本发明揭示了一种高硅无取向电工钢及其生产方法。该方法包括：1）钢水冶炼并连铸成坯；2）加热并保温，之后热轧得到热轧卷板，其中粗轧出口温度940±20℃，精轧终轧温度840±20℃，卷取温度650±20℃；3）常化，常化温度((732~742)+3000[Si])℃，常化时长4min~5min；4）常化后直接进行冷轧，而后连续退火和涂层，退火温度940℃~990℃且退火时长1.5min~3min；5）涂层处理后的钢板加工成型，而后进行去应力退火，退火温度为((761~766)+3000[Si])℃。如此，在保证磁性能的同时，解决了冷轧难度大的问题。

研究了铝和铬元素在无取向电工钢晶粒长大过程中对织构及晶界变化的影响规律。试验结果表明:电工钢在晶粒长大过程中的主要织构组分均为{111}<112>。在晶粒生长期间,不加铝的1号试样中,{111}<112>、{111}<110>织构组分强化,而{100}<001>织构组分弱化;与1号试样相比,在加入0.2%的铝(质量分数,下同)的2号试样中,{111}<112>、{111}<110>织构组分强化(增加)的速率下降,{100}<001>织构组分变化不明显,甚至稍有增加。在含铝的试样中再加入0.3 5%的铬之后(3号试样),{111}<112>{、111}<110>和{100}<001>织构组分的变化规律与1号试样相似,但当电工钢中加入0.72%的铬之后(4号试样),上述3种织构组分的变化规律与2号试样相似。对于在晶粒生长期间持续变化的3种织构组分而言,1号试样的{1 1 1}<112>和{111}<110>织构组分的高(低)取向差角度晶界频率下降(... The effect rule of Aluminm and Chromium on texture and grain boundary transformation in the nonoriented electrical steel during grain growth was investigated.The experimental result shows that the main texture component is {111}<112> in the electrical steel.The {111}<112> and {111}<110> components in specimen 1 without Alumium were strengthened during grain growth whereas {100}<001> component was weakened.But the growth rate of {111}<112> and {111}<110> compon... 

本发明公开了一种取向硅钢产品的在线性能判级与精确分切装置和方法，使得同一个分卷上的性能分布均匀，避免分卷出现性能废品或多个性能等级的情况，提高分卷性能稳定性。提供的一种取向硅钢产品的在线性能判级与精准分切方法包括生产数据采集、铁损曲线自学习、数据存储、性能在线判级、缺陷数据采集、缺陷判级、智能分切等模块，依据修正后的磁性能全长数据，得到产品的性能判级结果，结合表面缺陷判级结果，综合确定分切位置，制定最佳分切方案。本发明可以实现取向硅钢生产过程中的性能在线判级和精准分切，得到性能均匀、表面质量好的分卷，减少分卷性能不稳定带来的损失。

本实用新型涉及一种硅钢冲压片质量筛查分拣装置，包括：第一组传送带机构，第一摄像头，设置于第一组传送带机构的上方，用于对硅钢冲压片的第一表面的残损进行检测；第一机械手机构，设置于第一组传送带机构的上方且位于所述第一摄像头的后方；翻转装置，设置第一组传送带机构的后方，用于对第一组传送带机构传输的初检良品进行翻面并将翻面后的初检良品传输给第二组传送带机构；第二组传送带机构，设置于翻转装置的后方；第二摄像头，设置于第二组传送带机构的上方，用于对硅钢冲压片的第二表面的残损进行检测；第二机械手机构，设置于第二组传送带机构的上方且位于第二摄像头的后方。本实用新型可高效的检测每一个产品的外观质量。

本发明公开了一种激光刻痕降低取向硅钢铁损的制造方法，采用0.23‑0.35mm厚取向硅钢作为原材料，钢带在拉伸热平整线出炉后进行激光刻痕处理，细化磁畴，进而降低取向硅钢成品铁损值，达到优化磁性能的目的。本发明的激光刻痕处理后取向硅钢的铁损改善率可达到9‑16％，且经过500℃以上退火后，铁损又恢复到刻痕前状态。

主要研究了氧化锌对以Al(H2PO4)3为基料的无铬无取向硅钢绝缘涂层各项性能的影响.用盐雾实验和动电位极化研究了不同氧化锌含量对硅钢绝缘涂层的耐蚀性和电化学行为的影响.采用SEM和体视显微镜对涂层的表面形貌和附着性能进行研究.结果表明,氧化锌含量为4.0%时,氧化锌能完全中和涂层表面的游离磷酸,涂层的耐蚀性和附着性最好;氧化锌含量过少或过多时,涂层的耐蚀性和附着性都较差. This paper studies the influence of zinc oxide on the performance of chromium-free non-oriented silicon steel insulating coating which based on aluminum dihydrogen phosphate.Salt spray experiment and potentiodynamic polarization were used to study the influence of zinc oxide content on the corrosion resistance and electrochemical behavior of the insulation coating of silicon steel.The surface morphology and adhesion of coating were tested by SEM and stereo microscope.The results show that when t... 

借助实验室设备研究了B元素对高牌号无取向硅钢热轧板组织和磁性能的影响。结果表明,与无硼钢相比,含硼钢的热轧板晶粒尺寸略小,析出物的类型和尺寸没有区别,主要是AlN和(AlN+MnS)复合析出物,少量的MnS析出物,尺寸集中在1.0～2.5μm范围内。未发现BN析出物。在力学性能方面,B对钢的软化作用不明显。在磁性能方面,含硼钢的铁损为3.215W/kg,磁感为1.710T,综合磁性能比无硼钢差。 Influences of boron on microstructure and properties of hot rolled band in high-grade non-oriented silicon steel are researched in this paper by experimental equipments.Compared with boron-free steel,the result shows that boron-bearing steel has smaller grain size,but the type and size of precipitations have no differences.The main precipitates are AlN,(MnS + AlN) composite precipitate and few MnS,the range of which are between 1.0 μm and 2.5 μm.BN precipitation is not found.With reward to mecha... 

本发明公开了叠片装置，以及采用该叠片装置的硅钢片收料设备，包括分料装置和本发明第一方面实施例的叠片装置，分料装置包括有分料件、上分料传送带和下分料传送带，上分料传送带的一端和下分料传送带的一端与分料件连接，分料件用于将硅钢片分别输送至上分料传送带和下分料传送带，本发明第一方面实施例的叠片装置，叠片装置的数量为两个，两个叠片装置上下平行设置，并且分别与上分料传送带和下分料传送带的远离分料件的一端连接。根据本发明的叠片装置，以及采用该叠片装置的硅钢片收料设备，可实现硅钢片的自动叠片，提高生产效率。

本实用新型涉及一种硅钢片纵剪边料收卷装置，包括：用于将收卷装置固定于地面的机架底座，机架底座一端设置固定支架，固定支架上安装电动定尺收料盘；在机架底座上设置电动可移动支架，电动可移动支架在机架底座的长方向上相对固定支架移动，电动可移动支架上安装电动可调收料盘；电动可移动支架、电动定尺收料盘、电动可调收料盘与PLC控制系统连接，PLC控制系统用于控制电动可移动支架的移动距离、以及控制电动定尺收料盘和电动可调收料盘的收料速度。将本实用新型的硅钢片纵剪边料收卷装置安装在硅钢片滚剪线切刀后面的输送平台的下部，卧式布局，不占用外部空间，和滚剪线无缝集成在一起，自动完成硅钢片纵剪边料的收卷工作。

本发明属于智慧物流技术领域，具体的说是一种用于硅钢卷运输的智慧物流系统及防塌卷装置，包括运输模块、支撑模块、感应模块与分析模块；所述支撑模块以设置在硅钢卷内圈的支撑组件为载体；所述感应模块以设置在支撑组件上的感应组件为载体，且所述感应组件内设置有若干个均匀分布的压力感应器；所述分析模块以中央处理器为载体；本发明通过在支撑硅钢卷的支撑组件上设置感应组件，使得工作人员对硅钢卷内部的清洁度与杂质位置进行有效的判断，并通过定点清理其内部的杂质，减少硅钢卷内部的硅钢片在支撑时被压伤的情况，提高了硅钢卷在物流运输时的安全性。

根据本发明的一个实施例的双取向电工钢板，以重量％计，所述钢板包含Si：2.0至4.0％、Al：0.01至0.04％、S：0.0004至0.02％、Mn：0.05至0.3％、N：0.01％以下且0％除外、C：0.005％以下且0％除外、P：0.005至0.15％、Ti：0.001至0.005％、Ca：0.0001至0.005％和Mg：0.0001至0.005％，余量包含Fe和其他不可避免的杂质，具有从{100}＆lt;001＆gt;起15°以内的取向的晶粒的面积分数为60至99％，具有从{100}＆lt;025＆gt;起15°以内的取向的晶粒的面积分数为1至30％。