硅钢资料

对低温法生产的以AlN为主抑制剂的Hi-B取向硅钢高温退火过程进行了中断实验,借助EBSD及TEM技术对高温退火连续升温过程中织构与析出物的演变进行了研究。实验结果表明,800℃时ODF图出现高斯织构组分,但强度很弱,高斯晶粒偏离角在10°以上;950~1 000℃时高斯晶粒异常长大,偏离角3~6°;高温退火过程析出物主要有球形、规则立方形及不规则多面体形3种形貌,由于渗N的影响,Zener因子先增大再减小,并且析出物在高斯晶界前沿优先粗化。 The annealing process at high temperature of Hi-B silicon steel using low slab reheat temperature and with AlN as the inhibitor has been studied by interrupting test,and the evolution of texture and precipitates during continuous heating-up in the annealing process at high temperature was analyzed by EBSD and TEM. The results showed that Goss texture appears in ODF at 800 ℃,but the intensity of Goss texture was very weak and the deviation angle was more than10°. Goss grains grow abnormally durin... 

采用非水溶液电解方法来提取无取向硅钢中夹杂物。通过扫描电镜(SEM)观察结果表明:无取向硅钢中主要夹杂物为六棱柱的AlN、不规则硅酸盐及球状的铁的硫化物和氧化物,其中AlN夹杂尺寸在1~5μm,数量较多,还有部分AlN的复合夹杂。进一步研究了AlN复合夹杂形成机理,采用了Thermo-Calc热力学计算软件计算出该钢样中AlN、MnS析出温度分别为1 240℃、1 200℃,而Al2O3析出温度大于1 800℃,从而为AlN复合夹杂形成机理提供了一个理论依据。 Extracting inclusions from non-oriented silicon steel in non-aqueous electrolysis is a nondestructive method to gain inclusions.Scanning electron microscopy shows that the main inclusions in non-oriented silicon steel were hexagonal AlN,which was of large quantity,irregular silicate,spherical iron sulfide and oxide.The size of AlN inclusions ranged from 1to 5μm,and there were some duplex inclusions of AlN.To further study the formation mechanism of AlN duplex inclusions,Thermo-Calc thermodynamic... 

本申请提供一种电工钢及其制备方法，制备方法包括：将电工钢的板坯进行热轧获得钢卷；将热轧后的钢卷进行酸洗冷轧；将酸洗冷轧后的钢卷进行第一次罩式退火；将第一次罩式退火后的钢卷进行平整；将平整后的钢卷进行第二次罩式退火；将第二次罩式退火后的钢卷进行重卷，以获得电工钢。本申请提供的电工钢的制备方法采用两次罩式退火，退火的主要目的是消除酸洗冷轧工序产生的加工硬化，使钢板充分再结晶，获得理想的铁损及磁感应强度。而采用两次罩式退火，相对于一次罩式退火工序来说，能够进一步降低铁损，提高电工钢的磁性能。

本发明实施例涉及一种硅钢片冲剪设备及冲剪工艺，该设备包括冲床、送料台、第一刀模、第二刀模和第三刀模；送料台用于传送待加工的硅钢条；第一刀模用于冲剪硅钢条以在硅钢条上形成预设形状的第一凹槽，第一凹槽处构成“工”字形硅钢片的一侧凹部；第二刀模用于冲剪硅钢条以在硅钢条上形成预设形状的第二凹槽，第二凹槽与所述第一凹槽相对应，第二凹槽处构成“工”字形硅钢片的另一侧凹部，第二刀模与硅钢条在硅钢条的横向方向上能够产生预设距离的相对位移；第三刀模用于沿硅钢条的横向方向剪断硅钢条。该设备能够采用硅钢片低成本、高效率地制造“工”字形硅钢片。

本文介绍了无取向硅钢C6涂液的性能,研究了配水量、固化程度和涂层厚度等因素对无取向硅钢C6涂层性能的影响。结果表明,随着配水量的增加,完全固化所需的时间增加,涂液固体含量降低,涂层厚度减小;随着固化程度的提高,涂层硬度先增大然后趋于恒定,而柔韧性逐渐变差,在过固化后急剧恶化;涂层厚度对涂层的表面外观、附着性和绝缘层间电阻均有显著影响。 Based on the introduction about the performance of C6 varnish for non-oriented silicon steel sheets,effects of water amount,curing degree and coating thickness are discussed. Results show that with the increase of water amount,the time required to cure completely extends,and both the solid content of C6 varnish and the coating thickness decrease. As the curing degree increases,the hardness of the coating increases first and then tends to be constant,however the flexibility degenerates,especially... 

采用自主研发的脉冲磁场退火装置，在取向硅钢脱碳退火过程中分别施加不同强度的磁场，并采用光学显微镜和X射线衍射仪研究了脉冲磁场脱碳退火后试样的显微组织和宏观织构。结果表明，脱碳退火过程中施加脉冲磁场后取向硅钢的平均晶粒尺寸均增加，当磁场强度为40 mT时，平均晶粒尺寸最大，为13.06μm。此外，取向硅钢试样的立方织构{001}<100>强度减弱，高斯织构{110}<001>和{111}<112>织构增强，有利于获得更好的成品织构和磁性能。 Self-developed pulsed magnetic field annealing device was used to apply magnetic field of different intensities during decarburization annealing of an oriented silicon steel, and microstructure and macro-texture of the specimens after decarburization annealing in a pulsed magnetic field were studied by using optical microscope and X-ray diffractometer. The results show that the average grain size of the oriented silicon steel increases with the application of pulsed magnetic field during decarbu... 

本发明提供了一种可修饰取向硅钢表面的无机绝缘涂料及其制备和使用方法，该涂料按照重量份计，包括：大颗粒硅溶胶5‑35份、磷酸二氢铝10‑30份、小颗粒硅溶胶5‑35份、铬酐0.5‑5份、增稠剂1‑10份、钛白粉0.01‑0.5份及去离子水0‑78.49份；该涂料的固含量为20‑40％。该涂料制备方法为：将增稠剂、去离子水、磷酸二氢铝、大颗粒硅溶胶、小颗粒硅溶胶，铬酐和钛白粉依次加入反应器中搅拌均匀，室温静置0.5‑1h。该涂料在使用时，需先将取向硅钢片进行清洁干燥预处理后，再将涂料辊涂在取向硅钢片上固化烧结并控制膜厚。本发明所提供的涂料制成的涂层表面平整均匀、颜色光亮，具有优良的附着性、耐蚀性、热稳定性和绝缘性，并且能修饰因硅酸镁底层质量不良引起的露晶亮点缺陷。

介绍了EB5325涂层液的主要性能和中冶新材生产冷轧无取向电工钢所用的涂层设备,通过多次试验摸索出使用EB5325涂层液的工艺,对涂层出现的缺陷进行分析研究,并提出解决方法,使中冶新材生产的冷轧无取向电工钢的涂层质量满足了用户的要求。 This article introduces the main properties of EB5325 and the coating equipments for cold-rolled non-oriented electrical steel. A process using EB5325 coating liquid is made through many time experiments and exploration. The appeared defects in the coating are studied and analyzed,and the solutions are proposed. The coating quality meets clients’ requirements of cold rolled non-oriented electrical steel. 

本发明公开了一种酸洗低牌号无取向硅钢的方法，从酸洗线前拉矫机的延伸率设定、酸液浓度、酸液温度、酸洗槽内液位的控制、酸液中铁离子的含量等方面入手，解决酸洗低牌号无取向硅钢的问题。

一种无取向性电磁钢板，其母材的化学组成以质量％计为：C：0.0010～0.0040％、Si：3.5～4.9％、Mn：0.05～0.20％、Al：0.05～0.45％、P：0.030％以下、S：0.0030％以下、N：0.0030％以下、O：0.0100～0.0400％、Ca：不足0.0010％、Ti：不足0.0050％、Nb：不足0.0050％、Zr：不足0.0050％、V：不足0.0050％、Cu：不足0.20％、Ni：不足0.50％、Sn：0～0.05％、Sb：0～0.05％、剩余部分：Fe和杂质；满足[4.0≦Si+Al≦5.0]；除了从母材的表面到深度方向10μm的位置以外的区域的O含量不足0.0050％。

本实用新型公开了一种用于硅钢片自动排列叠片装置，包括：第一壳体，所述第一壳体的一侧开设有第一条形孔，所述第一壳体的内侧顶部安装有两个气缸，所述第一壳体内部位于气缸下方设有第一固定板，两个所述气缸的活塞杆均与第一固定板固定连接，所述第一壳体的内侧底部焊接有两个弹簧，所述弹簧的顶部焊接有第二固定板，所述第一壳体的内侧底部安装有第一触碰开关，所述第二固定板底部靠近第一触碰开关的一侧焊接有第一固定块；本实用新型在使用时，通过设置气缸推动第一固定板带动硅钢片运动，使硅钢片移动至第二固定板上，完成对硅钢片的自动叠片工作，无需人工手动对硅钢片进行叠片，提高硅钢片的叠片效率并减少人工劳动负担。

本发明揭示了一种无取向硅钢及其生产方法。该无取向硅钢的化学成分：Si:2.95%~3.15%，Al:0.75%~0.95%，Si+2Al:4.6%~4.9%，Mn:0.5%~0.7%，Sn:0.03%~0.04%，Cu≤0.03%，Cr≤0.03%，Ni≤0.03%，Nb≤0.004%，V≤0.004%，Ti≤0.004%，C≤0.0025%，P≤0.015%，S≤0.0015%，N≤0.004%，余量铁；Mn/S≥380，Al/N≥200；无取向硅钢的再结晶晶粒尺寸50~80μm。本发明在保证磁性能的同时，提高了强度，解决了现有技术所存在的磁性能和强度的兼顾问题。