硅钢资料

本实用新型涉及硅钢生产设备技术领域，具体公开了一种硅钢清洗用多段式清洗辊结构，包括中间辊和可拆卸连接在中间辊两端的支撑辊，所述中间辊和支撑辊的外径相等，中间辊与支撑辊的外壁上均固定有刷毛，所述支撑辊远离中间辊的端部为封闭设置，且同轴固定有转轴。采用本专利中的清洗辊结构，只用更换中间辊即可，无需对整个清洗辊进行更换，节省了设备成本投入；另外将支撑辊远离中间辊的端部为封闭设置，则是为了防止在工作时，液体渗入，避免对清洗辊的内部结构产生腐蚀等问题。

本实用新型公开了一种用于硅钢绝缘涂料生产的吸尘装置，包括底板、支撑平台和集尘箱，所述底板底端四角处通过螺栓连接固定有可制动万向轮，所述底板上端四角处焊接有导向套。有益效果在于：本实用新型通过设置真空泵、集尘箱、万向吸气臂、吸尘罩以及活性炭滤网，可在硅钢绝缘涂料生产过程中将逸出的物料粉尘进行有效的收集，确保硅钢绝缘涂料生产环境的洁净，有利于人体健康，通过设置电机、螺套、螺杆、导向柱以及导向套，可实现根据实际吸尘的需要实现装置高度的便捷调节，提高了装置的实用性。

试验研究了球刻痕法对高磁感取向硅钢的铁损、矫顽力、相对磁导率、巴克豪森噪声等磁学性能的影响.研究结果表明:经过球刻痕处理后,高磁感取向硅钢的铁损明显降低,矫顽力下降,8 mm球刻痕过后铁损值与矫顽力分别下降16.2%和14.7%,且铁损和矫顽力均随刻痕间距降低而减少.刻痕后的高磁感取向硅钢磁导率在高磁感应强度下明显上升,刻痕后巴克豪森噪声值明显降低,经过对比分析确定8 mm为球刻痕的最佳刻痕间距.从磁畴观察、细化磁畴的原理等方面解释了细化磁畴对高磁感取向硅钢性能的影响原因. The effects of the ball scribing on magnetic properties of high permeability grain-oriented silicon steels,including the iron loss,coercive force,relative permeability,and Barkhausen noise were investigated. The results showed that the iron loss and coercive force of the high permeability grain-oriented silicon steels apparently decreased 16. 2% and 14. 7% respectively after 8 mm ball scribing and they both decreased with the decrease of the scribing spacing at the same magnetic flux density. At... 

本发明公开了一种直流换流阀饱和电抗器用超薄硅钢铁心质量的评估方法，包括以下步骤：S1、外观评价；S2、叠装系数评价；S3、磁性能评价；S4、噪声评价；S5、耐受环境温度变化评价和S6、长期运行性能评价，本发明考虑了直流换流阀饱和电抗器对超薄硅钢铁心外观、叠装系数、磁性能、噪声及长期运行等特性要求，实现了超薄硅钢铁心外形外观的性能评估、铁心基本参数评估、电磁性能评估、耐受环境温度变化评估及长期电热运行特性评估，为直流换流阀饱和电抗器用超薄硅钢铁心可靠运行提供了保障。

本文以热轧常化板为初始材料,采用二次冷轧法与三次冷轧法制备了0.1 mm厚的取向硅钢薄带,测定相应的磁性能,并通过EBSD取向成像技术检测了二次冷轧法与三次冷轧法各工艺过程中织构与组织演变规律。结果表明,采用最终冷轧压下率适中的三次冷轧法,能在冷轧至0.1 mm时保存较多的高斯晶核,使得高温退火后的磁性能明显优于二次冷轧法。最终冷轧压下率通过影响脱碳退火后样品中的{111}<112>织构组分及Goss晶粒数量对最终二次再结晶产生重要影响。 Grain-oriented silicon steel sheets with a thickness of 0. 1 mm were produced from hot-rolled and normalized sheets by two-step-rolling and three-step-rolling methods. Their magnetic properties were measured,and the textures were detected by EBSD technique. The results show that the three-step-rolling method,which has a moderate reduction rate of final cold rolling,can maintain more { 110} < 001 >nucleus,and thus obtaining better magnetic properties compared with the two-step-method. The f... 

本发明提供一种电磁屏蔽用1050铝/50W800无取向电工钢钢板生产方法，包括S1)、将轧制好的铝卷和钢卷分别放置在两个开卷机上开卷；S2)、开卷后分别采用HCl、NaOH溶液清洗；S3)、用旋转钢丝刷法对铝板、钢板待结合面进行机械处理10‑15s；S4)、将铝板、钢板置于丙酮溶液中超声波清洗2‑3min；S5)、将表面处理后的铝板、钢板进行预拉伸或者预压缩，S6)、将预应力处理的铝板、钢板边部进行焊接；S7)、将焊接好的钢铝板进行轧前的预热处理；S8)、然后进行连续退火炉中进行退火处理，本发明将金属铝板、钢板通过热轧轧制复合化结合在一起，界面剪切强度≥100MPa，反复弯曲次数≥10次。

采用拉伸试验和显微组织观测的方法确定了GTN损伤模型中的9个损伤参数,运用GTN损伤模型对冷轧硅钢薄板边部缺陷的扩展及边裂的产生进行了有限元模拟,并与预置缺口的钢板轧制试验进行对比。结果表明:轧制过程中边部缺陷是造成钢板边部裂纹萌生和扩展的一个重要原因,GTN损伤模型可用来预测含边部缺陷硅钢薄板在冷轧过程中边裂的产生;预测结果与试验结果基本一致。 The crack initiation and propagation of silicon steel strip with edge defect during cold rolling process was studied by using GTN damage model in this paper.Nine damage parameters in GTN model were identified by tensile testing and microstructure observing,and then the FE simulation of edge defect evolution of silicon steel strip during rolling process was conducted on the base of GTN damage model,and then the results were compared with rolling experimental results.The results show that the edge... 

以试验室模拟CSP工艺生产的Fe-3Si热轧钢带为研究对象,采用正交试验及方差分析的方法,研究了取向硅钢初次再结晶退火工艺对高温退火后获得锋锐的高斯织构的影响。结果表明:取向硅钢两段式初次再结晶脱碳退火工艺参数加热段保温时间及加热温度是高温退火后获得锋锐高斯织构的主要影响因素,其可信度分别在90%和85%以上;在本试验条件下,通过正交试验获得的最佳退火工艺为:冷硬板经600℃保温3 min和850℃保温6 min。 Fe-3Si hot rolled strip was produced by simulating CSP technology in the laboratory.Orthogonal experiment and analysis of variance were carried out to investigate the influence of primary recrystallization on the sharp Goss texture of the oriented silicon steel.The results show that holding time of the heating section and the heating temperature for a sharp Goss texture of the samples annealed has important implications in this experiment conditions,the two-step decarburization annealing process... 

本发明公开了一种无瓦楞状缺陷的高磁感低铁损无取向电工钢板，其各化学元素质量百分含量为：0＜C≤0.0035％、Si：1.2～2.8％、Mn：0.2～1.0％、P：0.04～0.15％、Sn+Sb：0.02～0.2％，余量为Fe和其他不可避免的杂质。此外，本发明还公开了上述高磁感低铁损无取向电工钢板的制造方法，其包括步骤：(1)冶炼和连铸，其中在该步骤不采用电磁搅拌；(2)热轧，其包括：粗轧、精轧、卷取和均热；其中在粗轧步骤采用2～6道次进行轧制，且粗轧单道次压下率控制在20％～40％之间；(3)上述热轧步骤后不进行常化步骤而直接进行冷轧；(4)连续退火。本发明所述的无瓦楞状缺陷的高磁感低铁损无取向电工钢板在保证较低生产成本的同时，还具有高磁感和低铁损的特性。

本发明涉及一种具有优异铁损和磁性能的无取向电工钢及其生产方法，电工钢成分及质量含量为C≤0.0015%，Si:1.10‑1.40%，Mn：0.35‑0.55%，P≤0.018%，S≤0.003%，Al：0.20‑0.30%，Ti≤0.0015%，N≤0.0028%，O≤0.0015%，N＋O≤0.0040%，余量为Fe和不可避免的杂质。生产方法包括铁水预处理、转炉冶炼、RH精炼、连铸、轧制、常化、冷轧、连退和涂层工序。本发明电工钢热轧成品微观晶粒尺寸70‑95μm，对铁损和磁性能有利的（100）组织织构控制在82‑92%，成品P15/50:3.5‑4.0w/kg，B50:1.70‑1.98T。

本实用新型公开了一种硅钢碎断刀具曲面车削加工装置，属刀具曲面车削加工定位工装领域。包括主体，周向设置在主体上的多个限位槽，以及对刀具横向施压并安装在对应限位槽处的施压机构，施压机构包括沿限位槽宽度方向运动并对刀具作用的施压块，以及将施压块与主体可调节安装的调节件，施压块相对刀具的一侧设置有滚动体三。通过调节调节件将施压块沿限位槽宽度方向移动，进而将刀具夹紧在限位槽内部，通过滚动体三的设置利于在加工完成后刀具和施压块分离，防止出现卡滞的现象发生，利于刀具的高效生产制作。

针对攀枝花钢钒有限公司难以稳定生产w(S)≤0.006%高级别电工钢的问题,通过开发RH脱硫剂、钢包渣改性及工艺参数控制,形成了RH脱硫系统工艺技术。经工业试验表明,采用该工艺技术后,钢水脱硫率最高达到42%,成品w(S)控制在0.005%以下,全氧、氮含量也得到了较好的控制,且脱硫剂没有引起钢水增碳,满足高级别电工钢的生产要求。 In light of the difficulty of production of high level electrical steel w(S)≤0.006 % steadily in Panzhihua steel & vanadium Co.,Ltd.the process technology of RH desulfurization system has been formed by developing the RH desulfurizer,modifying the ladle slag and controlling the process parameters.Industrial experiments show that the desulfurization rate of hot metal rises to 42 % and the w(S) of the finished products is controlled in below 0.005 % and total oxygen and nitrogen contents are a...