对商用50W330型无取向硅钢成品在930℃下保温2 h固溶并以不同方式冷却处理,利用磁性检测仪检测分析了处理前后的磁感和铁损变化,应用光学显微镜、扫描电子显微镜、X射线衍射仪观测分析了显微组织结构的演变。考察了平均晶粒尺寸、织构组分比及第二相粒子状态对磁性能的影响规律,结果表明:固溶处理前后平均晶粒尺寸的变化对硅钢磁性能的影响非常显著;当平均晶粒尺寸相差不大时,织构组分比[Goss+{100}]/{111}越大,磁感会越高;固溶处理会将细小弥散的第二相粒子重新回溶到基体中,减小了其对磁畴壁的钉扎作用,铁损随之下降。 The commercial 50W330 non-oriented silicon steel samples were heat treated at 930℃ for 2 h and cooled in different ways,then the iron loss and the magnetic induction of the samples before and after solution treatment were measured with a magnetic detector.The evolution of microstructural texture was analyzed by optical microscopy,scanning electron microscopy and X-ray diffractometry.The effects of average grain size,texture composition ratio and the second phase particles on the magnetic propert... 

本实用新型涉及一种硅钢片叠装用上下料装置，包括一供料单元，供料单元包括供料板、放置板、供料支架、供料辊、支撑组件；一上料单元，包括上料支架、上料板、第一升降丝杆、上料辊；一过渡组件，包括过渡支架、过渡底座、过渡升降丝杠，在过渡支架上安装有上下层分布的两组过渡输送辊组，位于上层的过渡输送辊组为容供料板输送的上料输送路径，上层的过渡输送辊组与下层的过渡输送辊组之间形成容供料板输送的下料输送路径。本实用新型的优点在于：通过供料单元、上料单元及过渡组件之间的相互配合，从而能够实现将满料的供料板输送给上料板或将空料的供料板输送给供料支架，完成了对满料或空料的供料板的自动输送，无需再由人工输送，非常的方便。

本发明提供了一种无取向电工钢，包括：C0.001～0.010％，Si0.5～4.0％，Mn0.05～0.8％，Al0.2～1.5％，P≤0.002％，S≤0.0015％，O≤0.002％，N≤0.0015％，各成分均为质量百分比；还提供一种无取向电工钢制造方法，包括：冶炼钢水、薄带连铸、常化酸洗、冷轧以及退火涂层。本发明中，在冶炼钢水时，控制钢水中C、Si、Mn、Al、P、S、O以及N几种成分的含量，且通过常化工艺，可以有效控制无取向电工钢成品的产品质量，具有较低的铁损以及较高的电磁性能，另外整体制造流程比较短，能够达到节能环保的目的，而通过冷连扎，有利于提高产品的质量、成材率和生产效率。

冷轧无取向硅钢（/%:0.003C,2.35Si,0.22Mn,0.011P,0.002S,0.36A1,0.003 0N）经890℃或940℃3 min常化的2.3 mm热轧板冷轧成0.35 mm薄板。研究了常化温度和800⁹20℃3 min退火对该钢高频（400Hz）磁性能和抗拉强度的影响。结果表明,830⁹20℃退火时高频铁损P_10/400值最低,随退火温度增加,晶粒尺寸增大,钢的抗拉强度降低;该钢的最佳热处理工艺为常化温度940℃,退火温度830℃,其抗拉强度R_m、高频铁损P_10/400和磁感应强度J₅₀分别为565 MPa,21.5 W/kg和1.69 T。 The cold-rolled non-oriented silicon steel（/%:0.003C,2.35Si,0.22Mn,0.011P,0.002S,0.36A1,0.003 0N） is cold-rolled to 0.35 mm sheet from 2.3 mm hot-rolled plate normalized at 890 ℃ or 940℃ for 3 min.The effect of normalizing temperature and annealing process at 800 ⁹20 °C for 3 min on high frequency（400 Hz） magnetic properties and tensile strength of the steel has been tested and studied.Results show that with annealing at 830 920 ℃the high frequency iron loss value P_10... 

含铜抑制剂作为取向硅钢的主抑制剂或辅助抑制剂不仅可以抑制初次晶粒的长大,促进二次再结晶,还可以降低铸坯的加热温度。取向硅钢中主要抑制剂为10～50 nm Cu₂S,在钢的铸坯、热轧、冷轧、脱碳等工艺过程均可析出;（Cu,Mn）_1.8S、Cu_1.8S、ε-Cu等主要作为辅助抑制剂,尺寸一般为30～50 nm（或大于50 nm）,主要在热轧阶段析出。总结了国内外有关取向硅钢中含铜抑制剂析出行为的研究进展,当前主要研究不同生产流程和工序中含铜抑制剂的析出行为和作用机理。 As main inhibitor or auxiliary inhibitor for grain-oriented silicon steel,the particles of inhibitor bearing copper not only inhibit the primary crystal growing and promote the secondary recrystallization,but also decrease the heat temperature of casting slab.The main inhibitor for grain-oriented silicon steel is 10～50 nm Cu₂S,which precipitate in process and procedure including steel casting slab,hot rolling,cold rolling and decarburizing process,while the 30～50 nm or more than 50 nm... 

分析了电感耦合等离子体发射光谱法(ICP-AES)测定硅钢中铌的检测过程,讨论了该检测过程中不确定度的主要来源,建立了该方法的定量的数学模型,并根据这一模型计算出了检测结果的合成标准不确定度和扩展不确定度。 The measurement of niobium content in silicon steel by inductively coupled plasma atomic emission spectrometry(ICP-AES) was analyzed,by which the main factors affecting the uncertainty of the measurement were ascertained and the calculation formula was given.Finally,according to the formula the combined uncertainty and expanded uncertainty were obtained. 

本实用新型属于冷轧硅钢技术领域的一种冷轧硅钢无压回水自动控制设备，包括底座，底座外表面的上端固定连接有工作台，工作台外表面上端的两侧分别固定连接有固定柱和压辊主体，工作台外表面上端的中部滑动连接有移动架，压辊主体的下端设置有集水槽，集水槽的内表面设置有浮球液位传感器。液压杆工作推动移动架位移到合适的位置，再通过气缸使伸缩管发生位移，使出水口接近钢板，设置的水箱高于出水口所以水可以在重力的作用下流淌，流出的水流到集水槽内，水流在集水槽内聚集，水流使浮球液位传感器的浮球上升，上升到合适的位置时，浮球液位传感器通过电缆发生电信号至控制器，此设置可以实现设备的自动控制，省去人工进行操作。

叠片系数是冷轧无取向电工钢的重要质量指标。为了提高叠片系数,必须保证无取向电工钢板形良好以及横向厚差小。针对攀钢冷轧厂4机架HC轧机轧制无取向电工钢的边部减薄问题,以无取向电工钢横向厚差最小作为目标函数,建立了一套针对无取向电工钢边部减薄控制的辊型曲线优化数学模型,开发了无取向电工钢专用辊型曲线,使无取向电工钢横向厚差从25μm降低到10μm以下,取得了良好的控制效果。 The lamination factor is an important quality index of non-oriented silicon steel strip.Considering the lamination factor,the non-oriented silicon steel must have a good shape and a smaller transverse thickness difference.In order to solve the edge thinning of non-oriented silicon steel strip in Panzhihua Steel,a mathematic model for designing the roll shape is built.In the model,the transverse thickness difference of non-oriented silicon steel strip is taken as the objective function.Based on t... 

本发明公开了一种改善高牌号无取向硅钢表面色差缺陷的方法，属于冷轧卷板表面质量改进技术领域。所述方法为：将连铸坯依次进行热轧、常化、酸洗、单机架轧制和连续退火工序，其中按重量百分数计，所述的连铸坯含有如下成分：C＜0.003%、Si1.6~2.0%、Mn0.35~0.65%、Al0.35~0.65%、P＜0.02%、S＜0.0025%、余量为Fe和其他不可避免的杂质元素，所有成分合计100%；其中热轧工序的卷取温度为620~640℃。本发明所述方法能够降低带钢表面氧化铁厚度并改变带钢表面氧化铁结构，改善高牌号无取向硅钢表面色差缺陷。

本发明揭示了一种无取向硅钢及其生产方法。所述生产方法包括：按照Si0.8～1.1％、Mn0.2～0.4％、不添加Sn和Sb进行炼钢，并制坯；将铸坯加热到1060～1120℃并保温150min以上，而后轧成厚度40～45mm的中间坯，再经精轧、卷取得到厚度为3.00±0.25mm的热轧卷板，精轧开轧温度≤872℃+1000*(11*[Si]‑14*[Mn]+21*[Al])；精轧终轧温度≤820℃，卷取温度≤560℃；常化、酸连轧，得到厚度为0.500±0.005mm的冷硬卷，常化温度850～900℃；成品退火温度820～880℃，退火后经冷却、涂层和精整，得到无取向硅钢。

本发明涉及一种冷轧硅钢厚度缺陷识别方法、装置及系统，本发明的方法包括如下步骤：采集带钢设定厚度及其实际测量厚度并保存；将带钢实际测量厚度与带钢设定厚度相减得到实时厚度差；根据实时厚度差计算厚度缺陷评分；根据评分结果，确定带钢在厚度这一指标的缺陷等级。本发明评估过程考虑了厚度波动情况，并进行量化，能成功识别冷轧硅钢的厚度缺陷，设别准确性较高，提高了冷轧硅钢生产水平，为冷轧硅钢质量控制提供依据。

【摘要】 <正>3月底,宝钢\"低温高磁感取向硅钢制造...