硅钢资料

利用场发射电镜及能谱仪研究了取向电工钢薄、厚板坯铸锭中不同区域的析出相差异,确定了MnS、AlN及Fe3C的析出顺序和形貌特征。结果表明AlN以先析出的MnS为形核核心,形成粗大微米级的复合析出相。针状Fe3C既可以在复合析出相表面形成也可以在基体中单独出现,主要受冷却速度的影响。在1250℃保温1～2 h,AlN、Fe3C均可完全回溶,但部分MnS仍不回溶。MnS尺寸随着保温时间延长而增大。导致热轧板中沿轧向分布的粗大MnS,减弱了粒子钉扎力。 Precipitates in thin and thick slabs of electrical silicon steel were investigated by means of field emission SEM and EDS analysis.The precipitation sequence and the morphology of MnS,AlN and Fe3C particles were identified.AlN particles are observed to be nucleated on surface of MnS forming micron-meter-sized complex particles.Acicular Fe3C can precipitate on surface of the complex MnS/AlN particles or directly from matrix depending on cooling rate of the slabs.After holding at 1250 ℃ for 1-2 h,... 

对冷轧无取向硅钢在冶炼过程中各个工序的顶渣进行了检测,分析了顶渣变化原因,并得出结论:硅钢生产宜采用复吹转炉,以降低吹炼终点渣中TFe含量,进而减轻对精炼的压力;使用低S、低Al2O3含量中间包覆盖剂;RH脱氧及合金化顺序采用先加硅铁后加铝;首罐宜经LF提温并降低渣中TFe。 The top-surface slag used for the various production processes in smelting coldrolled non-oriented electrical steel is tested and based on tested results the cause of the top surface slag change is analyzed.So it is concluded that the combined blown converter is more suitable to be used for smelting electrical steel in order to reduce the content of TFe in slag at blow end point and then much better results can be achieved during the period of refining.Secondly the tundish flux contenting low co... 

为开发高效电机用冷轧无取向电工钢,借助实验室薄板坯连铸连轧模拟设备及扫描电镜、透射电镜等检验手段研究了成分、组织、织构和析出物等对无取向电工钢磁性能的影响规律;结果表明:常化处理使组织均匀化并增加有利于磁性提高的织构组分;采用CSP流程开发的高效电机用无取向电工钢铁损平均值3.4 0 W/kg,磁感≥1.68 T。 In order to develop electrical steel for high efficiency motor,effect of components,microstructure,texture and precipitation on magnetic property of electrical steel are analyzed.From the result,normalizing treatment makes microstructure uniform and increases component of favorable texture.Iron loss of electrical steel developed by CSP line is 3.40W/kg and magnetic induction is more than 1.68T. 

本发明公开了一种无取向电工钢清洗工艺，包括以下步骤：1)在脱脂剂箱体中添加脱脂剂溶剂，通过喷射泵将脱脂剂分别从上下两路管道喷出，经过流量控制电磁阀进入喷射梁，通过喷嘴喷洒在带钢表面；2)带钢轧制后温度为100～150℃，速度为600～1000m/min，带钢表面高温确保脱脂剂与带钢表面残留油脂反应充分，且在高速下喷射的脱脂剂与带钢相向而行，使带钢表面反应后残留硅泥、铁粉被迅速带走；3)喷射后的脱脂剂流入收集槽中，通过泵重新打入脱脂剂箱体中，实现脱脂剂的循环利用。其利用轧制时产生的高温及高速对带钢表面残留乳化液斑迹、铁粉、硅泥进行清洗，清洗彻底高效。

本发明公开了一种批量稳定生产高牌号无取向电工钢的方法，包括以下步骤：开卷→加热→水套冷却→水雾冷却→水喷淋冷却→抛丸→酸洗→切边→卷取→使用单机架六辊轧机进行轧制成卷；该方法可实现高牌号无取向电工钢在六辊UCM轧机冷轧后无边裂产生，可将带钢板形值控制在‑5I～+5I，厚度精度控制在±3μm，该方法生产的高牌号无取向电工钢无板形及表面质量缺陷，产品质量良好，可实现高牌号无取向电工钢的批量稳定轧制。

为了消除硅钢在连续退火机组产生的浪形缺陷,对浪形缺陷产生的主要原因进行了分析。制定了相应控制措施,对炉内带钢张力、冷却段输出、碳套辊与带钢的同步性、无氧化炉燃烧状态等参数进行了调整;在生产组织上安排高低牌号宽窄规格穿插生产、定期更换碳套辊等,实施后效果明显。 The main cause leading to waviness defects of silicon steel is analyzed in order to eliminate the waviness defects of silicon steel in continuous annealing line.And thus corresponding measures for controlling these defects are made by means of adjusting these parameters such as the tension of silicon steel coils in continuous annealing furnace,the output in cooling section and the combusting condition of the non-oxidation furnace as well as keeping the synchronization between carbon sleeved roll... 

本发明涉及一种提高取向硅钢冷轧加工性的生产方法，工艺流程为：冶炼、连铸、热轧、常化、酸洗、冷轧、脱碳渗氮、涂MgO、高温退火、涂绝缘层及热拉伸平整；粗轧中坯厚度35‑45mm，两段常化后进行带钢横向分段式冷却水分布。本发明通过对热轧中坯厚度、终轧温度及卷取温度，常化冷却水量及控制方式的调控，使轧前表层晶粒尺寸降低5‑10μm、珠光体体积分数降低6％，轧材冷轧加工性明显改善、成材率可提高8％以上。通过后续冷轧、脱碳退火和高温退火等工序处理，可保证完善的二次再结晶组织及良好磁性能。

针对马钢无取向电工钢孔洞缺陷的分布规律及形貌特征,对缺陷样进行了显微分析,并利用生产实绩数据分析了该缺陷产生的原因。结合热轧生产过程,主要通过避免带钢撞击导卫以及降低导卫结瘤的产生等措施,可有效抑制热卷异物压入产生,从而降低冷轧工序孔洞的产生。 In viewing of the distribution and morphology characteristics of the hole defect of non-oriented electrical steel in Maanshan Iron and Steel Co.,Ltd.,the causes of the defect were analyzed by micro analysis of the defect sample and the production data.Combined with the production process of hot rolling,by avoiding the impact of strip steel on the guide and reducing the nodule formation on the guide,the pressing of foreign bodies in hot coiling could be effectively suppressed,thus reducing the fo... 

本发明公开了一种宽频率低铁损变频电机用无取向电工钢及制造方法，属于无取向电工钢领域。针对现有无取向钢在较宽频率范围内电磁性较差的问题，本发明提供一种宽频率低铁损变频电机用无取向电工钢，包括如下重量百分比的各组分：Si：2.80％～3.50％；Als：0.20％～0.60％；Mn：0.20％～0.60％；P：0.01％～0.20％；C：≤0.005％；S：≤0.02％；N：≤0.02％；Ti：≤0.005％；其余为铁和不可避免的杂质；其中C、S、N和Ti的重量百分比满足下式：C％+S％+N％+Ti％≤0.009％。通过控制合金元素的含量达到电工钢电阻率增加、磁滞伸缩减小，涡流和磁滞损耗均降低的目的。通过本发明提供的制造方法在正火过程中选用低温工艺，改善随着合金元素量的增加金属强度增加、塑性降低、冷加工性能降低的问题，使其最终在较宽频率范围内电磁性能优异。

本发明提供了一种CSP流程生产高效冷轧无取向电工钢及生产方法，成分：C≤0.0030％、Si 1.00‑1.70％、Als≤0.0050％、Mn 0.10‑0.30％、Sn0.01‑0.3％、P≤0.050％、S≤0.0080％、N≤0.0030％、Nb≤0.0030％、V≤0.0030％、Ti≤0.0030％，其余为Fe以及不可避免的杂质。与现有技术相比，本发明CSP流程生产高效冷轧无取向电工钢的方法，通过控制钢中的化学成分，并采用合适的生产工艺，实现了表面质量优良，低铁损、高磁感、低制造成本且生产高效。

本发明涉及一种取向硅钢热轧钢带的板形控制方法，所述取向硅钢热轧钢带的工艺流程包括铸坯加热过程、轧制过程及层流冷却过程；其中轧制过程中采取取向硅钢与普钢交叉轧制的方式；粗轧过程采取R1轧制1道次、R2轧制5道次的1+5轧制工艺，并控制轧制工艺参数；精轧过程中控制F1～F7轧制工艺参数。本发明通过设定合理的交叉轧制工艺及取向硅钢热轧工艺，使取向硅钢的轧制稳定性大幅提高，取向硅钢带形控制良好，凸度控制在30～50μm之内，楔形控制在30μm之内，板形平坦度控制在25iu之内；从而为冷轧工序提供了优质原料。

本发明提供了一种无取向硅钢RH顶枪喷粉脱硫工艺，RH脱碳结束测温定氧，立即加入铝粒脱氧合金化、之后立即依次连续加入合金进行成分调整，合金加完后立即开始顶枪喷粉；加入铝粒的量＝铝粒理论加入量+0.2‑0.4kg/t钢；喷粉时，控制喷粉速度与钢液循环流量相匹配；本发明从真空条件下脱硫热力学和动力学角度出发对具有顶枪喷粉功能的RH脱硫工艺进行改进，提高脱硫率。