采用电解法和扫描电镜研究了300 t转炉-RH精炼钙处理对无取向硅钢板（%:≤0.005C、1.2～2.2Si、0.2～0.6Mn、≤0.20P、≤0.005S、0.2～0.6Al、0～0.01Ca）中夹杂物的影响。结果表明,钢中Al含量为0.25%和0.35%时,钢中溶解氧均小于1×10^-4%,钙处理后都会产生CaS夹杂物,尤其是含0.35%Al的钢水;钙处理可以有效减少钢中的夹杂物数量,尤其是0.5μm以下的微细夹杂物数量;钙处理后夹杂物的种类以AlN、CaS为主,同时还含有少量的氧化物夹杂物以及AlN-CaS复合夹杂物,尺寸主要为1.5～5.0μm。 The effect of 300 t converter-RH refining calcium treatment on inclusions in non-oriented silicon steel sheet （%:≤0.005C,1.2～2.2Si,0.2～0.6Mn,≤0.20P,≤0.005S,0.2～0.6A1,0～0.01Ca） has been studied by electrolysis and scanning electron microscope.Results show that with 0.25%and 0.35%Al content in steel,all the dissolved oxygen in liquid is less than 1×10^-4%,and the CaS inclusions are produced after calcium treatment,especial for the liquid containing 0.35%Al;the amount of inclusions in ste... 

采用RH精炼添加钙合金方式对硅钢进行钙处理,结果表明,钙合金添加量为0.67、1.00和1.67 kg/t钢时,钢中Ca含量分别为0、2×10-6和4×10-(6质量分数);随着钙合金添加量的增加,钢中夹杂物粒度逐渐由0～2μm向2～4μm、4～6μm偏移;不同钙处理条件下,钢中均存在粒径小于1μm和粒径为1～5μm的MnS、CuxS夹杂物,后者或单独存在,或与AlN、CaS夹杂复合;钢中粒径为5～10μm的夹杂物基本以Ca的氧化物和硫化物为主。与未经钙处理的炉次相比,钙合金添加量为0.67、1.00和1.67 kg/t钢时,粒径小于1.0μm的夹杂物减少幅度分别为68.06%、87.50%和94.94%。钙合金添加量为1.67 kg/t钢时,可以去除钢中绝大部分的微细夹杂物。 In order to improve the properties of final silicon steels,the calcium treatment was adopted by adding Ca alloys into the liquid steel during the RH refining process.Results show that when the addition of Ca alloys is 0.67 kg/t,1.00 kg/t and 1.67 kg/t,the corresponding Ca content in silicon steels is 0,2 × 10-6 and 4 × 10-6 respectively.With the increase of Ca alloy addition,the particle sizes of inclusions in steels become 2～4 μm and 4～6 μm,from 0～2 μm.Under different calcium treatments,there e... 

结合工业化生产的无取向硅钢,探讨了氧硫交互作用对钢中夹杂物生成的影响。借助非水溶液电解+扫描电镜法,研究了不同O、S含量下钢中夹杂物的变化规律。结果表明,本实验条件下,提高O含量、降低S含量,会劣化热轧组织再结晶效果。在劣化效果上,O的作用大于S;低Si、无Al硅钢中,应尽可能降低O含量、适当提高S含量,以粗化钢中微细夹杂物,减少尺寸小于1.0μm的夹杂物的数量;O、S含量与钢中夹杂物数量不具有关联性。生产过程中,不仅要严格控制O、S含量,还要严格控制生产工艺,以免生成较多的有害夹杂物。 Based on the industrial production of non-oriented silicon steel,the effects of interaction between oxygen and sulfur on the formation of inclusions were discussed.The change of non-metallic inclusions in steel sheets was investigated by means of electrolysis with non-aqueous solution under different oxygen and sulfur content.Results show that the recrystallization microstructure of hot rolled sheets will be deteriorated with the increase of oxygen content and the decrease of sulfur content.The ... 

针对宝钢硅钢常化退火过程中产生的退火炉辊印缺陷问题,通过实际生产的大数据与产品质量问题相结合,将数据挖掘、数据分析方法应用到实际,一定程度上解决了现场实际生产中的痛点,为现场生产提供决策支撑,避免了以前通过人工识别判定存在疏漏和无法定量判断的问题,形成了一套具有鲁棒性和可操作性的钢铁生产过程数据分析方法。通过智慧决策系统平台获取实际生产和表检仪数据,基于Pearson相关系数算法进行变量挑选和特征工程,并应用随机森林算法对数据建立分类预测模型,实现了质量问题的溯源和监控,通过数据量化预测了炉辊印缺陷是否可通过轧制消除的质量问题,识别准确率达到96.43%。 In views of the normalizing annealing furnace roll marks problem occurred in the process of normalizing annealing of silicon steel in Baosteel,by combining big data from actual production with product quality problems,data mining and data analysis methods were applied to actual production to solve the pain points and provide decision support,a robust and practical data analysis method for the steel production process has been developed,which avoided the previous problems of omission and non-quan... 

一种生产取向硅钢的氧化镁涂层烘烤质量控制方法，通过对带钢的实时温度测量建立对烘烤输出功率的实时反馈调节，据此形成基于烘烤输出功率的烘烤质量的实时控制。本发明的一种生产取向硅钢的氧化镁涂层烘烤质量控制方法，通过在烘烤炉出口的带钢上方增加一套可在带钢横向方向移动的在线板温计，基于在线板温检测值对烘烤炉状态进行监控，并建立烘烤输出功率控制系统实时调整，使得氧化镁涂层烘烤质量均匀，提高取向硅钢产品质量稳定性，节省能源消耗。

对两种硅钢水溶性极厚绝缘涂层进行了不同温度的热老化实验。通过TG-DTA,GDS,FT-IR,SEM和光泽度仪等测试方法对老化的涂层进行分析表征,提出了评估硅钢水溶性极厚绝缘涂层热老化性能的合理温度区间,探讨了涂层热老化行为,并分析了两种涂层热老化性能的差异。结果表明,涂层附着性随着老化时间的延长逐渐下降。FT-IR表征结果显示,热老化过程中,涂料交联形成的化学键未发生断裂,交联剂氨基树脂的三嗪环被破坏是聚合物三维网络结构坍塌的主要原因。 Thermal aging expriments at different temperature were carried out on two types of water-soluble and extra-thick insulation coatings for non-oriented silicon steel,and a series of test methods such as glossmeters,TG-DTA,FT-IR,GDS,SEM were applied in analysis.For evaluating the thermal aging effect of this kind of insulation coating,the proper temperature range was proposed.The difference of aging performance between two coatings was been investigated and the related behaviors were been discussed... 

结合工业化生产的50A1300牌号无取向硅钢,分析了化学成分、RH精炼脱氧方式、板坯装炉温度以及热轧平整工艺等对磁性能的影响,探讨成品钢磁性能的改善。结果表明,采取改善后,50A1300牌号无取向硅钢的磁性能得到明显改善。2012年,该钢种平均铁损、磁感应强度分别达到5.26 W/kg、1.762 T,能够较好地满足用户市场需求及同行对标需要。 Based on the industrial manufacture of 50A1300 grade non-oriented silicon steel sheets,effects of chemical composition,deoxidization method in RH vacuum refining,charging temperature of steel slabs,hot rolling and flattening progress on magnetic properties are analyzed.The optimization methods of magnetic properties of steels are discussed. Results show that the magnetic properties are obviously improved by the adopted measures above. In 2012,the average core loss and the magnetic induction of 5... 

本发明公开了一种无瓦楞状缺陷的高磁感低铁损无取向电工钢板，其各化学元素质量百分含量为：0＜C≤0.0035％、Si：1.2～2.8％、Mn：0.2～1.0％、P：0.04～0.15％、Sn+Sb：0.02～0.2％，余量为Fe和其他不可避免的杂质。此外，本发明还公开了上述高磁感低铁损无取向电工钢板的制造方法，其包括步骤：(1)冶炼和连铸，其中在该步骤不采用电磁搅拌；(2)热轧，其包括：粗轧、精轧、卷取和均热；其中在粗轧步骤采用2～6道次进行轧制，且粗轧单道次压下率控制在20％～40％之间；(3)上述热轧步骤后不进行常化步骤而直接进行冷轧；(4)连续退火。本发明所述的无瓦楞状缺陷的高磁感低铁损无取向电工钢板在保证较低生产成本的同时，还具有高磁感和低铁损的特性。

本发明公开了一种电化学评价取向硅钢氧化层的装置及方法，包括电解池、设于电解池一侧的磁铁组、设于电解池上的饱和甘汞电极和铂电极以及与电解池连接的电化学工作站；磁铁组包括固定在电解池上的固定磁铁和与固定磁铁磁性连接的移动磁铁，移动磁铁设于电解池侧面的出口上；参比电极设于磁铁组与辅助电极之间；参比电极和辅助电极与电化学工作站连接。本发明的评价方法通过电化学测量取向硅钢试样的电位‑时间曲线，计算出取向硅钢氧化层各分层的溶解电量，实现了对取向硅钢氧化层各分层的快速、准确测定，可以区分出Mg2SiO4玻璃膜底层、SiN层、SiO2层、FeO及铁橄榄石层等分层性能，为取向硅钢生产工艺参数的控制提供指导。

本发明公开了一种高磁感取向硅钢，其含有Fe及不可避免的杂质元素，其还含有质量百分含量如下的下述各化学元素：C：0.02～0.08％，Si：2.0～4.5％，Mn：0.02～0.30％，S≤0.0050％，Als：0.01～0.04％，N：0.002～0.01％，Nb：0.0050～0.0600％；以及P：0.01～0.1％，Sn：0.01～0.30％，Cu：0.01～0.50％的至少其中一种。此外，本发明还公开了上述高磁感取向硅钢的制造方法，其包括步骤：(1)制得板坯；(2)板坯加热；(3)热轧，其包括：粗轧、在热卷箱内卷取保温，以及精轧；其中粗轧结束温度高于970℃；卷取温度为800～1050℃，卷取时间为30～200s；精轧开始温度低于1050℃；(4)冷轧；(5)脱碳退火；(6)渗氮；(7)涂覆退火隔离剂；(8)高温退火；(9)涂覆绝缘涂层和激光刻痕。

无取向硅钢中夹杂物的存在会抑止晶粒生长,使基体的均匀连续性中断,其在钢中的形态、含量及分布情况都不同程度影响着硅钢的性能,尤其是对磁性能起关键的作用。因此,全尺度分布考察夹杂物对无取向硅钢夹杂物的研究极为重要。本实验确定了适用于不同牌号无取向硅钢夹杂物全尺度分布的分析方法:样品制备—小样电解—过滤喷金—根据不同牌号的要求选择合适的放大倍率扫描观测—夹杂物颗粒的分类统计。通过统计的结果,结合电解的失重量可以得到不同尺度的体积分布数据。实验分析了不同牌号和工艺无取向硅钢夹杂物的种类、形貌、大小和尺度分布,并初步考查了夹杂物与磁性能的关系,对无取向硅钢的工艺研究具有一定参考价值。 Inclusions in non-oriented silica steel could inhibit the growth of grain and cause discontinuity of micro-structure.The configuration,content and size distribution of inclusion have different effects on the performance of silica steel,especially significant on the magnetic property.Therefore,it is very useful to completely characterize inclusions with full size distribution in silica steel.In our research,full size analysis method for inclusion in silica steel had been established as follows: s... 

本发明公开了一种硅钢氧化镁废水回用处理与污泥资源化工艺，包括：预过滤：氧化镁废水进入过滤容器，过滤得到的水，返回调节池中，直至预过滤澄清；过滤过程：氧化镁废水在预过滤阶段逐渐澄清后进入过滤程序，产生的过滤水满足要求后，自流入产水箱；滤饼干燥：停止过滤后，将过滤容器中的水排空至调节池，之后按照与过滤相同的方向通压缩空气，通过压缩使滤饼干燥；反吹排泥：滤饼干燥完成后，通反向的压缩空气，之后进入下一个过滤周期；经过处理后，过滤阶段产生的合格水循环利用；滤饼干燥后进一步进行资源化处理。本发明实现了废水回用；产生的沉淀污泥经处理后可分别作为钛白粉的生产原料和土壤改良剂，具有良好的社会效益和环境效益。