硅钢资料

研究了CSP工艺流程生产的硅含量为1.5%的无取向电工钢在不同常化温度下对磁性能的变化。研究结果表明:随着常化温度的提高,热轧板的晶粒尺寸增大,且组织均匀性提高;此外成品的有利织构组分{100}<0vw>、α、η增强,不利织构组分减弱;铁损P1.5/50呈下降趋势,磁感B50上升平缓。在常化工艺为970℃×2.5min下,对应的铁损P1.5/50<3.4W/kg,磁感B50>1.74T。 The effect of normalizing temperature on the magnetic properties of non-oriented electrical steel containing 1.5%silicon produced by CSP process was studied.The results show that with increasing normalizing temperature,the average grain size of hot-rolled plate increases and the microstructure uniformity is improved.Furthermore,the texture components of finished products are improved through enhancing of{100}<0vw>,αandηtextures and weakening of{111}<112>texture;the core loss P1.5/50 ... 

采用光学显微镜和X射线衍射仪研究了常化退火处理对无取向硅钢热轧板和成品退火板显微组织和织构的影响。结果表明:常化退火处理消除了热轧板中的变形组织,促使变形晶粒完成再结晶;常化退火处理使高斯织构和立方织构易通过再结晶在变形带内形核和长大,可显著降低成品退火板的{111}和{112}不利织构组分的占有率,提高{100}和{110}有利织构组分的占有率,从而有利于提高无取向硅钢成品板的磁性能。 The effect of normalizing annealing treatment on microstructure and texture of non-oriented silicon steel hot rolled plates and final products were investigated by means of optical microscope and X-ray diffractometer analysis.The results show that the deformed microstructure of the hot rolled plates transformed into recrystallized grain after normalizing annealing treatment.The grains of Goss texture and cubic texture crystallographic orientation were formed and grown by recrystallization in the... 

针对目前大部分无取向电工钢处理液为含铬处理液、且需在较高温度下固化的情况,在分析成膜物质性质的基础上,试验研究了一种可低温快速固化的电工钢环保绝缘处理液,研究了其涂装工艺,并测定了涂层的附着性、绝缘性、耐热性、耐蚀性等性能。试验结果表明:该处理液可在150~250℃下快速烘干固化,涂层表面光滑且致密均匀,性能优良,可满足中小电机的使用要求。 At present,most of the insulating fluid for non-oriented electrical steel contains chromium,and should be cured at high temperature.On the basis of analyzing the characteristics of the film-forming substance,a kind of eco-friendly insulating fluid with lower curing temperature for non-oriented electrical steel sheet was developed in the experiments.Then its coating process was studied,and the adhesiveness,insulativity,heat resistance,corrosion resistance and other properties of the coating was m... 

本实用新型涉及一种具有在线测量功能的电工钢片横剪线，包括床身，床身上沿其长度方向安装有导轨，电工钢片在外部驱动辊带动下以导轨为导向移动；位于导轨一端端头外部的床身上安装有测量辊组件，位于导轨另一端处的床身上安装有影像测量组件；测量辊组件、导轨和影像测量组件的中心位于同一直线上，影像测量组件横跨设置于导轨上方；位于测量辊组件和影像测量组件之间的床身上依次安装有冲孔组件、V冲组件和斜剪组件；本实用新型通过测量辊组件对电工钢片行进长度进行检测，通过影像测量组件对电工钢片成型尺寸进行检测，从而便利于及时调整横剪线整体的运行状态，有效助力于保证合格率，并降低了人工负担。

本实用新型公开了一种电机硅钢片用激光切割机的高压空气冷却干燥装置，包括一端侧带密封端盖且另一端侧设出气接头的换热筒、设在密封端盖的制冷剂进液管和回气管，密封端盖设有进气接头，换热筒内设热交换器，热交换器由换热盘管、换热翅片和下截圆挡板、上截圆挡板组成，下截圆挡板的平底切边、上截圆挡板的平顶切边分别与换热筒内壁具有间隔；制冷剂进液管的一端与制冷系统的一端连接而其另一端顺次连接分液头、毛细管、换热盘管的上端入口，回气管的一端与制冷系统的另一端连接而其另一端依次连接回气汇总管、换热盘管的下端出口；换热筒的底部安装有带放水阀的自动排水部件。通过本装置换热后可获得冷却干燥的高压空气以供激光切割机使用。

针对某硅钢车间ST机组的除尘系统除尘效率较低、排放浓度不达标、二次污染较严重的问题,通过现场调研,对除尘系统、含尘气体组分与物性参数等进行测试和分析,运用管道伴热技术改善粉尘黏性后,再选取合适的除尘器对粉尘进行除尘处理,大大地提高了系统的除尘效率。 To solve the problems of low dust removal efficiency, substandard emission concentration and severe secondary pollution, some investigations are conducted to test and analyze the dust removal system,dust-gas composition and relevant physical parameters.Moreover, dust removal efficiency is greatly improved by the use of pipe heat tracing technology and by choosing appropriate dust remover. 

为了确保硅钢铬酸盐涂料的环保性,需要严格控制涂料的固化工艺,保证涂料固化过程中涂料中的六价铬充分转化为三价铬。对涂料及原料进行热重分析(TG)及差示扫描量热法分析(DSC)。结果表明,MgO与铬酐混合转化为MgCrO4,使六价铬稳定性增强,其中大部分Cr6+转变为Cr3+发生在620~700℃,在450~500℃高于铬酐发生大量失重,因此必须加入还原剂保证涂料中六价铬被充分还原;超过360℃后树脂会发生分解,因此实际板温不能超过360℃;加入了还原剂的整体涂料的失重温度区间主要在260~320℃,因此涂料固化时钢板的实际温度最佳区间为320~360℃。 Because of the silicon steel chromate coating’s environmental requirements,the paint curing process must be controlled strictly to ensure all Cr( Ⅵ) transforms to Cr( Ⅲ). The TG and DSC analyses of the paint are studied. The reaction of MgO and CrO3 would generate MgCrO4,enhancing the stability of Cr( Ⅵ). The most r( Ⅵ) in MgCrO4 changes to Cr( Ⅲ) at 620-700 ℃,while the CrO3 has a large weight loss at 450-500 ℃. The reductant must be added in the paint to make sure the Cr( Ⅵ) could transform suf... 

本实用新型公开了一种取向硅钢绝缘涂层液生产用分散机，包括固定底座，固定底座顶端的一侧固定安装有套筒，套筒的内部滑动设有活塞杆，套筒的内部设有电动液压升降柱，电动液压升降柱的底端固定安装在固定底座顶端的中部，电动液压升降柱的顶端与活塞杆的底端固定连接，活塞杆的顶端固定连接有箱体，箱体底端的一侧固定安装有伺服电机，本实用新型的有益效果是：通过滑块、橡胶块、空心转轴和伺服电机的配合使涂层液搅拌分散的更加均匀，通过固定装置可以将盛有涂层液的桶固定住，防止涂层液桶转动，这样可以使涂层液进行充分搅拌，不需要时刻对其调整固定，这样也可以提升工作效率，提高生产速率，而且操作方便。

硅钢连续退火线是无取向硅钢生产的成品线。由于受机组布置的影响,带钢经转向辊进出口活套后,当套量达到60%后就出现偏离生产线的情况,从而影响最终产品的质量及成材率,甚至损坏设备。针对某冷轧厂硅钢连续退火机组出口活套入口处带钢跑偏开展纠偏研究,利用Matlab对该纠偏系统进行动态仿真研究,分析系统的稳定性。 Silicon steel continuous annealing line is non oriented silicon steel production of finished product line.Due to the influence of unit layout,strip by roll Import & Export loop,when the set volume reached 60% after the emergence of deviation from the production line,thus affecting the quality of the final product and the rate of finished products,and even damage the equipment.For the export of continuous annealing line in cold rolling silicon steel strip deviation rectification loop at the e... 

【机构】 宝山钢铁股份有限公司规划与科技部； ...

本发明涉及一种基于全流程数据的冷轧硅钢厚度控制方法、装置，该方法包括：针对某个冷轧钢卷，首道次默认使用监控AGC，在进入冷轧机工序生产之前，获取其前序全流程的生产工艺和质量数据，并进行预鉴定，若发现硅钢性能波动，则首道次额外再使用秒流量AGC；若发现硅钢厚度波动不剧烈，则首道次额外再使用前馈AGC。本发明无需人工干涉，采用上述规则在生产前就能自动确定最优的AGC生产模式，保证了硅钢产品厚度精度，避免硅钢厚度指标上的缺陷。

无取向硅钢中夹杂物的存在会抑止晶粒生长,使基体的均匀连续性中断,其在钢中的形态、含量及分布情况都不同程度影响着硅钢的性能,尤其是对磁性能起关键的作用。因此,全尺度分布考察夹杂物对无取向硅钢夹杂物的研究极为重要。本实验确定了适用于不同牌号无取向硅钢夹杂物全尺度分布的分析方法:样品制备—小样电解—过滤喷金—根据不同牌号的要求选择合适的放大倍率扫描观测—夹杂物颗粒的分类统计。通过统计的结果,结合电解的失重量可以得到不同尺度的体积分布数据。实验分析了不同牌号和工艺无取向硅钢夹杂物的种类、形貌、大小和尺度分布,并初步考查了夹杂物与磁性能的关系,对无取向硅钢的工艺研究具有一定参考价值。 Inclusions in non-oriented silica steel could inhibit the growth of grain and cause discontinuity of micro-structure.The configuration,content and size distribution of inclusion have different effects on the performance of silica steel,especially significant on the magnetic property.Therefore,it is very useful to completely characterize inclusions with full size distribution in silica steel.In our research,full size analysis method for inclusion in silica steel had been established as follows: s...