对1990~2010年在我国申请的冷轧无取向硅钢涂层的专利数量、专利技术领域分布进行了统计,对典型涂层专利技术进行了分析,探讨了无取向硅钢涂层的发展趋势。统计分析结果表明,目前无取向硅钢涂层典型的专利技术主要有自粘结涂层、无铬含稀土元素涂层、含钼酸盐环保涂层及采用有机-无机纳米杂化材料为主成膜物形成的涂层等。无取向硅钢涂层发展的趋势主要是无铬环保的半无机、半有机型涂层。 The patent quantity of cold-rolled non-oriented silicon steel coating and distribution of technology fields applied in China in 1990-2010 were summarized.The analysis results indicate that typical patent technologies include self-adhesion coating,chromium-free and with rare earth element coating,environment-friendly and with molybdate coating,coatings with organic-inorganic hybrid materials as main forming agent and so on.The main development trends of coatings on silicon steel are among semi-in... 

取向硅钢利用析出物作为抑制剂,抑制初次再结晶晶粒的长大,抑制剂是取向硅钢发生二次再结晶的基本条件之一。文中通过低温板坯加热技术制备取向硅钢,采用透射电镜(TEM)观察并研究了高温退火阶段抑制剂的演化过程。结果表明,渗氮后形成的非晶态Si3N4析出物不稳定,在700～750℃退火升温阶段转化为(Al,Si)N;(Al,Si)N颗粒在800℃发生团聚,随后长大并粗化;(Al,Si)N是低温取向硅钢主要抑制剂,随退火温度的升高,(Al,Si)N抑制力大幅下降。 Precipitates as inhibitor are used to inhibit the grain growth of primary recrystallization in grain-oriented silicon steel,and inhibitor is one of the basic conditions for occurring of secondary recrystallization.The grain-oriented silicon steel was produced by low temperature slab heating and nitriding technique.The evolution of inhibitor was observed by transmission electron microscopy.The results show that Si3N4 particles are precipitated after nitriding,and Si3N4 particles are amorphous and... 

应用CAFE法对6.5%Si高硅钢铸锭凝固组织进行了模拟研究,确定出了适合高硅钢组织模拟的模型。进一步用该模型研究了过热度及冷却条件对凝固组织的影响,结果表明,随着过热度的降低,凝固组织中柱状晶比例和晶粒平均面积均减小。水冷条件下,高硅钢铸锭凝固组织几乎全是柱状晶,而且晶粒粗大。空冷条件下,等轴晶区扩大,但柱状晶仍占主要部分。缓冷条件下,等轴晶区占主要部分,晶粒平均面积和空冷条件下相当。 The solidification structure of 6. 5% Si steel ingot was simulated based on CAFE method and the model suitable for simulating the structure of high silicon steel wad ascertained. The influence of superheat and cooling condition on the solidification structure were studied. It was shown that with the superheat decreasing,the proportion of columnar crystals decrease,and the average grain size become smaller. Under water cooling condition,the solidification structure of casting was composed of almo... 

介绍了EB5325涂层液的主要性能和中冶新材生产冷轧无取向电工钢所用的涂层设备,通过多次试验摸索出使用EB5325涂层液的工艺,对涂层出现的缺陷进行分析研究,并提出解决方法,使中冶新材生产的冷轧无取向电工钢的涂层质量满足了用户的要求。 This article introduces the main properties of EB5325 and the coating equipments for cold-rolled non-oriented electrical steel. A process using EB5325 coating liquid is made through many time experiments and exploration. The appeared defects in the coating are studied and analyzed,and the solutions are proposed. The coating quality meets clients’ requirements of cold rolled non-oriented electrical steel. 

无取向硅钢特别是中牌号以上的无取向硅钢,随着含硅量的提高,常温下塑性较差,冷轧过程中轧制力明显提高,如果存在原料质量问题,极易发生断带事故,影响硅钢冷轧过程的成材率和生产效率。通过优化冷轧工艺参数,可提高冷轧稳定性。生产中通过合理分配冷轧各道次压下量和轧制速度,保证了轧制过程的稳定,很大程度减少了冷轧断带事故的发生。 Non-oriented silicon steel, especially in the low and middle grade, with the increase of silicon content, plasticity is poor at room temperature, rolling force in cold rolling process significantly improved .If there is the quality defect of raw materials , easily sheet is rolling off. Affect finished product rate and production efficiency in process of cold-rolled silicon steel. Through optimization of cold rolled process parameter , improve the stability of cold-rolling process. Through reason... 

结合硅钢退火炉项目中应用PDSOFT软件进行三维配管设计的案例,描述PDSOFT软件的应用过程,总结其使用要点,分析其优缺点,并提出了推广三维设计软件的思路,对今后PDSOFT在相似项目中的推广应用有参考和借鉴价值。 Combining the case of using PDSOFT software to design the three-dimensional piping,the application process of the PDSOFT software is described,the using points are summarized,the advantages and disadvantages are analyzed,and the ideas of promoting the three-dimensional design software are put forward,which have a strong reference value for the promotion and application of PDSOFT in similar projects in the future. 

采用EBSD技术研究了有、无拉应力作用下无取向硅钢在晶粒长大过程中织构转变及晶界变化的规律。结果表明:在晶粒生长期间,无应力作用下的硅钢中,{111}〈112〉,{111}〈110〉织构组分强化,而{100}〈001〉织构组分弱化;与无拉应力作用下的情况相比,施加5MPa的拉应力时,{111}〈112〉,{111}〈110〉织构组分强化的速率下降,{100}〈001〉织构组分变化不明显。对于在晶粒生长期间持续变化的{111}〈112〉,{111}〈110〉和{100}〈001〉织构组分而言,虽然有、无拉应力作用下硅钢的{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率均下降,而{100}〈001〉织构组分的高取向差角度晶界频率则上升,但当有拉应力作用后,{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率下降的速率变小,{100}〈001〉织构组分的高取向差角度晶界频率上升的速率稍有变小。通过对无取向硅钢在晶粒长大过程中织构转变及晶界变化规律的研究,分析了合金原子在晶界的偏聚行为。 The rules of texture and grain boundary transformation in the nonoriented silicon steel under applied stress or without applied stress during grain growth were investigated by EBSD.The results show that the {111}〈112〉 and {111}〈110〉 components in the nonoriented silicon steel without stress are strengthened during grain growth whereas {100}〈001〉 component is weakened,but the growth rate of {111}〈112〉 and {111}〈110〉 component decreases,while the area fraction of {100}〈001〉 component doesn’t chang... 

本发明公开了硅钢片铁芯生产线，包括放卷机构、剪切机构、送料机构、叠片机构和下料机构，送料机构包括磁性传送带、送料件和第一定位杆，磁性传送带包括上传送带和下传送带，送料件可沿磁性传送带的正交方向平行伸出，其中，第一送料分台和第二送料分台安装于上传送带的下方并且相背运动，第三送料分台和第四送料分台安装于下传送带的下方并且相背运动，第一定位杆用于定位硅钢片，叠片机构包括叠放台、悬梁和两个六自由度机械手，六自由度机械手吊装于悬梁上，包括有电永磁铁，用于吸取硅钢片，下料机构包括滑板，叠放台放置于滑板上。根据本发明的硅钢片铁芯生产线，可提高设备自动化程度，提高叠片速度，从而提高生产线的生产效率。

【作者】 朱一知； 陈山； ...

本发明涉及一种高压电机用无取向硅钢50SBW600的制备方法，包括，S1，将装有精炼钢水的钢包运至回转台，回转台转到浇铸位置后，将钢水注入中间包；S2，中间包通过水口将所述钢水分配至若干个结晶器中，所述结晶器中设置有浸入式水口，S3,钢水在结晶器内生成晶核，结晶器将带有晶核的钢水下放至通道；S4，通道上设有第二电磁搅拌器，第二电磁搅拌器对通道内钢水进行电磁搅拌,所述钢水在通道中逐步转换为钢坯；S5,拉矫辊将的所述钢坯拉出通道并对钢坯进行形态矫正；S6,切断装置所述钢坯进行切割。本发明通过在无取向硅钢50SBW600制备过程中设置双电磁搅拌装置，充分保证连铸过程中钢坯中的等轴晶数量，保障了产品表面缺陷质量。

本实用新型实施例涉及一种硅钢片冲剪设备，该设备包括冲床、送料台、第一刀模、第二刀模和第三刀模；送料台用于传送待加工的硅钢条；第一刀模用于冲剪硅钢条以在硅钢条上形成预设形状的第一凹槽，第一凹槽处构成“工”字形硅钢片的一侧凹部；第二刀模用于冲剪硅钢条以在硅钢条上形成预设形状的第二凹槽，第二凹槽与所述第一凹槽相对应，第二凹槽处构成“工”字形硅钢片的另一侧凹部，第二刀模与硅钢条在硅钢条的横向方向上能够产生预设距离的相对位移；第三刀模用于沿硅钢条的横向方向剪断硅钢条。该设备能够采用硅钢片低成本、高效率地制造“工”字形硅钢片。

本发明公开了一种无底层取向硅钢的制备方法，包括以下步骤：S1、坯料预处理、S2、脱碳退火、S3、涂覆隔离剂、S4、高温退火、S5、拉伸热平整和S6、激光去除底层，所述激光去除底层的工艺参数为：激光400‑500W，重复频率100‑150kHz，振镜扫描速度6000‑7000mm/s。本发明利用激光刻痕的物理方法制备了无底层取向硅钢，代替了传统的用酸去除取向硅钢涂层或硅酸镁底层，制备的取向硅钢表面光亮，不含涂层或硅酸镁底层，同时通过退火补偿了激光制备过程中对钢带产生的塑性变形，制备的无底层取向硅钢，磁性能稳定。