硅钢资料

冷轧无取向硅钢是高技术含量、高附加值产品,工艺复杂,生产周期长,过程控制难度大,被誉为钢铁产品中的\"工艺品\"。热轧生产工艺又是无取向硅钢生产的重中之重,直接决定了硅钢的铁损和电磁性等多项指标。 Cold rolled non-oriented silicon steel is high technology content 、high added value product. Its process is complex, its production cycle is of length, and its process control is difficult, which is known as the iron and steel products \" Arts and crafts\". Hot rolling production process is the top priority of non-oriented silicon steel, which directly determines iron loss of the silicon steel and electromagnetic property,as well as other many index. 

本实用新型公开了一种高磁感取向硅钢加工用拉伸装置，涉及硅钢加工技术领域，包括安装架，所述安装架的后端安装有两个驱动电机，两个所述驱动电机的输出端均连接有下输送辊，所述下输送辊的左侧设置有下调节辊，所述下调节辊和下输送辊的末端均固定有限位圈，所述下输送辊的上方设置有上输送辊，所述上输送辊的左侧设置有上调节辊，所述上调节辊和下调节辊的内部均设置有连接杆，所述连接杆的外表面设置有卡块。该高磁感取向硅钢加工用拉伸装置通过设置的驱动电机，能够带动下输送辊转动，从而对工件进行输送，通过设置的连接杆和卡块，使得下输送辊转动时能够带动下调节辊转动，提高工件的输送效率。

本发明特别涉及一种控制边部翘皮的热轧电工钢的生产方法和生产系统，属于钢表面质量检测技术领域，方法包括：建立热轧电工钢边部翘皮的数据库，数据库包括翘皮类型及各翘皮类型的翘皮发生原因和翘皮发生的区域；对待质检的热轧电工钢表面进行识别，并对比数据库，获得待质检的热轧电工钢表面翘皮的翘皮类型；根据待质检的热轧电工钢表面翘皮的俏皮类型获得该类型翘皮的翘皮发生原因和翘皮发生的区域；根据翘皮发生原因和翘皮发生的区域，调整生产操作，用以减少热轧电工钢的边部翘皮；通过对边部翘皮进行准确分类及识别，能够准确的分辨出边部翘皮的产生原因，采取有针对性的措施防止缺陷扩大，最大程度的降低缺陷发生量，提高质量控制水平。

本发明公开了一种减少低温高磁感取向硅钢点状露金缺陷的方法。本发明通过控制低温高磁感取向硅钢的脱碳和渗氮工艺，特别是通过控制脱碳露点、渗氮露点、脱碳氧化度、脱碳时间来调节钢板经脱碳渗氮后表面形成的内氧化层中FeO/SiO2的比例，结合氧化镁退火隔离剂的含水率控制，获得了一种可避免点状露金缺陷的低温高磁感取向硅钢生产方法。

本发明公开了一种硅钢冷连轧轧制过程温度获取方法、装置及电子设备，通过获取硅钢冷连轧生产过程的工业参数数据以及各机架间硅钢的实际温度测试数据，然后基于工业参数数据以及预设初始模型，确定硅钢冷连轧生产过程的温度预测模型，接着基于硅钢轧制前的预热温度以及温度预测模型，得到硅钢冷连轧轧制过程各机架变形区出口与下一机架变形区入口之间的预测温度数据，再将预测温度数据与实际温度测试数据进行对比，并根据对比结果中的温度差异值对相应机架间的乳化液参数进行修正，直至温度差异值小于预设阈值，得到修正后的温度预测模型，能够用于实现硅钢冷连轧轧制过程中，任意采样点硅钢温度的获取。

本发明公开了一种硅钢片宽度偏差检测装置及其检测方法，属于硅钢片检测领域。一种硅钢片宽度偏差检测装置，包括检测装置上的第一输送机体，还包括：多个均匀分布的隔板，均固定安装在第一输送机体的皮带表面；开槽，设置在所述第一输送机体的侧壁；装置盒，通过上下滑动机构与所述第一输送机体连接，其中，所述装置盒内通过顶紧机构滑动安装有滚轮；第一支架，固定安装在第一输送机体的侧壁；装置板，通过转轴转动连接在第一支架的侧壁，所述转轴位于装置板的侧壁中部，所述装置板两端设有自动推料机构；本发明中的硅钢片宽度偏差检测装置不仅可以更高精度的检测硅钢片的宽度，并且还能将不达标的硅钢片自动筛选出来，使用更加的方便。

基于BOF→RH→CSP生产工艺,研究了RH精炼过程钢中夹杂物类型演变及MgO·Al2O3夹杂物形成规律,同时对MgO·Al2O3夹杂物的形成条件进行了热力学计算,借助CFD数值模拟软件研究了RH精炼过程卷渣行为。研究发现,RH精炼过程20和30 min时,w([MgO])/w([Al2O3])为0.005~0.020,未发现MgO·Al2O3夹杂物;RH出站后夹杂物w([MgO])/w([Al2O3])为0.3~0.5,且RH精炼结束后MgO·Al2O3夹杂物占夹杂物总量的58.4%;另外,RH精炼过程钢液表面速度CFD模拟结果为0.57 m/s,大于临界卷渣速度0.45 m/s,且顶渣成分与夹杂物成分相近,存在卷渣现象。热力学计算表明,钢液与炉渣平衡时钢中w([Al])为0.31%~0.37%,w([Mg])为0.00024%~0.00028%,在MgO·Al2O3生成区域之内。减少RH处理过程卷渣,浇铸过程下渣及控制顶渣和包衬相中MgO质量分数可抑制MgO·Al2O3夹杂物形成。 Based on the practical production of non-oriented silicon steel, the evolution of inclusion type and the formation of MgO·Al2O3inclusion were analyzed in the process of BOF→RH→CSP. The thermodynamic conditions for forming MgO·Al2O3inclusion were discussed and the behavior of slag entrapment of molten steel was also simulated by CFD software during RH refining. The results showed that the value of w([MgO])/w([Al2O3]) was in the range of 0.005-0.020 and no MgO · Al2O3 inclusion was observed at 20 ... 

介绍了CSP工艺生产无取向电工钢各工序的设备特点、采用的工艺控制手段和电工钢产品质量情况,结合生产实践证明了马钢CSP工艺开发的无取向电工钢产品丰富了薄板坯连铸连轧的品种结构,发挥了薄板坯连铸连轧生产无取向电工钢性能均一、稳定的特点。 The equipment characteristic,the process control method and the quality of non-orientated silicon steel by CSP process were introduced.Combined with the production situation,it is proved that production of non-orientated silicon steel developed on Masteel CSP line would enrich product structure of thin slab continuous casting and rolling,and it exerts stable performance of non-orientated silicon steel. 

借助光学显微镜、扫描电镜、交流磁性能测量仪和万能拉伸试验机研究了0.3 mm厚高强无取向电工钢冷轧板在780、820、860和900℃退火保温2 min后的组织、织构和性能。结果表明:在退火温度范围内,试验钢均发生了完全再结晶,得到等轴状的铁素体晶粒;随着退火温度的升高,平均晶粒尺寸从9.2μm增长到41.3μm,工频铁损和400 Hz高频铁损均先大幅减小后趋于平缓,磁感应强度先升高后降低。在820℃退火时,铁损P_1.5/50=5.51 W/kg,P_1.0/400=33.22 W/kg均处于较低值,磁感应强度B₅₀₀₀最大,为1.649 T。试验钢的屈服强度和抗拉强度均随退火温度的升高而降低,780℃退火时屈服强度为496 MPa, 900℃退火时降低至407 MPa。综合磁性能和力学性能考虑,试验钢的最佳退火温度是820℃。 Microstructure, texture and properties of 0.3 mm thick high strength non-oriented electrical steel cold rolled sheet annealed at 780 ℃, 820 ℃, 860 ℃ and 900 ℃ for 2 min were studied by means of optical microscope, scanning electron microscopy, AC magnetic property tester and universal tensile testing machine. The results show that in the annealing temperature range, complete recrystallization of the experimental steel occurs and equiaxed ferrite grains are obtained. With the increase of annealin... 

本发明揭示了一种高牌号无取向硅钢及其生产方法。所述无取向硅钢的化学成分以质量百分比计包含：C:0.002～0.004％，S≤0.003％，Si:1.4～1.7％，Mn:0.7～0.95％，P≤0.03％，Sn:0.015～0.035％，11×([Si]‑1.4％)＝14×([Mn]‑0.7％)。所述无取向硅钢的生产方法中，连铸坯加热温度1120～1150℃，精轧终轧温度为890±15℃，最后一道次精轧的压下量≥30％且最后两道次精轧的总压下量≥50％，卷取温度650±20℃；在酸连轧之前不需要进行常化处理，且所得无取向硅钢的磁性能佳，表面无瓦楞缺陷，满足低成本高牌号无取向硅钢的需求。

6.5%(质量分数)Si高硅钢具有优异的软磁性能和广阔的应用前景,然而其室温脆性和低的热加工性极大地制约了它的发展。近年来,人们对高硅钢制备技术的研究已经取得了很大的进展,如何通过织构的优化提高高硅钢的磁性能越来越受到人们的关注,归纳和总结了不同工艺制备的高硅钢中的织构演变规律和特点,以及对应的典型磁性能。 6.5wt% Si high silicon steel has excellent soft magnetic properties and wide application prospect.However,the brittleness of room-temperature and poor workability of cold rolling limit its deve-lopment.Recently,the researches of the preparations of high silicon steel have been already made great breakthroughs,and then,more and more attentions are focused on how to optimizing the texture of high silicon steel so as to obtain the best magnetic properties.The evolution of textures of 6.5% Si high s... 

通过对辉光放电发射光谱法分析电工钢样品光谱行为的研究,分析其工作参数如:电压、电流、预溅射时间和积分时间对光谱强度和稳定性的影响,并以铁为内标元素,优化了工作参数。确定了直流辉光放电光谱法测定电工钢中碳、硅、锰、磷、硫、铬、镍、铜共8种元素的定量分析方法,并对该方法分析的精密度和准确度进行验证,结果表明,各元素的测定结果与认定值和其他方法测定值一致,测量元素结果RSD值小于2%。 Based on research on analyzing the spectrum behavior of the sample taken from the electrical steel by glow discharge optical emission spectrometry,the effect of its operational parameters such as current,voltage,pre-sputtering time and integrating time on the spectral intensity and spectral stability is analyzed.Taking the Fe as an element applied by internal standard method,these operational parameters are optimized,and therefore the quantitative analysis method for testing eight kinds of eleme...