硅钢资料

本文研究了丙烯酸树脂含量对以Al(H2PO4)3为基料的无铬无取向硅钢绝缘涂层各项性能的影响.用盐雾实验、动电位极化及交流阻抗等试验手段研究了不同树脂含量对硅钢绝缘涂层的耐盐雾性能和电化学行为的影响,同时采用SEM对涂层的表面形貌和附着性进行研究.结果表明,树脂含量为19.9~29.4%时,涂层的耐蚀性和附着性最好;树脂含量过多时,涂层的耐蚀性和附着性均较差. This paper studies the influence of acrylic resin on the performance of insulating coating of aluminum dihydrogen phosphate on chromium-free non-oriented silicon steel.Salt spray experiment,potentiodynamic polarization and electrochemical impedance spectroscopy were used to study the influence of acrylic resin content on the salt spray resistance and electrochemical behavior of the insulation coating of nonoriented silicon steel.The surface morphologys and adhesion of coating were tested by SEM.... 

采用X-射线衍射分析技术测定了取向硅钢热轧板在不同压下率下不同厚度处的织构。结果表明,在压下率低于80%的情况下,几乎所有试样的不同厚度处的织构均为旋转立方织构类型{100}<011>,但不同压下率、不同厚度处的织构强度存在很大差异;在压下率大于80%的情况下,不同试样的不同厚度处的织构类型发生了变化,其织构类型为旋转立方织构或高斯织构{011}<100>,且当织构类型为旋转立方织构时,织构强度存在很大差异,而当织构类型为高斯织构时,织构强度差异相对较小。 The texture of the grain oriented silicon steel hot rolled plate at different compressibility has been measured.The experimental results have shown that the texture of all samples at different thickness is {100}<011> when the compressibility is below 80%,and its intensity at different compressibility and thickness is difference.The texture of all samples at different thickness is variable when the compressibility is above 80%,it is {100}<011> or {011}<100>,and the intensity of ... 

利用场发射扫描电镜观察了以MnS为主要抑制剂的普通取向电工钢加工过程中第二相粒子的分布状态,统计了粒子面密度、平均尺寸以及相应的尺寸分布.结果显示,热轧加工造成了大量第二相粒子弥散、细小地析出,同时基体仍保持过饱和状态.冷轧变形会造成第二相粒子的回溶行为,而基体的过饱和状态会减弱回溶现象.中间退火与脱碳退火过程中会同时存在新粒子的形核及已析出粒子的粗化两个过程,而在最终二次再结晶升温阶段则以第二相粒子明显粗化为主. The distribution of second phase particles in conventional grain-oriented electrical steels during manufacturing processes with MnS as inhibitors was observed by field emission scanning electron microscopy,while the areal particle density,the average particle size and the corresponding size distribution were statistically determined.It is indicated that hot rolling leads to dispersive precipitation of a large amount of fine second phase particles and the matrix keeps a supersaturated state furth... 

本发明公开了硅钢片均衡堆垛分料系统，包括分料机构和接料机构，分料机构包括料架，料架上具有托板，托板两侧设有第一滚筒架，第一滚筒架顶部设有分料结构；分料结构可实现上下、水平移动；分料结构包括支撑架，支撑架上设有倒吸件；倒吸件包括磁块槽和挡料板，磁块槽设于挡料板上方，磁块槽底部设有磁块，磁块槽上方设有压料胶条，磁块槽和压料胶条可上下移动，接料机构的接料底座可平移，剪力臂架可升降，以改变第二滚筒架高度和水平位置。本发明的优点在于：通过分料结构的倒吸件吸附硅钢片，再将数个硅钢片同时放置于托板侧边数排滚筒上的放置板上，可实现多柱硅钢片的均衡堆垛，通过接料机构可进行多柱硅钢片的同时稳定出料，转运效率高。

应用CAFE法对6.5%Si高硅钢铸锭凝固组织进行了模拟研究,确定出了适合高硅钢组织模拟的模型。进一步用该模型研究了过热度及冷却条件对凝固组织的影响,结果表明,随着过热度的降低,凝固组织中柱状晶比例和晶粒平均面积均减小。水冷条件下,高硅钢铸锭凝固组织几乎全是柱状晶,而且晶粒粗大。空冷条件下,等轴晶区扩大,但柱状晶仍占主要部分。缓冷条件下,等轴晶区占主要部分,晶粒平均面积和空冷条件下相当。 The solidification structure of 6. 5% Si steel ingot was simulated based on CAFE method and the model suitable for simulating the structure of high silicon steel wad ascertained. The influence of superheat and cooling condition on the solidification structure were studied. It was shown that with the superheat decreasing,the proportion of columnar crystals decrease,and the average grain size become smaller. Under water cooling condition,the solidification structure of casting was composed of almo... 

森吉米尔二十辊轧机是冷轧电工钢的主要机型,具有整体刚度大,辊径小,轧制道次压下量大,产品精度高等特点,简要介绍了近年来冷轧电工钢森吉米尔二十辊轧机领域进展,在轧机结构、厚度自动控制、板形自动控制等方面的技术及研究。 20-h Sendzmir reversible mill is the main type of cold rolled electrical steel which has the characteristic of high integral stiffness,small roller diameter,high pass reduction and high product quality.In this paper,the recent progress of frame structure,automatic gauge control,automatic flatness control of Sendzmir mill is introduced. 

本实用新型涉及板材加工设备领域，具体为变压器铁芯硅钢片打磨设备，包括本体，本体内部开设有工作腔，本体内部设置有用于运输硅钢片的运输机构，本体内部设置有用于打磨硅钢片的打磨机构，本体内部设置有用检测硅钢片边缘整洁程度的检测机构，本实用新型通过运输机构和打磨机构进行配合从而对硅钢片进行去除毛刺和毛边，从而保证铁芯中每组硅钢片均不直接接触；通过检测机构对加工完成的硅钢片进行毛刺和毛边的检测，进一步保证了每组硅钢片的整体质量以及尺寸的精准。

本发明涉及一种取向硅钢热轧钢带的板形控制方法，所述取向硅钢热轧钢带的工艺流程包括铸坯加热过程、轧制过程及层流冷却过程；其中轧制过程中采取取向硅钢与普钢交叉轧制的方式；粗轧过程采取R1轧制1道次、R2轧制5道次的1+5轧制工艺，并控制轧制工艺参数；精轧过程中控制F1～F7轧制工艺参数。本发明通过设定合理的交叉轧制工艺及取向硅钢热轧工艺，使取向硅钢的轧制稳定性大幅提高，取向硅钢带形控制良好，凸度控制在30～50μm之内，楔形控制在30μm之内，板形平坦度控制在25iu之内；从而为冷轧工序提供了优质原料。

本实用新型公开了一种堆垛硅钢片接料装置，它涉及变压器零部件加工技术领域。导向滚轮沿平移轨道滚动带动接料底座沿平移轨道移动；接料底座上设有剪力臂架，升降油缸驱动剪力臂架调节高度带动滚筒架升降，滚筒架上安装有数排滚筒，滚筒为双链轮滚筒，每排的数个滚筒中，相邻滚筒间通过链条与链轮的配合连接，电机驱动一个滚筒转动带动一排的数个滚筒同时转动；每排的数个滚筒上方两侧分别设有导向槽板，导向槽板与滚筒架固定连接。本实用新型的优点在于：可对左右侧、不同层的硅钢片柱进行出料，可同时对多柱硅钢片进行出料，出料效率高；接料的稳定性提高，接料底座移动稳定性提高，接料后硅钢片柱可直接输送至叠装处，操作便捷，转运效率高。

冷轧无取向硅钢是高技术含量、高附加值产品,工艺复杂,生产周期长,过程控制难度大,被誉为钢铁产品中的\"工艺品\"。热轧生产工艺又是无取向硅钢生产的重中之重,直接决定了硅钢的铁损和电磁性等多项指标。 Cold rolled non-oriented silicon steel is high technology content、high addedvalue product. Its process is complex, Its production cycle is of Length, and Its Process control is difficult. Which is known as the iron and steel products \" Arts and crafts\". Hot rolling production process is the top priority of non-oriented silicon steel, Which Directly determines iron loss of the silicon steel and electromagnetic property, etc many index. 

本发明公开了一种免常化中间退火的无取向电工钢板，其各化学元素质量百分含量为：0＜C≤0.004％、Si：1.0～2.6％、Mn：0.2～1.0％、Al：0.2～1.6％、Ca：0.0003％～0.0035％，余量为Fe和其他不可避免的杂质。此外本发明还公开了上述无取向电工钢板的制造方法，其包括步骤：(1)冶炼和连铸，其中在该步骤不采用电磁搅拌；(2)热轧，其包括：粗轧、精轧、卷取和保温；其中控制粗轧之后、精轧之前的中间坯温度≥950℃；(3)上述热轧步骤后不进行常化中间退火或罩式炉中间退火而直接进行冷轧；(4)连续退火。本发明所述的无取向电工钢板通过采用合理的化学成分和工艺设计，可以在保证较低生产成本的同时，获得高磁感和低铁损的特性。

本实用新型公开了一种取向硅钢绝缘涂液用废液回收利用装置，涉及取向硅钢绝缘涂液技术领域，为解决现有取向硅钢绝缘涂液的废液在回收时没有进行多层热分解，导致回收利用率低的问题。所述下料筒的下端设置有调节筒，所述调节筒的下端设置有分流筒，所述分流筒的下端设置有出料筒，所述调节筒的内部设置有下料板，所述下料板的一端设置有转轴，所述转轴的一端设置有交流电机，所述下料板的侧表面设置有外接孔，所述下料筒的筒壁内设置有加热板，所述下料筒的内部设置有一级过滤网，所述分流筒的内部设置有隔挡板，所述隔挡板的一侧设置有二级过滤网。