硅钢资料

本实用新型公开了一种变压器硅钢片剪切收料装置，其包括底板和存放架推出机构，底板的前侧中部设置有用于放置外设剪切设备的放置区；存放架推出机构包括滑动板座、锁紧组件，滑动板座可左右滑动地安装于底板的上表面，在滑动板的上表面设置有两个用于放置外设的硅钢片存放架的存放架放置槽，两个存放架放置槽呈左右间隔设置，锁紧组件用于锁紧滑动板座与底板之间的相对位置。当该硅钢片存放架存放完后，将滑动板座推动至使得另外一个存放架放置槽设置于放置区的正后方，另外的硅钢片存放架继续接受剪切设备掉落的硅钢片体，可连续地实现硅钢片体的落料存放，令转运和落料的操作不相互干涉，提高生产的效率。

针对马钢无取向电工钢孔洞缺陷的分布规律及形貌特征,对缺陷样进行了显微分析,并利用生产实绩数据分析了该缺陷产生的原因。结合热轧生产过程,主要通过避免带钢撞击导卫以及降低导卫结瘤的产生等措施,可有效抑制热卷异物压入产生,从而降低冷轧工序孔洞的产生。 In viewing of the distribution and morphology characteristics of the hole defect of non-oriented electrical steel in Maanshan Iron and Steel Co.,Ltd.,the causes of the defect were analyzed by micro analysis of the defect sample and the production data.Combined with the production process of hot rolling,by avoiding the impact of strip steel on the guide and reducing the nodule formation on the guide,the pressing of foreign bodies in hot coiling could be effectively suppressed,thus reducing the fo... 

采用磁控溅射方法,分别在纯Fe以及低硅钢基片上沉积富Si膜,并对其进行真空扩散热处理.通过能谱分析及X射线衍射研究了Si在纯Fe与低硅钢基体中的扩散特征,运用DICTRA软件建立了扩散模型.研究发现Si在纯Fe基体中扩散时发生γ-Fe(Si)→α-Fe(Si)相转变,扩散速率受控于相界面的迁移.当沿截面Si含量梯度不足以驱动相界面正向迁移时,延长扩散时间会发生相界面回迁现象,最终趋于单一相内均匀化扩散过程.Si在低硅钢基体中的扩散符合Fick扩散第二定律. Si-rich films were deposited on pure iron and low-Si steel substrates by direct current magnetron sputtering,and then were subjected to vacuum annealing.The distribution characteristics of Si across Fe and low-Si steel substrates were studied by energy spectrum analysis(EDS) and X-ray diffraction(XRD).DICTRA software was used to simulate the diffusion models.It is found that the diffusion behavior of Si in the Fe substrate is from γ-Fe(Si) phase to α-Fe(Si) phase and the rate of diffusion is con... 

利用电子探针面分析、状态分析及电子背散射衍射相分析技术研究硅钢高温氧化铁皮的显微结构。电子探针面分析可以直观的看出元素的分布状态,初步判断氧化铁皮的结构,而状态分析可以准确表征常规氧化铁皮中铁元素的状态,对于合金元素富集区域则通过电子背散射衍射相分析技术来标定。结果表明,高温氧化铁皮的结构主要有4层,即最外层为厚度约为10μm的Fe2O3相,次外层为Fe3O4相,中间层为FeO相上分布有颗粒状的Fe3O4相,最内层为FeO相和Si元素富集的Fe2SiO4相。其中Fe2SiO4层的分布特征与加热温度密切相关:1 100℃时,Fe2SiO4相呈颗粒状,弥散分布在FeO层;1 200℃时,Fe2SiO4相呈液态,侵入基体和疏松的FeO层,且沿着FeO晶界呈网状分布。 The microstructure of high temperature oxide scale on silicon steel was characterized by electron probe microanalyzer(EPMA)mapping analysis,state analysis and electron backscatter diffraction(EBSD)phase analysis.The element distribution and the initial structure of the oxide scale could be detected by EPMA mapping analysis apparently.And the state of iron in the conventional oxide scales could be determined by state analysis.Meanwhile,the alloy-rich region could be identified by EBSD phase analy... 

本发明公开了一种用于测量电工钢片的二维磁性能的系统及方法，所述系统通过将承载待测样品的托盘与旋转机构连接，在测量各个角度的二维磁性能时只需控制旋转机构驱动待测样品转动，旋转机构的负载很小，旋转机构的制作较为简单。而且，励磁测量线圈是绕制在托盘的外围，而不是在磁轭上，这样使得待测样品相当于处于一个均匀的螺线管中，磁场更加均匀，保证了磁场测量的准确性，并且励磁源不需要像RSST一样要保证两路励磁机构的相位差的准确度，从而使得励磁源的制作更加简单，降低了制作的成本和门槛。同时，不需要对待测样品打孔来绕制线圈，待测样品无破坏，可以保证待测样品的完整性以及数据的重复性和可对比性，测量结果更可靠。

应用CAFE法对6.5%Si高硅钢铸锭凝固组织进行了模拟研究,确定出了适合高硅钢组织模拟的模型。进一步用该模型研究了过热度及冷却条件对凝固组织的影响,结果表明,随着过热度的降低,凝固组织中柱状晶比例和晶粒平均面积均减小。水冷条件下,高硅钢铸锭凝固组织几乎全是柱状晶,而且晶粒粗大。空冷条件下,等轴晶区扩大,但柱状晶仍占主要部分。缓冷条件下,等轴晶区占主要部分,晶粒平均面积和空冷条件下相当。 The solidification structure of 6. 5% Si steel ingot was simulated based on CAFE method and the model suitable for simulating the structure of high silicon steel wad ascertained. The influence of superheat and cooling condition on the solidification structure were studied. It was shown that with the superheat decreasing,the proportion of columnar crystals decrease,and the average grain size become smaller. Under water cooling condition,the solidification structure of casting was composed of almo... 

抑制回硅是低硅品种钢冶炼的重点和难点,南钢中厚板卷厂通过转炉出钢弱脱氧操作,精炼炉弱脱氧升温,脱氧、脱硫造渣,连铸严格的保护浇注及吹氩塞棒、吹氩浸入式上水口的应用等一系列工艺优化和操作的改进,使整个冶炼过程钢水回硅量稳定控制在200×10-6以内,钢水终点成分完全满足低硅钢要求。 Control of increasing silicon is the emphasis and difficulty in low silicon varieties steel smelting.The Nisco Wide Plate/Coil Plant can control the silicon content in molten steel keeping within 200×10-6 through whole steelmaking process by using oxygen residual operation in converter tapping,oxygen residual and increasing temperature,deoxidation,desulfurization,slag refining,protection cast,blowing argon by plugged nozzle,blowing argon by submerged entry nozzle in continuous casting,and other ... 

采用双辊薄带连铸工艺试制了2.6 mm厚5.28%Si-1.11%Al高硅钢薄带,对比了1050℃×5 min正火及不正火铸带280℃冷轧至0.5 mm后,再经900～1100℃退火的磁性能。结果表明,高硅钢铸带显微组织为等轴晶组织,正火后铸带边部晶粒长大,中心层晶粒变化较小。成品中析出物主要为较粗大的AlN和AlN+MnS复合析出物,尺寸为0.5～2.5μm。与不正火试样相比,正火试样成品铁损大幅降低,磁感小幅下降;随退火温度的升高,两种工艺下铁损和磁感都是先降低后升高,在1050℃出现最低值。 2.6 mm thickness 5.28% Si-1.11% Al non-oriented high silicon steel was produced by twin roll thin strip casting.Magnetic property of the strip un-normalized and normalized at 1050 ℃×5 min was contrasted after cold rolled to 0.5 mm at 280 ℃ and 900-1100 ℃ final annealing.The results show that microstructure of the strip is equiaxed crystal.The surface grain is coarsened and the center layer grain has little change of the normalized strip.The main precipitates are AlN and MnS+AlN with 0.5-2.5 μm s... 

本发明特别涉及一种控制边部质量的低牌号无取向硅钢的热轧生产方法，属于无取向硅钢热轧生产技术领域，方法包括：将低牌号无取向硅钢的板坯进行第一次粗轧，将第一次粗轧后的板坯进行第二次粗轧，其中，在第二次粗轧机前的立辊上设置立辊润滑装置，所述立辊润滑装置向所述立辊供给的润滑油的油量为100mL/min‑400mL/min；将第二次粗轧后的板坯进行精除鳞、精轧和卷取，获得边部质量合格的热轧卷；保证良好的立辊辊面状态，可有效解决边部粗糙，有效解决了低牌号无取向硅钢边部粗糙状态，极大的提高了冷轧后工序毛边轧制率，提高了硅钢全工序成材率。

以能量平衡和辐射换热理论为基础,通过合理假定,建立了硅钢无氧化加热炉数学模型。采用数值计算的方法,通过自编程序,完成对带钢加热过程温度场的仿真。结果显示:数学模型能够反映带钢在无氧化炉内的加热过程,其升温曲线能够与工艺曲线相吻合;现行炉温分布并非最优,数学模型能够为炉温分布的优化、炉段的设计提供理论依据。 Mathematical model of NOF Section of Continuous Annealing Furnace is established based on energy balance and radiation heat exchange. The temperature field of steel is simulated by mathematical computation. The simulating results show that the mathematical model can reflect the heating process of silicon steel in NOF section, and the heat-up curve is coincide with the processing curve. From the results,it is known that the current furnace temperature gradient is not the best, and the mathematica... 

本发明提供一种优化无取向硅钢连续退火工艺的铁损预测方法，步骤包括：S1.建立预测模型回归方程表达式；S2.将无取向硅钢中的硅、锰、铝质量含量及预设的退火速度、退火温度代入S1中的回归方程表达式中进行计算；S3.将步骤S2计算得到的预测值与目标值进行比较，如果预测值在目标值的允许误差范围内，则按照预设的退火速度、退火温度进行生产；否则对预设的退火速度、退火温度进行调整，直至预测值能够达到目标值的要求后再进行生产。本发明提供的模型能够提高产品质量，对优化无取向硅钢连续退火工艺具有指导意义。

本实用新型公开了一种用于电机生产的硅钢片放料机构，包括用于传输硅钢片的传送机构和用于堆叠的放料机构以及用于旋转位移的旋转机构，所述传送机构出料端设置有所述放料机构，所述放料机构安装在所述旋转机构上端，所述放料机构下侧设置有推动机构。本实用新型利用传送机构、放料机构配合，保证了硅钢片的传输效果和放料效果，从而保证了硅钢片在放料堆叠过程的稳定性和安全性，提高加工效率，利用放料机构、推动机构配合，在后期放料堆叠后能够快速进行捆扎和运输。