硅钢资料

通过固溶度积公式计算及热模拟实验,对不同热装和加热温度条件下的无取向硅钢铸坯中析出相进行了研究.在低于950℃热装时,铸坯中AlN的析出量和尺寸不再变化,但MnS和AlN-MnS的数量及平均尺寸随着热装温度降低而进一步增加,并在温度低于600℃时达到最大值后保持不变.与1200℃相比,1100℃加热的铸坯中AlN、MnS的总固溶量相对更少.相比850℃热装,600℃热装再加热到1100℃的铸坯中AlN和MnS的总固溶量更少,且AlN和MnS尺寸更大.合适的热装温度和加热温度分别为600℃和1100℃. Based on solubility product calculation and thermal simulation experiments,precipitated phases in continuous casting slabs of non-oriented silicon steel were systematically studied at different hot charging and heating temperatures.When the hot charging temperature is below 950 ℃,the content and size of AlN remain unchanged,but the quantity and size of MnS and AlN-MnS increase when the hot charging temperature decreases,reach maximum and remain unchanged when the hot charging temperature is belo... 

本发明涉及一种提高热连轧无取向硅钢厚度精度的方法，包括以下步骤：1）降低粗轧终轧温度和精轧入口温度，减少精轧轧制过程中奥氏体向铁素体相变的体积数，提高轧制力模型预估的精度；2）降低精轧机活套张力，减少因张力带来的厚度扰动。本发明通过降低粗轧终轧温度、精轧开轧温度和调整精轧机张力，可以有效提高精轧机轧制力预估精度，提高厚度精度以及宽度精度。

介绍了硅钢氧化镁制备方法及高质量硅钢氧化镁制备技术的研究进展,并对利用我国丰富的卤水资源制备硅钢氧化镁进行了展望。 The preparation methods of silicon steel magnesium oxide and research progress of high quality silicon steel magnesium oxide preparation technology were introduced.The use of abundant brine resources in the preparation of silicon steel magnesium oxide was prospected. 

本发明的一个实施方案提供一种取向电工钢板及其制造方法，以重量％计，所述取向电工钢板包含：Si：3.0‑4.5％、Mn：0.05‑0.2％、Al：0.015‑0.035％、C：0.0015％以下(0％除外)、N：0.0015％以下(0％除外)、S：0.0015％以下(0％除外)、余量的Fe及其它不可避免的杂质，并且满足以下关系式1和关系式2。[关系式1](W13/50/W17/50)≤0.57[关系式2](W15/50/W17/50)≤0.76(其中，所述关系式1中，Wx/y表示施加磁场的大小为x/10T且频率为yHz的条件下的铁损值)。

本实用新型公开了一种变压器硅钢片剪切收料装置，其包括底板和存放架推出机构，底板的前侧中部设置有用于放置外设剪切设备的放置区；存放架推出机构包括滑动板座、锁紧组件，滑动板座可左右滑动地安装于底板的上表面，在滑动板的上表面设置有两个用于放置外设的硅钢片存放架的存放架放置槽，两个存放架放置槽呈左右间隔设置，锁紧组件用于锁紧滑动板座与底板之间的相对位置。当该硅钢片存放架存放完后，将滑动板座推动至使得另外一个存放架放置槽设置于放置区的正后方，另外的硅钢片存放架继续接受剪切设备掉落的硅钢片体，可连续地实现硅钢片体的落料存放，令转运和落料的操作不相互干涉，提高生产的效率。

本发明公开了硅钢片铁芯生产线，包括放卷机构、剪切机构、送料机构、叠片机构和下料机构，送料机构包括磁性传送带、送料件和第一定位杆，磁性传送带包括上传送带和下传送带，送料件可沿磁性传送带的正交方向平行伸出，其中，第一送料分台和第二送料分台安装于上传送带的下方并且相背运动，第三送料分台和第四送料分台安装于下传送带的下方并且相背运动，第一定位杆用于定位硅钢片，叠片机构包括叠放台、悬梁和两个六自由度机械手，六自由度机械手吊装于悬梁上，包括有电永磁铁，用于吸取硅钢片，下料机构包括滑板，叠放台放置于滑板上。根据本发明的硅钢片铁芯生产线，可提高设备自动化程度，提高叠片速度，从而提高生产线的生产效率。

利用加热炉模拟、动态再结晶以及热模拟等试验方法以及扫描电镜、金相显微镜等分析观察手段对无取向硅钢边裂的成因进行了探讨。结果表明,长时间加热使得板坯边部晶粒异常长大,晶界氧化并脱碳,轧制过程中边部温度过低,动态再结晶过程变弱,使得板坯边部延伸性能变差,是导致硅钢边裂的主要原因。建议通过适当降低铸坯加热温度、缩短保温时间、提高终轧温度来改善硅钢边裂缺陷。 The behaviors of high temperature oxidation,dynamic recrystallization,and hot ductility,microstructure evolution were investigated on the non-oriented electrical steel sheets to discuss the formation of edge crack.The key causes of cracking was found to be the coarse as-cast microstructure,grain boundary oxidation and decarburization in reheating furnace,as well as reduced temperature at strip edge region during hot rolling process resulting in reduced hot ductility and lack of enough dynamic re... 

研究了含铜低碳低硅无取向电工钢中的析出相及其析出机理.由能谱(EDS)及选区电子衍射(SAED)分析可知,铁素体基体上存在的大量弥散分布的等轴状析出相为类B2结构的铜.这些铜析出相的析出机理可以是一般析出、位错析出、台阶机理相间析出和弓出机理相间析出:一般析出在550、650和750℃三个等温温度均可发生;位错析出只发生在较低的等温温度(550℃),此时析出相呈特殊的平行短列状;台阶机理相间析出也可在上述三个等温温度下发生,但650℃等温时最有利于台阶机理相间析出,此时析出相平直列状分布;弓出机理相间析出只发生在较高的等温温度(750℃),析出相弯曲列状分布. Precipitates in low-carbon low-silicon non-oriented electrical steel containing Cu were studied and the precipitation mechanism was analyzed by means of energy dispersive spectrometry(EDS) and selected area electron diffraction(SAED).It is found that the equiaxed precipitates of Cu with B2-like structure distribute dispersively in the non-oriented electrical steel.The precipitation mechanism involves general precipitation,dislocation precipitation,interphase precipitations formed by the ledge me... 

研究了应用电感耦合等离子体质谱(ICP-MS)同时测定硅钢中痕量铝、钼、钒、钛、铌元素的分析方法。通过条件试验对测量参数进行了优化,确定RF功率1 400 W,泵速30rpm,采样深度140,雾化压力0.90。样品采用硝酸分解,以Be、Y混合内标校正了测量过程中高基体引起的信号漂移。根据测量时存在的质谱干扰情况,选择同位素27 Al、98 Mo、51 V、47 Ti和93 Nb作为测定同位素,同时通过调节仪器参数使得双电荷离子和氧化物离子的产率最低,以减少其带来的干扰。采用基体匹配法配制校准溶液,以标准加入法建立工作曲线,并扣除试剂空白。该方法各元素的测定下限均可达到1μg/g。用于硅钢标准样品的测定,所得结果与参考值完全吻合,各元素的RSD小于5.2%。 A method for the determination of trace aluminum,molybdenum,vanadium,titanium and niobium in silicon steel by inductively coupled plasma mass spectrometry(ICP-MS) was described.A series of single parameter condition experiment was conducted.The optimized operation parameters with RF power 1 400 W,turbo pump rate 30 rpm,sampling depth 140 and nebulizer pressure 0.90 were obtained.The samples were dissolved by HNO3,and the Be and Y mixing internal standard were used to eliminate the signal drift c... 

本发明的一种方式的无取向性电磁钢板用热轧钢板，以质量％计含有：C：0.0050％以下、Si：0.5％以上3.5％以下、Mn：0.1％以上1.5％以下、Al：0.1％以上1.5％以下、Cu：0.01％以上0.10％以下、Sn：0.01％以上0.20％以下；剩余部分由Fe和杂质构成；在从表面到深度10μm的范围内，具有0.12％以上的Cu的浓度峰值。

取向硅钢成品的晶粒尺寸非常大,其易磁化方向[001]晶向对于轧向的偏差角度对其磁性能影响极大。本文介绍了取向硅钢二次再结晶后成品晶粒位向的几种测定方法,包括侵蚀法、劳厄法、OIM法、极图法和非对称X射线衍射法等,并对这几种测量方法进行了比较。 The finished product of grain-oriented silicon steel has immense grain size ranging from millimeters to centimeters and the deviation angles of easy magnetization direction from rolling direction plays a remarkable role in magnetic properties of grain-oriented silicon steel.The methods in common use for determining the deviation angles of crystal direction are introduced,which include the etch-figure method,the Laue method,the OIM method,the pole figure method and the asymmetrical X-Ray diffract... 

本实用新型公开一种硅钢片卷料悬吊上料装置，包括装配架，装配架之间装配有若干个左右间隔设置的硅钢片卷料限位装置，所述硅钢片卷料限位装置用于装载硅钢片卷料、装配架包括前后对称设置的架板，所述架板上具有矩形凸出端、前、后部位之间所述矩形凸出端之间装配有若干个左右间隔设置的长螺杆、长螺杆贯穿所述硅钢片卷料限位装置，所述长螺杆的端部螺纹连接有螺母、架板的底部固定连接有两个左右间隔设置的轮架杆，所述轮架杆的左右两端均转动连接有滚轮、轮架杆之间固定连接有C形架杆，所述C形架杆上固定连接有悬吊环体，实现将大量生产加工使用的硅钢片卷料进行上料。采用上述方式不仅实现将大量生产加工需要的硅钢片卷料进行输送。