通过试验确定氩气分析流量为3.5L/min,静态流量为0.75L/min,冲洗时间为3s,预燃时间为12s,积分时间为5s的激发条件,采用火花源原子发射光谱法测定取向硅钢中碳、硅、锰、磷、硫。分别采用铣床铣样、砂轮磨样两种制样方式进行了精密度考察,发现制样方式对结果影响不大;讨论了取向硅钢样品中碳、硅、锰、磷、硫测定时可能存在的共存元素干扰,发现硅对锰元素的干扰不可忽略,采用干扰系数法进行了校正,据此拟合得到各元素校准曲线的相关系数均在0.999 0以上。精密度考察结果表明,碳、硅、锰、磷、硫的相对标准偏差(n=10)在0.71%~9.4%之间。对两块取向硅钢生产样品进行分析,并与钢铁研究总院进行比对分析,结果一致,且偏差均在允许范围内。 Carbon,silicon,manganese,phosphorus and sulfur in oriented silicon steel were determined by spark source atomic emission spectrometry.The selected excitation conditions were as follows:the analytical flow rate of argon was 3.5L/min,the static flow rate was 0.75L/min,the flush time was3s,the precombustion time was 12sand the integration time was 5s.Two sample preparation methods,including milling machine and grinding wheel,were investigated.The precision test results showed that,the determination... 

本发明涉及一种含磷无铝高效无取向硅钢生产方法，生产方法取消常化工艺，具体步骤如下：1)将钢水冶炼至目标成分后，浇铸成坯；2)板坯热装，热装温度≥500℃，热轧板坯加热炉均热段板坯温度1150～1200℃；终轧温度控制在860～930℃，卷取温度700～800℃3)酸洗后冷轧，控制冷轧整体压下率80％以内，至成品厚度；4)连续退火炉快速加热段温度设定1050～1180℃，增加有利织构组织形核，均热段温度设定830～950℃，全氮气干气氛保护，退火工艺速度120～150m/min，满足晶粒度8～4级。本发明不需进行热轧卷常化处理，降低了制造成本。

利用X-射线衍射织构分析和线形分析技术测定了交叉轧制双取向硅钢在制备工艺各阶段的织构及微结构,进而探讨了立方织构({100}<001>)的形成过程。通过对实验结果的分析可知,二次冷轧和交叉轧制工艺为立方织构提供了内能优势和有利的形变织构,而低温预退火工艺既强化了立方织构的内能优势,又为立方织构的异常长大提供了有利的组织保证,最终在抑制剂(AlN和MnS)的协同作用下,硅钢在二次再结晶退火后形成了强烈的立方织构。 The texture and substructure of the double oriented electrical steels produced by the cross rolling technology during the difference process has been measured by means of the X-ray texture and diffraction peak profile analysis technology,and research the formation mechanism of cube texture,{100}<001>.The results show that the dominances of inner energy and deformation texture were supplied by secondary cold rolling and the cross rolling technology and strengthened by pre-annealing at a low... 

本申请公开了一种低铝无取向硅钢结晶器液面波动的控制方法，包括：步骤1：KR脱硫，脱硫后铁水硫含量≤0.0015%；步骤2：转炉吹炼，转炉出钢后钢包顶渣厚度≤30mm；步骤3：RH真空处理，RH脱碳结束后，加入铝粒脱氧后钢液循环3‑5min，提升气体流量至0.8‑1.0m3/（h·t）；随后加入合金进行脱氧合金化，提升气体流量至0.5‑0.7m3/（h·t）；步骤4：连续浇注，长水口氩气流量150‑200L/min，连铸塞棒氩气流量5‑10L/min，背压≥0.05bar。本申请的控制方法控制结晶器液面波动≤±1.5mm的比例稳定在90%以上。

本发明公开了一种改善取向硅钢边部变形的热处理辅助方法，在高温退火工序前，在钢卷的下端预设位置处放置阻热环并固定；在高温退火完成后，拆除固定件并移除所述阻热环。本发明通过施加阻热环，降低了取向硅钢卷在高温退火过程中的升温速率，降低了钢卷在升温及冷却过程中的胀缩量，有效改善了边部变形情况。同时，本发明由于采用一体式隔热材料，其装配及移除难度大幅度降低，有利于推广应用。

采用低温板坯加热制备取向硅钢,通过透射电镜(TEM)观察并研究热轧板中的析出物,用ODF织构法研究热轧板距表面1/8、1/4和1/2处的织构分布。结果表明,热轧板中的析出物主要是密排六方AlN,AlN形貌呈规则长方形,AlN颗粒大小不等,分布密度低;热轧板中的织构沿板厚方向,由亚表层的{110}<001>织构向1/2中心层的α线织构变化,其中{110}<001>织构在热轧板距表面1/4层处最强。 The low temperature grain-oriented silicon steels were produced by acquired inhibitor method.The precipitates in hot rolling strip were observed and studied by transmission electron microscope,and the texture distribution in 1/8,1/4 and 1/2 layers of hot rolling strip were analyzed by ODF method.The results showed that the square shaped h-AlN is the main precipitates in hot rolling strip.The precipitates are varying in size and distribution.The texture of hot rolling strip in thick direction are... 

本实用新型属于输送设备技术领域，具体涉及一种硅钢酸洗用耐酸污水泵，包括泵体，泵体上设有进水口和出水口，泵体内设有叶轮和开有腔室，泵体上还设有喷淋机构，喷淋机构包括水箱、转轴和电机，转轴内开有空腔，转轴的一端伸出水箱并伸入腔室内，转轴上开有与空腔连通并位于腔室内的喷水孔；水箱内滑动连接有密封板，转轴穿过密封板并与密封板螺纹连接，水箱内设有限位部；水箱的上下两侧均连接有进水管，进水管上设有单向进水阀；转轴上设有两个均能与空腔连通的单向排水阀，两个单向排水阀分别位于水箱的两侧。在本方案中，设置喷淋机构，对污水泵内部残留的酸液进行冲洗、稀释，避免酸液残留腐蚀泵体，能有效延长污水泵的使用寿命。

本发明公开了硅钢片铁芯叠片机构，包括送料装置和叠片装置，送料装置包括有磁性传送带、送料件和第一定位杆，磁性传送带用于将已剪切的硅钢片传送至送料件，送料件安装于磁性传送带的下方，并且可沿磁性传送带的正交方向平行伸出，第一定位杆安装于送料件上，用于定位硅钢片，叠片装置设置于送料件的伸出的一方，包括有叠放台、第二定位杆和机械手，叠放台用于叠放硅钢片，第二定位杆用于定位硅钢片，机械手用于将送料件的硅钢片搬运至叠放台上，机械手包括有转动臂和取料单元，取料单元安装于转动臂的端部，包括有电永磁铁，电永磁铁用于吸取硅钢片。根据本发明的硅钢片铁芯叠片机构，可有效提高叠片速度，降低能耗，提高生产效率。

本发明公开一种高牌号无取向硅钢的轧制方法，用于控制森基米尔二十辊轧机对原料带钢进行轧制，所述方法包括：根据所述原料带钢的规格参数，确定所述森基米尔二十辊轧机的第一中间辊的辊型及第二中间辊的辊型；根据所述原料带钢的合金含量及所述规格参数，确定所述第一中间辊的有效平面量；根据所述规格参数，确定所述森基米尔二十辊轧机的径向调整机构的凸度值；根据所述合金含量，设定所述森基米尔二十辊轧机进行轧制时的负荷分配和张力；按照所设定的负荷分配和张力分配对所述原料带钢进行轧制，且在轧制过程中以预设乳化液流量进行喷淋，以制得成品。本发明可减少高牌号无取向硅钢在轧制过程中发生脆性断裂，提高轧制的稳定性及生产效率。

本发明公开了一种硅钢片漆，该硅钢片漆采用特定的聚酰胺酰亚胺乳液制备，通过使偏苯三酸酐与组合形式的双端氨基化合物反应，添加三乙胺进一步提升反应进行的程度，并赋予整体更好的柔性和韧性，而磷酸三丁酯能够进一步通过物理改性改善体系的韧性，之后蒸出全部的有机溶剂，并添加一定量的水溶性有机溶剂，然后加入组合形式的活化剂，混合，再滴入水，形成稳定的乳液，最后添加双马来酰亚胺封端剩余的活性基团，该硅钢片漆不仅可以采用水作为主体溶剂，提升了环保型，而且还兼具耐高温、高粘结强度、电气性能强等优点，并有好的环境抗性与施工性能。

本实用新型涉及一种硅钢片图像采集装置，在固定支架上设置有工业相机，所述的工业相机可以沿垂直方向上下移动或者沿水平方向前后移动，通过上下移动或者前后移动对硅钢片的形状和尺寸、硅钢片叠积形成的铁芯进行实时图像采集。固定支架包括：固定底座、支撑杆和工作台面，一对固定底座平行对称设置，所述的固定底座上对称设置两条竖直支撑杆，竖直支撑杆的上端面固定连接工作台面，在两条竖直支撑杆的中间位置设置升降丝杆，水平支撑杆的两端分别与升降丝杆的升降螺母固定连接，相机滑台活动设置在水平支撑杆上。本实用新型通过工业相机的上下前后移动，实现了硅钢片形状尺寸和硅钢片高度即时拍照测量，较人工测量提高了测量精度及准确性。

【作者】 安斌； ...