本发明公开了一种降低无取向硅钢W800头部窄尺的控制方法，步骤1、筛选板坯长度，并使板坯进入加热炉后头部均朝向轧机方向；步骤2、控制板坯头部温差小于10℃；步骤3、固定粗轧到精轧区间内的轧机机架轧制速度；步骤4、固定相变机架，使板坯的奥氏体‑铁素体相变发生在F2和F3机架中；步骤5、调整精轧机架间的负荷分配，降低F2和F3机架的压下量；步骤6、调整活套张力，降低F2和F3机架的活套单位张力补偿；步骤7、降低模型AGC增益，降低F2和F3机架的AGC补偿的辊缝波动量。本发明通过控制固定相变机架、优化相变机架的负荷分配、AGC补偿系数、活套张力等，使秒流量保持平衡，减少无取向硅钢W800头部窄尺。

变压器D21硅钢铁芯片采用冲压工艺生产。首先对其工艺进行了分析,确定了冲压方案。对产品进行了排样设计,计算了冲压力,确定了压力中心。然后,设计了单工序落料模具,完成了模具装配图。 D21 silicon steel chips for transformer are produced by stamping.First,its stamping process was analyzed and the scheme of the stamping process was determined.The product layout was designed,the punching pressure was calculated,the pressure center was determined.Then,the blanking die with single procedure was designed,the die assembly drawing was completed. 

采用RH精炼添加钙合金方式对硅钢进行钙处理,结果表明,钙合金添加量为0.67、1.00和1.67 kg/t钢时,钢中Ca含量分别为0、2×10-6和4×10-(6质量分数);随着钙合金添加量的增加,钢中夹杂物粒度逐渐由0～2μm向2～4μm、4～6μm偏移;不同钙处理条件下,钢中均存在粒径小于1μm和粒径为1～5μm的MnS、CuxS夹杂物,后者或单独存在,或与AlN、CaS夹杂复合;钢中粒径为5～10μm的夹杂物基本以Ca的氧化物和硫化物为主。与未经钙处理的炉次相比,钙合金添加量为0.67、1.00和1.67 kg/t钢时,粒径小于1.0μm的夹杂物减少幅度分别为68.06%、87.50%和94.94%。钙合金添加量为1.67 kg/t钢时,可以去除钢中绝大部分的微细夹杂物。 In order to improve the properties of final silicon steels,the calcium treatment was adopted by adding Ca alloys into the liquid steel during the RH refining process.Results show that when the addition of Ca alloys is 0.67 kg/t,1.00 kg/t and 1.67 kg/t,the corresponding Ca content in silicon steels is 0,2 × 10-6 and 4 × 10-6 respectively.With the increase of Ca alloy addition,the particle sizes of inclusions in steels become 2～4 μm and 4～6 μm,from 0～2 μm.Under different calcium treatments,there e... 

本实用新型涉及变压器材料检测技术领域，具体为一种硅钢片检测装置，包括材料检测装置主体，材料检测装置主体包括相互连接的铁损测试仪主机及磁导计，磁导计的顶端设置有清洁机构，清洁机构包括固定盒、拉块及刷块，固定盒固接于磁导计上，拉块插设于固定盒中、能够在固定盒中上下移动，固定盒的内部底面上及拉块的底端上分别安装有刷块，铁损测试仪主机上还设有束线机构。本实用新型使得用户可在检测硅钢片前，对硅钢片两面沾染的灰尘污渍进行擦拭，避免灰尘污渍影响对硅钢片的测定结果，可方便地对刷块进行清洁更换，使得用户可方便地对电源线和导线进行收纳。

通过对连退线SF炉内的电加热体的焊接技术进行总结分析,得出焊接时应采用的主要方法,采用本焊接方法可提高电加热体的焊接速度和焊接质量,保证了焊接质量和施工工期。 SF furnace for continuous annealing line heating body welding technology summary,the main method used in welding,welding method by using the electric heater to improve the welding speed and welding quality through the implementation of this method to ensure the welding quality and Construction period. 

为开发高效电机用冷轧无取向电工钢,借助实验室薄板坯连铸连轧模拟设备及扫描电镜、透射电镜等检验手段研究了成分、组织、织构和析出物等对无取向电工钢磁性能的影响规律;结果表明:常化处理使组织均匀化并增加有利于磁性提高的织构组分;采用CSP流程开发的高效电机用无取向电工钢铁损平均值3.4 0 W/kg,磁感≥1.68 T。 In order to develop electrical steel for high efficiency motor,effect of components,microstructure,texture and precipitation on magnetic property of electrical steel are analyzed.From the result,normalizing treatment makes microstructure uniform and increases component of favorable texture.Iron loss of electrical steel developed by CSP line is 3.40W/kg and magnetic induction is more than 1.68T. 

利用OM、SEM、TEM等实验方法研究了卷取工艺对一种新型含铜无取向电工钢晶粒度和析出相的影响。结果表明,该电工钢热轧带卷取后的晶粒尺寸为18～24μm,在卷取过程中,热轧带中有一定数量的第二相析出,经EDS能谱及选区电子衍射分析,这些析出相主要为AlN。随着卷取工艺的变化,该电工钢的晶粒度大小变化不明显,析出相的类型、尺寸大小不发生改变,体积分数发生一定的改变。 The effects of coiling process on grain size and precipitates of a new copper-bearing non-oriented electrical steel were investigated by OM,TEM and other experimental method.The results show that the grain size of hot-rolled bands after coiling is 18～24 μm.The second phases precipitate during coiling process.They are mainly AlN by EDS spectra and selected area electron diffraction.With the change of coiling process,the grain size of the electrical steel does not change significantly;the type and... 

无取向硅钢的磁性能主要取决于铁素体的晶粒尺寸、晶体织构和钢中的夹杂物。通过合适的化学成分设计以及采用适宜的夹杂物控制技术,可以获得最佳的夹杂物控制效果,使其纯净度大幅度提高或者无害,最终获得磁性能优良的高级别无取向硅钢。同时,为满足节能、环保、高效需求,无取向硅钢正朝着节能降耗、环境友好以及多功能、高效率、易加工等方向发展。 The magnetic properties of non-oriented silicon steel mainly depend on the grain size of ferrite,the crystallographic texture,and the inclusions in the steel.The optimum inclusion control effects can be obtained through a suitable chemical composition design and an appropriate inclusion control technique,and then the liquid steel will get be clean or the inclusion will get be harmless,finally the excellent magnetic property of the non-oriented silicon steel can be obtained.Meanwhile,in order to ... 

本发明是高磁感取向硅钢的脱碳退火工艺，首先对硅钢卷进行放卷、活套、清洗；再对硅钢进行脱碳、渗氮处理，氨气流量6‑20m3/h、加湿槽温度30‑70℃，脱碳温度780‑880℃、机组速度45‑75m/min、气氛中氢气比例20‑60％、氮气比例40％‑80％，然后冷却到常温；对硅钢进行活套；再对硅钢进行涂覆氧化镁，涂覆量4‑10g/㎡；最后对硅钢进行干燥和收卷成硅钢卷；通过本发明对高磁感取向硅钢的脱碳退火工艺流程进行了优化设计，调整了脱碳退火工艺中氨气流量、气氛、加湿槽水温等参数，优化了高磁感取向硅钢中碳元素、氮元素和氧元素的含量，最终使高磁感取向硅钢实现稳定的性能，磁感达1.92T。

【作者】 陈迪安； 李春生； ...

本发明涉及变压器硅钢片技术领域，尤其是涉及一种变压器硅钢片组件成型冲裁机械及成型冲裁方法，包括基座、收卷装置、挤压装置、滚动装置和冲压装置，所述基座的上端位于四角处均固定连接有竖杆，竖杆的上端共同连接有横板，横板的下端设置有冲压装置，基座的上端设置有收卷装置，基座的上端位于收卷装置的后方设置有挤压装置，基座的上端位于挤压装置的后方设置有滚动装置；通过拉动拉环，带动圆板和推杆挤压第一弹簧，第一弹簧的挤压，使得推杆远离推槽，进而可取出模具，对模具进行更换；通过往凹槽内加入放置板，防止压板在撞击模具时，对模具进行支撑，防止模具发生变形。

本实用新型涉及硅钢片加工领域，且公开了一种用于硅钢片钢卷制造的清洗装置，解决了目前市场上用于硅钢片钢卷制造的清洗装置工作效率低下，清洗效果不明显的问题，其包括包括清洗箱，所述清洗箱内腔的顶部与底部均安装有清洗导管，两个清洗导管的表面均等距离安装有清洗喷头，清洗箱两侧的下部分别安装有限位框和清刷框，清洗箱的一侧通过支架固定连接有安装板，安装板的表面转动连接有硅钢卷本体，硅钢卷本体的一端依次贯穿限位框、清洗箱和清刷框并延伸至清洗箱外部，该用于硅钢片钢卷制造的清洗装置，结构设计合理，清洗操作平稳，清洗干净，工作效率高，大大的提高了清洗效率和提高了清洗质量，极具推广应用价值。