硅钢资料

【作者】 卢鹏； ...

本发明公开了一种轻便电动自行车轮毂电机用无取向电工钢及制造方法，属于无取向钢领域。针对现有小型电机无取向钢加工难度大，效率低的问题，本发明提供一种轻便电动自行车轮毂电机用无取向电工钢，包括如下重量百分比的各组分：Si：1.50％～3.00％；Als：0.50％～2.00％；Mn：0.20％～1.00％；P：0.01％～0.20％；C：≤0.005％S：≤0.03％；N：≤0.03％；Ti：≤0.005％,其余为铁和不可避免的杂质；其中C、S、N和Ti的重量百分比满足下式：C％+S％+N％+Ti％≤0.01％。本发明通过合理控制元素含量提高硅钢的延塑性，便于加工。本发明提供的制造方法降低卷绕铁芯中的涡流和磁滞损耗，同时能够避免钢卷表面氧化和表面氮化物析出，降低铁芯损耗，与现有同铁损级别无取向硅钢相比延伸率较高，后续冷加工性能更加优异。在保证优良性能的同时便于加工。

通过对辉光放电发射光谱法分析电工钢样品光谱行为的研究,分析其工作参数如:电压、电流、预溅射时间和积分时间对光谱强度和稳定性的影响,并以铁为内标元素,优化了工作参数。确定了直流辉光放电光谱法测定电工钢中碳、硅、锰、磷、硫、铬、镍、铜共8种元素的定量分析方法,并对该方法分析的精密度和准确度进行验证,结果表明,各元素的测定结果与认定值和其他方法测定值一致,测量元素结果RSD值小于2%。 Based on research on analyzing the spectrum behavior of the sample taken from the electrical steel by glow discharge optical emission spectrometry,the effect of its operational parameters such as current,voltage,pre-sputtering time and integrating time on the spectral intensity and spectral stability is analyzed.Taking the Fe as an element applied by internal standard method,these operational parameters are optimized,and therefore the quantitative analysis method for testing eight kinds of eleme... 

本实用新型公开了一种适用于自动线的硅钢叠装系数性能检测装置，涉及实验仪器自动化技术领域，为解决机器人自动上样至叠装系数测量仪经常发生碰撞的问题；本实用新型包括框架、上压板、下压板、压紧驱动机构、高度探规和加载力值传感器，其中压紧驱动机构设置于框架上端，下压板固定于框架内的下端，上压板安装于下压板上方且与压紧驱动机构的输出端传动连接，加载力值传感器安装于上压板与压紧驱动机构的输出端之间，高度探规安装在上压板上，且探头向下伸出上压板下端面，框架为“C”字形一体式刚性结构，其设有上下两个水平板，以及位于一侧的竖直板；本实用新型能够避免机器人自动上样时碰撞到框架，以及下压时高度探规压到试样。

本发明公开了一种超高效变频空调压缩机用无取向硅钢薄带及其制造方法，属于无取向硅钢技术领域。本发明包括以下重量百分比的组分：C≤0.003％，Si：2.0％～2.5％，Mn：0.15％～0.5％，Als：0.3％～0.7％，Sn：0.05％～0.11％，S≤0.003％，P≤0.03％，B：0.002％～0.004％，Ca：0.003％～0.005％，N≤0.003％，Ti≤0.003％，其余为Fe及不可避免的杂质，且Mn/S比控制在20～60范围内，B/N比控制在0.7～1.5，Ca/S的比例≥1。为解决现有技术中存在的问题，本发明通过添加合金元素以及偏析元素，配合连铸、热轧、常化和连续退火等热处理工艺，以及优良的冷轧板形控制技术，实现0.30～0.35mm厚度薄规格的高效无取向硅钢产品，具备优异的磁性能和高屈强比的力学性能，满足高效变频空调压缩机电机磁性能和关节式定子高速冲裁对力学性能和板形的高标准要求。

结合冶炼无取向硅钢的生产实际,对钢中硫的来源,以及炉渣性质、钢水温度、底吹强度对脱硫的影响进行了分析。研究表明,转炉钢中硫的主要来源为铁水、废钢、铁水渣及石灰带入;冶炼硅钢时,终渣碱度为3.0~3.5,w((FeO))≤20%,终点钢水温度大于等于1 680℃,加大底吹搅拌强度能提高转炉脱硫效果。硅钢平均出钢硫的质量分数为0.004 8%,能满足无取向硅钢对硫含量的要求。 With the actual production of non-oriented silicon steel,the source of sulphur and the effect of metallugic parameters like slag properties,temperature of molten steel and bottom stirring on desulphurizing ability were investigated.The results show that the main source of sulphur is molten metal,scrap,the remaining slag volume in hot metal and lime.The degree of desulphurization for smelting silicon steel can be increased through adopting the following measures,such as the basicity of finishing ... 

取向硅钢热轧板中织构梯度对发展完善的二次再结晶十分关键,通过添加铜可以显著降低取向硅钢板坯加热温度,从而影响热轧板织构分布。利用X射线衍射仪,分析了实验室模拟薄板坯连铸连轧(TSCR)工艺的3种不同铜含量的取向硅钢热轧板织构。结果表明:不同铜含量热轧板表面到厚度1/4处均为弱的热轧织构,热轧板心部主要为{100}面织构;铜含量约在0.4%时,热轧板次表层的{110}<001>织构比例最高,而热轧板心部的{100}<110>织构比例最低;铜含量对热轧织构中{114}<110>和{001}<100>织构发展有显著影响。 The texture gradient in hot rolled grain oriented silicon steel strip is one of the essential factors to achieve a perfect secondary recrystallization.The addition of copper can significantly reduce the slab reheating temperature of grain oriented silicon steel,so as to impact the texture distribution in the hot rolled strip.The texture of hot rolled grain oriented silicon steel strip as-rolled by thin slab casting and rolling process(TSCR) in laboratory with three different copper contents was ... 

【作者】 王磊； ...

本发明公开了一种宽频率低铁损变频电机用无取向电工钢及制造方法，属于无取向电工钢领域。针对现有无取向钢在较宽频率范围内电磁性较差的问题，本发明提供一种宽频率低铁损变频电机用无取向电工钢，包括如下重量百分比的各组分：Si：2.80％～3.50％；Als：0.20％～0.60％；Mn：0.20％～0.60％；P：0.01％～0.20％；C：≤0.005％；S：≤0.02％；N：≤0.02％；Ti：≤0.005％；其余为铁和不可避免的杂质；其中C、S、N和Ti的重量百分比满足下式：C％+S％+N％+Ti％≤0.009％。通过控制合金元素的含量达到电工钢电阻率增加、磁滞伸缩减小，涡流和磁滞损耗均降低的目的。通过本发明提供的制造方法在正火过程中选用低温工艺，改善随着合金元素量的增加金属强度增加、塑性降低、冷加工性能降低的问题，使其最终在较宽频率范围内电磁性能优异。

本发明公开了一种新能源汽车驱动电机用低铁损高强度无取向电工钢及其制造方法，所述无取向电工钢的化学成分及重量百分比包括C：0.001‑0.005％、Si：2.4‑3.0％、Mn：0.25‑0.5％、Al：0.70‑1.10％、P：≤0.02％、S：≤0.005％、0.015％≤Ce+Sn≤0.035％，余量为铁和不可避免的杂质，本发明通过加入Ce和Sn，净化钢质、微合金化提高无取向电工钢强度和磁性能，不需要添加固溶金属元素，且避免了高Si体系下的轧制困难问题，且不需要高温退火，解决了退火温度过高使晶粒异常长大，晶粒尺寸均匀性降低的问题，生产出的无取向电工钢具有较高强度的同时，还具有优良的磁性能。

本发明涉及一种取向硅钢热轧钢带的板形控制方法，所述取向硅钢热轧钢带的工艺流程包括铸坯加热过程、轧制过程及层流冷却过程；其中轧制过程中采取取向硅钢与普钢交叉轧制的方式；粗轧过程采取R1轧制1道次、R2轧制5道次的1+5轧制工艺，并控制轧制工艺参数；精轧过程中控制F1～F7轧制工艺参数。本发明通过设定合理的交叉轧制工艺及取向硅钢热轧工艺，使取向硅钢的轧制稳定性大幅提高，取向硅钢带形控制良好，凸度控制在30～50μm之内，楔形控制在30μm之内，板形平坦度控制在25iu之内；从而为冷轧工序提供了优质原料。

本发明公开了一种批量稳定生产高牌号无取向电工钢的方法，包括以下步骤：开卷→加热→水套冷却→水雾冷却→水喷淋冷却→抛丸→酸洗→切边→卷取→使用单机架六辊轧机进行轧制成卷；该方法可实现高牌号无取向电工钢在六辊UCM轧机冷轧后无边裂产生，可将带钢板形值控制在‑5I～+5I，厚度精度控制在±3μm，该方法生产的高牌号无取向电工钢无板形及表面质量缺陷，产品质量良好，可实现高牌号无取向电工钢的批量稳定轧制。