采用自主研发的脉冲磁场退火装置，在取向硅钢脱碳退火过程中分别施加不同强度的磁场，并采用光学显微镜和X射线衍射仪研究了脉冲磁场脱碳退火后试样的显微组织和宏观织构。结果表明，脱碳退火过程中施加脉冲磁场后取向硅钢的平均晶粒尺寸均增加，当磁场强度为40 mT时，平均晶粒尺寸最大，为13.06μm。此外，取向硅钢试样的立方织构{001}<100>强度减弱，高斯织构{110}<001>和{111}<112>织构增强，有利于获得更好的成品织构和磁性能。 Self-developed pulsed magnetic field annealing device was used to apply magnetic field of different intensities during decarburization annealing of an oriented silicon steel, and microstructure and macro-texture of the specimens after decarburization annealing in a pulsed magnetic field were studied by using optical microscope and X-ray diffractometer. The results show that the average grain size of the oriented silicon steel increases with the application of pulsed magnetic field during decarbu... 

本发明涉及一种硅钢热处理方法，尤其涉及一种取向硅钢极薄带绝缘层涂覆方法，包括以下步骤：(1)接入普碳钢引带的准备工作；(2)各炉段张力的设定工作；(3)炉内气氛及温度的调节工作；(4)绝缘层厚度及厚度的检测工作；(5)极薄带涂层涂覆及烘干工作；(6)极薄带表面绝缘涂层及磁性能检测工作。本发明采用与极薄带厚度相当的普碳钢作为引带，通过引带测试产线张力和绝缘层涂覆的厚度，一方面可通过普碳钢薄带的运行加速炉内温度和气氛的稳定性，节约炉内稳定时间；另一方面可通过成本较低的普碳钢检测炉内张力和温度的设定，及绝缘涂层的涂覆效果，避免开始采用硅钢带出现断带，及涂覆不合格后造成产品报废带来的成本升高。

本实用新型涉及电机生产设备技术领域，特别涉及一种硅钢板冲裁余料处理工装，出料带通过支撑架平放在地面上，出料带的上方平行设置有安装在支撑架上的支撑砧板；支撑砧板的上方平行设置有上下滑动安装在支撑架上的刀架，刀架上设有切刀；支撑砧板的一端邻接有上料带，上料带将硅钢板冲裁余料送入到支撑砧板上。本实用新型的有益效果是：本实用新型可将成条的硅钢板冲裁余料进行自动裁切处理，裁切后的三角形的边角料会掉落到出料带中送出，此设备节省了大量的人力成本，提高了车间生产的安全性。

本发明涉及含Cu无取向硅钢的生产方法，转炉炼钢，真空处理过后连铸成坯；铸坯化学成分：1.0≤Si/Cu≤3.0,3.0≤Si+Cu≤5.5％，S≤0.0015％，(Mn+Cu)/S≥3000，其他为Fe,Als,P以及不可避免的杂质元素；对铸坯进行粗轧；粗轧后的中间坯采用热卷机进行强制卷取，开卷后中间坯进入保温箱，控制保温箱内冷却速度≤5℃/s；进入保温箱的中间坯温度T1满足：1000‑(Si+Cu)×103≤T1≤1100‑(Si+Cu)×103；高压除鳞，精轧，层流冷却，卷取；连续酸洗；冷轧到目标厚度，成品退火，涂层；成品卷进行时效处理。成品卷具有较低的中高频铁损，高磁感和高屈服强度。

本发明涉及一种防止低温加热取向硅钢热轧边裂的方法，包括：1)控制取向硅钢铸坯进入加热炉前的表面温度；2)控制加热段各段炉气温度；3)二加热段采用加速加热；4)控制总加热时间；5)控制出炉温度；6)控制精轧道次及侧压量；7)控制精轧道次及终轧温度；8)精轧前对钢带边部进行加热补偿。本发明通过合理制定取向硅钢的加热温度、加热时间和轧制工艺制度，避免或消除了低温加热取向硅钢热轧边裂问题。

本发明提供了一种超低铁损无取向硅钢薄带，以质量百分比计，其成分包括C≤0.005％，Si：3.5～4.0％，Mn：0.1～0.3％，Als≤0.005％，P≤0.05％，S≤0.005％，Cu≤0.08％，N≤0.003％，Sn：0.04～0.08％，其余为Fe及不可避免杂质，所述硅钢薄带中Mn与S的含量比Mn/S≥50，所述硅钢薄带厚度为0.3‑0.4mm。本发明还提供了一种超低铁损无取向硅钢薄带的制备方法。本发明提供的一种超低铁损无取向硅钢薄带，具有高磁感、低铁损等优良性能，且其制备工艺流程短、容易实现、生产效率高、生产成本低、节能降耗明显。

采用光学显微镜、X射线衍射仪等分析了宁波钢铁有限公司生产的取向硅钢不同工序下的组织及织构演变规律。结果表明:铸坯经过热轧后,沿着厚度方向组织不均匀;一次冷轧并经脱碳退火后,组织由条状纤维状变成等轴状的初次再结晶晶粒,初次再结晶平均晶粒尺寸为18.17μm,织构主要以α织构和γ织构为主;在二次冷轧后,晶粒再次被压缩,转变为纤维状,织构主要为γ织构;经过高温退火后,发生二次再结晶,晶粒异常长大,晶粒尺寸达到厘米级,织构成分为单一且锋锐的Goss织构。 The microstructure and texture evolution of oriented silicon steel produced by Ningbo Iron and Steel Co.,Ltd.were analyzed by optical microscope and X-ray diffraction.The results showed that the microstructure of the slab was inhomogenous along the thickness direction after hot rolling.After first cold rolling and decarburizing annealing,the microstructure changed from strip fibrous to equiaxed primary recrystallized grains,and the average grain size of the primary recrystallization microstructu... 

结合实际生产0.4%Si无取向硅钢，统计了不含Sn和0.025%Sn无取向硅钢的磁性能变化，利用金相显微镜、X射线衍射仪观察分析不同成分下试样的显微组织和微观织构。试验结果表明：Sn元素可以显著降低无取向硅钢的晶粒尺寸，0.025%Sn试样的平均晶粒尺寸比不含Sn减小28.4%;加入Sn元素后抑制了无取向硅钢中不利于磁性能的{111}面织构组分强度，提高了对磁性能有利的{100}面织构组分强度，0.025%Sn与不含Sn相比磁感均值从1.756 T提升至1.768 T,铁损均值从5.476 W/kg降低至5.204 W/kg,明显改善了无取向硅钢磁性能。 In this paper combined with the actual production of 0.4% Si non oriented silicon steel, the magnetic properties of non oriented silicon steel without Sn and 0.025% Sn were counted. The microstructure and microtexture of samples with different compositions were observed and analyzed by metallographic microscope and X-ray diffraction. The results show that: Sn can significantly reduce the grain size of non oriented silicon steel, and the average grain size of 0.025% Sn sample is 28.4% smaller tha... 

本实用新型属于抛丸设备技术领域，具体涉及一种硅钢抛丸用耐磨抛丸头，包括壳体、进丸管、定向套、分丸轮、多块截面呈工字形的叶片和两块对称设置的护板，多块叶片沿护板的周向均匀分布，叶片安装在两块护板之间；叶片的左右两侧分别设有一组卡槽，一组卡槽包括两个卡槽，一组卡槽上滑动连接有能与叶片表面接触的耐磨板；叶片上设有用于固定耐磨板位置的固定件；壳体内可拆卸的安装有耐磨衬板。在本方案中，将耐磨板可拆除的安装在叶片中，耐磨板对叶片有保护的作用，能避免叶片被磨损；当耐磨板损坏后只需更换新的耐磨板，而不需更换叶片，能够有效节省成本。同样的耐磨衬板对壳体也有保护作用，能够在很大程度上减少壳体被磨损。

实验室模拟薄板坯连铸连轧(TSCR)流程制造高磁感取向硅钢,借助电子背散射衍射(EBSD)技术对不同Sn含量的热轧板织构进行了研究。研究结果表明:不同Sn含量热轧板表层及次表层均为高斯织构、铜型织构及黄铜织构的混合织构,中心层为{100}面织构;Sn含量为0.1%时,热轧板表层及次表层高斯织构组分最多,取向密度最大,成品磁感最高,达到1.875 T。 Texture of grain oriented silicon steel hot rolled by thin slab casting and rolling process(TSCR) in laboratory with different Sn contents was analyzed by electron back-scattered diffraction(EBSD).The results show that the hot rolled slabs with different Sn contents have the same texture,i.e.,Goss,Copper and Brass.Specifically,the texture of core layer is {100};While the hot rolled slab with 0.10% Sn,the surface layer and subsurface layer have a sharpness Goss texture and the finished products h... 

冷轧无取向硅钢是高技术含量、高附加值产品,工艺复杂,生产周期长,过程控制难度大,被誉为钢铁产品中的\"工艺品\"。热轧生产工艺又是无取向硅钢生产的重中之重,直接决定了硅钢的铁损和电磁性等多项指标。 Cold rolled non-oriented silicon steel is high technology content 、high added value product. Its process is complex, its production cycle is of length, and its process control is difficult, which is known as the iron and steel products \" Arts and crafts\". Hot rolling production process is the top priority of non-oriented silicon steel, which directly determines iron loss of the silicon steel and electromagnetic property,as well as other many index. 

本实用新型涉及一种用于叠装变压器铁芯硅钢片的装置，包括托板，托板的上表面固定设置有固定板，固定板的内部开设有沉槽；双向螺纹杆，双向螺纹杆设置在固定板的内部，双向螺纹杆的一端贯穿固定板的侧壁并连接有把手；支撑柱，支撑柱的表面开设有连接槽，连接槽的内部铰接有连接杆；有益效果为：本实用新型提出的一种用于叠装变压器铁芯硅钢片的装置在托板的左右两侧设置有两组对称分布的固定板，通过对双向螺纹杆的旋转，螺接在双向螺纹杆表面的两组滑块将会相对移动，铰接在滑块上表面的两组支撑柱将会形成三角形对铁芯进行防护。