本申请提供了涂布的晶粒取向电工钢板及其生产方法。在一个示例性实施方案中，所述方法包括生产具有约2.5至约4重量％的硅、约0.005至约0.1重量％的碳和约90至约97.5重量％的铁的熔融钢。将熔融钢浇铸成板坯并且然后冷轧成具有表面的板。使用脱碳退火对板进行脱碳，然后使用重结晶退火进行重结晶以生产晶粒取向电工钢。施加涂层覆盖所述表面，其中所述涂层包括有机可辐射固化交联剂和光引发剂。通过将涂层暴露于辐射源来固化涂层。

冷轧中中低牌号的无取向硅钢多采用万能凸度轧机(Universal crown mill,UCM)生产,其板形好坏受制于UCM轧机板形调节手段的协调使用。为掌握UCM轧机的板形控制特点,建立基于二维变厚度有限元的辊系弹性变形和基于三维差分的轧件塑性变形的六辊轧机耦合模型,对UCM轧机的板形调控性能进行详尽的分析,包括工作辊和中间辊弯辊、中间辊窜辊的调控功效、辊间接触压力分布等。在此基础上,提出可用指导生产的板形控制策略,指出UCM轧机在横向厚差控制方面的不足。针对工业生产中UCM轧机轧制无取向硅钢横向厚差大的问题,在大量仿真计算的基础上,开发具有高次曲线函数的边部变凸度(Edge variable crown,EVC)的工作辊。采用该工作辊后,各种品种的无取向硅钢的横向厚差不大于10μm的百分比由24%提高到99%,横向厚差的均值小于6μm,远小于之前的13μm。 Medium-low grade non-oriented silicon steel is rolled often by universal crown mill(UCM) during cold rolling.Its shape quality is dependent on the coordinated control of several shape adjustment devices of UCM.In order to understand the shape control characteristics of UCM,coupling model of six-high rolling mill,based on two-dimensional varying thickness finite element rolls elastic deformation model and three-dimensional finite difference strip plastic deformation model,is setup for the detaile... 

本实用新型公开了一种硅钢板带生产加工用除油烘干装置，包括壳体，所述壳体的外表面上对称设置有电机，所述电机的输出端固定连接有输送带，所述壳体的顶部设置有机体，所述机体的内部设置有除油机构，所述除油机构的一侧设置油烘干机构，所述壳体的底部设置油收集箱，所述收集箱的内部设置有收集槽。本实用新型，利用除油机构可对成硅钢板带生产后进行一定的除油处理，除油的效果更好更彻底，同时相比以往的方式提高了一定的工作效率，具有一定的实用性，利用烘干机构可进行除油后的成硅钢板带进行烘干处理，防止水渍残留在表面上，影响一定的美观效果，具有一定的实用性。

本实用新型公开了一种新型取向硅钢薄板，所述硅钢薄板包括薄板主体,薄板主体呈方形,薄板主体的内部具有硅钢基板,所述薄板主体的上部具有耐磨层,耐磨层底部还具有抗压层，耐磨层具有若干均匀分布的耐磨条,耐磨层之间分别等距间隔布置，间隔的耐磨条之间形成透气槽,透气槽具有两个侧边，透气槽底部具有透气通孔,所述透气槽两侧具有导风侧凸条,导风侧凸条具有根部和端部，根部分布在透气槽的底部左侧和右侧位置，所述端部延向透气槽两侧边部上部，所述耐磨条为均匀排列的若干双V型结构，双V型结构纵向排列，耐磨条和抗压层之间具有硬质包覆层，在不影响耐磨作用的前提下能够起到透气通风的效果，不需要增加硅钢薄板的厚度。

本发明公开了一种轻便电动自行车轮毂电机用无取向电工钢及制造方法，属于无取向钢领域。针对现有小型电机无取向钢加工难度大，效率低的问题，本发明提供一种轻便电动自行车轮毂电机用无取向电工钢，包括如下重量百分比的各组分：Si：1.50％～3.00％；Als：0.50％～2.00％；Mn：0.20％～1.00％；P：0.01％～0.20％；C：≤0.005％S：≤0.03％；N：≤0.03％；Ti：≤0.005％,其余为铁和不可避免的杂质；其中C、S、N和Ti的重量百分比满足下式：C％+S％+N％+Ti％≤0.01％。本发明通过合理控制元素含量提高硅钢的延塑性，便于加工。本发明提供的制造方法降低卷绕铁芯中的涡流和磁滞损耗，同时能够避免钢卷表面氧化和表面氮化物析出，降低铁芯损耗，与现有同铁损级别无取向硅钢相比延伸率较高，后续冷加工性能更加优异。在保证优良性能的同时便于加工。

利用电子背散射衍射(EBSD)技术和场发射电子扫描显微镜(FESEM)研究了电工钢中柱状晶不同初始取向50%热压缩变形后的演变规律及其对粒子析出行为的影响。结果表明:〈100〉晶粒形变后仍为〈100〉取向,只发生绕ND∥〈100〉方向的转动,具有遗传性,粒子析出数量少。柱状晶长轴与压缩轴的偏转度增加,取向的稳定性变差,超过40°,可形成〈111〉取向,期间发生复杂的滑移系交互作用,产生较高的缺陷密度,促进粒子析出。MnS粒子主要在晶内析出,变形温度高、形变量低,粒子均无法充分析出。回复时,形变晶粒内高的储能和缺陷密度是促进粒子进一步析出的必要条件。 The evolution of initial orientations and their influence on precipitation of columnar-grained electrical steel after 50% hot compression deformation were investigated by electron backscatter diffraction technique and field emission scanning electron microscopy.The results indicate that the〈100〉orientated columnar grains remain still〈100〉after hot compression deformation,with only rotation around ND parallel to〈100〉direction,with heredity,and less precipitation.As the deviation angle between the... 

测试了高强无取向电工钢的S-N曲线,并借助光学显微镜、扫描电子显微镜、透射电子显微镜分析了实验钢组织,疲劳断口形貌和位错结构。结果表明:室温条件下,频率为20Hz,应力比R为0.1,循环10~7周次时,实验钢的疲劳强度为360MPa,疲劳裂纹萌生于实验钢的次表面,裂纹萌生点附近有沿晶开裂现象,疲劳裂纹扩展区域有解理台阶与疲劳条纹,瞬间断裂区是韧性断裂,有大量韧窝。实验钢在循环应力作用下基体中产生了大量位错,并有驻留滑移带终止在晶界位置。 The S-N curve of a high strength non-oriented electrical steel was tested.The microstructure and fatigue fracture morphology and dislocation were analyzed by optical microscope,scanning electron microscope,transmission electron microscope.The results showed that:at room temperature and the frequency of 20 Hz and the stress ratio Rof 0.1,the fatigue strength of the experimental steel was 360 MPa when the cycle was 10~7 cycles.The fatigue crack initiation at the surface of the steel and the interg... 

本发明公开了一种含铝无取向硅钢中残余元素的控制方法。工艺流程包括KR脱硫‑转炉冶炼‑RH处理‑连铸。转炉控制合理的炉料结构，采用多渣吹炼，挡渣出钢。所用废钢中Ti、V、Nb等残余元素的质量分数之和≤0.005％，废钢和铁水的比例为0.2‑0.3。转炉吹炼终点炉渣成分中Ti、V、Nb等残余元素的氧化物含量之和为0.1‑0.5％，出钢后钢包顶渣厚度为50‑60mm；RH脱碳、脱氧、合金化后，净循环时间≤5min。通过本发明的实施，含铝无取向硅钢成品中Ti、V的含量≤0.002％，Nb含量≤0.001％，硅钢的磁性能显著提高。

【摘要】 <正>2014年5月9日,从武钢硅钢事业部获悉,...

对两种硅钢水溶性极厚绝缘涂层进行了不同温度的热老化实验。通过TG-DTA,GDS,FT-IR,SEM和光泽度仪等测试方法对老化的涂层进行分析表征,提出了评估硅钢水溶性极厚绝缘涂层热老化性能的合理温度区间,探讨了涂层热老化行为,并分析了两种涂层热老化性能的差异。结果表明,涂层附着性随着老化时间的延长逐渐下降。FT-IR表征结果显示,热老化过程中,涂料交联形成的化学键未发生断裂,交联剂氨基树脂的三嗪环被破坏是聚合物三维网络结构坍塌的主要原因。 Thermal aging expriments at different temperature were carried out on two types of water-soluble and extra-thick insulation coatings for non-oriented silicon steel,and a series of test methods such as glossmeters,TG-DTA,FT-IR,GDS,SEM were applied in analysis.For evaluating the thermal aging effect of this kind of insulation coating,the proper temperature range was proposed.The difference of aging performance between two coatings was been investigated and the related behaviors were been discussed... 

【作者】 马芳； 张春红； ...

本实用新型公开了一种电工钢加工用绝缘喷涂装置，包括底板，所述底板顶部外壁的中央位置设有安装通孔，所述安装通孔的两侧内壁上均通过轴承连接有转杆，所述底板的一侧外壁上固定连接有第一电机，第一电机输出轴的一端连接有连接杆，连接杆的一端固定连接在一个转杆的一端，两个所述转杆的一端固定连接有同一个放置架，所述放置架的两侧内壁上均固定连接有两个伸缩杆，四个所述伸缩杆活塞杆的外壁上均设有复位弹簧。本实用新型第二电机可以驱动每一个空心管转动的过程中，空心管内的绝缘漆从管壁的喷孔喷洒而出，而空心管外的扇板则配合交错分布的喷孔将雾化喷洒的绝缘漆打乱喷洒在电工钢上，全面且充分的完成喷涂。