借助光学显微镜、扫描电镜、交流磁性能测量仪和万能拉伸试验机研究了0.3 mm厚高强无取向电工钢冷轧板在780、820、860和900℃退火保温2 min后的组织、织构和性能。结果表明:在退火温度范围内,试验钢均发生了完全再结晶,得到等轴状的铁素体晶粒;随着退火温度的升高,平均晶粒尺寸从9.2μm增长到41.3μm,工频铁损和400 Hz高频铁损均先大幅减小后趋于平缓,磁感应强度先升高后降低。在820℃退火时,铁损P_1.5/50=5.51 W/kg,P_1.0/400=33.22 W/kg均处于较低值,磁感应强度B₅₀₀₀最大,为1.649 T。试验钢的屈服强度和抗拉强度均随退火温度的升高而降低,780℃退火时屈服强度为496 MPa, 900℃退火时降低至407 MPa。综合磁性能和力学性能考虑,试验钢的最佳退火温度是820℃。 Microstructure, texture and properties of 0.3 mm thick high strength non-oriented electrical steel cold rolled sheet annealed at 780 ℃, 820 ℃, 860 ℃ and 900 ℃ for 2 min were studied by means of optical microscope, scanning electron microscopy, AC magnetic property tester and universal tensile testing machine. The results show that in the annealing temperature range, complete recrystallization of the experimental steel occurs and equiaxed ferrite grains are obtained. With the increase of annealin... 

本实用新型公开了一种变压器铁芯硅钢片的堆叠装置，包括底座、摆动机构、摆动板和垫高倾板，所述底座上设置有摆动机构，所述摆动板的一端铰接设置在底座上，且所述摆动板间距于摆动轴线的板体与摆动机构对应设置，所述摆动机构驱动摆动板在竖向面内进行往复摆动，所述垫高倾板间距于摆动板设置在底座上，且所述垫高倾板与摆动板之间构成用于叠放硅钢片的叠放区，所述叠放区的底部呈高低倾斜设置，且所述叠放区的低端侧朝向于摆动板，能够使得硅钢片的收集简单，且十分整齐。

本实用新型涉及硅钢片加工领域，且公开了一种用于硅钢片钢卷制造的清洗装置，解决了目前市场上用于硅钢片钢卷制造的清洗装置工作效率低下，清洗效果不明显的问题，其包括包括清洗箱，所述清洗箱内腔的顶部与底部均安装有清洗导管，两个清洗导管的表面均等距离安装有清洗喷头，清洗箱两侧的下部分别安装有限位框和清刷框，清洗箱的一侧通过支架固定连接有安装板，安装板的表面转动连接有硅钢卷本体，硅钢卷本体的一端依次贯穿限位框、清洗箱和清刷框并延伸至清洗箱外部，该用于硅钢片钢卷制造的清洗装置，结构设计合理，清洗操作平稳，清洗干净，工作效率高，大大的提高了清洗效率和提高了清洗质量，极具推广应用价值。

本发明提供能够制造实现高磁通密度且磁特性优异的方向性电磁钢板的新颖并且得以改良的方向性电磁钢板的制造方法。本发明的一方案提供一种方向性电磁钢板的制造方法，其特征在于，其包含热轧工序、冷轧工序、一次再结晶退火工序、最终退火工序及平坦化退火工序，并进行喷丸处理和/或矫平加工处理及与溶液相接触的处理，上述溶液含有规定量的Cu等，pH为‑1.5以上且低于7，液温为15℃以上且100℃以下，钢板在上述溶液中浸渍的时间为5秒以上且200秒以下。

本实用新型涉及电机技术领域，具体涉及一种具有低应力结构的硅钢片、转子和电机。包括硅钢片、开设在硅钢片上的磁钢槽和嵌设在所述磁钢槽内的磁钢组件，所述磁钢组件包括多个磁钢组，所述磁钢组包括靠近转子边缘的一对小永磁体和靠近转子内侧的一对大永磁体，所述硅钢片在转子轭部沿周向分布有径向开槽，且所述径向开槽从硅钢片的中心向边缘延伸。其通过在转子轭部沿周向分设置从硅钢片的中心向边缘延伸的径向开槽，能降低大永磁体左右两侧铁芯刚度差距，从而有效降低隔磁桥处的应力，防止磁钢和铁芯产生形变而断裂。其无需改变电机转子外圆结构，在保证转矩输出的前提下，防止高速旋转时带来空气啸叫声。

借助实验室设备研究了B元素对高牌号无取向硅钢热轧板组织和磁性能的影响。结果表明,与无硼钢相比,含硼钢的热轧板晶粒尺寸略小,析出物的类型和尺寸没有区别,主要是AlN和(AlN+MnS)复合析出物,少量的MnS析出物,尺寸集中在1.0～2.5μm范围内。未发现BN析出物。在力学性能方面,B对钢的软化作用不明显。在磁性能方面,含硼钢的铁损为3.215W/kg,磁感为1.710T,综合磁性能比无硼钢差。 Influences of boron on microstructure and properties of hot rolled band in high-grade non-oriented silicon steel are researched in this paper by experimental equipments.Compared with boron-free steel,the result shows that boron-bearing steel has smaller grain size,but the type and size of precipitations have no differences.The main precipitates are AlN,(MnS + AlN) composite precipitate and few MnS,the range of which are between 1.0 μm and 2.5 μm.BN precipitation is not found.With reward to mecha... 

本文研究了丙烯酸树脂含量对以Al(H2PO4)3为基料的无铬无取向硅钢绝缘涂层各项性能的影响.用盐雾实验、动电位极化及交流阻抗等试验手段研究了不同树脂含量对硅钢绝缘涂层的耐盐雾性能和电化学行为的影响,同时采用SEM对涂层的表面形貌和附着性进行研究.结果表明,树脂含量为19.9~29.4%时,涂层的耐蚀性和附着性最好;树脂含量过多时,涂层的耐蚀性和附着性均较差. This paper studies the influence of acrylic resin on the performance of insulating coating of aluminum dihydrogen phosphate on chromium-free non-oriented silicon steel.Salt spray experiment,potentiodynamic polarization and electrochemical impedance spectroscopy were used to study the influence of acrylic resin content on the salt spray resistance and electrochemical behavior of the insulation coating of nonoriented silicon steel.The surface morphologys and adhesion of coating were tested by SEM.... 

本实用新型公开了一种变压器用硅钢板滑石丸粘接加工设备，用于对变压器用硅钢片进行贴片，其结构包括：机械臂、抓取头、分道排序机构，所述抓取头位于机械臂的末端，用于抓取滑石丸，在抓取头上能够同时抓取多个滑石丸，配合机械视觉系统，就能够更精确的确定贴片位置，并完成贴片，提高了生产效率；所述分道排序机构包括：振动盘、排料板，振动盘中储存有一定的滑石丸，振动盘顶部的出料口与排料板连接，工作时振动盘中的滑石丸依次从出料口进入排料板中，在排料板上的物料通道中运动，物料通道的末端是多条分支，且末端向外敞开，抓取头能够在物料通道末端同时抓取多个滑石丸。

本实用新型公开了一种大型硅钢片生产用输送装置，包括支撑座，所述支撑座的顶部安装有第一支架和第二支架，且第一支架位于第二支架的上方，所述第二支架的一端伸出支撑座的底部，其中，所述第一支架的外部套设有多组第一皮带，所述第一支架的内部安装有多组气缸，且气缸的一侧安装有感应器；所述第二支架的外部套设有两组第二皮带以及两组第三皮带，且两组第二皮带分别位于第二支架的两侧，两组所述第三皮带位于两组第二皮带之间，且第三皮带的长度小于第二皮带的长度。本实用新型所述的一种大型硅钢片生产用输送装置，通过对第一皮带增加磁性，并对调整第三皮带之间间距，能够轻松将转子和定子进行分类堆叠，节省机械手运行的时间。

采用扫描电镜、原子力显微镜研究了铬酸镁半无机绝缘涂层的微观结构。结果表明,涂层厚度为数微米,涂层中的有机树脂乳液颗粒均匀分布在无机涂层的表面,从而保证了涂层具有良好的冲片性能。采用极化曲线研究了涂层的耐蚀性能,发现铬酸镁与铬酸锌绝缘涂层的耐蚀性能相当。 In this paper,the microstructure and anti-corrosion property of magnesium chromate coating on non-oriented silicon steel were studied.The microstructure was observed by SEM and AFM.The anti-corrosion properties were evaluated by polarization curves.The results show that the thickness of coating is several microns and the polymer particles were scattered on the surface of inorganic coating,which is the guarantee for lamination property.The corrosion resistance of the magnesium chromate film was e... 

本发明涉及一种硅钢热处理方法，尤其涉及一种取向硅钢极薄带绝缘层涂覆方法，包括以下步骤：(1)接入普碳钢引带的准备工作；(2)各炉段张力的设定工作；(3)炉内气氛及温度的调节工作；(4)绝缘层厚度及厚度的检测工作；(5)极薄带涂层涂覆及烘干工作；(6)极薄带表面绝缘涂层及磁性能检测工作。本发明采用与极薄带厚度相当的普碳钢作为引带，通过引带测试产线张力和绝缘层涂覆的厚度，一方面可通过普碳钢薄带的运行加速炉内温度和气氛的稳定性，节约炉内稳定时间；另一方面可通过成本较低的普碳钢检测炉内张力和温度的设定，及绝缘涂层的涂覆效果，避免开始采用硅钢带出现断带，及涂覆不合格后造成产品报废带来的成本升高。

本实用新型公开了一种将硅钢片堆栈模块化的电机转子，包括：堆栈模块、转子端板和电机轴；堆栈模块卡接在电机轴的外侧，且堆栈模块的两端通过转子端板连接固定；堆栈模块包括多个相互连接的硅钢片，每个硅钢片上均设有连接件，硅钢片通过连接件相互连接。本实用新型通过在硅钢片上增设连接件将多个硅钢片叠加成堆栈模块，降低了固定难度和管理难度，而且可以使用机器人自动化产线的大规模生产，生产效率高。