本发明涉及冶金技术领域，具体涉及一种多组分{100}织构无取向电工钢的制备方法。本发明通过控制薄带连铸参数制备1.5～2.5mm厚的无取向电工钢铸带，直接冷轧至厚度为0.35～0.50mm后，先进行预回复退火，再进行成品退火，此过程中控制退火温度、时间以及升降温速率。本发明所制备的无取向电工钢具有多组分{100}织构，包括{100}＆lt;001＆gt;、{100}＆lt;012＆gt;和{100}＆lt;011＆gt;，{100}织构组分体积分数达到25～39％，其轧向磁感值1.71～1.78T，横向磁感值1.70～1.76T，板面45°方向磁感值达到1.65～1.67T。本发明通过优化退火工艺，利用{100}变形组织的强回复与再结晶协同作用，从而显著增强{100}退火织构，方法简单有效。

为了解决目前冷轧产线硅钢现有切边技术存在的微裂纹、应力、毛刺和边浪等问题,采用光纤激光器进行了高速切割实验,对激光功率、切割速度、激光模式等影响因素进行了分析,同时对高速切割时的切割前沿形状进行了研究。结果表明,切割最高速度随着功率的增加而增加;随着离焦量的增加,切割质量下降,挂渣增多,切缝宽度增加,切割深度变浅;基模激光器能量密度更高,所以薄板切割时的切割速度高于多模激光器;切割前沿随着切割速度的增加会变得平缓,速度足够大时,切割前沿甚至接近与切割方向平行,此时切缝下部存在挂渣现象。 In order to solve the problems such as micro crack,stress,burr,edge waves and so on,existing in cold rolling production line of silicon steel side cutting,experimentsof high speed laser cutting using fiber laser were carried out.Laser power,cutting speed,laser mode and other factors were analyzed,at the same time,cutting front geometries were studied.The results show that the maximum speed increases with power.And the increases of defocus result in poor quality,wider kerf and shallowerkerf.Energ... 

本发明公开了一种耐热刻痕型取向硅钢涂层用涂液，其溶剂为水，其含有：磷酸盐、胶态二氧化硅、铬酐和乙醇。本发明还公开了一种耐热刻痕型取向硅钢板，其包括基板，所述基板表面具有采用上述的耐热刻痕型取向硅钢涂层用涂液涂覆在基板上而形成的涂层。相应地，本发明还公开了上述取向硅钢板的制造方法，其包括步骤：在基板表面涂覆所述涂液，基板的刻痕沟槽涂液填充率＞95％；进行烧结处理，其中烧结处理中的板温为780‑900℃。本发明的耐热刻痕型取向硅钢涂层用涂液具有良好的流动性，其可以涂覆于耐热刻痕取向硅钢基板的表面中，涂覆后，能有效填充基板的刻痕沟槽，且可以在其表面形成涂层，保证耐热刻痕取向硅钢在具有低铁损的同时具备更高的安全性。

研究二次冷轧压下率对于硅的质量分数为3.0%的无取向硅钢组织结构和磁性能的影响。结果表明:当第二次冷轧压下率从0变化至16.7%时,铁损逐渐增加,磁感逐渐降低。当第二次冷轧压下率大于16.7%时,随压下率的增加,铁损逐渐减小,磁感逐渐增加。当第二次冷轧压下率大于38%时,二次冷轧法所能获得的磁性能明显优于一次冷轧法。 Effect of double cold reduction on magnetic,microstructure and texture of 3.0% Si non-oriented silicon steel sheets was investigated.The results show that the iron loss increases and magnetic induction reduces as the percentage redcution in secondary cold rolling changes from 0 to 16.7%.The core loss can be reduced remarkably,and magnetic induction can get a little benefit if the percentage redcution in double cold reduction is higher 16.7%.In case of higher than 38% of the percentage redcution ... 

本实用新型公开了一种变压器铁芯用硅钢片卷放料装置，其包括底座、换位旋转机构，换位旋转机构包括设置于底座上端的旋转座、换位旋转驱动组件、至少两个以上的放卷工位，换位旋转驱动组件用于驱动旋转座相对于底座绕设置的换位旋转轴线旋转，至少两个以上放卷工位以换位旋转轴线为圆心呈环形间隔设置于旋转座，放卷工位包括有可转动安装于旋转座上的放卷筒。当其中一个放卷筒进行放卷送料时，另外的放卷筒进行上卷，当该放卷筒放卷完后，换位旋转驱动组件驱动旋转座转动，使得另外的装有硅钢片卷的放卷筒转动至放卷送料的位置，而该放卷筒就可进行上卷，如此循环操作，实现了放料装置对硅钢片卷的同步放卷放料和上卷，提高生产的效率。

【作者】 刘玲月； 李军辉； ...

借助光学显微镜、扫描电镜、交流磁性能测量仪和万能拉伸试验机研究了0.3 mm厚高强无取向电工钢冷轧板在780、820、860和900℃退火保温2 min后的组织、织构和性能。结果表明:在退火温度范围内,试验钢均发生了完全再结晶,得到等轴状的铁素体晶粒;随着退火温度的升高,平均晶粒尺寸从9.2μm增长到41.3μm,工频铁损和400 Hz高频铁损均先大幅减小后趋于平缓,磁感应强度先升高后降低。在820℃退火时,铁损P_1.5/50=5.51 W/kg,P_1.0/400=33.22 W/kg均处于较低值,磁感应强度B₅₀₀₀最大,为1.649 T。试验钢的屈服强度和抗拉强度均随退火温度的升高而降低,780℃退火时屈服强度为496 MPa, 900℃退火时降低至407 MPa。综合磁性能和力学性能考虑,试验钢的最佳退火温度是820℃。 Microstructure, texture and properties of 0.3 mm thick high strength non-oriented electrical steel cold rolled sheet annealed at 780 ℃, 820 ℃, 860 ℃ and 900 ℃ for 2 min were studied by means of optical microscope, scanning electron microscopy, AC magnetic property tester and universal tensile testing machine. The results show that in the annealing temperature range, complete recrystallization of the experimental steel occurs and equiaxed ferrite grains are obtained. With the increase of annealin... 

借助于EBSD对比研究了常化退火对高牌号无取向电工钢热轧组织和织构演变的影响,分析了常化退火对热轧板各厚度层织构的演变规律。结果表明,常化退火改善了热轧组织的均匀性,并弱化了热轧变形的γ纤维织构。升高常化退火温度,可增大热轧板的晶粒尺寸,提高{100}和{110}织构组分占有率,有利于提高无取向电工钢成品板的磁性能。 Effects of normalizing annealing on microstructure and texture of high-grade non-oriented electrical steel hot-rolled sheet were investigated by EBSD. Emphasis was put on the effects of normalizing annealing on texture evolution in the sheet thickness. The results show that the hot-rolled microstructure homogeneity is improved and the γ-fiber texture is weakened by normalizing annealing treatment. The grain size of hot-rolled sheet and intensity of the {100} and {110} favorable texture can be in... 

采用EBSD检测技术,分析了50W800无取向电工钢在重要生产工序间织构的演变以及织构沿带钢宽度方向上的差异性。结果表明:热轧板织构沿带钢宽度方向上的差异性主要体现在表层织构。带钢边部表层织构主要由旋转立方织构、α纤维织构以及少量的γ纤维织构组成,带钢宽度1/4处的表层织构主要存在高斯织构,带钢宽度1/2处的表层织构主要为(110)面织构以及少量的铜型织构。各处的带钢宽度1/4处和1/2处的织构类型基本一致,都以α纤维织构和旋转立方织构为主。冷轧后,各处的表层织构类型差异较小,均为γ纤维织构和α纤维织构。由板宽边部至中心处织构强度值逐渐降低。退火后,各处织构的组分基本一致,为较强的γ纤维织构和较弱的(100)面织构。各处织构强度值差异较小,变化趋势与冷轧板一致。 The texture of non-oriented electrical steel 50W800 was detected by EBSD technique.The evolution of the texture between important processes and the difference of texture along the width direction of strip were analyzed.The result shows that the difference along the width direction of strip of texture at the surface of hot rolled plate is most obvious.The texture at the surface of strip edge is primarily made of rotating cube texture,αfiber texture and weakγfiber texture.Goss texture is mainly co... 

本发明公开了一种高效无取向硅钢极薄带的工业连续化生产方法，其包括异步轧制、脱脂、热处理、急速冷却、涂绝缘层、烘干烧结、卷取收集各工序；其中，异步轧制中的异步比为1:1.05～1:1.24；脱脂、热处理、急速冷却、涂绝缘层、烘干烧结、卷取收集工序为连续化生产工艺；热处理工序中，第一步为预热，预热温度为500℃～720℃，预热时间20秒～125秒；第二步为相变热处理，相变热处理温度为840℃～940℃，相变热处理时间100秒～600秒；急速冷却工序中，30秒内将钢带温度降温至350℃以下。优点在于:实现工业化连续生产无取向硅钢极薄带，有效提高产能，生产的无取向硅钢极薄带具备高磁感、低铁损等磁性能。

本发明属于退火工艺技术领域，公开了一种高牌号无取向硅钢剪切方法，包括：待剪切带钢由夹送辊输送到达剪切位后，夹送辊释放对所述待剪切带钢的夹持；位于所述待剪切带钢下方的下剪刃上移，推顶所述待剪切带钢在低张力状态下持续向上运动；在所述待剪切带钢与上剪刃接触后，将所述待剪切带钢剪断。本发明提供的高牌号无取向硅钢剪切方法能够极大的减少高牌号无取向硅钢的剪切缺陷，降低废品量，提升剪切效率。

本申请提供了一种取向硅钢铸坯的制备方法及铸坯系统，该制备方法用于对精炼后的钢水进行连铸处理，所述连铸处理包括以下步骤：进行凝固处理，以使所述精炼后的部分钢水凝固形成坯壳；凝固处理时，进行电磁搅拌，以使所述精炼后的剩余钢水最终形成铸坯，其中，所述电磁搅拌的位置和结晶器出口的间距为0.3～1.5m，所述电磁搅拌的电流范围为0A～900A。上述制备方法通过调节电磁搅拌的位置和电流大小来调节电磁搅拌的强度，进而通过电磁搅拌的强度来调节等轴晶的生成量，扩大等轴晶率的范围。