硅钢资料

试验研究了球刻痕法对高磁感取向硅钢的铁损、矫顽力、相对磁导率、巴克豪森噪声等磁学性能的影响.研究结果表明:经过球刻痕处理后,高磁感取向硅钢的铁损明显降低,矫顽力下降,8 mm球刻痕过后铁损值与矫顽力分别下降16.2%和14.7%,且铁损和矫顽力均随刻痕间距降低而减少.刻痕后的高磁感取向硅钢磁导率在高磁感应强度下明显上升,刻痕后巴克豪森噪声值明显降低,经过对比分析确定8 mm为球刻痕的最佳刻痕间距.从磁畴观察、细化磁畴的原理等方面解释了细化磁畴对高磁感取向硅钢性能的影响原因. The effects of the ball scribing on magnetic properties of high permeability grain-oriented silicon steels,including the iron loss,coercive force,relative permeability,and Barkhausen noise were investigated. The results showed that the iron loss and coercive force of the high permeability grain-oriented silicon steels apparently decreased 16. 2% and 14. 7% respectively after 8 mm ball scribing and they both decreased with the decrease of the scribing spacing at the same magnetic flux density. At... 

本发明公开了一种无瓦楞状缺陷的高磁感低铁损无取向电工钢板，其各化学元素质量百分含量为：0＜C≤0.0035％、Si：1.2～2.8％、Mn：0.2～1.0％、P：0.04～0.15％、Sn+Sb：0.02～0.2％，余量为Fe和其他不可避免的杂质。此外，本发明还公开了上述高磁感低铁损无取向电工钢板的制造方法，其包括步骤：(1)冶炼和连铸，其中在该步骤不采用电磁搅拌；(2)热轧，其包括：粗轧、精轧、卷取和均热；其中在粗轧步骤采用2～6道次进行轧制，且粗轧单道次压下率控制在20％～40％之间；(3)上述热轧步骤后不进行常化步骤而直接进行冷轧；(4)连续退火。本发明所述的无瓦楞状缺陷的高磁感低铁损无取向电工钢板在保证较低生产成本的同时，还具有高磁感和低铁损的特性。

针对马钢无取向电工钢孔洞缺陷的分布规律及形貌特征,对缺陷样进行了显微分析,并利用生产实绩数据分析了该缺陷产生的原因。结合热轧生产过程,主要通过避免带钢撞击导卫以及降低导卫结瘤的产生等措施,可有效抑制热卷异物压入产生,从而降低冷轧工序孔洞的产生。 In viewing of the distribution and morphology characteristics of the hole defect of non-oriented electrical steel in Maanshan Iron and Steel Co.,Ltd.,the causes of the defect were analyzed by micro analysis of the defect sample and the production data.Combined with the production process of hot rolling,by avoiding the impact of strip steel on the guide and reducing the nodule formation on the guide,the pressing of foreign bodies in hot coiling could be effectively suppressed,thus reducing the fo... 

本实用新型涉及硅钢生产设备技术领域，具体公开了一种硅钢清洗用张力刷辊结构，包括中空的辊筒，辊筒两端固定有连接盘，连接盘上固定有转轴，辊筒的表面开设有若干排水槽，若干排水槽沿辊筒的周向等间距分布，辊筒的中部设有积水环槽，积水环槽内开设有连通辊筒内壁的进水孔，排水槽为倾斜设置，且排水槽的低端与积水环槽连通，连接盘上开设有排水孔。本专利中对硅钢带进行张紧时，完成清洗的硅钢带表面的水会沿着排水槽进入积水环槽，并从积水环槽进入到辊筒的内部，后排走，这样防止钢带上的水滞留在辊筒的表面，使得辊筒与钢带之间出现打滑的情况；另外多个排水槽的设置，还能够提高钢带与辊筒之间的贴附性，防止出现打滑的问题产生。

本发明揭示了一种高硅无取向电工钢及其生产方法。该方法包括：1）钢水冶炼并连铸成坯；2）加热并保温，之后热轧得到热轧卷板，其中粗轧出口温度940±20℃，精轧终轧温度840±20℃，卷取温度650±20℃；3）常化，常化温度((732~742)+3000[Si])℃，常化时长4min~5min；4）常化后直接进行冷轧，而后连续退火和涂层，退火温度940℃~990℃且退火时长1.5min~3min；5）涂层处理后的钢板加工成型，而后进行去应力退火，退火温度为((761~766)+3000[Si])℃。如此，在保证磁性能的同时，解决了冷轧难度大的问题。

本发明涉及一种消除硅钢边部翘皮的方法及硅钢，包括预处理板坯；加热预处理后的板坯，并控制所述板坯在加热炉的预热段时间不低于40分钟；粗轧板坯，并调整所述板坯侧压的减宽量为成品硅钢宽度的0.8％～1.2％；以及控制侧压立辊的凸缘与所述板坯的边部之间保留间隙。本发明所述的消除硅钢边部翘皮的方法及硅钢，能够显著消除硅钢的边部翘皮，以及在不能完全消除边部翘皮缺陷的情况下，约束翘皮位置发生在距离边部＜8mm区域，工艺调整简单易操作，不需要调整现有设备和系统架构，显著提升硅钢表面质量。

为研究退火工艺对普通取向硅钢初次再结晶组织的影响,对经不同温度、保温时间和升温速率退火后的材料组织进行了分析。结果表明:在等温退火条件下,加热至600℃时开始发生初次再结晶,800℃以上初次再结晶组织发展完善;而在最终冷轧板直接进行最终高温退火的情况下,加热温度在500～700℃时,将升温速率提高到80℃/h,初次再结晶组织更易于发展完善。 To investigate the influence of annealing process on the recrystallization of common grain oriented silicon steel,microstructures of sheets annealed at different temperature,soaking time and heating rate are observed.Results show that under the condition of isothermal annealing,recrystallization begins at 600℃ and fully develops above 800℃,while in the case that the final cold rolled sheets are directly thrown to final high temperature annealing,recrystallization is likely to develop with the he... 

通过热力学计算,分析了实验钢中主要析出物析出的可能性。结果表明:在液相和固液两相区中,AlN和MnS均不能析出;在奥氏体区,AlN和MnS具备热力学析出条件,平衡析出温度分别为1547、1582 K。成品退火板中的析出物主要为AlN和MnS。扫描电镜下观察到的AlN形貌多为长条状,MnS形貌多为棒状或近似球形。这两种析出物占了析出物总量的85%以上,尺寸集中分布在400~800nm;复合析出物主要是(Al2O3+MnS)和(AlN+MnS),形貌不规则,尺寸集中在0.7~1.5μm;透射电镜下观察到了少量100nm以下独立的AlN析出。 According to thermodynamic calculation, the precipitation probability of precipitates was analyzed, AlN and MnS can not precipitate in liquid phase area and solid-liquid two-phase area. In austenite area, both the AlN and MnS have precipitation condition in thermodynamics and precipitates at 1547 K and 1582 K, respectively. The precipitates in annealing plate are mainly AlN and MnS. The shape of AlN is mostly strip, and MnS is stick or near sphericity. They accounted for over 85% of the total qu... 

本实用新型公开了一种新型嵌线结构的硅钢片组件，包括硅钢片组和骨架，硅钢片组由若干相同形状的硅钢片堆叠而成，硅钢片为倒U型的薄片体，骨架由一限位框架和两固定杆组成，限位框架由一矩形框架和位于矩形框架四角的限位凸块组成，硅钢片组卡设在矩形框架上，限位凸块对硅钢片组进行限位，两固定杆平行设置在硅钢片组的上方，且固定杆的两末端分别与限位凸块相固定。本实用新型具有装配简单、不易变形的优点。

一种薄规格中高牌号无取向硅钢酸轧生产工艺，属于无取向硅钢冷轧成型技术领域，该生产工艺在焊接前对焊缝预加热和焊接后对焊缝两次后加热，采用五机架六辊冷连轧机组轧制，其压下率分别为35％‑45％、35％‑45％，30％‑36％，25％‑30％，1％‑10％，第一二冷轧机间、第二三冷轧机间、第三四冷轧机间、第四五冷轧机间的单位张力分别为120‑130KN/mm2、130‑140KN/mm2、150‑160KN/mm2和160‑180KN/mm2，本发明的有益效果是，本发明通过对冷连轧的工艺进行改进优化，提高了薄规格中高牌号无取向硅钢带的轧制效率，提高了同板差的合格率，降低了轧制的断带率和轧烂率。

利用FE-SEM、EDS分析了含不同抑制剂成分的成品取向硅钢中夹杂物的组成和形貌,统计其尺寸及数量分布;结合对磁性能测试的结果,分析了Sn、Cu、Nb和Cr对取向硅钢磁性能影响的机理。结果表明:含Sn的取向硅钢试样中夹杂物主要为块状的微米级Al-Ti-C-N-O复合物,还有少量的球形Al-N-O颗粒和块状Ti-C-N-O颗粒,棒状夹杂物较少;含Cr的取向硅钢试样中夹杂物主要为球形的微米级Al2O3,还有少量Cu-Al-N-O-S复合物,棒状夹杂物和不规则夹杂物均较少;含Cr试样中1~3μm夹杂物的平均尺寸较含Sn试样小,但数量多,而大于3μm夹杂物的平均尺寸较含Sn试样大,但数量很少。磁性能测试结果表明,外场为800A/m和2500A/m时,含Cr试样磁感应强度偏低,铁损值P1.7/50较含Sn试样高,为1.171W/kg。 The composition and morphology of inclusions in the finished grain-oriented silicon steels are analyzed by using FE-SEM and EDS, and the number density and size distribution of the inclusions are counted. The influence mechanism of Sn, Cu, Nb, and Cr on the magnetic properties of the steel is also discussed. Results show that the inclusions composition in the grain-oriented silicon steel samples containing Sn is mainly block Al-Ti-C-N-O, compounding with a few spherical Al-N-O and block Ti-C-N-O... 

本发明公开一种硅钢片叠片装置，涉及硅钢片叠加领域，包括：上料机构，其包括第一定位装置，第一定位装置包括多个第一轴向定位柱，第一轴向定位柱与周向开孔一一对应，多个第一轴向定位柱分别穿过不同位置的周向开孔；精定位机构，其周向定位硅钢片；下料机构，其包括第二定位装置，第二定位装置包括用于与硅钢片的中心孔相配合的中心定位柱；用于将设置于第一轴向定位柱上的硅钢片移动至精定位机构的移载机构；摄像装置；机器臂，摄像装置与机器臂通信连接，机器臂根据摄像装置拍的键槽方口特征调整硅钢片的角度、并将硅钢片移动至中心定位柱。该硅钢片叠片装置能够有效降低人工劳动强度，并提高叠放效率。