以青海盐湖氯化镁为初级原料,采用喷雾热解法制备原料氧化镁。原料氧化镁通过水化制备氢氧化镁。将氢氧化镁过滤、洗涤、烘干、粉碎、煅烧,制备硅钢级氧化镁。本文重点考察煅烧温度、煅烧时间、料层厚度等因素对氧化镁水化率的影响,采用均匀实验设计和DPS数据处理,确定最优煅烧实验条件为:煅烧温度1250℃,煅烧保温时间4小时,料层厚度0.5cm。在此条件下得到的硅钢级氧化镁完全满足硅钢及氧化镁的行业标准。 The magnesium oxide is prepared by Spray pyrolysis process,which magnesium chloride from Qinghai Salt Lake is used as primary raw material,and hydrated to magnesium hydroxide,then obtained silicon steel magnesia through filtering,washing,drying,crushing and calcinations.In this paper,influences of some factors on magnesia hydration rate are studied,such as calcination temperature,calcination time and material thickness.After average experimental design and DPS data processing,optimal calcination... 

对取向硅钢在不同气氛下的高温退火工艺进行实验室模拟，利用X射线衍射仪（XRD）分析了硅钢退火至900℃和1170℃时的样品表面氧化层和底层的物相组成，采用场发射扫描电镜（SEM）观察了样品表面氧化层和底层在截面方向上的微观形貌特征，并计算了高温退火一次升温阶段氧化反应的吉布斯自由能以及900℃时退火气氛的氧分压。结果表明：当退火气氛的露点温度保持一定时，较高的氢气含量有利于生成完整连续的底层；当退火气氛的水氢分压比保持一定时，在露点温度与氢气含量两者较低的条件下，底层附着性不佳易脱落，较高条件下，底层中夹杂着较多的铁单质；当氧化层中无FeO时，底层完整连续但易脱落，当FeO层较薄时，底层下方存在部分未反应的SiO₂,当FeO层较厚时，底层不完整连续且有分层。 The high temperature annealing process of grain-oriented silicon steel in different atmospheres was simulated in the laboratory. X-ray diffractometer（XRD） was used to analyze the phase compositions of the surface oxide layer and forsterite film of the silicon steel annealed to 900 ℃ and 1170 ℃. Field-emission scanning electron microscopy（SEM） was used to observe the micro morphology characteristics of the surface oxide layer and forsterite film of the samples in the cross section direction. The ... 

本实用新型涉及硅钢片生产技术领域，特别涉及一种电机硅钢片冲槽生产线，包括支架，支架下方依次设有:毛坯料垛，毛坯料垛由待冲毛坯片堆成，待冲毛坯片中心具有通孔；理片机；定子冲槽机，定子冲槽机用于在毛坯片上冲裁形成已冲毛坯片，已冲毛坯片包括定子片和转子坯片；第一液压升降机，第一液压升降机用于承载定子片；转子冲槽机，转子冲槽机用于冲裁转子坯片从而形成转子片；第二液压升降机，第二液压升降机用于承载冲裁得到的转子片；输送装置，输送装置用于输送待冲毛坯片、已冲毛坯片、转子坯片或转子片，本实用新型提出一种适用范围广、运行效率高、结构简单、价格适宜的电机硅钢片冲槽自动线。

根据本发明的一个实施例的无取向电工钢板，以重量％计，所述钢板包含Si：2.2至4.5％、Mn：0.5％以下且0％除外、Al：0.001至0.5％、Sn：0.07至0.25％和N：0.0010至0.0090％，余量包含Fe和不可避免的杂质。所述钢板包含从钢板表面向内存在的表层部和存在于表层部里面的中心部，中心部包含0.005重量％以下的N，所述表层部比中心部更包含0.001重量％以上的N，表层部的平均晶粒粒径为60μm以下，中心部的平均晶粒为70至300μm。

一种在取向硅钢中获得沿晶断口的方法：将取向硅钢样品加工成俄歇电子能谱仪标准试样；对标准试样进行表面清理；充氢：将标准试样所设定的预设断口处放入充氢装置的含硫脲溶液中，并使取向硅钢样品为阴极；将铂片置入并作为阳极；阴极充氢电流为1.25～1.35A，充氢电流密度在0.1～0.8A/m2，充氢时间在12～50h，充氢电压为36～39V；进行表面分析。本发明不仅工艺简单，便于操作，用时短，所用毒化剂是硫脲，从而避免了采用剧毒的三氧化二砷作为毒化剂，对人体健康有极大威胁的问题，且所获得的取向硅钢断口均为典型沿晶断口，适用于取向硅钢晶界偏聚行为以及晶界微区成分分析。

研究了退火温度对3.1%Si无取向硅钢组织和磁性能的影响规律。结果表明:退火温度从940℃提高至1 000℃,平均晶粒尺寸由98μm增加到145μm,铁损P_1.5/50从2.576 W/kg降低至2.408W/kg。随着退火温度的升高,γ不利织构组分强度逐渐降低,{111}〈112〉织构组分强度降低约16%,磁感B₅₀逐渐升高,磁性能水平提高。 The effects of annealing temperature on microstructure and texture and magnetic properties of 3.1%Si non-oriented silicon steel were investigated in this paper.The results showed that,when the annealing temperature increased from 940℃ to 1 000℃,the average grain size of metallographic structure increased from 98μm to 145μm,the iron loss value P_1.5/50 decreased from2.576 W/kg to 2.408 W/kg.And as the annealing temperature increased,the strength of the unfavorable texture componentγgrad... 

从取向硅钢生产路线的选择、工艺技术的改进和生产设备的改造三方面进行了生产取向硅钢的节能降耗技术改造.通过完善多元抑制剂配方生产低温取向硅钢,通过加抛丸的酸洗、带面超声波清洗、改进连续退火炉以及余热循环利用等技术改造,使2012年取向硅钢的产量与未进行技术改造前的2009年相比提高了2.5倍,产品磁性上升了一个半牌号,能耗下降了8.9%,成材率提高了6.4%,生产成本下降了22%,综合效益显著. Energy saving technological transformation was carried out in the production of grain oriented silicon steel from three aspects of the oriented silicon steel production process route selection,technology improvement and equipment renovation.Through the improvement of multiple inhibitor formulations for producing low-temperature grain-oriented silicon steel,and by adding the blasting pickling,the belt surface ultrasonic cleaning,improvement of continuous annealing furnace,waste heat recycling tec... 

本发明涉及一种常化后免酸洗生产取向硅钢的方法，取向硅钢的生产工艺路线为：冶炼→连铸→热轧→常化退火→拉伸矫直→抛丸→冷轧→脱碳退火→渗氮→涂MgO→高温退火→热拉伸平整及涂绝缘膜；本发明在常化退火后通过物理方法去除带钢表面的氧化铁皮，且效率高、效果好、操作简单、易于控制；与常规工艺相比，省去了酸洗及后续废酸处理工作，排除了酸雾对环境的污染，消除了取向硅钢带因酸洗而产生的潜在缺陷，产品质量更加稳定可靠。

本实用新型公开了一种硅钢碎断刀具曲面车削加工装置，属刀具曲面车削加工定位工装领域。包括主体，周向设置在主体上的多个限位槽，以及对刀具横向施压并安装在对应限位槽处的施压机构，施压机构包括沿限位槽宽度方向运动并对刀具作用的施压块，以及将施压块与主体可调节安装的调节件，施压块相对刀具的一侧设置有滚动体三。通过调节调节件将施压块沿限位槽宽度方向移动，进而将刀具夹紧在限位槽内部，通过滚动体三的设置利于在加工完成后刀具和施压块分离，防止出现卡滞的现象发生，利于刀具的高效生产制作。

本实用新型属于硅钢技术领域，具体的说是一种硅钢前处理高液回流装置，包括机体；所述机体的侧端固接有一号导管；所述一号导管上安装有二号导管；所述机体的顶端固接有连接管；所述连接管上安装有入泡管；所述二号导管的内侧壁固接有电机；所述电机的输出端固接有扇叶；所述二号导管的顶端内侧壁固接有定位板；所述定位板的侧端转动连接有旋转叶轮；所述二号导管的底端固接有排泡管；通过一号导管和二号导管的配合可以把溢出的泡沫进行导向，通过扇叶和旋转叶轮的配合可以使泡沫快速流动，再通过排泡管排出进入机体的内部，可以使泡沫循环使用，避免泡沫的溢流造成环境的污染及碱液的浪费。

本发明涉及一种硅钢热处理方法，尤其涉及一种取向硅钢极薄带绝缘层涂覆方法，包括以下步骤：(1)接入普碳钢引带的准备工作；(2)各炉段张力的设定工作；(3)炉内气氛及温度的调节工作；(4)绝缘层厚度及厚度的检测工作；(5)极薄带涂层涂覆及烘干工作；(6)极薄带表面绝缘涂层及磁性能检测工作。本发明采用与极薄带厚度相当的普碳钢作为引带，通过引带测试产线张力和绝缘层涂覆的厚度，一方面可通过普碳钢薄带的运行加速炉内温度和气氛的稳定性，节约炉内稳定时间；另一方面可通过成本较低的普碳钢检测炉内张力和温度的设定，及绝缘涂层的涂覆效果，避免开始采用硅钢带出现断带，及涂覆不合格后造成产品报废带来的成本升高。

本实用新型公开了一种变压器铁芯硅钢片的横剪打磨装置，包括出料平台、传送机构和打磨机构，所述出料平台的出料端设置有打磨机构，且两组所述打磨机构对称设置在硅钢片的上下两侧，两组所述打磨机构之间构成打磨通道，所述传送机构靠近于出料平台的出料端设置在出料平台上，且所述出料平台上的硅钢片通过传送机构依次朝向打磨通道内位移，通过两组对称设置的打磨机构对硅钢片的两侧面进行同时打磨，具有较高的打磨效率。