本文研究了丙烯酸树脂含量对以Al(H2PO4)3为基料的无铬无取向硅钢绝缘涂层各项性能的影响.用盐雾实验、动电位极化及交流阻抗等试验手段研究了不同树脂含量对硅钢绝缘涂层的耐盐雾性能和电化学行为的影响,同时采用SEM对涂层的表面形貌和附着性进行研究.结果表明,树脂含量为19.9~29.4%时,涂层的耐蚀性和附着性最好;树脂含量过多时,涂层的耐蚀性和附着性均较差. This paper studies the influence of acrylic resin on the performance of insulating coating of aluminum dihydrogen phosphate on chromium-free non-oriented silicon steel.Salt spray experiment,potentiodynamic polarization and electrochemical impedance spectroscopy were used to study the influence of acrylic resin content on the salt spray resistance and electrochemical behavior of the insulation coating of nonoriented silicon steel.The surface morphologys and adhesion of coating were tested by SEM.... 

采用ZMLMC超高梯度定向凝固装置,研究了5种凝固速率(10、35、80、150和450μm/s)对定向凝固50W600无取向硅钢的固液界面稳定性转变规律和一次、二次枝晶间距的影响。研究结果表明,在特定的温度梯度下,随着凝固速率的增加,定向凝固的固液界面由胞状晶转变为胞状枝晶,再转变为细小的树枝晶。随着凝固速率的增加,定向凝固组织的枝晶形貌逐渐细化,一次和二次枝晶间距逐渐减小,且与冷却速率之间都符合指数关系:λ1=151.73×(G L·R)-0.31,λ2=22.07×(G L·R)-0.44。当冷却速率达到4.275℃/s时,一次、二次枝晶间距分别为112μm、14.1μm。 Under the conditions of certain temperature gradient and different solidification rate,the directional solidification experiment of non-oriented electrical steel 50W600 was carried out.The microstructure of 50W600 steel was also analyzed in different solidification rate.The result shows that the solid/liquid interface of the steel undergoes an evolution from cellular,cellular dendrite and finally to fine dendrite morphologies.The dendrite refines gradually and the distance between dendrites decr... 

本发明公开了一种用于风力发电机定子铁芯扇形硅钢片的保护工装，包括第一防护罩和第二防护罩，第一防护罩、第二防护罩均为扇形罩体，其由弧形底板和两个扇形侧板构成，第一防护罩的两端连接有能够折叠收纳的柔性罩；第一防护罩滑动套设在扇形硅钢的外侧，第二防护罩滑动套设在第一防护罩的外侧。本发明提供的保护工装主要有两个功能，当扇形硅钢片处于运输过程中时，利用第一防护罩、第二防护罩、柔性罩协同配合为其防刮伤防护；当扇形硅钢片装配后，利用第一防护罩内部的冷却散热系统提供散热防护，防止出现高温过热现象；通过这种方式，本发明保护工装满足大规格定子铁芯扇形硅钢片的防护需求。

本发明涉及涂层液技术领域，且公开了取向硅钢绝缘涂层液，其配比为：二氧化硅10‑15%、硼酸5‑8%、磷酸二氢盐2‑5%、金属溶胶20‑25%、氢氧化铝占5‑6%、有机酸处理的复合盐溶液20‑30%、分散剂0.5‑1%，其余为水，采用硅溶胶作为辅助成膜物，粘结力较强，对附着性影响很大。硅溶胶能够很均匀地包裹在被胶结物质的表面，通过自干成膜，保持了很高的常温结合强度；而磷酸盐涂层的固化是通过受热分解，脱水聚合完成的，低温强度差，中温强度高，充分利用了硅溶胶低温的结合强度和磷酸盐中、高温时的结合性能，消除了常规涂层烘烤时容易出现的收缩、起泡现象，阻止了微气孔的形成，提高了涂层的表面光滑度，粘结强度和稳定性同时保持绝缘涂层的光泽、光滑和稳定性。

本发明涉及一种电力变压器取向硅钢片自动化加工系统，包括支撑台、支撑板、传动机构、堆叠机构和调整机构，所述的支撑台上端左右两侧对称设置有支撑板，支撑板相对面设置有传动机构，支撑台上端中部设置有堆叠机构，支撑台上端面上且位于堆叠机构左右两侧对称设置有调整机构；本发明能解决以下问题：本发明通过传动机构对硅钢片前后移动，通过推动支链对硅钢片移位、放置、拿取，增加对硅钢片进行自动化堆叠效果；通过调整机构对硅钢片X方向面和Y方向面进行感应式自动调整；通过堆叠机构对硅钢片二次调整，避免硅钢片发生移动，从而使硅钢片堆叠的更加整齐，并且节约制造成本。

阐述了电工钢在\"双碳\"中的作用,强调了电工钢的生产工艺技术及在减少碳排放、降低能耗中的作用,对下游能效升级带来明显的节能及降碳成果。同时,分析了2021年电工钢的生产运行情况,介绍了电工钢的未来发展,并针对如何减少碳排放以及生产更多的更低铁损、更高磁感的电工钢谈了几点启示。 The effects of electrical steels on carbon peak and carbon neutralization were expounded,especially on the achievements of obvious energy saving and carbon reduction to the downstream energy efficiency upgrading bringing from the production technology of electrical steels and their effects to reducing carbon emission and energy consumption.Meanwhile the production situation of electrical steels in 2021 was analyzed,and the future development of electrical steels was introduced,and some advices w... 

分别采用传统冷轧轧制液和纳米TiO₂的冷轧轧制液,对无取向硅钢板进行了四辊冷轧实验.重点研究两种冷轧轧制液的轧制润滑性能和对轧后硅钢薄带表面质量和耐蚀性能的影响.通过场发射电子显微镜和能谱仪对使用两种轧制液轧后得到的硅钢薄带表面形貌和成分进行了分析.给出了轧制液中TiO₂纳米粒子在轧制过程中的抗磨减摩机理.在轧制载荷较高时,纳米TiO₂轧制液具有优良的轧制润滑性能并能显著改善轧后硅钢薄带的表面质量.同时在高载荷作用下,TiO₂纳米粒子被压入硅钢薄带基体,形成一个滑动系来支撑载荷,从而使润滑膜的耐磨性提高. Non-oriented silicon steel strips were rolled on a four-high cold rolling mill lubricated by a traditional cold rolling liquid and a nano-TiO₂ cold rolling liquid,with emphasis on studying the rolling lubrication performance of both the liquids and their effect on the surface quality and corrosion resisting property of the silicon steel strips.The surface micrograph and composition of the silicon steel strips after being rolled with both the liquids were characterized by field emissio... 

变压器D21硅钢铁芯片采用冲压工艺生产。首先对其工艺进行了分析,确定了冲压方案。对产品进行了排样设计,计算了冲压力,确定了压力中心。然后,设计了单工序落料模具,完成了模具装配图。 D21 silicon steel chips for transformer are produced by stamping.First,its stamping process was analyzed and the scheme of the stamping process was determined.The product layout was designed,the punching pressure was calculated,the pressure center was determined.Then,the blanking die with single procedure was designed,the die assembly drawing was completed. 

结合工业化生产的高效硅钢,进行了RH精炼稀土处理试验研究。针对不同的稀土处理条件,观察了夹杂物的形貌和尺寸分布,探讨了稀土处理后钢中的夹杂物形成、变化规律。结果表明:试验条件下,最佳的稀土合金添加数量为0.6～0.9 kg/t。经过合适的稀土处理后,可以有效抑制尺寸相对较小的、不规则的AlN、MnS复合夹杂生成,促进钢中微细夹杂物的聚合、上浮,钢质纯净度得到明显提高。此时,钢中全氧含量最低,脱硫效果最佳,钢中的夹杂物主要是尺寸相对较大的、近似球形或者椭球形的稀土类夹杂。 Based on the industrial production of non-oriented silicon steel,the experiment on RE treatment during the RH refining process was studied.The morphology and the size distribution were observed for the steel specimens treated with different RE treatment conditions.Further more,the formation and change of inclusions of final steel sheets after RE treatment were discussed.The results show that the suitable RE added amount was 0.6～0.9 kg/t.After the suitable RE treatment,the formation of AlN and Mn... 

1.本外观设计产品的名称：硅钢片。;2.本外观设计产品的用途：多片硅钢片用来共同组成马达的转子的其中一个部件。;3.本外观设计产品的设计要点：在于本外观设计产品的形状。;4.最能表明设计要点的图片或照片：立体图。;

{100}织构因具有两个易磁化方向能够明显的提高磁性能,因此如何在表面获得具有{100}织构一直是无取向电工钢研究焦点。本文主要介绍了获得{100}织构的主要工艺方法及其基本原理,并结合实际生产过程对各工艺方法的优缺点进行了分析;一方面,优化无取向电工钢的成分,降低碳、锰元素含量以避免脱碳退火和真空退火,简化生产工艺;另一方面,调节升温速度、降温速度和退火气氛,使{100}晶面的表面能或弹性应变能最低,制备具有{100}织构柱状晶组织的无取向电工钢是今后的发展方向。 Because { 100} texture has two easy magnetization directions,which can significantly improve magnetization properfies,how to develop { 100} texture is a focus for researchers and manufactures. In the paper,main manufacturing processes and basic principle are introdued,and their advantages and disadvantages in practical production are analyzed. On the one hand,the production process can be simplified by optimizing chemical compositions,such as reducing the content of C and Mn,which can avoid deca... 

本发明涉及低温取向硅钢片制造领域，具体为一种重质硅钢级氧化镁的生产工艺。为提升现有取向硅钢片的表面质量，将工业氧化镁、聚乙烯醇粘结剂和水在不锈钢反应罐中水热合成氢氧化镁，经压滤、煅烧、冷却、气流粉碎、包装产物为重质硅钢级氧化镁。产品具有生产工艺独特、成本较低，能明显提高取向硅钢片的表面质量和增加磁感应强度，降低铁损，提高取向硅钢片的正品率。可针对性在取向硅钢片生产厂家推广使用。