研究了常化对CSP流程生产的wSi=1.6%的无取向电工钢组织、织构和成品磁性能的影响。结果表明,经CSP流程生产,且在相同的冷轧及退火制度下,经1 000℃×2min常化处理的wSi=1.6%的无取向电工钢热轧板,其最终退火成品的铁损P15/50比不常化试样下降了10.5%,磁感B50比不常化试样提高了2.5%;常化使wSi=1.6%的无取向电工钢成品的平均晶粒尺寸增大,成品铁损P15/50相应减小;同时,常化使wSi=1.6%的无取向电工钢成品中高斯织构的强度增加,γ纤维织构的强度减弱,这有利于成品磁感B50的提高。 The effect of normalizing on microstructure,texture and magnetic properties of non-oriented electrical steel with wSi=1.6% produced by CSP process was investigated.The results show that,under the same cold rolling and annealing system,the iron loss(P15/50) of annealed samples whose hot bands has been normalized by 1 000 ℃×2 min process decreases by 10.5% and magnetic induction(B50) increases by 2.5% compared with the samples whose hot bands was not normalized.The average grain size of non-orient... 

分析总结退火工艺各参数对冷轧无取向硅钢磁性能的影响,结合设计和生产实践经验介绍退火工艺中各参数的实际生产取值,并针对现生产工艺过程中出现的典型问题提出解决办法。 It is analyzed and summarized the great influences on magnetism of cold rolled non-oriented silicon steel affected by various annealing process data in this article.The relevant settled ways is raised.According to the actual value presetting ways for various annealing process data based on design and production,as well as typical problems occurred during production. 

本发明涉及硅钢片铁芯性能测试技术领域，公开了CD型硅钢片铁芯性能测试工装，包括：机台，上部后侧固定有竖直向上的后侧板；托板，水平设置在所述机台上方；夹持机构，设置在所述机台上，所述夹持机构包括：第二气缸，其驱动杆端部固定套接有夹持块，夹持块外端部固定有橡胶缓冲块；橡胶垫，固定在所述托板右侧上部。本发明通过设置第一气缸驱动连接于托板，可以先根据硅钢片的厚度，通过操作气缸控制器控制第一气缸工作带动托板在机台上进行升降高度，从而调整托板与夹持块的高度差，提高装置的实用性和广泛性，较为实用，适合广泛推广和使用。

本发明提出了一种可修饰取向硅钢表面的无铬无机绝缘涂料及其制备方法，该涂料按照重量份计包括以下组份：磷‑硅溶胶40‑70份、钛改性增稠剂预溶胶25份、抑泡剂0.2‑1份、流平剂0.05‑0.2份和去离子水3.8‑34.75份。该涂料的制备方法为：先制备磷‑硅溶胶和钛改性增稠剂预溶胶；然后向磷‑硅溶胶中加入抑泡剂并搅拌均匀；再加入去离子水并搅拌均匀；再分次缓慢加入钛改性增稠剂预溶胶并搅拌均匀；最后加入流平剂并搅拌均匀。本发明所制备的无铬无机绝缘涂料可修饰取向硅钢表面瑕疵露晶等形貌缺陷；在取向硅钢表面形成的绝缘涂层具有良好的附着力和耐热性；涂料采用的原料均为无污染的环保材料，解决了含铬绝缘涂料带来的环境危害。

本发明涉及电力、冶金领域，尤其涉及一种轧制高牌号硅钢焊缝免冲孔的方法。一种轧制高牌号硅钢焊缝免冲孔的方法，包括如下步骤：步骤一：“一选”，步骤二：“二看”，步骤三：“三按”，步骤四：“四调整”。本发明的有益效果是：1、满足测量精度要求，符合工艺要求，为连轧机硅钢的生产提供了强大的技术保障。2、该方案采用低成本设计，运行稳定性较高，测量精度达标，如推广使用，将为使用单位节省大量设备费用，符合降本增效的原则，具有较大推广价值。

近年来，在节能减排背景之下，国内外众多研究者对无取向电工钢磁性能的提升做了大量研究。为了探索无取向电工钢磁性能提升的方法，对锡或锑对无取向电工钢磁性能的作用机制(晶粒尺寸和晶体织构的控制)进行分析。基于该作用机制，介绍锡或锑的添加对无取向电工钢磁性能的影响。经研究发现，适量的锡或锑在晶界偏聚，不会阻碍晶界的移动并且致使晶粒尺寸降低；与此同时，锡或锑在晶界偏聚不仅抑制{111}织构在原始晶界处形核及生长，还降低(100)晶粒表面能，促进(100)晶粒生长。因此，适量添加锡或锑，可使无取向电工钢铁损下降、磁感提升。最后结合生产工艺，建议无取向电工钢的研究方向应为稀土含量对高牌号无取向硅钢夹杂物尺寸和数量分布的影响，锡或锑的添加量和常化工艺参数(常化时间、常化温度)对常化晶粒尺寸的影响。 In recent years, due to the background of energy saving and emission reduction, numerous researchers all around the world have done a lot of investigations on the improvement of magnetic properties for non-oriented electrical steel. In order to explore the method of improving the magnetic properties of non-oriented electrical steel, the mechanism of tin or antimony on the magnetic properties(the control of grain size and crystallographic texture) of non-oriented electrical steel is illuminated. ... 

本实用新型公开了硅钢专用消泡剂生产温度控制装置，包括底板及设置在底板上端的温控桶，所述温控桶的内部设置有温控腔，所述温控桶的上下两端分别安装有进料口及出料口，所述温控桶的内部设置有便于温度控制的温度控制机构，所述底板上设置有用于搅拌的搅拌机构；所述温度控制机构包括安装在温控桶上的进气管及出气管，所述进气管及出气管与温控腔的内部相通设置。本实用新型的硅钢专用消泡剂生产温度控制装置，整个温控处理操作简单、实施便捷，便于对消泡剂进行温度控制，且冷却介质或者加热介质可以直接对消泡剂进行加热或是降温，降低了输送过程中的能量消耗，提高了消泡剂温度控制的效率。

介绍了普通取向硅钢(CGO)和高磁感取向硅钢(Hi-B)铸坯高温加热两次冷轧、一次冷轧和铸坯低温加热两次冷轧、一次冷轧法4种成熟生产工艺的主要技术参数,取向硅钢理论研究(Goss晶核和抑制剂)和生产技术现状。取向钢的发展趋势为:提高(110)[001]晶粒取向度,降低取向硅钢铁损,发展铸坯低温加热(≤1 300℃)和薄板坯连铸连轧流程生产取向硅钢工艺。 Main technology parameters of four developed process:cast bloom higher temperature heating-double cold rolling or single cold rolling,lower temperature heating-double cold rolling or single rolling process for production of common grain oriented silicon steel(CGO) and high magnetic induction grain oriented silicon steel(Hi-B),theory research on grain oriented steel(Goss nucleus and inhibitor) and present situation of process are summarized in this paper.The development trend of grain oriented si... 

针对采用含钒铁水生产无取向电工钢存在的铁水脱硫率低、转炉冶炼过程回硫量大、成品硫含量偏高的问题,通过对含钒钛铁水脱硫,减少转炉冶炼过程回硫以及RH脱硫技术等方面的研究,大幅度降低了电工钢成品硫含量。生产表明钢中w(S)=0.001 9%～0.006 9%,平均为0.004 2%;w(S)≤0.008%的比例达到了100%,且w(S)≤0.005%的比例也达到了91.43%。 In cognizance of the problems of low desulphurization rate for hot metal,large sulfur-recovery in converter as well as high sulfur content in products in producing non-orientation electrical steel with vanadium-content hot metal countermeasures have been carried out.Sulfur content in non-orientation electrical steel is decreased obviously by way of study on technologies of desulphurization for hot metal with vanadium & titanium,sulfur-recovery control in converter and desulphurization in RH ... 

一种硅钢片测量装置，属变压器绝缘件生产技术领域，包括工作台、止动滑块、纵梁和测量部，止动滑块安装在工作台上，纵梁架设在止动滑块和工作台上，测量部安装在纵梁上。工作台包括台面、立柱和横向燕尾槽，四个立柱将台面支撑于地面，台面的下侧安装一个横向燕尾槽。止动滑块安装在横向燕尾槽内，止动滑块包括块体、推杆、楔块、挡片、弹簧和蘑菇头，块体横向具有通孔，通孔内安装推杆和弹簧，块体纵向具有一对侧槽，侧槽内安装楔块，通孔内具有一个凸台，凸台位于靠近蘑菇头的一侧，蘑菇头用于弹簧的限位。止动滑块上安装纵梁，纵梁包括滑板、纵向燕尾槽，滑板的一端安装在止动滑块上，滑板上具有纵向燕尾槽，纵向燕尾槽上安装测量部。

本发明公开一种硅钢级氧化镁制备方法、硅钢级氧化镁保护膜，涉及氧化镁制备技术领域。将得到的粗氧化镁产品进行净化处理；将净化处理后的粗氧化镁产品与金属镁碳还原剂，在真空状态下，利用真空碳热还原技术进行金属镁的置换，制得金属镁；金属镁碳还原剂与粗氧化镁产品的质量比为（1~1.5）：1；制得的金属镁在纯氧下制得氧化镁；将制得氧化镁根据实际需求获得不同粒径硅钢级氧化镁颗粒。本发明产品各项指标优于企业标准的硅钢级氧化镁。而且不会受原料中含有的钙等杂质的影响，产品纯度很容易达标，同时，还存在能耗较低、生产成本低等优点，解决了业在降低能耗方面的突破可应用于工业化生产。

从影响高牌号无取向硅钢退火工艺的主要参数入手,介绍高牌号无取向硅钢退火炉在加热、气氛控制、冷却、涂层烘烤方面的新技术,并展望无取向硅钢退火炉的发展方向。 Based on the technology parameters of high-grade non-oriented silicon steel annealing,the new technology of the annealing line,which includes heating,atmosphere control,cooling,coating baking,is introduced,and the development direction of non-oriented silicon steel annealing furnace is pointed out.