研究的两种取向硅钢（%:No1-0.042C、3.16Si、0.009Al、0.07Mn、0.50Cu、0.015S、0.0084N和No2-0.040C、3.20Si、0.014Al、0.22Mn、0.49Cu、0.016S、0.008 2N）由50 kg真空感应炉冶炼,锻成（mm）350×120×35板坯,经1 250℃30 min加热,开轧温度1 100℃,5道次热轧成2.3 mm板,终轧温度950～1 000℃。实验结果表明,两热轧板沿板厚方向存在组织和织构的不均匀性,热轧板次表层为再结晶组织,有较强的Goss织构组分;中心层为形变组织,具有典型的形变织构。含0.22%Mn的No2钢次表层{110}〈001〉织构组分比含0.07%Mn的No1钢弱,中心层{001}〈110〉织构组分大大强于0.07%Mn No1钢,导致两者磁性能差异,0.22%Mn No2钢磁感应强度(B₈₀₀)和铁损(P_1.7/50)分别为1.87 T和1.24 W/kg,0.07%Mn No1钢分别为1.88 T和1.18 W/kg。 Studied both grain-oriented silicon steels（%:No1- 0.042C,3.16Si,0.009Al,0.07Mn,0.50Cu, 0.015S,0.0084N and No2-0.040C,3.20Si,0.014Al,0.22Mn,0.49Cu,0.016S,0.0082N） are melted by a 50 kg vacuum induction furnace,forged to（mm） 350×120×35 slab,heated at 1 250℃for 30 min,with beginning rolling temperature 1 100℃hot-rolled to 2.3 mm plate by 5 passes,finishing-rolled at 950～1000℃.Test results show that the structure and texture along thickness of both hot-rolled plates are inhomogeneous:the subsurface ... 

本发明公开了一种低碳低硅钢铝质复合脱氧剂及其制备和使用方法，属于钢铁冶金技术领域。本发明为改善低碳低硅钢种可浇性差、夹杂降级率高的问题，提供了一种低碳低硅钢铝质复合脱氧剂，其包括：金属铝：50～60％；7Al2O3·12CaO预熔渣：10～20％，钝化CaO：10％～20％，Fe：10～20％，其余为微量杂质元素。本发明通过深入研究铝脱氧后钢中夹杂物的行为，提供了一种低碳低硅钢铝质复合脱氧剂，通过在转炉出钢过程加入该脱氧剂，能够有效降低钢中大型夹杂比例、对夹杂物改性，在不延长精炼时间的情况下降低夹杂物总量，改善目前此类钢种生产过程中存在的可浇性差，夹杂降级率高的问题。

一种高强型高频电磁性能优异的硅钢薄带板，钢中化学成分按重量百分比计为：C≤0.0027％、Si3.10％～3.35％、Als0.80％～1.2％、Mn0.20％～0.85％、P≤0.050％、S≤0.0020％、N≤0.0020％、Ti≤0.0020％、V≤0.0020％、Nb0.0050％～0.080％，其余为Fe和不可避免的杂质。本发明的无取向硅钢薄带产品用于新能源汽车驱动电机的制造，其强度高，中高频电磁特性优异。

本发明涉及变压器硅钢片技术领域，尤其是涉及一种变压器硅钢片组件成型冲裁机械及成型冲裁方法，包括基座、收卷装置、挤压装置、滚动装置和冲压装置，所述基座的上端位于四角处均固定连接有竖杆，竖杆的上端共同连接有横板，横板的下端设置有冲压装置，基座的上端设置有收卷装置，基座的上端位于收卷装置的后方设置有挤压装置，基座的上端位于挤压装置的后方设置有滚动装置；通过拉动拉环，带动圆板和推杆挤压第一弹簧，第一弹簧的挤压，使得推杆远离推槽，进而可取出模具，对模具进行更换；通过往凹槽内加入放置板，防止压板在撞击模具时，对模具进行支撑，防止模具发生变形。

本发明揭示了一种无取向硅钢的生产方法。所述生产方法中：按照Si:0.3～1.2％炼钢、制坯；将铸坯加热到1050～1150℃并保温150min以上，而后轧成厚度40～45mm的中间坯，再经精轧、卷取得到厚度为3.00±0.25mm的热轧卷板，精轧开轧温度≤Ar1＝872℃+1000*(11*[Si]‑14*[Mn]+21*[Al])；当Ar1≥1000℃，终轧温度T≤840℃，否则T≤Ar1‑160℃；卷取温度≤550℃；经常化、酸连轧得到0.500±0.005mm的冷硬卷，常化温度为850～950℃；退火温度820～950℃，经成品退火、冷却、涂层和精整，得到无取向硅钢成品。

研究了热处理工艺(退火温度、保温时间、冷却方式)对含Mn的Fe-6.5wt%Si高硅钢热轧带的显微组织及硬度的影响。结果表明,退火温度对Fe-6.5wt%Si合金的组织和显微硬度均有较大影响,随退火温度升高,平均晶粒尺寸和显微硬度均明显增大。小于1 h退火时,晶粒长大缓慢,而长时间(>1 h)退火时,一些次表层晶粒将发生异常长大。水冷组织比空冷组织略细小,但水冷显著降低了显微硬度。Mn含量提高能抑制850℃退火时晶粒的长大,并且促进退火后高硅钢的软化。 The influences of heat treatment process(annealing temperature,heating time,cooling methods) on the microstructure and microhardness of Fe-6.5wt%Si high silicon steel containing manganese for hot rolled strip were studied.The results show that the annealing temperature has a great effect on the microstructure and microhardness of Fe-6.5wt%Si alloy,and as the annealing temperature increases,the average grain sizes and microhardness will significantly increase.When annealing time for less than 1 h... 

本发明涉及一种硅钢片自动化纵剪裁切加工设备及加工方法，包括固定架、放卷筒、纵剪装置和裁切装置，所述的固定架的下端与已有地面相连，固定架前后对称分布，前后正相对的固定架之间转动连接有放卷筒，放卷筒的右侧从左至右依次设置有纵剪装置和裁切装置，本发明通过电机、转轴、转动杆做同步高速旋转运动转动杆带动切割刀做同步高速旋转运动，从而可实现切割刀对硅钢卷进行纵向裁剪的功能，使较宽的硅钢卷一分为二形成较窄的硅钢卷，以便提高后续对硅钢进行进一步的加工的速率。

本实用新型公开了一种取向硅钢加工用的酸洗除杂装置，包括装置主体，所述装置主体一侧固定安装有进气机构，所述装置主体内部活动安装有硅钢片，所述装置主体上方活动安装有一号转杆，所述一号转杆一侧活动安装有二号转杆，所述一号转杆和所述二号转杆外侧表面均安装有柔性吸附套筒，所述一号转杆和所述二号转杆一侧均活动安装有刮杆，所述装置主体前表面固定嵌入安装有一号进气管。本实用新型所述的一种取向硅钢加工用的酸洗除杂装置，能够在取向硅钢酸洗时，加快取向硅钢上方和下方的溶液流通，使酸洗装置内部的溶液浓度保持均匀，且使取向硅钢在酸洗后表面的溶液能快速风干，避免酸溶液过度与取向硅钢发生反应，以免对取向硅钢造成损伤。

​6月28日国联证券发布：《电力设备出海2024年中期投资策略：需求方兴未艾，供给释...

本实用新型公开了一种环保型无取向硅钢绝缘涂层液生产用篮式研磨机，包括底座，底座顶端的一侧固定安装有支撑柱，支撑柱的顶端固定安装有顶板，顶板的底端设有研磨组件，研磨组件包括两个固定板，两个固定板分别固定安装的顶板底端的中部和底端的另一侧，底座上设有固定组件，固定组件包括四个支撑板，四个支撑板均固定设置底座顶端的另一侧，四个支撑板的顶端固定安装有固定环，固定环的内部放置有料缸，本实用新型的有益效果是：通过研磨组件在粗磨后快速切换至细磨，不需要切换研磨机，提高研磨的效率，通过固定组件将放置在固定环内部的料缸进行固定，防止研磨过程中料缸发生移动。

本发明公开了一种电机制造硅钢片酸洗处理设备及其酸洗处理方法，该电机制造硅钢片酸洗处理设备包括开卷机、一号安装台、二号安装台、一号限位机构、二号限位机构、打磨装置、酸洗装置、干燥装置和切分装置。此外本发明还提一种电机制造硅钢片酸洗处理设备的使用方法,包括以下步骤：S1、硅钢卷安装开卷；S2、表面打磨；S3、硅钢酸洗；S4、表面干燥；S5、硅钢切分。本发明能够在硅钢片在酸洗前对其表面进行打磨处理，有效去除硅钢片表面较为明显的锈迹或者粘附有杂物，使得酸溶液能够与硅钢片表面充分接触反应，而且在硅钢片酸洗后能够及时干燥，有效防止酸溶液继续与硅钢片过度反应，达到提高产品质量的目的。

本实用新型公开了一种变压器硅钢片整平工装，涉及变压器装配技术领域，包括底板，所述底板顶部一角处安装有第一气缸，所述第一气缸的输出端固定有支撑块，所述支撑块一端设置有第一L型垫块，所述第一L型垫块两端皆开设有配合槽。本实用新型通过设置有第一L型垫块、第二L型垫块、传动带、第一气缸和第二气缸之间的配合，通过第二L型垫块内侧对运动中的变压器硅钢片进行拦截，第一气缸的输出端伸出带动第一L型垫块进行移动，使第一L型垫块将变压器硅钢片推至第二L型垫块拐角处，工作人员通过控制第一气缸输出端来回伸缩对硅钢片进行反复挤压整平，有效提高了变压器硅钢片整平机的工作效率，节约成本。