测试了高强无取向电工钢的S-N曲线,并借助光学显微镜、扫描电子显微镜、透射电子显微镜分析了实验钢组织,疲劳断口形貌和位错结构。结果表明:室温条件下,频率为20Hz,应力比R为0.1,循环10~7周次时,实验钢的疲劳强度为360MPa,疲劳裂纹萌生于实验钢的次表面,裂纹萌生点附近有沿晶开裂现象,疲劳裂纹扩展区域有解理台阶与疲劳条纹,瞬间断裂区是韧性断裂,有大量韧窝。实验钢在循环应力作用下基体中产生了大量位错,并有驻留滑移带终止在晶界位置。 The S-N curve of a high strength non-oriented electrical steel was tested.The microstructure and fatigue fracture morphology and dislocation were analyzed by optical microscope,scanning electron microscope,transmission electron microscope.The results showed that:at room temperature and the frequency of 20 Hz and the stress ratio Rof 0.1,the fatigue strength of the experimental steel was 360 MPa when the cycle was 10~7 cycles.The fatigue crack initiation at the surface of the steel and the interg... 

本发明公开了一种改善高牌号无取向硅钢表面色差缺陷的方法，属于冷轧卷板表面质量改进技术领域。所述方法为：将连铸坯依次进行热轧、常化、酸洗、单机架轧制和连续退火工序，其中按重量百分数计，所述的连铸坯含有如下成分：C＜0.003%、Si1.6~2.0%、Mn0.35~0.65%、Al0.35~0.65%、P＜0.02%、S＜0.0025%、余量为Fe和其他不可避免的杂质元素，所有成分合计100%；其中热轧工序的卷取温度为620~640℃。本发明所述方法能够降低带钢表面氧化铁厚度并改变带钢表面氧化铁结构，改善高牌号无取向硅钢表面色差缺陷。

针对攀钢高硫铁水冶炼现状,结合不同生产工艺路线,论述了攀钢近年来为实现低硫电工钢的生产,在铁水预处理、转炉冶炼、钢水精炼过程中硫控制技术的开发与应用,形成了低硫洁净钢生产工艺技术,实现了低硫电工钢的生产。低硫电工钢RH脱硫率可达到20%左右,成品[S]控制在0.006%左右。 According to the smelting situations of hot metal with high sulphur content at Panzhihua Steel,combined with different produce processes,technologies for controlling the sulfur content during hot metal pretreatment,converter smelting,and second refining are developed. Technologies in low-sulfur clean steelmaking are formed. Low-sulfur electric steel are produced. As for the desulfurization rate of lowsulfur electric steel can reach about 20%,and the content of [S] in products is controlled to ab... 

本实用新型涉及硅钢片加工领域，且公开了一种用于硅钢片钢卷制造的风冷装置，解决了目前市场上的用于硅钢片钢卷制造的风冷装置工作效率低下，风冷效果不佳的问题，其包括风冷箱，所述风冷箱两侧的下部分别开设有输入口和输出口，风冷箱的内部通过输入口和输出口活动连接有硅钢片本体，风冷箱内腔的顶部固定连接有制冷框，制冷框内腔的两侧之间安装有制冷环形管，制冷框内腔的顶部通过支架固定连接有吹风罩，风冷箱底部的两侧均安装有稳定架，该用于硅钢片钢卷制造的风冷装置，结构设计巧妙、降温迅速、操作便捷，通过制冷框与集风架进行对硅钢片本体进行双重风冷处理，大大提高了整个装置的风冷效果和工作效率，并且人工维护少、生产成本低。

适用范围 本标准规定了特高压变压器用冷轧取向电工钢带的术语和定义、分...

以轻烧氧化镁粉为原料,经消化、碳化制得重镁水,在热解反应前采用络合剂对重镁水中的杂质钙、铁进行络合掩蔽,再经热解得到碱式碳酸镁,碱式碳酸镁经煅烧可制得钙、铁杂质含量较低的氧化镁。在重镁水络合除杂过程中,考察了络合剂三乙醇胺、柠檬酸、草酸单独和复合使用的除铁、除钙效果。以三乙醇胺为络合剂时,在200 mL重镁水中加10 mL三乙醇胺(1∶1),氧化镁产品中w(氧化镁)=99.3%、w(氧化钙)=0.31%、w(氧化铁)=0.042%;使用草酸和柠檬酸作为复合络合剂时,在200 mL重镁水中加入1.0 g柠檬酸和2.0 g草酸,氧化镁产品中w(氧化镁)=98.2%、w(氧化钙)=0.24%、w(氧化铁)=0.030%。 Light-burned magnesia as a raw material was hydrated and carbonated to obtain magnesium bicarbonate liquor.Before the pyrolyzing of magnesium bicarbonate liquor,complexants were used to cover Fe and Ca impurities.Then the treated liquid was pyrolyzed to obtain basic magnesium carbonate which was calcined to magnesium oxide with low calcium and iron content.During the complexing purification of magnesium bicarbonate liquor,the Fe and Ca removing effects of single or compound complexing agents,suc... 

本发明特别涉及一种中频用取向硅钢极薄带及其钢基板的制备方法，属于硅钢极薄带制备技术领域，方法包括：将硅钢原料进行冷轧，获得硅钢薄带；将硅钢薄带进行退火，退火采用至少3段式连续退火工艺，获得钢基板；采用本法制得的钢基板制备的中频用取向硅钢极薄带具备优良的磁性能和板形，采用多段式退火，获得稳定的成品性能，制造工艺简单，可实施性高，采用无底层取向硅钢作为母材，节能环保，产品表面质量好，产品可满足中频条件下(≧400Hz)的使用要求。

分析了高转矩和高转速条件下高效驱动马达铁芯材料对无取向硅钢磁性能要求,讨论了无取向硅钢的高磁通密度和低铁损对电机转矩和效率的影响,介绍了国内外高磁感无取向硅钢发展情况。在生产工艺上,提高钢质纯净度,弱化夹杂物和第二相粒子对畴壁移动和再结晶晶粒长大的钉扎作用,添加微量晶界和带钢表面的偏析元素促使有利织构发展等技术可提高无取向硅钢的磁通密度。 The requirements of high efficient drive motor core materials under the conditions of high torque and high speed were analyzed.The effects of high magnetic flux density of non-oriented silicon steel on the torque and efficiency of the motor were discussed.The development of non-oriented silicon steel with high magnetic was introduced.The magnetic flux density of non-oriented silicon steel sheet can be obviously improved by some production technologies,such as purification steel,weakening the pin... 

采用光学显微镜、X射线衍射仪等分析了宁波钢铁有限公司生产的取向硅钢不同工序下的组织及织构演变规律。结果表明:铸坯经过热轧后,沿着厚度方向组织不均匀;一次冷轧并经脱碳退火后,组织由条状纤维状变成等轴状的初次再结晶晶粒,初次再结晶平均晶粒尺寸为18.17μm,织构主要以α织构和γ织构为主;在二次冷轧后,晶粒再次被压缩,转变为纤维状,织构主要为γ织构;经过高温退火后,发生二次再结晶,晶粒异常长大,晶粒尺寸达到厘米级,织构成分为单一且锋锐的Goss织构。 The microstructure and texture evolution of oriented silicon steel produced by Ningbo Iron and Steel Co.,Ltd.were analyzed by optical microscope and X-ray diffraction.The results showed that the microstructure of the slab was inhomogenous along the thickness direction after hot rolling.After first cold rolling and decarburizing annealing,the microstructure changed from strip fibrous to equiaxed primary recrystallized grains,and the average grain size of the primary recrystallization microstructu... 

本实用新型公开了超薄硅钢铁芯卷绕张力控制装置和纠偏装置，包括工作台、固定架和底座，工作台的顶部安装有固定架，所述工作台的底部设置有按压杆组件，所述按压杆组件的底部连接有底座，所述工作台顶部的前端和尾端均安装有固定板，所述固定板的内壁设置有收捆轴，所述工作台的顶部安装有滑轨板，且滑轨板位于固定板的内侧。本实用新型通过导向辊和衔接板的设置，工作人员在使用时，根据收捆轴上铁芯的缠绕位置，对两侧导向辊进行调节，从而通过导向辊的转动性对铁芯的活动起到定位作用，两侧导向辊的主要作用是起到带料输送出来时的导向作用，能够保证带料快速平稳的送料时不发生跑偏现象。

本实用新型公开了一种硅钢片用叠压装置，包括机架，机架上设有工作平台，工作平台的顶面上沿轴向并排设有定位块和可远离或者靠近定位块的抵紧块，定位块的水平截面呈L状，且其与定位块之间形成叠压区，叠压区的上方水平设有可竖直移动的传动板，传动板上竖向滑动穿设有若干均匀分布的导杆，导杆的两端均伸出传动板，且顶端设有限位块，底端共同安装有水平设置的压板，导杆上套设有位于压板和传动板之间的弹簧，机架上还设有与传动板和抵紧块均相连的可编程控制器。本实用新型解决了如何能高效且保质地对硅钢片进行叠压的技术问题，具有工人劳动强度低、叠压效率高且叠压质量好等优点。

本实用新型公开了一种用于硅钢片叠装的工装，包括安装底座，所述安装底座上设置有限位装置，所述限位装置包括多个水平限位柱和多个竖直限位柱；各个水平限位柱之间的缝隙的尺寸等于其对应放置的硅钢片的宽度，各个竖直限位柱与安装底座的底边之间的距离等于其对应放置的硅钢片的总长度；所述各个竖直限位柱设置在各个水平限位柱之间的缝隙所正对的位置；采用多个水平限位柱和多个竖直限位柱进行水平和竖直方向上均对硅钢片进行定位；使用此工装叠装出来的成品，长短一致，侧面相当整齐；本实用新型，结构简单，操作方便。