硅钢资料

本发明公开了一种精确控制高磁感取向硅钢板坯Als含量的方法，转炉出钢20～40秒时，定量加入金属铝，加入量按0.15～0.35kg/吨钢；转炉出钢及合金加入后，底吹搅拌均匀3～5min后，加入一定量金属铝后再底吹搅拌均匀3～5min后将钢水吊运至RH开始精炼处理，铝加入量按[WAls目标+(0.009～0.0120％)]范围控制；钢水在RH精炼过程经过2～3次酸溶铝的成分微调后结束精炼，精炼结束Als按[WAls目标+(0.0030～0.0045％)]目标范围控制；RH精炼结束样酸溶铝检测结果出来后，在连铸开浇前，在钢包内补加铝线使钢液中Als在[WAls目标+Δ浇注Als损]目标范围内；连铸进行氩气环流保护浇注，其中氩气环流流量控制在6～12m3/h；浇注成合格板坯后按正常工艺进行热轧及后工序生产。

介绍了CSP工艺生产无取向电工钢各工序的设备特点、采用的工艺控制手段和电工钢产品质量情况,结合生产实践证明了马钢CSP工艺开发的无取向电工钢产品丰富了薄板坯连铸连轧的品种结构,发挥了薄板坯连铸连轧生产无取向电工钢性能均一、稳定的特点。 The equipment characteristic,the process control method and the quality of non-orientated silicon steel by CSP process were introduced.Combined with the production situation,it is proved that production of non-orientated silicon steel developed on Masteel CSP line would enrich product structure of thin slab continuous casting and rolling,and it exerts stable performance of non-orientated silicon steel. 

本发明公开了一种基于硅钢服役特性的立体卷铁心单框损耗测量方法及系统，根据硅钢片在立体卷铁心中的服役特性，获得测量铁心单框所需的非正弦励磁电压波形，通过所述立体卷铁心的心柱绕组电压和单框绕组电压之间的关系，确定所述被测立体卷铁心单框所需的电压有效值，再通过计算机、数据采集卡D/A转换器、功率放大器、隔离变压器和示波器，直接在所述立体卷铁心单框上加载励磁电压，利用功率表测量立体卷铁心单框损耗。本发明利用硅钢的服役特性，获得测量立体卷铁心单框所需的非正弦励磁电压波形和电压有效值，再将励磁电压直接加载到被测立体卷铁心单框，测量立体卷单框铁心损耗。

采用光学显微镜、X射线衍射仪等分析了宁波钢铁有限公司生产的取向硅钢不同工序下的组织及织构演变规律。结果表明:铸坯经过热轧后,沿着厚度方向组织不均匀;一次冷轧并经脱碳退火后,组织由条状纤维状变成等轴状的初次再结晶晶粒,初次再结晶平均晶粒尺寸为18.17μm,织构主要以α织构和γ织构为主;在二次冷轧后,晶粒再次被压缩,转变为纤维状,织构主要为γ织构;经过高温退火后,发生二次再结晶,晶粒异常长大,晶粒尺寸达到厘米级,织构成分为单一且锋锐的Goss织构。 The microstructure and texture evolution of oriented silicon steel produced by Ningbo Iron and Steel Co.,Ltd.were analyzed by optical microscope and X-ray diffraction.The results showed that the microstructure of the slab was inhomogenous along the thickness direction after hot rolling.After first cold rolling and decarburizing annealing,the microstructure changed from strip fibrous to equiaxed primary recrystallized grains,and the average grain size of the primary recrystallization microstructu... 

冷轧无取向硅钢是高技术含量、高附加值产品,工艺复杂,生产周期长,过程控制难度大,被誉为钢铁产品中的\"工艺品\"。热轧生产工艺又是无取向硅钢生产的重中之重,直接决定了硅钢的铁损和电磁性等多项指标。 Cold rolled non-oriented silicon steel is high technology content 、high added value product. Its process is complex, its production cycle is of length, and its process control is difficult, which is known as the iron and steel products \" Arts and crafts\". Hot rolling production process is the top priority of non-oriented silicon steel, which directly determines iron loss of the silicon steel and electromagnetic property,as well as other many index. 

本文介绍了无取向硅钢C6涂液的性能,研究了配水量、固化程度和涂层厚度等因素对无取向硅钢C6涂层性能的影响。结果表明,随着配水量的增加,完全固化所需的时间增加,涂液固体含量降低,涂层厚度减小;随着固化程度的提高,涂层硬度先增大然后趋于恒定,而柔韧性逐渐变差,在过固化后急剧恶化;涂层厚度对涂层的表面外观、附着性和绝缘层间电阻均有显著影响。 Based on the introduction about the performance of C6 varnish for non-oriented silicon steel sheets,effects of water amount,curing degree and coating thickness are discussed. Results show that with the increase of water amount,the time required to cure completely extends,and both the solid content of C6 varnish and the coating thickness decrease. As the curing degree increases,the hardness of the coating increases first and then tends to be constant,however the flexibility degenerates,especially... 

无取向硅钢特别是中牌号以上的无取向硅钢,随着含硅量的提高,常温下塑性较差,冷轧过程中轧制力明显提高,如果存在原料质量问题,极易发生断带事故,影响硅钢冷轧过程的成材率和生产效率。通过优化冷轧工艺参数,可提高冷轧稳定性。生产中通过合理分配冷轧各道次压下量和轧制速度,保证了轧制过程的稳定,很大程度减少了冷轧断带事故的发生。 Non-oriented silicon steel, especially in the low and middle grade, with the increase of silicon content, plasticity is poor at room temperature, rolling force in cold rolling process significantly improved .If there is the quality defect of raw materials , easily sheet is rolling off. Affect finished product rate and production efficiency in process of cold-rolled silicon steel. Through optimization of cold rolled process parameter , improve the stability of cold-rolling process. Through reason... 

本发明公开了一种硅钢冷连轧轧制过程温度获取方法、装置及电子设备，通过获取硅钢冷连轧生产过程的工业参数数据以及各机架间硅钢的实际温度测试数据，然后基于工业参数数据以及预设初始模型，确定硅钢冷连轧生产过程的温度预测模型，接着基于硅钢轧制前的预热温度以及温度预测模型，得到硅钢冷连轧轧制过程各机架变形区出口与下一机架变形区入口之间的预测温度数据，再将预测温度数据与实际温度测试数据进行对比，并根据对比结果中的温度差异值对相应机架间的乳化液参数进行修正，直至温度差异值小于预设阈值，得到修正后的温度预测模型，能够用于实现硅钢冷连轧轧制过程中，任意采样点硅钢温度的获取。

本实用新型公开一种电机加工硅钢片上料装置，包括上料底座，上料底座的顶部固定连接有若干个硅钢片卷料限位柱，上述装置还包括设置在上料底座上方的上料顶座，上料顶座的底部固定连接有若干个与硅钢片卷料限位柱配合的定位柱，上料底座与上料顶座之间滑动连接有两个对称设置的滑动螺杆，滑动螺杆滑动连接所述上料顶座，滑动螺杆的上端螺纹连接有装配螺母，上料底座的左右侧壁部位均装配有第一折形板，上料顶座左右侧壁部位均装配有与第一折形板对称设置的第二折形板，第一折形板与第二折形板之间装配有悬吊组件。采用上述方式不仅实现将若干个硅钢片卷料采用一个夹持定位设备进行夹持定位，且上述装置部件设计安全上料。

本实用新型提供了一种带连接筋的硅钢盘，包括多个周向间隔排列的硅钢块，任意相邻的两所述硅钢块之间连接至少两连接筋，以将相邻的两所述硅钢块之间的空间分割为分设在所述硅钢盘轴向两侧的转子槽，及位于两所述转子槽之间的若干个收纳孔。多个所述硅钢块通过连接筋连接，并形成一整体的硅钢盘，相对现有技术独立成型多个硅钢块来说，不仅避免硅钢块丢失，还有效提升硅钢盘装配为转子盘的成型效率，以及保证各硅钢块在转子盘上的位置一致性，并且增加所述连接筋的数量，有效增强相邻两硅钢块的连接性能，从而大幅增强转子盘的机械可靠性。

针对本钢薄板坯铸机在生产无取向电工硅钢的过程中存在的铸坯拉断、中包增碳、增氮等问题,进行了连铸工艺优化。通过采用新型无碳中间包覆盖剂、环保中间包干式料及专用结晶器保护渣后,降低了铸坯增碳量;通过控制钢包到中间包的增氮环节,降低钢水增氮;适当增大二冷水量,控制钢水过热度,防止铸坯拉断等生产事故的发生。改进工艺后,精炼后到成品铸坯的平均增碳量能控制在10×10-6以内,平均增氮量能控制在4×10-6以内。 The technology optimization has been adopted for preventing nitrogen increasing and carbon increasing in Benxi thin slab producing non-oriented silicon steel.Measures accordingly were adopted and satisfactory results were achieved. 

本发明提供能够制造磁特性与被膜密合性优异的电磁钢板的新颖并且得以改良的电磁钢板的制造方法。一种电磁钢板的制造方法，其特征在于，其包括以下工序：使电磁钢板与溶液相接触，所述电磁钢板以质量％计含有C：超过0％且0.10％以下、Si：2.5％以上且4.5％以下、Mn：0.01％以上且5.0％以下、S、Se及Te中的1种或2种以上的合计：超过0％且0.050％以下、酸可溶性Al：超过0％且5.0％以下、N：超过0％且0.015％以下、P：超过0％且1.0％以下、剩余部分由Fe及杂质构成，其中，上述溶液含有Cu、Hg、Ag、Pb、Cd、Co、Zn及Ni中的1种或2种以上，各元素的浓度合计为0.00001％以上且1.0000％以下。