硅钢资料

以质量分数为25%的丙烯酸乳液MC-102、15%Al(H2PO4)3溶液、0.01%H3BO3、0.01%Zn(Ac)2·2H2O和2%二乙二醇丁醚组分,在不同固化工艺下制备涂层。极化曲线和电导率测试发现300℃处理60 s得到的涂层具有良好的耐腐蚀性和绝缘性;水煮实验证明该涂层具有良好的耐水性;断口线扫描发现涂层具有良好的附着性。 A formula comprising MC-102 acrylic emulsion 25%,aluminium dihydrogen phosphate15%,boric acid 0. 01%,zinc acetate dihydrate 0. 01% and diethylene glycol monobutyl ether 2% was used to prepare coatings via different treatment process. The conductivity test and polarization curves revealed that a coating cured at 300 ℃ for 60 s showed good insulative and anticorrosive properties. The water boiling test indicated that the said coating had good water resistance. A cross section of the coating was in... 

本发明涉及一种超纯净无取向冷轧硅钢中非金属夹杂物形貌的原位观察方法，包括如下步骤：制备无取向冷轧硅钢样品，将待测试面用打磨至1000#，使样品表面平整光滑，并进行机械抛光和表面清洗。对处理好的样品在电化学工作站上进行电化学腐蚀，电解液为：1~8wt%氯化物MCl溶液，余量为去离子水，通入CO2气体至饱和，加入适量NaHCO3和三乙醇胺作为稳定剂调节pH值将其稳定在6.0~6.5之间。电化学设定参数：开路：0.5~2h，动电位极化测试：扫描速率:0.1mV/S~1.0mV/S，测试区间：VS.SCE‑0.8V~0.2V，测试温度为：10~25℃。取不同区间内做完电化学腐蚀的样品用去离子水冲洗，吹干。通过扫描电子显微镜+能谱仪对非金属夹杂物的形貌进行原位观察和成分分析。

采用Nb对Fe-6.5%Si(质量分数)高硅钢进行微合金化处理,结果表明:Nb在高硅钢薄板制备过程中细晶效果明显.铸态、锻态和热轧态组织的晶粒分别细化了17.50%,24.51%和30.13%.铸态样品压缩强度由1365 MPa提高至1520 MPa,延伸率提高77.78%;温轧板试样室温拉伸强度由573 MPa提高至621 MPa,延伸率提高44.44%.利用XRD对厚度为0.30—1.68 mm的温轧板的板面织构演变过程进行跟踪测量,结果发现:初始织构以(011)〈100〉Goss织构为主,单道次变形量为26.2%的情况下,Goss织构完全转化为(100)〈011〉旋转立方织构,随后,在单道次变形为22.6%的情况下,旋转立方织构完全转化为{111}面织构,即纤维织构,并稳定保持至0.30 mm. Fe-6.5%Si（mass fraction） alloy possess perfect magnetic properties,though intermetallics of Fe₁₄Si₂ phase brought 6.5%Si leads to room temperature brittleness and hinder this significant materials industrialization.Nb was adopted into micro-alloying of Fe-6.5%Si high silicon steel. OM,thermal simulated test machine and XRD were employed to study the influence of Nb on high silicon steel in processing stages.Textures of warm-rolled high silicon steel strips were determined b... 

本实用新型公开了一种具有自动接料机构的变压器硅钢加工用防刮伤剪床，包括支撑座，所述支撑座的上端固定连接有相互对称的进料机构与出料机构，所述进料机构上设置有调节机构，所述进料机构与出料机构之间设置有切割底座，所述切割底座的两端设置有气缸，所述气缸的内侧设置有切割机构，所述切割机构上设置有卡接机构，所述出料机构的一侧设置有接料机构；本实用新型涉及剪床技术领域。该具有自动接料机构的变压器硅钢加工用防刮伤剪床，切割后的硅钢，通过出料机构输送至承接板上，挡板与侧板能够使得硅钢能够自动叠放整齐，自动叠放整齐相对于人工接料可明显节省时间，提高剪床的运行效率，减少人力成本，提高运行的安全性。

借助OM、激光共聚焦显微镜、质谱仪和电解萃取等设备和方法，研究了添加微量稀土La（质量分数0.001 1%）的取向硅钢在轧制前采用不同加热保温时间对抑制剂固溶行为的影响。结果表明：当稀土取向硅钢在1 250℃分别保温10、20、30 min后，试验钢晶粒尺寸随保温时间延长有先快后慢的长大趋势；三种抑制剂元素Mn、Cu和Al均发生固溶，保温时间对Mn和Cu两种元素的固溶影响明显，固溶量分别由69.8%和43.7%增加至84.2%和85.2%；随着保温时间的延长，稀土取向硅钢中抑制剂的小尺寸未溶物逐渐减少直至消失，较大尺寸未溶物（300～600 nm）逐渐转变为小尺寸未溶物逐步溶入基体中，数量减少且未溶物的类型由复杂逐渐转变为单一。 In this paper the solid solution behavior of the inhibitor under various holding time in 0.001 1 %La oriented silicon steel during reheating had been investigated by using OM, LM, methods of electrolytic extraction and mass spectrometer. The results showed that grain size of the test steel increased significantly with the holding time prolonging when the rare earth oriented silicon steel was heated to1 250 ℃ and held for 10, 20 min and 30 min respectively, and the growth trend slowed down after ... 

运用电子背散射衍射(EBSD)技术,研究了50W600无取向硅钢在热轧→冷轧→退火工序间织构的演变。结果表明:由于热轧板沿板厚方向的应力场和温度场存在差异,导致热轧板不同层织构类型和强度存在差异;热轧板表层主要存在铜型、黄铜和高斯织构,1/4层织构主要为α纤维织构和较弱的高斯织构,中心层织构较单一,主要为α纤维织构;和热轧板相比,冷轧板各层织构差异较小,为典型的轧制织构(α纤维织构和γ纤维织构);退火板各层都表现为γ纤维织构增强、α纤维织构减弱,旋转立方织构基本消失。 The texture evolution of 50W600non-oriented silicon steel in hot rolling,cold rolling and annealing process was investigated by electron back-scatter diffraction(EBSD)technology.Results show that the hot rolled plate texture types and intensities along thickness direction were different because of the different stress fields and temperature fields.The major texture types in the surface of hot rolled plate were copper,brass and Gauss texture.The texture was composed ofαfibre texture and weaker Ga... 

本实用新型公开了一种适用于自动线的硅钢叠装系数性能检测装置，涉及实验仪器自动化技术领域，为解决机器人自动上样至叠装系数测量仪经常发生碰撞的问题；本实用新型包括框架、上压板、下压板、压紧驱动机构、高度探规和加载力值传感器，其中压紧驱动机构设置于框架上端，下压板固定于框架内的下端，上压板安装于下压板上方且与压紧驱动机构的输出端传动连接，加载力值传感器安装于上压板与压紧驱动机构的输出端之间，高度探规安装在上压板上，且探头向下伸出上压板下端面，框架为“C”字形一体式刚性结构，其设有上下两个水平板，以及位于一侧的竖直板；本实用新型能够避免机器人自动上样时碰撞到框架，以及下压时高度探规压到试样。

本发明公开一种高牌号无取向硅钢的轧制方法，用于控制森基米尔二十辊轧机对原料带钢进行轧制，所述方法包括：根据所述原料带钢的规格参数，确定所述森基米尔二十辊轧机的第一中间辊的辊型及第二中间辊的辊型；根据所述原料带钢的合金含量及所述规格参数，确定所述第一中间辊的有效平面量；根据所述规格参数，确定所述森基米尔二十辊轧机的径向调整机构的凸度值；根据所述合金含量，设定所述森基米尔二十辊轧机进行轧制时的负荷分配和张力；按照所设定的负荷分配和张力分配对所述原料带钢进行轧制，且在轧制过程中以预设乳化液流量进行喷淋，以制得成品。本发明可减少高牌号无取向硅钢在轧制过程中发生脆性断裂，提高轧制的稳定性及生产效率。

本发明公开一种硅钢片叠片装置，涉及硅钢片叠加领域，包括：上料机构，其包括第一定位装置，第一定位装置包括多个第一轴向定位柱，第一轴向定位柱与周向开孔一一对应，多个第一轴向定位柱分别穿过不同位置的周向开孔；精定位机构，其周向定位硅钢片；下料机构，其包括第二定位装置，第二定位装置包括用于与硅钢片的中心孔相配合的中心定位柱；用于将设置于第一轴向定位柱上的硅钢片移动至精定位机构的移载机构；摄像装置；机器臂，摄像装置与机器臂通信连接，机器臂根据摄像装置拍的键槽方口特征调整硅钢片的角度、并将硅钢片移动至中心定位柱。该硅钢片叠片装置能够有效降低人工劳动强度，并提高叠放效率。

一种分步调控制备高磁感高强度无取向电工钢的方法，按以下步骤进行：(1)按设定成分采用转炉冶炼钢水，制成连铸坯，含C0.001～0.008％，Si1.5～4.8％，Cu0.5～2％，Ni0.5～1.5％，Al0.2～1％，Mn0.2～1.5％，P＆lt;0.005％，S＆lt;0.005％，其余为Fe；(2)将连铸坯置于均热炉保温，多道次热轧相邻两道次间隔时间为30～180s；空冷；(3)常化处理；(4)多道次冷轧；(5)退火处理；(6)时效处理。本发明的方法成本较低、工艺简单，生产的无取向电工钢兼具优异的力、磁性能，能够很好的满足驱动/牵引电机的使用需求。

本实用新型公开了硅钢片卷材加工用张力机构以及硅钢片剪切机，包括安装架、转动装置和按压装置，安装架的上安装块、连接块和下安装块组成凹槽，转动装置包括下转轴和转动驱动单元，下转轴水平设置，可转动地安装于下安装块上，设置于凹槽中，按压装置包括有上转轴和按压驱动单元，上转轴水平设置于下转轴的上方，可转动地安装于上安装块上，设置于凹槽中，并且可沿上安装块上下运动，其中，上转轴可与下转轴抵接。根据本实用新型的硅钢片卷材加工用张力机构以及硅钢片剪切机，可加强硅钢片卷材输送过程中的张力，降低硅钢片卷材输送的位置偏差率，提高产品合格率，提高原材料利用率，从而提高生产效率。

本发明涉及一种电机定子硅钢片激光焊接装置，其包括底座；工作台，其安装于所述底座；下压旋转组件，其包括：焊接支座，其安装于所述底座上；用于压紧定子硅钢片的下压组件，所述下压组件位于所述工作台的上方，且可沿垂直于所述工作台的板面的方向移动；用于驱动所述定子硅钢片旋转的旋转组件，其安装于所述下压组件靠近所述工作台的一端，所述旋转组件可绕所述下压组件的轴线旋转；以及激光焊接头组件，其固定于所述底座。通过在焊接工作台上设置下压旋转组件，下压组件可以驱动下压使定子硅钢片压紧，旋转组件可以驱动定子硅钢片旋转，进行下一道焊缝焊接，直到该定子硅钢片所有焊缝焊接完成，使用方便，省时省力。