硅钢资料

用还原分离-原子荧光光谱法分析了硅钢中的痕量汞.分析方法的不确定度主要来自测量重复性,样品溶液浓度,工作曲线变动性,标准溶液,移取、配制标准溶液,仪器变动性等.文章分别对上述构成合成不确定度大小的分量进行了计算讨论. Trace mercury in silicon steel and galvanized sheet was analyzed by adopting reduced separation-atomic fluorescence spectrometry.The uncertainty of the analysis method mainly comes from measurement repeatability,sample concentration,working curve volatility,standard solution,pipetting and preparation of standard solution,and instrument variability,etc.The essay conducted all calculations and discussions on the above components that determine uncertainty. 

以构建高磁感、低铁损、免轧制高硅电工钢铁芯为出发点,提出采用单辊甩带制备非晶铁硅合金薄带、微氧化法在铁硅合金粉末表面包覆高电阻率铁硅氧化物薄膜制备核壳异质结构高硅电工钢纳米粉末、放电等离子烧结快速成形制备颗粒间绝缘的高硅电工钢铁芯。研究了不同氧化包覆时间对SPS烧结试样密度、物相组成、微观结构和静磁性能的影响。研究表明,在氧化包覆5h烧结温度800℃工艺条件下,制备的6.5%Si高硅电工钢铁芯的静磁性能最佳,饱和磁化强度为128.84A.m2/kg、矫顽力为2.25kA/m、剩磁为3.47A.m2/kg。其饱和磁化强度与粉末压延法制备的高硅钢相当,但矫顽力降低了1/3。 The paper takes preparation 6.5%Si steel with high induction,low core loss and removing rolling as the starting point,amorphous Fe-Si ribbons was synthesized by melt spinning method,6.5%Si steel nanopowders with high resietivity core shell structure was prepared by the slight oxidation process and 6.5% Si steel iron core with evaluating internal was sintered by spark plasma sintering process(SPS).The essay focuses studies the effects of different oxidation cladding time on sample density,phase c... 

在15 kg真空感应炉上,用CaO-Al2O3-SiO2-MgO渣系进行脱硫试验,探讨了脱硫渣系碱度、MI、Al2O3、CaF2对脱硫效果的影响。研究结果表明,随脱硫渣系碱度、MI、Al2O3和CaF2含量的增加,脱硫率都呈现先增加后减少的趋势。初始硫含量为0.009 33%~0.010 73%,加入脱硫渣系4 min时间内表观脱硫速率为(0.000 96~0.001 49)%/min,平均脱硫率为81.2%,最高达86.8%。当脱硫渣中w(CaO)=58.15%、w(SiO2)=4.85%、w(Al2O3)=25%、w(MgO)=6%、w(CaF2)=6%,脱硫效果最好,此时钢液中硫为0.001 33%。 Experiments on desulfurization of molten steel using CaO-Al2O3-SiO2-MgO based desulfurization slag was carried out in a 15 kg vacuum induction furnace. The effects of desulfurization slag basicity,MI, Al2O3and CaF2on desulfurization of molten steel were studied. The results show that with the increase of basicity,MI,Al2O3or CaF2in desulfurization slag,the desulfurization rate rises initially and then decreases. In addition,as the initial sulfur content is 0. 009 33% ~ 0. 010 73%,the apparent des... 

本发明提供一种硅锰镇静无取向硅钢冶炼方法。该无取向硅钢化学成分质量百分比为C≤0.005％，Si：0.25％‑1.20％，Mn：0.2％‑0.8％，P：0.015％‑0.065％，S≤0.005％，Als≤0.005％，余量为Fe及不可避免的杂质。其生产方法包括转炉出钢结束加石灰、渣面脱氧剂调渣；RH真空精炼脱碳结束后进行脱氧合金化，合金化后3‑5min由真空室料仓加入合成渣，处理一段时间后净循环8‑12min，破空出钢运至连铸浇注。得到钢水中主要为SiO2‑CaO‑Al2O3系夹杂，一方面避免了钢水中生成低熔点SiO2‑MnO系夹杂，轧制过程沿轧制向伸长，阻碍晶粒长大；另一方面也避免了生成纯SiO2或高SiO2组分类酸性夹杂，导致冶炼过程耐火材料的严重侵蚀。本发明可控制钢中非金属夹杂物类型，提高钢水洁净度，改善冶炼过程中对耐火材料的侵蚀。

利用光学显微镜、TEM和EBSD研究了退火温度对双辊连铸无取向硅钢再结晶组织的影响。结果表明,900℃退火后组织分布不均匀,有大量带状组织,平均晶粒尺寸29.5μm。提高退火温度,晶粒尺寸增大,组织均匀化程度增加,1050℃退火时,带状组织基本消失,平均晶粒尺寸42.2μm。 Effect of annealing temperature on recrystallization microstructure of non-oriented electrical steel produced by twin-roll casting process was investigated using OM,TEM and EBSD.The results show that the recrystallization microstructure is uneven because of many banded grains existing,average grain size is 29.5 μm.With annealing temperature increasing,the recrystallization grain size increases,microstructure becomes more homogeneous.When 1050 ℃ annealing,the banded structure almost disappear and... 

利用背散射衍射技术(EBSD)和XRD,研究了两段式脱碳退火工艺对取向硅钢纵截面初次再结晶的微区取向、取向差分布、特殊晶界(CSL)及高温退火试样高斯织构。分析了初次再结晶晶界特征对取向硅钢高温退火后宏观织构的影响。结果表明:初次再结晶的纵截面基体中Σ3和Σ5晶界使得高斯晶粒有着较高的迁移率,在高温退火时借助20o～45°的大角度晶界的界面能吞并周围{111}<112>晶粒迅速长大,形成密度水平较高的高斯织构。 Micro area orientation of primary recrystallization,the misorientation distribution,special boundaries under different two-stage decarburization annealing and the Goss texture under high temperature annealing the longitudinal section of grain-oriented silicon steel were detected by electron back scattering diffraction(EBSD) and X-ray diffraction(XRD).The effect of primary recrystallization grain boundary on macrotexture after high temperature annealing was analyzed.The results show that the Σ3 a... 

本发明相对于板厚较薄的电磁钢板提供不会导致磁特性劣化的基于激光的加工方法。在对电磁钢板进行使用激光的熔断并将该电磁钢板加工成规定的形状的电磁钢板的加工方法中，使上述激光的扫描速度成为10000mm/min以上来进行上述熔断。

【作者】 朱一知； 高军军； ...

本发明涉及金属冶炼工艺，尤其是一种降低无取向硅钢W800冶炼成本的方法，开吹阶段，着火后，加入头批渣料，石灰加入量占石灰总加入量的70%，石灰石加入量占石灰石总加入总量的100%，轻烧白云石加入量占轻烧白云石总加入总量的100%，待化渣后，枪位降低；化渣后将剩余30%石灰加入，加入剩余石灰过程中利用矿石调整温度；吹炼后期，并逐步压枪，终点拉碳枪位至1.4m，并使枪位在此高度不少于30s；到达冶炼终点。本工艺通过降低转炉渣量、提碳降氧和提高终点温度来减少铁水锰氧化量和促进氧化锰还原量，进而降低RH金属锰加入量，降低生产成本。

本发明涉及收卷装置技术领域，且公开了一种用于硅钢片横剪线的卷料自动上料装置，包括底座，所述底座顶端固定连接有底托，所述底托的顶端活动连接有外筒，所述外筒的中间通过轴承活动连接有阻力轴，所述阻力轴的正面固定连接有内筒，所述内筒外侧与外筒内侧的中间活动连接有连轴，所述连轴的中间固定连接有送料电机，所述送料电机的一侧固定连接有卷轴卡辊。本发明将原本固定式卡辊及送料电机，设置为可绕外筒内壁进行移动的活动式卡辊，在进行上料时通过外筒将卷轴卡辊旋动至底端进行直接上料，无需停机替换，提高了卷料替换的连续性，同时避免了使用吊车进行吊装过程中吊装不稳定造成的上料精度不高和卷轴掉落损坏等问题。

本发明涉及一种用于控制硅钢毛刺状厚度波动的工艺，包括如下步骤；将连铸坯送入加热炉中进行加热，连铸坯入炉温度为400‑680℃，连铸坯在炉时间为185‑220min；将加热后的连铸坯进行热轧，轧辊偏心量为0‑0.025mm，将热轧后的带钢进行卷取；将卷取后的带钢酸洗后进行冷轧，冷轧操作模式由多次阶段升降速模式调整为一次性升降速模式，且在一次性升降速阶段将MN‑AGC增益系数增大；将冷轧后的带钢进行卷取，退火后得到硅钢片成品。本发明所公开的用于控制硅钢毛刺状厚度波动的工艺，该工艺对加热、热轧、卷取及冷轧各工序进行优化协调，能够有效解决硅钢毛刺状厚度波动的问题，实现无取向硅钢全长厚度控制精度的提升，而且无需进行设备和系统改造，容易实现，易于推广。

本实用新型涉及一种摩托车点火器线圈用硅钢片，包括E型件和I型件，所述E型件和I型件可组合成日字形；所述E型件包括竖边和设置在竖边三个横边，所述竖边与三个横边接触的位置设置孔眼；所述孔眼内径从为变径结构；位于E型件正面设置散热线槽，所述散热线槽一端与孔眼贯通，另一端指向凸部；位于E型件背面在散热线槽正对位置设置外凸线，所述I型件一侧设置与凸部匹配的凹部，在所述凹部之间凸台；所述凸台与凹台重叠；在凸台与凹部之间设置凸棱，所述凸棱位于I型件外侧。本实用新型设计新颖，改进巧妙，由于E型件具有弧形边可以有利于拾取，方便工作操作，同时采用采用接触的方式接触，增加了组合体的稳定性。