冷轧中中低牌号的无取向硅钢多采用万能凸度轧机(Universal crown mill,UCM)生产,其板形好坏受制于UCM轧机板形调节手段的协调使用。为掌握UCM轧机的板形控制特点,建立基于二维变厚度有限元的辊系弹性变形和基于三维差分的轧件塑性变形的六辊轧机耦合模型,对UCM轧机的板形调控性能进行详尽的分析,包括工作辊和中间辊弯辊、中间辊窜辊的调控功效、辊间接触压力分布等。在此基础上,提出可用指导生产的板形控制策略,指出UCM轧机在横向厚差控制方面的不足。针对工业生产中UCM轧机轧制无取向硅钢横向厚差大的问题,在大量仿真计算的基础上,开发具有高次曲线函数的边部变凸度(Edge variable crown,EVC)的工作辊。采用该工作辊后,各种品种的无取向硅钢的横向厚差不大于10μm的百分比由24%提高到99%,横向厚差的均值小于6μm,远小于之前的13μm。 Medium-low grade non-oriented silicon steel is rolled often by universal crown mill(UCM) during cold rolling.Its shape quality is dependent on the coordinated control of several shape adjustment devices of UCM.In order to understand the shape control characteristics of UCM,coupling model of six-high rolling mill,based on two-dimensional varying thickness finite element rolls elastic deformation model and three-dimensional finite difference strip plastic deformation model,is setup for the detaile... 

本发明提供一种改善表面麻点缺陷的薄规格中低牌号无取向硅钢及其生产方法，成分C≤0.0025％，1.2≤Si≤1.65％，0.25％≤Mn≤0.35％，0.06％≤P≤0.11％，0.1％≤Als≤0.2％，S≤0.0025％、N≤0.0025％，Ti≤0.0025％，其余为Fe及不可避免的杂质。与现有技术相比，本发明采用较低氢气浓度，防止炉内氧化铁皮还原，减轻碳套辊的腐蚀程度，减少碳套辊结瘤率，改善带钢表面质量；采用合理合金成分设计，提高带钢的力学强度，降低碳套辊结瘤对带钢表面的影响程度，改善带钢表面质量。产品厚度为0.35mm，板面麻点发生率降低，无手感，且辊身周长周期范围内麻点个数≤5个。

【作者】 吴清； ...

本实用新型公开了一种具有防护功能的变压器硅钢剪床，所述辅助机构包括沿着剪切机构前后对称设置的固定架，所述固定架的底部与床台的顶部固定连接，所述固定架上螺纹连接有调节螺杆，所述调节螺杆的底端转动连接有横架，所述横架的底部开设有凹槽，所述凹槽的内部固定连接有固定杆，所述固定杆的外表面固定连接有固定柱，本实用新型涉及剪床技术领域。该具有防护功能的变压器硅钢剪床，通过在固定架、调节螺杆、横架、凹槽、固定杆、固定柱和横杆的配合使用下，对板材进行扶持，降低安全隐患，解决了现有的剪床没有对板材进行扶持的措施，板材掉落不仅会对板材发生损坏，也有可能对工作人员带来伤害的问题。

本发明涉及一种取向硅钢连续高温罩式退火炉及其退火工艺，其包括梯度窑炉，所述梯度窑炉包括A1段退火炉、B段退火炉、C段退火炉、D1段退火炉、A2段退火炉和D2段退火炉；所述A1段退火炉、B段退火炉、C段退火炉、D1段退火炉、A2段退火炉和D2段退火炉依次连接；其中，A1段退火炉、B段退火炉、C段退火炉和D1段退火炉炉顶高度不同，A1段退火炉与A2段退火炉炉顶高度相同，D1段退火炉与D2段退火炉炉顶高度相同。上述在炉顶结构上根据生产工艺，采用的梯度分层次布局，使其在炉顶形成障碍，减缓气流的流通速度达到节能的目的，同时对各个工艺段炉窑内温度的均匀性有提升，并且能够提高产品的质量。

利用本钢技术中心试验厂技术手段,并与北京钢铁研究院合作,试制了用作家电用电机、微电机、小电机或部分中型电机铁芯的冷轧无取向电工钢。试制钢硅含量小于0.5%,钢板表面平滑,公称厚度0.5mm,且厚度均匀偏差小,性能测定结果表明,产品的磁性能、力学性能满足其使用要求。 BX STEELTechnology Center pilot plant using technical means,and with Beijing Iron and Steel Research Institute,trial cold rolled non-oriented electrical steel that has been used as appliance motor core,micro motor core,small motor core,or part of the medium-sized motor core。Trial steel of silicon content is less than 0.5%,steel plate surface is smooth,the nominal thickness of 0.5mm,and the thickness deviation is small,performance measurement results show that the magnetic properties,mechanical p... 

【摘要】 <正>2012年3月29日中国钢铁工业协会在上...

本发明公开了一种精确控制高磁感取向硅钢板坯Als含量的方法，转炉出钢20～40秒时，定量加入金属铝，加入量按0.15～0.35kg/吨钢；转炉出钢及合金加入后，底吹搅拌均匀3～5min后，加入一定量金属铝后再底吹搅拌均匀3～5min后将钢水吊运至RH开始精炼处理，铝加入量按[WAls目标+(0.009～0.0120％)]范围控制；钢水在RH精炼过程经过2～3次酸溶铝的成分微调后结束精炼，精炼结束Als按[WAls目标+(0.0030～0.0045％)]目标范围控制；RH精炼结束样酸溶铝检测结果出来后，在连铸开浇前，在钢包内补加铝线使钢液中Als在[WAls目标+Δ浇注Als损]目标范围内；连铸进行氩气环流保护浇注，其中氩气环流流量控制在6～12m3/h；浇注成合格板坯后按正常工艺进行热轧及后工序生产。

运用EBSD和光学显微镜,研究了0.25%~0.45%Cu对无取向电工钢热轧板显微组织,成品板显微组织、织构和磁性能的影响。实验结果表明:卷取过程中Cu元素在热轧板表层的偏聚作用显著阻碍了热轧板表层再结晶晶粒长大,导致热轧板表层晶粒尺寸随着Cu含量增加而逐渐较小,但热轧板中间晶粒尺寸变化不大。同时发现Cu元素能够明显改善织构类型,使有利织构组分增加,不利织构组分减少,同时减弱织构强度。从实验结果可知0.35%Cu能够显著改善电工钢的磁性能,铁损P15/50最低达到4.1 W/kg,磁感B50最高值达到1.8 T。 Effects of high content Cu on microstructure of hot rolled plates and microstructure,texture and magnetic properties of annealed finish product plates of non-oriented electrical steel were examined by means of EBSD technique and optical microscope. The results show that surface segregation of Cu significantly hindered recrystallized grain growth of surface layer in hot rolled plate during the coiling,as a result,the surface grain sizes of the hot-rohed plates decrease with the increase of Cu con... 

一种无取向性电磁钢板：以质量％计其母材的化学组成为：C：0.0010～0.0040％、Si：4.0～5.0％、Mn：0.20％以下、Al：0.010％以上且不足0.050％、P：0.030％以下、S：0.0030％以下、N：0.0005～0.0030％、O：0.0100～0.0400％、Ca：不足0.0010％、Ti：不足0.0050％、Nb：不足0.0050％、Zr：不足0.0050％、V：不足0.0050％、Cu：不足0.20％、Ni：不足0.50％、Sn：0～0.05％、Sb：0～0.05％、剩余部分：Fe和杂质；从母材表面到深度方向10μm的位置为止以外的区域中的O含量不足0.0050％。

本发明公开了一种控制无取向电工钢横向同板差的装置，包括热轧机、圆盘剪、冷轧机和输送辊道，圆盘剪安装在输送辊道两侧且位于热轧机和冷轧机之间，无取向电工钢在输送辊道的运输下依次经过热轧机、圆盘剪和冷轧机，设定热轧机对无取向电工钢的楔形和凸度进行控制，控制无取向电工钢的楔形在20微米内、凸度为20～45微米，冷轧机的工作辊设有倒角。冷轧机为UCM五连轧轧机，UCM五连轧轧机中1#和2#轧机工作辊的单边设有倒角，1#和2#轧机中上工作辊的操作端设有倒角，下工作辊的传动端设有倒角。倒角的深度为0.2～0.3mm，倒角在工作辊上的起始位置到工作辊端面的距离为265‑285mm。本发明还公开了一种控制无取向电工钢横向同板差的方法。

采用电解法和扫描电镜研究了300 t转炉-RH精炼钙处理对无取向硅钢板（%:≤0.005C、1.2～2.2Si、0.2～0.6Mn、≤0.20P、≤0.005S、0.2～0.6Al、0～0.01Ca）中夹杂物的影响。结果表明,钢中Al含量为0.25%和0.35%时,钢中溶解氧均小于1×10^-4%,钙处理后都会产生CaS夹杂物,尤其是含0.35%Al的钢水;钙处理可以有效减少钢中的夹杂物数量,尤其是0.5μm以下的微细夹杂物数量;钙处理后夹杂物的种类以AlN、CaS为主,同时还含有少量的氧化物夹杂物以及AlN-CaS复合夹杂物,尺寸主要为1.5～5.0μm。 The effect of 300 t converter-RH refining calcium treatment on inclusions in non-oriented silicon steel sheet （%:≤0.005C,1.2～2.2Si,0.2～0.6Mn,≤0.20P,≤0.005S,0.2～0.6A1,0～0.01Ca） has been studied by electrolysis and scanning electron microscope.Results show that with 0.25%and 0.35%Al content in steel,all the dissolved oxygen in liquid is less than 1×10^-4%,and the CaS inclusions are produced after calcium treatment,especial for the liquid containing 0.35%Al;the amount of inclusions in ste...