硅钢资料

本发明一种基于冷轧全流程数据的硅钢铁损预测方法，其对冷轧硅钢进行全流程物料跟踪，以基于聚类算法分类，并选取代表性工艺作为神经网络的训练集来对冷轧硅钢铁损进行预测，以探明冷轧各机组工艺对冷轧硅钢铁损的影响。

为满足用户对无取向电工钢中硫含量的要求,采用CaO-CaF2复合渣系为脱硫剂,利用RH投入法对无取向电工钢进行深脱硫试验。试验结果表明,RH精炼渣成分控制在w CaO43%~51%、w Al2O325%~31%、w MgO4%~6%、w SiO29%~12%、w(FeO+MnO)3%~6%,在脱硫剂加入量为6~8 kg/t时,钢中平均硫含量从32×10-6降低到18×10-6,RH平均脱硫率为43.3%,最高达47.1%。利用KTH模型计算精炼终渣平均硫容量为0.003 1,RH精炼结束时渣-钢间实际平均硫分配比从14增加到52。 In order to satisfy the requirements of consumers on sulfur content in non-oriented electrical steel,taking( CaO-CaF 2) based flux as desulfurizer,industrial experiments on deep desulphurization of non-oriented electrical steel were carried out during RH process. The results show that as the compositions of refining slag are appropriately controlled with w CaO of 43% ~ 51%,w Al2O3 of 25% ~ 31%,w MgO of 4% ~ 6%,w SiO2 of 9% ~ 12%,and w( FeO + MnO) of 3% ~ 6%,and the desulfurizer added are at 6 ~ ... 

本发明的一个实施方案提供一种取向电工钢板及其制造方法，以重量％计，所述取向电工钢板包含：Si：3.0‑4.5％、Mn：0.05‑0.2％、Al：0.015‑0.035％、C：0.0015％以下(0％除外)、N：0.0015％以下(0％除外)、S：0.0015％以下(0％除外)、余量的Fe及其它不可避免的杂质，并且满足以下关系式1和关系式2。[关系式1](W13/50/W17/50)≤0.57[关系式2](W15/50/W17/50)≤0.76(其中，所述关系式1中，Wx/y表示施加磁场的大小为x/10T且频率为yHz的条件下的铁损值)。

研究了常化对CSP流程生产的wSi=1.6%的无取向电工钢组织、织构和成品磁性能的影响。结果表明,经CSP流程生产,且在相同的冷轧及退火制度下,经1 000℃×2min常化处理的wSi=1.6%的无取向电工钢热轧板,其最终退火成品的铁损P15/50比不常化试样下降了10.5%,磁感B50比不常化试样提高了2.5%;常化使wSi=1.6%的无取向电工钢成品的平均晶粒尺寸增大,成品铁损P15/50相应减小;同时,常化使wSi=1.6%的无取向电工钢成品中高斯织构的强度增加,γ纤维织构的强度减弱,这有利于成品磁感B50的提高。 The effect of normalizing on microstructure,texture and magnetic properties of non-oriented electrical steel with wSi=1.6% produced by CSP process was investigated.The results show that,under the same cold rolling and annealing system,the iron loss(P15/50) of annealed samples whose hot bands has been normalized by 1 000 ℃×2 min process decreases by 10.5% and magnetic induction(B50) increases by 2.5% compared with the samples whose hot bands was not normalized.The average grain size of non-orient... 

本实用新型公开了一种便于操作的硅钢板带加工用打标装置，包括工作台，所述工作台的下端固定连接有多个支撑地脚，所述工作台的两端上下侧均转动连接有限位辊筒。本实用新型在进行打标时，速度监测仪会对不锈钢带的移动速度进行监测，位移机构会带动打标机构以与不锈钢带位移方向相同、与不锈钢带移动速度相等的状态进行移动，在打标机构移动的过程中，激光打标头对不锈钢带进行打标，打标结束后，位移机构带动打标机构反向位移，回到起始点，再进行下一次打标，从而可以使得不锈钢带在保持移动的状态下，使用打标机构对不锈钢带进行打标，提高打标效率，且打标机构可以对激光打标头的位置和高度进行调节，可以对不同尺寸的不锈钢带进行打标。

目前高磁感冷轧硅钢生产过程中，采用经验方法确定的乳化液流量设定值往往会造成硅钢产品的磁感性能达不到预期目标，针对此情况，基于轧机轧制机理研究了的乳化液流量数学模型，确定了乳化液流量设定值。实践表明，使用该数学模型输出的乳化液流量设定值，可提高轧制过程中乳化液流量控制精度，从而提高高磁感冷轧硅钢的轧制性能。 In view of the current production process of high magnetically inductive cold-rolled silicon steel, the mathematical model of emulsified fluid flow based on mill rolling mechanism is studied in view of the situation in which the magnetic sensing performance of silicon steel products is often not up to the expected target by using empirical method to determine the emulsified liquid flow setting. Practice shows that the emulsified fluid flow setting value output from this mathematical model improv... 

利用FE-SEM、EDS分析了含不同抑制剂成分的成品取向硅钢中夹杂物的组成和形貌,统计其尺寸及数量分布;结合对磁性能测试的结果,分析了Sn、Cu、Nb和Cr对取向硅钢磁性能影响的机理。结果表明:含Sn的取向硅钢试样中夹杂物主要为块状的微米级Al-Ti-C-N-O复合物,还有少量的球形Al-N-O颗粒和块状Ti-C-N-O颗粒,棒状夹杂物较少;含Cr的取向硅钢试样中夹杂物主要为球形的微米级Al2O3,还有少量Cu-Al-N-O-S复合物,棒状夹杂物和不规则夹杂物均较少;含Cr试样中1~3μm夹杂物的平均尺寸较含Sn试样小,但数量多,而大于3μm夹杂物的平均尺寸较含Sn试样大,但数量很少。磁性能测试结果表明,外场为800A/m和2500A/m时,含Cr试样磁感应强度偏低,铁损值P1.7/50较含Sn试样高,为1.171W/kg。 The composition and morphology of inclusions in the finished grain-oriented silicon steels are analyzed by using FE-SEM and EDS, and the number density and size distribution of the inclusions are counted. The influence mechanism of Sn, Cu, Nb, and Cr on the magnetic properties of the steel is also discussed. Results show that the inclusions composition in the grain-oriented silicon steel samples containing Sn is mainly block Al-Ti-C-N-O, compounding with a few spherical Al-N-O and block Ti-C-N-O... 

本发明公开一种表面状态良好的无取向电工钢板，其含有Fe和不可避免的杂质，其还含有质量百分含量如下的下述各化学元素：0＜C≤0.005％，Si：1.0～2.0％，Mn：0.2～1.0％，Al：0.2～1.0％，Ca：0.0003～0.010％，Sb：0.005～0.2％，其中Si+Al：1.4～2.6％。此外，本发明还公开了一种上述的无取向电工钢板的制造方法，其包括步骤：(1)冶炼；(2)铸造：控制连铸坯在连铸机出口位置处的表面温度≥780℃，以使得连铸坯在其厚度方向上与宽度方向上的晶粒尺寸之比为2.5～6.0；(3)热轧：在热轧粗轧结束之后，控制中间坯头尾温度之差≤25℃；(4)冷轧；(5)连续退火。该表面状态良好的无取向电工钢板无瓦楞缺陷，其具有较低的铁损以及优良的磁感，其具有十分良好的推广前景和应用价值。

本发明提出了一种无机绝缘漆，由下列物质组成，其重量百分比为：质量百分含量为50～55％的磷酸二氢铝溶液：30～70％；质量百分含量为60～70％的磷酸二氢锰溶液：10～15％；质量百分含量为80～85％的硼酸溶液：5～6％；质量百分含量为99％的硅烷偶联剂溶液：1～5％；质量百分含量为30～35％的硝酸盐溶液：0.1～0.5％；硅溶胶：10～15％；纳米硅酸铝：10～15％；纳米二氧化硅：20～30％；消泡剂：1～5％；水溶剂：适量。本发明采用磷酸二氢铝、纳米二氧化硅为主料制备了一种极薄硅钢带薄绝缘无机绝缘漆的涂层，涂层厚度均匀性好，涂层表面光亮、附着性强、绝缘电阻系数高。

本实用新型公开了硅钢片生产用上料装置，属于硅钢片生产领域，包括本体，所述本体包括侧板和U型板，所述侧板固定连接在U型板的一侧，所述本体的顶部横向设置有平移机构，所述平移机构上安装有气缸，所述气缸的底部安装有吸盘，所述U型板内腔的底部竖向固定连接有弹簧，所述弹簧远离U型板的一端水平固定连接有升降板，所述平移机构包括电机、螺纹杆、限位板和移动块，所述电机安装在侧板的顶部，所述电机的输出轴与螺纹杆的一端固定连接，通过设置弹簧，在第一个物料从上料装置移出后弹簧的弹力推动剩余物料，使得剩余物料进行上升，避免吸盘触碰不到物料的问题，简化吸盘移动轨迹，加快上料速度。

常化快冷是生产高牌号无取向硅钢和高磁感取向硅钢不可缺少的一个工艺环节,气-雾冷却则是实现常化快冷的关键方式之一。介绍了国内自主设计建设的常化酸洗机组气雾冷却系统的技术特性,并对其特点进行了系统分析,最后给出该系统在设计、运行参数的选择上若干注意事项,对气-雾冷却系统设计和使用具有一定的指导作用。 The normalizing rapid cooling is a indispensable process to high grade non-oriented silicon steel and high magnetic induction oriented silicon steel’ s production. The fog cooling is a key ways of coming true the normalizing rapid cooling. This paper introduces the technical features of the fog cooling system in normalizing pickling line which is the domestic independent design and construction. Meanwhile,the fog cooling system’s characteristic is analyzed systematacially. In the end,this paper ... 

该电磁钢板用涂敷组合物含有环氧树脂、潜伏性环氧树脂固化剂和热塑性弹性体，上述热塑性弹性体的熔点为100℃～200℃，并且弯曲弹性模量为超过5MPa且为100MPa以下，相对于上述环氧树脂与上述潜伏性环氧树脂固化剂的合计100质量份，上述热塑性弹性体的含量为10质量份以上且低于40质量份。