借助电子背散射衍射(EBSD)及ZEISS-200MAT金相显微镜对某钢厂普通取向硅钢(CGO)进行研究,研究结果表明:热轧板组织、织构沿板厚方向存在明显的不均匀性,在热轧板表层及次表层发生再结晶,同时存在强度较高的Goss织构,中心层存在较强的{001}<110>变形织构。冷轧组织均呈纤维状条带组织,一次冷轧后,热轧板中的Goss织构消失,织构主要为α、γ织构,经中间脱碳退火后,α、γ织构强度减弱,并出现一定强度的Goss织构和利于Goss织构发展的{554}<225>、{332}<113>等织构,经二次冷轧后,二次冷轧织构类型与一次冷轧织构一致,但织构强度不同。 The grain-oriented silicon steel produced by a steel factory was investigated by EBSD and ZEISS-200 MAT metallographic microscope.The results show that the textures and microstructures along thickness of hot rolled slab are inhomogeneous.The surface layer and the layer near that are recrystallized structure which has a high Goss texture,but there is deformation texture{001}<110>in the central layer.The structure after cold rolling is a structure like fiber strip.After the first cold rollin... 

对高磁感取向硅钢冷轧板分别进行800、950、1050和1120℃不脱碳的预退火处理,在800℃预退火,成品的磁性能较好。织构分析的结果表明,随着预退火温度升高,初次再结晶后有利织构组分{111}<112>与不利织构组分(118)[110]的比值f(111)/f(118)逐渐降低,初次再结晶织构的变化是成品磁性的影响因素之一。 Preliminary annealing process at different temperatures for cold-rolled strips of a high permeability grain-oriented silicon steel was investigated to study the effect of the annealing temperature on microstructure and magnetic performance of the steel.Results show that the magnetic performances of the products annealed at 800 ℃ are best.Analysis of primary recrystallization texture indicates that with rising temperature,f(111)/f(118) which is the ratio of the favorable component {111}<112>... 

分析了电感耦合等离子体发射光谱法(ICP-AES)测定硅钢中铌的检测过程,讨论了该检测过程中不确定度的主要来源,建立了该方法的定量的数学模型,并根据这一模型计算出了检测结果的合成标准不确定度和扩展不确定度。 The measurement of niobium content in silicon steel by inductively coupled plasma atomic emission spectrometry(ICP-AES) was analyzed,by which the main factors affecting the uncertainty of the measurement were ascertained and the calculation formula was given.Finally,according to the formula the combined uncertainty and expanded uncertainty were obtained. 

对两种硅钢水溶性极厚绝缘涂层进行了不同温度的热老化实验。通过TG-DTA,GDS,FT-IR,SEM和光泽度仪等测试方法对老化的涂层进行分析表征,提出了评估硅钢水溶性极厚绝缘涂层热老化性能的合理温度区间,探讨了涂层热老化行为,并分析了两种涂层热老化性能的差异。结果表明,涂层附着性随着老化时间的延长逐渐下降。FT-IR表征结果显示,热老化过程中,涂料交联形成的化学键未发生断裂,交联剂氨基树脂的三嗪环被破坏是聚合物三维网络结构坍塌的主要原因。 Thermal aging expriments at different temperature were carried out on two types of water-soluble and extra-thick insulation coatings for non-oriented silicon steel,and a series of test methods such as glossmeters,TG-DTA,FT-IR,GDS,SEM were applied in analysis.For evaluating the thermal aging effect of this kind of insulation coating,the proper temperature range was proposed.The difference of aging performance between two coatings was been investigated and the related behaviors were been discussed... 

本实用新型涉及硅钢片切割设备领域，具体涉及一种变压器铁芯硅钢板的剪切装置，包括操作台，操作台的顶部安装有传送辊，传送辊的侧部安装有限位装置，限位装置的侧部依次安装有送料装置和切割装置，切割装置包括固定座，固定座的顶部固定连接有底板，底板的两侧固定连接有导向柱，导向柱的顶部安装有顶板，导向柱上且位于顶板的下方滑动设置有刀架，刀架上安装有切割刀，顶板上安装有液压缸，液压缸的自由端的端部与刀架的顶部固定连接；解决现有的硅钢片切割效率低的问题。

采用双辊薄带连铸技术试制了3.98%Si-0.71%Al无取向硅钢铸带,研究了二次冷轧法对硅钢组织和磁性能的影响。结果表明:硅钢铸带显微组织为等轴晶组织,铸带再结晶较完全,常化对铸带显微组织影响较小。二次冷轧工艺和一次冷轧工艺下,最终退火后成品显微组织为等轴晶组织,二次冷轧法最终退火后的晶粒尺寸小于一次冷轧法。二次冷轧法能够提高成品磁性能. Effect of double cold rolling on magnetic properties and microstructure of 3.98%Si-0.71%Al non-oriented silicon Steel Sheets cast by twin-roll thin strip casting process were investigated.The results show that the structure of the thin strip is equiaxed crystal,the recrystallization is complete and normalizing has lesser effect on microstructure.Using both cold rolled and double cold rolled process,the microstructure is equiaxed grain after final annealing.The average grain size of annealed shee... 

本发明涉及一种高性能取向硅钢冷轧工艺，具体涉及取向硅钢制造技术领域。本发明的冷轧工艺包括一次冷轧和二次冷轧，其中，取向硅钢热轧板厚度在2.0～3.0mm，一次冷轧轧制采用4或5道次轧制，轧至厚度0.60～0.62mm，轧制温度为100℃～105℃；二次冷轧轧制采用2道次，轧至厚度0.24～0.26mm，轧制温度为95℃～100℃。本发明通过对一次冷轧和二次冷轧中各道次的压下率、轧制张力、轧制速度、轧制温度进行优化设计，从而能够进一步优化织构，确保二次冷轧板高斯织构含量在0.8～1.5％，且轧制稳定性高，进而有效保证了所得取向硅钢的磁性能。

本发明公开了一种可替代高磁感取向硅钢常化退火的热处理方法。该方法包括对所述取向硅钢的铸坯依次进行热轧、酸洗和冷轧，省去了常化酸洗工序中的常化退火工艺。所述热轧工序包括加热、粗轧和精轧过程，所述精轧过程中，热轧板离开精轧机最后一个机架时的温度达到1000～1050℃；或者，所述酸洗工序后，对热轧板进行通电加热至1000～1050℃；然后，对热轧板采用短时通电加热控制冷却速度，通电加热2‑5s使热轧板的温度降至940～960℃。采用该热处理方法得到高磁感取向硅钢常化板等效织构，满足生产高磁感取向硅钢的织构组分条件，其简化了高磁感取向硅钢的制造工艺，降低了生产成本和能耗，提高了生产效率。

本实用新型公开了一种取向硅钢绝缘涂液用深度过滤装置，涉及深度过滤装置技术领域，为解决现有深度过滤装置在工作过滤时，一般都是依靠液体本身流动的力量穿过滤网，但液体流速较慢，工作效率不高的问题。所述过滤装置主体的下端安装有出水管，所述过滤装置主体外表面的一侧安装有进水管，所述进水管与出水管的一端均安装有安装底座，且安装底座设置有两个，所述安装底座的一侧安装有六角固定螺母，且六角固定螺母设置有十二个，所述安装底座的另一侧安装有密封橡胶垫圈，且密封橡胶垫圈设置有两个，所述进水管的内部设置有进水口。

本发明提供了一种取向硅钢制作的电机凸极转子，包括由取向硅钢一体制作而成的凸极极身、轭部与极靴，整个转子的易磁方向为径向，通过对轭部厚度、相邻凸极根部中心点距离、凸极极身宽度和极靴尺寸等进行特殊结构设计，能够提高电机功率密度与效率，且无二次气隙与额外的工艺需求。

本发明提出了一种控制磁畴结构来降低铁损的取向性电磁钢板的制造方法中，即使在实施了去应力退火的情况下，也能够保持铁损降低效果，并且在磁畴控制处理后磁通密度不会降低的方法。本发明的制造方法中，在取向性电磁钢板的表面，沿与钢板的轧制方向交叉的方向线状地照射周边比中心低的环状的强度分布的激光。

本发明的一个实施方案提供一种取向电工钢板及其制造方法，以重量％计，所述取向电工钢板包含：Si：3.0‑4.5％、Mn：0.05‑0.2％、Al：0.015‑0.035％、C：0.0015％以下(0％除外)、N：0.0015％以下(0％除外)、S：0.0015％以下(0％除外)、余量的Fe及其它不可避免的杂质，并且满足以下关系式1和关系式2。[关系式1](W13/50/W17/50)≤0.57[关系式2](W15/50/W17/50)≤0.76(其中，所述关系式1中，Wx/y表示施加磁场的大小为x/10T且频率为yHz的条件下的铁损值)。