硅钢资料

本发明公开了一种新能源汽车驱动电机用35WD1600电工钢及其生产方法。属于新能源汽车驱动电机电工钢生产技术领域，主要解决的是现有技术新能源驱动电机电工钢性能较差的技术问题，包括以下化学元素成分及重量百分比：C≤0.005％，Si为2.5～2.8％，Mn为0.2～0.4％，P为0.08～0.12％，S≤0.008％，Cu为0.20～0.30％，Ni为0.16～0.25％，Al为0.3～0.5％，其余为Fe及不可避免的杂质。生产方法包括以下步骤：(1)铁水预处理；(2)转炉冶炼；(3)RH精炼；(4)连铸连轧；(5)酸洗；(6)第一次冷轧脱碳退火；(7)第二次冷轧脱碳退火；(8)涂层；(9)烧结卷取。本发明的新能源汽车驱动电机用35WD1600电工钢，性能达到新能源汽车驱动电机用冷轧无取向电工钢带国家标准及客户性的要求，焊接性能、板形、冲片性能良好。

借助电子背散射衍射(EBSD)及ZEISS-200MAT金相显微镜对某钢厂普通取向硅钢(CGO)进行研究,研究结果表明:热轧板组织、织构沿板厚方向存在明显的不均匀性,在热轧板表层及次表层发生再结晶,同时存在强度较高的Goss织构,中心层存在较强的{001}<110>变形织构。冷轧组织均呈纤维状条带组织,一次冷轧后,热轧板中的Goss织构消失,织构主要为α、γ织构,经中间脱碳退火后,α、γ织构强度减弱,并出现一定强度的Goss织构和利于Goss织构发展的{554}<225>、{332}<113>等织构,经二次冷轧后,二次冷轧织构类型与一次冷轧织构一致,但织构强度不同。 The grain-oriented silicon steel produced by a steel factory was investigated by EBSD and ZEISS-200 MAT metallographic microscope.The results show that the textures and microstructures along thickness of hot rolled slab are inhomogeneous.The surface layer and the layer near that are recrystallized structure which has a high Goss texture,but there is deformation texture{001}<110>in the central layer.The structure after cold rolling is a structure like fiber strip.After the first cold rollin... 

根据本发明的一个实施例的双取向电工钢板，具有从{100}＆lt;001＆gt;起15°以内的取向的晶粒的分数为50至75％，并且具有从{100}＆lt;380＆gt;起15°以内的取向的晶粒的分数为50至75％。

试验研究了球刻痕法对高磁感取向硅钢的铁损、矫顽力、相对磁导率、巴克豪森噪声等磁学性能的影响.研究结果表明:经过球刻痕处理后,高磁感取向硅钢的铁损明显降低,矫顽力下降,8 mm球刻痕过后铁损值与矫顽力分别下降16.2%和14.7%,且铁损和矫顽力均随刻痕间距降低而减少.刻痕后的高磁感取向硅钢磁导率在高磁感应强度下明显上升,刻痕后巴克豪森噪声值明显降低,经过对比分析确定8 mm为球刻痕的最佳刻痕间距.从磁畴观察、细化磁畴的原理等方面解释了细化磁畴对高磁感取向硅钢性能的影响原因. The effects of the ball scribing on magnetic properties of high permeability grain-oriented silicon steels,including the iron loss,coercive force,relative permeability,and Barkhausen noise were investigated. The results showed that the iron loss and coercive force of the high permeability grain-oriented silicon steels apparently decreased 16. 2% and 14. 7% respectively after 8 mm ball scribing and they both decreased with the decrease of the scribing spacing at the same magnetic flux density. At... 

通过对35W300高牌号0.35 mm冷轧无取向电工钢卷(/%:0.002C、2.71Si、0.22Mn、0.015P、0.003S、0.0020N、0.55Als)头、中、尾组织、织构及对应的磁性能的试验研究,发现因热轧时12 MPa高压水连续冷却造成接触轧辊的钢卷头、中、尾在不同温度下轧制,卷取后钢卷头部处于卷心、温度略高而冷却速度略低于钢卷尾部,致使钢卷纵向组织、织构不同,成品卷头、尾各250 m内磁感逐渐增加,铁损逐渐降低,250 m外至钢卷中部磁性能稳定。通过将热轧辊的冷却方式改为周期冷却和卷取后的层流冷却改为钢卷70 m后开始冷却,至钢卷尾部70 m前停止冷却的方式使得钢卷纵向铁损差异明显减小,磁感差异略有改善。 According to the test research on structure and texture of head,meddle and end of 35W300 high grade 0.35 mm cold rolled non-oriented electrical steel strip coil(/%:0.002C,2.71Si,0.22Mn,0.015P,0.003S,0.002 0 N,0.55Als) and corresponding magnetic properties,It is found that due to 12 MPa high pressure water continuous cooling the roller in hot rolling process led to head,middle and tail of strip rolling at different temperature and after coiling the head of strip coil being in center of coil led t... 

为研究退火工艺对普通取向硅钢初次再结晶组织的影响,对经不同温度、保温时间和升温速率退火后的材料组织进行了分析。结果表明:在等温退火条件下,加热至600℃时开始发生初次再结晶,800℃以上初次再结晶组织发展完善;而在最终冷轧板直接进行最终高温退火的情况下,加热温度在500～700℃时,将升温速率提高到80℃/h,初次再结晶组织更易于发展完善。 To investigate the influence of annealing process on the recrystallization of common grain oriented silicon steel,microstructures of sheets annealed at different temperature,soaking time and heating rate are observed.Results show that under the condition of isothermal annealing,recrystallization begins at 600℃ and fully develops above 800℃,while in the case that the final cold rolled sheets are directly thrown to final high temperature annealing,recrystallization is likely to develop with the he... 

对CSP流程生产的无取向电工钢M50W800不同尺寸样品的磁性能进行了测试和分析,结果表明:采用不同单片检测的磁性能结果与标准的Epstein方圈样品检测对比,存在明显的偏差;且同一尺寸的单片纵横向样品之间相比较,对应的磁性能差异性也较大。几种不同尺寸的单片样品,以320mm×30mm尺寸的纵横向平均值最接近标准Epstein方圈样的性能值,其铁损偏差最小。 The magnetic properties of M50W800 non-oriented electrical steel produced by CSP process were tested and analyzed with samples of different sizes,showing that significant deviation existed compared to that of Epstein square circle sample.In particular,obvious difference in magnetic properties also existed between longitudinal and transverse samples of the same size.For test samples of different sizes,the average magnetic properties of 320mm×30mm samples are the closest to that of Epstein square ... 

根据本发明的一个实施例的无取向电工钢板，以重量％计，所述钢板包含Si：1.5％以下、C：0.01％以下且0％除外、Mn：0.03至3％、P：0.01至0.2％、S：0.001至0.02％、Al：0.01％以下且0％除外、N：0.005％以下且0％除外、和Cu：0.02至0.3％，Ca和Mg各自单独或以合计含量包含0.0001至0.005重量％，Sb和Sn各自单独或以合计含量包含0.001至0.2重量％，余量包含Fe和不可避免的杂质。

以能量平衡和辐射换热理论为基础,通过合理假定,建立了硅钢无氧化加热炉数学模型。采用数值计算的方法,通过自编程序,完成对带钢加热过程温度场的仿真。结果显示:数学模型能够反映带钢在无氧化炉内的加热过程,其升温曲线能够与工艺曲线相吻合;现行炉温分布并非最优,数学模型能够为炉温分布的优化、炉段的设计提供理论依据。 Mathematical model of NOF Section of Continuous Annealing Furnace is established based on energy balance and radiation heat exchange. The temperature field of steel is simulated by mathematical computation. The simulating results show that the mathematical model can reflect the heating process of silicon steel in NOF section, and the heat-up curve is coincide with the processing curve. From the results,it is known that the current furnace temperature gradient is not the best, and the mathematica... 

一种使铋收得率不低于70%的含铋取向硅钢冶炼方法，其步骤：常规转炉冶炼并出钢至钢包中；RH精炼处理，其间：控制渣层厚度不低于45mm，且渣成分在：Al2O3：25～35wt%，CaO：40～50wt%，MgO:10～15wt%，且结束时钢水温度控制在1530～1590℃；真空精炼结束后进行镇静；后将铋颗粒与石灰石颗粒混装容器加入钢水中；保护浇注和后工序生产。本发明将铋颗粒与石灰石颗粒混合加入，石灰石在钢液中分解产生的气体不仅可以减缓铋颗粒下沉速度，使铋能够快速扩散均匀，更主要的是还可以强化铋颗粒在钢液中的扩散，最终可获得铋收得率高于70%即在71～75%的理想效果。

本发明的一个实施方案提供一种取向电工钢板及其制造方法，以重量％计，所述取向电工钢板包含：Si：3.0‑4.5％、Mn：0.05‑0.2％、Al：0.015‑0.035％、C：0.0015％以下(0％除外)、N：0.0015％以下(0％除外)、S：0.0015％以下(0％除外)、余量的Fe及其它不可避免的杂质，并且满足以下关系式1和关系式2。[关系式1](W13/50/W17/50)≤0.57[关系式2](W15/50/W17/50)≤0.76(其中，所述关系式1中，Wx/y表示施加磁场的大小为x/10T且频率为yHz的条件下的铁损值)。

结合工业化生产的高效硅钢,进行了RH精炼稀土处理试验研究。针对不同的稀土处理条件,观察了夹杂物的形貌和尺寸分布,探讨了稀土处理后钢中的夹杂物形成、变化规律。结果表明:试验条件下,最佳的稀土合金添加数量为0.6～0.9 kg/t。经过合适的稀土处理后,可以有效抑制尺寸相对较小的、不规则的AlN、MnS复合夹杂生成,促进钢中微细夹杂物的聚合、上浮,钢质纯净度得到明显提高。此时,钢中全氧含量最低,脱硫效果最佳,钢中的夹杂物主要是尺寸相对较大的、近似球形或者椭球形的稀土类夹杂。 Based on the industrial production of non-oriented silicon steel,the experiment on RE treatment during the RH refining process was studied.The morphology and the size distribution were observed for the steel specimens treated with different RE treatment conditions.Further more,the formation and change of inclusions of final steel sheets after RE treatment were discussed.The results show that the suitable RE added amount was 0.6～0.9 kg/t.After the suitable RE treatment,the formation of AlN and Mn...