本发明提供一种无取向电工钢的制造方法，包括连铸和RH精炼工序，连铸坯化学元素质量含量为C≤0.0050%、Si：0.50~2.20%、Mn：0.20~1.20%、P：0.020~0.040%、S≤0.0020%、Als≤0.0050%、Ti≤0.0005%、N≤0.0025%，余量为Fe及不可避免的杂质；且0.4≤Mn/Si≤0.6；RH精炼工序，脱碳结束后向钢中同时加入铝粒、微碳硅铁复合脱氧，使用铝粒脱除氧量与使用微碳硅铁脱除氧量之比为1/15~1/5，钢中主要生成低熔点MnO‑SiO2‑Al2O3夹杂，能被快速去除，钢水洁净度高。本发明电工钢与现有的电工钢相比，在相同磁感应强度下铁损更低。

研究了锰含量对w(Si)=1.8%Si无取向电工钢组织和性能的影响。结果表明,钢中锰含量从0.3%增加到1.2%时,由于α_γ相变的产生,铸坯低倍组织、热轧板金相组织及成品织构等均发生了不同程度的变化,对成品表面质量及磁性能产生了明显的影响。 The effects of manganese content on structure and properties of w(Si)=1.8% non-oriented electrical steels have been studied.Results show that with increasing manganese content to 1.2% from 0.3%,macrostructure of continuous casting slab,hot rolled band metallurgical structure and finished product texture vary in some extent because of the occurrence of α-γ phase transformation,the surface quality and magnetic properties of finished product are affected greatly. 

就冷轧硅钢废水处理生产中面临的主要问题进行分析,从技术角度及运行管理角度提出工艺优化升级改进措施及应对策略;同时从后续深度处理,逐步实现零排放目标的角度进行探讨,为冷轧硅钢废水减量化、出路乃至废水零排放提供一些思路。 The main problems in the wastewater treatment process of cold-rolled silicon steel lines are analyzed and process upgrading measures and optimization strategy are put forward from both technical and management views.At the same time,downstream deep treatment to gradually achieve the target of zero discharge is discussed,to provide some ideas for reduction or even zero discharge of wastewater from cold-rolled silicon steel lines. 

​6月28日国联证券发布：《电力设备出海2024年中期投资策略：需求方兴未艾，供给释...

本发明公开了一种硅钢氧化镁废水资源化处理方法及处理系统，硅钢氧化镁废水进入过滤浓缩干化一体化装置经预过滤、过滤、干燥、排泥后得到清液和泥饼；泥饼经烘干后得到烘干泥饼；烘干泥饼溶解于硫酸溶液中，反应后的混合液固液分离得到上层清液和沉淀物，上层清液经中和、蒸发结晶后得到结晶物，沉淀物进行清洗、烘干处理。本发明还设计了实现上述处理方法的处理系统，该系统包括过滤浓缩干化一体化装置、烘干装置、溶解装置以及产水箱；本发明的硅钢氧化镁废水经处理后的清液满足回用要求，可返回机组循环利用，实现废水回用，泥饼经烘干、溶解后可分别作为钛白粉生产原料和土壤改良剂，具有经济环保双重效果，以及良好的社会效益和环境效益。

本发明适用于电机硅钢片卷绕成型，用于各种条形冲带的电机定子铁芯卷绕机构，它包括PLC控制系统、人机操作面板、精密双轨道移动架、锁紧机构、同步电机、条形硅钢片导向槽、左右立板、一对可调整平导轮、一对齿轮、传动主轴、气（液）可调节机构、上锥形压辊、下锥形压辊、凸轮盘、驱动定位销、从动轴、左右移动护板、调整锁紧螺母、硅钢片收紧定型器、收集旋转盘、成型螺栓、特制吊装螺栓、旋转电机及机架等。采用本机构，可将各种规格条形冲带辊压成螺旋状，经收紧定型器处理后，定型的叠片不会出现褶皱,可满足不同电机定子铁芯的要求，加工质量较佳。

研究了无取向硅钢钙处理前后夹杂物的行为,重点考察了钙处理前后夹杂物的成分、类型、形貌和尺寸研究的变化情况,为实际生产中无取向硅钢的钙处理提供理论指导。试验发现:钙处理前夹杂物主要以Al2O3、Al2O3-MgO为主,且在夹杂物表面有AlN析出,钙处理后夹杂物以Al2O3-MgO-CaS-CaO系复合夹杂物为主,还含有少量的SiO2或AlN;钙处理前后,夹杂物形貌由多边形或不规则形逐渐向球形或近似球形转变,并且夹杂物尺寸不断增大;钙处理前后,含钙夹杂物的比例发生突变,由10%增大到74.5%,且随着钙处理时间的延长,含钙夹杂物比例下降,表明钙处理使夹杂物变性后易聚集长大并上浮去除。 Behavior of inclusions before and after calcium treatment in non-oriented silicon steel was researched by investigating changes of compositions,types,shapes and sizes of inclusions before and after calcium treatment,for the purpose of providing theoretical guidance for calcium treatment of non-oriented silicon steel in actual situation. Results indicated that Al2O3 and Al2O3-MgO were main types of inclusions before calcium treatment,sometimes AlN maybe precipitate in the outer of inclusions. Al2... 

针对传统工艺生产硅钢周期长、能耗大等缺点,采用双辊连铸工艺制备3%Si无取向硅钢连铸薄带,利用MEM,SEM和TEM观察了铸带的组织、织构及析出物,同时对比了Al的质量分数为0.6%和0.9%的连铸薄带在组织、织构及析出物特征方面的异同.结果表明:双辊连铸工艺生产的3%Si无取向硅钢铸带的组织为均匀等轴晶粒,平均晶粒尺寸约为300μm;织构组成随Al质量分数的不同具有明显差别,Al质量分数为0.9%的铸带中{100}织构强度是随机织构的7倍;铸带中的析出物为AlN和MnS,最大尺寸分别为500和50 nm左右. Given the lengthy production cycle,high energy consumption,and other shortcomings of the traditional process for producing silicon steel,a twin-roll casting process was used to produce 3%Si non-oriented silicon steel casting strips. MEM,SEM,and TEM were used to compare micro-structure,texture,and precipitate characteristics of a casting strip containing 0.6%Al with another containing 0.9%Al.The structure of 3%Si non-oriented silicon steel produced by the twin-roll casting process was a uniform i... 

研究了热处理工艺(退火温度、保温时间、冷却方式)对含Mn的Fe-6.5wt%Si高硅钢热轧带的显微组织及硬度的影响。结果表明,退火温度对Fe-6.5wt%Si合金的组织和显微硬度均有较大影响,随退火温度升高,平均晶粒尺寸和显微硬度均明显增大。小于1 h退火时,晶粒长大缓慢,而长时间(>1 h)退火时,一些次表层晶粒将发生异常长大。水冷组织比空冷组织略细小,但水冷显著降低了显微硬度。Mn含量提高能抑制850℃退火时晶粒的长大,并且促进退火后高硅钢的软化。 The influences of heat treatment process(annealing temperature,heating time,cooling methods) on the microstructure and microhardness of Fe-6.5wt%Si high silicon steel containing manganese for hot rolled strip were studied.The results show that the annealing temperature has a great effect on the microstructure and microhardness of Fe-6.5wt%Si alloy,and as the annealing temperature increases,the average grain sizes and microhardness will significantly increase.When annealing time for less than 1 h... 

本发明提供退火隔离剂的制备方法以及退火隔离剂和方向性电磁钢板。由该方法得到的退火隔离剂纯度高、分散性以及密接强度优异，可以在方向性电磁钢板表面形成均匀致密的镁橄榄石层。退火隔离剂的制备方法，其包括：工序(1)：将氧化镁和铵盐溶液混合并反应，制备镁盐溶液和氨，然后使精制的镁盐溶液与氨反应而得到氢氧化镁；工序(2)：将得到的氢氧化镁的一部分在155～230℃下高温熟化，并且将得到的氢氧化镁的另一部分在10～100℃下低温熟化；工序(3)：将在上述各条件下熟化的氢氧化镁混合、烧成，得到氧化镁用于退火隔离剂。

以市场上购买的取向硅钢成品板为原料，经不同压下率冷轧至0.23～0.08 mm不等。借助X射线衍射仪(XRD)检测了冷轧后样品中的织构组分及其含量，利用电子背散射技术(EBSD)测量了试样的取向因子分布情况。观察了孪晶的形貌与晶体学特征，分析了硅钢超薄带的塑性变形行为。结果发现，在平面压缩应力下，{112}<111>滑移系的取向因子较大。随冷轧压下率的增加，Goss织构的含量逐渐减少，{212}<141>织构组分的含量先增加后减少，{111}<112>织构组分的含量逐渐增加，织构组分以{110}<001>→{212}<141>→{111}<112>顺序演变。冷轧后样品中出现了孪晶，其晶体取向为{001}<110>,冷轧过程中孪晶取向没有发生变化。 The commercial finished oriented silicon steel plate as the raw material were rolled to 0.23-0.08 mm. With the X-ray diffractometer(XRD), the texture components and their volume fractions in the cold-rolled samples were detected. And the orientation factor distribution of the cross-section of the samples was measured by the electron backscattering technique(EBSD). The morphology and crystallographic characteristics of twins were observed, and the plastic deformation behaviors of the ultra-thin o... 

本发明公开了用于激光切割硅钢片及超薄件的高效快速定位夹紧装置，属于激光切割机技术领域。用于激光切割硅钢片及超薄件的高效快速定位夹紧装置，包括基体，所述基体内设有储渣腔，还包括：长条板，通过支块对称固定连接在所述基体的两侧；两组传送辊，转动连接在所述长条板上，本发明可以对硅钢片快速的进行锁紧固定，防止激光切割机在对硅钢片进行切割时，硅钢片发生移动，有效的提高了对硅钢片的切割精度和切割效率，同时切割产生的废料则会在自身重力的作用下掉落进储渣腔内进行收集，从而便于工作人员后续对废料进行集中处理，在对硅钢片进行传送时，可以增大硅钢片与传送辊之间的摩擦力，有效的提高了在传送硅钢片时的稳定性。