研究的两种取向硅钢（%:No1-0.042C、3.16Si、0.009Al、0.07Mn、0.50Cu、0.015S、0.0084N和No2-0.040C、3.20Si、0.014Al、0.22Mn、0.49Cu、0.016S、0.008 2N）由50 kg真空感应炉冶炼,锻成（mm）350×120×35板坯,经1 250℃30 min加热,开轧温度1 100℃,5道次热轧成2.3 mm板,终轧温度950～1 000℃。实验结果表明,两热轧板沿板厚方向存在组织和织构的不均匀性,热轧板次表层为再结晶组织,有较强的Goss织构组分;中心层为形变组织,具有典型的形变织构。含0.22%Mn的No2钢次表层{110}〈001〉织构组分比含0.07%Mn的No1钢弱,中心层{001}〈110〉织构组分大大强于0.07%Mn No1钢,导致两者磁性能差异,0.22%Mn No2钢磁感应强度(B₈₀₀)和铁损(P_1.7/50)分别为1.87 T和1.24 W/kg,0.07%Mn No1钢分别为1.88 T和1.18 W/kg。 Studied both grain-oriented silicon steels（%:No1- 0.042C,3.16Si,0.009Al,0.07Mn,0.50Cu, 0.015S,0.0084N and No2-0.040C,3.20Si,0.014Al,0.22Mn,0.49Cu,0.016S,0.0082N） are melted by a 50 kg vacuum induction furnace,forged to（mm） 350×120×35 slab,heated at 1 250℃for 30 min,with beginning rolling temperature 1 100℃hot-rolled to 2.3 mm plate by 5 passes,finishing-rolled at 950～1000℃.Test results show that the structure and texture along thickness of both hot-rolled plates are inhomogeneous:the subsurface ... 

根据本发明的一个实施例的取向电工钢板用退火隔离剂组合物，其包含复合金属氧化物，复合金属氧化物包含Mg和金属M，金属M是Be、Ca、Ba、Sr、Sn、Mn、Fe、Co、Ni、Cu和Zn中的一种以上。

本实用新型公开了一种变压器铁芯硅钢片叠装对齐工装，包括叠装平台、定位板、推齐板和下压板；定位板和推齐板分别位于叠装平台的两侧，下压板位于叠装平台的上方；定位板用于对铁芯长度或宽度侧进行定位；推齐板平推铁芯使各硅钢片抵靠定位板而对齐；下压板下压铁芯使各硅钢片叠装紧密。本实用新型提供的一种变压器铁芯硅钢片叠装对齐工装，能够提高铁芯生产精度，并提高硅钢片叠装效率。

本实用新型涉及一种具有在线测量功能的电工钢片横剪线，包括床身，床身上沿其长度方向安装有导轨，电工钢片在外部驱动辊带动下以导轨为导向移动；位于导轨一端端头外部的床身上安装有测量辊组件，位于导轨另一端处的床身上安装有影像测量组件；测量辊组件、导轨和影像测量组件的中心位于同一直线上，影像测量组件横跨设置于导轨上方；位于测量辊组件和影像测量组件之间的床身上依次安装有冲孔组件、V冲组件和斜剪组件；本实用新型通过测量辊组件对电工钢片行进长度进行检测，通过影像测量组件对电工钢片成型尺寸进行检测，从而便利于及时调整横剪线整体的运行状态，有效助力于保证合格率，并降低了人工负担。

本实用新型公开了一种包容产品转子硅钢片叠加公差的模具机构，包括上下设置的定模固定板和动模固定板，定模固定板下面设置有定模仁，定模仁内穿设有定模型芯，定模型芯的上端设置有定模型芯限位块，定模型芯限位块套设在导向销下端，导向销上套设有定模型芯浮动弹簧B，定模型芯底部设置有台阶面，定模型芯上套设有定模型芯浮动弹簧A，定模仁外圈设置有定模浮动型芯，定模浮动型芯与动模固定板之间设置有动模浮动板，动模固定板中心设置有动模仁，动模仁上套设有产品转子，产品转子上端与定模型芯下端接触。本实用新型提供的一种包容产品转子硅钢片叠加公差的模具机构，能够省去高度调整工序，降低成本和品质管控风险。

本实用新型公开了一种硅钢炉底辊套管生产用原料破碎装置，包括外壳和固定圆板，所述外壳的端面设置有密封盖和两组电机，两组所述电机的输出端均贯穿外壳的端面，两组所述电机的输出端均卡接安装有破碎辊，所述外壳的内部转动安装有循环滤网管，两组所述破碎辊的下方安装有提示收集箱，所述外壳的下部固定贯穿安装有出料管，且出料管的侧壁安装有电磁阀，所述密封盖的端面固定贯穿安装有四组进料管，且四组所述进料管的外置端端部均固定安装有安装法兰。有益效果：本实用新型采用了循环滤网管，通过设置的循环滤网管，能够对不合格的原料颗粒进行多次破碎，为硅钢炉底辊套管生产用原料破碎装置的破碎工作带来一种保障。

利用EBSD技术研究了电工钢中不同的柱状晶尺寸及退火工艺下{100}织构的演变规律。结果表明,初始晶粒尺寸的影响最显著。细小柱状晶热轧后经过常化处理,组织已均匀,但中心层有强{100}织构。粗大柱状晶中{100}织构的遗传性强,常化及中间退火后,中心层仍有粗大的以{100}取向为主的晶粒;脱碳退火后才能完成组织均匀化和织构梯度的弱化。常化时的升温速度也对织构演变存在影响,低的升温速度有利于{100}织构的保留,但升温速度的影响没有初始晶粒尺寸及退火次数的影响显著。细小柱状晶样品经过热轧及三次退火工艺适合制备取向电工钢。 Evolution of {100} texture of different columnar grains and annealing process was investigated in electrical steels with the help of EBSD technique.The results show that the effect of initial grain size is the strongest.The initial fine-grained specimen shows uniform microstructure after the normalizing process,while {100} grains appear preferentially in the central layer of sheets.The heredity of {100} texture in the initial coarse-grained specimen is more significant.{100} mainly-oriented coar... 

本发明属于双取向硅钢技术领域，公开了一种双取向硅钢薄带及其制备方法，包括：选取具有Si、Al、Mn、C和Fe，且具有一定取向的硅钢薄带；将其进行冷轧；将冷轧板在N2、H2保护气氛中进行退火处理。本发明通过合理的轧制和退火工艺搭配，使具有Goss取向的硅钢薄带转变为具有旋转立方取向的硅钢薄带，将单取向硅钢转变为双取向硅钢。本发明具有工艺简单和便于利用钢铁企业现有设备的特点，所制备的双取向硅钢薄带具有双向铁损低和磁感高的性能。本发明制备的双取向硅钢薄带在与轧向成45°的两个方向上具有优异的双向磁性能，解决了现有双取向硅钢薄带的制备工艺复杂、设备要求高、不利于工业生产的问题。

针对马钢无取向电工钢孔洞缺陷的分布规律及形貌特征,对缺陷样进行了显微分析,并利用生产实绩数据分析了该缺陷产生的原因。结合热轧生产过程,主要通过避免带钢撞击导卫以及降低导卫结瘤的产生等措施,可有效抑制热卷异物压入产生,从而降低冷轧工序孔洞的产生。 In viewing of the distribution and morphology characteristics of the hole defect of non-oriented electrical steel in Maanshan Iron and Steel Co.,Ltd.,the causes of the defect were analyzed by micro analysis of the defect sample and the production data.Combined with the production process of hot rolling,by avoiding the impact of strip steel on the guide and reducing the nodule formation on the guide,the pressing of foreign bodies in hot coiling could be effectively suppressed,thus reducing the fo... 

实验室模拟薄板坯连铸连轧(TSCR)流程制造高磁感取向硅钢,借助电子背散射衍射(EBSD)技术对不同Sn含量的热轧板织构进行了研究。研究结果表明:不同Sn含量热轧板表层及次表层均为高斯织构、铜型织构及黄铜织构的混合织构,中心层为{100}面织构;Sn含量为0.1%时,热轧板表层及次表层高斯织构组分最多,取向密度最大,成品磁感最高,达到1.875 T。 Texture of grain oriented silicon steel hot rolled by thin slab casting and rolling process(TSCR) in laboratory with different Sn contents was analyzed by electron back-scattered diffraction(EBSD).The results show that the hot rolled slabs with different Sn contents have the same texture,i.e.,Goss,Copper and Brass.Specifically,the texture of core layer is {100};While the hot rolled slab with 0.10% Sn,the surface layer and subsurface layer have a sharpness Goss texture and the finished products h... 

针对硅钢连续退火机组的主要能源介质消耗现状,对现有生产工艺和设备研究采取机组循环用水、增加清洗段漂洗级数等措施可节约大概27 m3/h的过滤水量,并可减少78%的弱碱处理量;将炉子烟气换热系统增加一级余热回收,每年回收的余热相当于583 t标煤消耗,可节约蒸汽5 368 t。 The present situation of energy consumption for silicon steel annealing line is analyzed in this paper.In existing process and equipment conditions,increasing the number of cleaning series will lead to a saving of about 27 m3/h of filter water and reduce 78 % of weak base processing volume.For the flue gas heat-exchange system,adding a waste heat recovery device will recover waste heat equivalent to 583 tons of standard coal per year,corresponding to a saving of steam 5 368 t per year. 