硅钢资料

取向硅钢因其高磁导率、低矫顽力和大电阻系数等特性，被广泛应用于大中型变压器和大型电动机铁芯的制造。因取向硅钢性能和成分控制严格，生产工艺复杂，故其产品代表了钢铁企业特殊钢生产的最高水平。本文介绍了新钢公司卷板厂1580热连轧线生产取向硅钢过程中出现的窄尺问题，研究了取向硅钢产品的特点，分析了热轧过程中的组织转变，并结合生产实际提出了改进措施。通过对加热炉钢坯加热模式、粗轧轧制策略、精轧轧制工艺、二级模型等方面的优化和改进，取向硅钢窄尺情况明显好转，提高了产品的成材率和市场口碑。 The oriented silicon steel is widely used in the iron core manufacture of large and mediumsized transformers and large motors because of its high permeability, low coercivity and large resistance coefficient. Due to the performance and composition control of oriented silicon steel is strict, the production process is complex,therefore, its products represent the highest level of special steel production in iron and steel enterprises. This paper introduces the problem of narrow gauge in the produ... 

本申请提供了一种提高高磁感取向硅钢渗氮效率的方法，属于高磁感取向硅钢渗氮处理技术领域，包括所述高磁感取向硅钢按重量百分比包括：Si：2.8～3.4％、C：0.040～0.070％、Als：0.015～0.045％、Mn：0.06～0.14％、S：0.003～0.020％、N：0.003～0.010％、Cu：0.01～0.025％、Sn：0.03％～0.07％、Cr及Ni，Cr和Ni的总含量小于0.5％，其余为Fe和不可避免杂质物，其特征在于，控制脱碳退火后钢带表层氧化物中铁系氧化物的比例，该装置能够增加脱碳退火后钢带表面氧化层中铁系氧化物占整个氧化层重量的比例，从而在获得同等渗氮量的情况下实现了快速渗氮，缩短渗氮时间，提高渗氮效率。

本发明公开了一种硅钢片冲压设备及其使用方法，包括底座，所述底座顶部的左侧固定连接有侧板，所述侧板表面的中心处开设有限位滑孔，所述底座内腔底部的左侧固定连接有伺服电机，所述伺服电机的输出轴固定连接有螺纹杆。本发明通过设置伺服电机、螺纹杆、螺纹套和限位滑杆，能够带动支撑板和气缸进行高度调节，同时能够带动上板和冲压板进行高度调节，方便使用者适应不同厚度的硅钢片，同时支撑杆、套筒和复位弹簧能够带动顶板在不受力的情况下复位至活动槽的外部，方便使用，解决了现有的硅钢片冲压设备在使用时不能根据硅钢片的厚度进行冲压高度的调节，因此不能很好的适应使用需要的问题。

本发明涉及一种冷轧硅钢厚度缺陷识别方法、装置及系统，本发明的方法包括如下步骤：采集带钢设定厚度及其实际测量厚度并保存；将带钢实际测量厚度与带钢设定厚度相减得到实时厚度差；根据实时厚度差计算厚度缺陷评分；根据评分结果，确定带钢在厚度这一指标的缺陷等级。本发明评估过程考虑了厚度波动情况，并进行量化，能成功识别冷轧硅钢的厚度缺陷，设别准确性较高，提高了冷轧硅钢生产水平，为冷轧硅钢质量控制提供依据。

取向硅钢热轧板中织构梯度对发展完善的二次再结晶十分关键,通过添加铜可以显著降低取向硅钢板坯加热温度,从而影响热轧板织构分布。利用X射线衍射仪,分析了实验室模拟薄板坯连铸连轧(TSCR)工艺的3种不同铜含量的取向硅钢热轧板织构。结果表明:不同铜含量热轧板表面到厚度1/4处均为弱的热轧织构,热轧板心部主要为{100}面织构;铜含量约在0.4%时,热轧板次表层的{110}<001>织构比例最高,而热轧板心部的{100}<110>织构比例最低;铜含量对热轧织构中{114}<110>和{001}<100>织构发展有显著影响。 The texture gradient in hot rolled grain oriented silicon steel strip is one of the essential factors to achieve a perfect secondary recrystallization.The addition of copper can significantly reduce the slab reheating temperature of grain oriented silicon steel,so as to impact the texture distribution in the hot rolled strip.The texture of hot rolled grain oriented silicon steel strip as-rolled by thin slab casting and rolling process(TSCR) in laboratory with three different copper contents was ... 

本实用新型提供了一种带连接筋的硅钢盘，包括多个周向间隔排列的硅钢块，任意相邻的两所述硅钢块之间连接至少两连接筋，以将相邻的两所述硅钢块之间的空间分割为分设在所述硅钢盘轴向两侧的转子槽，及位于两所述转子槽之间的若干个收纳孔。多个所述硅钢块通过连接筋连接，并形成一整体的硅钢盘，相对现有技术独立成型多个硅钢块来说，不仅避免硅钢块丢失，还有效提升硅钢盘装配为转子盘的成型效率，以及保证各硅钢块在转子盘上的位置一致性，并且增加所述连接筋的数量，有效增强相邻两硅钢块的连接性能，从而大幅增强转子盘的机械可靠性。

采用电子背散射衍射技术测定50SW1300冷轧无取向硅钢中不同尺寸范围晶粒的含量,利用主成分回归分析法,综合研究不同尺寸范围晶粒的含量对无取向硅钢磁性能的影响。结果表明:通过主成分回归分析法能够从不同尺寸范围晶粒的含量的多个影响因素中获取主要的因素,定量研究它们对无取向硅钢磁性能的影响规律。分析表明,无取向硅钢的铁损与不同尺寸范围晶粒的含量之间存在着可靠的多元线性关系,在一定范围内,较大尺寸晶粒的含量越多,其对铁损优化的作用越明显;而无取向硅钢的磁感与不同尺寸范围晶粒的含量之间并无线性关系。 Distribution of grain size in cold rolled non-oriented silicon steel 50SW1300 was measured by EBSD.The effects of the distribution of grain size on magnetic properties of the non-oriented silicon steel were comprehensively researched by means of principal component regression method.The results indicate that the main factors influencing the magnetic properties in the distribution of grain sizes,which can be used to guantitative study the magnetlic properies of the steel,are obtained by principal... 

对低温加热工艺生产的以AlN为主抑制剂的高磁感取向硅钢高温退火过程进行中断实验,借助电子背散射衍射技术对高温退火过程中高斯晶粒的演变进行了研究.在升温过程中高斯晶粒平均尺寸先减小再增大.800℃时取向分布函数图出现高斯织构组分,但强度很弱,高斯晶粒偏离角在10°以上;900℃时高斯晶粒平均生长速率超过其他晶粒;950~1000℃时高斯晶粒异常长大,偏离角3°~6°;在1000℃之前高斯取向晶粒相比于其他晶粒没有尺寸优势. The high-temperature annealing process of high permeability grain-oriented silicon steel with AlN as an inhibitor was studied by interrupting test.The evolution of Goss texture in this process was analyzed by electron back-scattered diffraction.It is found that the Goss grain size first decreases and then increases with the rise of temperature.Goss texture appears in the orientation distribution function at 800 ℃,but the intensity is very weak and the deviation angle is more than 10°.The average... 

本实用新型公开了一种优化取向硅钢底层质量的打孔隔板，包括取向硅钢底层和分隔板，所述取向硅钢底层的上方安装有分隔板，且分隔板的内部设置有通孔，所述通孔的下方安装有卡合板，且卡合板的下方安装有硅胶密封垫，所述分隔板的右侧安装有三脚架，且三脚架的右侧安装有螺钉，所述三脚架的左侧安装有螺母，且三脚架的下方安装有固定横杆，所述分隔板的上方安装有定位套筒，且定位套筒的内部设置有内螺纹，所述内螺纹的内部安装有定位横杆，且定位横杆的两侧设置有外螺纹。该种优化取向硅钢底层质量的打孔隔板中，通过设置的通孔，分隔板将取向硅钢底层分隔时，通过通孔可以将分隔连通，减少在使用时分隔板阻拦取向硅钢底层的磁感性能。

借助光学显微镜、扫描电镜、交流磁性能测量仪和万能拉伸试验机研究了0.3 mm厚高强无取向电工钢冷轧板在780、820、860和900℃退火保温2 min后的组织、织构和性能。结果表明:在退火温度范围内,试验钢均发生了完全再结晶,得到等轴状的铁素体晶粒;随着退火温度的升高,平均晶粒尺寸从9.2μm增长到41.3μm,工频铁损和400 Hz高频铁损均先大幅减小后趋于平缓,磁感应强度先升高后降低。在820℃退火时,铁损P_1.5/50=5.51 W/kg,P_1.0/400=33.22 W/kg均处于较低值,磁感应强度B₅₀₀₀最大,为1.649 T。试验钢的屈服强度和抗拉强度均随退火温度的升高而降低,780℃退火时屈服强度为496 MPa, 900℃退火时降低至407 MPa。综合磁性能和力学性能考虑,试验钢的最佳退火温度是820℃。 Microstructure, texture and properties of 0.3 mm thick high strength non-oriented electrical steel cold rolled sheet annealed at 780 ℃, 820 ℃, 860 ℃ and 900 ℃ for 2 min were studied by means of optical microscope, scanning electron microscopy, AC magnetic property tester and universal tensile testing machine. The results show that in the annealing temperature range, complete recrystallization of the experimental steel occurs and equiaxed ferrite grains are obtained. With the increase of annealin... 

本发明属于冶金技术领域，涉及一种超短流程稀土取向硅钢及其制备方法，化学组成及其重量百分比为Si：2.0～4.5％，C：≤0.003％，Y：0.001～0.05％，Mn：0.15～0.35％，Al：0.03～0.04％，Cu：0～0.5％，S：0.025～0.04％，N：0.011～0.013％，其余为Fe和不可避免的杂质元素。制备工艺包括：钢水冶炼、薄带连铸、冷轧、再结晶退火。与常规生产方式相比，取消了连铸、粗轧、热连轧、常化和脱碳退火等工序，极大简化了生产流程。通过添加稀土元素钇，促进了抑制剂的析出，还显著细化了薄带连铸硅钢的凝固组织，提高组织均匀性，获得了均匀细小的等轴晶，优化了取向硅钢的性能。

根据本发明的一个实施例的粘接涂料组合物，其包含聚乙烯丙烯酸酯，所述聚乙烯丙烯酸酯包含由以下化学式1表示的重复单元和由以下化学式2表示的重复单元，所述聚乙烯丙烯酸酯包含65至90重量％的由以下化学式1表示的重复单元、10至35重量％的由以下化学式2表示的重复单元。