冷轧无取向硅钢是高技术含量、高附加值产品,工艺复杂,生产周期长,过程控制难度大,被誉为钢铁产品中的\"工艺品\"。热轧生产工艺又是无取向硅钢生产的重中之重,直接决定了硅钢的铁损和电磁性等多项指标。 Cold rolled non-oriented silicon steel is high technology content 、high added value product. Its process is complex, its production cycle is of length, and its process control is difficult, which is known as the iron and steel products \" Arts and crafts\". Hot rolling production process is the top priority of non-oriented silicon steel, which directly determines iron loss of the silicon steel and electromagnetic property,as well as other many index. 

试验2.3Si无取向硅钢(/%:0.003C,2.30Si,0.16Mn,≤0.020P,≤0.005S,0.54Al)冷轧板由常化和未常化的2.5 mm热轧板冷轧至0.6 mm(压下率76%),经750~950℃2.5 min中间退火后再冷轧至0.5 mm(压下率16.7%),成品板经890℃+960℃2.5 min退火。研究了中间退火温度对该钢晶粒尺寸、织构和磁性能的影响。结果表明,随中间退火温度的升高,二次冷轧前晶粒和成品晶粒增大,成品中不利织构组分{111}和{112}减弱,磁性能得到改善。热轧板经过常化时的磁性能明显好于未经常化时的磁性能,但中间退火温度较高时常化对磁性能的有利作用减弱。 The test cold sheet of 2.3Si non-oriented silicon steel(/%:0.003C,2.30Si,0.16Mn,≤0.020P,≤0.005S,0.54Al) is first cold-rolled from normalized and un-normalizing 2.5 mm hot-rolled plate to 0.6 mm sheet(reduction 76%),then intermediate annealed at 750~950℃ for 2.5 min and double cold-rolled to 0.5 mm sheet(reduction16.7%),the finished sheet annealed at 890℃+960℃ for 2.5 min.Effect of the intermediate annealing temperature on grain size,texture and magnetic performance of the steel has been studied.... 

针对本钢薄板坯铸机在生产无取向电工硅钢的过程中存在的铸坯拉断、中包增碳、增氮等问题,进行了连铸工艺优化。通过采用新型无碳中间包覆盖剂、环保中间包干式料及专用结晶器保护渣后,降低了铸坯增碳量;通过控制钢包到中间包的增氮环节,降低钢水增氮;适当增大二冷水量,控制钢水过热度,防止铸坯拉断等生产事故的发生。改进工艺后,精炼后到成品铸坯的平均增碳量能控制在10×10-6以内,平均增氮量能控制在4×10-6以内。 The technology optimization has been adopted for preventing nitrogen increasing and carbon increasing in Benxi thin slab producing non-oriented silicon steel.Measures accordingly were adopted and satisfactory results were achieved. 

本实用新型涉及变压器铁芯装配技术领域，具体公开了一种硅钢片铁芯的装配工装，包括底座、对称设于底座上的两个承压条以及快速装夹机构；所述快速装夹机构包括设于两个承压条一侧的安装框架、安装于安装框架两侧的侧挡板、紧固组件以及将安装框架和承压条之间定位的卡接组件；所述卡接组件包括安装于安装框架一侧的定位块、以及开设于承压条一侧的定位槽，所述定位块的内部开设有安装槽，本实用新型通过快速装夹机构能够实现安装框架的快速定位，从而便于安装框架的安装，有效的提高了安装框架的拆装效率，有助于硅钢片铁芯的快速装配，可提高硅钢片铁芯的装配效率，增加硅钢片铁芯的生产效益。

提供能够稳定地制造磁特性优异且钢卷长度方向的铁损的偏差少的取向性电磁钢板的取向性电磁钢板的制造方法。本发明是一种取向性电磁钢板的制造方法，包括如下工序：对钢坯进行热轧，根据情况实施退火，然后通过1次冷轧或夹有中间退火的2次以上的冷轧来制成具有最终板厚的冷轧板，接着对上述具有最终板厚的冷轧板进行脱碳退火，然后实施二次再结晶退火；在最终的冷轧之前，将钢板以100℃/s以上的升温速度加热到100℃～350℃的加热温度，上述钢板从达到加热温度到进入最终的冷轧的第1道次的时间为5秒以内。

基于BOF→RH→CSP生产工艺,研究了RH精炼过程钢中夹杂物类型演变及MgO·Al2O3夹杂物形成规律,同时对MgO·Al2O3夹杂物的形成条件进行了热力学计算,借助CFD数值模拟软件研究了RH精炼过程卷渣行为。研究发现,RH精炼过程20和30 min时,w([MgO])/w([Al2O3])为0.005~0.020,未发现MgO·Al2O3夹杂物;RH出站后夹杂物w([MgO])/w([Al2O3])为0.3~0.5,且RH精炼结束后MgO·Al2O3夹杂物占夹杂物总量的58.4%;另外,RH精炼过程钢液表面速度CFD模拟结果为0.57 m/s,大于临界卷渣速度0.45 m/s,且顶渣成分与夹杂物成分相近,存在卷渣现象。热力学计算表明,钢液与炉渣平衡时钢中w([Al])为0.31%~0.37%,w([Mg])为0.00024%~0.00028%,在MgO·Al2O3生成区域之内。减少RH处理过程卷渣,浇铸过程下渣及控制顶渣和包衬相中MgO质量分数可抑制MgO·Al2O3夹杂物形成。 Based on the practical production of non-oriented silicon steel, the evolution of inclusion type and the formation of MgO·Al2O3inclusion were analyzed in the process of BOF→RH→CSP. The thermodynamic conditions for forming MgO·Al2O3inclusion were discussed and the behavior of slag entrapment of molten steel was also simulated by CFD software during RH refining. The results showed that the value of w([MgO])/w([Al2O3]) was in the range of 0.005-0.020 and no MgO · Al2O3 inclusion was observed at 20 ... 

本实用新型公开了一种硅钢卷上料装置，包括两支撑台和设置在两支撑台之间的输送组件，所述输送组件包括轨道和设置在轨道上的输送件，所述输送件包括滑板、支撑板、承重板和气缸，所述轨道平行于两支撑台设置在两支撑台之间，所述滑板可滑动设置在轨道上，所述支撑板通过气缸可升降设置在滑板上，所述承重板设置在支撑板上，所述承重板的截面呈U型，其上设置有第二缓冲条。其可实现硅钢卷的轻松上料，省时省力的同时，安全性大大提高。

本实用新型公开了一种变压器铁芯硅钢片板材滚切后打磨装置，包括机体、导向机构、隔板、前端打磨体和后端打磨体，所述导向机构设置在机体上，且所述导向机构导向若干料带的位移，所述导向机构之间设置有若干隔板，所述前端打磨体设置在料带传送方向上的前端，所述后端打磨体设置在料带传送方向上的后端，且所述前端打磨体、后端打磨体分别设置在两两相邻的料带之间；传送状态下的料带切割边缘相对于前端打磨体、后端打磨体打磨。在料带传动的同时，通过前端打磨体和后端打磨体的相对运动同时对两个料带的边缘进行打磨，结构简单，成本低，且能够提升料带外观质量。

通过对辉光放电发射光谱法分析电工钢样品光谱行为的研究,分析其工作参数如:电压、电流、预溅射时间和积分时间对光谱强度和稳定性的影响,并以铁为内标元素,优化了工作参数。确定了直流辉光放电光谱法测定电工钢中碳、硅、锰、磷、硫、铬、镍、铜共8种元素的定量分析方法,并对该方法分析的精密度和准确度进行验证,结果表明,各元素的测定结果与认定值和其他方法测定值一致,测量元素结果RSD值小于2%。 Based on research on analyzing the spectrum behavior of the sample taken from the electrical steel by glow discharge optical emission spectrometry,the effect of its operational parameters such as current,voltage,pre-sputtering time and integrating time on the spectral intensity and spectral stability is analyzed.Taking the Fe as an element applied by internal standard method,these operational parameters are optimized,and therefore the quantitative analysis method for testing eight kinds of eleme... 

本申请实施例公开了一种硅钢片卷绕机调节装置，包括底部支撑座，所述底部支撑座一侧的内部活动套接有伸缩调节板，所述伸缩调节板的上部固定连接有上部定位套，所述上部定位套内部的上端活动套接有第一定位板，所述上部定位套的内部安装有第一螺纹定位杆。该硅钢片卷绕机调节装置，通过带动硅钢片夹持在上下两个夹持板之间，即可带动夹持板之间的挤压力，带动硅钢片两侧位置进行限定，避免硅钢片收卷时出现振动和偏移的问题，同时装置夹持板的内部活动套接有滚轮，即可在硅钢片移动过程中，可带动滚轮旋转，即可带动硅钢片与滚轮之间的摩擦阻力降低，至此可带动硅钢片移动时的灵活性，避免硅钢片移动时出现卡死的问题。

本发明公开了一种自主学习的高硅钢软磁复合铁芯智能化生产系统及生产方法，属于软磁复合铁芯智能化生产技术领域。本发明的生产系统包括数据输入模块、数据分析模块、数据输出模块、通信模块、数据修正模块；生产方法为：用户通过输入模块选择目标性能参数及生产控制模式，系统生成生产过程关键参数，并由输出模块输出给用户；用户确认后形成控制指令，并发送至生产设备进行生产。本发明的系统不仅能够根据高硅钢铁芯产品的目标性能参数自动生成合理的操作条件，还能根据历史数据和产品检化结果对系统内置的关系模型不断进行优化、完善，能够有效提高产品产量和质量、减少浪费、降低成本。

本发明公开了硅钢片铁芯叠片机构，包括送料装置和叠片装置，送料装置包括有磁性传送带、送料件和第一定位杆，磁性传送带用于将已剪切的硅钢片传送至送料件，送料件安装于磁性传送带的下方，并且可沿磁性传送带的正交方向平行伸出，第一定位杆安装于送料件上，用于定位硅钢片，叠片装置设置于送料件的伸出的一方，包括有叠放台、第二定位杆和机械手，叠放台用于叠放硅钢片，第二定位杆用于定位硅钢片，机械手用于将送料件的硅钢片搬运至叠放台上，机械手包括有转动臂和取料单元，取料单元安装于转动臂的端部，包括有电永磁铁，电永磁铁用于吸取硅钢片。根据本发明的硅钢片铁芯叠片机构，可有效提高叠片速度，降低能耗，提高生产效率。