根据本发明的一个实施例的取向电工钢板的制造方法，其包含：对板坯进行热轧，以制造热轧钢板的步骤；对热轧钢板进行热轧板退火的步骤；对热轧板退火后的热轧钢板进行一次冷轧的步骤；对一次冷轧后的钢板进行一次脱碳退火的步骤；对完成脱碳退火的钢板进行二次冷轧的步骤；对完成二次冷轧的钢板进行二次脱碳退火的步骤；以及对二次脱碳退火后的钢板进行连续退火的步骤。

对西昌钢钒炼钢厂200 t BOF(顶底复吹)-RH-CC工艺生产50PRW800无取向硅钢RH精炼过程中主要成份进行了分析。找出了目前工艺中影响钢液质量的主要因素是钢水脱氧处理不彻底,造成加入的部分硅元素烧损。操作工艺改为铝的脱氧即合金化操作一步完成,保证了钢水中氧处于一个较低的范围,从而减少对硅元素的烧损,提高合金收得率。 The factors of BOF-RH-CC process affecting the compositions of liquid steel were systematically investigated and studied of Xichang Steel and Vanadium Company. The main factors affecting the steel cleanliness were picked out. All results showed that the loss of silicon elements resulting from the deoxidization of liquid steel was not completely. It was suggested that the addition of aluminum for deoxidizing and alloying of molten steel was executed as one step in order to lower the oxygen potent... 

本实用新型涉及一种硅钢片图像采集装置，在固定支架上设置有工业相机，所述的工业相机可以沿垂直方向上下移动或者沿水平方向前后移动，通过上下移动或者前后移动对硅钢片的形状和尺寸、硅钢片叠积形成的铁芯进行实时图像采集。固定支架包括：固定底座、支撑杆和工作台面，一对固定底座平行对称设置，所述的固定底座上对称设置两条竖直支撑杆，竖直支撑杆的上端面固定连接工作台面，在两条竖直支撑杆的中间位置设置升降丝杆，水平支撑杆的两端分别与升降丝杆的升降螺母固定连接，相机滑台活动设置在水平支撑杆上。本实用新型通过工业相机的上下前后移动，实现了硅钢片形状尺寸和硅钢片高度即时拍照测量，较人工测量提高了测量精度及准确性。

研究了硅钢铸坯再加热过程中夹杂物的析出行为。采用非水溶液电解提取+扫描电镜观察方法,观察了试样的显微组织,统计了夹杂物的尺寸、种类、数量、分布。结果表明,均热温度为1 523 K时,水淬试样的夹杂物尺寸绝大部分小于0.5μm,0.5～5.0μm的夹杂物数量很少,没有发现5.0μm以上的夹杂物。此外,均热时间为10、30、60、90、120、240 min时,对应试样中0.05～0.2μm的夹杂物数量分别为4.04×104、4.73×104、3.70×104、3.33×104、3.10×104、1.56×104个/mm3。绝大部分夹杂物以MnS、AlN、CuxS类为主,并以三类夹杂物中的两类复合或三类复合居多。三类复合夹杂物总量占每组试样夹杂物总量的90%或以上。随均热时间延长,典型的夹杂物组成会发生如下变化:MnS+AlN+CuxS MnS+AlN AlN。与此同时,MnS、AlN、CuxS三者复合比例从45.2%(均热10 min)降为9.7%(均热240 min)。 The methods of electrolysis extraction from nonaqueous solution and scanning electron microscope were adopted to study the precipitation behavior of non-metallic inclusions in Si steel slabs during reheating processes.The morphologies,chemical compositions,quantity and size distribution of non-metallic inclusions in these steel samples were analyzed.Results show that,when the soaking temperature is 1 523 K,almost all of the non-metallic inclusions are smaller than 0.5 μm,few are in the range of ... 

对欧盟市场汽车压缩机专用产品进行技术解析,对比分析了其电磁性能、退火和发蓝处理、物理性能、化学成分、应用特点等参数。探讨国内外电工钢产品应用方式的不同特点,并结合鞍钢自身工艺装备和炼钢、热轧、冷轧工艺参数介绍了其生产可行性。提供了冶金工艺流程下,后工序电工钢专业生产线及传统冷轧系统生产线两种生产方式,均能满足用户最终使用要求。 The technology of automotive compressor accommodation manufacture of European Economic and Monetary Union market was described.The magnetic properties,annealing bluing,physical properties,chemical composition,application parameters were analysed.The different characteristics of the application of electrical steel products,the feasibility of manufacture on the existing technology and equipment,steelmaking,hot rolled,cold rolled technical parameters were discussed.The professional product line of ... 

根据本发明的一个实施例的双取向电工钢板，以重量％计，所述钢板包含Si：2.0至4.0％、Al：0.01至0.04％、S：0.0004至0.02％、Mn：0.05至0.3％、N：0.01％以下且0％除外、C：0.005％以下且0％除外、P：0.005至0.15％、Ti：0.001至0.005％、Ca：0.0001至0.005％和Mg：0.0001至0.005％，余量包含Fe和其他不可避免的杂质，具有从{100}＆lt;001＆gt;起15°以内的取向的晶粒的面积分数为60至99％，具有从{100}＆lt;025＆gt;起15°以内的取向的晶粒的面积分数为1至30％。

以太钢热连轧厂的硅钢为研究对象,利用凸度仪测量热轧带钢出口凸度值,采用矩阵和失效模式的分析方法了解影响带钢凸度变化的主次因素。研究结果表明:通过有效控制轧制过程中的加热温度、时间及采用合理的辊型,硅钢凸度精度提高了4.34%左右。 In this paper,we take the hot-rolled silicon steelsheet of Taigang as the research symbol,exit profile was measured by convex instrument,the primary and secondary factors that affect the strip profile were measured by using matrix and failure mode analysis methed.The results indicate that convexity accuracy has significantly improved by nearly 4.34% through the effective control of the heating temperature,heating time and the use of correct roller type in the process of hot rolling. 

本发明公开了一种拉矫机矫直低牌号无取向硅钢的方法，当焊缝达到拉矫机前面时，生产线的整体速度降低至28‑32m/min、拉矫机的辊系辊缝全部打开同时辊系不接触钢带、拉矫机的延伸率降到0.08％‑0.12％、拉矫机前后张力辊的压辊全部压下，焊缝通过拉矫机后，均恢复到正常水平。本发明的目的是提供一种拉矫机矫直低牌号无取向硅钢的方法，解决焊缝经过拉矫机时焊缝在拉矫机的拉伸矫直作用下发生断带的事故的问题。

本发明公开了一种取向硅钢产品的在线性能判级与精确分切装置和方法，使得同一个分卷上的性能分布均匀，避免分卷出现性能废品或多个性能等级的情况，提高分卷性能稳定性。提供的一种取向硅钢产品的在线性能判级与精准分切方法包括生产数据采集、铁损曲线自学习、数据存储、性能在线判级、缺陷数据采集、缺陷判级、智能分切等模块，依据修正后的磁性能全长数据，得到产品的性能判级结果，结合表面缺陷判级结果，综合确定分切位置，制定最佳分切方案。本发明可以实现取向硅钢生产过程中的性能在线判级和精准分切，得到性能均匀、表面质量好的分卷，减少分卷性能不稳定带来的损失。

本发明公开了一种新能源汽车驱动电机用35WD1600电工钢及其生产方法。属于新能源汽车驱动电机电工钢生产技术领域，主要解决的是现有技术新能源驱动电机电工钢性能较差的技术问题，包括以下化学元素成分及重量百分比：C≤0.005％，Si为2.5～2.8％，Mn为0.2～0.4％，P为0.08～0.12％，S≤0.008％，Cu为0.20～0.30％，Ni为0.16～0.25％，Al为0.3～0.5％，其余为Fe及不可避免的杂质。生产方法包括以下步骤：(1)铁水预处理；(2)转炉冶炼；(3)RH精炼；(4)连铸连轧；(5)酸洗；(6)第一次冷轧脱碳退火；(7)第二次冷轧脱碳退火；(8)涂层；(9)烧结卷取。本发明的新能源汽车驱动电机用35WD1600电工钢，性能达到新能源汽车驱动电机用冷轧无取向电工钢带国家标准及客户性的要求，焊接性能、板形、冲片性能良好。

本实用新型公开了一种铁芯硅钢片卷料的上料装置，包括升降机构、固定座、转动执行机构和转动平台，所述固定座固定设置在地面上，所述升降机构相邻设置在固定座的一侧，所述固定座对立于升降机构的一侧设置有转动平台，所述转动平台的一端铰接设置在固定座上，且所述转动平台的另一端为自由端，所述转动平台在竖向面内朝向或远离于升降机构偏转，所述固定座上设置有转动执行机构，所述转动执行机构驱动转动平台转动；所述转动平台上的物料通过转动可位移至固定座和升降机构上，能够安全的、快速的将卷料转移至升降机构上，从而便于上料。

本发明公开了一种低碳低硅钢铝质复合脱氧剂及其制备和使用方法，属于钢铁冶金技术领域。本发明为改善低碳低硅钢种可浇性差、夹杂降级率高的问题，提供了一种低碳低硅钢铝质复合脱氧剂，其包括：金属铝：50～60％；7Al2O3·12CaO预熔渣：10～20％，钝化CaO：10％～20％，Fe：10～20％，其余为微量杂质元素。本发明通过深入研究铝脱氧后钢中夹杂物的行为，提供了一种低碳低硅钢铝质复合脱氧剂，通过在转炉出钢过程加入该脱氧剂，能够有效降低钢中大型夹杂比例、对夹杂物改性，在不延长精炼时间的情况下降低夹杂物总量，改善目前此类钢种生产过程中存在的可浇性差，夹杂降级率高的问题。