本发明公开了一种适应高频率工况下低铁损无取向电工钢及其生产方法,所述生产方法包括以下步骤:钢水连续浇铸成板坯—热轧—正火—酸洗—冷轧—连续退火—涂绝缘涂层并固化;所述冷轧步骤中,采用六辊单机架往复式轧机经5道次一次冷轧至目标厚度,冷轧过程中前三道次采用变速异步轧制方法,使钢板表层在剪应力作用下位错密度增加,这样在退火后表层晶粒尺寸细化而心部晶粒粗大,通过本发明的方法可生产得到心部为粗大等轴晶粒,表层为纳米级细等轴晶粒的电工钢产品,该产品的铁损P1.5/50≤2.35W/kg,P1.0/400≤14.0W/kg。
2021-07-09 101 6.8

本发明公开了一种新能源汽车驱动电机用低铁损高强度无取向电工钢及其制造方法,所述无取向电工钢的化学成分及重量百分比包括C:0.001‑0.005%、Si:2.4‑3.0%、Mn:0.25‑0.5%、Al:0.70‑1.10%、P:≤0.02%、S:≤0.005%、0.015%≤Ce+Sn≤0.035%,余量为铁和不可避免的杂质,本发明通过加入Ce和Sn,净化钢质、微合金化提高无取向电工钢强度和磁性能,不需要添加固溶金属元素,且避免了高Si体系下的轧制困难问题,且不需要高温退火,解决了退火温度过高使晶粒异常长大,晶粒尺寸均匀性降低的问题,生产出的无取向电工钢具有较高强度的同时,还具有优良的磁性能。
2021-10-29 122 6.8

对高牌号无取向电工钢国内生产情况、工艺技术、产品性能及应用领域等进行了阐述,并探讨了高牌号无取向电工钢产品的发展趋势。 This paper introduces basic facts on the production status,process technology and products’ properties and their applications of non-oriented electrical steel with high grade at home,and then discusses the development trend on technology for producing the non-oriented electrical steel with high grade. 
2011-02-28 96 5.8

对应用动态加热进行短时温度退火的取向电工钢进行了二次再结晶研究。所进行研究的实验用取向电工钢是经过终冷轧和后续罩式退火后的一条工业化生产线生产的。研究结果表明,运用短时热处理条件可引起研究钢完全的异常晶粒长大。在实验室处理的材料的织构和金相组织与工业化生产的经过终退火而获得的相同的取向电工钢类似。但是,在实验室处理的取向电工钢的二次再结晶的矩阵中可观测到\"寄生\"晶粒。从磁性观点看,这些\"寄生\"晶粒含有不理想的{111}取向织构。 The present study was made to investigate secondary recrystallization in grain-oriented steels annealed at short time temperature exposures with application of dynamical heating.The investigated GO(Grain Oriented) steels for experiments were taken from one industrial line after final cold rolling reduction and subsequent box annealing.It was shown that application of short time heat treatment conditions could lead to complete abnormal grain growth in the investigated GO steel.The texture and mic... 
2011-04-28 81 5.8

对欧盟市场汽车压缩机专用产品进行技术解析,对比分析了其电磁性能、退火和发蓝处理、物理性能、化学成分、应用特点等参数。探讨国内外电工钢产品应用方式的不同特点,并结合鞍钢自身工艺装备和炼钢、热轧、冷轧工艺参数介绍了其生产可行性。提供了冶金工艺流程下,后工序电工钢专业生产线及传统冷轧系统生产线两种生产方式,均能满足用户最终使用要求。 The technology of automotive compressor accommodation manufacture of European Economic and Monetary Union market was described.The magnetic properties,annealing bluing,physical properties,chemical composition,application parameters were analysed.The different characteristics of the application of electrical steel products,the feasibility of manufacture on the existing technology and equipment,steelmaking,hot rolled,cold rolled technical parameters were discussed.The professional product line of ... 
2013-06-28 91 5.8

本发明涉及一种转炉冶炼回炉高硅钢水的方法,转炉中兑入回炉高硅钢水,再兑入铁水至预定装入量,使转炉中的钢水硅含量≤1.0%;转炉采用双渣冶炼的方法,加入的造渣料包括活性石灰、白云石、轻烧白云石、烧结矿;吹炼时氧累达到83%‑85%时使用副枪测量TSC,按TSC测量数据吹炼至钢水目标成分和目标温度后提枪,出钢。本发明实现转炉冶炼回炉高硅钢水的稳定控制。降低钢厂经济损失,减少炼钢生产事故率。提高了炼钢生产作业率。
2021-09-14 96 6.8

本发明涉及一种冷连轧法生产无取向高硅钢的方法,RH真空脱碳处理后,铝脱氧及部分铝合金化,合金化后大罐钢水净循环大于3次或大于5分钟;熔炼合格钢水至连铸开浇前静置时间大于二十分钟;控制过热度5~15℃;采用电磁搅拌,控制等轴晶比例45%以上;3)热轧工序板坯装炉温度大于750℃;常化使晶粒尺寸在90~110μm范围内;连续退火炉加热段温度设定950~1150℃,均热段温度设定900~1050℃,全氮气干气氛保护,控制晶粒尺寸120~170μm。生产全过程中的热履历参数控制,充分发挥设计的微合金元素功能,改变析出物的组成、大小、形态及分布。
2021-08-19 89 6.8

研究了CSP工艺流程生产的硅含量为1.5%的无取向电工钢在不同常化温度下对磁性能的变化。研究结果表明:随着常化温度的提高,热轧板的晶粒尺寸增大,且组织均匀性提高;此外成品的有利织构组分{100}<0vw>、α、η增强,不利织构组分减弱;铁损P1.5/50呈下降趋势,磁感B50上升平缓。在常化工艺为970℃×2.5min下,对应的铁损P1.5/50<3.4W/kg,磁感B50>1.74T。 The effect of normalizing temperature on the magnetic properties of non-oriented electrical steel containing 1.5%silicon produced by CSP process was studied.The results show that with increasing normalizing temperature,the average grain size of hot-rolled plate increases and the microstructure uniformity is improved.Furthermore,the texture components of finished products are improved through enhancing of{100}<0vw>,αandηtextures and weakening of{111}<112>texture;the core loss P1.5/50 ... 
2014-03-28 84 5.8

针对马钢无取向电工钢孔洞缺陷的分布规律及形貌特征,对缺陷样进行了显微分析,并利用生产实绩数据分析了该缺陷产生的原因。结合热轧生产过程,主要通过避免带钢撞击导卫以及降低导卫结瘤的产生等措施,可有效抑制热卷异物压入产生,从而降低冷轧工序孔洞的产生。 In viewing of the distribution and morphology characteristics of the hole defect of non-oriented electrical steel in Maanshan Iron and Steel Co.,Ltd.,the causes of the defect were analyzed by micro analysis of the defect sample and the production data.Combined with the production process of hot rolling,by avoiding the impact of strip steel on the guide and reducing the nodule formation on the guide,the pressing of foreign bodies in hot coiling could be effectively suppressed,thus reducing the fo... 
2022-01-28 99 5.8

通过对35W300高牌号0.35 mm冷轧无取向电工钢卷(/%:0.002C、2.71Si、0.22Mn、0.015P、0.003S、0.0020N、0.55Als)头、中、尾组织、织构及对应的磁性能的试验研究,发现因热轧时12 MPa高压水连续冷却造成接触轧辊的钢卷头、中、尾在不同温度下轧制,卷取后钢卷头部处于卷心、温度略高而冷却速度略低于钢卷尾部,致使钢卷纵向组织、织构不同,成品卷头、尾各250 m内磁感逐渐增加,铁损逐渐降低,250 m外至钢卷中部磁性能稳定。通过将热轧辊的冷却方式改为周期冷却和卷取后的层流冷却改为钢卷70 m后开始冷却,至钢卷尾部70 m前停止冷却的方式使得钢卷纵向铁损差异明显减小,磁感差异略有改善。 According to the test research on structure and texture of head,meddle and end of 35W300 high grade 0.35 mm cold rolled non-oriented electrical steel strip coil(/%:0.002C,2.71Si,0.22Mn,0.015P,0.003S,0.002 0 N,0.55Als) and corresponding magnetic properties,It is found that due to 12 MPa high pressure water continuous cooling the roller in hot rolling process led to head,middle and tail of strip rolling at different temperature and after coiling the head of strip coil being in center of coil led t... 
2013-05-28 105 5.8

冷轧中中低牌号的无取向硅钢多采用万能凸度轧机(Universal crown mill,UCM)生产,其板形好坏受制于UCM轧机板形调节手段的协调使用。为掌握UCM轧机的板形控制特点,建立基于二维变厚度有限元的辊系弹性变形和基于三维差分的轧件塑性变形的六辊轧机耦合模型,对UCM轧机的板形调控性能进行详尽的分析,包括工作辊和中间辊弯辊、中间辊窜辊的调控功效、辊间接触压力分布等。在此基础上,提出可用指导生产的板形控制策略,指出UCM轧机在横向厚差控制方面的不足。针对工业生产中UCM轧机轧制无取向硅钢横向厚差大的问题,在大量仿真计算的基础上,开发具有高次曲线函数的边部变凸度(Edge variable crown,EVC)的工作辊。采用该工作辊后,各种品种的无取向硅钢的横向厚差不大于10μm的百分比由24%提高到99%,横向厚差的均值小于6μm,远小于之前的13μm。 Medium-low grade non-oriented silicon steel is rolled often by universal crown mill(UCM) during cold rolling.Its shape quality is dependent on the coordinated control of several shape adjustment devices of UCM.In order to understand the shape control characteristics of UCM,coupling model of six-high rolling mill,based on two-dimensional varying thickness finite element rolls elastic deformation model and three-dimensional finite difference strip plastic deformation model,is setup for the detaile... 
2011-10-28 88 5.8

本发明提供了一种超高磁感无取向硅钢及其制造方法和在汽车发电机生产中的应用,成分:C:≤0.005%、Si:0.5‑1.2%、Mn:0.1‑0.5%、P:0.01‑0.1%、S:≤0.004%、Al:≤0.005%、N:≤0.005%、Ti:≤0.003%,余量为铁和不可避免的杂质。通过成分设计,配合CSP薄板坯连铸连轧工艺、常化工艺,不用添加贵金属元素,不添加贵金属元素,流程短、成本低、磁感高、性能稳定;节省成本的同时,具有优良的磁性能,采用本发明生产的汽车发电机铁芯,与常规产品生产的铁芯相比,重量可减轻15%以上,缩小了发电机尺寸,满足汽车发电机小型化、高效化的要求。
2021-07-20 80 6.8