硅钢资料

通过对湿H2气氛下,相同退火温度、不同退火时间的CGO硅钢初次再结晶样品进行金相组织观察,并进行了EBSD微观织构分析,研究了CGO硅钢初次再结晶过程中的组织及再结晶织构演变行为。结果表明,在湿H2气氛下,820℃保温,CGO硅钢初次再结晶过程约在120 s时完成。随着退火时间的延长,γ面上{111}<112>织构含量逐渐减少,{111}<110>织构先减少后增多,随着再结晶的完成,部分{111}<112>取向晶粒向高斯{110}<001>取向转化的同时,也向{111}<110>取向转化,高斯{110}<001>织构含量逐渐增多。高斯取向晶粒较多是由{111}<112>取向晶粒转化而来,同时也证明了CGO硅钢高斯取向晶粒的二次再结晶异常长大生长机制为择优形核。 Microstructure development and texture evolution of conventional grain oriented silicon steel,which were annealed at same annealing temperature and different annealing time under wet H2 atmosphere,were investigated through metallographic observation and electron backscattered diffraction analyzing.The results show that the primary recrystallization finishes in 120 s at 820 ℃ under wet H2 atmosphere.With the extending of annealing time,{111}<112> texture decreases,{111}<110> texture d... 

结合工业化生产的无取向硅钢,进行了RH精炼添加稀土合金实验。结果表明,1.15%(质量分数)Si钢的脱硫反应,主要发生在添加稀土合金之后的前5min。最佳的稀土合金添加量为0.6～0.9kg/t钢。钢液经过稀土处理后,加入的稀土总量越多,稀土氧硫化物夹杂物的尺寸就越大,但热轧带钢再结晶效果会逐渐变差,成品带钢晶粒尺寸先是快速长大,而后逐渐减小。最佳的钢中存留稀土含量与钢的化学成分有关,应严格控制在2.0×10-3%～6.0×10-3%(质量分数)。在此范围内,钢的铁损先是快速降低,而后缓慢升高,钢的磁感应强度则单调降低。 Based on the industrial production of non-oriented electrical steel,rare earth(RE) alloy treatment during the RH refining process was studied.The results showed that the effects of desulfurization and total concentration of RE remained in steel mainly depended on the chemical compositions of different steel grades.For 1.15wt% Si steel grade,the desulfurization reaction mainly focused on the initial 5min after RE alloy added during the RH refining process.The suitable RE alloy addition was 0.6-0.... 

本实用新型涉及一种点火器线圈硅钢片结构，包括E型件和I型件，其特征在于：所述E型件和I型件可组合成日字形；所述E型件和I型件的棱面外周顶面和底面均设置切棱；所述E型件包括竖边和设置在竖边三个横边，其中所述竖边的转角位置圆角处理，竖边外侧为弧形边；所述竖边与三个横边接触的位置设置孔眼；位于中间位置横边外侧设置凹部，位于下端横边外侧设置凸部；所述I型件靠近E型件一侧中间和下端位置设置凸部和凹部，其上端与E型件上端横边外侧重合接触。本实用新型设计新颖，改进巧妙，由于E型件具有弧形边可以有利于拾取，方便工作操作，同时采用采用接触的方式接触，增加了组合体的稳定性。

【作者】 卢鹏； ...

从取向硅钢生产路线的选择、工艺技术的改进和生产设备的改造三方面进行了生产取向硅钢的节能降耗技术改造.通过完善多元抑制剂配方生产低温取向硅钢,通过加抛丸的酸洗、带面超声波清洗、改进连续退火炉以及余热循环利用等技术改造,使2012年取向硅钢的产量与未进行技术改造前的2009年相比提高了2.5倍,产品磁性上升了一个半牌号,能耗下降了8.9%,成材率提高了6.4%,生产成本下降了22%,综合效益显著. Energy saving technological transformation was carried out in the production of grain oriented silicon steel from three aspects of the oriented silicon steel production process route selection,technology improvement and equipment renovation.Through the improvement of multiple inhibitor formulations for producing low-temperature grain-oriented silicon steel,and by adding the blasting pickling,the belt surface ultrasonic cleaning,improvement of continuous annealing furnace,waste heat recycling tec... 

本发明属于退火工艺技术领域，公开了一种高牌号无取向硅钢剪切方法，包括：待剪切带钢由夹送辊输送到达剪切位后，夹送辊释放对所述待剪切带钢的夹持；位于所述待剪切带钢下方的下剪刃上移，推顶所述待剪切带钢在低张力状态下持续向上运动；在所述待剪切带钢与上剪刃接触后，将所述待剪切带钢剪断。本发明提供的高牌号无取向硅钢剪切方法能够极大的减少高牌号无取向硅钢的剪切缺陷，降低废品量，提升剪切效率。

为了提升新能源车用驱动电机的功率密度,各大电机厂商都在不断地提升电机转速,随之而来的问题就是电机的铁耗也在不断增高,如何降低电机铁耗成为了电机厂商必须要解决的难题。本文讨论了电机铁耗的组成部分及影响因素,并对1台8极48槽的永磁同步电机分别使用3种不同厚度的材料进行仿真,对比其效率及铁耗分布,推导出驱动电机中硅钢厚度、铁耗及成本的关系,最后对驱动电机选材提出建议。 In order to increase the power density of traction motor for new energy vehicles,major motor manufacturers have been constantly increasing the motor speed.The following problem that manufacturers have to solve is how to reduce the increasing iron loss when the motor speed is increased.The components and influencing factors of motors’ iron loss were discussed in this paper,and an 8-pole 48-slot permanent magnet synchronous motor using three different thickness materials was simulated.To compare i... 

叠片系数是冷轧无取向电工钢的重要质量指标。为了提高叠片系数,必须保证无取向电工钢板形良好以及横向厚差小。针对攀钢冷轧厂4机架HC轧机轧制无取向电工钢的边部减薄问题,以无取向电工钢横向厚差最小作为目标函数,建立了一套针对无取向电工钢边部减薄控制的辊型曲线优化数学模型,开发了无取向电工钢专用辊型曲线,使无取向电工钢横向厚差从25μm降低到10μm以下,取得了良好的控制效果。 The lamination factor is an important quality index of non-oriented silicon steel strip.Considering the lamination factor,the non-oriented silicon steel must have a good shape and a smaller transverse thickness difference.In order to solve the edge thinning of non-oriented silicon steel strip in Panzhihua Steel,a mathematic model for designing the roll shape is built.In the model,the transverse thickness difference of non-oriented silicon steel strip is taken as the objective function.Based on t... 

针对某厂DMS森吉米尔轧机生产无取向硅钢表面麻面缺陷的问题，根据生产实际，对其形成原因从乳化液及工作辊两方面因素进行了分析。结果表明：乳化液对麻面缺陷的产生有一定影响，但不是主要因素，主要原因是由于二十辊森吉米尔轧机工作辊辊径较小，轧制相同长度带钢轧辊运转周期较大，容易产生疲劳失效而导致。为此，提出通过调整冷轧工序成品轧制道次的压下率以减小轧制力，从而减小工作辊的磨损疲劳；通过对轧制乳化液浓度、温度的合理控制，以改善润滑效果、提高轧制速度，而进一步缓解轧辊疲劳的改进措施，使该钢厂无取向硅钢麻面缺陷发生率由原来的18%降至0.8%,带钢表面质量明显改善。 For the problem of surface pockmarks of non-oriented silicon steel strip produced by a DMS Sendzimir mill, based on the production practice, the formation causes were analyzed from two aspects of emulsion and working roll. The results show that the emulsion has a certain effect on the formation of surface pockmarks defects, but it is not the main factor. The main reason is that the working roll diameter of the 20-high Sendzimir mill is small, and the running period of the roll rolling the same l... 

该电磁钢板用涂布组合物含有环氧树脂、酚类固化剂(A)、以及从芳香族胺和双氰胺中选择的一种以上的胺类固化剂(B)，所述酚类固化剂(A)的含量相对于所述环氧树脂100质量份为1～40质量份，所述胺类固化剂(B)的含量相对于所述环氧树脂100质量份为0.5～5质量份。

本发明涉及一种取向硅钢连续高温罩式退火炉及其退火工艺，其包括梯度窑炉，所述梯度窑炉包括A1段退火炉、B段退火炉、C段退火炉、D1段退火炉、A2段退火炉和D2段退火炉；所述A1段退火炉、B段退火炉、C段退火炉、D1段退火炉、A2段退火炉和D2段退火炉依次连接；其中，A1段退火炉、B段退火炉、C段退火炉和D1段退火炉炉顶高度不同，A1段退火炉与A2段退火炉炉顶高度相同，D1段退火炉与D2段退火炉炉顶高度相同。上述在炉顶结构上根据生产工艺，采用的梯度分层次布局，使其在炉顶形成障碍，减缓气流的流通速度达到节能的目的，同时对各个工艺段炉窑内温度的均匀性有提升，并且能够提高产品的质量。

本实用新型公开了一种电工钢加工用绝缘喷涂装置，包括底板，所述底板顶部外壁的中央位置设有安装通孔，所述安装通孔的两侧内壁上均通过轴承连接有转杆，所述底板的一侧外壁上固定连接有第一电机，第一电机输出轴的一端连接有连接杆，连接杆的一端固定连接在一个转杆的一端，两个所述转杆的一端固定连接有同一个放置架，所述放置架的两侧内壁上均固定连接有两个伸缩杆，四个所述伸缩杆活塞杆的外壁上均设有复位弹簧。本实用新型第二电机可以驱动每一个空心管转动的过程中，空心管内的绝缘漆从管壁的喷孔喷洒而出，而空心管外的扇板则配合交错分布的喷孔将雾化喷洒的绝缘漆打乱喷洒在电工钢上，全面且充分的完成喷涂。