硅钢资料

试验研究了0.3 mm取向硅钢冷轧板(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005A1)的退火温度(760~880℃7 min)和退火时间(820℃3~9 min)对该钢的晶粒尺寸,再结晶和织构的影响。结果表明,最佳初次再结晶退火工艺为820℃5 min,该钢的平均晶粒尺寸为14.20μm,完全再结晶率为92%,不利{111}<110>结构含量为3.16%,有利织构{111}<112>,{012}<001>和高斯织构含量分别0.40%,4.73%和2.46%。 The effect of annealing temperature(at 760 ~ 880 X.for 7 min) and time(at 820℃ for 3~9 min) on grain size,recrystallization rate and texture of 0.3 mm cold-rolled sheet of oriented silicon steel(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005Al) has been tested and studied.Results show that with optimum recrystallized annealing at 820℃ for 5 min,the silicon steel average grain size is 14.20 fun,the complete recrystaUization rate is 92%,the unfavourable-texture {111}< 110 > content in steel is ... 

取向硅钢热轧板中织构梯度对发展完善的二次再结晶十分关键,通过添加铜可以显著降低取向硅钢板坯加热温度,从而影响热轧板织构分布。利用X射线衍射仪,分析了实验室模拟薄板坯连铸连轧(TSCR)工艺的3种不同铜含量的取向硅钢热轧板织构。结果表明:不同铜含量热轧板表面到厚度1/4处均为弱的热轧织构,热轧板心部主要为{100}面织构;铜含量约在0.4%时,热轧板次表层的{110}<001>织构比例最高,而热轧板心部的{100}<110>织构比例最低;铜含量对热轧织构中{114}<110>和{001}<100>织构发展有显著影响。 The texture gradient in hot rolled grain oriented silicon steel strip is one of the essential factors to achieve a perfect secondary recrystallization.The addition of copper can significantly reduce the slab reheating temperature of grain oriented silicon steel,so as to impact the texture distribution in the hot rolled strip.The texture of hot rolled grain oriented silicon steel strip as-rolled by thin slab casting and rolling process(TSCR) in laboratory with three different copper contents was ... 

一种电工钢切片用辅助定位装置，涉及电工钢加工技术领域，包括加工台、支撑腿、定位块、侧板、滑杆、移动板、顶板、滑动架、伸缩杆、切片装置、定位杆和挡板；支撑腿设置在加工台底部；定位块设置有两组，两组定位块均设置在加工台上，两组定位块沿横向分布，每组定位块设置有两个，每组的两个定位块沿纵向分布；侧板设置有两个，两个侧板均设置在加工台纵向一侧，两个侧板沿横向分布；滑杆设置在两个侧板之间；移动板沿横向滑动设置在滑杆上；顶板设置在移动板靠近加工台的纵向一侧，顶板位于移动板上端。本实用新型能够方便工作人员切割出一定尺寸的电工钢切片，且切割精度很高。

本发明涉及一种提高取向硅钢冷轧加工性的生产方法，工艺流程为：冶炼、连铸、热轧、常化、酸洗、冷轧、脱碳渗氮、涂MgO、高温退火、涂绝缘层及热拉伸平整；粗轧中坯厚度35‑45mm，两段常化后进行带钢横向分段式冷却水分布。本发明通过对热轧中坯厚度、终轧温度及卷取温度，常化冷却水量及控制方式的调控，使轧前表层晶粒尺寸降低5‑10μm、珠光体体积分数降低6％，轧材冷轧加工性明显改善、成材率可提高8％以上。通过后续冷轧、脱碳退火和高温退火等工序处理，可保证完善的二次再结晶组织及良好磁性能。

针对节能电机对无取向电工钢在磁性能方面的特殊要求,采用普通W600牌号的热轧板为原料,通过大量的现场工艺试验,研究总结出了\"超低张力\"的运行工艺、\"先快后慢\"的加热工艺、\"先湿后干\"的退火脱碳工艺、\"先缓后急\"的冷却工艺,生产出P1.5/50≤4.0 W/kg、B50≥1.70 T的冷轧电工钢产品,满足了节能电机的要求。 Based on the special requirements of no-oriented electrical steel for saving energy motor in magnetic aspects,using common W600 brand of hot rolled plate as raw material,through a large number of real tests,an ultra-low tension process,heating process which was quick at first and then slow,annealing decarburization process which was dry after the first wet,and a cooling technology of \"slow after the first urgent\" were concluded.Electrical steel product with P1.5/50≤4.0W/kg,B50≥1.70T was produced... 

本实用新型涉及卷绕机技术领域，具体为一种双条硅钢片铁芯卷绕机，包括转盘，用于驱动转盘旋转的电机，固设于转盘顶端中心上的铁芯型模，以及两个分立于铁芯型模的两侧且通过第一推力轴承转动连接转盘的转轴；转轴上套设有带盘，带盘上成卷绕制有硅钢片，且两个带盘上的硅钢片关于铁芯型模的中心呈中心对称分布，带盘的旋转方向与转盘的旋转方向相同。本实用新型通过两个带盘上的硅钢片同时卷绕在一个铁芯型模上，并使两个硅钢片的薄厚边叠加，弥补硅钢片的自身偏差对铁芯造成的影响，从而保证了铁芯性能的稳定性，并使铁芯卷绕速度增加一倍，提高了生产效率。

采用SEM、EDS和XRD对不同加热温度下W470连铸坯氧化铁皮的微观形貌及相结构进行研究。结果表明,W470氧化铁皮难以除去的原因是氧化铁皮熔化,液相包裹着FeO,凝固时发生共晶反应,生成FeO/Fe2SiO4共晶混合物,并深嵌入基体。降低加热炉的加热温度,使连铸坯全程在FeO/Fe2SiO4共晶混合物熔点(1177℃)以下加热,可降低氧化铁皮与基体的结合力,能够有效解决W470除鳞困难问题。 The microstructure and phase structure of iron scale of W470 continuous casting billet at different heating temperatures were investigated by SEM,EDS,and XRD.The results show that the reason why the iron scale of W470 removes hardly is that iron scale is melted and the FeO is surrounded by the liquid phase,which forms FeO / Fe2SiO4eutectic mixture and is embedded into the matrix after solidification.Lowering the heating temperature and keeping the continuous casting billet heating under the melt... 

对西昌钢钒炼钢厂200 t BOF(顶底复吹)-RH-CC工艺生产50PRW800无取向硅钢RH精炼过程中主要成份进行了分析。找出了目前工艺中影响钢液质量的主要因素是钢水脱氧处理不彻底,造成加入的部分硅元素烧损。操作工艺改为铝的脱氧即合金化操作一步完成,保证了钢水中氧处于一个较低的范围,从而减少对硅元素的烧损,提高合金收得率。 The factors of BOF-RH-CC process affecting the compositions of liquid steel were systematically investigated and studied of Xichang Steel and Vanadium Company. The main factors affecting the steel cleanliness were picked out. All results showed that the loss of silicon elements resulting from the deoxidization of liquid steel was not completely. It was suggested that the addition of aluminum for deoxidizing and alloying of molten steel was executed as one step in order to lower the oxygen potent... 

为探究铬、锰元素及退火温度对高强无取向硅钢性能的影响规律,借助OM、SEM、EBSD与万能拉伸试验机等分析不同制造工艺下3组不同含量铬、锰元素的无取向硅钢热轧、常化及退火处理后组织与性能。结果表明,试验钢热轧后组织不均匀,心部为沿轧向分布纤维状组织,边部为少量再结晶晶粒,常化处理能显著改善热轧板组织均匀性,消除热轧板中心部位的纤维状组织。经冷轧及退火后得到多边形铁素体晶粒,其中960℃退火,晶粒尺寸偏大,有利织构{100}组分体积分数减少,不利织构{111}组分体积分数增加,成分为0.2Mn-1Cr的1号试验钢960℃退火后铁损最大,磁感强度偏小;成分为0.5Mn-1Cr的2号试验钢930℃退火后,磁性能与强度等综合性能最佳,工频铁损P_1.5/50为2.41W/kg,高频铁损P_1.0/400为17.36W/kg,磁感应强度B_{5 000}为1.638T,抗拉强度为685MPa。 In order to study the effect of Cr,Mn and annealing temperature on the properties of high-strength non-oriented silicon steel,the microstructure and properties of three groups of non-oriented silicon steel with different Cr,Mn content under different manufacturing processes were analyzed by means of OM,SEM,EBSD and universal tensile tester.The results show that the structure of experimental steel is not uniform after hot rolling,and the core is distributed in fibrous structure along the rolling ... 

采用传统的轧制和退火工艺制备了0.30mm厚的6.5%(质量分数)Si高硅电工钢薄板,采用X射线衍射技术对退火过程中的再结晶织构进行了研究。冷轧高硅钢薄板700℃退火形成以{111}〈112〉为峰值的γ织构(〈111〉∥ND)和以{001}〈210〉为峰值的{001}织构;而900℃以上温度退火则形成强{001}〈210〉织构。进一步的研究表明是在晶粒长大过程中{001}〈210〉发展成为主要再结晶织构组分。 High silicon steel thin sheets with thickness of 0.3mm were successfully produced by conventional rolling and annealing methods.Recrystallization texture was investigated by means of X-ray diffraction.It is found that recrystallization texture is mainly composed of γ fiber(〈111〉∥ND)with peak at {111}〈112〉 and {001} fiber with peak at {001}〈210〉 after annealing at 700℃,while strong {001}〈210〉 component dominates recrystallization texture after annealing above 900℃.It is during grain growth that {... 

本发明属于冶金技术领域，具体涉及一种基于纳米析出强化制备高强度无取向硅钢的方法。该无取向硅钢包括如下重量百分比的化学成分：Si2.5～4.5wt.％，Ni2.5～6.5wt.％，Al1.0～3.0wt.％，Mn0.1～1.0wt.％，Cu0～1.0wt.％，(C+N+O+S)≤100ppm，其余为Fe；该无取向硅钢的制造方法包括：真空冶炼、浇铸锻造及热轧加工(或者薄带连铸)、常化热处理、酸洗与冷轧加工、再结晶退火、时效热处理。本发明制备的新能源汽车驱动电机转子用高强无取向硅钢厚度为0.20～0.50mm，磁感应强度B50为1.60～1.70T，P10/400为10～31W/kg，屈服强度Rp0.2为700～1000MPa，抗拉强度Rm为740～1150MPa，延伸率A为8～20％，可以满足用户对新能源汽车驱动电机用无取向硅钢性能要求。

本发明公开了一种硅钢轧制系统，包括：轧机组，所述轧机组包括M架轧机，用于轧制硅钢，所述M架轧机的前N架轧机的轧辊为高速钢轧辊，其中，M、N为正整数；硅钢检测装置，位于所述轧机组最后一架轧机的出口处，用于对出口硅钢的参数信息进行检测；控制器，与所述硅钢检测装置通信连接，用于在所述参数信息不满足预设参数条件时，控制所述轧机组停止工作；磨床，用于在所述轧机组停止工作后，对所述N架轧机中的每架轧机进行辊形精度检测，对不满足预设辊形精度范围的轧辊进行磨削。