硅钢资料

本实用新型涉及一种摩托车点火器线圈用硅钢片，包括E型件和I型件，所述E型件和I型件可组合成日字形；所述E型件包括竖边和设置在竖边三个横边，所述竖边与三个横边接触的位置设置孔眼；所述孔眼内径从为变径结构；位于E型件正面设置散热线槽，所述散热线槽一端与孔眼贯通，另一端指向凸部；位于E型件背面在散热线槽正对位置设置外凸线，所述I型件一侧设置与凸部匹配的凹部，在所述凹部之间凸台；所述凸台与凹台重叠；在凸台与凹部之间设置凸棱，所述凸棱位于I型件外侧。本实用新型设计新颖，改进巧妙，由于E型件具有弧形边可以有利于拾取，方便工作操作，同时采用采用接触的方式接触，增加了组合体的稳定性。

对CSP流程生产的无取向电工钢M50W800不同尺寸样品的磁性能进行了测试和分析,结果表明:采用不同单片检测的磁性能结果与标准的Epstein方圈样品检测对比,存在明显的偏差;且同一尺寸的单片纵横向样品之间相比较,对应的磁性能差异性也较大。几种不同尺寸的单片样品,以320mm×30mm尺寸的纵横向平均值最接近标准Epstein方圈样的性能值,其铁损偏差最小。 The magnetic properties of M50W800 non-oriented electrical steel produced by CSP process were tested and analyzed with samples of different sizes,showing that significant deviation existed compared to that of Epstein square circle sample.In particular,obvious difference in magnetic properties also existed between longitudinal and transverse samples of the same size.For test samples of different sizes,the average magnetic properties of 320mm×30mm samples are the closest to that of Epstein square ... 

概述了高磁感取向硅钢生产工艺的研究现状及发展趋势。介绍了国内外薄板坯连铸连轧流程生产高磁感取向硅钢的研究现状。从流程工序特点、热履历、组织与抑制剂控制方面进行对比,分析了薄板坯连铸连轧流程相对传统板坯流程生产高磁感取向硅钢的技术优势,在此基础上提出了利用该流程生产高磁感取向硅钢需要解决的主要技术难点。 The current status and development trend of production process for high magnetic induction grain-oriented silicon steel are summarized.The research status of producing high magnetic induction grain-oriented silicon steel by thin slab casting and rolling process at home and abroad is introduced.The potential technical advantages of producing high magnetic induction grain-oriented silicon steel by thin slab casting and rolling process are obtained by analyzing in terms of process characteristics,t... 

本发明公开了一种硅钢高温加热炉用铬基高氮合金垫块及其制备方法，所述合金垫块含有Cr、Mo、N、La、Ce和Fe，不含有钨；所述合金垫块在高温抗氧化性能和高温抗蠕变性能上，优于现有技术的铬铁合金；本发明可以优化替代现有的硅钢高温加热炉用铬铁合金垫块，满足硅钢在加热炉中的加热需求，大规模工厂化生产，拥有极高的使用价值和广阔的应用市场。

【机构】 武钢研究院； ...

绝缘涂层可以有效提高硅钢片的耐蚀、耐腐、磁、绝缘等性能，因此取向硅钢涂装绝缘涂层是取向硅钢生产过程中重要的一环。本文对取向硅钢含铬无机绝缘涂层以及氮化铬涂层的性能优缺点进行了介绍，并对国内无机含铬取向硅钢绝缘涂层及氮化铬涂层的研究现状进行了综述。最后对未来含铬无机绝缘涂层的研发方向进行了展望。 Insulation coating can effectively improve the corrosion resistance of silicon steel sheet, such as corrosion, magnetic, insulation performance, thus oriented silicon steel insulation coating is the important part of oriented silicon steel production process. In this paper, the inorganic insulation coating oriented silicon steel containing chromium and chromium nitride coating performance advantages and disadvantages are introduced.In addition, the research status of insulation coating and chrom... 

利用本钢技术中心试验厂技术手段,并与北京钢铁研究院合作,试制了用作家电用电机、微电机、小电机或部分中型电机铁芯的冷轧无取向电工钢。试制钢硅含量小于0.5%,钢板表面平滑,公称厚度0.5mm,且厚度均匀偏差小,性能测定结果表明,产品的磁性能、力学性能满足其使用要求。 BX STEELTechnology Center pilot plant using technical means,and with Beijing Iron and Steel Research Institute,trial cold rolled non-oriented electrical steel that has been used as appliance motor core,micro motor core,small motor core,or part of the medium-sized motor core。Trial steel of silicon content is less than 0.5%,steel plate surface is smooth,the nominal thickness of 0.5mm,and the thickness deviation is small,performance measurement results show that the magnetic properties,mechanical p... 

层叠铁芯使用的电磁钢板是在母材钢板(2)的表面具有涂布电磁钢板用涂布组合物而形成的绝缘被膜(3)的电磁钢板，所述电磁钢板用涂布组合物以特定的比率配合有环氧树脂、由烷基酚构成的第一固化剂、由苯酚甲阶酚醛树脂和苯酚酚醛清漆树脂中的任意一方或双方构成的第二固化剂。

本发明涉及电工钢生产技术领域，具体涉及一种冷轧取向电工钢钢带的渗氮处理工艺，旨在解决现有技术渗氮速度慢，渗氮效果不佳，能耗大，生产周期长的问题，包括以下步骤：S1、经过冶炼、连铸后，对铸坯进行热连轧、常化酸洗、冷轧及脱碳退火的工序；S2、在渗氮炉内进行两段渗氮处理：S21、第一段渗氮处理的渗氮温度为750‑950℃，渗氮时间为25‑35s,另外，渗氮介质的喷射压力为0.15‑0.25MPa,渗氮介质的流量为5‑20NL/min；S22、经稀土溶液浸泡1‑2小时后，继续第二段渗氮处理，其渗氮温度为460‑560℃，渗氮时间为10‑25s，另外，渗氮介质的喷射压力为0.15‑0.25MPa,渗氮介质的流量为1‑10NL/min；S3、涂隔离剂、高温净化退火后得到成品。

本发明公开了一种高牌号硅钢的穿带激光焊接方法，包括：将焊缝中硅含量降低到Si焊＜1.9%。采用激光+填丝焊接，填丝ER50‑6碳钢焊丝；根据焊缝截面积和激光焊接速度；激光填丝焊接时，激光线能量应足够大，达到填丝在熔池中充分混合，均匀分布，不至于填丝的成分浮在熔池的上半部分。采用此方法使焊缝组织从粗大铁素体变成细小、致密的无碳贝氏体，晶内沉淀相和晶间脆性相相对大幅减少，提高了焊缝韧性和成形性能，保证了高硅硅钢带的穿带焊接和连续生产。

一种无取向性电磁钢板，其母材的化学组成以质量％计为：C：0.0010～0.0040％、Si：3.5～4.9％、Mn：0.05～0.20％、Al：0.05～0.45％、P：0.030％以下、S：0.0030％以下、N：0.0030％以下、O：0.0100～0.0400％、Ca：不足0.0010％、Ti：不足0.0050％、Nb：不足0.0050％、Zr：不足0.0050％、V：不足0.0050％、Cu：不足0.20％、Ni：不足0.50％、Sn：0～0.05％、Sb：0～0.05％、剩余部分：Fe和杂质；满足[4.0≦Si+Al≦5.0]；除了从母材的表面到深度方向10μm的位置以外的区域的O含量不足0.0050％。

本发明提供一种能够有效地抑制去应力退火中的渗碳、氮化的，实施了耐热型的磁畴细化处理的取向性电磁钢板。该取向性电磁钢板在一侧面具有多个槽，在所述钢板的表面至少具备镁橄榄石被膜，该多个槽是朝向横切轧制方向的方向线状地延伸且在该轧制方向隔着间隔地并列，并且，形成于所述槽的底部的所述镁橄榄石被膜厚度的平均值为0.45μm以上，并且该厚度的标准偏差σ为0.34μm以下。