硅钢资料

利用OM、EBSD等手段研究了热轧板两段式正火时在700℃保温不同时间(0、10、30、60 min)对含Sb冷轧无取向电工钢磁性能的影响。结果表明,700℃保温10 min处理的样品铁损最小,磁感最高。对成品板的组织分析结果表明,试样的晶粒尺寸随700℃保温时间的延长先增大后减小,保温10 min时晶粒尺寸达到最大;分析成品试样织构发现,有利织构组分随700℃保温时间的延长先增加后减少,保温10 min时有利织构组分所占百分比最高。因此,含Sb冷轧无取向电工钢两段式正火时在700℃保温10 min时磁性能最好。 Effect of two-stage normalization on magnetic property of non-oriented electrical steel containing antimony was investigated by using optical microscope(OM) and electron back-scattered diffraction technology(EBSD).The experimental results show that the iron loss and magnetic permeability of the specimen insulated at 700 ℃ for 10 min are lowest and highest respectively.The grain size of the finish specimens increases first and then decreases with the increase of holding time.Similarly,the advanta... 

对无取向硅钢炼钢全流程钢液增钛的原因进行了分析,认为铁水钛含量、转炉出钢温度、转炉下渣量、精炼渣TiO₂含量、钢水罐及RH浸入管混钢种生产是影响钢液增钛的主要原因。通过采取低钛铁水冶炼,减少转炉下渣量,提高出钢温度,添加白灰改质精炼渣等措施,均能够降低钢液中的钛含量。 After analyzing the causes leading to increased content of titanium in molten nonoriented silicon steel during whole steelmaking process, it was concluded that such factors as content of titanium in hot metal, tapping temperature from converter, quantity of roughing slag entered into the ladle from converter, content of TiO₂ in refining slag, molten steel ladle car,carrying out the steelmaking of different steel grades by the same ladle and same RH immersion tube were the main causes ... 

本实用新型公开了硅钢片生产用上料装置，属于硅钢片生产领域，包括本体，所述本体包括侧板和U型板，所述侧板固定连接在U型板的一侧，所述本体的顶部横向设置有平移机构，所述平移机构上安装有气缸，所述气缸的底部安装有吸盘，所述U型板内腔的底部竖向固定连接有弹簧，所述弹簧远离U型板的一端水平固定连接有升降板，所述平移机构包括电机、螺纹杆、限位板和移动块，所述电机安装在侧板的顶部，所述电机的输出轴与螺纹杆的一端固定连接，通过设置弹簧，在第一个物料从上料装置移出后弹簧的弹力推动剩余物料，使得剩余物料进行上升，避免吸盘触碰不到物料的问题，简化吸盘移动轨迹，加快上料速度。

本申请提供了一种取向硅钢铸坯的制备方法及铸坯系统，该制备方法用于对精炼后的钢水进行连铸处理，所述连铸处理包括以下步骤：进行凝固处理，以使所述精炼后的部分钢水凝固形成坯壳；凝固处理时，进行电磁搅拌，以使所述精炼后的剩余钢水最终形成铸坯，其中，所述电磁搅拌的位置和结晶器出口的间距为0.3～1.5m，所述电磁搅拌的电流范围为0A～900A。上述制备方法通过调节电磁搅拌的位置和电流大小来调节电磁搅拌的强度，进而通过电磁搅拌的强度来调节等轴晶的生成量，扩大等轴晶率的范围。

本实用新型公开了一种硅钢片焊接模具，包括底座，底座上均匀排布有多条滑槽，每条滑槽内连接有一根垂直设置的定位杆，定位杆底部穿过底座连接一气缸，气缸连接在底座底部。本实用新型结构设计合理巧妙，移动不同位置的定位杆，将定位杆与硅钢片贴合，不同滑槽内的定位杆之间相互错位，并利用气缸将硅钢片定位，这种结构不可以适用于各种形状的硅钢片，使用方便快捷。

本实用新型公开了一种成品取向硅钢片加工用的卷绕装置，包括机箱和卷绕机，所述机箱的下表面固定安装有底座，所述机箱的一侧表面靠近上方固定安装有控制箱，所述机箱的两侧表面靠近前方固定安装有伸缩机，所述机箱的前端面固定安装有挡板，所述挡板的前端设有卷绕机，所述底座的上表面且位于卷绕机的下方固定安装有定位筒，所述定位筒的内部活动安装有托杆。本实用新型所述的一种成品取向硅钢片加工用的卷绕装置，可以有效的控制卷绕机卷绕取向硅钢片的厚度，从而保证每次卷绕取向硅钢片的厚度都相同，利用伸缩机可以对不同宽度的取向硅钢片进行边缘位置的夹紧，并且可以控制卷绕板与卷绕机之间的间距，从而控制卷绕后取向硅钢片的内径大小。

分析了影响脱碳效果和结晶行为的各种要素及其相互制约关系,提出了Hi-B连续退火工艺曲线,总结得出快速加热及合理稳态气氛是实现工艺制度的关键。结合实际工程,介绍了在连续退火炉设计中快速加热和气氛设计的考虑方法,并指出随着Hi-B产品的发展,如何改进这些方法将是连退工程研发的方向之一。 The factors which affect decarbonization and crystallization and the mutual restriction between them were analyzed.A complete continuous annealing process for Hi-B was put forward.As a result,the rapid heating and the proper steady atmosphere were two important factors.According to an actual project,the consider methods for designing rapid heating and proper steady atmosphere were introduced,and it is pointed that with the development of Hi-B technique,how to improve these techniques would be on... 

本实用新型提供了一种去角硅钢片铁芯加工用的吊装装置，包括安装板，所述安装板下设有防护筒，所述防护筒包括左半筒和右半筒，所述安装板上设有移动组件，所述移动组件包括气缸，所述气缸连接有伸缩杆，所述伸缩杆另一端连接有安放框架；所述左半筒和右半筒底壁皆设为开口状且侧壁上设有连通槽，所述左半筒和右半筒上分别设有防护组件，所述防护组件包括异型板和连接盒，所述异型板底部连接有固定板，所述固定板和连接盒之间连接有挤压弹簧，所述挤压弹簧内部设有传动杆，所述左半筒和右半筒内部两侧分别设有防护板。本实用新型可以有效挂住硅钢片，不会挤压坏封胶，且具有防护措施。

介绍了普通取向硅钢(CGO)和高磁感取向硅钢(Hi-B)铸坯高温加热两次冷轧、一次冷轧和铸坯低温加热两次冷轧、一次冷轧法4种成熟生产工艺的主要技术参数,取向硅钢理论研究(Goss晶核和抑制剂)和生产技术现状。取向钢的发展趋势为:提高(110)[001]晶粒取向度,降低取向硅钢铁损,发展铸坯低温加热(≤1 300℃)和薄板坯连铸连轧流程生产取向硅钢工艺。 Main technology parameters of four developed process:cast bloom higher temperature heating-double cold rolling or single cold rolling,lower temperature heating-double cold rolling or single rolling process for production of common grain oriented silicon steel(CGO) and high magnetic induction grain oriented silicon steel(Hi-B),theory research on grain oriented steel(Goss nucleus and inhibitor) and present situation of process are summarized in this paper.The development trend of grain oriented si... 

利用X-射线衍射织构分析和线形分析技术测定了交叉轧制双取向硅钢在制备工艺各阶段的织构及微结构,进而探讨了立方织构({100}<001>)的形成过程。通过对实验结果的分析可知,二次冷轧和交叉轧制工艺为立方织构提供了内能优势和有利的形变织构,而低温预退火工艺既强化了立方织构的内能优势,又为立方织构的异常长大提供了有利的组织保证,最终在抑制剂(AlN和MnS)的协同作用下,硅钢在二次再结晶退火后形成了强烈的立方织构。 The texture and substructure of the double oriented electrical steels produced by the cross rolling technology during the difference process has been measured by means of the X-ray texture and diffraction peak profile analysis technology,and research the formation mechanism of cube texture,{100}<001>.The results show that the dominances of inner energy and deformation texture were supplied by secondary cold rolling and the cross rolling technology and strengthened by pre-annealing at a low... 

本发明涉及一种含磷无铝高效无取向硅钢生产方法，生产方法取消常化工艺，具体步骤如下：1)将钢水冶炼至目标成分后，浇铸成坯；2)板坯热装，热装温度≥500℃，热轧板坯加热炉均热段板坯温度1150～1200℃；终轧温度控制在860～930℃，卷取温度700～800℃3)酸洗后冷轧，控制冷轧整体压下率80％以内，至成品厚度；4)连续退火炉快速加热段温度设定1050～1180℃，增加有利织构组织形核，均热段温度设定830～950℃，全氮气干气氛保护，退火工艺速度120～150m/min，满足晶粒度8～4级。本发明不需进行热轧卷常化处理，降低了制造成本。

本实用新型公开了E字型硅钢片的级进模冲压装置，属于冲压模具设备领域，所述下模具包括与冲孔凸模、冲方孔凸模、切断凸模分别对应且相适配的冲孔凹模、冲方孔凹模、切断凹模，所述上模具上设有对条料板进行输送的导料板，所述冲孔凸模、冲孔凹模均设有两对并且并排设置，且每对冲孔凸模、冲孔凹模均设有两个，每个所述冲孔凸模、冲方孔凸模、切断凸模的顶端均用微米级间隙固定安装于上模具上，所述冲孔凹模、冲方孔凹模、切断凹模的底端均用微米级间隙固定安装在下模具上。本实用新型中各个凸、凹模分别采用硬质合金拼块、镶块式的结构并用微米级间隙固定安装在上、下模具上，这样不仅可节省材料的费用，同时还便于人们后期对模具的维修和使用。