硅钢资料

采用X射线衍射仪分析无取向硅钢冷轧织构和再结晶退火织构的演化,研究了热轧组织对无取向硅钢织构以及磁性能的影响。结果表明,具有均匀、粗大晶粒组织的热轧板,冷轧形成更多的剪切带,导致成品板形成高的高斯织构组分,并提高了{100}织构强度,降低了γ纤维织构,最终导致成品磁感应强度升高,铁损下降。 The texture evolution of non-oriented silicon steel during cold-rolling and recrystallization annealing was investigated by X-ray diffractometer.The effects of hot band microstructure on the texture and magnetic properties of non-oriented silicon steel were analyzed.The results show that more shear bands appear during cold rolling due to homogeneous coarse grain in hot band.So strong{110}<001> texture after recrystallization annealing forms.At the same time,the {100} texture components inc... 

通过对取向硅钢进行脉冲磁场退火实验,发现在相同的退火时间(6.0 min)内,低于1 T的脉冲磁场可以在一定程度上提高取向硅钢的磁感(B8),而高于1 T的脉冲磁场则会使取向硅钢的磁性能急剧恶化.同时发现,脉冲直流电加热方式会使取向硅钢的磁性能恶化.研究表明,脉冲磁场退火有望成为一种调控材料微观结构的有效手段. We have carried out experiments of annealing by pulse magnetic field.The results show that a pulse magnetic field with intensity lower than 1 T can promote magnetic induction density(B8) of grain-oriented silicon steel,while the magnetic properties deteriorate sharply when intensity is higher than 1 T.It has also been found that heating by using pulse direct current can cause the magnetic properties to deteriorate,in contrast to the traditional heating using resistance furnace.Our research shows... 

本发明公开了一种控制无取向电工钢横向同板差的装置，包括热轧机、圆盘剪、冷轧机和输送辊道，圆盘剪安装在输送辊道两侧且位于热轧机和冷轧机之间，无取向电工钢在输送辊道的运输下依次经过热轧机、圆盘剪和冷轧机，设定热轧机对无取向电工钢的楔形和凸度进行控制，控制无取向电工钢的楔形在20微米内、凸度为20～45微米，冷轧机的工作辊设有倒角。冷轧机为UCM五连轧轧机，UCM五连轧轧机中1#和2#轧机工作辊的单边设有倒角，1#和2#轧机中上工作辊的操作端设有倒角，下工作辊的传动端设有倒角。倒角的深度为0.2～0.3mm，倒角在工作辊上的起始位置到工作辊端面的距离为265‑285mm。本发明还公开了一种控制无取向电工钢横向同板差的方法。

本实用新型公开了一种取向硅钢绝缘涂液用废液回收利用装置，涉及取向硅钢绝缘涂液技术领域，为解决现有取向硅钢绝缘涂液的废液在回收时没有进行多层热分解，导致回收利用率低的问题。所述下料筒的下端设置有调节筒，所述调节筒的下端设置有分流筒，所述分流筒的下端设置有出料筒，所述调节筒的内部设置有下料板，所述下料板的一端设置有转轴，所述转轴的一端设置有交流电机，所述下料板的侧表面设置有外接孔，所述下料筒的筒壁内设置有加热板，所述下料筒的内部设置有一级过滤网，所述分流筒的内部设置有隔挡板，所述隔挡板的一侧设置有二级过滤网。

本实用新型涉及硅钢轧制油反应设备技术领域，尤其是一种硅钢轧制油专用反应装置，它包括反应罐，所述反应罐的内底部焊接有导热板，所述导热板的底面安装有安装壳，所述安装壳的内部固定安装有电热盘，所述反应罐的右侧面底部固定安装有温度传感器，所述反应罐内设置有搅拌机构，本实用新型通过设有温度传感器、电热盘和控制器，能够有效控制反应罐内部的温度，使其内部的温度能够达到设定的温度值，防止因温度过高而爆炸，提高了安全性，而且，通过由搅拌电机、搅拌轴、主搅拌叶、分搅拌叶和螺旋搅拌杆组成的新型搅拌机构，该搅拌机构的搅拌覆盖率大，搅拌效果较好，能够进一步加快物料间化学反应的速率，提高生产效率。

本实用新型公开了一种高磁感低铁损取向硅钢加工用预热装置，包括加工台和预热箱，所述预热箱固定连接在加工台上端中间位置，所述加工台上端且位于预热箱内开设有一个驱动槽，所述驱动槽内转动连接有一组驱动转轴，所述驱动转轴上均固定连接有一个驱动辊，所述预热箱内滑动连接有一个升降板，所述升降板上且与驱动辊相对应位置均开设有一个安装槽，所述安装槽内均转动连接有一个加热转辊，本实用新型的有益效果是：通过驱动辊的转动，可以使金属板位于预热箱内滑动，并且通过加热转辊与金属板表面加热，实现对金属板的预热，利用加热转辊与金属板直接接触，使热传递更加迅速，从而缩短了预热时间。

以水氯镁石为原料,采用氨法沉镁-煅烧-添加剂的方法制备硅钢级氧化镁。考察了反应温度、反应pH值、陈化时间对中间体氢氧化镁纯度及转化率的影响;研究了煅烧温度和煅烧时间对氧化镁水化率的影响及添加剂的量对氧化镁悬浮性能的影响。控制实验条件为:反应温度55℃,pH值为9.5,陈化时间2h,煅烧温度1050℃,煅烧时间2h,添加剂量为0.8%,制得氧化镁的纯度为98.99%、水化率为2.92%、悬浮性能为3mm/h,达到硅钢级氧化镁的要求。 Using bischofite as raw material,the preparation of magnesium oxide with silico-steel grade was studied.The effects of reaction temperature,reaction pH value and aging time on the intermediate magnesium hydroxide purity and conversion rate were studied.Calcinations temperature,calcinations time relationship to the hydration rate of MgO and amount of additive to the suspension performance of MgO were investigated.The results indicated that the optimum technological conditions were as follows:reac... 

本发明涉及低温取向硅钢片制造领域，具体为一种重质硅钢级氧化镁的生产工艺。为提升现有取向硅钢片的表面质量，将工业氧化镁、聚乙烯醇粘结剂和水在不锈钢反应罐中水热合成氢氧化镁，经压滤、煅烧、冷却、气流粉碎、包装产物为重质硅钢级氧化镁。产品具有生产工艺独特、成本较低，能明显提高取向硅钢片的表面质量和增加磁感应强度，降低铁损，提高取向硅钢片的正品率。可针对性在取向硅钢片生产厂家推广使用。

一种适合冷连轧的高效变频压缩机用无取向硅钢，其化学成分及wt%为：C：≤0.0025%、Si：2.4~2.8%、Mn：0.35~0.65%、Al：0.5~0.8%、S：≤0.0020%、N：≤0.0025%、P：≤0.03%、Sb或Sn：0.03~0.08%；生产方法：冶炼浇注；对铸坯加热；粗轧；精轧；卷取；常化；经酸洗后冷连轧；退火；涂敷及精整。本发明产品性能既保证产品磁性能又提高生产效率、提高成材率和降低生产成本的效果，五机架连轧机只需要一次轧过即可，且连轧机相比单机架轧机减少了来回轧制的带头带尾切废量，因而可提高成材率，生产效率和成材率提高，自然降低生产成本。

本实用新型公开了一种取向电工钢的多项性能检测装置，涉及取向电工钢技术领域，为解决检测装置在对取向电工钢涂层性能检测时较为繁杂，增加了检测难度，检测的误差增加，且检测装置的性能检测较为单一，检测效果不佳的问题。所述底座的上方设置有安装架和吊梁架，所述安装架上设置有输料辊，输料辊设置有两个，两个所述输料辊之间设置有输送带，所述吊梁架的下方设置有弹性胶带，所述弹性胶带上方的两侧均设置有第三电动伸缩杆，且第三电动伸缩杆的两端分别与吊梁架和弹性胶带通过螺钉连接，所述弹性胶带的一侧设置有检测架，所述检测架上设置有激光灯、第一滤光片、接收器、第二滤光片和聚光片，所述激光灯和第一滤光片设置在弹性胶带的上方。

通过测试取向硅钢不同工艺条件下的碳含量,探讨了CGO取向硅钢碳含量控制的最优处理条件,研究了脱碳温度和脱碳时间对相同初始碳含量取向硅钢的脱碳效果的影响。结果表明,在气氛为(15%~20%)H2+(75%~80%)N2,炉压差为10~20 Pa的条件下,CGO取向硅钢合适的脱碳温度为1 073 K~1 123 K,脱碳时间为10~20 min。在该处理条件下,能取得较好的脱碳效果。 By means of testing carbon content of oriented silicon steel below the distinct technical conditions,inquires the excellent handle terms of carbon content controlling for CGO oriented silicon steel,studies effects of decarburization annealing temperature and decarburization annealing time to the oriented silicon steel decarburization efficiency in same initial carbon content.The results show that,under the condition of atmosphere(15% ~ 20%) H2+(75% ~ 80%)N2 and furnace pressure difference 10 ~ 2... 

本实用新型公开了一种硅钢片制作用防止硅胶泄露结构，包括运行组件与固定密封组件，所述运行组件的内侧壁设有固定密封组件，所述运行组件包括板体、第一凹槽、壳体、硅钢片、支撑板、连接块、密封圈、防护板和通孔，所述板体的内侧壁开设有第一凹槽，所述第一凹槽的内部设有壳体，所述壳体的内侧壁设有硅钢片，所述硅钢片的两侧相互对称焊接有四个连接块，四个所述连接块相斥一侧均贴合于第一凹槽的内侧壁，本实用新型首先通过硅钢片两侧密封圈保障密封效果，设置的橡胶管起到二次密封防护作用，并借助其内部的弹簧及U型板实现防偏移的效果，最后一方面可以在壳体相邻组件内侧加胶并且提高其内部硅钢片的厚度，以此实现多重密封防漏。