综述了国内外大钢铁企业与研究机构采用获得抑制剂法生产低温高磁感取向硅钢的开发及应用情况,分析了以该法生产高磁感取向硅钢过程中抑制剂的控制技术,包括固有抑制剂组成方案、气态渗氮方式与工艺及高温退火工艺的制定.研究表明,固有抑制剂组成方案的设计思路大体一致,化合物抑制剂以AlN为主、硫化物为辅,同时添加少量Sn,Sb等单元素抑制剂,但组成元素含量存在一定差别;在脱碳退火后用NH3进行非平衡渗氮处理已成为气态渗氮的主要方式,但最佳方式仍未明确,具体选择需依据实际生产条件,相应脱碳及渗氮工艺的控制条件差别较大;高温退火工艺中升温制度差别不大,升温阶段退火气氛中N2含量的选择存在差别.此外,分析了抑制剂控制技术目前存在的关键问题,并指出了进一步的研究方向. The current application and exploitation on production of low-temperature high magnetic induction grain-oriented silicon steel with acquired inhibitor method at both iron and steel enterprises and research institutions in the world are reviewed. The control techniques of inhibitors, which include the composition design for inherent inhibitors, nitriding method and process, and secondary recrystallization annealing, are thoroughly analyzed and proposed. It is indicated that the design ideas for i... 

本实用新型涉及一种硅钢片横剪线用转运系统，包括一暂存组件，所述暂存组件包括一暂存支架，在暂存支架上安装有若干存放条料卷用的凸台；一转运组件，包括一转运底座，该转运底座由第一水平移动机构驱动进行往复移动，在转运底座上安装有一转运支架，所述转运支架由一旋转机构驱动进行转动，且转运支架由第二水平移动机构驱动进行水平移动，在转运支架上安装有一转运托架，所述转运托架由一升降机构驱动上下升降。本实用新型的优点在于：通过暂存组件与转运组件之间的相互配合，实现了条料卷的竖直存放，方便了后续人员选用所需宽度的条料卷，也实现了条料卷的自动流转，有效的降低了人工劳动强度，对于人力资源的消耗也减少了。

本发明揭示了一种无取向硅钢及其生产方法。该无取向硅钢的化学成分：Si:2.95%~3.15%，Al:0.75%~0.95%，Si+2Al:4.6%~4.9%，Mn:0.5%~0.7%，Sn:0.03%~0.04%，Cu≤0.03%，Cr≤0.03%，Ni≤0.03%，Nb≤0.004%，V≤0.004%，Ti≤0.004%，C≤0.0025%，P≤0.015%，S≤0.0015%，N≤0.004%，余量铁；Mn/S≥380，Al/N≥200；无取向硅钢的再结晶晶粒尺寸50~80μm。本发明在保证磁性能的同时，提高了强度，解决了现有技术所存在的磁性能和强度的兼顾问题。

晶界和{100}柱状晶在硅钢生产过程中对织构的遗传和演变有关键作用,因此本文利用晶体塑性有限元方法进行立方和旋转立方取向双晶在晶界不同位向时晶体取向演变的全场模拟。模拟显示,三种晶界位向下,晶界都具有诱发晶内产生S形状形变不均匀和缓解局部形变不均匀区取向转动的特点,立方和旋转立方取向双晶在带有剪切作用的轧制条件下都显示明显的取向稳定性。GB⊥RD(表示晶界垂直于轧向)晶界位向时,旋转立方取向晶粒优先在晶界中心位置发生取向转动,而立方取向则优先在远离晶界的端部发生取向转动。GB⊥TD(表示晶界垂直于横向)的晶界位向下,其晶界阻碍作用最小,双晶内产生的取向漫散度大,织构强度较低;除绕TD转动外,也具有复杂的绕RD、ND的取向转动。GB⊥ND(表示晶界垂直于法向)的晶界位向下,取向转动与GB⊥RD时相近,但有少量取向绕ND转动。 Grain boundaries and initial{100}columnar grains play a key role in the inheritance and evolution of texture in the production of electrical steels.In this paper,the crystal plasticity finite element method was used to simulate the grain orientation evolution of cube and rotated-cube oriented bicrystals when grain boundary was set to different orientations.It was shown that the grain boundary in three grain boundary orientations demonstrated the characteristics of inducing Sshape deformation inh... 

目前高磁感冷轧硅钢生产过程中，采用经验方法确定的乳化液流量设定值往往会造成硅钢产品的磁感性能达不到预期目标，针对此情况，基于轧机轧制机理研究了的乳化液流量数学模型，确定了乳化液流量设定值。实践表明，使用该数学模型输出的乳化液流量设定值，可提高轧制过程中乳化液流量控制精度，从而提高高磁感冷轧硅钢的轧制性能。 In view of the current production process of high magnetically inductive cold-rolled silicon steel, the mathematical model of emulsified fluid flow based on mill rolling mechanism is studied in view of the situation in which the magnetic sensing performance of silicon steel products is often not up to the expected target by using empirical method to determine the emulsified liquid flow setting. Practice shows that the emulsified fluid flow setting value output from this mathematical model improv... 

采用固溶强化、细晶强化和位错强化方法,模拟TSCR流程试开发高强度无取向电工钢,试开发钢的主要合金成分为3%Si、0.83%Al和2.99%Mn。分析热轧、常化、退火后的钢板组织,并针对不同的成品板组织,详尽地分析了相应的力学性能和磁性能。试验电工钢平均晶粒直径为12.37μm时,R p0.2为530 MPa,R m为618 MPa;当退火制度为700℃×4 min,成品组织完全为未再结晶的回复组织时,R p0.2为853.5 MPa,R m为895.5 MPa。该成分的电工钢P15/50或P10/400最小时,对应的平均晶粒直径都大于59.67μm;P10/800或P10/1000最小时,对应的平均晶粒直径都处于12.37~59.67μm尺寸区间。 TSCR was simulated to develop high-strength non-oriented electrical steel with 3% of Si,0.83% of Al and 2.99% of Mn by solution strengthening,grain refinement strengthening and dislocation strengthening.The microstructures of hot rolled plates,normalized plates and annealed plates were analyzed.Furthermore,the mechanical properties and magnetic properties of products with different microstructures were detailedly studied.As the average grain diameter of the steel was 12.37 μm,the yield strength ... 

研究了退火温度和退火时间对电沉积硅钢试样中的断面层组织、硅在试样中的分布情况、织构分布和磁性能的影响。结果表明:退火温度为1000℃、退火时间为210 min时得到的试样晶粒分布均匀、硅在试样中分布均匀、硅平均浓度为6.3715%(接近6.5%)。试样的织构分析及磁性能检测的结果表明,在较高温度下延长退火时间可增加{100}和{110}面织构,降低铁损,所得试样的磁性能较为良好。 The effect of annealing temperature and time on the microstructure, distribution of silicon,texture and magnetism of the high silicon steel prepared by electrodeposition was investigated. The results showed that after annealing at 1000℃ for 210 min, the mean grain size of steel was about 190 μm with a uniform grain size distribution, and the silicon is also uniformly distributed on the entire cross section with an average Si concentration 6.3715%(close to 6.5%); With the increasing annealing tim... 

本发明涉及一种无取向电工钢片绝缘涂液，它的主要有效成分包括有机树脂、水溶性磷酸二氢盐、硅溶胶、涂料助剂、和特定水溶性金属盐。上述各组分的质量组成比例为：有机树脂100份，水溶性磷酸二氢盐100‑250份，硅溶胶0‑100份、涂料助剂0‑20份，特定水溶性金属盐10‑50份，其余为水，涂液的固含量为15～40％。其中特定水溶性金属盐是指水溶性磷酸二氢盐以外的二价或多价金属盐，这种盐可以在磷酸二氢盐溶液中稳定存在，但是在电工钢涂层烧结温区会氧化或分解。本发明的绝缘涂液固化速度快且固化彻底，涂层具有优异的耐盐雾性能。

本发明涉及一种在连续的退火和覆层线(1)中对非晶粒取向的电工钢带(2)进行再结晶退火的方法，其中电工钢带(2)在感应炉(5)中以至少80K/s的加热速率加热到至少680℃的温度，并且然后在可能的第二连续炉(8)中以最大20K/s的加热速率加热到至少820℃的温度，其中在感应炉(5)上游将电工钢带(2)首先经由第一连续炉(3)以至多60K/s的加热速率加热到至少300℃的温度。

本实用新型属于检测设备技术领域，尤其为永磁同步电动机硅钢片的检测设备，包括检测台板，所述检测台板的两侧固定连接有立固框，所述立固框的上端固定连接有交叉式顶板，所述交叉式顶板的上端固定安装有液压缸，所述液压缸的输出端固定连接有挤压板，所述检测台板的上端表面固定连接有立固块，所述立固块上插设有拔拉杆，所述拔拉杆的一端固定连接有夹固板，所述检测台板的上端表面开设有条形槽，所述条形槽的内部固定连接有横固杆，所述横固杆的外围套设有弹簧。本实用新型通过设置夹固机构，使得硅钢片冲片在进行抗压检测之前能够得到更好的固定，从而避免检测的过程中产生飞弹现象，确保了设备的使用安全性。

通过对35W300高牌号0.35 mm冷轧无取向电工钢卷(/%:0.002C、2.71Si、0.22Mn、0.015P、0.003S、0.0020N、0.55Als)头、中、尾组织、织构及对应的磁性能的试验研究,发现因热轧时12 MPa高压水连续冷却造成接触轧辊的钢卷头、中、尾在不同温度下轧制,卷取后钢卷头部处于卷心、温度略高而冷却速度略低于钢卷尾部,致使钢卷纵向组织、织构不同,成品卷头、尾各250 m内磁感逐渐增加,铁损逐渐降低,250 m外至钢卷中部磁性能稳定。通过将热轧辊的冷却方式改为周期冷却和卷取后的层流冷却改为钢卷70 m后开始冷却,至钢卷尾部70 m前停止冷却的方式使得钢卷纵向铁损差异明显减小,磁感差异略有改善。 According to the test research on structure and texture of head,meddle and end of 35W300 high grade 0.35 mm cold rolled non-oriented electrical steel strip coil(/%:0.002C,2.71Si,0.22Mn,0.015P,0.003S,0.002 0 N,0.55Als) and corresponding magnetic properties,It is found that due to 12 MPa high pressure water continuous cooling the roller in hot rolling process led to head,middle and tail of strip rolling at different temperature and after coiling the head of strip coil being in center of coil led t... 

为研究退火工艺对普通取向硅钢初次再结晶组织的影响,对经不同温度、保温时间和升温速率退火后的材料组织进行了分析。结果表明:在等温退火条件下,加热至600℃时开始发生初次再结晶,800℃以上初次再结晶组织发展完善;而在最终冷轧板直接进行最终高温退火的情况下,加热温度在500～700℃时,将升温速率提高到80℃/h,初次再结晶组织更易于发展完善。 To investigate the influence of annealing process on the recrystallization of common grain oriented silicon steel,microstructures of sheets annealed at different temperature,soaking time and heating rate are observed.Results show that under the condition of isothermal annealing,recrystallization begins at 600℃ and fully develops above 800℃,while in the case that the final cold rolled sheets are directly thrown to final high temperature annealing,recrystallization is likely to develop with the he...