硅钢资料

采用自主研发的脉冲磁场退火装置，在取向硅钢脱碳退火过程中分别施加不同强度的磁场，并采用光学显微镜和X射线衍射仪研究了脉冲磁场脱碳退火后试样的显微组织和宏观织构。结果表明，脱碳退火过程中施加脉冲磁场后取向硅钢的平均晶粒尺寸均增加，当磁场强度为40 mT时，平均晶粒尺寸最大，为13.06μm。此外，取向硅钢试样的立方织构{001}<100>强度减弱，高斯织构{110}<001>和{111}<112>织构增强，有利于获得更好的成品织构和磁性能。 Self-developed pulsed magnetic field annealing device was used to apply magnetic field of different intensities during decarburization annealing of an oriented silicon steel, and microstructure and macro-texture of the specimens after decarburization annealing in a pulsed magnetic field were studied by using optical microscope and X-ray diffractometer. The results show that the average grain size of the oriented silicon steel increases with the application of pulsed magnetic field during decarbu... 

【作者】 姚昌国； ...

在15 kg真空感应炉上,用CaO-Al2O3-SiO2-MgO渣系进行脱硫试验,探讨了脱硫渣系碱度、MI、Al2O3、CaF2对脱硫效果的影响。研究结果表明,随脱硫渣系碱度、MI、Al2O3和CaF2含量的增加,脱硫率都呈现先增加后减少的趋势。初始硫含量为0.009 33%~0.010 73%,加入脱硫渣系4 min时间内表观脱硫速率为(0.000 96~0.001 49)%/min,平均脱硫率为81.2%,最高达86.8%。当脱硫渣中w(CaO)=58.15%、w(SiO2)=4.85%、w(Al2O3)=25%、w(MgO)=6%、w(CaF2)=6%,脱硫效果最好,此时钢液中硫为0.001 33%。 Experiments on desulfurization of molten steel using CaO-Al2O3-SiO2-MgO based desulfurization slag was carried out in a 15 kg vacuum induction furnace. The effects of desulfurization slag basicity,MI, Al2O3and CaF2on desulfurization of molten steel were studied. The results show that with the increase of basicity,MI,Al2O3or CaF2in desulfurization slag,the desulfurization rate rises initially and then decreases. In addition,as the initial sulfur content is 0. 009 33% ~ 0. 010 73%,the apparent des... 

取向硅钢热轧板中组织、织构梯度对发展完善的二次再结晶十分关键,通过对2种不同热轧工艺生产取向硅钢的组织、织构进行研究,结果表明:采用后道次大压下热轧工艺时热轧板表层再结区晶粒平均尺寸增加,再结晶区厚度增加,高温退火后二次晶粒尺寸减小;采用后道次大压下热轧工艺热轧时,热轧板中平均等效应变高,热轧板厚度心部{100}〈011〉和{100}〈001〉位向取向强度降低,({111}～{113})〈110〉位向取向强度提高,高温退火后{110}〈001〉位向偏离角降低,磁性能提高。 The texture and microstructure gradient in hot rolled grain oriented silicon steel strip was one of the essential factors to achieve a perfect secondary recrystallization.The texture and microstructure of grain oriented silicon steel strip as-rolled with two different hot rolling parameters was investigated.The results show that with big reduction at the end rolling process,the intensity of {100}〈011〉 and {100}〈001〉 orientation reduces with({111}-{113})〈110〉 orientation intensity enhanced in hot... 

本发明是高磁感取向硅钢的脱碳退火工艺，首先对硅钢卷进行放卷、活套、清洗；再对硅钢进行脱碳、渗氮处理，氨气流量6‑20m3/h、加湿槽温度30‑70℃，脱碳温度780‑880℃、机组速度45‑75m/min、气氛中氢气比例20‑60％、氮气比例40％‑80％，然后冷却到常温；对硅钢进行活套；再对硅钢进行涂覆氧化镁，涂覆量4‑10g/㎡；最后对硅钢进行干燥和收卷成硅钢卷；通过本发明对高磁感取向硅钢的脱碳退火工艺流程进行了优化设计，调整了脱碳退火工艺中氨气流量、气氛、加湿槽水温等参数，优化了高磁感取向硅钢中碳元素、氮元素和氧元素的含量，最终使高磁感取向硅钢实现稳定的性能，磁感达1.92T。

对低温加热工艺生产的普通取向(common grain-oriented,CGO)硅钢的高温退火过程进行了中断实验,材料为含3.0%Si、0.5%Cu、0.009 8%S(均为质量分数)的以Cu2S为主抑制剂的普通取向CGO钢。原始板坯厚度为230 mm,于1 200℃均热后经4道次粗轧、7道次精轧至2.3mm;热轧板采用两次冷轧法轧至0.3mm,中间完全脱碳退火,最后于1 200℃高温退火。最后样品的磁性能:铁损P17/50为1.182W/kg,磁感应强度B8为1.897T。借助配有EDAX OIM电子背散射衍射(EBSD)系统的ZEISS SUPRA 55VP扫描电子显微镜,对高温退火过程中高斯晶粒的演变进行了研究,结果表明:升温过程中晶粒尺寸增长缓慢,650℃时取向分布函数(ODF)图出现高斯织构组分,但强度很弱,高斯晶粒偏离角小于9°;950℃时高斯晶粒平均生长速度超过其他晶粒;950~1 000℃时高斯晶粒异常长大,偏离角降至约3°;在950℃之前高斯取向晶粒相比于其他晶粒没有尺寸优势。 The high-temperature annealing process of common grain-oriented(CGO)silicon steel was investigated by interrupting test.The samples were rolled from CGO silicon steel slab under low reheating temperature.The CGO silicon steel,taking Cu2S as the main inhibitor,contains3.0%Si,0.5%Cu,and 0.0098%S.The original casting slab is 230mm in thickness.After 1 200℃reheating,four-pass rough rolling and seven-pass finish rolling were conducted to make the thickness of the slab get to 2.3mm.Then the hot rolled... 

采用传统的轧制和退火工艺制备了0.30mm厚的6.5%(质量分数)Si高硅电工钢薄板,采用X射线衍射技术对退火过程中的再结晶织构进行了研究。冷轧高硅钢薄板700℃退火形成以{111}〈112〉为峰值的γ织构(〈111〉∥ND)和以{001}〈210〉为峰值的{001}织构;而900℃以上温度退火则形成强{001}〈210〉织构。进一步的研究表明是在晶粒长大过程中{001}〈210〉发展成为主要再结晶织构组分。 High silicon steel thin sheets with thickness of 0.3mm were successfully produced by conventional rolling and annealing methods.Recrystallization texture was investigated by means of X-ray diffraction.It is found that recrystallization texture is mainly composed of γ fiber(〈111〉∥ND)with peak at {111}〈112〉 and {001} fiber with peak at {001}〈210〉 after annealing at 700℃,while strong {001}〈210〉 component dominates recrystallization texture after annealing above 900℃.It is during grain growth that {... 

本实用新型公开了一种电工钢自粘涂层液生产用搅拌釜，包括釜体，釜体的内部通过两个第一隔板分隔成第一安装腔、第二安装腔和搅拌腔，釜体的内部设有传动组件，传动组件包括伺服电机、主动轴和两个从动轴，伺服电机固定安装在釜体顶端的中部，伺服电机的输出轴与主动轴的顶端固定连接，本实用新型的有益效果是：通过设有八个与十二个搅拌叶片相交错的挡板，避免搅拌轴在搅拌过程中产生离心力造成漩涡，使自粘内外侧的涂层液得到充分搅拌，通过设有循环泵机、第二隔板和流通槽使搅拌釜内的自粘涂层液处于流通的状态，使底部不易被搅拌的涂层液能够得到充分搅拌，在提高搅拌釜的灵活性的同时，保留其原有的稳定性。

本发明属于取向硅钢制备技术领域，具体涉及一种软磁材料取向硅钢退火工艺。所述退火工艺主要包括：涂覆隔离剂、按照一定速率升温后进行保温，以5‑10℃/min的速率进行降温；在降温过程中施加恒定磁场，之后继续降温即可实现。该退火工艺能够有效降低铁损失，提高磁感强度。同时具有较好的耐腐蚀性能和机械性能。

本实用新型公开了一种具有导气槽的低空载损耗电工钢用罩式炉，包括：炉台，顶部设置有加热元件以及连通炉台外缘至中心凹陷的导气通道；炉板，压设于炉台上，设置有与中心凹陷上下对应的中心通孔；砂封槽，设置于炉台的外周，槽底低于导气通道；炉罩，罩设于炉台的顶部及外周形成炉腔，与砂封槽相压接；进气通道，穿设于炉台的中心凹陷中，具有开口向上的排气口；炉罩的炉台套接段内壁设置有导气槽，导气槽的延伸方向与炉罩的高度方向一致，导气槽将气流导向炉台外缘的导气通道进气口。该具有导气槽的低空载损耗电工钢用罩式炉的炉罩设置有导气槽，利用导气槽将硅钢卷外周下行的气流导入炉台的导气通道中，改善钢卷热处理过程中的流场和温度场。

本发明公开了一种极薄取向硅钢铁芯及其制造方法，所述制造方法，包括：S1、剪切分条：将取向硅钢根据制作铁芯的宽度要求进行分条剪切；S2、卷绕：根据铁芯的规格型号要求，选取铁芯模具进行卷绕；S3、压块固定：将卷绕好的铁芯用压块固定；S4、退火加工：将固定好的铁芯，阶梯式升温至780℃保温3h退火处理，保护气氛为氮气，之后冷却降温；S5、浸胶：将降温后的铁芯，进行真空浸胶处理；S6、烘干：将浸胶处理后的铁芯烘干处理；S7、装配。该发明制造的极薄取向硅钢铁芯，能彻底消除内应力，磁路各处均无高磁阻存在，空载电流与励磁电流均大幅度下降，从而最大限度的恢复了极薄取向硅钢加工后原有择优取向织构及电磁性能。

研究表明,硅钢中的夹杂物对成品带钢的磁性能有显著影响。为研究冶炼过程硅钢中的夹杂物遗传变化,进而提出更有效的控制措施加以去除,本文结合典型的无取向硅钢生产炉次,采用非水溶液电解提取+扫描电镜观察方法分析冶炼过程中上述炉次典型试样的夹杂物。结果表明:转炉冶炼结束、RH精炼开始时,钢的氧化物夹杂总量最大,约为0.23%;RH精炼过程中,氧化物夹杂总量不断降低,并在脱碳结束时达到最低,约为0.02%;连铸过程中,氧化物夹杂总量仍有不断降低趋势,但夹杂物的平均尺寸变化不大。本试验条件下,中间包试样的夹杂物数量约为1.59×104个/mm3。 As we all know, the non-metallic inclusion effects magnetic properties of silicon steel sheets obviously. The article aims to study the heredity of non-metallic inclusion in non-oriented silicon steels during the steel making process, and then provides a more effective controlling measure to remove the inclusions. Based on the typical non-oriented silicon steel charges, the non-aqueous solution extraction and SEM observation were adopted to analyze the non-metallic inclusions. Results show that,...