一种含Bi高磁感取向硅钢热轧带钢边部质量控制方法：炼钢；连铸；铸坯加热；粗轧，粗轧道次不低于4道次，各道次压下率控制在20~33%；规精轧及进行后工序。本发明通过对热轧工序的控制，能使热轧带钢边部开裂的尺寸降低至不超过5mm，且边部开裂≤2mm比率能达到95%以上，后工序切边量很少甚至无需切边即可进行冷轧，使产品成材率能比现有技术提高2~4%；且由于铸坯加热温度的降低使能耗也随之降低。

本实用新型公开了一种高磁感低铁损取向硅钢生产用切割装置，包括激光切割台，所述激光切割台上端滑动连接有一个滑动导轨，所述滑动导轨上滑动连接有一个切割主机，所述激光切割台上端且与切割主机相对应位置均匀固定连接有一组锯齿板，所述激光切割台上端且与锯齿板相对应位置活动连接有一个升降板，所述升降板上且与锯齿板相对应位置均开设有一个穿孔，所述升降板上端均匀转动连接有一组滚珠，本实用新型的有益效果是：通过螺纹杆的转动，可以使螺纹套和滑动块滑动，从而利用连接转杆的传动，可以将升降板顶起，使待切割的板材可以在滚珠上滑动，方便对板材位置的调节，并且将升降板下降后，不会影响板材的正常切割。

简述了无取向硅钢环保涂层发展背景,分析了硅钢环保涂层的特点及国内、外研究进展,提出了硅钢保涂层下一步的发展方向。 The back ground of environmental protection coating of non-oriented silicon steel was described in this paper.The characteristics and study progress in domestic and foreign of environmental protection coating of non-oriented silicon steel were analysised.The next development direction of environmental protection coating of non-oriented silicon steel was put forward. 

本发明公开了一种新能源汽车驱动电机用低铁损高强度无取向电工钢及其制造方法，所述无取向电工钢的化学成分及重量百分比包括C：0.001‑0.005％、Si：2.4‑3.0％、Mn：0.25‑0.5％、Al：0.70‑1.10％、P：≤0.02％、S：≤0.005％、0.015％≤Ce+Sn≤0.035％，余量为铁和不可避免的杂质，本发明通过加入Ce和Sn，净化钢质、微合金化提高无取向电工钢强度和磁性能，不需要添加固溶金属元素，且避免了高Si体系下的轧制困难问题，且不需要高温退火，解决了退火温度过高使晶粒异常长大，晶粒尺寸均匀性降低的问题，生产出的无取向电工钢具有较高强度的同时，还具有优良的磁性能。

本发明属于涂料技术领域，具体涉及一种用于硅钢水性无机绝缘涂料的助剂及其制备方法，用于硅钢水性无机绝缘涂料的助剂，包括以下质量份配比的材料：磷酸二氢铝溶液10‑40份、氧化镁0.1‑5份、增稠剂0.01‑5份和水1‑80份。本发明还提供了上述助剂的制备方法，通过向磷酸二氢铝溶液中加入氧化镁悬浮液，得到铝镁混合液备用，然后在室温及搅拌条件下，向铝镁混合液中加入增稠剂预溶胶得到所需助剂，利用本申请的助剂制备了无机物料，结果表明，本发明提供的助剂适用于硅钢水性无机绝缘涂料，能改善涂料的稳定性，有效提高硅钢绝缘涂层的附着力和耐腐蚀性，改善硅钢涂层的综合性能。

利用加热炉模拟、动态再结晶以及热模拟等试验方法以及扫描电镜、金相显微镜等分析观察手段对无取向硅钢边裂的成因进行了探讨。结果表明,长时间加热使得板坯边部晶粒异常长大,晶界氧化并脱碳,轧制过程中边部温度过低,动态再结晶过程变弱,使得板坯边部延伸性能变差,是导致硅钢边裂的主要原因。建议通过适当降低铸坯加热温度、缩短保温时间、提高终轧温度来改善硅钢边裂缺陷。 The behaviors of high temperature oxidation,dynamic recrystallization,and hot ductility,microstructure evolution were investigated on the non-oriented electrical steel sheets to discuss the formation of edge crack.The key causes of cracking was found to be the coarse as-cast microstructure,grain boundary oxidation and decarburization in reheating furnace,as well as reduced temperature at strip edge region during hot rolling process resulting in reduced hot ductility and lack of enough dynamic re... 

利用OM、SEM、TEM等实验方法研究了卷取工艺对一种新型含铜无取向电工钢晶粒度和析出相的影响。结果表明,该电工钢热轧带卷取后的晶粒尺寸为18～24μm,在卷取过程中,热轧带中有一定数量的第二相析出,经EDS能谱及选区电子衍射分析,这些析出相主要为AlN。随着卷取工艺的变化,该电工钢的晶粒度大小变化不明显,析出相的类型、尺寸大小不发生改变,体积分数发生一定的改变。 The effects of coiling process on grain size and precipitates of a new copper-bearing non-oriented electrical steel were investigated by OM,TEM and other experimental method.The results show that the grain size of hot-rolled bands after coiling is 18～24 μm.The second phases precipitate during coiling process.They are mainly AlN by EDS spectra and selected area electron diffraction.With the change of coiling process,the grain size of the electrical steel does not change significantly;the type and... 

【作者】 宋波； 朱一知； ...

分析了高转矩和高转速条件下高效驱动马达铁芯材料对无取向硅钢磁性能要求,讨论了无取向硅钢的高磁通密度和低铁损对电机转矩和效率的影响,介绍了国内外高磁感无取向硅钢发展情况。在生产工艺上,提高钢质纯净度,弱化夹杂物和第二相粒子对畴壁移动和再结晶晶粒长大的钉扎作用,添加微量晶界和带钢表面的偏析元素促使有利织构发展等技术可提高无取向硅钢的磁通密度。 The requirements of high efficient drive motor core materials under the conditions of high torque and high speed were analyzed.The effects of high magnetic flux density of non-oriented silicon steel on the torque and efficiency of the motor were discussed.The development of non-oriented silicon steel with high magnetic was introduced.The magnetic flux density of non-oriented silicon steel sheet can be obviously improved by some production technologies,such as purification steel,weakening the pin... 

利用光学显微镜（OM）和扫描电镜（SEM）研究了不同稀土Ce含量的50W470无取向硅钢的铸坯、热轧板和冷轧退火板的宏观和微观组织，并采用磁性能测试仪测定其磁性能。结果表明：当稀土Ce的加入量从0增加到66×10^-6（质量分数）时，铸坯的柱状晶平均宽度从3.82 mm减小到3.24 mm,等轴晶率从43.1%增加到51.3%;热轧板的平均晶粒尺寸逐渐增加，从26.2μm增加到33.3μm,再结晶百分数从24%增加到37%;退火板的平均晶粒尺寸从36.2μm增加到39.3μm;磁性能测试表明，微观组织的变化有利于50W470无取向硅钢铁损降低和磁感提高。 Macro-structure and microstructure of as-cast plate, hot rolled plate and cold rolled annealed plate of 50 W470 non-oriented silicon steel with different rare earth Ce content was studied by optical microscope（OM） and scanning electron microscopy（SEM）, and their magnetic properties were measured by magnetic property tester. The results show that when the addition amount of rare earth Ce increases from 0 to 66×10^-6（mass fraction）, the average width of columnar crystal of the as-cast pl... 

本实用新型涉及拆包装置技术领域，且公开了一种硅钢片钢卷原料拆包装置，解决了现有的硅钢片钢卷原料拆包装置不具备便捷移动功能的问题，其包括装置本体，所述装置本体的底部设有安装块，安装块顶部的两端均安装有螺纹销，安装块的两端均安装有稳定机构，安装块底部的两端均固定连接有支撑板，安装块底部的两侧均安装有连接板，两个连接板底部的两端均安装有移动轮，安装块底部的中部安装有一对气缸；使本装置能够在需要时便捷的进行移动，并且能够有效的保持连接板的稳定，同时能够有效的对插板进行固定，使置物板能够有效的保持稳定，从而能够在需要时便捷的搬运本装置，进而提高了本装置的实用性。

本发明涉及硅钢片切片领域，具体涉及一种硅钢片自动切片设备，包括下拉机构、推料机构、硅钢片输送机构、硅钢片推动机构、压片机构、导料壳、两个斜切机构、连接机构和三角切边机构，该硅钢片自动切片设备，通过移动连接机构，使得该设备能够进行两种硅钢片的切割加工，使得该设备能够满足多种硅钢片的加工，通过在移动三角切边机构和斜切机构的位置，使得该设备能够加工出各种硅钢片，且能够单一旋转加工那种硅钢片，并且一次加工出两张硅钢片，通过硅钢片输送机构带动推料机构进行同时运动，避免两个硅钢片之间叠起，当原料与推料机构的端部接触时，由于推料机构的拉动速度比硅钢片推动机构的速度快，避免原料上发生褶皱而影响切割的位置。