借助电子背散射衍射(EBSD)及ZEISS-200MAT金相显微镜对某钢厂普通取向硅钢(CGO)进行研究,研究结果表明:热轧板组织、织构沿板厚方向存在明显的不均匀性,在热轧板表层及次表层发生再结晶,同时存在强度较高的Goss织构,中心层存在较强的{001}<110>变形织构。冷轧组织均呈纤维状条带组织,一次冷轧后,热轧板中的Goss织构消失,织构主要为α、γ织构,经中间脱碳退火后,α、γ织构强度减弱,并出现一定强度的Goss织构和利于Goss织构发展的{554}<225>、{332}<113>等织构,经二次冷轧后,二次冷轧织构类型与一次冷轧织构一致,但织构强度不同。 The grain-oriented silicon steel produced by a steel factory was investigated by EBSD and ZEISS-200 MAT metallographic microscope.The results show that the textures and microstructures along thickness of hot rolled slab are inhomogeneous.The surface layer and the layer near that are recrystallized structure which has a high Goss texture,but there is deformation texture{001}<110>in the central layer.The structure after cold rolling is a structure like fiber strip.After the first cold rollin... 

采用化学气相沉积(CVD)渗硅处理工艺连续制备6.5%Si高硅钢,具有优质的软磁性能,通过理论研究化学反应并且用简单的试验设备做进一步的探讨。根据试验的结果对连续制备6.5%Si高硅钢的CVD工艺构造提出全面、有效的建议,实现制备6.5%Si高硅钢系统。 CVD method for continuously manufacturing 6.5%Si Steel Sheet has excellent soft magnetic.Carried out a theoretical study of related chemical reaction and performing basic research with a simple test apparatus.Based on the results,finally proposed an overall process configuration to realize such a production-CVD method for continuously manufacturing 6.5%Si Steel Sheet. 

本实用新型公开了一种适用于自动线的硅钢叠装系数性能检测装置，涉及实验仪器自动化技术领域，为解决机器人自动上样至叠装系数测量仪经常发生碰撞的问题；本实用新型包括框架、上压板、下压板、压紧驱动机构、高度探规和加载力值传感器，其中压紧驱动机构设置于框架上端，下压板固定于框架内的下端，上压板安装于下压板上方且与压紧驱动机构的输出端传动连接，加载力值传感器安装于上压板与压紧驱动机构的输出端之间，高度探规安装在上压板上，且探头向下伸出上压板下端面，框架为“C”字形一体式刚性结构，其设有上下两个水平板，以及位于一侧的竖直板；本实用新型能够避免机器人自动上样时碰撞到框架，以及下压时高度探规压到试样。

研究了CSP工艺流程生产的硅含量为1.5%的无取向电工钢在不同常化温度下对磁性能的变化。研究结果表明:随着常化温度的提高,热轧板的晶粒尺寸增大,且组织均匀性提高;此外成品的有利织构组分{100}<0vw>、α、η增强,不利织构组分减弱;铁损P1.5/50呈下降趋势,磁感B50上升平缓。在常化工艺为970℃×2.5min下,对应的铁损P1.5/50<3.4W/kg,磁感B50>1.74T。 The effect of normalizing temperature on the magnetic properties of non-oriented electrical steel containing 1.5%silicon produced by CSP process was studied.The results show that with increasing normalizing temperature,the average grain size of hot-rolled plate increases and the microstructure uniformity is improved.Furthermore,the texture components of finished products are improved through enhancing of{100}<0vw>,αandηtextures and weakening of{111}<112>texture;the core loss P1.5/50 ... 

本发明涉及无取向硅钢技术领域，尤其涉及一种改善高牌号无取向硅钢冷轧断带的控制方法。按重量百分比计：[Si+Al]≥4.0％；Mn、S含量满足：S≤0.0015，[Mn]/[S]:200～400；1)热轧过程中使用保温罩，热轧轧制时投入边部加热，头尾100米内卷曲温度提高15～30℃；2)常化机组圆盘剪进行边部剪边前增加加热装置，剪切后增加毛刺打磨装置，采用煤气明火加热，保证钢板温度在韧脆转变温度以上；3)圆盘剪间隙满足关系式：ds＝(0.15～0.45)d0ds:圆盘剪间隙，μm；d0:常化板板厚，mm；4)常化采用快速加热，控制钢带的预热段升温速度320～380℃/min，机组速度20～30m/min；5)常化工艺后，控制边部小于20μm的晶粒占比在5％以内。有效的减少了冷轧断带的发生，提高成材率1.30％以上，降低了生产成本。

本发明公开了硅钢片铁芯叠片机构，包括送料装置和叠片装置，送料装置包括有磁性传送带、送料件和第一定位杆，磁性传送带用于将已剪切的硅钢片传送至送料件，送料件安装于磁性传送带的下方，并且可沿磁性传送带的正交方向平行伸出，第一定位杆安装于送料件上，用于定位硅钢片，叠片装置设置于送料件的伸出的一方，包括有叠放台、第二定位杆和机械手，叠放台用于叠放硅钢片，第二定位杆用于定位硅钢片，机械手用于将送料件的硅钢片搬运至叠放台上，机械手包括有转动臂和取料单元，取料单元安装于转动臂的端部，包括有电永磁铁，电永磁铁用于吸取硅钢片。根据本发明的硅钢片铁芯叠片机构，可有效提高叠片速度，降低能耗，提高生产效率。

本实用新型公开了一种用于硅钢片自动叠片的机械手，包括底板与第一竖杆，所述底板上端一侧设置有第一竖杆，所述底板与第一竖杆固定连接，所述底板上端轴心处设置有垂直传动机构，本实用新型中在放置架的内部设置有重力传感器，并且该重力传感器通过程序设定，当上端物品的重力达到设定值时，这时重力传感器就会将警报灯的电源接通，这时警报灯就会进行工作，从而可以提醒工作人员堆码完成，本实用新型中在放置架的底端设置有垫脚，这样可以方便叉车将该放置架进行移动，本实用新型中通过在夹持机构内部靠近机械手的一侧设置有工业相机，这样可以使得机械手通过工业相机观察到传输带上方的工件，这样可以使得夹持的更加便捷。

目前高磁感冷轧硅钢生产过程中，采用经验方法确定的乳化液流量设定值往往会造成硅钢产品的磁感性能达不到预期目标，针对此情况，基于轧机轧制机理研究了的乳化液流量数学模型，确定了乳化液流量设定值。实践表明，使用该数学模型输出的乳化液流量设定值，可提高轧制过程中乳化液流量控制精度，从而提高高磁感冷轧硅钢的轧制性能。 In view of the current production process of high magnetically inductive cold-rolled silicon steel, the mathematical model of emulsified fluid flow based on mill rolling mechanism is studied in view of the situation in which the magnetic sensing performance of silicon steel products is often not up to the expected target by using empirical method to determine the emulsified liquid flow setting. Practice shows that the emulsified fluid flow setting value output from this mathematical model improv... 

测试了高强无取向电工钢的S-N曲线,并借助光学显微镜、扫描电子显微镜、透射电子显微镜分析了实验钢组织,疲劳断口形貌和位错结构。结果表明:室温条件下,频率为20Hz,应力比R为0.1,循环10~7周次时,实验钢的疲劳强度为360MPa,疲劳裂纹萌生于实验钢的次表面,裂纹萌生点附近有沿晶开裂现象,疲劳裂纹扩展区域有解理台阶与疲劳条纹,瞬间断裂区是韧性断裂,有大量韧窝。实验钢在循环应力作用下基体中产生了大量位错,并有驻留滑移带终止在晶界位置。 The S-N curve of a high strength non-oriented electrical steel was tested.The microstructure and fatigue fracture morphology and dislocation were analyzed by optical microscope,scanning electron microscope,transmission electron microscope.The results showed that:at room temperature and the frequency of 20 Hz and the stress ratio Rof 0.1,the fatigue strength of the experimental steel was 360 MPa when the cycle was 10~7 cycles.The fatigue crack initiation at the surface of the steel and the interg... 

分析了影响脱碳效果和结晶行为的各种要素及其相互制约关系,提出了Hi-B连续退火工艺曲线,总结得出快速加热及合理稳态气氛是实现工艺制度的关键。结合实际工程,介绍了在连续退火炉设计中快速加热和气氛设计的考虑方法,并指出随着Hi-B产品的发展,如何改进这些方法将是连退工程研发的方向之一。 The factors which affect decarbonization and crystallization and the mutual restriction between them were analyzed.A complete continuous annealing process for Hi-B was put forward.As a result,the rapid heating and the proper steady atmosphere were two important factors.According to an actual project,the consider methods for designing rapid heating and proper steady atmosphere were introduced,and it is pointed that with the development of Hi-B technique,how to improve these techniques would be on... 

研究二次冷轧压下率对于硅的质量分数为3.0%的无取向硅钢组织结构和磁性能的影响。结果表明:当第二次冷轧压下率从0变化至16.7%时,铁损逐渐增加,磁感逐渐降低。当第二次冷轧压下率大于16.7%时,随压下率的增加,铁损逐渐减小,磁感逐渐增加。当第二次冷轧压下率大于38%时,二次冷轧法所能获得的磁性能明显优于一次冷轧法。 Effect of double cold reduction on magnetic,microstructure and texture of 3.0% Si non-oriented silicon steel sheets was investigated.The results show that the iron loss increases and magnetic induction reduces as the percentage redcution in secondary cold rolling changes from 0 to 16.7%.The core loss can be reduced remarkably,and magnetic induction can get a little benefit if the percentage redcution in double cold reduction is higher 16.7%.In case of higher than 38% of the percentage redcution ... 

本发明提供一种以热轧卷为单元观察时具有在长边方向整个长度上均匀的织构，磁特性的变动小的取向性电磁钢板的制造方法。上述取向性电磁钢板的制造方法，包括如下步骤：将具有规定的成分组成的钢坯热轧而制成热轧板，将上述热轧板退火而制成热轧板退火板，对上述热轧板退火板实施1次或者隔着中间退火的2次以上的冷轧而制成最终板厚的冷轧板，对上述冷轧板实施一次再结晶退火和二次再结晶退火；至少1次冷轧的总压下率为80％以上，并且利用连轧机进行，利用上述连轧机的至少一个机架进行的轧制在压下率为30％以上且上述机架的工作辊的咬入温度T0℃的条件下进行，其中，将上述热轧板退火板的前端和尾端中的一方或两方的上述工作辊的咬入温度设为70℃以上且比上述钢板的温度T0℃高10℃以上的温度。