硅钢资料

介绍了双蓄热燃烧技术的特点和高温硅钢加热炉的特点,探讨了双蓄热燃烧技术在高温硅钢加热炉中使用的技术难点,分析了双蓄热燃烧技术在高温硅钢加热炉上使用的可能性。 Introduced characteristics of double regenerative combustion technology and high temperature silicon steel reheating furnace,discussed technical difficulties for using double regenerative combustion technology,analyzed the possibility of double regenerative combustion technology applied to high temperature silicon steel reheating furnace. 

采用自主研发的脉冲磁场退火装置，在取向硅钢脱碳退火过程中分别施加不同强度的磁场，并采用光学显微镜和X射线衍射仪研究了脉冲磁场脱碳退火后试样的显微组织和宏观织构。结果表明，脱碳退火过程中施加脉冲磁场后取向硅钢的平均晶粒尺寸均增加，当磁场强度为40 mT时，平均晶粒尺寸最大，为13.06μm。此外，取向硅钢试样的立方织构{001}<100>强度减弱，高斯织构{110}<001>和{111}<112>织构增强，有利于获得更好的成品织构和磁性能。 Self-developed pulsed magnetic field annealing device was used to apply magnetic field of different intensities during decarburization annealing of an oriented silicon steel, and microstructure and macro-texture of the specimens after decarburization annealing in a pulsed magnetic field were studied by using optical microscope and X-ray diffractometer. The results show that the average grain size of the oriented silicon steel increases with the application of pulsed magnetic field during decarbu... 

1.本外观设计产品的名称：硅钢片。;2.本外观设计产品的用途：多片硅钢片用来共同组成马达的转子的其中一个部件。;3.本外观设计产品的设计要点：在于本外观设计产品的形状。;4.最能表明设计要点的图片或照片：立体图。;

常化快冷是生产高牌号无取向硅钢和高磁感取向硅钢不可缺少的一个工艺环节,气-雾冷却则是实现常化快冷的关键方式之一。介绍了国内自主设计建设的常化酸洗机组气雾冷却系统的技术特性,并对其特点进行了系统分析,最后给出该系统在设计、运行参数的选择上若干注意事项,对气-雾冷却系统设计和使用具有一定的指导作用。 The normalizing rapid cooling is a indispensable process to high grade non-oriented silicon steel and high magnetic induction oriented silicon steel’ s production. The fog cooling is a key ways of coming true the normalizing rapid cooling. This paper introduces the technical features of the fog cooling system in normalizing pickling line which is the domestic independent design and construction. Meanwhile,the fog cooling system’s characteristic is analyzed systematacially. In the end,this paper ... 

本发明的一种方式的无取向性电磁钢板用热轧钢板，以质量％计含有：C：0.0050％以下、Si：0.5％以上3.5％以下、Mn：0.1％以上1.5％以下、Al：0.1％以上1.5％以下、Cu：0.01％以上0.10％以下、Sn：0.01％以上0.20％以下；剩余部分由Fe和杂质构成；在从表面到深度10μm的范围内，具有0.12％以上的Cu的浓度峰值。

通过试验确定氩气分析流量为3.5L/min,静态流量为0.75L/min,冲洗时间为3s,预燃时间为12s,积分时间为5s的激发条件,采用火花源原子发射光谱法测定取向硅钢中碳、硅、锰、磷、硫。分别采用铣床铣样、砂轮磨样两种制样方式进行了精密度考察,发现制样方式对结果影响不大;讨论了取向硅钢样品中碳、硅、锰、磷、硫测定时可能存在的共存元素干扰,发现硅对锰元素的干扰不可忽略,采用干扰系数法进行了校正,据此拟合得到各元素校准曲线的相关系数均在0.999 0以上。精密度考察结果表明,碳、硅、锰、磷、硫的相对标准偏差(n=10)在0.71%~9.4%之间。对两块取向硅钢生产样品进行分析,并与钢铁研究总院进行比对分析,结果一致,且偏差均在允许范围内。 Carbon,silicon,manganese,phosphorus and sulfur in oriented silicon steel were determined by spark source atomic emission spectrometry.The selected excitation conditions were as follows:the analytical flow rate of argon was 3.5L/min,the static flow rate was 0.75L/min,the flush time was3s,the precombustion time was 12sand the integration time was 5s.Two sample preparation methods,including milling machine and grinding wheel,were investigated.The precision test results showed that,the determination... 

【作者】 王爱华； ...

电工钢试样加工产生的剪切应力会恶化钢板的磁性,对不同牌号硅钢片的横向、纵向试样退火前后磁性能的变化进行研究,结果表明:无取向硅钢片在剪切过程中横向、纵向的磁性受到剪切应力影响是不一样的。 The electrical steel sample processing magnetic of electrical steel will worsen due to the shear stress of sample. In this paper,the magnetic change of transverse,longitudinal specimens of different type of silicon steel sheet before and after annealing are studied. The results show that the magnetic of non- oriented silicon steel sheet affected in the process of shear is not the same in horizontal and vertical direction. 

本发明属于钢铁冶炼技术领域，涉及一种超低铝极低硫无取向硅钢的冶炼方法，包括如下步骤：KR铁水预处理→BOF复吹转炉冶炼→RH真空炉精炼→LF精炼→连铸；采用本发明中的冶炼方法，铁水脱后硫可以适当放宽，转炉出钢温度可以适当降低，RH工序无需采用OB法升温，也无需RH顶枪喷粉或者加入合成渣脱硫，LF只需实现微调成分、调节温度、平衡炉机节奏以及适当脱硫。此种冶炼方法充分利用并发挥了各工序优势，避免了在某一工序完成所有冶炼任务，一旦发生事故，容易造成生产中断，产品质量难以保证。

本发明公开了一种直流换流阀饱和电抗器用超薄硅钢铁心质量的评估方法，包括以下步骤：S1、外观评价；S2、叠装系数评价；S3、磁性能评价；S4、噪声评价；S5、耐受环境温度变化评价和S6、长期运行性能评价，本发明考虑了直流换流阀饱和电抗器对超薄硅钢铁心外观、叠装系数、磁性能、噪声及长期运行等特性要求，实现了超薄硅钢铁心外形外观的性能评估、铁心基本参数评估、电磁性能评估、耐受环境温度变化评估及长期电热运行特性评估，为直流换流阀饱和电抗器用超薄硅钢铁心可靠运行提供了保障。

本发明提供一种优化无取向硅钢连续退火工艺的铁损预测方法，步骤包括：S1.建立预测模型回归方程表达式；S2.将无取向硅钢中的硅、锰、铝质量含量及预设的退火速度、退火温度代入S1中的回归方程表达式中进行计算；S3.将步骤S2计算得到的预测值与目标值进行比较，如果预测值在目标值的允许误差范围内，则按照预设的退火速度、退火温度进行生产；否则对预设的退火速度、退火温度进行调整，直至预测值能够达到目标值的要求后再进行生产。本发明提供的模型能够提高产品质量，对优化无取向硅钢连续退火工艺具有指导意义。

本发明揭示了一种高硅无取向电工钢及其生产方法。该方法包括：1）钢水冶炼并连铸成坯；2）加热并保温，之后热轧得到热轧卷板，其中粗轧出口温度940±20℃，精轧终轧温度840±20℃，卷取温度650±20℃；3）常化，常化温度((732~742)+3000[Si])℃，常化时长4min~5min；4）常化后直接进行冷轧，而后连续退火和涂层，退火温度940℃~990℃且退火时长1.5min~3min；5）涂层处理后的钢板加工成型，而后进行去应力退火，退火温度为((761~766)+3000[Si])℃。如此，在保证磁性能的同时，解决了冷轧难度大的问题。