采用双辊薄带连铸工艺制备了厚度为2.4mm的3.98%Si-0.71%Al无取向硅钢带,经常化、冷轧、不同温度退火后,对其显微组织、析出物、织构和磁性能进行了检测分析。结果表明:随着退火温度的提高,退火板晶粒尺寸增大,组织均匀性提高;退火板析出物主要是AlN和MnS与AlN复合析出物,尺寸较粗大,达0.5~2.5μm;退火板织构沿厚度方向变化明显,表层和1/2层存在较强的{100}织构,1/2层还存在较强的{111}织构,1/4层主要是{112}织构;随退火温度的升高相应的铁损和磁感应强度均降低。 Using twin roll thin strip continuous casting technique,the 3.98%Si-0.71%Al no-oriented silicon steel strip in thickness of 2.4mm was produced.The microstructure,precipitates,texture,and magnetic properties of the sheet after normalizing,cold rolling and annealing at different temperatures were studied.The results show that with annealing temperature increase,the grain size and uniformity of annealed sheet increased.The main precipitates in coarse size of 0.5-2.5μm in annealed sheet were AlN and... 

一种无取向硅钢用轧制工作辊，属于轧机工作辊技术领域，该轧制工作辊，包括锥形曲面段和平直段，锥形曲面段包括弧形段Ⅰ和弧形段Ⅱ，弧形段Ⅰ的弧面内凹，弧形段Ⅱ的弧面外凸，弧形段Ⅱ和平直段与带钢接触，弧形段Ⅰ的一端水平向外延伸，弧形段Ⅰ的另一端与弧形段Ⅱ的一端相切，弧形段Ⅱ的另一端与平直段相切，本实用新型的有益效果是，该工作辊整体结构简单，轧制效率高，降低了辊耗，消除了工作辊边部的急剧弹性压扁、弹性变形，降低了轧制断带的风险，可有效控制钢带边部的边降和形状。

适用范围 本标准规定了700 MW及以上级大电机用冷轧无取向电工钢带的术语和...

提供一种可以制造具有优异特性的变压器的、兼顾低铁损和良好的磁致伸缩特性的方向性电磁钢板。本发明的方向性电磁钢板具有在与轧制方向交叉的方向上线状延伸的线状应变区域，线状应变区域具有在轧制方向上具有压缩应力的区域，在与该具有压缩应力的区域的轧制方向邻接的区域具有在轧制方向上具有拉伸应力的区域。

【作者】 常波； ...

【作者】 汤婧； ...

针对新能源汽车的发展，制备了含Ni固溶强化、含Cu析出强化以及含Ni+Cu复合强化3%Si无取向硅钢，研究了强化方式对无取向硅钢组织、织构和性能的影响。结果表明：固溶强化型无取向硅钢热轧板中形成了粗大{221}<221>晶粒，冷轧过程中剪切变形明显并在退火后形成良好再结晶织构。析出强化型无取向硅钢热轧板中心层形成γ取向粗大晶粒，在后续的加工中γ织构逐渐增强并最终得到相对细小的再结晶晶粒。复合强化型无取向硅钢热轧板中保留了强λ取向带状组织，退火后形成了有益的Goss织构和λ织构。固溶强化型与复合强化型无取向硅钢磁感应强度B₅₀分别达到1.742、1.688 T,高于析出强化型无取向硅钢的1.645 T。同时，复合强化型无取向硅钢高频铁损最低，其P_1.0/400和P_{1.0/1 000}分别低至20.97、82.69 W/kg,这与其较小的晶粒尺寸和织构改善有关。强度计算结果表明：Ni元素固溶强化对强度的提高有限，屈服强度为468 MPa,纳米Cu析出可显著提高屈服强度（强度增量约200 MPa）,且主要来自于模量强... For the development of new energy vehicles, 3%Si non-oriented silicon steel were processed by solid solution strengthening with Ni, precipitation strengthening with Cu, and composite strengthening with Ni and Cu. The effects of different strengthening methods on the microstructure, texture and properties of high-strength non oriented silicon steel were studied.The results show that coarse {221}<221> grains are formed in the hot rolled sheet of solution strengthened non-oriented silicon ste... 

【作者】 王桦； 舒子龙； ...

【摘要】 <正>据武钢股份公司提供的消息,武钢将与...

本发明一种基于冷轧全流程数据的硅钢铁损预测方法，其对冷轧硅钢进行全流程物料跟踪，以基于聚类算法分类，并选取代表性工艺作为神经网络的训练集来对冷轧硅钢铁损进行预测，以探明冷轧各机组工艺对冷轧硅钢铁损的影响。

介绍了EB5325涂层液的主要性能和中冶新材生产冷轧无取向电工钢所用的涂层设备,通过多次试验摸索出使用EB5325涂层液的工艺,对涂层出现的缺陷进行分析研究,并提出解决方法,使中冶新材生产的冷轧无取向电工钢的涂层质量满足了用户的要求。 This article introduces the main properties of EB5325 and the coating equipments for cold-rolled non-oriented electrical steel. A process using EB5325 coating liquid is made through many time experiments and exploration. The appeared defects in the coating are studied and analyzed,and the solutions are proposed. The coating quality meets clients’ requirements of cold rolled non-oriented electrical steel. 

本发明涉及硅钢片叠片领域，具体涉及一种硅钢片自动叠片设备，包括滑移架、安装座和若干个单层碟片机，每个单层碟片机均包括码放架、横向拉移机构、下压机构、两个同步拉进机构、双层同步下压机构、传动连接器、第二弹性安装座、三个第一弹性安装座和五个电磁铁，通过双层同步下压机构，通过传动板能够与传动连接器之间自动分离，避免使用驱动源进行分离，降低了设备成本，通过传动连接器带动传动管进行移动，减少使用驱动源，降低设备的成本，传动连接器进行下降时也将带动传动管进行下降，使得中部硅钢片、两个纵向硅钢片和横向硅钢片之间进行同时下降，增加了工人的观察时间，减少出现硅钢片偏移的风险。