本发明提供了一种无取向硅钢RH顶枪喷粉脱硫工艺,RH脱碳结束测温定氧,立即加入铝粒脱氧合金化、之后立即依次连续加入合金进行成分调整,合金加完后立即开始顶枪喷粉;加入铝粒的量=铝粒理论加入量+0.2‑0.4kg/t钢;喷粉时,控制喷粉速度与钢液循环流量相匹配;本发明从真空条件下脱硫热力学和动力学角度出发对具有顶枪喷粉功能的RH脱硫工艺进行改进,提高脱硫率。
2021-11-30 146 6.8

对冷轧无取向硅钢在冶炼过程中各个工序的顶渣进行了检测,分析了顶渣变化原因,并得出结论:硅钢生产宜采用复吹转炉,以降低吹炼终点渣中TFe含量,进而减轻对精炼的压力;使用低S、低Al2O3含量中间包覆盖剂;RH脱氧及合金化顺序采用先加硅铁后加铝;首罐宜经LF提温并降低渣中TFe。 The top-surface slag used for the various production processes in smelting coldrolled non-oriented electrical steel is tested and based on tested results the cause of the top surface slag change is analyzed.So it is concluded that the combined blown converter is more suitable to be used for smelting electrical steel in order to reduce the content of TFe in slag at blow end point and then much better results can be achieved during the period of refining.Secondly the tundish flux contenting low co... 
2013-03-28 140 5.8

研究了CSP工艺流程生产的硅含量为1.5%的无取向电工钢在不同常化温度下对磁性能的变化。研究结果表明:随着常化温度的提高,热轧板的晶粒尺寸增大,且组织均匀性提高;此外成品的有利织构组分{100}<0vw>、α、η增强,不利织构组分减弱;铁损P1.5/50呈下降趋势,磁感B50上升平缓。在常化工艺为970℃×2.5min下,对应的铁损P1.5/50<3.4W/kg,磁感B50>1.74T。 The effect of normalizing temperature on the magnetic properties of non-oriented electrical steel containing 1.5%silicon produced by CSP process was studied.The results show that with increasing normalizing temperature,the average grain size of hot-rolled plate increases and the microstructure uniformity is improved.Furthermore,the texture components of finished products are improved through enhancing of{100}<0vw>,αandηtextures and weakening of{111}<112>texture;the core loss P1.5/50 ... 
2014-03-28 137 5.8

本发明涉及一种提高取向硅钢冷轧加工性的生产方法,工艺流程为:冶炼、连铸、热轧、常化、酸洗、冷轧、脱碳渗氮、涂MgO、高温退火、涂绝缘层及热拉伸平整;粗轧中坯厚度35‑45mm,两段常化后进行带钢横向分段式冷却水分布。本发明通过对热轧中坯厚度、终轧温度及卷取温度,常化冷却水量及控制方式的调控,使轧前表层晶粒尺寸降低5‑10μm、珠光体体积分数降低6%,轧材冷轧加工性明显改善、成材率可提高8%以上。通过后续冷轧、脱碳退火和高温退火等工序处理,可保证完善的二次再结晶组织及良好磁性能。
2021-05-25 186 6.8

本发明公开了一种适宜缠绕式加工的低铁损无取向硅钢及其生产方法,属于硅钢生产技术领域。本发明的无取向硅钢包括以下质量百分比的元素:Si:1.5~2.5%,Mn:0.15~1.0%、Als:0.5~1.5%,其余为Fe及不可避免的杂质。其生产工艺步骤为:铁水预处理、转炉冶炼、真空处理、连铸;加热热轧;常化处理;冷轧、退火;保温、冷却;涂覆绝缘层。本发明通过对无取向硅钢的组分及其配比,结合工艺操作进行优化,能够生产得到电磁性能及延伸率均优异的无取向硅钢,从而能够有效满足电工钢缠绕式加工及使用需求,且其制造工序流程短、成本相对较低。
2021-10-25 154 6.8

【作者】 卢鹏; ...
2013-03-28 105 5.8

对CSP流程生产的高磁感无取向电工钢50W1300在偏离轧制方向不同角度处的磁性能进行了测试和分析。结果表明:在偏离轧向不同角度处,磁性能差异显著,尤其在α=60°时磁感最低;偏离轧制方向不同角度处的磁性能大小取决于织构类型、强度及分布状态;增强{100}<0vw>和α、η取向的有利织构组分,降低不利的γ取向织构组分,且使有利织构组分分布越漫散,磁各向异性越小。 Magnetic properties of high magnetic induction non-oriented electrical steel 50W1300 produced by CSP processes were investigated with different direction in relation to the rolling direction.The result shows that magnetic properties are significantly different in relation to the rolling direction,in particular,the minimum magnetic induction occurs at 60° in relation to the rolling direction.Magnetic properties of different directions in relation to rolling direction depend on type and distributi... 
2011-04-28 158 5.8

本发明一种解决取向硅钢热轧板晶粒粗大的方法,在取向硅钢的成分设计中减少固溶温度较高的MnS的含量,降低铸坯加热温度,同时计算实际取向硅钢成分中γ‑相含量与温度之间的关系,依据计算结果设计取向硅钢的热轧工艺,可以保证20%~30%的γ‑相数量,成功解决取向硅钢热轧板晶粒粗大的问题。
2021-04-15 135 6.8

【作者】 卢鹏; ...
2014-03-28 114 5.8

本发明公开了一种轻便电动自行车轮毂电机用无取向电工钢及制造方法,属于无取向钢领域。针对现有小型电机无取向钢加工难度大,效率低的问题,本发明提供一种轻便电动自行车轮毂电机用无取向电工钢,包括如下重量百分比的各组分:Si:1.50%~3.00%;Als:0.50%~2.00%;Mn:0.20%~1.00%;P:0.01%~0.20%;C:≤0.005%S:≤0.03%;N:≤0.03%;Ti:≤0.005%,其余为铁和不可避免的杂质;其中C、S、N和Ti的重量百分比满足下式:C%+S%+N%+Ti%≤0.01%。本发明通过合理控制元素含量提高硅钢的延塑性,便于加工。本发明提供的制造方法降低卷绕铁芯中的涡流和磁滞损耗,同时能够避免钢卷表面氧化和表面氮化物析出,降低铁芯损耗,与现有同铁损级别无取向硅钢相比延伸率较高,后续冷加工性能更加优异。在保证优良性能的同时便于加工。
2021-03-29 126 6.8

为开发高效电机用冷轧无取向电工钢,借助实验室薄板坯连铸连轧模拟设备及扫描电镜、透射电镜等检验手段研究了成分、组织、织构和析出物等对无取向电工钢磁性能的影响规律;结果表明:常化处理使组织均匀化并增加有利于磁性提高的织构组分;采用CSP流程开发的高效电机用无取向电工钢铁损平均值3.4 0 W/kg,磁感≥1.68 T。 In order to develop electrical steel for high efficiency motor,effect of components,microstructure,texture and precipitation on magnetic property of electrical steel are analyzed.From the result,normalizing treatment makes microstructure uniform and increases component of favorable texture.Iron loss of electrical steel developed by CSP line is 3.40W/kg and magnetic induction is more than 1.68T. 
2011-01-28 170 5.8

本发明涉及一种含磷无铝高效无取向硅钢生产方法,生产方法取消常化工艺,具体步骤如下:1)将钢水冶炼至目标成分后,浇铸成坯;2)板坯热装,热装温度≥500℃,热轧板坯加热炉均热段板坯温度1150~1200℃;终轧温度控制在860~930℃,卷取温度700~800℃3)酸洗后冷轧,控制冷轧整体压下率80%以内,至成品厚度;4)连续退火炉快速加热段温度设定1050~1180℃,增加有利织构组织形核,均热段温度设定830~950℃,全氮气干气氛保护,退火工艺速度120~150m/min,满足晶粒度8~4级。本发明不需进行热轧卷常化处理,降低了制造成本。
2021-08-19 160 6.8