硅钢资料

本实用新型公开了一种无取向硅钢厚涂层涂层液生产用纯水制水机，包括底板，底板顶端的两侧分别固定设有固定座和存水筒，固定座顶端的中部设有蒸馏组件，蒸馏组件包括球形釜，球形釜设置在固定座的顶部，球形釜的外部固定套设有导热层，导热层的内部固定嵌设有电热丝，导热层的外部固定套设有隔热层，本实用新型的有益效果是：通过设置的电热丝通过导热层对球形釜内部的水进行加热，球形釜提供更加均匀的受热效果，水蒸气通过V形管进入L形管，通过设置的环状冷却管内部的液氮对水蒸气进行冷却，便于提供更高效的蒸馏处理，通过设置的防腐蚀磁铁网格滤板、无纺布滤层、活性炭滤层和高密度滤网层，便于提供更好的过滤效果。

通过热力学计算,分析了实验钢中主要析出物析出的可能性。结果表明:在液相和固液两相区中,AlN和MnS均不能析出;在奥氏体区,AlN和MnS具备热力学析出条件,平衡析出温度分别为1547、1582 K。成品退火板中的析出物主要为AlN和MnS。扫描电镜下观察到的AlN形貌多为长条状,MnS形貌多为棒状或近似球形。这两种析出物占了析出物总量的85%以上,尺寸集中分布在400~800nm;复合析出物主要是(Al2O3+MnS)和(AlN+MnS),形貌不规则,尺寸集中在0.7~1.5μm;透射电镜下观察到了少量100nm以下独立的AlN析出。 According to thermodynamic calculation, the precipitation probability of precipitates was analyzed, AlN and MnS can not precipitate in liquid phase area and solid-liquid two-phase area. In austenite area, both the AlN and MnS have precipitation condition in thermodynamics and precipitates at 1547 K and 1582 K, respectively. The precipitates in annealing plate are mainly AlN and MnS. The shape of AlN is mostly strip, and MnS is stick or near sphericity. They accounted for over 85% of the total qu... 

提供一种可以制造具有优异特性的变压器的、兼顾低铁损和良好的磁致伸缩特性的方向性电磁钢板。本发明的方向性电磁钢板具有在与轧制方向交叉的方向上线状延伸的线状应变区域，线状应变区域具有在轧制方向上具有压缩应力的区域，在与该具有压缩应力的区域的轧制方向邻接的区域具有在轧制方向上具有拉伸应力的区域。

本发明涉及一种含磷高磁感无取向硅钢的生产方法，工艺路线：铁水脱硫－转炉冶炼－RH精炼－连铸－热轧－酸洗－冷轧－连续炉退火－涂层－性能检验－包装，具体步骤包括：1)将钢水冶炼至目标成分后采用连铸方式将钢水铸成坯；2)热轧板坯加热炉均热段板坯温度950～1050℃，终轧温度控制在780～830℃，卷取温度600～680℃；3)酸洗后冷轧，控制冷轧整体压下率80％以上，至成品厚度，增加剪切带组织；4)连续退火炉快速加热段温度设定1000～1150℃，增加有利织构组织形核；均热段温度设定750～830℃，全氮气干气氛保护，退火工艺速度110～150m/min，满足晶粒度8～4级。本发明在减少硅、铝、锰合金添加量的情况下，改善铁损提高磁感性能，提高机械性能。

本发明涉及磁悬浮电机轴硅钢片叠压领域，尤其涉及一种永磁电机内嵌式硅钢片的叠压装置、叠压工装及方法和磁悬浮鼓风机。该装置包括带槽钢板和多个长钢板；带槽钢板设置有转轴孔，转轴孔面积大于电机转轴套合硅钢片部分的截面积并且被电机转轴穿过；多个长钢板底端分别与带槽钢板相连接，并且带槽钢板上表面与硅钢片相贴合；多个长钢板竖直分布并且其分布位置与硅钢片中的多个磁钢槽相对应，长钢板外表面与硅钢片中的磁钢槽相配合。该装置通过对硅钢片的磁钢槽进行定位，保证叠压后的硅钢片的磁钢槽对齐，提高硅钢片内嵌磁钢质量。

本实用新型公开了一种铁芯硅钢片卷材的自动放卷上料装置，包括放卷机、导向平台和防折组件，所述导向平台间距设置在放卷机的下方，所述导向平台与放卷机之间构成供料带缓冲的缓冲空间，所述料带在缓冲空间内呈U型状走向，所述导向平台的上方间距设置有防折组件，所述防折组件与导向平台之间构成供所述料带通过的导向通道，所述防折组件设置在料带的内弯侧。通过防折组件对料带的内弯侧进行支撑，能够有效的防止料带被过度弯折，能够对料带进行缓冲和缓冲保护，保证料带放卷上料的稳定性。

轧制力是影响冷轧带钢厚度精度的关键因素。为实现高精度的冷轧带钢厚度控制,通过优化变形抗力模型参数和摩擦系数模型参数提高冷轧轧制力模型计算精度,并使用指数平滑法的自学习算法保证轧制力精度的稳定性。在首钢股份公司迁安钢铁公司20辊森基米尔轧机生产线进行S12硅钢钢种轧制力优化试验,将优化的模型参数应用于L2并投入现场生产,结果表明该优化方法不仅提高了轧制力设定精度,而且减小了冷轧硅钢的厚度超差长度,提高了成材率。 The rolling force is the key factor which influences the accuracy of cold-rolling strip thickness. To implement high precision control of cold-rolling strip thickness,we optimize the deformation resistance model parameters and friction coefficient model parameters to improve the calculation precision of cold-rolling force model,and use exponential smoothing self-learn algorithm to ensure the stability of rolling force accuracy. In Shougang Qiangang 20-high Sendzimir mill single stand production ... 

采用双辊薄带连铸工艺试制了2.6 mm厚5.28%Si-1.11%Al高硅钢薄带,对比了1050℃×5 min正火及不正火铸带280℃冷轧至0.5 mm后,再经900～1100℃退火的磁性能。结果表明,高硅钢铸带显微组织为等轴晶组织,正火后铸带边部晶粒长大,中心层晶粒变化较小。成品中析出物主要为较粗大的AlN和AlN+MnS复合析出物,尺寸为0.5～2.5μm。与不正火试样相比,正火试样成品铁损大幅降低,磁感小幅下降;随退火温度的升高,两种工艺下铁损和磁感都是先降低后升高,在1050℃出现最低值。 2.6 mm thickness 5.28% Si-1.11% Al non-oriented high silicon steel was produced by twin roll thin strip casting.Magnetic property of the strip un-normalized and normalized at 1050 ℃×5 min was contrasted after cold rolled to 0.5 mm at 280 ℃ and 900-1100 ℃ final annealing.The results show that microstructure of the strip is equiaxed crystal.The surface grain is coarsened and the center layer grain has little change of the normalized strip.The main precipitates are AlN and MnS+AlN with 0.5-2.5 μm s... 

通过固溶度积公式计算及热模拟实验,对不同热装和加热温度条件下的无取向硅钢铸坯中析出相进行了研究.在低于950℃热装时,铸坯中AlN的析出量和尺寸不再变化,但MnS和AlN-MnS的数量及平均尺寸随着热装温度降低而进一步增加,并在温度低于600℃时达到最大值后保持不变.与1200℃相比,1100℃加热的铸坯中AlN、MnS的总固溶量相对更少.相比850℃热装,600℃热装再加热到1100℃的铸坯中AlN和MnS的总固溶量更少,且AlN和MnS尺寸更大.合适的热装温度和加热温度分别为600℃和1100℃. Based on solubility product calculation and thermal simulation experiments,precipitated phases in continuous casting slabs of non-oriented silicon steel were systematically studied at different hot charging and heating temperatures.When the hot charging temperature is below 950 ℃,the content and size of AlN remain unchanged,but the quantity and size of MnS and AlN-MnS increase when the hot charging temperature decreases,reach maximum and remain unchanged when the hot charging temperature is belo... 

本实用新型涉及烟气收集净化技术领域，尤其是一种用于取向硅钢激光刻痕设备的烟尘收集装置。其包括集尘罩，所述集尘罩左右两侧对称设置第一集尘仓和第二集尘仓，第一集尘仓和第二集尘仓沿着集尘罩长度方向分布设置；所述第一集尘仓内侧和集尘罩内腔连通，第一集尘仓外侧分别设置多个进气口，所述第二集尘仓内侧和集尘罩内腔连通，第二集尘仓外侧分别设置多个出气口；所述集尘罩左右两侧分别设置第一分流器和第二分流器，第一分流器一侧并排设置多个第一分流器出气口。本实用新型通过设置在第一分流器进风口的鼓风机主动送风，与吸风口吸尘设备配合，在密闭集尘罩内形成顺畅且稳定的、方向固定的风流，将烟尘带走。

本实用新型提供一种定子铁心硅钢片固定结构，包括硅钢片堆叠结构、扣片，所述硅钢片堆叠结构由多个硅钢片层层堆叠而成，所述硅钢片沿边缘处设有多个凹槽，多个硅钢片堆叠后，其凹槽形成一条条通槽，所述扣片扣在通槽上，其扣片的两端设有弯折面将硅钢片堆叠结构的两端卡住，利用扣片的方式进行硅钢片固定，减少硅钢片导通现象，达到减少涡流损失的目的，扣片有极易更换的方便性，可轻易改变硅钢叠片的厚度，只需要更换扣片长度即可。

本发明公开了一种硅钢片组扣件自动压平装置，包括：定位单元，定位单元包括转盘、校位板和第一驱动组件，第一驱动组件连接并驱动校位板沿竖直方向运动，校位板滑动连接有第一校位柱，第一校位柱相对转盘偏心布置；第一推送单元，位于转盘的一侧，第一推送单元包括第一推送气缸和第一推块，第一推送气缸连接并驱动第一推块沿水平方向运动；冲压单元，位于转盘背离第一推送气缸的一侧，冲压单元包括第二驱动组件和冲压柱，第二驱动组件连接并驱动冲压柱沿竖直方向运动。转盘、校位柱和第一驱动组件配合，周向定位硅钢片组，再通过冲压柱将凸出于硅钢片组的扣件压平，完成硅钢片组的整形，整体更为美观，方便后续的装配使用。