硅钢资料

硅钢连续退火线是无取向硅钢生产的成品线。由于受机组布置的影响,带钢经转向辊进出口活套后,当套量达到60%后就出现偏离生产线的情况,从而影响最终产品的质量及成材率,甚至损坏设备。针对某冷轧厂硅钢连续退火机组出口活套入口处带钢跑偏开展纠偏研究,利用Matlab对该纠偏系统进行动态仿真研究,分析系统的稳定性。 Silicon steel continuous annealing line is non oriented silicon steel production of finished product line.Due to the influence of unit layout,strip by roll Import & Export loop,when the set volume reached 60% after the emergence of deviation from the production line,thus affecting the quality of the final product and the rate of finished products,and even damage the equipment.For the export of continuous annealing line in cold rolling silicon steel strip deviation rectification loop at the e... 

本发明公开了一种硅钢冷轧吹扫辊，涉及硅钢加工设备领域，包括安装架、上轧辊和下轧辊、下调节机构、上调节机构以及吹扫机构；所述下调节机构包括调节支撑底板、楔形插块以及调节油缸；所述上调节机构包括顶升油缸、顶升杠杆和顶升连杆；所述吹扫机构包括吹扫连接座、吹扫管道和吹扫排管。本发明通过在上轧辊和下轧辊的出料端安装吹扫机构能够便于对出料的钢带表面进行吹扫清洁，能够有效提升钢带成品的表面质量；由于下轧辊在轧制过程中承受的重量较大，通过调节油缸带动下轧辊两侧的楔形插块来回移动的方式对下轧辊的高度进行微调，能够保证下轧辊在轧制过程中整体的稳定可靠性。

本实用新型涉及一种摩托车点火器线圈用硅钢片，包括E型件和I型件，所述E型件和I型件可组合成日字形；所述E型件包括竖边和设置在竖边三个横边，所述竖边与三个横边接触的位置设置孔眼；所述孔眼内径从为变径结构；位于E型件正面设置散热线槽，所述散热线槽一端与孔眼贯通，另一端指向凸部；位于E型件背面在散热线槽正对位置设置外凸线，所述I型件一侧设置与凸部匹配的凹部，在所述凹部之间凸台；所述凸台与凹台重叠；在凸台与凹部之间设置凸棱，所述凸棱位于I型件外侧。本实用新型设计新颖，改进巧妙，由于E型件具有弧形边可以有利于拾取，方便工作操作，同时采用采用接触的方式接触，增加了组合体的稳定性。

通过热力学计算,分析了实验钢中主要析出物析出的可能性。结果表明:在液相和固液两相区中,AlN和MnS均不能析出;在奥氏体区,AlN和MnS具备热力学析出条件,平衡析出温度分别为1547、1582 K。成品退火板中的析出物主要为AlN和MnS。扫描电镜下观察到的AlN形貌多为长条状,MnS形貌多为棒状或近似球形。这两种析出物占了析出物总量的85%以上,尺寸集中分布在400~800nm;复合析出物主要是(Al2O3+MnS)和(AlN+MnS),形貌不规则,尺寸集中在0.7~1.5μm;透射电镜下观察到了少量100nm以下独立的AlN析出。 According to thermodynamic calculation, the precipitation probability of precipitates was analyzed, AlN and MnS can not precipitate in liquid phase area and solid-liquid two-phase area. In austenite area, both the AlN and MnS have precipitation condition in thermodynamics and precipitates at 1547 K and 1582 K, respectively. The precipitates in annealing plate are mainly AlN and MnS. The shape of AlN is mostly strip, and MnS is stick or near sphericity. They accounted for over 85% of the total qu... 

一种高磁感低铁损取向硅钢生产用修复装置，包括：工作台，工作台上方设有放置板，放置板两端均设有L形夹板，放置板两侧位于两个L形夹板相对位置均开设有驱动槽，两个驱动槽内底部均水平设有一号螺杆，本实用新型具有以下优点：通过一号电机带动一号螺杆进行转动，使两个L形夹板相互靠近，便于对放置板上的取向硅钢片进行夹持固定，提高其修复过程的稳定性，避免其修复过程中发生移动；通过风机组将修复过程中产生的残渣吹至收集口，并落入收集箱内，提高工作台表面的清洁度；通过电动滑轨以及二号电机带动二号螺杆进行转动，便于使修复装置主体对准取向硅钢片修复部位，降低时间和劳动力的消耗，提高工作效率。

在现普通冷轧无取向硅钢的基础上,降低Si含量,复合添加少量辅助元素,组合热轧板处理和成品退火加热技术,研制出了免常化处理的高磁感、低铁损并具有良好耐酸腐蚀性能的新系列无取向电工钢。 Based on existing common cold rolled non-oriented silicon steel,a new series of non-orientedelectrical steel with high induction,low core loss and excellent anti-corrosion property has been developed by reducing Si element,adding complexly a small amount of supplementary elements,and employing combined treatment of hot rolled sheet and finished product annealed heated technology. 

根据新日铁、JFE及浦项等国外钢铁公司2008年以来在日本专利局、欧洲专利局(EP)及世界知识产权组织(WIPO)申请公开的有关生产Hi-B取向电工钢典型专利技术,概述了近年来国外大型钢铁企业采用低温板坯加热(坯加热温度<1 280℃)技术生产Hi-B取向电工钢主要技术重点,即将调节关键化学成分Al、N、Sn及Sb等与工艺改进相结合。最后介绍了国外大型钢铁企业采用低温板坯加热技术生产Hi-B取向电工钢实例。 The latest developments on technology for manufacturing Hi-B grain oriented electrical steel sheets developed by Nippon Steel Corp.,JFE Steel and POSCO were described according to the patents published by World Intellectual Property Organization,Japan Patent Office and European Patent Office over the recent years.The low temperature slab heating process(particularly slab-heating temperature<1 280 ℃) together with suitably adjusting key chemical elements such as Al,N,Sn and Sb elements was the... 

本发明属于金属材料加工技术领域，具体涉及取向硅钢罩式炉高温退火低保温阶段节能工艺，包括：1)将涂镁取向硅钢卷装入密闭的罩式炉中，并向罩式炉内通入氮气将炉内氧气充分排出，使炉内氧含量浓度≤300PPm；2)通电升温并将氮气转换为10m3/h氮气与氨分解气的混合气体，升温2h将温度升温至500‑600℃后，恒温13h；3)将温度氮气与氨分解气的混合气体转换为12m3/h氨分解气，并升温2h将温度升至650℃恒温15h，使内部气体露点小于‑10℃；本发明提供退火工艺，钢卷在高温下不被水蒸汽氧化，消除钢带表面露金、发红、发黑、水印、色泽不均、导通缺陷，降低钢带铁损、提高磁感、降低生产成本。此外，本发明进一步减少退火过程中氨分解气的用量，具有极高的工业应用价值。

涂层技术在高磁感取向硅钢生产中起着重要的作用.根据生产实践,介绍了高磁感取向硅钢生产中涂层的种类和作用、涂料的成分和对产品性能的影响、涂层工艺质量控制要点和检验方法等,并提出了通过优化涂层工艺改善高磁感取向硅钢性能和外观质量的方法. Surface coating technique plays an important role in producing high magnetic inductivity grain-oriented silicon steel.Based on production practice,this paper describes the types and function of the coating,the composition of the coating and its effect on the product performance,the quality control and inspection method for the coatings,as well as proposes ways to improve the magnetic property and surface quality of the steel by optimizing the coating process. 

本实用新型公开了一种取向硅钢绝缘涂液用废液回收利用装置，涉及取向硅钢绝缘涂液技术领域，为解决现有取向硅钢绝缘涂液的废液在回收时没有进行多层热分解，导致回收利用率低的问题。所述下料筒的下端设置有调节筒，所述调节筒的下端设置有分流筒，所述分流筒的下端设置有出料筒，所述调节筒的内部设置有下料板，所述下料板的一端设置有转轴，所述转轴的一端设置有交流电机，所述下料板的侧表面设置有外接孔，所述下料筒的筒壁内设置有加热板，所述下料筒的内部设置有一级过滤网，所述分流筒的内部设置有隔挡板，所述隔挡板的一侧设置有二级过滤网。

本发明涉及一种硅钢片纵剪边料收卷装置，包括：用于将收卷装置固定于地面的机架底座，机架底座一端设置固定支架，固定支架上安装电动定尺收料盘；在机架底座上设置电动可移动支架，电动可移动支架在机架底座的长方向上相对固定支架移动，电动可移动支架上安装电动可调收料盘；电动可移动支架、电动定尺收料盘、电动可调收料盘与PLC控制系统连接，PLC控制系统用于控制电动可移动支架的移动距离、以及控制电动定尺收料盘和电动可调收料盘的收料速度。本发明还涉及一种硅钢片纵剪边料收卷方法。将本发明的收卷装置安装在硅钢片滚剪线切刀后面的输送平台下部，卧式布局，不占用外部空间，和滚剪线无缝集成在一起，自动完成硅钢片纵剪边料收卷工作。

本发明公开了一种高磁感取向硅钢高效脱碳退火工艺，主要工艺流程为：炼钢连铸→热轧→酸洗常化→冷轧→脱碳和初次再结晶退火→渗氮处理(低温Hi‑B)→涂覆氧化镁隔离剂→高温退火→拉伸平整退火→涂覆绝缘涂层→精整，低温HiB不同于高温Hi‑B的工艺流程主要是在脱碳退火后增加了渗氮段。本发明在保证产品实物质量不低于现有水平(国内领先水平)的前提下，使Hi‑B钢退火效率达到世界领先，制造成本大幅降低。