硅钢资料

本发明提供一种改善表面麻点缺陷的薄规格中低牌号无取向硅钢及其生产方法，成分C≤0.0025％，1.2≤Si≤1.65％，0.25％≤Mn≤0.35％，0.06％≤P≤0.11％，0.1％≤Als≤0.2％，S≤0.0025％、N≤0.0025％，Ti≤0.0025％，其余为Fe及不可避免的杂质。与现有技术相比，本发明采用较低氢气浓度，防止炉内氧化铁皮还原，减轻碳套辊的腐蚀程度，减少碳套辊结瘤率，改善带钢表面质量；采用合理合金成分设计，提高带钢的力学强度，降低碳套辊结瘤对带钢表面的影响程度，改善带钢表面质量。产品厚度为0.35mm，板面麻点发生率降低，无手感，且辊身周长周期范围内麻点个数≤5个。

通过对取向硅钢进行脉冲磁场退火实验,发现在相同的退火时间(6.0 min)内,低于1 T的脉冲磁场可以在一定程度上提高取向硅钢的磁感(B8),而高于1 T的脉冲磁场则会使取向硅钢的磁性能急剧恶化.同时发现,脉冲直流电加热方式会使取向硅钢的磁性能恶化.研究表明,脉冲磁场退火有望成为一种调控材料微观结构的有效手段. We have carried out experiments of annealing by pulse magnetic field.The results show that a pulse magnetic field with intensity lower than 1 T can promote magnetic induction density(B8) of grain-oriented silicon steel,while the magnetic properties deteriorate sharply when intensity is higher than 1 T.It has also been found that heating by using pulse direct current can cause the magnetic properties to deteriorate,in contrast to the traditional heating using resistance furnace.Our research shows... 

本发明公开了一种去除无取向硅钢夹杂物的方法，在中间包预设脉冲电流装置，将所述脉冲电流装置的正极连接在上挡渣堰处，负极连接在下导流坝处，在钢水浇注过程中，施加电脉冲处理即可。本发明基于中间包钢水流场的研究，在中间包上挡渣堰和下导流坝之间施加脉冲电场，扩大了脉冲电场作用的钢水区域，且随着钢水流场运动，流场与脉冲电场相互作用，使得细小的SiO2和MnS夹杂物在钢水运动过程中更有效的碰撞、聚集、长大，并有充足的时间充分上浮，从而达到有效去除铸坯夹杂物，降低铸坯中S和O含量，大幅提高钢水纯净度，进而提高硅钢成品磁性能。

本发明提供一种无取向硅钢低温无铬环保绝缘涂层立式干燥固化工艺，冷轧无取向硅钢在镀锌机组经过退火后，通过涂层机涂覆低温无铬环保绝缘涂层，再经过立式干燥炉完成干燥固化，生产冷轧无取向硅钢产品。低温无铬环保绝缘涂层厚度0.8~1.0μm；立式干燥炉各段炉温：加热一段炉温420~450℃，加热二段炉温460~490℃，加热三段炉温500~530℃，加热三段出口板温200~240℃，冷却段出口板温60~65℃；立式干燥炉各段加热时间：加热一段、加热二段、加热三段的加热时间均为3.5~4s。采用本发明工艺不仅能保证钢带涂层均匀，使最终产品的涂层具有优异的绝缘性、耐蚀性、附着性、冲片性、焊接性和耐热性，满足下游工序要求，还可提高产品合格率，减少废品，保证生产顺行。

本发明提供了一种超高磁感无取向硅钢及其制造方法和在汽车发电机生产中的应用，成分：C：≤0.005％、Si：0.5‑1.2％、Mn：0.1‑0.5％、P：0.01‑0.1％、S：≤0.004％、Al：≤0.005％、N：≤0.005％、Ti：≤0.003％，余量为铁和不可避免的杂质。通过成分设计，配合CSP薄板坯连铸连轧工艺、常化工艺，不用添加贵金属元素，不添加贵金属元素，流程短、成本低、磁感高、性能稳定；节省成本的同时，具有优良的磁性能，采用本发明生产的汽车发电机铁芯，与常规产品生产的铁芯相比，重量可减轻15％以上，缩小了发电机尺寸，满足汽车发电机小型化、高效化的要求。

Fe-6.5%Si高硅钢是一种具有高磁导率、低矫顽力和低铁损等优异软磁性能的合金,但是其室温脆性和低的热加工性能严重影响了其在工业领域的应用。综述了Fe-6.5%Si高硅钢的性能,评述了合金的改性法、特殊轧制法、快速凝固法、沉积扩散法、粉末冶金法等制备工艺。 It is well known that 6.5%Si high silicon steel is one kind of soft magnetic materials with higher re-lative permeability,lower coercive force and iron loss than those of conventional industrial silicon steel.However,their room-temperature embrittleness and poor workability limit their practical applications in the industry.The pre-paration technique such as modification treatment on alloy,special rolling,rapid solidification,CVD and powder me-tallurgy is reviewed. 

本发明涉及一种低耗高效硅钢常化酸洗工艺及酸洗设备，其有效利用常化炉出口余温作为加热带钢的介质，使带钢与低温的酸液接触表面发生强烈的物理化学反应，快速酸洗剥离表层粗大的氧化铁皮，降低酸洗系统的酸液温度，通过调控溶液氧化还原特性提高酸洗效率去除残留的铁橄榄石，节约了能耗，同时取消了高投资高运行成本的抛丸工艺，实现了低耗高效硅钢常化酸洗的目的。

采用硅钢自动测量装置及X射线衍射仪检测出样品在实验前后的磁性能参数和织构强度.结果表明:较低的电压、9 Hz、较长的处理时间以及退火温度为650℃有利于增高铁损降低比例;较低的电压、较高的频率以及退火温度为650℃有利于增加磁感应强度增高比例.最佳的提高磁性能的实验参数是:频率为9 Hz,电压为500 V,处理时间为6 min,退火温度为650℃.通过织构分析可以验证:取向硅钢磁感应强度的变化取决于{110}<001>晶粒取向度值,而{110}<001>取向度值可看成是一个反映总体平均偏离角大小情况的综合值. An automatic measurement system for silicon steel and an X-ray diffraction meter were used for measuring the magnetic property parameters and texture of ex-processed samples and processed samples.It is shown that under the condition of a lower voltage,9Hz,a longer processed time and an annealing temperature of 650℃,the decrease rate of iron loss can be increased;a lower voltage,a higher frequency and an annealing temperature of 650℃ are in favor of improving the increase rate of magnetic inducti... 

运用EBSD和光学显微镜,研究了0.25%~0.45%Cu对无取向电工钢热轧板显微组织,成品板显微组织、织构和磁性能的影响。实验结果表明:卷取过程中Cu元素在热轧板表层的偏聚作用显著阻碍了热轧板表层再结晶晶粒长大,导致热轧板表层晶粒尺寸随着Cu含量增加而逐渐较小,但热轧板中间晶粒尺寸变化不大。同时发现Cu元素能够明显改善织构类型,使有利织构组分增加,不利织构组分减少,同时减弱织构强度。从实验结果可知0.35%Cu能够显著改善电工钢的磁性能,铁损P15/50最低达到4.1 W/kg,磁感B50最高值达到1.8 T。 Effects of high content Cu on microstructure of hot rolled plates and microstructure,texture and magnetic properties of annealed finish product plates of non-oriented electrical steel were examined by means of EBSD technique and optical microscope. The results show that surface segregation of Cu significantly hindered recrystallized grain growth of surface layer in hot rolled plate during the coiling,as a result,the surface grain sizes of the hot-rohed plates decrease with the increase of Cu con... 

本实用新型涉及电机生产设备技术领域，特别涉及一种硅钢板冲裁余料处理工装，出料带通过支撑架平放在地面上，出料带的上方平行设置有安装在支撑架上的支撑砧板；支撑砧板的上方平行设置有上下滑动安装在支撑架上的刀架，刀架上设有切刀；支撑砧板的一端邻接有上料带，上料带将硅钢板冲裁余料送入到支撑砧板上。本实用新型的有益效果是：本实用新型可将成条的硅钢板冲裁余料进行自动裁切处理，裁切后的三角形的边角料会掉落到出料带中送出，此设备节省了大量的人力成本，提高了车间生产的安全性。

为进行磷酸盐系无铬无取向硅钢涂层烧结固化工艺研究,首先对磷酸盐系无铬无取向硅钢涂层进行热重-差示扫描量热(TG-DSC)分析;然后在不同烧结固化温度条件下,测定涂层板温随时间变化曲线;最终获得涂层烧结固化温度与时间(T-t)工艺曲线。通过中性盐雾试验、动电位极化、交流阻抗、涂层附着力以及扫描电子显微镜(SEM)和能谱(EDS)分析验证。结果表明,根据涂层烧结固化温度与时间(T-t)工艺曲线制备的涂层结构致密、性能优异,证明该工艺曲线具有合理性与正确性。 In order to study the curing process of chromium-free non-oriented silicon steel coatings,phosphatic chromium-free non-oriented silicon steel insulating coating was prepared and TG-DSC analysis of the coating was conducted,then the change of the actual temperature of the coated non-oriented silicon steel sheet with time at different curing temperatures was studied. Based on the experiments,the processing curves of curing temperature vs. curing time( T-t) for the chromium-free non-oriented silico... 

1.本外观设计产品的名称：硅钢片。;2.本外观设计产品的用途：多片硅钢片用来共同组成马达的转子的其中一个部件。;3.本外观设计产品的设计要点：在于本外观设计产品的形状。;4.最能表明设计要点的图片或照片：立体图。;