本发明公开了一种硅钢轧制系统，包括：轧机组，所述轧机组包括M架轧机，用于轧制硅钢，所述M架轧机的前N架轧机的轧辊为高速钢轧辊，其中，M、N为正整数；硅钢检测装置，位于所述轧机组最后一架轧机的出口处，用于对出口硅钢的参数信息进行检测；控制器，与所述硅钢检测装置通信连接，用于在所述参数信息不满足预设参数条件时，控制所述轧机组停止工作；磨床，用于在所述轧机组停止工作后，对所述N架轧机中的每架轧机进行辊形精度检测，对不满足预设辊形精度范围的轧辊进行磨削。

采用磁控溅射方法,分别在纯Fe以及低硅钢基片上沉积富Si膜,并对其进行真空扩散热处理.通过能谱分析及X射线衍射研究了Si在纯Fe与低硅钢基体中的扩散特征,运用DICTRA软件建立了扩散模型.研究发现Si在纯Fe基体中扩散时发生γ-Fe(Si)→α-Fe(Si)相转变,扩散速率受控于相界面的迁移.当沿截面Si含量梯度不足以驱动相界面正向迁移时,延长扩散时间会发生相界面回迁现象,最终趋于单一相内均匀化扩散过程.Si在低硅钢基体中的扩散符合Fick扩散第二定律. Si-rich films were deposited on pure iron and low-Si steel substrates by direct current magnetron sputtering,and then were subjected to vacuum annealing.The distribution characteristics of Si across Fe and low-Si steel substrates were studied by energy spectrum analysis(EDS) and X-ray diffraction(XRD).DICTRA software was used to simulate the diffusion models.It is found that the diffusion behavior of Si in the Fe substrate is from γ-Fe(Si) phase to α-Fe(Si) phase and the rate of diffusion is con... 

本文对某厂硅钢DR510温度、成分及过程控制水平和成品的组织、力学性能进行了研究,并在此基础上提出了工艺优化方案,有一定的借鉴和推广价值。 In this paper,the critical process and the products quality,including temperature,composition and process controlling level,the organization and mechanical properties of the finished product,were studied.On the basis of that the optimized technical plan provided,and this control technology is worth using and spreading. 

本发明公开了一种高磁感取向硅钢实验室轧机一次冷轧方法，包括：1)取样，实验室冷轧材料选取经过常化酸洗后的厚度为2.3mm的取向硅钢试样；2)制样，利用取向硅钢专用剪板机，裁剪试样尺寸为轧向600mm×横向150mm；将试样表层轻涂一层薄薄的轧制油；3)冷轧轧制规程制定，轧前厚度为2.3mm；其中：轧制总道次为6次时轧后厚度为0.35mm，轧制总道次为7次时轧后厚度为0.27mm，轧制总道次为8次时轧后厚度为0.23mm。本发明的目的是提供一种高磁感取向硅钢实验室轧机一次冷轧方法，为工业试制提供一定的技术参考，以及后续工艺研究提供了更加可靠的试样和条件。

简述了无取向硅钢环保涂层发展背景,分析了硅钢环保涂层的特点及国内、外研究进展,提出了硅钢保涂层下一步的发展方向。 The back ground of environmental protection coating of non-oriented silicon steel was described in this paper.The characteristics and study progress in domestic and foreign of environmental protection coating of non-oriented silicon steel were analysised.The next development direction of environmental protection coating of non-oriented silicon steel was put forward. 

本实用新型属于硅钢片加工技术领域，尤其是一种永磁同步电机生产用硅钢片加工装置，针对了对硅钢片在进行加工过程中的稳定性与对尘屑的防护效果较差的问题，现提出如下方案，其包括工作台，工作台的顶端侧壁固定有支撑架，支撑架的一侧侧壁固定有转动电机，转动电机的输出端连接有打磨头，工作台的一侧内壁转动连接有转动杆；本实用新型中通过转动杆的转动，使其能够带动转动齿轮与传动齿轮进行转动，实现防护组件对硅钢片在进行加工中的防护效果，实现对硅钢片在进行加工中的固定限位效果，提高其在加工过程中的稳定性与防护功能，通过移动杆的上下移动，使其能够对加工完成的硅钢片进行推动，便于工作人员对其进行拿取。

【作者】 朱传芳； 潘恒韬； ...

结合扫描电镜和大样电解研究了CSP流程W800牌号无取向电工钢表面线状缺陷中夹杂物成分及来源，采用SPSS软件回归分析了生产过程各因素对表面线状缺陷的影响。研究表明：稳态浇铸过程铸坯中大型夹杂物含量为5.39 mg/10 kg。引起无取向电工钢表面线状缺陷的大型夹杂物主要为脱氧产物、镁铝尖晶石和钢包顶渣，主要类型为Al₂O₃、MgO-Al₂O₃、CaO-Al₂O₃-MgO和CaO-Al₂O₃-SiO₂。非稳态浇铸过程钢水洁净度明显降低，热轧板表面线状缺陷比例上升。影响表面线状缺陷的主要因素为RH出站时顶渣的w（CaO）/w（Al₂O₃）、RH脱氧结束氧位及中间包最低吨位。 Combining scanning electron microscopy and large sample electrolysis, the composition and source of inclusions in the surface linear defects of W800 grade non-oriented electrical steel in the CSP process were studied. SPSS software was used to regress and analyze the main factors which affected the surface linear defects in the steelmaking process. Research shows that the content of large inclusions in the steady state casting process is 5.39 mg/10 kg. The large inclusions which cause linear def... 

本实用新型涉及风电磁钢盒技术领域，且公开了一种风电磁钢盒高精度加工模具，包括上模和下模，上模位于下模的上方，下模的前侧通过多个螺栓螺纹连接有安装板，安装板的前侧固定设有两个对称设置的固定板，两个固定板之间固定设有固定杆，固定杆的杆壁两端均通过第一转动轴承转动连接有套筒，套筒的两侧均开设有环形槽，两个环形槽的槽壁内部均设有限位机构，两个固定板相靠近一侧均开设有四个呈四角对称设置的插孔，套筒的两端均通过套环固定设有环形板，环形板的两侧均开设有滑槽，两个滑槽之间设有推动机构。本实用新型能够消除风电磁钢盒加工过程中人工将板件送至模具之间所带来的的危险。

测试了高强无取向电工钢的S-N曲线,并借助光学显微镜、扫描电子显微镜、透射电子显微镜分析了实验钢组织,疲劳断口形貌和位错结构。结果表明:室温条件下,频率为20Hz,应力比R为0.1,循环10~7周次时,实验钢的疲劳强度为360MPa,疲劳裂纹萌生于实验钢的次表面,裂纹萌生点附近有沿晶开裂现象,疲劳裂纹扩展区域有解理台阶与疲劳条纹,瞬间断裂区是韧性断裂,有大量韧窝。实验钢在循环应力作用下基体中产生了大量位错,并有驻留滑移带终止在晶界位置。 The S-N curve of a high strength non-oriented electrical steel was tested.The microstructure and fatigue fracture morphology and dislocation were analyzed by optical microscope,scanning electron microscope,transmission electron microscope.The results showed that:at room temperature and the frequency of 20 Hz and the stress ratio Rof 0.1,the fatigue strength of the experimental steel was 360 MPa when the cycle was 10~7 cycles.The fatigue crack initiation at the surface of the steel and the interg... 

研究表明,硅钢中的夹杂物对成品带钢的磁性能有显著影响。为研究冶炼过程硅钢中的夹杂物遗传变化,进而提出更有效的控制措施加以去除,本文结合典型的无取向硅钢生产炉次,采用非水溶液电解提取+扫描电镜观察方法分析冶炼过程中上述炉次典型试样的夹杂物。结果表明:转炉冶炼结束、RH精炼开始时,钢的氧化物夹杂总量最大,约为0.23%;RH精炼过程中,氧化物夹杂总量不断降低,并在脱碳结束时达到最低,约为0.02%;连铸过程中,氧化物夹杂总量仍有不断降低趋势,但夹杂物的平均尺寸变化不大。本试验条件下,中间包试样的夹杂物数量约为1.59×104个/mm3。 As we all know, the non-metallic inclusion effects magnetic properties of silicon steel sheets obviously. The article aims to study the heredity of non-metallic inclusion in non-oriented silicon steels during the steel making process, and then provides a more effective controlling measure to remove the inclusions. Based on the typical non-oriented silicon steel charges, the non-aqueous solution extraction and SEM observation were adopted to analyze the non-metallic inclusions. Results show that,... 

该电磁钢板包括母材钢板、第1绝缘被膜及第2绝缘被膜，该第1绝缘被膜被形成于所述母材钢板的第1面，并具有粘结能量，该第2绝缘被膜被形成于作为所述母材钢板的所述第1面的背面的第2面，并具有粘结能量，所述第1绝缘被膜的平均铅笔硬度为HB以上3H以下，所述第2绝缘被膜的平均铅笔硬度比所述第1绝缘被膜的平均铅笔硬度更高。