硅钢资料

研究了应用电感耦合等离子体质谱(ICP-MS)同时测定硅钢中痕量铝、钼、钒、钛、铌元素的分析方法。通过条件试验对测量参数进行了优化,确定RF功率1 400 W,泵速30rpm,采样深度140,雾化压力0.90。样品采用硝酸分解,以Be、Y混合内标校正了测量过程中高基体引起的信号漂移。根据测量时存在的质谱干扰情况,选择同位素27 Al、98 Mo、51 V、47 Ti和93 Nb作为测定同位素,同时通过调节仪器参数使得双电荷离子和氧化物离子的产率最低,以减少其带来的干扰。采用基体匹配法配制校准溶液,以标准加入法建立工作曲线,并扣除试剂空白。该方法各元素的测定下限均可达到1μg/g。用于硅钢标准样品的测定,所得结果与参考值完全吻合,各元素的RSD小于5.2%。 A method for the determination of trace aluminum,molybdenum,vanadium,titanium and niobium in silicon steel by inductively coupled plasma mass spectrometry(ICP-MS) was described.A series of single parameter condition experiment was conducted.The optimized operation parameters with RF power 1 400 W,turbo pump rate 30 rpm,sampling depth 140 and nebulizer pressure 0.90 were obtained.The samples were dissolved by HNO3,and the Be and Y mixing internal standard were used to eliminate the signal drift c... 

本发明涉及一种三相变压器铁芯硅钢片叠装设备，包括工作台、传输装置和移动装置，所述的工作台的上端面由左至右依次设置有传输装置和移动装置，所述的移动装置包括匚形板、一号矩形通槽、转动杆、圆头板、移动架、限位架、水平板、夹紧架和挤压架，本发明无需通过人工对变压器铁芯硅钢片进行单个叠装，避免了传统的人工叠装造成的操作繁琐和增大劳动力的问题，本发明能够对叠装之后的变压器铁芯硅钢片进行快速整理限位，从而保证了叠装之后的变压器铁芯硅钢片的整齐度，本发明能够对叠装之后的变压器铁芯硅钢片进行快速压紧，从而提高了压紧效果。

本发明提供退火隔离剂的制备方法以及退火隔离剂和方向性电磁钢板。由该方法得到的退火隔离剂纯度高、分散性以及密接强度优异，可以在方向性电磁钢板表面形成均匀致密的镁橄榄石层。退火隔离剂的制备方法，其包括：工序(1)：将氧化镁和铵盐溶液混合并反应，制备镁盐溶液和氨，然后使精制的镁盐溶液与氨反应而得到氢氧化镁；工序(2)：将得到的氢氧化镁的一部分在155～230℃下高温熟化，并且将得到的氢氧化镁的另一部分在10～100℃下低温熟化；工序(3)：将在上述各条件下熟化的氢氧化镁混合、烧成，得到氧化镁用于退火隔离剂。

采用EBSD技术研究了有、无拉应力作用下无取向硅钢在晶粒长大过程中织构转变及晶界变化的规律。结果表明:在晶粒生长期间,无应力作用下的硅钢中,{111}〈112〉,{111}〈110〉织构组分强化,而{100}〈001〉织构组分弱化;与无拉应力作用下的情况相比,施加5MPa的拉应力时,{111}〈112〉,{111}〈110〉织构组分强化的速率下降,{100}〈001〉织构组分变化不明显。对于在晶粒生长期间持续变化的{111}〈112〉,{111}〈110〉和{100}〈001〉织构组分而言,虽然有、无拉应力作用下硅钢的{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率均下降,而{100}〈001〉织构组分的高取向差角度晶界频率则上升,但当有拉应力作用后,{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率下降的速率变小,{100}〈001〉织构组分的高取向差角度晶界频率上升的速率稍有变小。通过对无取向硅钢在晶粒长大过程中织构转变及晶界变化规律的研究,分析了合金原子在晶界的偏聚行为。 The rules of texture and grain boundary transformation in the nonoriented silicon steel under applied stress or without applied stress during grain growth were investigated by EBSD.The results show that the {111}〈112〉 and {111}〈110〉 components in the nonoriented silicon steel without stress are strengthened during grain growth whereas {100}〈001〉 component is weakened,but the growth rate of {111}〈112〉 and {111}〈110〉 component decreases,while the area fraction of {100}〈001〉 component doesn’t chang... 

本实用新型属于硅钢技术领域，具体的说是一种硅钢前处理高液回流装置，包括机体；所述机体的侧端固接有一号导管；所述一号导管上安装有二号导管；所述机体的顶端固接有连接管；所述连接管上安装有入泡管；所述二号导管的内侧壁固接有电机；所述电机的输出端固接有扇叶；所述二号导管的顶端内侧壁固接有定位板；所述定位板的侧端转动连接有旋转叶轮；所述二号导管的底端固接有排泡管；通过一号导管和二号导管的配合可以把溢出的泡沫进行导向，通过扇叶和旋转叶轮的配合可以使泡沫快速流动，再通过排泡管排出进入机体的内部，可以使泡沫循环使用，避免泡沫的溢流造成环境的污染及碱液的浪费。

采用双辊连铸工艺制备了硅的质量分数分别为0.5%,1.0%,3.0%,4.5%的硅钢薄带,用光学显微镜观察其组织,并研究了后处理工艺对薄带组织和性能的影响。结果表明:硅含量为0.5%和1.0%的薄带适合采用一次冷轧+850～950℃退火的后处理工艺,而硅含量在3.0%以上的薄带适合采用二次冷轧+950℃退火的后处理工艺;硅含量为3.0%和4.5%的薄带在冷轧并950℃退火后,其磁性能最佳,铁芯损耗约为4.30 W·kg^-1,磁感应强度约为1.68T。 Silicon steel thin strips with silicon content of 0.5wt%,1.0wt%,3.0wt%and 4.5wt%were prepared by twin-roll continuous casting process,and the microstructure of the strips were observed by means of optical microscopy,and on the basis,the effect of post-treatment process on microstructure and properties of the strips was studied.The results show that the post-treatment process of one-time cold rolling and annealing between 850—950℃was suitable for the strips with silicon content of 0.5wt%and 1.0wt... 

研究了CSP流程试制50W270高牌号无取向硅钢热轧→常化→冷轧→退火过程中织构的演变.利用电子背散射衍射技术对全流程织构进行测量和分析.发现热轧板织构在厚度方向上存在较大差异,表层主要为铜型、黄铜和高斯织构,1/4层存在微弱的高斯织构和旋转立方织构,中心层以γ纤维织构和旋转立方织构为主,还含有较弱的α纤维织构.与热轧板相比,常化板表层和1/4层织构变化不大,中心层旋转立方织构和α纤维织构增强.冷轧板各层均具有α纤维织构和γ纤维织构.与冷轧板相比,成品板各层中α纤维织构基本消失,还出现了立方织构和高斯织构. This article focuses on texture evolution in 50W270 high-brand non-oriented silicon steel produced by CSP in hot rolling,normalizing,cold rolling,and annealing processes.The texture in the whole process was measured and analyzed by electron back-scatter diffraction.It is found that the texture along the thickness direction in hot-rolled strips changes obviously;there are mainly copper,brass,and Goss textures in the surface layer;the 1/4 layer has weak Goss texture and rotating cube texture;γ-fib... 

本发明公开了一种改善高牌号无取向硅钢表面色差缺陷的方法，属于冷轧卷板表面质量改进技术领域。所述方法为：将连铸坯依次进行热轧、常化、酸洗、单机架轧制和连续退火工序，其中按重量百分数计，所述的连铸坯含有如下成分：C＜0.003%、Si1.6~2.0%、Mn0.35~0.65%、Al0.35~0.65%、P＜0.02%、S＜0.0025%、余量为Fe和其他不可避免的杂质元素，所有成分合计100%；其中热轧工序的卷取温度为620~640℃。本发明所述方法能够降低带钢表面氧化铁厚度并改变带钢表面氧化铁结构，改善高牌号无取向硅钢表面色差缺陷。

本实用新型涉及一种便捷型铁芯硅钢片组装系统。该便捷型铁芯硅钢片组装系统包括硅钢片叠放装置，硅钢片叠放装置包括固定座，固定座上通过轴承转动装配有齿圈，固定座上固定连接有与齿圈同轴的固定盘，固定盘的中心设有中心孔，固定盘上设有六个沿固定盘径向延伸的滑槽，六个滑槽沿固定盘周向均匀分布，每个滑槽内分别滑动装配有滑块，齿圈的上侧面设有上螺纹，滑槽的下侧面设有与上螺纹相匹配的下螺纹，滑块的内端设有定位板，定位板的外侧面上设有用于与硅钢片中心孔孔壁上的割槽相匹配的定位条。相比于现有技术，本实用新型能够对硅钢片进行定位，从而确保各片硅钢片的中心孔以及割槽相对应，提高了硅钢片叠放效率，从而提高了生产效率。

通过对取向硅钢进行脉冲磁场退火实验,发现在相同的退火时间(6.0 min)内,低于1 T的脉冲磁场可以在一定程度上提高取向硅钢的磁感(B8),而高于1 T的脉冲磁场则会使取向硅钢的磁性能急剧恶化.同时发现,脉冲直流电加热方式会使取向硅钢的磁性能恶化.研究表明,脉冲磁场退火有望成为一种调控材料微观结构的有效手段. We have carried out experiments of annealing by pulse magnetic field.The results show that a pulse magnetic field with intensity lower than 1 T can promote magnetic induction density(B8) of grain-oriented silicon steel,while the magnetic properties deteriorate sharply when intensity is higher than 1 T.It has also been found that heating by using pulse direct current can cause the magnetic properties to deteriorate,in contrast to the traditional heating using resistance furnace.Our research shows... 

【摘要】 <正>编号:2012016获奖等级:特等完成单位:...

介绍了烟气余热利用系统的工艺流程及控制思想,结合该系统在钢厂硅钢连续退火机组中的应用实践,估算出烟气余热利用系统每年可节约蒸汽5 040 t,经济效益良好,同时分析了该系统存在的问题及对策。 Introduced a method about the process and control of the application of waste heat system, which had been used into a silicon steel continuous annealing line and profiting a good economic benefit by saving a large number of steam every year, which has been estimated about 5 040 tons, and analyzed the problems and solutions existed in this system.