研究了热处理工艺(退火温度、保温时间、冷却方式)对含Mn的Fe-6.5wt%Si高硅钢热轧带的显微组织及硬度的影响。结果表明,退火温度对Fe-6.5wt%Si合金的组织和显微硬度均有较大影响,随退火温度升高,平均晶粒尺寸和显微硬度均明显增大。小于1 h退火时,晶粒长大缓慢,而长时间(>1 h)退火时,一些次表层晶粒将发生异常长大。水冷组织比空冷组织略细小,但水冷显著降低了显微硬度。Mn含量提高能抑制850℃退火时晶粒的长大,并且促进退火后高硅钢的软化。 The influences of heat treatment process(annealing temperature,heating time,cooling methods) on the microstructure and microhardness of Fe-6.5wt%Si high silicon steel containing manganese for hot rolled strip were studied.The results show that the annealing temperature has a great effect on the microstructure and microhardness of Fe-6.5wt%Si alloy,and as the annealing temperature increases,the average grain sizes and microhardness will significantly increase.When annealing time for less than 1 h... 

本发明公开了一种低磁致伸缩取向硅钢的制造方法，其包括步骤：(1)在硅钢基板上进行单面激光刻痕，其中进行激光刻痕的表面为第一表面，第一表面的背向一侧表面为第二表面；(2)基于激光刻痕的功率确定第一表面和第二表面的挠度差；(3)基于挠度差获得第一表面和第二表面所涂覆的绝缘涂层的涂覆量差；(4)基于涂覆量差，在第一表面和第二表面上涂覆绝缘涂层，其中第二表面的绝缘涂层涂覆量大于第一表面的绝缘涂层涂覆量。相应地，本发明还公开了采用上述制造方法所制得的低磁致伸缩取向硅钢，其第一表面和第二表面的磁致伸缩偏差≤2db(A)，并且所述低磁致伸缩取向硅钢的平均磁致伸缩≤55db(A)。

无取向硅钢中夹杂物的存在会抑止晶粒生长,使基体的均匀连续性中断,其在钢中的形态、含量及分布情况都不同程度影响着硅钢的性能,尤其是对磁性能起关键的作用。因此,全尺度分布考察夹杂物对无取向硅钢夹杂物的研究极为重要。本实验确定了适用于不同牌号无取向硅钢夹杂物全尺度分布的分析方法:样品制备—小样电解—过滤喷金—根据不同牌号的要求选择合适的放大倍率扫描观测—夹杂物颗粒的分类统计。通过统计的结果,结合电解的失重量可以得到不同尺度的体积分布数据。实验分析了不同牌号和工艺无取向硅钢夹杂物的种类、形貌、大小和尺度分布,并初步考查了夹杂物与磁性能的关系,对无取向硅钢的工艺研究具有一定参考价值。 Inclusions in non-oriented silica steel could inhibit the growth of grain and cause discontinuity of micro-structure.The configuration,content and size distribution of inclusion have different effects on the performance of silica steel,especially significant on the magnetic property.Therefore,it is very useful to completely characterize inclusions with full size distribution in silica steel.In our research,full size analysis method for inclusion in silica steel had been established as follows: s... 

为了弄清楚高硫硅钢中的硫化物析出行为及其对钢的微观组织和电磁性能的影响，以便为工业化生产制定更为合理的硫含量控制标准和采取更为有效措施减轻炼钢生产的硫含量控制压力，结合0.25% Si 无取向硅钢 ，采用非水溶液电解提取 + 扫描电镜/透射电镜观察相结合的方法 ，研究了0.006 8%、0.010 2%、0.025 5% 和 0.035 3% 硫含量条件下，钢中的硫化物夹杂物组成和存在形式及其形貌、种类、尺寸、数量变化，以及相应的热轧、成品试样的微观组织和电磁性能变化。结果表明，随着钢中硫含量的增加，钢中的硫化物逐渐由 MnS→MnS+Cu₂S→Cu₂S转变，数量逐渐增多，尺寸向高低两个方向发展。相应地，导致热轧再结晶组织劣化和抑制了成品晶粒尺寸长大。随着钢中硫含量的增加，钢的磁感、铁损劣化程度逐渐增大。钢中的硫含量平均每增加 0.01%，涡流损耗、磁滞损耗分别劣化0.24 W/kg 和 0.41 W/kg，而磁感会劣化 0.009 T。但是 ，在硫含量为 0.010 2% 时 ，铁损可以低于 6.0W/kg，而在硫含量为 0.025 5% ... In order to find out the precipitation behavior of sulfide inclusions and the corresponding changes of microstructure and electromagnetic properties of high sulfur silicon steel sheets, so that to design more suitable sulfur concentration controlling limit for industrial manufacture and to release the steel-making difficulty effectively, Based on the change of given sulfur concentration 0.006 8%, 0.010 2%0.025 3% and 0.035 3%, the type and composition, the size and number, and the size distribut... 

【机构】 宝山钢铁股份有限公司规划与科技部； ...

对碳-锰-硅钢进行不同配分温度的Q&P(Quenching and Partitioning)处理,测试了热处理后不同钢的力学性能和残余奥氏体含量,并用扫描电子显微镜和透射电镜观察其显微组织,分析了配分温度对显微组织和力学性能的影响。结果表明:试验钢显微组织基本由低碳板条状马氏体、块状铁素体和条状残余奥氏体组成;随配分温度的升高,试验钢的抗拉强度呈下降趋势,伸长率与奥氏体含量的变化趋势相同,但变化规律不确定;提高锰含量能稳定残余奥氏体,从而提高试验钢的伸长率,并使伸长率对配分温度不敏感。 The C-Mn-Si steel was quenched and partitioned at different partitioning temperatures,the mechanical properties and residual austenite contents were investigated,the microstructure was observed by SEM and TEM,and the effect of partitioning temperature on microstructure and mechanical properties was analyzed.The results show that the microstructure of the tested steel consisted of lath martensite with low carbon,nubby ferrite and banded residual austenite.The tensile strength of the tested steel ... 

本发明公开了一种利用取向硅钢氧化镁废弃物生产镁质球团的方法，采用取向硅钢生产过程中的废氧化镁污泥、废氧化镁粉等氧化镁废弃物，以及粗粒铁矿粉、镜像赤铁矿、磁铁精矿、膨润土和石灰石粉为原料，依次经预处理、配料、造球后，再在链箅机‑回转窑‑环冷机上进行干燥预热、焙烧和冷却，得到镁质球团。本发明利用氧化镁废弃物制备镁质球团，既有利于减少氧化镁废弃物带来的环保压力及其外运时产生的处置费用，也能显著降低镁质球团的制造成本，综合利用了钢铁厂的现有资源，生产出环境友好、低成本的镁质球团，为高炉提供优质原料，最终降低炼铁过程的污染物排放，减少环境污染。

本发明公开一种表面状态良好的无取向电工钢板，其含有Fe和不可避免的杂质，其还含有质量百分含量如下的下述各化学元素：0＜C≤0.005％，Si：1.0～2.0％，Mn：0.2～1.0％，Al：0.2～1.0％，Ca：0.0003～0.010％，Sb：0.005～0.2％，其中Si+Al：1.4～2.6％。此外，本发明还公开了一种上述的无取向电工钢板的制造方法，其包括步骤：(1)冶炼；(2)铸造：控制连铸坯在连铸机出口位置处的表面温度≥780℃，以使得连铸坯在其厚度方向上与宽度方向上的晶粒尺寸之比为2.5～6.0；(3)热轧：在热轧粗轧结束之后，控制中间坯头尾温度之差≤25℃；(4)冷轧；(5)连续退火。该表面状态良好的无取向电工钢板无瓦楞缺陷，其具有较低的铁损以及优良的磁感，其具有十分良好的推广前景和应用价值。

本发明公开了一种硅钢环形炉内罩的内圆直径自动检测装置及方法，该内圆直径自动检测装置包括设置在检测点地面上的水平工作台，设置在所述水平工作台上的水平调节机构，设置在所述水平工作台上的扫描机构，以及与所述扫描机构通信互联的检测处理机构。该内圆直径自动检测装置是非接触式设备，不受内罩温度的限制，使用方便灵活，设备可靠性好，安全性高，对环境无污染，不仅能够有效节约校圆机的使用频次，而且大大增强了炉子的安全可靠性。

本发明公开了一种耐热刻痕型取向硅钢涂层用涂液，其溶剂为水，其含有：磷酸盐、胶态二氧化硅、铬酐和乙醇。本发明还公开了一种耐热刻痕型取向硅钢板，其包括基板，所述基板表面具有采用上述的耐热刻痕型取向硅钢涂层用涂液涂覆在基板上而形成的涂层。相应地，本发明还公开了上述取向硅钢板的制造方法，其包括步骤：在基板表面涂覆所述涂液，基板的刻痕沟槽涂液填充率＞95％；进行烧结处理，其中烧结处理中的板温为780‑900℃。本发明的耐热刻痕型取向硅钢涂层用涂液具有良好的流动性，其可以涂覆于耐热刻痕取向硅钢基板的表面中，涂覆后，能有效填充基板的刻痕沟槽，且可以在其表面形成涂层，保证耐热刻痕取向硅钢在具有低铁损的同时具备更高的安全性。

一种适用于取向电工钢产线的一体化生产计划排程方法，基于L4，建立基于如下步骤的整条取向电工钢产线的自动生产计划排程，S1：以排程所需的必要数据为基础，按核心工序为排程起点，分别依次递进式完成前工序、后工序的排程，形成初始计划排程；S2：对初始计划排程建立基于设定的评价因子构成的综合评估，形成由综合评估结果构成的综合评估结果数据集；S3：对综合评估结果数据集建立优化算法运算，根据运算结果确定生产计划排程。本发明的一种适用于取向电工钢产线的一体化生产计划排程方法，可实现较大程度的自动化，提高生产计划编制效率，增强操作人员对生产计划的整体情况掌握，并可根据设备状态及计划执行情况自动对计划作出快速响应。

本发明公开了一种电化学评价取向硅钢氧化层的装置及方法，包括电解池、设于电解池一侧的磁铁组、设于电解池上的饱和甘汞电极和铂电极以及与电解池连接的电化学工作站；磁铁组包括固定在电解池上的固定磁铁和与固定磁铁磁性连接的移动磁铁，移动磁铁设于电解池侧面的出口上；参比电极设于磁铁组与辅助电极之间；参比电极和辅助电极与电化学工作站连接。本发明的评价方法通过电化学测量取向硅钢试样的电位‑时间曲线，计算出取向硅钢氧化层各分层的溶解电量，实现了对取向硅钢氧化层各分层的快速、准确测定，可以区分出Mg2SiO4玻璃膜底层、SiN层、SiO2层、FeO及铁橄榄石层等分层性能，为取向硅钢生产工艺参数的控制提供指导。