本实用新型公开了一种将硅钢片堆栈模块化的电机转子，包括：堆栈模块、转子端板和电机轴；堆栈模块卡接在电机轴的外侧，且堆栈模块的两端通过转子端板连接固定；堆栈模块包括多个相互连接的硅钢片，每个硅钢片上均设有连接件，硅钢片通过连接件相互连接。本实用新型通过在硅钢片上增设连接件将多个硅钢片叠加成堆栈模块，降低了固定难度和管理难度，而且可以使用机器人自动化产线的大规模生产，生产效率高。

【作者】 胡志强； 张文康； ...

利用FE-SEM、EDS分析了含不同抑制剂成分的成品取向硅钢中夹杂物的组成和形貌,统计其尺寸及数量分布;结合对磁性能测试的结果,分析了Sn、Cu、Nb和Cr对取向硅钢磁性能影响的机理。结果表明:含Sn的取向硅钢试样中夹杂物主要为块状的微米级Al-Ti-C-N-O复合物,还有少量的球形Al-N-O颗粒和块状Ti-C-N-O颗粒,棒状夹杂物较少;含Cr的取向硅钢试样中夹杂物主要为球形的微米级Al2O3,还有少量Cu-Al-N-O-S复合物,棒状夹杂物和不规则夹杂物均较少;含Cr试样中1~3μm夹杂物的平均尺寸较含Sn试样小,但数量多,而大于3μm夹杂物的平均尺寸较含Sn试样大,但数量很少。磁性能测试结果表明,外场为800A/m和2500A/m时,含Cr试样磁感应强度偏低,铁损值P1.7/50较含Sn试样高,为1.171W/kg。 The composition and morphology of inclusions in the finished grain-oriented silicon steels are analyzed by using FE-SEM and EDS, and the number density and size distribution of the inclusions are counted. The influence mechanism of Sn, Cu, Nb, and Cr on the magnetic properties of the steel is also discussed. Results show that the inclusions composition in the grain-oriented silicon steel samples containing Sn is mainly block Al-Ti-C-N-O, compounding with a few spherical Al-N-O and block Ti-C-N-O... 

本发明的一种超低碳含钇取向硅钢及其制备方法，化学组成及质量百分比为Si：2.0～4.5％，C：≤0.003％，Y：0.001～0.1％，Mn：0.1～0.25％，Al：0.01～0.02％，Cu:0～0.3％，S：0.02～0.035％，N：0.009～0.011％，其余为Fe和不可避免的杂质元素。生产工艺为：连铸、铸坯加热、热轧、常化、冷轧、初次再结晶退火、二次再结晶退火。本发明采用超低碳的成分，取消了常规取向硅钢脱碳退火工艺，简化了生产流程。通过稀土微合金化解决了因超低碳成分导致的单向铁素体组织抑制剂析出困难的技术难题。本发明制备的含钇取向硅钢厚度为0.2～0.35mm，磁感应强度B8为1.85～1.94T，铁损P17/50为0.9～1.2W/kg，可以用于变压器的铁芯材料，制备流程更为简洁。

本实用新型公开了一种硅钢片分流导料机构，属于硅钢片导料领域，包括传送带，所述传送带包括主带和副带，所述副带设置在主带的前面，所述主带横向设置，所述主带的后面设置有导流机构，所述导流机构包括电机、导流板和助力组件，所述主带的后面设置有安装架，所述安装架的顶部竖向固定连接有连接板，所述电机安装在连接板上，所述电机的输出轴与导流板的顶部固定套接，通过启动电机，电机带动导流板旋转，导流板在连接组件下带动助力组件旋转，使得主带上的物品被导流板进行阻挡，通过助力组件传送到副带上，避免了传送带方向单一，容易导致硅钢片对堆积的问题，从而减少硅钢片的损坏量，进而节约成本。

本发明涉及取向硅钢高温连续退火炉领域，尤其涉及一种取向硅钢高温连续退火炉隔离装置，包括安装在炉壳上的隔离炉门及设置在隔离炉门四周的密封井；隔离炉门顶部两侧安装有水冷却装置；水冷却装置上部设有隔离炉门动力牵引装置；密封井包括固定密封井和伸缩密封井，伸缩密封井位于固定密封井内部并与固定密封井滑动连接，伸缩密封井与固定密封井端部连接处设有密封装置。本发明可以确保隔离炉门升降过程中实现无缝全密封状态，提高密封效果，且采用伸缩密封井实际降低了密封井的高度，间接降低了水冷却装置连接管道上升至最高点的净空标高，与传统固定式密封井高度相比可以降低高度50％～80％，从而降低厂房净空标高，节省厂房基建投资。

本发明涉及取向硅钢技术领域，且公开了包括以下步骤：步骤一：冶炼，冶炼经转炉和RH精炼后得到钢水，在进行冶炼的过程中通入空气并设置总进气量100‑300Nl/min，且通入的空气中氧含量为20‑21％之间。该磁性优良的高磁感取向硅钢的气氛控制工艺，通过在不同的流程中，加入一定配比的氧气和氮气的含量，有效的提升每个阶段的气氛控制精度，从而得到最终的高磁感取向硅钢达到优良，避免了因气压、流量等因素影响最终高磁感取向硅钢磁力效果，炉渣中FeO含量减少，提高钢回收率和炉衬寿命，进而也起到降低生产成本的效果，且进行精确的气氛控制，使得在进行高磁感取向硅钢的冶炼中，使得冶炼的效果更好，使得冶炼出来的高磁感取向硅钢的磁性更加的优良。

本申请公开了一种低铝无取向硅钢结晶器液面波动的控制方法，包括：步骤1：KR脱硫，脱硫后铁水硫含量≤0.0015%；步骤2：转炉吹炼，转炉出钢后钢包顶渣厚度≤30mm；步骤3：RH真空处理，RH脱碳结束后，加入铝粒脱氧后钢液循环3‑5min，提升气体流量至0.8‑1.0m3/（h·t）；随后加入合金进行脱氧合金化，提升气体流量至0.5‑0.7m3/（h·t）；步骤4：连续浇注，长水口氩气流量150‑200L/min，连铸塞棒氩气流量5‑10L/min，背压≥0.05bar。本申请的控制方法控制结晶器液面波动≤±1.5mm的比例稳定在90%以上。

采用低温板坯加热制备取向硅钢,通过透射电镜(TEM)观察并研究热轧板中的析出物,用ODF织构法研究热轧板距表面1/8、1/4和1/2处的织构分布。结果表明,热轧板中的析出物主要是密排六方AlN,AlN形貌呈规则长方形,AlN颗粒大小不等,分布密度低;热轧板中的织构沿板厚方向,由亚表层的{110}<001>织构向1/2中心层的α线织构变化,其中{110}<001>织构在热轧板距表面1/4层处最强。 The low temperature grain-oriented silicon steels were produced by acquired inhibitor method.The precipitates in hot rolling strip were observed and studied by transmission electron microscope,and the texture distribution in 1/8,1/4 and 1/2 layers of hot rolling strip were analyzed by ODF method.The results showed that the square shaped h-AlN is the main precipitates in hot rolling strip.The precipitates are varying in size and distribution.The texture of hot rolling strip in thick direction are... 

绝缘涂层可以有效提高硅钢片的耐蚀、耐腐、磁、绝缘等性能，因此取向硅钢涂装绝缘涂层是取向硅钢生产过程中重要的一环。本文对取向硅钢含铬无机绝缘涂层以及氮化铬涂层的性能优缺点进行了介绍，并对国内无机含铬取向硅钢绝缘涂层及氮化铬涂层的研究现状进行了综述。最后对未来含铬无机绝缘涂层的研发方向进行了展望。 Insulation coating can effectively improve the corrosion resistance of silicon steel sheet, such as corrosion, magnetic, insulation performance, thus oriented silicon steel insulation coating is the important part of oriented silicon steel production process. In this paper, the inorganic insulation coating oriented silicon steel containing chromium and chromium nitride coating performance advantages and disadvantages are introduced.In addition, the research status of insulation coating and chrom... 

对无取向硅钢炼钢全流程钢液增钛的原因进行了分析,认为铁水钛含量、转炉出钢温度、转炉下渣量、精炼渣TiO₂含量、钢水罐及RH浸入管混钢种生产是影响钢液增钛的主要原因。通过采取低钛铁水冶炼,减少转炉下渣量,提高出钢温度,添加白灰改质精炼渣等措施,均能够降低钢液中的钛含量。 After analyzing the causes leading to increased content of titanium in molten nonoriented silicon steel during whole steelmaking process, it was concluded that such factors as content of titanium in hot metal, tapping temperature from converter, quantity of roughing slag entered into the ladle from converter, content of TiO₂ in refining slag, molten steel ladle car,carrying out the steelmaking of different steel grades by the same ladle and same RH immersion tube were the main causes ... 

研究的两种取向硅钢（%:No1-0.042C、3.16Si、0.009Al、0.07Mn、0.50Cu、0.015S、0.0084N和No2-0.040C、3.20Si、0.014Al、0.22Mn、0.49Cu、0.016S、0.008 2N）由50 kg真空感应炉冶炼,锻成（mm）350×120×35板坯,经1 250℃30 min加热,开轧温度1 100℃,5道次热轧成2.3 mm板,终轧温度950～1 000℃。实验结果表明,两热轧板沿板厚方向存在组织和织构的不均匀性,热轧板次表层为再结晶组织,有较强的Goss织构组分;中心层为形变组织,具有典型的形变织构。含0.22%Mn的No2钢次表层{110}〈001〉织构组分比含0.07%Mn的No1钢弱,中心层{001}〈110〉织构组分大大强于0.07%Mn No1钢,导致两者磁性能差异,0.22%Mn No2钢磁感应强度(B₈₀₀)和铁损(P_1.7/50)分别为1.87 T和1.24 W/kg,0.07%Mn No1钢分别为1.88 T和1.18 W/kg。 Studied both grain-oriented silicon steels（%:No1- 0.042C,3.16Si,0.009Al,0.07Mn,0.50Cu, 0.015S,0.0084N and No2-0.040C,3.20Si,0.014Al,0.22Mn,0.49Cu,0.016S,0.0082N） are melted by a 50 kg vacuum induction furnace,forged to（mm） 350×120×35 slab,heated at 1 250℃for 30 min,with beginning rolling temperature 1 100℃hot-rolled to 2.3 mm plate by 5 passes,finishing-rolled at 950～1000℃.Test results show that the structure and texture along thickness of both hot-rolled plates are inhomogeneous:the subsurface ...