硅钢资料

本申请提供了一种提高高磁感取向硅钢渗氮效率的方法，属于高磁感取向硅钢渗氮处理技术领域，包括所述高磁感取向硅钢按重量百分比包括：Si：2.8～3.4％、C：0.040～0.070％、Als：0.015～0.045％、Mn：0.06～0.14％、S：0.003～0.020％、N：0.003～0.010％、Cu：0.01～0.025％、Sn：0.03％～0.07％、Cr及Ni，Cr和Ni的总含量小于0.5％，其余为Fe和不可避免杂质物，其特征在于，控制脱碳退火后钢带表层氧化物中铁系氧化物的比例，该装置能够增加脱碳退火后钢带表面氧化层中铁系氧化物占整个氧化层重量的比例，从而在获得同等渗氮量的情况下实现了快速渗氮，缩短渗氮时间，提高渗氮效率。

提出了一种基于爱泼斯坦方圈族(包括标准25cm爱泼斯坦方圈、缩比的17.5cm和20cm爱泼斯坦方圈)和二级加权处理方法对爱泼斯坦测试数据,包括有效磁路长度、比损耗、励磁功率,进行处理的晶粒取向电工钢磁性能扩展模拟方法。详细地考察了励磁频率、试样剪切角度和环境温度对爱泼斯坦方圈测量结果的影响。研究结果表明,利用本文提出的爱泼斯坦方圈组合以及二级加权处理技术,可以有效地建立取向电工钢损耗模拟模型,从而更加准确地确定了取向电工钢的损耗,改善并提高了爱泼斯坦磁性能测试数据的应用价值。 The extended modeling of the magnetic properties of GO(grain oriented) electrical steel is presented in this paper which is based on a set of standard and scaled-down Epstein frames and a proposed two-level weighted processing of Epstein data, including the mean magnetic path length, specific magnetization loss and exciting power. The effects of excitation frequency, strip angle and ambient temperature on the results obtained from the Epstein frames are investigated. It is shown that using the p... 

本实用新型公开了一种环保型无取向硅钢绝缘涂层液生产用篮式研磨机，包括底座，底座顶端的一侧固定安装有支撑柱，支撑柱的顶端固定安装有顶板，顶板的底端设有研磨组件，研磨组件包括两个固定板，两个固定板分别固定安装的顶板底端的中部和底端的另一侧，底座上设有固定组件，固定组件包括四个支撑板，四个支撑板均固定设置底座顶端的另一侧，四个支撑板的顶端固定安装有固定环，固定环的内部放置有料缸，本实用新型的有益效果是：通过研磨组件在粗磨后快速切换至细磨，不需要切换研磨机，提高研磨的效率，通过固定组件将放置在固定环内部的料缸进行固定，防止研磨过程中料缸发生移动。

提供能够稳定地制造磁特性优异且钢卷长度方向的铁损的偏差少的取向性电磁钢板的取向性电磁钢板的制造方法。本发明是一种取向性电磁钢板的制造方法，包括如下工序：对钢坯进行热轧，根据情况实施退火，然后通过1次冷轧或夹有中间退火的2次以上的冷轧来制成具有最终板厚的冷轧板，接着对上述具有最终板厚的冷轧板进行脱碳退火，然后实施二次再结晶退火；在最终的冷轧之前，将钢板以100℃/s以上的升温速度加热到100℃～350℃的加热温度，上述钢板从达到加热温度到进入最终的冷轧的第1道次的时间为5秒以内。

无取向硅钢的磁性能主要取决于铁素体的晶粒尺寸、晶体织构和钢中的夹杂物。通过合适的化学成分设计以及采用适宜的夹杂物控制技术,可以获得最佳的夹杂物控制效果,使其纯净度大幅度提高或者无害,最终获得磁性能优良的高级别无取向硅钢。同时,为满足节能、环保、高效需求,无取向硅钢正朝着节能降耗、环境友好以及多功能、高效率、易加工等方向发展。 The magnetic properties of non-oriented silicon steel mainly depend on the grain size of ferrite,the crystallographic texture,and the inclusions in the steel.The optimum inclusion control effects can be obtained through a suitable chemical composition design and an appropriate inclusion control technique,and then the liquid steel will get be clean or the inclusion will get be harmless,finally the excellent magnetic property of the non-oriented silicon steel can be obtained.Meanwhile,in order to ... 

研究了常化对CSP流程生产的wSi=1.6%的无取向电工钢组织、织构和成品磁性能的影响。结果表明,经CSP流程生产,且在相同的冷轧及退火制度下,经1 000℃×2min常化处理的wSi=1.6%的无取向电工钢热轧板,其最终退火成品的铁损P15/50比不常化试样下降了10.5%,磁感B50比不常化试样提高了2.5%;常化使wSi=1.6%的无取向电工钢成品的平均晶粒尺寸增大,成品铁损P15/50相应减小;同时,常化使wSi=1.6%的无取向电工钢成品中高斯织构的强度增加,γ纤维织构的强度减弱,这有利于成品磁感B50的提高。 The effect of normalizing on microstructure,texture and magnetic properties of non-oriented electrical steel with wSi=1.6% produced by CSP process was investigated.The results show that,under the same cold rolling and annealing system,the iron loss(P15/50) of annealed samples whose hot bands has been normalized by 1 000 ℃×2 min process decreases by 10.5% and magnetic induction(B50) increases by 2.5% compared with the samples whose hot bands was not normalized.The average grain size of non-orient... 

采用节能、环保、经济型的生产技术与工艺来制造高磁感取向硅钢目前已成为世界各大取向硅钢生产厂的研发热点。总结了国内外各大钢铁企业与研究机构采用低温板坯加热技术生产高磁感取向硅钢的开发及应用情况,概括了传统流程实现低温板坯加热技术的方法。介绍了薄板坯连铸连轧与双辊薄带连铸等短流程工艺生产高磁感取向硅钢的研发现状。在此基础上,探讨了高磁感取向硅钢生产技术与工艺的发展趋势及方向。 Utilizing energy-efficient,environmentally friendly,economic production processes and technologies to manufacture high magnetic induction grain-oriented silicon steel has become the focus of current research work.Based on using low-temperature slab reheating techniques to produce high magnetic induction grain-oriented silicon steel at both iron and steel enterprises and research institutions all over the world,the current application and exploitation was thoroughly generalized;the implementation... 

本实用新型公开了一种镀铝锌硅钢钣冲压装置,包括安装板，所述安装板的上表面延伸至下表面开设有上下管贯通的板件交换槽，所述安装板的上表面且位于板件交换槽的正上方通过固定螺栓固定连接有模座板。本实用新型，通过设置二次镀膜箱，对冲压后的硅钢钣进行二次铝锌镀膜，避免了冲裁面的暴露导致硅钢钣慢性腐蚀，提升了镀铝锌硅钢板的质量和使用寿命，通过设置夹取机构，对硅钢钣自动取放操作，减少了人力操作，提高了效率的同时，提高了设备安全性，通过设置废料回收槽，对冲压产生的边角料进行集中回收在利用，提升了生产过程中的环保性，通过优化结构设计，提高了镀锌硅钢钣的生产效率，降低生产成本。

本发明公开了一种硅钢高温加热炉用铬基高氮合金垫块及其制备方法，所述合金垫块含有Cr、Mo、N、La、Ce和Fe，不含有钨；所述合金垫块在高温抗氧化性能和高温抗蠕变性能上，优于现有技术的铬铁合金；本发明可以优化替代现有的硅钢高温加热炉用铬铁合金垫块，满足硅钢在加热炉中的加热需求，大规模工厂化生产，拥有极高的使用价值和广阔的应用市场。

本实用新型公开了一种无取向硅钢的绝缘涂料喷涂装置，包括喷涂支架，所述喷涂支架安装有输送装置，所述喷涂支架的顶端侧壁水平方向固定有横向支撑板；本实用新型通过电机与第二行程开关接触启动工作，带动齿轮转动，驱动支撑杆左移，使喷涂喷头左移喷涂硅钢左端上表面，当电机接触到第一行程开关后，使电机工作带动齿轮反向转动，驱动支撑杆和喷涂喷头右移，在一定范围内，使喷涂喷头可以喷涂不同宽度的硅钢，通过施力转动螺杆，使螺杆左移、右移，使第一行程开关在水平方向移动，调节第一行程开关和第二行程开关之间的水平距离，从而调节喷涂喷头水平方向活动范围，根据硅钢宽度需求喷涂。

为了确定普通冷轧取向硅钢最优的中间完全脱碳退火工艺,在其一次冷轧后进行5种不同工艺的脱碳退火处理,借助扫描电镜及电子背散射衍射技术研究了不同工艺脱碳退火后的组织、织构和脱碳效果。结果表明:经5种工艺脱碳退火处理后,初次再结晶的平均晶粒尺寸均约为19μm,且不随退火温度和时间的变化而变化;经840℃×10min工艺退火后的晶粒最均匀,高斯织构位向更准确,高斯织构面积分数最多,为3.1%,可将碳脱至0.003 5%。 In order to determine the optimal intermediate complete decarburizing annealing processes for common grain-oriented(CGO)silicon steel,five kinds of intermediate decarburizing annealing processes were conducted,the microstructure,texture and decarbonization after different decarburizing annealing processes were studied by scanning electron microscopy and electro back-scattered diffraction(EBSD)technology.The results show that the average grains sizes of primary recrystallization were about 19μm a... 

本实用新型属于检测设备技术领域，尤其为永磁同步电动机硅钢片的检测设备，包括检测台板，所述检测台板的两侧固定连接有立固框，所述立固框的上端固定连接有交叉式顶板，所述交叉式顶板的上端固定安装有液压缸，所述液压缸的输出端固定连接有挤压板，所述检测台板的上端表面固定连接有立固块，所述立固块上插设有拔拉杆，所述拔拉杆的一端固定连接有夹固板，所述检测台板的上端表面开设有条形槽，所述条形槽的内部固定连接有横固杆，所述横固杆的外围套设有弹簧。本实用新型通过设置夹固机构，使得硅钢片冲片在进行抗压检测之前能够得到更好的固定，从而避免检测的过程中产生飞弹现象，确保了设备的使用安全性。