硅钢资料

针对采用含钒铁水生产无取向电工钢存在的铁水脱硫率低、转炉冶炼过程回硫量大、成品硫含量偏高的问题,通过对含钒钛铁水脱硫,减少转炉冶炼过程回硫以及RH脱硫技术等方面的研究,大幅度降低了电工钢成品硫含量。生产表明钢中w(S)=0.001 9%～0.006 9%,平均为0.004 2%;w(S)≤0.008%的比例达到了100%,且w(S)≤0.005%的比例也达到了91.43%。 In cognizance of the problems of low desulphurization rate for hot metal,large sulfur-recovery in converter as well as high sulfur content in products in producing non-orientation electrical steel with vanadium-content hot metal countermeasures have been carried out.Sulfur content in non-orientation electrical steel is decreased obviously by way of study on technologies of desulphurization for hot metal with vanadium & titanium,sulfur-recovery control in converter and desulphurization in RH ... 

本发明公开了一种高磁感取向硅钢，其含有Fe及不可避免的杂质元素，其还含有质量百分含量如下的下述各化学元素：C：0.02～0.08％，Si：2.0～4.5％，Mn：0.02～0.30％，S≤0.0050％，Als：0.01～0.04％，N：0.002～0.01％，Nb：0.0050～0.0600％；以及P：0.01～0.1％，Sn：0.01～0.30％，Cu：0.01～0.50％的至少其中一种。此外，本发明还公开了上述高磁感取向硅钢的制造方法，其包括步骤：(1)制得板坯；(2)板坯加热；(3)热轧，其包括：粗轧、在热卷箱内卷取保温，以及精轧；其中粗轧结束温度高于970℃；卷取温度为800～1050℃，卷取时间为30～200s；精轧开始温度低于1050℃；(4)冷轧；(5)脱碳退火；(6)渗氮；(7)涂覆退火隔离剂；(8)高温退火；(9)涂覆绝缘涂层和激光刻痕。

本发明提供的一种耐热型低损耗取向硅钢，取向硅钢的单面采用激光刻痕形成平行线状沟槽；所述激光刻痕为取向硅钢制备工艺中的渗氮步骤之后和在涂覆MgO涂层步骤之前实施；在渗氮步骤之后和在涂覆MgO涂层步骤之前进行激光刻痕加工不会破坏高温退火后形成的硅酸镁底层，底层完整性好，刻痕形成的沟槽位于取向硅钢带材金属基体表面，在高温退火过程中沟槽内直接反应生成硅酸镁底层，最终取向硅钢带材表面涂覆张应力涂层后光滑、平整、无凹凸，取向硅钢带材损耗低、叠片系数高、耐热，成品取向硅钢带材既可用于制备立体卷铁心变压器也可用于制备叠片铁心变压器。

本实用新型涉及取向硅钢高温连续退火炉领域，尤其涉及一种取向硅钢高温连续退火炉隔离装置，包括安装在炉壳上的隔离炉门及设置在隔离炉门四周的密封井；隔离炉门顶部两侧安装有水冷却装置；水冷却装置上部设有隔离炉门动力牵引装置；密封井包括固定密封井和伸缩密封井，伸缩密封井位于固定密封井内部并与固定密封井滑动连接，伸缩密封井与固定密封井端部连接处设有密封装置。本实用新型可以确保隔离炉门升降过程中实现无缝全密封状态，提高密封效果，且采用伸缩密封井实际降低了密封井的高度，间接降低了水冷却装置连接管道上升至最高点的净空标高，与传统固定式密封井高度相比可以降低高度50％～80％，从而降低厂房净空标高，节省厂房基建投资。

本发明公开了一种控制无取向电工钢横向同板差的装置，包括热轧机、圆盘剪、冷轧机和输送辊道，圆盘剪安装在输送辊道两侧且位于热轧机和冷轧机之间，无取向电工钢在输送辊道的运输下依次经过热轧机、圆盘剪和冷轧机，设定热轧机对无取向电工钢的楔形和凸度进行控制，控制无取向电工钢的楔形在20微米内、凸度为20～45微米，冷轧机的工作辊设有倒角。冷轧机为UCM五连轧轧机，UCM五连轧轧机中1#和2#轧机工作辊的单边设有倒角，1#和2#轧机中上工作辊的操作端设有倒角，下工作辊的传动端设有倒角。倒角的深度为0.2～0.3mm，倒角在工作辊上的起始位置到工作辊端面的距离为265‑285mm。本发明还公开了一种控制无取向电工钢横向同板差的方法。

本发明公开了一种用于无取向硅钢清洗液的洁净度检测分析方法，包括以下步骤：步骤1：从清洗液循环槽中取含有污物的清洗液样品，并进行脱水、烘干、研磨，得到污物粉末样品；步骤2：根据含有污物的清洗液样品和污物粉末样品计算清洗液循环槽中清洗液的洁净度；步骤3：根据含有污物的清洗液样品的洁净度建立清洗液洁净度评定标准；步骤4：根据清洗液洁净度评定标准控制含有污物的清洗液的排放和换液。本发明能简便且直观的了解当前清洗段循环槽内清洗液的状态，并可以根据清洗液的洁净度评级对清洗液的使用和排放做出及时的在线调整。

为了优化激光刻痕降低取向硅钢铁损的工艺,寻找刻痕速度、脉冲能量、扫描间距等重要刻痕参数的最佳匹配关系,提出了一种基于人工神经网络与遗传算法的优化模型,并利用这种模型对30Q130取向硅钢材料的刻痕工艺进行了优化实验,结果表明,这种模型稳定可靠,可以作为取向硅钢刻痕工艺优化的一种有效的措施。 A laser is often considered to scribe the grain-oriented silicon steel surfaces after cold-rolling and annealing to reduce the core loss.It is necessary to select the best scribing parameters to maximize the reduction in this process.This paper proposes an optimization method of genetic algorithm during laser scribing of 30Q130 steel,by developing an artificial neural network prediction model using a database form a designed orthogonal experiment.The objective is to determine the best combinatio... 

采用SEM、EDS和XRD对不同加热温度下W470连铸坯氧化铁皮的微观形貌及相结构进行研究。结果表明,W470氧化铁皮难以除去的原因是氧化铁皮熔化,液相包裹着FeO,凝固时发生共晶反应,生成FeO/Fe2SiO4共晶混合物,并深嵌入基体。降低加热炉的加热温度,使连铸坯全程在FeO/Fe2SiO4共晶混合物熔点(1177℃)以下加热,可降低氧化铁皮与基体的结合力,能够有效解决W470除鳞困难问题。 The microstructure and phase structure of iron scale of W470 continuous casting billet at different heating temperatures were investigated by SEM,EDS,and XRD.The results show that the reason why the iron scale of W470 removes hardly is that iron scale is melted and the FeO is surrounded by the liquid phase,which forms FeO / Fe2SiO4eutectic mixture and is embedded into the matrix after solidification.Lowering the heating temperature and keeping the continuous casting billet heating under the melt... 

本发明涉及冶金技术领域，具体涉及一种高牌号硅钢用连铸结晶器保护渣及其制备方法和应用。本发明提供的连铸结晶器保护渣，所述保护渣包括如下质量百分比的化学成分：SiO2：40‑45％、CaO：20‑27％、MgO：1.0‑2.5％、Al2O3：1‑3％、Na2O：12‑16％、F：10‑13％、C：1‑3％，其余为不可避免的杂质；其中所述保护渣的二元碱度CaO/SiO2为0.5‑0.6，熔点为950‑1000℃，1300℃下的粘度为0.25‑0.35Pa·s。本发明提供的连铸结晶器保护渣，通过低碱度、低熔点、低粘度的保护渣可有效抑制高牌号硅钢材料在连铸时铸坯表面易出现凹陷和裂纹的现象。

一种无取向电磁钢板用热轧钢板，其以质量％计，含有C：0.0010～0.0050％、Si：1.90％～3.50％、Al：0.10％～3.00％、Mn：0.05～2.00％、P：0.100％以下、S：0.005％以下、N：0.0040％以下、B：0.0060％以下、Sn：0～0.50％、Sb：0～0.50％、Cu：0～0.50％、REM：0～0.0400％、Ca：0～0.0400％及Mg：0～0.0400％，剩余部分为Fe及杂质；该无取向电磁钢板用热轧钢板的特征在于，在无取向电磁钢板用热轧钢板的板宽方向端部中，板厚中心部(t/2位置)的加工组织的硬度HD为Hv220以下。

针对新日铁公开的相关专利,总结日本高强度无取向电工钢的研究进展,分析了各专利化学成分、生产工艺及产品性能的特点,指出固溶强化、细晶强化、析出强化、位错强化都有可能被用来提高无取向电工钢的强度。在高强度无取向电工钢的研发过程中,需要根据其具体用途确定目标性能,再采用合适的强化手段,从而实现力学性能、磁性能和生产性能之间的平衡。 Authors summarize the research progress of high strength non-oriented electrical steel in Japan by learning related patents brought into the public by Nippon Steel. Authors also analyze the characteristics of the chemical composition, production technology and properties of products in the patents and point out that any ones of solution strengthening method, fine-grain strengthening method, precipitation strengthening method or dislocations strengthening method may be used to improve the strengt... 

本发明属于硅钢制造技术领域，具体涉及一种改善硅钢热轧板边部质量的加工方法，包括：连铸、铸坯预变形处理、铸坯加热处理和热轧处理；其中，所述铸坯预变形处理包括：在所述铸坯的温度为500～900℃下，对所述铸坯的沿长度方向的两侧壁通过立辊施加压力，直至形变量h为10～50mm；所述铸坯加热处理的加热温度为1100～1200℃，保温时间为4～6h。本发明提供的改善硅钢热轧板边部质量的加工方法，采用铸坯两侧壁的侧压工艺，有效解决了热轧板边部裂纹的缺陷，提高了边部塑性，提高了成材率并降低了生产成本。