研究了含铜低碳低硅无取向电工钢中的析出相及其析出机理.由能谱(EDS)及选区电子衍射(SAED)分析可知,铁素体基体上存在的大量弥散分布的等轴状析出相为类B2结构的铜.这些铜析出相的析出机理可以是一般析出、位错析出、台阶机理相间析出和弓出机理相间析出:一般析出在550、650和750℃三个等温温度均可发生;位错析出只发生在较低的等温温度(550℃),此时析出相呈特殊的平行短列状;台阶机理相间析出也可在上述三个等温温度下发生,但650℃等温时最有利于台阶机理相间析出,此时析出相平直列状分布;弓出机理相间析出只发生在较高的等温温度(750℃),析出相弯曲列状分布. Precipitates in low-carbon low-silicon non-oriented electrical steel containing Cu were studied and the precipitation mechanism was analyzed by means of energy dispersive spectrometry(EDS) and selected area electron diffraction(SAED).It is found that the equiaxed precipitates of Cu with B2-like structure distribute dispersively in the non-oriented electrical steel.The precipitation mechanism involves general precipitation,dislocation precipitation,interphase precipitations formed by the ledge me... 

【作者】 谌剑； ...

本发明公开了一种新能源汽车驱动电机用低铁损高强度无取向电工钢及其制造方法，所述无取向电工钢的化学成分及重量百分比包括C：0.001‑0.005％、Si：2.4‑3.0％、Mn：0.25‑0.5％、Al：0.70‑1.10％、P：≤0.02％、S：≤0.005％、0.015％≤Ce+Sn≤0.035％，余量为铁和不可避免的杂质，本发明通过加入Ce和Sn，净化钢质、微合金化提高无取向电工钢强度和磁性能，不需要添加固溶金属元素，且避免了高Si体系下的轧制困难问题，且不需要高温退火，解决了退火温度过高使晶粒异常长大，晶粒尺寸均匀性降低的问题，生产出的无取向电工钢具有较高强度的同时，还具有优良的磁性能。

研究了锰含量对w(Si)=1.8%Si无取向电工钢组织和性能的影响。结果表明,钢中锰含量从0.3%增加到1.2%时,由于α_γ相变的产生,铸坯低倍组织、热轧板金相组织及成品织构等均发生了不同程度的变化,对成品表面质量及磁性能产生了明显的影响。 The effects of manganese content on structure and properties of w(Si)=1.8% non-oriented electrical steels have been studied.Results show that with increasing manganese content to 1.2% from 0.3%,macrostructure of continuous casting slab,hot rolled band metallurgical structure and finished product texture vary in some extent because of the occurrence of α-γ phase transformation,the surface quality and magnetic properties of finished product are affected greatly. 

对高磁感取向硅钢冷轧板分别进行800、950、1050和1120℃不脱碳的预退火处理,在800℃预退火,成品的磁性能较好。织构分析的结果表明,随着预退火温度升高,初次再结晶后有利织构组分{111}<112>与不利织构组分(118)[110]的比值f(111)/f(118)逐渐降低,初次再结晶织构的变化是成品磁性的影响因素之一。 Preliminary annealing process at different temperatures for cold-rolled strips of a high permeability grain-oriented silicon steel was investigated to study the effect of the annealing temperature on microstructure and magnetic performance of the steel.Results show that the magnetic performances of the products annealed at 800 ℃ are best.Analysis of primary recrystallization texture indicates that with rising temperature,f(111)/f(118) which is the ratio of the favorable component {111}<112>... 

本发明涉及一种常化后免酸洗生产取向硅钢的方法，取向硅钢的生产工艺路线为：冶炼→连铸→热轧→常化退火→拉伸矫直→抛丸→冷轧→脱碳退火→渗氮→涂MgO→高温退火→热拉伸平整及涂绝缘膜；本发明在常化退火后通过物理方法去除带钢表面的氧化铁皮，且效率高、效果好、操作简单、易于控制；与常规工艺相比，省去了酸洗及后续废酸处理工作，排除了酸雾对环境的污染，消除了取向硅钢带因酸洗而产生的潜在缺陷，产品质量更加稳定可靠。

采用拉伸试验和显微组织观测的方法确定了GTN损伤模型中的9个损伤参数,运用GTN损伤模型对冷轧硅钢薄板边部缺陷的扩展及边裂的产生进行了有限元模拟,并与预置缺口的钢板轧制试验进行对比。结果表明:轧制过程中边部缺陷是造成钢板边部裂纹萌生和扩展的一个重要原因,GTN损伤模型可用来预测含边部缺陷硅钢薄板在冷轧过程中边裂的产生;预测结果与试验结果基本一致。 The crack initiation and propagation of silicon steel strip with edge defect during cold rolling process was studied by using GTN damage model in this paper.Nine damage parameters in GTN model were identified by tensile testing and microstructure observing,and then the FE simulation of edge defect evolution of silicon steel strip during rolling process was conducted on the base of GTN damage model,and then the results were compared with rolling experimental results.The results show that the edge... 

本实用新型公开了一种高磁感低铁损取向硅钢生产用切割装置，包括激光切割台，所述激光切割台上端滑动连接有一个滑动导轨，所述滑动导轨上滑动连接有一个切割主机，所述激光切割台上端且与切割主机相对应位置均匀固定连接有一组锯齿板，所述激光切割台上端且与锯齿板相对应位置活动连接有一个升降板，所述升降板上且与锯齿板相对应位置均开设有一个穿孔，所述升降板上端均匀转动连接有一组滚珠，本实用新型的有益效果是：通过螺纹杆的转动，可以使螺纹套和滑动块滑动，从而利用连接转杆的传动，可以将升降板顶起，使待切割的板材可以在滚珠上滑动，方便对板材位置的调节，并且将升降板下降后，不会影响板材的正常切割。

本发明提供方向性电磁钢板，能够同时实现充分低的变压器铁损与低噪音。一种方向性电磁钢板，其在表面具备张力被膜，实施了通过生成沿与轧制垂直方向在30°以内的方向延伸的线状的闭合磁畴而进行的磁畴细化处理，其中，邻接的闭合磁畴的平均间隔L为15mm以下，用规定式计算出的上述闭合磁畴相对于板厚的深度比率rd为35％以上，用规定式计算出的上述闭合磁畴的体积率rv为0.30％以上3.0％以下，用规定式计算出的上述闭合磁畴的面积率rs为0.50％以上4.0％以下。

试验的铸态取向硅钢（/%:0.044⁰.056C,3.12³.32Si,0.08⁰.11Mn,0.002⁰.008S,0.002 9⁰.029 1Als,0.006 2⁰.010 9N）由30 kg高频真空感应炉熔炼。通过场发射扫描电子显微镜/能谱仪（FE-SEM/EDS）研究结果表明,0.002 9%Als钢中氧化物主要为SiO₂,存在片状、棒状及近似球状的独立MnS,未发现含铝的氧化物或氮化物;0.0090%Als钢中出现以Al₂O₃为主的复合氧化夹杂物,存在MnS与AlN的复合析出物。钢中Als增加,复合析出物多呈簇状发展。氧化物容易成为MnS-AlN复合析出的核心,钢中Als含量越低,夹杂物中的MnS含量越高;作为核心的氧化物夹杂的尺寸越小,形成的复合夹杂物的形状越规则,尺寸也越小。热力学计算结果表明,钢中Als含量主要影响了钢中氧化物夹杂的组成和AlN的析出温度及析出量。 Test as-cast grain-oriented silicon steel（/%:0.044 ⁰.056C,3.12 3.32Si,0.08 0.11Mn,0.002⁰.008S,0.002 9⁰.029 1 Als,0.006 2⁰.010 9N） is melted by a 30 kg high frequency vacuum induction furnace.The research results by using field emission-scanning electron microscope/energy dispersive spectrometer（FE-SEM/EDS） show that in 0.002 9%Als steel the main oxide is SiO₂,and there is independent laminable,rod-like and approximate ... 

本发明公开了一种硅钢冷连轧轧制过程温度获取方法、装置及电子设备，通过获取硅钢冷连轧生产过程的工业参数数据以及各机架间硅钢的实际温度测试数据，然后基于工业参数数据以及预设初始模型，确定硅钢冷连轧生产过程的温度预测模型，接着基于硅钢轧制前的预热温度以及温度预测模型，得到硅钢冷连轧轧制过程各机架变形区出口与下一机架变形区入口之间的预测温度数据，再将预测温度数据与实际温度测试数据进行对比，并根据对比结果中的温度差异值对相应机架间的乳化液参数进行修正，直至温度差异值小于预设阈值，得到修正后的温度预测模型，能够用于实现硅钢冷连轧轧制过程中，任意采样点硅钢温度的获取。