本发明特别涉及一种控制边部翘皮的热轧电工钢的生产方法和生产系统，属于钢表面质量检测技术领域，方法包括：建立热轧电工钢边部翘皮的数据库，数据库包括翘皮类型及各翘皮类型的翘皮发生原因和翘皮发生的区域；对待质检的热轧电工钢表面进行识别，并对比数据库，获得待质检的热轧电工钢表面翘皮的翘皮类型；根据待质检的热轧电工钢表面翘皮的俏皮类型获得该类型翘皮的翘皮发生原因和翘皮发生的区域；根据翘皮发生原因和翘皮发生的区域，调整生产操作，用以减少热轧电工钢的边部翘皮；通过对边部翘皮进行准确分类及识别，能够准确的分辨出边部翘皮的产生原因，采取有针对性的措施防止缺陷扩大，最大程度的降低缺陷发生量，提高质量控制水平。

研究了取向硅钢制备过程中常见的两种冷轧工艺,主要研究了一阶段冷轧与两阶段冷轧+中间退火工艺对初次再结晶组织及织构的影响.结果表明:采用两阶段冷轧+中间退火工艺制备以Cu2S为主抑制剂的取向硅钢,其初次再结晶平均晶粒尺寸为18.1μm,高斯晶粒的体积分数为0.6%,迁移性强的重位点阵晶界(Σ5+Σ9)和高能晶界(20°~45°取向偏差角)所占比例分别为1.8%和50.4%.与一阶段冷轧工艺相比,其初次再结晶晶粒较细,且高斯晶核与特征晶界所占的比例较高,有利于高斯晶粒发生二次再结晶. Two common cold-rolling processes of grain oriented silicon steel and the effects of the single stage cold rolling and tw o-stage cold rolling w ith intermediate annealing processes on the primary recrystallization microstructure and texture w ere investigated. The results revealed that for the grain oriented silicon steel prepared under the tw o-stage cold rolling process w ith intermediate annealing w ith Cu 2 S as the main inhibitor,the average grain size of the primary recrystallization micr... 

通过微观组织表征、高温拉伸和断口形貌分析,研究了钇(Y)元素对6.5%Si无取向硅钢组织、高温拉伸及断裂机制的影响。研究结果表明,添加Y元素可以在钢液中形成YS和YP的复合析出。YS和YP可以充当异质形核基底,提高形核率,细化凝固组织。热轧组织不均匀,由表层至芯部分别形成等轴晶、等轴晶/拉长晶和拉长晶的混合组织。退火后,热轧变形组织转变为等轴晶,含Y实验钢的退火组织得到明显细化。500℃时效处理后,含Y实验钢具备较低的有序度,300℃的拉伸断口呈现韧性断裂特征,断后伸长率达到20.2%。相反,无Y实验钢发生脆性断裂,断后伸长率仅为2.1%。研究结果证实,Y元素可以通过组织细化和降低有序度提高6.5%Si无取向硅钢的中温塑性。 The effects of yttrium(Y)on microstructure,elevated-temperature tensile properties and fracture mechanism of 6.5% Si non-oriented electrical steel were investigated by means of microstructure characterization,high-temperature tensile test and fracture analysis.The results showed that the doping of Y introduced composite Y-rich precipitates(YS/YP)in the melt.YS and YP precipitates were qualified for heterogeneous nucleation agents,which thus raised the nucleation rate and refined the solidificati... 

本发明公开了一种精确控制高磁感取向硅钢板坯Als含量的方法，转炉出钢20～40秒时，定量加入金属铝，加入量按0.15～0.35kg/吨钢；转炉出钢及合金加入后，底吹搅拌均匀3～5min后，加入一定量金属铝后再底吹搅拌均匀3～5min后将钢水吊运至RH开始精炼处理，铝加入量按[WAls目标+(0.009～0.0120％)]范围控制；钢水在RH精炼过程经过2～3次酸溶铝的成分微调后结束精炼，精炼结束Als按[WAls目标+(0.0030～0.0045％)]目标范围控制；RH精炼结束样酸溶铝检测结果出来后，在连铸开浇前，在钢包内补加铝线使钢液中Als在[WAls目标+Δ浇注Als损]目标范围内；连铸进行氩气环流保护浇注，其中氩气环流流量控制在6～12m3/h；浇注成合格板坯后按正常工艺进行热轧及后工序生产。

本发明公开了一种基于硅钢服役特性的立体卷铁心单框损耗测量方法及系统，根据硅钢片在立体卷铁心中的服役特性，获得测量铁心单框所需的非正弦励磁电压波形，通过所述立体卷铁心的心柱绕组电压和单框绕组电压之间的关系，确定所述被测立体卷铁心单框所需的电压有效值，再通过计算机、数据采集卡D/A转换器、功率放大器、隔离变压器和示波器，直接在所述立体卷铁心单框上加载励磁电压，利用功率表测量立体卷铁心单框损耗。本发明利用硅钢的服役特性，获得测量立体卷铁心单框所需的非正弦励磁电压波形和电压有效值，再将励磁电压直接加载到被测立体卷铁心单框，测量立体卷单框铁心损耗。

本发明属于取向硅钢制备技术领域，具体涉及一种软磁材料取向硅钢退火工艺。所述退火工艺主要包括：涂覆隔离剂、按照一定速率升温后进行保温，以5‑10℃/min的速率进行降温；在降温过程中施加恒定磁场，之后继续降温即可实现。该退火工艺能够有效降低铁损失，提高磁感强度。同时具有较好的耐腐蚀性能和机械性能。

研究了电工钢SXRC的显微结构和疲劳性能,并与DP钢进行了比较。结果表明,退火温度低温化能够有效的抑制电工钢的再结晶。该钢在固溶铌的作用下,能够在保证电机磁性的同时具有一定的强度。与DP钢相比,SXRC钢的抗疲劳性能更好。 The microstructures and fatigue properties of the electrical steel SXRC we re investigated, and the properties were also compared with the steel DP. The results show that the recrystallization of the electrical steel can be suppressed at lower annealing temperature. The steel presents favorable motor magnetic and also a compatible strength with the help of solid-solution Nb. Compared with the steel DP, the fatigue resistance of the steel SXRC is preferable. 

冷轧无取向硅钢是高技术含量、高附加值产品,工艺复杂,生产周期长,过程控制难度大,被誉为钢铁产品中的\"工艺品\"。热轧生产工艺又是无取向硅钢生产的重中之重,直接决定了硅钢的铁损和电磁性等多项指标。 Cold rolled non-oriented silicon steel is high technology content 、high added value product. Its process is complex, its production cycle is of length, and its process control is difficult, which is known as the iron and steel products \" Arts and crafts\". Hot rolling production process is the top priority of non-oriented silicon steel, which directly determines iron loss of the silicon steel and electromagnetic property,as well as other many index. 

本实用新型公开了叠片装置，以及采用该叠片装置的硅钢片收料设备，包括分料装置和本实用新型第一方面实施例的叠片装置，分料装置包括有分料件、上分料传送带和下分料传送带，上分料传送带的一端和下分料传送带的一端与分料件连接，分料件用于将硅钢片分别输送至上分料传送带和下分料传送带，本实用新型第一方面实施例的叠片装置，叠片装置的数量为两个，两个叠片装置上下平行设置，并且分别与上分料传送带和下分料传送带的远离分料件的一端连接。根据本实用新型的叠片装置，以及采用该叠片装置的硅钢片收料设备，可实现硅钢片的自动叠片，提高生产效率。

通过对辉光放电发射光谱法分析电工钢样品光谱行为的研究,分析其工作参数如:电压、电流、预溅射时间和积分时间对光谱强度和稳定性的影响,并以铁为内标元素,优化了工作参数。确定了直流辉光放电光谱法测定电工钢中碳、硅、锰、磷、硫、铬、镍、铜共8种元素的定量分析方法,并对该方法分析的精密度和准确度进行验证,结果表明,各元素的测定结果与认定值和其他方法测定值一致,测量元素结果RSD值小于2%。 Based on research on analyzing the spectrum behavior of the sample taken from the electrical steel by glow discharge optical emission spectrometry,the effect of its operational parameters such as current,voltage,pre-sputtering time and integrating time on the spectral intensity and spectral stability is analyzed.Taking the Fe as an element applied by internal standard method,these operational parameters are optimized,and therefore the quantitative analysis method for testing eight kinds of eleme... 

本发明公开了一种控制无取向硅钢厚度稳定性的轧制工艺，涉及硅钢厚度控制方法领域。本发明通过降低硅钢精轧入口温度，并调节粗轧区域、精轧区域和卷取区域的生产参数，保证后续卷取工序的轧制稳定性及卷形质量，严格控制无取向硅钢的厚度稳定性。本发明提供的轧制工艺使硅钢的厚度命中率得到了明显提升，提升了后续冷轧工艺的轧制速度，轧制力波动减小，提高了产品质量。

本发明涉及一种农用电机用无取向硅钢的生产方法，包括钢水化学成分设计、热轧工艺和冷轧工艺等步骤；钢水化学成分包括：C≤0.04％、Si0.35‑0.55％、Mn0.10‑0.30％、Als0.02‑0.06％、P≤0.030％、S≤0.0040％、O≤0.003％、N≤0.003％，余量为Fe及不可避免的夹杂物。本发明方法生产出的硅钢与家用电机目前使用的普通无取向电工钢50BW1300相比，磁感提高0.02T以上，而且采用普通C含量≤0.040％设计，不需要深脱碳，大幅降低炼钢工序成本，采用无Al无P，低Mn含量，降低合金成本，与普通50BW1300无取向电工钢产品相比，生产成本大幅降低。