分析总结退火工艺各参数对冷轧无取向硅钢磁性能的影响,结合设计和生产实践经验介绍退火工艺中各参数的实际生产取值,并针对现生产工艺过程中出现的典型问题提出解决办法。 It is analyzed and summarized the great influences on magnetism of cold rolled non-oriented silicon steel affected by various annealing process data in this article.The relevant settled ways is raised.According to the actual value presetting ways for various annealing process data based on design and production,as well as typical problems occurred during production. 

硅钢连续退火线是无取向硅钢生产的成品线。由于受机组布置的影响,带钢经转向辊进出口活套后,当套量达到60%后就出现偏离生产线的情况,从而影响最终产品的质量及成材率,甚至损坏设备。针对某冷轧厂硅钢连续退火机组出口活套入口处带钢跑偏开展纠偏研究,利用Matlab对该纠偏系统进行动态仿真研究,分析系统的稳定性。 Silicon steel continuous annealing line is non oriented silicon steel production of finished product line.Due to the influence of unit layout,strip by roll Import & Export loop,when the set volume reached 60% after the emergence of deviation from the production line,thus affecting the quality of the final product and the rate of finished products,and even damage the equipment.For the export of continuous annealing line in cold rolling silicon steel strip deviation rectification loop at the e... 

本发明公开了一种变压器用硅钢片冲切设备，包括输送机、双向冲压机构、缓冲抬升机构和磁吸式清洁器四部分，输送机的末端安装有支撑架，双向冲压机构安装于支撑架上且由驱动机构、导向板、冲压头、连接器和冲切刀片组成，驱动机构的底部垂直安装于导向板的中部，导向板的两端与支撑架相连接，冲压头分设有两组且对称滑动设置于导向板上，驱动机构的两端与两组冲压头相连接，连接器安装于冲压头的末端，两组连接器的下端与冲切刀片的上沿转动连接。本发明所设计的冲切设备采用全自动运作的方式，并且配合有缓冲式的冲压机构，可以减小冲切过程中的形变率，整个机体的运作通过PLC控制器进行控制运作，提高装置的智能化程度。

本实用新型涉及一种多物理因素耦合作用电工钢片矢量磁特性自动测量系统，多物理因素耦合作用电工钢片矢量磁特性自动测量系统包括上位机、数据采集卡、低通滤波器、功率放大器、隔离放大器、励磁装置、矢量B‑H传感器、x方向励磁线圈、y方向励磁线圈、单片机系统、电源、温度自动加载模块和应力自动加载模块。本实用新型实现了电工钢片复杂磁特性测量过程中温度和应力的自动加载，解决了人为操作繁琐，耗时的缺点，使得电工钢片复杂磁特性的测量过程更加方便，高效，可行性更高。

结合工业化生产的无取向硅钢,探讨了氧硫交互作用对钢中夹杂物生成的影响。借助非水溶液电解+扫描电镜法,研究了不同O、S含量下钢中夹杂物的变化规律。结果表明,本实验条件下,提高O含量、降低S含量,会劣化热轧组织再结晶效果。在劣化效果上,O的作用大于S;低Si、无Al硅钢中,应尽可能降低O含量、适当提高S含量,以粗化钢中微细夹杂物,减少尺寸小于1.0μm的夹杂物的数量;O、S含量与钢中夹杂物数量不具有关联性。生产过程中,不仅要严格控制O、S含量,还要严格控制生产工艺,以免生成较多的有害夹杂物。 Based on the industrial production of non-oriented silicon steel,the effects of interaction between oxygen and sulfur on the formation of inclusions were discussed.The change of non-metallic inclusions in steel sheets was investigated by means of electrolysis with non-aqueous solution under different oxygen and sulfur content.Results show that the recrystallization microstructure of hot rolled sheets will be deteriorated with the increase of oxygen content and the decrease of sulfur content.The ... 

本发明涉及一种用于控制硅钢毛刺状厚度波动的工艺，包括如下步骤；将连铸坯送入加热炉中进行加热，连铸坯入炉温度为400‑680℃，连铸坯在炉时间为185‑220min；将加热后的连铸坯进行热轧，轧辊偏心量为0‑0.025mm，将热轧后的带钢进行卷取；将卷取后的带钢酸洗后进行冷轧，冷轧操作模式由多次阶段升降速模式调整为一次性升降速模式，且在一次性升降速阶段将MN‑AGC增益系数增大；将冷轧后的带钢进行卷取，退火后得到硅钢片成品。本发明所公开的用于控制硅钢毛刺状厚度波动的工艺，该工艺对加热、热轧、卷取及冷轧各工序进行优化协调，能够有效解决硅钢毛刺状厚度波动的问题，实现无取向硅钢全长厚度控制精度的提升，而且无需进行设备和系统改造，容易实现，易于推广。

【作者】 王磊； ...

结合工业化生产的无取向硅钢,进行了RH精炼添加稀土合金实验。结果表明,1.15%(质量分数)Si钢的脱硫反应,主要发生在添加稀土合金之后的前5min。最佳的稀土合金添加量为0.6～0.9kg/t钢。钢液经过稀土处理后,加入的稀土总量越多,稀土氧硫化物夹杂物的尺寸就越大,但热轧带钢再结晶效果会逐渐变差,成品带钢晶粒尺寸先是快速长大,而后逐渐减小。最佳的钢中存留稀土含量与钢的化学成分有关,应严格控制在2.0×10-3%～6.0×10-3%(质量分数)。在此范围内,钢的铁损先是快速降低,而后缓慢升高,钢的磁感应强度则单调降低。 Based on the industrial production of non-oriented electrical steel,rare earth(RE) alloy treatment during the RH refining process was studied.The results showed that the effects of desulfurization and total concentration of RE remained in steel mainly depended on the chemical compositions of different steel grades.For 1.15wt% Si steel grade,the desulfurization reaction mainly focused on the initial 5min after RE alloy added during the RH refining process.The suitable RE alloy addition was 0.6-0.... 

本发明公开了一种高磁感取向硅钢实验室轧机一次冷轧方法，包括：1)取样，实验室冷轧材料选取经过常化酸洗后的厚度为2.3mm的取向硅钢试样；2)制样，利用取向硅钢专用剪板机，裁剪试样尺寸为轧向600mm×横向150mm；将试样表层轻涂一层薄薄的轧制油；3)冷轧轧制规程制定，轧前厚度为2.3mm；其中：轧制总道次为6次时轧后厚度为0.35mm，轧制总道次为7次时轧后厚度为0.27mm，轧制总道次为8次时轧后厚度为0.23mm。本发明的目的是提供一种高磁感取向硅钢实验室轧机一次冷轧方法，为工业试制提供一定的技术参考，以及后续工艺研究提供了更加可靠的试样和条件。

本发明提供一种无取向硅钢用涂层溶液及其制备方法和应用，以所述无取向硅钢用涂层溶液的总质量为基础计，所述无取向硅钢用涂层溶液包括如下质量百分含量的原料组分：磷酸盐溶液55％～60％；树脂溶液20％～25％；二乙二醇丁醚2％～4％；改性剂3％～5％；余量为水。由本发明所述无取向硅钢用涂层溶液形成的绝缘涂层厚度均匀，表面光滑，具有优良的绝缘性、耐腐蚀性、附着性，而且硅钢片的冲片性能好、叠片系数高。

本发明公开了一种半无机硅钢片漆及其制备方法和应用，其包括：聚酰胺酰亚胺清乳液、二氧化钛、二氧化硅、硫酸钡和氨基树脂，聚酰胺酰亚胺清乳液的制备：在保护气体保护下和回流状态下，使偏苯三酸酐与特定的复合双端氨基化合物在第一有机溶剂中反应，加入磷酸三丁酯、三乙胺，反应；向外蒸出第一有机溶剂，加入第二有机溶剂，加入直链烷基苯磺酸钠、脂肪醇聚氧乙烯醚硫酸钠和脂肪醇聚氧乙烯醚，混合，在搅拌条件下滴加水，滴加完之后，加入双马来酰亚胺进行封端，制成；该半无机硅钢片漆通过将各组分混合超声分散而制成，可在硅钢片中作为覆盖漆应用，且不仅可以采用水作为主体溶剂，环保型好，而且还兼具耐高温、高粘结强度、电气性能强等优点。

依据GB/T 15616—2008《金属及合金的电子探针定量分析方法》,采用电子探针波谱仪对某W600硅钢中的硅含量进行了定量测定,对影响其定量测定结果的不确定度分量进行了分析,并对不确定度的各个分量进行了计算和合成,最后给出了硅钢中硅含量测定结果的不确定度报告:该硅钢中的硅含量(质量分数)为1.50%,扩展不确定度U=0.20%,取包含因子k=2。 According to GB/T 15616-2008\"Quantitative Method for Electron Prohe Microanalysis of Metals and Alloys\",the quantitative results of Si content in some W600 silicon steel was measured hy EPMA-WDS.The uncertainty components which might affect the measurement results were considered,calculated and synthesized. Finally the uncertainty result for the quantitative value of Si content in the silicon steel was got.The mass content of Si was 1.50%,and expanded uncertainty U=0.20%under the condition of co...