硅钢资料

采用轧制法制备出具有低铁损高磁感0.23mm厚6.4%(质量分数)Si高硅钢。沿轧制方向的最终磁性能为B8=1.474 T,B50=1.714 T;P10/50=0.30W/kg,P15/50=0.88W/kg。利用X射线衍射及背散射电子衍射(EBSD)技术分析了高硅钢在轧制及退火过程中的织构演变过程。结果表明,通过采用大压下率热轧,确保热轧板次表层中产生更多的高斯织构,随后进行遗传;温轧板中粗大的晶粒有利于冷轧剪切带的形成;冷轧板经脱碳退火后生成强{210}〈001〉织构及次表层较强的高斯织构是在轧向上获得高磁感的原因,归因于其在{111}〈112〉冷轧形变晶粒内的剪切带优先形核并长大;最终退火后虽出现了随机取向,但以{310}〈001〉织构为代表的η织构得以保留并且增强,进一步提高了磁感。随着退火温度的升高及保温时间的延长,高硅钢薄板晶粒尺寸不断增大,铁损明显降低。 6.4wt%Si high silicon steel sheets(0.23mm thick)with low iron loss and high magnetic induction were successfully produced by rolling process.The final magnetic properties along the rolling direction(RD) were:B8=1.474T,B50=1.714T;P10/50=0.30 W/kg,P15/50=0.88 W/kg.The texture evolution during rolling and annealing was investigated by means of X-ray diffraction and electron backscatter diffraction(EBSD).It was found that more Goss textures formed in the subsurface of hot rolled plates by using larg... 

本实用新型公开了一种硅钢片制作用防止硅胶泄露结构，包括运行组件与固定密封组件，所述运行组件的内侧壁设有固定密封组件，所述运行组件包括板体、第一凹槽、壳体、硅钢片、支撑板、连接块、密封圈、防护板和通孔，所述板体的内侧壁开设有第一凹槽，所述第一凹槽的内部设有壳体，所述壳体的内侧壁设有硅钢片，所述硅钢片的两侧相互对称焊接有四个连接块，四个所述连接块相斥一侧均贴合于第一凹槽的内侧壁，本实用新型首先通过硅钢片两侧密封圈保障密封效果，设置的橡胶管起到二次密封防护作用，并借助其内部的弹簧及U型板实现防偏移的效果，最后一方面可以在壳体相邻组件内侧加胶并且提高其内部硅钢片的厚度，以此实现多重密封防漏。

连续酸洗退火机组(CPAL)对于当前生产高磁感取向硅钢和高牌号无取向硅钢是必不可少的一个环节。常化炉是常化酸洗机组关键的组成部分。本文对国内自主建造的两条退火酸洗机组的工艺流程,特别是常化炉段进行了对比分析。总结出了常化炉的工艺及组成特点,对生产过程中暴露的问题进行了仔细的分析并提出了改进的意见,对于以后新建常化炉具有一定的提示作用。 The continous pickling annealing line(CPAL) is an essential step in producing high magnetic induction grain-oriented silicon steel and high grade non-oriented silicon steel.The normalizing furnace is a very important part of the CAPL.In this paper,the process flows of two CAPL with independent manufacture in our country have been compared,especially the part of normalizing furnaces.The characteristics of process and component are summarized and problems of the normalizing furnace during the prod... 

本发明涉及磁悬浮电机轴硅钢片叠压领域，尤其涉及一种永磁电机内嵌式硅钢片的叠压装置、叠压工装及方法和磁悬浮鼓风机。该装置包括带槽钢板和多个长钢板；带槽钢板设置有转轴孔，转轴孔面积大于电机转轴套合硅钢片部分的截面积并且被电机转轴穿过；多个长钢板底端分别与带槽钢板相连接，并且带槽钢板上表面与硅钢片相贴合；多个长钢板竖直分布并且其分布位置与硅钢片中的多个磁钢槽相对应，长钢板外表面与硅钢片中的磁钢槽相配合。该装置通过对硅钢片的磁钢槽进行定位，保证叠压后的硅钢片的磁钢槽对齐，提高硅钢片内嵌磁钢质量。

本发明公开了一种消除取向硅钢单边浪缺陷的方法，其包括如下步骤：1)、制作专用盖板；所述专用盖板包括环形板，所述环形板外边缘设有多个剪开处；2)、将待装炉的取向硅钢钢卷吊运至高温退火炉炉台；3)、将专用盖板铺于取向硅钢钢卷上端面外圈；4)、将专用盖板上的各剪开处向下弯折，勾住取向硅钢钢卷外沿；5)、扣上内罩，内罩底边砂封；6)、钢卷进炉，完成高温退火过程。本发明能有效保护钢卷边部，防止钢卷上端面翻边；该方法还能将钢卷内部水分排出，避免钢带表面氧化。

利用XRD和EBSD研究了长轴分别平行于轧向(RD)、横向(TD)和轧面法向(ND)的柱状晶样品在热轧、冷轧及退火过程中的组织、织构演变规律,并分别从几何诱导和取向诱导两个方面分析了晶界的交互作用.结果表明,热轧时由表面摩擦剪切作用引起的组织和织构梯度直接影响并遗传给后续冷轧及退火样品.热轧后,不同样品的初始晶粒形状各向异性差异消失,形成相同的各向异性晶界组织,但晶体学各向异性发生改变,导致随后冷轧、退火组织及织构的变化均不同于直接冷轧的柱状晶样品.研究中特别关注了对磁性能有利的{100}取向区域与晶界的关系. Columnar grains show their special characteristics of morphological and crystallographic anisotropies, and thus markedly influence the microstructure and texture evolution during rolling and annealing process in electrical steel. The rolling and annealing microstructure and texture of three columnar grained samples with the long axes arranged along different directions were investigated by means of XRD and EBSD techniques, and the effects of columnar grain boundaries were analyzed from the view ... 

研究的两种取向硅钢（%:No1-0.042C、3.16Si、0.009Al、0.07Mn、0.50Cu、0.015S、0.0084N和No2-0.040C、3.20Si、0.014Al、0.22Mn、0.49Cu、0.016S、0.008 2N）由50 kg真空感应炉冶炼,锻成（mm）350×120×35板坯,经1 250℃30 min加热,开轧温度1 100℃,5道次热轧成2.3 mm板,终轧温度950～1 000℃。实验结果表明,两热轧板沿板厚方向存在组织和织构的不均匀性,热轧板次表层为再结晶组织,有较强的Goss织构组分;中心层为形变组织,具有典型的形变织构。含0.22%Mn的No2钢次表层{110}〈001〉织构组分比含0.07%Mn的No1钢弱,中心层{001}〈110〉织构组分大大强于0.07%Mn No1钢,导致两者磁性能差异,0.22%Mn No2钢磁感应强度(B₈₀₀)和铁损(P_1.7/50)分别为1.87 T和1.24 W/kg,0.07%Mn No1钢分别为1.88 T和1.18 W/kg。 Studied both grain-oriented silicon steels（%:No1- 0.042C,3.16Si,0.009Al,0.07Mn,0.50Cu, 0.015S,0.0084N and No2-0.040C,3.20Si,0.014Al,0.22Mn,0.49Cu,0.016S,0.0082N） are melted by a 50 kg vacuum induction furnace,forged to（mm） 350×120×35 slab,heated at 1 250℃for 30 min,with beginning rolling temperature 1 100℃hot-rolled to 2.3 mm plate by 5 passes,finishing-rolled at 950～1000℃.Test results show that the structure and texture along thickness of both hot-rolled plates are inhomogeneous:the subsurface ... 

本发明属于硅钢制造技术领域，具体涉及一种改善硅钢热轧板边部质量的加工方法，包括：连铸、铸坯预变形处理、铸坯加热处理和热轧处理；其中，所述铸坯预变形处理包括：在所述铸坯的温度为500～900℃下，对所述铸坯的沿长度方向的两侧壁通过立辊施加压力，直至形变量h为10～50mm；所述铸坯加热处理的加热温度为1100～1200℃，保温时间为4～6h。本发明提供的改善硅钢热轧板边部质量的加工方法，采用铸坯两侧壁的侧压工艺，有效解决了热轧板边部裂纹的缺陷，提高了边部塑性，提高了成材率并降低了生产成本。

本发明公开了硅钢片铁芯生产线，包括放卷机构、剪切机构、送料机构、叠片机构和下料机构，送料机构包括磁性传送带、送料件和第一定位杆，磁性传送带包括上传送带和下传送带，送料件可沿磁性传送带的正交方向平行伸出，其中，第一送料分台和第二送料分台安装于上传送带的下方并且相背运动，第三送料分台和第四送料分台安装于下传送带的下方并且相背运动，第一定位杆用于定位硅钢片，叠片机构包括叠放台、悬梁和两个六自由度机械手，六自由度机械手吊装于悬梁上，包括有电永磁铁，用于吸取硅钢片，下料机构包括滑板，叠放台放置于滑板上。根据本发明的硅钢片铁芯生产线，可提高设备自动化程度，提高叠片速度，从而提高生产线的生产效率。

本发明提供了一种高硅钢及其制备方法，所述高硅钢由如下质量分数的化学成分组成：Si：5.0‑7.0％，Ni：0.001‑0.05％，Ce：0.0001‑0.0002％，其余为Fe和不可避免的杂质。本发明提供的高硅钢的延伸率为15‑22％，抗拉强度为739‑824MPa，磁感应强度B8为1.26‑1.29T，铁损P2/10k＝68‑80W/kg，矫顽力为10.6‑13.4/m，最大磁导率为19000‑25000，具有良好的磁性能和延伸性能，易加工且可大规模生产应用。

本实用新型公开了一种无取向硅钢厚涂层涂层液生产用纯水制水机，包括底板，底板顶端的两侧分别固定设有固定座和存水筒，固定座顶端的中部设有蒸馏组件，蒸馏组件包括球形釜，球形釜设置在固定座的顶部，球形釜的外部固定套设有导热层，导热层的内部固定嵌设有电热丝，导热层的外部固定套设有隔热层，本实用新型的有益效果是：通过设置的电热丝通过导热层对球形釜内部的水进行加热，球形釜提供更加均匀的受热效果，水蒸气通过V形管进入L形管，通过设置的环状冷却管内部的液氮对水蒸气进行冷却，便于提供更高效的蒸馏处理，通过设置的防腐蚀磁铁网格滤板、无纺布滤层、活性炭滤层和高密度滤网层，便于提供更好的过滤效果。

本发明一种解决取向硅钢热轧板晶粒粗大的方法，在取向硅钢的成分设计中减少固溶温度较高的MnS的含量，降低铸坯加热温度，同时计算实际取向硅钢成分中γ‑相含量与温度之间的关系，依据计算结果设计取向硅钢的热轧工艺，可以保证20％～30％的γ‑相数量，成功解决取向硅钢热轧板晶粒粗大的问题。