can be suppressed at lower annealing temperature. The steel presents favorable motor magnetic and also a compatible strength with the help of solid-solution Nb. Compared with the steel DP, the fatigue resistance of the steel SXRC is preferable. 

本实用新型公开了一种硅钢炉底辊套管生产用原料破碎装置，包括外壳和固定圆板，所述外壳的端面设置有密封盖和两组电机，两组所述电机的输出端均贯穿外壳的端面，两组所述电机的输出端均卡接安装有破碎辊，所述外壳的内部转动安装有循环滤网管，两组所述破碎辊的下方安装有提示收集箱，所述外壳的下部固定贯穿安装有出料管，且出料管的侧壁安装有电磁阀，所述密封盖的端面固定贯穿安装有四组进料管，且四组所述进料管的外置端端部均固定安装有安装法兰。有益效果：本实用新型采用了循环滤网管，通过设置的循环滤网管，能够对不合格的原料颗粒进行多次破碎，为硅钢炉底辊套管生产用原料破碎装置的破碎工作带来一种保障。