研究了薄板坯连铸连轧流程(TSCR)条件下热轧工艺对3.2%Si-0.7%Al无取向硅钢组织、织构演变及磁性能的影响规律。结果表明,提高均热温度和热轧温度有助于获得粗大的变形组织和强烈的{001}〈110〉织构,进而对后续的组织、织构演变进程及磁性能产生有利的遗传影响。与低温均热和低温热轧相比,高温均热和高温热轧得到的最终成品板的再结晶晶粒较粗大,λ纤维再结晶织构较强而γ纤维再结晶织构较弱,磁感应强度较高。 It was investigated that the effects of thin slab cast rolling(TSCR) hot rolling processes on microstructural,textural evolution and magnetic properties of 3.2%Si-0.7%Al non-oriented silicon steel.The results show that much larger hot rolling deformed microstructure and much stronger {001}〈110〉 texture could be obtained by increasing the soaking and hot rolling temperatures,which had good heritable effects on subsequent microstructural,textural evolution and magnetic properties.The final sheets ... 

采用RH精炼添加钙合金方式对硅钢进行钙处理。结果表明,钙合金添加量为0.67、1.00、1.67kg/t钢时,钢中钙含量分别为0、2×10-6、4×10-6;随着钙合金添加量增大,钢中夹杂物粒度逐渐由0～2μm向2～4、4～6μm偏移;不同钙处理条件下,钢中均存在粒径小于1μm和粒径为1～5μm的MnS、CuxS夹杂物,后者或单独存在,或同AlN、CaS夹杂复合;粒径为5～10μm区间,钢中的夹杂物基本以钙的氧、硫化物为主。与钙处理前相比,钙合金添加量为0.67、1.00、1.67kg/t钢时,粒径小于1.0μm的微细夹杂物减少幅度分别为68.06%、87.50%、94.94%。钙合金添加量为1.67kg/t钢时,可以去除钢中绝大部分的微细夹杂物。 Ca alloy was added into the liquid steel during RH refining,and the results show that Ca concentration in final Si steel sheets is insignificant,about 0,2×10-6 and 4×10-6 when the added amount of Ca is 0.67,1.00 and 1.67 kg/t steel,respectively.With the increase in the added Ca alloy amount,the inclusions in the steel gradually change from those of 0～2 μm to those of 2～4 and 4～6 μm.Under different Ca treatments,there exist MnS and CuxS inclusions whose size is below 1 μm as well as MnS and CuxS ... 

本实用新型属于清洁度检测装置领域，具体的说是硅钢前处理带钢表面清洁度在线检测系统，包括操作台和清洁单元；所述清洁单元设置在操作台的端部；所述操作台的端部固接有支撑腿；所述支撑腿的端部固接有顶板；通过设置的清洁单元，对工业相机的镜头表面进行清洁，转动轮盘调节角度，推动推板将水箱内部的水分喷洒在镜头的表面，按压连接杆的端部，橡胶柱和弹簧受力，使用刮板对镜头的表面进行刮擦清理，将镜头的表面灰尘清理干净，避免了灰尘堵塞镜头，影响拍摄效果。

本实用新型提供了一种带连接筋的硅钢盘，包括多个周向间隔排列的硅钢块，任意相邻的两所述硅钢块之间连接至少两连接筋，以将相邻的两所述硅钢块之间的空间分割为分设在所述硅钢盘轴向两侧的转子槽，及位于两所述转子槽之间的若干个收纳孔。多个所述硅钢块通过连接筋连接，并形成一整体的硅钢盘，相对现有技术独立成型多个硅钢块来说，不仅避免硅钢块丢失，还有效提升硅钢盘装配为转子盘的成型效率，以及保证各硅钢块在转子盘上的位置一致性，并且增加所述连接筋的数量，有效增强相邻两硅钢块的连接性能，从而大幅增强转子盘的机械可靠性。

以构建高磁感、低铁损、免轧制高硅电工钢铁芯为出发点,提出采用单辊甩带制备非晶铁硅合金薄带、微氧化法在铁硅合金粉末表面包覆高电阻率铁硅氧化物薄膜制备核壳异质结构高硅电工钢纳米粉末、放电等离子烧结快速成形制备颗粒间绝缘的高硅电工钢铁芯。研究了不同氧化包覆时间对SPS烧结试样密度、物相组成、微观结构和静磁性能的影响。研究表明,在氧化包覆5h烧结温度800℃工艺条件下,制备的6.5%Si高硅电工钢铁芯的静磁性能最佳,饱和磁化强度为128.84A.m2/kg、矫顽力为2.25kA/m、剩磁为3.47A.m2/kg。其饱和磁化强度与粉末压延法制备的高硅钢相当,但矫顽力降低了1/3。 The paper takes preparation 6.5%Si steel with high induction,low core loss and removing rolling as the starting point,amorphous Fe-Si ribbons was synthesized by melt spinning method,6.5%Si steel nanopowders with high resietivity core shell structure was prepared by the slight oxidation process and 6.5% Si steel iron core with evaluating internal was sintered by spark plasma sintering process(SPS).The essay focuses studies the effects of different oxidation cladding time on sample density,phase c... 

对应用动态加热进行短时温度退火的取向电工钢进行了二次再结晶研究。所进行研究的实验用取向电工钢是经过终冷轧和后续罩式退火后的一条工业化生产线生产的。研究结果表明,运用短时热处理条件可引起研究钢完全的异常晶粒长大。在实验室处理的材料的织构和金相组织与工业化生产的经过终退火而获得的相同的取向电工钢类似。但是,在实验室处理的取向电工钢的二次再结晶的矩阵中可观测到\"寄生\"晶粒。从磁性观点看,这些\"寄生\"晶粒含有不理想的{111}取向织构。 The present study was made to investigate secondary recrystallization in grain-oriented steels annealed at short time temperature exposures with application of dynamical heating.The investigated GO(Grain Oriented) steels for experiments were taken from one industrial line after final cold rolling reduction and subsequent box annealing.It was shown that application of short time heat treatment conditions could lead to complete abnormal grain growth in the investigated GO steel.The texture and mic... 

本发明公开了一种适宜缠绕式加工的低铁损无取向硅钢及其生产方法，属于硅钢生产技术领域。本发明的无取向硅钢包括以下质量百分比的元素：Si：1.5～2.5％，Mn：0.15～1.0％、Als：0.5～1.5％，其余为Fe及不可避免的杂质。其生产工艺步骤为：铁水预处理、转炉冶炼、真空处理、连铸；加热热轧；常化处理；冷轧、退火；保温、冷却；涂覆绝缘层。本发明通过对无取向硅钢的组分及其配比，结合工艺操作进行优化，能够生产得到电磁性能及延伸率均优异的无取向硅钢，从而能够有效满足电工钢缠绕式加工及使用需求，且其制造工序流程短、成本相对较低。

本实用新型属于硅钢技术领域，具体的说是一种硅钢前处理高液回流装置，包括机体；所述机体的侧端固接有一号导管；所述一号导管上安装有二号导管；所述机体的顶端固接有连接管；所述连接管上安装有入泡管；所述二号导管的内侧壁固接有电机；所述电机的输出端固接有扇叶；所述二号导管的顶端内侧壁固接有定位板；所述定位板的侧端转动连接有旋转叶轮；所述二号导管的底端固接有排泡管；通过一号导管和二号导管的配合可以把溢出的泡沫进行导向，通过扇叶和旋转叶轮的配合可以使泡沫快速流动，再通过排泡管排出进入机体的内部，可以使泡沫循环使用，避免泡沫的溢流造成环境的污染及碱液的浪费。

本实用新型公开了一种生产硅钢片的轧制装置，包括工作台，所述工作台的正面开设有收集腔，收集腔的内底壁滑动连接有收纳盒，工作台的上表面分别固定连接有两个支撑板和倒L型滑动台，两个支撑板的相对面分别转动连接有上压辊和下压辊，上压辊的外表面套设有两个调节环，两个调节环的相对面均固定连接有切刀，工作台的上表面开设有与收集腔相连通的下料孔，下料孔的内侧壁开设有滑动槽。该生产硅钢片的轧制装置，通过设置上压辊、下压辊与驱动电机，便于对硅钢片进行传动，通过设置调节环、切刀与固定螺栓，便于根据生产需求调节硅钢片切边的距离，从而使整个装置具有方便对轧制后硅钢片进行切边处理的效果，方便后续轧制工作的进行。

本发明涉及一种用于控制硅钢毛刺状厚度波动的工艺，包括如下步骤；将连铸坯送入加热炉中进行加热，连铸坯入炉温度为400‑680℃，连铸坯在炉时间为185‑220min；将加热后的连铸坯进行热轧，轧辊偏心量为0‑0.025mm，将热轧后的带钢进行卷取；将卷取后的带钢酸洗后进行冷轧，冷轧操作模式由多次阶段升降速模式调整为一次性升降速模式，且在一次性升降速阶段将MN‑AGC增益系数增大；将冷轧后的带钢进行卷取，退火后得到硅钢片成品。本发明所公开的用于控制硅钢毛刺状厚度波动的工艺，该工艺对加热、热轧、卷取及冷轧各工序进行优化协调，能够有效解决硅钢毛刺状厚度波动的问题，实现无取向硅钢全长厚度控制精度的提升，而且无需进行设备和系统改造，容易实现，易于推广。

本实用新型涉及一种用于叠装变压器铁芯硅钢片的装置，包括托板，托板的上表面固定设置有固定板，固定板的内部开设有沉槽；双向螺纹杆，双向螺纹杆设置在固定板的内部，双向螺纹杆的一端贯穿固定板的侧壁并连接有把手；支撑柱，支撑柱的表面开设有连接槽，连接槽的内部铰接有连接杆；有益效果为：本实用新型提出的一种用于叠装变压器铁芯硅钢片的装置在托板的左右两侧设置有两组对称分布的固定板，通过对双向螺纹杆的旋转，螺接在双向螺纹杆表面的两组滑块将会相对移动，铰接在滑块上表面的两组支撑柱将会形成三角形对铁芯进行防护。

一种低温高磁感取向硅钢的热轧方法：经转炉冶炼并浇注成坯；对铸坯加热后进行粗轧：首先确定粗轧减宽量；根据所确定的粗轧减宽量进行粗轧；进行精轧；常规进行下工序。本发明采用低温板坯加热技术，降低了板坯烧损和修炉负担，且边裂发生率比现有技术的不低于18%的基础上能降低5%以上，由此节约资源及降低能耗。