本发明属于金属材料加工技术领域，具体涉及取向硅钢罩式炉高温退火低保温阶段节能工艺，包括：1)将涂镁取向硅钢卷装入密闭的罩式炉中，并向罩式炉内通入氮气将炉内氧气充分排出，使炉内氧含量浓度≤300PPm；2)通电升温并将氮气转换为10m3/h氮气与氨分解气的混合气体，升温2h将温度升温至500‑600℃后，恒温13h；3)将温度氮气与氨分解气的混合气体转换为12m3/h氨分解气，并升温2h将温度升至650℃恒温15h，使内部气体露点小于‑10℃；本发明提供退火工艺，钢卷在高温下不被水蒸汽氧化，消除钢带表面露金、发红、发黑、水印、色泽不均、导通缺陷，降低钢带铁损、提高磁感、降低生产成本。此外，本发明进一步减少退火过程中氨分解气的用量，具有极高的工业应用价值。

采用中、厚板坯生产技术对取向硅钢进行了研制和开发,对热轧及后工序样品进行了金相组织观察和EBSD分析,探讨了两种组织及织构的差异性,研究结果表明:除高温退火样品外,中板坯生产的取向硅钢各工序样品平均晶粒尺寸大;厚板坯生产的取向硅钢热轧和常化样品亚表层Goss织构强;中板坯和厚板坯的脱碳退火板织构没有明显区别。中板坯生产的取向硅钢成本低,产品磁性能和质量与厚板坯相当。 Grain oriented silicon steel was researched and developed by medium thickness slab and thick slab.Microstructures observation and EBSD analysis to the samples of hot rolling and following processes were carried out,respectively.The differences between the two kinds of microstructures and textures were discussed.The results show that the average grain sizes of every process samples are larger except that of high temperature annealing samples of grain oriented silicon steel produced by medium thic... 

提出一种基于粒子群优化算法实现的硅钢涂层厚度近红外光谱检测新方法。首先,采用近红外光谱仪采集获得了硅钢表面绝缘涂层的近红外光谱,然后,采用离散粒子群算法筛选出近红外光谱数据的最佳波长变量并组成新的光谱数据,最后,建立涂层厚度的核偏最小二乘定量分析模型。实验显示,所建定量分析模型对检验样本分析的绝对误差范围为-0.12～0.19μm,最大相对误差为14.31%,完全符合现场检验需要。研究表明,离散粒子群算法可以有效地筛选出携带更多有用信息的波长变量,提高定量分析模型的分析准确度和速度,是一种有效的近红外光谱波长筛选方法,同时,近红外光谱法也是一种有效的硅钢绝缘涂层厚度检测方法。 A novel thickness measurement NIR spectrometry for surface insulation coating of silicon steel based on discrete binary particle swarm optimization(DBPSO) algorithm is presented.First,we used NIR spectrometer to collect the NIR spectra of insulation coating of silicon steel,and then,DBPSO algorithm was used to select the optimal wavelength variates and composed a new spectra set.Last,the authors created the thickness quantitative analysis model using kernel partial least square algorithm.The exp... 

本实用新型涉及钢卷加热装置技术领域，且公开了一种用于硅钢片钢卷制造的加热装置，目前硅钢片钢卷加热不均匀的问题，其包括加热箱，所述加热箱的内腔一侧活动安装有主动轴，主动轴的外侧固定安装有主动齿轮，主动轴的左侧固定安装有位于加热箱外侧的电机，主动轴的两侧均活动安装有从动轴，两个从动轴的外侧均固定安装有从动齿轮，本实用新型，通过电机和主动轴以及主动齿轮的配合，可使得主动轴转动，并通过主动齿轮与两个从动齿轮的啮合，进而使得从动齿轮和主动齿轮同时转动，并通过两个加热盘对加热箱内部进行加热，从而使得固定盘和连接盘之间的钢卷边转动边加热，从而解决了硅钢片钢卷加热不均匀的问题。

【作者】 侯桂芹； 张颖； ...

采用电解法和扫描电镜研究了300 t转炉-RH精炼钙处理对无取向硅钢板（%:≤0.005C、1.2～2.2Si、0.2～0.6Mn、≤0.20P、≤0.005S、0.2～0.6Al、0～0.01Ca）中夹杂物的影响。结果表明,钢中Al含量为0.25%和0.35%时,钢中溶解氧均小于1×10^-4%,钙处理后都会产生CaS夹杂物,尤其是含0.35%Al的钢水;钙处理可以有效减少钢中的夹杂物数量,尤其是0.5μm以下的微细夹杂物数量;钙处理后夹杂物的种类以AlN、CaS为主,同时还含有少量的氧化物夹杂物以及AlN-CaS复合夹杂物,尺寸主要为1.5～5.0μm。 The effect of 300 t converter-RH refining calcium treatment on inclusions in non-oriented silicon steel sheet （%:≤0.005C,1.2～2.2Si,0.2～0.6Mn,≤0.20P,≤0.005S,0.2～0.6A1,0～0.01Ca） has been studied by electrolysis and scanning electron microscope.Results show that with 0.25%and 0.35%Al content in steel,all the dissolved oxygen in liquid is less than 1×10^-4%,and the CaS inclusions are produced after calcium treatment,especial for the liquid containing 0.35%Al;the amount of inclusions in ste... 

从影响高牌号无取向硅钢退火工艺的主要参数入手,介绍高牌号无取向硅钢退火炉在加热、气氛控制、冷却、涂层烘烤方面的新技术,并展望无取向硅钢退火炉的发展方向。 Based on the technology parameters of high-grade non-oriented silicon steel annealing,the new technology of the annealing line,which includes heating,atmosphere control,cooling,coating baking,is introduced,and the development direction of non-oriented silicon steel annealing furnace is pointed out. 

涂层技术在高磁感取向硅钢生产中起着重要的作用.根据生产实践,介绍了高磁感取向硅钢生产中涂层的种类和作用、涂料的成分和对产品性能的影响、涂层工艺质量控制要点和检验方法等,并提出了通过优化涂层工艺改善高磁感取向硅钢性能和外观质量的方法. Surface coating technique plays an important role in producing high magnetic inductivity grain-oriented silicon steel.Based on production practice,this paper describes the types and function of the coating,the composition of the coating and its effect on the product performance,the quality control and inspection method for the coatings,as well as proposes ways to improve the magnetic property and surface quality of the steel by optimizing the coating process. 

一种变压器硅钢片转运吊车，属变压器生产技术领域，包括车架、驱动部和承载部，驱动部连接车架和承载部，承载部上承载硅钢片。车架包括底板、支撑单耳、后耳片，底板前端两侧向前上方各延伸一个支撑单耳，支撑单耳连接驱动部，底板的中后部两侧各具有一个后耳片，后耳片也连接驱动部。驱动部包括连杆、底双耳、支撑双耳、轴座、转轴和液压缸，连杆具有一对，连杆下端具有底双耳，连杆的中下部具有支撑双耳，连杆的顶部具有轴座，底双耳铰接在支撑单耳上，转轴安装在两个连杆顶部的轴座上，液压缸的两端分别连接在后耳片和支撑双耳上。承载部包括托盘、侧部耳片、拉杆、下双耳和上挂耳，托盘两侧各具有一对侧部耳片，拉杆呈倒Y字形结构。

【作者】 李波； 杨晓江； ...

本发明涉及薄规格高牌号无取向硅钢冷轧领域。一种提高超薄规格高牌号无取向硅钢厚度精度的冷轧方法，硅钢成品厚度规格在0.15mm～0.25mm，坯料采用常化酸洗切边后的硅钢卷，初始厚度为2.0～2.3mm，采用二十辊单机架轧机轧制，在轧制过程中，对整个轧制过程进行控制。本发明的有益效果是：解决二十辊轧机超薄规格无取向冷轧硅钢纵向厚度波动同时减小横向同板差的方法。

本实用新型涉及一种堆叠定子硅钢片复位装置，主要包括气动按压装置与弹簧悬架，弹簧悬架中设有的硅钢片放置板，硅钢片放置板中心部位嵌入式连接有滑动杆，滑动杆的一侧设有固定顶针，且滑动杆的顶部还设有弧形倒角，滑动杆一端套接有硅钢片，另一端与固定板连接；固定板两侧上套接有轴套，轴套内滑动设置有定位滑轴，定位滑轴的外部套接有螺旋弹簧组成弹簧减震器，且螺旋弹簧设置在轴套上底面与硅钢片放置板下底面之间；这种结构的设置通过硅钢片放置板上设置的固定顶针，使得硅钢片与硅钢片放置板之间的连接更加稳定，同时通过弹簧减震器的设置可以降低机器手下压的压力，从而增强硅钢片的承受力。