【作者】 刘彤； ...

本发明公开了一种电力变压器硅钢片自动叠片生产设备，包括支撑板和叠片立板，其中一组所述支撑板的表面安装有叠片立板，另一组所述支撑板的顶部安装有检测立板；所述叠片立板的背面安装有连杆，所述连杆的尾端连接有限位环，所述限位环的内部等距贯穿安装有第一电动伸缩杆，所述第一电动伸缩杆的尾端表面套接有橡胶套，所述叠片立板的背面设有滑槽，所述滑槽的底壁安装有缓冲弹簧，所述滑槽的顶壁安装有第二电动伸缩杆，所述第二电动伸缩杆的尾端连接有拦截条，两组所述支撑板的顶部均安装有立块。本发明通过设置有叠片立板、限位环、拦截条以及缓冲弹簧的配合，可简化本叠片设备的整体占地面积，简化叠片加工程序。

为进行磷酸盐系无铬无取向硅钢涂层烧结固化工艺研究,首先对磷酸盐系无铬无取向硅钢涂层进行热重-差示扫描量热(TG-DSC)分析;然后在不同烧结固化温度条件下,测定涂层板温随时间变化曲线;最终获得涂层烧结固化温度与时间(T-t)工艺曲线。通过中性盐雾试验、动电位极化、交流阻抗、涂层附着力以及扫描电子显微镜(SEM)和能谱(EDS)分析验证。结果表明,根据涂层烧结固化温度与时间(T-t)工艺曲线制备的涂层结构致密、性能优异,证明该工艺曲线具有合理性与正确性。 In order to study the curing process of chromium-free non-oriented silicon steel coatings,phosphatic chromium-free non-oriented silicon steel insulating coating was prepared and TG-DSC analysis of the coating was conducted,then the change of the actual temperature of the coated non-oriented silicon steel sheet with time at different curing temperatures was studied. Based on the experiments,the processing curves of curing temperature vs. curing time( T-t) for the chromium-free non-oriented silico... 

结合工业化生产的高效硅钢,进行了RH精炼稀土处理试验研究。针对不同的稀土处理条件,观察了夹杂物的形貌和尺寸分布,探讨了稀土处理后钢中的夹杂物形成、变化规律。结果表明:试验条件下,最佳的稀土合金添加数量为0.6～0.9 kg/t。经过合适的稀土处理后,可以有效抑制尺寸相对较小的、不规则的AlN、MnS复合夹杂生成,促进钢中微细夹杂物的聚合、上浮,钢质纯净度得到明显提高。此时,钢中全氧含量最低,脱硫效果最佳,钢中的夹杂物主要是尺寸相对较大的、近似球形或者椭球形的稀土类夹杂。 Based on the industrial production of non-oriented silicon steel,the experiment on RE treatment during the RH refining process was studied.The morphology and the size distribution were observed for the steel specimens treated with different RE treatment conditions.Further more,the formation and change of inclusions of final steel sheets after RE treatment were discussed.The results show that the suitable RE added amount was 0.6～0.9 kg/t.After the suitable RE treatment,the formation of AlN and Mn... 

本文介绍了无取向硅钢C6涂液的性能,研究了配水量、固化程度和涂层厚度等因素对无取向硅钢C6涂层性能的影响。结果表明,随着配水量的增加,完全固化所需的时间增加,涂液固体含量降低,涂层厚度减小;随着固化程度的提高,涂层硬度先增大然后趋于恒定,而柔韧性逐渐变差,在过固化后急剧恶化;涂层厚度对涂层的表面外观、附着性和绝缘层间电阻均有显著影响。 Based on the introduction about the performance of C6 varnish for non-oriented silicon steel sheets,effects of water amount,curing degree and coating thickness are discussed. Results show that with the increase of water amount,the time required to cure completely extends,and both the solid content of C6 varnish and the coating thickness decrease. As the curing degree increases,the hardness of the coating increases first and then tends to be constant,however the flexibility degenerates,especially... 

对两种硅钢水溶性极厚绝缘涂层进行了不同温度的热老化实验。通过TG-DTA,GDS,FT-IR,SEM和光泽度仪等测试方法对老化的涂层进行分析表征,提出了评估硅钢水溶性极厚绝缘涂层热老化性能的合理温度区间,探讨了涂层热老化行为,并分析了两种涂层热老化性能的差异。结果表明,涂层附着性随着老化时间的延长逐渐下降。FT-IR表征结果显示,热老化过程中,涂料交联形成的化学键未发生断裂,交联剂氨基树脂的三嗪环被破坏是聚合物三维网络结构坍塌的主要原因。 Thermal aging expriments at different temperature were carried out on two types of water-soluble and extra-thick insulation coatings for non-oriented silicon steel,and a series of test methods such as glossmeters,TG-DTA,FT-IR,GDS,SEM were applied in analysis.For evaluating the thermal aging effect of this kind of insulation coating,the proper temperature range was proposed.The difference of aging performance between two coatings was been investigated and the related behaviors were been discussed... 

无取向硅钢特别是中牌号以上的无取向硅钢,随着含硅量的提高,常温下塑性较差,冷轧过程中轧制力明显提高,如果存在原料质量问题,极易发生断带事故,影响硅钢冷轧过程的成材率和生产效率。通过优化冷轧工艺参数,可提高冷轧稳定性。生产中通过合理分配冷轧各道次压下量和轧制速度,保证了轧制过程的稳定,很大程度减少了冷轧断带事故的发生。 Non-oriented silicon steel, especially in the low and middle grade, with the increase of silicon content, plasticity is poor at room temperature, rolling force in cold rolling process significantly improved .If there is the quality defect of raw materials , easily sheet is rolling off. Affect finished product rate and production efficiency in process of cold-rolled silicon steel. Through optimization of cold rolled process parameter , improve the stability of cold-rolling process. Through reason... 

本发明涉及一种混合硅钢定子结构及与其配套的转子结构及永磁电机，属于电机技术领域，包括：定子，由多个第一硅钢片叠压构成；多个线圈绕组，均匀设置在定子的内壁上；第一硅钢片包括：多个连接块与多个连接臂，连接块与连接臂交替排列构成硅钢环片，连接块采用无取向硅钢且与两侧的连接臂通过拼合结构连接，连接臂采用取向硅钢；多个定子齿，呈放射状均匀设置在硅钢环片的内侧，定子齿与连接块也通过拼合结构连接，定子齿采用取向硅钢；本发明通过取向硅钢、无取向硅钢混合组成的定子，能够有效提导磁性能；本发明能够稳定提升定子上的磁性能，增加电机的输出能力，实用性强，值得推广。

为了更好的解决电力系统防污闪涂料RTV-Ⅰ长期应用暴露出来的问题以及目前RTV-Ⅱ防污闪涂料存在的一些不足,结合具体实际需求,在电力系统外绝缘领域,应用新型防污闪硬质涂层——防污闪纳米硅钢涂层,并对分别喷涂了防污闪纳米硅钢涂层以及RTV涂料的绝缘子进行对比运行情况研究分析。研究结果表明,防污闪纳米硅钢涂层是一种同时具有优异憎水性迁移性能和自洁性能的新型涂层,具有良好的应用前景。 In order to solve the problem exposed of anti-pollution flashover coating RTV-Ⅰwhich has been used long-term in power system,as well as to better solve some shortcomings of the current anti-pollution flashover coating RTV-Ⅱ,in this paper,a new anti-pollution flashover hard coating — anti-pollution flashover nanometer silicon hard coating(NSHC) is applied in the field of power system insulation for the specific practical needs.At the same time insulators which are separately sprayed by the NSHC a... 

本实用新型属于冷轧硅钢技术领域的一种冷轧硅钢无压回水自动控制设备，包括底座，底座外表面的上端固定连接有工作台，工作台外表面上端的两侧分别固定连接有固定柱和压辊主体，工作台外表面上端的中部滑动连接有移动架，压辊主体的下端设置有集水槽，集水槽的内表面设置有浮球液位传感器。液压杆工作推动移动架位移到合适的位置，再通过气缸使伸缩管发生位移，使出水口接近钢板，设置的水箱高于出水口所以水可以在重力的作用下流淌，流出的水流到集水槽内，水流在集水槽内聚集，水流使浮球液位传感器的浮球上升，上升到合适的位置时，浮球液位传感器通过电缆发生电信号至控制器，此设置可以实现设备的自动控制，省去人工进行操作。

本发明涉及一种硅钢片纵剪边料收卷装置，包括：用于将收卷装置固定于地面的机架底座，机架底座一端设置固定支架，固定支架上安装电动定尺收料盘；在机架底座上设置电动可移动支架，电动可移动支架在机架底座的长方向上相对固定支架移动，电动可移动支架上安装电动可调收料盘；电动可移动支架、电动定尺收料盘、电动可调收料盘与PLC控制系统连接，PLC控制系统用于控制电动可移动支架的移动距离、以及控制电动定尺收料盘和电动可调收料盘的收料速度。本发明还涉及一种硅钢片纵剪边料收卷方法。将本发明的收卷装置安装在硅钢片滚剪线切刀后面的输送平台下部，卧式布局，不占用外部空间，和滚剪线无缝集成在一起，自动完成硅钢片纵剪边料收卷工作。

用于层叠铁芯的电磁钢板为一种在母材钢板(2)的表面具有绝缘被膜(3)的电磁钢板，该绝缘被膜(3)是涂布电磁钢板用涂布组合物而构成的，所述电磁钢板用涂布组合物以特定的比例配合有环氧树脂、第1固化剂及第2固化剂，该第1固化剂由包含具有烷基及烷氧基中的任意一者或两者的酚骨架的酚醛树脂构成，该第2固化剂为从酚醛甲阶树脂及苯酚酚醛清漆树脂中选择的1种以上。