硅钢资料

【摘要】 <正>3月15日,随着第5754卷HiB钢下线,武钢...

研究了常化对CSP流程生产的wSi=1.6%的无取向电工钢组织、织构和成品磁性能的影响。结果表明,经CSP流程生产,且在相同的冷轧及退火制度下,经1 000℃×2min常化处理的wSi=1.6%的无取向电工钢热轧板,其最终退火成品的铁损P15/50比不常化试样下降了10.5%,磁感B50比不常化试样提高了2.5%;常化使wSi=1.6%的无取向电工钢成品的平均晶粒尺寸增大,成品铁损P15/50相应减小;同时,常化使wSi=1.6%的无取向电工钢成品中高斯织构的强度增加,γ纤维织构的强度减弱,这有利于成品磁感B50的提高。 The effect of normalizing on microstructure,texture and magnetic properties of non-oriented electrical steel with wSi=1.6% produced by CSP process was investigated.The results show that,under the same cold rolling and annealing system,the iron loss(P15/50) of annealed samples whose hot bands has been normalized by 1 000 ℃×2 min process decreases by 10.5% and magnetic induction(B50) increases by 2.5% compared with the samples whose hot bands was not normalized.The average grain size of non-orient... 

采用电解法和扫描电镜研究了300 t转炉-RH精炼钙处理对无取向硅钢板（%:≤0.005C、1.2～2.2Si、0.2～0.6Mn、≤0.20P、≤0.005S、0.2～0.6Al、0～0.01Ca）中夹杂物的影响。结果表明,钢中Al含量为0.25%和0.35%时,钢中溶解氧均小于1×10^-4%,钙处理后都会产生CaS夹杂物,尤其是含0.35%Al的钢水;钙处理可以有效减少钢中的夹杂物数量,尤其是0.5μm以下的微细夹杂物数量;钙处理后夹杂物的种类以AlN、CaS为主,同时还含有少量的氧化物夹杂物以及AlN-CaS复合夹杂物,尺寸主要为1.5～5.0μm。 The effect of 300 t converter-RH refining calcium treatment on inclusions in non-oriented silicon steel sheet （%:≤0.005C,1.2～2.2Si,0.2～0.6Mn,≤0.20P,≤0.005S,0.2～0.6A1,0～0.01Ca） has been studied by electrolysis and scanning electron microscope.Results show that with 0.25%and 0.35%Al content in steel,all the dissolved oxygen in liquid is less than 1×10^-4%,and the CaS inclusions are produced after calcium treatment,especial for the liquid containing 0.35%Al;the amount of inclusions in ste... 

本实用新型属于硅钢技术领域，具体的说是一种硅钢前处理高液回流装置，包括机体；所述机体的侧端固接有一号导管；所述一号导管上安装有二号导管；所述机体的顶端固接有连接管；所述连接管上安装有入泡管；所述二号导管的内侧壁固接有电机；所述电机的输出端固接有扇叶；所述二号导管的顶端内侧壁固接有定位板；所述定位板的侧端转动连接有旋转叶轮；所述二号导管的底端固接有排泡管；通过一号导管和二号导管的配合可以把溢出的泡沫进行导向，通过扇叶和旋转叶轮的配合可以使泡沫快速流动，再通过排泡管排出进入机体的内部，可以使泡沫循环使用，避免泡沫的溢流造成环境的污染及碱液的浪费。

研究了退火温度和退火时间对电沉积硅钢试样中的断面层组织、硅在试样中的分布情况、织构分布和磁性能的影响。结果表明:退火温度为1000℃、退火时间为210 min时得到的试样晶粒分布均匀、硅在试样中分布均匀、硅平均浓度为6.3715%(接近6.5%)。试样的织构分析及磁性能检测的结果表明,在较高温度下延长退火时间可增加{100}和{110}面织构,降低铁损,所得试样的磁性能较为良好。 The effect of annealing temperature and time on the microstructure, distribution of silicon,texture and magnetism of the high silicon steel prepared by electrodeposition was investigated. The results showed that after annealing at 1000℃ for 210 min, the mean grain size of steel was about 190 μm with a uniform grain size distribution, and the silicon is also uniformly distributed on the entire cross section with an average Si concentration 6.3715%(close to 6.5%); With the increasing annealing tim... 

概述了高磁感取向硅钢生产工艺的研究现状及发展趋势。介绍了国内外薄板坯连铸连轧流程生产高磁感取向硅钢的研究现状。从流程工序特点、热履历、组织与抑制剂控制方面进行对比,分析了薄板坯连铸连轧流程相对传统板坯流程生产高磁感取向硅钢的技术优势,在此基础上提出了利用该流程生产高磁感取向硅钢需要解决的主要技术难点。 The current status and development trend of production process for high magnetic induction grain-oriented silicon steel are summarized.The research status of producing high magnetic induction grain-oriented silicon steel by thin slab casting and rolling process at home and abroad is introduced.The potential technical advantages of producing high magnetic induction grain-oriented silicon steel by thin slab casting and rolling process are obtained by analyzing in terms of process characteristics,t... 

【作者】 朱一知； 高军军； ...

本发明一种焊接压力容器用碳锰硅钢钢板及其生产方法，钢板化学成分及其重量百分含量为：C：0.18‑0.26%，Si：0.18‑0.65%，Mn：0.92‑1.72%，P≤0.008%，S≤0.002%，Cu：0.30‑0.40%，Ni：0.25‑0.35%，Cr：0.25‑0.35%，Mo≤0.10%，V≤0.10%，B：0.003‑0.005%，余量为Fe及不可避免的杂质元素。本发明钢板中加入的贵合金元素含量相对较少，冶炼成本及后续的生产成本控制较低，市场潜力和竞争力很大。

本发明公开了一种基于硅钢服役特性的立体卷铁心单框损耗测量方法及系统，根据硅钢片在立体卷铁心中的服役特性，获得测量铁心单框所需的非正弦励磁电压波形，通过所述立体卷铁心的心柱绕组电压和单框绕组电压之间的关系，确定所述被测立体卷铁心单框所需的电压有效值，再通过计算机、数据采集卡D/A转换器、功率放大器、隔离变压器和示波器，直接在所述立体卷铁心单框上加载励磁电压，利用功率表测量立体卷铁心单框损耗。本发明利用硅钢的服役特性，获得测量立体卷铁心单框所需的非正弦励磁电压波形和电压有效值，再将励磁电压直接加载到被测立体卷铁心单框，测量立体卷单框铁心损耗。

一种通过粉末烧结制备高磁性能含磷硅钢薄片的方法，属于粉末冶金技术领域。本发明通过真空熔炼气雾化制备成分范围为Fe‑(3‑6.5)wt.％Si‑(0.05‑1)wt.％P的合金粉，将其放置在陶瓷坩埚中均匀振实并放置重物压住，随后进行高温烧结使其冶金结合，再经热轧、冷轧、退火等处理后，得到具有优异性能的含磷硅钢薄片。本发明在硅钢材料体系中加入P元素，能够有效降低铁损、优化磁性能并促进活化烧结；采用气雾化粉末能够很好地保证产品的少夹杂和纯净度；在低熔点P元素及粉末压烧的协同作用下解决了球形气雾化粉末难以成形的缺陷，并避免了需添加成形剂导致的工艺复杂性及后续的脱胶残碳问题，有效缩短制备工艺流程，具有操作简单、生产效率高、工艺流程短、性能优异等优点。

【摘要】 <正>由西电集团、保定天威集团使用迁钢公...

本实用新型涉及一种硅钢片叠压精准定位设备，包括压台、压板和仿形燕尾键，所述压台上开有与仿形燕尾键下端相对的限位槽，所述压板设置与压台上方，所述压板上开有与仿形燕尾键上端相对的限位孔。本技术方案当硅钢片叠放压合之后，仿形燕尾键可以去除，并能够在硅钢片组成的铁芯上形成燕尾槽，用于后期燕尾键的组装，且能够保证燕尾槽内的结构规则，便于后期燕尾键组装。