硅钢资料

通过热力学计算与模拟试验研究了含钒钛取向硅钢中氮化物析出相的析出规律与析出行为,并探讨了含钒钛元素的氮化物析出相作为薄板坯连铸连轧流程制备取向硅钢中辅助抑制剂的可行性.研究表明,在所冶炼的含钒钛取向硅钢的成分范围内,Ti N在钢液凝固末期便具备析出的热力学条件,而Al N与VN只可能在凝固后的α+γ或α+Fe3C两相区内析出.含钒钛取向硅钢中氮化物析出相以成分复杂的复合析出相为主,且随着钒钛加入量的增加,钢中抑制剂析出相总的分布密度由于含钒钛元素的氮化物析出相的增加而明显提高,使抑制剂抑制初次再结晶晶粒正常长大的能力得以加强,最终成品的磁感应强度值B8由1.857 T提升至1.898 T.同时,加入不高于0.007%的Ti与不高于0.005%的V不会影响中间脱碳退火工序的脱碳效果以及高温退火净化阶段硫、氮的脱除效果,其形成的含钒钛元素的纳米级氮化物析出相适合作为薄板坯连铸连轧流程制备取向硅钢的辅助抑制剂. The precipitation behavior of nitride precipitates in grain-oriented silicon steel containing vanadium and titanium elements produced by thin slab casting and rolling process was studied by thermodynamic calculation and simulation experiment. The feasibility of nitride precipitates containing V and Ti elements as auxiliary inhibitors was also investigated. It is found that Ti N is likely to precipitate at the final stage of solidification in the grain-oriented silicon steel,but VN and Al N can p... 

采用扫描电镜、原子力显微镜研究了铬酸镁半无机绝缘涂层的微观结构。结果表明,涂层厚度为数微米,涂层中的有机树脂乳液颗粒均匀分布在无机涂层的表面,从而保证了涂层具有良好的冲片性能。采用极化曲线研究了涂层的耐蚀性能,发现铬酸镁与铬酸锌绝缘涂层的耐蚀性能相当。 In this paper,the microstructure and anti-corrosion property of magnesium chromate coating on non-oriented silicon steel were studied.The microstructure was observed by SEM and AFM.The anti-corrosion properties were evaluated by polarization curves.The results show that the thickness of coating is several microns and the polymer particles were scattered on the surface of inorganic coating,which is the guarantee for lamination property.The corrosion resistance of the magnesium chromate film was e... 

对低温法生产的以AlN为主抑制剂的Hi-B取向硅钢高温退火过程进行了中断实验,借助EBSD及TEM技术对高温退火连续升温过程中织构与析出物的演变进行了研究。实验结果表明,800℃时ODF图出现高斯织构组分,但强度很弱,高斯晶粒偏离角在10°以上;950~1 000℃时高斯晶粒异常长大,偏离角3~6°;高温退火过程析出物主要有球形、规则立方形及不规则多面体形3种形貌,由于渗N的影响,Zener因子先增大再减小,并且析出物在高斯晶界前沿优先粗化。 The annealing process at high temperature of Hi-B silicon steel using low slab reheat temperature and with AlN as the inhibitor has been studied by interrupting test,and the evolution of texture and precipitates during continuous heating-up in the annealing process at high temperature was analyzed by EBSD and TEM. The results showed that Goss texture appears in ODF at 800 ℃,but the intensity of Goss texture was very weak and the deviation angle was more than10°. Goss grains grow abnormally durin... 

本发明涉及取向硅钢制造技术领域，公开了一种快速判断取向硅钢初次再结晶晶粒直径的方法，包括如下步骤：选取取向硅钢热轧来料，进行生产，对产出的钢板在同部位各取若干个拉伸试样，加工拉伸和分析，取得屈服强度，在拉伸试样部位两侧连续制取金相试样，计算对应拉伸试样的平均晶粒直径D，将性能数据和平均晶粒直径进行统计分析，建立屈服强度与晶粒直径的对应关系，实际生产时，在产出的钢板上取判断试样，取得判断试样的屈服强度，进而取得判断试样的晶粒直径。本发明快速判断取向硅钢初次再结晶晶粒直径的方法，通过机械性能检验，来间接指示初次晶粒的大小，检测速度快，评价更准确。

对硅钢板材分别进行异步和同步轧制,研究了轧制参数包括速比、压下量和道次对板材表面显微组织的演变的作用.结果表明,异步轧制硅钢板材表面形成了晶粒尺寸为10~50 nm,取向接近随机分布的纳米晶,而同步轧制板材的表面只形成了位错胞,证明异步轧制可以诱发表面纳米化.异步轧制板材表面纳米晶的形成过程为:在剪切力的反复作用下,高密度位错形成、滑移、湮灭和重组形成亚微米尺度的亚微晶/位错胞.随着压下量和轧制道次增加,高密度位错重复以上过程使晶粒尺寸减小、取向差增大,最终形成取向接近随机分布的纳米晶组织.大压下量和多道次是异步轧制诱发板材表面纳米化的关键,而速比的增加可以加快纳米化进程. Surface nanocrystallization(SNC) can effectively enhance the surface and global properties of the metallic materials,such as microhardness,intensity,fatigue,wear and corrosion resistances,therefore provides more promising practical industrial applicability.Up to now,several SNC treatment methods were developed based either on the principles of ball impactions or friction sliding,however,difficulty still exists for the surface treatment of large-dimensional samples with high efficiency.Recently,m... 

针对某厂DMS森吉米尔轧机生产无取向硅钢表面麻面缺陷的问题，根据生产实际，对其形成原因从乳化液及工作辊两方面因素进行了分析。结果表明：乳化液对麻面缺陷的产生有一定影响，但不是主要因素，主要原因是由于二十辊森吉米尔轧机工作辊辊径较小，轧制相同长度带钢轧辊运转周期较大，容易产生疲劳失效而导致。为此，提出通过调整冷轧工序成品轧制道次的压下率以减小轧制力，从而减小工作辊的磨损疲劳；通过对轧制乳化液浓度、温度的合理控制，以改善润滑效果、提高轧制速度，而进一步缓解轧辊疲劳的改进措施，使该钢厂无取向硅钢麻面缺陷发生率由原来的18%降至0.8%,带钢表面质量明显改善。 For the problem of surface pockmarks of non-oriented silicon steel strip produced by a DMS Sendzimir mill, based on the production practice, the formation causes were analyzed from two aspects of emulsion and working roll. The results show that the emulsion has a certain effect on the formation of surface pockmarks defects, but it is not the main factor. The main reason is that the working roll diameter of the 20-high Sendzimir mill is small, and the running period of the roll rolling the same l... 

本实用新型公开了一种高磁感取向硅钢用钢带纠偏装置，包括支架，所述支架的顶部外壁通过螺栓固定连接有传送电机、安装柱和固定板，所述安装柱的顶部外壁通过螺栓固定连接有侧边板，所述侧边板的两边内壁均开有滑动槽，所述滑动槽的内壁通过螺钉固定连接有滑动轨道，所述滑动轨道的内壁滑动连接有滑动板，所述侧边板的一侧内壁设有推力弹簧，所述滑动板的底部外壁通过轴承连接有抵边轮。本实用新型对带钢产生更大的推力，使得带钢归位，推力弹簧的弹性使得装置对带钢的力比较缓和，不易使得带钢形变，顶压板和防抖轮会在带钢的顶部对带钢施加一个垂直向下的压力，使得带钢在运输过程中不易上下抖动。

本实用新型公开了一种具有导气槽的低空载损耗电工钢用罩式炉，包括：炉台，顶部设置有加热元件以及连通炉台外缘至中心凹陷的导气通道；炉板，压设于炉台上，设置有与中心凹陷上下对应的中心通孔；砂封槽，设置于炉台的外周，槽底低于导气通道；炉罩，罩设于炉台的顶部及外周形成炉腔，与砂封槽相压接；进气通道，穿设于炉台的中心凹陷中，具有开口向上的排气口；炉罩的炉台套接段内壁设置有导气槽，导气槽的延伸方向与炉罩的高度方向一致，导气槽将气流导向炉台外缘的导气通道进气口。该具有导气槽的低空载损耗电工钢用罩式炉的炉罩设置有导气槽，利用导气槽将硅钢卷外周下行的气流导入炉台的导气通道中，改善钢卷热处理过程中的流场和温度场。

本实用新型公开了一种形成优质玻璃膜的取向硅钢脱碳退火板，包括主体，所述主体的中部安装有组合架机构，所述组合架机构的前后两端安装有开边架，且组合架机构的底端安装有固定机构，所述主体的中部开设有槽口架，所述组合架机构的中部安装有拼接机构。该形成优质玻璃膜的取向硅钢脱碳退火板设置有拼接机构，便于使用者将内退板与拼接板进行组合使用，通过内退板的四角安装的扣体卡合安装在内槽进行固定锁紧，便于将内退板与拼接板进行组合，加强主体的防护性，便于使用者多次使用和来回使用，由于退火板可反复利用，方便后期形成优质玻璃膜，通过拼接板通过中心凸板与凸槽板进行组合，方便将拼接板的大小进行调节与更换。

6.5%Si电工钢是一种优异的软磁材料,织构对其磁性能影响很大。利用温轧工艺对6.5%Si电工钢热轧板进行不同压下率轧制,研究了温轧板织构随压下率的变化规律。实验结果显示,随着压下率的增大,{100}〈110〉、{110}〈100〉和γ纤维织构在薄板表层中的强度先增强后减弱,当压下率达到75%时,沿板厚方向形成3个组织区域:表层细晶粒区({110}〈100〉取向为主)、过渡层({111}〈110〉和{111}〈112〉变形晶粒区)和中心层(以拉长的γ纤维织构和{100}〈110〉取向晶粒为主),这种组织和织构不均性对后期织构的发展有重大影响。 6.5wt% Si electric steel has excellent soft magnetic properties,on which texture play important role.In this experiment,warm rolling technique was employed to investigate the effect of rolling reduction on texture.It was found that the density of {100}〈110〉,{110}〈100〉 and γ-fiber textures first increased and then decreased with increasing of the rolling reduction.At 75% reduction,the microstructure along the thickness of the sheet formed three zones,containing surface layer with {110}〈100〉 orien... 

本发明涉及一种无取向电工钢片绝缘涂液，它的主要有效成分包括有机树脂、水溶性磷酸二氢盐、硅溶胶、涂料助剂、和特定水溶性金属盐。上述各组分的质量组成比例为：有机树脂100份，水溶性磷酸二氢盐100‑250份，硅溶胶0‑100份、涂料助剂0‑20份，特定水溶性金属盐10‑50份，其余为水，涂液的固含量为15～40％。其中特定水溶性金属盐是指水溶性磷酸二氢盐以外的二价或多价金属盐，这种盐可以在磷酸二氢盐溶液中稳定存在，但是在电工钢涂层烧结温区会氧化或分解。本发明的绝缘涂液固化速度快且固化彻底，涂层具有优异的耐盐雾性能。

磁性能指标是硅钢产品最关键的质量指标之一，但是目前磁性能判定100%依赖于样品的离线实验室检测结果，生产线配置的在线检测仪的测量结果由于精度问题，不宜直接用于成品牌号判级。本文在现有硅钢产品质量管控体系基础上，利用大数据技术对生产数据进行分析与建模，构建不同磁性能指标在线检测模型，并在现有信息系统上完成模型库的集成部署，实现硅钢产品全长、多指标磁性能结果的拟合数据输出，支撑取样优化、精准分切、辅助综合判定等功能应用，进一步优化硅钢产品质量管控体系。 The magnetic performance index of silicon steel products is one of the most critical quality indexes.However,at present,100%determination of magnetic performance depends on the offline laboratory test results of samples,and the measurement results of the online detector configured in the production line cannot be applied in practice due to the accuracy problem.Based on the existing quality control system of silicon steel products,big data technology was used to analyze and model the production d...