硅钢资料

对两种硅钢水溶性极厚绝缘涂层进行了不同温度的热老化实验。通过TG-DTA,GDS,FT-IR,SEM和光泽度仪等测试方法对老化的涂层进行分析表征,提出了评估硅钢水溶性极厚绝缘涂层热老化性能的合理温度区间,探讨了涂层热老化行为,并分析了两种涂层热老化性能的差异。结果表明,涂层附着性随着老化时间的延长逐渐下降。FT-IR表征结果显示,热老化过程中,涂料交联形成的化学键未发生断裂,交联剂氨基树脂的三嗪环被破坏是聚合物三维网络结构坍塌的主要原因。 Thermal aging expriments at different temperature were carried out on two types of water-soluble and extra-thick insulation coatings for non-oriented silicon steel,and a series of test methods such as glossmeters,TG-DTA,FT-IR,GDS,SEM were applied in analysis.For evaluating the thermal aging effect of this kind of insulation coating,the proper temperature range was proposed.The difference of aging performance between two coatings was been investigated and the related behaviors were been discussed... 

某冷连轧机生产无取向硅钢板材时,其边缘降的长度合格率频繁超标。为满足用户的叠片厚度精度要求,这类产品必须以增大切边量的方式来保证交货质量,而这种方式又直接降低了金属收得率,提高了生产成本。基于此,以该产线现有设备特性为基础,详细分析其软、硬件功能模式,分别对辊形与反馈控制进行全面分析与优化改进。通过现场试验论证,充分明确依托辊形优化与反馈控制程序的改进能显著提高边缘降的控制水平,该技术的使用为生产现场的边缘降控制提供了合理的技术支撑。 A cold rolling mill production of non-oriented silicon steel sheet,the thickness difference of the edge( edge-drop) is usually exceed the preset standard value,In order to meet the accuracy requirements of the user flatness,these production must be trimed wider length to meet the delivery quality of the user need, which directly reduce the metal yield and increase the manufacturing cost. Therefor,the software and hardware of the production line has been analyzed, and the work roll shape and feed... 

针对宝钢硅钢常化退火过程中产生的退火炉辊印缺陷问题,通过实际生产的大数据与产品质量问题相结合,将数据挖掘、数据分析方法应用到实际,一定程度上解决了现场实际生产中的痛点,为现场生产提供决策支撑,避免了以前通过人工识别判定存在疏漏和无法定量判断的问题,形成了一套具有鲁棒性和可操作性的钢铁生产过程数据分析方法。通过智慧决策系统平台获取实际生产和表检仪数据,基于Pearson相关系数算法进行变量挑选和特征工程,并应用随机森林算法对数据建立分类预测模型,实现了质量问题的溯源和监控,通过数据量化预测了炉辊印缺陷是否可通过轧制消除的质量问题,识别准确率达到96.43%。 In views of the normalizing annealing furnace roll marks problem occurred in the process of normalizing annealing of silicon steel in Baosteel,by combining big data from actual production with product quality problems,data mining and data analysis methods were applied to actual production to solve the pain points and provide decision support,a robust and practical data analysis method for the steel production process has been developed,which avoided the previous problems of omission and non-quan... 

本发明公开了一种硅钢氧化镁废水资源化处理方法及处理系统，硅钢氧化镁废水进入过滤浓缩干化一体化装置经预过滤、过滤、干燥、排泥后得到清液和泥饼；泥饼经烘干后得到烘干泥饼；烘干泥饼溶解于硫酸溶液中，反应后的混合液固液分离得到上层清液和沉淀物，上层清液经中和、蒸发结晶后得到结晶物，沉淀物进行清洗、烘干处理。本发明还设计了实现上述处理方法的处理系统，该系统包括过滤浓缩干化一体化装置、烘干装置、溶解装置以及产水箱；本发明的硅钢氧化镁废水经处理后的清液满足回用要求，可返回机组循环利用，实现废水回用，泥饼经烘干、溶解后可分别作为钛白粉生产原料和土壤改良剂，具有经济环保双重效果，以及良好的社会效益和环境效益。

提出以“云边一体化架构”构建硅钢智慧决策系统，来解决原硅钢制造L1～L5系统架构模式下的数字信息孤岛、业务功能割裂等问题。在此基础上，开发了云边协同的自学习型控制模型及业务决策模型，构建起硅钢“智慧大脑”，形成了以研发、制造、服务等核心业务数字化融合的智能化决策支持新模式，探索出一条钢铁制造业数字化、智能化转型之路。 SIDS(Silicon-steel Intelligent Decision-making System)based on \"cloud-edge integration architecture\" was proposed to solve the problems of data silos and business function fragmentation in the original L1～L5 system architecture.On this basis,the self-learning control model and decision-making model of cloud-edge collaboration were developed,the \"smart brain\" of silicon steel department was constructed,and a new intelligent decision-making support model of digital integration of core businesses s... 

利用DSC、XRD,结合热焓分析对硅钢级氧化镁和二氧化硅的固相反应行为进行了研究。比较了不同二氧化硅原料及混合方法对硅钢级氧化镁反应性的影响,找到了一种更为有效的硅钢级氧化镁反应性的评估方法,克服了传统柠檬酸活性法在比较不同厂家生产的氧化镁的反应性上的局限性。进一步研究了Na₂B₄O₇添加剂、TiO₂添加剂对氧化镁和二氧化硅反应行为的影响,结果表明,Na₂B₄O₇添加剂含量的增加对反应有利,而TiO₂添加剂对反应有阻碍作用。 The solid-state reaction behavior between silicon-steel grade MgO and SiO₂ was investigated by DSC and XRD combined with enthalpimetric analysis.The influence of different kinds of SiO₂ and different preparation methods were studied and a specifical measurement that is more reliable was proposed to evaluate reactivity of silicon steel grade MgO.It overcomes the limitation of the traditional citric acid activity（CAA） method,which can not be used to evaluate the reactivity of... 

一种生产取向硅钢的氧化镁涂层烘烤质量控制方法，通过对带钢的实时温度测量建立对烘烤输出功率的实时反馈调节，据此形成基于烘烤输出功率的烘烤质量的实时控制。本发明的一种生产取向硅钢的氧化镁涂层烘烤质量控制方法，通过在烘烤炉出口的带钢上方增加一套可在带钢横向方向移动的在线板温计，基于在线板温检测值对烘烤炉状态进行监控，并建立烘烤输出功率控制系统实时调整，使得氧化镁涂层烘烤质量均匀，提高取向硅钢产品质量稳定性，节省能源消耗。

为了弄清楚高硫硅钢中的硫化物析出行为及其对钢的微观组织和电磁性能的影响，以便为工业化生产制定更为合理的硫含量控制标准和采取更为有效措施减轻炼钢生产的硫含量控制压力，结合0.25% Si 无取向硅钢 ，采用非水溶液电解提取 + 扫描电镜/透射电镜观察相结合的方法 ，研究了0.006 8%、0.010 2%、0.025 5% 和 0.035 3% 硫含量条件下，钢中的硫化物夹杂物组成和存在形式及其形貌、种类、尺寸、数量变化，以及相应的热轧、成品试样的微观组织和电磁性能变化。结果表明，随着钢中硫含量的增加，钢中的硫化物逐渐由 MnS→MnS+Cu₂S→Cu₂S转变，数量逐渐增多，尺寸向高低两个方向发展。相应地，导致热轧再结晶组织劣化和抑制了成品晶粒尺寸长大。随着钢中硫含量的增加，钢的磁感、铁损劣化程度逐渐增大。钢中的硫含量平均每增加 0.01%，涡流损耗、磁滞损耗分别劣化0.24 W/kg 和 0.41 W/kg，而磁感会劣化 0.009 T。但是 ，在硫含量为 0.010 2% 时 ，铁损可以低于 6.0W/kg，而在硫含量为 0.025 5% ... In order to find out the precipitation behavior of sulfide inclusions and the corresponding changes of microstructure and electromagnetic properties of high sulfur silicon steel sheets, so that to design more suitable sulfur concentration controlling limit for industrial manufacture and to release the steel-making difficulty effectively, Based on the change of given sulfur concentration 0.006 8%, 0.010 2%0.025 3% and 0.035 3%, the type and composition, the size and number, and the size distribut... 

本发明公开了一种硅钢氧化镁废水回用处理与污泥资源化工艺，包括：预过滤：氧化镁废水进入过滤容器，过滤得到的水，返回调节池中，直至预过滤澄清；过滤过程：氧化镁废水在预过滤阶段逐渐澄清后进入过滤程序，产生的过滤水满足要求后，自流入产水箱；滤饼干燥：停止过滤后，将过滤容器中的水排空至调节池，之后按照与过滤相同的方向通压缩空气，通过压缩使滤饼干燥；反吹排泥：滤饼干燥完成后，通反向的压缩空气，之后进入下一个过滤周期；经过处理后，过滤阶段产生的合格水循环利用；滤饼干燥后进一步进行资源化处理。本发明实现了废水回用；产生的沉淀污泥经处理后可分别作为钛白粉的生产原料和土壤改良剂，具有良好的社会效益和环境效益。

本发明公开了一种硅钢产品生产方案的智能设计评估方法，包括以下步骤：1、采集数据，并集成用户数据、实验室研发数据和大生产数据；2、构建用户数据主题、实验室研发数据主题和大生产数据主题；3、输入硅钢产品的种类、规格和性能需求的需求信息，并根据需求信息生成若干个硅钢产品的生产方案，生产方案包括优化产品的生产方案和新产品的生产方案；4、多维度综合评估步骤3中生成的每个硅钢产品的生产方案，得到硅钢产品生产方案的绿色设计指数，并根据绿色设计指数推荐生产方案。本发明基于产品设计需求，融合实验研发数据和大生产数据，生成并评估产品设计方案模型，缩短研发周期，提高研发效率。

一种适用于取向电工钢产线的一体化生产计划排程方法，基于L4，建立基于如下步骤的整条取向电工钢产线的自动生产计划排程，S1：以排程所需的必要数据为基础，按核心工序为排程起点，分别依次递进式完成前工序、后工序的排程，形成初始计划排程；S2：对初始计划排程建立基于设定的评价因子构成的综合评估，形成由综合评估结果构成的综合评估结果数据集；S3：对综合评估结果数据集建立优化算法运算，根据运算结果确定生产计划排程。本发明的一种适用于取向电工钢产线的一体化生产计划排程方法，可实现较大程度的自动化，提高生产计划编制效率，增强操作人员对生产计划的整体情况掌握，并可根据设备状态及计划执行情况自动对计划作出快速响应。