硅钢资料

【作者】 康凌晨； 王丽娜； ...

结合实际生产0.4%Si无取向硅钢，统计了不含Sn和0.025%Sn无取向硅钢的磁性能变化，利用金相显微镜、X射线衍射仪观察分析不同成分下试样的显微组织和微观织构。试验结果表明：Sn元素可以显著降低无取向硅钢的晶粒尺寸，0.025%Sn试样的平均晶粒尺寸比不含Sn减小28.4%;加入Sn元素后抑制了无取向硅钢中不利于磁性能的{111}面织构组分强度，提高了对磁性能有利的{100}面织构组分强度，0.025%Sn与不含Sn相比磁感均值从1.756 T提升至1.768 T,铁损均值从5.476 W/kg降低至5.204 W/kg,明显改善了无取向硅钢磁性能。 In this paper combined with the actual production of 0.4% Si non oriented silicon steel, the magnetic properties of non oriented silicon steel without Sn and 0.025% Sn were counted. The microstructure and microtexture of samples with different compositions were observed and analyzed by metallographic microscope and X-ray diffraction. The results show that: Sn can significantly reduce the grain size of non oriented silicon steel, and the average grain size of 0.025% Sn sample is 28.4% smaller tha... 

本发明公开了一种普通级稀土取向硅钢制备方法，通过添加稀土元素，利用第二相作用，对铸坯组织、热轧组织、初次再结晶晶粒和二次再结晶晶粒的影响，改善成品磁性能，即降低铁损，提高磁感。

本发明涉及一种三相变压器铁芯硅钢片叠装设备，包括工作台、传输装置和移动装置，所述的工作台的上端面由左至右依次设置有传输装置和移动装置，所述的移动装置包括匚形板、一号矩形通槽、转动杆、圆头板、移动架、限位架、水平板、夹紧架和挤压架，本发明无需通过人工对变压器铁芯硅钢片进行单个叠装，避免了传统的人工叠装造成的操作繁琐和增大劳动力的问题，本发明能够对叠装之后的变压器铁芯硅钢片进行快速整理限位，从而保证了叠装之后的变压器铁芯硅钢片的整齐度，本发明能够对叠装之后的变压器铁芯硅钢片进行快速压紧，从而提高了压紧效果。

本发明公开了一种适用于无取向硅钢极薄带表面涂覆的涂液，它由水溶性丙烯树脂、成膜助剂、耐盐雾助剂、流平剂、纳米氢氧化锆、消泡剂、水按质量比100:(2～8):(1～3):(1～5):(0～1):(0.1～0.5):(70～130)组成。将该涂液在无取向硅钢极薄带表面可表现出良好的涂覆性，经烘烤固化后形成的绝缘涂层表面透明光滑，附着性和绝缘性能优良，可有效提升无取向硅钢极薄带的综合性能，适合推广应用。

本实用新型提供一种硅钢片模具产品的吸料装置，包括固定架、电动伸缩杆、微型吸气泵、操作台、吸气机构以及放置机构，所述固定架上表面设有电动伸缩杆，所述固定架上表面设有微型吸气泵，所述微型吸气泵右端面设有吸气口，所述吸气口右端设有气管，所述电动伸缩杆底部设有吸气机构，所述吸气机构底部设有操作台，所述操作台上表面设有固定柱，所述固定柱前表面设有放置机构，与现有技术相比，本实用新型具有如下的有益效果：通过设置的橡胶套，代替手进行硅钢片的取料，通过设置固定杆，实现橡胶套的自动放料，更安全，通过设置的放置机构，实现硅钢片倾斜放置，方便进行硅钢片的拿取进行变压器装配。

试验研究了0.3 mm取向硅钢冷轧板(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005A1)的退火温度(760~880℃7 min)和退火时间(820℃3~9 min)对该钢的晶粒尺寸,再结晶和织构的影响。结果表明,最佳初次再结晶退火工艺为820℃5 min,该钢的平均晶粒尺寸为14.20μm,完全再结晶率为92%,不利{111}<110>结构含量为3.16%,有利织构{111}<112>,{012}<001>和高斯织构含量分别0.40%,4.73%和2.46%。 The effect of annealing temperature(at 760 ~ 880 X.for 7 min) and time(at 820℃ for 3~9 min) on grain size,recrystallization rate and texture of 0.3 mm cold-rolled sheet of oriented silicon steel(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005Al) has been tested and studied.Results show that with optimum recrystallized annealing at 820℃ for 5 min,the silicon steel average grain size is 14.20 fun,the complete recrystaUization rate is 92%,the unfavourable-texture {111}< 110 > content in steel is ... 

对低温法生产的以AlN为主抑制剂的Hi-B取向硅钢高温退火过程进行了中断实验,借助EBSD及TEM技术对高温退火连续升温过程中织构与析出物的演变进行了研究。实验结果表明,800℃时ODF图出现高斯织构组分,但强度很弱,高斯晶粒偏离角在10°以上;950~1 000℃时高斯晶粒异常长大,偏离角3~6°;高温退火过程析出物主要有球形、规则立方形及不规则多面体形3种形貌,由于渗N的影响,Zener因子先增大再减小,并且析出物在高斯晶界前沿优先粗化。 The annealing process at high temperature of Hi-B silicon steel using low slab reheat temperature and with AlN as the inhibitor has been studied by interrupting test,and the evolution of texture and precipitates during continuous heating-up in the annealing process at high temperature was analyzed by EBSD and TEM. The results showed that Goss texture appears in ODF at 800 ℃,but the intensity of Goss texture was very weak and the deviation angle was more than10°. Goss grains grow abnormally durin... 

对取向硅钢在不同气氛下的高温退火工艺进行实验室模拟，利用X射线衍射仪（XRD）分析了硅钢退火至900℃和1170℃时的样品表面氧化层和底层的物相组成，采用场发射扫描电镜（SEM）观察了样品表面氧化层和底层在截面方向上的微观形貌特征，并计算了高温退火一次升温阶段氧化反应的吉布斯自由能以及900℃时退火气氛的氧分压。结果表明：当退火气氛的露点温度保持一定时，较高的氢气含量有利于生成完整连续的底层；当退火气氛的水氢分压比保持一定时，在露点温度与氢气含量两者较低的条件下，底层附着性不佳易脱落，较高条件下，底层中夹杂着较多的铁单质；当氧化层中无FeO时，底层完整连续但易脱落，当FeO层较薄时，底层下方存在部分未反应的SiO₂,当FeO层较厚时，底层不完整连续且有分层。 The high temperature annealing process of grain-oriented silicon steel in different atmospheres was simulated in the laboratory. X-ray diffractometer（XRD） was used to analyze the phase compositions of the surface oxide layer and forsterite film of the silicon steel annealed to 900 ℃ and 1170 ℃. Field-emission scanning electron microscopy（SEM） was used to observe the micro morphology characteristics of the surface oxide layer and forsterite film of the samples in the cross section direction. The ... 

本实用新型公开了一种硅钢片用叠压装置，包括机架，机架上设有工作平台，工作平台的顶面上沿轴向并排设有定位块和可远离或者靠近定位块的抵紧块，定位块的水平截面呈L状，且其与定位块之间形成叠压区，叠压区的上方水平设有可竖直移动的传动板，传动板上竖向滑动穿设有若干均匀分布的导杆，导杆的两端均伸出传动板，且顶端设有限位块，底端共同安装有水平设置的压板，导杆上套设有位于压板和传动板之间的弹簧，机架上还设有与传动板和抵紧块均相连的可编程控制器。本实用新型解决了如何能高效且保质地对硅钢片进行叠压的技术问题，具有工人劳动强度低、叠压效率高且叠压质量好等优点。

试验研究了球刻痕法对高磁感取向硅钢的铁损、矫顽力、相对磁导率、巴克豪森噪声等磁学性能的影响.研究结果表明:经过球刻痕处理后,高磁感取向硅钢的铁损明显降低,矫顽力下降,8 mm球刻痕过后铁损值与矫顽力分别下降16.2%和14.7%,且铁损和矫顽力均随刻痕间距降低而减少.刻痕后的高磁感取向硅钢磁导率在高磁感应强度下明显上升,刻痕后巴克豪森噪声值明显降低,经过对比分析确定8 mm为球刻痕的最佳刻痕间距.从磁畴观察、细化磁畴的原理等方面解释了细化磁畴对高磁感取向硅钢性能的影响原因. The effects of the ball scribing on magnetic properties of high permeability grain-oriented silicon steels,including the iron loss,coercive force,relative permeability,and Barkhausen noise were investigated. The results showed that the iron loss and coercive force of the high permeability grain-oriented silicon steels apparently decreased 16. 2% and 14. 7% respectively after 8 mm ball scribing and they both decreased with the decrease of the scribing spacing at the same magnetic flux density. At... 

根据本发明的一个实施例的粘接涂料组合物，其包含聚乙烯丙烯酸酯100重量份和无机颗粒3至25重量份，所述聚乙烯丙烯酸酯包含由以下化学式1表示的重复单元和由以下化学式2表示的重复单元，所述聚乙烯丙烯酸酯包含75至95重量％的由以下化学式1表示的重复单元、5至25重量％的由以下化学式2表示的重复单元。