在Gleeble-3500热/力模拟试验机上对HW600钢进行高温压缩试验,研究在不同试验条件下的变形抗力。试验结果表明:变形温度对变形抗力的影响最为显著,在相同的变形速率下,随着变形温度的升高,变形抗力降低;在同一变形温度下,变形速率增大,变形抗力增加;在同一变形温度、变形速率下,随着变形程度的增加,变形抗力急剧增大,真应变达到0.1后,变形抗力增加趋势变缓。 The high-temperature compression test is done for HW600 steel with Gleeble-3500 thermal simulation testing machine to research its resistance to deformation under different test conditions.It is showed from result that deformation temperature has greatest effect on the resistance,and along with the temperature getting higher the resistance lowered under same deformation rate;the resistance increases along with deformation rate getting greater under same temperature;and under same deformation tem... 

【作者】 朱传芳； 潘恒韬； ...

本发明提供一种硅锰镇静无取向硅钢冶炼方法。该无取向硅钢化学成分质量百分比为C≤0.005％，Si：0.25％‑1.20％，Mn：0.2％‑0.8％，P：0.015％‑0.065％，S≤0.005％，Als≤0.005％，余量为Fe及不可避免的杂质。其生产方法包括转炉出钢结束加石灰、渣面脱氧剂调渣；RH真空精炼脱碳结束后进行脱氧合金化，合金化后3‑5min由真空室料仓加入合成渣，处理一段时间后净循环8‑12min，破空出钢运至连铸浇注。得到钢水中主要为SiO2‑CaO‑Al2O3系夹杂，一方面避免了钢水中生成低熔点SiO2‑MnO系夹杂，轧制过程沿轧制向伸长，阻碍晶粒长大；另一方面也避免了生成纯SiO2或高SiO2组分类酸性夹杂，导致冶炼过程耐火材料的严重侵蚀。本发明可控制钢中非金属夹杂物类型，提高钢水洁净度，改善冶炼过程中对耐火材料的侵蚀。

本发明涉及一种消除硅钢边部翘皮的方法及硅钢，包括预处理板坯；加热预处理后的板坯，并控制所述板坯在加热炉的预热段时间不低于40分钟；粗轧板坯，并调整所述板坯侧压的减宽量为成品硅钢宽度的0.8％～1.2％；以及控制侧压立辊的凸缘与所述板坯的边部之间保留间隙。本发明所述的消除硅钢边部翘皮的方法及硅钢，能够显著消除硅钢的边部翘皮，以及在不能完全消除边部翘皮缺陷的情况下，约束翘皮位置发生在距离边部＜8mm区域，工艺调整简单易操作，不需要调整现有设备和系统架构，显著提升硅钢表面质量。

运用EBSD和光学显微镜,研究了0.25%~0.45%Cu对无取向电工钢热轧板显微组织,成品板显微组织、织构和磁性能的影响。实验结果表明:卷取过程中Cu元素在热轧板表层的偏聚作用显著阻碍了热轧板表层再结晶晶粒长大,导致热轧板表层晶粒尺寸随着Cu含量增加而逐渐较小,但热轧板中间晶粒尺寸变化不大。同时发现Cu元素能够明显改善织构类型,使有利织构组分增加,不利织构组分减少,同时减弱织构强度。从实验结果可知0.35%Cu能够显著改善电工钢的磁性能,铁损P15/50最低达到4.1 W/kg,磁感B50最高值达到1.8 T。 Effects of high content Cu on microstructure of hot rolled plates and microstructure,texture and magnetic properties of annealed finish product plates of non-oriented electrical steel were examined by means of EBSD technique and optical microscope. The results show that surface segregation of Cu significantly hindered recrystallized grain growth of surface layer in hot rolled plate during the coiling,as a result,the surface grain sizes of the hot-rohed plates decrease with the increase of Cu con... 

【摘要】 <正>为了确保电工钢的产品质量,在生产线...

本实用新型公开了一种用于硅钢板带加工的整平装置，包括底座，所述底座的上表面固定设有下安装座，所述下安装座上设有下整平机构，所述底座的上表面固定连接有门型安装架，所述门型安装架的顶部贯穿设有螺杆，所述螺杆的底面设有上安装座，所述上安装座的正面通过轴承座转动连接有第三转轴，所述第三转轴的外表面固定连接有调向齿轮，所述上安装座上设有上整平机构。本实用新型通过设置通过设置多组上整平辊和下整平辊，改善该装置的整平效果，且通过转动齿轮与调向齿轮的设置，使该装置的多个上整平辊同步转动，且相邻两个整平辊之间的间隙可以设置的较小，使该装置结构紧凑，提高空间利用率。

结合硅钢退火炉项目中应用PDSOFT软件进行三维配管设计的案例,描述PDSOFT软件的应用过程,总结其使用要点,分析其优缺点,并提出了推广三维设计软件的思路,对今后PDSOFT在相似项目中的推广应用有参考和借鉴价值。 Combining the case of using PDSOFT software to design the three-dimensional piping,the application process of the PDSOFT software is described,the using points are summarized,the advantages and disadvantages are analyzed,and the ideas of promoting the three-dimensional design software are put forward,which have a strong reference value for the promotion and application of PDSOFT in similar projects in the future. 

通过Axio Imager金相显微镜考察4.5%~7.0%硅(质量分数)对高硅钢材料组织形貌的影响,并利用Fe-6.5%Si高硅钢薄板制备方法对其进行轧制,通过DDL50电子万能试验机对阶段产品进行力学性能测试。结果证明,硅含量为5.58%的高硅钢在实验硅含量区间内存在最大延伸率及最小铸态组织晶粒尺寸。 An investigation about the influence of 4.5%-7.0% Si on microstructure and mechanical properties of high-silicon steel was presented.SEM was adopted to take an observation towards microstructure during fabrication,and DDL50electronic universal testing machine was applied into the detection of tensile curves.The results show that silicon steel with 5.58% Si provides the maximum elongation and minimum grain size as cast. 

采用扫描电镜、原子力显微镜研究了铬酸镁半无机绝缘涂层的微观结构。结果表明,涂层厚度为数微米,涂层中的有机树脂乳液颗粒均匀分布在无机涂层的表面,从而保证了涂层具有良好的冲片性能。采用极化曲线研究了涂层的耐蚀性能,发现铬酸镁与铬酸锌绝缘涂层的耐蚀性能相当。 In this paper,the microstructure and anti-corrosion property of magnesium chromate coating on non-oriented silicon steel were studied.The microstructure was observed by SEM and AFM.The anti-corrosion properties were evaluated by polarization curves.The results show that the thickness of coating is several microns and the polymer particles were scattered on the surface of inorganic coating,which is the guarantee for lamination property.The corrosion resistance of the magnesium chromate film was e... 

本发明属于涂料技术领域，具体公开了一种用于取向硅钢的无铬无机绝缘涂料，包括以下重量份配比的原料：小颗粒硅溶胶10‑50份、大颗粒硅溶胶10‑50份、磷酸二氢铝溶液5‑50份、助剂0.1‑10份及水10‑100份。本发明还提供了一种用于取向硅钢的无铬无机绝缘涂料的制备方法，通过将小颗粒硅溶胶和大颗粒硅溶胶混合均匀成硅溶胶混合液后加水得到混合硅溶胶水溶液；再依次向其中加入磷酸二氢铝和助剂并持续拌至均匀，得到用于取向硅钢的无铬无机绝缘涂料。本发明提供的无铬无机绝缘涂料适用于取向硅钢，使取向硅钢环保无害的同时具有与含铬取向硅钢相当的耐腐蚀时效，从而实现取向硅钢产业绿色化并大大改善取向硅钢的综合性能。

主要研究了0.7%Si无取向电工钢退火试样的组织、晶粒尺寸和织构对其磁性能的影响。结果表明,随着退火温度的升高,晶粒尺寸逐渐增大,组织的均匀性得到改善;ɑ取向线上的纤维织构多集中于{114}<110>和{223}<110>附近,再结晶结束后,织构含量变化不大。{111}<110>织构取向密度值随温度升高而下降,{112}<111>织构与{111}<110>织构变化相反。晶粒尺寸增大对磁感强度的影响较小,而对铁损的影响较大。 Influences of microstructure,grain size and texture on the magnetic properties of 0.7% Si non-oriented electrical steels annealed samples were studied.The results show that with annealing temperature increasing the average grain size is increased gradually.Uniformity of the microstructure is improved;the textures of ɑ-fiber gathered in the vicinity of the { 114} < 110 > and { 223 } < 110 > texture.After recrystallization,the volume fraction of texture changes small.{ 111} < 110 &g...