综述了退火温度、时间对无取向电工钢磁性的影响。退火温度主要影响无取向电工钢不同织构的占有率,退火时间主要影响晶粒尺寸的大小,晶粒尺寸的变化对织构的形成也有一定的影响。磁感最高点出现在纤维组织完全消失,(111)面织构组分较弱的组织状态。铁损的降低主要依赖于磁滞损耗的降低,织构的影响不大。 The effects of annealing temperature and time on the non-oriented electrical steel magnetic properties were reviewed.Annealing temperature and time mainly affects the different textures share and the grain sizes of non-oriented electrical steel respectively.Changes of the grain sizes also have a certain effect on textures formation.The highest point of the magnetic induction value in the fibrous tissue completely disappears and{111} plane texture has a lower state of the component content.Iron l... 

试验研究了退火温度(850~950℃)和时间(5~18 min)对2.3 mm热轧硅钢板(/%:0.036C,3.15Si,0.21Mn,0.005P,0.007S,0.032A1)6道次轧制的0.35 mm冷轧板组织和织构的影响。结果表明,退火温度越高,晶粒平均尺寸越大,900℃5 min退火时平均晶粒尺寸41.39μm,试样织构主要集中在γ取向线上的{111}<112>织构组分和{111}<110>织构组分;900℃18 min退火时平均晶粒尺寸为48.08μm,试样的{111}面织构和{112}面织构密度都明显减弱,{001}面织构增强,磁性能较优。 The effect of annealing temperature(850 ~950 ℃) and holding time(5 ~ 18 min) on structure and texture of 0.35 mm sheet by 6 passes cold-rolling from 2.3 mm hot-rolled plate of silicon steel(/%:0.036 C,3.15 Si,0.21 Mn,0.005 P,0.007 S,0.032A1) has been tested and studied.Results show that the higher the annealing temperature the coarser the average grain size;As annealing at 900 ℃ for 5 min the average grain size of steel sheet is 41.39 μm,and the texture in sample is mainly concentrated in y orie... 

一种在取向硅钢中获得沿晶断口的方法：将取向硅钢样品加工成俄歇电子能谱仪标准试样；对标准试样进行表面清理；充氢：将标准试样所设定的预设断口处放入充氢装置的含硫脲溶液中，并使取向硅钢样品为阴极；将铂片置入并作为阳极；阴极充氢电流为1.25～1.35A，充氢电流密度在0.1～0.8A/m2，充氢时间在12～50h，充氢电压为36～39V；进行表面分析。本发明不仅工艺简单，便于操作，用时短，所用毒化剂是硫脲，从而避免了采用剧毒的三氧化二砷作为毒化剂，对人体健康有极大威胁的问题，且所获得的取向硅钢断口均为典型沿晶断口，适用于取向硅钢晶界偏聚行为以及晶界微区成分分析。

本实用新型涉及变压器组装辅助设备领域，具体涉及一种变压器铁芯硅钢板的夹紧装置，包括操作台，操作台的侧部安装有安装板，安装板的顶部固定连接有陶瓷管，安装板的一侧安装有连接座，连接座的底部连接有上连接有接线螺栓，接线螺栓上连接有用于切割泡沫棒的钨丝，接线螺栓与电源相连接；解决现有的泡沫棒人工切割效率低的问题。

以构建高磁感、低铁损、免轧制高硅电工钢铁芯为出发点,提出采用单辊甩带制备非晶铁硅合金薄带、微氧化法在铁硅合金粉末表面包覆高电阻率铁硅氧化物薄膜制备核壳异质结构高硅电工钢纳米粉末、放电等离子烧结快速成形制备颗粒间绝缘的高硅电工钢铁芯。研究了不同氧化包覆时间对SPS烧结试样密度、物相组成、微观结构和静磁性能的影响。研究表明,在氧化包覆5h烧结温度800℃工艺条件下,制备的6.5%Si高硅电工钢铁芯的静磁性能最佳,饱和磁化强度为128.84A.m2/kg、矫顽力为2.25kA/m、剩磁为3.47A.m2/kg。其饱和磁化强度与粉末压延法制备的高硅钢相当,但矫顽力降低了1/3。 The paper takes preparation 6.5%Si steel with high induction,low core loss and removing rolling as the starting point,amorphous Fe-Si ribbons was synthesized by melt spinning method,6.5%Si steel nanopowders with high resietivity core shell structure was prepared by the slight oxidation process and 6.5% Si steel iron core with evaluating internal was sintered by spark plasma sintering process(SPS).The essay focuses studies the effects of different oxidation cladding time on sample density,phase c... 

采用EBSD检测技术,分析了50W800无取向电工钢在重要生产工序间织构的演变以及织构沿带钢宽度方向上的差异性。结果表明:热轧板织构沿带钢宽度方向上的差异性主要体现在表层织构。带钢边部表层织构主要由旋转立方织构、α纤维织构以及少量的γ纤维织构组成,带钢宽度1/4处的表层织构主要存在高斯织构,带钢宽度1/2处的表层织构主要为(110)面织构以及少量的铜型织构。各处的带钢宽度1/4处和1/2处的织构类型基本一致,都以α纤维织构和旋转立方织构为主。冷轧后,各处的表层织构类型差异较小,均为γ纤维织构和α纤维织构。由板宽边部至中心处织构强度值逐渐降低。退火后,各处织构的组分基本一致,为较强的γ纤维织构和较弱的(100)面织构。各处织构强度值差异较小,变化趋势与冷轧板一致。 The texture of non-oriented electrical steel 50W800 was detected by EBSD technique.The evolution of the texture between important processes and the difference of texture along the width direction of strip were analyzed.The result shows that the difference along the width direction of strip of texture at the surface of hot rolled plate is most obvious.The texture at the surface of strip edge is primarily made of rotating cube texture,αfiber texture and weakγfiber texture.Goss texture is mainly co... 

提出了一种基于爱泼斯坦方圈族(包括标准25cm爱泼斯坦方圈、缩比的17.5cm和20cm爱泼斯坦方圈)和二级加权处理方法对爱泼斯坦测试数据,包括有效磁路长度、比损耗、励磁功率,进行处理的晶粒取向电工钢磁性能扩展模拟方法。详细地考察了励磁频率、试样剪切角度和环境温度对爱泼斯坦方圈测量结果的影响。研究结果表明,利用本文提出的爱泼斯坦方圈组合以及二级加权处理技术,可以有效地建立取向电工钢损耗模拟模型,从而更加准确地确定了取向电工钢的损耗,改善并提高了爱泼斯坦磁性能测试数据的应用价值。 The extended modeling of the magnetic properties of GO(grain oriented) electrical steel is presented in this paper which is based on a set of standard and scaled-down Epstein frames and a proposed two-level weighted processing of Epstein data, including the mean magnetic path length, specific magnetization loss and exciting power. The effects of excitation frequency, strip angle and ambient temperature on the results obtained from the Epstein frames are investigated. It is shown that using the p... 

本发明公开了一种适宜缠绕式加工的低铁损无取向硅钢及其生产方法，属于硅钢生产技术领域。本发明的无取向硅钢包括以下质量百分比的元素：Si：1.5～2.5％，Mn：0.15～1.0％、Als：0.5～1.5％，其余为Fe及不可避免的杂质。其生产工艺步骤为：铁水预处理、转炉冶炼、真空处理、连铸；加热热轧；常化处理；冷轧、退火；保温、冷却；涂覆绝缘层。本发明通过对无取向硅钢的组分及其配比，结合工艺操作进行优化，能够生产得到电磁性能及延伸率均优异的无取向硅钢，从而能够有效满足电工钢缠绕式加工及使用需求，且其制造工序流程短、成本相对较低。

本实用新型公开了一种硅钢片切割装置，包括底座和硅钢片本体，所述底座的上表面分别设置有驱动机构和切割框，驱动机构的表面设置有激光切割机构，切割框的内底壁开设有条形槽，条形槽的内壁转动连接有丝杠，丝杠的表面螺纹连接有滑动块，滑动块的上表面固定安装有定位框，定位框的内壁设置有电动推杆，电动推杆的推送端设置有定位板。该硅钢片切割装置，在对硅钢片进行切割时，能够通过小型电机的转动使定位框从切割框内移出，从而便于操作人员对硅钢片本体的放置，放置完成后，小型电机反转，使定位框带动硅钢片本体进入切割框内并与在转动辊的作用下滑动进入定位槽内，从而实现对硅钢片本体的有效定位，提高了切割的精确性。

本实用新型涉及硅钢片钢卷制造技术领域，且公开了一种用于硅钢片钢卷制造的收卷装置，解决了现有硅钢片钢卷制造过程中不便于更好的进行收卷的问题，其包括收卷辊，所述收卷辊的两侧边均对称安装有固定连接杆，固定连接杆远离收卷辊的一端安装有连接板，连接板远离固定连接杆的一侧边中部安装有连接轴，收卷辊的顶部与底部均对称连接有活动挡板，收卷辊的内部开设有安装槽，安装槽的内部安装有调节机构，且调节机构与活动挡板连接；本实用新型，便于能够确保在收卷过程中硅钢片钢卷不会发生偏移，以便于能够达到更好的收卷效果。

用于层叠铁芯的电磁钢板为一种在母材钢板(2)的表面具有绝缘被膜(3)的电磁钢板，该绝缘被膜(3)是涂布电磁钢板用涂布组合物而构成的，所述电磁钢板用涂布组合物以特定的比例配合有环氧树脂、第1固化剂及第2固化剂，该第1固化剂由包含具有烷基及烷氧基中的任意一者或两者的酚骨架的酚醛树脂构成，该第2固化剂为从酚醛甲阶树脂及苯酚酚醛清漆树脂中选择的1种以上。

本发明相对于板厚较薄的电磁钢板提供不会导致磁特性劣化的基于激光的加工方法。在对电磁钢板进行使用激光的熔断并将该电磁钢板加工成规定的形状的电磁钢板的加工方法中，使上述激光的扫描速度成为10000mm/min以上来进行上述熔断。