本发明提供了一种CSP流程生产高效冷轧无取向电工钢及生产方法，成分：C≤0.0030％、Si 1.00‑1.70％、Als≤0.0050％、Mn 0.10‑0.30％、Sn0.01‑0.3％、P≤0.050％、S≤0.0080％、N≤0.0030％、Nb≤0.0030％、V≤0.0030％、Ti≤0.0030％，其余为Fe以及不可避免的杂质。与现有技术相比，本发明CSP流程生产高效冷轧无取向电工钢的方法，通过控制钢中的化学成分，并采用合适的生产工艺，实现了表面质量优良，低铁损、高磁感、低制造成本且生产高效。

对应用动态加热进行短时温度退火的取向电工钢进行了二次再结晶研究。所进行研究的实验用取向电工钢是经过终冷轧和后续罩式退火后的一条工业化生产线生产的。研究结果表明,运用短时热处理条件可引起研究钢完全的异常晶粒长大。在实验室处理的材料的织构和金相组织与工业化生产的经过终退火而获得的相同的取向电工钢类似。但是,在实验室处理的取向电工钢的二次再结晶的矩阵中可观测到\"寄生\"晶粒。从磁性观点看,这些\"寄生\"晶粒含有不理想的{111}取向织构。 The present study was made to investigate secondary recrystallization in grain-oriented steels annealed at short time temperature exposures with application of dynamical heating.The investigated GO(Grain Oriented) steels for experiments were taken from one industrial line after final cold rolling reduction and subsequent box annealing.It was shown that application of short time heat treatment conditions could lead to complete abnormal grain growth in the investigated GO steel.The texture and mic... 

对高牌号无取向电工钢国内生产情况、工艺技术、产品性能及应用领域等进行了阐述,并探讨了高牌号无取向电工钢产品的发展趋势。 This paper introduces basic facts on the production status,process technology and products’ properties and their applications of non-oriented electrical steel with high grade at home,and then discusses the development trend on technology for producing the non-oriented electrical steel with high grade. 

本发明公开了一种批量稳定生产高牌号无取向电工钢的方法，包括以下步骤：开卷→加热→水套冷却→水雾冷却→水喷淋冷却→抛丸→酸洗→切边→卷取→使用单机架六辊轧机进行轧制成卷；该方法可实现高牌号无取向电工钢在六辊UCM轧机冷轧后无边裂产生，可将带钢板形值控制在‑5I～+5I，厚度精度控制在±3μm，该方法生产的高牌号无取向电工钢无板形及表面质量缺陷，产品质量良好，可实现高牌号无取向电工钢的批量稳定轧制。

本发明公开了一种自主学习的高硅钢软磁复合铁芯智能化生产系统及生产方法，属于软磁复合铁芯智能化生产技术领域。本发明的生产系统包括数据输入模块、数据分析模块、数据输出模块、通信模块、数据修正模块；生产方法为：用户通过输入模块选择目标性能参数及生产控制模式，系统生成生产过程关键参数，并由输出模块输出给用户；用户确认后形成控制指令，并发送至生产设备进行生产。本发明的系统不仅能够根据高硅钢铁芯产品的目标性能参数自动生成合理的操作条件，还能根据历史数据和产品检化结果对系统内置的关系模型不断进行优化、完善，能够有效提高产品产量和质量、减少浪费、降低成本。

本发明涉及一种冷连轧法生产无取向高硅钢的方法，RH真空脱碳处理后，铝脱氧及部分铝合金化，合金化后大罐钢水净循环大于3次或大于5分钟；熔炼合格钢水至连铸开浇前静置时间大于二十分钟；控制过热度5～15℃；采用电磁搅拌，控制等轴晶比例45％以上；3)热轧工序板坯装炉温度大于750℃；常化使晶粒尺寸在90～110μm范围内；连续退火炉加热段温度设定950～1150℃，均热段温度设定900～1050℃，全氮气干气氛保护，控制晶粒尺寸120～170μm。生产全过程中的热履历参数控制，充分发挥设计的微合金元素功能，改变析出物的组成、大小、形态及分布。

针对马钢无取向电工钢孔洞缺陷的分布规律及形貌特征,对缺陷样进行了显微分析,并利用生产实绩数据分析了该缺陷产生的原因。结合热轧生产过程,主要通过避免带钢撞击导卫以及降低导卫结瘤的产生等措施,可有效抑制热卷异物压入产生,从而降低冷轧工序孔洞的产生。 In viewing of the distribution and morphology characteristics of the hole defect of non-oriented electrical steel in Maanshan Iron and Steel Co.,Ltd.,the causes of the defect were analyzed by micro analysis of the defect sample and the production data.Combined with the production process of hot rolling,by avoiding the impact of strip steel on the guide and reducing the nodule formation on the guide,the pressing of foreign bodies in hot coiling could be effectively suppressed,thus reducing the fo... 

对冷轧无取向硅钢在冶炼过程中各个工序的顶渣进行了检测,分析了顶渣变化原因,并得出结论:硅钢生产宜采用复吹转炉,以降低吹炼终点渣中TFe含量,进而减轻对精炼的压力;使用低S、低Al2O3含量中间包覆盖剂;RH脱氧及合金化顺序采用先加硅铁后加铝;首罐宜经LF提温并降低渣中TFe。 The top-surface slag used for the various production processes in smelting coldrolled non-oriented electrical steel is tested and based on tested results the cause of the top surface slag change is analyzed.So it is concluded that the combined blown converter is more suitable to be used for smelting electrical steel in order to reduce the content of TFe in slag at blow end point and then much better results can be achieved during the period of refining.Secondly the tundish flux contenting low co... 

本发明公开了一种轻便电动自行车轮毂电机用无取向电工钢及制造方法，属于无取向钢领域。针对现有小型电机无取向钢加工难度大，效率低的问题，本发明提供一种轻便电动自行车轮毂电机用无取向电工钢，包括如下重量百分比的各组分：Si：1.50％～3.00％；Als：0.50％～2.00％；Mn：0.20％～1.00％；P：0.01％～0.20％；C：≤0.005％S：≤0.03％；N：≤0.03％；Ti：≤0.005％,其余为铁和不可避免的杂质；其中C、S、N和Ti的重量百分比满足下式：C％+S％+N％+Ti％≤0.01％。本发明通过合理控制元素含量提高硅钢的延塑性，便于加工。本发明提供的制造方法降低卷绕铁芯中的涡流和磁滞损耗，同时能够避免钢卷表面氧化和表面氮化物析出，降低铁芯损耗，与现有同铁损级别无取向硅钢相比延伸率较高，后续冷加工性能更加优异。在保证优良性能的同时便于加工。

本发明涉及一种防止低温加热取向硅钢热轧边裂的方法，包括：1)控制取向硅钢铸坯进入加热炉前的表面温度；2)控制加热段各段炉气温度；3)二加热段采用加速加热；4)控制总加热时间；5)控制出炉温度；6)控制精轧道次及侧压量；7)控制精轧道次及终轧温度；8)精轧前对钢带边部进行加热补偿。本发明通过合理制定取向硅钢的加热温度、加热时间和轧制工艺制度，避免或消除了低温加热取向硅钢热轧边裂问题。

采用中、厚板坯生产技术对取向硅钢进行了研制和开发,对热轧及后工序样品进行了金相组织观察和EBSD分析,探讨了两种组织及织构的差异性,研究结果表明:除高温退火样品外,中板坯生产的取向硅钢各工序样品平均晶粒尺寸大;厚板坯生产的取向硅钢热轧和常化样品亚表层Goss织构强;中板坯和厚板坯的脱碳退火板织构没有明显区别。中板坯生产的取向硅钢成本低,产品磁性能和质量与厚板坯相当。 Grain oriented silicon steel was researched and developed by medium thickness slab and thick slab.Microstructures observation and EBSD analysis to the samples of hot rolling and following processes were carried out,respectively.The differences between the two kinds of microstructures and textures were discussed.The results show that the average grain sizes of every process samples are larger except that of high temperature annealing samples of grain oriented silicon steel produced by medium thic... 

本发明涉及一种含磷无铝高效无取向硅钢生产方法，生产方法取消常化工艺，具体步骤如下：1)将钢水冶炼至目标成分后，浇铸成坯；2)板坯热装，热装温度≥500℃，热轧板坯加热炉均热段板坯温度1150～1200℃；终轧温度控制在860～930℃，卷取温度700～800℃3)酸洗后冷轧，控制冷轧整体压下率80％以内，至成品厚度；4)连续退火炉快速加热段温度设定1050～1180℃，增加有利织构组织形核，均热段温度设定830～950℃，全氮气干气氛保护，退火工艺速度120～150m/min，满足晶粒度8～4级。本发明不需进行热轧卷常化处理，降低了制造成本。