本发明提供一种在同一卷材内得到稳定的磁特性的方向性电磁钢板的制造方法。上述方向性电磁钢板的制造方法，包括如下步骤：将具有规定的成分组成的钢坯热轧而制成热轧板，将上述热轧板退火而制成热轧板退火板，对上述热轧板退火板实施1次或隔着中间退火的2次以上的冷轧而制成最终板厚的冷轧板，对上述冷轧板实施一次再结晶退火和二次再结晶退火；上述冷轧包括至少1次的压下率为80％以上且轧制速度为设定值R0(mpm)期间的钢板温度T0(℃)与轧制速度为0.5×R0(mpm)以下期间的钢板温度T1(℃)满足式(1)的冷轧。

以CaO-CaF2复合渣系为脱硫剂,在RH精炼过程采用真空投入法进行高牌号无取向电工钢深脱硫工业试验,采用KTH模型计算分析了RH炉渣成分对硫容量CS的影响。研究结果表明,炉渣成分控制在w((CaO))/w((SiO2))为5~7,w((CaO))/w((Al2O3))为1.5~1.8,w((Al2O3))为25%~30%,w((FeO+MnO))<5%,脱硫剂加入量为6~8kg/t时,钢中硫质量分数从平均0.003 1%降低到0.001 8%,最高脱硫率达到47.1%,平均脱硫率为41.7%。 The industrial trials on deep desulphurization of high grade non-oriented electrical steel were finished through using CaO-CaF2complex based fluxes in RH process.Using the KTH model,the effect of refining slag composition on the sulfide capacities was analyzed.The results show that the chemical composition of refining slag(mass fraction,%)is w((CaO/SiO2))between 5to 7,w((CaO))/w((Al2O3))beween 1.5to 1.8,w((Al2O3)) between 25%to 30%,w((FeO+MnO))less than 5%,and the desulphurizer addition level of... 

本发明揭示了一种无取向硅钢及其生产方法。该无取向硅钢的化学成分：Si:2.95%~3.15%，Al:0.75%~0.95%，Si+2Al:4.6%~4.9%，Mn:0.5%~0.7%，Sn:0.03%~0.04%，Cu≤0.03%，Cr≤0.03%，Ni≤0.03%，Nb≤0.004%，V≤0.004%，Ti≤0.004%，C≤0.0025%，P≤0.015%，S≤0.0015%，N≤0.004%，余量铁；Mn/S≥380，Al/N≥200；无取向硅钢的再结晶晶粒尺寸50~80μm。本发明在保证磁性能的同时，提高了强度，解决了现有技术所存在的磁性能和强度的兼顾问题。

针对目前大部分无取向电工钢处理液为含铬处理液、且需在较高温度下固化的情况,在分析成膜物质性质的基础上,试验研究了一种可低温快速固化的电工钢环保绝缘处理液,研究了其涂装工艺,并测定了涂层的附着性、绝缘性、耐热性、耐蚀性等性能。试验结果表明:该处理液可在150~250℃下快速烘干固化,涂层表面光滑且致密均匀,性能优良,可满足中小电机的使用要求。 At present,most of the insulating fluid for non-oriented electrical steel contains chromium,and should be cured at high temperature.On the basis of analyzing the characteristics of the film-forming substance,a kind of eco-friendly insulating fluid with lower curing temperature for non-oriented electrical steel sheet was developed in the experiments.Then its coating process was studied,and the adhesiveness,insulativity,heat resistance,corrosion resistance and other properties of the coating was m... 

本实用新型公开了一种优化取向硅钢底层质量的打孔隔板，包括取向硅钢底层和分隔板，所述取向硅钢底层的上方安装有分隔板，且分隔板的内部设置有通孔，所述通孔的下方安装有卡合板，且卡合板的下方安装有硅胶密封垫，所述分隔板的右侧安装有三脚架，且三脚架的右侧安装有螺钉，所述三脚架的左侧安装有螺母，且三脚架的下方安装有固定横杆，所述分隔板的上方安装有定位套筒，且定位套筒的内部设置有内螺纹，所述内螺纹的内部安装有定位横杆，且定位横杆的两侧设置有外螺纹。该种优化取向硅钢底层质量的打孔隔板中，通过设置的通孔，分隔板将取向硅钢底层分隔时，通过通孔可以将分隔连通，减少在使用时分隔板阻拦取向硅钢底层的磁感性能。

采用CVD法制备6.5%Si高硅钢,介绍了具体的制备工艺过程,研究了温度对渗硅速率和试样质量减轻的影响,同时分析了扩散时间对高硅钢中硅分布的影响。结果表明:在CVD反应过程中,反应温度高于1050℃将大大提高渗硅速率,但当温度大于1200℃后,渗硅速率趋于稳定;渗硅后,试样会减轻、减薄,随着温度升高,试样质量减轻的速率逐渐增大,在1200℃左右趋于稳定;扩散时间越长,硅分布越均匀,结合制备效率进行考虑,满足Δw表-中/b≤5的时间为适宜的扩散时间。 6.5%Si high silicon steel was manufactured by using CVD method and the process was introduced,the influence of temperature on the siliconizing rate and quality reducing rate,diffusion time on silicon distribution were investigated.Results as follows: the siliconizing rate will increase quickly when the temperature is higher than 1050 ℃,but the siliconizing rate will become steadily as the temperature up to 1200 ℃;The quality reducing rate will increase with the elevating of temperature and the r... 

以质量分数为25%的丙烯酸乳液MC-102、15%Al(H2PO4)3溶液、0.01%H3BO3、0.01%Zn(Ac)2·2H2O和2%二乙二醇丁醚组分,在不同固化工艺下制备涂层。极化曲线和电导率测试发现300℃处理60 s得到的涂层具有良好的耐腐蚀性和绝缘性;水煮实验证明该涂层具有良好的耐水性;断口线扫描发现涂层具有良好的附着性。 A formula comprising MC-102 acrylic emulsion 25%,aluminium dihydrogen phosphate15%,boric acid 0. 01%,zinc acetate dihydrate 0. 01% and diethylene glycol monobutyl ether 2% was used to prepare coatings via different treatment process. The conductivity test and polarization curves revealed that a coating cured at 300 ℃ for 60 s showed good insulative and anticorrosive properties. The water boiling test indicated that the said coating had good water resistance. A cross section of the coating was in... 

【作者】 陶永根； ...

结合工业化生产的无取向硅钢,探讨了氧硫交互作用对钢中夹杂物生成的影响。借助非水溶液电解+扫描电镜法,研究了不同O、S含量下钢中夹杂物的变化规律。结果表明,本实验条件下,提高O含量、降低S含量,会劣化热轧组织再结晶效果。在劣化效果上,O的作用大于S;低Si、无Al硅钢中,应尽可能降低O含量、适当提高S含量,以粗化钢中微细夹杂物,减少尺寸小于1.0μm的夹杂物的数量;O、S含量与钢中夹杂物数量不具有关联性。生产过程中,不仅要严格控制O、S含量,还要严格控制生产工艺,以免生成较多的有害夹杂物。 Based on the industrial production of non-oriented silicon steel,the effects of interaction between oxygen and sulfur on the formation of inclusions were discussed.The change of non-metallic inclusions in steel sheets was investigated by means of electrolysis with non-aqueous solution under different oxygen and sulfur content.Results show that the recrystallization microstructure of hot rolled sheets will be deteriorated with the increase of oxygen content and the decrease of sulfur content.The ... 

一种电工钢切片用辅助定位装置，涉及电工钢加工技术领域，包括加工台、支撑腿、定位块、侧板、滑杆、移动板、顶板、滑动架、伸缩杆、切片装置、定位杆和挡板；支撑腿设置在加工台底部；定位块设置有两组，两组定位块均设置在加工台上，两组定位块沿横向分布，每组定位块设置有两个，每组的两个定位块沿纵向分布；侧板设置有两个，两个侧板均设置在加工台纵向一侧，两个侧板沿横向分布；滑杆设置在两个侧板之间；移动板沿横向滑动设置在滑杆上；顶板设置在移动板靠近加工台的纵向一侧，顶板位于移动板上端。本实用新型能够方便工作人员切割出一定尺寸的电工钢切片，且切割精度很高。

介绍了微合金元素锡、铌、稀土对无取向硅钢性能的影响,并扼要分析了这些元素对硅钢性能的影响机理:晶界偏聚元素Sn可细化晶粒提高硅钢磁性能;微合金元素Nb细化铁素体晶粒,提高硅钢的强度、韧性和塑性及磁性能;稀土元素(RE)在硅钢中的主要作用包括净化钢液、变质夹杂物、改善铸态组织和性能及微合金化,减少晶界上出现偏析的几率。 The influence of micro-alloy elements on properties of non-oriented silicon steel and the mechanism for effect of the micro-alloy elements including Sn、Nb and RE on the properties of steel are presented and analyzed in this paper.Grain boundary segregation elements Sn in steel can grain refinement and improve the magnetic properties;Micro-alloy elements Nb can refine the ferrite grain,increase the silicon steel strength,toughness and plastic;The main role of the RE in the silicon steel including... 

本发明涉及含Cu无取向硅钢的生产方法，转炉炼钢，真空处理过后连铸成坯；铸坯化学成分：1.0≤Si/Cu≤3.0,3.0≤Si+Cu≤5.5％，S≤0.0015％，(Mn+Cu)/S≥3000，其他为Fe,Als,P以及不可避免的杂质元素；对铸坯进行粗轧；粗轧后的中间坯采用热卷机进行强制卷取，开卷后中间坯进入保温箱，控制保温箱内冷却速度≤5℃/s；进入保温箱的中间坯温度T1满足：1000‑(Si+Cu)×103≤T1≤1100‑(Si+Cu)×103；高压除鳞，精轧，层流冷却，卷取；连续酸洗；冷轧到目标厚度，成品退火，涂层；成品卷进行时效处理。成品卷具有较低的中高频铁损，高磁感和高屈服强度。