硅钢资料

本发明公开了一种适宜缠绕式加工的低铁损无取向硅钢及其生产方法，属于硅钢生产技术领域。本发明的无取向硅钢包括以下质量百分比的元素：Si：1.5～2.5％，Mn：0.15～1.0％、Als：0.5～1.5％，其余为Fe及不可避免的杂质。其生产工艺步骤为：铁水预处理、转炉冶炼、真空处理、连铸；加热热轧；常化处理；冷轧、退火；保温、冷却；涂覆绝缘层。本发明通过对无取向硅钢的组分及其配比，结合工艺操作进行优化，能够生产得到电磁性能及延伸率均优异的无取向硅钢，从而能够有效满足电工钢缠绕式加工及使用需求，且其制造工序流程短、成本相对较低。

通过对辉光放电发射光谱参数的优化,以铁元素为内标来消除基体效应,建立了测定硅钢薄板中微量硼元素的方法。优化的实验参数为:放电电压1200 V,放电电流50 mA,预溅射时间40 s,积分时间10 s。校准曲线硼元素含量范围0.0001%~0.022%,相关系数大于0.999,测量结果与认定值一致,相对标准偏差小于10%。完全能够满足日常分析测试的要求。 A glow discharge optical emission spectrometry(GD-OES) method for determining trace boron element in silicon steel sheets were established through optimization of instrumental parameters and using Fe element as an internal standard to eliminate the matrix effect.The optimized instrumental parameters included discharge voltage,discharge current,pre-sputtering time and integration time,which are 1200 V,50 mA,40 s,and 10 s,respectively.The content of boron element that can be determined from the ca... 

本发明公开了一种宽频率低铁损无取向电工钢及其制备方法，属于无取向电工钢生产制造技术领域。它从电工钢表面向内依次包括0.005mm～0.1mm的渗透层和钢材内芯；所述渗透层是由硅原子向电工钢内渗透形成，渗透层中的硅元素含量为3wt％～8wt％；所述钢材内芯包括2.0wt％～5.5wt％的硅元素和不少于93.2wt％的铁元素。本发明能保证无取向电工钢具有低频低铁损性能同时有效降低高频条件下的铁损，具体铁损性能为：铁损P1.5/50≤2.35W/kg，铁损P1.0/400≤13.8W/kg。

本发明涉及一种常化后免酸洗生产取向硅钢的方法，取向硅钢的生产工艺路线为：冶炼→连铸→热轧→常化退火→拉伸矫直→抛丸→冷轧→脱碳退火→渗氮→涂MgO→高温退火→热拉伸平整及涂绝缘膜；本发明在常化退火后通过物理方法去除带钢表面的氧化铁皮，且效率高、效果好、操作简单、易于控制；与常规工艺相比，省去了酸洗及后续废酸处理工作，排除了酸雾对环境的污染，消除了取向硅钢带因酸洗而产生的潜在缺陷，产品质量更加稳定可靠。

本发明涉及一种取向硅钢热轧钢带的板形控制方法，所述取向硅钢热轧钢带的工艺流程包括铸坯加热过程、轧制过程及层流冷却过程；其中轧制过程中采取取向硅钢与普钢交叉轧制的方式；粗轧过程采取R1轧制1道次、R2轧制5道次的1+5轧制工艺，并控制轧制工艺参数；精轧过程中控制F1～F7轧制工艺参数。本发明通过设定合理的交叉轧制工艺及取向硅钢热轧工艺，使取向硅钢的轧制稳定性大幅提高，取向硅钢带形控制良好，凸度控制在30～50μm之内，楔形控制在30μm之内，板形平坦度控制在25iu之内；从而为冷轧工序提供了优质原料。

本发明公开了一种低铁损高磁导率无取向电工钢及其生产方法，所述生产方法包括以下步骤：钢水连续浇铸成板坯，板坯经加热炉加热，再经热轧得到热轧板，然后经空冷和水冷后在500～650℃进行卷取；热轧板经常化处理、盐酸酸洗；酸洗后在可逆轧机上进行冷轧；最后经成品退火，退火温度为840～900℃，加热时间为240～500s；然后以不超过3℃/s的冷却速度冷却至500℃以下；涂覆绝缘涂层、固化，后经二次退火，即可得到低铁损高磁导率无取向电工钢，其磁性能满足P1.5/50≤3.50W/kg，μ1.5≥3800Gs/Oe，B5000≥1.76T的要求。

采用中、厚板坯生产技术对取向硅钢进行了研制和开发,对热轧及后工序样品进行了金相组织观察和EBSD分析,探讨了两种组织及织构的差异性,研究结果表明:除高温退火样品外,中板坯生产的取向硅钢各工序样品平均晶粒尺寸大;厚板坯生产的取向硅钢热轧和常化样品亚表层Goss织构强;中板坯和厚板坯的脱碳退火板织构没有明显区别。中板坯生产的取向硅钢成本低,产品磁性能和质量与厚板坯相当。 Grain oriented silicon steel was researched and developed by medium thickness slab and thick slab.Microstructures observation and EBSD analysis to the samples of hot rolling and following processes were carried out,respectively.The differences between the two kinds of microstructures and textures were discussed.The results show that the average grain sizes of every process samples are larger except that of high temperature annealing samples of grain oriented silicon steel produced by medium thic... 

一种增大压下率的电工钢冷轧装置及冷轧方法，属于电工钢冷轧技术领域，该电工钢冷轧装置，包括单机架可逆轧机，单机架可逆轧机的两侧均设置有电磁感应加热装置和氮气风冷装置，氮气风冷装置靠近单机架可逆轧机的轧制进口或入口设置，本发明的有益效果是，本发明通过在单机架可逆轧机两侧增设电磁感应加热装置和氮气风冷装置，对每道次轧制过程中可在线调节电磁感应加热温度，实现了边去应力退火边轧制，保证了正常的轧制工作，达到了高效轧制更薄规格电工钢产品的目的和消化生产CSP热轧超厚过渡坯的目的。

对冷轧无取向硅钢在冶炼过程中各个工序的顶渣进行了检测,分析了顶渣变化原因,并得出结论:硅钢生产宜采用复吹转炉,以降低吹炼终点渣中TFe含量,进而减轻对精炼的压力;使用低S、低Al2O3含量中间包覆盖剂;RH脱氧及合金化顺序采用先加硅铁后加铝;首罐宜经LF提温并降低渣中TFe。 The top-surface slag used for the various production processes in smelting coldrolled non-oriented electrical steel is tested and based on tested results the cause of the top surface slag change is analyzed.So it is concluded that the combined blown converter is more suitable to be used for smelting electrical steel in order to reduce the content of TFe in slag at blow end point and then much better results can be achieved during the period of refining.Secondly the tundish flux contenting low co... 

本发明涉及硅钢技术领域，尤其涉及一种硅钢连退炉辊除瘤方法及装置。包括连杆、手柄、磨削片、密封盖、端盖与套筒；磨削片垂直固接在连杆一端的外壁上，手柄固接在连杆的另一端，手柄与磨削片处于同一平面上；连杆套接在套筒内，连杆能沿套筒轴向移动，套筒固接在端盖上；硅钢连退炉辊下方的炉墙设有与连杆及磨削片相应的磨辊孔，端盖或密封盖固接在磨辊孔处。1)确定结瘤炉辊；2)确定结瘤在碳套辊上的位置；3)插入除瘤装置；4)磨削；5)抽出。本发明降低废品量，提高成材率；减少停炉处理结瘤时间，降低能耗，提高生产率；提高难磨瘤辊的修复率，降低炉辊成本。

本发明涉及一种转炉冶炼回炉高硅钢水的方法，转炉中兑入回炉高硅钢水，再兑入铁水至预定装入量，使转炉中的钢水硅含量≤1.0％；转炉采用双渣冶炼的方法，加入的造渣料包括活性石灰、白云石、轻烧白云石、烧结矿；吹炼时氧累达到83％‑85％时使用副枪测量TSC，按TSC测量数据吹炼至钢水目标成分和目标温度后提枪，出钢。本发明实现转炉冶炼回炉高硅钢水的稳定控制。降低钢厂经济损失，减少炼钢生产事故率。提高了炼钢生产作业率。

对高牌号无取向电工钢国内生产情况、工艺技术、产品性能及应用领域等进行了阐述,并探讨了高牌号无取向电工钢产品的发展趋势。 This paper introduces basic facts on the production status,process technology and products’ properties and their applications of non-oriented electrical steel with high grade at home,and then discusses the development trend on technology for producing the non-oriented electrical steel with high grade.