硅钢资料

在现普通冷轧无取向硅钢的基础上,降低Si含量,复合添加少量辅助元素,组合热轧板处理和成品退火加热技术,研制出了免常化处理的高磁感、低铁损并具有良好耐酸腐蚀性能的新系列无取向电工钢。 Based on existing common cold rolled non-oriented silicon steel,a new series of non-orientedelectrical steel with high induction,low core loss and excellent anti-corrosion property has been developed by reducing Si element,adding complexly a small amount of supplementary elements,and employing combined treatment of hot rolled sheet and finished product annealed heated technology. 

结合工业化生产的50A1300牌号无取向硅钢,分析了化学成分、RH精炼脱氧方式、板坯装炉温度以及热轧平整工艺等对磁性能的影响,探讨成品钢磁性能的改善。结果表明,采取改善后,50A1300牌号无取向硅钢的磁性能得到明显改善。2012年,该钢种平均铁损、磁感应强度分别达到5.26 W/kg、1.762 T,能够较好地满足用户市场需求及同行对标需要。 Based on the industrial manufacture of 50A1300 grade non-oriented silicon steel sheets,effects of chemical composition,deoxidization method in RH vacuum refining,charging temperature of steel slabs,hot rolling and flattening progress on magnetic properties are analyzed.The optimization methods of magnetic properties of steels are discussed. Results show that the magnetic properties are obviously improved by the adopted measures above. In 2012,the average core loss and the magnetic induction of 5... 

本实用新型涉及一种改进的点火器线圈硅钢片结构，包括E型件和I型件，所述E型件和I型件组合成日字形，它们可相互转动；所述E型件包括竖边和设置在竖边三个横边，三个横边分别为上横边，中横边和下横边，它们分别与竖边垂直连接；其中所述竖边的转角位置圆角处理，竖边外侧为弧形边；所述上横边的端面设置插缝；所述中横边的端头设置凹部；所述下横边的端头设置凸部；所述I型件上端两侧对称设置凹台；所述凹台具有弧形凹边；所述I型件通过凹台设置在插缝可以旋转。本实用新型设计新颖，改进巧妙，由于E型件具有弧形边可以有利于拾取，方便工作操作，E型件和I型件采用插合的方式，整体结构稳定，便于安装，增加了组合体的稳定性。

本实用新型公开了一种硅钢加热保温装置，包括安装板，所述安装板上表面固定连接有加热箱，所述加热箱背面通过固定板连接有多个伺服电机，所述伺服电机输出端固定连接有第一螺杆，所述第一螺杆远离伺服电机的一端贯穿加热箱并螺纹连接有置物板，所述加热箱内侧壁转动连接有多个第二螺杆，所述第一螺杆与相邻的第二螺杆之间通过锥轮组件相连接，所述第二螺杆外侧壁螺纹连接有螺纹块，所述螺纹块上表面通过连接组件连接有夹板。本实用新型，这种保温方式，操作简单，使硅钢在这个过程中，硅钢裸露在空气的时间短，能够起到较好的保温效果，避免因保温不当造成硅钢成品质量降低，从而有效的提高硅钢成品合格率。

本实用新型公开了一种无取向硅钢喷涂用即时干燥装置，包括干燥箱，所述干燥箱内滑动连接有加热台，所述干燥箱顶部设置有加热箱，所述加热箱左右两侧分别设置有进风管和出风管，所述进风管和出风管均与干燥箱连通，所述加热箱内部从左到有依次固定连接有风机和加热网，所述干燥箱内设有带式传送机，通过带式传送机使喷涂过后的硅钢在干燥箱中移动，首先经过加热台加热，使涂层表面干燥硬化，不会变形，然后再经过加热箱吹出的风对硅钢表面的涂层进行进一步的烘干，从而保证干燥过程中涂层不会起褶皱。

利用光学显微镜、TEM和EBSD研究了退火温度对双辊连铸无取向硅钢再结晶组织的影响。结果表明,900℃退火后组织分布不均匀,有大量带状组织,平均晶粒尺寸29.5μm。提高退火温度,晶粒尺寸增大,组织均匀化程度增加,1050℃退火时,带状组织基本消失,平均晶粒尺寸42.2μm。 Effect of annealing temperature on recrystallization microstructure of non-oriented electrical steel produced by twin-roll casting process was investigated using OM,TEM and EBSD.The results show that the recrystallization microstructure is uneven because of many banded grains existing,average grain size is 29.5 μm.With annealing temperature increasing,the recrystallization grain size increases,microstructure becomes more homogeneous.When 1050 ℃ annealing,the banded structure almost disappear and... 

本文中简要介绍了武汉钢铁有限公司采用薄板坯连铸连轧CSP(compact strip production, CSP)工艺生产中低牌号无取向硅钢的实践情况.CSP工艺生产的硅钢具有成品磁性均匀、板形好的优势，但是在利用该技术生产中低牌号无取向硅钢时，常存在成品板表面瓦楞状缺陷严重、连铸生产效率低等问题.通过优化炼钢成分、热轧等相关工艺，可消除热轧板厚度方向中心的粗大形变组织，从源头上避免了粗大{100}<011>纤维组织的出现，消除了瓦楞状缺陷；通过提升冶炼效率和控制钢中夹杂物总量，可优化隧道炉的加热温度与在炉时间，大幅度提升了连铸生产效率，实现了中低牌号无取向硅钢的批量稳定制造，使CSP产线成为中低牌号无取向硅钢热轧板原料的主要供给生产线.如何进一步提升钢水纯洁度、提高连铸生产效率、降低生产成本，以及挖掘该产线生产薄带钢的技术优点，是未来工作的重点. This paper briefly introduces the practice of producing medium and low grade non oriented silicon steel(NGO) with CSP(compact strip production, CSP)technology in Wuhan Iron and Steel Co., Ltd.. This technology has the inherent advantages of uniform magnetic properties and good shape for silicon steel finished strip. However, in the actual production process, there are serious corrugated defects on the surface of silicon steel finished strip, and production efficiency of continuous casting is low... 

本发明公布了以铜析出粒子为抑制剂的一类取向电工钢及其生产方法，所述取向电工钢化学成分的质量百分比为：C：0.001％～0.07％；Si：2.5％～3.5％；Si+Mn+Al：≤3.5％；Cu：1.0％～2.0％；S：≤0.003％；N：≤0.0045％；其余为Fe和不可避免杂质元素。该取向电工钢的生产工艺步骤可以包括：连铸坯板坯加热、热轧、常化、冷轧、脱碳处理、时效处理、二次再结晶退火处理等。本方法免除了高温热轧加热和二次再结晶后高温长时间加热以净化钢板基体的退火环节，进而可实现连续式二次再结晶退火，大幅度降低了生产能耗，并显著提高生产效率。

该电磁钢板用涂敷组合物含有环氧树脂、潜伏性环氧树脂固化剂和热塑性弹性体，上述热塑性弹性体的熔点为100℃～200℃，并且弯曲弹性模量为超过5MPa且为100MPa以下，相对于上述环氧树脂与上述潜伏性环氧树脂固化剂的合计100质量份，上述热塑性弹性体的含量为10质量份以上且低于40质量份。

【作者】 侯桂芹； 张颖； ...

通过观察冲剪边缘组织,测量冲剪边缘的显微硬度、残余应力的分布情况和磁性能的变化研究了冲剪加工对无取向硅钢50WW800边缘组织和磁性能的影响。对冲剪后硅钢片进行750℃退火,分析退火对组织和磁性能的影响。结果表明,硅钢片剪切边缘会存在0.4 mm的形变硬化层,边缘应力大,铁损增加。退火后变形减小,形变硬化层变小,残余应力大幅度减少,铁损减少。 The influence of punching process on cutting edge microstructure and magnetic properties of non-oriented silicon steel 50WW800was studied by observing microstructure and measuring microhardness near cutting edge.The residual stress distribution in the silicon steel tooth and magnetic properties were measured.Effect of annealing at 750 ℃ on microstructure and magnetic properties of the silicon steel was analyzed.The results show that a cut-edge hardening layer up to 0.4 mm is observed,residual st... 

本实用新型公开了一种硅钢片立式送料装置，包括装置主体，装置主体上方安装有固定板架和活动板架，固定板架和活动板架上方均安装有料架，固定板架通过螺栓固定在装置主体的上方，活动板架滑动安装在装置主体的上方；装置主体内部位于固定板架和活动板架的下方安装有推料板，本实用新型适用于硅钢片生产，该装置通过将其中一个料架安装安装在活动板架的上方，而装置主体的两侧上方开设有滑槽，滑槽沿装置主体的长度方向开设，活动板架采用倒“U”型结构，活动板架的两个竖直端滑动卡合在滑槽内，这样的结构设置使得活动板架能够在水平方向移动调整位置，从而使两个料架的间距可调，使该装置能够适用于不同大小型号的物料使用。