硅钢资料

抑制回硅是低硅品种钢冶炼的重点和难点,南钢中厚板卷厂通过转炉出钢弱脱氧操作,精炼炉弱脱氧升温,脱氧、脱硫造渣,连铸严格的保护浇注及吹氩塞棒、吹氩浸入式上水口的应用等一系列工艺优化和操作的改进,使整个冶炼过程钢水回硅量稳定控制在200×10-6以内,钢水终点成分完全满足低硅钢要求。 Control of increasing silicon is the emphasis and difficulty in low silicon varieties steel smelting.The Nisco Wide Plate/Coil Plant can control the silicon content in molten steel keeping within 200×10-6 through whole steelmaking process by using oxygen residual operation in converter tapping,oxygen residual and increasing temperature,deoxidation,desulfurization,slag refining,protection cast,blowing argon by plugged nozzle,blowing argon by submerged entry nozzle in continuous casting,and other ... 

本发明涉及一种用于控制硅钢毛刺状厚度波动的工艺，包括如下步骤；将连铸坯送入加热炉中进行加热，连铸坯入炉温度为400‑680℃，连铸坯在炉时间为185‑220min；将加热后的连铸坯进行热轧，轧辊偏心量为0‑0.025mm，将热轧后的带钢进行卷取；将卷取后的带钢酸洗后进行冷轧，冷轧操作模式由多次阶段升降速模式调整为一次性升降速模式，且在一次性升降速阶段将MN‑AGC增益系数增大；将冷轧后的带钢进行卷取，退火后得到硅钢片成品。本发明所公开的用于控制硅钢毛刺状厚度波动的工艺，该工艺对加热、热轧、卷取及冷轧各工序进行优化协调，能够有效解决硅钢毛刺状厚度波动的问题，实现无取向硅钢全长厚度控制精度的提升，而且无需进行设备和系统改造，容易实现，易于推广。

以轻烧氧化镁粉为原料,经消化、碳化制得重镁水,在热解反应前采用络合剂对重镁水中的杂质钙、铁进行络合掩蔽,再经热解得到碱式碳酸镁,碱式碳酸镁经煅烧可制得钙、铁杂质含量较低的氧化镁。在重镁水络合除杂过程中,考察了络合剂三乙醇胺、柠檬酸、草酸单独和复合使用的除铁、除钙效果。以三乙醇胺为络合剂时,在200 mL重镁水中加10 mL三乙醇胺(1∶1),氧化镁产品中w(氧化镁)=99.3%、w(氧化钙)=0.31%、w(氧化铁)=0.042%;使用草酸和柠檬酸作为复合络合剂时,在200 mL重镁水中加入1.0 g柠檬酸和2.0 g草酸,氧化镁产品中w(氧化镁)=98.2%、w(氧化钙)=0.24%、w(氧化铁)=0.030%。 Light-burned magnesia as a raw material was hydrated and carbonated to obtain magnesium bicarbonate liquor.Before the pyrolyzing of magnesium bicarbonate liquor,complexants were used to cover Fe and Ca impurities.Then the treated liquid was pyrolyzed to obtain basic magnesium carbonate which was calcined to magnesium oxide with low calcium and iron content.During the complexing purification of magnesium bicarbonate liquor,the Fe and Ca removing effects of single or compound complexing agents,suc... 

本实用新型公开了一种变压器硅钢片整平工装，涉及变压器装配技术领域，包括底板，所述底板顶部一角处安装有第一气缸，所述第一气缸的输出端固定有支撑块，所述支撑块一端设置有第一L型垫块，所述第一L型垫块两端皆开设有配合槽。本实用新型通过设置有第一L型垫块、第二L型垫块、传动带、第一气缸和第二气缸之间的配合，通过第二L型垫块内侧对运动中的变压器硅钢片进行拦截，第一气缸的输出端伸出带动第一L型垫块进行移动，使第一L型垫块将变压器硅钢片推至第二L型垫块拐角处，工作人员通过控制第一气缸输出端来回伸缩对硅钢片进行反复挤压整平，有效提高了变压器硅钢片整平机的工作效率，节约成本。

1.本外观设计产品的名称：硬质合金刀（硅钢片刃切剪用）。;2.本外观设计产品的用途：用于硅钢片刃的剪切。;3.本外观设计产品的设计要点：在于其整体形状。;4.最能表明设计要点的图片或照片：立体图。;5.使用时为安装面，故不常见，省略后视图。;

以青海盐湖氯化镁为初级原料,采用喷雾热解法制备原料氧化镁。原料氧化镁通过水化制备氢氧化镁。将氢氧化镁过滤、洗涤、烘干、粉碎、煅烧,制备硅钢级氧化镁。本文重点考察煅烧温度、煅烧时间、料层厚度等因素对氧化镁水化率的影响,采用均匀实验设计和DPS数据处理,确定最优煅烧实验条件为:煅烧温度1250℃,煅烧保温时间4小时,料层厚度0.5cm。在此条件下得到的硅钢级氧化镁完全满足硅钢及氧化镁的行业标准。 The magnesium oxide is prepared by Spray pyrolysis process,which magnesium chloride from Qinghai Salt Lake is used as primary raw material,and hydrated to magnesium hydroxide,then obtained silicon steel magnesia through filtering,washing,drying,crushing and calcinations.In this paper,influences of some factors on magnesia hydration rate are studied,such as calcination temperature,calcination time and material thickness.After average experimental design and DPS data processing,optimal calcination... 

采用固溶强化、细晶强化和位错强化方法,模拟TSCR流程试开发高强度无取向电工钢,试开发钢的主要合金成分为3%Si、0.83%Al和2.99%Mn。分析热轧、常化、退火后的钢板组织,并针对不同的成品板组织,详尽地分析了相应的力学性能和磁性能。试验电工钢平均晶粒直径为12.37μm时,R p0.2为530 MPa,R m为618 MPa;当退火制度为700℃×4 min,成品组织完全为未再结晶的回复组织时,R p0.2为853.5 MPa,R m为895.5 MPa。该成分的电工钢P15/50或P10/400最小时,对应的平均晶粒直径都大于59.67μm;P10/800或P10/1000最小时,对应的平均晶粒直径都处于12.37~59.67μm尺寸区间。 TSCR was simulated to develop high-strength non-oriented electrical steel with 3% of Si,0.83% of Al and 2.99% of Mn by solution strengthening,grain refinement strengthening and dislocation strengthening.The microstructures of hot rolled plates,normalized plates and annealed plates were analyzed.Furthermore,the mechanical properties and magnetic properties of products with different microstructures were detailedly studied.As the average grain diameter of the steel was 12.37 μm,the yield strength ... 

本发明提供一种高磁感低铁损硅钢极薄带的生产方法，包括：对硅钢极薄带进行清洗，并对清洗后的所述硅钢极薄带进行烘干；对烘干后的硅钢极薄带进行涂覆隔离层；将涂覆有所述隔离层的硅钢极薄带进行高温退火处理，其中，高温退火过程包括：快速升温至300～600℃，慢速升温至800～1300℃，并在预设温度时进行保温，保温至预设时间后进行冷却，冷却至50～300℃；对退火处理后的硅钢极薄带进行表面清洗、干燥以及涂覆绝缘层；将涂敷绝缘涂层的硅钢极薄带进行烘干烧结处理，并卷取成品。利用本发明，解决目前硅钢极薄带在连续退火涂层工艺存中存在张力不易控制，而导致硅钢带材的板形变差且极易发生断带等问题。

本实用新型公开了一种便于操作的硅钢板带加工用打标装置，包括工作台，所述工作台的下端固定连接有多个支撑地脚，所述工作台的两端上下侧均转动连接有限位辊筒。本实用新型在进行打标时，速度监测仪会对不锈钢带的移动速度进行监测，位移机构会带动打标机构以与不锈钢带位移方向相同、与不锈钢带移动速度相等的状态进行移动，在打标机构移动的过程中，激光打标头对不锈钢带进行打标，打标结束后，位移机构带动打标机构反向位移，回到起始点，再进行下一次打标，从而可以使得不锈钢带在保持移动的状态下，使用打标机构对不锈钢带进行打标，提高打标效率，且打标机构可以对激光打标头的位置和高度进行调节，可以对不同尺寸的不锈钢带进行打标。

本发明属于退火工艺技术领域，公开了一种高牌号无取向硅钢剪切方法，包括：待剪切带钢由夹送辊输送到达剪切位后，夹送辊释放对所述待剪切带钢的夹持；位于所述待剪切带钢下方的下剪刃上移，推顶所述待剪切带钢在低张力状态下持续向上运动；在所述待剪切带钢与上剪刃接触后，将所述待剪切带钢剪断。本发明提供的高牌号无取向硅钢剪切方法能够极大的减少高牌号无取向硅钢的剪切缺陷，降低废品量，提升剪切效率。

从影响高牌号无取向硅钢退火工艺的主要参数入手,介绍高牌号无取向硅钢退火炉在加热、气氛控制、冷却、涂层烘烤方面的新技术,并展望无取向硅钢退火炉的发展方向。 Based on the technology parameters of high-grade non-oriented silicon steel annealing,the new technology of the annealing line,which includes heating,atmosphere control,cooling,coating baking,is introduced,and the development direction of non-oriented silicon steel annealing furnace is pointed out. 

本发明提供一种含铜一般取向硅钢及其制备方法，制备方法包括：对钢板进行脱碳退火，得到脱碳钢，其中，将所述脱碳钢的氧含量控制在如下公式计算的范围内：ψO＝(0.0504×ωSi×H2±0.00005)×106，其中，ψO为脱碳钢的氧含量，单位为ppm；ωSi为钢板中Si的重量百分含量；H为钢板的厚度，单位为mm；将所述脱碳钢进行冷轧、涂布氧化镁涂层、卷曲和成卷退火，得到退火钢卷；对所述退火钢卷进行开卷，再涂敷张应力涂层和拉伸平整退火，制得含铜一般取向硅钢。本发明根据钢板中Si的实际含量及钢板厚度，调整脱碳钢的氧含量，以获得表面质量良好、磁性水平稳定的含铜一般取向硅钢产品。