硅钢资料

根据本发明的一个实施例的无取向电工钢板，以重量％计，所述钢板包含Si：1.5％以下、C：0.01％以下且0％除外、Mn：0.03至3％、P：0.01至0.2％、S：0.001至0.02％、Al：0.01％以下且0％除外、N：0.005％以下且0％除外、和Cu：0.02至0.3％，Ca和Mg各自单独或以合计含量包含0.0001至0.005重量％，Sb和Sn各自单独或以合计含量包含0.001至0.2重量％，余量包含Fe和不可避免的杂质。

采用铸坯低倍组织检验和化学分析的方法,研究板坯连铸机二冷区电磁搅拌器电流和频率参数对无取向电工钢XG800WR板坯中心偏析和等轴晶率的影响,结果表明:铸坯等轴晶率随着搅拌器电流强度和电流频率的增大而增加。采用二冷区电磁搅拌可减小中心易偏析元素S的偏析,试验得出:减小铸坯S偏析效果最好的电磁搅拌参数为电流380～400A,频率6Hz。 The effect of electromagnetic stirring current and frequency parameter at secondary cooling area on the central segregation and equiaxed crystal ratio of XG800WR non - oriented electrical steels slab was investigated through the methods of chemical and macrostructure analysis.The results shows that the rate of equiaxed crystal zone is going up with increasing of current intensity and current frequency.Electromagnetic stirring in the secondary cooling area can be easily reduced segregation caused... 

介绍了电工钢生产线连退机组的表面处理工艺,特别是电解清洗系统的工作机理、设备构造、生产工艺及各种影响因素。 This paper introduces the technology of surface treatment of continuous annealing unit in electrical steel production line,in particular the working mechanism,structure of equipment,production techniques and various influence factors of the electrolytic cleaning system. 

本发明涉及金属冶炼工艺，尤其是一种降低无取向硅钢W800冶炼成本的方法，开吹阶段，着火后，加入头批渣料，石灰加入量占石灰总加入量的70%，石灰石加入量占石灰石总加入总量的100%，轻烧白云石加入量占轻烧白云石总加入总量的100%，待化渣后，枪位降低；化渣后将剩余30%石灰加入，加入剩余石灰过程中利用矿石调整温度；吹炼后期，并逐步压枪，终点拉碳枪位至1.4m，并使枪位在此高度不少于30s；到达冶炼终点。本工艺通过降低转炉渣量、提碳降氧和提高终点温度来减少铁水锰氧化量和促进氧化锰还原量，进而降低RH金属锰加入量，降低生产成本。

本实用新型公开了一种硅钢板带运输使用的固定设备，所述壳体的侧壁固定连接有多个第一放置轴，所述壳体的侧壁固定连接有多个第一限位套，且第一限位套与第一放置轴同轴心，所述第一限位套的内部设置有第一压板，所述壳体的内部设置有第一滑槽及第二滑槽，所述壳体的一侧设置有滑板。本实用新型通过将硅钢板带卷起后用绑线绑紧后，放入第一放置轴外表面后推入第一限位套内部，放好一行成硅钢板带后将将第一个滑板底部的滑杆放入第一滑槽内，推动滑板进入壳体内，使插杆插入凹槽内，再对下一列的硅钢板带进行放置，安装完成后，将挡板放入第二滑槽内，推动滑板向壳体内移动，将挡板向壳体内移动。

针对采用含钒铁水生产无取向电工钢存在的铁水脱硫率低、转炉冶炼过程回硫量大、成品硫含量偏高的问题,通过对含钒钛铁水脱硫,减少转炉冶炼过程回硫以及RH脱硫技术等方面的研究,大幅度降低了电工钢成品硫含量。生产表明钢中w(S)=0.001 9%～0.006 9%,平均为0.004 2%;w(S)≤0.008%的比例达到了100%,且w(S)≤0.005%的比例也达到了91.43%。 In cognizance of the problems of low desulphurization rate for hot metal,large sulfur-recovery in converter as well as high sulfur content in products in producing non-orientation electrical steel with vanadium-content hot metal countermeasures have been carried out.Sulfur content in non-orientation electrical steel is decreased obviously by way of study on technologies of desulphurization for hot metal with vanadium & titanium,sulfur-recovery control in converter and desulphurization in RH ... 

通过对辉光放电发射光谱法分析电工钢样品光谱行为的研究,分析其工作参数如:电压、电流、预溅射时间和积分时间对光谱强度和稳定性的影响,并以铁为内标元素,优化了工作参数。确定了直流辉光放电光谱法测定电工钢中碳、硅、锰、磷、硫、铬、镍、铜共8种元素的定量分析方法,并对该方法分析的精密度和准确度进行验证,结果表明,各元素的测定结果与认定值和其他方法测定值一致,测量元素结果RSD值小于2%。 Based on research on analyzing the spectrum behavior of the sample taken from the electrical steel by glow discharge optical emission spectrometry,the effect of its operational parameters such as current,voltage,pre-sputtering time and integrating time on the spectral intensity and spectral stability is analyzed.Taking the Fe as an element applied by internal standard method,these operational parameters are optimized,and therefore the quantitative analysis method for testing eight kinds of eleme... 

近年来，在节能减排背景之下，国内外众多研究者对无取向电工钢磁性能的提升做了大量研究。为了探索无取向电工钢磁性能提升的方法，对锡或锑对无取向电工钢磁性能的作用机制(晶粒尺寸和晶体织构的控制)进行分析。基于该作用机制，介绍锡或锑的添加对无取向电工钢磁性能的影响。经研究发现，适量的锡或锑在晶界偏聚，不会阻碍晶界的移动并且致使晶粒尺寸降低；与此同时，锡或锑在晶界偏聚不仅抑制{111}织构在原始晶界处形核及生长，还降低(100)晶粒表面能，促进(100)晶粒生长。因此，适量添加锡或锑，可使无取向电工钢铁损下降、磁感提升。最后结合生产工艺，建议无取向电工钢的研究方向应为稀土含量对高牌号无取向硅钢夹杂物尺寸和数量分布的影响，锡或锑的添加量和常化工艺参数(常化时间、常化温度)对常化晶粒尺寸的影响。 In recent years, due to the background of energy saving and emission reduction, numerous researchers all around the world have done a lot of investigations on the improvement of magnetic properties for non-oriented electrical steel. In order to explore the method of improving the magnetic properties of non-oriented electrical steel, the mechanism of tin or antimony on the magnetic properties(the control of grain size and crystallographic texture) of non-oriented electrical steel is illuminated. ... 

用Gleeble1500D模拟试验机在变形温度为950～1 200℃、应变速率为0.01～8s-1、最大变形程度为60%的条件下,对硅钢50A1300做单道次压缩试验,首先分析了不同参数对流变应力的影响,然后用回归法确定了应力模型中的变形激活能及材料常数,得到硅钢50A1300在峰值应力条件和稳态应力条件下的变形激活能分别为270.360和91.557kJ/mol,同时得到了流变峰值应力模型,模型的相关系数为0.997。最后通过作lnθ-ε图的方法找到了硅钢50A1300发生动态再结晶的临界应变量,并回归得到峰值应变量、临界应变量与参数Z/C的关系式。 To analyze the effects of different parameters on the flow stress and critical strain of the dynamic recrystallization,single-pass compression experiments were carried out with silicon steel 50A1300 specimens using a Gleeble1500D thermal simulator at a temperature range of 950-1 200 ℃ and strain rate range of 0.01-8 s-1 under the condition of maximum deformation of 60%.The average deformation activation energy is respectively 270.360 and 91.557 kJ/mol under the peak stress and steady-state stres... 

【作者】 O.M.Гбанов； A.E.Чеглов； ...

本发明涉及无取向硅钢技术领域，尤其涉及一种改善高牌号无取向硅钢冷轧断带的控制方法。按重量百分比计：[Si+Al]≥4.0％；Mn、S含量满足：S≤0.0015，[Mn]/[S]:200～400；1)热轧过程中使用保温罩，热轧轧制时投入边部加热，头尾100米内卷曲温度提高15～30℃；2)常化机组圆盘剪进行边部剪边前增加加热装置，剪切后增加毛刺打磨装置，采用煤气明火加热，保证钢板温度在韧脆转变温度以上；3)圆盘剪间隙满足关系式：ds＝(0.15～0.45)d0ds:圆盘剪间隙，μm；d0:常化板板厚，mm；4)常化采用快速加热，控制钢带的预热段升温速度320～380℃/min，机组速度20～30m/min；5)常化工艺后，控制边部小于20μm的晶粒占比在5％以内。有效的减少了冷轧断带的发生，提高成材率1.30％以上，降低了生产成本。

研究了传统工艺流程生产的2%Si无取向电工钢在不同退火温度下的磁性能。研究结果表明,随着退火温度的升高,显微组织均匀性提高且晶粒尺寸增大;有利织构组分{100}<0vw>、α、η增强,不利织构组分减弱;成品的铁损P1.5/50先下降后略有上升,磁感B50上升平缓;在890℃×2 min的退火工艺条件下,成品电工钢的磁性能最佳,对应的铁损P1.5/50小于3.2 W/kg,磁感B50高于1.74 T。 In this paper,the effect of annealing temperature on magnetic properties of non-oriented electrical steel with 2% silicon was studied.Results show that the uniformity of microstructure and the average grain size increase with the rise of annealing temperature.The texture components of annealing can be improved by enhancing {100} <0vw>,α,η fiber textures and weakening {111} <112> fiber texture.The tendency of core loss P1.5/50 shows that it decreases first and then increases,while the...