硅钢资料

本发明涉及薄规格高牌号无取向硅钢冷轧领域。一种提高超薄规格高牌号无取向硅钢厚度精度的冷轧方法，硅钢成品厚度规格在0.15mm～0.25mm，坯料采用常化酸洗切边后的硅钢卷，初始厚度为2.0～2.3mm，采用二十辊单机架轧机轧制，在轧制过程中，对整个轧制过程进行控制。本发明的有益效果是：解决二十辊轧机超薄规格无取向冷轧硅钢纵向厚度波动同时减小横向同板差的方法。

本发明提供的一种耐热型低损耗取向硅钢，取向硅钢的单面采用激光刻痕形成平行线状沟槽；所述激光刻痕为取向硅钢制备工艺中的渗氮步骤之后和在涂覆MgO涂层步骤之前实施；在渗氮步骤之后和在涂覆MgO涂层步骤之前进行激光刻痕加工不会破坏高温退火后形成的硅酸镁底层，底层完整性好，刻痕形成的沟槽位于取向硅钢带材金属基体表面，在高温退火过程中沟槽内直接反应生成硅酸镁底层，最终取向硅钢带材表面涂覆张应力涂层后光滑、平整、无凹凸，取向硅钢带材损耗低、叠片系数高、耐热，成品取向硅钢带材既可用于制备立体卷铁心变压器也可用于制备叠片铁心变压器。

针对不同牌号的无取向硅钢产生结疤缺陷的难易程度和表面结疤缺陷的外形特征及分布规律,分析了该缺陷产生的原因。通过调整剪前导板的对中度,设置精轧侧导板开度余量及短行程数值,及时修补与更换侧导板,减少带坯与侧导板挤撞程度,有效地降低了结疤缺陷发生率。 This article analyses the cause of the scab defects according to the defects appearance characters and distribution law,degree of difficulty to form scar of non-oriented silicon steel. It can effectively decrease the scabs by different methods,such as adjusting the center line of guide plate,setting the opening margin and short stroke value of the side guide on finishing mill,timely repairing and replacing of side guide,decreasing the collision between the strip and side guide. 

借助于EBSD对比研究了常化退火对高牌号无取向电工钢热轧组织和织构演变的影响,分析了常化退火对热轧板各厚度层织构的演变规律。结果表明,常化退火改善了热轧组织的均匀性,并弱化了热轧变形的γ纤维织构。升高常化退火温度,可增大热轧板的晶粒尺寸,提高{100}和{110}织构组分占有率,有利于提高无取向电工钢成品板的磁性能。 Effects of normalizing annealing on microstructure and texture of high-grade non-oriented electrical steel hot-rolled sheet were investigated by EBSD. Emphasis was put on the effects of normalizing annealing on texture evolution in the sheet thickness. The results show that the hot-rolled microstructure homogeneity is improved and the γ-fiber texture is weakened by normalizing annealing treatment. The grain size of hot-rolled sheet and intensity of the {100} and {110} favorable texture can be in... 

本发明涉及硅钢技术领域，尤其涉及一种硅钢连退炉辊除瘤方法及装置。包括连杆、手柄、磨削片、密封盖、端盖与套筒；磨削片垂直固接在连杆一端的外壁上，手柄固接在连杆的另一端，手柄与磨削片处于同一平面上；连杆套接在套筒内，连杆能沿套筒轴向移动，套筒固接在端盖上；硅钢连退炉辊下方的炉墙设有与连杆及磨削片相应的磨辊孔，端盖或密封盖固接在磨辊孔处。1)确定结瘤炉辊；2)确定结瘤在碳套辊上的位置；3)插入除瘤装置；4)磨削；5)抽出。本发明降低废品量，提高成材率；减少停炉处理结瘤时间，降低能耗，提高生产率；提高难磨瘤辊的修复率，降低炉辊成本。

本实用新型公开了一种无取向硅钢喷涂用即时干燥装置，包括干燥箱，所述干燥箱内滑动连接有加热台，所述干燥箱顶部设置有加热箱，所述加热箱左右两侧分别设置有进风管和出风管，所述进风管和出风管均与干燥箱连通，所述加热箱内部从左到有依次固定连接有风机和加热网，所述干燥箱内设有带式传送机，通过带式传送机使喷涂过后的硅钢在干燥箱中移动，首先经过加热台加热，使涂层表面干燥硬化，不会变形，然后再经过加热箱吹出的风对硅钢表面的涂层进行进一步的烘干，从而保证干燥过程中涂层不会起褶皱。

含铜抑制剂作为取向硅钢的主抑制剂或辅助抑制剂不仅可以抑制初次晶粒的长大,促进二次再结晶,还可以降低铸坯的加热温度。取向硅钢中主要抑制剂为10～50 nm Cu₂S,在钢的铸坯、热轧、冷轧、脱碳等工艺过程均可析出;（Cu,Mn）_1.8S、Cu_1.8S、ε-Cu等主要作为辅助抑制剂,尺寸一般为30～50 nm（或大于50 nm）,主要在热轧阶段析出。总结了国内外有关取向硅钢中含铜抑制剂析出行为的研究进展,当前主要研究不同生产流程和工序中含铜抑制剂的析出行为和作用机理。 As main inhibitor or auxiliary inhibitor for grain-oriented silicon steel,the particles of inhibitor bearing copper not only inhibit the primary crystal growing and promote the secondary recrystallization,but also decrease the heat temperature of casting slab.The main inhibitor for grain-oriented silicon steel is 10～50 nm Cu₂S,which precipitate in process and procedure including steel casting slab,hot rolling,cold rolling and decarburizing process,while the 30～50 nm or more than 50 nm... 

利用本钢技术中心试验厂技术手段,并与北京钢铁研究院合作,试制了用作家电用电机、微电机、小电机或部分中型电机铁芯的冷轧无取向电工钢。试制钢硅含量小于0.5%,钢板表面平滑,公称厚度0.5mm,且厚度均匀偏差小,性能测定结果表明,产品的磁性能、力学性能满足其使用要求。 BX STEELTechnology Center pilot plant using technical means,and with Beijing Iron and Steel Research Institute,trial cold rolled non-oriented electrical steel that has been used as appliance motor core,micro motor core,small motor core,or part of the medium-sized motor core。Trial steel of silicon content is less than 0.5%,steel plate surface is smooth,the nominal thickness of 0.5mm,and the thickness deviation is small,performance measurement results show that the magnetic properties,mechanical p... 

以太钢热连轧厂的硅钢为研究对象,利用凸度仪测量热轧带钢出口凸度值,采用矩阵和失效模式的分析方法了解影响带钢凸度变化的主次因素。研究结果表明:通过有效控制轧制过程中的加热温度、时间及采用合理的辊型,硅钢凸度精度提高了4.34%左右。 In this paper,we take the hot-rolled silicon steelsheet of Taigang as the research symbol,exit profile was measured by convex instrument,the primary and secondary factors that affect the strip profile were measured by using matrix and failure mode analysis methed.The results indicate that convexity accuracy has significantly improved by nearly 4.34% through the effective control of the heating temperature,heating time and the use of correct roller type in the process of hot rolling. 

一种厚度≤0.15mm无取向硅钢带，其组分及wt%为：Si：2.0～6.5%，Mn：0.13～0.40%，S≤0.020%，P≤0.020%，Als：0.15～0.9%，C≤0.010%；工艺：经冶炼、浇注成坯后热轧至中间坯厚度；冷轧；常温脱脂；光亮罩式退火；经碱洗后涂覆；分条。本发明在保证铁损P1.0/400£13W/kg,磁感B2000³1.5T下，还使钢带厚度公差不超过±0.005mm,最小叠装系数³0.92完全满足连续冲制要求。

本发明提供一种优化无取向硅钢连续退火工艺的铁损预测方法，步骤包括：S1.建立预测模型回归方程表达式；S2.将无取向硅钢中的硅、锰、铝质量含量及预设的退火速度、退火温度代入S1中的回归方程表达式中进行计算；S3.将步骤S2计算得到的预测值与目标值进行比较，如果预测值在目标值的允许误差范围内，则按照预设的退火速度、退火温度进行生产；否则对预设的退火速度、退火温度进行调整，直至预测值能够达到目标值的要求后再进行生产。本发明提供的模型能够提高产品质量，对优化无取向硅钢连续退火工艺具有指导意义。

一种无取向硅钢用轧制工作辊，属于轧机工作辊技术领域，该轧制工作辊，包括锥形曲面段和平直段，锥形曲面段包括弧形段Ⅰ和弧形段Ⅱ，弧形段Ⅰ的弧面内凹，弧形段Ⅱ的弧面外凸，弧形段Ⅱ和平直段与带钢接触，弧形段Ⅰ的一端水平向外延伸，弧形段Ⅰ的另一端与弧形段Ⅱ的一端相切，弧形段Ⅱ的另一端与平直段相切，本实用新型的有益效果是，该工作辊整体结构简单，轧制效率高，降低了辊耗，消除了工作辊边部的急剧弹性压扁、弹性变形，降低了轧制断带的风险，可有效控制钢带边部的边降和形状。