取向硅钢热轧板中组织、织构梯度对发展完善的二次再结晶十分关键,通过对2种不同热轧工艺生产取向硅钢的组织、织构进行研究,结果表明:采用后道次大压下热轧工艺时热轧板表层再结区晶粒平均尺寸增加,再结晶区厚度增加,高温退火后二次晶粒尺寸减小;采用后道次大压下热轧工艺热轧时,热轧板中平均等效应变高,热轧板厚度心部{100}〈011〉和{100}〈001〉位向取向强度降低,({111}～{113})〈110〉位向取向强度提高,高温退火后{110}〈001〉位向偏离角降低,磁性能提高。 The texture and microstructure gradient in hot rolled grain oriented silicon steel strip was one of the essential factors to achieve a perfect secondary recrystallization.The texture and microstructure of grain oriented silicon steel strip as-rolled with two different hot rolling parameters was investigated.The results show that with big reduction at the end rolling process,the intensity of {100}〈011〉 and {100}〈001〉 orientation reduces with({111}-{113})〈110〉 orientation intensity enhanced in hot... 

本实用新型公开了一种用于变压器硅钢片加工的剪切装置，属于变压器生产设备技术领域，包括工作台，所述工作台的侧壁处固接有侧板，侧板的侧壁上固接有固定板一和固定板二，固定板一上安装有电机，电机的输出轴与旋转轴一的一端固接，旋转轴一靠近电机一端的外侧壁上固接有不完全齿轮一，不完全齿轮一与柱齿轮一相啮合，柱齿轮一固接在旋转轴二的一端处；可进行持续剪切工作，切刀旋转进行剪切工作，需要的剪切力更小，同时不易容易损伤切刀和硅钢片，自动化程度高，能满足硅钢片的大批量生产需求，在对硅钢片进行传送时，受到挡板的两侧限位作用，从而确保硅钢片不易发生倾斜，确保硅钢片的成品质量。

试验研究了退火温度(850~950℃)和时间(5~18 min)对2.3 mm热轧硅钢板(/%:0.036C,3.15Si,0.21Mn,0.005P,0.007S,0.032A1)6道次轧制的0.35 mm冷轧板组织和织构的影响。结果表明,退火温度越高,晶粒平均尺寸越大,900℃5 min退火时平均晶粒尺寸41.39μm,试样织构主要集中在γ取向线上的{111}<112>织构组分和{111}<110>织构组分;900℃18 min退火时平均晶粒尺寸为48.08μm,试样的{111}面织构和{112}面织构密度都明显减弱,{001}面织构增强,磁性能较优。 The effect of annealing temperature(850 ~950 ℃) and holding time(5 ~ 18 min) on structure and texture of 0.35 mm sheet by 6 passes cold-rolling from 2.3 mm hot-rolled plate of silicon steel(/%:0.036 C,3.15 Si,0.21 Mn,0.005 P,0.007 S,0.032A1) has been tested and studied.Results show that the higher the annealing temperature the coarser the average grain size;As annealing at 900 ℃ for 5 min the average grain size of steel sheet is 41.39 μm,and the texture in sample is mainly concentrated in y orie... 

对熔融态钢液进行处理,研究了电脉冲对于取向硅钢凝固组织的影响作用,利用正交试验法研究了脉冲电容、频率、处理时间和电压等脉冲参数的作用效果。结果表明:电脉冲对钢锭晶粒组织具有明显的细化作用,凝固组织的等轴晶比例大幅上升,影响等轴晶比例的最显著性因素为脉冲频率,最优正交试验参数为电容1 200μF,脉冲频率1 Hz,处理时间5 s,脉冲电压800 V。随着输入能量的增大等轴晶率先增大后减小,脉冲输入能量为某值时,等轴晶率最大,利用经典形核理论和热力学对这一现象进行了解释。 The influence of electric pulse on the solidification structure of oriented silicon steel was investigated by applying electric pulse in molten steel.The affection due to different electric pulse parameters such as electric capacity,frequency,applied time and voltage was studied by orthogonal design test.The result showed that solidification structure of oriented silicon steel could be improved by the electric pulse,and the equiaxed crystal ratio increased obviously.The most influential paramete... 

本实用新型公开了一种电工钢自粘涂层液生产用搅拌釜，包括釜体，釜体的内部通过两个第一隔板分隔成第一安装腔、第二安装腔和搅拌腔，釜体的内部设有传动组件，传动组件包括伺服电机、主动轴和两个从动轴，伺服电机固定安装在釜体顶端的中部，伺服电机的输出轴与主动轴的顶端固定连接，本实用新型的有益效果是：通过设有八个与十二个搅拌叶片相交错的挡板，避免搅拌轴在搅拌过程中产生离心力造成漩涡，使自粘内外侧的涂层液得到充分搅拌，通过设有循环泵机、第二隔板和流通槽使搅拌釜内的自粘涂层液处于流通的状态，使底部不易被搅拌的涂层液能够得到充分搅拌，在提高搅拌釜的灵活性的同时，保留其原有的稳定性。

以试验室模拟CSP工艺生产的Fe-3Si热轧钢带为研究对象,采用正交试验及方差分析的方法,研究了取向硅钢初次再结晶退火工艺对高温退火后获得锋锐的高斯织构的影响。结果表明:取向硅钢两段式初次再结晶脱碳退火工艺参数加热段保温时间及加热温度是高温退火后获得锋锐高斯织构的主要影响因素,其可信度分别在90%和85%以上;在本试验条件下,通过正交试验获得的最佳退火工艺为:冷硬板经600℃保温3 min和850℃保温6 min。 Fe-3Si hot rolled strip was produced by simulating CSP technology in the laboratory.Orthogonal experiment and analysis of variance were carried out to investigate the influence of primary recrystallization on the sharp Goss texture of the oriented silicon steel.The results show that holding time of the heating section and the heating temperature for a sharp Goss texture of the samples annealed has important implications in this experiment conditions,the two-step decarburization annealing process... 

利用本钢技术中心试验厂技术手段,并与北京钢铁研究院合作,试制了用作家电用电机、微电机、小电机或部分中型电机铁芯的冷轧无取向电工钢。试制钢硅含量小于0.5%,钢板表面平滑,公称厚度0.5mm,且厚度均匀偏差小,性能测定结果表明,产品的磁性能、力学性能满足其使用要求。 BX STEELTechnology Center pilot plant using technical means,and with Beijing Iron and Steel Research Institute,trial cold rolled non-oriented electrical steel that has been used as appliance motor core,micro motor core,small motor core,or part of the medium-sized motor core。Trial steel of silicon content is less than 0.5%,steel plate surface is smooth,the nominal thickness of 0.5mm,and the thickness deviation is small,performance measurement results show that the magnetic properties,mechanical p... 

本发明公开了一种低牌号无取向电工钢的制造方法，包括：在炼钢时，增加所述低牌号无取向电工钢的板坯的铝元素含量，增加量按重量百分比计为0.08％～0.12％；在热轧板坯加热时，控制所述板坯的出炉温度为1150℃～1200℃；在热轧粗轧时，控制所述板坯的粗轧RT2温度为1000～1050℃；上述方法通过提高铝含量，以升高低牌号无取向电工钢的相转变温度，再结合板坯的出炉温度控制和粗轧RT2温度控制，保证低牌号无取向电工钢在精轧过程中不会因为相变区轧制而产生轧制力波动，从而稳定精轧轧制过程，提高精轧后低牌号无取向电工钢板卷的尺寸和板型精度。

西安重型机械研究所为武钢开发了目前国内第一台自动化水平较高的先进可靠的硅钢热轧试验轧机。本文介绍了该轧机的工艺参数、设备组成,技术特点及轧制流程,该轧机在规定的终轧温度范围内,实现了2.5 m/s的快速轧制速度,保证了控制系统准确及时的采集到轧件进出轧辊时的信号,缩短道次间隙时间,实现了自动控制,保证了产品板形及精度的高水平要求,对于硅钢尤其是对其取向硅钢新产品、新工艺的开发具有深远意义。 An experimental prototype of 400 mm silicon steel hot rolling mill was developed by Xi’an Heavy Machinery Research Institue for Wu Gang.The technological parameters,configuration and characteristic of advanced control system in the experimental prototype are introduced in detail.The experimental prototype was realized the fast rolling of 2.5 m/s in the range of specified rolling temperature.Its automatic rolling control system can acquisite the signals that a rolled piece enters in and exits fro... 

6.5%Si电工钢是一种优异的软磁材料,织构对其磁性能影响很大。利用温轧工艺对6.5%Si电工钢热轧板进行不同压下率轧制,研究了温轧板织构随压下率的变化规律。实验结果显示,随着压下率的增大,{100}〈110〉、{110}〈100〉和γ纤维织构在薄板表层中的强度先增强后减弱,当压下率达到75%时,沿板厚方向形成3个组织区域:表层细晶粒区({110}〈100〉取向为主)、过渡层({111}〈110〉和{111}〈112〉变形晶粒区)和中心层(以拉长的γ纤维织构和{100}〈110〉取向晶粒为主),这种组织和织构不均性对后期织构的发展有重大影响。 6.5wt% Si electric steel has excellent soft magnetic properties,on which texture play important role.In this experiment,warm rolling technique was employed to investigate the effect of rolling reduction on texture.It was found that the density of {100}〈110〉,{110}〈100〉 and γ-fiber textures first increased and then decreased with increasing of the rolling reduction.At 75% reduction,the microstructure along the thickness of the sheet formed three zones,containing surface layer with {110}〈100〉 orien... 

本发明公开一种高牌号无取向硅钢的轧制方法，用于控制森基米尔二十辊轧机对原料带钢进行轧制，所述方法包括：根据所述原料带钢的规格参数，确定所述森基米尔二十辊轧机的第一中间辊的辊型及第二中间辊的辊型；根据所述原料带钢的合金含量及所述规格参数，确定所述第一中间辊的有效平面量；根据所述规格参数，确定所述森基米尔二十辊轧机的径向调整机构的凸度值；根据所述合金含量，设定所述森基米尔二十辊轧机进行轧制时的负荷分配和张力；按照所设定的负荷分配和张力分配对所述原料带钢进行轧制，且在轧制过程中以预设乳化液流量进行喷淋，以制得成品。本发明可减少高牌号无取向硅钢在轧制过程中发生脆性断裂，提高轧制的稳定性及生产效率。