硅钢资料

阐述了影响硅钢卷材下料利用率的因素,并结合具体事例利用计算机排样系统进行了详细分析,对提高硅钢卷材的利用率具有一定的指导作用。 It describes the factors influenceing the the utilization ratio of the roll of Silicon steel,and analyzes it in detail combined with concrete examples by a computer arrangement system,which can give a guide for increasing the utilization ratio of the roll of Silicon steel. 

对CSP流程生产的高磁感无取向电工钢50W1300在偏离轧制方向不同角度处的磁性能进行了测试和分析。结果表明:在偏离轧向不同角度处,磁性能差异显著,尤其在α=60°时磁感最低;偏离轧制方向不同角度处的磁性能大小取决于织构类型、强度及分布状态;增强{100}<0vw>和α、η取向的有利织构组分,降低不利的γ取向织构组分,且使有利织构组分分布越漫散,磁各向异性越小。 Magnetic properties of high magnetic induction non-oriented electrical steel 50W1300 produced by CSP processes were investigated with different direction in relation to the rolling direction.The result shows that magnetic properties are significantly different in relation to the rolling direction,in particular,the minimum magnetic induction occurs at 60° in relation to the rolling direction.Magnetic properties of different directions in relation to rolling direction depend on type and distributi... 

试验研究了退火温度(850~950℃)和时间(5~18 min)对2.3 mm热轧硅钢板(/%:0.036C,3.15Si,0.21Mn,0.005P,0.007S,0.032A1)6道次轧制的0.35 mm冷轧板组织和织构的影响。结果表明,退火温度越高,晶粒平均尺寸越大,900℃5 min退火时平均晶粒尺寸41.39μm,试样织构主要集中在γ取向线上的{111}<112>织构组分和{111}<110>织构组分;900℃18 min退火时平均晶粒尺寸为48.08μm,试样的{111}面织构和{112}面织构密度都明显减弱,{001}面织构增强,磁性能较优。 The effect of annealing temperature(850 ~950 ℃) and holding time(5 ~ 18 min) on structure and texture of 0.35 mm sheet by 6 passes cold-rolling from 2.3 mm hot-rolled plate of silicon steel(/%:0.036 C,3.15 Si,0.21 Mn,0.005 P,0.007 S,0.032A1) has been tested and studied.Results show that the higher the annealing temperature the coarser the average grain size;As annealing at 900 ℃ for 5 min the average grain size of steel sheet is 41.39 μm,and the texture in sample is mainly concentrated in y orie... 

本发明涉及一种冷连轧法生产无取向高硅钢的方法，RH真空脱碳处理后，铝脱氧及部分铝合金化，合金化后大罐钢水净循环大于3次或大于5分钟；熔炼合格钢水至连铸开浇前静置时间大于二十分钟；控制过热度5～15℃；采用电磁搅拌，控制等轴晶比例45％以上；3)热轧工序板坯装炉温度大于750℃；常化使晶粒尺寸在90～110μm范围内；连续退火炉加热段温度设定950～1150℃，均热段温度设定900～1050℃，全氮气干气氛保护，控制晶粒尺寸120～170μm。生产全过程中的热履历参数控制，充分发挥设计的微合金元素功能，改变析出物的组成、大小、形态及分布。

本发明公开了一种高效无取向硅钢极薄带的工业连续化生产方法，其包括异步轧制、脱脂、热处理、急速冷却、涂绝缘层、烘干烧结、卷取收集各工序；其中，异步轧制中的异步比为1:1.05～1:1.24；脱脂、热处理、急速冷却、涂绝缘层、烘干烧结、卷取收集工序为连续化生产工艺；热处理工序中，第一步为预热，预热温度为500℃～720℃，预热时间20秒～125秒；第二步为相变热处理，相变热处理温度为840℃～940℃，相变热处理时间100秒～600秒；急速冷却工序中，30秒内将钢带温度降温至350℃以下。优点在于:实现工业化连续生产无取向硅钢极薄带，有效提高产能，生产的无取向硅钢极薄带具备高磁感、低铁损等磁性能。

一种高磁感低铁损取向硅钢生产用表面涂层涂覆装置，包括：加工台，加工台上端固定连接支撑架，支撑架下端一侧固定连接伺服电机，伺服电机输出端固定连接第一齿轮，第一齿轮下端啮合连接第二齿轮，第二齿轮中部固定连接螺纹杆，螺纹杆上螺纹连接移动环，螺纹杆远离第二齿轮一侧转动连接支撑板，支撑板上端固定连接支撑架，移动环下端固定连接伸缩杆，支撑架下端前后部均固定连接连接框，本实用新型的有益效果是：通过设置的伺服电机、第一齿轮、第二齿轮、螺纹杆和移动环等结构，能够实现伸缩板带动硅钢板移动，从而能够完成自动化推料，减少工人劳力支出的同时，也能够避免工作人员手臂靠近涂层辊，从而避免安全事故的发生。

对应用动态加热进行短时温度退火的取向电工钢进行了二次再结晶研究。所进行研究的实验用取向电工钢是经过终冷轧和后续罩式退火后的一条工业化生产线生产的。研究结果表明,运用短时热处理条件可引起研究钢完全的异常晶粒长大。在实验室处理的材料的织构和金相组织与工业化生产的经过终退火而获得的相同的取向电工钢类似。但是,在实验室处理的取向电工钢的二次再结晶的矩阵中可观测到\"寄生\"晶粒。从磁性观点看,这些\"寄生\"晶粒含有不理想的{111}取向织构。 The present study was made to investigate secondary recrystallization in grain-oriented steels annealed at short time temperature exposures with application of dynamical heating.The investigated GO(Grain Oriented) steels for experiments were taken from one industrial line after final cold rolling reduction and subsequent box annealing.It was shown that application of short time heat treatment conditions could lead to complete abnormal grain growth in the investigated GO steel.The texture and mic... 

本实用新型涉及硅钢片加工领域，且公开了一种用于硅钢片钢卷制造的清洗装置，解决了目前市场上用于硅钢片钢卷制造的清洗装置工作效率低下，清洗效果不明显的问题，其包括包括清洗箱，所述清洗箱内腔的顶部与底部均安装有清洗导管，两个清洗导管的表面均等距离安装有清洗喷头，清洗箱两侧的下部分别安装有限位框和清刷框，清洗箱的一侧通过支架固定连接有安装板，安装板的表面转动连接有硅钢卷本体，硅钢卷本体的一端依次贯穿限位框、清洗箱和清刷框并延伸至清洗箱外部，该用于硅钢片钢卷制造的清洗装置，结构设计合理，清洗操作平稳，清洗干净，工作效率高，大大的提高了清洗效率和提高了清洗质量，极具推广应用价值。

为满足用户对无取向电工钢中硫含量的要求,采用CaO-CaF2复合渣系为脱硫剂,利用RH投入法对无取向电工钢进行深脱硫试验。试验结果表明,RH精炼渣成分控制在w CaO43%~51%、w Al2O325%~31%、w MgO4%~6%、w SiO29%~12%、w(FeO+MnO)3%~6%,在脱硫剂加入量为6~8 kg/t时,钢中平均硫含量从32×10-6降低到18×10-6,RH平均脱硫率为43.3%,最高达47.1%。利用KTH模型计算精炼终渣平均硫容量为0.003 1,RH精炼结束时渣-钢间实际平均硫分配比从14增加到52。 In order to satisfy the requirements of consumers on sulfur content in non-oriented electrical steel,taking( CaO-CaF 2) based flux as desulfurizer,industrial experiments on deep desulphurization of non-oriented electrical steel were carried out during RH process. The results show that as the compositions of refining slag are appropriately controlled with w CaO of 43% ~ 51%,w Al2O3 of 25% ~ 31%,w MgO of 4% ~ 6%,w SiO2 of 9% ~ 12%,and w( FeO + MnO) of 3% ~ 6%,and the desulfurizer added are at 6 ~ ... 

一种硅钢生产线退火炉前的换热装置，包含有抽风机（1）、立柱（2）、热交换器（3）、软管（4）和热风机（5）；其特征在于：所述的热交换器（3）由若干组U形不锈钢管连接而成，一端固定在轴套（8）上，另一端通过链条（10）连接在立柱（2）顶端的链条盘（9）上，当链条盘（9）转动时，链条（10）拉动热交换器（3）绕着横轴（7）抬起或放下。本发明通过抽风机（1）将清洁空气抽到热交换器（3）内进行加热，然后再通过软管（4）将热空气输送到热风机（5）内来加热硅钢板（14），有效的利用了热能，避免了凝露导致的板面发蓝现象。

本实用新型公开了一种硅钢卷放卷辅助装置，包括支撑板、摆臂、气缸和连动杆，所述摆臂一端通过第一转轴枢接在支撑板上，所述连动杆的一端通过第二转轴枢接在摆臂的中部，另一端通过转轴与气缸的输出端连接，所述气缸的缸筒固定在支撑板上，所述摆臂远离支撑板的一端设置有承载座，所述承载座上开设有弧形槽口，所述槽口处设置有滚动组件；所述滚动组件包括设置在承载座上的第一支撑架和可转动设置在第一支撑架上的滚柱。其可有效防止硅钢卷从辊筒上掉落，保证了生产的安全性。

热卷箱位于热连轧带钢生产线粗轧与精轧机之间,是热连轧生产中比较理想的中间保温设备。由于取向硅钢变形温度区间较窄,在生产中易出现边裂现象,同时中间坯的边部温度难于得到保证,因此一般不采用热卷箱设备生产,限制了传统热连轧生产线产品开发的品种。通过合理优化热卷箱控制工艺参数,解决了某厂传统热连轧生产线用热卷箱生产取向硅钢的边部质量问题,成功地生产出取向硅钢带。 The hot coil-box is an ideal heat retaining apparatus for hot rolling,lined between roughing mill and finishing mill. But oriented silicon steel has a narrow deformation temperature range,so that the edge crack easily occurs and it is difficult to insure the temperature of the intermediate blank. Therefore,the hot coil-box is rarely used in producing oriented silicon steel,which restricts the product development of the traditional hot rolling line. The article reasonable optimized process parame...