本发明涉及一种硅钢片铁芯用自动叠装系统，托板、上料单元、精定位单元、叠装单元、抓取单元，所述上料单元有一个，位于中部位置，所述精定位单元一共有两个，分别位于上料单元的两侧，所述叠装单元一共有两个，分别位于两个精定位单元的两侧，从而使得整个自动叠装系统由中间向两侧方向均依次为上料单元、精定位单元、叠装单元。本发明的优点在于：通过对上料单元、精定位单元、叠装单元的数量及排布位置进行重新设计，采用由中间向两侧供料的方式，使得两侧的上料顺序均独立运行，不存在相互干涉的风险，确保单侧的上料顺序的顺利进行，相对应的也就降低了程序设计的复杂程度，减轻了设计人员的工作强度。

采用双辊薄带连铸工艺试制了2.6 mm厚5.28%Si-1.11%Al高硅钢薄带,对比了1050℃×5 min正火及不正火铸带280℃冷轧至0.5 mm后,再经900～1100℃退火的磁性能。结果表明,高硅钢铸带显微组织为等轴晶组织,正火后铸带边部晶粒长大,中心层晶粒变化较小。成品中析出物主要为较粗大的AlN和AlN+MnS复合析出物,尺寸为0.5～2.5μm。与不正火试样相比,正火试样成品铁损大幅降低,磁感小幅下降;随退火温度的升高,两种工艺下铁损和磁感都是先降低后升高,在1050℃出现最低值。 2.6 mm thickness 5.28% Si-1.11% Al non-oriented high silicon steel was produced by twin roll thin strip casting.Magnetic property of the strip un-normalized and normalized at 1050 ℃×5 min was contrasted after cold rolled to 0.5 mm at 280 ℃ and 900-1100 ℃ final annealing.The results show that microstructure of the strip is equiaxed crystal.The surface grain is coarsened and the center layer grain has little change of the normalized strip.The main precipitates are AlN and MnS+AlN with 0.5-2.5 μm s... 

本发明涉及一种具有优异铁损和磁性能的无取向电工钢及其生产方法，电工钢成分及质量含量为C≤0.0015%，Si:1.10‑1.40%，Mn：0.35‑0.55%，P≤0.018%，S≤0.003%，Al：0.20‑0.30%，Ti≤0.0015%，N≤0.0028%，O≤0.0015%，N＋O≤0.0040%，余量为Fe和不可避免的杂质。生产方法包括铁水预处理、转炉冶炼、RH精炼、连铸、轧制、常化、冷轧、连退和涂层工序。本发明电工钢热轧成品微观晶粒尺寸70‑95μm，对铁损和磁性能有利的（100）组织织构控制在82‑92%，成品P15/50:3.5‑4.0w/kg，B50:1.70‑1.98T。

招商证券建筑钢铁团队视频第三弹！本团队基于下方两篇电工钢行业深度报告推出本期...

根据本发明的一个实施例的取向电工钢板用退火隔离剂组合物，其包含复合金属氧化物，复合金属氧化物包含Mg和金属M，金属M是Be、Ca、Ba、Sr、Sn、Mn、Fe、Co、Ni、Cu和Zn中的一种以上。

采用热模拟方法及EBSD技术,研究Fe-3 wt%Si电工钢在不同温度下组织的动、静态再结晶及晶粒取向特征,特别是少量奥氏体对铁素体动、静态再结晶组织及取向的影响。结果表明,不同温度形变的组织主要分三类:形变长条铁素体、珠光体和等轴细小铁素体。长条形变铁素体内发生动态回复或连续式的动态再结晶,奥氏体周围的铁素体动态再结晶加速,部分以传统的不连续方式动态再结晶。铁素体、奥氏体都可发生静态再结晶。奥氏体的静态再结晶在1050℃以上明显,铁素体的静态再结晶随温度的升高逐渐进行,最显著的再结晶发生在1050℃。不同温度形变的样品,其形变晶粒取向主要以<111>和<100>为主,小等轴铁素体晶粒除与大形变铁素体取向相近外,出现了<110>取向及其它取向。 Static and dynamic recrystallization and grain orientations in a hot-compressed Fe-3 wt% Si electrical steels were studied at different temperatures using Gleeble simulator and EBSD technique,particularly focusing on the effect of small amount of austenite on ferritic microstructure and orientations.The results show that microstructure of the compressed steel,depending on deformation temperature,consisted of elongated and deformed ferrite,pearlite and fine equal-axed ferrite.The elongated ferrit... 

测试了高强无取向电工钢的S-N曲线,并借助光学显微镜、扫描电子显微镜、透射电子显微镜分析了实验钢组织,疲劳断口形貌和位错结构。结果表明:室温条件下,频率为20Hz,应力比R为0.1,循环10~7周次时,实验钢的疲劳强度为360MPa,疲劳裂纹萌生于实验钢的次表面,裂纹萌生点附近有沿晶开裂现象,疲劳裂纹扩展区域有解理台阶与疲劳条纹,瞬间断裂区是韧性断裂,有大量韧窝。实验钢在循环应力作用下基体中产生了大量位错,并有驻留滑移带终止在晶界位置。 The S-N curve of a high strength non-oriented electrical steel was tested.The microstructure and fatigue fracture morphology and dislocation were analyzed by optical microscope,scanning electron microscope,transmission electron microscope.The results showed that:at room temperature and the frequency of 20 Hz and the stress ratio Rof 0.1,the fatigue strength of the experimental steel was 360 MPa when the cycle was 10~7 cycles.The fatigue crack initiation at the surface of the steel and the interg... 

通过观察冲剪边缘组织,测量冲剪边缘的显微硬度、残余应力的分布情况和磁性能的变化研究了冲剪加工对无取向硅钢50WW800边缘组织和磁性能的影响。对冲剪后硅钢片进行750℃退火,分析退火对组织和磁性能的影响。结果表明,硅钢片剪切边缘会存在0.4 mm的形变硬化层,边缘应力大,铁损增加。退火后变形减小,形变硬化层变小,残余应力大幅度减少,铁损减少。 The influence of punching process on cutting edge microstructure and magnetic properties of non-oriented silicon steel 50WW800was studied by observing microstructure and measuring microhardness near cutting edge.The residual stress distribution in the silicon steel tooth and magnetic properties were measured.Effect of annealing at 750 ℃ on microstructure and magnetic properties of the silicon steel was analyzed.The results show that a cut-edge hardening layer up to 0.4 mm is observed,residual st... 

【作者】 陶永根； ...

本发明涉及一种硅钢片视觉识别与无损检测方法，测量硅钢片的厚度并且计算已经叠积完成的硅钢片的总高度，记录最后叠积的一片硅钢片的形状和两定位孔坐标，计算和输出当前硅钢片的形状、两定位孔坐标的位置偏差值和两定位孔坐标的定位孔间距，记录硅钢片两端的接缝宽度和坐标并且输出搭接形状，判断定位孔间距、两定位孔位置、接缝宽度是否符合标准，以及两片硅钢片是否已经搭接上，通过打齐硅钢片使之符合要求、或者停机人工调整。本发明还涉及一种硅钢片视觉识别与无损检测装置。本发明利用激光测距仪、相机实现了无损检测，实现了每片硅钢片高度值、定位孔、接缝宽度的即时自动测量，通过PLC控制系统将控制信息传输至机械臂进行放置精度微调。

本发明公开了一种直流换流阀饱和电抗器用超薄硅钢铁心质量的评估方法，包括以下步骤：S1、外观评价；S2、叠装系数评价；S3、磁性能评价；S4、噪声评价；S5、耐受环境温度变化评价和S6、长期运行性能评价，本发明考虑了直流换流阀饱和电抗器对超薄硅钢铁心外观、叠装系数、磁性能、噪声及长期运行等特性要求，实现了超薄硅钢铁心外形外观的性能评估、铁心基本参数评估、电磁性能评估、耐受环境温度变化评估及长期电热运行特性评估，为直流换流阀饱和电抗器用超薄硅钢铁心可靠运行提供了保障。

本发明属于退火工艺技术领域，公开了一种高牌号无取向硅钢剪切方法，包括：待剪切带钢由夹送辊输送到达剪切位后，夹送辊释放对所述待剪切带钢的夹持；位于所述待剪切带钢下方的下剪刃上移，推顶所述待剪切带钢在低张力状态下持续向上运动；在所述待剪切带钢与上剪刃接触后，将所述待剪切带钢剪断。本发明提供的高牌号无取向硅钢剪切方法能够极大的减少高牌号无取向硅钢的剪切缺陷，降低废品量，提升剪切效率。