选用Q235和Q345钢,在纯锌浴和含钛量分别为0.05%、0.10%、0.15%、0.20%(质量分数)的合金浴中浸镀0.5、1、3、5、8 min。利用扫描电子显微镜和能谱仪研究了钛对热浸镀锌组织和生长动力学的影响,并提出钛对含硅钢铁锌反应抑制作用的机理。结果表明:钛的加入缩短了Γ的孕育期,促进了合金层中δ的生长和ζ的消失,δ的生长依然受扩散控制,呈抛物线生长规律;Zn-0.05%Ti锌浴可以很好的抑制高硅钢的硅反应性;含硅钢热浸镀锌钛合金浴时,在锌浴中会形成锌铁钛三元T相,该相能吸收ζ晶界处富集的硅,从而抑制了铁锌反应。 Both Q235 and Q345 steels were immersed for 0.5 to 8 min in Zn bath with different amount of Ti,ranging from 0 to 0.20 mass%,for galvanization.The effect of Ti in Zn bath on microstructure and growth kinetics of hot-dip galvanizing coatings on the two steels were investigated by means of SEM and EDS analysis.Base on the experiment,the mechanism of Ti additions in controlling Fe-Zn reaction was proposed.The results show that addition of Ti in the zinc bath decreases the incubation time of Γ phase... 

采用双辊连铸工艺制备了硅的质量分数分别为0.5%,1.0%,3.0%,4.5%的硅钢薄带,用光学显微镜观察其组织,并研究了后处理工艺对薄带组织和性能的影响。结果表明:硅含量为0.5%和1.0%的薄带适合采用一次冷轧+850～950℃退火的后处理工艺,而硅含量在3.0%以上的薄带适合采用二次冷轧+950℃退火的后处理工艺;硅含量为3.0%和4.5%的薄带在冷轧并950℃退火后,其磁性能最佳,铁芯损耗约为4.30 W·kg^-1,磁感应强度约为1.68T。 Silicon steel thin strips with silicon content of 0.5wt%,1.0wt%,3.0wt%and 4.5wt%were prepared by twin-roll continuous casting process,and the microstructure of the strips were observed by means of optical microscopy,and on the basis,the effect of post-treatment process on microstructure and properties of the strips was studied.The results show that the post-treatment process of one-time cold rolling and annealing between 850—950℃was suitable for the strips with silicon content of 0.5wt%and 1.0wt... 

采用EBSD技术研究了有、无拉应力作用下无取向硅钢在晶粒长大过程中织构转变及晶界变化的规律。结果表明:在晶粒生长期间,无应力作用下的硅钢中,{111}〈112〉,{111}〈110〉织构组分强化,而{100}〈001〉织构组分弱化;与无拉应力作用下的情况相比,施加5MPa的拉应力时,{111}〈112〉,{111}〈110〉织构组分强化的速率下降,{100}〈001〉织构组分变化不明显。对于在晶粒生长期间持续变化的{111}〈112〉,{111}〈110〉和{100}〈001〉织构组分而言,虽然有、无拉应力作用下硅钢的{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率均下降,而{100}〈001〉织构组分的高取向差角度晶界频率则上升,但当有拉应力作用后,{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率下降的速率变小,{100}〈001〉织构组分的高取向差角度晶界频率上升的速率稍有变小。通过对无取向硅钢在晶粒长大过程中织构转变及晶界变化规律的研究,分析了合金原子在晶界的偏聚行为。 The rules of texture and grain boundary transformation in the nonoriented silicon steel under applied stress or without applied stress during grain growth were investigated by EBSD.The results show that the {111}〈112〉 and {111}〈110〉 components in the nonoriented silicon steel without stress are strengthened during grain growth whereas {100}〈001〉 component is weakened,but the growth rate of {111}〈112〉 and {111}〈110〉 component decreases,while the area fraction of {100}〈001〉 component doesn’t chang... 

本发明提供一种超低铝无取向硅钢夹杂物控制方法。该钢种化学成分质量百分比为C≤0.005％，Si：0.25％‑1.50％，Mn：0.15％‑0.55％，P：0.02％‑0.06％，S≤0.005％，Als≤0.005％，余量为Fe及不可避免的杂质。工艺流程为：KR→BOF→RH→连铸。转炉出钢严格控制下渣量，出钢结束加石灰、渣面脱氧剂调渣；RH脱碳结束后，先加低碳低硫硅铁、金属铝或铝钙铁合金复合脱氧，最后加入金属锰、磷铁进行合金化，然后净循环6‑10min，破空出钢运至连铸浇注。得到钢水中主要为SiO2‑Al2O3系夹杂，避免了生成低熔点SiO2‑MnO系夹杂，轧制延展变长，影响晶粒长大；同时也避免了生成高SiO2组分类酸性夹杂，导致耐材的侵蚀。可显著改善钢中非金属夹杂物类型，提高无取向硅钢的性能，并提高了钢水浇注性能。

介绍了硅钢CSP工程辊底式均热炉的技术特性,详细阐述了辊底式均热炉工艺特点。根据硅钢均热要求,通过采取不同烧嘴布置方法和燃烧控制技术,选用耐火纤维模块和绝热材料等相关技术措施,满足了出钢温度要求。 The technical specialty for roller hearth furnace of silicon steel CSP Plant was introduced,and the technology characteristics of the roller hearth furnace were illuminated in detail.According to the reheating require of the silicon steel,different burner arrangement and combustion control methods were applied,and technology measures such as selecting refractory fiber module and insulation material and so on were taken,the temperature requirement of silicon steel was met. 

1.本外观设计产品的名称：硅钢片。;2.本外观设计产品的用途：多片硅钢片用来共同组成马达的转子的其中一个部件。;3.本外观设计产品的设计要点：在于本外观设计产品的形状。;4.最能表明设计要点的图片或照片：立体图。;

通过热力学计算,分析了实验钢中主要析出物析出的可能性。结果表明:在液相和固液两相区中,AlN和MnS均不能析出;在奥氏体区,AlN和MnS具备热力学析出条件,平衡析出温度分别为1547、1582 K。成品退火板中的析出物主要为AlN和MnS。扫描电镜下观察到的AlN形貌多为长条状,MnS形貌多为棒状或近似球形。这两种析出物占了析出物总量的85%以上,尺寸集中分布在400~800nm;复合析出物主要是(Al2O3+MnS)和(AlN+MnS),形貌不规则,尺寸集中在0.7~1.5μm;透射电镜下观察到了少量100nm以下独立的AlN析出。 According to thermodynamic calculation, the precipitation probability of precipitates was analyzed, AlN and MnS can not precipitate in liquid phase area and solid-liquid two-phase area. In austenite area, both the AlN and MnS have precipitation condition in thermodynamics and precipitates at 1547 K and 1582 K, respectively. The precipitates in annealing plate are mainly AlN and MnS. The shape of AlN is mostly strip, and MnS is stick or near sphericity. They accounted for over 85% of the total qu... 

本发明公开了一种无取向硅钢用预熔型结晶器保护渣，涉及冶金技术领域，其化学成份按质量百分比计为：CaO：25.2%‑25.6%，SiO2：39.2%‑39.6%，MgO：1.9%‑2.1%，Al2O3：2.9%‑3.1%，Na2O+K2O：10.5%‑10.7%，F：9.9%‑10.1%，Li2O：1.9%‑2.1%，MnO：2.0%‑2.2%，C固：1.9‑2.1%，余量为不可避免的杂质，熔点：1000‑1040℃，粘度at1300℃：0.18‑0.19Pa.S，通过喷雾造粒制成中空颗粒。制备的无取向硅钢结晶器保护渣是空心颗粒，堆比重轻，空心颗粒提高了铺展性，喷雾造粒的空心球颗粒能形成绝热层，可有效地降低钢水向外传热速度，隔热保温效果好。

本发明提供在金属带钢表面以所希望的槽宽度形成线状槽进而磁特性极其优异的方向性电磁钢板。在金属带钢的至少单面形成抗蚀剂被膜，接着，对上述抗蚀剂被膜一边在横穿上述金属带钢的轧制方向的方向进行扫描一边照射激光，除去经上述激光照射的部分的上述抗蚀剂被膜，接着，对上述金属带钢的除去了上述抗蚀剂被膜的部分实施蚀刻处理而形成线状槽，上述抗蚀剂被膜以固体成分换算计含有20质量％以上的无机化合物，在上述金属带钢表面，上述激光具有长轴直径与短轴直径之比为5.0以上的椭圆状的射束形状，并且扫描正交方向的射束直径为10μm～100μm。

本发明涉及涂层液技术领域，且公开了取向硅钢绝缘涂层液，其配比为：二氧化硅10‑15%、硼酸5‑8%、磷酸二氢盐2‑5%、金属溶胶20‑25%、氢氧化铝占5‑6%、有机酸处理的复合盐溶液20‑30%、分散剂0.5‑1%，其余为水，采用硅溶胶作为辅助成膜物，粘结力较强，对附着性影响很大。硅溶胶能够很均匀地包裹在被胶结物质的表面，通过自干成膜，保持了很高的常温结合强度；而磷酸盐涂层的固化是通过受热分解，脱水聚合完成的，低温强度差，中温强度高，充分利用了硅溶胶低温的结合强度和磷酸盐中、高温时的结合性能，消除了常规涂层烘烤时容易出现的收缩、起泡现象，阻止了微气孔的形成，提高了涂层的表面光滑度，粘结强度和稳定性同时保持绝缘涂层的光泽、光滑和稳定性。

【作者】 罗海文； 向睿； ...

本实用新型公开了一种高磁感取向硅钢用钢带纠偏装置，包括支架，所述支架的顶部外壁通过螺栓固定连接有传送电机、安装柱和固定板，所述安装柱的顶部外壁通过螺栓固定连接有侧边板，所述侧边板的两边内壁均开有滑动槽，所述滑动槽的内壁通过螺钉固定连接有滑动轨道，所述滑动轨道的内壁滑动连接有滑动板，所述侧边板的一侧内壁设有推力弹簧，所述滑动板的底部外壁通过轴承连接有抵边轮。本实用新型对带钢产生更大的推力，使得带钢归位，推力弹簧的弹性使得装置对带钢的力比较缓和，不易使得带钢形变，顶压板和防抖轮会在带钢的顶部对带钢施加一个垂直向下的压力，使得带钢在运输过程中不易上下抖动。