本实用新型公开了一种硅钢片二次搭接夹具，包括底座、位于底座顶部的调节板以及位于调节板顶部一端的固定杆，所述底座包括设置在底座内部顶端中间位置处的活动槽。本实用新型通过连接块将第一夹钳与第二液压缸的输出端相连接，通过第一夹钳和第二夹钳对硅钢片进行固定，将焊条焊接在一组硅钢片上，伺服电机带动调节杆发生转动，调节杆外侧的外螺纹和活动块内部的螺纹孔相互配合，可使活动块在活动槽内部发生活动，通过活动块带动调节板发生前后移动，从而使对硅钢片进行前后一端，通过滑轨使调节板的移动更加稳定，使两组硅钢片相对齐，通过固定块使第一液压缸带动调节架左右移动，使焊条与两组硅钢片紧密接触，实现二次搭接。

采用节能、环保、经济型的生产技术与工艺来制造高磁感取向硅钢目前已成为世界各大取向硅钢生产厂的研发热点。总结了国内外各大钢铁企业与研究机构采用低温板坯加热技术生产高磁感取向硅钢的开发及应用情况,概括了传统流程实现低温板坯加热技术的方法。介绍了薄板坯连铸连轧与双辊薄带连铸等短流程工艺生产高磁感取向硅钢的研发现状。在此基础上,探讨了高磁感取向硅钢生产技术与工艺的发展趋势及方向。 Utilizing energy-efficient,environmentally friendly,economic production processes and technologies to manufacture high magnetic induction grain-oriented silicon steel has become the focus of current research work.Based on using low-temperature slab reheating techniques to produce high magnetic induction grain-oriented silicon steel at both iron and steel enterprises and research institutions all over the world,the current application and exploitation was thoroughly generalized;the implementation... 

本申请提供了一种提高高磁感取向硅钢渗氮效率的方法，属于高磁感取向硅钢渗氮处理技术领域，包括所述高磁感取向硅钢按重量百分比包括：Si：2.8～3.4％、C：0.040～0.070％、Als：0.015～0.045％、Mn：0.06～0.14％、S：0.003～0.020％、N：0.003～0.010％、Cu：0.01～0.025％、Sn：0.03％～0.07％、Cr及Ni，Cr和Ni的总含量小于0.5％，其余为Fe和不可避免杂质物，其特征在于，控制脱碳退火后钢带表层氧化物中铁系氧化物的比例，该装置能够增加脱碳退火后钢带表面氧化层中铁系氧化物占整个氧化层重量的比例，从而在获得同等渗氮量的情况下实现了快速渗氮，缩短渗氮时间，提高渗氮效率。

本发明提供能够制造实现高磁通密度且磁特性优异的方向性电磁钢板的新颖并且得以改良的方向性电磁钢板的制造方法。本发明的一方案提供一种方向性电磁钢板的制造方法，其特征在于，其包含热轧工序、冷轧工序、一次再结晶退火工序、最终退火工序及平坦化退火工序，并进行喷丸处理和/或矫平加工处理及与溶液相接触的处理，上述溶液含有规定量的Cu等，pH为‑1.5以上且低于7，液温为15℃以上且100℃以下，钢板在上述溶液中浸渍的时间为5秒以上且200秒以下。

本发明特别涉及一种中频用取向硅钢极薄带及其钢基板的制备方法，属于硅钢极薄带制备技术领域，方法包括：将硅钢原料进行冷轧，获得硅钢薄带；将硅钢薄带进行退火，退火采用至少3段式连续退火工艺，获得钢基板；采用本法制得的钢基板制备的中频用取向硅钢极薄带具备优良的磁性能和板形，采用多段式退火，获得稳定的成品性能，制造工艺简单，可实施性高，采用无底层取向硅钢作为母材，节能环保，产品表面质量好，产品可满足中频条件下(≧400Hz)的使用要求。

本发明公开了一种半无机硅钢片漆及其制备方法和应用，其包括：聚酰胺酰亚胺清乳液、二氧化钛、二氧化硅、硫酸钡和氨基树脂，聚酰胺酰亚胺清乳液的制备：在保护气体保护下和回流状态下，使偏苯三酸酐与特定的复合双端氨基化合物在第一有机溶剂中反应，加入磷酸三丁酯、三乙胺，反应；向外蒸出第一有机溶剂，加入第二有机溶剂，加入直链烷基苯磺酸钠、脂肪醇聚氧乙烯醚硫酸钠和脂肪醇聚氧乙烯醚，混合，在搅拌条件下滴加水，滴加完之后，加入双马来酰亚胺进行封端，制成；该半无机硅钢片漆通过将各组分混合超声分散而制成，可在硅钢片中作为覆盖漆应用，且不仅可以采用水作为主体溶剂，环保型好，而且还兼具耐高温、高粘结强度、电气性能强等优点。

为提高无取向硅钢导磁性能,研究了不同剪切方式对无取向硅钢剪切处磁畴结构的影响。利用纳米磁流体观测无取向硅钢剪切后边部磁畴结构。结果表明,硅钢无论在机械剪切还是线切割后的边部磁畴都会发生不同程度的改变:线切割对边部磁畴结构改变较小,边部磁畴分布均匀且连续,在距边缘0～20μm范围内出现磁畴宽度变小现象;机械剪切对磁畴的改变较为严重,剪切处磁畴零乱且不连续,在距边缘20μm处仍难以观察到完整的磁畴结构。 The effects of different shearing modes on magnetic domain structure of cold rolled non-oriented silicon steel are studied in this paper.The magnetic domain of cold rolled non-oriented silicon steel is observed by nanometer magnetic fluid pattern method.The results show that the edge magnetic domain structure will be changed by mechanical shear and wire-electrode cutting,the variation of edge magnetic domain structure wire-electrode cutting edge is very small,the magnetic domain structure is wel... 

【作者】 宋波； ...

本发明公开了一种激光刻痕降低取向硅钢铁损的制造方法，采用0.23‑0.35mm厚取向硅钢作为原材料，钢带在拉伸热平整线出炉后进行激光刻痕处理，细化磁畴，进而降低取向硅钢成品铁损值，达到优化磁性能的目的。本发明的激光刻痕处理后取向硅钢的铁损改善率可达到9‑16％，且经过500℃以上退火后，铁损又恢复到刻痕前状态。

借助于EBSD对比研究了常化退火对高牌号无取向电工钢热轧组织和织构演变的影响,分析了常化退火对热轧板各厚度层织构的演变规律。结果表明,常化退火改善了热轧组织的均匀性,并弱化了热轧变形的γ纤维织构。升高常化退火温度,可增大热轧板的晶粒尺寸,提高{100}和{110}织构组分占有率,有利于提高无取向电工钢成品板的磁性能。 Effects of normalizing annealing on microstructure and texture of high-grade non-oriented electrical steel hot-rolled sheet were investigated by EBSD. Emphasis was put on the effects of normalizing annealing on texture evolution in the sheet thickness. The results show that the hot-rolled microstructure homogeneity is improved and the γ-fiber texture is weakened by normalizing annealing treatment. The grain size of hot-rolled sheet and intensity of the {100} and {110} favorable texture can be in... 

对硅钢板材分别进行异步和同步轧制,研究了轧制参数包括速比、压下量和道次对板材表面显微组织的演变的作用.结果表明,异步轧制硅钢板材表面形成了晶粒尺寸为10~50 nm,取向接近随机分布的纳米晶,而同步轧制板材的表面只形成了位错胞,证明异步轧制可以诱发表面纳米化.异步轧制板材表面纳米晶的形成过程为:在剪切力的反复作用下,高密度位错形成、滑移、湮灭和重组形成亚微米尺度的亚微晶/位错胞.随着压下量和轧制道次增加,高密度位错重复以上过程使晶粒尺寸减小、取向差增大,最终形成取向接近随机分布的纳米晶组织.大压下量和多道次是异步轧制诱发板材表面纳米化的关键,而速比的增加可以加快纳米化进程. Surface nanocrystallization(SNC) can effectively enhance the surface and global properties of the metallic materials,such as microhardness,intensity,fatigue,wear and corrosion resistances,therefore provides more promising practical industrial applicability.Up to now,several SNC treatment methods were developed based either on the principles of ball impactions or friction sliding,however,difficulty still exists for the surface treatment of large-dimensional samples with high efficiency.Recently,m... 

测试了高强无取向电工钢的S-N曲线,并借助光学显微镜、扫描电子显微镜、透射电子显微镜分析了实验钢组织,疲劳断口形貌和位错结构。结果表明:室温条件下,频率为20Hz,应力比R为0.1,循环10~7周次时,实验钢的疲劳强度为360MPa,疲劳裂纹萌生于实验钢的次表面,裂纹萌生点附近有沿晶开裂现象,疲劳裂纹扩展区域有解理台阶与疲劳条纹,瞬间断裂区是韧性断裂,有大量韧窝。实验钢在循环应力作用下基体中产生了大量位错,并有驻留滑移带终止在晶界位置。 The S-N curve of a high strength non-oriented electrical steel was tested.The microstructure and fatigue fracture morphology and dislocation were analyzed by optical microscope,scanning electron microscope,transmission electron microscope.The results showed that:at room temperature and the frequency of 20 Hz and the stress ratio Rof 0.1,the fatigue strength of the experimental steel was 360 MPa when the cycle was 10~7 cycles.The fatigue crack initiation at the surface of the steel and the interg...