硅钢资料

通过实验室25 kg真空感应炉冶炼和锻轧研究了0.26%～0.95%Al含量对0.5 mm 2.2%Si无取向硅钢冷轧板组织、织构和磁性能的影响。试验结果表明,0.26%～0.81%Al含量时,随钢中Al含量的增加,成品退火钢板的晶粒尺寸增加同时铁损减少;当Al含量大于0.81%时,随Al含量增加,钢板的晶粒尺寸减小,同时铁损增加。Al含量对硅钢板磁感的影响没有明显的规律。2.2%Si无取向硅钢的合适Al含量为0.48%～0.81%。 The effect of 0.26%～0.95%Al content on structure,texture and magnetic performance of 0.5 mm cold rolled sheet of 2.2%Si non-oriented silicon steel has been studied by a 25 kg vacuum induction furnace smelting,and forging -rolling in laboratory.Results show that as 0.26%～0.81%Al,with increasing Al content in steel the grain size of annealed finished sheet increases while iron loss of sheet decreases,and as Al content in steel is more than 0.81%,the grain size of sheet decreases while iron loss in... 

本实用新型公开了一种硅钢片二次搭接夹具，包括底座、位于底座顶部的调节板以及位于调节板顶部一端的固定杆，所述底座包括设置在底座内部顶端中间位置处的活动槽。本实用新型通过连接块将第一夹钳与第二液压缸的输出端相连接，通过第一夹钳和第二夹钳对硅钢片进行固定，将焊条焊接在一组硅钢片上，伺服电机带动调节杆发生转动，调节杆外侧的外螺纹和活动块内部的螺纹孔相互配合，可使活动块在活动槽内部发生活动，通过活动块带动调节板发生前后移动，从而使对硅钢片进行前后一端，通过滑轨使调节板的移动更加稳定，使两组硅钢片相对齐，通过固定块使第一液压缸带动调节架左右移动，使焊条与两组硅钢片紧密接触，实现二次搭接。

本发明提供了一种超高磁感无取向硅钢及其制造方法和在汽车发电机生产中的应用，成分：C：≤0.005％、Si：0.5‑1.2％、Mn：0.1‑0.5％、P：0.01‑0.1％、S：≤0.004％、Al：≤0.005％、N：≤0.005％、Ti：≤0.003％，余量为铁和不可避免的杂质。通过成分设计，配合CSP薄板坯连铸连轧工艺、常化工艺，不用添加贵金属元素，不添加贵金属元素，流程短、成本低、磁感高、性能稳定；节省成本的同时，具有优良的磁性能，采用本发明生产的汽车发电机铁芯，与常规产品生产的铁芯相比，重量可减轻15％以上，缩小了发电机尺寸，满足汽车发电机小型化、高效化的要求。

本实用新型公开了一种变压器硅钢片卷吊装件，包括横梁和两个吊钩组件，在横梁两端之间的中部设置有吊挂连接构件；两个吊钩组件呈左右对称设置于横梁，吊钩组件与横梁滑动连接，在吊钩组件与横梁之间设置有第一锁紧机构，横梁通过吊挂连接构件与吊机上的吊索连接，在对不同宽度的硅钢片卷进行吊装时，松开两个第一锁紧机构，调节好其中一个吊钩组件的位置，并锁紧固定好，使得固定好的吊钩组件插入硅钢片卷其中一端内，最后将另外一个吊钩组件插入硅钢片卷另一端内，并锁紧固定，本实用新型通过两个吊钩组件来勾住硅钢片卷的两端，可避免硅钢片卷在起吊过程中损坏卷边，也可满足不同宽度的硅钢片卷的吊装。

本实用新型公开了硅钢片铁芯叠片机构，包括送料装置和叠片装置，送料装置包括有磁性传送带、送料件和第一定位杆，磁性传送带用于将已剪切的硅钢片传送至送料件，送料件安装于磁性传送带的下方，并且可沿磁性传送带的正交方向平行伸出，第一定位杆安装于送料件上，用于定位硅钢片，叠片装置设置于送料件的伸出的一方，包括有叠放台、第二定位杆和机械手，叠放台用于叠放硅钢片，第二定位杆用于定位硅钢片，机械手用于将送料件的硅钢片搬运至叠放台上，机械手包括有转动臂和取料单元，取料单元安装于转动臂的端部，包括有电永磁铁，电永磁铁用于吸取硅钢片。根据本实用新型的硅钢片铁芯叠片机构，可有效提高叠片速度，降低能耗，提高生产效率。

本实用新型公开了一种变压器铁芯用硅钢片成型铁测量平台，包括游标测量尺及定位台；定位台包括基架、操作台及至少两根的定位销，操作台I及操作台II分别设置于基架的横向两端，且操作台I及操作台II之间留有宽度a的间距区，操作台II上设置有至少一组的沿横向均匀分布的定位孔组，且至少两根的定位销能够与该定位孔组的定位孔配合，游标测量尺设置于基架上间距区处。在操作台II上设置有至少一组的沿横向均匀分布的定位孔组，且至少两根的定位销能够与定位孔配合，以将该硅钢片成型铁定位区域限定在操作台II台面上，采用多个定位孔和定位销配合结构，同时能够沿横向调整硅钢片成型铁定位位置，以便测量各个区域尺寸。

本实用新型公开了一种硅钢环形炉台车用垫片，垫片为多个陶瓷纤维高密度板拼接而成的环状，垫片的内边缘和外边缘均呈正八边形；陶瓷纤维高密度板的导热系数不大于0.15W/(m·k)。上述垫片在实际使用时，铺设于台车的底座，并在垫片上砌筑耐火砖，最后在耐火砖上浇筑耐火浇注料。因垫片的导热系数很低，因此能够减少台车底座背面热量的散失，并且能够避免高温对台车内钢卷造成影响，保证了钢卷的质量。因此，本实用新型提出的硅钢环形炉台车用垫片，对台车进行了改进，保证了钢卷的品质，解决了现阶段该领域的难题。

通过热力学计算,分析了实验钢中主要析出物析出的可能性。结果表明:在液相和固液两相区中,AlN和MnS均不能析出;在奥氏体区,AlN和MnS具备热力学析出条件,平衡析出温度分别为1547、1582 K。成品退火板中的析出物主要为AlN和MnS。扫描电镜下观察到的AlN形貌多为长条状,MnS形貌多为棒状或近似球形。这两种析出物占了析出物总量的85%以上,尺寸集中分布在400~800nm;复合析出物主要是(Al2O3+MnS)和(AlN+MnS),形貌不规则,尺寸集中在0.7~1.5μm;透射电镜下观察到了少量100nm以下独立的AlN析出。 According to thermodynamic calculation, the precipitation probability of precipitates was analyzed, AlN and MnS can not precipitate in liquid phase area and solid-liquid two-phase area. In austenite area, both the AlN and MnS have precipitation condition in thermodynamics and precipitates at 1547 K and 1582 K, respectively. The precipitates in annealing plate are mainly AlN and MnS. The shape of AlN is mostly strip, and MnS is stick or near sphericity. They accounted for over 85% of the total qu... 

研究了采用高温卷取热轧态原料和常化态原料生产高牌号冷轧无取向电工钢组织、织构和磁性能。研究发现钢卷采用750℃高温卷取,下线后立即采用\"保温罩\"对钢卷进行保温,时间96h,然后空冷至100℃时上线生产的工艺可取代常化工艺生产高牌号冷轧无取向电工钢。冷轧上线前,热轧态原料的表层为大量的再结晶组织,这部分组织包括了热轧轧制时保留下来的动态再结晶组织,钢卷本身高温回复后产生再结晶晶粒,以及在保温罩内保温时形成的再结晶组织。高温卷取的热轧态和常化态的热轧卷作为原料时,试样织构类型相似,取向分布密度接近,再结晶后织构类型仍然相似,取向分布密度仍然接近。Goss织构对磁性能增加有促进作用。实验钢中较好的磁性能对应的织构[{100}+Goss]/{111}的比值较高,体现了织构的遗传性。 Microstructure,texture and magnetic properties of high grade cold rolled nonoriented electrical steel which made of hot rolled material with high temperature coiling and with normalization were studied.Steels coiled in high temperature(at 750 ℃),stacked with insulation cover for 96hand air cooled to 100 ℃ were using to manufacture high grade nonoriented electrical steel.The process can replace the normalization process.There are a lot of recrystallized grains in the surface layer of the coil wit... 

本发明公开了一种新能源汽车驱动电机用低铁损高强度无取向电工钢及其制造方法，所述无取向电工钢的化学成分及重量百分比包括C：0.001‑0.005％、Si：2.4‑3.0％、Mn：0.25‑0.5％、Al：0.70‑1.10％、P：≤0.02％、S：≤0.005％、0.015％≤Ce+Sn≤0.035％，余量为铁和不可避免的杂质，本发明通过加入Ce和Sn，净化钢质、微合金化提高无取向电工钢强度和磁性能，不需要添加固溶金属元素，且避免了高Si体系下的轧制困难问题，且不需要高温退火，解决了退火温度过高使晶粒异常长大，晶粒尺寸均匀性降低的问题，生产出的无取向电工钢具有较高强度的同时，还具有优良的磁性能。

本发明公开了一种含铝无取向硅钢中残余元素的控制方法。工艺流程包括KR脱硫‑转炉冶炼‑RH处理‑连铸。转炉控制合理的炉料结构，采用多渣吹炼，挡渣出钢。所用废钢中Ti、V、Nb等残余元素的质量分数之和≤0.005％，废钢和铁水的比例为0.2‑0.3。转炉吹炼终点炉渣成分中Ti、V、Nb等残余元素的氧化物含量之和为0.1‑0.5％，出钢后钢包顶渣厚度为50‑60mm；RH脱碳、脱氧、合金化后，净循环时间≤5min。通过本发明的实施，含铝无取向硅钢成品中Ti、V的含量≤0.002％，Nb含量≤0.001％，硅钢的磁性能显著提高。

利用本钢技术中心试验厂技术手段,并与北京钢铁研究院合作,试制了用作家电用电机、微电机、小电机或部分中型电机铁芯的冷轧无取向电工钢。试制钢硅含量小于0.5%,钢板表面平滑,公称厚度0.5mm,且厚度均匀偏差小,性能测定结果表明,产品的磁性能、力学性能满足其使用要求。 BX STEELTechnology Center pilot plant using technical means,and with Beijing Iron and Steel Research Institute,trial cold rolled non-oriented electrical steel that has been used as appliance motor core,micro motor core,small motor core,or part of the medium-sized motor core。Trial steel of silicon content is less than 0.5%,steel plate surface is smooth,the nominal thickness of 0.5mm,and the thickness deviation is small,performance measurement results show that the magnetic properties,mechanical p...