本发明公开了一种低磁致伸缩取向硅钢的制造方法，其包括步骤：(1)在硅钢基板上进行单面激光刻痕，其中进行激光刻痕的表面为第一表面，第一表面的背向一侧表面为第二表面；(2)基于激光刻痕的功率确定第一表面和第二表面的挠度差；(3)基于挠度差获得第一表面和第二表面所涂覆的绝缘涂层的涂覆量差；(4)基于涂覆量差，在第一表面和第二表面上涂覆绝缘涂层，其中第二表面的绝缘涂层涂覆量大于第一表面的绝缘涂层涂覆量。相应地，本发明还公开了采用上述制造方法所制得的低磁致伸缩取向硅钢，其第一表面和第二表面的磁致伸缩偏差≤2db(A)，并且所述低磁致伸缩取向硅钢的平均磁致伸缩≤55db(A)。

利用EBSD技术研究了电工钢中长轴平行于轧向的柱状晶样品在热轧和退火过程中组织和取向的演变规律,并与长轴平行于板法向的样品的已有研究结果进行对比。结果表明,无论柱状晶按何种方向排列,只要表面存在剪切力,热轧后都可形成剪切织构,同时中心形成轧制织构,主要包括旋转立方织构和{112}<1-10>。柱状晶造成的影响主要体现在板中心层,长轴平行于轧向排列的样品热轧时形成的粗大旋转立方晶粒要到脱碳退火后才能完全消除,但破坏了正常的不同取向晶粒间的取向差分布及尺寸均匀性,导致二次再结晶不完全及磁性能降低。 The evolution of microstructure and grain orientation in an electrical steel containing columnar grains with its long axis being parallel to the rolling direction of sheet was studied during hot rolling and annealing by EBSD technique.The results are compared with those of samples containing columnar grains being parallel to normal direction of sheet reported in the reference [3].It was shown that,whether the long axis of columnar grains was arranged in RD or ND,shear textures can be formed in t... 

日本住友金属成功地开发了一种资源节约型高强度无取向电工钢SXRC,这种电工钢是通过固溶铌适度抑制位错的合并对消而得到一种特殊的微观组织,因此兼具很高的力学性能和磁性,特别适用于HEV、EV驱动电机转子。而且,不使用昂贵的镍就可以达到期望的强度,合金成本可控,是一种优越的资源节约型产品。 Sumitomo metal industries ltd of Japan successfully developed a type of high strength non-orientation electrical steel SXRC of resources-saving.The steel has both high mechanical performance and good magnetic property thanks to the special microstructure produced by the formation of Nb solid solution serving to appropriately inhibit the combination and cancellation of dislocations.The material is,in particular,suitable for manufacturing rotors of HEV and EV driving motors.Besides,expected streng... 

本发明提供了一种超低铁损无取向硅钢薄带，以质量百分比计，其成分包括C≤0.005％，Si：3.5～4.0％，Mn：0.1～0.3％，Als≤0.005％，P≤0.05％，S≤0.005％，Cu≤0.08％，N≤0.003％，Sn：0.04～0.08％，其余为Fe及不可避免杂质，所述硅钢薄带中Mn与S的含量比Mn/S≥50，所述硅钢薄带厚度为0.3‑0.4mm。本发明还提供了一种超低铁损无取向硅钢薄带的制备方法。本发明提供的一种超低铁损无取向硅钢薄带，具有高磁感、低铁损等优良性能，且其制备工艺流程短、容易实现、生产效率高、生产成本低、节能降耗明显。

通过后天抑制剂获得法制备了取向硅钢,对渗氮前后和高温退火升温阶段析出物的析出和转化规律进行了研究。研究结果表明,渗氮前脱碳退火态基体中存在少量的粗大AlN颗粒和细小AlN颗粒,渗氮处理后新析出大量的Si3N4析出物,高温退火升温阶段Si3N4将转化为(Al,Si)N,随着温度的继续升高(Al,Si)N颗粒将发生粗化,(Al,Si)N是后天抑制剂获得法制备取向硅钢的主要抑制剂。 Grain-oriented silicon steels were produced by acquired inhibitor method.The rule of precipitate transformation was studied after nitriding treatment and high-temperature finishing annealing.The results show that a small amount of large AlN and fine AlN are found in matrix before nitriding treatment,and a large amount of Si3N4 is precipitated in matrix after nitriding treatment.During the temperature rising period of high-temperature finishing annealing,Si3N4 would transform into(Al,Si)N,and(Al,... 

以轻烧氧化镁粉为原料,经消化、碳化制得重镁水,在热解反应前采用络合剂对重镁水中的杂质钙、铁进行络合掩蔽,再经热解得到碱式碳酸镁,碱式碳酸镁经煅烧可制得钙、铁杂质含量较低的氧化镁。在重镁水络合除杂过程中,考察了络合剂三乙醇胺、柠檬酸、草酸单独和复合使用的除铁、除钙效果。以三乙醇胺为络合剂时,在200 mL重镁水中加10 mL三乙醇胺(1∶1),氧化镁产品中w(氧化镁)=99.3%、w(氧化钙)=0.31%、w(氧化铁)=0.042%;使用草酸和柠檬酸作为复合络合剂时,在200 mL重镁水中加入1.0 g柠檬酸和2.0 g草酸,氧化镁产品中w(氧化镁)=98.2%、w(氧化钙)=0.24%、w(氧化铁)=0.030%。 Light-burned magnesia as a raw material was hydrated and carbonated to obtain magnesium bicarbonate liquor.Before the pyrolyzing of magnesium bicarbonate liquor,complexants were used to cover Fe and Ca impurities.Then the treated liquid was pyrolyzed to obtain basic magnesium carbonate which was calcined to magnesium oxide with low calcium and iron content.During the complexing purification of magnesium bicarbonate liquor,the Fe and Ca removing effects of single or compound complexing agents,suc... 

研究了电工钢SXRC的显微结构和疲劳性能,并与DP钢进行了比较。结果表明,退火温度低温化能够有效的抑制电工钢的再结晶。该钢在固溶铌的作用下,能够在保证电机磁性的同时具有一定的强度。与DP钢相比,SXRC钢的抗疲劳性能更好。 The microstructures and fatigue properties of the electrical steel SXRC we re investigated, and the properties were also compared with the steel DP. The results show that the recrystallization of the electrical steel can be suppressed at lower annealing temperature. The steel presents favorable motor magnetic and also a compatible strength with the help of solid-solution Nb. Compared with the steel DP, the fatigue resistance of the steel SXRC is preferable. 

为了解决在纹理背景下冷轧硅钢表面缺陷的分割问题,提出了基于局部信息结构张量和活动轮廓模型的硅钢表面缺陷分割方法。将图像的局部信息引入到结构张量中;在结构张量提取的特征空间中,以KL距离作为区域的概率密度相似性度量建立分割图像的活动轮廓模型;采用Split-Bregman数值解法对模型进行求解。运用提出的分割方法对硅钢表面的一些常见缺陷如纵向划伤、横向划伤、异物和孔洞等进行分割实验。实验结果表明,该方法可以准确地分割出硅钢表面缺陷区域,验证了该方法的有效性。 In order to address the segmentation problem for cold rolled silicon steel surface defect based on the texture background,a novel method based on structure tensor and active contour model is proposed.Image local information is introduced to the structure tensor.In the extracted feature space of structure tensor,KL distance is treated as a regional similarity measure of the probability density to establish active contour model for image segmentation.The numerical solution of Split-Bregman is used... 

通过对连退线SF炉内的电加热体的焊接技术进行总结分析,得出焊接时应采用的主要方法,采用本焊接方法可提高电加热体的焊接速度和焊接质量,保证了焊接质量和施工工期。 SF furnace for continuous annealing line heating body welding technology summary,the main method used in welding,welding method by using the electric heater to improve the welding speed and welding quality through the implementation of this method to ensure the welding quality and Construction period. 

【作者】 杨佳直； ...

本发明公开了一种硅钢片漆，该硅钢片漆采用特定的聚酰胺酰亚胺乳液制备，通过使偏苯三酸酐与组合形式的双端氨基化合物反应，添加三乙胺进一步提升反应进行的程度，并赋予整体更好的柔性和韧性，而磷酸三丁酯能够进一步通过物理改性改善体系的韧性，之后蒸出全部的有机溶剂，并添加一定量的水溶性有机溶剂，然后加入组合形式的活化剂，混合，再滴入水，形成稳定的乳液，最后添加双马来酰亚胺封端剩余的活性基团，该硅钢片漆不仅可以采用水作为主体溶剂，提升了环保型，而且还兼具耐高温、高粘结强度、电气性能强等优点，并有好的环境抗性与施工性能。

本实用新型涉及变压器材料检测技术领域，具体为一种硅钢片检测装置，包括材料检测装置主体，材料检测装置主体包括相互连接的铁损测试仪主机及磁导计，磁导计的顶端设置有清洁机构，清洁机构包括固定盒、拉块及刷块，固定盒固接于磁导计上，拉块插设于固定盒中、能够在固定盒中上下移动，固定盒的内部底面上及拉块的底端上分别安装有刷块，铁损测试仪主机上还设有束线机构。本实用新型使得用户可在检测硅钢片前，对硅钢片两面沾染的灰尘污渍进行擦拭，避免灰尘污渍影响对硅钢片的测定结果，可方便地对刷块进行清洁更换，使得用户可方便地对电源线和导线进行收纳。