硅钢资料

利用光学显微镜、TEM和EBSD研究了退火温度对双辊连铸无取向硅钢再结晶组织的影响。结果表明,900℃退火后组织分布不均匀,有大量带状组织,平均晶粒尺寸29.5μm。提高退火温度,晶粒尺寸增大,组织均匀化程度增加,1050℃退火时,带状组织基本消失,平均晶粒尺寸42.2μm。 Effect of annealing temperature on recrystallization microstructure of non-oriented electrical steel produced by twin-roll casting process was investigated using OM,TEM and EBSD.The results show that the recrystallization microstructure is uneven because of many banded grains existing,average grain size is 29.5 μm.With annealing temperature increasing,the recrystallization grain size increases,microstructure becomes more homogeneous.When 1050 ℃ annealing,the banded structure almost disappear and... 

介绍在取向硅钢生产中抑制剂的作用以及多元抑制剂的机理和应用情况,分析多元抑制剂方案中各种元素对高磁感取向硅钢性能的影响,并根据生产实践提出了进一步研究的方向. The role of an inhibitor in the production of grain oriented silicon steel,and the mechanism of multiplex inhibitor in the production are described in the present article.In addition,the influence of various elements in the multiplex inhibitor on the performance of grain oriented silicon steel with high magnetic induction is elucidated.Further work needed in this research is also indicated. 

依据GB/T 15616—2008《金属及合金的电子探针定量分析方法》,采用电子探针波谱仪对某W600硅钢中的硅含量进行了定量测定,对影响其定量测定结果的不确定度分量进行了分析,并对不确定度的各个分量进行了计算和合成,最后给出了硅钢中硅含量测定结果的不确定度报告:该硅钢中的硅含量(质量分数)为1.50%,扩展不确定度U=0.20%,取包含因子k=2。 According to GB/T 15616-2008\"Quantitative Method for Electron Prohe Microanalysis of Metals and Alloys\",the quantitative results of Si content in some W600 silicon steel was measured hy EPMA-WDS.The uncertainty components which might affect the measurement results were considered,calculated and synthesized. Finally the uncertainty result for the quantitative value of Si content in the silicon steel was got.The mass content of Si was 1.50%,and expanded uncertainty U=0.20%under the condition of co... 

本实用新型涉及具有搅拌器的装置领域。尤其涉及硅钢绝缘涂层液循环罐，包括罐体，罐体的顶部设有进液口，罐体的侧壁上设有出液口，罐体上端设有盖板，罐体的盖板上设有涡轮室，罐体与涡轮室上贯穿有竖直的中空轴，涡轮室的顶部设有热水口，涡轮室内设有涡轮叶片，涡轮叶片固定在中空轴上，涡轮叶片与罐体上端之间的中空轴上贯穿有流水口，中空轴上设有若干侧管，侧管位于罐体内，所述侧管的两端与中空轴连通，中空轴的内侧封堵有隔板，侧管的两端分别位于隔板的上侧与下侧，中空轴与罐本体以及中空轴与上空腔的结合部均设有密封圈。从而本实用新型可实现对硅钢绝缘涂层液进行均匀加热。

本实用新型公开了一种变压器铁芯硅钢片叠装对齐工装，包括叠装平台、定位板、推齐板和下压板；定位板和推齐板分别位于叠装平台的两侧，下压板位于叠装平台的上方；定位板用于对铁芯长度或宽度侧进行定位；推齐板平推铁芯使各硅钢片抵靠定位板而对齐；下压板下压铁芯使各硅钢片叠装紧密。本实用新型提供的一种变压器铁芯硅钢片叠装对齐工装，能够提高铁芯生产精度，并提高硅钢片叠装效率。

本实用新型涉及一种摩托车点火器线圈用硅钢片，包括E型件和I型件，所述E型件和I型件可组合成日字形；所述E型件包括竖边和设置在竖边三个横边，所述竖边与三个横边接触的位置设置孔眼；所述孔眼内径从为变径结构；位于E型件正面设置散热线槽，所述散热线槽一端与孔眼贯通，另一端指向凸部；位于E型件背面在散热线槽正对位置设置外凸线，所述I型件一侧设置与凸部匹配的凹部，在所述凹部之间凸台；所述凸台与凹台重叠；在凸台与凹部之间设置凸棱，所述凸棱位于I型件外侧。本实用新型设计新颖，改进巧妙，由于E型件具有弧形边可以有利于拾取，方便工作操作，同时采用采用接触的方式接触，增加了组合体的稳定性。

研究了无取向硅钢钙处理前后夹杂物的行为,重点考察了钙处理前后夹杂物的成分、类型、形貌和尺寸研究的变化情况,为实际生产中无取向硅钢的钙处理提供理论指导。试验发现:钙处理前夹杂物主要以Al2O3、Al2O3-MgO为主,且在夹杂物表面有AlN析出,钙处理后夹杂物以Al2O3-MgO-CaS-CaO系复合夹杂物为主,还含有少量的SiO2或AlN;钙处理前后,夹杂物形貌由多边形或不规则形逐渐向球形或近似球形转变,并且夹杂物尺寸不断增大;钙处理前后,含钙夹杂物的比例发生突变,由10%增大到74.5%,且随着钙处理时间的延长,含钙夹杂物比例下降,表明钙处理使夹杂物变性后易聚集长大并上浮去除。 Behavior of inclusions before and after calcium treatment in non-oriented silicon steel was researched by investigating changes of compositions,types,shapes and sizes of inclusions before and after calcium treatment,for the purpose of providing theoretical guidance for calcium treatment of non-oriented silicon steel in actual situation. Results indicated that Al2O3 and Al2O3-MgO were main types of inclusions before calcium treatment,sometimes AlN maybe precipitate in the outer of inclusions. Al2... 

一种硅钢生产线上的牵引装置，包含有底座（1）、支架（2）、平移机构（3）、上压板（4）、下托板（5）、气缸（6）、转向辊（7）和对中摄像头（8）；所述的平移机构（3）包含有长条齿轮（14）、齿轮（15）、电机（16）和滚轮轴承（17）；其特征在于：所述的齿轮（15）固定在电机（16）的输出轴上，并且与长条齿轮（14）啮合；使得平移机构（3）可以由电机（16）驱动在导轨（10）上左右滑动。本发明通过气缸（6）驱动上压板（4）和下托板（5）夹紧钢带（9），由平移机构（3）带动钢带（9）进行左右平移，避免了原先夹送辊刮伤钢带（9）表面涂层，减少了带头的浪费。

研究稀土Ce的添加对含Sn高磁感无取向电工钢磁性能及夹杂物的影响。对比分析了两种成分钢的磁性能以及各过程工艺条件下夹杂物种类和分布情况。结果表明,在含Sn高磁感无取向电工钢中加入稀土元素Ce可以粗化夹杂物,提高成品晶粒的均匀性,有效降低铁损;同时Ce的添加不影响Sn元素提高磁感的效果,磁感保持不变。 Effect of Ce on magnetic properties and inclusion of Sn-bearing high permeability non-oriented electrical steel was investigated. A comparative analysis of the magnetic properties and the types and distributions of inclusion in the two sheets with different composition shows that the addition of Ce to the Sn-bearing high permeability non-oriented electrical steel can coarse the inclusion,improve the homogeneity of the finished grain and effectively decrease the core loss. Also,the addition of Ce... 

本发明公开了一种低铁损高磁导率无取向电工钢及其生产方法，所述生产方法包括以下步骤：钢水连续浇铸成板坯，板坯经加热炉加热，再经热轧得到热轧板，然后经空冷和水冷后在500～650℃进行卷取；热轧板经常化处理、盐酸酸洗；酸洗后在可逆轧机上进行冷轧；最后经成品退火，退火温度为840～900℃，加热时间为240～500s；然后以不超过3℃/s的冷却速度冷却至500℃以下；涂覆绝缘涂层、固化，后经二次退火，即可得到低铁损高磁导率无取向电工钢，其磁性能满足P1.5/50≤3.50W/kg，μ1.5≥3800Gs/Oe，B5000≥1.76T的要求。

本发明公开了一种带有紧固硅钢带的非晶合金铁心制造方法，包括以下步骤：步骤(1)：切割非晶带材片和紧固硅钢带；步骤(2)：对所述非晶带材片和紧固硅钢带进行套装与成型，每组非晶带材片两端搭接，紧固硅钢带设置于非晶带材片之间，得到成型铁心；步骤(3)：对所述成型铁心进行磁场热处理；步骤(4)：对所述成型铁心进行表面涂封。通过本发明提供的方法生产非晶合金铁心，操作方便、提升非晶合金铁心的结构稳定性，并且进一步降低铁心因磁致伸缩产生的噪声。

本发明公开了一种高磁感取向硅钢实验室轧机一次冷轧方法，包括：1)取样，实验室冷轧材料选取经过常化酸洗后的厚度为2.3mm的取向硅钢试样；2)制样，利用取向硅钢专用剪板机，裁剪试样尺寸为轧向600mm×横向150mm；将试样表层轻涂一层薄薄的轧制油；3)冷轧轧制规程制定，轧前厚度为2.3mm；其中：轧制总道次为6次时轧后厚度为0.35mm，轧制总道次为7次时轧后厚度为0.27mm，轧制总道次为8次时轧后厚度为0.23mm。本发明的目的是提供一种高磁感取向硅钢实验室轧机一次冷轧方法，为工业试制提供一定的技术参考，以及后续工艺研究提供了更加可靠的试样和条件。