采用RH精炼添加钙合金方式对硅钢进行钙处理。结果表明,钙合金添加量为0.67、1.00、1.67kg/t钢时,钢中钙含量分别为0、2×10-6、4×10-6;随着钙合金添加量增大,钢中夹杂物粒度逐渐由0～2μm向2～4、4～6μm偏移;不同钙处理条件下,钢中均存在粒径小于1μm和粒径为1～5μm的MnS、CuxS夹杂物,后者或单独存在,或同AlN、CaS夹杂复合;粒径为5～10μm区间,钢中的夹杂物基本以钙的氧、硫化物为主。与钙处理前相比,钙合金添加量为0.67、1.00、1.67kg/t钢时,粒径小于1.0μm的微细夹杂物减少幅度分别为68.06%、87.50%、94.94%。钙合金添加量为1.67kg/t钢时,可以去除钢中绝大部分的微细夹杂物。 Ca alloy was added into the liquid steel during RH refining,and the results show that Ca concentration in final Si steel sheets is insignificant,about 0,2×10-6 and 4×10-6 when the added amount of Ca is 0.67,1.00 and 1.67 kg/t steel,respectively.With the increase in the added Ca alloy amount,the inclusions in the steel gradually change from those of 0～2 μm to those of 2～4 and 4～6 μm.Under different Ca treatments,there exist MnS and CuxS inclusions whose size is below 1 μm as well as MnS and CuxS ... 

利用XRD和EBSD研究了长轴分别平行于轧向(RD)、横向(TD)和轧面法向(ND)的柱状晶样品在热轧、冷轧及退火过程中的组织、织构演变规律,并分别从几何诱导和取向诱导两个方面分析了晶界的交互作用.结果表明,热轧时由表面摩擦剪切作用引起的组织和织构梯度直接影响并遗传给后续冷轧及退火样品.热轧后,不同样品的初始晶粒形状各向异性差异消失,形成相同的各向异性晶界组织,但晶体学各向异性发生改变,导致随后冷轧、退火组织及织构的变化均不同于直接冷轧的柱状晶样品.研究中特别关注了对磁性能有利的{100}取向区域与晶界的关系. Columnar grains show their special characteristics of morphological and crystallographic anisotropies, and thus markedly influence the microstructure and texture evolution during rolling and annealing process in electrical steel. The rolling and annealing microstructure and texture of three columnar grained samples with the long axes arranged along different directions were investigated by means of XRD and EBSD techniques, and the effects of columnar grain boundaries were analyzed from the view ... 

本实用新型涉及一种硅钢片自动分拨装置，包括U型座，U型座内倒扣有同为U型结构的盖磁板，U型座和盖磁板之间构成封闭的容纳空间，容纳空间内放置有磁铁，紧贴着盖磁板外顶面安装有压板；U型座开口处的两臂之间安装有手杆，U型座外底面间隔平行设置有外凸的肋筋；将分拨装置设置有肋筋的底面靠近堆叠的硅钢片端面，容纳空间中的磁铁将硅钢片磁化，磁化后的硅钢片由于同性相斥的原理，堆叠上部的相邻硅钢片之间自动分拨开，从而便于工人的手工作业，降低了作业难度，极大地减轻了人员工作负担，提高了叠装效率，并且体积小巧携带方便，安全性能好。

对硅钢板材分别进行异步和同步轧制,研究了轧制参数包括速比、压下量和道次对板材表面显微组织的演变的作用.结果表明,异步轧制硅钢板材表面形成了晶粒尺寸为10~50 nm,取向接近随机分布的纳米晶,而同步轧制板材的表面只形成了位错胞,证明异步轧制可以诱发表面纳米化.异步轧制板材表面纳米晶的形成过程为:在剪切力的反复作用下,高密度位错形成、滑移、湮灭和重组形成亚微米尺度的亚微晶/位错胞.随着压下量和轧制道次增加,高密度位错重复以上过程使晶粒尺寸减小、取向差增大,最终形成取向接近随机分布的纳米晶组织.大压下量和多道次是异步轧制诱发板材表面纳米化的关键,而速比的增加可以加快纳米化进程. Surface nanocrystallization(SNC) can effectively enhance the surface and global properties of the metallic materials,such as microhardness,intensity,fatigue,wear and corrosion resistances,therefore provides more promising practical industrial applicability.Up to now,several SNC treatment methods were developed based either on the principles of ball impactions or friction sliding,however,difficulty still exists for the surface treatment of large-dimensional samples with high efficiency.Recently,m... 

利用光学显微镜（OM）和扫描电镜（SEM）研究了不同稀土Ce含量的50W470无取向硅钢的铸坯、热轧板和冷轧退火板的宏观和微观组织，并采用磁性能测试仪测定其磁性能。结果表明：当稀土Ce的加入量从0增加到66×10^-6（质量分数）时，铸坯的柱状晶平均宽度从3.82 mm减小到3.24 mm,等轴晶率从43.1%增加到51.3%;热轧板的平均晶粒尺寸逐渐增加，从26.2μm增加到33.3μm,再结晶百分数从24%增加到37%;退火板的平均晶粒尺寸从36.2μm增加到39.3μm;磁性能测试表明，微观组织的变化有利于50W470无取向硅钢铁损降低和磁感提高。 Macro-structure and microstructure of as-cast plate, hot rolled plate and cold rolled annealed plate of 50 W470 non-oriented silicon steel with different rare earth Ce content was studied by optical microscope（OM） and scanning electron microscopy（SEM）, and their magnetic properties were measured by magnetic property tester. The results show that when the addition amount of rare earth Ce increases from 0 to 66×10^-6（mass fraction）, the average width of columnar crystal of the as-cast pl... 

【作者】 潘恒韬； 欧阳帆； ...

本实用新型涉及一种硅钢片抓取平台，其包括抓取框架，包括抓取框架，所述抓取框架上设有多个支架，对应于非切割区域的支架上设有大真空吸盘，对应于切割区域的支架上设有小真空吸盘。本实用新型结构简单，通过多个真空吸盘来进行硅钢片的抓取也不会损坏加工后的硅钢片，还提高了硅钢片的搬运效率。此外，通过气动系统实现对吸盘的自动吸气，提高了对吸盘操作的便利性。

本实用新型公开一种稀土永磁变频电机加工硅钢片冷却装置，包括左、右间隔设置的悬架端杆；悬架端杆之间装配连接有若干个前后间隔设置的硅钢片卷料收卷部件，硅钢片卷料收卷部件均包括转动连接在悬架端杆上的旋转座，旋转座之间固定连接有若干个折形搭料杆，折形搭料杆包括横杆部，所述横杆部的左右两端均具有一体成型的折形端，折形端均固定连接在旋转座上；硅钢片卷料收卷部件之间通过传动部件传动连接；上述装置还包括若干个装配连接在悬架端杆顶部之间的风冷部件。采用上述装置部件设计实现对热处理加工的硅钢片快速卷绕，并且卷绕收卷过程中快速对物料进行冷却，有效提高了加工过程中硅钢片物料的冷却、收卷效率。

【作者】 潘恒韬； 刘涛； ...

本实用新型公开了用于变压器铁芯硅钢片的叠片翻转支架，包括槽板，所述槽板内部卡装有转板，转板两侧对称安装有卡杆，槽板底部安装有风扇；所述转板另外两侧对称安装有放置槽，放置槽底部卡装有电磁铁，转板两侧皆设置有两组开关；在开关不受到压力时，此时开关所在电路处于通电状态，开关与电磁铁为电性连接，每个开关独立控制一组电磁铁，电磁铁处于工作状态，电磁铁正常运行产生的磁吸力，使得铁芯硅钢片固定在放置槽内，在使用机械臂取用铁芯硅钢片时，机械臂底部连接的触发条持续压迫开关，此时开关所在电路处于断路状态，开关所控制的相应电磁铁不产生磁力，机械臂可以较为容易的取用铁芯硅钢片。

本实用新型提供了一种无取向硅钢涂层喷涂装置，属于冶金行业涂层技术领域，包括上涂辊和下涂辊，所述上涂辊一侧设有上喷淋管，下涂辊一侧设有下喷淋管，在上涂辊和下涂辊间的水平面上方设置一个倾斜挡板，所述上喷淋管对准倾斜挡板，下喷淋管对准下涂辊，所述下涂辊下方设置一个涂液收集槽，下涂辊部分置于涂液收集槽中，涂液收集槽底板设有涂液回流口，所述涂液收集槽通过一个升降装置调节自身高度。该装置稳定性好，可靠性高，能够有效保证无取向硅钢下表面涂层质量，避免出现漏涂或者涂层条纹缺陷，提高无取向硅钢涂层质量。

本实用新型公开了一种用于硅钢件的高效激光焊接机，涉及激光焊接机技术领域。本实用新型包括机体、底座和控制柜，底座上表面固定安装有工作平台，机体上表面设置有转动盘，转动盘上表面设置有焊接臂，焊接臂一端设置有连接头，连接头下表面设置有焊接头，焊接头、连接头和焊接臂均与机体电性连接，焊接臂一端设置有转动轴，转动轴一端固定连接有过渡仓，过渡仓一端设置有抽风机，过渡仓另一端设置有出风口，出风口通过过渡仓与抽风机相连通。本实用新型通过在焊接臂一端设置抽风机对着工作平台，将焊接产生的浓烟进行吸收并通过出风口排出避免对人体健康产生影响，通过设置具有防火花和强光功能的防护罩对工作人员的眼睛提供保护作用。