二次冷轧法与三次冷轧法制备取向硅钢薄带的织构转变规律
本文以热轧常化板为初始材料,采用二次冷轧法与三次冷轧法制备了0.1 mm厚的取向硅钢薄带,测定相应的磁性能,并通过EBSD取向成像技术检测了二次冷轧法与三次冷轧法各工艺过程中织构与组织演变规律。结果表明,采用最终冷轧压下率适中的三次冷轧法,能在冷轧至0.1 mm时保存较多的高斯晶核,使得高温退火后的磁性能明显优于二次冷轧法。最终冷轧压下率通过影响脱碳退火后样品中的{111}<112>织构组分及Goss晶粒数量对最终二次再结晶产生重要影响。 Grain-oriented silicon steel sheets with a thickness of 0. 1 mm were produced from hot-rolled and normalized sheets by two-step-rolling and three-step-rolling methods. Their magnetic properties were measured,and the textures were detected by EBSD technique. The results show that the three-step-rolling method,which has a moderate reduction rate of final cold rolling,can maintain more { 110} < 001 >nucleus,and thus obtaining better magnetic properties compared with the two-step-method. The f...
CN202110777440.8一种适应高频率工况下低铁损无取向电工钢及其生产方法
本发明公开了一种适应高频率工况下低铁损无取向电工钢及其生产方法,所述生产方法包括以下步骤:钢水连续浇铸成板坯—热轧—正火—酸洗—冷轧—连续退火—涂绝缘涂层并固化;所述冷轧步骤中,采用六辊单机架往复式轧机经5道次一次冷轧至目标厚度,冷轧过程中前三道次采用变速异步轧制方法,使钢板表层在剪应力作用下位错密度增加,这样在退火后表层晶粒尺寸细化而心部晶粒粗大,通过本发明的方法可生产得到心部为粗大等轴晶粒,表层为纳米级细等轴晶粒的电工钢产品,该产品的铁损P1.5/50≤2.35W/kg,P1.0/400≤14.0W/kg。
CN202110201290.6一种批量稳定生产高牌号无取向电工钢的方法
本发明公开了一种批量稳定生产高牌号无取向电工钢的方法,包括以下步骤:开卷→加热→水套冷却→水雾冷却→水喷淋冷却→抛丸→酸洗→切边→卷取→使用单机架六辊轧机进行轧制成卷;该方法可实现高牌号无取向电工钢在六辊UCM轧机冷轧后无边裂产生,可将带钢板形值控制在‑5I~+5I,厚度精度控制在±3μm,该方法生产的高牌号无取向电工钢无板形及表面质量缺陷,产品质量良好,可实现高牌号无取向电工钢的批量稳定轧制。
冷轧无取向硅钢冶炼过程炉渣分析
对冷轧无取向硅钢在冶炼过程中各个工序的顶渣进行了检测,分析了顶渣变化原因,并得出结论:硅钢生产宜采用复吹转炉,以降低吹炼终点渣中TFe含量,进而减轻对精炼的压力;使用低S、低Al2O3含量中间包覆盖剂;RH脱氧及合金化顺序采用先加硅铁后加铝;首罐宜经LF提温并降低渣中TFe。 The top-surface slag used for the various production processes in smelting coldrolled non-oriented electrical steel is tested and based on tested results the cause of the top surface slag change is analyzed.So it is concluded that the combined blown converter is more suitable to be used for smelting electrical steel in order to reduce the content of TFe in slag at blow end point and then much better results can be achieved during the period of refining.Secondly the tundish flux contenting low co...
成品第二次退火工艺对高牌号无取向电工钢35W300组织和性能的影响
对高牌号无取向电工钢35W300的成品进行了第二次退火,对第二次退火后的成品性能、纵横向磁性能差异和组织变化进行了分析。结果表明,随着第二次退火温度的升高,晶粒长大,磁性能优化。铁损平均值下降0.087 5W/kg,磁感平均值升高0.008T。第二次退火温度为820℃的产品的磁性能能够满足用户使用要求。 The product of high grade non-oriented electrical steel 35W300 was annealed at the second time.Microstructure,the difference of magnetic properties in the vertical and horizontal and were studied.The results show that the grain grew up and magnetic properties optimized with the increase of annealing temperature for the second time.Iron loss average declines in 0.0875 W/kg,magnetic induction average increases 0.008 T.The magnetic properties can meet the requirements of users at the second anneali...
CN202111010835.1一种无取向电工钢清洗工艺
本发明公开了一种无取向电工钢清洗工艺,包括以下步骤:1)在脱脂剂箱体中添加脱脂剂溶剂,通过喷射泵将脱脂剂分别从上下两路管道喷出,经过流量控制电磁阀进入喷射梁,通过喷嘴喷洒在带钢表面;2)带钢轧制后温度为100~150℃,速度为600~1000m/min,带钢表面高温确保脱脂剂与带钢表面残留油脂反应充分,且在高速下喷射的脱脂剂与带钢相向而行,使带钢表面反应后残留硅泥、铁粉被迅速带走;3)喷射后的脱脂剂流入收集槽中,通过泵重新打入脱脂剂箱体中,实现脱脂剂的循环利用。其利用轧制时产生的高温及高速对带钢表面残留乳化液斑迹、铁粉、硅泥进行清洗,清洗彻底高效。
高温卷取的热轧态原料与常化态原料生产高牌号无取向硅钢的比较
研究了采用高温卷取热轧态原料和常化态原料生产高牌号冷轧无取向电工钢组织、织构和磁性能。研究发现钢卷采用750℃高温卷取,下线后立即采用\"保温罩\"对钢卷进行保温,时间96h,然后空冷至100℃时上线生产的工艺可取代常化工艺生产高牌号冷轧无取向电工钢。冷轧上线前,热轧态原料的表层为大量的再结晶组织,这部分组织包括了热轧轧制时保留下来的动态再结晶组织,钢卷本身高温回复后产生再结晶晶粒,以及在保温罩内保温时形成的再结晶组织。高温卷取的热轧态和常化态的热轧卷作为原料时,试样织构类型相似,取向分布密度接近,再结晶后织构类型仍然相似,取向分布密度仍然接近。Goss织构对磁性能增加有促进作用。实验钢中较好的磁性能对应的织构[{100}+Goss]/{111}的比值较高,体现了织构的遗传性。 Microstructure,texture and magnetic properties of high grade cold rolled nonoriented electrical steel which made of hot rolled material with high temperature coiling and with normalization were studied.Steels coiled in high temperature(at 750 ℃),stacked with insulation cover for 96hand air cooled to 100 ℃ were using to manufacture high grade nonoriented electrical steel.The process can replace the normalization process.There are a lot of recrystallized grains in the surface layer of the coil wit...
CN202110953215.5一种含磷高磁感无取向硅钢的生产方法
本发明涉及一种含磷高磁感无取向硅钢的生产方法,工艺路线:铁水脱硫-转炉冶炼-RH精炼-连铸-热轧-酸洗-冷轧-连续炉退火-涂层-性能检验-包装,具体步骤包括:1)将钢水冶炼至目标成分后采用连铸方式将钢水铸成坯;2)热轧板坯加热炉均热段板坯温度950~1050℃,终轧温度控制在780~830℃,卷取温度600~680℃;3)酸洗后冷轧,控制冷轧整体压下率80%以上,至成品厚度,增加剪切带组织;4)连续退火炉快速加热段温度设定1000~1150℃,增加有利织构组织形核;均热段温度设定750~830℃,全氮气干气氛保护,退火工艺速度110~150m/min,满足晶粒度8~4级。本发明在减少硅、铝、锰合金添加量的情况下,改善铁损提高磁感性能,提高机械性能。
在动态热处理条件下对取向电工钢二次再结晶的研究
对应用动态加热进行短时温度退火的取向电工钢进行了二次再结晶研究。所进行研究的实验用取向电工钢是经过终冷轧和后续罩式退火后的一条工业化生产线生产的。研究结果表明,运用短时热处理条件可引起研究钢完全的异常晶粒长大。在实验室处理的材料的织构和金相组织与工业化生产的经过终退火而获得的相同的取向电工钢类似。但是,在实验室处理的取向电工钢的二次再结晶的矩阵中可观测到\"寄生\"晶粒。从磁性观点看,这些\"寄生\"晶粒含有不理想的{111}取向织构。 The present study was made to investigate secondary recrystallization in grain-oriented steels annealed at short time temperature exposures with application of dynamical heating.The investigated GO(Grain Oriented) steels for experiments were taken from one industrial line after final cold rolling reduction and subsequent box annealing.It was shown that application of short time heat treatment conditions could lead to complete abnormal grain growth in the investigated GO steel.The texture and mic...
CN202110953170.1一种冷连轧法生产无取向高硅钢的方法
本发明涉及一种冷连轧法生产无取向高硅钢的方法,RH真空脱碳处理后,铝脱氧及部分铝合金化,合金化后大罐钢水净循环大于3次或大于5分钟;熔炼合格钢水至连铸开浇前静置时间大于二十分钟;控制过热度5~15℃;采用电磁搅拌,控制等轴晶比例45%以上;3)热轧工序板坯装炉温度大于750℃;常化使晶粒尺寸在90~110μm范围内;连续退火炉加热段温度设定950~1150℃,均热段温度设定900~1050℃,全氮气干气氛保护,控制晶粒尺寸120~170μm。生产全过程中的热履历参数控制,充分发挥设计的微合金元素功能,改变析出物的组成、大小、形态及分布。
120t转炉冶炼无取向硅钢脱硫技术研究
结合冶炼无取向硅钢的生产实际,对钢中硫的来源,以及炉渣性质、钢水温度、底吹强度对脱硫的影响进行了分析。研究表明,转炉钢中硫的主要来源为铁水、废钢、铁水渣及石灰带入;冶炼硅钢时,终渣碱度为3.0~3.5,w((FeO))≤20%,终点钢水温度大于等于1 680℃,加大底吹搅拌强度能提高转炉脱硫效果。硅钢平均出钢硫的质量分数为0.004 8%,能满足无取向硅钢对硫含量的要求。 With the actual production of non-oriented silicon steel,the source of sulphur and the effect of metallugic parameters like slag properties,temperature of molten steel and bottom stirring on desulphurizing ability were investigated.The results show that the main source of sulphur is molten metal,scrap,the remaining slag volume in hot metal and lime.The degree of desulphurization for smelting silicon steel can be increased through adopting the following measures,such as the basicity of finishing ...
CN202110953161.2一种含磷无铝高效无取向硅钢生产方法
本发明涉及一种含磷无铝高效无取向硅钢生产方法,生产方法取消常化工艺,具体步骤如下:1)将钢水冶炼至目标成分后,浇铸成坯;2)板坯热装,热装温度≥500℃,热轧板坯加热炉均热段板坯温度1150~1200℃;终轧温度控制在860~930℃,卷取温度700~800℃3)酸洗后冷轧,控制冷轧整体压下率80%以内,至成品厚度;4)连续退火炉快速加热段温度设定1050~1180℃,增加有利织构组织形核,均热段温度设定830~950℃,全氮气干气氛保护,退火工艺速度120~150m/min,满足晶粒度8~4级。本发明不需进行热轧卷常化处理,降低了制造成本。