利用背散射衍射技术(EBSD)和XRD,研究了两段式脱碳退火工艺对取向硅钢纵截面初次再结晶的微区取向、取向差分布、特殊晶界(CSL)及高温退火试样高斯织构。分析了初次再结晶晶界特征对取向硅钢高温退火后宏观织构的影响。结果表明:初次再结晶的纵截面基体中Σ3和Σ5晶界使得高斯晶粒有着较高的迁移率,在高温退火时借助20o～45°的大角度晶界的界面能吞并周围{111}<112>晶粒迅速长大,形成密度水平较高的高斯织构。 Micro area orientation of primary recrystallization,the misorientation distribution,special boundaries under different two-stage decarburization annealing and the Goss texture under high temperature annealing the longitudinal section of grain-oriented silicon steel were detected by electron back scattering diffraction(EBSD) and X-ray diffraction(XRD).The effect of primary recrystallization grain boundary on macrotexture after high temperature annealing was analyzed.The results show that the Σ3 a... 

为了提升新能源车用驱动电机的功率密度,各大电机厂商都在不断地提升电机转速,随之而来的问题就是电机的铁耗也在不断增高,如何降低电机铁耗成为了电机厂商必须要解决的难题。本文讨论了电机铁耗的组成部分及影响因素,并对1台8极48槽的永磁同步电机分别使用3种不同厚度的材料进行仿真,对比其效率及铁耗分布,推导出驱动电机中硅钢厚度、铁耗及成本的关系,最后对驱动电机选材提出建议。 In order to increase the power density of traction motor for new energy vehicles,major motor manufacturers have been constantly increasing the motor speed.The following problem that manufacturers have to solve is how to reduce the increasing iron loss when the motor speed is increased.The components and influencing factors of motors’ iron loss were discussed in this paper,and an 8-pole 48-slot permanent magnet synchronous motor using three different thickness materials was simulated.To compare i... 

叠片系数是冷轧无取向电工钢的重要质量指标。为了提高叠片系数,必须保证无取向电工钢板形良好以及横向厚差小。针对攀钢冷轧厂4机架HC轧机轧制无取向电工钢的边部减薄问题,以无取向电工钢横向厚差最小作为目标函数,建立了一套针对无取向电工钢边部减薄控制的辊型曲线优化数学模型,开发了无取向电工钢专用辊型曲线,使无取向电工钢横向厚差从25μm降低到10μm以下,取得了良好的控制效果。 The lamination factor is an important quality index of non-oriented silicon steel strip.Considering the lamination factor,the non-oriented silicon steel must have a good shape and a smaller transverse thickness difference.In order to solve the edge thinning of non-oriented silicon steel strip in Panzhihua Steel,a mathematic model for designing the roll shape is built.In the model,the transverse thickness difference of non-oriented silicon steel strip is taken as the objective function.Based on t... 

针对某厂DMS森吉米尔轧机生产无取向硅钢表面麻面缺陷的问题，根据生产实际，对其形成原因从乳化液及工作辊两方面因素进行了分析。结果表明：乳化液对麻面缺陷的产生有一定影响，但不是主要因素，主要原因是由于二十辊森吉米尔轧机工作辊辊径较小，轧制相同长度带钢轧辊运转周期较大，容易产生疲劳失效而导致。为此，提出通过调整冷轧工序成品轧制道次的压下率以减小轧制力，从而减小工作辊的磨损疲劳；通过对轧制乳化液浓度、温度的合理控制，以改善润滑效果、提高轧制速度，而进一步缓解轧辊疲劳的改进措施，使该钢厂无取向硅钢麻面缺陷发生率由原来的18%降至0.8%,带钢表面质量明显改善。 For the problem of surface pockmarks of non-oriented silicon steel strip produced by a DMS Sendzimir mill, based on the production practice, the formation causes were analyzed from two aspects of emulsion and working roll. The results show that the emulsion has a certain effect on the formation of surface pockmarks defects, but it is not the main factor. The main reason is that the working roll diameter of the 20-high Sendzimir mill is small, and the running period of the roll rolling the same l... 

对无取向硅钢炼钢全流程钢液增钛的原因进行了分析,认为铁水钛含量、转炉出钢温度、转炉下渣量、精炼渣TiO₂含量、钢水罐及RH浸入管混钢种生产是影响钢液增钛的主要原因。通过采取低钛铁水冶炼,减少转炉下渣量,提高出钢温度,添加白灰改质精炼渣等措施,均能够降低钢液中的钛含量。 After analyzing the causes leading to increased content of titanium in molten nonoriented silicon steel during whole steelmaking process, it was concluded that such factors as content of titanium in hot metal, tapping temperature from converter, quantity of roughing slag entered into the ladle from converter, content of TiO₂ in refining slag, molten steel ladle car,carrying out the steelmaking of different steel grades by the same ladle and same RH immersion tube were the main causes ... 

无氧化炉具有加热效率高、投资与运营成本低、作业率高、表面质量及板型良好、NOx排放相对低等优势,在硅钢热处理领域应用前景广泛。本文阐述了确定无氧化炉(NOF)加热能力详细过程,涵盖炉温、炉断面尺寸、炉长、热平衡结算、加热能力计算等,为今后无氧化炉(NOF)在硅钢热处理应用时的设计提供了借鉴,同时也为今后明火直接加热的工业炉设计提供了参考。 Non-oxidation furnace has the advantage s of high heating efficiency, low investment and operation cost, high operation rate, good surface quality and plate shape, and relatively low NOxemission,and it still has wide application prospect in the field of silicon steel heat treatment. The detailed process of determining the heating capacity of a non-oxidizing furnace(NOF) is described, covering furnace temperature, furnace section size, furnace length, heat balance settlement, heating capacity cal... 

一种高磁感低铁损取向硅钢生产用表面涂层涂覆装置，包括：加工台，加工台上端固定连接支撑架，支撑架下端一侧固定连接伺服电机，伺服电机输出端固定连接第一齿轮，第一齿轮下端啮合连接第二齿轮，第二齿轮中部固定连接螺纹杆，螺纹杆上螺纹连接移动环，螺纹杆远离第二齿轮一侧转动连接支撑板，支撑板上端固定连接支撑架，移动环下端固定连接伸缩杆，支撑架下端前后部均固定连接连接框，本实用新型的有益效果是：通过设置的伺服电机、第一齿轮、第二齿轮、螺纹杆和移动环等结构，能够实现伸缩板带动硅钢板移动，从而能够完成自动化推料，减少工人劳力支出的同时，也能够避免工作人员手臂靠近涂层辊，从而避免安全事故的发生。

本实用新型公开了硅钢片生产用上料装置，属于硅钢片生产领域，包括本体，所述本体包括侧板和U型板，所述侧板固定连接在U型板的一侧，所述本体的顶部横向设置有平移机构，所述平移机构上安装有气缸，所述气缸的底部安装有吸盘，所述U型板内腔的底部竖向固定连接有弹簧，所述弹簧远离U型板的一端水平固定连接有升降板，所述平移机构包括电机、螺纹杆、限位板和移动块，所述电机安装在侧板的顶部，所述电机的输出轴与螺纹杆的一端固定连接，通过设置弹簧，在第一个物料从上料装置移出后弹簧的弹力推动剩余物料，使得剩余物料进行上升，避免吸盘触碰不到物料的问题，简化吸盘移动轨迹，加快上料速度。

本发明提供了一种无取向硅钢RH顶枪喷粉脱硫工艺，RH脱碳结束测温定氧，立即加入铝粒脱氧合金化、之后立即依次连续加入合金进行成分调整，合金加完后立即开始顶枪喷粉；加入铝粒的量＝铝粒理论加入量+0.2‑0.4kg/t钢；喷粉时，控制喷粉速度与钢液循环流量相匹配；本发明从真空条件下脱硫热力学和动力学角度出发对具有顶枪喷粉功能的RH脱硫工艺进行改进，提高脱硫率。

本发明揭示了一种超低铁损无取向硅钢及其生产方法，生产方法包括：依次采用铁水脱硫、转炉冶炼、RH炉精炼进行冶钢，最终所得钢水化学成分以质量百分比计为：C≤0.003％、Si：2.8～3.4％、Mn：0.1～0.5％、Al：0.6～1.3％、S≤0.0015％、N≤0.0020％、P≤0.03％、Ti≤0.003％、V≤0.003％、Nb≤0.003％，且同时满足3.80％≤Si+Al≤4.15％，其余为Fe以及不可避免的杂质；将冶炼所得钢水连铸成连铸坯；对连铸坯加热后经过多道次轧制得到热轧卷板；对热轧卷板的两侧边部进行剪切；常化酸洗，常化温度为900～930℃，常化时间为30～60s；经多道次冷轧成厚度为0.35～0.5mm的无取向硅钢，其中，第一道次冷轧时的压下率≥37％，轧制速率为70～180m/min。本发明制备的无取向硅钢具有超低铁损，而且冷轧时不易断带。

本发明公开了一种高磁感取向硅钢，其含有Fe及不可避免的杂质元素，其还含有质量百分含量如下的下述各化学元素：C：0.02～0.08％，Si：2.0～4.5％，Mn：0.02～0.30％，S≤0.0050％，Als：0.01～0.04％，N：0.002～0.01％，Nb：0.0050～0.0600％；以及P：0.01～0.1％，Sn：0.01～0.30％，Cu：0.01～0.50％的至少其中一种。此外，本发明还公开了上述高磁感取向硅钢的制造方法，其包括步骤：(1)制得板坯；(2)板坯加热；(3)热轧，其包括：粗轧、在热卷箱内卷取保温，以及精轧；其中粗轧结束温度高于970℃；卷取温度为800～1050℃，卷取时间为30～200s；精轧开始温度低于1050℃；(4)冷轧；(5)脱碳退火；(6)渗氮；(7)涂覆退火隔离剂；(8)高温退火；(9)涂覆绝缘涂层和激光刻痕。

本发明公开了一种电工钢片磁致伸缩模型的建模方法，包括：测量不同旋转磁场下电工钢片磁致伸缩对称蝴蝶曲线εk；对所测量的对称蝴蝶曲线进行辨识，构建磁致伸缩蝴蝶曲线εk的Everett函数数据库；将输入的矢量磁场B波形用旋转磁场形状参数Bmax,最大值方向的方向角θ和椭圆长短轴的长度比λ拟合，得到拟合后结果；通过线性插值法在磁致伸缩Everett函数数据库中进行插值，获得拟合后结果所对应的磁致伸缩Everett函数值Ek；根据Everett函数值Ek计算得出对应的磁致伸缩蝴蝶曲线εk。应用本发明实施例，不仅可以描述矢量磁致伸缩特性，还可以通过计算估算出旋转磁场下的瞬态磁致伸缩。此外，还能够考虑磁致伸缩的各向异性特性。