对取向硅钢熔融态钢液进行处理,对比研究了不同脉冲参数的作用效果。结果表明,电脉冲对钢锭晶粒组织具有明显的细化作用,凝固组织等轴晶比例大幅上升。在脉冲电容、频率、处理时间和电压中,影响等轴晶比例的最显著性因素为脉冲频率;最优正交实验参数为:电容1 200μF,脉冲频率1 Hz,处理时间5 s,脉冲电压800 V;随着输入能量的增大,等轴晶率先增大后减小,脉冲输入能量为某值时,等轴晶率最大,通过经典形核理论和热力学对这一现象进行了解释。 Research on the influence of the electric pulse on the solidification structure of oriented silicon steel was preformed.Electric pulses in different parameters were applied to molten steel and results were compared.The result shows that solidification structure of oriented silicon steel can be improved by the electric pulse,and the equiaxed crystal ratio increases obviously.Among the four parameter factors of electric capacity,frequency,applied time and voltage,the most effective factor is frequ... 

本实用新型公开了一种硅钢卷放卷辅助装置，包括支撑板、摆臂、气缸和连动杆，所述摆臂一端通过第一转轴枢接在支撑板上，所述连动杆的一端通过第二转轴枢接在摆臂的中部，另一端通过转轴与气缸的输出端连接，所述气缸的缸筒固定在支撑板上，所述摆臂远离支撑板的一端设置有承载座，所述承载座上开设有弧形槽口，所述槽口处设置有滚动组件；所述滚动组件包括设置在承载座上的第一支撑架和可转动设置在第一支撑架上的滚柱。其可有效防止硅钢卷从辊筒上掉落，保证了生产的安全性。

通过对辉光放电发射光谱法分析电工钢样品光谱行为的研究,分析其工作参数如:电压、电流、预溅射时间和积分时间对光谱强度和稳定性的影响,并以铁为内标元素,优化了工作参数。确定了直流辉光放电光谱法测定电工钢中碳、硅、锰、磷、硫、铬、镍、铜共8种元素的定量分析方法,并对该方法分析的精密度和准确度进行验证,结果表明,各元素的测定结果与认定值和其他方法测定值一致,测量元素结果RSD值小于2%。 Based on research on analyzing the spectrum behavior of the sample taken from the electrical steel by glow discharge optical emission spectrometry,the effect of its operational parameters such as current,voltage,pre-sputtering time and integrating time on the spectral intensity and spectral stability is analyzed.Taking the Fe as an element applied by internal standard method,these operational parameters are optimized,and therefore the quantitative analysis method for testing eight kinds of eleme... 

本发明涉及一种含磷无铝高效无取向硅钢生产方法，生产方法取消常化工艺，具体步骤如下：1)将钢水冶炼至目标成分后，浇铸成坯；2)板坯热装，热装温度≥500℃，热轧板坯加热炉均热段板坯温度1150～1200℃；终轧温度控制在860～930℃，卷取温度700～800℃3)酸洗后冷轧，控制冷轧整体压下率80％以内，至成品厚度；4)连续退火炉快速加热段温度设定1050～1180℃，增加有利织构组织形核，均热段温度设定830～950℃，全氮气干气氛保护，退火工艺速度120～150m/min，满足晶粒度8～4级。本发明不需进行热轧卷常化处理，降低了制造成本。

本发明提供能够制造磁特性与被膜密合性优异的电磁钢板的新颖并且得以改良的电磁钢板的制造方法。一种电磁钢板的制造方法，其特征在于，其包括以下工序：使电磁钢板与溶液相接触，所述电磁钢板以质量％计含有C：超过0％且0.10％以下、Si：2.5％以上且4.5％以下、Mn：0.01％以上且5.0％以下、S、Se及Te中的1种或2种以上的合计：超过0％且0.050％以下、酸可溶性Al：超过0％且5.0％以下、N：超过0％且0.015％以下、P：超过0％且1.0％以下、剩余部分由Fe及杂质构成，其中，上述溶液含有Cu、Hg、Ag、Pb、Cd、Co、Zn及Ni中的1种或2种以上，各元素的浓度合计为0.00001％以上且1.0000％以下。

试验了通过NaCl-KCl-NaF-SiO₂熔盐在电流密度50 mA/cm²、电沉积脉冲电流正反向比9:1和750⁸50℃60min电沉积下阴极（/mm）20×20×0.5的1.6Si无取向冷轧硅钢片断面层硅的分布,并通过计算得出Si的扩散系数。结果表明,电沉积温度由750℃提高至850℃时,试样中Si含量增加,扩散的深度由18μm提高到40μm;电沉积温度与Si在钢中的扩散系数近似符合Arrhenius指数关系。 The distribution of silicon at cross section of cathode（/mm） 20 × 20 × 0.5 sheet of 1.6Si non-oriented cold rolled silicon steel after electro-deposit treatment by NaCl-KCl-NaF-SiO₂ molten salt with current intensity 50 mA/cm²,electro-deposit pulse current positive-negative ratio 9:1 at 750 850 ℃ for 60 min has been tested and the diffusion coefficient of Si is obtained by calculation.Results show that with increasing electro-deposit temperature from 750 ℃ to 85... 

研究了CSP流程试制50W270高牌号无取向硅钢热轧→常化→冷轧→退火过程中织构的演变.利用电子背散射衍射技术对全流程织构进行测量和分析.发现热轧板织构在厚度方向上存在较大差异,表层主要为铜型、黄铜和高斯织构,1/4层存在微弱的高斯织构和旋转立方织构,中心层以γ纤维织构和旋转立方织构为主,还含有较弱的α纤维织构.与热轧板相比,常化板表层和1/4层织构变化不大,中心层旋转立方织构和α纤维织构增强.冷轧板各层均具有α纤维织构和γ纤维织构.与冷轧板相比,成品板各层中α纤维织构基本消失,还出现了立方织构和高斯织构. This article focuses on texture evolution in 50W270 high-brand non-oriented silicon steel produced by CSP in hot rolling,normalizing,cold rolling,and annealing processes.The texture in the whole process was measured and analyzed by electron back-scatter diffraction.It is found that the texture along the thickness direction in hot-rolled strips changes obviously;there are mainly copper,brass,and Goss textures in the surface layer;the 1/4 layer has weak Goss texture and rotating cube texture;γ-fib... 

本发明的取向性电磁钢板的制造方法能够稳定地制造被膜特性和磁特性优异的取向性电磁钢板。其包括：对含有规定的添加元素的钢坯进行热轧；冷轧制成最终板厚；进行脱碳退火；涂布以MgO为主剂的退火分离剂；进行最终退火，其中，上述退火分离剂的主剂的BET比表面积比率H2O/N2为0.6～1.6且浆料状态下粒径40μm以上的粒子的比例为5质量％以下。

根据本发明的一个实施例的双取向电工钢板，以重量％计，所述钢板包含Si：2.0至4.0％、Al：0.01至0.04％、S：0.0004至0.02％、Mn：0.05至0.3％、N：0.01％以下且0％除外、C：0.005％以下且0％除外、P：0.005至0.15％、Ti：0.001至0.005％、Ca：0.0001至0.005％和Mg：0.0001至0.005％，余量包含Fe和其他不可避免的杂质，具有从{100}＆lt;001＆gt;起15°以内的取向的晶粒的面积分数为60至99％，具有从{100}＆lt;025＆gt;起15°以内的取向的晶粒的面积分数为1至30％。

本发明公开了一种基于硅钢服役特性的立体卷铁心单框损耗测量方法及系统，根据硅钢片在立体卷铁心中的服役特性，获得测量铁心单框所需的非正弦励磁电压波形，通过所述立体卷铁心的心柱绕组电压和单框绕组电压之间的关系，确定所述被测立体卷铁心单框所需的电压有效值，再通过计算机、数据采集卡D/A转换器、功率放大器、隔离变压器和示波器，直接在所述立体卷铁心单框上加载励磁电压，利用功率表测量立体卷铁心单框损耗。本发明利用硅钢的服役特性，获得测量立体卷铁心单框所需的非正弦励磁电压波形和电压有效值，再将励磁电压直接加载到被测立体卷铁心单框，测量立体卷单框铁心损耗。

在50Kg氧化镁坩埚真空感应炉上进行高硅电工钢的脱氧试验。结果表明,通过控制原料的成分、高真空下的碳氧反应和炉衬分解向钢液中的供氧,可使钢液的总氧含量≤15×10-6;在维持高温高真空条件下,当钢液中的反应达到一定程度后,延长精炼时间并不能降低钢液的总氧含量;完成精炼后加入硅钙合金沉淀脱氧可进一步降低钢液的总含氧量,但脱氧效果有限。 The test of high-silicon electric steel deoxidation has been carried out in 50Kg vacuum induction furnace with magnesium oxide crucible.Results show that the total oxygen could be ≤15×10-6in molten steel by controlling material components,carbon-oxygen reaction in high vacuum and oxygen contamination from crucible materials on molten steel;And when the reaction was carried through to a certain extent,total oxygen in molten steel could not be reduced by the extension of refining period in high va... 

从影响高牌号无取向硅钢退火工艺的主要参数入手,介绍高牌号无取向硅钢退火炉在加热、气氛控制、冷却、涂层烘烤方面的新技术,并展望无取向硅钢退火炉的发展方向。 Based on the technology parameters of high-grade non-oriented silicon steel annealing,the new technology of the annealing line,which includes heating,atmosphere control,cooling,coating baking,is introduced,and the development direction of non-oriented silicon steel annealing furnace is pointed out.