硅钢资料

取向硅钢热轧板中织构梯度对发展完善的二次再结晶十分关键,通过添加铜可以显著降低取向硅钢板坯加热温度,从而影响热轧板织构分布。利用X射线衍射仪,分析了实验室模拟薄板坯连铸连轧(TSCR)工艺的3种不同铜含量的取向硅钢热轧板织构。结果表明:不同铜含量热轧板表面到厚度1/4处均为弱的热轧织构,热轧板心部主要为{100}面织构;铜含量约在0.4%时,热轧板次表层的{110}<001>织构比例最高,而热轧板心部的{100}<110>织构比例最低;铜含量对热轧织构中{114}<110>和{001}<100>织构发展有显著影响。 The texture gradient in hot rolled grain oriented silicon steel strip is one of the essential factors to achieve a perfect secondary recrystallization.The addition of copper can significantly reduce the slab reheating temperature of grain oriented silicon steel,so as to impact the texture distribution in the hot rolled strip.The texture of hot rolled grain oriented silicon steel strip as-rolled by thin slab casting and rolling process(TSCR) in laboratory with three different copper contents was ... 

本发明涉及无取向硅钢技术领域，尤其涉及一种改善高牌号无取向硅钢冷轧断带的控制方法。按重量百分比计：[Si+Al]≥4.0％；Mn、S含量满足：S≤0.0015，[Mn]/[S]:200～400；1)热轧过程中使用保温罩，热轧轧制时投入边部加热，头尾100米内卷曲温度提高15～30℃；2)常化机组圆盘剪进行边部剪边前增加加热装置，剪切后增加毛刺打磨装置，采用煤气明火加热，保证钢板温度在韧脆转变温度以上；3)圆盘剪间隙满足关系式：ds＝(0.15～0.45)d0ds:圆盘剪间隙，μm；d0:常化板板厚，mm；4)常化采用快速加热，控制钢带的预热段升温速度320～380℃/min，机组速度20～30m/min；5)常化工艺后，控制边部小于20μm的晶粒占比在5％以内。有效的减少了冷轧断带的发生，提高成材率1.30％以上，降低了生产成本。

针对马钢无取向电工钢孔洞缺陷的分布规律及形貌特征,对缺陷样进行了显微分析,并利用生产实绩数据分析了该缺陷产生的原因。结合热轧生产过程,主要通过避免带钢撞击导卫以及降低导卫结瘤的产生等措施,可有效抑制热卷异物压入产生,从而降低冷轧工序孔洞的产生。 In viewing of the distribution and morphology characteristics of the hole defect of non-oriented electrical steel in Maanshan Iron and Steel Co.,Ltd.,the causes of the defect were analyzed by micro analysis of the defect sample and the production data.Combined with the production process of hot rolling,by avoiding the impact of strip steel on the guide and reducing the nodule formation on the guide,the pressing of foreign bodies in hot coiling could be effectively suppressed,thus reducing the fo... 

结合冶炼无取向硅钢的生产实际,对钢中硫的来源,以及炉渣性质、钢水温度、底吹强度对脱硫的影响进行了分析。研究表明,转炉钢中硫的主要来源为铁水、废钢、铁水渣及石灰带入;冶炼硅钢时,终渣碱度为3.0~3.5,w((FeO))≤20%,终点钢水温度大于等于1 680℃,加大底吹搅拌强度能提高转炉脱硫效果。硅钢平均出钢硫的质量分数为0.004 8%,能满足无取向硅钢对硫含量的要求。 With the actual production of non-oriented silicon steel,the source of sulphur and the effect of metallugic parameters like slag properties,temperature of molten steel and bottom stirring on desulphurizing ability were investigated.The results show that the main source of sulphur is molten metal,scrap,the remaining slag volume in hot metal and lime.The degree of desulphurization for smelting silicon steel can be increased through adopting the following measures,such as the basicity of finishing ... 

【作者】 王磊； ...

研究了采用高温卷取热轧态原料和常化态原料生产高牌号冷轧无取向电工钢组织、织构和磁性能。研究发现钢卷采用750℃高温卷取,下线后立即采用\"保温罩\"对钢卷进行保温,时间96h,然后空冷至100℃时上线生产的工艺可取代常化工艺生产高牌号冷轧无取向电工钢。冷轧上线前,热轧态原料的表层为大量的再结晶组织,这部分组织包括了热轧轧制时保留下来的动态再结晶组织,钢卷本身高温回复后产生再结晶晶粒,以及在保温罩内保温时形成的再结晶组织。高温卷取的热轧态和常化态的热轧卷作为原料时,试样织构类型相似,取向分布密度接近,再结晶后织构类型仍然相似,取向分布密度仍然接近。Goss织构对磁性能增加有促进作用。实验钢中较好的磁性能对应的织构[{100}+Goss]/{111}的比值较高,体现了织构的遗传性。 Microstructure,texture and magnetic properties of high grade cold rolled nonoriented electrical steel which made of hot rolled material with high temperature coiling and with normalization were studied.Steels coiled in high temperature(at 750 ℃),stacked with insulation cover for 96hand air cooled to 100 ℃ were using to manufacture high grade nonoriented electrical steel.The process can replace the normalization process.There are a lot of recrystallized grains in the surface layer of the coil wit... 

对CSP流程生产的高磁感无取向电工钢50W1300在偏离轧制方向不同角度处的磁性能进行了测试和分析。结果表明:在偏离轧向不同角度处,磁性能差异显著,尤其在α=60°时磁感最低;偏离轧制方向不同角度处的磁性能大小取决于织构类型、强度及分布状态;增强{100}<0vw>和α、η取向的有利织构组分,降低不利的γ取向织构组分,且使有利织构组分分布越漫散,磁各向异性越小。 Magnetic properties of high magnetic induction non-oriented electrical steel 50W1300 produced by CSP processes were investigated with different direction in relation to the rolling direction.The result shows that magnetic properties are significantly different in relation to the rolling direction,in particular,the minimum magnetic induction occurs at 60° in relation to the rolling direction.Magnetic properties of different directions in relation to rolling direction depend on type and distributi... 

本发明公开了一种无取向电工钢清洗工艺，包括以下步骤：1)在脱脂剂箱体中添加脱脂剂溶剂，通过喷射泵将脱脂剂分别从上下两路管道喷出，经过流量控制电磁阀进入喷射梁，通过喷嘴喷洒在带钢表面；2)带钢轧制后温度为100～150℃，速度为600～1000m/min，带钢表面高温确保脱脂剂与带钢表面残留油脂反应充分，且在高速下喷射的脱脂剂与带钢相向而行，使带钢表面反应后残留硅泥、铁粉被迅速带走；3)喷射后的脱脂剂流入收集槽中，通过泵重新打入脱脂剂箱体中，实现脱脂剂的循环利用。其利用轧制时产生的高温及高速对带钢表面残留乳化液斑迹、铁粉、硅泥进行清洗，清洗彻底高效。

取向硅钢热轧板中组织、织构梯度对发展完善的二次再结晶十分关键,通过对2种不同热轧工艺生产取向硅钢的组织、织构进行研究,结果表明:采用后道次大压下热轧工艺时热轧板表层再结区晶粒平均尺寸增加,再结晶区厚度增加,高温退火后二次晶粒尺寸减小;采用后道次大压下热轧工艺热轧时,热轧板中平均等效应变高,热轧板厚度心部{100}〈011〉和{100}〈001〉位向取向强度降低,({111}～{113})〈110〉位向取向强度提高,高温退火后{110}〈001〉位向偏离角降低,磁性能提高。 The texture and microstructure gradient in hot rolled grain oriented silicon steel strip was one of the essential factors to achieve a perfect secondary recrystallization.The texture and microstructure of grain oriented silicon steel strip as-rolled with two different hot rolling parameters was investigated.The results show that with big reduction at the end rolling process,the intensity of {100}〈011〉 and {100}〈001〉 orientation reduces with({111}-{113})〈110〉 orientation intensity enhanced in hot... 

本发明提供了一种超高磁感无取向硅钢及其制造方法和在汽车发电机生产中的应用，成分：C：≤0.005％、Si：0.5‑1.2％、Mn：0.1‑0.5％、P：0.01‑0.1％、S：≤0.004％、Al：≤0.005％、N：≤0.005％、Ti：≤0.003％，余量为铁和不可避免的杂质。通过成分设计，配合CSP薄板坯连铸连轧工艺、常化工艺，不用添加贵金属元素，不添加贵金属元素，流程短、成本低、磁感高、性能稳定；节省成本的同时，具有优良的磁性能，采用本发明生产的汽车发电机铁芯，与常规产品生产的铁芯相比，重量可减轻15％以上，缩小了发电机尺寸，满足汽车发电机小型化、高效化的要求。

本发明公开了一种批量稳定生产高牌号无取向电工钢的方法，包括以下步骤：开卷→加热→水套冷却→水雾冷却→水喷淋冷却→抛丸→酸洗→切边→卷取→使用单机架六辊轧机进行轧制成卷；该方法可实现高牌号无取向电工钢在六辊UCM轧机冷轧后无边裂产生，可将带钢板形值控制在‑5I～+5I，厚度精度控制在±3μm，该方法生产的高牌号无取向电工钢无板形及表面质量缺陷，产品质量良好，可实现高牌号无取向电工钢的批量稳定轧制。

对欧盟市场汽车压缩机专用产品进行技术解析,对比分析了其电磁性能、退火和发蓝处理、物理性能、化学成分、应用特点等参数。探讨国内外电工钢产品应用方式的不同特点,并结合鞍钢自身工艺装备和炼钢、热轧、冷轧工艺参数介绍了其生产可行性。提供了冶金工艺流程下,后工序电工钢专业生产线及传统冷轧系统生产线两种生产方式,均能满足用户最终使用要求。 The technology of automotive compressor accommodation manufacture of European Economic and Monetary Union market was described.The magnetic properties,annealing bluing,physical properties,chemical composition,application parameters were analysed.The different characteristics of the application of electrical steel products,the feasibility of manufacture on the existing technology and equipment,steelmaking,hot rolled,cold rolled technical parameters were discussed.The professional product line of ...