分析了冲裁硅钢芯片时出现的质量问题,针对影响硅钢芯片冲裁质量的4大因素——人、原材料状态、工艺和工装进行了工艺试验和分析,根据原材料状态的差异,采用不同工艺方案,特别是如何合理选择冲裁模具间隙,解决了硅钢芯片冲裁时产生的主要质量问题,使冲裁的硅钢芯片达到最佳质量状态,并满足硅钢芯片的使用性能。 The problems occurred during silicon steel chip punching and the factors that affect the quality of silicon steel chip punching were analyzed,the factors include 4aspects,that is,people,raw material status,process and frock,at the same time,process tests and analysis aimed at the factors that affect punching quality were did,according to the difference of raw material status,corresponding process schedules wee taken,especially in how to reasonably select punching dies clearance,which solved the ... 

本发明属于硅钢制备技术领域，具体涉及一种无底层取向硅钢的制备方法。其中，所述脱碳退火的过程中，带钢表层的氧化膜厚度为1.5～2.5μm；所述氧化膜中Si元素和Fe元素的原子重量比满足：Si/(Si+Fe)≥0.76；所述高温退火的过程中，冷却段依次包括：在温度为1200～500℃时，罩内冷却；其中，保护气体为包括有氮气和氢气的混合气体，所述混合气体中氢气的体积百分比＞3％；在温度为500～200℃时，罩内冷却；其中，保护气体为氮气；在温度＜200℃时，揭开内罩进行空气冷却。本发明提供的无底层取向硅钢的制备方法中，通过控制带钢在脱碳退火阶段的氧化膜厚度以及高温退火的冷却段等一些工艺，从而得到了表面光洁化好、表面均质化好、成材率高、磁性能优良的无底层取向硅钢。

冷轧中中低牌号的无取向硅钢多采用万能凸度轧机(Universal crown mill,UCM)生产,其板形好坏受制于UCM轧机板形调节手段的协调使用。为掌握UCM轧机的板形控制特点,建立基于二维变厚度有限元的辊系弹性变形和基于三维差分的轧件塑性变形的六辊轧机耦合模型,对UCM轧机的板形调控性能进行详尽的分析,包括工作辊和中间辊弯辊、中间辊窜辊的调控功效、辊间接触压力分布等。在此基础上,提出可用指导生产的板形控制策略,指出UCM轧机在横向厚差控制方面的不足。针对工业生产中UCM轧机轧制无取向硅钢横向厚差大的问题,在大量仿真计算的基础上,开发具有高次曲线函数的边部变凸度(Edge variable crown,EVC)的工作辊。采用该工作辊后,各种品种的无取向硅钢的横向厚差不大于10μm的百分比由24%提高到99%,横向厚差的均值小于6μm,远小于之前的13μm。 Medium-low grade non-oriented silicon steel is rolled often by universal crown mill(UCM) during cold rolling.Its shape quality is dependent on the coordinated control of several shape adjustment devices of UCM.In order to understand the shape control characteristics of UCM,coupling model of six-high rolling mill,based on two-dimensional varying thickness finite element rolls elastic deformation model and three-dimensional finite difference strip plastic deformation model,is setup for the detaile... 

本实用新型涉及一种便于拼装硅钢片的变压器铁芯，包括铁芯，设置在固定座的上方；硅钢片，固定安装在铁芯的侧壁上；连接座，固定在铁芯的底部，并安装在固定座上；有益效果是：本实用新型通过加入固定座和连接座的结构，方便将铁芯固定安装在固定座上，防止在对铁芯和硅钢片的拼装时，铁芯位置变化，造成铁芯和硅钢片碰撞磨损，通过转动环的转动结构，以及牵引绳的从动结构，有效控制卡柱的收缩，方便将连接座安装在固定座上，防止卡柱与连接座底部碰撞造成其损伤，硅钢片的两端均设置有规格相同的卡块，防止硅钢片出现反向安装的情况出现。

本实用新型公开了一种硅钢片二次搭接夹具，包括底座、位于底座顶部的调节板以及位于调节板顶部一端的固定杆，所述底座包括设置在底座内部顶端中间位置处的活动槽。本实用新型通过连接块将第一夹钳与第二液压缸的输出端相连接，通过第一夹钳和第二夹钳对硅钢片进行固定，将焊条焊接在一组硅钢片上，伺服电机带动调节杆发生转动，调节杆外侧的外螺纹和活动块内部的螺纹孔相互配合，可使活动块在活动槽内部发生活动，通过活动块带动调节板发生前后移动，从而使对硅钢片进行前后一端，通过滑轨使调节板的移动更加稳定，使两组硅钢片相对齐，通过固定块使第一液压缸带动调节架左右移动，使焊条与两组硅钢片紧密接触，实现二次搭接。

本实用新型公开了一种变压器硅钢片剪切收料装置，其包括底板和存放架推出机构，底板的前侧中部设置有用于放置外设剪切设备的放置区；存放架推出机构包括滑动板座、锁紧组件，滑动板座可左右滑动地安装于底板的上表面，在滑动板的上表面设置有两个用于放置外设的硅钢片存放架的存放架放置槽，两个存放架放置槽呈左右间隔设置，锁紧组件用于锁紧滑动板座与底板之间的相对位置。当该硅钢片存放架存放完后，将滑动板座推动至使得另外一个存放架放置槽设置于放置区的正后方，另外的硅钢片存放架继续接受剪切设备掉落的硅钢片体，可连续地实现硅钢片体的落料存放，令转运和落料的操作不相互干涉，提高生产的效率。

本实用新型涉及硅钢技术领域，尤其为一种用于硅钢绝缘涂料生产用储存装置，包括储存装置、顶盖和定位板，所述储存装置与顶盖铰链连接，所述顶盖内侧后端固定连接有定位块，所述定位块前端转动连接有连接块，所述连接块的另一端内侧转动连接有转动杆，通过设置的定位块、连接块、转动块、转动杆、推杆、档杆、挡块、弹簧、固定板和垫片，在使用时，盖上顶盖后，通过推动推杆，使推杆通过转动块带动转动杆在连接块内转动，推杆推动挡块，使挡块通过档杆挤压弹簧，从而对推杆进行限位，然后带动连接块在定位块上转动，从而使连接块挤压固定板，使固定板带动垫片，使垫片与储存装置贴合更紧，防止漏气，防止空气进去，防止涂料干燥。

主要研究了0.7%Si无取向电工钢退火试样的组织、晶粒尺寸和织构对其磁性能的影响。结果表明,随着退火温度的升高,晶粒尺寸逐渐增大,组织的均匀性得到改善;ɑ取向线上的纤维织构多集中于{114}<110>和{223}<110>附近,再结晶结束后,织构含量变化不大。{111}<110>织构取向密度值随温度升高而下降,{112}<111>织构与{111}<110>织构变化相反。晶粒尺寸增大对磁感强度的影响较小,而对铁损的影响较大。 Influences of microstructure,grain size and texture on the magnetic properties of 0.7% Si non-oriented electrical steels annealed samples were studied.The results show that with annealing temperature increasing the average grain size is increased gradually.Uniformity of the microstructure is improved;the textures of ɑ-fiber gathered in the vicinity of the { 114} < 110 > and { 223 } < 110 > texture.After recrystallization,the volume fraction of texture changes small.{ 111} < 110 &g... 

以太钢热连轧厂的硅钢为研究对象,利用凸度仪测量热轧带钢出口凸度值,采用矩阵和失效模式的分析方法了解影响带钢凸度变化的主次因素。研究结果表明:通过有效控制轧制过程中的加热温度、时间及采用合理的辊型,硅钢凸度精度提高了4.34%左右。 In this paper,we take the hot-rolled silicon steelsheet of Taigang as the research symbol,exit profile was measured by convex instrument,the primary and secondary factors that affect the strip profile were measured by using matrix and failure mode analysis methed.The results indicate that convexity accuracy has significantly improved by nearly 4.34% through the effective control of the heating temperature,heating time and the use of correct roller type in the process of hot rolling. 

针对宝钢集团、日本新日铁住金和JFE公司公开的相关专利等资料,总结了国内外高强度无取向电工钢的研究进展,分析了不同电工钢的化学成分、生产工艺及产品性能,指出固溶强化、细晶强化、析出强化、位错强化都有可能被用来提高无取向电工钢的强度,并阐述了四种强化方式的优缺点;指出在高强度无取向电工钢的研发过程中,需根据其具体用途确定目标性能,再采用合适的强化手段,最终实现力学性能、磁性能和生产性能之间的平衡。 The research progress of high strength non-oriented electrical steels at home and abroad is summarized according to related patents brought into the public by Baosteel,Nippon Steel & Sumitomo Metal corporation and JFE corporation.The characteristics of chemical composition,production technology and properties of products in the patents are analyzed.Each of solution strengthening method,fine-grain strengthening method, precipitation strengthening method or dislocations strengthening method ma... 

对冷轧无取向硅钢在冶炼过程中各个工序的顶渣进行了检测,分析了顶渣变化原因,并得出结论:硅钢生产宜采用复吹转炉,以降低吹炼终点渣中TFe含量,进而减轻对精炼的压力;使用低S、低Al2O3含量中间包覆盖剂;RH脱氧及合金化顺序采用先加硅铁后加铝;首罐宜经LF提温并降低渣中TFe。 The top-surface slag used for the various production processes in smelting coldrolled non-oriented electrical steel is tested and based on tested results the cause of the top surface slag change is analyzed.So it is concluded that the combined blown converter is more suitable to be used for smelting electrical steel in order to reduce the content of TFe in slag at blow end point and then much better results can be achieved during the period of refining.Secondly the tundish flux contenting low co... 

文章以国内某公司硅钢厂连续退火机组1号辐射管加热段为研究对象,分析炉内传热机理,建立并开发了辐射管加热段的传热模型。采用生产实际数据对模型进行了验证,以总燃料消耗量最小为目标,得出该炉段长度方向上燃料的最佳分配机制。所得结论为该公司连续退火机组节能控制提供理论依据。 Taking the radiant tube heating section of No.1 continuous annealing unit in a silicon steel plant of a domestic company as the research object, the heat transfer mechanism in the furnace is analyzed, and the heat transfer model of the radiant tube heating section is established and developed. The model is verified by the actual production data. Aiming at the minimum total fuel consumption, the optimal fuel distribution mechanism in the length direction of the furnace section is obtained. The co...