硅钢资料

通过对湿H2气氛下,相同退火温度、不同退火时间的CGO硅钢初次再结晶样品进行金相组织观察,并进行了EBSD微观织构分析,研究了CGO硅钢初次再结晶过程中的组织及再结晶织构演变行为。结果表明,在湿H2气氛下,820℃保温,CGO硅钢初次再结晶过程约在120 s时完成。随着退火时间的延长,γ面上{111}<112>织构含量逐渐减少,{111}<110>织构先减少后增多,随着再结晶的完成,部分{111}<112>取向晶粒向高斯{110}<001>取向转化的同时,也向{111}<110>取向转化,高斯{110}<001>织构含量逐渐增多。高斯取向晶粒较多是由{111}<112>取向晶粒转化而来,同时也证明了CGO硅钢高斯取向晶粒的二次再结晶异常长大生长机制为择优形核。 Microstructure development and texture evolution of conventional grain oriented silicon steel,which were annealed at same annealing temperature and different annealing time under wet H2 atmosphere,were investigated through metallographic observation and electron backscattered diffraction analyzing.The results show that the primary recrystallization finishes in 120 s at 820 ℃ under wet H2 atmosphere.With the extending of annealing time,{111}<112> texture decreases,{111}<110> texture d... 

本实用新型涉及一种无取向硅钢蠕变性能测试装置，包括基座，基座的顶部和侧面设有开口；试样夹持装置，试样夹持装置安装在基座的顶部，用于夹持硅钢蠕变试样；转换力杆，转换力杆安装在基座的侧面，与试样夹持装置连接；可调节式砝码盘，可调节式砝码盘安装在转换力杆上，可调节式砝码盘上能够放置不同重量的砝码，转换力杆将砝码的重力转换成水平力，以实现对硅钢蠕变试样不同应力水平的加载；可调节式灯座，设置在试验腔内并与基座的侧面插接；加热装置，放置到可调节式灯座上，用于给硅钢蠕变试样加热。本实用新型具有解决无法实现不同应力和温度下硅钢材料的蠕变研究的问题的效果。

本发明涉及取向硅钢高温连续退火炉领域，尤其涉及一种取向硅钢高温连续退火炉隔离装置，包括安装在炉壳上的隔离炉门及设置在隔离炉门四周的密封井；隔离炉门顶部两侧安装有水冷却装置；水冷却装置上部设有隔离炉门动力牵引装置；密封井包括固定密封井和伸缩密封井，伸缩密封井位于固定密封井内部并与固定密封井滑动连接，伸缩密封井与固定密封井端部连接处设有密封装置。本发明可以确保隔离炉门升降过程中实现无缝全密封状态，提高密封效果，且采用伸缩密封井实际降低了密封井的高度，间接降低了水冷却装置连接管道上升至最高点的净空标高，与传统固定式密封井高度相比可以降低高度50％～80％，从而降低厂房净空标高，节省厂房基建投资。

本发明揭示了一种高牌号无取向硅钢及其生产方法，生产方法包括冶炼、连铸、热轧、酸洗、切边、常化、冷轧，冶炼最终所得钢水化学成分以质量百分比计为：C≤0.005％、Si≥2.8％、Als0.5～1.2％、Mn0.25～0.8％、P≤0.02％、S≤0.0040％、N≤0.0020％、Nb≤0.0020％、V≤0.0020％、Ti≤0.0020％，其余为Fe以及不可避免的杂质；切边工序对热轧卷板的两侧进行切边，单侧的剪切宽度为10～20mm；常化在罩式退火炉中进行，均热温度为T＝{(990～1010)‑100×[30×(Si)+20×(Al)]}℃，(Si)为Si的质量百分比，(Al)为Al的质量百分比，均热时间为6h，之后冷却；钢卷在罩式退火炉中冷却至预设温度T0时取出送至冷轧线冷轧，T0为120～180℃，第一道次轧制时的轧制力恒定且轧制力为11000～12000kN。本发明可避免高牌号无取向硅钢在冷轧过程中由于脆性高而导致的频繁断带。

本实用新型涉及一种硅钢片图像采集装置，在固定支架上设置有工业相机，所述的工业相机可以沿垂直方向上下移动或者沿水平方向前后移动，通过上下移动或者前后移动对硅钢片的形状和尺寸、硅钢片叠积形成的铁芯进行实时图像采集。固定支架包括：固定底座、支撑杆和工作台面，一对固定底座平行对称设置，所述的固定底座上对称设置两条竖直支撑杆，竖直支撑杆的上端面固定连接工作台面，在两条竖直支撑杆的中间位置设置升降丝杆，水平支撑杆的两端分别与升降丝杆的升降螺母固定连接，相机滑台活动设置在水平支撑杆上。本实用新型通过工业相机的上下前后移动，实现了硅钢片形状尺寸和硅钢片高度即时拍照测量，较人工测量提高了测量精度及准确性。

概述了无抑制剂法生产取向电工钢的特性及其用途;总结无抑制剂生产取向电工钢的原理及工艺方案.重点讨论了成分方案,即元素对磁性能的影响和最终高温退火方案对二次再结晶的影响.研究结果表明,无抑制剂取向硅钢化学成分范围没有普通取向硅钢和高磁感取向硅钢严格,提高了成材率;最终高温退火决定了二次再结晶的好坏,从而最终决定成品磁性能,最佳的高温退火温度在850～950℃之间. This article provides an overview on the characteristics and uses of inhibitorless process producing grain-oriented electrical steels.The mechanism of inhibitorless process and technology programs were discussed.The results show that the chemical composition and final annealing were determined according to magnetic properties.The inhibitor-free grain oriented silicon steel has loose range of chemical composition;Secondary recrystallization occurs mainly in the final annealing and the best anneal... 

分析了高转矩和高转速条件下高效驱动马达铁芯材料对无取向硅钢磁性能要求,讨论了无取向硅钢的高磁通密度和低铁损对电机转矩和效率的影响,介绍了国内外高磁感无取向硅钢发展情况。在生产工艺上,提高钢质纯净度,弱化夹杂物和第二相粒子对畴壁移动和再结晶晶粒长大的钉扎作用,添加微量晶界和带钢表面的偏析元素促使有利织构发展等技术可提高无取向硅钢的磁通密度。 The requirements of high efficient drive motor core materials under the conditions of high torque and high speed were analyzed.The effects of high magnetic flux density of non-oriented silicon steel on the torque and efficiency of the motor were discussed.The development of non-oriented silicon steel with high magnetic was introduced.The magnetic flux density of non-oriented silicon steel sheet can be obviously improved by some production technologies,such as purification steel,weakening the pin... 

本发明涉及一种控制高牌号硅钢退火产生月牙印缺陷的方法，多次调整硅钢退火线入炉及出炉张力参数，使带钢处于预设悬垂量内；本发明避免高速运行下带钢撞在炉辊上，从而产生月牙印缺陷，提高了产品的质量。

介绍了双蓄热燃烧技术的特点和高温硅钢加热炉的特点,探讨了双蓄热燃烧技术在高温硅钢加热炉中使用的技术难点,分析了双蓄热燃烧技术在高温硅钢加热炉上使用的可能性。 Introduced characteristics of double regenerative combustion technology and high temperature silicon steel reheating furnace,discussed technical difficulties for using double regenerative combustion technology,analyzed the possibility of double regenerative combustion technology applied to high temperature silicon steel reheating furnace. 

本申请提供了一种取向硅钢铸坯的制备方法及铸坯系统，该制备方法用于对精炼后的钢水进行连铸处理，所述连铸处理包括以下步骤：进行凝固处理，以使所述精炼后的部分钢水凝固形成坯壳；凝固处理时，进行电磁搅拌，以使所述精炼后的剩余钢水最终形成铸坯，其中，所述电磁搅拌的位置和结晶器出口的间距为0.3～1.5m，所述电磁搅拌的电流范围为0A～900A。上述制备方法通过调节电磁搅拌的位置和电流大小来调节电磁搅拌的强度，进而通过电磁搅拌的强度来调节等轴晶的生成量，扩大等轴晶率的范围。

该电磁钢板为母材钢板的其中一个或两个表面中的至少一部分被具有接合能力的绝缘被膜覆盖的电磁钢板，所述绝缘被膜的25～100℃的温度范围的对数衰减率为0.3以下。

本发明公开了一种高磁感取向硅钢高效脱碳退火工艺，主要工艺流程为：炼钢连铸→热轧→酸洗常化→冷轧→脱碳和初次再结晶退火→渗氮处理(低温Hi‑B)→涂覆氧化镁隔离剂→高温退火→拉伸平整退火→涂覆绝缘涂层→精整，低温HiB不同于高温Hi‑B的工艺流程主要是在脱碳退火后增加了渗氮段。本发明在保证产品实物质量不低于现有水平(国内领先水平)的前提下，使Hi‑B钢退火效率达到世界领先，制造成本大幅降低。