硅钢资料

通过后天抑制剂获得法制备了取向硅钢,对渗氮前后和高温退火升温阶段析出物的析出和转化规律进行了研究。研究结果表明,渗氮前脱碳退火态基体中存在少量的粗大AlN颗粒和细小AlN颗粒,渗氮处理后新析出大量的Si3N4析出物,高温退火升温阶段Si3N4将转化为(Al,Si)N,随着温度的继续升高(Al,Si)N颗粒将发生粗化,(Al,Si)N是后天抑制剂获得法制备取向硅钢的主要抑制剂。 Grain-oriented silicon steels were produced by acquired inhibitor method.The rule of precipitate transformation was studied after nitriding treatment and high-temperature finishing annealing.The results show that a small amount of large AlN and fine AlN are found in matrix before nitriding treatment,and a large amount of Si3N4 is precipitated in matrix after nitriding treatment.During the temperature rising period of high-temperature finishing annealing,Si3N4 would transform into(Al,Si)N,and(Al,... 

简述了无取向硅钢环保涂层发展背景,分析了硅钢环保涂层的特点及国内、外研究进展,提出了硅钢保涂层下一步的发展方向。 The back ground of environmental protection coating of non-oriented silicon steel was described in this paper.The characteristics and study progress in domestic and foreign of environmental protection coating of non-oriented silicon steel were analysised.The next development direction of environmental protection coating of non-oriented silicon steel was put forward. 

一种不含铬取向电磁钢板用涂料、其制备方法及带涂层的不含铬取向电磁钢板的制备方法，属于取向电磁钢板技术领域。所述涂料按质量份配比组成如下：100份磷酸盐、60～120份二氧化硅溶胶、5～50份氧化锡溶胶、2～40份硼酸和0.5～10份二氧化硅粉体。本发明所述制备方法环境友好、能够满足规模化生产要求，制备的涂料不含铬、具有良好的稳定性和涂敷性，并且本发明所述涂料能够使取向电磁钢板表面涂层具有良好的耐吸湿性、耐腐蚀性、耐热性、张力效果和抗粘片性。

一种提高有效氮和底层质量的高磁感取向硅钢制造方法：冶炼后连铸成坯；对铸坯加热；热轧、常化及酸洗后时效冷轧；在湿式气氛下脱碳退火；在湿式混合气氛下均热；在湿式混合气氛下渗氮退火；进行后工序。本发明与现有技术相比，通过合理控制渗氮过程，提高渗氮后钢板基体内氮含量与总氮量之间的比例达到80%以上，使无点状露晶产生，最终获得产品的底层质量优异。

本发明属于酸洗设备技术领域，具体涉及一种硅钢生产用酸洗设备，包括酸洗池、放卷机构和收卷机构，酸洗池被依次分隔为第一酸洗腔、第二酸洗腔、浸泡腔和喷洗腔；第一酸洗腔和第二酸洗腔内滑动连接有刷洗架，浸泡腔内滑动连接有定位架，喷洗腔内滑动连接有喷洗架；刷洗架、定位架和喷洗架上均转动连接有多根转辊，转辊上设有刷毛；刷洗架和喷洗架上设有用于驱动转辊转动的驱动件；喷洗架上的转辊开有空腔和多个与空腔连通的喷孔，喷洗架上开有与空腔连通的通道和与通道连通的进水口；喷洗腔的底部和侧壁设有多个喷头；酸洗池内转动连接有多根位于第一隔墙上方的刷辊。在本方案，通过酸洗以及充分的刷洗，能够充分有效的除去硅钢表面的氧化皮。

【作者】 杨得草； ...

通过观察冲剪边缘组织,测量冲剪边缘的显微硬度、残余应力的分布情况和磁性能的变化研究了冲剪加工对无取向硅钢50WW800边缘组织和磁性能的影响。对冲剪后硅钢片进行750℃退火,分析退火对组织和磁性能的影响。结果表明,硅钢片剪切边缘会存在0.4 mm的形变硬化层,边缘应力大,铁损增加。退火后变形减小,形变硬化层变小,残余应力大幅度减少,铁损减少。 The influence of punching process on cutting edge microstructure and magnetic properties of non-oriented silicon steel 50WW800was studied by observing microstructure and measuring microhardness near cutting edge.The residual stress distribution in the silicon steel tooth and magnetic properties were measured.Effect of annealing at 750 ℃ on microstructure and magnetic properties of the silicon steel was analyzed.The results show that a cut-edge hardening layer up to 0.4 mm is observed,residual st... 

【摘要】 <正>为了确保电工钢的产品质量,在生产线...

本发明揭示了一种高牌号无取向硅钢及其生产方法。所述无取向硅钢的化学成分以质量百分比计包含：C:0.002～0.004％，S≤0.003％，Si:1.4～1.7％，Mn:0.7～0.95％，P≤0.03％，Sn:0.015～0.035％，11×([Si]‑1.4％)＝14×([Mn]‑0.7％)。所述无取向硅钢的生产方法中，连铸坯加热温度1120～1150℃，精轧终轧温度为890±15℃，最后一道次精轧的压下量≥30％且最后两道次精轧的总压下量≥50％，卷取温度650±20℃；在酸连轧之前不需要进行常化处理，且所得无取向硅钢的磁性能佳，表面无瓦楞缺陷，满足低成本高牌号无取向硅钢的需求。

本申请提供一种电工钢及其制备方法，制备方法包括：将电工钢的板坯进行热轧获得钢卷；将热轧后的钢卷进行酸洗冷轧；将酸洗冷轧后的钢卷进行第一次罩式退火；将第一次罩式退火后的钢卷进行平整；将平整后的钢卷进行第二次罩式退火；将第二次罩式退火后的钢卷进行重卷，以获得电工钢。本申请提供的电工钢的制备方法采用两次罩式退火，退火的主要目的是消除酸洗冷轧工序产生的加工硬化，使钢板充分再结晶，获得理想的铁损及磁感应强度。而采用两次罩式退火，相对于一次罩式退火工序来说，能够进一步降低铁损，提高电工钢的磁性能。

一种增大压下率的电工钢冷轧装置及冷轧方法，属于电工钢冷轧技术领域，该电工钢冷轧装置，包括单机架可逆轧机，单机架可逆轧机的两侧均设置有电磁感应加热装置和氮气风冷装置，氮气风冷装置靠近单机架可逆轧机的轧制进口或入口设置，本发明的有益效果是，本发明通过在单机架可逆轧机两侧增设电磁感应加热装置和氮气风冷装置，对每道次轧制过程中可在线调节电磁感应加热温度，实现了边去应力退火边轧制，保证了正常的轧制工作，达到了高效轧制更薄规格电工钢产品的目的和消化生产CSP热轧超厚过渡坯的目的。

以能量平衡和辐射换热理论为基础,通过合理假定,建立了硅钢无氧化加热炉数学模型。采用数值计算的方法,通过自编程序,完成对带钢加热过程温度场的仿真。结果显示:数学模型能够反映带钢在无氧化炉内的加热过程,其升温曲线能够与工艺曲线相吻合;现行炉温分布并非最优,数学模型能够为炉温分布的优化、炉段的设计提供理论依据。 Mathematical model of NOF Section of Continuous Annealing Furnace is established based on energy balance and radiation heat exchange. The temperature field of steel is simulated by mathematical computation. The simulating results show that the mathematical model can reflect the heating process of silicon steel in NOF section, and the heat-up curve is coincide with the processing curve. From the results,it is known that the current furnace temperature gradient is not the best, and the mathematica...