对CSP流程生产的高磁感无取向电工钢50W1300在偏离轧制方向不同角度处的磁性能进行了测试和分析。结果表明:在偏离轧向不同角度处,磁性能差异显著,尤其在α=60°时磁感最低;偏离轧制方向不同角度处的磁性能大小取决于织构类型、强度及分布状态;增强{100}<0vw>和α、η取向的有利织构组分,降低不利的γ取向织构组分,且使有利织构组分分布越漫散,磁各向异性越小。 Magnetic properties of high magnetic induction non-oriented electrical steel 50W1300 produced by CSP processes were investigated with different direction in relation to the rolling direction.The result shows that magnetic properties are significantly different in relation to the rolling direction,in particular,the minimum magnetic induction occurs at 60° in relation to the rolling direction.Magnetic properties of different directions in relation to rolling direction depend on type and distributi... 

本发明公开了一种轻便电动自行车轮毂电机用无取向电工钢及制造方法，属于无取向钢领域。针对现有小型电机无取向钢加工难度大，效率低的问题，本发明提供一种轻便电动自行车轮毂电机用无取向电工钢，包括如下重量百分比的各组分：Si：1.50％～3.00％；Als：0.50％～2.00％；Mn：0.20％～1.00％；P：0.01％～0.20％；C：≤0.005％S：≤0.03％；N：≤0.03％；Ti：≤0.005％,其余为铁和不可避免的杂质；其中C、S、N和Ti的重量百分比满足下式：C％+S％+N％+Ti％≤0.01％。本发明通过合理控制元素含量提高硅钢的延塑性，便于加工。本发明提供的制造方法降低卷绕铁芯中的涡流和磁滞损耗，同时能够避免钢卷表面氧化和表面氮化物析出，降低铁芯损耗，与现有同铁损级别无取向硅钢相比延伸率较高，后续冷加工性能更加优异。在保证优良性能的同时便于加工。

本发明涉及硅钢技术领域，尤其涉及一种硅钢连退炉辊除瘤方法及装置。包括连杆、手柄、磨削片、密封盖、端盖与套筒；磨削片垂直固接在连杆一端的外壁上，手柄固接在连杆的另一端，手柄与磨削片处于同一平面上；连杆套接在套筒内，连杆能沿套筒轴向移动，套筒固接在端盖上；硅钢连退炉辊下方的炉墙设有与连杆及磨削片相应的磨辊孔，端盖或密封盖固接在磨辊孔处。1)确定结瘤炉辊；2)确定结瘤在碳套辊上的位置；3)插入除瘤装置；4)磨削；5)抽出。本发明降低废品量，提高成材率；减少停炉处理结瘤时间，降低能耗，提高生产率；提高难磨瘤辊的修复率，降低炉辊成本。

本发明公开了一种低铁损高磁导率无取向电工钢及其生产方法，所述生产方法包括以下步骤：钢水连续浇铸成板坯，板坯经加热炉加热，再经热轧得到热轧板，然后经空冷和水冷后在500～650℃进行卷取；热轧板经常化处理、盐酸酸洗；酸洗后在可逆轧机上进行冷轧；最后经成品退火，退火温度为840～900℃，加热时间为240～500s；然后以不超过3℃/s的冷却速度冷却至500℃以下；涂覆绝缘涂层、固化，后经二次退火，即可得到低铁损高磁导率无取向电工钢，其磁性能满足P1.5/50≤3.50W/kg，μ1.5≥3800Gs/Oe，B5000≥1.76T的要求。

取向硅钢热轧板中组织、织构梯度对发展完善的二次再结晶十分关键,通过对2种不同热轧工艺生产取向硅钢的组织、织构进行研究,结果表明:采用后道次大压下热轧工艺时热轧板表层再结区晶粒平均尺寸增加,再结晶区厚度增加,高温退火后二次晶粒尺寸减小;采用后道次大压下热轧工艺热轧时,热轧板中平均等效应变高,热轧板厚度心部{100}〈011〉和{100}〈001〉位向取向强度降低,({111}～{113})〈110〉位向取向强度提高,高温退火后{110}〈001〉位向偏离角降低,磁性能提高。 The texture and microstructure gradient in hot rolled grain oriented silicon steel strip was one of the essential factors to achieve a perfect secondary recrystallization.The texture and microstructure of grain oriented silicon steel strip as-rolled with two different hot rolling parameters was investigated.The results show that with big reduction at the end rolling process,the intensity of {100}〈011〉 and {100}〈001〉 orientation reduces with({111}-{113})〈110〉 orientation intensity enhanced in hot... 

本文以热轧常化板为初始材料,采用二次冷轧法与三次冷轧法制备了0.1 mm厚的取向硅钢薄带,测定相应的磁性能,并通过EBSD取向成像技术检测了二次冷轧法与三次冷轧法各工艺过程中织构与组织演变规律。结果表明,采用最终冷轧压下率适中的三次冷轧法,能在冷轧至0.1 mm时保存较多的高斯晶核,使得高温退火后的磁性能明显优于二次冷轧法。最终冷轧压下率通过影响脱碳退火后样品中的{111}<112>织构组分及Goss晶粒数量对最终二次再结晶产生重要影响。 Grain-oriented silicon steel sheets with a thickness of 0. 1 mm were produced from hot-rolled and normalized sheets by two-step-rolling and three-step-rolling methods. Their magnetic properties were measured,and the textures were detected by EBSD technique. The results show that the three-step-rolling method,which has a moderate reduction rate of final cold rolling,can maintain more { 110} < 001 >nucleus,and thus obtaining better magnetic properties compared with the two-step-method. The f... 

本发明公开了一种批量稳定生产高牌号无取向电工钢的方法，包括以下步骤：开卷→加热→水套冷却→水雾冷却→水喷淋冷却→抛丸→酸洗→切边→卷取→使用单机架六辊轧机进行轧制成卷；该方法可实现高牌号无取向电工钢在六辊UCM轧机冷轧后无边裂产生，可将带钢板形值控制在‑5I～+5I，厚度精度控制在±3μm，该方法生产的高牌号无取向电工钢无板形及表面质量缺陷，产品质量良好，可实现高牌号无取向电工钢的批量稳定轧制。

本发明涉及一种取向硅钢热轧钢带的板形控制方法，所述取向硅钢热轧钢带的工艺流程包括铸坯加热过程、轧制过程及层流冷却过程；其中轧制过程中采取取向硅钢与普钢交叉轧制的方式；粗轧过程采取R1轧制1道次、R2轧制5道次的1+5轧制工艺，并控制轧制工艺参数；精轧过程中控制F1～F7轧制工艺参数。本发明通过设定合理的交叉轧制工艺及取向硅钢热轧工艺，使取向硅钢的轧制稳定性大幅提高，取向硅钢带形控制良好，凸度控制在30～50μm之内，楔形控制在30μm之内，板形平坦度控制在25iu之内；从而为冷轧工序提供了优质原料。

本发明公开了一种适宜缠绕式加工的低铁损无取向硅钢及其生产方法，属于硅钢生产技术领域。本发明的无取向硅钢包括以下质量百分比的元素：Si：1.5～2.5％，Mn：0.15～1.0％、Als：0.5～1.5％，其余为Fe及不可避免的杂质。其生产工艺步骤为：铁水预处理、转炉冶炼、真空处理、连铸；加热热轧；常化处理；冷轧、退火；保温、冷却；涂覆绝缘层。本发明通过对无取向硅钢的组分及其配比，结合工艺操作进行优化，能够生产得到电磁性能及延伸率均优异的无取向硅钢，从而能够有效满足电工钢缠绕式加工及使用需求，且其制造工序流程短、成本相对较低。

【作者】 王磊； ...

【作者】 卢鹏； ...

通过对35W300高牌号0.35 mm冷轧无取向电工钢卷(/%:0.002C、2.71Si、0.22Mn、0.015P、0.003S、0.0020N、0.55Als)头、中、尾组织、织构及对应的磁性能的试验研究,发现因热轧时12 MPa高压水连续冷却造成接触轧辊的钢卷头、中、尾在不同温度下轧制,卷取后钢卷头部处于卷心、温度略高而冷却速度略低于钢卷尾部,致使钢卷纵向组织、织构不同,成品卷头、尾各250 m内磁感逐渐增加,铁损逐渐降低,250 m外至钢卷中部磁性能稳定。通过将热轧辊的冷却方式改为周期冷却和卷取后的层流冷却改为钢卷70 m后开始冷却,至钢卷尾部70 m前停止冷却的方式使得钢卷纵向铁损差异明显减小,磁感差异略有改善。 According to the test research on structure and texture of head,meddle and end of 35W300 high grade 0.35 mm cold rolled non-oriented electrical steel strip coil(/%:0.002C,2.71Si,0.22Mn,0.015P,0.003S,0.002 0 N,0.55Als) and corresponding magnetic properties,It is found that due to 12 MPa high pressure water continuous cooling the roller in hot rolling process led to head,middle and tail of strip rolling at different temperature and after coiling the head of strip coil being in center of coil led t...