硅钢资料

基于简化的取向硅钢片模型,系统地对不同的交流激励下的硅钢叠片内铁损、交链磁通和空气中指定位置的法向漏磁的分布进行了\"单片级\"的测量,并建立了相应的硅钢叠片级问题的三维有限元分析模型,进行了大规模的数值计算分析。模型实验和数值分析的结果表明垂直进入硅钢片的漏磁通和损耗呈现浅透入的特点,在硅钢片内引起的涡流损耗在总铁损中占据了\"举足轻重\"的份额。用电磁场有限元分析软件MagNet瞬态场时步法计算结果与测量结果相吻合,说明本文方法研究复杂的硅钢叠片问题的有效性。 The measurement and 3D finite element analysis of the iron loss,interlinkage flux inside the laminated silicon steel sheets and the magnetic flux densities at the specified positions are carried out based on a verifying silicon steel sheet model.The modeling results show that the leakage flux vertically through the silicon steel sheets has the peculiarity of shin effect,and the eddy current loss caused by the AC leakage flux is a significant component of the total iron loss.The calculated result... 

依据GB/T 15616—2008《金属及合金的电子探针定量分析方法》,采用电子探针波谱仪对某W600硅钢中的硅含量进行了定量测定,对影响其定量测定结果的不确定度分量进行了分析,并对不确定度的各个分量进行了计算和合成,最后给出了硅钢中硅含量测定结果的不确定度报告:该硅钢中的硅含量(质量分数)为1.50%,扩展不确定度U=0.20%,取包含因子k=2。 According to GB/T 15616-2008\"Quantitative Method for Electron Prohe Microanalysis of Metals and Alloys\",the quantitative results of Si content in some W600 silicon steel was measured hy EPMA-WDS.The uncertainty components which might affect the measurement results were considered,calculated and synthesized. Finally the uncertainty result for the quantitative value of Si content in the silicon steel was got.The mass content of Si was 1.50%,and expanded uncertainty U=0.20%under the condition of co... 

取向硅钢利用析出物作为抑制剂,抑制初次再结晶晶粒的长大,抑制剂是取向硅钢发生二次再结晶的基本条件之一。文中通过低温板坯加热技术制备取向硅钢,采用透射电镜(TEM)观察并研究了高温退火阶段抑制剂的演化过程。结果表明,渗氮后形成的非晶态Si3N4析出物不稳定,在700～750℃退火升温阶段转化为(Al,Si)N;(Al,Si)N颗粒在800℃发生团聚,随后长大并粗化;(Al,Si)N是低温取向硅钢主要抑制剂,随退火温度的升高,(Al,Si)N抑制力大幅下降。 Precipitates as inhibitor are used to inhibit the grain growth of primary recrystallization in grain-oriented silicon steel,and inhibitor is one of the basic conditions for occurring of secondary recrystallization.The grain-oriented silicon steel was produced by low temperature slab heating and nitriding technique.The evolution of inhibitor was observed by transmission electron microscopy.The results show that Si3N4 particles are precipitated after nitriding,and Si3N4 particles are amorphous and... 

为进行磷酸盐系无铬无取向硅钢涂层烧结固化工艺研究,首先对磷酸盐系无铬无取向硅钢涂层进行热重-差示扫描量热(TG-DSC)分析;然后在不同烧结固化温度条件下,测定涂层板温随时间变化曲线;最终获得涂层烧结固化温度与时间(T-t)工艺曲线。通过中性盐雾试验、动电位极化、交流阻抗、涂层附着力以及扫描电子显微镜(SEM)和能谱(EDS)分析验证。结果表明,根据涂层烧结固化温度与时间(T-t)工艺曲线制备的涂层结构致密、性能优异,证明该工艺曲线具有合理性与正确性。 In order to study the curing process of chromium-free non-oriented silicon steel coatings,phosphatic chromium-free non-oriented silicon steel insulating coating was prepared and TG-DSC analysis of the coating was conducted,then the change of the actual temperature of the coated non-oriented silicon steel sheet with time at different curing temperatures was studied. Based on the experiments,the processing curves of curing temperature vs. curing time( T-t) for the chromium-free non-oriented silico... 

对冷轧无取向硅钢在冶炼过程中各个工序的顶渣进行了检测,分析了顶渣变化原因,并得出结论:硅钢生产宜采用复吹转炉,以降低吹炼终点渣中TFe含量,进而减轻对精炼的压力;使用低S、低Al2O3含量中间包覆盖剂;RH脱氧及合金化顺序采用先加硅铁后加铝;首罐宜经LF提温并降低渣中TFe。 The top-surface slag used for the various production processes in smelting coldrolled non-oriented electrical steel is tested and based on tested results the cause of the top surface slag change is analyzed.So it is concluded that the combined blown converter is more suitable to be used for smelting electrical steel in order to reduce the content of TFe in slag at blow end point and then much better results can be achieved during the period of refining.Secondly the tundish flux contenting low co... 

本发明公开了一种酸洗低牌号无取向硅钢的方法，从酸洗线前拉矫机的延伸率设定、酸液浓度、酸液温度、酸洗槽内液位的控制、酸液中铁离子的含量等方面入手，解决酸洗低牌号无取向硅钢的问题。

本实用新型公开了一种硅钢片组扣件自动压平装置，包括：定位单元，定位单元包括转盘、校位板和第一驱动组件，第一驱动组件连接并驱动校位板沿竖直方向运动，校位板滑动连接有第一校位柱，第一校位柱相对转盘偏心布置；第一推送单元，位于转盘的一侧，第一推送单元包括第一推送气缸和第一推块，第一推送气缸连接并驱动第一推块沿水平方向运动；冲压单元，位于转盘背离第一推送气缸的一侧，冲压单元包括第二驱动组件和冲压柱，第二驱动组件连接并驱动冲压柱沿竖直方向运动。转盘、校位柱和第一驱动组件配合，周向定位硅钢片组，再通过冲压柱将凸出于硅钢片组的扣件压平，完成硅钢片组的整形，整体更为美观，方便后续的装配使用。

本发明涉及卷取领域，具体涉及硅钢卷取机卷筒结构，包括机架、收卷辊和按压捆绑机构，按压捆绑机构位于收卷辊一侧，按压捆绑机构包括按压单元和捆绑单元，捆绑单元包括捆绑辊、转动辊、成卷的胶带和两个滑块，两个滑块均滑动设置于机架上，滑块的下端固定有能与机架相抵的下卡块，捆绑辊固定设置于两个滑块之间，捆绑辊上设有凹槽；按压单元包括两个按压部，每个按压部包括按压管和弹簧，按压管通过弹簧与凹槽的侧壁连接，转动辊设置于按压管内，成卷的胶带套设于转动辊上，凹槽的侧壁设有供胶带通过的通槽。采用本技术方案时，有利于避免成卷的硅钢卷松动且能对硅钢卷进行捆绑。

本文对某厂硅钢DR510温度、成分及过程控制水平和成品的组织、力学性能进行了研究,并在此基础上提出了工艺优化方案,有一定的借鉴和推广价值。 In this paper,the critical process and the products quality,including temperature,composition and process controlling level,the organization and mechanical properties of the finished product,were studied.On the basis of that the optimized technical plan provided,and this control technology is worth using and spreading. 

此无取向性电磁钢板具有预定的化学组成，所述化学组成满足(2×[Mn]+2.5×[Ni]+[Cu])－([Si]+2×[sol.Al]+4×[P])≧1.50％，以SEM－EBSD测定距表面1/2板厚深度的与轧制面平行的面时，将{hkl}＜uvw＞取向的晶粒相对于全部视野的面积率记为Ahkl－uvw时，A411－011在15.0％以上，且平均晶体粒径为50μm～150μm。

本发明涉及涂层液技术领域，且公开了取向硅钢绝缘涂层液，其配比为：二氧化硅10‑15%、硼酸5‑8%、磷酸二氢盐2‑5%、金属溶胶20‑25%、氢氧化铝占5‑6%、有机酸处理的复合盐溶液20‑30%、分散剂0.5‑1%，其余为水，采用硅溶胶作为辅助成膜物，粘结力较强，对附着性影响很大。硅溶胶能够很均匀地包裹在被胶结物质的表面，通过自干成膜，保持了很高的常温结合强度；而磷酸盐涂层的固化是通过受热分解，脱水聚合完成的，低温强度差，中温强度高，充分利用了硅溶胶低温的结合强度和磷酸盐中、高温时的结合性能，消除了常规涂层烘烤时容易出现的收缩、起泡现象，阻止了微气孔的形成，提高了涂层的表面光滑度，粘结强度和稳定性同时保持绝缘涂层的光泽、光滑和稳定性。

本发明公开了一种用于测量电工钢片的二维磁性能的系统及方法，所述系统通过将承载待测样品的托盘与旋转机构连接，在测量各个角度的二维磁性能时只需控制旋转机构驱动待测样品转动，旋转机构的负载很小，旋转机构的制作较为简单。而且，励磁测量线圈是绕制在托盘的外围，而不是在磁轭上，这样使得待测样品相当于处于一个均匀的螺线管中，磁场更加均匀，保证了磁场测量的准确性，并且励磁源不需要像RSST一样要保证两路励磁机构的相位差的准确度，从而使得励磁源的制作更加简单，降低了制作的成本和门槛。同时，不需要对待测样品打孔来绕制线圈，待测样品无破坏，可以保证待测样品的完整性以及数据的重复性和可对比性，测量结果更可靠。