硅钢资料

采用RH精炼添加钙合金方式对硅钢进行钙处理。结果表明,钙合金添加量为0.67、1.00、1.67kg/t钢时,钢中钙含量分别为0、2×10-6、4×10-6;随着钙合金添加量增大,钢中夹杂物粒度逐渐由0～2μm向2～4、4～6μm偏移;不同钙处理条件下,钢中均存在粒径小于1μm和粒径为1～5μm的MnS、CuxS夹杂物,后者或单独存在,或同AlN、CaS夹杂复合;粒径为5～10μm区间,钢中的夹杂物基本以钙的氧、硫化物为主。与钙处理前相比,钙合金添加量为0.67、1.00、1.67kg/t钢时,粒径小于1.0μm的微细夹杂物减少幅度分别为68.06%、87.50%、94.94%。钙合金添加量为1.67kg/t钢时,可以去除钢中绝大部分的微细夹杂物。 Ca alloy was added into the liquid steel during RH refining,and the results show that Ca concentration in final Si steel sheets is insignificant,about 0,2×10-6 and 4×10-6 when the added amount of Ca is 0.67,1.00 and 1.67 kg/t steel,respectively.With the increase in the added Ca alloy amount,the inclusions in the steel gradually change from those of 0～2 μm to those of 2～4 and 4～6 μm.Under different Ca treatments,there exist MnS and CuxS inclusions whose size is below 1 μm as well as MnS and CuxS ... 

电工钢试样加工产生的剪切应力会恶化钢板的磁性,对不同牌号硅钢片的横向、纵向试样退火前后磁性能的变化进行研究,结果表明:无取向硅钢片在剪切过程中横向、纵向的磁性受到剪切应力影响是不一样的。 The electrical steel sample processing magnetic of electrical steel will worsen due to the shear stress of sample. In this paper,the magnetic change of transverse,longitudinal specimens of different type of silicon steel sheet before and after annealing are studied. The results show that the magnetic of non- oriented silicon steel sheet affected in the process of shear is not the same in horizontal and vertical direction. 

本实用新型公开了硅钢片铁芯叠片机构，包括送料装置和叠片装置，送料装置包括有磁性传送带、送料件和第一定位杆，磁性传送带用于将已剪切的硅钢片传送至送料件，送料件安装于磁性传送带的下方，并且可沿磁性传送带的正交方向平行伸出，第一定位杆安装于送料件上，用于定位硅钢片，叠片装置设置于送料件的伸出的一方，包括有叠放台、第二定位杆和机械手，叠放台用于叠放硅钢片，第二定位杆用于定位硅钢片，机械手用于将送料件的硅钢片搬运至叠放台上，机械手包括有转动臂和取料单元，取料单元安装于转动臂的端部，包括有电永磁铁，电永磁铁用于吸取硅钢片。根据本实用新型的硅钢片铁芯叠片机构，可有效提高叠片速度，降低能耗，提高生产效率。

本发明涉及硅钢带的制备技术领域，具体公开一种软磁性高硅钢极薄带及其制备方法。所述软磁性高硅钢极薄带的制备方法包括熔炼、包覆CaF2和TiB2偶合涂层、微波热压成型、酸洗、渗氮、一次退火、三道热轧、二次退火、三次温轧和三次退火。本发明提供的软磁性高硅钢极薄带的制备方法制得的软磁性高硅钢极薄带的晶粒细化程度高、组织均匀，改变了传统的相析出路径，有效消除了有序相的形成，使其具有优异的延展性，并具备更高的磁感和更低的铁损。

本实用新型涉及硅钢片铁芯装配组件技术领域，公开了一种硅钢片铁芯的装配工装，包括装配组件，所述装配组件的内部上方安装有液压伸缩杆，所述液压伸缩杆的底端固定连接有压板，所述压板的表面开设有孔槽，所述装配组件的底端安装有铁芯，且铁芯的顶端贯穿孔槽的内部，所述铁芯的外部套设有硅钢片，所述硅钢片的外壁对称设有限位辊，所述装配组件的内壁对称安装有电动滑台，且电动滑台的内部设有滑块，本实用新型通过在液压伸缩杆的顶端安装有压板，并且压板的表面开设有与铁芯相匹配的孔槽，液压伸缩杆带动压板升降，对硅钢片进行压实，减少硅钢片之间的缝隙，使得硅钢片之间连接的更加紧凑，减少了工作人员的劳动量。

以能量平衡和辐射换热理论为基础,通过合理假定,建立了硅钢无氧化加热炉数学模型。采用数值计算的方法,通过自编程序,完成对带钢加热过程温度场的仿真。结果显示:数学模型能够反映带钢在无氧化炉内的加热过程,其升温曲线能够与工艺曲线相吻合;现行炉温分布并非最优,数学模型能够为炉温分布的优化、炉段的设计提供理论依据。 Mathematical model of NOF Section of Continuous Annealing Furnace is established based on energy balance and radiation heat exchange. The temperature field of steel is simulated by mathematical computation. The simulating results show that the mathematical model can reflect the heating process of silicon steel in NOF section, and the heat-up curve is coincide with the processing curve. From the results,it is known that the current furnace temperature gradient is not the best, and the mathematica... 

本发明是改善硅钢边缘裂边的工艺，包括：S1：对普通取向硅钢卷进行放卷、活套、清洗、加热、冷却；S2：对硅钢进行收卷，收卷张力系数为3‑9kg/mm2；S3：对硅钢卷用收紧带收紧打包，打包带张力为3‑8kg；S4：罩式炉进行炉底板检测，炉底板不平度＜2mm；S5：将收紧打包后的硅钢卷送入罩式炉内进行高温退火处理；本发明的优点：通过调整取向硅钢材料生产过程中对CA线收卷张力的控制、CA收紧带的使用与控制、罩式炉炉底板的平整度，实现1200mm以上宽度材料平均不良切边宽度≤45mm，边部裂边尺寸减少40％。有效提高了加工材料成材率，提高了纵剪材料使用率，降低了吨钢成本，减少了纵剪生产停顿，提高了效率。

采用硅钢自动测量装置及X射线衍射仪检测出样品在实验前后的磁性能参数和织构强度.结果表明:较低的电压、9 Hz、较长的处理时间以及退火温度为650℃有利于增高铁损降低比例;较低的电压、较高的频率以及退火温度为650℃有利于增加磁感应强度增高比例.最佳的提高磁性能的实验参数是:频率为9 Hz,电压为500 V,处理时间为6 min,退火温度为650℃.通过织构分析可以验证:取向硅钢磁感应强度的变化取决于{110}<001>晶粒取向度值,而{110}<001>取向度值可看成是一个反映总体平均偏离角大小情况的综合值. An automatic measurement system for silicon steel and an X-ray diffraction meter were used for measuring the magnetic property parameters and texture of ex-processed samples and processed samples.It is shown that under the condition of a lower voltage,9Hz,a longer processed time and an annealing temperature of 650℃,the decrease rate of iron loss can be increased;a lower voltage,a higher frequency and an annealing temperature of 650℃ are in favor of improving the increase rate of magnetic inducti... 

目前高磁感冷轧硅钢生产过程中，采用经验方法确定的乳化液流量设定值往往会造成硅钢产品的磁感性能达不到预期目标，针对此情况，基于轧机轧制机理研究了的乳化液流量数学模型，确定了乳化液流量设定值。实践表明，使用该数学模型输出的乳化液流量设定值，可提高轧制过程中乳化液流量控制精度，从而提高高磁感冷轧硅钢的轧制性能。 In view of the current production process of high magnetically inductive cold-rolled silicon steel, the mathematical model of emulsified fluid flow based on mill rolling mechanism is studied in view of the situation in which the magnetic sensing performance of silicon steel products is often not up to the expected target by using empirical method to determine the emulsified liquid flow setting. Practice shows that the emulsified fluid flow setting value output from this mathematical model improv... 

本实用新型公开了一种硅钢板带生产加工用除油烘干装置，包括壳体，所述壳体的外表面上对称设置有电机，所述电机的输出端固定连接有输送带，所述壳体的顶部设置有机体，所述机体的内部设置有除油机构，所述除油机构的一侧设置油烘干机构，所述壳体的底部设置油收集箱，所述收集箱的内部设置有收集槽。本实用新型，利用除油机构可对成硅钢板带生产后进行一定的除油处理，除油的效果更好更彻底，同时相比以往的方式提高了一定的工作效率，具有一定的实用性，利用烘干机构可进行除油后的成硅钢板带进行烘干处理，防止水渍残留在表面上，影响一定的美观效果，具有一定的实用性。

采用固溶强化、细晶强化和位错强化方法,模拟TSCR流程试开发高强度无取向电工钢,试开发钢的主要合金成分为3%Si、0.83%Al和2.99%Mn。分析热轧、常化、退火后的钢板组织,并针对不同的成品板组织,详尽地分析了相应的力学性能和磁性能。试验电工钢平均晶粒直径为12.37μm时,R p0.2为530 MPa,R m为618 MPa;当退火制度为700℃×4 min,成品组织完全为未再结晶的回复组织时,R p0.2为853.5 MPa,R m为895.5 MPa。该成分的电工钢P15/50或P10/400最小时,对应的平均晶粒直径都大于59.67μm;P10/800或P10/1000最小时,对应的平均晶粒直径都处于12.37~59.67μm尺寸区间。 TSCR was simulated to develop high-strength non-oriented electrical steel with 3% of Si,0.83% of Al and 2.99% of Mn by solution strengthening,grain refinement strengthening and dislocation strengthening.The microstructures of hot rolled plates,normalized plates and annealed plates were analyzed.Furthermore,the mechanical properties and magnetic properties of products with different microstructures were detailedly studied.As the average grain diameter of the steel was 12.37 μm,the yield strength ... 

为了解决在纹理背景下冷轧硅钢表面缺陷的分割问题,提出了基于局部信息结构张量和活动轮廓模型的硅钢表面缺陷分割方法。将图像的局部信息引入到结构张量中;在结构张量提取的特征空间中,以KL距离作为区域的概率密度相似性度量建立分割图像的活动轮廓模型;采用Split-Bregman数值解法对模型进行求解。运用提出的分割方法对硅钢表面的一些常见缺陷如纵向划伤、横向划伤、异物和孔洞等进行分割实验。实验结果表明,该方法可以准确地分割出硅钢表面缺陷区域,验证了该方法的有效性。 In order to address the segmentation problem for cold rolled silicon steel surface defect based on the texture background,a novel method based on structure tensor and active contour model is proposed.Image local information is introduced to the structure tensor.In the extracted feature space of structure tensor,KL distance is treated as a regional similarity measure of the probability density to establish active contour model for image segmentation.The numerical solution of Split-Bregman is used...