硅钢资料

结合工业化生产的高效硅钢,进行了RH精炼稀土处理试验研究。针对不同的稀土处理条件,观察了夹杂物的形貌和尺寸分布,探讨了稀土处理后钢中的夹杂物形成、变化规律。结果表明:试验条件下,最佳的稀土合金添加数量为0.6～0.9 kg/t。经过合适的稀土处理后,可以有效抑制尺寸相对较小的、不规则的AlN、MnS复合夹杂生成,促进钢中微细夹杂物的聚合、上浮,钢质纯净度得到明显提高。此时,钢中全氧含量最低,脱硫效果最佳,钢中的夹杂物主要是尺寸相对较大的、近似球形或者椭球形的稀土类夹杂。 Based on the industrial production of non-oriented silicon steel,the experiment on RE treatment during the RH refining process was studied.The morphology and the size distribution were observed for the steel specimens treated with different RE treatment conditions.Further more,the formation and change of inclusions of final steel sheets after RE treatment were discussed.The results show that the suitable RE added amount was 0.6～0.9 kg/t.After the suitable RE treatment,the formation of AlN and Mn... 

简要介绍了宝钢无取向电工钢的发展历程、产品大纲、电磁性能控制情况,以及高附加值新产品的开发、应用情况。概述了近年来宝钢无取向电工钢生产技术进步,主要包括夹杂物控制技术、连轧机高牌号硅钢制造技术、同板差控制技术、环保涂层开发技术等。 This paper briefly summarizes the development history, product catalogue, and magnetic properties of non-oriented electrical steel sheets at Baosteel, as well as the development and application of high-value-added steel grades. Recent advances in manufacturing electrical steel sheets are also introduced, including technologies for controlling inclusion, producing high-grade steel strips by a tandem rolling mill, and controlling the transverse thickness difference of steel sheets, as well as the ... 

结合工业化生产的无取向硅钢,进行了RH精炼喂CaSi线去除钢中的非金属夹杂物试验研究。针对不同的钙处理条件,分析了CaS夹杂生成热力学,观察了夹杂物的形貌和尺寸分布,确定了夹杂物的类型、数量,探讨了钙处理后钢中夹杂物的变化规律。结果表明,本试验条件下,钙处理可以有效抑制MnS、AlN夹杂物的生成,有效促进钢中微细夹杂物的聚合、上浮、去除,钢质纯净度明显提高。经过合适的钙处理后,钢中的夹杂物以独立存在的CaO为主,同时有少量含CaO、SiO2、MgO的复合夹杂,没有发现CaS夹杂存在。这部分夹杂物的尺寸集中分布在2～20μm,数量约为1.8×105个/mm3。 Experimental study on removal of non-metallic inclusions in non-oriented silicon steel obtained from industrial production by CaSi wire feeding during RH refining process was carried out.The thermodynamics of CaS inclusion formation was analyzed,the morphology and the size distribution of inclusions were observed,and the numbers and types of inclusions were also determined for the steel specimens treated under different calcium treatment conditions.Furthermore,the variation of inclusion characte... 

本发明公开了一种电化学评价取向硅钢氧化层的装置及方法，包括电解池、设于电解池一侧的磁铁组、设于电解池上的饱和甘汞电极和铂电极以及与电解池连接的电化学工作站；磁铁组包括固定在电解池上的固定磁铁和与固定磁铁磁性连接的移动磁铁，移动磁铁设于电解池侧面的出口上；参比电极设于磁铁组与辅助电极之间；参比电极和辅助电极与电化学工作站连接。本发明的评价方法通过电化学测量取向硅钢试样的电位‑时间曲线，计算出取向硅钢氧化层各分层的溶解电量，实现了对取向硅钢氧化层各分层的快速、准确测定，可以区分出Mg2SiO4玻璃膜底层、SiN层、SiO2层、FeO及铁橄榄石层等分层性能，为取向硅钢生产工艺参数的控制提供指导。

研究了硅钢铸坯再加热过程中夹杂物的析出行为。采用非水溶液电解提取+扫描电镜观察方法,观察了试样的显微组织,统计了夹杂物的尺寸、种类、数量、分布。结果表明,均热温度为1 523 K时,水淬试样的夹杂物尺寸绝大部分小于0.5μm,0.5～5.0μm的夹杂物数量很少,没有发现5.0μm以上的夹杂物。此外,均热时间为10、30、60、90、120、240 min时,对应试样中0.05～0.2μm的夹杂物数量分别为4.04×104、4.73×104、3.70×104、3.33×104、3.10×104、1.56×104个/mm3。绝大部分夹杂物以MnS、AlN、CuxS类为主,并以三类夹杂物中的两类复合或三类复合居多。三类复合夹杂物总量占每组试样夹杂物总量的90%或以上。随均热时间延长,典型的夹杂物组成会发生如下变化:MnS+AlN+CuxS MnS+AlN AlN。与此同时,MnS、AlN、CuxS三者复合比例从45.2%(均热10 min)降为9.7%(均热240 min)。 The methods of electrolysis extraction from nonaqueous solution and scanning electron microscope were adopted to study the precipitation behavior of non-metallic inclusions in Si steel slabs during reheating processes.The morphologies,chemical compositions,quantity and size distribution of non-metallic inclusions in these steel samples were analyzed.Results show that,when the soaking temperature is 1 523 K,almost all of the non-metallic inclusions are smaller than 0.5 μm,few are in the range of ... 

 

本发明公开了一种硅钢含铬涂层废液处理过程中六价铬浓度在线监控方法，提出一种准确检测废液中六价铬含量的方法和检测时间的确定，实现了含铬废水原液中六价铬含量预测和焦亚硫酸溶液添加量的确定及六价铬在线检测预处理系统的启动时间的确定，确保处理装置安全高效运行。在酸化还原罐上安装氧化还原电位检测仪，实时检测含铬废液在整个处理过程中ORP的变化，推测含铬涂层废液中六价铬还原情况，初步判断还原过程的终点，为在线六价铬自动检测仪的启动提供依据，最终实现解毒后废液六价铬的含量低于0.05mg/L，达到六价铬含量超低处理的要求。

聚焦无取向硅钢产品标准,从电磁性能、表面性能、机械性能以及尺寸公差与边部质量等维度对国际标准IEC、EN、JIS、ASTM以及国标GB进行了分析研究。分析得出,各类标准在电磁性能方面要求基本一致;ASTM标准的机械性能要求有别于其他几个标准。 In this paper,non-oriented silicon steel standards of EN,JIS,GB and ASTM were compared and analyzed. It is showed that,all types of standards in electromagnetic performance requirements are basically the same. Surface properties in ASTM standard are expressed in the most detailed. The mechanical properties requirements of the standards,except for ASTM,are basically the same. 

本发明公开了一种硅钢氧化镁废水资源化处理方法及处理系统，硅钢氧化镁废水进入过滤浓缩干化一体化装置经预过滤、过滤、干燥、排泥后得到清液和泥饼；泥饼经烘干后得到烘干泥饼；烘干泥饼溶解于硫酸溶液中，反应后的混合液固液分离得到上层清液和沉淀物，上层清液经中和、蒸发结晶后得到结晶物，沉淀物进行清洗、烘干处理。本发明还设计了实现上述处理方法的处理系统，该系统包括过滤浓缩干化一体化装置、烘干装置、溶解装置以及产水箱；本发明的硅钢氧化镁废水经处理后的清液满足回用要求，可返回机组循环利用，实现废水回用，泥饼经烘干、溶解后可分别作为钛白粉生产原料和土壤改良剂，具有经济环保双重效果，以及良好的社会效益和环境效益。

研究了热处理工艺(退火温度、保温时间、冷却方式)对含Mn的Fe-6.5wt%Si高硅钢热轧带的显微组织及硬度的影响。结果表明,退火温度对Fe-6.5wt%Si合金的组织和显微硬度均有较大影响,随退火温度升高,平均晶粒尺寸和显微硬度均明显增大。小于1 h退火时,晶粒长大缓慢,而长时间(>1 h)退火时,一些次表层晶粒将发生异常长大。水冷组织比空冷组织略细小,但水冷显著降低了显微硬度。Mn含量提高能抑制850℃退火时晶粒的长大,并且促进退火后高硅钢的软化。 The influences of heat treatment process(annealing temperature,heating time,cooling methods) on the microstructure and microhardness of Fe-6.5wt%Si high silicon steel containing manganese for hot rolled strip were studied.The results show that the annealing temperature has a great effect on the microstructure and microhardness of Fe-6.5wt%Si alloy,and as the annealing temperature increases,the average grain sizes and microhardness will significantly increase.When annealing time for less than 1 h... 

本发明一种铝镇静含硅钢的脱氧方法，包括转炉冶炼、LF炉精炼工序，转炉工序：转炉出钢过程采用含硅脱氧剂进行脱氧，出钢完毕后，向钢液表面加入顶渣改质剂，数量为400±25kg/炉，所述顶渣改质剂的成分及其质量百分含量为：Al2O3：9％±1％，CaO：27.5％±1.5％，SiO2：3％±1％，Al：50％±2％，CaF2：7％±1％。精炼工序：采用铝脱氧剂进行脱氧、造渣。本发明通过两步脱氧工艺，大幅降低脱氧成本同时提高钢水质量，由于硅脱氧相对于铝脱氧在钢水中形成的夹杂物更容易上浮，所以也提高了钢水纯净度，提高钢水质量。

某冷连轧机生产无取向硅钢板材时,其边缘降的长度合格率频繁超标。为满足用户的叠片厚度精度要求,这类产品必须以增大切边量的方式来保证交货质量,而这种方式又直接降低了金属收得率,提高了生产成本。基于此,以该产线现有设备特性为基础,详细分析其软、硬件功能模式,分别对辊形与反馈控制进行全面分析与优化改进。通过现场试验论证,充分明确依托辊形优化与反馈控制程序的改进能显著提高边缘降的控制水平,该技术的使用为生产现场的边缘降控制提供了合理的技术支撑。 A cold rolling mill production of non-oriented silicon steel sheet,the thickness difference of the edge( edge-drop) is usually exceed the preset standard value,In order to meet the accuracy requirements of the user flatness,these production must be trimed wider length to meet the delivery quality of the user need, which directly reduce the metal yield and increase the manufacturing cost. Therefor,the software and hardware of the production line has been analyzed, and the work roll shape and feed...