测试了高强无取向电工钢的S-N曲线,并借助光学显微镜、扫描电子显微镜、透射电子显微镜分析了实验钢组织,疲劳断口形貌和位错结构。结果表明:室温条件下,频率为20Hz,应力比R为0.1,循环10~7周次时,实验钢的疲劳强度为360MPa,疲劳裂纹萌生于实验钢的次表面,裂纹萌生点附近有沿晶开裂现象,疲劳裂纹扩展区域有解理台阶与疲劳条纹,瞬间断裂区是韧性断裂,有大量韧窝。实验钢在循环应力作用下基体中产生了大量位错,并有驻留滑移带终止在晶界位置。 The S-N curve of a high strength non-oriented electrical steel was tested.The microstructure and fatigue fracture morphology and dislocation were analyzed by optical microscope,scanning electron microscope,transmission electron microscope.The results showed that:at room temperature and the frequency of 20 Hz and the stress ratio Rof 0.1,the fatigue strength of the experimental steel was 360 MPa when the cycle was 10~7 cycles.The fatigue crack initiation at the surface of the steel and the interg... 

热轧轧制工艺对产品性能和轧制稳定性影响很大,对中低牌号无取向电工钢,当在两相区轧制时,热轧塑性明显降低,板形变坏,易出现边裂等情况。以50W1000为例,通过对其变形抗力进行研究,得出把两相区控制在F4与F5之间为最佳轧制工艺的结论。在此基础上制定了一套较为合理的热轧工艺制度。采用新的轧制工艺后,50W1000热轧精轧的稳定性明显改善,热轧产品合格率由开发初期的40%左右提高到95%以上。 The hot rolling process has great influence on product′s performance and rolling stability.For the low medium grade non-oriented electrical steel,when non-oriented electrical steel is rolled in tow phase region,the hot rolling plasticity reduces obviously,the shape of strip goes bad and easily to crack at the edge.The deformation resistance of 50W1000 steel was investigated.The results show that the optimal rolling process is to control the two phase region between F4 and F5.Based on the results... 

本发明公开了一种电工钢片磁致伸缩模型的建模方法，包括：测量不同旋转磁场下电工钢片磁致伸缩对称蝴蝶曲线εk；对所测量的对称蝴蝶曲线进行辨识，构建磁致伸缩蝴蝶曲线εk的Everett函数数据库；将输入的矢量磁场B波形用旋转磁场形状参数Bmax,最大值方向的方向角θ和椭圆长短轴的长度比λ拟合，得到拟合后结果；通过线性插值法在磁致伸缩Everett函数数据库中进行插值，获得拟合后结果所对应的磁致伸缩Everett函数值Ek；根据Everett函数值Ek计算得出对应的磁致伸缩蝴蝶曲线εk。应用本发明实施例，不仅可以描述矢量磁致伸缩特性，还可以通过计算估算出旋转磁场下的瞬态磁致伸缩。此外，还能够考虑磁致伸缩的各向异性特性。

本发明属于双取向硅钢技术领域，公开了一种双取向硅钢薄带及其制备方法，包括：选取具有Si、Al、Mn、C和Fe，且具有一定取向的硅钢薄带；将其进行冷轧；将冷轧板在N2、H2保护气氛中进行退火处理。本发明通过合理的轧制和退火工艺搭配，使具有Goss取向的硅钢薄带转变为具有旋转立方取向的硅钢薄带，将单取向硅钢转变为双取向硅钢。本发明具有工艺简单和便于利用钢铁企业现有设备的特点，所制备的双取向硅钢薄带具有双向铁损低和磁感高的性能。本发明制备的双取向硅钢薄带在与轧向成45°的两个方向上具有优异的双向磁性能，解决了现有双取向硅钢薄带的制备工艺复杂、设备要求高、不利于工业生产的问题。

【作者】 谌剑； ...

本实用新型公开了一种用于硅钢绝缘涂料生产的吸尘装置，包括底板、支撑平台和集尘箱，所述底板底端四角处通过螺栓连接固定有可制动万向轮，所述底板上端四角处焊接有导向套。有益效果在于：本实用新型通过设置真空泵、集尘箱、万向吸气臂、吸尘罩以及活性炭滤网，可在硅钢绝缘涂料生产过程中将逸出的物料粉尘进行有效的收集，确保硅钢绝缘涂料生产环境的洁净，有利于人体健康，通过设置电机、螺套、螺杆、导向柱以及导向套，可实现根据实际吸尘的需要实现装置高度的便捷调节，提高了装置的实用性。

聚焦无取向硅钢产品标准,从电磁性能、表面性能、机械性能以及尺寸公差与边部质量等维度对国际标准IEC、EN、JIS、ASTM以及国标GB进行了分析研究。分析得出,各类标准在电磁性能方面要求基本一致;ASTM标准的机械性能要求有别于其他几个标准。 In this paper,non-oriented silicon steel standards of EN,JIS,GB and ASTM were compared and analyzed. It is showed that,all types of standards in electromagnetic performance requirements are basically the same. Surface properties in ASTM standard are expressed in the most detailed. The mechanical properties requirements of the standards,except for ASTM,are basically the same. 

本发明涉及硅钢带的制备技术领域，具体公开一种软磁性高硅钢极薄带及其制备方法。所述软磁性高硅钢极薄带的制备方法包括熔炼、包覆CaF2和TiB2偶合涂层、微波热压成型、酸洗、渗氮、一次退火、三道热轧、二次退火、三次温轧和三次退火。本发明提供的软磁性高硅钢极薄带的制备方法制得的软磁性高硅钢极薄带的晶粒细化程度高、组织均匀，改变了传统的相析出路径，有效消除了有序相的形成，使其具有优异的延展性，并具备更高的磁感和更低的铁损。

研究稀土Ce的添加对含Sn高磁感无取向电工钢磁性能及夹杂物的影响。对比分析了两种成分钢的磁性能以及各过程工艺条件下夹杂物种类和分布情况。结果表明,在含Sn高磁感无取向电工钢中加入稀土元素Ce可以粗化夹杂物,提高成品晶粒的均匀性,有效降低铁损;同时Ce的添加不影响Sn元素提高磁感的效果,磁感保持不变。 Effect of Ce on magnetic properties and inclusion of Sn-bearing high permeability non-oriented electrical steel was investigated. A comparative analysis of the magnetic properties and the types and distributions of inclusion in the two sheets with different composition shows that the addition of Ce to the Sn-bearing high permeability non-oriented electrical steel can coarse the inclusion,improve the homogeneity of the finished grain and effectively decrease the core loss. Also,the addition of Ce... 

本实用新型公开了一种取向硅钢加工用的酸洗除杂装置，包括装置主体，所述装置主体一侧固定安装有进气机构，所述装置主体内部活动安装有硅钢片，所述装置主体上方活动安装有一号转杆，所述一号转杆一侧活动安装有二号转杆，所述一号转杆和所述二号转杆外侧表面均安装有柔性吸附套筒，所述一号转杆和所述二号转杆一侧均活动安装有刮杆，所述装置主体前表面固定嵌入安装有一号进气管。本实用新型所述的一种取向硅钢加工用的酸洗除杂装置，能够在取向硅钢酸洗时，加快取向硅钢上方和下方的溶液流通，使酸洗装置内部的溶液浓度保持均匀，且使取向硅钢在酸洗后表面的溶液能快速风干，避免酸溶液过度与取向硅钢发生反应，以免对取向硅钢造成损伤。

本发明涉及到一种铸铝转子硅钢片及采用该硅钢片的转子，该铸铝转子硅钢片包括圆形板片状本体，本体中心开设有转轴孔，本体上还以转轴孔为中心周向均布有多个铸铝孔，本体外缘设置有与铸铝孔一一对应的凹槽，本体两侧侧面均涂覆有绝缘层。采用上述硅钢片的转子包括转轴，所述转轴上套接有铁芯，该铁芯由大量上述的硅钢片层层叠压而成，每片硅钢片上的铸铝孔均相互正对，在铁芯上形成多条贯穿铁芯的通孔，每条通孔内设置有一条导条，铁芯两端分别连接有导电端环，各导条的两端分别伸出通孔与导电端环电性连接，各导条对两导电端环的拉力使两导电端环紧压在铁芯两端。

本发明公开了一种风电磁钢粘接包角专用装置，其包括：工作台；磁钢限位台，其设置于所述工作台上，所述磁钢限位台上设置有多个挡块，用以在风电磁钢放置于磁钢限位台上时，围挡风电磁钢有包角粘附的左右侧面及无包角粘附的后侧面；三个抵压机构，三个抵压机构设置于工作台上，且分别位于磁钢限位台左右两侧及正前方，所述抵压机构包括伸缩元件和连接于伸缩元件上的压块，用以在粘附有包角的风电磁钢放置于磁钢限位台上时，伸缩元件驱动压块抵压住包角，使包角粘实。本发明能够将风电磁钢和包角快速定位粘接，节约人力，保证产品粘接的一致性。