在Gleeble-3500热/力模拟试验机上对HW600钢进行高温压缩试验,研究在不同试验条件下的变形抗力。试验结果表明:变形温度对变形抗力的影响最为显著,在相同的变形速率下,随着变形温度的升高,变形抗力降低;在同一变形温度下,变形速率增大,变形抗力增加;在同一变形温度、变形速率下,随着变形程度的增加,变形抗力急剧增大,真应变达到0.1后,变形抗力增加趋势变缓。 The high-temperature compression test is done for HW600 steel with Gleeble-3500 thermal simulation testing machine to research its resistance to deformation under different test conditions.It is showed from result that deformation temperature has greatest effect on the resistance,and along with the temperature getting higher the resistance lowered under same deformation rate;the resistance increases along with deformation rate getting greater under same temperature;and under same deformation tem... 

本实用新型公开了一种电工钢表面清洗装置，包括机架、第一传送链和叶片，所述机架的上端固定有顶板，且顶板的内部连接有加料杆，并且加料杆的上端内部设置有固定帽，所述顶板的侧面固定有第一电动机，且第一电动机的一端连接有丝杆，所述丝杆的外侧设置有电动推杆，所述第二转动轴的侧面连接有第二传送链，所述顶板的下端连接有连接架，且连接架的内部设置有第三电动机，所述连接架的底部设置有第二清洁杆，所述机架的内部开设有固定孔。该电工钢表面清洗装置，往加料杆的内部加入清洁液，清洁液会被加料干底部的海绵吸收，当料与加料杆的底部摩擦时，清洁液就会附着在料的表面，从而实现定量的往装置的内部加入清洁液。

本发明涉及一种防止低温加热取向硅钢热轧边裂的方法，包括：1)控制取向硅钢铸坯进入加热炉前的表面温度；2)控制加热段各段炉气温度；3)二加热段采用加速加热；4)控制总加热时间；5)控制出炉温度；6)控制精轧道次及侧压量；7)控制精轧道次及终轧温度；8)精轧前对钢带边部进行加热补偿。本发明通过合理制定取向硅钢的加热温度、加热时间和轧制工艺制度，避免或消除了低温加热取向硅钢热轧边裂问题。

利用EBSD技术研究了电工钢中不同的柱状晶尺寸及退火工艺下{100}织构的演变规律。结果表明,初始晶粒尺寸的影响最显著。细小柱状晶热轧后经过常化处理,组织已均匀,但中心层有强{100}织构。粗大柱状晶中{100}织构的遗传性强,常化及中间退火后,中心层仍有粗大的以{100}取向为主的晶粒;脱碳退火后才能完成组织均匀化和织构梯度的弱化。常化时的升温速度也对织构演变存在影响,低的升温速度有利于{100}织构的保留,但升温速度的影响没有初始晶粒尺寸及退火次数的影响显著。细小柱状晶样品经过热轧及三次退火工艺适合制备取向电工钢。 Evolution of {100} texture of different columnar grains and annealing process was investigated in electrical steels with the help of EBSD technique.The results show that the effect of initial grain size is the strongest.The initial fine-grained specimen shows uniform microstructure after the normalizing process,while {100} grains appear preferentially in the central layer of sheets.The heredity of {100} texture in the initial coarse-grained specimen is more significant.{100} mainly-oriented coar... 

广泛应用于电子电力行业的取向硅钢材料的磁性能与其晶体取向密切关联，对取向硅钢晶体衍射花样的研究非常重要.采用理论计算的方式研究了取向硅钢的晶体衍射花样特征，并绘制了取向硅钢的高斯织构理论极图、理论单晶透射电子衍射斑点花样和理论电子背散射衍射(Electron backscatter diffraction, EBSD)菊池花样.取向硅钢理论单晶衍射花样不仅可以为以后标定样品实测晶体衍射花样提供一种简单快捷的方法，也可以为样品检测提供一种标准.这种研究方法不仅限于取向硅钢，也被期待应用于其他材料晶体衍射花样研究. The magnetic properties of oriented silicon steels which are widely used in electronic and power industries are closely related to their crystal orientations, so it is very important to study the crystal diffraction patterns of oriented silicon steels. The characteristics of crystal diffraction patterns of oriented silicon steels are studied by means of theoretical calculation. The theoretical pole figures, theoretical single crystal transmitted electron diffraction patterns and theoretical elec... 

采用轧制法制备出具有低铁损高磁感0.23mm厚6.4%(质量分数)Si高硅钢。沿轧制方向的最终磁性能为B8=1.474 T,B50=1.714 T;P10/50=0.30W/kg,P15/50=0.88W/kg。利用X射线衍射及背散射电子衍射(EBSD)技术分析了高硅钢在轧制及退火过程中的织构演变过程。结果表明,通过采用大压下率热轧,确保热轧板次表层中产生更多的高斯织构,随后进行遗传;温轧板中粗大的晶粒有利于冷轧剪切带的形成;冷轧板经脱碳退火后生成强{210}〈001〉织构及次表层较强的高斯织构是在轧向上获得高磁感的原因,归因于其在{111}〈112〉冷轧形变晶粒内的剪切带优先形核并长大;最终退火后虽出现了随机取向,但以{310}〈001〉织构为代表的η织构得以保留并且增强,进一步提高了磁感。随着退火温度的升高及保温时间的延长,高硅钢薄板晶粒尺寸不断增大,铁损明显降低。 6.4wt%Si high silicon steel sheets(0.23mm thick)with low iron loss and high magnetic induction were successfully produced by rolling process.The final magnetic properties along the rolling direction(RD) were:B8=1.474T,B50=1.714T;P10/50=0.30 W/kg,P15/50=0.88 W/kg.The texture evolution during rolling and annealing was investigated by means of X-ray diffraction and electron backscatter diffraction(EBSD).It was found that more Goss textures formed in the subsurface of hot rolled plates by using larg... 

冷轧无取向硅钢是高技术含量、高附加值产品,工艺复杂,生产周期长,过程控制难度大,被誉为钢铁产品中的\"工艺品\"。热轧生产工艺又是无取向硅钢生产的重中之重,直接决定了硅钢的铁损和电磁性等多项指标。 Cold rolled non-oriented silicon steel is high technology content 、high added value product. Its process is complex, its production cycle is of length, and its process control is difficult, which is known as the iron and steel products \" Arts and crafts\". Hot rolling production process is the top priority of non-oriented silicon steel, which directly determines iron loss of the silicon steel and electromagnetic property,as well as other many index. 

通过制备磷酸二氢铝硅钢涂层,研究了氧化锌对无铬涂层耐盐雾性能、电化学性能和附着性的影响。结果表明,硅钢表面涂层含有4.0%的氧化锌时,涂层具有最高的耐腐蚀性能和电化学性能,而且其致密表面最为平整,没有裂纹出现。 The effects of ZnO on the salt spray resistance property, electrochemical performance and adhesiveness of silicon steel insulating coating were studied. The results show that the best corrosion resistance and electrochemical properties can be obtained when the coating contains 4.0% oxide zinc, and the dense surface is smooth without cracks. 

本实用新型公开了一种具有柔性压料机构的飞剪式硅钢剪床，压料机构包括对称设置的支板和侧板，两个侧板位于两个支板之间，且两个侧板位于传送系统传送带顶部的左右两侧，两个支板通过回位组件在底板的顶部进行转动，本实用新型涉及剪床技术领域。该具有柔性压料机构的飞剪式硅钢剪床，通过设置压料机构，当带状硅钢发生跑偏时，其侧边会对一侧的侧板施压，受压的侧板对其连接的弹簧进行压缩，弹簧弹力抵消硅钢跑偏的侧向力，通过侧板推动硅钢复位，且压辊会对硅钢进行平复压实，从而避免了带状硅钢因跑偏而造成剪切尺寸不合格，通过上述结构的组合解决了现有的硬性压料装置容易导致带状硅钢在传送时发生形变的问题。

本发明公开了一种去除无取向硅钢夹杂物的方法，在中间包预设脉冲电流装置，将所述脉冲电流装置的正极连接在上挡渣堰处，负极连接在下导流坝处，在钢水浇注过程中，施加电脉冲处理即可。本发明基于中间包钢水流场的研究，在中间包上挡渣堰和下导流坝之间施加脉冲电场，扩大了脉冲电场作用的钢水区域，且随着钢水流场运动，流场与脉冲电场相互作用，使得细小的SiO2和MnS夹杂物在钢水运动过程中更有效的碰撞、聚集、长大，并有充足的时间充分上浮，从而达到有效去除铸坯夹杂物，降低铸坯中S和O含量，大幅提高钢水纯净度，进而提高硅钢成品磁性能。

本发明涉及电机技术领域，具体涉及一种具有低应力隔磁桥的硅钢片和电机转子。包括硅钢片、开设在硅钢片上的若干个磁钢槽组和永磁体，若干个磁钢槽组沿所述硅钢片周向分布，每个磁钢槽组均至少包括一对沿径向对称分布的磁钢槽，永磁体嵌设于磁钢槽内，磁钢槽朝向硅钢片内侧的一端设有空腔，一对磁钢槽的空腔之间通过隔磁桥隔离，隔磁桥的空腔上壁面与空腔侧壁面之间通过第一椭圆弧过渡连接，隔磁桥的空腔下壁面与空腔侧壁面之间通过第二椭圆弧过渡连接。有效降低该处隔磁桥在拐角处所受应力，进而提高该隔磁桥的强度，避免磁钢和铁芯产生形变而断裂。

本发明揭示了一种超低铁损无取向硅钢及其生产方法，生产方法包括：依次采用铁水脱硫、转炉冶炼、RH炉精炼进行冶钢，最终所得钢水化学成分以质量百分比计为：C≤0.003％、Si：2.8～3.4％、Mn：0.1～0.5％、Al：0.6～1.3％、S≤0.0015％、N≤0.0020％、P≤0.03％、Ti≤0.003％、V≤0.003％、Nb≤0.003％，且同时满足3.80％≤Si+Al≤4.15％，其余为Fe以及不可避免的杂质；将冶炼所得钢水连铸成连铸坯；对连铸坯加热后经过多道次轧制得到热轧卷板；对热轧卷板的两侧边部进行剪切；常化酸洗，常化温度为900～930℃，常化时间为30～60s；经多道次冷轧成厚度为0.35～0.5mm的无取向硅钢，其中，第一道次冷轧时的压下率≥37％，轧制速率为70～180m/min。本发明制备的无取向硅钢具有超低铁损，而且冷轧时不易断带。