硅钢资料

阐述了国内外高磁感取向硅钢的生产研究水平与发展趋势,包括通过提高高斯晶粒取向度、细化磁畴、涂覆张力涂层、减薄钢片厚度进一步降低铁损以及低温加热技术和短流程技术新工艺。分析高磁感取向硅钢在我国大型电力变压器上的应用情况,结果表明,发展更薄规格高磁感、低铁损、低磁致伸缩取向硅钢可为大型变压器的安全性、节能性及环保性提供有效保障。 The research progress and development trend of high magnetic induction grain-oriented silicon steel at home and abroad are summarized,including the technology of improving the Goss alignment,refining domain wall,adding stress coating,decreasing thickness of sheet,and the new technique of reducing heating temperature of casting slab and shortening operational.Moreover,the application of high magnetic induction grain-oriented silicon in power transformer is presented.Developing grain-oriented sili... 

研究了硼酸对以Al(H2PO4)3为基料的无铬无取向硅钢绝缘涂层各项性能的影响。用盐雾实验、动电位极化及交流阻抗等试验手段研究了不同硼酸含量对硅钢绝缘涂层的耐蚀性和电化学行为的影响,同时采用SEM对涂层的表面形貌进行了研究。结果表明,硼酸含量为9.7%时,涂层的耐盐雾性及电化学性能最好;硼酸含量过少或过多时,涂层的耐蚀性和电化学性能都较差。 Influence of boric acid on the performance of chromium-free non-oriented silicon steel insulating coating based on aluminum dihydrogen phosphate was investigated.Salt spray experiment,potentiodynamic polarization and electrochemical impedance spectroscopy were used to study the influence of boric acid content on the corrosion resistance and electrochemical behavior of the insulation coating of silicon steel.Surface morphologies of the coatings were tested by SEM.Result shows that when the boric ... 

为了确定普通冷轧取向硅钢最优的中间完全脱碳退火工艺,在其一次冷轧后进行5种不同工艺的脱碳退火处理,借助扫描电镜及电子背散射衍射技术研究了不同工艺脱碳退火后的组织、织构和脱碳效果。结果表明:经5种工艺脱碳退火处理后,初次再结晶的平均晶粒尺寸均约为19μm,且不随退火温度和时间的变化而变化;经840℃×10min工艺退火后的晶粒最均匀,高斯织构位向更准确,高斯织构面积分数最多,为3.1%,可将碳脱至0.003 5%。 In order to determine the optimal intermediate complete decarburizing annealing processes for common grain-oriented(CGO)silicon steel,five kinds of intermediate decarburizing annealing processes were conducted,the microstructure,texture and decarbonization after different decarburizing annealing processes were studied by scanning electron microscopy and electro back-scattered diffraction(EBSD)technology.The results show that the average grains sizes of primary recrystallization were about 19μm a... 

提供能够稳定地制造磁特性优异且钢卷长度方向的铁损的偏差少的取向性电磁钢板的取向性电磁钢板的制造方法。本发明是一种取向性电磁钢板的制造方法，包括如下工序：对钢坯进行热轧，根据情况实施退火，然后通过1次冷轧或夹有中间退火的2次以上的冷轧来制成具有最终板厚的冷轧板，接着对上述具有最终板厚的冷轧板进行脱碳退火，然后实施二次再结晶退火；在最终的冷轧之前，将钢板以100℃/s以上的升温速度加热到100℃～350℃的加热温度，上述钢板从达到加热温度到进入最终的冷轧的第1道次的时间为5秒以内。

本实用新型提供一种硅钢片模具产品的吸料装置，包括固定架、电动伸缩杆、微型吸气泵、操作台、吸气机构以及放置机构，所述固定架上表面设有电动伸缩杆，所述固定架上表面设有微型吸气泵，所述微型吸气泵右端面设有吸气口，所述吸气口右端设有气管，所述电动伸缩杆底部设有吸气机构，所述吸气机构底部设有操作台，所述操作台上表面设有固定柱，所述固定柱前表面设有放置机构，与现有技术相比，本实用新型具有如下的有益效果：通过设置的橡胶套，代替手进行硅钢片的取料，通过设置固定杆，实现橡胶套的自动放料，更安全，通过设置的放置机构，实现硅钢片倾斜放置，方便进行硅钢片的拿取进行变压器装配。

对硅钢板材分别进行异步和同步轧制,研究了轧制参数包括速比、压下量和道次对板材表面显微组织的演变的作用.结果表明,异步轧制硅钢板材表面形成了晶粒尺寸为10~50 nm,取向接近随机分布的纳米晶,而同步轧制板材的表面只形成了位错胞,证明异步轧制可以诱发表面纳米化.异步轧制板材表面纳米晶的形成过程为:在剪切力的反复作用下,高密度位错形成、滑移、湮灭和重组形成亚微米尺度的亚微晶/位错胞.随着压下量和轧制道次增加,高密度位错重复以上过程使晶粒尺寸减小、取向差增大,最终形成取向接近随机分布的纳米晶组织.大压下量和多道次是异步轧制诱发板材表面纳米化的关键,而速比的增加可以加快纳米化进程. Surface nanocrystallization(SNC) can effectively enhance the surface and global properties of the metallic materials,such as microhardness,intensity,fatigue,wear and corrosion resistances,therefore provides more promising practical industrial applicability.Up to now,several SNC treatment methods were developed based either on the principles of ball impactions or friction sliding,however,difficulty still exists for the surface treatment of large-dimensional samples with high efficiency.Recently,m... 

为满足用户对无取向电工钢中硫含量的要求,采用CaO-CaF2复合渣系为脱硫剂,利用RH投入法对无取向电工钢进行深脱硫试验。试验结果表明,RH精炼渣成分控制在w CaO43%~51%、w Al2O325%~31%、w MgO4%~6%、w SiO29%~12%、w(FeO+MnO)3%~6%,在脱硫剂加入量为6~8 kg/t时,钢中平均硫含量从32×10-6降低到18×10-6,RH平均脱硫率为43.3%,最高达47.1%。利用KTH模型计算精炼终渣平均硫容量为0.003 1,RH精炼结束时渣-钢间实际平均硫分配比从14增加到52。 In order to satisfy the requirements of consumers on sulfur content in non-oriented electrical steel,taking( CaO-CaF 2) based flux as desulfurizer,industrial experiments on deep desulphurization of non-oriented electrical steel were carried out during RH process. The results show that as the compositions of refining slag are appropriately controlled with w CaO of 43% ~ 51%,w Al2O3 of 25% ~ 31%,w MgO of 4% ~ 6%,w SiO2 of 9% ~ 12%,and w( FeO + MnO) of 3% ~ 6%,and the desulfurizer added are at 6 ~ ... 

一种生产取向硅钢的氧化镁涂层烘烤质量控制方法，通过对带钢的实时温度测量建立对烘烤输出功率的实时反馈调节，据此形成基于烘烤输出功率的烘烤质量的实时控制。本发明的一种生产取向硅钢的氧化镁涂层烘烤质量控制方法，通过在烘烤炉出口的带钢上方增加一套可在带钢横向方向移动的在线板温计，基于在线板温检测值对烘烤炉状态进行监控，并建立烘烤输出功率控制系统实时调整，使得氧化镁涂层烘烤质量均匀，提高取向硅钢产品质量稳定性，节省能源消耗。

本实用新型涉及硅钢技术领域，尤其为一种用于硅钢绝缘涂料生产用储存装置，包括储存装置、顶盖和定位板，所述储存装置与顶盖铰链连接，所述顶盖内侧后端固定连接有定位块，所述定位块前端转动连接有连接块，所述连接块的另一端内侧转动连接有转动杆，通过设置的定位块、连接块、转动块、转动杆、推杆、档杆、挡块、弹簧、固定板和垫片，在使用时，盖上顶盖后，通过推动推杆，使推杆通过转动块带动转动杆在连接块内转动，推杆推动挡块，使挡块通过档杆挤压弹簧，从而对推杆进行限位，然后带动连接块在定位块上转动，从而使连接块挤压固定板，使固定板带动垫片，使垫片与储存装置贴合更紧，防止漏气，防止空气进去，防止涂料干燥。

选用国内外无取向硅钢标杆企业A、B、C的产品,采用非水溶液电解提取+SEM(EDS)方法,分析了其典型牌号对应成品试样中的夹杂物。结果表明,从磁性能控制角度而言,受钢的化学成分及生产工艺影响,A、B、C企业成品试样的夹杂物尺寸、种类、数量存在差异,这些差异对其磁性能产生显著影响;从夹杂物控制角度而言,A、B、C企业对应成品试样的夹杂物,以MnS、CuxS复合或者AlN、MnS、CuxS复合为主,其中1.0μm以下的夹杂物数量分别为2.34×107个/mm3、2.98×107个/mm3和11.98×107个/mm3,1.0μm以上夹杂物数量均很少,夹杂物的平均尺寸从大到小依次为A企业、B企业、C企业。 According to the production of three benchmarking manufacture enterprises A,B and C of non-oriented silicon steel at home and abroad,the inclusions in finished steel samples with typical grades were investigated by electrolytic extraction from non-aqueous solution and SEM(EDS).Results show that,from the viewpoint of improving the magnetic properties,affected by chemical composition and production technique,the size,type and amount of inclusions in finished steel samples are various,which will af... 

本实用新型公开了一种用于硅钢片叠装的工装，包括安装底座，所述安装底座上设置有限位装置，所述限位装置包括多个水平限位柱和多个竖直限位柱；各个水平限位柱之间的缝隙的尺寸等于其对应放置的硅钢片的宽度，各个竖直限位柱与安装底座的底边之间的距离等于其对应放置的硅钢片的总长度；所述各个竖直限位柱设置在各个水平限位柱之间的缝隙所正对的位置；采用多个水平限位柱和多个竖直限位柱进行水平和竖直方向上均对硅钢片进行定位；使用此工装叠装出来的成品，长短一致，侧面相当整齐；本实用新型，结构简单，操作方便。

本实用新型涉及一种三角硅钢片检测吸附装置，包括：成品硅钢片传送机构，成品硅钢片传送机构的上方依次设置有初检相机、吸附捕捉装置和废料盒。初检相机用于检测成品硅钢片上是否粘附有三角硅钢片，吸附捕捉装置用于将成品硅钢片上粘附的三角硅钢片吸附捕捉，废料盒用于集中存放吸附的三角硅钢片。初检相机和吸附捕捉装置分别与控制系统连接，控制系统用于通过初检相机拍摄的图像识别成品硅钢片上是否粘附有三角硅钢片。本实用新型通过初检相机实现三角硅钢片的精准识别，通过吸附装置将粘附在成品硅钢片上的三角硅钢片吸附捕捉，通过废料盒使得三角硅钢片的集中存储和清理更加便捷，通过本装置节省了人力、并且比人工操作更加精准。