分析总结退火工艺各参数对冷轧无取向硅钢磁性能的影响,结合设计和生产实践经验介绍退火工艺中各参数的实际生产取值,并针对现生产工艺过程中出现的典型问题提出解决办法。 It is analyzed and summarized the great influences on magnetism of cold rolled non-oriented silicon steel affected by various annealing process data in this article.The relevant settled ways is raised.According to the actual value presetting ways for various annealing process data based on design and production,as well as typical problems occurred during production. 

利用OM、EBSD等手段研究了热轧板两段式正火时在700℃保温不同时间(0、10、30、60 min)对含Sb冷轧无取向电工钢磁性能的影响。结果表明,700℃保温10 min处理的样品铁损最小,磁感最高。对成品板的组织分析结果表明,试样的晶粒尺寸随700℃保温时间的延长先增大后减小,保温10 min时晶粒尺寸达到最大;分析成品试样织构发现,有利织构组分随700℃保温时间的延长先增加后减少,保温10 min时有利织构组分所占百分比最高。因此,含Sb冷轧无取向电工钢两段式正火时在700℃保温10 min时磁性能最好。 Effect of two-stage normalization on magnetic property of non-oriented electrical steel containing antimony was investigated by using optical microscope(OM) and electron back-scattered diffraction technology(EBSD).The experimental results show that the iron loss and magnetic permeability of the specimen insulated at 700 ℃ for 10 min are lowest and highest respectively.The grain size of the finish specimens increases first and then decreases with the increase of holding time.Similarly,the advanta... 

为了更好的解决电力系统防污闪涂料RTV-Ⅰ长期应用暴露出来的问题以及目前RTV-Ⅱ防污闪涂料存在的一些不足,结合具体实际需求,在电力系统外绝缘领域,应用新型防污闪硬质涂层——防污闪纳米硅钢涂层,并对分别喷涂了防污闪纳米硅钢涂层以及RTV涂料的绝缘子进行对比运行情况研究分析。研究结果表明,防污闪纳米硅钢涂层是一种同时具有优异憎水性迁移性能和自洁性能的新型涂层,具有良好的应用前景。 In order to solve the problem exposed of anti-pollution flashover coating RTV-Ⅰwhich has been used long-term in power system,as well as to better solve some shortcomings of the current anti-pollution flashover coating RTV-Ⅱ,in this paper,a new anti-pollution flashover hard coating — anti-pollution flashover nanometer silicon hard coating(NSHC) is applied in the field of power system insulation for the specific practical needs.At the same time insulators which are separately sprayed by the NSHC a... 

本发明公开了一种取向硅钢高温退火底板，涉及钢卷生产技术领域，解决了钢卷的尺寸变形导致钢卷切边量过大的技术问题。包括应变诱导板，应变诱导板的板面开设有若干凹槽，相邻凹槽之间于应变诱导板的板面形成凸楞，钢卷放置于应变诱导板的板面上，其中部分的钢卷端面支撑于凸楞上，其余的钢卷端面悬置于凹槽上。本发明通过在应变诱导板上设置凹槽与凸楞，钢卷在高温退火过程中同样受重力产生蠕变变形，但蠕变变形按照凸楞所设定的方向进行，从而将产生的不均匀的“大浪”分割成碎化均匀的“细浪”，使得钢卷边部的变形细小、均匀、可控，从而降低了大象脚变形的缺陷影响程度，减小了钢卷的切边量，提高了成材率，同时能够获得良好的边部板形。

一种取向硅钢极薄冷轧板钢带的焊接系统及方法，于该系统内设有焊轮及与焊轮电连接的焊接控制器；所述焊轮由前后呈直线布设的主焊轮、副焊轮构成；所述焊接控制器由分别与主焊轮电连接的第一焊接控制器、与副焊轮电连接的第二焊接控制器构成。所述焊接基于单排焊，仅使用一次焊接行程，通过设置的第一次焊接与第二次碾压焊接依次作业完成。本发明的一种取向硅钢极薄冷轧板钢带的焊接系统及方法，针对取向硅钢极薄钢带冷轧板焊接的问题，对传统电阻焊焊机拥有的碾压轮改造及建立的相应焊接工艺。平衡了热量积累与质量保证两者，解决了取向硅钢极薄钢带冷轧板焊接容易发生虚焊、爆焊和焊接时间长等问题。同时和传统电阻焊焊机相比焊接工艺窗口更大，焊接效率更高。

根据本发明的一个实施例的粘接涂料组合物，其包含聚乙烯丙烯酸酯100重量份和无机颗粒3至25重量份，所述聚乙烯丙烯酸酯包含由以下化学式1表示的重复单元和由以下化学式2表示的重复单元，所述聚乙烯丙烯酸酯包含75至95重量％的由以下化学式1表示的重复单元、5至25重量％的由以下化学式2表示的重复单元。

【作者】 宋波； 朱一知； ...

以轻烧氧化镁粉为原料,经消化、碳化制得重镁水,在热解反应前采用络合剂对重镁水中的杂质钙、铁进行络合掩蔽,再经热解得到碱式碳酸镁,碱式碳酸镁经煅烧可制得钙、铁杂质含量较低的氧化镁。在重镁水络合除杂过程中,考察了络合剂三乙醇胺、柠檬酸、草酸单独和复合使用的除铁、除钙效果。以三乙醇胺为络合剂时,在200 mL重镁水中加10 mL三乙醇胺(1∶1),氧化镁产品中w(氧化镁)=99.3%、w(氧化钙)=0.31%、w(氧化铁)=0.042%;使用草酸和柠檬酸作为复合络合剂时,在200 mL重镁水中加入1.0 g柠檬酸和2.0 g草酸,氧化镁产品中w(氧化镁)=98.2%、w(氧化钙)=0.24%、w(氧化铁)=0.030%。 Light-burned magnesia as a raw material was hydrated and carbonated to obtain magnesium bicarbonate liquor.Before the pyrolyzing of magnesium bicarbonate liquor,complexants were used to cover Fe and Ca impurities.Then the treated liquid was pyrolyzed to obtain basic magnesium carbonate which was calcined to magnesium oxide with low calcium and iron content.During the complexing purification of magnesium bicarbonate liquor,the Fe and Ca removing effects of single or compound complexing agents,suc... 

通过热力学计算与模拟试验研究了含钒钛取向硅钢中氮化物析出相的析出规律与析出行为,并探讨了含钒钛元素的氮化物析出相作为薄板坯连铸连轧流程制备取向硅钢中辅助抑制剂的可行性.研究表明,在所冶炼的含钒钛取向硅钢的成分范围内,Ti N在钢液凝固末期便具备析出的热力学条件,而Al N与VN只可能在凝固后的α+γ或α+Fe3C两相区内析出.含钒钛取向硅钢中氮化物析出相以成分复杂的复合析出相为主,且随着钒钛加入量的增加,钢中抑制剂析出相总的分布密度由于含钒钛元素的氮化物析出相的增加而明显提高,使抑制剂抑制初次再结晶晶粒正常长大的能力得以加强,最终成品的磁感应强度值B8由1.857 T提升至1.898 T.同时,加入不高于0.007%的Ti与不高于0.005%的V不会影响中间脱碳退火工序的脱碳效果以及高温退火净化阶段硫、氮的脱除效果,其形成的含钒钛元素的纳米级氮化物析出相适合作为薄板坯连铸连轧流程制备取向硅钢的辅助抑制剂. The precipitation behavior of nitride precipitates in grain-oriented silicon steel containing vanadium and titanium elements produced by thin slab casting and rolling process was studied by thermodynamic calculation and simulation experiment. The feasibility of nitride precipitates containing V and Ti elements as auxiliary inhibitors was also investigated. It is found that Ti N is likely to precipitate at the final stage of solidification in the grain-oriented silicon steel,but VN and Al N can p... 

本发明公开了一种消除取向硅钢单边浪缺陷的方法，其包括如下步骤：1)、制作专用盖板；所述专用盖板包括环形板，所述环形板外边缘设有多个剪开处；2)、将待装炉的取向硅钢钢卷吊运至高温退火炉炉台；3)、将专用盖板铺于取向硅钢钢卷上端面外圈；4)、将专用盖板上的各剪开处向下弯折，勾住取向硅钢钢卷外沿；5)、扣上内罩，内罩底边砂封；6)、钢卷进炉，完成高温退火过程。本发明能有效保护钢卷边部，防止钢卷上端面翻边；该方法还能将钢卷内部水分排出，避免钢带表面氧化。

本发明公开了一种高硅钢的冷轧生产工艺。该生产工艺属于机械制造技术领域，其中的处理工序的加热工序通过电磁感应加热装置加热，待处理钢经过加热工序的速度为30‑200mpm，加热工序的加热温度为70‑120℃。本发明具有生产效率高和生产质量高的特点，特别是在加热工序中对待处理钢采用电磁感应加热装置进行加热，使其可以快速有效地提升温度，以满足高硅钢的冷轧生产工艺要求，减少断带事故，具有很好的实用性和创新性。

对无取向硅钢炼钢全流程钢液增钛的原因进行了分析,认为铁水钛含量、转炉出钢温度、转炉下渣量、精炼渣TiO₂含量、钢水罐及RH浸入管混钢种生产是影响钢液增钛的主要原因。通过采取低钛铁水冶炼,减少转炉下渣量,提高出钢温度,添加白灰改质精炼渣等措施,均能够降低钢液中的钛含量。 After analyzing the causes leading to increased content of titanium in molten nonoriented silicon steel during whole steelmaking process, it was concluded that such factors as content of titanium in hot metal, tapping temperature from converter, quantity of roughing slag entered into the ladle from converter, content of TiO₂ in refining slag, molten steel ladle car,carrying out the steelmaking of different steel grades by the same ladle and same RH immersion tube were the main causes ...