结合工业化生产过程中出现的同卷带钢头、尾磁性能差异现象,对50SW1300牌号无取向硅钢同卷带钢头、尾试样的夹杂物、晶体织构和显微组织进行了分析研究。结果表明,夹杂物、晶体织构是影响成品钢卷磁性能的重要因素。夹杂物是造成同卷带钢头、尾铁损差异的主要原因。夹杂物数量越多,尤其是小尺寸的夹杂物数量越多,对成品带钢的磁性能影响越大,对于本试验而言,AlN和MnS是影响成品带钢磁性能的主要夹杂物。晶体织构是造成同卷带钢头、尾磁感应强度差异的主要原因。有益的{100}和Goss织构含量越大,有害的{111}<110>和{111}<112>织构含量越小,即有益织构与有害织构含量比越大,成品带钢的磁感应强度越大。 Based on the industrial manufacture of non-oriented silicon steel sheets 50SW1300, the magnetic property variation of head and tail of the same finished steel sheets was discussed by analyzing non-metallic inclusion, crystal texture, and microstructure. Results show that, both of the non-metallic inclusion and the crystal texture will affect the magnetic properties significantly. The non-metallic inclusion is the key factor of the core loss variation of head and tail of the same finished steel s... 

介绍了CSP工艺生产无取向电工钢各工序的设备特点、采用的工艺控制手段和电工钢产品质量情况,结合生产实践证明了马钢CSP工艺开发的无取向电工钢产品丰富了薄板坯连铸连轧的品种结构,发挥了薄板坯连铸连轧生产无取向电工钢性能均一、稳定的特点。 The equipment characteristic,the process control method and the quality of non-orientated silicon steel by CSP process were introduced.Combined with the production situation,it is proved that production of non-orientated silicon steel developed on Masteel CSP line would enrich product structure of thin slab continuous casting and rolling,and it exerts stable performance of non-orientated silicon steel. 

【作者】 刘玲月； 李军辉； ...

结合实际生产0.4%Si无取向硅钢，统计了不含Sn和0.025%Sn无取向硅钢的磁性能变化，利用金相显微镜、X射线衍射仪观察分析不同成分下试样的显微组织和微观织构。试验结果表明：Sn元素可以显著降低无取向硅钢的晶粒尺寸，0.025%Sn试样的平均晶粒尺寸比不含Sn减小28.4%;加入Sn元素后抑制了无取向硅钢中不利于磁性能的{111}面织构组分强度，提高了对磁性能有利的{100}面织构组分强度，0.025%Sn与不含Sn相比磁感均值从1.756 T提升至1.768 T,铁损均值从5.476 W/kg降低至5.204 W/kg,明显改善了无取向硅钢磁性能。 In this paper combined with the actual production of 0.4% Si non oriented silicon steel, the magnetic properties of non oriented silicon steel without Sn and 0.025% Sn were counted. The microstructure and microtexture of samples with different compositions were observed and analyzed by metallographic microscope and X-ray diffraction. The results show that: Sn can significantly reduce the grain size of non oriented silicon steel, and the average grain size of 0.025% Sn sample is 28.4% smaller tha... 

本发明公开了硅钢片均衡堆垛分料系统，包括分料机构和接料机构，分料机构包括料架，料架上具有托板，托板两侧设有第一滚筒架，第一滚筒架顶部设有分料结构；分料结构可实现上下、水平移动；分料结构包括支撑架，支撑架上设有倒吸件；倒吸件包括磁块槽和挡料板，磁块槽设于挡料板上方，磁块槽底部设有磁块，磁块槽上方设有压料胶条，磁块槽和压料胶条可上下移动，接料机构的接料底座可平移，剪力臂架可升降，以改变第二滚筒架高度和水平位置。本发明的优点在于：通过分料结构的倒吸件吸附硅钢片，再将数个硅钢片同时放置于托板侧边数排滚筒上的放置板上，可实现多柱硅钢片的均衡堆垛，通过接料机构可进行多柱硅钢片的同时稳定出料，转运效率高。

本实用新型涉及一种硅钢片点数机，包括底座、分拣器、收拢器和输送器。其中，分拣器通过机架倾斜连接于底座上，用于分拣硅钢片，分拣器上设置有计数器，计数器依次计数分拣器分拣的硅钢片的数量。收拢器包括托盘和振动器，托盘设于分拣器的下方，用于承装分拣器分拣的硅钢片，振动器设于底座上，与托盘上硅钢片抵接，振动器振动能够将托盘上的硅钢片收拢整齐。输送器与底座和托盘相连，输送器工作能够带动托盘移动，以将托盘上的硅钢片输送至下一工位。本实用新型采用的是分拣清点的方式，事先无需摆放整齐，将每片硅钢片进行分拣计数，有效避免了摆放不整齐造成的计数不精确的问题。

利用DSC、XRD,结合热焓分析对硅钢级氧化镁和二氧化硅的固相反应行为进行了研究。比较了不同二氧化硅原料及混合方法对硅钢级氧化镁反应性的影响,找到了一种更为有效的硅钢级氧化镁反应性的评估方法,克服了传统柠檬酸活性法在比较不同厂家生产的氧化镁的反应性上的局限性。进一步研究了Na₂B₄O₇添加剂、TiO₂添加剂对氧化镁和二氧化硅反应行为的影响,结果表明,Na₂B₄O₇添加剂含量的增加对反应有利,而TiO₂添加剂对反应有阻碍作用。 The solid-state reaction behavior between silicon-steel grade MgO and SiO₂ was investigated by DSC and XRD combined with enthalpimetric analysis.The influence of different kinds of SiO₂ and different preparation methods were studied and a specifical measurement that is more reliable was proposed to evaluate reactivity of silicon steel grade MgO.It overcomes the limitation of the traditional citric acid activity（CAA） method,which can not be used to evaluate the reactivity of... 

以不断增长的薄板坯流程为背景,与传统流程对比分析了薄板坯流程无取向电工钢热轧晶粒组织特征;以50W800和50W1300钢为典型实例,探讨了两种流程下成品板晶粒组织、织构、磁性能及其磁时效行为的基体差异和相关原理。研究表明,薄板坯流程热轧板组织较粗大,有利于在成品板中获得粗大的晶粒和有利的织构,从而得到较低的铁损和较高的磁感。然而,薄板坯流程会造成第二相粒子的细小弥散分布与不充分析出,容易因磁时效而使磁性能恶化。 Based on the rapid development of compact strip production(CSP) processing,the characteristics of hot band grain structure produced by CSP processing were analyzed in comparison with those of conventional technology.The basic differences in grain size,texture,magnetic properties and the magnetic aging behaviors of the final sheet products produced by the two processing technologies and the corresponding principles were discussed,while steel 50W800 and 50W1300 were taken as examples.It is indicat... 

本实用新型公开了一种铁芯硅钢片卷料的上料装置，包括升降机构、固定座、转动执行机构和转动平台，所述固定座固定设置在地面上，所述升降机构相邻设置在固定座的一侧，所述固定座对立于升降机构的一侧设置有转动平台，所述转动平台的一端铰接设置在固定座上，且所述转动平台的另一端为自由端，所述转动平台在竖向面内朝向或远离于升降机构偏转，所述固定座上设置有转动执行机构，所述转动执行机构驱动转动平台转动；所述转动平台上的物料通过转动可位移至固定座和升降机构上，能够安全的、快速的将卷料转移至升降机构上，从而便于上料。

对应用动态加热进行短时温度退火的取向电工钢进行了二次再结晶研究。所进行研究的实验用取向电工钢是经过终冷轧和后续罩式退火后的一条工业化生产线生产的。研究结果表明,运用短时热处理条件可引起研究钢完全的异常晶粒长大。在实验室处理的材料的织构和金相组织与工业化生产的经过终退火而获得的相同的取向电工钢类似。但是,在实验室处理的取向电工钢的二次再结晶的矩阵中可观测到\"寄生\"晶粒。从磁性观点看,这些\"寄生\"晶粒含有不理想的{111}取向织构。 The present study was made to investigate secondary recrystallization in grain-oriented steels annealed at short time temperature exposures with application of dynamical heating.The investigated GO(Grain Oriented) steels for experiments were taken from one industrial line after final cold rolling reduction and subsequent box annealing.It was shown that application of short time heat treatment conditions could lead to complete abnormal grain growth in the investigated GO steel.The texture and mic... 

本发明涉及硅钢片横剪线技术领域，具体为一种用于硅钢片横剪线的冲孔和剪切的数控自动化车床，包括底座，底座的左侧上方与基座的底部上方设置有基座，基座的前侧中部设置有钢片辊，基座的右侧设置有凹槽，凹槽设置在底座内部，凹槽的左右两侧端部设置有齿轮，齿轮的外侧设置有皮带，凹槽的右侧上方设置有挡板，有益效果是：挡板的开口结构，使硅钢片自左向右经过挡板后，会处于底座上方正中间，方便调整硅钢片的水平位置，并使其可以准确进入夹板内部。通过弹簧的弹力作用，控制拉绳的位置，以此来实现拉绳带动夹块的关闭，使绕片筒在转动过程中，夹块可以将硅钢片的端部牢牢固定住。

本发明公开了一种硅钢片漆，该硅钢片漆采用特定的聚酰胺酰亚胺乳液制备，通过使偏苯三酸酐与组合形式的双端氨基化合物反应，添加三乙胺进一步提升反应进行的程度，并赋予整体更好的柔性和韧性，而磷酸三丁酯能够进一步通过物理改性改善体系的韧性，之后蒸出全部的有机溶剂，并添加一定量的水溶性有机溶剂，然后加入组合形式的活化剂，混合，再滴入水，形成稳定的乳液，最后添加双马来酰亚胺封端剩余的活性基团，该硅钢片漆不仅可以采用水作为主体溶剂，提升了环保型，而且还兼具耐高温、高粘结强度、电气性能强等优点，并有好的环境抗性与施工性能。