本实用新型公开了一种用于硅钢件的高效激光焊接机，涉及激光焊接机技术领域。本实用新型包括机体、底座和控制柜，底座上表面固定安装有工作平台，机体上表面设置有转动盘，转动盘上表面设置有焊接臂，焊接臂一端设置有连接头，连接头下表面设置有焊接头，焊接头、连接头和焊接臂均与机体电性连接，焊接臂一端设置有转动轴，转动轴一端固定连接有过渡仓，过渡仓一端设置有抽风机，过渡仓另一端设置有出风口，出风口通过过渡仓与抽风机相连通。本实用新型通过在焊接臂一端设置抽风机对着工作平台，将焊接产生的浓烟进行吸收并通过出风口排出避免对人体健康产生影响，通过设置具有防火花和强光功能的防护罩对工作人员的眼睛提供保护作用。

本发明公开了一种高效无取向电工钢的制备方法,属于电工钢技术领域，具体步骤包括:开卷→焊接→清洗→连续退火脱碳→冷却→涂层→绝缘涂层干燥→绝缘涂层烧结→空冷→表面质量检查→分卷包装。本发明使产品的铁损为3.08w/kg，磁感为1.711T，达到了高效无取向电工钢的产品要求，并通过稳定生产，其铁损稳定在3.1w/kg，磁感稳定在1.71T，完全能达到产品需求。

为进行磷酸盐系无铬无取向硅钢涂层烧结固化工艺研究,首先对磷酸盐系无铬无取向硅钢涂层进行热重-差示扫描量热(TG-DSC)分析;然后在不同烧结固化温度条件下,测定涂层板温随时间变化曲线;最终获得涂层烧结固化温度与时间(T-t)工艺曲线。通过中性盐雾试验、动电位极化、交流阻抗、涂层附着力以及扫描电子显微镜(SEM)和能谱(EDS)分析验证。结果表明,根据涂层烧结固化温度与时间(T-t)工艺曲线制备的涂层结构致密、性能优异,证明该工艺曲线具有合理性与正确性。 In order to study the curing process of chromium-free non-oriented silicon steel coatings,phosphatic chromium-free non-oriented silicon steel insulating coating was prepared and TG-DSC analysis of the coating was conducted,then the change of the actual temperature of the coated non-oriented silicon steel sheet with time at different curing temperatures was studied. Based on the experiments,the processing curves of curing temperature vs. curing time( T-t) for the chromium-free non-oriented silico... 

一种冷轧硅钢生产线的带钢卷曲控制装置，由卷取机、导向辊、液压站、伺服阀及其油缸、计算机控制系统、卷取机位移传感器和带钢边部位置探测器组成的卷曲机系统，该系统在带钢辊道的两侧各装有一个带钢边部位置探测器，以分别检测带钢的两个边缘在辊道上的位置，其检测信号分别传送到计算机控制系统中去。计算机控制系统可对两个带钢边部位置探测器输入的信号进行带钢的中心位置计算，并与卷取机位移传感器输入的卷取机中心位移信号进行比较，根据比较结果控制油缸的推杆推动卷取机移动，以使卷取机的卷曲中心与带钢的中心线保持一致。本发明的有益效果是：实现了使卷取机的卷曲中心与带钢的中心线保持一致，因而不再切边，提高了带钢的成材率。

本实用新型公开了一种堆垛硅钢片接料装置，它涉及变压器零部件加工技术领域。导向滚轮沿平移轨道滚动带动接料底座沿平移轨道移动；接料底座上设有剪力臂架，升降油缸驱动剪力臂架调节高度带动滚筒架升降，滚筒架上安装有数排滚筒，滚筒为双链轮滚筒，每排的数个滚筒中，相邻滚筒间通过链条与链轮的配合连接，电机驱动一个滚筒转动带动一排的数个滚筒同时转动；每排的数个滚筒上方两侧分别设有导向槽板，导向槽板与滚筒架固定连接。本实用新型的优点在于：可对左右侧、不同层的硅钢片柱进行出料，可同时对多柱硅钢片进行出料，出料效率高；接料的稳定性提高，接料底座移动稳定性提高，接料后硅钢片柱可直接输送至叠装处，操作便捷，转运效率高。

利用FE-SEM、EDS分析了含不同抑制剂成分的成品取向硅钢中夹杂物的组成和形貌,统计其尺寸及数量分布;结合对磁性能测试的结果,分析了Sn、Cu、Nb和Cr对取向硅钢磁性能影响的机理。结果表明:含Sn的取向硅钢试样中夹杂物主要为块状的微米级Al-Ti-C-N-O复合物,还有少量的球形Al-N-O颗粒和块状Ti-C-N-O颗粒,棒状夹杂物较少;含Cr的取向硅钢试样中夹杂物主要为球形的微米级Al2O3,还有少量Cu-Al-N-O-S复合物,棒状夹杂物和不规则夹杂物均较少;含Cr试样中1~3μm夹杂物的平均尺寸较含Sn试样小,但数量多,而大于3μm夹杂物的平均尺寸较含Sn试样大,但数量很少。磁性能测试结果表明,外场为800A/m和2500A/m时,含Cr试样磁感应强度偏低,铁损值P1.7/50较含Sn试样高,为1.171W/kg。 The composition and morphology of inclusions in the finished grain-oriented silicon steels are analyzed by using FE-SEM and EDS, and the number density and size distribution of the inclusions are counted. The influence mechanism of Sn, Cu, Nb, and Cr on the magnetic properties of the steel is also discussed. Results show that the inclusions composition in the grain-oriented silicon steel samples containing Sn is mainly block Al-Ti-C-N-O, compounding with a few spherical Al-N-O and block Ti-C-N-O... 

无取向硅钢中夹杂物的存在会抑止晶粒生长,使基体的均匀连续性中断,其在钢中的形态、含量及分布情况都不同程度影响着硅钢的性能,尤其是对磁性能起关键的作用。因此,全尺度分布考察夹杂物对无取向硅钢夹杂物的研究极为重要。本实验确定了适用于不同牌号无取向硅钢夹杂物全尺度分布的分析方法:样品制备—小样电解—过滤喷金—根据不同牌号的要求选择合适的放大倍率扫描观测—夹杂物颗粒的分类统计。通过统计的结果,结合电解的失重量可以得到不同尺度的体积分布数据。实验分析了不同牌号和工艺无取向硅钢夹杂物的种类、形貌、大小和尺度分布,并初步考查了夹杂物与磁性能的关系,对无取向硅钢的工艺研究具有一定参考价值。 Inclusions in non-oriented silica steel could inhibit the growth of grain and cause discontinuity of micro-structure.The configuration,content and size distribution of inclusion have different effects on the performance of silica steel,especially significant on the magnetic property.Therefore,it is very useful to completely characterize inclusions with full size distribution in silica steel.In our research,full size analysis method for inclusion in silica steel had been established as follows: s... 

本文对某厂硅钢DR510温度、成分及过程控制水平和成品的组织、力学性能进行了研究,并在此基础上提出了工艺优化方案,有一定的借鉴和推广价值。 In this paper,the critical process and the products quality,including temperature,composition and process controlling level,the organization and mechanical properties of the finished product,were studied.On the basis of that the optimized technical plan provided,and this control technology is worth using and spreading. 

研究了铝和铬元素在无取向电工钢晶粒长大过程中对织构及晶界变化的影响规律。试验结果表明:电工钢在晶粒长大过程中的主要织构组分均为{111}<112>。在晶粒生长期间,不加铝的1号试样中,{111}<112>、{111}<110>织构组分强化,而{100}<001>织构组分弱化;与1号试样相比,在加入0.2%的铝(质量分数,下同)的2号试样中,{111}<112>、{111}<110>织构组分强化(增加)的速率下降,{100}<001>织构组分变化不明显,甚至稍有增加。在含铝的试样中再加入0.3 5%的铬之后(3号试样),{111}<112>{、111}<110>和{100}<001>织构组分的变化规律与1号试样相似,但当电工钢中加入0.72%的铬之后(4号试样),上述3种织构组分的变化规律与2号试样相似。对于在晶粒生长期间持续变化的3种织构组分而言,1号试样的{1 1 1}<112>和{111}<110>织构组分的高(低)取向差角度晶界频率下降(... The effect rule of Aluminm and Chromium on texture and grain boundary transformation in the nonoriented electrical steel during grain growth was investigated.The experimental result shows that the main texture component is {111}<112> in the electrical steel.The {111}<112> and {111}<110> components in specimen 1 without Alumium were strengthened during grain growth whereas {100}<001> component was weakened.But the growth rate of {111}<112> and {111}<110> compon... 

采用化学气相沉积(CVD)渗硅处理工艺连续制备6.5%Si高硅钢,具有优质的软磁性能,通过理论研究化学反应并且用简单的试验设备做进一步的探讨。根据试验的结果对连续制备6.5%Si高硅钢的CVD工艺构造提出全面、有效的建议,实现制备6.5%Si高硅钢系统。 CVD method for continuously manufacturing 6.5%Si Steel Sheet has excellent soft magnetic.Carried out a theoretical study of related chemical reaction and performing basic research with a simple test apparatus.Based on the results,finally proposed an overall process configuration to realize such a production-CVD method for continuously manufacturing 6.5%Si Steel Sheet. 

【摘要】 <正>为了确保电工钢的产品质量,在生产线...

结合工业化生产的50A1300牌号无取向硅钢,分析了化学成分、RH精炼脱氧方式、板坯装炉温度以及热轧平整工艺等对磁性能的影响,探讨成品钢磁性能的改善。结果表明,采取改善后,50A1300牌号无取向硅钢的磁性能得到明显改善。2012年,该钢种平均铁损、磁感应强度分别达到5.26 W/kg、1.762 T,能够较好地满足用户市场需求及同行对标需要。 Based on the industrial manufacture of 50A1300 grade non-oriented silicon steel sheets,effects of chemical composition,deoxidization method in RH vacuum refining,charging temperature of steel slabs,hot rolling and flattening progress on magnetic properties are analyzed.The optimization methods of magnetic properties of steels are discussed. Results show that the magnetic properties are obviously improved by the adopted measures above. In 2012,the average core loss and the magnetic induction of 5...