本发明公开了一种取向硅钢产品的在线性能判级与精确分切装置和方法，使得同一个分卷上的性能分布均匀，避免分卷出现性能废品或多个性能等级的情况，提高分卷性能稳定性。提供的一种取向硅钢产品的在线性能判级与精准分切方法包括生产数据采集、铁损曲线自学习、数据存储、性能在线判级、缺陷数据采集、缺陷判级、智能分切等模块，依据修正后的磁性能全长数据，得到产品的性能判级结果，结合表面缺陷判级结果，综合确定分切位置，制定最佳分切方案。本发明可以实现取向硅钢生产过程中的性能在线判级和精准分切，得到性能均匀、表面质量好的分卷，减少分卷性能不稳定带来的损失。

研究表明,硅钢中的夹杂物对成品带钢的磁性能有显著影响。为研究冶炼过程硅钢中的夹杂物遗传变化,进而提出更有效的控制措施加以去除,本文结合典型的无取向硅钢生产炉次,采用非水溶液电解提取+扫描电镜观察方法分析冶炼过程中上述炉次典型试样的夹杂物。结果表明:转炉冶炼结束、RH精炼开始时,钢的氧化物夹杂总量最大,约为0.23%;RH精炼过程中,氧化物夹杂总量不断降低,并在脱碳结束时达到最低,约为0.02%;连铸过程中,氧化物夹杂总量仍有不断降低趋势,但夹杂物的平均尺寸变化不大。本试验条件下,中间包试样的夹杂物数量约为1.59×104个/mm3。 As we all know, the non-metallic inclusion effects magnetic properties of silicon steel sheets obviously. The article aims to study the heredity of non-metallic inclusion in non-oriented silicon steels during the steel making process, and then provides a more effective controlling measure to remove the inclusions. Based on the typical non-oriented silicon steel charges, the non-aqueous solution extraction and SEM observation were adopted to analyze the non-metallic inclusions. Results show that,... 

本发明一种铝镇静含硅钢的脱氧方法，包括转炉冶炼、LF炉精炼工序，转炉工序：转炉出钢过程采用含硅脱氧剂进行脱氧，出钢完毕后，向钢液表面加入顶渣改质剂，数量为400±25kg/炉，所述顶渣改质剂的成分及其质量百分含量为：Al2O3：9％±1％，CaO：27.5％±1.5％，SiO2：3％±1％，Al：50％±2％，CaF2：7％±1％。精炼工序：采用铝脱氧剂进行脱氧、造渣。本发明通过两步脱氧工艺，大幅降低脱氧成本同时提高钢水质量，由于硅脱氧相对于铝脱氧在钢水中形成的夹杂物更容易上浮，所以也提高了钢水纯净度，提高钢水质量。

本发明公开了一种无瓦楞状缺陷的高磁感低铁损无取向电工钢板，其各化学元素质量百分含量为：0＜C≤0.0035％、Si：1.2～2.8％、Mn：0.2～1.0％、P：0.04～0.15％、Sn+Sb：0.02～0.2％，余量为Fe和其他不可避免的杂质。此外，本发明还公开了上述高磁感低铁损无取向电工钢板的制造方法，其包括步骤：(1)冶炼和连铸，其中在该步骤不采用电磁搅拌；(2)热轧，其包括：粗轧、精轧、卷取和均热；其中在粗轧步骤采用2～6道次进行轧制，且粗轧单道次压下率控制在20％～40％之间；(3)上述热轧步骤后不进行常化步骤而直接进行冷轧；(4)连续退火。本发明所述的无瓦楞状缺陷的高磁感低铁损无取向电工钢板在保证较低生产成本的同时，还具有高磁感和低铁损的特性。

结合工业化生产的高效硅钢,进行了RH精炼稀土处理试验研究。针对不同的稀土处理条件,观察了夹杂物的形貌和尺寸分布,探讨了稀土处理后钢中的夹杂物形成、变化规律。结果表明:试验条件下,最佳的稀土合金添加数量为0.6～0.9 kg/t。经过合适的稀土处理后,可以有效抑制尺寸相对较小的、不规则的AlN、MnS复合夹杂生成,促进钢中微细夹杂物的聚合、上浮,钢质纯净度得到明显提高。此时,钢中全氧含量最低,脱硫效果最佳,钢中的夹杂物主要是尺寸相对较大的、近似球形或者椭球形的稀土类夹杂。 Based on the industrial production of non-oriented silicon steel,the experiment on RE treatment during the RH refining process was studied.The morphology and the size distribution were observed for the steel specimens treated with different RE treatment conditions.Further more,the formation and change of inclusions of final steel sheets after RE treatment were discussed.The results show that the suitable RE added amount was 0.6～0.9 kg/t.After the suitable RE treatment,the formation of AlN and Mn... 

研究了热处理工艺(退火温度、保温时间、冷却方式)对含Mn的Fe-6.5wt%Si高硅钢热轧带的显微组织及硬度的影响。结果表明,退火温度对Fe-6.5wt%Si合金的组织和显微硬度均有较大影响,随退火温度升高,平均晶粒尺寸和显微硬度均明显增大。小于1 h退火时,晶粒长大缓慢,而长时间(>1 h)退火时,一些次表层晶粒将发生异常长大。水冷组织比空冷组织略细小,但水冷显著降低了显微硬度。Mn含量提高能抑制850℃退火时晶粒的长大,并且促进退火后高硅钢的软化。 The influences of heat treatment process(annealing temperature,heating time,cooling methods) on the microstructure and microhardness of Fe-6.5wt%Si high silicon steel containing manganese for hot rolled strip were studied.The results show that the annealing temperature has a great effect on the microstructure and microhardness of Fe-6.5wt%Si alloy,and as the annealing temperature increases,the average grain sizes and microhardness will significantly increase.When annealing time for less than 1 h... 

对两种硅钢水溶性极厚绝缘涂层进行了不同温度的热老化实验。通过TG-DTA,GDS,FT-IR,SEM和光泽度仪等测试方法对老化的涂层进行分析表征,提出了评估硅钢水溶性极厚绝缘涂层热老化性能的合理温度区间,探讨了涂层热老化行为,并分析了两种涂层热老化性能的差异。结果表明,涂层附着性随着老化时间的延长逐渐下降。FT-IR表征结果显示,热老化过程中,涂料交联形成的化学键未发生断裂,交联剂氨基树脂的三嗪环被破坏是聚合物三维网络结构坍塌的主要原因。 Thermal aging expriments at different temperature were carried out on two types of water-soluble and extra-thick insulation coatings for non-oriented silicon steel,and a series of test methods such as glossmeters,TG-DTA,FT-IR,GDS,SEM were applied in analysis.For evaluating the thermal aging effect of this kind of insulation coating,the proper temperature range was proposed.The difference of aging performance between two coatings was been investigated and the related behaviors were been discussed... 

本发明公开了一种硅钢含铬涂层废液处理过程中六价铬浓度在线监控方法，提出一种准确检测废液中六价铬含量的方法和检测时间的确定，实现了含铬废水原液中六价铬含量预测和焦亚硫酸溶液添加量的确定及六价铬在线检测预处理系统的启动时间的确定，确保处理装置安全高效运行。在酸化还原罐上安装氧化还原电位检测仪，实时检测含铬废液在整个处理过程中ORP的变化，推测含铬涂层废液中六价铬还原情况，初步判断还原过程的终点，为在线六价铬自动检测仪的启动提供依据，最终实现解毒后废液六价铬的含量低于0.05mg/L，达到六价铬含量超低处理的要求。

本发明公开了一种用于无取向硅钢清洗液的洁净度检测分析方法，包括以下步骤：步骤1：从清洗液循环槽中取含有污物的清洗液样品，并进行脱水、烘干、研磨，得到污物粉末样品；步骤2：根据含有污物的清洗液样品和污物粉末样品计算清洗液循环槽中清洗液的洁净度；步骤3：根据含有污物的清洗液样品的洁净度建立清洗液洁净度评定标准；步骤4：根据清洗液洁净度评定标准控制含有污物的清洗液的排放和换液。本发明能简便且直观的了解当前清洗段循环槽内清洗液的状态，并可以根据清洗液的洁净度评级对清洗液的使用和排放做出及时的在线调整。

利用DSC、XRD,结合热焓分析对硅钢级氧化镁和二氧化硅的固相反应行为进行了研究。比较了不同二氧化硅原料及混合方法对硅钢级氧化镁反应性的影响,找到了一种更为有效的硅钢级氧化镁反应性的评估方法,克服了传统柠檬酸活性法在比较不同厂家生产的氧化镁的反应性上的局限性。进一步研究了Na₂B₄O₇添加剂、TiO₂添加剂对氧化镁和二氧化硅反应行为的影响,结果表明,Na₂B₄O₇添加剂含量的增加对反应有利,而TiO₂添加剂对反应有阻碍作用。 The solid-state reaction behavior between silicon-steel grade MgO and SiO₂ was investigated by DSC and XRD combined with enthalpimetric analysis.The influence of different kinds of SiO₂ and different preparation methods were studied and a specifical measurement that is more reliable was proposed to evaluate reactivity of silicon steel grade MgO.It overcomes the limitation of the traditional citric acid activity（CAA） method,which can not be used to evaluate the reactivity of... 

 

本发明公开了一种低磁致伸缩取向硅钢的制造方法，其包括步骤：(1)在硅钢基板上进行单面激光刻痕，其中进行激光刻痕的表面为第一表面，第一表面的背向一侧表面为第二表面；(2)基于激光刻痕的功率确定第一表面和第二表面的挠度差；(3)基于挠度差获得第一表面和第二表面所涂覆的绝缘涂层的涂覆量差；(4)基于涂覆量差，在第一表面和第二表面上涂覆绝缘涂层，其中第二表面的绝缘涂层涂覆量大于第一表面的绝缘涂层涂覆量。相应地，本发明还公开了采用上述制造方法所制得的低磁致伸缩取向硅钢，其第一表面和第二表面的磁致伸缩偏差≤2db(A)，并且所述低磁致伸缩取向硅钢的平均磁致伸缩≤55db(A)。