硅钢资料

通过对35W300高牌号0.35 mm冷轧无取向电工钢卷(/%:0.002C、2.71Si、0.22Mn、0.015P、0.003S、0.0020N、0.55Als)头、中、尾组织、织构及对应的磁性能的试验研究,发现因热轧时12 MPa高压水连续冷却造成接触轧辊的钢卷头、中、尾在不同温度下轧制,卷取后钢卷头部处于卷心、温度略高而冷却速度略低于钢卷尾部,致使钢卷纵向组织、织构不同,成品卷头、尾各250 m内磁感逐渐增加,铁损逐渐降低,250 m外至钢卷中部磁性能稳定。通过将热轧辊的冷却方式改为周期冷却和卷取后的层流冷却改为钢卷70 m后开始冷却,至钢卷尾部70 m前停止冷却的方式使得钢卷纵向铁损差异明显减小,磁感差异略有改善。 According to the test research on structure and texture of head,meddle and end of 35W300 high grade 0.35 mm cold rolled non-oriented electrical steel strip coil(/%:0.002C,2.71Si,0.22Mn,0.015P,0.003S,0.002 0 N,0.55Als) and corresponding magnetic properties,It is found that due to 12 MPa high pressure water continuous cooling the roller in hot rolling process led to head,middle and tail of strip rolling at different temperature and after coiling the head of strip coil being in center of coil led t... 

本发明涉及一种冷连轧法生产无取向高硅钢的方法，RH真空脱碳处理后，铝脱氧及部分铝合金化，合金化后大罐钢水净循环大于3次或大于5分钟；熔炼合格钢水至连铸开浇前静置时间大于二十分钟；控制过热度5～15℃；采用电磁搅拌，控制等轴晶比例45％以上；3)热轧工序板坯装炉温度大于750℃；常化使晶粒尺寸在90～110μm范围内；连续退火炉加热段温度设定950～1150℃，均热段温度设定900～1050℃，全氮气干气氛保护，控制晶粒尺寸120～170μm。生产全过程中的热履历参数控制，充分发挥设计的微合金元素功能，改变析出物的组成、大小、形态及分布。

对欧盟市场汽车压缩机专用产品进行技术解析,对比分析了其电磁性能、退火和发蓝处理、物理性能、化学成分、应用特点等参数。探讨国内外电工钢产品应用方式的不同特点,并结合鞍钢自身工艺装备和炼钢、热轧、冷轧工艺参数介绍了其生产可行性。提供了冶金工艺流程下,后工序电工钢专业生产线及传统冷轧系统生产线两种生产方式,均能满足用户最终使用要求。 The technology of automotive compressor accommodation manufacture of European Economic and Monetary Union market was described.The magnetic properties,annealing bluing,physical properties,chemical composition,application parameters were analysed.The different characteristics of the application of electrical steel products,the feasibility of manufacture on the existing technology and equipment,steelmaking,hot rolled,cold rolled technical parameters were discussed.The professional product line of ... 

本发明公开了一种切口耐蚀性良好的无取向硅钢及其生产方法，属于电工钢生产技术领域。本发明的无取向硅钢包括以下质量百分比的元素：Si：0.2～2.7％，Mn：0.15～1.0％、Als：0.5～1.0％，Cr：0.1～0.3％；Ni:0.2～0.5％，P：≤0.01％，其余为Fe及不可避免的杂质。其生产工艺为：铁水预处理、转炉炼钢、真空处理、连铸、加热、热轧、酸洗、冷轧、退火处理和涂覆绝缘层。本发明通过合理的成分配比以及相匹配的生产工艺进行生产，最终得到了切口耐蚀性优良的低铁损、高磁感的无取向硅钢，从而能够有效满足电工钢的使用需求。

本发明公开了一种轻便电动自行车轮毂电机用无取向电工钢及制造方法，属于无取向钢领域。针对现有小型电机无取向钢加工难度大，效率低的问题，本发明提供一种轻便电动自行车轮毂电机用无取向电工钢，包括如下重量百分比的各组分：Si：1.50％～3.00％；Als：0.50％～2.00％；Mn：0.20％～1.00％；P：0.01％～0.20％；C：≤0.005％S：≤0.03％；N：≤0.03％；Ti：≤0.005％,其余为铁和不可避免的杂质；其中C、S、N和Ti的重量百分比满足下式：C％+S％+N％+Ti％≤0.01％。本发明通过合理控制元素含量提高硅钢的延塑性，便于加工。本发明提供的制造方法降低卷绕铁芯中的涡流和磁滞损耗，同时能够避免钢卷表面氧化和表面氮化物析出，降低铁芯损耗，与现有同铁损级别无取向硅钢相比延伸率较高，后续冷加工性能更加优异。在保证优良性能的同时便于加工。

对CSP流程生产的无取向电工钢M50W800不同尺寸样品的磁性能进行了测试和分析,结果表明:采用不同单片检测的磁性能结果与标准的Epstein方圈样品检测对比,存在明显的偏差;且同一尺寸的单片纵横向样品之间相比较,对应的磁性能差异性也较大。几种不同尺寸的单片样品,以320mm×30mm尺寸的纵横向平均值最接近标准Epstein方圈样的性能值,其铁损偏差最小。 The magnetic properties of M50W800 non-oriented electrical steel produced by CSP process were tested and analyzed with samples of different sizes,showing that significant deviation existed compared to that of Epstein square circle sample.In particular,obvious difference in magnetic properties also existed between longitudinal and transverse samples of the same size.For test samples of different sizes,the average magnetic properties of 320mm×30mm samples are the closest to that of Epstein square ... 

利用场发射电镜及能谱仪研究了取向电工钢薄、厚板坯铸锭中不同区域的析出相差异,确定了MnS、AlN及Fe3C的析出顺序和形貌特征。结果表明AlN以先析出的MnS为形核核心,形成粗大微米级的复合析出相。针状Fe3C既可以在复合析出相表面形成也可以在基体中单独出现,主要受冷却速度的影响。在1250℃保温1～2 h,AlN、Fe3C均可完全回溶,但部分MnS仍不回溶。MnS尺寸随着保温时间延长而增大。导致热轧板中沿轧向分布的粗大MnS,减弱了粒子钉扎力。 Precipitates in thin and thick slabs of electrical silicon steel were investigated by means of field emission SEM and EDS analysis.The precipitation sequence and the morphology of MnS,AlN and Fe3C particles were identified.AlN particles are observed to be nucleated on surface of MnS forming micron-meter-sized complex particles.Acicular Fe3C can precipitate on surface of the complex MnS/AlN particles or directly from matrix depending on cooling rate of the slabs.After holding at 1250 ℃ for 1-2 h,... 

针对马钢无取向电工钢孔洞缺陷的分布规律及形貌特征,对缺陷样进行了显微分析,并利用生产实绩数据分析了该缺陷产生的原因。结合热轧生产过程,主要通过避免带钢撞击导卫以及降低导卫结瘤的产生等措施,可有效抑制热卷异物压入产生,从而降低冷轧工序孔洞的产生。 In viewing of the distribution and morphology characteristics of the hole defect of non-oriented electrical steel in Maanshan Iron and Steel Co.,Ltd.,the causes of the defect were analyzed by micro analysis of the defect sample and the production data.Combined with the production process of hot rolling,by avoiding the impact of strip steel on the guide and reducing the nodule formation on the guide,the pressing of foreign bodies in hot coiling could be effectively suppressed,thus reducing the fo... 

根据新日铁、JFE及浦项等国外钢铁公司2008年以来在日本专利局、欧洲专利局(EP)及世界知识产权组织(WIPO)申请公开的有关生产Hi-B取向电工钢典型专利技术,概述了近年来国外大型钢铁企业采用低温板坯加热(坯加热温度<1 280℃)技术生产Hi-B取向电工钢主要技术重点,即将调节关键化学成分Al、N、Sn及Sb等与工艺改进相结合。最后介绍了国外大型钢铁企业采用低温板坯加热技术生产Hi-B取向电工钢实例。 The latest developments on technology for manufacturing Hi-B grain oriented electrical steel sheets developed by Nippon Steel Corp.,JFE Steel and POSCO were described according to the patents published by World Intellectual Property Organization,Japan Patent Office and European Patent Office over the recent years.The low temperature slab heating process(particularly slab-heating temperature<1 280 ℃) together with suitably adjusting key chemical elements such as Al,N,Sn and Sb elements was the... 

研究了CSP工艺生产≤0.005%C-1.1%Si的2.2mm无取向电工钢热轧板在800～1000℃常化对0.5mm冷轧板840℃退火后组织和磁性能的影响。结果表明,热轧板常化温度升高,冷轧板退火后的再结晶晶粒增大,铁损降低,磁感增加;热轧板常化温度超过900℃,因第二相固溶而后弥散析出,退火后冷轧晶粒细化,铁损增加,因此该无取向电工钢热轧板最佳常化温度为900℃。 The effect of normalizing at 800-1000℃ of CSP produced plate(≤0.005%C-1.1%Si) on the microstructure and magnetic properties of downstream cold-rolled non-oriented electrical steel annealed at 840℃ was studied.Results show that with increasing normalizing temperature of hot-rolled material the recrystallized grain size of annealed sheet increases,iron loss reduced and magnetic induction increases.As normalizing temperature excesses 900℃,grain is refined and iron loss increases after annealing due... 

本发明涉及一种转炉冶炼回炉高硅钢水的方法，转炉中兑入回炉高硅钢水，再兑入铁水至预定装入量，使转炉中的钢水硅含量≤1.0％；转炉采用双渣冶炼的方法，加入的造渣料包括活性石灰、白云石、轻烧白云石、烧结矿；吹炼时氧累达到83％‑85％时使用副枪测量TSC，按TSC测量数据吹炼至钢水目标成分和目标温度后提枪，出钢。本发明实现转炉冶炼回炉高硅钢水的稳定控制。降低钢厂经济损失，减少炼钢生产事故率。提高了炼钢生产作业率。

【作者】 王磊； ...