试验研究了退火温度(850~950℃)和时间(5~18 min)对2.3 mm热轧硅钢板(/%:0.036C,3.15Si,0.21Mn,0.005P,0.007S,0.032A1)6道次轧制的0.35 mm冷轧板组织和织构的影响。结果表明,退火温度越高,晶粒平均尺寸越大,900℃5 min退火时平均晶粒尺寸41.39μm,试样织构主要集中在γ取向线上的{111}<112>织构组分和{111}<110>织构组分;900℃18 min退火时平均晶粒尺寸为48.08μm,试样的{111}面织构和{112}面织构密度都明显减弱,{001}面织构增强,磁性能较优。 The effect of annealing temperature(850 ~950 ℃) and holding time(5 ~ 18 min) on structure and texture of 0.35 mm sheet by 6 passes cold-rolling from 2.3 mm hot-rolled plate of silicon steel(/%:0.036 C,3.15 Si,0.21 Mn,0.005 P,0.007 S,0.032A1) has been tested and studied.Results show that the higher the annealing temperature the coarser the average grain size;As annealing at 900 ℃ for 5 min the average grain size of steel sheet is 41.39 μm,and the texture in sample is mainly concentrated in y orie... 

本发明公开了一种高磁感取向硅钢实验室轧机一次冷轧方法，包括：1)取样，实验室冷轧材料选取经过常化酸洗后的厚度为2.3mm的取向硅钢试样；2)制样，利用取向硅钢专用剪板机，裁剪试样尺寸为轧向600mm×横向150mm；将试样表层轻涂一层薄薄的轧制油；3)冷轧轧制规程制定，轧前厚度为2.3mm；其中：轧制总道次为6次时轧后厚度为0.35mm，轧制总道次为7次时轧后厚度为0.27mm，轧制总道次为8次时轧后厚度为0.23mm。本发明的目的是提供一种高磁感取向硅钢实验室轧机一次冷轧方法，为工业试制提供一定的技术参考，以及后续工艺研究提供了更加可靠的试样和条件。

硅钢是钢铁产品中的\"工艺品\",是高附加值产品,通过对我国主要硅钢生产厂家的工艺设备,市场情况分析,简要介绍了我国硅钢生产消费现状,未来生产能力预测及硅钢未来发展趋势。 Silicon steel is the \"crafts\" of steel products,also is high value-added product.By analyzing process equipment and market condition of major silicon steel-making plant of China,it briefly introduces our current production consumption status,future production capacity prediction and future development trend of silicon steel. 

本申请实施例公开了一种硅钢铁芯生产用多功能卷绕机，包括平台板，所述平台板底部的左侧固定连接有旋转电机，所述旋转电机的输出端固定连接有旋转杆，所述旋转杆的顶部固定连接有转盘，所述转盘的顶部固定连接有铁芯型模，所述铁芯型模的外表面活动连接有限定座，所述平台板顶部中心的左侧固定连接有第一U型板。第一弹簧和升降板的配合使用，可以让使用者下压升降板，使得升降板带动安装杆进行向下移动，继而使得安装杆脱离第二U型板所开设的轴槽，继而使得安装杆的顶部存在一定的间隙，进而可以通过间隙将带盘插入在安装杆上，该方式装卸起来简单快捷，可以有效的减少装卸带盘所消耗的时间，从而提高了设备的工作效率。

介绍在取向硅钢生产中抑制剂的作用以及多元抑制剂的机理和应用情况,分析多元抑制剂方案中各种元素对高磁感取向硅钢性能的影响,并根据生产实践提出了进一步研究的方向. The role of an inhibitor in the production of grain oriented silicon steel,and the mechanism of multiplex inhibitor in the production are described in the present article.In addition,the influence of various elements in the multiplex inhibitor on the performance of grain oriented silicon steel with high magnetic induction is elucidated.Further work needed in this research is also indicated. 

一种甩带法制备高磁性能含磷硅钢薄带的方法，属于合金材料领域。本发明以硅钢(Fe‑(3‑6.5)wt.％Si)块体为母合金，并添加一定量的硅铁合金及磷铁合金，放置于中频感应炉中，熔融后经快速凝固‑甩带、冷轧、热处理工艺，得到具有优异性能的含磷硅钢薄带。对于硅钢而言，P元素的少量加入能够有效的提升电阻率从而显著降低铁损，且具备优化软磁性能的作用。而采用甩带法能够充分利用其快速凝固的特征，从根本上避免了P元素在传统熔炼冷却过程中严重偏析的缺陷，极佳地保证了产品的组织优势与软磁性能。本发明具有操作简单、生产效率高、产品精度高、工艺流程短、无污染与夹杂、性能优异等优点。

通过在实验室条件下模拟薄板坯连铸连轧流程,并在以Cu2S为主抑制剂制造普通取向硅钢(CGO)的基础上,加入适量钒钛,研究了钒钛对取向硅钢组织与磁性能的影响。结果表明,适量钒钛使热轧板和脱碳退火板组织更好,尤其使脱碳退火板的晶粒更加细小和均匀;加入适量钒钛不但使热轧板表面高斯织构强度更高,更使脱碳退火板中有利于高斯织构发展的γ织构强度更高;适量钒钛能形成Cu2S+(V,Ti)N等复合析出物,起到辅助抑制剂作用,加强抑制能力。细小均匀的晶粒、强度更高的有利织构和更强的抑制能力使CGO钢磁性能更佳。 Effect of V and Ti on microstructure and magnetic properties of conventional grain-oriented silicon steel(CGO) were investigated under simulated thin slab continuous casting and rolling process in laboratory with Cu2 S as the dominant inhibitor. The results show that appropriate amount V and Ti make the microstructures of the hot rolled sheet and the decarburizing annealed sheet better,especially make the grains of the decarburizing annealed sheet more tiny and uniform. Adding appropriate V and ... 

【作者】 罗海文； 向睿； ...

本实用新型涉及一种硅钢片叠压精准定位设备，包括压台、压板和仿形燕尾键，所述压台上开有与仿形燕尾键下端相对的限位槽，所述压板设置与压台上方，所述压板上开有与仿形燕尾键上端相对的限位孔。本技术方案当硅钢片叠放压合之后，仿形燕尾键可以去除，并能够在硅钢片组成的铁芯上形成燕尾槽，用于后期燕尾键的组装，且能够保证燕尾槽内的结构规则，便于后期燕尾键组装。

以CaO-CaF2复合渣系为脱硫剂,在RH精炼过程采用真空投入法进行高牌号无取向电工钢深脱硫工业试验,采用KTH模型计算分析了RH炉渣成分对硫容量CS的影响。研究结果表明,炉渣成分控制在w((CaO))/w((SiO2))为5~7,w((CaO))/w((Al2O3))为1.5~1.8,w((Al2O3))为25%~30%,w((FeO+MnO))<5%,脱硫剂加入量为6~8kg/t时,钢中硫质量分数从平均0.003 1%降低到0.001 8%,最高脱硫率达到47.1%,平均脱硫率为41.7%。 The industrial trials on deep desulphurization of high grade non-oriented electrical steel were finished through using CaO-CaF2complex based fluxes in RH process.Using the KTH model,the effect of refining slag composition on the sulfide capacities was analyzed.The results show that the chemical composition of refining slag(mass fraction,%)is w((CaO/SiO2))between 5to 7,w((CaO))/w((Al2O3))beween 1.5to 1.8,w((Al2O3)) between 25%to 30%,w((FeO+MnO))less than 5%,and the desulphurizer addition level of... 

本发明涉及到一种铸铝转子硅钢片、采用该硅钢片的转子及制造转子的方法，该铸铝转子硅钢片包括圆形板片状本体，本体中心开设有转轴孔，本体上还以转轴孔为中心周向均布有多个铸铝孔，本体外缘设置有与铸铝孔一一对应的凹槽，本体两侧侧面均涂覆有绝缘层。采用上述硅钢片的转子包括转轴，所述转轴上套接有铁芯，该铁芯由大量上述的硅钢片层层叠压而成，每片硅钢片上的铸铝孔均相互正对，在铁芯上形成多条贯穿铁芯的通孔，每条通孔内设置有一条导条，铁芯两端分别连接有导电端环，各导条的两端分别伸出通孔与导电端环电性连接，各导条对两导电端环的拉力使两导电端环紧压在铁芯两端。

本实用新型公开了一种电机硅钢片用激光切割机的高压空气冷却干燥装置，包括一端侧带密封端盖且另一端侧设出气接头的换热筒、设在密封端盖的制冷剂进液管和回气管，密封端盖设有进气接头，换热筒内设热交换器，热交换器由换热盘管、换热翅片和下截圆挡板、上截圆挡板组成，下截圆挡板的平底切边、上截圆挡板的平顶切边分别与换热筒内壁具有间隔；制冷剂进液管的一端与制冷系统的一端连接而其另一端顺次连接分液头、毛细管、换热盘管的上端入口，回气管的一端与制冷系统的另一端连接而其另一端依次连接回气汇总管、换热盘管的下端出口；换热筒的底部安装有带放水阀的自动排水部件。通过本装置换热后可获得冷却干燥的高压空气以供激光切割机使用。