硅钢资料

采用轧制法制备出具有低铁损高磁感0.23mm厚6.4%(质量分数)Si高硅钢。沿轧制方向的最终磁性能为B8=1.474 T,B50=1.714 T;P10/50=0.30W/kg,P15/50=0.88W/kg。利用X射线衍射及背散射电子衍射(EBSD)技术分析了高硅钢在轧制及退火过程中的织构演变过程。结果表明,通过采用大压下率热轧,确保热轧板次表层中产生更多的高斯织构,随后进行遗传;温轧板中粗大的晶粒有利于冷轧剪切带的形成;冷轧板经脱碳退火后生成强{210}〈001〉织构及次表层较强的高斯织构是在轧向上获得高磁感的原因,归因于其在{111}〈112〉冷轧形变晶粒内的剪切带优先形核并长大;最终退火后虽出现了随机取向,但以{310}〈001〉织构为代表的η织构得以保留并且增强,进一步提高了磁感。随着退火温度的升高及保温时间的延长,高硅钢薄板晶粒尺寸不断增大,铁损明显降低。 6.4wt%Si high silicon steel sheets(0.23mm thick)with low iron loss and high magnetic induction were successfully produced by rolling process.The final magnetic properties along the rolling direction(RD) were:B8=1.474T,B50=1.714T;P10/50=0.30 W/kg,P15/50=0.88 W/kg.The texture evolution during rolling and annealing was investigated by means of X-ray diffraction and electron backscatter diffraction(EBSD).It was found that more Goss textures formed in the subsurface of hot rolled plates by using larg... 

无取向硅钢特别是中牌号以上的无取向硅钢,随着含硅量的提高,常温下塑性较差,冷轧过程中轧制力明显提高,如果存在原料质量问题,极易发生断带事故,影响硅钢冷轧过程的成材率和生产效率。通过优化冷轧工艺参数,可提高冷轧稳定性。生产中通过合理分配冷轧各道次压下量和轧制速度,保证了轧制过程的稳定,很大程度减少了冷轧断带事故的发生。 Non-oriented silicon steel, especially in the low and middle grade, with the increase of silicon content, plasticity is poor at room temperature, rolling force in cold rolling process significantly improved .If there is the quality defect of raw materials , easily sheet is rolling off. Affect finished product rate and production efficiency in process of cold-rolled silicon steel. Through optimization of cold rolled process parameter , improve the stability of cold-rolling process. Through reason... 

综述了电工钢从生产到成品过程中涉及到的检测项目、检测方法及仪器,并通过对电工钢标准的发展改进,详细阐述了我国现有的电工钢技术标准体系,同时对代表企业的电工钢重点指标进行了摘录对比,为综合应用电工钢检测方法并促进电工钢的发展提供了一定的参考。 This article summarizes the testing items,methods,and instruments involved in the process from manufacturing to finished products of electric steel. The current electric steel technical standards system in our country is also elaborated in detail,along with the development and improvement of electric steel standards. Meanwhile,by comparison of electric steel KPI in representitive companies,this article provides references for comprehensive application of electric steels testing methods and promo... 

介绍在取向硅钢生产中抑制剂的作用以及多元抑制剂的机理和应用情况,分析多元抑制剂方案中各种元素对高磁感取向硅钢性能的影响,并根据生产实践提出了进一步研究的方向. The role of an inhibitor in the production of grain oriented silicon steel,and the mechanism of multiplex inhibitor in the production are described in the present article.In addition,the influence of various elements in the multiplex inhibitor on the performance of grain oriented silicon steel with high magnetic induction is elucidated.Further work needed in this research is also indicated. 

本发明公开了一种减少低温高磁感取向硅钢点状露金缺陷的方法。本发明通过控制低温高磁感取向硅钢的脱碳和渗氮工艺，特别是通过控制脱碳露点、渗氮露点、脱碳氧化度、脱碳时间来调节钢板经脱碳渗氮后表面形成的内氧化层中FeO/SiO2的比例，结合氧化镁退火隔离剂的含水率控制，获得了一种可避免点状露金缺陷的低温高磁感取向硅钢生产方法。

以CaO-CaF2复合渣系为脱硫剂,在RH精炼过程采用真空投入法进行高牌号无取向电工钢深脱硫工业试验,采用KTH模型计算分析了RH炉渣成分对硫容量CS的影响。研究结果表明,炉渣成分控制在w((CaO))/w((SiO2))为5~7,w((CaO))/w((Al2O3))为1.5~1.8,w((Al2O3))为25%~30%,w((FeO+MnO))<5%,脱硫剂加入量为6~8kg/t时,钢中硫质量分数从平均0.003 1%降低到0.001 8%,最高脱硫率达到47.1%,平均脱硫率为41.7%。 The industrial trials on deep desulphurization of high grade non-oriented electrical steel were finished through using CaO-CaF2complex based fluxes in RH process.Using the KTH model,the effect of refining slag composition on the sulfide capacities was analyzed.The results show that the chemical composition of refining slag(mass fraction,%)is w((CaO/SiO2))between 5to 7,w((CaO))/w((Al2O3))beween 1.5to 1.8,w((Al2O3)) between 25%to 30%,w((FeO+MnO))less than 5%,and the desulphurizer addition level of... 

本发明公开了一种低牌号无取向电工钢的制造方法，包括：在炼钢时，增加所述低牌号无取向电工钢的板坯的铝元素含量，增加量按重量百分比计为0.08％～0.12％；在热轧板坯加热时，控制所述板坯的出炉温度为1150℃～1200℃；在热轧粗轧时，控制所述板坯的粗轧RT2温度为1000～1050℃；上述方法通过提高铝含量，以升高低牌号无取向电工钢的相转变温度，再结合板坯的出炉温度控制和粗轧RT2温度控制，保证低牌号无取向电工钢在精轧过程中不会因为相变区轧制而产生轧制力波动，从而稳定精轧轧制过程，提高精轧后低牌号无取向电工钢板卷的尺寸和板型精度。

【作者】 张煜； 朱国辉； ...

聚焦无取向硅钢产品标准,从电磁性能、表面性能、机械性能以及尺寸公差与边部质量等维度对国际标准IEC、EN、JIS、ASTM以及国标GB进行了分析研究。分析得出,各类标准在电磁性能方面要求基本一致;ASTM标准的机械性能要求有别于其他几个标准。 In this paper,non-oriented silicon steel standards of EN,JIS,GB and ASTM were compared and analyzed. It is showed that,all types of standards in electromagnetic performance requirements are basically the same. Surface properties in ASTM standard are expressed in the most detailed. The mechanical properties requirements of the standards,except for ASTM,are basically the same. 

本实用新型公开了一种高磁感低铁损取向硅钢生产用切割装置，包括激光切割台，所述激光切割台上端滑动连接有一个滑动导轨，所述滑动导轨上滑动连接有一个切割主机，所述激光切割台上端且与切割主机相对应位置均匀固定连接有一组锯齿板，所述激光切割台上端且与锯齿板相对应位置活动连接有一个升降板，所述升降板上且与锯齿板相对应位置均开设有一个穿孔，所述升降板上端均匀转动连接有一组滚珠，本实用新型的有益效果是：通过螺纹杆的转动，可以使螺纹套和滑动块滑动，从而利用连接转杆的传动，可以将升降板顶起，使待切割的板材可以在滚珠上滑动，方便对板材位置的调节，并且将升降板下降后，不会影响板材的正常切割。

该电磁钢板为母材钢板的其中一个或两个表面中的至少一部分被具有接合能力的绝缘被膜覆盖的电磁钢板，所述绝缘被膜的25～100℃的温度范围的对数衰减率为0.3以下。

【作者】 常波； ...