硅钢资料

结合工业化生产的50A1300牌号无取向硅钢,分析了化学成分、RH精炼脱氧方式、板坯装炉温度以及热轧平整工艺等对磁性能的影响,探讨成品钢磁性能的改善。结果表明,采取改善后,50A1300牌号无取向硅钢的磁性能得到明显改善。2012年,该钢种平均铁损、磁感应强度分别达到5.26 W/kg、1.762 T,能够较好地满足用户市场需求及同行对标需要。 Based on the industrial manufacture of 50A1300 grade non-oriented silicon steel sheets,effects of chemical composition,deoxidization method in RH vacuum refining,charging temperature of steel slabs,hot rolling and flattening progress on magnetic properties are analyzed.The optimization methods of magnetic properties of steels are discussed. Results show that the magnetic properties are obviously improved by the adopted measures above. In 2012,the average core loss and the magnetic induction of 5... 

研究了传统工艺流程生产的2%Si无取向电工钢在不同退火温度下的磁性能。研究结果表明,随着退火温度的升高,显微组织均匀性提高且晶粒尺寸增大;有利织构组分{100}<0vw>、α、η增强,不利织构组分减弱;成品的铁损P1.5/50先下降后略有上升,磁感B50上升平缓;在890℃×2 min的退火工艺条件下,成品电工钢的磁性能最佳,对应的铁损P1.5/50小于3.2 W/kg,磁感B50高于1.74 T。 In this paper,the effect of annealing temperature on magnetic properties of non-oriented electrical steel with 2% silicon was studied.Results show that the uniformity of microstructure and the average grain size increase with the rise of annealing temperature.The texture components of annealing can be improved by enhancing {100} <0vw>,α,η fiber textures and weakening {111} <112> fiber texture.The tendency of core loss P1.5/50 shows that it decreases first and then increases,while the... 

本实用新型公开了一种变压器铁芯硅钢片纵剪滚切装置，包括纵剪机本体、弹性压覆机构和涂油机构，所述纵剪机本体的进料端设置有弹性压覆机构，料带通过弹性压覆机构压覆在纵剪机本体的支撑平台上，所述支撑平台上凹设有安装凹槽，所述安装凹槽内设置有涂油机构，所述涂油机构朝向于料带的底面涂油，通过涂油机构对板材的切割面进行涂油，能够对料带起到润滑和冷却的作用，提升料带切割质量。

分析了冲裁硅钢芯片时出现的质量问题,针对影响硅钢芯片冲裁质量的4大因素——人、原材料状态、工艺和工装进行了工艺试验和分析,根据原材料状态的差异,采用不同工艺方案,特别是如何合理选择冲裁模具间隙,解决了硅钢芯片冲裁时产生的主要质量问题,使冲裁的硅钢芯片达到最佳质量状态,并满足硅钢芯片的使用性能。 The problems occurred during silicon steel chip punching and the factors that affect the quality of silicon steel chip punching were analyzed,the factors include 4aspects,that is,people,raw material status,process and frock,at the same time,process tests and analysis aimed at the factors that affect punching quality were did,according to the difference of raw material status,corresponding process schedules wee taken,especially in how to reasonably select punching dies clearance,which solved the ... 

本发明属于酸洗设备技术领域，具体涉及一种硅钢生产用酸洗设备，包括酸洗池、放卷机构和收卷机构，酸洗池被依次分隔为第一酸洗腔、第二酸洗腔、浸泡腔和喷洗腔；第一酸洗腔和第二酸洗腔内滑动连接有刷洗架，浸泡腔内滑动连接有定位架，喷洗腔内滑动连接有喷洗架；刷洗架、定位架和喷洗架上均转动连接有多根转辊，转辊上设有刷毛；刷洗架和喷洗架上设有用于驱动转辊转动的驱动件；喷洗架上的转辊开有空腔和多个与空腔连通的喷孔，喷洗架上开有与空腔连通的通道和与通道连通的进水口；喷洗腔的底部和侧壁设有多个喷头；酸洗池内转动连接有多根位于第一隔墙上方的刷辊。在本方案，通过酸洗以及充分的刷洗，能够充分有效的除去硅钢表面的氧化皮。

本发明公开了一种宽频率低铁损无取向电工钢及其制备方法，属于无取向电工钢生产制造技术领域。它从电工钢表面向内依次包括0.005mm～0.1mm的渗透层和钢材内芯；所述渗透层是由硅原子向电工钢内渗透形成，渗透层中的硅元素含量为3wt％～8wt％；所述钢材内芯包括2.0wt％～5.5wt％的硅元素和不少于93.2wt％的铁元素。本发明能保证无取向电工钢具有低频低铁损性能同时有效降低高频条件下的铁损，具体铁损性能为：铁损P1.5/50≤2.35W/kg，铁损P1.0/400≤13.8W/kg。

采用轧制法制备出具有低铁损高磁感0.23mm厚6.4%(质量分数)Si高硅钢。沿轧制方向的最终磁性能为B8=1.474 T,B50=1.714 T;P10/50=0.30W/kg,P15/50=0.88W/kg。利用X射线衍射及背散射电子衍射(EBSD)技术分析了高硅钢在轧制及退火过程中的织构演变过程。结果表明,通过采用大压下率热轧,确保热轧板次表层中产生更多的高斯织构,随后进行遗传;温轧板中粗大的晶粒有利于冷轧剪切带的形成;冷轧板经脱碳退火后生成强{210}〈001〉织构及次表层较强的高斯织构是在轧向上获得高磁感的原因,归因于其在{111}〈112〉冷轧形变晶粒内的剪切带优先形核并长大;最终退火后虽出现了随机取向,但以{310}〈001〉织构为代表的η织构得以保留并且增强,进一步提高了磁感。随着退火温度的升高及保温时间的延长,高硅钢薄板晶粒尺寸不断增大,铁损明显降低。 6.4wt%Si high silicon steel sheets(0.23mm thick)with low iron loss and high magnetic induction were successfully produced by rolling process.The final magnetic properties along the rolling direction(RD) were:B8=1.474T,B50=1.714T;P10/50=0.30 W/kg,P15/50=0.88 W/kg.The texture evolution during rolling and annealing was investigated by means of X-ray diffraction and electron backscatter diffraction(EBSD).It was found that more Goss textures formed in the subsurface of hot rolled plates by using larg... 

本发明揭示了一种无取向硅钢的生产方法。所述生产方法中：按照Si:0.3～1.2％炼钢、制坯；将铸坯加热到1050～1150℃并保温150min以上，而后轧成厚度40～45mm的中间坯，再经精轧、卷取得到厚度为3.00±0.25mm的热轧卷板，精轧开轧温度≤Ar1＝872℃+1000*(11*[Si]‑14*[Mn]+21*[Al])；当Ar1≥1000℃，终轧温度T≤840℃，否则T≤Ar1‑160℃；卷取温度≤550℃；经常化、酸连轧得到0.500±0.005mm的冷硬卷，常化温度为850～950℃；退火温度820～950℃，经成品退火、冷却、涂层和精整，得到无取向硅钢成品。

本发明公开了一种电工钢片磁致伸缩模型的建模方法，包括：测量不同旋转磁场下电工钢片磁致伸缩对称蝴蝶曲线εk；对所测量的对称蝴蝶曲线进行辨识，构建磁致伸缩蝴蝶曲线εk的Everett函数数据库；将输入的矢量磁场B波形用旋转磁场形状参数Bmax,最大值方向的方向角θ和椭圆长短轴的长度比λ拟合，得到拟合后结果；通过线性插值法在磁致伸缩Everett函数数据库中进行插值，获得拟合后结果所对应的磁致伸缩Everett函数值Ek；根据Everett函数值Ek计算得出对应的磁致伸缩蝴蝶曲线εk。应用本发明实施例，不仅可以描述矢量磁致伸缩特性，还可以通过计算估算出旋转磁场下的瞬态磁致伸缩。此外，还能够考虑磁致伸缩的各向异性特性。

本发明属于冶金技术领域，涉及一种超短流程稀土取向硅钢及其制备方法，化学组成及其重量百分比为Si：2.0～4.5％，C：≤0.003％，Y：0.001～0.05％，Mn：0.15～0.35％，Al：0.03～0.04％，Cu：0～0.5％，S：0.025～0.04％，N：0.011～0.013％，其余为Fe和不可避免的杂质元素。制备工艺包括：钢水冶炼、薄带连铸、冷轧、再结晶退火。与常规生产方式相比，取消了连铸、粗轧、热连轧、常化和脱碳退火等工序，极大简化了生产流程。通过添加稀土元素钇，促进了抑制剂的析出，还显著细化了薄带连铸硅钢的凝固组织，提高组织均匀性，获得了均匀细小的等轴晶，优化了取向硅钢的性能。

本发明涉及电机技术领域，具体涉及一种具有低应力隔磁桥的硅钢片和电机转子。包括硅钢片、开设在硅钢片上的若干个磁钢槽组和永磁体，若干个磁钢槽组沿所述硅钢片周向分布，每个磁钢槽组均至少包括一对沿径向对称分布的磁钢槽，永磁体嵌设于磁钢槽内，磁钢槽朝向硅钢片内侧的一端设有空腔，一对磁钢槽的空腔之间通过隔磁桥隔离，隔磁桥的空腔上壁面与空腔侧壁面之间通过第一椭圆弧过渡连接，隔磁桥的空腔下壁面与空腔侧壁面之间通过第二椭圆弧过渡连接。有效降低该处隔磁桥在拐角处所受应力，进而提高该隔磁桥的强度，避免磁钢和铁芯产生形变而断裂。

本发明是关于一种薄规格无取向硅钢35BW440，该无取向硅钢35BW440包括以下质量百分比的元素：C：≤0.003％，Si：0.8％‑2.0％，Mn：0.4％‑1.2％，P：≤0.015％，S：≤0.003％，Als：0.25％‑0.6％，N：≤0.003％，Sb：0.04％‑0.1％，O：≤0.0025％，其余为Fe及不可避免的杂质。在没有电磁搅拌设备增加无取向硅钢磁感应强度的前提下，通过加入Sb元素，增加对电磁性能有利的{110}和{100}织构组分，提高电磁性能，采用二次冷轧及中间连续退火的工艺，提高无取向硅钢的表面质量。