硅钢资料

运用EBSD和光学显微镜,研究了0.25%~0.45%Cu对无取向电工钢热轧板显微组织,成品板显微组织、织构和磁性能的影响。实验结果表明:卷取过程中Cu元素在热轧板表层的偏聚作用显著阻碍了热轧板表层再结晶晶粒长大,导致热轧板表层晶粒尺寸随着Cu含量增加而逐渐较小,但热轧板中间晶粒尺寸变化不大。同时发现Cu元素能够明显改善织构类型,使有利织构组分增加,不利织构组分减少,同时减弱织构强度。从实验结果可知0.35%Cu能够显著改善电工钢的磁性能,铁损P15/50最低达到4.1 W/kg,磁感B50最高值达到1.8 T。 Effects of high content Cu on microstructure of hot rolled plates and microstructure,texture and magnetic properties of annealed finish product plates of non-oriented electrical steel were examined by means of EBSD technique and optical microscope. The results show that surface segregation of Cu significantly hindered recrystallized grain growth of surface layer in hot rolled plate during the coiling,as a result,the surface grain sizes of the hot-rohed plates decrease with the increase of Cu con... 

从影响高牌号无取向硅钢退火工艺的主要参数入手,介绍高牌号无取向硅钢退火炉在加热、气氛控制、冷却、涂层烘烤方面的新技术,并展望无取向硅钢退火炉的发展方向。 Based on the technology parameters of high-grade non-oriented silicon steel annealing,the new technology of the annealing line,which includes heating,atmosphere control,cooling,coating baking,is introduced,and the development direction of non-oriented silicon steel annealing furnace is pointed out. 

采用EBSD技术研究了有、无拉应力作用下无取向硅钢在晶粒长大过程中织构转变及晶界变化的规律。结果表明:在晶粒生长期间,无应力作用下的硅钢中,{111}〈112〉,{111}〈110〉织构组分强化,而{100}〈001〉织构组分弱化;与无拉应力作用下的情况相比,施加5MPa的拉应力时,{111}〈112〉,{111}〈110〉织构组分强化的速率下降,{100}〈001〉织构组分变化不明显。对于在晶粒生长期间持续变化的{111}〈112〉,{111}〈110〉和{100}〈001〉织构组分而言,虽然有、无拉应力作用下硅钢的{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率均下降,而{100}〈001〉织构组分的高取向差角度晶界频率则上升,但当有拉应力作用后,{111}〈112〉和{111}〈110〉织构组分的高取向差角度晶界频率下降的速率变小,{100}〈001〉织构组分的高取向差角度晶界频率上升的速率稍有变小。通过对无取向硅钢在晶粒长大过程中织构转变及晶界变化规律的研究,分析了合金原子在晶界的偏聚行为。 The rules of texture and grain boundary transformation in the nonoriented silicon steel under applied stress or without applied stress during grain growth were investigated by EBSD.The results show that the {111}〈112〉 and {111}〈110〉 components in the nonoriented silicon steel without stress are strengthened during grain growth whereas {100}〈001〉 component is weakened,but the growth rate of {111}〈112〉 and {111}〈110〉 component decreases,while the area fraction of {100}〈001〉 component doesn’t chang... 

本实用新型公开了一种取向硅钢绝缘涂层液生产用分散机，包括固定底座，固定底座顶端的一侧固定安装有套筒，套筒的内部滑动设有活塞杆，套筒的内部设有电动液压升降柱，电动液压升降柱的底端固定安装在固定底座顶端的中部，电动液压升降柱的顶端与活塞杆的底端固定连接，活塞杆的顶端固定连接有箱体，箱体底端的一侧固定安装有伺服电机，本实用新型的有益效果是：通过滑块、橡胶块、空心转轴和伺服电机的配合使涂层液搅拌分散的更加均匀，通过固定装置可以将盛有涂层液的桶固定住，防止涂层液桶转动，这样可以使涂层液进行充分搅拌，不需要时刻对其调整固定，这样也可以提升工作效率，提高生产速率，而且操作方便。

本实用新型公开了一种防溢出的无取向硅钢绝缘涂液存储装置，涉及无取向硅钢绝缘涂液技术领域，为解决现有无取向硅钢绝缘涂液存储设备在存储过程中存在涂液过满，导致液体溢出产生浪费现象的问题。所述绝缘涂液存储机构本体上方的一侧设置有液位监测器，所述液位监测器的下端设置有监测杆，所述液位监测器的输出端设置有单片机，且液位监测器的输出端与单片机电性连接，所述绝缘涂液存储机构本体的内壁设置有压力传感器，且压力传感器设置有若干个，所述压力传感器的输出端与单片机的输入端电性连接，所述绝缘涂液存储机构本体的内部设置有泵体，且泵体设置有两个，所述泵体的一端设置有溢流输送管。

本发明涉及一种基于全流程数据的冷轧硅钢厚度控制方法、装置，该方法包括：针对某个冷轧钢卷，首道次默认使用监控AGC，在进入冷轧机工序生产之前，获取其前序全流程的生产工艺和质量数据，并进行预鉴定，若发现硅钢性能波动，则首道次额外再使用秒流量AGC；若发现硅钢厚度波动不剧烈，则首道次额外再使用前馈AGC。本发明无需人工干涉，采用上述规则在生产前就能自动确定最优的AGC生产模式，保证了硅钢产品厚度精度，避免硅钢厚度指标上的缺陷。

综述了国内外大钢铁企业与研究机构采用获得抑制剂法生产低温高磁感取向硅钢的开发及应用情况,分析了以该法生产高磁感取向硅钢过程中抑制剂的控制技术,包括固有抑制剂组成方案、气态渗氮方式与工艺及高温退火工艺的制定.研究表明,固有抑制剂组成方案的设计思路大体一致,化合物抑制剂以AlN为主、硫化物为辅,同时添加少量Sn,Sb等单元素抑制剂,但组成元素含量存在一定差别;在脱碳退火后用NH3进行非平衡渗氮处理已成为气态渗氮的主要方式,但最佳方式仍未明确,具体选择需依据实际生产条件,相应脱碳及渗氮工艺的控制条件差别较大;高温退火工艺中升温制度差别不大,升温阶段退火气氛中N2含量的选择存在差别.此外,分析了抑制剂控制技术目前存在的关键问题,并指出了进一步的研究方向. The current application and exploitation on production of low-temperature high magnetic induction grain-oriented silicon steel with acquired inhibitor method at both iron and steel enterprises and research institutions in the world are reviewed. The control techniques of inhibitors, which include the composition design for inherent inhibitors, nitriding method and process, and secondary recrystallization annealing, are thoroughly analyzed and proposed. It is indicated that the design ideas for i... 

用于层叠铁芯的电磁钢板为一种电磁钢板，其在母材钢板(2)的表面，具有涂布电磁钢板用涂布组合物而成的绝缘被膜(3)，所述电磁钢板用涂布组合物含有环氧树脂、环氧树脂固化剂、以及弹性体改性酚醛树脂，所述弹性体改性酚醛树脂的含量相对于所述环氧树脂100质量份，为10质量份以上100质量份以下。

根据相关的取向电工钢典型专利技术,概述了日本高磁感低铁损取向电工钢低温板坯加热、抑制剂合理调节、关键成分Mn、C、Sn和Sb调节与利用、新型退火剂和绝缘溶液的制备及细化磁畴等生产工艺最新动态和进展情况,并提出了国内企业申请取向电工钢专利时应当借鉴之处。 According to related typical patent technology for grain-oriented electrical steel sheets,the recent trends and progress situation for production process of grain-oriented electrical steel sheets with high magnetic flux density and low core loss in Japan are summarized including low temperature slab heating,suitably regulating inhibitors,adjusting and utilizing key element Mn,C,Sn and Sb,manufacturing for new annealing agent and insulating solutions,and fining magnetic domain,and some suggestion... 

研究了CSP流程试制50W270高牌号无取向硅钢热轧→常化→冷轧→退火过程中织构的演变.利用电子背散射衍射技术对全流程织构进行测量和分析.发现热轧板织构在厚度方向上存在较大差异,表层主要为铜型、黄铜和高斯织构,1/4层存在微弱的高斯织构和旋转立方织构,中心层以γ纤维织构和旋转立方织构为主,还含有较弱的α纤维织构.与热轧板相比,常化板表层和1/4层织构变化不大,中心层旋转立方织构和α纤维织构增强.冷轧板各层均具有α纤维织构和γ纤维织构.与冷轧板相比,成品板各层中α纤维织构基本消失,还出现了立方织构和高斯织构. This article focuses on texture evolution in 50W270 high-brand non-oriented silicon steel produced by CSP in hot rolling,normalizing,cold rolling,and annealing processes.The texture in the whole process was measured and analyzed by electron back-scatter diffraction.It is found that the texture along the thickness direction in hot-rolled strips changes obviously;there are mainly copper,brass,and Goss textures in the surface layer;the 1/4 layer has weak Goss texture and rotating cube texture;γ-fib... 

本发明涉及一种硅钢片叠压设备，包括加压机构，加压机构包括压台和压板，压台四角均设置导向柱，导向柱下端与压台固定连接，上端垂直向上延伸且穿透压板四角，压板上方设置有加力机构，加力机构包括固定板、活动板和挤压弹簧，固定板、活动板和压板平行设置，固定板设置与最上方且与导向柱上端固定连接，活动板设置于固定板和压板之间，固定板上穿透有多个螺杆，螺杆下端抵靠活动板顶面；活动板与压板之间均匀分布有多个挤压弹簧。本技术方案压台和压板构成了用于挤压叠放的硅钢片，通过转动螺杆可以将活动板向下推动，进而使活动板通过挤压弹簧将压板向下推动对叠放的硅钢片进行施压，装置结构简单、操作简单方便。

层叠铁芯使用的电磁钢板是在母材钢板(2)的表面具有涂布电磁钢板用涂布组合物而形成的绝缘被膜(3)的电磁钢板，所述电磁钢板用涂布组合物以特定的比率配合有环氧树脂、由烷基酚构成的第一固化剂、由苯酚甲阶酚醛树脂和苯酚酚醛清漆树脂中的任意一方或双方构成的第二固化剂。