真空感应炉熔炼高硅电工钢脱氧工艺的研究
在50Kg氧化镁坩埚真空感应炉上进行高硅电工钢的脱氧试验。结果表明,通过控制原料的成分、高真空下的碳氧反应和炉衬分解向钢液中的供氧,可使钢液的总氧含量≤15×10-6;在维持高温高真空条件下,当钢液中的反应达到一定程度后,延长精炼时间并不能降低钢液的总氧含量;完成精炼后加入硅钙合金沉淀脱氧可进一步降低钢液的总含氧量,但脱氧效果有限。 The test of high-silicon electric steel deoxidation has been carried out in 50Kg vacuum induction furnace with magnesium oxide crucible.Results show that the total oxygen could be ≤15×10-6in molten steel by controlling material components,carbon-oxygen reaction in high vacuum and oxygen contamination from crucible materials on molten steel;And when the reaction was carried through to a certain extent,total oxygen in molten steel could not be reduced by the extension of refining period in high va...
CN202111432309.4一种新能源汽车驱动电机用35WD1600电工钢及其生产方法
本发明公开了一种新能源汽车驱动电机用35WD1600电工钢及其生产方法。属于新能源汽车驱动电机电工钢生产技术领域,主要解决的是现有技术新能源驱动电机电工钢性能较差的技术问题,包括以下化学元素成分及重量百分比:C≤0.005%,Si为2.5~2.8%,Mn为0.2~0.4%,P为0.08~0.12%,S≤0.008%,Cu为0.20~0.30%,Ni为0.16~0.25%,Al为0.3~0.5%,其余为Fe及不可避免的杂质。生产方法包括以下步骤:(1)铁水预处理;(2)转炉冶炼;(3)RH精炼;(4)连铸连轧;(5)酸洗;(6)第一次冷轧脱碳退火;(7)第二次冷轧脱碳退火;(8)涂层;(9)烧结卷取。本发明的新能源汽车驱动电机用35WD1600电工钢,性能达到新能源汽车驱动电机用冷轧无取向电工钢带国家标准及客户性的要求,焊接性能、板形、冲片性能良好。
CN202110671549.3无取向硅钢的生产方法
本发明揭示了一种无取向硅钢的生产方法。所述生产方法中:按照Si:0.3~1.2%炼钢、制坯;将铸坯加热到1050~1150℃并保温150min以上,而后轧成厚度40~45mm的中间坯,再经精轧、卷取得到厚度为3.00±0.25mm的热轧卷板,精轧开轧温度≤Ar1=872℃+1000*(11*[Si]‑14*[Mn]+21*[Al]);当Ar1≥1000℃,终轧温度T≤840℃,否则T≤Ar1‑160℃;卷取温度≤550℃;经常化、酸连轧得到0.500±0.005mm的冷硬卷,常化温度为850~950℃;退火温度820~950℃,经成品退火、冷却、涂层和精整,得到无取向硅钢成品。
取向硅钢生产工艺技术分析和发展趋势
介绍了普通取向硅钢(CGO)和高磁感取向硅钢(Hi-B)铸坯高温加热两次冷轧、一次冷轧和铸坯低温加热两次冷轧、一次冷轧法4种成熟生产工艺的主要技术参数,取向硅钢理论研究(Goss晶核和抑制剂)和生产技术现状。取向钢的发展趋势为:提高(110)[001]晶粒取向度,降低取向硅钢铁损,发展铸坯低温加热(≤1 300℃)和薄板坯连铸连轧流程生产取向硅钢工艺。 Main technology parameters of four developed process:cast bloom higher temperature heating-double cold rolling or single cold rolling,lower temperature heating-double cold rolling or single rolling process for production of common grain oriented silicon steel(CGO) and high magnetic induction grain oriented silicon steel(Hi-B),theory research on grain oriented steel(Goss nucleus and inhibitor) and present situation of process are summarized in this paper.The development trend of grain oriented si...
CN202123000262.2一种取向硅钢喷涂用涂料的加工上料装置
本实用新型公开了一种取向硅钢喷涂用涂料的加工上料装置,包括底座,所述底座固定连接有立柱,所述立柱固定连接有搅拌桶,所述立柱上滑动连接有桶盖和电机支架,所述电机支架固定连接有电机,所述电机的输出端固定连接有搅拌杆,所述搅拌杆穿过桶盖并固定连接有搅拌叶片,所述电机支架与桶盖之间固定连接有弹簧,所述滑槽中位于电机支架和桶盖之间固定设有限位块,通过电机、搅拌杆、搅拌叶片之间的配合,使涂料在配制时能够混合均匀;通过电机支架、桶盖、弹簧和限位块之间的配合,使得在搅拌过程中,桶盖始终紧紧盖住搅拌桶,防止搅拌过程中涂料洒漏。
RH精炼添加钙合金去除硅钢夹杂物研究
采用RH精炼添加钙合金方式对硅钢进行钙处理。结果表明,钙合金添加量为0.67、1.00、1.67kg/t钢时,钢中钙含量分别为0、2×10-6、4×10-6;随着钙合金添加量增大,钢中夹杂物粒度逐渐由0~2μm向2~4、4~6μm偏移;不同钙处理条件下,钢中均存在粒径小于1μm和粒径为1~5μm的MnS、CuxS夹杂物,后者或单独存在,或同AlN、CaS夹杂复合;粒径为5~10μm区间,钢中的夹杂物基本以钙的氧、硫化物为主。与钙处理前相比,钙合金添加量为0.67、1.00、1.67kg/t钢时,粒径小于1.0μm的微细夹杂物减少幅度分别为68.06%、87.50%、94.94%。钙合金添加量为1.67kg/t钢时,可以去除钢中绝大部分的微细夹杂物。 Ca alloy was added into the liquid steel during RH refining,and the results show that Ca concentration in final Si steel sheets is insignificant,about 0,2×10-6 and 4×10-6 when the added amount of Ca is 0.67,1.00 and 1.67 kg/t steel,respectively.With the increase in the added Ca alloy amount,the inclusions in the steel gradually change from those of 0~2 μm to those of 2~4 and 4~6 μm.Under different Ca treatments,there exist MnS and CuxS inclusions whose size is below 1 μm as well as MnS and CuxS ...
退火工艺对普通取向硅钢初次再结晶组织的影响
为研究退火工艺对普通取向硅钢初次再结晶组织的影响,对经不同温度、保温时间和升温速率退火后的材料组织进行了分析。结果表明:在等温退火条件下,加热至600℃时开始发生初次再结晶,800℃以上初次再结晶组织发展完善;而在最终冷轧板直接进行最终高温退火的情况下,加热温度在500~700℃时,将升温速率提高到80℃/h,初次再结晶组织更易于发展完善。 To investigate the influence of annealing process on the recrystallization of common grain oriented silicon steel,microstructures of sheets annealed at different temperature,soaking time and heating rate are observed.Results show that under the condition of isothermal annealing,recrystallization begins at 600℃ and fully develops above 800℃,while in the case that the final cold rolled sheets are directly thrown to final high temperature annealing,recrystallization is likely to develop with the he...
不同尺寸电工钢样品磁性能检测对比分析
对CSP流程生产的无取向电工钢M50W800不同尺寸样品的磁性能进行了测试和分析,结果表明:采用不同单片检测的磁性能结果与标准的Epstein方圈样品检测对比,存在明显的偏差;且同一尺寸的单片纵横向样品之间相比较,对应的磁性能差异性也较大。几种不同尺寸的单片样品,以320mm×30mm尺寸的纵横向平均值最接近标准Epstein方圈样的性能值,其铁损偏差最小。 The magnetic properties of M50W800 non-oriented electrical steel produced by CSP process were tested and analyzed with samples of different sizes,showing that significant deviation existed compared to that of Epstein square circle sample.In particular,obvious difference in magnetic properties also existed between longitudinal and transverse samples of the same size.For test samples of different sizes,the average magnetic properties of 320mm×30mm samples are the closest to that of Epstein square ...
CN202110326532.4一种低磁场条件下高磁感应强度无取向电工钢及其生产方法
本发明公开了一种低磁场条件下高磁感应强度无取向电工钢及生产方法,步骤包括:冶炼:炼钢、连铸生产铸坯,所述铸坯中:以质量百分比计,Si2.0%、Mn0.2‑0.5%、ALs0.3‑0.6%、N≤0.002%、S≤0.002%、Ca≤0.001%,余量为Fe及不可避免的杂质;板坯热轧、卷取;常化处理;退火处理。本发明通过合理的电工钢成分设定、生产工艺、稳定的控制精度,从一贯制角度对产品进行设计及控制,最终能够保证产品质量稳定、具有低磁场条件下高磁感应强度的Si含量2%的0.35mm厚度无取向电工钢产品。
高硫硅钢的硫化物析出行为及其微观组织和电磁性能变化
为了弄清楚高硫硅钢中的硫化物析出行为及其对钢的微观组织和电磁性能的影响,以便为工业化生产制定更为合理的硫含量控制标准和采取更为有效措施减轻炼钢生产的硫含量控制压力,结合0.25% Si 无取向硅钢 ,采用非水溶液电解提取 + 扫描电镜/透射电镜观察相结合的方法 ,研究了0.006 8%、0.010 2%、0.025 5% 和 0.035 3% 硫含量条件下,钢中的硫化物夹杂物组成和存在形式及其形貌、种类、尺寸、数量变化,以及相应的热轧、成品试样的微观组织和电磁性能变化。结果表明,随着钢中硫含量的增加,钢中的硫化物逐渐由 MnS→MnS+Cu2S→Cu2S转变,数量逐渐增多,尺寸向高低两个方向发展。相应地,导致热轧再结晶组织劣化和抑制了成品晶粒尺寸长大。随着钢中硫含量的增加,钢的磁感、铁损劣化程度逐渐增大。钢中的硫含量平均每增加 0.01%,涡流损耗、磁滞损耗分别劣化0.24 W/kg 和 0.41 W/kg,而磁感会劣化 0.009 T。但是 ,在硫含量为 0.010 2% 时 ,铁损可以低于 6.0W/kg,而在硫含量为 0.025 5% ... In order to find out the precipitation behavior of sulfide inclusions and the corresponding changes of microstructure and electromagnetic properties of high sulfur silicon steel sheets, so that to design more suitable sulfur concentration controlling limit for industrial manufacture and to release the steel-making difficulty effectively, Based on the change of given sulfur concentration 0.006 8%, 0.010 2%0.025 3% and 0.035 3%, the type and composition, the size and number, and the size distribut...
CN202111458743.X一种超短流程稀土取向硅钢及其制备方法
本发明属于冶金技术领域,涉及一种超短流程稀土取向硅钢及其制备方法,化学组成及其重量百分比为Si:2.0~4.5%,C:≤0.003%,Y:0.001~0.05%,Mn:0.15~0.35%,Al:0.03~0.04%,Cu:0~0.5%,S:0.025~0.04%,N:0.011~0.013%,其余为Fe和不可避免的杂质元素。制备工艺包括:钢水冶炼、薄带连铸、冷轧、再结晶退火。与常规生产方式相比,取消了连铸、粗轧、热连轧、常化和脱碳退火等工序,极大简化了生产流程。通过添加稀土元素钇,促进了抑制剂的析出,还显著细化了薄带连铸硅钢的凝固组织,提高组织均匀性,获得了均匀细小的等轴晶,优化了取向硅钢的性能。