硅钢资料

本发明提供一种超低铝无取向硅钢夹杂物控制方法。该钢种化学成分质量百分比为C≤0.005％，Si：0.25％‑1.50％，Mn：0.15％‑0.55％，P：0.02％‑0.06％，S≤0.005％，Als≤0.005％，余量为Fe及不可避免的杂质。工艺流程为：KR→BOF→RH→连铸。转炉出钢严格控制下渣量，出钢结束加石灰、渣面脱氧剂调渣；RH脱碳结束后，先加低碳低硫硅铁、金属铝或铝钙铁合金复合脱氧，最后加入金属锰、磷铁进行合金化，然后净循环6‑10min，破空出钢运至连铸浇注。得到钢水中主要为SiO2‑Al2O3系夹杂，避免了生成低熔点SiO2‑MnO系夹杂，轧制延展变长，影响晶粒长大；同时也避免了生成高SiO2组分类酸性夹杂，导致耐材的侵蚀。可显著改善钢中非金属夹杂物类型，提高无取向硅钢的性能，并提高了钢水浇注性能。

目前随着电工钢用户冲压设备的升级,冲压速度逐步提高,对电工钢产品的硬度和强度指标提出了更高的要求。与普通硬度级别的无取向硅钢相比,高硬度50BW600的Hv硬度提高15~20,达到125以上,同时对电磁性能指标也有较高要求。本钢通过化学成份和热轧及冷轧连退生产工艺的设计,经过小批量生产试验,满足用户要求。通过对工艺的严格控制,在大批量生产过程中,保证了产品的力学性能和电磁性的检验合格率。 Currently with upgrading of stamping equipment of silicon steel user, gradually increasing of stamping speed, propose higher demand for hardness and strength of silicon steel. Compared with conventional 50BW600, high hardness 50BW600 have higher hardness, reach greater than 125Hv. Through design of chemical composition with hot mill and annealing, production test of small quantities, stamping performance meet user request. 

一种硅钢变压器绕线模具，包括模具本体、顶梁、举升梁、螺杆、绕盘，其特征在于顶梁设置在模具本体的顶部，举升梁设置在模具本体的下端，模具本体的顶端设有螺丝杆，顶梁穿过螺丝杆通过活动螺母固定，模具本体的中部设有镂空，螺杆转动设置在镂空中，螺杆穿过模具本体下端与绕盘连接，模具本体的中部设有至少两个连接梁，举升梁在连接梁中穿过移动，并且中部穿过螺杆，模具本体的底部设有槽体，模具本体的中部连接梁与槽体底部链接，举升梁移动到最低点时设置在槽体内，本方案通过螺杆和绕盘以及举升梁的相互作用将线圈通过机械能作用顶出模具，省去了人为的力量。

根据本发明的一个实施例的取向电工钢板用退火隔离剂组合物，其包含复合金属氧化物，复合金属氧化物包含Mg和金属M，金属M是Be、Ca、Ba、Sr、Sn、Mn、Fe、Co、Ni、Cu和Zn中的一种以上。

本实用新型涉及硅钢开卷领域，具体涉及一种方便更换硅钢卷的结构，包括机架、支撑台、动力件、支撑块、支撑辊、第一挡环和第二挡环，动力件滑动设置于支撑台上，支撑辊与动力件连接，支撑辊的自由端与支撑块接触；第一挡环靠近支撑台且与支撑辊固定连接，第二挡环靠近支撑块且与支撑辊滑动连接，支撑辊沿其轴向设有键槽，第二挡环上固定有滑键，滑键滑动设置于键槽内；第二挡环上设有弧形通槽，机架上设有连接件，连接件能穿过弧形通槽与第二挡环固定连接。采用本技术方案时，有利于防止硅钢卷发生偏移，另外方便更换硅钢卷。

一种电工钢切片用导向装置，涉及电工钢生产装置技术领域，包括导向台、支撑腿、安装块、转轴、辊体、电动机、安装板、滑杆、移动板和导向板；支撑腿设置在导向台底部；安装块设置有两个，两个安装块均设置在导向台横向一侧，两个安装块沿纵向分布；转轴转动设置在两个安装块之间；辊体设置在转轴上，辊体位于两个安装块之间，辊体位于导向台上方；电动机设置在安装块上，电动机与转轴驱动连接；安装板设置有两个，两个安装板分别设置在导向台纵向两侧上部；滑杆设置有两个，两个滑杆均设置在两个安装板之间，两个滑杆沿横向分布。本实用新型能够在电工钢的钢带切片之前进行导向限位工步，使得电工钢切割时不会被切割歪，切片的精度高。

热卷箱位于热连轧带钢生产线粗轧与精轧机之间,是热连轧生产中比较理想的中间保温设备。由于取向硅钢变形温度区间较窄,在生产中易出现边裂现象,同时中间坯的边部温度难于得到保证,因此一般不采用热卷箱设备生产,限制了传统热连轧生产线产品开发的品种。通过合理优化热卷箱控制工艺参数,解决了某厂传统热连轧生产线用热卷箱生产取向硅钢的边部质量问题,成功地生产出取向硅钢带。 The hot coil-box is an ideal heat retaining apparatus for hot rolling,lined between roughing mill and finishing mill. But oriented silicon steel has a narrow deformation temperature range,so that the edge crack easily occurs and it is difficult to insure the temperature of the intermediate blank. Therefore,the hot coil-box is rarely used in producing oriented silicon steel,which restricts the product development of the traditional hot rolling line. The article reasonable optimized process parame... 

本发明属于取向硅钢制备技术领域，具体涉及一种软磁材料取向硅钢退火工艺。所述退火工艺主要包括：涂覆隔离剂、按照一定速率升温后进行保温，以5‑10℃/min的速率进行降温；在降温过程中施加恒定磁场，之后继续降温即可实现。该退火工艺能够有效降低铁损失，提高磁感强度。同时具有较好的耐腐蚀性能和机械性能。

研究了传统工艺流程生产的2%Si无取向电工钢在不同退火温度下的磁性能。研究结果表明,随着退火温度的升高,显微组织均匀性提高且晶粒尺寸增大;有利织构组分{100}<0vw>、α、η增强,不利织构组分减弱;成品的铁损P1.5/50先下降后略有上升,磁感B50上升平缓;在890℃×2 min的退火工艺条件下,成品电工钢的磁性能最佳,对应的铁损P1.5/50小于3.2 W/kg,磁感B50高于1.74 T。 In this paper,the effect of annealing temperature on magnetic properties of non-oriented electrical steel with 2% silicon was studied.Results show that the uniformity of microstructure and the average grain size increase with the rise of annealing temperature.The texture components of annealing can be improved by enhancing {100} <0vw>,α,η fiber textures and weakening {111} <112> fiber texture.The tendency of core loss P1.5/50 shows that it decreases first and then increases,while the... 

本实用新型提供了一种轴向磁通电机转子的硅钢盘，所述硅钢盘具有沿周向间隔排列的多组转子槽，相邻的两组转子槽之间界定了一硅钢块，每组转子槽的数量为两个，且相对设置于所述硅钢盘轴向的两侧，每组的两所述转子槽之间界定了一连接相邻两所述硅钢块的连接筋，多个所述硅钢块通过连接筋连接，并形成一整体的硅钢盘，相对现有技术独立成型多个硅钢块来说，不仅避免硅钢块丢失，还有效提升硅钢盘装配为转子盘的成型效率，以及保证各硅钢块在转子盘上的位置一致性，从而大幅增强转子盘的机械可靠性。

本实用新型公开了高牌号取向硅钢生产用辊轧机，包括辊轧机本体和夹送辊，所述辊轧机本体的底端安置于承托组件的顶端，且承托组件的两侧对称设置有机架，所述辊轧机本体一侧的机架顶端对称安装有两个换向机构，且两个换向机构顶部的一侧共同设置有上下两个夹送辊。该种高牌号取向硅钢生产用辊轧机中不仅能够通过两个液压缸同步伸缩，带动横担的两端反向旋转，从而灵活调节夹送辊的相对水平高度，进而提高了钢带输送角度的调节效率；而且在夹送辊旋转输送钢带时，换热介质经由两组导液管、旋转接头在夹送辊中输入、输出，通过直接接触进行全面换热，如此循环往复，进一步提高了对钢带的冷却效率。

借助实验室设备研究了B元素对高牌号无取向硅钢热轧板组织和磁性能的影响。结果表明,与无硼钢相比,含硼钢的热轧板晶粒尺寸略小,析出物的类型和尺寸没有区别,主要是AlN和(AlN+MnS)复合析出物,少量的MnS析出物,尺寸集中在1.0～2.5μm范围内。未发现BN析出物。在力学性能方面,B对钢的软化作用不明显。在磁性能方面,含硼钢的铁损为3.215W/kg,磁感为1.710T,综合磁性能比无硼钢差。 Influences of boron on microstructure and properties of hot rolled band in high-grade non-oriented silicon steel are researched in this paper by experimental equipments.Compared with boron-free steel,the result shows that boron-bearing steel has smaller grain size,but the type and size of precipitations have no differences.The main precipitates are AlN,(MnS + AlN) composite precipitate and few MnS,the range of which are between 1.0 μm and 2.5 μm.BN precipitation is not found.With reward to mecha...