根据本发明的一个实施例的双取向电工钢板，以重量％计，所述钢板包含Si：2.0至4.0％、Al：0.01至0.04％、S：0.0004至0.02％、Mn：0.05至0.3％、N：0.01％以下且0％除外、C：0.005％以下且0％除外、P：0.005至0.15％、Ti：0.001至0.005％、Ca：0.0001至0.005％和Mg：0.0001至0.005％，余量包含Fe和其他不可避免的杂质，具有从{100}＆lt;001＆gt;起15°以内的取向的晶粒的面积分数为60至99％，具有从{100}＆lt;025＆gt;起15°以内的取向的晶粒的面积分数为1至30％。

以马鞍山钢铁集团公司电工钢板形优化控制研究项目为背景,系统地研究了热轧、冷连轧和单机架轧机在电工钢生产过程中的边缘降控制问题。通过现场数据采集、工况数值模拟计算和工业化大生产试验,设计出适用、合理的电工钢板形控制的辊型优化曲线,满足了不同工序、不同机型的板形控制策略要求,解决了电工钢板形质量问题,取得了显著的经济效益。 Based on the project of electric steel strip shape optimization control,problem of edge drop control was systematically studied in production of electric steel of hot-rolling mill,cold-rolling mill and single stand mill.Roll optimization contour was designed out in point and reasonable by collection of work condition data,numerical simulation and test of industrial production.The shape control system can meet with the different working steps and difference mills,and quality problem of electric s... 

一种甩带法制备高磁性能含磷硅钢薄带的方法，属于合金材料领域。本发明以硅钢(Fe‑(3‑6.5)wt.％Si)块体为母合金，并添加一定量的硅铁合金及磷铁合金，放置于中频感应炉中，熔融后经快速凝固‑甩带、冷轧、热处理工艺，得到具有优异性能的含磷硅钢薄带。对于硅钢而言，P元素的少量加入能够有效的提升电阻率从而显著降低铁损，且具备优化软磁性能的作用。而采用甩带法能够充分利用其快速凝固的特征，从根本上避免了P元素在传统熔炼冷却过程中严重偏析的缺陷，极佳地保证了产品的组织优势与软磁性能。本发明具有操作简单、生产效率高、产品精度高、工艺流程短、无污染与夹杂、性能优异等优点。

本发明公开了一种用于取向硅钢卷的焊缝切除方法，包括在焊接机组完成钢卷焊接后，在距离焊缝预设距离位置处冲孔；而后，钢卷到达成品退火工序时，利用孔洞检测装置检测焊缝冲孔，并根据焊缝冲孔得到焊缝位置，并记录该焊缝位置；并在分卷工序中，根据记录得到的焊缝位置对焊缝进行切除。这样，该方法利用焊缝冲孔，结合孔洞检测装置，将焊缝位置信息传递到分切工序，使得焊缝识别切除率较高，有效解决了取向硅钢焊缝无法精准定位切除的问题，实现了卷中焊缝多工序结合精准切除。

本发明公开一种冷轧硅钢的横向同板差控制方法，具体如下：S1、确定冷轧钢板横向同板差的影响因子，包括：热轧钢卷的热卷凸度、工作辊辊型插入量、中间辊窜动值及冷轧钢卷的总切边量；S2、以影响因子为变量构建冷轧钢板横向同板差的计算模型；S3、将热轧钢卷的热卷凸度及冷轧钢板的目标横向同板差输入计算模型，确定最小冷轧钢卷总切边量下的工作辊辊型插入量及中间辊窜动值。明确客户所需的横向同板差，通过改变工作辊辊型插入量X2及工作辊窜动值X3，以此得到冷轧成品钢卷的总切边量最小值，在满足客户对横向同板差的使用要求前提下，降低生产成本，提高产品竞争力。

本发明提供了一种超低铁损无取向硅钢薄带，以质量百分比计，其成分包括C≤0.005％，Si：3.5～4.0％，Mn：0.1～0.3％，Als≤0.005％，P≤0.05％，S≤0.005％，Cu≤0.08％，N≤0.003％，Sn：0.04～0.08％，其余为Fe及不可避免杂质，所述硅钢薄带中Mn与S的含量比Mn/S≥50，所述硅钢薄带厚度为0.3‑0.4mm。本发明还提供了一种超低铁损无取向硅钢薄带的制备方法。本发明提供的一种超低铁损无取向硅钢薄带，具有高磁感、低铁损等优良性能，且其制备工艺流程短、容易实现、生产效率高、生产成本低、节能降耗明显。

取向硅钢常化工序主要采用现场实测带钢温度的方式测定冷却速率，并通过稳定冷却水温、调整冷却水量及喷梁运行数量等方式保证合理的冷却速率，给常化工艺设计和生产带来诸多不便。通过对常化工艺水冷过程带钢的传热分析求解，在建立带钢水冷温度模型的基础上，研究了不同冷却工艺参数对带钢温度及冷却速率的影响规律以及冷却工艺的交互作用结果。结果表明：模型计算结果能够较好地反映取向硅钢在常化水冷过程中的温度及冷却速率的变化，其计算误差为0.80%～4.11%;在特定取向硅钢厚度规格和常化工艺下，随着常化冷却水量及有效冷却长度的增加，带钢水冷温度及冷却速率与呈非线性变化；常化水冷工艺主要通过调控带钢与冷却水之间热交换量和交换时间实现对带钢温度的控制，实际生产中需综合考虑机组速度、冷却水量及有效冷却长度之间的交互作用，选定喷梁投入数量和冷却水量以获得稳定的冷却速率。 The cooling rate of normalization process mainly determined by measuring the grain oriented silicon steel strip temperature on site, and ensures the cooling rate by stabilizing the cooling water temperature, adjusting the cooling water volume and the operation quantity of spray beam, which brings inconvenience to the normalization process design and production. Based on the heat transfer of strip in the water cooling section of normalization process, the water cooling temperature model for the n... 

对高牌号无取向电工钢国内生产情况、工艺技术、产品性能及应用领域等进行了阐述,并探讨了高牌号无取向电工钢产品的发展趋势。 This paper introduces basic facts on the production status,process technology and products’ properties and their applications of non-oriented electrical steel with high grade at home,and then discusses the development trend on technology for producing the non-oriented electrical steel with high grade. 

在50Kg氧化镁坩埚真空感应炉上进行高硅电工钢的脱氧试验。结果表明,通过控制原料的成分、高真空下的碳氧反应和炉衬分解向钢液中的供氧,可使钢液的总氧含量≤15×10-6;在维持高温高真空条件下,当钢液中的反应达到一定程度后,延长精炼时间并不能降低钢液的总氧含量;完成精炼后加入硅钙合金沉淀脱氧可进一步降低钢液的总含氧量,但脱氧效果有限。 The test of high-silicon electric steel deoxidation has been carried out in 50Kg vacuum induction furnace with magnesium oxide crucible.Results show that the total oxygen could be ≤15×10-6in molten steel by controlling material components,carbon-oxygen reaction in high vacuum and oxygen contamination from crucible materials on molten steel;And when the reaction was carried through to a certain extent,total oxygen in molten steel could not be reduced by the extension of refining period in high va... 

本发明特别涉及一种控制边部翘皮的热轧电工钢的生产方法和生产系统，属于钢表面质量检测技术领域，方法包括：建立热轧电工钢边部翘皮的数据库，数据库包括翘皮类型及各翘皮类型的翘皮发生原因和翘皮发生的区域；对待质检的热轧电工钢表面进行识别，并对比数据库，获得待质检的热轧电工钢表面翘皮的翘皮类型；根据待质检的热轧电工钢表面翘皮的俏皮类型获得该类型翘皮的翘皮发生原因和翘皮发生的区域；根据翘皮发生原因和翘皮发生的区域，调整生产操作，用以减少热轧电工钢的边部翘皮；通过对边部翘皮进行准确分类及识别，能够准确的分辨出边部翘皮的产生原因，采取有针对性的措施防止缺陷扩大，最大程度的降低缺陷发生量，提高质量控制水平。

本发明公开了一种显示取向硅钢高温退火试样显微组织的方法，其主要流程为：取样→制样→腐蚀→金相观察；本发明提供的方法显示的试样晶界清晰完整，达到人工和金相分析软件的评级要求，对于精确测量取向硅钢显微组织和磁性能分析提供了更加可靠的条件。

某冷连轧机生产无取向硅钢板材时,其边缘降的长度合格率频繁超标。为满足用户的叠片厚度精度要求,这类产品必须以增大切边量的方式来保证交货质量,而这种方式又直接降低了金属收得率,提高了生产成本。基于此,以该产线现有设备特性为基础,详细分析其软、硬件功能模式,分别对辊形与反馈控制进行全面分析与优化改进。通过现场试验论证,充分明确依托辊形优化与反馈控制程序的改进能显著提高边缘降的控制水平,该技术的使用为生产现场的边缘降控制提供了合理的技术支撑。 A cold rolling mill production of non-oriented silicon steel sheet,the thickness difference of the edge( edge-drop) is usually exceed the preset standard value,In order to meet the accuracy requirements of the user flatness,these production must be trimed wider length to meet the delivery quality of the user need, which directly reduce the metal yield and increase the manufacturing cost. Therefor,the software and hardware of the production line has been analyzed, and the work roll shape and feed...