一种生产取向硅钢的氧化镁涂层烘烤质量控制方法，通过对带钢的实时温度测量建立对烘烤输出功率的实时反馈调节，据此形成基于烘烤输出功率的烘烤质量的实时控制。本发明的一种生产取向硅钢的氧化镁涂层烘烤质量控制方法，通过在烘烤炉出口的带钢上方增加一套可在带钢横向方向移动的在线板温计，基于在线板温检测值对烘烤炉状态进行监控，并建立烘烤输出功率控制系统实时调整，使得氧化镁涂层烘烤质量均匀，提高取向硅钢产品质量稳定性，节省能源消耗。

连续酸洗退火机组(CPAL)对于当前生产高磁感取向硅钢和高牌号无取向硅钢是必不可少的一个环节。常化炉是常化酸洗机组关键的组成部分。本文对国内自主建造的两条退火酸洗机组的工艺流程,特别是常化炉段进行了对比分析。总结出了常化炉的工艺及组成特点,对生产过程中暴露的问题进行了仔细的分析并提出了改进的意见,对于以后新建常化炉具有一定的提示作用。 The continous pickling annealing line(CPAL) is an essential step in producing high magnetic induction grain-oriented silicon steel and high grade non-oriented silicon steel.The normalizing furnace is a very important part of the CAPL.In this paper,the process flows of two CAPL with independent manufacture in our country have been compared,especially the part of normalizing furnaces.The characteristics of process and component are summarized and problems of the normalizing furnace during the prod... 

本实用新型涉及熔融石英陶瓷生产技术领域，且公开了一种高密度熔融石英陶瓷高磁感硅钢炉，包括底板，所述底板的顶部固定连接有高磁感硅钢炉本体，所述高磁感硅钢炉本体的顶部固定连接有密封轨，所述底板顶部的左右两端均固定连接有立柱，所述立柱的顶部固定连接有箱体，所述箱体的右侧固定连接有调节电机，所述调节电机的输出轴固定连接有螺杆，所述螺杆外表面的左右两端均螺纹连接有滑块，所述滑块的底部铰接有连杆，所述连杆的底部铰接有封板。该高密度熔融石英陶瓷高磁感硅钢炉，通过将调节电机的旋转力，转换为封板的上下移动力，无需人工手动开启或关闭，消除了安全隐患的同时，省时省力，操作简便。

本申请提供一种电工钢及其制备方法，制备方法包括：将电工钢的板坯进行热轧获得钢卷；将热轧后的钢卷进行酸洗冷轧；将酸洗冷轧后的钢卷进行第一次罩式退火；将第一次罩式退火后的钢卷进行平整；将平整后的钢卷进行第二次罩式退火；将第二次罩式退火后的钢卷进行重卷，以获得电工钢。本申请提供的电工钢的制备方法采用两次罩式退火，退火的主要目的是消除酸洗冷轧工序产生的加工硬化，使钢板充分再结晶，获得理想的铁损及磁感应强度。而采用两次罩式退火，相对于一次罩式退火工序来说，能够进一步降低铁损，提高电工钢的磁性能。

本发明属于酸洗设备技术领域，具体涉及一种硅钢生产用酸洗设备，包括酸洗池、放卷机构和收卷机构，酸洗池被依次分隔为第一酸洗腔、第二酸洗腔、浸泡腔和喷洗腔；第一酸洗腔和第二酸洗腔内滑动连接有刷洗架，浸泡腔内滑动连接有定位架，喷洗腔内滑动连接有喷洗架；刷洗架、定位架和喷洗架上均转动连接有多根转辊，转辊上设有刷毛；刷洗架和喷洗架上设有用于驱动转辊转动的驱动件；喷洗架上的转辊开有空腔和多个与空腔连通的喷孔，喷洗架上开有与空腔连通的通道和与通道连通的进水口；喷洗腔的底部和侧壁设有多个喷头；酸洗池内转动连接有多根位于第一隔墙上方的刷辊。在本方案，通过酸洗以及充分的刷洗，能够充分有效的除去硅钢表面的氧化皮。

本实用新型公开了一种取向电工钢的多项性能检测装置，涉及取向电工钢技术领域，为解决检测装置在对取向电工钢涂层性能检测时较为繁杂，增加了检测难度，检测的误差增加，且检测装置的性能检测较为单一，检测效果不佳的问题。所述底座的上方设置有安装架和吊梁架，所述安装架上设置有输料辊，输料辊设置有两个，两个所述输料辊之间设置有输送带，所述吊梁架的下方设置有弹性胶带，所述弹性胶带上方的两侧均设置有第三电动伸缩杆，且第三电动伸缩杆的两端分别与吊梁架和弹性胶带通过螺钉连接，所述弹性胶带的一侧设置有检测架，所述检测架上设置有激光灯、第一滤光片、接收器、第二滤光片和聚光片，所述激光灯和第一滤光片设置在弹性胶带的上方。

针对硅钢连续生产线设备存在的故障、隐患以及精度等影响产品质量的问题进行分析及改造,实现保证生产线设备稳定运行、提高设备精度及硅钢产品质量的目的。 This paper analyzes and transforms the electrical equipment failures, risks existed in slicon continuous production line, and the effect of accuracy to product quality, in order to ensure stable operation of equipment in production line and improve the accuracy of device, quality of silicon. 

在实验室模拟CSP流程制备了不同含量稀土铈(质量分数0~0.018%)的1.2%Si无取向电工钢,并对其进行1 000℃×5min的再结晶退火处理,研究了铈质量分数对无取向电工钢夹杂物、显微组织、再结晶织构和磁性能的影响。结果表明:随着铈质量分数的增加,微细夹杂物数量、再结晶晶粒尺寸、{100}和{110}织构组分、磁感应强度先增后减,{111}织构组分、铁损先减后增;铈的质量分数为0.005 1%时,钢中的夹杂物数量最少,再结晶晶粒尺寸最大,有利织构最多,磁性能最优,铁损P15/50为3.253W·kg-1,磁感应强度B50为1.751T。 Non-oriented electrical steels containing different contents rare earth Ce element(0-0.018wt%) were prepared in the laboratory by simulated CSP(compact strip production)process,and then recrystallization annealing at 1 000 ℃ for 5 min were performed,the effects of Ce content on inclusion,microstructure, recrystallization texture and magnetic properties of non-oriented electrical steels were studied.The results show that with the increase of Ce content,the amounts of fine inclusion,the size of re... 

试验2.3Si无取向硅钢(/%:0.003C,2.30Si,0.16Mn,≤0.020P,≤0.005S,0.54Al)冷轧板由常化和未常化的2.5 mm热轧板冷轧至0.6 mm(压下率76%),经750~950℃2.5 min中间退火后再冷轧至0.5 mm(压下率16.7%),成品板经890℃+960℃2.5 min退火。研究了中间退火温度对该钢晶粒尺寸、织构和磁性能的影响。结果表明,随中间退火温度的升高,二次冷轧前晶粒和成品晶粒增大,成品中不利织构组分{111}和{112}减弱,磁性能得到改善。热轧板经过常化时的磁性能明显好于未经常化时的磁性能,但中间退火温度较高时常化对磁性能的有利作用减弱。 The test cold sheet of 2.3Si non-oriented silicon steel(/%:0.003C,2.30Si,0.16Mn,≤0.020P,≤0.005S,0.54Al) is first cold-rolled from normalized and un-normalizing 2.5 mm hot-rolled plate to 0.6 mm sheet(reduction 76%),then intermediate annealed at 750~950℃ for 2.5 min and double cold-rolled to 0.5 mm sheet(reduction16.7%),the finished sheet annealed at 890℃+960℃ for 2.5 min.Effect of the intermediate annealing temperature on grain size,texture and magnetic performance of the steel has been studied.... 

利用场发射电镜及能谱仪研究了取向电工钢薄、厚板坯铸锭中不同区域的析出相差异,确定了MnS、AlN及Fe3C的析出顺序和形貌特征。结果表明AlN以先析出的MnS为形核核心,形成粗大微米级的复合析出相。针状Fe3C既可以在复合析出相表面形成也可以在基体中单独出现,主要受冷却速度的影响。在1250℃保温1～2 h,AlN、Fe3C均可完全回溶,但部分MnS仍不回溶。MnS尺寸随着保温时间延长而增大。导致热轧板中沿轧向分布的粗大MnS,减弱了粒子钉扎力。 Precipitates in thin and thick slabs of electrical silicon steel were investigated by means of field emission SEM and EDS analysis.The precipitation sequence and the morphology of MnS,AlN and Fe3C particles were identified.AlN particles are observed to be nucleated on surface of MnS forming micron-meter-sized complex particles.Acicular Fe3C can precipitate on surface of the complex MnS/AlN particles or directly from matrix depending on cooling rate of the slabs.After holding at 1250 ℃ for 1-2 h,... 

本实用新型涉及硅钢片切条技术领域，尤其涉及一种硅钢片分体式绕卷机构。包括所述切刀在固定座长度方向上设置有四组，四组切刀运动互不干涉，所述机架右侧中部上下两侧设置有支撑座和收卷驱动机构，所述第一收卷轴和第三收卷轴设置在上方的支撑座和收卷驱动机构上，所述第二收卷轴和第四收卷轴设置在下方的支撑座和收卷驱动机构上，硅钢片切条后，分别通过四组收卷轴进行收卷，四组收卷轴工作互不干涉，上下错位独立收卷，并且有独立横切刀控制单卷收卷长度，可根据客户要求将硅钢带分切并收卷成多卷不同重量的大小钢卷，使用效果好；并且采用独立收卷方式，硅钢带收卷的力度比较统一，不会出现收卷松动的现象。

取向硅钢利用析出物作为抑制剂,抑制初次再结晶晶粒的长大,抑制剂是取向硅钢发生二次再结晶的基本条件之一。文中通过低温板坯加热技术制备取向硅钢,采用透射电镜(TEM)观察并研究了高温退火阶段抑制剂的演化过程。结果表明,渗氮后形成的非晶态Si3N4析出物不稳定,在700～750℃退火升温阶段转化为(Al,Si)N;(Al,Si)N颗粒在800℃发生团聚,随后长大并粗化;(Al,Si)N是低温取向硅钢主要抑制剂,随退火温度的升高,(Al,Si)N抑制力大幅下降。 Precipitates as inhibitor are used to inhibit the grain growth of primary recrystallization in grain-oriented silicon steel,and inhibitor is one of the basic conditions for occurring of secondary recrystallization.The grain-oriented silicon steel was produced by low temperature slab heating and nitriding technique.The evolution of inhibitor was observed by transmission electron microscopy.The results show that Si3N4 particles are precipitated after nitriding,and Si3N4 particles are amorphous and...