试验研究了0.3 mm取向硅钢冷轧板(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005A1)的退火温度(760~880℃7 min)和退火时间(820℃3~9 min)对该钢的晶粒尺寸,再结晶和织构的影响。结果表明,最佳初次再结晶退火工艺为820℃5 min,该钢的平均晶粒尺寸为14.20μm,完全再结晶率为92%,不利{111}<110>结构含量为3.16%,有利织构{111}<112>,{012}<001>和高斯织构含量分别0.40%,4.73%和2.46%。 The effect of annealing temperature(at 760 ~ 880 X.for 7 min) and time(at 820℃ for 3~9 min) on grain size,recrystallization rate and texture of 0.3 mm cold-rolled sheet of oriented silicon steel(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005Al) has been tested and studied.Results show that with optimum recrystallized annealing at 820℃ for 5 min,the silicon steel average grain size is 14.20 fun,the complete recrystaUization rate is 92%,the unfavourable-texture {111}< 110 > content in steel is ... 

本实用新型公开了一种硅钢板带加工用表面成型设备，包括底座，所述底座的上端固定连接有底部支撑架，所述底部支撑架的上端固定连接有机体，所述机体的上端固定连接有密封盖。本实用新型在打磨过程中，水泵可以将过滤箱内的冷却液通过进液机构上的进液管泵入到进液机构内，再经过进液孔进入到第二转轴内，再进入到打磨辊筒内，最后经过喷头喷到钢带表面，对钢带表面进行冷却，且可以将打磨下来的粉末带走，防止粉末飘散；冷却在喷出后，经过集液斗的收集，进入到过滤箱内，在过滤箱内设置过滤网可以对冷却液进行过滤，从而可以对冷却液进行重复使用。

【作者】 胡志强； 张文康； ...

在50Kg氧化镁坩埚真空感应炉上进行高硅电工钢的脱氧试验。结果表明,通过控制原料的成分、高真空下的碳氧反应和炉衬分解向钢液中的供氧,可使钢液的总氧含量≤15×10-6;在维持高温高真空条件下,当钢液中的反应达到一定程度后,延长精炼时间并不能降低钢液的总氧含量;完成精炼后加入硅钙合金沉淀脱氧可进一步降低钢液的总含氧量,但脱氧效果有限。 The test of high-silicon electric steel deoxidation has been carried out in 50Kg vacuum induction furnace with magnesium oxide crucible.Results show that the total oxygen could be ≤15×10-6in molten steel by controlling material components,carbon-oxygen reaction in high vacuum and oxygen contamination from crucible materials on molten steel;And when the reaction was carried through to a certain extent,total oxygen in molten steel could not be reduced by the extension of refining period in high va... 

一种分步调控制备高磁感高强度无取向电工钢的方法，按以下步骤进行：(1)按设定成分采用转炉冶炼钢水，制成连铸坯，含C0.001～0.008％，Si1.5～4.8％，Cu0.5～2％，Ni0.5～1.5％，Al0.2～1％，Mn0.2～1.5％，P＆lt;0.005％，S＆lt;0.005％，其余为Fe；(2)将连铸坯置于均热炉保温，多道次热轧相邻两道次间隔时间为30～180s；空冷；(3)常化处理；(4)多道次冷轧；(5)退火处理；(6)时效处理。本发明的方法成本较低、工艺简单，生产的无取向电工钢兼具优异的力、磁性能，能够很好的满足驱动/牵引电机的使用需求。

采用双辊薄带连铸工艺制备了厚度为2.4mm的3.98%Si-0.71%Al无取向硅钢带,经常化、冷轧、不同温度退火后,对其显微组织、析出物、织构和磁性能进行了检测分析。结果表明:随着退火温度的提高,退火板晶粒尺寸增大,组织均匀性提高;退火板析出物主要是AlN和MnS与AlN复合析出物,尺寸较粗大,达0.5~2.5μm;退火板织构沿厚度方向变化明显,表层和1/2层存在较强的{100}织构,1/2层还存在较强的{111}织构,1/4层主要是{112}织构;随退火温度的升高相应的铁损和磁感应强度均降低。 Using twin roll thin strip continuous casting technique,the 3.98%Si-0.71%Al no-oriented silicon steel strip in thickness of 2.4mm was produced.The microstructure,precipitates,texture,and magnetic properties of the sheet after normalizing,cold rolling and annealing at different temperatures were studied.The results show that with annealing temperature increase,the grain size and uniformity of annealed sheet increased.The main precipitates in coarse size of 0.5-2.5μm in annealed sheet were AlN and... 

对西昌钢钒炼钢厂200 t BOF(顶底复吹)-RH-CC工艺生产50PRW800无取向硅钢RH精炼过程中主要成份进行了分析。找出了目前工艺中影响钢液质量的主要因素是钢水脱氧处理不彻底,造成加入的部分硅元素烧损。操作工艺改为铝的脱氧即合金化操作一步完成,保证了钢水中氧处于一个较低的范围,从而减少对硅元素的烧损,提高合金收得率。 The factors of BOF-RH-CC process affecting the compositions of liquid steel were systematically investigated and studied of Xichang Steel and Vanadium Company. The main factors affecting the steel cleanliness were picked out. All results showed that the loss of silicon elements resulting from the deoxidization of liquid steel was not completely. It was suggested that the addition of aluminum for deoxidizing and alloying of molten steel was executed as one step in order to lower the oxygen potent... 

【作者】 康凌晨； 王丽娜； ...

从影响高牌号无取向硅钢退火工艺的主要参数入手,介绍高牌号无取向硅钢退火炉在加热、气氛控制、冷却、涂层烘烤方面的新技术,并展望无取向硅钢退火炉的发展方向。 Based on the technology parameters of high-grade non-oriented silicon steel annealing,the new technology of the annealing line,which includes heating,atmosphere control,cooling,coating baking,is introduced,and the development direction of non-oriented silicon steel annealing furnace is pointed out. 

利用电子探针面分析、状态分析及电子背散射衍射相分析技术研究硅钢高温氧化铁皮的显微结构。电子探针面分析可以直观的看出元素的分布状态,初步判断氧化铁皮的结构,而状态分析可以准确表征常规氧化铁皮中铁元素的状态,对于合金元素富集区域则通过电子背散射衍射相分析技术来标定。结果表明,高温氧化铁皮的结构主要有4层,即最外层为厚度约为10μm的Fe2O3相,次外层为Fe3O4相,中间层为FeO相上分布有颗粒状的Fe3O4相,最内层为FeO相和Si元素富集的Fe2SiO4相。其中Fe2SiO4层的分布特征与加热温度密切相关:1 100℃时,Fe2SiO4相呈颗粒状,弥散分布在FeO层;1 200℃时,Fe2SiO4相呈液态,侵入基体和疏松的FeO层,且沿着FeO晶界呈网状分布。 The microstructure of high temperature oxide scale on silicon steel was characterized by electron probe microanalyzer(EPMA)mapping analysis,state analysis and electron backscatter diffraction(EBSD)phase analysis.The element distribution and the initial structure of the oxide scale could be detected by EPMA mapping analysis apparently.And the state of iron in the conventional oxide scales could be determined by state analysis.Meanwhile,the alloy-rich region could be identified by EBSD phase analy... 

本实用新型公开了一种用于电机生产的硅钢片放料机构，包括用于传输硅钢片的传送机构和用于堆叠的放料机构以及用于旋转位移的旋转机构，所述传送机构出料端设置有所述放料机构，所述放料机构安装在所述旋转机构上端，所述放料机构下侧设置有推动机构。本实用新型利用传送机构、放料机构配合，保证了硅钢片的传输效果和放料效果，从而保证了硅钢片在放料堆叠过程的稳定性和安全性，提高加工效率，利用放料机构、推动机构配合，在后期放料堆叠后能够快速进行捆扎和运输。

本发明提供了一种超高磁感无取向硅钢及其制造方法和在汽车发电机生产中的应用，成分：C：≤0.005％、Si：0.5‑1.2％、Mn：0.1‑0.5％、P：0.01‑0.1％、S：≤0.004％、Al：≤0.005％、N：≤0.005％、Ti：≤0.003％，余量为铁和不可避免的杂质。通过成分设计，配合CSP薄板坯连铸连轧工艺、常化工艺，不用添加贵金属元素，不添加贵金属元素，流程短、成本低、磁感高、性能稳定；节省成本的同时，具有优良的磁性能，采用本发明生产的汽车发电机铁芯，与常规产品生产的铁芯相比，重量可减轻15％以上，缩小了发电机尺寸，满足汽车发电机小型化、高效化的要求。