本发明涉及变压器硅钢片技术领域，尤其是涉及一种变压器硅钢片组件成型冲裁机械及成型冲裁方法，包括基座、收卷装置、挤压装置、滚动装置和冲压装置，所述基座的上端位于四角处均固定连接有竖杆，竖杆的上端共同连接有横板，横板的下端设置有冲压装置，基座的上端设置有收卷装置，基座的上端位于收卷装置的后方设置有挤压装置，基座的上端位于挤压装置的后方设置有滚动装置；通过拉动拉环，带动圆板和推杆挤压第一弹簧，第一弹簧的挤压，使得推杆远离推槽，进而可取出模具，对模具进行更换；通过往凹槽内加入放置板，防止压板在撞击模具时，对模具进行支撑，防止模具发生变形。

针对马钢无取向电工钢孔洞缺陷的分布规律及形貌特征,对缺陷样进行了显微分析,并利用生产实绩数据分析了该缺陷产生的原因。结合热轧生产过程,主要通过避免带钢撞击导卫以及降低导卫结瘤的产生等措施,可有效抑制热卷异物压入产生,从而降低冷轧工序孔洞的产生。 In viewing of the distribution and morphology characteristics of the hole defect of non-oriented electrical steel in Maanshan Iron and Steel Co.,Ltd.,the causes of the defect were analyzed by micro analysis of the defect sample and the production data.Combined with the production process of hot rolling,by avoiding the impact of strip steel on the guide and reducing the nodule formation on the guide,the pressing of foreign bodies in hot coiling could be effectively suppressed,thus reducing the fo... 

利用热模拟试验机、光学显微镜和X射线衍射仪对Fe-3.2%Si低温取向硅钢热轧工艺参数对组织及织构的影响进行了研究。结果表明,Fe-3.2%Si硅钢在1110℃粗轧、880℃终轧,轧后以10℃/s的速度冷却到550℃卷取,然后空冷到室温,热轧硅钢板沿板厚方向的显微组织不均匀性显著,对后续发展完善的二次再结晶有重要作用。无论是热轧板,常化板还是冷轧板,它们的织构集中分布在γ取向线上,γ取向线的织构除取向密度不同外,织构种类是一致的,这说明γ取向线上织构是有继承性的。从热轧到常化,织构取向密度显著减小,经二次冷轧后,织构密度又显著升高,可见,轧制变形有助于织构的形成并使织构强度升高。 The influence of hot-rolled process parameters on the microstructure and texture of Fe-3.2%Si low temperature hot rolled grain-oriented silicon steel were researched by hot simulation experiment machine,light microscope and X-ray diffractometer.The results show that,Fe-3.2%Si silicon steel is rolled by the technology with a temperature of rough rolling of1110℃,finish rolling of 880℃,coiling with the speed of 10℃ /s,and then cooled to room temperature with air.The microstructure of hot-rolled sil... 

作为一种具有优异高频铁磁性能的合金,Fe-6.5%Si(质量分数)高硅钢在高频工况条件下降损效果明显,对电气行业应用器件高频化、小型化、节能等具有十分重要的意义。通过与取向硅钢测量B-P数据对比,验证了高硅钢高频超低损特性,且轧制高硅钢与日本CVD法生产高硅钢存在基本相同的铁损值。采用国标Epstein Square法对0.30mm高硅钢薄板进行单片测试,并对由0.30mm高硅钢薄板首次装配成的电感器进行铁损测试,对比测试结果表明,元件测试与单片测试数据基本吻合,高磁感应强度条件下,元件测试结果略低于单片测试,分析原因为:线圈引起励磁压降;元件叠片间出现短路,电流增大,损耗增加;气隙板厚度过大。 As one core material with excellent high-frequency ferromagnetism,Fe-6.5%Si performs obviously reduction on core loss in high field frequency which means much to high frequency,minimization,energy conservation in electric industry.Super low loss was verified by drawing B-P curves based on detected experimental data,and which went equal to Fe-6.5%Si thin strip fabricated by CVD in Japan.Fe-6.5%Si was firstly fabricated as inductor in this research,and its core loss was determined for comparison w... 

本实用新型涉及一种硅钢片抓取平台，其包括抓取框架，包括抓取框架，所述抓取框架上设有多个支架，对应于非切割区域的支架上设有大真空吸盘，对应于切割区域的支架上设有小真空吸盘。本实用新型结构简单，通过多个真空吸盘来进行硅钢片的抓取也不会损坏加工后的硅钢片，还提高了硅钢片的搬运效率。此外，通过气动系统实现对吸盘的自动吸气，提高了对吸盘操作的便利性。

本实用新型公开了一种具有废料回收机构的硅钢板带加工用切割装置，包括箱体，所述箱体的前侧靠近顶部处设有电机，所述箱体的顶部靠近前侧处固定连接有竖板，本实用新型一种具有废料回收机构的硅钢板带加工用切割装置，电机在工作时既能带动切割刀进行切割作业，同时还能带动第一筛板和第二筛板以相邻转轴为中心上下摆动，切割的废屑从切割槽穿过达到箱体内腔，第一筛板和第二筛板对废料进行筛分处理，通过隔板设置，隔板将集料盒分为两个存储空间，隔板右侧存储穿过第一筛板和第二筛板的细料，隔板的左侧存储被第一筛板和第二筛板过滤下来的粗料，既方便操作人员对废料进行集中处理，还对废料进行了筛分处理，以此方便对废料进行分类重复利用。

运用电子背散射衍射(EBSD)和X射线衍射(XRD)技术对硅钢热轧板的织构在板厚方向的分布进行了研究,并分析了两种织构测量方法的特点。EBSD技术能直观给出板厚方向的微观织构,XRD能得到钢板的宏观统计织构信息,结合两种技术的分析,能更直观更精确的研究不同织构在板厚方向的分布。 The texture distribution along the thickness of the silicon steel has been investigated by electron backscatter diffraction(EBSD) and X-ray diffraction(XRD) technique.The characteristics of two technique of texture analysis have been investigated.Combined the two techniques,the texture distribution along the thickness of the silicon steel could be realized distinctly and accurately. 

研究了电工钢SXRC的显微结构和疲劳性能,并与DP钢进行了比较。结果表明,退火温度低温化能够有效的抑制电工钢的再结晶。该钢在固溶铌的作用下,能够在保证电机磁性的同时具有一定的强度。与DP钢相比,SXRC钢的抗疲劳性能更好。 The microstructures and fatigue properties of the electrical steel SXRC we re investigated, and the properties were also compared with the steel DP. The results show that the recrystallization of the electrical steel can be suppressed at lower annealing temperature. The steel presents favorable motor magnetic and also a compatible strength with the help of solid-solution Nb. Compared with the steel DP, the fatigue resistance of the steel SXRC is preferable. 

本发明公开了一种用于取向硅钢卷的焊缝切除方法，包括在焊接机组完成钢卷焊接后，在距离焊缝预设距离位置处冲孔；而后，钢卷到达成品退火工序时，利用孔洞检测装置检测焊缝冲孔，并根据焊缝冲孔得到焊缝位置，并记录该焊缝位置；并在分卷工序中，根据记录得到的焊缝位置对焊缝进行切除。这样，该方法利用焊缝冲孔，结合孔洞检测装置，将焊缝位置信息传递到分切工序，使得焊缝识别切除率较高，有效解决了取向硅钢焊缝无法精准定位切除的问题，实现了卷中焊缝多工序结合精准切除。

根据现场实际的生产控制情况,指出了热轧原料断面轮廓缺陷以一定的比列遗传给了冷轧带钢,分析了不同热轧原料断面轮廓对冷轧电工钢尺寸精度的具体影响,提出了相应的规律。并阐明了严格控制热轧原料断面轮廓形貌,对保证冷轧电工钢尺寸精度具有重大意义,对于中国现行的冷轧电工钢生产具有指导意义。 Based on the actual situation of production control,it was pointed out that the section profile defects of hot-rolled raw materials were geneticed to the cold-rolled strip.The specific impact analysis for the profile of different hot-rolled raw materials to the dimensional accuracy of cold-rolled silicon steel was analyzed.As a result, the corresponding orderliness are given;And the strict control to section profile of the hot-rolled material is of great significance to ensure the dimensional ac... 

本发明公开了一种新能源汽车驱动电机用35WD1600电工钢及其生产方法。属于新能源汽车驱动电机电工钢生产技术领域，主要解决的是现有技术新能源驱动电机电工钢性能较差的技术问题，包括以下化学元素成分及重量百分比：C≤0.005％，Si为2.5～2.8％，Mn为0.2～0.4％，P为0.08～0.12％，S≤0.008％，Cu为0.20～0.30％，Ni为0.16～0.25％，Al为0.3～0.5％，其余为Fe及不可避免的杂质。生产方法包括以下步骤：(1)铁水预处理；(2)转炉冶炼；(3)RH精炼；(4)连铸连轧；(5)酸洗；(6)第一次冷轧脱碳退火；(7)第二次冷轧脱碳退火；(8)涂层；(9)烧结卷取。本发明的新能源汽车驱动电机用35WD1600电工钢，性能达到新能源汽车驱动电机用冷轧无取向电工钢带国家标准及客户性的要求，焊接性能、板形、冲片性能良好。

为了优化激光刻痕降低取向硅钢铁损的工艺,寻找刻痕速度、脉冲能量、扫描间距等重要刻痕参数的最佳匹配关系,提出了一种基于人工神经网络与遗传算法的优化模型,并利用这种模型对30Q130取向硅钢材料的刻痕工艺进行了优化实验,结果表明,这种模型稳定可靠,可以作为取向硅钢刻痕工艺优化的一种有效的措施。 A laser is often considered to scribe the grain-oriented silicon steel surfaces after cold-rolling and annealing to reduce the core loss.It is necessary to select the best scribing parameters to maximize the reduction in this process.This paper proposes an optimization method of genetic algorithm during laser scribing of 30Q130 steel,by developing an artificial neural network prediction model using a database form a designed orthogonal experiment.The objective is to determine the best combinatio...