硅钢资料

针对采用含钒铁水生产无取向电工钢存在的铁水脱硫率低、转炉冶炼过程回硫量大、成品硫含量偏高的问题,通过对含钒钛铁水脱硫,减少转炉冶炼过程回硫以及RH脱硫技术等方面的研究,大幅度降低了电工钢成品硫含量。生产表明钢中w(S)=0.001 9%～0.006 9%,平均为0.004 2%;w(S)≤0.008%的比例达到了100%,且w(S)≤0.005%的比例也达到了91.43%。 In cognizance of the problems of low desulphurization rate for hot metal,large sulfur-recovery in converter as well as high sulfur content in products in producing non-orientation electrical steel with vanadium-content hot metal countermeasures have been carried out.Sulfur content in non-orientation electrical steel is decreased obviously by way of study on technologies of desulphurization for hot metal with vanadium & titanium,sulfur-recovery control in converter and desulphurization in RH ... 

本发明涉及一种混合硅钢定子结构及与其配套的转子结构及永磁电机，属于电机技术领域，包括：定子，由多个第一硅钢片叠压构成；多个线圈绕组，均匀设置在定子的内壁上；第一硅钢片包括：多个连接块与多个连接臂，连接块与连接臂交替排列构成硅钢环片，连接块采用无取向硅钢且与两侧的连接臂通过拼合结构连接，连接臂采用取向硅钢；多个定子齿，呈放射状均匀设置在硅钢环片的内侧，定子齿与连接块也通过拼合结构连接，定子齿采用取向硅钢；本发明通过取向硅钢、无取向硅钢混合组成的定子，能够有效提导磁性能；本发明能够稳定提升定子上的磁性能，增加电机的输出能力，实用性强，值得推广。

本实用新型公开了一种具有自动接料机构的变压器硅钢加工用防刮伤剪床，包括支撑座，所述支撑座的上端固定连接有相互对称的进料机构与出料机构，所述进料机构上设置有调节机构，所述进料机构与出料机构之间设置有切割底座，所述切割底座的两端设置有气缸，所述气缸的内侧设置有切割机构，所述切割机构上设置有卡接机构，所述出料机构的一侧设置有接料机构；本实用新型涉及剪床技术领域。该具有自动接料机构的变压器硅钢加工用防刮伤剪床，切割后的硅钢，通过出料机构输送至承接板上，挡板与侧板能够使得硅钢能够自动叠放整齐，自动叠放整齐相对于人工接料可明显节省时间，提高剪床的运行效率，减少人力成本，提高运行的安全性。

介绍了微合金元素锡、铌、稀土对无取向硅钢性能的影响,并扼要分析了这些元素对硅钢性能的影响机理:晶界偏聚元素Sn可细化晶粒提高硅钢磁性能;微合金元素Nb细化铁素体晶粒,提高硅钢的强度、韧性和塑性及磁性能;稀土元素(RE)在硅钢中的主要作用包括净化钢液、变质夹杂物、改善铸态组织和性能及微合金化,减少晶界上出现偏析的几率。 The influence of micro-alloy elements on properties of non-oriented silicon steel and the mechanism for effect of the micro-alloy elements including Sn、Nb and RE on the properties of steel are presented and analyzed in this paper.Grain boundary segregation elements Sn in steel can grain refinement and improve the magnetic properties;Micro-alloy elements Nb can refine the ferrite grain,increase the silicon steel strength,toughness and plastic;The main role of the RE in the silicon steel including... 

【作者】 张正贵； 李战库； ...

为研究常化温度对热轧无取向硅钢组织与织构的影响,采用光学显微镜、背电子散射衍射技术研究了不同常化温度对其影响。结果表明,实验硅钢板在700～850℃温度下常化时,随常化温度的升高,晶粒尺寸增大,有利组分α织构增强,不利组分γ织构降低。对比研究了800℃和850℃常化热轧板CSL晶界分布图与取向差分布图,在本文研究条件下,Goss织构易在Σ=3,9的CSL晶界及晶粒取向差为30°～55°处形成。 The hot strips normalized at different temperatures were investigated by optical microscope and EBSD to study the effect of normalizing temperature on microstructure and texture of hot-rolled non-oriented silicon steel sheets.The results show that the grain size increases,the intensity of α-fibre texture increases,and the γ-fibre texture decreases when the hot strips are normalized at the 700-850 ℃.And CSL boundaries of Σ=3 and 15,and misorientation angles between 30° and 55° are more likely rel... 

研究了退火温度和退火时间对电沉积硅钢试样中的断面层组织、硅在试样中的分布情况、织构分布和磁性能的影响。结果表明:退火温度为1000℃、退火时间为210 min时得到的试样晶粒分布均匀、硅在试样中分布均匀、硅平均浓度为6.3715%(接近6.5%)。试样的织构分析及磁性能检测的结果表明,在较高温度下延长退火时间可增加{100}和{110}面织构,降低铁损,所得试样的磁性能较为良好。 The effect of annealing temperature and time on the microstructure, distribution of silicon,texture and magnetism of the high silicon steel prepared by electrodeposition was investigated. The results showed that after annealing at 1000℃ for 210 min, the mean grain size of steel was about 190 μm with a uniform grain size distribution, and the silicon is also uniformly distributed on the entire cross section with an average Si concentration 6.3715%(close to 6.5%); With the increasing annealing tim... 

采用双辊连铸工艺制备了硅的质量分数分别为0.5%,1.0%,3.0%,4.5%的硅钢薄带,用光学显微镜观察其组织,并研究了后处理工艺对薄带组织和性能的影响。结果表明:硅含量为0.5%和1.0%的薄带适合采用一次冷轧+850～950℃退火的后处理工艺,而硅含量在3.0%以上的薄带适合采用二次冷轧+950℃退火的后处理工艺;硅含量为3.0%和4.5%的薄带在冷轧并950℃退火后,其磁性能最佳,铁芯损耗约为4.30 W·kg^-1,磁感应强度约为1.68T。 Silicon steel thin strips with silicon content of 0.5wt%,1.0wt%,3.0wt%and 4.5wt%were prepared by twin-roll continuous casting process,and the microstructure of the strips were observed by means of optical microscopy,and on the basis,the effect of post-treatment process on microstructure and properties of the strips was studied.The results show that the post-treatment process of one-time cold rolling and annealing between 850—950℃was suitable for the strips with silicon content of 0.5wt%and 1.0wt... 

通过对辉光放电发射光谱法分析电工钢样品光谱行为的研究,分析其工作参数如:电压、电流、预溅射时间和积分时间对光谱强度和稳定性的影响,并以铁为内标元素,优化了工作参数。确定了直流辉光放电光谱法测定电工钢中碳、硅、锰、磷、硫、铬、镍、铜共8种元素的定量分析方法,并对该方法分析的精密度和准确度进行验证,结果表明,各元素的测定结果与认定值和其他方法测定值一致,测量元素结果RSD值小于2%。 Based on research on analyzing the spectrum behavior of the sample taken from the electrical steel by glow discharge optical emission spectrometry,the effect of its operational parameters such as current,voltage,pre-sputtering time and integrating time on the spectral intensity and spectral stability is analyzed.Taking the Fe as an element applied by internal standard method,these operational parameters are optimized,and therefore the quantitative analysis method for testing eight kinds of eleme... 

本发明提供了一种取向硅钢的磁畴细化方法，属于高磁感取向硅钢生产技术领域技术领域，包括：采用激光在带钢表面烧蚀出若干沟槽；采用腐蚀液对所述沟槽进行腐蚀，获得刻槽；其中，所述沟槽与带钢宽度方向的夹角为0‑20°；所述沟槽的深度为0.5～20μm，宽度为30～200μm；所述刻槽深度为0.5～30μm、宽度为30～300μm。该方法能够显著的细化磁畴，降低取向硅钢片单位损耗，同时细化磁畴的效果能够承受800℃‑900℃的消除应力退火。本发明还提供了一种取向硅钢的磁畴细化方法在取向硅钢生产中的应用。

本实用新型公开了一种硅钢片组扣件自动压平装置，包括：定位单元，定位单元包括转盘、校位板和第一驱动组件，第一驱动组件连接并驱动校位板沿竖直方向运动，校位板滑动连接有第一校位柱，第一校位柱相对转盘偏心布置；第一推送单元，位于转盘的一侧，第一推送单元包括第一推送气缸和第一推块，第一推送气缸连接并驱动第一推块沿水平方向运动；冲压单元，位于转盘背离第一推送气缸的一侧，冲压单元包括第二驱动组件和冲压柱，第二驱动组件连接并驱动冲压柱沿竖直方向运动。转盘、校位柱和第一驱动组件配合，周向定位硅钢片组，再通过冲压柱将凸出于硅钢片组的扣件压平，完成硅钢片组的整形，整体更为美观，方便后续的装配使用。

本发明公开了一种硅钢轧制系统，包括：轧机组，所述轧机组包括M架轧机，用于轧制硅钢，所述M架轧机的前N架轧机的轧辊为高速钢轧辊，其中，M、N为正整数；硅钢检测装置，位于所述轧机组最后一架轧机的出口处，用于对出口硅钢的参数信息进行检测；控制器，与所述硅钢检测装置通信连接，用于在所述参数信息不满足预设参数条件时，控制所述轧机组停止工作；磨床，用于在所述轧机组停止工作后，对所述N架轧机中的每架轧机进行辊形精度检测，对不满足预设辊形精度范围的轧辊进行磨削。