硅钢资料

【作者】 彭志华； ...

借助电子背散射(EBSD)技术对AlN为主抑制剂的Hi-B取向硅钢常化工艺的中间冷却制度进行了研究。结果表明:常化后试样均发生了完全再结晶,在60℃/s冷速下组织最均匀;在合适的冷却制度下常化板表层保留了强的Goss织构,它深入到1/4厚度处,并且形成对Goss织构有利的强{554}<225>织构。 The intermediate cooling system of Hi-B oriented silicon steel with AlN main inhibitor in normalizing process was studied by means of electron back diffraction(EBSD) technique. The results show that:the specimens after normalizing are fully recrystallization, and the microstructure is most uniform under the intermediate cooling rate of 60℃/s; under suitable cooling system, normalized plate surface retains strong Goss texture, it penetrates into the 1/4 thickness of the plate and forming strong {... 

本申请提供了一种取向硅钢铸坯的制备方法及铸坯系统，该制备方法用于对精炼后的钢水进行连铸处理，所述连铸处理包括以下步骤：进行凝固处理，以使所述精炼后的部分钢水凝固形成坯壳；凝固处理时，进行电磁搅拌，以使所述精炼后的剩余钢水最终形成铸坯，其中，所述电磁搅拌的位置和结晶器出口的间距为0.3～1.5m，所述电磁搅拌的电流范围为0A～900A。上述制备方法通过调节电磁搅拌的位置和电流大小来调节电磁搅拌的强度，进而通过电磁搅拌的强度来调节等轴晶的生成量，扩大等轴晶率的范围。

本发明提供了一种无取向硅钢RH顶枪喷粉脱硫工艺，RH脱碳结束测温定氧，立即加入铝粒脱氧合金化、之后立即依次连续加入合金进行成分调整，合金加完后立即开始顶枪喷粉；加入铝粒的量＝铝粒理论加入量+0.2‑0.4kg/t钢；喷粉时，控制喷粉速度与钢液循环流量相匹配；本发明从真空条件下脱硫热力学和动力学角度出发对具有顶枪喷粉功能的RH脱硫工艺进行改进，提高脱硫率。

本发明属于金属材料加工技术领域，具体涉及取向硅钢罩式炉高温退火低保温阶段节能工艺，包括：1)将涂镁取向硅钢卷装入密闭的罩式炉中，并向罩式炉内通入氮气将炉内氧气充分排出，使炉内氧含量浓度≤300PPm；2)通电升温并将氮气转换为10m3/h氮气与氨分解气的混合气体，升温2h将温度升温至500‑600℃后，恒温13h；3)将温度氮气与氨分解气的混合气体转换为12m3/h氨分解气，并升温2h将温度升至650℃恒温15h，使内部气体露点小于‑10℃；本发明提供退火工艺，钢卷在高温下不被水蒸汽氧化，消除钢带表面露金、发红、发黑、水印、色泽不均、导通缺陷，降低钢带铁损、提高磁感、降低生产成本。此外，本发明进一步减少退火过程中氨分解气的用量，具有极高的工业应用价值。

本实用新型公开了一种铁芯硅钢片卷材的自动放卷上料装置，包括放卷机、导向平台和防折组件，所述导向平台间距设置在放卷机的下方，所述导向平台与放卷机之间构成供料带缓冲的缓冲空间，所述料带在缓冲空间内呈U型状走向，所述导向平台的上方间距设置有防折组件，所述防折组件与导向平台之间构成供所述料带通过的导向通道，所述防折组件设置在料带的内弯侧。通过防折组件对料带的内弯侧进行支撑，能够有效的防止料带被过度弯折，能够对料带进行缓冲和缓冲保护，保证料带放卷上料的稳定性。

本实用新型属于抛丸设备技术领域，具体涉及一种硅钢抛丸用耐磨抛丸头，包括壳体、进丸管、定向套、分丸轮、多块截面呈工字形的叶片和两块对称设置的护板，多块叶片沿护板的周向均匀分布，叶片安装在两块护板之间；叶片的左右两侧分别设有一组卡槽，一组卡槽包括两个卡槽，一组卡槽上滑动连接有能与叶片表面接触的耐磨板；叶片上设有用于固定耐磨板位置的固定件；壳体内可拆卸的安装有耐磨衬板。在本方案中，将耐磨板可拆除的安装在叶片中，耐磨板对叶片有保护的作用，能避免叶片被磨损；当耐磨板损坏后只需更换新的耐磨板，而不需更换叶片，能够有效节省成本。同样的耐磨衬板对壳体也有保护作用，能够在很大程度上减少壳体被磨损。

采用节能、环保、经济型的生产技术与工艺来制造高磁感取向硅钢目前已成为世界各大取向硅钢生产厂的研发热点。总结了国内外各大钢铁企业与研究机构采用低温板坯加热技术生产高磁感取向硅钢的开发及应用情况,概括了传统流程实现低温板坯加热技术的方法。介绍了薄板坯连铸连轧与双辊薄带连铸等短流程工艺生产高磁感取向硅钢的研发现状。在此基础上,探讨了高磁感取向硅钢生产技术与工艺的发展趋势及方向。 Utilizing energy-efficient,environmentally friendly,economic production processes and technologies to manufacture high magnetic induction grain-oriented silicon steel has become the focus of current research work.Based on using low-temperature slab reheating techniques to produce high magnetic induction grain-oriented silicon steel at both iron and steel enterprises and research institutions all over the world,the current application and exploitation was thoroughly generalized;the implementation... 

取向硅钢成品的晶粒尺寸非常大,其易磁化方向[001]晶向对于轧向的偏差角度对其磁性能影响极大。本文介绍了取向硅钢二次再结晶后成品晶粒位向的几种测定方法,包括侵蚀法、劳厄法、OIM法、极图法和非对称X射线衍射法等,并对这几种测量方法进行了比较。 The finished product of grain-oriented silicon steel has immense grain size ranging from millimeters to centimeters and the deviation angles of easy magnetization direction from rolling direction plays a remarkable role in magnetic properties of grain-oriented silicon steel.The methods in common use for determining the deviation angles of crystal direction are introduced,which include the etch-figure method,the Laue method,the OIM method,the pole figure method and the asymmetrical X-Ray diffract... 

采用传统的轧制和退火工艺制备了0.30mm厚的6.5%(质量分数)Si高硅电工钢薄板,采用X射线衍射技术对退火过程中的再结晶织构进行了研究。冷轧高硅钢薄板700℃退火形成以{111}〈112〉为峰值的γ织构(〈111〉∥ND)和以{001}〈210〉为峰值的{001}织构;而900℃以上温度退火则形成强{001}〈210〉织构。进一步的研究表明是在晶粒长大过程中{001}〈210〉发展成为主要再结晶织构组分。 High silicon steel thin sheets with thickness of 0.3mm were successfully produced by conventional rolling and annealing methods.Recrystallization texture was investigated by means of X-ray diffraction.It is found that recrystallization texture is mainly composed of γ fiber(〈111〉∥ND)with peak at {111}〈112〉 and {001} fiber with peak at {001}〈210〉 after annealing at 700℃,while strong {001}〈210〉 component dominates recrystallization texture after annealing above 900℃.It is during grain growth that {... 

通过在实验室条件下模拟薄板坯连铸连轧流程,并在以Cu2S为主抑制剂制造普通取向硅钢(CGO)的基础上,加入适量钒钛,研究了钒钛对取向硅钢组织与磁性能的影响。结果表明,适量钒钛使热轧板和脱碳退火板组织更好,尤其使脱碳退火板的晶粒更加细小和均匀;加入适量钒钛不但使热轧板表面高斯织构强度更高,更使脱碳退火板中有利于高斯织构发展的γ织构强度更高;适量钒钛能形成Cu2S+(V,Ti)N等复合析出物,起到辅助抑制剂作用,加强抑制能力。细小均匀的晶粒、强度更高的有利织构和更强的抑制能力使CGO钢磁性能更佳。 Effect of V and Ti on microstructure and magnetic properties of conventional grain-oriented silicon steel(CGO) were investigated under simulated thin slab continuous casting and rolling process in laboratory with Cu2 S as the dominant inhibitor. The results show that appropriate amount V and Ti make the microstructures of the hot rolled sheet and the decarburizing annealed sheet better,especially make the grains of the decarburizing annealed sheet more tiny and uniform. Adding appropriate V and ... 

本实用新型公开了一种新型取向硅钢薄板，所述硅钢薄板包括薄板主体,薄板主体呈方形,薄板主体的内部具有硅钢基板,所述薄板主体的上部具有耐磨层,耐磨层底部还具有抗压层，耐磨层具有若干均匀分布的耐磨条,耐磨层之间分别等距间隔布置，间隔的耐磨条之间形成透气槽,透气槽具有两个侧边，透气槽底部具有透气通孔,所述透气槽两侧具有导风侧凸条,导风侧凸条具有根部和端部，根部分布在透气槽的底部左侧和右侧位置，所述端部延向透气槽两侧边部上部，所述耐磨条为均匀排列的若干双V型结构，双V型结构纵向排列，耐磨条和抗压层之间具有硬质包覆层，在不影响耐磨作用的前提下能够起到透气通风的效果，不需要增加硅钢薄板的厚度。