对西昌钢钒炼钢厂200 t BOF(顶底复吹)-RH-CC工艺生产50PRW800无取向硅钢RH精炼过程中主要成份进行了分析。找出了目前工艺中影响钢液质量的主要因素是钢水脱氧处理不彻底,造成加入的部分硅元素烧损。操作工艺改为铝的脱氧即合金化操作一步完成,保证了钢水中氧处于一个较低的范围,从而减少对硅元素的烧损,提高合金收得率。 The factors of BOF-RH-CC process affecting the compositions of liquid steel were systematically investigated and studied of Xichang Steel and Vanadium Company. The main factors affecting the steel cleanliness were picked out. All results showed that the loss of silicon elements resulting from the deoxidization of liquid steel was not completely. It was suggested that the addition of aluminum for deoxidizing and alloying of molten steel was executed as one step in order to lower the oxygen potent... 

本发明涉及一种硅钢片铁芯用自动叠装系统，托板、上料单元、精定位单元、叠装单元、抓取单元，所述上料单元有一个，位于中部位置，所述精定位单元一共有两个，分别位于上料单元的两侧，所述叠装单元一共有两个，分别位于两个精定位单元的两侧，从而使得整个自动叠装系统由中间向两侧方向均依次为上料单元、精定位单元、叠装单元。本发明的优点在于：通过对上料单元、精定位单元、叠装单元的数量及排布位置进行重新设计，采用由中间向两侧供料的方式，使得两侧的上料顺序均独立运行，不存在相互干涉的风险，确保单侧的上料顺序的顺利进行，相对应的也就降低了程序设计的复杂程度，减轻了设计人员的工作强度。

为了弄清楚高硫硅钢中的硫化物析出行为及其对钢的微观组织和电磁性能的影响，以便为工业化生产制定更为合理的硫含量控制标准和采取更为有效措施减轻炼钢生产的硫含量控制压力，结合0.25% Si 无取向硅钢 ，采用非水溶液电解提取 + 扫描电镜/透射电镜观察相结合的方法 ，研究了0.006 8%、0.010 2%、0.025 5% 和 0.035 3% 硫含量条件下，钢中的硫化物夹杂物组成和存在形式及其形貌、种类、尺寸、数量变化，以及相应的热轧、成品试样的微观组织和电磁性能变化。结果表明，随着钢中硫含量的增加，钢中的硫化物逐渐由 MnS→MnS+Cu₂S→Cu₂S转变，数量逐渐增多，尺寸向高低两个方向发展。相应地，导致热轧再结晶组织劣化和抑制了成品晶粒尺寸长大。随着钢中硫含量的增加，钢的磁感、铁损劣化程度逐渐增大。钢中的硫含量平均每增加 0.01%，涡流损耗、磁滞损耗分别劣化0.24 W/kg 和 0.41 W/kg，而磁感会劣化 0.009 T。但是 ，在硫含量为 0.010 2% 时 ，铁损可以低于 6.0W/kg，而在硫含量为 0.025 5% ... In order to find out the precipitation behavior of sulfide inclusions and the corresponding changes of microstructure and electromagnetic properties of high sulfur silicon steel sheets, so that to design more suitable sulfur concentration controlling limit for industrial manufacture and to release the steel-making difficulty effectively, Based on the change of given sulfur concentration 0.006 8%, 0.010 2%0.025 3% and 0.035 3%, the type and composition, the size and number, and the size distribut... 

本发明特别涉及一种控制边部翘皮的热轧电工钢的生产方法和生产系统，属于钢表面质量检测技术领域，方法包括：建立热轧电工钢边部翘皮的数据库，数据库包括翘皮类型及各翘皮类型的翘皮发生原因和翘皮发生的区域；对待质检的热轧电工钢表面进行识别，并对比数据库，获得待质检的热轧电工钢表面翘皮的翘皮类型；根据待质检的热轧电工钢表面翘皮的俏皮类型获得该类型翘皮的翘皮发生原因和翘皮发生的区域；根据翘皮发生原因和翘皮发生的区域，调整生产操作，用以减少热轧电工钢的边部翘皮；通过对边部翘皮进行准确分类及识别，能够准确的分辨出边部翘皮的产生原因，采取有针对性的措施防止缺陷扩大，最大程度的降低缺陷发生量，提高质量控制水平。

通过制备磷酸二氢铝硅钢涂层,研究了氧化锌对无铬涂层耐盐雾性能、电化学性能和附着性的影响。结果表明,硅钢表面涂层含有4.0%的氧化锌时,涂层具有最高的耐腐蚀性能和电化学性能,而且其致密表面最为平整,没有裂纹出现。 The effects of ZnO on the salt spray resistance property, electrochemical performance and adhesiveness of silicon steel insulating coating were studied. The results show that the best corrosion resistance and electrochemical properties can be obtained when the coating contains 4.0% oxide zinc, and the dense surface is smooth without cracks. 

【作者】 陶永根； ...

一种含Bi高磁感取向硅钢热轧带钢边部质量控制方法：炼钢；连铸；铸坯加热；粗轧，粗轧道次不低于4道次，各道次压下率控制在20~33%；规精轧及进行后工序。本发明通过对热轧工序的控制，能使热轧带钢边部开裂的尺寸降低至不超过5mm，且边部开裂≤2mm比率能达到95%以上，后工序切边量很少甚至无需切边即可进行冷轧，使产品成材率能比现有技术提高2~4%；且由于铸坯加热温度的降低使能耗也随之降低。

研究了CSP流程试制50W270高牌号无取向硅钢热轧→常化→冷轧→退火过程中织构的演变.利用电子背散射衍射技术对全流程织构进行测量和分析.发现热轧板织构在厚度方向上存在较大差异,表层主要为铜型、黄铜和高斯织构,1/4层存在微弱的高斯织构和旋转立方织构,中心层以γ纤维织构和旋转立方织构为主,还含有较弱的α纤维织构.与热轧板相比,常化板表层和1/4层织构变化不大,中心层旋转立方织构和α纤维织构增强.冷轧板各层均具有α纤维织构和γ纤维织构.与冷轧板相比,成品板各层中α纤维织构基本消失,还出现了立方织构和高斯织构. This article focuses on texture evolution in 50W270 high-brand non-oriented silicon steel produced by CSP in hot rolling,normalizing,cold rolling,and annealing processes.The texture in the whole process was measured and analyzed by electron back-scatter diffraction.It is found that the texture along the thickness direction in hot-rolled strips changes obviously;there are mainly copper,brass,and Goss textures in the surface layer;the 1/4 layer has weak Goss texture and rotating cube texture;γ-fib... 

本实用新型提供了一种变压器硅钢片吊装工具，属于变压器技术领域。其技术方案为：一种变压器硅钢片吊装工具，包括勾体，所述勾体上端设置有吊环，所述勾体下端设置有吊台，所述吊台上设置有阻挡机构，所述阻挡机构设置在所述吊台的底面。本实用新型的有益效果为：本实用新型通过勾体对硅钢片进行起吊，可以有效的防止硅钢片两端卷边，从而减少了变压器空载损耗，阻挡机构可以有效的防止硅钢片在运输过程中从吊台上摔落，从而保护了硅钢片的完整性，提高了使用效率。

本实用新型公开了一种带缓冲保护装置的硅钢片纵剪线，包括工作台，工作台的顶部外壁设置有放料辊，工作台靠近放料辊的一侧设置有牵引辊，工作台靠近牵引辊的一侧设置有整平机构，工作台的内部设置有第一缓冲坑，第一缓冲坑的顶部设置有导料辊，第一缓冲坑的内部设置有第三转轴，第三转轴的外壁传动连接有皮带，皮带的内壁传动连接有第二转轴，皮带的外壁传动连接有第一转轴，第三转轴的外壁固定安装有转筒，转筒的外壁设置有伸缩杆，伸缩杆的外壁套接有弹簧，伸缩杆的底部设置有滚珠，通过设置的第一缓冲坑与第二缓冲坑结构，可防止硅钢片在进入第一缓冲坑与第二缓冲坑时弯曲程度过大导致的断裂，且双重的缓冲装置更有利于对硅钢片的保护。

本发明公开了大型风电电机硅钢片自动装配系统，涉及机械生产技术领域。该发明包括硅钢片、自动导引运输车、硅钢片标准运输箱、机械手、吸盘夹具和大型风电电机转子；自动导引运输车与硅钢片标准运输箱插接配合；吸盘夹具设置在机械手末端；大型风电电机转子周圈地面粘贴电磁轨道；自动导引运输车与电磁轨道滚动配合。本发明通过设置好的程序，自动导引运输车沿着电磁轨道移动，到达程序设定工位，自动导引运输车自动停止，机械手开始动作，通过吸盘夹具上的真空吸盘吸取硅钢片，然后机械手将吸取的硅钢片移动装配位置，此时红外位置传感器再次精确定位，机械手对硅钢片的位置进行微调，位置调整好后，机械手完成最后的自动叠片步骤。

针对不同牌号的无取向硅钢产生结疤缺陷的难易程度和表面结疤缺陷的外形特征及分布规律,分析了该缺陷产生的原因。通过调整剪前导板的对中度,设置精轧侧导板开度余量及短行程数值,及时修补与更换侧导板,减少带坯与侧导板挤撞程度,有效地降低了结疤缺陷发生率。 This article analyses the cause of the scab defects according to the defects appearance characters and distribution law,degree of difficulty to form scar of non-oriented silicon steel. It can effectively decrease the scabs by different methods,such as adjusting the center line of guide plate,setting the opening margin and short stroke value of the side guide on finishing mill,timely repairing and replacing of side guide,decreasing the collision between the strip and side guide.