对1990~2010年在我国申请的冷轧无取向硅钢涂层的专利数量、专利技术领域分布进行了统计,对典型涂层专利技术进行了分析,探讨了无取向硅钢涂层的发展趋势。统计分析结果表明,目前无取向硅钢涂层典型的专利技术主要有自粘结涂层、无铬含稀土元素涂层、含钼酸盐环保涂层及采用有机-无机纳米杂化材料为主成膜物形成的涂层等。无取向硅钢涂层发展的趋势主要是无铬环保的半无机、半有机型涂层。 The patent quantity of cold-rolled non-oriented silicon steel coating and distribution of technology fields applied in China in 1990-2010 were summarized.The analysis results indicate that typical patent technologies include self-adhesion coating,chromium-free and with rare earth element coating,environment-friendly and with molybdate coating,coatings with organic-inorganic hybrid materials as main forming agent and so on.The main development trends of coatings on silicon steel are among semi-in... 

测试了高强无取向电工钢的S-N曲线,并借助光学显微镜、扫描电子显微镜、透射电子显微镜分析了实验钢组织,疲劳断口形貌和位错结构。结果表明:室温条件下,频率为20Hz,应力比R为0.1,循环10~7周次时,实验钢的疲劳强度为360MPa,疲劳裂纹萌生于实验钢的次表面,裂纹萌生点附近有沿晶开裂现象,疲劳裂纹扩展区域有解理台阶与疲劳条纹,瞬间断裂区是韧性断裂,有大量韧窝。实验钢在循环应力作用下基体中产生了大量位错,并有驻留滑移带终止在晶界位置。 The S-N curve of a high strength non-oriented electrical steel was tested.The microstructure and fatigue fracture morphology and dislocation were analyzed by optical microscope,scanning electron microscope,transmission electron microscope.The results showed that:at room temperature and the frequency of 20 Hz and the stress ratio Rof 0.1,the fatigue strength of the experimental steel was 360 MPa when the cycle was 10~7 cycles.The fatigue crack initiation at the surface of the steel and the interg... 

一种硅钢厂调功器故障报警自动复位的方法，包括：通过人机界面对炼钢炉温度进行设定，并在炼钢过程中实时获取炼钢炉温度；将炼钢炉实时温度与设定温度进行对比，当炼钢炉实时温度低于设定温度时，启动调节器；调节器输出功率使电阻带加热，使炼钢炉实时温度达到设定温度；当调节器发生故障时，调节器将故障信号发送给后台服务器，后台服务器根据故障指令，按预设规则控制与调节器连接的继电器，控制继电器按压复位按钮，使调节器自动复位。本发明解决了现有技术中通过电气人员来通过复位消除故障状态，耽误时间长，容易产生废品的问题。

根据本发明的一个实施例的粘接涂料组合物，其包含聚乙烯丙烯酸酯100重量份和无机颗粒3至25重量份，所述聚乙烯丙烯酸酯包含由以下化学式1表示的重复单元和由以下化学式2表示的重复单元，所述聚乙烯丙烯酸酯包含75至95重量％的由以下化学式1表示的重复单元、5至25重量％的由以下化学式2表示的重复单元。

本发明一种焊接压力容器用碳锰硅钢钢板及其生产方法，钢板化学成分及其重量百分含量为：C：0.18‑0.26%，Si：0.18‑0.65%，Mn：0.92‑1.72%，P≤0.008%，S≤0.002%，Cu：0.30‑0.40%，Ni：0.25‑0.35%，Cr：0.25‑0.35%，Mo≤0.10%，V≤0.10%，B：0.003‑0.005%，余量为Fe及不可避免的杂质元素。本发明钢板中加入的贵合金元素含量相对较少，冶炼成本及后续的生产成本控制较低，市场潜力和竞争力很大。

根据本发明的一个实施例的无取向电工钢板，以重量％计，所述钢板包含Si：2.1至3.8％、Mn：0.001至0.6％、Al：0.001至0.6％、Bi：0.0005至0.003％和Ge：0.0003至0.001％，余量包含Fe和不可避免的杂质。

本实用新型涉及硅钢生产设备技术领域，具体公开了硅钢冷轧用厚壁套筒，包括外筒和内筒，所述外筒与内筒之间固定有若干连接板，所述外筒上开设有插缝槽，所述外筒的内壁上设有靠近插缝槽设置的限位件，所述限位件包括锁止板和弹性件，弹性件一端固定在外筒的内壁上，另一端固定在锁止板的顶部，所述锁止板上设有朝向插缝槽的斜面。本专利中通过外筒与内筒设置，既提高了整个套筒的厚度，使其能够承受硅钢带卷绕时的压力，同时也减少因提高套筒厚度使得套筒的重量增加的问题，这样设置整个套筒的质量较轻。

无取向硅钢特别是中牌号以上的无取向硅钢,随着含硅量的提高,常温下塑性较差,冷轧过程中轧制力明显提高,如果存在原料质量问题,极易发生断带事故,影响硅钢冷轧过程的成材率和生产效率。通过优化冷轧工艺参数,可提高冷轧稳定性。生产中通过合理分配冷轧各道次压下量和轧制速度,保证了轧制过程的稳定,很大程度减少了冷轧断带事故的发生。 Non-oriented silicon steel, especially in the low and middle grade, with the increase of silicon content, plasticity is poor at room temperature, rolling force in cold rolling process significantly improved .If there is the quality defect of raw materials , easily sheet is rolling off. Affect finished product rate and production efficiency in process of cold-rolled silicon steel. Through optimization of cold rolled process parameter , improve the stability of cold-rolling process. Through reason... 

针对节能电机对无取向电工钢在磁性能方面的特殊要求,采用普通W600牌号的热轧板为原料,通过大量的现场工艺试验,研究总结出了\"超低张力\"的运行工艺、\"先快后慢\"的加热工艺、\"先湿后干\"的退火脱碳工艺、\"先缓后急\"的冷却工艺,生产出P1.5/50≤4.0 W/kg、B50≥1.70 T的冷轧电工钢产品,满足了节能电机的要求。 Based on the special requirements of no-oriented electrical steel for saving energy motor in magnetic aspects,using common W600 brand of hot rolled plate as raw material,through a large number of real tests,an ultra-low tension process,heating process which was quick at first and then slow,annealing decarburization process which was dry after the first wet,and a cooling technology of \"slow after the first urgent\" were concluded.Electrical steel product with P1.5/50≤4.0W/kg,B50≥1.70T was produced... 

本发明提供了一种无取向电工钢，包括：C0.001～0.010％，Si0.5～4.0％，Mn0.05～0.8％，Al0.2～1.5％，P≤0.002％，S≤0.0015％，O≤0.002％，N≤0.0015％，各成分均为质量百分比；还提供一种无取向电工钢制造方法，包括：冶炼钢水、薄带连铸、常化酸洗、冷轧以及退火涂层。本发明中，在冶炼钢水时，控制钢水中C、Si、Mn、Al、P、S、O以及N几种成分的含量，且通过常化工艺，可以有效控制无取向电工钢成品的产品质量，具有较低的铁损以及较高的电磁性能，另外整体制造流程比较短，能够达到节能环保的目的，而通过冷连扎，有利于提高产品的质量、成材率和生产效率。

本实用新型公开了一种变压器硅钢片整平工装，涉及变压器装配技术领域，包括底板，所述底板顶部一角处安装有第一气缸，所述第一气缸的输出端固定有支撑块，所述支撑块一端设置有第一L型垫块，所述第一L型垫块两端皆开设有配合槽。本实用新型通过设置有第一L型垫块、第二L型垫块、传动带、第一气缸和第二气缸之间的配合，通过第二L型垫块内侧对运动中的变压器硅钢片进行拦截，第一气缸的输出端伸出带动第一L型垫块进行移动，使第一L型垫块将变压器硅钢片推至第二L型垫块拐角处，工作人员通过控制第一气缸输出端来回伸缩对硅钢片进行反复挤压整平，有效提高了变压器硅钢片整平机的工作效率，节约成本。

本发明提供能够制造实现高磁通密度且磁特性优异的方向性电磁钢板的新颖并且得以改良的方向性电磁钢板的制造方法。本发明的一方案提供一种方向性电磁钢板的制造方法，其特征在于，其包含热轧工序、冷轧工序、一次再结晶退火工序、最终退火工序及平坦化退火工序，并进行喷丸处理和/或矫平加工处理及与溶液相接触的处理，上述溶液含有规定量的Cu等，pH为‑1.5以上且低于7，液温为15℃以上且100℃以下，钢板在上述溶液中浸渍的时间为5秒以上且200秒以下。