本发明涉及一种提高取向硅钢冷轧加工性的生产方法，工艺流程为：冶炼、连铸、热轧、常化、酸洗、冷轧、脱碳渗氮、涂MgO、高温退火、涂绝缘层及热拉伸平整；粗轧中坯厚度35‑45mm，两段常化后进行带钢横向分段式冷却水分布。本发明通过对热轧中坯厚度、终轧温度及卷取温度，常化冷却水量及控制方式的调控，使轧前表层晶粒尺寸降低5‑10μm、珠光体体积分数降低6％，轧材冷轧加工性明显改善、成材率可提高8％以上。通过后续冷轧、脱碳退火和高温退火等工序处理，可保证完善的二次再结晶组织及良好磁性能。

取向硅钢热轧板中组织、织构梯度对发展完善的二次再结晶十分关键,通过对2种不同热轧工艺生产取向硅钢的组织、织构进行研究,结果表明:采用后道次大压下热轧工艺时热轧板表层再结区晶粒平均尺寸增加,再结晶区厚度增加,高温退火后二次晶粒尺寸减小;采用后道次大压下热轧工艺热轧时,热轧板中平均等效应变高,热轧板厚度心部{100}〈011〉和{100}〈001〉位向取向强度降低,({111}～{113})〈110〉位向取向强度提高,高温退火后{110}〈001〉位向偏离角降低,磁性能提高。 The texture and microstructure gradient in hot rolled grain oriented silicon steel strip was one of the essential factors to achieve a perfect secondary recrystallization.The texture and microstructure of grain oriented silicon steel strip as-rolled with two different hot rolling parameters was investigated.The results show that with big reduction at the end rolling process,the intensity of {100}〈011〉 and {100}〈001〉 orientation reduces with({111}-{113})〈110〉 orientation intensity enhanced in hot... 

介绍了CSP工艺生产无取向电工钢各工序的设备特点、采用的工艺控制手段和电工钢产品质量情况,结合生产实践证明了马钢CSP工艺开发的无取向电工钢产品丰富了薄板坯连铸连轧的品种结构,发挥了薄板坯连铸连轧生产无取向电工钢性能均一、稳定的特点。 The equipment characteristic,the process control method and the quality of non-orientated silicon steel by CSP process were introduced.Combined with the production situation,it is proved that production of non-orientated silicon steel developed on Masteel CSP line would enrich product structure of thin slab continuous casting and rolling,and it exerts stable performance of non-orientated silicon steel. 

对无取向硅钢炼钢全流程钢液增钛的原因进行了分析,认为铁水钛含量、转炉出钢温度、转炉下渣量、精炼渣TiO₂含量、钢水罐及RH浸入管混钢种生产是影响钢液增钛的主要原因。通过采取低钛铁水冶炼,减少转炉下渣量,提高出钢温度,添加白灰改质精炼渣等措施,均能够降低钢液中的钛含量。 After analyzing the causes leading to increased content of titanium in molten nonoriented silicon steel during whole steelmaking process, it was concluded that such factors as content of titanium in hot metal, tapping temperature from converter, quantity of roughing slag entered into the ladle from converter, content of TiO₂ in refining slag, molten steel ladle car,carrying out the steelmaking of different steel grades by the same ladle and same RH immersion tube were the main causes ... 

为开发高效电机用冷轧无取向电工钢,借助实验室薄板坯连铸连轧模拟设备及扫描电镜、透射电镜等检验手段研究了成分、组织、织构和析出物等对无取向电工钢磁性能的影响规律;结果表明:常化处理使组织均匀化并增加有利于磁性提高的织构组分;采用CSP流程开发的高效电机用无取向电工钢铁损平均值3.4 0 W/kg,磁感≥1.68 T。 In order to develop electrical steel for high efficiency motor,effect of components,microstructure,texture and precipitation on magnetic property of electrical steel are analyzed.From the result,normalizing treatment makes microstructure uniform and increases component of favorable texture.Iron loss of electrical steel developed by CSP line is 3.40W/kg and magnetic induction is more than 1.68T. 

【作者】 卢鹏； ...

【作者】 王磊； ...

研究了CSP工艺流程生产的硅含量为1.5%的无取向电工钢在不同常化温度下对磁性能的变化。研究结果表明:随着常化温度的提高,热轧板的晶粒尺寸增大,且组织均匀性提高;此外成品的有利织构组分{100}<0vw>、α、η增强,不利织构组分减弱;铁损P1.5/50呈下降趋势,磁感B50上升平缓。在常化工艺为970℃×2.5min下,对应的铁损P1.5/50<3.4W/kg,磁感B50>1.74T。 The effect of normalizing temperature on the magnetic properties of non-oriented electrical steel containing 1.5%silicon produced by CSP process was studied.The results show that with increasing normalizing temperature,the average grain size of hot-rolled plate increases and the microstructure uniformity is improved.Furthermore,the texture components of finished products are improved through enhancing of{100}<0vw>,αandηtextures and weakening of{111}<112>texture;the core loss P1.5/50 ... 

本发明公开了一种轻便电动自行车轮毂电机用无取向电工钢及制造方法，属于无取向钢领域。针对现有小型电机无取向钢加工难度大，效率低的问题，本发明提供一种轻便电动自行车轮毂电机用无取向电工钢，包括如下重量百分比的各组分：Si：1.50％～3.00％；Als：0.50％～2.00％；Mn：0.20％～1.00％；P：0.01％～0.20％；C：≤0.005％S：≤0.03％；N：≤0.03％；Ti：≤0.005％,其余为铁和不可避免的杂质；其中C、S、N和Ti的重量百分比满足下式：C％+S％+N％+Ti％≤0.01％。本发明通过合理控制元素含量提高硅钢的延塑性，便于加工。本发明提供的制造方法降低卷绕铁芯中的涡流和磁滞损耗，同时能够避免钢卷表面氧化和表面氮化物析出，降低铁芯损耗，与现有同铁损级别无取向硅钢相比延伸率较高，后续冷加工性能更加优异。在保证优良性能的同时便于加工。

一种冷轧硅钢生产线的带钢卷曲控制装置，由卷取机、导向辊、液压站、伺服阀及其油缸、计算机控制系统、卷取机位移传感器和带钢边部位置探测器组成的卷曲机系统，该系统在带钢辊道的两侧各装有一个带钢边部位置探测器，以分别检测带钢的两个边缘在辊道上的位置，其检测信号分别传送到计算机控制系统中去。计算机控制系统可对两个带钢边部位置探测器输入的信号进行带钢的中心位置计算，并与卷取机位移传感器输入的卷取机中心位移信号进行比较，根据比较结果控制油缸的推杆推动卷取机移动，以使卷取机的卷曲中心与带钢的中心线保持一致。本发明的有益效果是：实现了使卷取机的卷曲中心与带钢的中心线保持一致，因而不再切边，提高了带钢的成材率。

本发明涉及一种含磷无铝高效无取向硅钢生产方法，生产方法取消常化工艺，具体步骤如下：1)将钢水冶炼至目标成分后，浇铸成坯；2)板坯热装，热装温度≥500℃，热轧板坯加热炉均热段板坯温度1150～1200℃；终轧温度控制在860～930℃，卷取温度700～800℃3)酸洗后冷轧，控制冷轧整体压下率80％以内，至成品厚度；4)连续退火炉快速加热段温度设定1050～1180℃，增加有利织构组织形核，均热段温度设定830～950℃，全氮气干气氛保护，退火工艺速度120～150m/min，满足晶粒度8～4级。本发明不需进行热轧卷常化处理，降低了制造成本。

本发明公开了一种超高效变频空调压缩机用无取向硅钢薄带及其制造方法，属于无取向硅钢技术领域。本发明包括以下重量百分比的组分：C≤0.003％，Si：2.0％～2.5％，Mn：0.15％～0.5％，Als：0.3％～0.7％，Sn：0.05％～0.11％，S≤0.003％，P≤0.03％，B：0.002％～0.004％，Ca：0.003％～0.005％，N≤0.003％，Ti≤0.003％，其余为Fe及不可避免的杂质，且Mn/S比控制在20～60范围内，B/N比控制在0.7～1.5，Ca/S的比例≥1。为解决现有技术中存在的问题，本发明通过添加合金元素以及偏析元素，配合连铸、热轧、常化和连续退火等热处理工艺，以及优良的冷轧板形控制技术，实现0.30～0.35mm厚度薄规格的高效无取向硅钢产品，具备优异的磁性能和高屈强比的力学性能，满足高效变频空调压缩机电机磁性能和关节式定子高速冲裁对力学性能和板形的高标准要求。