硅钢资料

采用RH精炼添加钙合金方式对硅钢进行钙处理,结果表明,钙合金添加量为0.67、1.00和1.67 kg/t钢时,钢中Ca含量分别为0、2×10-6和4×10-(6质量分数);随着钙合金添加量的增加,钢中夹杂物粒度逐渐由0～2μm向2～4μm、4～6μm偏移;不同钙处理条件下,钢中均存在粒径小于1μm和粒径为1～5μm的MnS、CuxS夹杂物,后者或单独存在,或与AlN、CaS夹杂复合;钢中粒径为5～10μm的夹杂物基本以Ca的氧化物和硫化物为主。与未经钙处理的炉次相比,钙合金添加量为0.67、1.00和1.67 kg/t钢时,粒径小于1.0μm的夹杂物减少幅度分别为68.06%、87.50%和94.94%。钙合金添加量为1.67 kg/t钢时,可以去除钢中绝大部分的微细夹杂物。 In order to improve the properties of final silicon steels,the calcium treatment was adopted by adding Ca alloys into the liquid steel during the RH refining process.Results show that when the addition of Ca alloys is 0.67 kg/t,1.00 kg/t and 1.67 kg/t,the corresponding Ca content in silicon steels is 0,2 × 10-6 and 4 × 10-6 respectively.With the increase of Ca alloy addition,the particle sizes of inclusions in steels become 2～4 μm and 4～6 μm,from 0～2 μm.Under different calcium treatments,there e... 

本发明公开了一种耐热刻痕型取向硅钢涂层用涂液，其溶剂为水，其含有：磷酸盐、胶态二氧化硅、铬酐和乙醇。本发明还公开了一种耐热刻痕型取向硅钢板，其包括基板，所述基板表面具有采用上述的耐热刻痕型取向硅钢涂层用涂液涂覆在基板上而形成的涂层。相应地，本发明还公开了上述取向硅钢板的制造方法，其包括步骤：在基板表面涂覆所述涂液，基板的刻痕沟槽涂液填充率＞95％；进行烧结处理，其中烧结处理中的板温为780‑900℃。本发明的耐热刻痕型取向硅钢涂层用涂液具有良好的流动性，其可以涂覆于耐热刻痕取向硅钢基板的表面中，涂覆后，能有效填充基板的刻痕沟槽，且可以在其表面形成涂层，保证耐热刻痕取向硅钢在具有低铁损的同时具备更高的安全性。

本发明一种铝镇静含硅钢的脱氧方法，包括转炉冶炼、LF炉精炼工序，转炉工序：转炉出钢过程采用含硅脱氧剂进行脱氧，出钢完毕后，向钢液表面加入顶渣改质剂，数量为400±25kg/炉，所述顶渣改质剂的成分及其质量百分含量为：Al2O3：9％±1％，CaO：27.5％±1.5％，SiO2：3％±1％，Al：50％±2％，CaF2：7％±1％。精炼工序：采用铝脱氧剂进行脱氧、造渣。本发明通过两步脱氧工艺，大幅降低脱氧成本同时提高钢水质量，由于硅脱氧相对于铝脱氧在钢水中形成的夹杂物更容易上浮，所以也提高了钢水纯净度，提高钢水质量。

本发明公开了一种硅钢产品生产方案的智能设计评估方法，包括以下步骤：1、采集数据，并集成用户数据、实验室研发数据和大生产数据；2、构建用户数据主题、实验室研发数据主题和大生产数据主题；3、输入硅钢产品的种类、规格和性能需求的需求信息，并根据需求信息生成若干个硅钢产品的生产方案，生产方案包括优化产品的生产方案和新产品的生产方案；4、多维度综合评估步骤3中生成的每个硅钢产品的生产方案，得到硅钢产品生产方案的绿色设计指数，并根据绿色设计指数推荐生产方案。本发明基于产品设计需求，融合实验研发数据和大生产数据，生成并评估产品设计方案模型，缩短研发周期，提高研发效率。

研究表明,硅钢中的夹杂物对成品带钢的磁性能有显著影响。为研究冶炼过程硅钢中的夹杂物遗传变化,进而提出更有效的控制措施加以去除,本文结合典型的无取向硅钢生产炉次,采用非水溶液电解提取+扫描电镜观察方法分析冶炼过程中上述炉次典型试样的夹杂物。结果表明:转炉冶炼结束、RH精炼开始时,钢的氧化物夹杂总量最大,约为0.23%;RH精炼过程中,氧化物夹杂总量不断降低,并在脱碳结束时达到最低,约为0.02%;连铸过程中,氧化物夹杂总量仍有不断降低趋势,但夹杂物的平均尺寸变化不大。本试验条件下,中间包试样的夹杂物数量约为1.59×104个/mm3。 As we all know, the non-metallic inclusion effects magnetic properties of silicon steel sheets obviously. The article aims to study the heredity of non-metallic inclusion in non-oriented silicon steels during the steel making process, and then provides a more effective controlling measure to remove the inclusions. Based on the typical non-oriented silicon steel charges, the non-aqueous solution extraction and SEM observation were adopted to analyze the non-metallic inclusions. Results show that,... 

一种取向硅钢极薄冷轧板钢带的焊接系统及方法，于该系统内设有焊轮及与焊轮电连接的焊接控制器；所述焊轮由前后呈直线布设的主焊轮、副焊轮构成；所述焊接控制器由分别与主焊轮电连接的第一焊接控制器、与副焊轮电连接的第二焊接控制器构成。所述焊接基于单排焊，仅使用一次焊接行程，通过设置的第一次焊接与第二次碾压焊接依次作业完成。本发明的一种取向硅钢极薄冷轧板钢带的焊接系统及方法，针对取向硅钢极薄钢带冷轧板焊接的问题，对传统电阻焊焊机拥有的碾压轮改造及建立的相应焊接工艺。平衡了热量积累与质量保证两者，解决了取向硅钢极薄钢带冷轧板焊接容易发生虚焊、爆焊和焊接时间长等问题。同时和传统电阻焊焊机相比焊接工艺窗口更大，焊接效率更高。

本发明公开了一种硅钢环形炉内罩的内圆直径自动检测装置及方法，该内圆直径自动检测装置包括设置在检测点地面上的水平工作台，设置在所述水平工作台上的水平调节机构，设置在所述水平工作台上的扫描机构，以及与所述扫描机构通信互联的检测处理机构。该内圆直径自动检测装置是非接触式设备，不受内罩温度的限制，使用方便灵活，设备可靠性好，安全性高，对环境无污染，不仅能够有效节约校圆机的使用频次，而且大大增强了炉子的安全可靠性。

利用DSC、XRD,结合热焓分析对硅钢级氧化镁和二氧化硅的固相反应行为进行了研究。比较了不同二氧化硅原料及混合方法对硅钢级氧化镁反应性的影响,找到了一种更为有效的硅钢级氧化镁反应性的评估方法,克服了传统柠檬酸活性法在比较不同厂家生产的氧化镁的反应性上的局限性。进一步研究了Na₂B₄O₇添加剂、TiO₂添加剂对氧化镁和二氧化硅反应行为的影响,结果表明,Na₂B₄O₇添加剂含量的增加对反应有利,而TiO₂添加剂对反应有阻碍作用。 The solid-state reaction behavior between silicon-steel grade MgO and SiO₂ was investigated by DSC and XRD combined with enthalpimetric analysis.The influence of different kinds of SiO₂ and different preparation methods were studied and a specifical measurement that is more reliable was proposed to evaluate reactivity of silicon steel grade MgO.It overcomes the limitation of the traditional citric acid activity（CAA） method,which can not be used to evaluate the reactivity of... 

结合工业化生产的无取向硅钢,进行了RH精炼喂CaSi线去除钢中的非金属夹杂物试验研究。针对不同的钙处理条件,分析了CaS夹杂生成热力学,观察了夹杂物的形貌和尺寸分布,确定了夹杂物的类型、数量,探讨了钙处理后钢中夹杂物的变化规律。结果表明,本试验条件下,钙处理可以有效抑制MnS、AlN夹杂物的生成,有效促进钢中微细夹杂物的聚合、上浮、去除,钢质纯净度明显提高。经过合适的钙处理后,钢中的夹杂物以独立存在的CaO为主,同时有少量含CaO、SiO2、MgO的复合夹杂,没有发现CaS夹杂存在。这部分夹杂物的尺寸集中分布在2～20μm,数量约为1.8×105个/mm3。 Experimental study on removal of non-metallic inclusions in non-oriented silicon steel obtained from industrial production by CaSi wire feeding during RH refining process was carried out.The thermodynamics of CaS inclusion formation was analyzed,the morphology and the size distribution of inclusions were observed,and the numbers and types of inclusions were also determined for the steel specimens treated under different calcium treatment conditions.Furthermore,the variation of inclusion characte... 

本发明公开了一种取向硅钢产品的在线性能判级与精确分切装置和方法，使得同一个分卷上的性能分布均匀，避免分卷出现性能废品或多个性能等级的情况，提高分卷性能稳定性。提供的一种取向硅钢产品的在线性能判级与精准分切方法包括生产数据采集、铁损曲线自学习、数据存储、性能在线判级、缺陷数据采集、缺陷判级、智能分切等模块，依据修正后的磁性能全长数据，得到产品的性能判级结果，结合表面缺陷判级结果，综合确定分切位置，制定最佳分切方案。本发明可以实现取向硅钢生产过程中的性能在线判级和精准分切，得到性能均匀、表面质量好的分卷，减少分卷性能不稳定带来的损失。

试验的铸态取向硅钢（/%:0.044⁰.056C,3.12³.32Si,0.08⁰.11Mn,0.002⁰.008S,0.002 9⁰.029 1Als,0.006 2⁰.010 9N）由30 kg高频真空感应炉熔炼。通过场发射扫描电子显微镜/能谱仪（FE-SEM/EDS）研究结果表明,0.002 9%Als钢中氧化物主要为SiO₂,存在片状、棒状及近似球状的独立MnS,未发现含铝的氧化物或氮化物;0.0090%Als钢中出现以Al₂O₃为主的复合氧化夹杂物,存在MnS与AlN的复合析出物。钢中Als增加,复合析出物多呈簇状发展。氧化物容易成为MnS-AlN复合析出的核心,钢中Als含量越低,夹杂物中的MnS含量越高;作为核心的氧化物夹杂的尺寸越小,形成的复合夹杂物的形状越规则,尺寸也越小。热力学计算结果表明,钢中Als含量主要影响了钢中氧化物夹杂的组成和AlN的析出温度及析出量。 Test as-cast grain-oriented silicon steel（/%:0.044 ⁰.056C,3.12 3.32Si,0.08 0.11Mn,0.002⁰.008S,0.002 9⁰.029 1 Als,0.006 2⁰.010 9N） is melted by a 30 kg high frequency vacuum induction furnace.The research results by using field emission-scanning electron microscope/energy dispersive spectrometer（FE-SEM/EDS） show that in 0.002 9%Als steel the main oxide is SiO₂,and there is independent laminable,rod-like and approximate ... 

磁性能指标是硅钢产品最关键的质量指标之一，但是目前磁性能判定100%依赖于样品的离线实验室检测结果，生产线配置的在线检测仪的测量结果由于精度问题，不宜直接用于成品牌号判级。本文在现有硅钢产品质量管控体系基础上，利用大数据技术对生产数据进行分析与建模，构建不同磁性能指标在线检测模型，并在现有信息系统上完成模型库的集成部署，实现硅钢产品全长、多指标磁性能结果的拟合数据输出，支撑取样优化、精准分切、辅助综合判定等功能应用，进一步优化硅钢产品质量管控体系。 The magnetic performance index of silicon steel products is one of the most critical quality indexes.However,at present,100%determination of magnetic performance depends on the offline laboratory test results of samples,and the measurement results of the online detector configured in the production line cannot be applied in practice due to the accuracy problem.Based on the existing quality control system of silicon steel products,big data technology was used to analyze and model the production d...