本发明涉及一种具有优异铁损和磁性能的无取向电工钢及其生产方法，电工钢成分及质量含量为C≤0.0015%，Si:1.10‑1.40%，Mn：0.35‑0.55%，P≤0.018%，S≤0.003%，Al：0.20‑0.30%，Ti≤0.0015%，N≤0.0028%，O≤0.0015%，N＋O≤0.0040%，余量为Fe和不可避免的杂质。生产方法包括铁水预处理、转炉冶炼、RH精炼、连铸、轧制、常化、冷轧、连退和涂层工序。本发明电工钢热轧成品微观晶粒尺寸70‑95μm，对铁损和磁性能有利的（100）组织织构控制在82‑92%，成品P15/50:3.5‑4.0w/kg，B50:1.70‑1.98T。

分析了影响脱碳效果和结晶行为的各种要素及其相互制约关系,提出了Hi-B连续退火工艺曲线,总结得出快速加热及合理稳态气氛是实现工艺制度的关键。结合实际工程,介绍了在连续退火炉设计中快速加热和气氛设计的考虑方法,并指出随着Hi-B产品的发展,如何改进这些方法将是连退工程研发的方向之一。 The factors which affect decarbonization and crystallization and the mutual restriction between them were analyzed.A complete continuous annealing process for Hi-B was put forward.As a result,the rapid heating and the proper steady atmosphere were two important factors.According to an actual project,the consider methods for designing rapid heating and proper steady atmosphere were introduced,and it is pointed that with the development of Hi-B technique,how to improve these techniques would be on... 

本实用新型涉及一种具有在线测量功能的电工钢片横剪线，包括床身，床身上沿其长度方向安装有导轨，电工钢片在外部驱动辊带动下以导轨为导向移动；位于导轨一端端头外部的床身上安装有测量辊组件，位于导轨另一端处的床身上安装有影像测量组件；测量辊组件、导轨和影像测量组件的中心位于同一直线上，影像测量组件横跨设置于导轨上方；位于测量辊组件和影像测量组件之间的床身上依次安装有冲孔组件、V冲组件和斜剪组件；本实用新型通过测量辊组件对电工钢片行进长度进行检测，通过影像测量组件对电工钢片成型尺寸进行检测，从而便利于及时调整横剪线整体的运行状态，有效助力于保证合格率，并降低了人工负担。

本申请公开了一种低铝无取向硅钢结晶器液面波动的控制方法，包括：步骤1：KR脱硫，脱硫后铁水硫含量≤0.0015%；步骤2：转炉吹炼，转炉出钢后钢包顶渣厚度≤30mm；步骤3：RH真空处理，RH脱碳结束后，加入铝粒脱氧后钢液循环3‑5min，提升气体流量至0.8‑1.0m3/（h·t）；随后加入合金进行脱氧合金化，提升气体流量至0.5‑0.7m3/（h·t）；步骤4：连续浇注，长水口氩气流量150‑200L/min，连铸塞棒氩气流量5‑10L/min，背压≥0.05bar。本申请的控制方法控制结晶器液面波动≤±1.5mm的比例稳定在90%以上。

本实用新型公开了一种堆垛硅钢片接料装置，它涉及变压器零部件加工技术领域。导向滚轮沿平移轨道滚动带动接料底座沿平移轨道移动；接料底座上设有剪力臂架，升降油缸驱动剪力臂架调节高度带动滚筒架升降，滚筒架上安装有数排滚筒，滚筒为双链轮滚筒，每排的数个滚筒中，相邻滚筒间通过链条与链轮的配合连接，电机驱动一个滚筒转动带动一排的数个滚筒同时转动；每排的数个滚筒上方两侧分别设有导向槽板，导向槽板与滚筒架固定连接。本实用新型的优点在于：可对左右侧、不同层的硅钢片柱进行出料，可同时对多柱硅钢片进行出料，出料效率高；接料的稳定性提高，接料底座移动稳定性提高，接料后硅钢片柱可直接输送至叠装处，操作便捷，转运效率高。

本发明特别涉及一种控制边部翘皮的热轧电工钢的生产方法和生产系统，属于钢表面质量检测技术领域，方法包括：建立热轧电工钢边部翘皮的数据库，数据库包括翘皮类型及各翘皮类型的翘皮发生原因和翘皮发生的区域；对待质检的热轧电工钢表面进行识别，并对比数据库，获得待质检的热轧电工钢表面翘皮的翘皮类型；根据待质检的热轧电工钢表面翘皮的俏皮类型获得该类型翘皮的翘皮发生原因和翘皮发生的区域；根据翘皮发生原因和翘皮发生的区域，调整生产操作，用以减少热轧电工钢的边部翘皮；通过对边部翘皮进行准确分类及识别，能够准确的分辨出边部翘皮的产生原因，采取有针对性的措施防止缺陷扩大，最大程度的降低缺陷发生量，提高质量控制水平。

本实用新型涉及一种硅钢片叠装上料用转运装置，包括一输送单元，输送单元包括输送支架、输送辊，在各个输送支架均配备有一用于接收裁切好的硅钢片并堆放形成硅钢片料堆的放置板；一供料单元，包括供料板、供料支架、供料辊、支撑组件；一转运单元，包括转运支架、转运底座、转运辊、推料板、推动机构、电磁铁、转运齿条、转运齿轮、转运导轨、转运导座、导向轮、行走滚轮。本实用新型的优点在于：通过输送单元、供料单元及转运单元之间的相互配合，从而能够将满料的放置板自动输送并呈日字形自动排布好，无需再由人工搬运放置，大大减少了人工劳动，降低了人工劳动强度。

本发明涉及硅钢板技术领域，尤其涉及一种硅钢板毛刺修整机，包括工作台，所述工作台顶端面的一侧通过升降座安装有打磨机构，工作台顶端的另一侧设置有连接柱，连接柱上部的一侧水平安装固定有横梁，横梁底端面的中部竖直安装有液压杆，液压杆的底端安装有打磨机构，且上、下两个打磨机构交错分布，本发明中通过上、下两个打磨机构的主打磨带对硅钢板的顶端面和底端面进行打磨，副打磨带对硅钢板的侧端面进行打磨，从而能够对硅钢板的水平端面以及侧端面同时进行打磨去毛刺，提高了硅钢板整体毛刺修整的效率。

试验研究了0.3 mm取向硅钢冷轧板(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005A1)的退火温度(760~880℃7 min)和退火时间(820℃3~9 min)对该钢的晶粒尺寸,再结晶和织构的影响。结果表明,最佳初次再结晶退火工艺为820℃5 min,该钢的平均晶粒尺寸为14.20μm,完全再结晶率为92%,不利{111}<110>结构含量为3.16%,有利织构{111}<112>,{012}<001>和高斯织构含量分别0.40%,4.73%和2.46%。 The effect of annealing temperature(at 760 ~ 880 X.for 7 min) and time(at 820℃ for 3~9 min) on grain size,recrystallization rate and texture of 0.3 mm cold-rolled sheet of oriented silicon steel(/%:0.046C,3.07Si,0.09Mn,0.029P,0.004S,0.005Al) has been tested and studied.Results show that with optimum recrystallized annealing at 820℃ for 5 min,the silicon steel average grain size is 14.20 fun,the complete recrystaUization rate is 92%,the unfavourable-texture {111}< 110 > content in steel is ... 

采用电子背散射衍射技术测定50SW1300冷轧无取向硅钢中不同尺寸范围晶粒的含量,利用主成分回归分析法,综合研究不同尺寸范围晶粒的含量对无取向硅钢磁性能的影响。结果表明:通过主成分回归分析法能够从不同尺寸范围晶粒的含量的多个影响因素中获取主要的因素,定量研究它们对无取向硅钢磁性能的影响规律。分析表明,无取向硅钢的铁损与不同尺寸范围晶粒的含量之间存在着可靠的多元线性关系,在一定范围内,较大尺寸晶粒的含量越多,其对铁损优化的作用越明显;而无取向硅钢的磁感与不同尺寸范围晶粒的含量之间并无线性关系。 Distribution of grain size in cold rolled non-oriented silicon steel 50SW1300 was measured by EBSD.The effects of the distribution of grain size on magnetic properties of the non-oriented silicon steel were comprehensively researched by means of principal component regression method.The results indicate that the main factors influencing the magnetic properties in the distribution of grain sizes,which can be used to guantitative study the magnetlic properies of the steel,are obtained by principal... 

本实用新型公开了一种硅钢片加工装置，涉及硅钢片加工领域，包括底板，所述底板的上方左右两端固定连接有液压伸缩杆，所述液压伸缩杆的顶部固定连接有连接板。该硅钢片加工装置，可灵活调节两组打孔机之间的距离，可使用该加工装置加工出不同孔距的硅钢片，也即可加工出所需不同种类的硅钢片，加工灵活性强，使用范围广泛，通过开启电机，最终可使得两组打孔机同时进行向内侧或外侧进行移动，实现调节硅钢片两组打孔的位置。

本发明涉及一种农用电机用无取向硅钢的生产方法，包括钢水化学成分设计、热轧工艺和冷轧工艺等步骤；钢水化学成分包括：C≤0.04％、Si0.35‑0.55％、Mn0.10‑0.30％、Als0.02‑0.06％、P≤0.030％、S≤0.0040％、O≤0.003％、N≤0.003％，余量为Fe及不可避免的夹杂物。本发明方法生产出的硅钢与家用电机目前使用的普通无取向电工钢50BW1300相比，磁感提高0.02T以上，而且采用普通C含量≤0.040％设计，不需要深脱碳，大幅降低炼钢工序成本，采用无Al无P，低Mn含量，降低合金成本，与普通50BW1300无取向电工钢产品相比，生产成本大幅降低。