采用XRD、SEM和激光粒度仪等手段,观察并研究了不同特性氧化镁在硅钢表面形成硅酸镁底层形貌特点,并结合热力学和差热-失重分析了MgO-SiO2的反应机理。研究结果表明:粒度小,活性值高的特种氧化镁在高温退火过程中与基体表面氧化物生成的硅酸镁底层,界面中硅酸镁底层嵌入基体较多,表面致密,颗粒细小,有利于形成附着性能优良的硅酸镁底层。 Surface microstructure of Mg2SiO4 coatings formed on the surface of oriented silicon steel coated with different kinds of MgO was investigated by XRD and SEM.The reaction mechanism between MgO and SiO2 was analyzed by TG-DSC and thermodynamic calculation.Results revealed that when the MgO with finer microstructure size and higher activity is employed,a dense Mg2SiO4 layer with finer microstructure and good binding to the steel substrate can be obtained.The results are very helpful for the prepar... 

一种薄规格带钢或者硅钢尾部卷取控制工艺，属于热连轧带钢卷取设备技术领域，解决薄规格带钢和硅钢尾部起套导致卸卷异常、卷形合格率下降的技术问题。解决方案为：在卷取厚度小于等于2.3mm的带钢或所卷取带钢的材质代码等于硅钢的材质代码的情况下，带钢尾部到达精轧F2机架时，G辊道速度V1=K1×D×ω×π/60；带钢尾部继续前行并到达精轧F6机架时，G辊道速度V2=K2×D×ω×π/60；在卷取厚度大于2.3mm的带钢且所卷取带钢的材质代码不等于硅钢的材质代码的情况下，G辊道投滞后速度的滞后率取值范围为90%~70%。本发明具有设计合理、工作效率高、产品质量好、可有效避免产品缺陷等优点。

本发明涉及冶金技术领域，具体涉及一种高牌号硅钢用连铸结晶器保护渣及其制备方法和应用。本发明提供的连铸结晶器保护渣，所述保护渣包括如下质量百分比的化学成分：SiO2：40‑45％、CaO：20‑27％、MgO：1.0‑2.5％、Al2O3：1‑3％、Na2O：12‑16％、F：10‑13％、C：1‑3％，其余为不可避免的杂质；其中所述保护渣的二元碱度CaO/SiO2为0.5‑0.6，熔点为950‑1000℃，1300℃下的粘度为0.25‑0.35Pa·s。本发明提供的连铸结晶器保护渣，通过低碱度、低熔点、低粘度的保护渣可有效抑制高牌号硅钢材料在连铸时铸坯表面易出现凹陷和裂纹的现象。

介绍了微合金元素锡、铌、稀土对无取向硅钢性能的影响,并扼要分析了这些元素对硅钢性能的影响机理:晶界偏聚元素Sn可细化晶粒提高硅钢磁性能;微合金元素Nb细化铁素体晶粒,提高硅钢的强度、韧性和塑性及磁性能;稀土元素(RE)在硅钢中的主要作用包括净化钢液、变质夹杂物、改善铸态组织和性能及微合金化,减少晶界上出现偏析的几率。 The influence of micro-alloy elements on properties of non-oriented silicon steel and the mechanism for effect of the micro-alloy elements including Sn、Nb and RE on the properties of steel are presented and analyzed in this paper.Grain boundary segregation elements Sn in steel can grain refinement and improve the magnetic properties;Micro-alloy elements Nb can refine the ferrite grain,increase the silicon steel strength,toughness and plastic;The main role of the RE in the silicon steel including... 

对两种硅钢水溶性极厚绝缘涂层进行了不同温度的热老化实验。通过TG-DTA,GDS,FT-IR,SEM和光泽度仪等测试方法对老化的涂层进行分析表征,提出了评估硅钢水溶性极厚绝缘涂层热老化性能的合理温度区间,探讨了涂层热老化行为,并分析了两种涂层热老化性能的差异。结果表明,涂层附着性随着老化时间的延长逐渐下降。FT-IR表征结果显示,热老化过程中,涂料交联形成的化学键未发生断裂,交联剂氨基树脂的三嗪环被破坏是聚合物三维网络结构坍塌的主要原因。 Thermal aging expriments at different temperature were carried out on two types of water-soluble and extra-thick insulation coatings for non-oriented silicon steel,and a series of test methods such as glossmeters,TG-DTA,FT-IR,GDS,SEM were applied in analysis.For evaluating the thermal aging effect of this kind of insulation coating,the proper temperature range was proposed.The difference of aging performance between two coatings was been investigated and the related behaviors were been discussed... 

为进行磷酸盐系无铬无取向硅钢涂层烧结固化工艺研究,首先对磷酸盐系无铬无取向硅钢涂层进行热重-差示扫描量热(TG-DSC)分析;然后在不同烧结固化温度条件下,测定涂层板温随时间变化曲线;最终获得涂层烧结固化温度与时间(T-t)工艺曲线。通过中性盐雾试验、动电位极化、交流阻抗、涂层附着力以及扫描电子显微镜(SEM)和能谱(EDS)分析验证。结果表明,根据涂层烧结固化温度与时间(T-t)工艺曲线制备的涂层结构致密、性能优异,证明该工艺曲线具有合理性与正确性。 In order to study the curing process of chromium-free non-oriented silicon steel coatings,phosphatic chromium-free non-oriented silicon steel insulating coating was prepared and TG-DSC analysis of the coating was conducted,then the change of the actual temperature of the coated non-oriented silicon steel sheet with time at different curing temperatures was studied. Based on the experiments,the processing curves of curing temperature vs. curing time( T-t) for the chromium-free non-oriented silico... 

取向硅钢利用析出物作为抑制剂,抑制初次再结晶晶粒的长大,抑制剂是取向硅钢发生二次再结晶的基本条件之一。文中通过低温板坯加热技术制备取向硅钢,采用透射电镜(TEM)观察并研究了高温退火阶段抑制剂的演化过程。结果表明,渗氮后形成的非晶态Si3N4析出物不稳定,在700～750℃退火升温阶段转化为(Al,Si)N;(Al,Si)N颗粒在800℃发生团聚,随后长大并粗化;(Al,Si)N是低温取向硅钢主要抑制剂,随退火温度的升高,(Al,Si)N抑制力大幅下降。 Precipitates as inhibitor are used to inhibit the grain growth of primary recrystallization in grain-oriented silicon steel,and inhibitor is one of the basic conditions for occurring of secondary recrystallization.The grain-oriented silicon steel was produced by low temperature slab heating and nitriding technique.The evolution of inhibitor was observed by transmission electron microscopy.The results show that Si3N4 particles are precipitated after nitriding,and Si3N4 particles are amorphous and... 

本实用新型涉及一种硅钢片叠装上料用转运装置，包括一输送单元，输送单元包括输送支架、输送辊，在各个输送支架均配备有一用于接收裁切好的硅钢片并堆放形成硅钢片料堆的放置板；一供料单元，包括供料板、供料支架、供料辊、支撑组件；一转运单元，包括转运支架、转运底座、转运辊、推料板、推动机构、电磁铁、转运齿条、转运齿轮、转运导轨、转运导座、导向轮、行走滚轮。本实用新型的优点在于：通过输送单元、供料单元及转运单元之间的相互配合，从而能够将满料的放置板自动输送并呈日字形自动排布好，无需再由人工搬运放置，大大减少了人工劳动，降低了人工劳动强度。

选用Q235和Q345钢,在纯锌浴和含钛量分别为0.05%、0.10%、0.15%、0.20%(质量分数)的合金浴中浸镀0.5、1、3、5、8 min。利用扫描电子显微镜和能谱仪研究了钛对热浸镀锌组织和生长动力学的影响,并提出钛对含硅钢铁锌反应抑制作用的机理。结果表明:钛的加入缩短了Γ的孕育期,促进了合金层中δ的生长和ζ的消失,δ的生长依然受扩散控制,呈抛物线生长规律;Zn-0.05%Ti锌浴可以很好的抑制高硅钢的硅反应性;含硅钢热浸镀锌钛合金浴时,在锌浴中会形成锌铁钛三元T相,该相能吸收ζ晶界处富集的硅,从而抑制了铁锌反应。 Both Q235 and Q345 steels were immersed for 0.5 to 8 min in Zn bath with different amount of Ti,ranging from 0 to 0.20 mass%,for galvanization.The effect of Ti in Zn bath on microstructure and growth kinetics of hot-dip galvanizing coatings on the two steels were investigated by means of SEM and EDS analysis.Base on the experiment,the mechanism of Ti additions in controlling Fe-Zn reaction was proposed.The results show that addition of Ti in the zinc bath decreases the incubation time of Γ phase... 

本发明提供方向性电磁钢板，能够同时实现充分低的变压器铁损与低噪音。一种方向性电磁钢板，其在表面具备张力被膜，实施了通过生成沿与轧制垂直方向在30°以内的方向延伸的线状的闭合磁畴而进行的磁畴细化处理，其中，邻接的闭合磁畴的平均间隔L为15mm以下，用规定式计算出的上述闭合磁畴相对于板厚的深度比率rd为35％以上，用规定式计算出的上述闭合磁畴的体积率rv为0.30％以上3.0％以下，用规定式计算出的上述闭合磁畴的面积率rs为0.50％以上4.0％以下。

本发明提供了一种取向硅钢制作的电机凸极转子，包括由取向硅钢一体制作而成的凸极极身、轭部与极靴，整个转子的易磁方向为径向，通过对轭部厚度、相邻凸极根部中心点距离、凸极极身宽度和极靴尺寸等进行特殊结构设计，能够提高电机功率密度与效率，且无二次气隙与额外的工艺需求。

本实用新型公开了硅钢片铁芯生产线，包括放卷机构、剪切机构、送料机构、叠片机构和下料机构，送料机构包括磁性传送带、送料件和第一定位杆，磁性传送带包括上传送带和下传送带，送料件可沿磁性传送带的正交方向平行伸出，其中，第一送料分台和第二送料分台安装于上传送带的下方并且相背运动，第三送料分台和第四送料分台安装于下传送带的下方并且相背运动，第一定位杆用于定位硅钢片，叠片机构包括叠放台、悬梁和两个六自由度机械手，六自由度机械手吊装于悬梁上，包括有电永磁铁，用于吸取硅钢片，下料机构包括滑板，叠放台放置于滑板上。根据本实用新型的硅钢片铁芯生产线，可提高设备自动化程度，提高叠片速度，从而提高生产线的生产效率。