硅钢资料

对无取向硅钢炼钢全流程钢液增钛的原因进行了分析,认为铁水钛含量、转炉出钢温度、转炉下渣量、精炼渣TiO₂含量、钢水罐及RH浸入管混钢种生产是影响钢液增钛的主要原因。通过采取低钛铁水冶炼,减少转炉下渣量,提高出钢温度,添加白灰改质精炼渣等措施,均能够降低钢液中的钛含量。 After analyzing the causes leading to increased content of titanium in molten nonoriented silicon steel during whole steelmaking process, it was concluded that such factors as content of titanium in hot metal, tapping temperature from converter, quantity of roughing slag entered into the ladle from converter, content of TiO₂ in refining slag, molten steel ladle car,carrying out the steelmaking of different steel grades by the same ladle and same RH immersion tube were the main causes ... 

通过对35W300高牌号0.35 mm冷轧无取向电工钢卷(/%:0.002C、2.71Si、0.22Mn、0.015P、0.003S、0.0020N、0.55Als)头、中、尾组织、织构及对应的磁性能的试验研究,发现因热轧时12 MPa高压水连续冷却造成接触轧辊的钢卷头、中、尾在不同温度下轧制,卷取后钢卷头部处于卷心、温度略高而冷却速度略低于钢卷尾部,致使钢卷纵向组织、织构不同,成品卷头、尾各250 m内磁感逐渐增加,铁损逐渐降低,250 m外至钢卷中部磁性能稳定。通过将热轧辊的冷却方式改为周期冷却和卷取后的层流冷却改为钢卷70 m后开始冷却,至钢卷尾部70 m前停止冷却的方式使得钢卷纵向铁损差异明显减小,磁感差异略有改善。 According to the test research on structure and texture of head,meddle and end of 35W300 high grade 0.35 mm cold rolled non-oriented electrical steel strip coil(/%:0.002C,2.71Si,0.22Mn,0.015P,0.003S,0.002 0 N,0.55Als) and corresponding magnetic properties,It is found that due to 12 MPa high pressure water continuous cooling the roller in hot rolling process led to head,middle and tail of strip rolling at different temperature and after coiling the head of strip coil being in center of coil led t... 

【作者】 卢鹏； ...

结合冶炼无取向硅钢的生产实际,对钢中硫的来源,以及炉渣性质、钢水温度、底吹强度对脱硫的影响进行了分析。研究表明,转炉钢中硫的主要来源为铁水、废钢、铁水渣及石灰带入;冶炼硅钢时,终渣碱度为3.0~3.5,w((FeO))≤20%,终点钢水温度大于等于1 680℃,加大底吹搅拌强度能提高转炉脱硫效果。硅钢平均出钢硫的质量分数为0.004 8%,能满足无取向硅钢对硫含量的要求。 With the actual production of non-oriented silicon steel,the source of sulphur and the effect of metallugic parameters like slag properties,temperature of molten steel and bottom stirring on desulphurizing ability were investigated.The results show that the main source of sulphur is molten metal,scrap,the remaining slag volume in hot metal and lime.The degree of desulphurization for smelting silicon steel can be increased through adopting the following measures,such as the basicity of finishing ... 

本发明涉及一种防止低温加热取向硅钢热轧边裂的方法，包括：1)控制取向硅钢铸坯进入加热炉前的表面温度；2)控制加热段各段炉气温度；3)二加热段采用加速加热；4)控制总加热时间；5)控制出炉温度；6)控制精轧道次及侧压量；7)控制精轧道次及终轧温度；8)精轧前对钢带边部进行加热补偿。本发明通过合理制定取向硅钢的加热温度、加热时间和轧制工艺制度，避免或消除了低温加热取向硅钢热轧边裂问题。

本发明公开了一种轻便电动自行车轮毂电机用无取向电工钢及制造方法，属于无取向钢领域。针对现有小型电机无取向钢加工难度大，效率低的问题，本发明提供一种轻便电动自行车轮毂电机用无取向电工钢，包括如下重量百分比的各组分：Si：1.50％～3.00％；Als：0.50％～2.00％；Mn：0.20％～1.00％；P：0.01％～0.20％；C：≤0.005％S：≤0.03％；N：≤0.03％；Ti：≤0.005％,其余为铁和不可避免的杂质；其中C、S、N和Ti的重量百分比满足下式：C％+S％+N％+Ti％≤0.01％。本发明通过合理控制元素含量提高硅钢的延塑性，便于加工。本发明提供的制造方法降低卷绕铁芯中的涡流和磁滞损耗，同时能够避免钢卷表面氧化和表面氮化物析出，降低铁芯损耗，与现有同铁损级别无取向硅钢相比延伸率较高，后续冷加工性能更加优异。在保证优良性能的同时便于加工。

本发明涉及一种冷连轧法生产无取向高硅钢的方法，RH真空脱碳处理后，铝脱氧及部分铝合金化，合金化后大罐钢水净循环大于3次或大于5分钟；熔炼合格钢水至连铸开浇前静置时间大于二十分钟；控制过热度5～15℃；采用电磁搅拌，控制等轴晶比例45％以上；3)热轧工序板坯装炉温度大于750℃；常化使晶粒尺寸在90～110μm范围内；连续退火炉加热段温度设定950～1150℃，均热段温度设定900～1050℃，全氮气干气氛保护，控制晶粒尺寸120～170μm。生产全过程中的热履历参数控制，充分发挥设计的微合金元素功能，改变析出物的组成、大小、形态及分布。

利用场发射电镜及能谱仪研究了取向电工钢薄、厚板坯铸锭中不同区域的析出相差异,确定了MnS、AlN及Fe3C的析出顺序和形貌特征。结果表明AlN以先析出的MnS为形核核心,形成粗大微米级的复合析出相。针状Fe3C既可以在复合析出相表面形成也可以在基体中单独出现,主要受冷却速度的影响。在1250℃保温1～2 h,AlN、Fe3C均可完全回溶,但部分MnS仍不回溶。MnS尺寸随着保温时间延长而增大。导致热轧板中沿轧向分布的粗大MnS,减弱了粒子钉扎力。 Precipitates in thin and thick slabs of electrical silicon steel were investigated by means of field emission SEM and EDS analysis.The precipitation sequence and the morphology of MnS,AlN and Fe3C particles were identified.AlN particles are observed to be nucleated on surface of MnS forming micron-meter-sized complex particles.Acicular Fe3C can precipitate on surface of the complex MnS/AlN particles or directly from matrix depending on cooling rate of the slabs.After holding at 1250 ℃ for 1-2 h,... 

本发明涉及一种含磷高磁感无取向硅钢的生产方法，工艺路线：铁水脱硫－转炉冶炼－RH精炼－连铸－热轧－酸洗－冷轧－连续炉退火－涂层－性能检验－包装，具体步骤包括：1)将钢水冶炼至目标成分后采用连铸方式将钢水铸成坯；2)热轧板坯加热炉均热段板坯温度950～1050℃，终轧温度控制在780～830℃，卷取温度600～680℃；3)酸洗后冷轧，控制冷轧整体压下率80％以上，至成品厚度，增加剪切带组织；4)连续退火炉快速加热段温度设定1000～1150℃，增加有利织构组织形核；均热段温度设定750～830℃，全氮气干气氛保护，退火工艺速度110～150m/min，满足晶粒度8～4级。本发明在减少硅、铝、锰合金添加量的情况下，改善铁损提高磁感性能，提高机械性能。

本发明公开了一种自主学习的高硅钢软磁复合铁芯智能化生产系统及生产方法，属于软磁复合铁芯智能化生产技术领域。本发明的生产系统包括数据输入模块、数据分析模块、数据输出模块、通信模块、数据修正模块；生产方法为：用户通过输入模块选择目标性能参数及生产控制模式，系统生成生产过程关键参数，并由输出模块输出给用户；用户确认后形成控制指令，并发送至生产设备进行生产。本发明的系统不仅能够根据高硅钢铁芯产品的目标性能参数自动生成合理的操作条件，还能根据历史数据和产品检化结果对系统内置的关系模型不断进行优化、完善，能够有效提高产品产量和质量、减少浪费、降低成本。

通过对辉光放电发射光谱参数的优化,以铁元素为内标来消除基体效应,建立了测定硅钢薄板中微量硼元素的方法。优化的实验参数为:放电电压1200 V,放电电流50 mA,预溅射时间40 s,积分时间10 s。校准曲线硼元素含量范围0.0001%~0.022%,相关系数大于0.999,测量结果与认定值一致,相对标准偏差小于10%。完全能够满足日常分析测试的要求。 A glow discharge optical emission spectrometry(GD-OES) method for determining trace boron element in silicon steel sheets were established through optimization of instrumental parameters and using Fe element as an internal standard to eliminate the matrix effect.The optimized instrumental parameters included discharge voltage,discharge current,pre-sputtering time and integration time,which are 1200 V,50 mA,40 s,and 10 s,respectively.The content of boron element that can be determined from the ca... 

对CSP流程生产的无取向电工钢M50W800不同尺寸样品的磁性能进行了测试和分析,结果表明:采用不同单片检测的磁性能结果与标准的Epstein方圈样品检测对比,存在明显的偏差;且同一尺寸的单片纵横向样品之间相比较,对应的磁性能差异性也较大。几种不同尺寸的单片样品,以320mm×30mm尺寸的纵横向平均值最接近标准Epstein方圈样的性能值,其铁损偏差最小。 The magnetic properties of M50W800 non-oriented electrical steel produced by CSP process were tested and analyzed with samples of different sizes,showing that significant deviation existed compared to that of Epstein square circle sample.In particular,obvious difference in magnetic properties also existed between longitudinal and transverse samples of the same size.For test samples of different sizes,the average magnetic properties of 320mm×30mm samples are the closest to that of Epstein square ...