稀土元素在许多钢中发挥着独特而且不可替代的重要作用。半个世纪以来,它的作用已经在各种低合金和特殊合金钢中的研究及应用中得到充分的证明;然而,作为具有稀土资源优势的中国,在属于重要功能材料的无取向电工钢中稀土的应用却落后于国外,本文就中国稀土在无取向电工钢中的应用研究作简要的评述,希望能够进一步推进此领域的研究,并且促进中国稀土在无取向电工钢中应用技术的发展,缩短与国外差距,并提出了在此应用领域今后需深入开展的研究方向。 Rare earth elements play a unique and irreplaceable role in a lot of steels,it has given the full proof by the practice of various low alloy steels and special alloy steels since half century.However,as our country has the advantage of rare earth resources,RE application technology in non-oriented electrical steels has lagged behind abroad.The application researches of rare earth in non-oriented electrical steel in our country are briefly reviewed in this paper,which hope to promote the research... 

热轧轧制工艺对产品性能和轧制稳定性影响很大,对中低牌号无取向电工钢,当在两相区轧制时,热轧塑性明显降低,板形变坏,易出现边裂等情况。以50W1000为例,通过对其变形抗力进行研究,得出把两相区控制在F4与F5之间为最佳轧制工艺的结论。在此基础上制定了一套较为合理的热轧工艺制度。采用新的轧制工艺后,50W1000热轧精轧的稳定性明显改善,热轧产品合格率由开发初期的40%左右提高到95%以上。 The hot rolling process has great influence on product′s performance and rolling stability.For the low medium grade non-oriented electrical steel,when non-oriented electrical steel is rolled in tow phase region,the hot rolling plasticity reduces obviously,the shape of strip goes bad and easily to crack at the edge.The deformation resistance of 50W1000 steel was investigated.The results show that the optimal rolling process is to control the two phase region between F4 and F5.Based on the results... 

本发明涉及一种消除硅钢边部翘皮的方法及硅钢，包括预处理板坯；加热预处理后的板坯，并控制所述板坯在加热炉的预热段时间不低于40分钟；粗轧板坯，并调整所述板坯侧压的减宽量为成品硅钢宽度的0.8％～1.2％；以及控制侧压立辊的凸缘与所述板坯的边部之间保留间隙。本发明所述的消除硅钢边部翘皮的方法及硅钢，能够显著消除硅钢的边部翘皮，以及在不能完全消除边部翘皮缺陷的情况下，约束翘皮位置发生在距离边部＜8mm区域，工艺调整简单易操作，不需要调整现有设备和系统架构，显著提升硅钢表面质量。

热卷箱位于热连轧带钢生产线粗轧与精轧机之间,是热连轧生产中比较理想的中间保温设备。由于取向硅钢变形温度区间较窄,在生产中易出现边裂现象,同时中间坯的边部温度难于得到保证,因此一般不采用热卷箱设备生产,限制了传统热连轧生产线产品开发的品种。通过合理优化热卷箱控制工艺参数,解决了某厂传统热连轧生产线用热卷箱生产取向硅钢的边部质量问题,成功地生产出取向硅钢带。 The hot coil-box is an ideal heat retaining apparatus for hot rolling,lined between roughing mill and finishing mill. But oriented silicon steel has a narrow deformation temperature range,so that the edge crack easily occurs and it is difficult to insure the temperature of the intermediate blank. Therefore,the hot coil-box is rarely used in producing oriented silicon steel,which restricts the product development of the traditional hot rolling line. The article reasonable optimized process parame... 

利用EBSD技术研究了电工钢中不同的柱状晶尺寸及退火工艺下{100}织构的演变规律。结果表明,初始晶粒尺寸的影响最显著。细小柱状晶热轧后经过常化处理,组织已均匀,但中心层有强{100}织构。粗大柱状晶中{100}织构的遗传性强,常化及中间退火后,中心层仍有粗大的以{100}取向为主的晶粒;脱碳退火后才能完成组织均匀化和织构梯度的弱化。常化时的升温速度也对织构演变存在影响,低的升温速度有利于{100}织构的保留,但升温速度的影响没有初始晶粒尺寸及退火次数的影响显著。细小柱状晶样品经过热轧及三次退火工艺适合制备取向电工钢。 Evolution of {100} texture of different columnar grains and annealing process was investigated in electrical steels with the help of EBSD technique.The results show that the effect of initial grain size is the strongest.The initial fine-grained specimen shows uniform microstructure after the normalizing process,while {100} grains appear preferentially in the central layer of sheets.The heredity of {100} texture in the initial coarse-grained specimen is more significant.{100} mainly-oriented coar... 

介绍了攀钢冶炼电工钢过程硫含量变化以及过程回硫、增硫情况,采取针对性措施,如:提高铁水装入量、转炉采用石英砂代替复合造渣剂造渣、RH脱硫等,降低钢中硫含量。结果表明:采取相应措施后,电工钢炼成率大幅提高,成品w[S]≤0.008%的比例由改进前的62%提高到92.4%,取得了明显的冶金效果。 The resulfurization and the change of sulphur content in production of electrical steel is analyzed.The targeted measures have been taken,such as increase the loaded quantity of liquid iron,quartz sand replaces the composite slagging agent in the converter and RH desulfurization to decrease the sulphur content of the steel.The result shows,after the measures have been taken,the finished product ratio of electrical steel increase a lot.The ratio of sulfur content of finished product no more than ... 

本实用新型公开了一种变压器硅钢片卷吊装件，包括横梁和两个吊钩组件，在横梁两端之间的中部设置有吊挂连接构件；两个吊钩组件呈左右对称设置于横梁，吊钩组件与横梁滑动连接，在吊钩组件与横梁之间设置有第一锁紧机构，横梁通过吊挂连接构件与吊机上的吊索连接，在对不同宽度的硅钢片卷进行吊装时，松开两个第一锁紧机构，调节好其中一个吊钩组件的位置，并锁紧固定好，使得固定好的吊钩组件插入硅钢片卷其中一端内，最后将另外一个吊钩组件插入硅钢片卷另一端内，并锁紧固定，本实用新型通过两个吊钩组件来勾住硅钢片卷的两端，可避免硅钢片卷在起吊过程中损坏卷边，也可满足不同宽度的硅钢片卷的吊装。

目前高磁感冷轧硅钢生产过程中，采用经验方法确定的乳化液流量设定值往往会造成硅钢产品的磁感性能达不到预期目标，针对此情况，基于轧机轧制机理研究了的乳化液流量数学模型，确定了乳化液流量设定值。实践表明，使用该数学模型输出的乳化液流量设定值，可提高轧制过程中乳化液流量控制精度，从而提高高磁感冷轧硅钢的轧制性能。 In view of the current production process of high magnetically inductive cold-rolled silicon steel, the mathematical model of emulsified fluid flow based on mill rolling mechanism is studied in view of the situation in which the magnetic sensing performance of silicon steel products is often not up to the expected target by using empirical method to determine the emulsified liquid flow setting. Practice shows that the emulsified fluid flow setting value output from this mathematical model improv... 

本发明公开了一种适应高频率工况下低铁损无取向电工钢及其生产方法，所述生产方法包括以下步骤：钢水连续浇铸成板坯—热轧—正火—酸洗—冷轧—连续退火—涂绝缘涂层并固化；所述冷轧步骤中，采用六辊单机架往复式轧机经5道次一次冷轧至目标厚度，冷轧过程中前三道次采用变速异步轧制方法，使钢板表层在剪应力作用下位错密度增加，这样在退火后表层晶粒尺寸细化而心部晶粒粗大，通过本发明的方法可生产得到心部为粗大等轴晶粒，表层为纳米级细等轴晶粒的电工钢产品，该产品的铁损P1.5/50≤2.35W/kg，P1.0/400≤14.0W/kg。

一种硅钢生产线上的牵引装置，包含有底座（1）、支架（2）、平移机构（3）、上压板（4）、下托板（5）、气缸（6）、转向辊（7）和对中摄像头（8）；所述的平移机构（3）包含有长条齿轮（14）、齿轮（15）、电机（16）和滚轮轴承（17）；其特征在于：所述的齿轮（15）固定在电机（16）的输出轴上，并且与长条齿轮（14）啮合；使得平移机构（3）可以由电机（16）驱动在导轨（10）上左右滑动。本实用新型通过气缸（6）驱动上压板（4）和下托板（5）夹紧钢带（9），由平移机构（3）带动钢带（9）进行左右平移，避免了原先夹送辊刮伤钢带（9）表面涂层，减少了带头的浪费。

一种无取向电磁钢板用热轧钢板，其以质量％计，含有C：0.0010～0.0050％、Si：1.90％～3.50％、Al：0.10％～3.00％、Mn：0.05～2.00％、P：0.100％以下、S：0.005％以下、N：0.0040％以下、B：0.0060％以下、Sn：0～0.50％、Sb：0～0.50％、Cu：0～0.50％、REM：0～0.0400％、Ca：0～0.0400％及Mg：0～0.0400％，剩余部分为Fe及杂质；该无取向电磁钢板用热轧钢板的特征在于，在无取向电磁钢板用热轧钢板的板宽方向端部中，板厚中心部(t/2位置)的加工组织的硬度HD为Hv220以下。

本实用新型公开了一种冲制电机硅钢片用高速冲床的润滑油温控调节装置，包括换热机体、呈上下布置在换热机体内的冷冻水出水汇总管与冷冻水进水分配管以及冷冻水热交换换热管，冷冻水进水分配管、冷冻水热交换换热管和冷冻水出水汇总管依次连接，冷冻水进口外接冷冻水流量调节阀，冷冻水出口流出的冷冻水回流至冷却水池；换热机体顶部的一侧、另一侧分别开有进油口、出油口，进油口设油温检测盲管，油温检测盲管内设感温探头，感温探头与冷冻水流量调节阀信号连接。采用冷冻水换热冷却高温润滑油，带走油液热量，通过对冷冻水的流量控制调节，冷却后的油液温度恒定，以满足冲床润滑、冷却需要，以及减少冲床的换油周期。